KR20110034304A

KR20110034304A - A blazier tea table

Info

Publication number: KR20110034304A
Application number: KR1020090091790A
Authority: KR
Inventors: 이연실
Original assignee: 이연실
Priority date: 2009-09-28
Filing date: 2009-09-28
Publication date: 2011-04-05

Abstract

PURPOSE: A method for manufacturing a tea table is provided to enable a user to enjoy tea while feeling a natural mood. CONSTITUTION: A method for manufacturing a tea table comprises: a step(S100) of making an upper plate by mixing granite soil and kaolin powder; a step(S200) of cutting a part where a furnace is installed on the upper plate; a step(S300) of mounting a furnace container of a hemi-spherical type under the upper plate; a step(S400) of mounting a support stand propping up the upper plate under the upper plate; a step(S500) of spreading soil water on the surface of the upper plate; and a dry step(S600).

Description

Tea table manufacturing method provided with a brazier {A Blazier tea table}

The present invention relates to a method for manufacturing a tea table having a brazier, and the present invention relates to a tea table in which a natural stone image is added to a tea table shaped as a natural stone texture and a stone. Equipped with clay to make the image of natural stone while taking several firings, you can enjoy the tea ceremony while feeling the natural atmosphere by incorporating the motif of natural stone into the tea table which is not easily accessible to modern people. It relates to a tea table manufacturing method having a brazier.

The present invention relates to a tea table manufacturing method having a brazier,

More specifically, after mixing the masato and kaolin powder on the upper side of the coarse clay (molding clay), it is provided on the upper side of the molding clay, the size of the brazier is set on the upper plate, the top plate is cut out, and then the gravel is installed on the upper side of the heater. Furnace was provided to install, after the top plate provided after the first firing of 12 hours at 850 degrees and then the secondary firing of 15 hours at 1250 degrees, and then subjected to firing at a high temperature as described above The present invention relates to a method of manufacturing a tea table having a brazier, characterized by the shape of the texture and stone of an image of natural stone, which takes a long time of firing but has less deformation of the appearance than a conventional tea table, and can be used for a long time. .

In the past, various shapes of patterns were printed, printed, or carved on a wooden material on the outside of a tea table, which was not only hassle but also complicated. In addition, the manufacturing process by the printing and coating of the pattern is excessively expensive for the tea table itself, and the coating is erased after long use, so that the printing and printing are erased, which makes it feel dirty and also used when carving the pattern. If the pattern itself breaks, it may not look good. In addition, it is equipped with only the tea table itself without additional functions, it is not only monotonous, it does not induce curiosity, and after time has passed after boiling tea, the tea has cooled down and it cannot feel the original aroma and taste of tea. In addition, the tea table made of hard wood, plastic, and iron made people feel a sense of distance.

In order to solve the above problem, as shown in FIG. 1, in application number 20-2005-0025178, the cylinder and ancillary mother-of-pearl made of a whole of a paulownia tree were attached and detached in order to feel natural beauty. In addition to the hassle, the mother-of-pearl hangs down when using it, and the process of sculpting and composing paulownia is complicated, and the process of composing paulownia is complicated. No, the distinction between the existing tea and the appearance is not large enough to induce curiosity, and did not feel the difference in appearance.

Therefore, the present invention is to solve and solve the above problems, to provide a brazier away from the monotonous tea table, by having a brazier, the tea table that loses its unique aroma and taste after a long time to cool In order to compensate for the shortcomings, it is necessary to have a brazier inside the tea table, and also to compensate for the problem of losing the original tea table shape over time due to the method of carving, printing, printing, and coating. The present invention relates to a method for manufacturing a tea table having a brazier configured to add a brazier function to a tea table in which a natural stone texture and a stone are formed based on an image of a natural stone rather than a hard tea table.

In order to solve the above problems, the present invention is to mix the masato and kaolin powder on a wide disk and then grafting coarse clay (molding clay) on the upper side of the upper plate to the desired shape and then to have a brazier after After cutting the upper plate of the furnace, it is necessary to embed the furnace barrel, and it is provided with a support to prevent the upper plate from flowing down during firing, and it makes the appearance of the stone by applying masato and molding soil to the wall of the product during drying. First bake 12 hours at a high temperature of 850 degrees, 15 hours secondary bake at a high temperature of 1250 degrees, and apply 3 to 4 matte glazes in turn to make the stone shape more modern. Characterized by the image of the natural stone can not feel.

In order to solve the above problems, the present invention is to mix the masato and kaolin powder on a wide disk and then grafting coarse clay (molding clay) on the upper side of the upper plate to the desired shape and then to have a brazier after After cutting the upper plate of the furnace, the brazier can be built in.The upper plate of the upper side is supported so that the upper plate does not flow down even when firing.As it is applied to the wall of the material during the drying, it makes the appearance of stone. By firing at high temperature of the degree and applying a matte glaze of 3 to 4 in order to make the shape of the stone even more, it is characterized by the image of natural stone that modern people can not feel.

Hereinafter, with reference to the accompanying drawings, preferred embodiments of the present invention will be described in detail. First, in adding reference numerals to the components of each drawing, it should be noted that the same reference numerals have the same reference numerals as much as possible even if displayed on different drawings. In describing the present invention, when it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted.

The configuration of the present invention relates to a tea table manufacturing method having a brazier,

2 is a view showing a process of coupling the top plate 60 of the brazier-type tea table 1 according to an embodiment of the present invention. FIG. 3 is a view illustrating a process in which the furnace lid 12 is disassembled and extracted from the upper plate 60 of the furnace-type tea table 1, and FIG. 4 is a support 50 and the second support 51 of the furnace-type tea table 1. ), Is a rear view showing the configuration of the furnace 11, Figure 5 is a perspective view of the furnace-type tea table (1) according to an embodiment of the present invention. Figure 6 is a flow chart showing a manufacturing method of a tea table provided with a brazier according to an embodiment of the present invention. The present invention according to the drawings described above is a work in which the function of a brazier is added to a natural stone image based on a natural stone image and a teat shaped stone.

The brazier-type tea table 1 is provided with a plate formed by mixing the Masato 40 and the kaolin powder 41 on the upper side of the wide disc as shown in FIG. On the upper side of the plate, the plate composed of coarse clay (molded clay) 30 is laid down to a thickness of 6 to 7 mm, and after the upper plate 60 is formed, it is cut to a desired shape. The shape of the foundation is characterized in that the oval, bent, etc. to be selected.

Due to the edge of the upper plate 60 is cut to 7 ~ 8cm in height, the angle of the upper plate becomes a smooth shape, characterized in that to achieve a natural curve.

In addition, the edge of the above is to build up the soil sputum so that the outer surface (器面) is treated with a curve so as to feel the natural stone gradually narrowed, and because of the narrowed curve of the leg when sitting on the furnace-type tea table (1) You will feel comfortable.

After all the configuration of the upper plate 60, as shown in Figs. 3 and 4 to determine the size of the furnace 10 and cut the upper plate 60 to the size of the furnace 10 and then the furnace 10 and The heater 20, the gravel 13 is to be provided with a furnace 11 is formed in a hemisphere of 10 ~ 15cm high so that it can be inserted.

As shown in FIG. 3, a portion of the upper plate 60 cut out according to the size of the brazier 10 may be provided as a brazier lid 12 to enable the opening and closing of the brazier 10, and the upper plate 60. The central portion of the portion is characterized in that for opening and closing the hearth 10 by drilling a hole to enter the finger.

The inside of the furnace 10 is provided with a sputum to create a jaw. By having the above-mentioned soil sputum inside the brazier to make the brazier lid 12 horizontal to the top plate 60,

The furnace 11 and the base surface of the tea table is characterized in that the electric heater 20 can be drilled out of a hole of a predetermined size so as to be connected.

As shown in FIG. 4, an elliptical support 50 is provided at the center of the rear surface of the tea table 1 so that the wall surface and the bottom of the oval support 50 and the furnace-type tea table 1 are connected to each other. It is to be provided with a plurality of second support 51 to minimize the possibility of drooping the narrow lower end compared to the upper plate 60 when firing at high temperature,

A hole is formed between the wall surface and the wall surface of the support 50 and the second support 51 to allow air to pass through, so that air does not pass during firing to prevent bursting.

After drying the brazier-type tea table (1) after the manufacturing process of about 50%, during drying, kneading the masato (40) and the earthenware soil (30) by tapping all the surfaces of the brazier-type tea table (1) to apply do. This is for the Masato 40 to be stuck to the surface.

In addition, after the drying of 60%, the upper and lower sides are replaced, and during drying, the surface is covered with vinyl for 3 to 4 weeks and dried slowly in the shade, which is supported by the back support 50 and the second support 51. This is to prevent bursting of the wall due to inconsistent drying. After 3-4 weeks, dry in the sun to allow complete drying.

After drying, do the first firing slowly at about 850 degrees for more than 12 hours. At this time, 3-4 kinds of matte glaze are applied to the sponge in turn and then patted to give a natural feeling when finished. After the matte glaze process, it is characterized in that for reducing at 1250 degrees.

As described above, the present invention relates to a manufacturing method of a brazier-type tea table provided with a brazier.

As shown in summary in Figure 6 through the step of making a top plate consisting of a mixture of Masato 40 and kaolin powder 41 (S100)

Cutting out a portion to be installed in the brazier (60) (S200),

Mounting a hemispherical furnace 11 under the upper plate 60 along the edge of the portion where the furnace 10 is to be mounted (S300);

Mounting the support 50 for holding the upper plate 60 under the upper plate 60 (S400),

Applying the surface of the upper plate 60, the soil water mixed with the Masato 40 and the molding soil 30 (S500),

Tea-making method having a brazier, characterized in that it comprises at least six steps of the step (S600) of dry firing.

In addition, to create a brazier lid (12) corresponding to the top plate 60 portion cut out by the size of the brazier 10, and after removing the brazier lid (12), attach the mud sputum to the bottom of the top plate 60 thickness It is characterized in that it further comprises the step of making the top plate and the horizontal when opening and closing the brazier lid (12).

The brazier-type tea table 1 according to the present invention is based on the image of natural stone, which could not be felt in the existing tea table, and the tea ceremony that did not previously feel as a tea table added with the function of a brazier to the tea table shaped natural stone. Not only can you feel the nature while enjoying the tea, but for a long time, you can feel the warm and incense taste and aroma by equipping the inside of the tea table to compensate for the shortcomings that you could not feel the original taste and aroma when the tea has cooled down. It was. In addition, it is characterized by minimizing the appearance change even after long use.

1 is a perspective view of a tea table according to an embodiment according to the prior art.

Figure 2 is a view showing a process of coupling the top plate of the brazier type tea table according to an embodiment of the present invention.

3 is an exploded view of the brazier lid from the top plate of the brazier type tea table according to an embodiment of the present invention.

Figure 4 is a rear view showing a supporter and a brazier of a brazier type tea table according to an embodiment of the present invention.

5 is a perspective view of a brazier-type tea table according to an embodiment of the present invention.

Figure 6 is a flow chart showing a tea table manufacturing method having a brazier in accordance with an embodiment of the present invention.

1: brazier type 10: brazier

11: brazier barrel 12: brazier lid

13: gravel 20: electric heater

30: coarse clay 40: masato

41: kaolin powder 50: support

51: second support 60: top plate

Claims

In the tea shop manufacturing method,

Making a top plate 60 composed of a mixture of masato 40 and kaolin powder 41 (S100);

Cutting out a portion on which the hearth is to be mounted on the upper plate (60) (S200);

Mounting a hemispherical furnace (11) below the upper plate (60) along an edge of a portion on which the furnace (10) is to be mounted (S300);

Mounting a support (50) supporting the upper plate (60) below the upper plate (60) (S400);

Applying a surface of the upper plate (60), mixed with soil water mixed with the masato (40) and the molding soil (S500);

Tea-making method having a brazier, characterized in that it comprises at least a step (S600) of dry firing.

The method of claim 1,

The method of manufacturing a tea table having a brazier, characterized in that it further comprises the step of making a brazier lid (12) corresponding to the upper plate (60) portion cut out to the size of the brazier (10).

The method of claim 1,

Tea table manufacturing method having a furnace, characterized in that further comprising the step of mounting a furnace (10) in the furnace (11).