KR20090104302A - The manufacturing process of fabric for dusters with fancy yarn - Google Patents

The manufacturing process of fabric for dusters with fancy yarn Download PDF

Info

Publication number
KR20090104302A
KR20090104302A KR1020080029660A KR20080029660A KR20090104302A KR 20090104302 A KR20090104302 A KR 20090104302A KR 1020080029660 A KR1020080029660 A KR 1020080029660A KR 20080029660 A KR20080029660 A KR 20080029660A KR 20090104302 A KR20090104302 A KR 20090104302A
Authority
KR
South Korea
Prior art keywords
yarn
polyester
fabric
adverb
design
Prior art date
Application number
KR1020080029660A
Other languages
Korean (ko)
Other versions
KR100957842B1 (en
Inventor
윤석천
Original Assignee
(주)풍전티.티
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)풍전티.티 filed Critical (주)풍전티.티
Priority to KR1020080029660A priority Critical patent/KR100957842B1/en
Publication of KR20090104302A publication Critical patent/KR20090104302A/en
Application granted granted Critical
Publication of KR100957842B1 publication Critical patent/KR100957842B1/en

Abstract

PURPOSE: A manufacturing method for washing fabric with fancy yarn is provided to offer superior effects for sloughing off dry skin while offering strong washing functions. CONSTITUTION: A manufacturing method for washing fabric with fancy yarn includes the following steps of: making a core yarn(1) with polyester of 150d/48f; using polyester of 300d/10f as a mother yarn for splitting; using the polyester of 150d/48f as a binding yarn; making the fancy yarn; making the fabric by weaving the manufactured fancy yarn with density of 18~30 strands/in; and dyeing the fabric.

Description

의장사를 이용한 닦이용 포의 제조방법{The manufacturing process of fabric for dusters with fancy yarn}The manufacturing process of fabric for dusters with fancy yarn}

본 발명은 합성섬유 로우 카운트사를 부사로 사용하는 의장사를 이용하여 닦이용 포를 제조하는 방법에 관한 것으로, 더욱 상세하게는 합성섬유 로우 카운트사를 단독으로 사용하거나, 합성섬유 로우 카운트사와 합성섬유 극세사를 함께 사용하여 부사로 하는 의장사를 일반적인 합성섬유, 천연섬유, 반합성섬유 등과 교호로 배열하여 제직하거나, 직물 조직을 2중직 이상 다층 직물로 구성하여 닦이용 포를 제조하는 방법에 관한 것이다.The present invention relates to a method for manufacturing a wiping cloth using a design yarn using a synthetic fiber low count yarn as an adverb, more specifically, using a synthetic fiber low count yarn alone, or a synthetic fiber low count yarn The present invention relates to a method of manufacturing a wiping cloth by arranging alternating yarns made of adverb using fiber microfiber together alternately with general synthetic fibers, natural fibers, and semi-synthetic fibers, or by constructing two or more multi-layered textile fabrics. .

통상적으로 닦음용 포의 기능성은 흡수성을 생각하게 되고, 이러한 개념에 따른 닦음용 포의 소재는 흡습성이 좋은 면 소재가 주로 사용되고 있지만 닦임성에서 만족스럽지 못한 측면이 있었다.In general, the functionality of the cleaning cloth is considered to be absorbent, the material of the cleaning cloth according to this concept is mainly used hygroscopic cotton material, but there was an unsatisfactory aspect in the wipeability.

닦음용 포는 오염 제거 능력과 흡습성을 고려하여, 나일론/폴리에스터 분할형 복합사를 주로 사용하거나, 해도형 복합사를 고수축성 폴리에스터 원사와 공기 교락하여 제조된 원사를 직물의 위사로 사용하여 제조하는 방법이 많이 시도되고 있으나, 나일론/폴리에스터 분할형 복합사의 경우는 0.2 데니어 이상으로 단위 길이 당 복합사의 밀도가 낮아 표면적이 적게 되므로 닦임성이 충분치 못한 문제점이 있었고, 또한 폴리에스터 해도형 복합사에 비해 상대적으로 고가인 점 때문에 다양화시켜 실용화 되지 못한 실정이었다.Wiping cloths are mainly made of nylon / polyester split type yarns in consideration of decontamination ability and hygroscopicity, or yarns made by air-entangled islands-in-the-sea composite yarns with highly shrinkable polyester yarns as fabric wefts. Although many methods have been tried, a nylon / polyester split composite yarn has a problem of insufficient wiping due to the low density of the composite yarn per unit length of 0.2 denier or more and a low surface area. Due to its relatively high price compared to the company, it was not practically diversified.

이러한 닦임성과 경제성을 개선하기 위하여 대한민국 실용신안등록 제336386호가 제시되고 있으며, 상기 실용신안 공보에는 경질섬유영역과 고흡수성 섬유 영역이 교차 배치되도록 하여 고흡수성 섬유영역이 세척기능을 주로 수행하고 경질섬유영역이 오염 제거기능을 수행하도록 한, 경질섬유와 고흡수성 섬유가 교차 배치된 직·편물로 이루어진 걸레 포가 게시되어 있지만, 이는 고흡수성 섬유로 인한 걸레의 속건성이 결여되어 위생적이지 못할 뿐만 아니라, 건조한 상태로 청소를 하는 과정에서 섬유 분진이 발생하는 문제와 그로 인한 사용 수명의 단축 문제 등이 있었다.Korean Utility Model Registration No. 336386 has been proposed to improve the cleanliness and economic efficiency, and the utility model publication has a hard fiber area and a super absorbent fiber area intersected so that the superabsorbent fiber area mainly performs a washing function and is hard. Mop cloths made of woven and knitted fabrics in which hard fibers and superabsorbent fibers are intersected have been posted, which makes the fiber area perform decontamination, but this is not only hygienic due to lack of fast drying of the mop due to superabsorbent fibers, In the dry cleaning process, there were problems such as fiber dust and shortened service life.

또한, 대한민국 공개특허 제2004-77598호에서는 해도형 복합사를 단독으로 사용하여 직물을 제직하고, 대상물과 원단과의 마찰을 줄이기 위하여 엠보싱 가공을 하여 닦임성과 실용성을 추구하는 방법이 제안되고 있지만, 이는 고밀도로 제직을 하더라도 알칼리 감량가공으로 원단의 형태가 헝클어지므로 실용적이지 못한 문제점이 있었다.In addition, Korean Patent Laid-Open Publication No. 2004-77598 proposes a method of weaving fabrics by using island-in-the-sea composite yarns alone and embossing to reduce the friction between the object and the fabric, thereby purifying wiping and practicality. This is not practical because the shape of the fabric is matted due to alkali weight loss processing even when weaving at high density.

또한, 대한민국 실용신안등록 제219431호에는 지조직에 키토산 등으로 항균 가공된 흡수성이 양호한 면사를 사용하여 정전기의 발생을 억제하고 세균의 발생을 저지함으로서 보다 위생적이며 깨끗하게 먼지를 제거할 수 있는 세척포를 제안하고 있으나, 이는 먼지의 제거에는 탁월한 효과가 있으나 수세미 작용을 하지 못하기 때문에 딱딱한 불순물을 제거하는 데에는 적합하지 않아 별도의 수세미를 준비하여야 하는 문제가 있었다.In addition, Korean Utility Model Registration No. 219431 uses a cotton yarn treated with chitosan and antibacterial absorbing material to prevent the generation of static electricity and prevent the generation of bacteria by using a cotton yarn with antibacterial treatment. Although it has been proposed, which has an excellent effect on the removal of dust, but because it does not work with a scrubber, there is a problem that you need to prepare a separate scrubber because it is not suitable for removing hard impurities.

본 발명은 상기한 바와 같이 종래 기술이 지니는 문제를 해결하기 위하여 사용 원사의 단사섬도가 굵은 원형단면 또는 이형단면 구조의 분섬모사(分纖母絲; Mother Yarn for splitting)가 외부로 표출되도록 제직 또는 편직하여 흡습성과 닦임성이 양호한 닦이용 포를 제공하기 위한 것이다.In order to solve the problems of the prior art as described above, weaving or weaving so that the single yarn fineness of the yarn used is a mother yarn for splitting having a thick circular cross-section or a hetero-cross section structure. It is to provide a wiping cloth for knitting and having good hygroscopicity and wiping property.

또한, 본 발명은 표면이 부드러워 촉감이 양호하면서 먼지와 같은 작고 부드러운 오물을 제거할 때에는 적은 힘으로 제거할 수 있으며, 포의 내면이 뻣뻣하기 때문에 딱딱한 불순물을 제거할 때에는 약간의 힘을 가하면서 닦아주면 용이하게 제거할 수 있어 수세미를 겸할 수 있는 닦이용 포를 제공하기 위한 것이다. In addition, the present invention can be removed with a small force when removing a small soft dirt, such as dust, while the surface is smooth and good feel, and because the inner surface of the fabric is stiff, wiping with a slight force to remove the hard impurities It is an object of the present invention to provide a wipe cloth that can be easily removed by giving a loofah.

또한, 본 발명은 단사섬도가 굵은 분섬모사를 이용하기 때문에 통기성이 양호하여 속건성이 있으므로 항상 위생적으로 이용할 수 있는 닦이용 포를 제공하기 위한 것이다.In addition, the present invention is to provide a wiping cloth that can always be used hygienically because it has good breathability and quick-drying, because the single yarn fineness is used for the coarse fine yarn.

본 발명은 상기한 목적을 달성하기 위한 것으로 도 1에 나타낸 바와 같은 의장사를 이용한 닦이용 포의 제조방법에 관한 것이다.The present invention relates to a method for producing a wiping cloth using a design yarn as shown in Figure 1 to achieve the above object.

즉, 본 발명은That is, the present invention

폴리에스터 150d/48f를 심사(1)로 하고 폴리에스터 200d/10f 2가닥 혹은 폴 리에스터 300d/10f 1가닥으로 되는 분섬모사(分纖母絲; Mother Yarn for splitting)를 부사(2)로 사용하며, 역시 폴리에스터 150d/48f를 압사(3)로 사용하며, 부사(2)를 심사(1)에 비하여 1.5~6.0배로 오버피드하여 의장사(P)를 만드는 단계; Polyester 150d / 48f is used as the screening (1), and mother yarn for splitting is used as the adverb (2), which consists of 2 strands of polyester 200d / 10f or 1 strand of polyester 300d / 10f. And using polyester 150d / 48f as an injectable yarn 3 and overfeeding the adverb 2 by 1.5 to 6.0 times as compared with the screening 1 to create a design yarn P;

제조된 의장사(P)를 경사와 위사 각각 18~30본/in의 밀도로 제직하여 원단을 만드는 단계; 및Weaving the prepared design yarn (P) to the density of 18-30 pieces / in each of the warp and weft yarn to make a fabric; And

제조된 원단을 통상의 방법으로 염색가공하는 단계로 이루어지는 것을 특징으로 하는 의장사를 이용한 닦이용 포의 제조방법에 관한 것이다. The present invention relates to a method for manufacturing a wipe cloth using a design yarn comprising the step of dyeing the fabric produced in a conventional manner.

한편, 본 발명은On the other hand, the present invention

상기한 의장사(P) 제조단계에서 부사(2)로 폴리에스터 200d/10f를 모두 사용하지 않고 폴리에스터 200d/10f 와 PN(폴리에스터/나일론) 160d/72f 분할사 또는 다른 섬유를 사용하므로서 PN 분할사나 다른 섬유에 의하여 미세먼지에 대한 닦임성이 증진되고, 폴리에스터 200d/10f에 의한 딱딱하고 큰 오염물에 대한 제거력을 가지며, 특히 폴리에스터 200d/10f 단독으로 사용할 때의 수분 흡수율이 낮은 단점을 보완하는 효과를 가진다.PN by using polyester 200d / 10f and PN (polyester / nylon) 160d / 72f split yarn or other fibers without using both polyester 200d / 10f as an adverb (2) in the above design yarn (P) manufacturing step Wiping ability to fine dust is improved by split yarn or other fibers, and it has the ability to remove hard and large contaminants by polyester 200d / 10f, and especially low water absorption when using polyester 200d / 10f alone. It has a complementary effect.

또한, 본 발명은 In addition, the present invention

상기한 의장사(P)와 폴리에스터 200d/10f 대신 모두 PN 160d/72f 분할사를 부사로 사용한 의장사를 각각 1:1로 배열할 뿐만 아니라 스트라이프와 체크무늬와 같이 무늬를 형성하도록 배열하여 제직한 후 염색가공 및 제단, 봉제하여 제품화 하여도 좋다.Instead of the above design yarns (P) and polyester 200d / 10f, we not only arrange the design yarns using PN 160d / 72f split yarns as adverbs in 1: 1, but also arrange them to form patterns like stripes and checkered patterns. After the dyeing process, altar and sewing may be commercialized.

한편, 상기에서는 일반 직물원단에 대하여 설명하였으나, 상기한 의장사를 이용하여 이중지로서 한쪽은 폴리에스터 200d/10f를 이용한 의장사가 배열되고, 반대쪽은 PN 160d/72f 분할사를 이용한 의장사가 배열된 원단을 제직할 수도 있으며, 딱딱하고 큰 오염물에 대한 제거하고자 할 때에는 폴리에스터 200d/10f를 이용한 의장사가 배열된 면을 이용하고, 비누칠을 하거나 부드러운 먼지를 제거하고자 할 때에는 PN 160d/72f 분할사를 이용한 의장사가 배열된 면을 이용하면 편리하게 사용할 수 있다.On the other hand, in the above description of the general fabric fabric, using the above-mentioned design yarn as a double paper, one of the design yarns using polyester 200d / 10f is arranged, the other side of the design yarns using PN 160d / 72f split yarn is arranged Weaving fabrics can also be used. For removing hard and large contaminants, use a cotton linen with polyester 200d / 10f, and use PN 160d / 72f split yarn to remove soap or soft dust. If you use the surface of the chairman using the array can be used conveniently.

상기에서 오버피드의 비율을 1.5배미만으로 하면 부사가 짧아져 의장사의 장식효과가 줄어들고, 그 비율이 6.0배를 초과하면 부사가 엉켜서 의장사 제조가 어려운 문제가 있다.If the ratio of the overfeed is less than 1.5 times, the adverb is shortened and the decorative effect of the chairman is reduced, and if the ratio exceeds 6.0 times, the adverb is entangled, making it difficult to manufacture the design yarn.

또한, 경사와 위사의 밀도가 각각 18본/in 미만이면 직물의 조직이 흐트러지고 강력이 저하되는 문제가 있고, 밀도가 30본/in을 초과하면 장식사로서 제직하기가 어려운 문제가 발생한다.In addition, if the density of the warp and weft yarn is less than 18 bones / in, there is a problem that the structure of the fabric is disturbed and strength is lowered, and if the density exceeds 30 bones / in, it is difficult to weave as a decorative yarn.

상기한 바와 같은 본 발명은 특히 20d 이상의 굵은 필라멘트로 구성된 강직한 원사가 돌출되어 있기 때문에 강한 오염 제거력을 가지므로 피부 각질 제거에 좋은 효과를 가지며, 이러한 강직성 사를 부사로 되어 있으므로 소재의 중량대비 원단의 부피감을 늘리는데 유리하고, 공극이 커서 비누거품 등이 잘 생성되고, 통기성이 양호하여 사용 후 쉽게 건조할 수 있어 보다 깨끗하고 위생적인 닦이용 포를 제공하는 장점이 있다.As described above, the present invention has a strong decontamination power because it has a strong decontamination power, especially because a rigid yarn composed of coarse filaments of 20 d or more is protruded, and thus has a good effect on skin exfoliation. It is advantageous to increase the volume of the pores, large pores, soap bubbles, etc. are well generated, and breathability is good to dry easily after use has the advantage of providing a cleaner and hygienic cleaning cloth.

상기에서, 심사로 폴리에스터 150d/48f를 사용하는 것으로 설명하고, 부사로서 폴리에스터 200d/10f 혹은 폴리에스터 300d/10f로 한정하여 설명하고 있으나, 이는 가장 보편적인 예를 보인 것일 뿐 심사로서 폴리에스터 150d/48f 전후의 실을 사용할 수 있고, 부사로서는 단사섬도가 20d 이상인 다른 합사를 사용할 수 있음은 물론이다.In the above description, it is described that the polyester 150d / 48f is used as the screening, and the description is limited to the polyester 200d / 10f or the polyester 300d / 10f as an adverb, but this is only the most common example and the polyester is the screening. Threads around 150d / 48f can be used, and of course, other plywood having a single yarn fineness of 20d or more can be used as an adverb.

상기와 같은 본 발명은 PN 160d/72f 분할사에 의하여 면포와 같은 부드러움과 흡습성을 지니면서 폴리에스터 200d/10f 혹은 폴리에스터 300d/10f 에 의한 강직성과 통기성 및 볼륨감을 갖는다.As described above, the present invention has a softness and hygroscopicity such as cotton cloth by PN 160d / 72f split yarn, and has rigidity, breathability, and volume by polyester 200d / 10f or polyester 300d / 10f.

또한, 본 발명은 20d 이상의 굵은 필라멘트로 구성된 강직한 원사가 돌출되어 있기 때문에 강한 오염 제거력을 가지므로 피부 각질 제거에 좋은 효과를 갖는다.In addition, the present invention has a strong decontamination power because the rigid yarn consisting of coarse filament of 20d or more is protruding, so it has a good effect on the exfoliation of the skin.

또한, 본 발명은 목용용품, 청소용품, 주방용품, 세차용품 등으로 그 용도가 다양한 효과를 갖는다.In addition, the present invention has a variety of effects, such as wooden supplies, cleaning supplies, kitchen appliances, car wash products.

이하에 본 발명의 내용을 실시예에 의하여 설명하지만 본 발명의 권리범위가 이들 실시예로 한정되는 것은 아니며, 실시예는 본 발명의 내용을 용이하게 이해할 수 있도록 제시되는 것일 뿐이다.The following describes the contents of the present invention by examples, but the scope of the present invention is not limited to these examples, the examples are only presented to facilitate understanding of the contents of the present invention.

<실시예 1><Example 1>

폴리에스터 150d/48f를 심사로 하고 폴리에스터 200d/10f 2가닥을 부사로 사용하고, 역시 폴리에스터 150d/48f를 압사로 사용하며, 부사를 2.0배로 오버피드하여 의장사를 만든 다음, 이 의장사를 경·위사 각각 24본/in의 평직으로 제직하여 원단을 만들고, 제조된 원단을 통상의 방법으로 염색가공, 제단, 봉제하여 제품화 하여 포장 및 출하하였다.The polyester 150d / 48f is used as the screening, and the polyester 200d / 10f 2-strand is used as the adverb, and the polyester 150d / 48f is used as the injector, and the design is made by overfeeding the adverb by 2.0 times. The fabrics were made by weaving them into plain weaves of 24 pieces / in each of light and weft yarns, and the manufactured fabrics were dyed, processed, and sewn into products in the usual manner for packaging and shipping.

얻어진 닦이용 포는 흡습성은 낮았으나, 뻣뻣한 촉감을 가지며 볼륨성이 양호하고 피부각질과 같은 딱딱한 오염물질을 제거하기에 적합하였다.The obtained wipes had low hygroscopicity, but had a stiff hand, had good volume, and was suitable for removing hard contaminants such as keratin.

<실시예 2><Example 2>

폴리에스터 200d/10f 2가닥 대신에 폴리에스터 200d/10f 한 가닥과 PN 160d/72f 분할사를 부사로 사용한 외에는 실시예 1과 같은 방법으로 닦이용 포를 제조하였다.A wiping cloth was prepared in the same manner as in Example 1, except that one strand of polyester 200d / 10f and a PN 160d / 72f split yarn were used as an adverb instead of two strands of polyester 200d / 10f.

얻어진 닦이용 포는 먼지와 같은 오물을 제거도 가능하고 흡습성과 닦임성이 양호하여 목욕용품으로 사용에 적합하였다.The obtained cleaning cloth was able to remove dirts such as dust, and was good for use as a bath article because of good hygroscopicity and wiping property.

<실시예 3><Example 3>

실시예 1에서 사용한 의장사와 폴리에스터 200d/10f 대신 모두 PN 160d/72f 분할사를 부사로 사용한 의장사를 각각 1:1로 배열하여 경·위사 각각 30본/in의 평직으로 제직하여 원단을 만들고 이를 염색가공, 제단, 봉제하여 제품화하여 포장 및 출하하였다.Instead of the yarn and polyester 200d / 10f used in Example 1, the yarns using PN 160d / 72f split yarns as adverbs were arranged one by one and weaved into 30 weaves / in of plain weave, respectively. It was dyed, altared, sewn, packaged and shipped.

얻어진 닦이용 포는 흡습성과 닦임성이 양호하여 세차용 포에 적합하였다.The obtained wipe cloth was good in hygroscopicity and wipeability, and was suitable for the wash cloth.

도 1은 본 발명에 이용되는 의장사를 보인 일예시도이다.1 is an exemplary view showing a design yarn used in the present invention.

* 도면의 주요부에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

1; 심사 One; judge

2; 부사 2; adverb

3; 압사3; Apsa

Claims (3)

닦음용 포의 제조방법에 있어서, 폴리에스터 150d/48f를 심사로 하고 폴리에스터 200d/10f 2가닥 혹은 폴리에스터 300d/10f 1가닥으로 되는 분섬모사(分纖母絲; Mother Yarn for splitting)를 부사로 사용하고, 역시 폴리에스터 150d/48f를 압사로 사용하며, 부사를 1.5~6.0배로 오버피드하여 의장사를 만드는 단계; In the manufacturing method of the cloth for wiping, polyester 150d / 48f is used as the screening, and the yarn yarn which is made up of two strands of polyester 200d / 10f or one strand of polyester 300d / 10f is attached. Using, and also using polyester 150d / 48f as an injectable sand, overfeeding the adverb 1.5 to 6.0 times to make a design yarn; 제조된 의장사를 경사와 위사 각각 18~30본/in의 밀도로 제직하여 원단을 만드는 단계; 및Weaving the prepared yarn with a density of 18-30 pieces / in of warp and weft yarns respectively to make a fabric; And 제조된 원단을 통상의 방법으로 염색가공하는 단계로 이루어지는 것을 특징으로 하는 의장사를 이용한 닦이용 포의 제조방법. Method of producing a wiping cloth using a design, characterized in that the dyeing process of the fabric prepared in a conventional method. 제1항에 있어서, The method of claim 1, 의장사는 폴리에스터 150d/48f를 심사로 하고 폴리에스터 200d/10f 와 PN 160d/72f 분할사 또는 다른 섬유를 부사로 사용하여 제조된 것을 특징으로 하는 의장사를 이용한 닦이용 포의 제조방법. The method of manufacturing a wiping cloth using a chairman yarn, characterized in that the chairman is manufactured using polyester 150d / 48f as the screening, polyester 200d / 10f and PN 160d / 72f split yarn or other fibers as an adverb. 닦음용 포의 제조방법에 있어서, In the manufacturing method of the cloth for wiping, 폴리에스터 150d/48f를 심사로 하고 폴리에스터 200d/10f 2가닥 혹은 폴리에스터 300d/10f 1가닥으로 되는 분섬모사(分纖母絲; Mother Yarn for splitting)를 부사로 사용하고, 역시 폴리에스터 150d/48f를 압사로 사용하며, 부사를 1.5~6.0배로 오버피드하여 제조된 의장사와, 폴리에스터 200d/10f 대신 모두 PN 160d/72f 분할사를 부사로 사용한 의장사를 각각 1:1로 배열하여 경·위사 각각 30본/in의 밀도로 제직하여 원단을 만드는 것을 특징으로 하는 의장사를 이용한 닦이용 포의 제조방법.Polyester 150d / 48f is used as the screening, and the yarn yarn (split) of mother 200n / 10f or polyester 300d / 10f is used as an adverb, and polyester 150d / is also used. 48f is used as an injector, and the design yarn manufactured by overfeeding the adverb 1.5 to 6.0 times and the design yarn using PN 160d / 72f split yarn as the adverbs in 1: 1 instead of polyester 200d / 10f. Method of manufacturing a wiping cloth using a weft yarn, characterized in that weaving each of the weaving yarn to a density of 30 pieces / inch.
KR1020080029660A 2008-03-31 2008-03-31 The manufacturing process of fabric for dusters with fancy yarn KR100957842B1 (en)