KR20110098224A - Biodegradable resin composition - Google Patents
Biodegradable resin composition Download PDFInfo
- Publication number
- KR20110098224A KR20110098224A KR1020100017726A KR20100017726A KR20110098224A KR 20110098224 A KR20110098224 A KR 20110098224A KR 1020100017726 A KR1020100017726 A KR 1020100017726A KR 20100017726 A KR20100017726 A KR 20100017726A KR 20110098224 A KR20110098224 A KR 20110098224A
- Authority
- KR
- South Korea
- Prior art keywords
- starch
- resin composition
- molded article
- plastic molded
- biodegradable polymer
- Prior art date
Abstract
본 발명은 생분해성 고분자 수지, 원두커피분말 및 전분을 포함하는 수지 조성물에 관한 것으로, 이로부터 형성된 물품은 환경 친화적이고 저렴하여 일회용 소재로 사용할 수 있다. The present invention relates to a resin composition comprising a biodegradable polymer resin, coffee beans and starch, the article formed therefrom is environmentally friendly and inexpensive and can be used as a disposable material.
Description
본 발명은 생분해성 고분자 수지, 원두커피분말 및 전분을 포함하는 수지 조성물과 이로부터 형성된 물품에 관한 것이다.
The present invention relates to a resin composition comprising a biodegradable polymer resin, coffee beans powder and starch, and an article formed therefrom.
일반적으로 음식점이나 가정에서 식사를 할 때, 식탁 위에 식사도구를 올려놓게 되는데, 식탁이 청결하지 않을 경우에는 식탁 위의 이물질이 수저에 묻을 염려가 있고, 식사도중에도 식탁 위에 수저를 올려놓게 되면, 수저의 사용 과정 중 수저에 묻은 음식물이 식탁에 묻어 비위생적이다. In general, when eating at a restaurant or at home, utensils are placed on the table. If the table is not clean, foreign objects on the table may get stuck on the table. If the table is placed on the table during meals, During the use of the cutlery, food on the cutlery is unsanitary because it is buried on the table.
따라서 식사도구를 식탁 위에 놓을 때, 식사도구의 사용부분이 식탁에 닿지 않도록 하는 받침대를 많이 사용하고 있으며, 통상적인 받침대는 소정의 높이를 가지는 직육면체의 받침몸체를 구비하여 받침몸체의 상면에 수저가 미끄러져 떨어지지 않도록 하는 복수개의 오목홈을 형성한 구조로 되어 있다. Therefore, when placing the eating utensils on the table, a lot of pedestals are used to prevent the use of the eating utensils from touching the dining table. A typical pedestal is provided with a cuboid body having a predetermined height and a cutlery is placed on the upper surface of the supporting body. It has a structure in which a plurality of concave grooves are formed so as not to slip.
그러나 이러한 받침대는 도자기, 금속, 나무 등의 재질로 제작되고 사용후 세척, 건조 등의 위생처리를 하여 재사용하여야 하는데, 이는 제조단가가 비싸고, 분실 위험 및 세척상의 번거로움이 존재한다. 또한 음식점 또는 가정에서 충분한 세정 과정 없이 재사용하는 경우가 대부분이어서 비위생적이라는 문제가 있다. However, these pedestals are made of ceramics, metal, wood, and the like, and must be reused by using sanitary treatments such as washing and drying after use, which is expensive to manufacture, and there is a risk of loss and hassle. In addition, there is a problem that it is unsanitary because most of the reuse in restaurants or homes without sufficient cleaning process.
따라서 필요에 따라 1회용으로 사용하고, 폐기시에도 자연계에 영향을 주지 않는 친환경적이고, 저렴한 소재의 개발이 요구된다.
Therefore, it is required to develop an eco-friendly and inexpensive material that is used once as needed and does not affect the natural world even when disposed.
따라서 상기 문제점을 해결하기 위하여, 본 발명의 일 실시예는 친환경적이고 저렴한 소재를 사용한 플라스틱 성형품을 제공한다.
Therefore, in order to solve the above problems, an embodiment of the present invention provides a plastic molded article using an environmentally friendly and inexpensive material.
상기 과제의 해결을 위해, 본 발명의 실시예들은 생분해성 고분자 수지, 원두커피분말 및 전분을 포함하는 수지 조성물을 제공한다.In order to solve the above problems, embodiments of the present invention provides a resin composition comprising a biodegradable polymer resin, coffee beans powder and starch.
또한 본 발명의 실시예들은 상기 수지 조성물로부터 형성된 플라스틱 성형품을 제공한다. Embodiments of the present invention also provide a plastic molded article formed from the resin composition.
또한 본 발명의 실시예들은 전분과 원두커피분말을 혼합하고 건조하여 건조물을 제조하는 단계;In addition, embodiments of the present invention comprises the steps of mixing and drying the starch and ground coffee powder to prepare a dried product;
상기 건조물을 파쇄하여 직경이 2 내지 5mm인 입자를 얻는 단계;Crushing the dried product to obtain particles having a diameter of 2 to 5 mm;
상기 입자와 생분해성 고분자 수지를 혼합하여 혼합물을 제조하는 단계 및Preparing a mixture by mixing the particles with a biodegradable polymer resin, and
상기 혼합물을 압축 성형하는 단계를 포함하는 플라스틱 성형품의 제조방법을 제공한다.
It provides a method for producing a plastic molded article comprising the step of compression molding the mixture.
본 발명의 일 실시예에 따라 제조된 플라스틱 성형품은, 제조비용이 저렴하고 생분해성 소재로 이루어진 바, 1회용으로 사용한 후 폐기가 가능하여 위생적이고 친환경적이다. 또한 다공성 원두커피 분말로 인해 냄새 제거 효과도 가지는 바, 식사 도구 받침용으로 유용하게 사용할 수 있다.
Plastic molded article manufactured according to an embodiment of the present invention, the manufacturing cost is low and made of biodegradable material, can be discarded after use for a single use is hygienic and environmentally friendly. In addition, it has a deodorizing effect due to the porous coffee beans powder, it can be usefully used as a meal stand.
본 발명의 실시예들은 생분해성 고분자 수지, 원두커피분말 및 전분을 포함하는 수지 조성물을 제공한다. Embodiments of the present invention provide a resin composition comprising a biodegradable polymer resin, coffee beans powder and starch.
본 발명의 발명자들은 환경 친화적인 생분해가 가능한 제품을 만들기 위해 생분해성 고분자 수지를 사용하여 플라스틱 성형품을 제조하고자 하였는데, 이의 값이 저렴하지 않아 일회용 제품으로 만들기에는 많은 어려움이 존재하였다.The inventors of the present invention attempted to manufacture plastic molded articles using biodegradable polymer resins in order to make environmentally friendly biodegradable products. However, the present inventors have had many difficulties in making disposable products because their values are not inexpensive.
따라서 생분해성 고분자 수지의 함량을 낮추기 위하여 적합한 충전제를 찾던 중, 원두커피 분말이 냄새제거 효능이 있고 수지와의 친화성이 좋다는 점을 발견하였고, 특히 원두커피분말은 사용 후 그냥 폐기되는 것으로, 이를 사용한다면 경제적인 측면이나 폐기물 재활용 측면에서 많은 도움이 되므로 이를 충전제로 사용하고자 하였다. Therefore, while searching for a suitable filler to lower the content of the biodegradable polymer resin, it was found that the coffee bean powder has an odor removal effect and good affinity with the resin, and in particular, the coffee bean powder is discarded after use. If it is used, it would be very helpful in terms of economics and waste recycling, so I wanted to use it as a filler.
그러나 저렴한 소재를 사용하여도 제조공정에서 많은 비용을 부담해야 한다면 원가가 높아질 것이고, 이를 방지하기 위해서는 저렴하고 간단한 제조공정을 이용해야 했다. 그런데 통상적으로 사용되는 압출 또는 사출 성형 방식은 고가의 가공기와 금형을 이용해야 하므로 제품의 가격이 올라가며, 마스터 배치를 만들기 위해서 많은 시간이 소요되고, 압출기 또는 사출기를 이용할 시 원두커피분말이 지나치게 곱게 분쇄되어 충전효과가 감소하게 된다는 단점이 존재하였다. 따라서 본 발명의 발명자들은 압축공정(compression molding)이라는 간단한 제조공정을 사용하였다. However, even if cheap materials were used, the cost would be high if the manufacturing process had to be expensive. To prevent this, a cheap and simple manufacturing process had to be used. However, the conventional extrusion or injection molding method requires expensive processors and molds, which increases the price of the product, takes a lot of time to make a master batch, and when the extruder or the injection machine is used, the ground coffee powder is too finely ground. There was a disadvantage that the filling effect is reduced. The inventors of the present invention therefore used a simple manufacturing process called compression molding.
그러나 압축 공정을 통해 플라스틱 성형품을 제조할 때, 생분해성 고분자 수지 입자에 비해 원두커피분말의 입자가 작기 때문에, 원두커피분말이 수지 입자 사이로 통과하여 한쪽으로 몰리는 현상이 발생하였다. 따라서 원두커피 분말의 입자 크기를 생분해성 고분자 수지 입자 크기에 맞게 가공하는 공정이 필요한데, 원두커피 분말 입자들끼리 적절히 뭉칠 수 있도록 전분을 구성요소로 추가하여 상기 몰림 현상을 없앰으로써 본 발명을 완성하였다.
However, when the plastic molded article is manufactured through the compression process, since the coffee bean powder particles are smaller than the biodegradable polymer resin particles, the coffee bean powder passes between the resin particles and is driven to one side. Therefore, a process for processing the particle size of the coffee beans powder to the biodegradable polymer resin particle size is required, and the starch is added as a component so that the coffee beans powder particles can be properly agglomerated to complete the present invention by eliminating the drooping phenomenon. .
본 발명의 한 구체예에서 상기 생분해성 고분자 수지는 사용 중에는 일반 고분자 수지와 같이 우수한 성질을 나타내고, 사용 후 폐기시 토양의 미생물에 의해 쉽게 분해되는 특성을 가지고 있는 물질로, 구체적으로 이에 제한되는 것은 아니나, 옥수수 등 곡물에서 추출한 당을 발효하여 생성된 락트산(Lactic acid)을 모노머로 하여 제조되는 폴리락틱산(polylactic acid 또는 polylactide), 폴리글리콜릭산, 폴리카프로락톤, 폴리하이드록시알카노에이트, 폴리에틸렌 석시네이트 및 폴리부틸렌 석시네이트로 이루어진 군에서 선택된 어느 하나 이상일 수 있다. In one embodiment of the present invention, the biodegradable polymer resin exhibits excellent properties as a general polymer resin during use, and has a property of being easily decomposed by microorganisms in the soil when discarded after use. However, polylactic acid (polylactic acid or polylactide), polyglycolic acid, polycaprolactone, polyhydroxyalkanoate, polyethylene, produced by fermenting sugar extracted from grains such as corn, as a monomer. At least one selected from the group consisting of succinate and polybutylene succinate.
본 발명의 또다른 구체예에서, 상기 원두커피분말은 커피나무 열매(Cherry)의 껍질을 벗기고 건조시킨 생두(green bean)를 볶은 후 분쇄한 것으로, 원액을 추출한 후의 것을 사용하는 것이 좋으며, 보다 구체적으로는 커피전문점, 패스트푸드점, 또는 가정 등에서 원액을 추출하고 버리는 원두커피분말을 사용한다. 원두커피분말은 한번 추출되었다 해도 커피 고유의 향기를 그대로 담고 있어 제품화 한 경우 사용자에게 좋은 냄새를 제공할 수 있으며, 다공성으로 인해 주위의 냄새를 흡수하는 효과도 있다. In another embodiment of the present invention, the ground coffee powder is ground by peeling the coffee beans and peeled and dried green beans, it is preferable to use the one after extracting the stock solution, more specifically For example, coffee beans, which are extracted from the coffee shop, fast food restaurant, or home, are discarded. Even if the coffee beans are extracted once, they contain the unique aroma of coffee as it is, and if they are commercialized, they can provide a good smell to the user.
본 발명의 또다른 구체예에서, 상기 전분은 옥수수전분, 감자전분, 밀전분 및 타피오카전분으로 이루어진 군에서 선택된 어느 하나 이상을 사용할 수 있다. In another embodiment of the present invention, the starch may be any one or more selected from the group consisting of corn starch, potato starch, wheat starch and tapioca starch.
본 발명의 또다른 구체예에서 원두커피 분말의 양은 전분 100중량부 대비 40 내지 900중량부, 100 내지 500 중량부 또는 120 내지 200중량부가 적당하다. In another embodiment of the present invention, the amount of ground coffee powder is suitably 40 to 900 parts by weight, 100 to 500 parts by weight or 120 to 200 parts by weight relative to 100 parts by weight of starch.
본 발명의 또다른 구체예에서, 전분 및 원두커피 분말 혼합물의 양은 생분해성 고분자 수지 100중량부 대비 0.001 내지 70중량부, 10 내지 65중량부, 또는 20 내지 60중량부가 적당하다.
In another embodiment of the present invention, the amount of starch and ground coffee powder mixture is suitably 0.001 to 70 parts by weight, 10 to 65 parts by weight, or 20 to 60 parts by weight relative to 100 parts by weight of the biodegradable polymer resin.
또한 본 발명의 실시예들은 상기 생분해성 고분자 수지, 원두커피분말 및 전분을 포함하는 수지 조성물로부터 형성된 플라스틱 성형품을 제공한다. In addition, embodiments of the present invention provides a plastic molded article formed from a resin composition comprising the biodegradable polymer resin, coffee beans and starch.
상기 플라스틱 성형품은 압축 공정을 통하여 제조될 수 있으며, 압축 공정에서 제조할 수 있는 임의의 모양이 모두 가능하다. 이는 제조비용이 저렴하고 생분해성 소재로 이루어진 바, 1회용으로 사용한 후 폐기가 가능하여 위생적이고 친환경적이다. The plastic molded article can be produced through a compression process, and any shape that can be produced in the compression process is possible. It is made of cheap biodegradable material and can be disposed of after being used for one time, which is hygienic and environmentally friendly.
본 발명의 한 구체예에 따르면, 플라스틱 성형품은 식사 도구 받침용일 수 있는데, 이는 식사 도구의 음식에 닿는 부위가 식탁과 접촉하는 것을 방지하기 위한 물품으로써, 이러한 목적을 위해 통상적으로 사용되는 임의의 형태로 제조될 수 있다. 상기 식사 도구는 식사시 음식과 접촉하며 사용되는 모든 기구, 장치등을 의미하며, 구체적으로는 숟가락, 젓가락, 나이프, 포크, 국자, 주걱 등이 있으나 이에 제한되는 것은 아니다. According to one embodiment of the invention, the plastic molded article may be for a meal utensil support, which is an article for preventing the food contact portion of the eating utensil from coming into contact with the table, in any form commonly used for this purpose. It can be prepared as. The meal utensil means all utensils, devices, etc. used in contact with food during a meal, and specifically, but not limited to a spoon, chopsticks, a knife, a fork, a ladle, a spatula, and the like.
본 발명의 한 구체예에 따르면, 플라스틱 성형품은 여러번 사용할 수 있으나, 제조비용이 저렴하고 생분해성 소재로 이루어진 바, 필요에 따라 일회용으로 사용할 수 있다.
According to one embodiment of the present invention, the plastic molded article can be used many times, but the manufacturing cost is low and is made of a biodegradable material, it can be used as a disposable if necessary.
또한 본 발명의 실시예들은 전분과 원두커피분말을 혼합하고 건조하여 건조물을 제조하는 단계; 상기 건조물을 파쇄하여 직경이 2 내지 5mm인 입자를 얻는 단계; 상기 입자와 생분해성 고분자 수지를 혼합하여 혼합물을 제조하는 단계 및 상기 혼합물을 압축 성형하는 단계를 포함하는 플라스틱 성형품의 제조방법을 제공한다. In addition, embodiments of the present invention comprises the steps of mixing and drying the starch and ground coffee powder to prepare a dried product; Crushing the dried product to obtain particles having a diameter of 2 to 5 mm; It provides a method for producing a plastic molded article comprising the step of preparing a mixture by mixing the particles and the biodegradable polymer resin.
이하 각 단계를 보다 상세히 설명한다. Each step will be described in more detail below.
전분과 원두커피분말을 혼합하고 건조하여 건조물을 제조하는 단계에서, 전분은 겔상의 전분을 사용할 수 있으며 이는 전분과 물을 혼합하고 저어주는 방법으로 제조된다. 이때 물의 온도는 40 내지 80℃, 50 내지 70℃, 또는 55 내지 65℃가 적당하다. In the step of mixing the starch and ground coffee powder and drying to prepare a dried product, the starch may be gelled starch, which is prepared by mixing and stirring starch and water. At this time, the temperature of the water is suitable 40 to 80 ℃, 50 to 70 ℃, or 55 to 65 ℃.
겔상의 전분과 원두커피분말을 혼합하면 페이스트 형태가 되는데, 이를 넓은 판에 도포하여 건조시킨다. 도포시의 두께는 1 내지 15mm, 1 내지 10mm, 또는 1 내지 5mm 가 적당하다. 건조시에는 오븐을 이용할 수 있으며, 자연 건조하여도 무방하다. When the gelled starch and the ground coffee powder are mixed, they form a paste, which is applied to a wide plate and dried. The thickness at the time of application | coating is 1-15 mm, 1-10 mm, or 1-5 mm is suitable. An oven may be used for drying, and may be naturally dried.
상기 혼합시에 원두커피분말의 양은 전분 100중량부 대비 40 내지 900중량부, 100 내지 500 중량부 또는 120 내지 200중량부가 적당하다. At the time of the mixing, the amount of coffee beans is 40 to 900 parts by weight, 100 to 500 parts by weight or 120 to 200 parts by weight relative to 100 parts by weight of starch.
건조물을 파쇄하여 직경이 2 내지 5mm인 입자를 얻는 단계는, 건조물에 충격을 가하여 부숴 원하는 크기의 입자를 얻는 단계이다. 건조 후에는 건조물에 자연적으로 많은 균열이 생기게 되는데, 여기에 충격이 가해지면 뭉친 알갱이로 용이하게 부서질 수 있다. 따라서 상기 건조물을 파쇄하여 입자의 크기가 생분해성 고분자 수지 입자의 크기와 같거나 약간 작은 것을 얻는데, 직경이 2 내지 5mm인 입자가 적당하다. 필요한 경우 체(sieve)를 사용할 수 있는데, 체의 매쉬 번호로는 4 내지 10번 정도가 적당하다. The step of crushing the dried product to obtain particles having a diameter of 2 to 5 mm is to obtain particles of a desired size by impacting the dried product. After drying, there are many cracks naturally in the building, which can be easily broken into agglomerated granules upon impact. Therefore, the dried product is crushed to obtain a particle having a size equal to or slightly smaller than that of a biodegradable polymer resin particle. Particles having a diameter of 2 to 5 mm are suitable. If necessary, a sieve may be used. As a mesh number of the sieve, 4 to 10 times are suitable.
상기 단계에서 전분과 혼합되는 커피 분말의 양이 전분 100중량부 대비 40중량부 이하이면 상대적으로 전분이 많아져 쉽게 부서지지 않고 큰 입자가 주로 생성될 수 있으며, 900중량부 이상이면 쉽게 부서지며 주로 작은 입자가 생성될 수 있다. If the amount of coffee powder mixed with starch in the above step is 40 parts by weight or less relative to 100 parts by weight of starch, relatively large amounts of starch may not be easily broken and large particles may be produced. Small particles can be produced.
상기 입자와 생분해성 고분자 수지를 혼합하여 혼합물을 제조하는 단계에서는 상기 전분과 원두커피 분말을 혼합하여 생성한 직경이 2 내지 5mm인 입자와 생분해성 고분자 수지를 혼합하는데, 이때 상기 입자의 양은 생분해성 고분자 수지 100중량부 대비 0.001 내지 70중량부가 적당하다. In the step of preparing a mixture by mixing the particles and the biodegradable polymer resin, a particle having a diameter of 2 to 5 mm and a biodegradable polymer resin produced by mixing the starch and ground coffee powder are mixed, wherein the amount of the particles is biodegradable. 0.001 to 70 parts by weight is suitable for 100 parts by weight of the polymer resin.
상기 혼합물을 압축 성형하는 단계에서는 상기 혼합 분말을 몰드에 투입하고 압축 성형하여 플라스틱 성형품을 제조한다. 플라스틱 성형품의 모양은 압축공정에서 제조할 수 있는 임의의 모양이 모두 가능하며, 이를 제조하기 위해서는 몰드를 이용하게 되는데, 몰드에는 제품의 형태를 만들기 위한 캐비티가 존재한다. 이 캐비티 안에 상기 혼합물을 투입하고 압력을 가하여 플라스틱 성형품을 제조한다. 몰드는 사용전에 미리 예열시키는 것이 좋으며, 예열 온도는 175 내지 220℃가 적당하다. 압력을 가하는 시간은 몰드의 온도에 따라 달라지나, 10 내지 40분 정도가 좋다. 몰드의 온도가 낮을 때는 보다 길게, 몰드의 온도가 높을 때는 보다 짧은 시간 압력을 가할 수 있다. In the compression molding of the mixture, the mixed powder is put into a mold and compression molded to prepare a plastic molded article. The shape of the plastic molded article can be any shape that can be manufactured in the compression process, and to manufacture it, a mold is used, and there is a cavity for forming the shape of the product. The mixture is introduced into this cavity and pressurized to produce a plastic molded article. The mold is preferably preheated before use, and the preheating temperature is suitably 175 to 220 ° C. The time to apply the pressure depends on the temperature of the mold, but it is preferably about 10 to 40 minutes. Longer times can be applied when the temperature of the mold is low, and shorter time pressure can be applied when the temperature of the mold is high.
압축 성형 방식을 사용함으로써, 몰드의 제작 형태에 따라 다양한 모양의 플라스틱 성형품을 제조할 수 있으며, 짧은 시간에 다량 제조가 가능하여 생산성이 우수하다는 장점이 있다.
By using a compression molding method, it is possible to manufacture a plastic molded article of various shapes according to the production form of the mold, there is an advantage that the productivity can be excellent because a large amount can be manufactured in a short time.
이하, 본 발명의 이해를 돕기 위하여 실시예를 들어 상세하게 설명하기로 한다. 다만 하기의 실시예는 본 발명의 내용을 예시하는 것일 뿐 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다. 본 발명의 실시예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다.
Hereinafter, examples will be described in detail to help understand the present invention. However, the following examples are merely to illustrate the content of the present invention is not limited to the scope of the present invention. The embodiments of the present invention are provided to more completely explain the present invention to those skilled in the art.
<<
실시예Example
> 식사 도구 받침용 플라스틱 성형품의 제조 > Manufacturing of Plastic Molds for Meal Support
1. One. 겔상의Gel 전분과 Starch 원두커피분말을Ground coffee powder 혼합하고 건조하는 단계 Mixing and drying steps
물 100ml를 비커에 담아 60℃로 가열한 후 여기에 전분 100g을 넣고 계속 저어 전분을 겔화시켰다. 이에 원두커피분말 150g을 넣고 혼합한 후, 이를 평평한 판 위에 두께가 약 5mm정도가 되도록 펼친 후 60℃ 오븐에 넣고 하루 건조시켰다.
100 ml of water was placed in a beaker, heated to 60 ° C., and 100 g of starch was added thereto, followed by stirring to gel the starch. 150 g of coffee beans were added and mixed, and the mixture was spread to a thickness of about 5 mm on a flat plate, and then dried in a 60 ° C. oven.
2. 건조물을 파쇄하여 2. Crush the dry matter 직경이Diameter 2 내지 5 2 to 5 mmmm 인 입자를 얻는 단계Obtaining Phosphorus Particles
건조물을 고무망치나 나무망치로 두드려 부신 후, 체로 걸러 부서진 알갱이중 입자크기가 2 내지 5mm인 알갱이를 취하였다.
The dried product was smashed with a rubber hammer or a wood hammer, and then sieved to obtain particles having a particle size of 2 to 5 mm.
3. 혼합 단계 3. Mixing step
상기 입자크기가 2 내지 5mm인 알갱이를 PLA(polylactic acid)수지 입자와 50:50으로 혼합하였다.
The particles having a particle size of 2 to 5 mm were mixed at 50:50 with PLA (polylactic acid) resin particles.
4. 압축 성형하는 단계4. step of compression molding
몰드를 200℃로 예열하고 몰드의 캐비티에 상기 혼합물을 넣고, 몰드에 약 20분 동안 압력을 가하였다. 압력을 풀고 몰드를 냉각시킨 후, 제품을 꺼내 완성된 식사도구 받침용 플라스틱 성형품을 얻었다.
The mold was preheated to 200 ° C. and the mixture was placed in the cavity of the mold and pressure was applied to the mold for about 20 minutes. After the pressure was released and the mold was cooled down, the product was taken out to obtain a finished plastic molding for mealware support.
이상으로 본 발명의 특정한 부분을 상세히 기술하였는 바, 당업계의 통상의 지식을 가진 자에게 있어서, 이러한 구체적 기술은 단지 바람직한 실시예일 뿐 이며, 이에 의해 본 발명의 범위가 제한되는 것이 아닌 점은 명백할 것이다. 따라서, 본 발명의 실질적인 범위는 첨부된 청구항들과 그것들의 등가물에 의하여 정의된다고 할 것이다.
Having described the specific part of the present invention in detail, it is apparent to those skilled in the art that such a specific description is only a preferred embodiment, thereby not limiting the scope of the present invention. something to do. Thus, the substantial scope of the present invention will be defined by the appended claims and their equivalents.
Claims (10)
A resin composition comprising a biodegradable polymer resin, coffee beans powder and starch.
The resin composition of claim 1, wherein the biodegradable polymer resin is at least one selected from the group consisting of polylactic acid, polyglycolic acid, polycaprolactone, polyhydroxyalkanoate, polyethylene succinate and polybutylene succinate.
The resin composition according to claim 1, wherein the ground coffee powder is ground coffee powder after extracting the stock solution.
The resin composition of claim 1, wherein the starch is at least one selected from the group consisting of corn starch, potato starch, wheat starch, and tapioca starch.
The resin composition of claim 1, wherein the amount of coffee beans is 40 to 900 parts by weight based on 100 parts by weight of starch.
The resin composition of claim 1, wherein the amount of coffee beans and starch is 0.001 to 70 parts by weight based on 100 parts by weight of the biodegradable polymer resin.
Plastic molded article formed from the resin composition of any one of Claims 1-6.
8. The plastic molded article according to claim 7, wherein the plastic molded article is for supporting a meal utensil.
8. The plastic molded article according to claim 7, wherein the plastic molded article is disposable.
상기 건조물을 파쇄하여 직경이 2 내지 5mm인 입자를 얻는 단계;
상기 입자와 생분해성 고분자 수지를 혼합하여 혼합물을 제조하는 단계 및
상기 혼합물을 압축 성형하는 단계를 포함하는 플라스틱 성형품의 제조방법.
Mixing starch and ground coffee powder and drying to prepare a dried product;
Crushing the dried product to obtain particles having a diameter of 2 to 5 mm;
Preparing a mixture by mixing the particles with a biodegradable polymer resin, and
Method for producing a plastic molded article comprising the step of compression molding the mixture.