CN108356929A - A kind of production method of new type compound glued board - Google Patents
A kind of production method of new type compound glued board Download PDFInfo
- Publication number
- CN108356929A CN108356929A CN201810219634.4A CN201810219634A CN108356929A CN 108356929 A CN108356929 A CN 108356929A CN 201810219634 A CN201810219634 A CN 201810219634A CN 108356929 A CN108356929 A CN 108356929A
- Authority
- CN
- China
- Prior art keywords
- press
- finished product
- new type
- molding
- type compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of glued board producing method of new type compound, production stage is：1, the high density fiberboard of 1 5mm thickness is selected to be used as upper and lower bottom panel；2, sandwich layer between upper and lower bottom panel lays the veneer wood skin for having applied glue and number of plies both forward and reverse directions interlock assembly molding as required；3, hot-press solidifying finished product in multi-daylight press is entered back into after assembly slab cold pressing exhaust after molding；4, the finished product after hot-press solidifying is molded by size requirement sawing again through cooling；5, after the molding finished product of sawing enters the fixed thick sanding of sander, quality inspection storage, shipping customers subsequently use melamine impregnated paper wainscot to process.It disclosure satisfy that production requirement, meet follow-up high-grade melamine impregnated paper wainscot requirement, have the characteristics that practicality is simple, improve production qualification rate, reduce production cost.
Description
Technical field
The invention belongs to artificial board technology fields, are related to a kind of production method of new type compound glued board.
Background technology
Conventional veneer boards production method：The all rounding veneer assemblies of harden structure, upper and lower surface top grade wood skin capping,
After through hot press molding, then Furniture manufacture to be used for after sanding patch melamine impregnated paper clad can.The glued board of produced in conventional processes is deposited
In following disadvantage：
1, because the upper and lower surface used in production is than relatively thin wood skin, damage shadow is highly susceptible in transport and hot pressing
Ring Qualified Products Rate.
2, because the upper and lower surface used in production is than relatively thin high-grade wood skin, cost is relatively high.
3, finished product thickness tolerance is difficult control in production process, influences following process production.
4, because the upper and lower surface used in production is than relatively thin high-grade wood skin, in subsequently patch melamine impregnated paper
Bad product rate is too high.
5, because the upper and lower surface used in production is than relatively thin wood skin, the melamine-impregnated of high request can not be overlayed
Paper（Such as：Bloom, light, patch PVC etc.）
6, because surface wood skin is thin and matter is soft, the bonding force of melamine impregnated paper wainscot and wood skin is poor, influences furniture quality.
Invention content
In order to overcome the disadvantages mentioned above of the prior art, the present invention to provide a kind of glued board producing method of new type compound,
It disclosure satisfy that production requirement, meet subsequently high-grade melamine impregnated paper wainscot requirement, with practical simple, raising production qualification
Rate reduces the features such as production cost.
The technical solution adopted by the present invention to solve the technical problems is：A kind of plywood production side of new type compound
Method, production stage are：
1, the high density fiberboard of 1-5mm thickness is selected to be used as upper and lower bottom panel；
2, the sandwich layer between upper and lower bottom panel lays the veneer wood skin for having applied glue and number of plies both forward and reverse directions are handed over as required
Wrong assembly molding；
3, hot-press solidifying finished product in multi-daylight press is entered back into after assembly slab cold pressing exhaust after molding；
4, the finished product after hot-press solidifying is molded by size requirement sawing again through cooling；
5, after the molding finished product of sawing enters the fixed thick sanding of sander, quality inspection storage, shipping customers subsequently use melamine to soak
Stain paper veneer is processed.
The environmental protection grade of the high density fiberboard：E1, E0 or without any one in aldehyde plate.
Veneer wood skin is any one in eucalyptus, poplar, pine or weedtree kind, and glue can select E1, E0 grades of ureaformaldehydes
Resin or Formaldehyde-free adhesive.
Multi-daylight press, single-layer hot press, hot press with high frequency any of which can be selected in the press.
The positive effect of the present invention is：After upper and lower surface is changed to thin high-density fiberboard capping, reduce to high forestick
The requirement of skin reduces production cost；After upper and lower surface is changed to thin high-density fiberboard capping, qualification rate is greatly improved
And production efficiency, reduce cost waste；After upper and lower surface is changed to thin high-density fiberboard capping, thickness deviation can after sanding
To control in 0.1mm, the required precision of veneer, Furniture manufacture disclosure satisfy that；Upper and lower surface is changed to thin high-density fiberboard
After capping, the high request of all melamine impregnated paper wainscots disclosure satisfy that, and greatly improve the conjunction of the quality after veneer
Lattice rate and veneer efficiency；After upper and lower surface is changed to thin high-density fiberboard capping, melamine impregnated paper wainscot can be improved
Bonding force improves product quality.
Specific implementation mode
With reference to embodiment, the present invention is further described.
A kind of glued board producing method of new type compound, production stage are：
1, the high density fiberboard of 1-5mm thickness is selected to be used as upper and lower bottom panel；
2, the sandwich layer between upper and lower bottom panel lays the veneer wood skin for having applied glue and number of plies both forward and reverse directions are handed over as required
Wrong assembly molding；
3, hot-press solidifying finished product in multi-daylight press is entered back into after assembly slab cold pressing exhaust after molding；
4, the finished product after hot-press solidifying is molded by size requirement sawing again through cooling；
5, after the molding finished product of sawing enters the fixed thick sanding of sander, quality inspection storage, shipping customers subsequently use melamine to soak
Stain paper veneer is processed.
The environmental protection grade of the high density fiberboard：E1, E0 or without any one in aldehyde plate.
Veneer wood skin is any one in eucalyptus, poplar, pine or weedtree kind, and glue can select E1, E0 grades of ureaformaldehydes
Resin or Formaldehyde-free adhesive.
Multi-daylight press, single-layer hot press, hot press with high frequency any of which can be selected in the press.
After upper and lower surface is changed to thin high-density fiberboard capping, reduces the requirement to high-grade wood skin and reduce and be produced into
This；After upper and lower surface is changed to thin high-density fiberboard capping, qualification rate and production efficiency are greatly improved, reduces cost wave
Take；After upper and lower surface is changed to thin high-density fiberboard capping, thickness deviation can control in 0.1mm after sanding, can
Meet the required precision of veneer, Furniture manufacture；After upper and lower surface is changed to thin high-density fiberboard capping, all three are disclosure satisfy that
The high request of poly cyanamid impregnated paper veneer, and greatly improve the quality pass rate after veneer and veneer efficiency；Upper following table
After face is changed to thin high-density fiberboard capping, the bonding force of melamine impregnated paper wainscot can be improved, improves product quality.
Claims (4)
1. a kind of glued board producing method of new type compound, it is characterised in that production stage is：
（1）The high density fiberboard of 1-5mm thickness is selected to be used as upper and lower bottom panel；
（2）Sandwich layer between upper and lower bottom panel lays the veneer wood skin for having applied glue and number of plies both forward and reverse directions are handed over as required
Wrong assembly molding；
（3）Hot-press solidifying finished product in multi-daylight press is entered back into after assembly slab cold pressing exhaust after molding；
（4）Finished product after hot-press solidifying is molded by size requirement sawing again through cooling；
（5）After the molding finished product of sawing enters the fixed thick sanding of sander, quality inspection storage, shipping customers subsequently use melamine to soak
Stain paper veneer is processed.
2. the glued board producing method of new type compound as described in claim 1, it is characterised in that：The high density fiberboard
Environmental protection grade：E1, E0 or without any one in aldehyde plate.
3. the glued board producing method of new type compound as described in claim 1, it is characterised in that：Veneer wood skin is eucalyptus, poplar
Any one in wood, pine or weedtree kind, glue can select E1, E0 grade urea-formaldehyde resin or Formaldehyde-free adhesive.
4. the glued board producing method of new type compound as described in claim 1, it is characterised in that：Multilayer can be selected in the press
Hot press, single-layer hot press, hot press with high frequency any of which.