KR20090048848A - Composite powder comprising omega oil and stauntonia hexaphulla extracts and powdery type color cosmetic composition comprising the composite powder - Google Patents

Abstract

The present invention is a composite powder coated with silicone oil by impregnating (collecting) a mixture of omega oil dissolved in a dipropylene glycol solvent and an omega oil dissolved in a dipropylene glycol solvent to improve skin roughness and skin moisturizing ability. The application can overcome the problems of the formulation of water-soluble active ingredients such as honeybee extract and the limitations of the use of water, and can overcome the shortcomings of omega oils such as discoloration and odor, thereby maximizing the effect of improving skin moisturizing power, and making the skin brighter and brighter It relates to a powder type color cosmetic composition capable of producing a sense. To this end, the composite powder for color cosmetics comprising an omega oil and an extract of beech according to the present invention is 2 to 10% by weight of omega oil, 10 to 20% by weight of dipropylene glycol, 8 to 15% by weight of beech extract, silicone oil 1 To 10 to 10% by weight and the balance comprises a porous silica, and provides a powder-type color cosmetic composition comprising a composite powder for color cosmetics comprising the omega oil and beech extract.

Beech extract, omega oil, dipropylene glycol, porous silica, composite powder, color cosmetic

Description

Composite powder for color cosmetics containing omega oil and beech extract and powder type color cosmetic composition comprising the same.

The present invention relates to a composite powder for color cosmetics comprising an omega oil and a beech extract and a powder type color cosmetic composition comprising the same, and more specifically, to the skin roughness and skin moisturizing effect of D. By collecting a mixture of omega oils dissolved in propylene glycol solvent on porous silica and applying composite powder coated with silicone oil to powder type color cosmetics, it is possible to solve the problem of formulation of water soluble active ingredients in powder type color cosmetics and the limitations of water use. It is possible to overcome, and to maximize the effect of improving the skin's moisturizing power without discoloration and discoloration, which is a disadvantage of the omega oil, and a composite powder for color cosmetics comprising an omega oil and an extract of the beech tree, which can produce a brighter and brighter makeup and including the same Powder Type Tint Cosmetic Tank It is about the relic.

Conventional color cosmetics have been developed with the main function of covering the skin defects such as freckles, blemishes, blemishes, etc., but expressing the skin color beautifully. Recently, there has been a change in the direction of developing cosmetics in which natural care, skin care elements such as sunscreen and treatments are added. In particular, the same cosmetic formulation technology as the basic cosmetics has been researched and developed for the skin care effect, and among them, the moisturizing effect.

Foundations of color cosmetics are classified into powder type foundation, O / W type emulsion type foundation, W / O type emulsion type foundation, and oil type foundation depending on the formulation. Moisturizing varies greatly. In particular, powder type foundation is composed of powder and small amount of oil-based ingredients, so it is difficult to mix water-soluble active ingredients such as honeybee extract and moisturizing ingredients such as polyols. It is a discontinuity. Because of this, the powder type foundation has a lower moisturizing effect than other formulations. However, in terms of simplicity and portability, the powder type foundation is the mainstream of the current color cosmetics, applying a variety of techniques to give a moisturizing effect.

Previously, a technique of coating a powder with excellent moisture retention properties such as collagen, hyaluronic acid and amino acid derivatives has been used (Japanese Patent Laid-Open No. 61-69710, Japanese Patent Laid-Open No. 61-28230, and Japanese Patent Laid-Open) Japanese Patent Application Laid-Open No. 62-127092, etc.), a technique of blending a highly moisturizing water-soluble chitin derivative and a water-soluble chitosan derivative with porous starch (Japanese Patent Laid-Open Publication No. Hei 7-76508), and a lipid two-molecule amino acid complex Various powder modification techniques such as coating technology (Japanese Patent Application Laid-open No. Hei 9-302260), coating technology of a gelatin protein fiber having a crosslinked structure and a moisturizer to the powder (Japanese Patent Publication No. Hei 8-92035) have been tried. It was.

However, even when the moisturizing ingredient is coated on the pigment, the moisturizing ingredient is separated from the pigment by sweat or sebum, and thus the moisturizing function is not exhibited, or under low humidity, the moisture is absorbed from the skin. There is a problem in that the sticky feeling may be exhibited when applied to the color cosmetics.

On the other hand, omega oil is a raw material commonly used in cosmetics and has a function of skin moisturizing and anti-inflammatory, and has been especially used in skin care cosmetic formulations. However, omega oils have the disadvantage of causing color change when formulated and inherent off-flavor due to rancidity upon contact with air.

In order to solve this problem, the acidification of the formulation is performed through a buffer solution of disodium hydrogen phosphate and citric acid or a buffer solution of potassium dihydrogen phosphate and disodium hydrogen phosphate. Efforts have been made to prevent technology (US Pat. No. 6,303,656). In addition, the application of omega oil in powder type color cosmetics where the use of water is extremely limited is limited. In Korea, several technologies, such as the development of water-in-oil type composition as a color cosmetic (Korea Patent Publication No. 2001-0065703), have been applied. It is just being tested.

The present invention has been made to solve the above problems, an object of the present invention is to provide a moisturizing effect on the skin without causing discoloration and discoloration due to rancidity when formulating omega oil and formulation of omega oil It is to provide a complex powder for color cosmetics comprising omega oil and beech extract that can maximize and produce a brighter and brighter makeup and powder type color cosmetic composition comprising the same.

Color composite cosmetic powder containing omega oil and beech extract according to the present invention, 2 to 10% by weight of omega oil, 10 to 20% by weight of dipropylene glycol, 8 to 15% by weight of beech extract, silicone oil 1 to It is characterized by comprising a porous silica as 10% by weight and the balance.

The composite powder may be formed by supporting the omega oil and dipropylene glycol on the porous silica and coating the porous silica on which the omega oil and dipropylene glycol are supported with silicone oil.

The composite powder may be formed by being supported on the porous silica in a solution state in which the omega oil is dissolved in the dipropylene glycol.

The porous silica constituting the composite powder may have an average particle diameter of 6 to 9 μm.

In addition, a powder type color cosmetic composition comprising a composite powder for color cosmetics comprising an omega oil and a beech extract according to the present invention, as a powder type color cosmetic composition, 2 to 10% by weight of omega oil, 10 to 10 dipropylene glycol 20 wt%, 8-15 wt% of beech extract, 1-10 wt% of silicone oil, and 5-15 wt% of the composite powder for color cosmetics comprising porous silica as a balance and a balance of a conventional color cosmetic composition Characterized in that made.

According to the present invention, the omega oil is dissolved in a dipropylene glycol solvent, not water, and then mixed with a beech extract, the mixture is collected in porous silica and applied to a powder-type color cosmetic, thereby limiting the formulation of water-soluble active ingredients and the use of water. It was able to overcome the limitations of the product, and it was able to maximize the skin's moisturizing power without discoloration and discoloration, which are disadvantages of the omega oil, and to produce a brighter and brighter makeup. There is an effect of providing a powder and a powder type color cosmetic composition comprising the same.

Hereinafter, the present invention will be described in detail with reference to embodiments of the present invention.

These examples are only for illustrating the present invention in more detail, it will be apparent to those skilled in the art that the scope of the present invention is not limited by these examples in accordance with the gist of the present invention. .

Color composite cosmetic powder containing omega oil and honey bee extract according to the present invention, omega oil 2 to 10% by weight, dipropylene glycol 10 to 20% by weight, beech extract 8 to 15% by weight, silicone oil 1 To 10% by weight and the balance is characterized by comprising a porous silica.

The omega oil is mainly used in various fields to give moisture, anti-inflammatory and soft texture to the stratum corneum. The omega oil is a raw material commonly used in cosmetics and has a function of skin moisturizing and anti-inflammatory, and has been used in particular in skin care cosmetic formulations. The omega oil contains the most polyunsaturated fatty acid among all oil species used by humans. It comprises about 48% alpha-linolenic acid (omega-3 oil), about 37% linolenic acid (omega-6 oil) and additionally about 8% oleic acid (omega-9 oil). It also contains large amounts of tocopherols. However, omega oils have the disadvantage of causing color change when formulated and inherent off-flavor due to rancidity upon contact with air. In order to apply the characteristics of the omega oil to the powder-type color cosmetics, the present inventors first use a polyol moisturizer such as dipropylene glycol to dissolve the omega oil in order to prevent the restriction of water use and the pH rise of the omega oil due to the characteristics of the powder. And in order to maximize the moisturizing effect of the omega oil dissolved dipropylene propylene glycol and beech extract. When the omega oil is used in less than 2% by weight, there may be a problem that it is difficult to expect the moisturizing effect by the omega oil, on the contrary, when it exceeds 10% by weight, it is difficult to dissolve in dipropylene glycol to the porous silica There may be a problem that the homogeneous loading of the becomes difficult.

The beech extract was mixed with butylene glycol and ethanol in the same mass ratio, and stirred to form a single phase, which is used as a cosolvent in an extraction process using a supercritical fluid. At this time, the material of the supercritical fluid may be carbon dioxide. Here, supercritical fluid (SCF) is defined as a material in a state having a condition above a critical pressure and a critical temperature, and has a unique characteristic different from a general liquid or gas. Critical point means a limit point at which a substance can exist in equilibrium in the liquid or gas phase. Under pressure and temperature conditions below the critical point, water or carbon dioxide is present in the gas, liquid and solid phases. As the temperature or pressure increases, the liquid phase decreases in density due to thermal expansion, and the gas phase continues its opposite change in density as the pressure increases. It will have the same value and there will be no distinction between the two phases. This state is called a supercritical state, and, unlike solids, it is called supercritical fluid (SCF) because it is easily deformed and has the characteristics of a free flowing fluid. For reference, the critical points of water are 221 bar and 374 ° C, and carbon dioxide is 73.8 bar and 31.1 ° C. The applications of supercritical fluids include separation by extraction and treatment of hardly degradable wastes using polymer polymerization or supercritical water oxidation. As mentioned above, research on the use of carbon dioxide, which is environmentally friendly and has a critical point of 73.8 bar and 31.1 ° C., is easy to handle technically and is abundant on the earth, thus securing economic feasibility. Supercritical carbon dioxide is already commercialized in supercritical fluid extraction (SFE) processes that remove caffeine from coffee or tea. In addition, a process for extracting hops, other natural products, precursors of chemicals, natural oils, and environmental pollutants by using supercritical carbon dioxide has been developed or commercialized. The basic principle of SFE is that, like general extraction, when the raw material containing the extract comes in contact with the SCFs, the first step is to distribute the volatiles into the supercritical phase and after the SCFs containing the extract are separated from the raw material. In addition, it can be thought of as a second step of separating the extract through the temperature / pressure control. In the case of SFE, in particular, in the case of carbon dioxide, since it is a gas state at room temperature and atmospheric pressure, it is possible to completely separate the extract and the solvent in the second step unlike the existing extraction process, and the separated solvent increases the temperature / pressure. Make it extractable supercritical and recycle. The beech tree is distributed in Korea, Japan, and Taiwan as a stalk (Stauntonia hexaphulla), and grows in valleys or forests of 700m or less in the southern part of the country, and is also called aspen. Stems and leaves contain saponins, phenols, and various amino acids. Fruits are oval, yellow, and polysaccharides, and are known for their excellent moisturizing properties. Seeds contain mubenin A, B and C, triterpenoid saponins. Stems and roots were used as herbal medicines such as anti-inflammatory, antipyretic, and sore throat in the herbal medicine, and the fruit is known to have analgesic effects in addition to polysaccharides. The mulberry tree is dried until its weight does not change, and leaves and stems and fruits are crushed to a size of 0.3 cm or less using a grinder. The pulverized beech pulverized tree and the co-solvent are mixed at a mass ratio of 1: 2, stirred for 30 minutes, and subjected to primary extraction for 3 hours using ultrasonic waves at 60 ° C. The co-solvent mixture is introduced into a supercritical extraction tank, sealed, and the pressure is increased by supplying carbon dioxide using a high pressure gas pump. The temperature in the extraction tank is gradually raised to 40 ° C., and then maintained for about 1 hour. The extract is released while supplying carbon dioxide, and the carbon dioxide and the beech extract are separated by depressurizing to atmospheric pressure. This extract is collected by a collector and used in the present invention. When the beech extract is used in less than 8% by weight, there may be a problem that it is difficult to expect a moisturizing effect by the beech extract, on the contrary, when it exceeds 15% by weight, diproylene glycol dissolved omega oil After mixing with the porous silica, the characteristics of the powder are lost, and there is a problem in that a light form can not be obtained due to agglomerated form.

The dipropylene glycol has a structure of Formula 1 below, a polyol moisturizer such as glycerin, sorbitol, propylene glycol, etc., has less skin irritation than other moisturizers, and has excellent miscibility with water-soluble active ingredients such as beech extract to dissolve omega oils. Suitable for solvents and auxiliary moisturizers.

The inventors of the present invention have studied omega oils that can be applied to powder-type color cosmetics. After dissolving omega oils in a dipropene glycol solvent rather than water, the mixture is mixed with beech extract and collected in porous silica powder to powder-type color cosmetics. The present invention was completed by finding out that it is possible to overcome the problems of the formulation of water-soluble active ingredients and the limitations of water use, and to eliminate discoloration and odor that are disadvantages of omega oil. The dipropylene glycol functions as a solvent of the omega oil to enable uniform loading on the porous silica, and when the amount of the dipropylene glycol is less than 10% by weight, the omega oil can be sufficiently dissolved. On the contrary, if it exceeds 20% by weight, after mixing with the beech extract and being collected in porous silica, the powder may lose its properties and become agglomerated to obtain a light feeling. have.

The porous silica has a structure represented by the following formula (2), it is preferable that the average particle diameter in the range of 6 to 9㎛ as inorganic fine particles.

When the average particle diameter of the porous silica is less than 6㎛, there may be a problem that the trapping capacity of the mixture of dipropylene glycol and honey bee extract in which omega oil is dissolved because the particles are too small, on the contrary if the particle exceeds 9㎛, Too large to feel the roughness when applied to the cosmetic powder-type cosmetics floating, there may be a problem that the adhesion is poor.

On the other hand, the present inventors know that the method of coating the powder surface with a moisturizing agent has a disadvantage in that the moisture resistance is improved but the water resistance is poor, and the surface treatment with silicone oil to improve this. That is, the composite powder is formed by supporting the omega oil and dipropylene glycol on the porous silica, and coating the porous silica on which the omega oil and dipropylene glycol are supported with silicone oil. After such a surface treatment, when applied to the skin, it was confirmed that the moisturizing ingredient gradually bleeds out and excellent in both water resistance and moisturizing power.After makeup, sebum or sweat secreted over time is absorbed by porous silica and more brightly expressed The present invention can achieve this. The silicone oil used for the surface treatment has a structure of Formula 3 below.

Wherein R is selected from the group consisting of hydrogen, methyl, fluoroalkyl (alkyl is an alkyl group of 1 to 20 carbon atoms), alkyl of 1 to 20 carbon atoms, aminoalkyl (alkyl is 1 to 20 carbon atoms), fatty acid or epoxy X and Y may be an integer of 15 to 20 as an integer of the same number, more preferably, the sum of X and Y may be an integer of 30. It can be understood that the silicone oil as such a coating agent is known to those skilled in the art to the extent that it is commercially available and can be used. Examples thereof include the product names KF-99P and KF-9901 of Shinwol Chemical Co., Ltd. , KF-9908, KF-9909 and KP-574, but the present invention is not limited thereto.

The composite powder may be formed by being supported on the porous silica in a solution state in which the omega oil is dissolved in the dipropylene glycol. This serves to ensure that the omega oil is homogeneously supported on the porous silica. This is because the omega oil is not supported in the pores of the porous silica even if the omega oil is mixed with the porous silica as it is because of the high viscosity of the omega oil.

In addition, a powder type color cosmetic composition comprising a composite powder for color cosmetics comprising an omega oil and a beech extract according to the present invention, as a powder type color cosmetic composition, 2 to 10% by weight of omega oil, 10 to 10 dipropylene glycol 20 wt%, 8-15 wt% of beech extract, 1-10 wt% of silicone oil, and 5-15 wt% of the composite powder for color cosmetics comprising porous silica as a balance and a balance of a conventional color cosmetic composition Characterized in that made.

That is, the powder-type color cosmetic composition according to the present invention is mixed with the composite powder for color cosmetics comprising the omega oil and the beech extract according to the present invention to a commonly known and commercially available cosmetic composition, and supported on the composite powder To improve the skin moisturizing effect by omega oil and beech extract, characterized in that it provides a cosmetic powder and easy-to-use powder type cosmetics, wherein the complex powder for color cosmetics comprising the omega oil and beech extract As described above, 2 to 10% by weight of omega oil, 10 to 20% by weight of dipropylene glycol, 8 to 15% by weight of mulberry extract, 1 to 10% by weight of silicone oil and the balance comprises porous silica.

Production Example  One

The method for preparing a composite powder in which a mixture of dipropylene glycol in which omega oil is dissolved and an extract of mulberry is supported on porous silica is as follows. Table 1 below shows the weight fractions of the components.

ingredient Preparation Example 1 Content (% by weight) Porous silica 60 Dipropylene glycol 20 Omega oil 5 Bee extract 10 Silicone oil 5

First, in order to dissolve the omega oil in dipropylene glycol, after heating to 90 ℃ to dissolve, the dissolved content is cooled to room temperature, and then mixed with the beech extract. Next, a porous silica was added to an Ace Homogenizer (Nihonseiki Kaisha, Ltd., Japan), and then the mixed contents were slowly added to the porous silica to collect (capture) the contents. At this time, the stirring speed was 5,000 to 10,000 rpm. After the contents were all supported, the mixture was further stirred for 3 minutes at the same stirring speed. Next, in order to perform the surface treatment, the coating agent was mixed with the solvent hexane in a weight ratio of 1: 4, and then slowly added to the ace homogenizer rotated at 5,000 to 10,000 rpm. After the addition of the coating agent, the mixture was stirred at the same speed for 2 minutes. After all the treatments were completed, finally put in a vacuum dryer (Kim Tech., South Korea), dried at 90 ℃ for 3 hours to evaporate the hexane used as a solvent containing the omega oil and honey bee extract according to the present invention A composite powder for color cosmetics was obtained.

Example  1 and 2

As a compact cosmetic composition containing a composite powder for color cosmetics, including the omega oil and the beech extract prepared in Preparation Example 1, a compact cosmetic composition according to a known method using a weight fraction as shown in Table 2 below Was prepared.

Ingredient Name Example 1 Example 2 Content (% by weight) Content (% by weight) Talc 28.7 38.7 Composite powder of Preparation Example 1 15 5 Boron nitride 5 5 Nylon 12 7 7 Titanium dioxide 10 10 Mica 25 25 Pigment (iron oxide) 2 2 Dimethicone 7 7 antiseptic 0.2 0.2 Spices 0.1 0.1

Comparative example  1 and 2

To prepare a conventional compact cosmetic composition (control not comprising a composite powder for color cosmetics comprising omega oil and beech extract according to the present invention) using the weight fraction in Table 3 by a conventional manufacturing method 1 And Comparative Example 2.

Ingredient Name Comparative Example 1 Comparative Example 2 Content (% by weight) Content (% by weight) Talc 33.7 38.7 Boron nitride 5 5 Silica 10 5 Nylon 12 7 7 Titanium dioxide 10 10 Mica 25 25 Pigment (iron oxide) 2 2 Dimethicone 7 7 antiseptic 0.2 0.2 Spices 0.1 0.1

Experimental Example  One

Moisturizing effect was confirmed using the compact cosmetic composition prepared in Example 1, Example 2, Comparative Example 1 and Comparative Example 2. The cosmetic composition was applied to the face twice a day for 20 healthy women (average age 31 years) in a room with a temperature of 22 to 24 ℃, relative humidity 55%, no air flow twice a day and then SKICON-200 ( Skincon 200, manufactured by IBS CO LTD. Of Japan, was used to measure the moisture content of the skin before and after application, and then measured the degree of moisturizing effect. The result (skin moisture content) is shown in Table 4 (unit: electric conductivity μΩ). Indicated.

Ingredient Name Before application 1 week after application Example 1 65 ± 10 80 ± 10 Example 2 62 ± 10 75 ± 10 Comparative Example 1 68 ± 10 66 ± 10 Comparative Example 2 60 ± 10 58 ± 10

As shown in Table 4, in the case of Example 1, the skin moisture content was most improved, and Example 2 also showed a clear improvement effect, but in the case of Comparative Example 1 and Comparative Example 2, the skin moisture content was It can be seen that it is not improved. This may be because dry feeling is caused by the sebum absorption ability peculiar to silica.

Experimental Example  2

Usability sensory evaluation

Using the compact cosmetic composition prepared in Example 1, Example 2, Comparative Example 1 and Comparative Example 2 was measured for adhesion, water resistance, sustainability, spreadability, moist. The measurement method was to use 20 healthy women in their mid 20's and mid 30's for a month, and then evaluated (the evaluation criteria were “5 points: very good, 4 points: good, 3 points: normal, 2 points: Poor, 1 point: very bad ”) and the average of the results are shown in Table 5 (Sensory evaluation results).

Tightness Water resistance Persistence Spreadability Moist Average Example 1 4.2 4.0 4.3 4.4 4.6 4.3 Example 2 4.0 3.8 4.0 4.2 4.1 4.0 Comparative Example 1 3.3 3.6 3.6 4.0 3.1 3.5 Comparative Example 2 3.7 3.8 3.7 3.9 3.2 3.7

As can be seen from the above results, the compact cosmetics of Examples 1 and 2 comprising the composite powder for color cosmetics comprising omega oil and the extract of the beech tree according to the present invention showed the best sensory results. And it was confirmed that Example 1 and Example 2 showed very excellent results in the moisturizing item indicating the degree of moisturizing.

Experimental Example  3

Measurement of skin color brightness and brightness

Color difference meter (CR-30) (manufactured by Japan) Minolta) was measured five times and the average value is shown in Table 6 (measurement results of brightness and brightness of skin color). The measurement method evaluated the result value before and after makeup on the panel of Experimental example 2. L represents the degree of lightness, a represents the degree of redness, b represents the degree of yellowness, and the higher the value of L, the brighter the skin color.

Item Brightness (saturation) L * a * b * Bare skin 72.54 (L ₁ ) 12.10 (a ₁ ) 16.25 (b ₁ ) - Example 1 75.62 (L ₂₎ 12.12 (a ₂ ) 18.98 (b ₂ ) 4.12 (C ₂ ) Comparative Example 2 72.87 (L ₃ ) 11.88 (a ₃ ) 18.02 (b ₃ ) 1.81 (C3)

As can be seen from the results of Table 6, it could be confirmed that Example 1 containing the composite powder for color cosmetics containing the omega oil and the beech extract according to the present invention is expressed brighter and brighter. Chroma is calculated by the following formula. A large C value means higher saturation.

Cn = √ [(L _n -L ₁ ) ² + (a _n -a ₁ ) ² + (b _n -b ₁ ) ² ]

Formulation example

On the basis of the results of the above experimental examples, a powder type cosmetic comprising a composite powder for color cosmetics comprising an omega oil and a beech extract according to the present invention is presented. However, the composition of the present invention is not intended to be limited to the following formulations (Table 7; Base Powder, Table 8; Two-Way Cake, Table 9; Eye Shadow) and is for illustration only.

Ingredient Name weight% Talc 80.3 kaoline 3 Composite powder of Preparation Example 1 12 Pigment (iron oxide) 2 antiseptic 0.2 Squalane One Hexyllaurate 0.5 Diisostearyl maleate One

Ingredient Name weight% Talc 47.7 Mica 20 Titanium dioxide 15 Pigment (iron oxide) 2 antiseptic 0.2 Composite powder of Preparation Example 1 10.0 Squalane 2.0 Hexyllaurate 1.5 Diisostearyl maleate 0.5 Phenyltrimethicone 1.0 incense 0.1

Ingredient Name weight% Talc 51 Zinc stearate 3 Boron nitride 3 Composite powder of Preparation Example 1 8 Mica 25 Pigment (iron oxide) 3 Mineral oil 5 Dimethicone 2

In the present specification, only a few examples of various preparations and assays performed by the present inventors are described, but the technical idea of the present invention is not limited thereto and may be variously modified and implemented by those skilled in the art. to be.

The present invention relates to a composite powder for color cosmetics comprising omega oil and beech extract, and to a powder type color cosmetic composition comprising the same, and may be used in a cosmetic manufacturing industry.

Claims (5)

2 to 10% by weight of omega oil, 10 to 20% by weight of dipropylene glycol, 8 to 15% by weight of beech extract, 1 to 10% by weight of silicone oil and remaining amount of omega oil and honey, characterized in that it comprises porous silica Complex powder for color cosmetics containing tree extract. The method of claim 1, The composite powder includes an omega oil and a beech extract, characterized in that the omega oil and dipropylene glycol are supported on the porous silica and the omega oil and the dipropylene glycol-supported porous silica are coated with silicone oil. Composite powder for color cosmetics to say. The method of claim 1, The composite powder for color cosmetics comprising omega oil and beech extract, characterized in that the composite powder is carried on the porous silica in a solution state in which the omega oil is dissolved in the dipropylene glycol. The method of claim 1, The composite powder for color cosmetics comprising omega oil and beech extract, characterized in that the porous silica constituting the composite powder has an average particle diameter of 6 to 9 μm. As a color type cosmetic composition of the powder type, 2 to 10% by weight of omega oils, 10 to 20% by weight of dipropylene glycol, 8 to 15% by weight of beech extract, 1 to 10% by weight of silicone oil and the remaining amount of composite powder for color cosmetics comprising porous silica as a balance 5 to 15 A powder type color cosmetic composition comprising a composite powder for color cosmetics comprising an omega oil and an extract of a beech tree, characterized by comprising a conventional color cosmetic composition as a weight% and the remaining amount.