KR20080007291A - High plywood board - Google Patents

High plywood board Download PDF

Info

Publication number
KR20080007291A
KR20080007291A KR1020070050877A KR20070050877A KR20080007291A KR 20080007291 A KR20080007291 A KR 20080007291A KR 1020070050877 A KR1020070050877 A KR 1020070050877A KR 20070050877 A KR20070050877 A KR 20070050877A KR 20080007291 A KR20080007291 A KR 20080007291A
Authority
KR
South Korea
Prior art keywords
plywood
impregnated paper
board
hdf
hard fiber
Prior art date
Application number
KR1020070050877A
Other languages
Korean (ko)
Other versions
KR100843750B1 (en
Inventor
천억주
Original Assignee
주식회사 원진종합목재
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 원진종합목재 filed Critical 주식회사 원진종합목재
Priority to KR1020070050877A priority Critical patent/KR100843750B1/en
Publication of KR20080007291A publication Critical patent/KR20080007291A/en
Application granted granted Critical
Publication of KR100843750B1 publication Critical patent/KR100843750B1/en

Abstract

A high plywood board for ship furniture is provided to retain the merits of a low pressure melamine-impregnated paper as a surface material and to have sufficient strength against external shocks and strong moisture or water resistance. A high plywood board for ship furniture includes a plywood(10) used as a base layer, a hard fiber board(20) adhered to the upside of the plywood, and a low pressure melamine-impregnated paper(30) adhered to the upside of the hard fiber board. The hard fiber board is obtained by making small-diameter wood into wood fibers, putting the wood fibers together using an adhesive, pressurizing and heating the adhesive-containing wood fibers into a hard board having a specific gravity of 0.8-1.1 and a thickness of 3-6 mm.

Description

선박가구용 강화 마감재{HIGH PLYWOOD BOARD}High Strength Finishing Material for Ship Furniture {HIGH PLYWOOD BOARD}

도 1은 종래의 강화 마감재의 일 예를 도시한 단면 구성도.1 is a cross-sectional view showing an example of a conventional reinforcement finish.

도 2는 본 발명의 바람직한 일실시예에 따른 선박가구용 강화 마감재의 단면 구성도. Figure 2 is a cross-sectional configuration of the reinforcement finish for ship furniture according to an embodiment of the present invention.

*도면의 주요 부분에 관한 부호의 설명** Explanation of symbols on main parts of the drawings *

10. 합판 20. 경질섬유판(HDF)10. Plywood 20. Hard Fiberboard (HDF)

30. 저압 멜라민 함침지(LPM)30. Low pressure melamine impregnated paper (LPM)

본 발명은 선박가구용 강화 마감재에 관한 것으로, 보다 상세하게는 합판과 경질섬유판(HDF) 및 저압 멜라민 함침지(LPM)를 고온, 고압에서 접착에 의한 다층으로 구성한 선박가구용 강화 마감재에 관한 것이다.The present invention relates to a reinforcing finish for ship furniture, and more particularly to a reinforcing finish for ship furniture consisting of a multi-layer by bonding the plywood and hard fiber board (HDF) and low pressure melamine impregnated paper (LPM) at high temperature, high pressure.

현재 우리나라의 조선산업은 날로 발전하여 명실공히 세계 1위 자리를 굳건히 견지하고 있다. 보드류를 원자재로 하여 제작하는 가구는 크게 나누어 아파트를 비롯한 고정된 주거문화에 설치되는 목재 및 보드가구인 육상가구와 여객선 및 화물운반선을 비롯한 해상이동용 움직이는 주거문화에 설치되는 목재 및 보드가구인 선박가구로 구분되어 설계 제작되고 있다.At present, Korea's shipbuilding industry has developed day by day and is firmly maintaining the number one position in the world. Furniture made from boards is divided into land and wooden furniture, which are installed in a fixed residential culture including apartments, and ship furniture, which is installed in a moving residential culture for maritime movement, including passenger ships and cargo carriers. It is divided into design and manufacture.

그 중에 선박가구용으로 널리 쓰이는 보드류는 단연 합판이다. 일반적으로 합판(PLYWOOD)은 두께가 0.5 ~ 4mm의 얇은 단판을 7매 또는 9매를 적층하여 접착제로 맞붙여 한 장의 널판지로 제조하는 것으로서, 접착강도가 우수하고, 재질 수명이 길며, 가볍고 스크류(SCREW) 조립 유지력이 가장 우수하다. 그러나 가격이 비싸고 두께 편차가 많으며 합판의 휨 현상이 많다. Among them, boards widely used for ship furniture are by far plywood. In general, PLYWOOD is made of a single board by laminating 7 or 9 sheets of thin single plate with a thickness of 0.5 ~ 4mm and bonding them with an adhesive, and has excellent adhesive strength, long material life, and light and screw ( SCREW) The best assembly holding power. However, the price is expensive, the thickness variation is large, and the plywood warpage phenomenon is large.

또한, 저압 멜라민 함침지(low pressure mela-mine impregnated paper:LPM)는 고압 멜라민 함침지(high pressure mela-mine impregnated paper:HPM)의 성형과정에 비해 낮은 압력에서 (10∼20kgf/cm²) 접착성형되기 때문에 고압 멜라민 함침지(HPM)보다 가격이 저렴하여 주로 가구 표면재로 많이 사용하고 있다. In addition, low pressure mela-mine impregnated paper (LPM) is an adhesive molding at low pressure (10-20 kgf / cm²) compared to the process of forming high pressure mela-mine impregnated paper (HPM). Since it is cheaper than high pressure melamine impregnated paper (HPM), it is mainly used as furniture surface material.

그런데, 통상 기재층인 합판의 상면에는 표면재로서 상기 저압 멜라민 함침지(LPM)의 가공이 안 된다는 문제점이 있다. By the way, there exists a problem that the said low pressure melamine impregnated paper (LPM) cannot be processed as a surface material on the upper surface of the plywood which is a base material layer normally.

따라서, 표면재로 저압 멜라민 함침지(LPM)를 가공하는 보드류에서는 기재층으로 중밀도 섬유판(Medium Density FiberBoard:MDF), 파티클보드(Particle Board:PB)를 사용하여 제조하고 있다.Therefore, in the boards processing low pressure melamine impregnated paper (LPM) as a surface material, a medium density fiber board (MDF) and a particle board (Particle Board: PB) are manufactured as a base material layer.

여기서 중밀도 섬유판(MDF)은 두께 편차와 휨 현상이 없고 모든 마감재의 접착이 용이하여 작업성이 좋지만, 스크류의 조립 유지력이 약해 재조립을 할 수 없고, 습기에 약하며 단면에 조립시 크랙이 발생하고 절단 치구 손상이 많은 문제점이 있다.Here, MDF has good workability because there is no thickness variation and warping phenomenon, and it is easy to bond all the finishing materials, but it cannot be reassembled due to weak assembly holding power of the screw, weak to moisture, and cracks when assembling on the cross section. Cutting jig damage has many problems.

또한, 파티클보드(PB)는 가격이 저렴하고 두께 편차가 없으며 모든 마감재의 접착이 용이한 장점은 있으나 습기나 수분에 약하며 스크류의 조립 유지력이 약해 재조립을 할 수 없고, 절단 치구 손상이 많고 무거운 문제점이 있다.In addition, the particle board (PB) is inexpensive, there is no thickness variation, it is easy to adhere to all the finishing materials, but it is weak to moisture or moisture, and the assembly and maintenance of the screw is weak, so it cannot be reassembled, and there is a lot of cutting jig damage and heavy There is a problem.

따라서, 선박용 마감재에 있어서 꼭 합판으로 사용해야 되는 부분에는 도 1에 도시된 바와 같이, 합판(1)의 표면을 고압 멜라민 함침지(HPM)(2)로 접착가공하여 선박용 마감재를 제조하고 있다.Therefore, as shown in Figure 1, the portion of the ship finish must be used as a plywood, the surface of the plywood 1 is bonded by a high-pressure melamine impregnated paper (HPM) (2) to manufacture a ship finish.

그런데, 상기 고압 멜라민 함침지(HPM)(2)는 맨 위의 종이에 멜라민 코팅을 하고 여러 겹의 페놀종이와 멜라민 종이 등을 접착하여 0.5 ~ 1.0mm의 두께로 제조됨으로써 저압 멜라민 함침지(LPM)보다 가격이 무려 5배나 비싸기 때문에 제조원가상 불이익이 많았다.By the way, the high-pressure melamine impregnated paper (HPM) (2) is a melamine coating on the top paper and adhered to several layers of phenolic paper and melamine paper, etc. to be produced in a thickness of 0.5 ~ 1.0mm low pressure melamine impregnated paper (LPM Because the price is five times more expensive than), there were many disadvantages in manufacturing cost.

본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로, 본 발명의 목적은 표면재로서 저압 멜라민 함침지(LPM)의 장점을 살리면서 경질섬유판(HDF)에 의한 외부 충격에 대한 충분한 강도가 제공되어 습기나 수분에 강한 선박가구용 강화 마감재를 제공함에 있다.The present invention has been made to solve the above problems, the object of the present invention is to provide sufficient strength against external impact by hard fiber plate (HDF) while taking advantage of low-pressure melamine impregnated paper (LPM) as a surface material To provide a reinforcement finish for ship furniture resistant to moisture and moisture.

또한, 본 발명의 다른 목적은 합판의 표면재로 저압 멜라민 함침지(LPM)를 사용할 수 있게 됨으로써 제조비용이 적게 들어 생산성이 향상된 선박가구용 강화 마감재를 제공함에 있다.In addition, another object of the present invention is to provide a low-pressure melamine impregnated paper (LPM) as a surface material of the plywood to reduce the production cost to provide a reinforcement finish for ship furniture improved productivity.

상기와 같은 목적을 달성하기 위하여 본 발명의 바람직한 일 실시예에 따른 선박가구용 강화 마감재는, 합판을 기재층으로 하여, 상기 합판의 상면에는 경질섬 유판(HDF)이 접착되고, 상기 경질섬유판(HDF)의 상면에는 저압 멜라민 함침지(LPM)가 접착되어 구성된 것을 특징으로 한다.In order to achieve the above object, reinforcing finish for ship furniture according to an embodiment of the present invention, the plywood as the base layer, the hard island plate (HDF) is bonded to the upper surface of the plywood, the hard fiber plate (HDF) Low pressure melamine impregnated paper (LPM) is bonded to the upper surface of the) is characterized in that it is configured.

그리고, 바람직하게 상기 경질섬유판(HDF)은, 상기 합판의 양면에 접착된 것이 바람직하다.Preferably, the hard fiber board (HDF) is preferably bonded to both sides of the plywood.

그리고, 바람직하게 상기 경질섬유판(HDF)은 직경이 적은 소경목을 목섬유상태로 만들어 합성수지 접착제로 결합시켜 가압 가열하여 비중이 0.8 내지 1.1, 두께가 3 내지 6mm의 하드보드로 이루어지는 것이 바람직하다.Preferably, the hard fiber board (HDF) is made of a small diameter wood of small diameter to make a wood fiber state, combined with a synthetic resin adhesive and heated by pressure, preferably made of a hard board having a specific gravity of 0.8 to 1.1 and a thickness of 3 to 6 mm.

그리고, 바람직하게 상기 저압 멜라민 함침지(LPM)는, 미립의 멜라민수지를 가압 가열하여 비중 0.67 내지 0.75, 두께가 0.075 내지 0.2mm의 판상으로 제조되는 것이 바람직하다.Preferably, the low-pressure melamine impregnated paper (LPM) is prepared by pressurizing and heating the fine melamine resin in a plate shape having a specific gravity of 0.67 to 0.75 and a thickness of 0.075 to 0.2 mm.

그리고, 바람직하게 상기 합판의 하면에는 경질섬유판(HDF)이 접착되고, 상기 경질섬유판(HDF)의 하면에는 저압 멜라민 함침지(LPM)가 접착되어 구성된 것이 바람직하다.Preferably, a hard fiber board (HDF) is bonded to the bottom surface of the plywood, and low pressure melamine impregnated paper (LPM) is bonded to the bottom surface of the hard fiber board (HDF).

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기로 한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 2는 본 발명의 바람직한 실시예에 따른 선박가구용 강화 마감재를 나타낸 도면이다.2 is a view showing a reinforcement finish for ship furniture according to a preferred embodiment of the present invention.

도 2에 도시된 바와 같이, 본 발명은 합판(10)과, 합판(10)의 상면에 경질섬유판(HDF)(20)과, 저압 멜라민 함침지(LPM)(30)를 순차적층하고 접착되어 구성된다.As shown in FIG. 2, the present invention sequentially laminates and adheres a plywood 10, a hard fiber plate (HDF) 20, and a low pressure melamine impregnated paper (LPM) 30 on an upper surface of the plywood 10. It is composed.

상기 합판(10)은 천연 목재의 특성과 장점을 그대로 보유하면서도 강도가 높고 변형되지 않으면 활용성이 뛰어나 건축계, 인테리어업계는 물론이고 가구를 비롯한 각종 목제품의 원부자재로 널리 사용되고 있는 것으로서, 통상의 합판의 제조과정과 동일하게 두께가 0.5 내지 4mm의 얇은 단판(베니어판)을 1매마다 섬유방향이 직각으로 물리게 하여 7매 또는 9매의 홀수로 겹쳐 쌓아 형성하되 열경화성수지 접착제로 맞붙여 제조된다. The plywood 10, while retaining the characteristics and advantages of natural wood as it is, high strength and excellent in utilization without deformation, widely used as raw materials for various wood products, including furniture, as well as the building industry, interior industry, and conventional plywood In the same manner as in the manufacturing process of a thin end plate (veneer plate) of 0.5 to 4mm thickness is formed by stacking 7 or 9 odd number of sheets so that the fiber direction is at right angles to each sheet, but is produced by bonding with a thermosetting resin adhesive.

특히, 상기 열경화성수지 접착제는 T1 수지로서, T1 수지는 Type 1(Melamine Formaldehyde Glue for Exterior)인 멜라민수지나 페놀(Phenol)수지를 말한다. 따라서, 상기 합판(10)은 상기 접착제로 사용된 T1 수지의 특성인 기계적인 강도에 의하여 강도가 한층 더 보강된다.In particular, the thermosetting resin adhesive is a T1 resin, T1 resin refers to melamine resin or phenol (Phenol) resin of Type 1 (Melamine Formaldehyde Glue for Exterior). Therefore, the plywood 10 is further reinforced by the mechanical strength that is characteristic of the T1 resin used as the adhesive.

그리고, 상기 경질섬유판(20)은 직경이 적은 소경목을 목섬유상태로 만들어 합성수지 접착제로 결합시켜 가압 가열하여 비중이 0.8 내지 1.1, 두께가 3 내지 6mm의 하드보드로서, 강도면에서 중밀도 섬유판(MDF)보다 우수하다.The hard fiber board 20 is made of a small diameter wood with a small diameter of wood fiber, combined with a synthetic resin adhesive, and heated under pressure to have a specific gravity of 0.8 to 1.1 and a thickness of 3 to 6 mm. MDF).

이와 같은 상기 경질섬유판(20)은 열경화성수지 접착제에 의하여 합판(10)의 상면 및 하면에 적층되어 접착된다. The hard fiber plate 20 is laminated and bonded to the upper and lower surfaces of the plywood 10 by the thermosetting resin adhesive.

또한, 상기 경질섬유판(20)의 상면으로 저압 멜라민 함침지(30)가 적층되어 접착된다.In addition, the low-pressure melamine impregnated paper 30 is laminated and bonded to the upper surface of the hard fiber plate 20.

상기 저압 멜라민 함침지(30)는 종이에 그라비어(gravure) 인쇄를 하여 모양지를 만들고, 이 모양지에 멜라민과 요소 수지를 함침시켜 만든 성형용 수지 시트로서, 두께 0.075 ~ 0.2mm으로 얇고 비중 0.67 ~ 0.75으로서 고압 멜라민 함침 지(HPM)보다 가격이 저렴하다.The low-pressure melamine-impregnated paper 30 is made of gravure printing on paper to make a shape paper, and is a resin sheet for molding made by impregnating melamine and urea resin on the paper, which is thin with a thickness of 0.075 to 0.2 mm and has a specific gravity of 0.67 to 0.75. It is cheaper than high pressure melamine impregnated paper (HPM).

상기 저압 멜라민 함침지(30)는 시트 자체의 함침수지가 접착제 역할을 하고 있기 때문에 별도의 접착제 없이도 상기 경질섬유판(20)에 고온고압으로 접착된다. The low-pressure melamine impregnated paper 30 is bonded to the hard fiber plate 20 at high temperature and high pressure without a separate adhesive because the impregnated resin of the sheet itself serves as an adhesive.

이상과 같이 본 발명에 따른 선박가구용 강화 마감재는 먼저 경질섬유판(20) 및 저압 멜라민 함침지(30)를 열경화성수지 접착제를 사용하여 접착한 후, 이를 합판(10)의 양면에 열 프레스에 의하여 130 내지 180℃의 온도, 10 내지 20㎏/㎤의 압력하에서 7 내지 8분간 가열압착함으로써 완성된 제품으로 생산된다.As described above, the reinforcing finish for ship furniture according to the present invention first adheres the hard fiber plate 20 and the low-pressure melamine impregnated paper 30 by using a thermosetting resin adhesive, and then, 130 by heat press on both sides of the plywood 10. It is produced as a finished product by heat-pressing for 7 to 8 minutes at a temperature of from 180 ° C. to a pressure of 10 to 20 kg / cm 3.

이러한 본 발명에 따른 선박가구용 강화 마감재는 종래의 마감재의 외부 충격 및 습기에 대한 취약성을 고려하여 외부 충격 및 습기에 충분히 견딜 수 있도록 합판(10)의 상면 또는 하면으로 경질섬유판(20)을 접착하고 그 위에 저압 멜라민 함침지(30)를 접착하여 형성함으로써 외부 충격 및 습기에 매우 강하며 트위스트(휨)현상이 없어 선박가구용 강화 마감재뿐만 아니라 경제적인 저압 멜라민 함침지(30)로 합판에 가공해야 하는 모든 부분을 대체할 수 있는 유용한 발명이다.The reinforcing finish for ship furniture according to the present invention is to adhere the hard fiber plate 20 to the upper or lower surface of the plywood 10 to sufficiently withstand the external shock and moisture in consideration of the vulnerability to the external shock and moisture of the conventional finish material. Formed by bonding low pressure melamine impregnated paper 30 thereon, it is very resistant to external shock and moisture, and there is no twist phenomenon, and it is required to process plywood with economical low pressure melamine impregnated paper 30 as well as reinforced furniture for ship furniture. It is a useful invention that can replace all parts.

이상과 같이, 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술사상과 아래에 기재될 실용신안등록청구범위의 균등범위 내에서 다양한 수정 및 변형이 가능함은 물론이다.As described above, although the present invention has been described by way of limited embodiments and drawings, the present invention is not limited thereto and is intended by those skilled in the art to which the present invention pertains. Various modifications and variations can be made within the equivalent scope of the utility model registration claims to be described.

상술한 바와 같이, 본 발명은 합판의 표면을 경질섬유판(HDF)에 의해 저압 멜라민 함침지(LPM)를 부착할 수 있어 도료의 도포나 벽지의 시공과 같은 마감처리 를 행하지 않더라도 표면상태가 저압 멜라민 함침지(LPM)에 의한 미려한 표면을 유지할 수 있으며, 이에 따라 마감처리의 불필요에 따른 원가절감과 함께 저압 멜라민 함침지(LPM)의 특성상 표면의 세척이나 청소가 용이하여 청결한 실내 분위기를 연출할 수 있는 효과가 있다.As described above, the present invention can attach the low pressure melamine impregnated paper (LPM) to the surface of the plywood by the hard fiber board (HDF), so that the surface state is low pressure melamine even without performing the finishing treatment such as coating of paint or application of wallpaper. It is possible to maintain a beautiful surface by impregnated paper (LPM), and thus, it is possible to reduce the cost due to the need for finishing treatment and to easily clean or clean the surface due to the characteristics of low pressure melamine impregnated paper (LPM) to produce a clean indoor atmosphere. It works.

또한, 본 발명은 고압 멜라민 함침지(HPM)를 사용하지 않고도 같은 효과를 낼 수 있으므로 생산원가가 저렴한 선박가구용 강화 마감재를 제공할 수 있는 효과가 있다.In addition, the present invention can achieve the same effect without using a high-pressure melamine impregnated paper (HPM), there is an effect that can provide a low cost production furniture reinforcement finish.

또한, 본 발명은 선박가구뿐만 아니라 경제적인 저압 멜라민 함침지(LPM)로 합판에 가공해야 하는 모든 부분을 대체할 수 있으며, 합판 위에는 고압 멜라민 함침지(HPM)가 아니면 접착가공 처리가 안 된다는 고정관념을 타파할 수 있는 효과가 있다.In addition, the present invention can replace all parts that need to be processed on plywood with economical low-pressure melamine impregnated paper (LPM) as well as ship furniture, fixed on the plywood is not adhesive processing unless the high-pressure melamine impregnated paper (HPM) It has the effect of breaking the notion.

Claims (5)

합판(10)을 기재층으로 하여, With the plywood 10 as the base layer, 상기 합판(10)의 상면에는 경질섬유판(HDF)(20)이 접착되고, 상기 경질섬유판(HDF)(20)의 상면에는 저압 멜라민 함침지(LPM)(30)가 접착되어 구성된 것을 특징으로 하는 선박가구용 강화 마감재.Hard fiber board (HDF) 20 is bonded to the upper surface of the plywood 10, low pressure melamine impregnated paper (LPM) 30 is bonded to the upper surface of the hard fiber board (HDF) (20) Reinforced finish for ship furniture. 제 1 항에 있어서, 상기 경질섬유판(HDF)은, The method of claim 1, wherein the hard fiber plate (HDF), 상기 합판(10)의 양면에 접착된 것을 특징으로 하는 선박가구용 강화 마감재.Reinforcement finish for ship furniture, characterized in that bonded to both sides of the plywood (10). 제 1 항 또는 제 2 항에 있어서, 상기 경질섬유판(HDF)(20)은,The method of claim 1 or 2, wherein the hard fiber plate (HDF) 20, 직경이 적은 소경목을 목섬유상태로 만들어 합성수지 접착제로 결합시켜 가압 가열하여 비중이 0.8 내지 1.1, 두께가 3 내지 6mm의 하드보드로 이루어지는 것을 특징으로 하는 선박가구용 강화 마감재.Reinforced finish for ship furniture, characterized in that the small diameter wood made of wood fiber state combined with a synthetic resin adhesive and pressurized and heated to a specific gravity of 0.8 to 1.1, a thickness of 3 to 6mm hard board. 제 1 항에 있어서, 상기 저압 멜라민 함침지(LPM)(30)는,The method of claim 1, wherein the low pressure melamine impregnated paper (LPM) 30, 미립의 멜라민수지를 가압 가열하여 비중이 0.67 내지 0.75, 두께가 0.075 내지 0.2mm의 판상으로 제조되는 것을 특징으로 하는 선박가구용 강화 마감재.Reinforcement finishing material for ship furniture, characterized in that the granular melamine resin is pressurized and heated to a plate shape of specific gravity 0.67 to 0.75, thickness 0.075 to 0.2mm. 제 1 항에 있어서,The method of claim 1, 상기 합판(10)의 하면에는 경질섬유판(HDF)(20)이 접착되고, 상기 경질섬유판(HDF)(20)의 하면에는 저압 멜라민 함침지(LPM)(30)가 접착되어 구성된 것을 특징으로 하는 선박가구용 강화 마감재.A hard fiber plate (HDF) 20 is bonded to the bottom surface of the plywood 10, and a low pressure melamine impregnated paper (LPM) 30 is bonded to the bottom surface of the hard fiber plate (HDF) 20. Reinforced finish for ship furniture.
KR1020070050877A 2007-05-25 2007-05-25 High plywood board KR100843750B1 (en)