KR20100105529A - Functional powder contain natural minerals and the manufacturing method - Google Patents
Functional powder contain natural minerals and the manufacturing method Download PDFInfo
- Publication number
- KR20100105529A KR20100105529A KR20100087971A KR20100087971A KR20100105529A KR 20100105529 A KR20100105529 A KR 20100105529A KR 20100087971 A KR20100087971 A KR 20100087971A KR 20100087971 A KR20100087971 A KR 20100087971A KR 20100105529 A KR20100105529 A KR 20100105529A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- fermentation
- powder
- weight parts
- Prior art date
Abstract
Description
본 발명은 천연 미네랄 기능성 분말 및 그의 제조방법에 관한 것으로서, 특히 오염수가 흐르는 물이나 정제된 하천, 호소, 댐, 양식장 등의 바닥에 퇴적된 유기슬러지를 서서히 자연 분해시킬 수 있으며, 100％ 친환경적인 성분으로 자연 생태계에 전혀 피해가 없이 오염생태계를 정화시킬 수 있을 뿐만 아니라, 용존 산소증가와 미생물 활동에 필요한 영양소를 방출시켜 혐기성 환경을 호기성으로 전환시켜 퇴적 슬러지를 서서히 자연 분해시켜 생태계를 복원시킬 수 있고, 오염배출원에서부터 오염물을 정화시킬 수 있는 광범위한 오염 현장에서 폭넓게 경제적으로 시설 투자비 없이 정화시킬 수 있으며 동물 사육시 사료 보조제로도 첨가하여 성장촉진과 면역력 향상에 도움을 줄 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법에 관한 것이다.The present invention relates to a natural mineral functional powder and a method for manufacturing the same, and in particular, it is possible to slowly decompose organic sludge deposited on the bottom of the flowing water or purified rivers, lakes, dams, farms, etc. Not only does it cleanse the contaminated ecosystem without damaging the natural ecosystem, but it also releases nutrients necessary for increasing dissolved oxygen and microbial activity, converting the anaerobic environment into aerobic and slowly decomposing sediment sludge to restore the ecosystem. And natural mineral functional powders that can be used to cleanse pollutants from pollutant sources at a wide range of contaminant sites, economically and without facility investment costs, and as feed supplements when raising animals to help promote growth and improve immunity. It relates to a manufacturing method thereof.
최근에 산업화, 도시화로 정화되지 않은 각종 오염 물질이 하천, 댐, 연안포구, 양식장 등에 퇴적되어 생활용수 공급 부족과 생물이 생존할 수 없는 생태계 파괴 현상이 심각한 상태로 막대한 준설비용과 오염물 처리비용, 시설 등의 소요로 친환경적인 기술개발이 절실히 필요한 시점이다.In recent years, various pollutants that have not been purified by industrialization and urbanization have been deposited in rivers, dams, coastal muds, and farms, resulting in a shortage of living water supply and destruction of ecosystems in which organisms cannot survive. It is a time when environment-friendly technology development is desperately needed due to the facilities.
또한 하절기 기온 상승시 각종 영양 염류로 인해 녹조와 적조를 유발하여 심각한 피해를 반복적으로 발생시키고 있으며 황토를 살포하거나 수중 펌프 등으로 펌핑 여과하는 방법으로 정화개선을 하고 있으나 근본적인 오염물을 정화 개선시키지 못하고 있다.In addition, when the temperature rises in summer, various nutrients cause green algae and red algae, causing serious damage repeatedly, and purifying and improving the soil by spraying or filtering it with an underwater pump. .
일반적으로 이와 같은 오염된 수질을 정화시키는 방법으로는 유용 미생물 성분을 응용한 제품과 여과 정화방법 등 수 많은 기술이 제안되어 있으나 수질정화와 퇴적 슬러지를 동시에 개선 정화시키는 제품이 없으며 특히 미생물 등의 제품은 특정 부분에는 효과가 뛰어나나 해수 등 염분 농도가 높은 물은 정화시킬 수 없다는 문제점이 있었다.In general, as a method of purifying the contaminated water quality, a number of technologies have been proposed, such as products using useful microbial components and filtration and purification methods, but there are no products to improve and purify water purification and sediment sludge at the same time, especially products such as microorganisms. There was a problem in that the specific portion is excellent in effect, but water of high salt concentration such as seawater cannot be purified.
[발명이 이루고자 하는 기술적 과제][Technical problem to be achieved]
따라서 본 발명은 상기 문제점을 해결하기 위하여 이루어진 것으로서, 본 발명의 목적은 오염된 수질을 생태계에 전혀 피해를 주지 않으며 수질오염 정화 물질은 수중에 자생하는 미생물들이 분해 작용하고 있는 자연정화원리를 감안하여 수중 용존 산소 증가와 미생물 활성제를 분말화하여 수중에 침투시켜 혐기성 환경을 호기성으로 전환시켜 친환경적으로 수질정화와 슬러지를 분해할 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Therefore, the present invention has been made to solve the above problems, and an object of the present invention is that the polluted water quality does not damage the ecosystem at all, and the water pollution purification material in consideration of the natural purification principle in which the microorganisms native to the water are decomposed and acting The present invention provides a natural mineral functional powder capable of decomposing water purification and sludge in an environmentally friendly manner by converting an anaerobic environment into aerobic by increasing the dissolved oxygen in the water and infiltrating into the water by pulverizing the microbial active agent.
본 발명의 다른 목적은 오염수가 흐르는 물이나 정제된 하천, 호소, 댐, 양식장, 가정용싱크대, 도시 하수관로 등의 바닥에 퇴적된 유기슬러지를 서서히 자연 분해시킬 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Another object of the present invention is to provide a natural mineral functional powder capable of slowly decomposing organic sludge deposited on the bottom of contaminated water or purified rivers, lakes, dams, fish farms, household sinks, urban sewer pipes, etc. To provide.
본 발명의 또 다른 목적은 100％ 친환경적인 성분으로 자연 생태계에 전혀 피해가 없이 오염생태계를 정화 시킬 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a natural mineral functional powder and a method for preparing the same, which are capable of purifying the contaminated ecosystem without damaging the natural ecosystem with 100% environmentally friendly ingredients.
본 발명의 또 다른 목적은 수중 용존 산소 증가와 자생 미생물 활성화시킬 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a natural mineral functional powder capable of increasing dissolved oxygen in water and activating native microorganisms, and a method for preparing the same.
본 발명의 또 다른 목적은 오염 생태계 연쇄 먹이사슬 복원하며, 녹조, 적조 원인 물질 제거할 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a natural mineral functional powder capable of restoring a contaminated ecosystem chain food chain and removing green algae, red tide causing substances, and a method of manufacturing the same.
본 발명의 또 다른 목적은 연안 포구 등 염분 농도가 높은 장소 퇴적 슬러지 분해시킬 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a natural mineral functional powder capable of decomposing sludge sediment with high salt concentration, such as coastal muzzle, and a method for producing the same.
본 발명의 또 다른 목적은 각종 동물 사육시 사료보조제로 첨가하여 동물 성장 촉진과 면역력 강화에도 도움을 주는 천연 미네랄 기능성 분말 및 그 외 제조 방법을 제공하는데 있다.Still another object of the present invention is to provide a natural mineral functional powder and other preparation methods that help to promote animal growth and strengthen immunity by adding as a feed aid when raising various animals.
본 발명의 또 다른 목적은 정화 비용 절감할 수 있는 천연 미네랄 기능성 분말 및 그의 제조방법을 제공하는데 있다.Still another object of the present invention is to provide a natural mineral functional powder and a method for producing the same, which can reduce the purification cost.
상기 목적을 달성하기 위하여 본 발명의 천연 미네랄 기능성 분말의 제조방법은 6 내지 10중량부의 감나무 잎, 6 내지 10중량부의 참나무 잎, 6 내지 10중량부의 당두충 잎을 4 내지 7중량부의 메론, 4 내지 7중량부의 파인애플, 4 내지 7중량부의 망고, 4 내지 7중량부의 감, 4 내지 7중량부의 바나나를 깨끗이 세정하여 20 내지 30중량부의 물, 18 내지 32중량부의 흑설탕을 교반기에 투입하여 분쇄혼합하는 분쇄혼합단계와; 상기 분쇄혼합단계에서 혼합된 혼합액을 발효용기에 저장하여 18 내지 22℃의 온도에서 45 내지 55일 동안 발효숙성시키는 1차 발효숙성단계와; 상기 1차 발효숙성단계에서 발효숙성된 발효숙성액을 여과포로 여과시키는 여과단계와; 상기 여과단계에서 여과된 30중량부의 발효숙성 여과액에 규소 분말이 65중량부 함유된 35 내지 45중량부의 맥반석 분말과 30 내지 40중량부의 제올라이트 분말을 교반기에 넣고 교반혼합하는 교반혼합단계와; 상기 교반혼합단계에서 교반혼합된 혼합액을 18 내지 25℃의 온도에서 45일 내지 55일 동안 숙성 발효시키는 2차 숙성발효단계와; 상기 2차 숙성발효단계에서 숙성발효된 숙성발효반죽을 태양광선에서 자연 건조시키는 건조단계와; 상기 건조단계에서 건조된 숙성발효 덩어리를 파쇄기로 파쇄하여 분말화시키는 분말화단계를 포함하는 것을 특징으로 한다.In order to achieve the above object, the method for preparing natural mineral functional powder of the present invention comprises 6 to 10 parts by weight of persimmon leaves, 6 to 10 parts by weight of oak leaves, 6 to 10 parts by weight of larvae, 4 to 7 parts by weight of melon, 4 4 to 7 parts by weight of pineapple, 4 to 7 parts by weight of mango, 4 to 7 parts by weight of persimmon, 4 to 7 parts by weight of bananas are thoroughly cleaned, and 20 to 30 parts by weight of water and 18 to 32 parts of brown sugar are added to the stirrer and mixed. Grinding and mixing step; A first fermentation aging step of storing the mixed solution mixed in the grinding mixing step in a fermentation vessel and fermenting and aging for 45 to 55 days at a temperature of 18 to 22 ° C .; A filtration step of filtering the fermentation aging liquid fermented in the first fermentation aging step with a filter cloth; A stirring and mixing step of putting in a stirrer and mixing 35 to 45 parts by weight of ganbanite powder and 30 to 40 parts by weight of zeolite powder containing 65 parts by weight of silicon powder in the 30 parts by weight of the fermentation aging filtrate filtered in the filtration step; A second aging fermentation step of fermenting the mixed mixture stirred in the stirring and mixing step for 45 to 55 days at a temperature of 18 to 25 ℃; A drying step of naturally drying the fermented fermented dough which has been aged in the second fermentation fermentation step in sunlight; It characterized in that it comprises a powdering step of powdering by crushing the aged fermentation lump dried in the drying step with a crusher.
본 발명에 따른 천연 미네랄 기능성 분말의 제조방법에 의해 제조된 천연 미네랄 기능성 분말은 오염수가 흐르는 물이나 정제된 하천, 호소, 댐, 양식장 등의 바닥에 퇴적된 유기 슬러지를 서서히 자연 분해시킬 수 있으며, 특히 100％ 친환경적인 성분으로 자연 생태계에 전혀 피해가 없이 오염생태계를 정화시킬 수 있을 뿐만 아니라, 용존 산소증가와 미생물 활동에 필요한 영양소를 방출시켜 혐기성 환경을 호기성으로 전환시켜 퇴적 슬러지를 서서히 자연 분해시켜 생태계를 복원시킬 수 있다는 효과가 있다.The natural mineral functional powder prepared by the method for producing a natural mineral functional powder according to the present invention may gradually decompose organic sludge deposited on the bottom of water flowing through contaminated water or purified rivers, lakes, dams, farms, etc. In particular, it is a 100% eco-friendly ingredient that not only can cleanse the polluted ecosystem without damaging the natural ecosystem, but also releases nutrients necessary for increasing dissolved oxygen and microbial activity, converting anaerobic environment into aerobic and slowly decomposing sediment sludge. The effect is to restore the ecosystem.
또한, 본 발명에 따른 천연 미네랄 기능성 분말의 제조방법에 의해 제조된 천연 미네랄 기능성 분말은 오염배출원에서부터 오염물을 정화시킬 수 있는 광범위한 오염 현장에서 폭넓게 경제적으로 시설 투자비 없이 정화 시킬 수 있으며, 가축 사육시 사료에 일정량을 희석해주면 소화촉진과 배설물 냄새제거로 성장촉진이 되고 면역력강화에 도움을 줄 수 있으며, 최근 논란이 가중되고 있는 하천, 수중보, 댐, 오·폐수처리장 등의 퇴적 슬러지를 적은 비용으로 정화함은 물론 양식장 등 각종 수질 오염을 방지할 수 있다는 등의 여러 가지 뛰어난 효과가 있다.In addition, the natural mineral functional powder produced by the method for producing a natural mineral functional powder according to the present invention can be purified at a wide range of pollution sites that can purify the contaminants from the source of pollution, economically and economically without facility investment, feed for livestock breeding A certain amount of dilution can promote growth and promote immunity by promoting digestion and eliminating odors, and purifies sediment sludge in rivers, underwater beams, dams, and wastewater treatment plants, which are recently being debated. In addition, there are many outstanding effects, such as being able to prevent various water pollution such as farms.
도 1은 본 발명의 일실시예에 따른 천연 미네랄 기능성 분말의 제조 순서를 도시한 순서도이다.
도 2는 하천, 수중보, 댐 등의 퇴적 슬러지를 정화시키기 전의 상태를 개략적으로 도시한 개념도이다.
도 3은 하천, 수중보, 댐 등의 퇴적 슬러지를 정화시킨 후의 상태를 개략적으로 도시한 개념도이다.
도 4는 슬러지 정화 과정 및 슬러지를 정화시킨 후의 상태를 개략적으로 도시한 도면이다.1 is a flow chart illustrating a manufacturing procedure of natural mineral functional powder according to an embodiment of the present invention.
2 is a conceptual diagram schematically showing a state before purification of sediment sludge such as rivers, underwater beams, dams, and the like.
3 is a conceptual diagram schematically illustrating a state after purification of sediment sludge such as a river, an underwater beam, a dam, and the like.
4 is a view schematically showing a sludge purification process and a state after the sludge has been purified.
이하, 본 발명의 일실시예에 의한 천연 미네랄 기능성 분말 및 그의 제조방법에 관하여 첨부 도면에 의거하여 상세히 설명한다.Hereinafter, a natural mineral functional powder and a preparation method thereof according to an embodiment of the present invention will be described in detail with reference to the accompanying drawings.
6중량부의 감나무 잎, 6중량부의 참나무 잎, 6중량부의 당두충 잎을 4중량부의 메론, 4중량부의 파인애플, 4중량부의 망고, 4중량부의 감, 4중량부의 바나나를 깨끗이 세정하여 30중량부의 물, 32중량부의 흑설탕을 교반기에 투입하여 분쇄혼합하고(분쇄혼합단계), 상기 분쇄혼합단계에서 혼합된 혼합액을 발효용기(항아리 또는 스테인레스 용기)에 저장하여 18 내지 22℃의 온도에서 45일 동안 발효숙성시키고(1차 발효숙성단계), 상기 1차 발효숙성단계에서 발효숙성된 발효숙성액을 여과포(필터)로 여과시키고(여과단계), 상기 여과단계에서 여과된 30중량부의 발효숙성 여과액에 규소(SiO2) 분말이 65중량부 함유된 35중량부의 맥반석 분말과 35중량부의 제올라이트 분말을 교반기에 넣고 교반혼합하고(교반혼합단계), 상기 교반혼합단계에서 교반혼합된 혼합액을 18 내지 25℃의 온도에서 30일 이상 숙성 발효시키고(2차 숙성발효단계), 상기 2차 숙성발효단계에서 숙성발효된 숙성발효반죽을 태양광선에서 자연 건조시키고(건조단계), 상기 건조단계에서 건조된 숙성발효 덩어리를 파쇄기로 파쇄하여 분말화시켜서(분말화단계) 본 발명의 천연 미네랄 기능성 분말을 제조하였다(도 1 참조).6 parts by weight of persimmon leaves, 6 parts by weight of oak leaves, and 6 parts by weight of green leaves are washed 4 parts by weight of melon, 4 parts by weight of pineapple, 4 parts by weight of mango, 4 parts by weight of persimmon and 4 parts by weight of banana. Water and 32 parts by weight of brown sugar were added to an agitator for pulverization and mixing (grinding and mixing), and the mixed solution mixed in the grinding and mixing step was stored in a fermentation vessel (jar or stainless container) for 45 days at a temperature of 18 to 22 ° C. Fermentation aging (first fermentation aging step), the fermentation aging liquid fermented in the first fermentation aging step filtered with a filter cloth (filter) (filtration step), 30 parts by weight of the fermentation aging filtrate filtered in the filtration step 35 parts by weight of ganbanite powder and 35 parts by weight of zeolite powder containing 65 parts by weight of silicon (SiO 2) powder were added to a stirrer and stirred and mixed (stirring mixing step), followed by stirring and mixing in the stirring and mixing step To fermentation for at least 30 days at a temperature of 18 to 25 ℃ (second fermentation fermentation step), the fermentation fermentation dough fermented in the second fermentation fermentation step is naturally dried in sunlight (drying step), the drying step The dried fermented lumps were dried by crushing with a crusher (powderization step) to prepare a natural mineral functional powder of the present invention (see FIG. 1).
상기 설명에 있어서, 감나무 잎, 참나무 잎, 당두충 잎은 각종 미네랄 성분이 풍부한 것이고, 메론, 파인애플, 망고, 감, 바나나는 당도가 풍부한 과일이다.In the above description, persimmon leaves, oak leaves, and cedar leaves are rich in various mineral components, and melon, pineapple, mango, persimmon, and banana are fruits rich in sugar.
상기 규소(SiO2) 분말 및 상기 맥반석 분말은 입도가 각각 250 내지 350㎛인 것을 사용하는 것이 바람직하다.Preferably, the silicon (SiO 2 ) powder and the elvan rock powder have a particle size of 250 to 350 μm.
10중량부의 감나무 잎, 10중량부의 참나무 잎, 10중량부의 당두충 잎을 5중량부의 메론, 5중량부의 파인애플, 5중량부의 망고, 5중량부의 감, 중량부의 바나나를 깨끗이 세정하여 20중량부의 물, 25중량부의 흑설탕을 교반기에 투입하여 분쇄혼합하고(분쇄혼합단계), 상기 분쇄혼합단계에서 혼합된 혼합액을 발효용기(항아리 또는 스테인레스 용기)에 저장하여 18 내지 22℃의 온도에서 50일 동안 발효숙성시키고(1차 발효숙성단계), 상기 1차 발효숙성단계에서 발효숙성된 발효숙성액을 여과포(필터)로 여과시키고(여과단계), 상기 여과단계에서 여과된 20중량부의 발효숙성 여과액에 규소(SiO2) 분말이 65중량부 함유된 40중량부의 맥반석 분말과 40중량부의 제올라이트 분말을 교반기에 넣고 교반혼합하고(교반혼합단계), 상기 교반혼합단계에서 교반혼합된 혼합액을 18 내지 25℃의 온도에서 50일 동안 숙성 발효시키고(2차 숙성발효단계), 상기 2차 숙성발효단계에서 숙성발효된 숙성발효반죽을 태양광선하에서 자연 건조시키고(건조단계), 상기 건조단계에서 건조된 숙성발효 덩어리를 파쇄기로 파쇄하여 분말화시켜서(분말화단계) 본 발명의 천연 미네랄 기능성 분말을 제조하였다(도 1 참조).10 parts by weight of persimmon leaves, 10 parts by weight of oak leaves, and 10 parts by weight of green leaves are cleaned by washing 5 parts by weight of melon, 5 parts by weight of pineapple, 5 parts by weight of mango, 5 parts by weight of persimmon and parts by weight of banana. , 25 parts by weight of brown sugar was added to the stirrer and pulverized and mixed (grinding and mixing step), the mixed solution mixed in the pulverizing and mixing step is stored in a fermentation vessel (jar or stainless container) to ferment for 50 days at a temperature of 18 to 22 ℃ After fermentation (first fermentation aging step), the fermentation aging liquid fermented in the first fermentation aging step is filtered with a filter cloth (filter), and filtered into 20 parts by weight of the fermentation aging filtrate filtered in the filtration step silicon (SiO 2) powder was put into 65 parts by weight containing 40 parts by weight of an elvan powder and 40 parts by weight of zeolite powder with a stirrer, and mixed with stirring (stirring step), stirred mixture of the horn in the stirring step The solution is aged and fermented at a temperature of 18 to 25 ° C. for 50 days (secondary fermentation fermentation step), and the fermented fermented dough fermented in the second fermentation fermentation step is naturally dried under sunlight (drying step), and the drying is performed. The mature fermented lump dried in the step was crushed with a crusher (powderization step) to prepare a natural mineral functional powder of the present invention (see Fig. 1).
8중량부의 감나무 잎, 8중량부의 참나무 잎, 8중량부의 당두충 잎을 7중량부의 메론, 7중량부의 파인애플, 7중량부의 망고, 7중량부의 감, 7중량부의 바나나를 깨끗이 세정하여 23중량부의 물, 18중량부의 흑설탕을 교반기에 투입하여 분쇄혼합하고(분쇄혼합단계), 상기 분쇄혼합단계에서 혼합된 혼합액을 발효용기(항아리 또는 스테인레스 용기)에 저장하여 18 내지 22℃의 온도에서 55일 동안 발효숙성시키고(1차 발효숙성단계), 상기 1차 발효숙성단계에서 발효숙성된 발효숙성액을 여과포(필터)로 여과시키고(여과단계), 상기 여과단계에서 여과된 25중량부의 발효숙성 여과액에 규소(SiO2) 분말이 65중량부 함유된 45중량부의 맥반석 분말과 30중량부의 제올라이트 분말을 교반기에 넣고 교반혼합하고(교반혼합단계), 상기 교반혼합단계에서 교반혼합된 혼합액을 18 내지 25℃의 온도에서 55일 동안 숙성 발효시키고(2차 숙성발효단계), 상기 2차 숙성발효단계에서 숙성발효된 숙성발효반죽을 태양광선에서 자연 건조시키고(건조단계), 상기 건조단계에서 건조된 숙성발효 덩어리를 파쇄기로 파쇄하여 분말화시켜서(분말화단계) 본 발명의 천연 미네랄 기능성 분말을 제조하였다(도 1 참조).8 parts by weight of persimmon leaves, 8 parts by weight of oak leaves, and 8 parts by weight of green leaves are washed 7 parts by weight of melon, 7 parts by weight of pineapple, 7 parts by weight of mango, 7 parts by weight of persimmon, and 7 parts by weight of bananas. Water and 18 parts by weight of brown sugar are added to a stirrer and pulverized and mixed (grinding and mixing step), and the mixed solution mixed in the pulverizing and mixing step is stored in a fermentation vessel (jar or stainless container) for 55 days at a temperature of 18 to 22 ° C. Fermentation aging (first fermentation aging step), the fermentation aging liquid fermented in the first fermentation aging step is filtered with a filter cloth (filter) (filtration step), 25 parts by weight of fermentation aging filtrate filtered in the filtration step 45 parts by weight of ganbanite powder containing 30 parts by weight of silicon (SiO 2 ) powder and 30 parts by weight of zeolite powder were put into a stirrer and mixed by stirring (stirring mixing step), followed by stirring and mixing in the stirring mixing step The solution is aged for 55 days at a temperature of 18 to 25 ° C. (secondary fermentation fermentation step), and the fermented fermented dough that has been fermented in the second fermentation fermentation step is naturally dried in sunlight (drying step), and the drying The mature fermented lump dried in the step was crushed with a crusher (powderization step) to prepare a natural mineral functional powder of the present invention (see Fig. 1).
[비교예][Comparative Example]
5중량부의 감나무 잎, 5중량부의 참나무 잎, 5중량부의 당두충 잎을 20중량부의 메론, 20중량부의 파인애플, 15중량부의 망고, 15중량부의 감, 15중량부의 바나나를 깨끗이 세정하여 23중량부의 물, 18중량부의 흑설탕을 교반기에 투입하여 분쇄혼합하고, 상기 분쇄혼합단계에서 혼합된 혼합액을 발효용기(항아리 또는 스테인레스 용기)에 저장하여 18 내지 22℃의 온도에서 55일 동안 발효숙성시키고, 상기 1차 발효숙성단계에서 발효숙성된 발효숙성액을 여과포(필터)로 여과시켜서 천연 미네랄 기능성 분말을 제조하였다.5 parts by weight of persimmon leaves, 5 parts by weight of oak leaves, and 5 parts by weight of green leaf leaves are 20 parts by weight of melon, 20 parts by weight of pineapple, 15 parts by weight of mango, 15 parts by weight of persimmon, and 15 parts by weight of bananas. Water and 18 parts by weight of brown sugar are added to a stirrer and pulverized and mixed, and the mixed solution mixed in the pulverized mixing is stored in a fermentation vessel (jar or stainless container) and fermented and matured at a temperature of 18 to 22 ° C. for 55 days. The fermentation ripening liquid fermented in the first fermentation aging step was filtered with a filter cloth (filter) to prepare a natural mineral functional powder.
상기 비교예에 있어서, 감나무 잎과 참나무 잎 및 당두충 잎을 각 5중량부 이하 혼합시 발효 효과가 미미하였고, 메론, 파인애플을 각각 20중량부를 초과하여 혼합시 발효숙성액의 상태가 점도가 높아 발효 숙성이 원활하지 못하여 바람직하지 못하였고, 맥반석 분멀 및 제올라이트 분말을 함유하지 않아 수중 용존 산소를 증가시키지 않았고, 혐기성 환경을 호기성으로 전환시키지도 못하였으며, 친환경적으로 수질정화와 슬러지를 분해할 수 없어서 천연 미네랄 기능성 분말로는 바람직하지 못하였다.In the comparative example, the fermentation effect was negligible when mixing persimmon leaves, oak leaves, and gingival leaves at 5 parts by weight or less, and when the mixture was mixed with more than 20 parts by weight of melon and pineapple, the state of the fermentation ripening liquid had a high viscosity. Fermentation aging was not preferred because it was not smooth, it did not increase the dissolved oxygen in the water because it did not contain the elvan powder and zeolite powder, and it could not convert the anaerobic environment to aerobic, and could not decompose water purification and sludge in an eco-friendly manner. It was not desirable as a mineral functional powder.
상기 실시예 1 내지 실시예 3에서 감나무 잎과 참나무 잎은 각종 미네랄 성분과 비타민C 등이 풍부하여 건강음료에도 이용되고 있으며 플라보노이드 성분은 세포 활성화 기능이 있다. 또한 탄닌 성분과 콜라겐 성분 카로틴 성분 등은 발효과정을 거쳐 생태계 전반에 영양원을 공급하는 효소 촉매제 역할을 하며 각종 유기물을 단백질과 아미노산으로 분해하는 작용을 도와주는 촉매 작용을 한다. 발효 숙성과정을 거친 엑기스 수용액을 생태계의 미생물 영양소인 유기산을 공급해 준다. 이러한 숙성을 촉진시키기 위해 당분이 풍부한 흑설탕을 용해하여 발효를 촉진시켜 미생물 활성 요건을 도와준다. 맥반석과 제오라이트는 다공성이 풍부한 광물질로서 250 내지 350㎛ 입도(입자 사이즈)의 분말 형태도 CEC이온교환 작용은 물론 산화, 환원, 촉매 작용과 광물질에 포함된 각종 미네랄 영양원과 효소 작용으로 수중 오염물질의 흡착, 분해 작용으로 악취제거는 물론 용존산소 공급과 미생물의 생리 활성 영양원으로 중요한 역할을 하는 것이 주지의 사실이다. 이러한 다공성 광물질에 유기물 분해 촉진에 관여하는 식물 엑기스 추출물을 함유시키며 숙성과정을 거치면 친환경 정화제로 기능을 향상시킨 개선제로 이용할 수 있게 되며 오염 수질과 퇴적된 슬러지를 분해 촉진시키는 기능을 수행하게 된다.In Examples 1 to 3, persimmon leaves and oak leaves are rich in various minerals, vitamin C, and the like, and are used in health drinks. Flavonoid components have a cell activation function. In addition, tannin component and collagen component carotene component act as an enzyme catalyst to supply nutrients to the whole ecosystem through fermentation process and catalyze the action of decomposing various organic substances into proteins and amino acids. Extract aqueous solution, fermented and matured, provides organic acid, the microbial nutrient of the ecosystem. To promote this ripening, sugar-rich brown sugar is dissolved to promote fermentation to help the microbial activity requirements. Elvan and zeolite are pore-rich minerals with 250-350 μm particle size (particle size), which are not only CEC ion exchange but also oxidation, reduction, catalysis and various mineral nutrients and enzymes contained in minerals. It is well known that the adsorption and decomposition action plays an important role in removing odor, supplying dissolved oxygen and bioactive nutrients of microorganisms. These porous minerals contain plant extract extracts that are involved in promoting organic decomposition and can be used as an eco-friendly purifier to improve the function as a result of the aging process, and to promote the decomposition of contaminated water quality and deposited sludge.
상기 제1 내지 제3 실시예의 설명에 있어서, 감나무 잎, 참나무 잎, 당두충 잎은 각종 미네랄 성분이 풍부한 것이고, 메론, 파인애플, 망고, 감, 바나나는 당도가 풍부한 과일이고, 상기 규소(SiO2) 분말 및 상기 맥반석 분말은 입도가 각각 250 내지 350㎛인 것을 사용하는 것이 바람직하다.In the description of the first to the third embodiments, persimmon leaves, oak leaves, and hemipteran leaves are rich in various mineral components, and melons, pineapples, mangoes, persimmons, bananas are sugar-rich fruits, and the silicon (SiO 2 ) Powder and the elvan powder are preferably used having a particle size of 250 to 350㎛.
상기 제1 내지 제3 실시예에 있어서, 감나무 잎, 참나무 잎 및 당두충 잎을 각각 10중량부를 초과해서 함유하면 혼합시 발효 효과가 미미하였고, 감나무 잎, 참나무 잎 및 당두충 잎을 각각 6중량부 미만 혼합시 멜론, 파이인내플, 망고 및 바나나의 함유 성분이 각각 증가하여 최종 엑기스 상태의 점도가 높아 발효 숙성에 원활하지 못하였다. 또한 35 내지 45중량부의 맥반석 분말과 30 내지 40중량부의 제올라이트 분말에 혼합 숙성 발효시키는 것이 수많은 실험결과 최적의 개선효과를 얻을 수 있었다. 또한 규소(Sio2) 성분이 최소 65중량부를 초과하여 함유하면, 250 내지 350㎛의 입도(입자 사이즈) 분말을 사용하는 것이 수질정화에 가장 양호한 성과를 나타내었다.In the first to the third embodiments, when the persimmon leaves, oak leaves and the leaves of more than 10 parts by weight of each, the fermentation effect was negligible when mixed, 6 weight each of persimmon leaves, oak leaves and leaves When the sub-parts were mixed, the components of melon, pieinnaple, mango, and banana were increased, respectively, and thus the viscosity of the final extract state was high. In addition, mixed aging and fermentation in 35 to 45 parts by weight of ganban stone powder and 30 to 40 parts by weight of zeolite powder was able to obtain the optimum improvement effect. In addition, when the silicon (Sio 2 ) component contained at least 65 parts by weight, using a particle size (particle size) powder of 250 to 350㎛ showed the best performance for water purification.
이와 같이 제조된 본 발명의 천연 미네랄 기능성 분말은 분말 자체로 사용할 수 있으며 현장 여건에 맞게 볼 형태나 비누 형태 등 여러 형태로 제작 성형 사용할 수 있다. H한 본 발명의 천연 미네랄 기능성 분말이 댐, 하천, 호소, 연안포구 등의 바닥에 침투시 볼 형태나 일정크기의 고형물로 제작하여 수량과 오염정도 또는 퇴적물 상태를 감안하여 일정량을 투입하면 수중에서 서서히 분해 작용을 하면서 혐기성 환경을 호기성으로 전환하여 수질을 정화시킬 수 있으며, 또한 슬러지를 분해시킨다(도 2 내지 도 4 참조).The natural mineral functional powder of the present invention prepared as described above can be used as the powder itself and can be manufactured and used in various forms such as ball form or soap form to suit the site conditions. H When the natural mineral functional powder of the present invention penetrates into the bottom of dams, rivers, lakes, coastal muzzles, etc., it is produced in the form of a ball or a certain size of solids, and given a certain amount in consideration of the quantity and degree of contamination or the state of sediments. While slowly degrading, the anaerobic environment can be converted into aerobic to purify the water quality, and also to decompose sludge (see FIGS. 2 to 4).
상기 설명에 있어서, 특정 실시예를 들어서 도시하고 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 예를 들면 본 발명의 개념을 이탈하지 않는 범위내에서 이 기술 분야의 통상의 지식을 가진 자에 의해 여러가지로 설계변경할 수 있음은 물론이고, 이와 같이 설계변경하는 것도 본 발명의 청구범위에 포함되는 것은 물론이다.In the above description, the specific embodiments have been shown and described, but the present invention is not limited thereto, for example, by those skilled in the art without departing from the concept of the present invention. Of course, the design can be changed in various ways, and the design change in this manner is also included in the claims of the present invention.
Claims (3)
상기 분쇄혼합단계에서 혼합된 혼합액을 발효용기에 저장하여 18 내지 22℃의 온도에서 45 내지 55일 동안 발효숙성시키는 1차 발효숙성단계와;
상기 1차 발효숙성단계에서 발효숙성된 발효숙성액을 여과포로 여과시키는 여과단계와;
상기 여과단계에서 여과된 30중량부의 발효숙성 여과액에 규소 분말이 65중량부 함유된 35 내지 45중량부의 맥반석 분말과 30 내지 40중량부의 제올라이트 분말을 교반기에 넣고 교반혼합하는 교반혼합단계와;
상기 교반혼합단계에서 교반혼합된 혼합액을 18 내지 25℃의 온도에서 45일 내지 55일 동안 숙성 발효시키는 2차 숙성발효단계와;
상기 2차 숙성발효단계에서 숙성발효된 숙성발효반죽을 태양광선에서 자연 건조시키는 건조단계와;
상기 건조단계에서 건조된 숙성발효 덩어리를 파쇄기로 파쇄하여 분말화시키는 분말화단계를 포함하는 것을 특징으로 하는 천연 미네랄 기능성 분말의 제조방법.6 to 10 parts by weight of persimmon leaves, 6 to 10 parts by weight of oak leaves, 6 to 10 parts by weight of the leaves of 4 to 7 parts by weight of melon, 4 to 7 parts by weight of pineapple, 4 to 7 parts by weight of mango, 4 to 7 weights A pulverized mixing step of rinsing the persimmon persimmon, 4 to 7 parts by weight of bananas, and mixing 20 to 30 parts by weight of water and 18 to 32 parts by weight of brown sugar to a stirrer to mix and grind it;
A first fermentation aging step of storing the mixed solution mixed in the grinding mixing step in a fermentation vessel and fermenting and aging for 45 to 55 days at a temperature of 18 to 22 ° C .;
A filtration step of filtering the fermentation aging liquid fermented in the first fermentation aging step with a filter cloth;
A stirring and mixing step of putting in a stirrer and mixing 35 to 45 parts by weight of ganbanite powder and 30 to 40 parts by weight of zeolite powder containing 65 parts by weight of silicon powder in the 30 parts by weight of the fermentation aging filtrate filtered in the filtration step;
A second aging fermentation step of fermenting the mixed mixture stirred in the stirring and mixing step for 45 to 55 days at a temperature of 18 to 25 ℃;
A drying step of naturally drying the fermented fermented dough which has been aged in the second fermentation fermentation step in sunlight;
Method for producing a natural mineral functional powder, characterized in that it comprises a powdering step of pulverizing the aging fermentation lump dried in the drying step by crushing.