KR20080072601A - Artificial fingernail having a multi layer - Google Patents

Artificial fingernail having a multi layer Download PDF

Info

Publication number
KR20080072601A
KR20080072601A KR1020080031143A KR20080031143A KR20080072601A KR 20080072601 A KR20080072601 A KR 20080072601A KR 1020080031143 A KR1020080031143 A KR 1020080031143A KR 20080031143 A KR20080031143 A KR 20080031143A KR 20080072601 A KR20080072601 A KR 20080072601A
Authority
KR
South Korea
Prior art keywords
nail
artificial nail
artificial
abs
eva
Prior art date
Application number
KR1020080031143A
Other languages
Korean (ko)
Inventor
김효선
Original Assignee
김효선
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김효선 filed Critical 김효선
Priority to KR1020080031143A priority Critical patent/KR20080072601A/en
Publication of KR20080072601A publication Critical patent/KR20080072601A/en

Abstract

An artificial nail of a multi-layer structure is provided to maintain the adhesion capacity effectively by forming an artificial nail with EVA and ABS or EVA to conform to the curvature of a natural nail. A placement recess is formed on the front side of an artificial nail(110) of a multi-layer structure, and a solidity reinforcing portion(120) is attached to the placement recess to improve the solidity. The artificial nail is made of EVA and acrylonitrile-butadiene-styrene copolymer(ABS) or styrene-butadiene-styrene block copolymer. The added amount of the EVA is 5 to 85 wt% and the added amount of acrylonitrile-butadiene-styrene copolymer(ABS) is 15 to 95 wt%. The artificial nail has the shape of a thin plate that corresponds to the shape of a natural nail.

Description

다층구조 인조손톱{Artificial fingernail having a multi layer}Artificial fingernail having a multi layer

도 1 은 본 발명의 일 실시예에 따른 다층구조 인조손톱을 도시한 사시도,1 is a perspective view showing a multi-layer artificial nail according to an embodiment of the present invention,

도 2 는 도 1의 A-A'선에 따른 단면도,2 is a cross-sectional view taken along line AA ′ of FIG. 1;

도 3 은 본 발명의 다른 실시예에 따른 다층구조 인조손톱을 도시한 사시도,3 is a perspective view showing a multi-layer artificial nail according to another embodiment of the present invention,

도 4 는 도 3의 B-B'선에 따른 단면도,4 is a cross-sectional view taken along line BB ′ of FIG. 3;

도 5 는 본 발명의 또 다른 실시예에 따른 다층구조 인조손톱을 도시한 사시도,5 is a perspective view showing a multi-layer artificial nail according to another embodiment of the present invention,

도 6 은 본 발명의 바람직한 실시예에 따른 다층구조 인조손톱의 사용 상태를 나타낸 사시도이다.6 is a perspective view showing a state of use of the multi-layer artificial nail according to a preferred embodiment of the present invention.

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

1,100,200 : 다층구조 인조손톱 10,110 : 인조손톱1,100,200: Multi-layered artificial nail 10,110: Artificial nail

20 : 액상물질 110a : 안착홈20: liquid material 110a: seating groove

120 : 경도 보강부 210 : 손톱 부착부120: hardness reinforcement portion 210: nail attachment portion

220 : 수용홈 안착부 300 : 사출 금형220: receiving groove seating portion 300: injection mold

본 발명은 다층구조 인조손톱에 관한 것으로, 보다 상세하게는 인조손톱을 형성한 후 여기에 액상의 경도 보강재를 부분적으로 도포 또는 코팅하거나, 인조손톱을 윗면과 아랫면으로 이중 사출하여 형성하거나, 경도가 보강된 기 사출된 조각을 손톱의 앞측에 부착하여 형성된 다층구조 인조손톱에 관한 것이다.The present invention relates to a multi-layered artificial nail, and more particularly, after forming artificial nail, the liquid hardness reinforcing material is partially applied or coated thereon, or artificial nail is formed by double injection into the upper and lower surfaces, or the hardness is It relates to a multi-layer artificial nail formed by attaching a reinforced extruded piece to the front side of the nail.

종래기술로서 한국특허공개 제10-2004-0026282호(2004.03.31) "인조 손톱 및 그 제조방법"이 개시되어 있다. 상기 종래기술은 ABS 합성수지로 형성된 네일 아트용 인조 손톱으로서, 천연 손톱과 동일 형상으로 형성되고 그 위에 글리터층, 데칼층 또는 원하는 문형이 묘화되는 상면부 및 상기 상면부와 일체로 이루어진 하면부로 이루어지고, 천연 손톱 상에 상기 인조 손톱을 부착할 때, 상기 천연 손톱과 상기 인조 손톱과의 단차가 형성되지 않도록 상기 하면부에는 천연 손톱과의 결합부분에 단차부가 형성되어 있는 것을 특징으로 하는 인조 손톱에 관한 것이다.Korean Patent Laid-Open No. 10-2004-0026282 (2004.03.31) discloses an artificial nail and a method of manufacturing the same. The prior art is an artificial nail for nail art formed of ABS synthetic resin, formed of the same shape as the natural nail and consists of a top surface portion and a lower surface portion integrally formed with the upper surface portion and the glitter layer, decal layer or the desired sentence pattern is drawn thereon When the artificial nail is attached on the natural nail, the artificial nail, characterized in that the step portion is formed in the coupling portion with the natural nail on the lower surface portion so that the step between the natural nail and the artificial nail is not formed. It is about.

상기 종래기술과 기타 선행기술의 인조손톱은 1가지 물질을 사용하여 사출 성형한다. 이 경우 사출된 인조손톱은 대부분 경도가 높은 재질을 사용하고, 모든 소비자의 손톱 곡률과 일치하지 않는 경우가 많다.The prior art and other prior art artificial nails are injection molded using one material. In this case, the injected artificial nails are mostly made of a hard material, and often do not match the curvature of nails of all consumers.

경도가 높은 재질의 인조손톱은 접착제를 사용하여 부칠 때 손톱의 곡률과 일치하지 않아 사용시 인조손톱이 떨어져 나갈 가능성이 크고, 소비자의 손톱에 붙어 있는 상태에서 계속 원래의 상태를 복원하려는 힘 때문에 불편한 점이 있었다.Artificial nails made of hard materials do not match the curvature of the nails when they are glued, and the nails are likely to fall off when they are used. there was.

이 문제를 해결하기 위해 연질의 물질을 사용하여 사출할 경우 전술할 문제는 감소 된다고 볼 수 있지만, 손톱의 앞면이 물렁물렁하게 되어 착용시 지속적으로 가해지는 외부의 충격 등으로 인하여 앞쪽이 쉽게 구부려지는 현상이 발생한다.In order to solve this problem, the above-mentioned problem is reduced when the injection is made using a soft material, but the front of the nail is soft and the front is easily bent due to the external impact continuously applied when worn. Phenomenon occurs.

따라서, 외부로부터의 충격이 많은 앞쪽은 강하게 그리고 사용자의 손에 가장 많이 접하는 뒤쪽은 연질의 물질로 되어 있는 것이 가장 이상적이라 할 수 있다.Therefore, it is most ideal that the front of the impact that is high from the outside is strong and the rear of the back most touching the user's hand is made of a soft material.

또한, 선행기술을 살펴보면 인조손톱의 윗면을 코팅 처리하는 기술이 개시되어 있는데 이는 인조손톱 표면의 보호 및 광택을 목적으로 하고 있다.In addition, looking at the prior art discloses a technique for coating the top surface of the artificial nail for the purpose of protecting and gloss of the artificial nail surface.

나아가, 종래의 선행기술은 인조손톱을 제거할 때 인조손톱이 부착된 자연 손톱을 아세톤 등의 약제에 상당시간 담근 후 인조손톱을 제거한다. 종래의 ABS수지의 인조손톱은 손톱의 전체 면과 견고하게 부착되어 있기 때문에, ABS수지로 제조된 인조손톱을 제거하기 위하여는 통상 10분 이상 소요된다.Furthermore, the prior art is to remove artificial nails after immersing natural nails with artificial nails in acetone or the like for a long time when removing artificial nails. Since the conventional nail of the ABS resin is firmly attached to the entire surface of the nail, it usually takes 10 minutes or more to remove the artificial nail made of ABS resin.

한편, ABS수지의 인조손톱은 순간접착제에 의하여 부착면이 완전히 녹아 손톱의 전체면에 접착되기 때문에, 인조손톱을 제거할 때 아세톤 등의 약제에 인조손톱이 부착된 자연 손톱을 장시간 담가야 하고, 매니큐어 스틱을 이용하여 손톱표면 을 긁어 이물질을 완전히 제거해야 하므로 인조손톱의 제거에 많은 시간이 소요되는 단점이 있다. On the other hand, since the artificial nail of ABS resin is completely melted by the instant adhesive and adheres to the entire surface of the nail, when removing the artificial nail, it is necessary to immerse the natural nail with artificial nail attached to acetone or the like for a long time. Using a stick to scratch the surface of the nail to remove the foreign matter completely takes a disadvantage that takes a long time to remove the artificial nail.

더욱이 아세톤에 손가락을 오랜 시간 동안 담가야 하므로 피부가 손상되는 문제점이 있었다.Moreover, there is a problem in that the skin is damaged because the finger must be immersed in acetone for a long time.

본 발명은 상술한 바와 같은 문제점을 해결하기 위해 안출 된 것으로, 본 발명의 일 실시예는 사용자의 천연 손톱 곡률과 일치되도록 하여 효과적인 부착성을 갖는 다층구조 인조손톱과 관련된다.The present invention has been made to solve the problems described above, an embodiment of the present invention relates to a multi-layer artificial nail having an effective adhesion to match the user's natural nail curvature.

또한, 인조손톱의 뒤쪽 부분의 경도를 낮게 하고 앞쪽은 경도를 높여서, 사용자가 착용시 인조손톱의 앞쪽에 가해지는 강한 충격에 대비함과 더불어 뒤쪽 부분에서 부드럽게 착용할 수 있는 다층구조 인조손톱과 관련된다.In addition, the hardness of the rear part of the artificial nail is lowered and the hardness of the front part is increased, so as to prepare for the strong impact applied to the front of the artificial nail when the user wears it, and related to the multilayered artificial nail that can be worn softly at the rear part. do.

나아가, 짧은 시간 안에 인조손톱을 제거할 수 있는 다층구조 인조손톱과 관련된다.Furthermore, it relates to a multi-layered artificial nail which can remove artificial nails in a short time.

상기의 목적을 달성하기 위하여 본 발명의 일 실시예는 천연 손톱에 부착되어 심미감을 더하기 위해 사용되는 인조손톱에 있어서, 인조손톱의 앞측에는 안착홈이 형성되며, 이 안착홈에 경도를 향상시키기 위해 경도 보강부가 부착되며, 인조손톱은 이브이에이(EVA)와 아크릴로니트릴-부타디엔-스티렌 공중합체(ABS) 또는 스티렌-부타디엔-스티렌 블록 공중합체(SBS block copolymer) 재질로 형성된 것을 특징으로 하는 다층구조 인조손톱을 제공한다.One embodiment of the present invention in order to achieve the above object in the artificial nail used to add aesthetics to the natural nails, the front of the artificial nail is formed with a seating groove, to improve the hardness in the seating groove The hardness reinforcement is attached, the artificial fingernail is a multilayer structure characterized in that it is formed of EVA and acrylonitrile-butadiene-styrene copolymer (ABS) or styrene-butadiene-styrene block copolymer (SBS block copolymer) material Provide artificial nails.

본 발명의 바람직한 실시예에 따른 인조손톱(10,110)은 전체적으로 손톱에 대응하는 형상 즉 얇은 판 형상으로 길이 방향으로 완만하게 굴곡져 있고, 좌우 폭은 완만한 반 타원 형상이다.Artificial nails (10,110) according to a preferred embodiment of the present invention is gently curved in the longitudinal direction in the shape corresponding to the nail, that is, a thin plate as a whole, the left and right width is a semi-elliptic shape gentle.

상기 인조손톱(10,110)은 바람직하게는 EAV(Ethylene Vinyl Acetate)와 ABS(Acrylonitrile Butadien Styrene)재질 또는 TPE(Thermoplastic Elastomer)와 ABS로 이루어지는데 EVA는 에틸렌과 비닐아세테이트를 공중합체(Copolymer)시킨 소재이다. 그 특징은 탄성과 투명성과 신장률, 인장 강도 등이 일반 호모폴리머(Homopolymer)인 LDPE에 비하여 우수하며 환경적 특징은 인체 무해하며 무공해 소재이다.The artificial nail (10,110) is preferably made of EAV (Ethylene Vinyl Acetate) and ABS (Acrylonitrile Butadien Styrene) or TPE (Thermoplastic Elastomer) and ABS. EVA is a material obtained by copolymerizing ethylene and vinyl acetate. . Its characteristics are excellent in elasticity, transparency, elongation rate and tensile strength compared to LDPE which is a general homopolymer, and its environmental features are harmless to humans and are pollution-free materials.

상기 ABS는 이를 구성하는 3 성분의 특성 즉, Styrene이 갖는 광택과 성형성, Acrylonitrile이 갖는 강성, 내약품성 및 뛰어난 기계적 성질, Butadiene이 갖는 내충격성 등의 장점만을 부여시킨 종합 Engineering Plastics이라 말할 수 있으며, ABS수지의 성형가공법은 그 주성분인 styrene의 영향을 받으므로 대단히 우수하다. 그러나 폴리스티렌에 비하면 유동성이 약간 떨어지고 또한 약간의 흡수성이 있다.The ABS can be said to be a comprehensive engineering plastics that gives only three characteristics, ie, gloss and moldability of styrene, stiffness of acrylonitrile, chemical resistance and excellent mechanical properties, and impact resistance of butadiene. The molding process of ABS resin is very good because it is influenced by its main component, styrene. However, compared to polystyrene, the fluidity is slightly inferior and slightly absorbent.

상기 TPE는 바람직하게는 SBS block copolymer(Styrene-Butadien-Styrene block copolymer)를 사용한다.The TPE is preferably a SBS block copolymer (Styrene-Butadien-Styrene block copolymer).

상기 EVA와 ABS를 혼합할 경우 바람직하게는 상기 EVA의 첨가량은 5 내지 85 wt%, ABS의 첨가량은 15 내지 95 wt% 이내에서 배합된다. 이 EVA는 인조손톱(10,110)을 물렁물렁하게 하는 성질이 있는 반면 ABS는 인조손톱(10,110)을 단단하게 하는 성질이 있다. 그 결과 자연 손톱과 접하는 부분은 물렁하게 하여 자연 손톱의 곡률에 따라 잘 부착될 수 있도록 하고, 자연 손톱으로부터 돌출되는 부분은 단단하게 하여 대상 물체에 닿았을 때 쉽게 구부러지지 않게 하는 이점이 있다.When the EVA and ABS are mixed, preferably, the amount of EVA added is 5 to 85 wt%, and the amount of ABS added is within 15 to 95 wt%. The EVA has a property of softening the artificial nails 10,110, while the ABS has a property of hardening the artificial nails 10,110. As a result, the part contacting with the natural nail is softened so that it can be attached well according to the curvature of the natural nail, and the part protruding from the natural nail is hardened so that it is not easily bent when touching the target object.

구체적으로 EVA의 첨가량은 40 wt%, ABS의 첨가량은 60 wt%인 것이 바람직하다. 이렇게 하면 손톱의 형상이 자연스럽게 형성됨과 더불어 적정한 유동성을 확보할 수 있어 인조손톱(10,110)의 끝 부분에서 자연 손톱의 곡률과 쉽게 일치시킬 수 있고, 이로 인해 사용자의 천연 손톱에 붙어 있는 상태에서 복원력이 발생 되지 않으므로 종래의 불편한 점을 해결할 수 있는 이점이 있다.Specifically, the amount of EVA added is 40 wt%, the amount of ABS is preferably 60 wt%. In this way, the shape of the nail is naturally formed and the proper fluidity can be secured so that the curvature of the natural nail can be easily matched with the curvature of the natural nail at the end of the artificial nail (10,110). Since it does not occur there is an advantage that can solve the conventional inconvenience.

상기 SBS block copolymer와 ABS의 혼합비율은 전술한 EVA와 ABS의 혼합 비율과 동일하다.The mixing ratio of the SBS block copolymer and ABS is the same as the mixing ratio of the above-described EVA and ABS.

상기 인조손톱(10,110)은 전술한 EVA, ABS 또는 SBS block copolymer 자체만 의 재질로 성형 될 수 있다.The artificial nails 10 and 110 may be molded of only the above-described EVA, ABS or SBS block copolymer itself.

도 1 은 본 발명의 바람직한 실시예에 따른 다층구조 인조손톱을 도시한 사시도이고, 도 2 는 도 1의 A-A'선에 따른 단면도이다.1 is a perspective view showing a multi-layer artificial nail according to a preferred embodiment of the present invention, Figure 2 is a cross-sectional view taken along the line AA 'of FIG.

본 발명의 바람직한 실시예에 따른 다층구조 인조손톱(1)은 전술한 인조손톱(10)에 액상물질(20)을 도포 또는 다층으로 도포하여 형성된다.Multi-layer artificial nail 1 according to a preferred embodiment of the present invention is formed by applying the liquid material 20 to the above-described artificial nail 10 or in a multi-layer.

상기 액상물질(20)은 우레탄(urethane)이나 아크릴릭 본드(acrylic bond)나 젤(gel)을 사용하는 것이 바람직하다. 이 액상물질(20)은 상기 인조손톱(10)의 앞측 밑면에 패드프린팅(Pad printing) 방법에 의해서 여러 번 도포 또는 코팅되어 인조손톱(10)의 앞측이 다층 구조, 상세하게는 도 2에 도시된 바와 같이 2 내지 3층의 구조를 갖도록 함이 바람직하다. The liquid material 20 is preferably urethane (urethane), acrylic bond (acrylic bond) or gel (gel). The liquid material 20 is applied or coated several times by a pad printing method on the front bottom surface of the artificial nail 10 so that the front side of the artificial nail 10 has a multi-layered structure, more specifically, shown in FIG. It is preferable to have a structure of 2-3 layers as described.

또한, 도 2에서는 인조손톱(10)의 하부에 다층구조를 형성하였으나 여기에 한정되지 않고 인조손톱(10)의 상부에도 다층구조를 형성할 수 있다.In addition, in FIG. 2, a multi-layer structure is formed on the lower portion of the artificial nail 10, but the present invention is not limited thereto.

상기 패드프린팅 방법은 실리콘 패드가 동판에서 인쇄내용을 묻혀오면 그것을 제품에 이동시키는 형태의 인쇄방식으로 평면 실크 인쇄를 닿을 수 없는 곳에 이 인쇄 방법을 사용하며 대량의 인쇄를 할 때 이 인쇄를 한다. 패드인쇄는 인쇄품 질이 실크인쇄(일반적으로 대부분의 선물용품에 쓰이는 인쇄방법)보다 좋고 요철이 있는 곳에도 인쇄에 큰 문제가 되지 않는 장점이 있다.The pad printing method is a printing method in which a silicon pad is buried in a copper plate and moves it to a product. The pad printing method uses this printing method where a flat silk print cannot be reached and performs this printing when a large amount of printing is performed. Pad printing has the advantage that printing quality is better than silk printing (typically the printing method used in most gifts) and does not have a big problem in printing even where there is irregularities.

도 3 은 본 발명의 다른 실시예에 따른 다층구조 인조손톱을 도시한 사시도이고, 도 4 는 도 3의 B-B'선에 따른 단면도이다.3 is a perspective view showing a multi-layer artificial nail according to another embodiment of the present invention, Figure 4 is a cross-sectional view taken along the line BB 'of FIG.

본 발명의 바람직한 다른 실시예에 따른 다층구조 인조손톱(100)은 전술한 방법에 의해 성형된 인조손톱(110)의 앞측 하부 밑면에 안착홈(110a)을 형성하고, 상기 안착홈(110a)에 경도 보강부(120)를 부착하여서 형성된다.Multi-layered artificial nail 100 according to another preferred embodiment of the present invention forms a seating groove (110a) in the front bottom lower surface of the artificial nail 110 formed by the above-described method, in the seating groove (110a) It is formed by attaching the hardness reinforcement portion 120.

상기 인조손톱(110) 성형시 사용되는 EVA, ABS 또는 SBS block copolymer의 성분 비율은 전술한 바와 동일하므로 여기에서는 설명을 생략한다.Since the component ratio of the EVA, ABS or SBS block copolymer used when forming the artificial nail 110 is the same as described above, description thereof will be omitted.

상기 안착홈(110a)은 바람직하게는 초승달 형상으로 도 4에 도시된 바와 같이 인조손톱(110)의 선단에서 후방으로 소정 길이 연장 형성되되, 자연 손톱의 선단과 만나는 지점까지 형성된다.The seating groove (110a) is preferably formed in a crescent shape extending to a predetermined length from the front end of the artificial nail 110, as shown in Figure 4, to a point that meets the front end of the natural nail.

상기 경도 보강부(120)는 바람직하게는 ABS 재질로 형성되며, 상기 안착홈(110a)과 대응하는 형상으로 형성되어 접착제 등으로 상기 안착홈(110a)에 부착된다.The hardness reinforcing portion 120 is preferably formed of an ABS material, is formed in a shape corresponding to the mounting groove (110a) is attached to the mounting groove (110a) with an adhesive or the like.

또한, 이 경도 보강부(120)가 안착홈(110a)에 부착되었을 경우 인조손톱(110)과 경도 보강부(120)가 맞닿는 부분에 틈이 생기거나 육안상 보기가 좋지 않기 때문에 그 부분에 아크릴이나 우레탄 등으로 도포하여 주는 것이 바람직하다.In addition, when the hardness reinforcement portion 120 is attached to the seating groove (110a), there is a gap in the portion where the artificial nail 110 and the hardness reinforcement portion (120) abut or acne on the part because the visual appearance is not good It is preferable to apply with urethane or the like.

도 5 는 본 발명의 또 다른 실시예에 따른 다층구조 인조손톱을 도시한 사시도이다.5 is a perspective view showing a multi-layered artificial nail according to another embodiment of the present invention.

본 발명의 또 다른 바람직한 실시예에 따른 다층구조 인조손톱(200)은 손톱 부착부(210)와 수용홈 안착부(220)로 구성된다.Multi-layer artificial nail 200 according to another preferred embodiment of the present invention is composed of a nail attachment portion 210 and the receiving groove seating portion 220.

손톱 부착부(210)는 EVA, ABS 또는 SBS block copolymer와로 사출 성형되며, EVA, ABS 또는 SBS block copolymer의 성분 비율은 전술한 바와 같다. 상기 손톱 부착부(210)는 자연 손톱과 유사한 형상과 크기를 갖고, 이 앞측에는 초승달 형상의 수용홈(210a)이 상면 또는 하면에 형성된다.Nail attachment portion 210 is injection molded with EVA, ABS or SBS block copolymer, the component ratio of EVA, ABS or SBS block copolymer is as described above. The nail attachment portion 210 has a shape and size similar to that of natural nail, and the crescent-shaped receiving groove 210a is formed on the upper or lower surface at the front side thereof.

수용홈 안착부(220)는 상기 손톱 부착부(210)에 일체화하기 위해 상기 수용홈(210a)과 동일한 형상을 갖고 동일한 위치에 위치하도록 2차 사출된다. 이 수용홈 안착부(220)는 경도를 향상시키기 위해 ABS 재질로 성형되는 것이 바람직하다.Receiving groove seating portion 220 is secondary injection to have the same shape and the same position as the receiving groove (210a) in order to integrate the nail attachment portion (210). The receiving groove seating portion 220 is preferably molded of an ABS material to improve the hardness.

상기 수용홈 안착부는 손톱 부착부의 수용홈에 안착 된 후 도 5a 내지 5b에 도시된 바와 같이 사출 금형(300)에 의해 이중 사출되어 결합 된다.The accommodating groove seating portion is seated in the accommodating groove of the nail attachment portion and then double injection is coupled by the injection mold 300 as shown in Figure 5a to 5b.

도 6 은 본 발명의 바람직한 실시예에 따른 다층구조 인조손톱의 사용 상태를 나타낸 사시도이다.6 is a perspective view showing a state of use of the multi-layer artificial nail according to a preferred embodiment of the present invention.

본 발명의 바람직한 실시예에 따른 다층구조 인조손톱(1)은 EVA, ABS 또는 SBS block copolymer로 형성되어 있어 사용자의 천연 손톱의 곡률과 쉽게 일치시킬 수 있고, 이에 의해서 천연 손톱에 부착된 후에도 종래와 달리 떨어져 나갈 가능성이 현저히 줄어드는 이점이 있다.Multi-layered artificial nail 1 according to a preferred embodiment of the present invention is formed of EVA, ABS or SBS block copolymer can be easily matched to the curvature of the user's natural nail, whereby even after attached to the natural nail There is an advantage that the possibility of falling off otherwise is significantly reduced.

또한, 사용자의 천연손톱에 붙어 있는 상태에서 원 상태로 복원되려는 힘이 제거되므로 종전의 불편함을 해결할 수 있다. 나아가, 경도 보강부(120)로 인조손톱(10)의 앞 부분을 다층 구조를 형성하여 외부의 충격으로 인하여 인조손톱(10)의 앞 부분이 쉽게 구부러지는 현상을 해결할 수 있는 이점이 있다.In addition, since the force to be restored to the original state is removed from the state attached to the natural nail of the user can solve the conventional inconvenience. Furthermore, there is an advantage that the front portion of the artificial nail 10 can be easily bent due to an external impact by forming a multilayer structure of the front portion of the artificial nail 10 with the hardness reinforcement 120.

특히, 사용 후 다층구조 인조손톱(1)을 제거하고자 할 때는 아세톤이나 그 밖의 간단한 휘발성 물질로도 접착제의 접찹력을 제거할 수 있어 제거 또한 간편하며, 부착된 다층구조 인조손톱(1) 상부에 도 6에 도시된 바와 같이 다양한 무늬와 모양을 디자인할 수 있는 이점이 있다.In particular, when removing the multi-layered artificial nail (1) after use, it is possible to remove the adhesive force of the adhesive even with acetone or other simple volatile materials, and also easy to remove, the upper part of the attached multi-layer artificial nail (1) As shown in Figure 6 there is an advantage that can design a variety of patterns and shapes.

본 발명은 특허청구범위에서 청구하는 청구의 요지를 벗어나지 않고도 당해의 기술분야에서 통상의 지식을 가진 자에 의하여 다양하게 변경 실시될 수 있으므로, 본 발명의 기술보호범위는 상술한 특정의 바람직한 실시예에 한정되지 않는다.As the present invention can be variously modified by those skilled in the art without departing from the scope of the claims claimed in the claims, the technical protection scope of the present invention is a specific preferred embodiment described above It is not limited to.

상술한 바와 같은 본 발명인 다층구조 인조손톱에 따르면, EVA 및 ABS 또는 EVA 만으로 인조손톱을 형성하여 사용자의 천연 손톱 곡률과 일치하도록 하여 효과적인 부착성을 유지할 수 있는 다층구조 인조손톱을 제공할 수 있는 효과가 있다.According to the multi-layered artificial nail of the present invention as described above, by forming an artificial nail with only EVA and ABS or EVA to match the curvature of the natural nail of the user, it is possible to provide a multi-layered artificial nail that can maintain effective adhesion There is.

또한, 인조손톱의 뒤쪽 부분의 경도를 낮게 하고 앞쪽은 경도를 높여서 사용자가 착용시 인조손톱의 앞쪽에 가해지는 강한 충격에 대비함과 더불어 뒤쪽 부분에서 부드럽게 착용할 수 있는 다층구조 인조손톱을 제공할 수 있는 효과가 있다.In addition, by lowering the hardness of the back portion of the artificial nails and the hardness of the front side to provide a multi-layered artificial nail that can be worn in the back portion in addition to the strong impact applied to the front of the artificial nail when worn. It can be effective.

나아가, 짧은 시간 안에 인조손톱을 제거할 수 있는 다층구조 인조손톱을 제공할 수 있는 효과가 있다.Furthermore, there is an effect of providing a multi-layered artificial nail that can remove the artificial nail in a short time.

Claims (3)

천연 손톱에 부착되어 심미감을 더하기 위해 사용되는 인조손톱에 있어서,In artificial nails attached to natural nails and used to add aesthetics, 상기 인조손톱의 앞측에는 안착홈이 형성되며, 상기 안착홈에 경도를 향상시키기 위해 경도 보강부가 부착되며, 상기 인조손톱은 이브이에이(EVA)와 아크릴로니트릴-부타디엔-스티렌 공중합체(ABS) 또는 스티렌-부타디엔-스티렌 블록 공중합체(SBS block copolymer) 재질로 형성된 것을 특징으로 하는 다층구조 인조손톱.A seating groove is formed at the front side of the artificial nail, and a hardness reinforcing part is attached to the seating groove to improve hardness, and the artificial nail is YB (EVA) and acrylonitrile-butadiene-styrene copolymer (ABS) or Multi-layered artificial nail, characterized in that formed of styrene-butadiene-styrene block copolymer (SBS block copolymer) material. 제 1 항에 있어서,The method of claim 1, 상기 이브이에이(EVA)의 첨가량은 5 내지 85 wt%, 아크릴로니트릴-부타디엔-스티렌 공중합체(ABS)의 첨가량은 15 내지 95 wt%인 것을 특징으로 하는 다층구조 인조손톱.The amount of the EVA (EVA) is 5 to 85 wt%, the amount of the acrylonitrile-butadiene-styrene copolymer (ABS) is 15 to 95 wt%, characterized in that the multi-layer artificial nail. 제 1 항에 있어서,The method of claim 1, 상기 스티렌-부타디엔-스티렌 블록 공중합체(SBS block copolymer)의 첨가량은 5 내지 85 wt%, 아크릴로니트릴-부타디엔-스티렌 공중합체(ABS)의 첨가량은 15 내지 95 wt% 이내인 것을 특징으로 하는 다층구조 인조손톱.The amount of the styrene-butadiene-styrene block copolymer added is 5 to 85 wt%, the amount of the acrylonitrile-butadiene-styrene copolymer (ABS) added is within 15 to 95 wt% Frame artificial nail.
KR1020080031143A 2008-04-03 2008-04-03 Artificial fingernail having a multi layer KR20080072601A (en)