KR20070114578A - Stainless brassware and it's manufacturing method - Google Patents

Stainless brassware and it's manufacturing method Download PDF

Info

Publication number
KR20070114578A
KR20070114578A KR1020060048334A KR20060048334A KR20070114578A KR 20070114578 A KR20070114578 A KR 20070114578A KR 1020060048334 A KR1020060048334 A KR 1020060048334A KR 20060048334 A KR20060048334 A KR 20060048334A KR 20070114578 A KR20070114578 A KR 20070114578A
Authority
KR
South Korea
Prior art keywords
stainless steel
surface portion
stainless
edge
organic
Prior art date
Application number
KR1020060048334A
Other languages
Korean (ko)
Inventor
오택문
Original Assignee
오택문
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 오택문 filed Critical 오택문
Priority to KR1020060048334A priority Critical patent/KR20070114578A/en
Publication of KR20070114578A publication Critical patent/KR20070114578A/en

Abstract

A stainless brassware and its manufacturing method are provided to have a function of brassware as a well-being kitchenware and to reduce the cost of raw materials at the same time. A stainless brassware includes an inner surface portion(10) and an outer surface portion(20). The inner surface portion is made of an alloy of copper and tin. The center portion of the inner surface portion is depressed to be concave to form the inner side of a bowl. The outer surface portion is made of a stainless steel, and the center portion of the outer surface portion is depressed to be concave. The outer surface portion is fixed to be adhered to the outer side of the inner surface portion and forms the outer side of the bowl. 4-6mm of the edge of the inner surface portion is bent.

Description

스테인레스 방짜유기 및 그 제조방법{Stainless brassware and it′s manufacturing method}Stainless steel salt organic and its manufacturing method {Stainless brassware and it's manufacturing method}

도 1은 본 발명의 일 실시예에 따른 스테인레스 방짜유기를 나타낸 단면도.1 is a cross-sectional view showing a stainless steel salt organic according to an embodiment of the present invention.

도 2는 본 발명의 일 실시예에 따른 스테인레스 방짜유기를 제조하는 공정을 나타낸 공정도.Figure 2 is a process diagram showing a process for producing a stainless steel organic cotton organic according to an embodiment of the present invention.

도 3은 본 발명의 다른 실시예에 따른 스테인레스 방짜유기를 나타낸 단면도.Figure 3 is a cross-sectional view showing a stainless steel salt organic according to another embodiment of the present invention.

<도면의 주요부호에 대한 설명><Description of Major Symbols in Drawing>

1, 2: 스테인레스 방짜유기 10 : 내면부1, 2: stainless steel organic organ 10: inner surface

20 : 외면부 30 : 굽20: outer surface 30: heel

본 발명은 스테인레스 방짜유기 및 그 제조방법에 관한 것으로, 더욱 상세하게는 그릇의 안쪽면은 방짜(놋쇠)로 형성하고 그릇의 바깥면은 스테인레스로 형성하여 방짜와 스테인레스가 갖는 특성을 복합시킨 스테인레스 방짜유기 및 그 제조방법에 관한 것이다.The present invention relates to a stainless steel organic cotton and a method of manufacturing the same, and more specifically, the inner surface of the bowl is formed of a bark (brass) and the outer surface of the bowl is formed of stainless stainless bark combined the characteristics of the bark and stainless An organic and a manufacturing method thereof.

우리나라에는 세계적으로 특이한 방짜라는 금속이 있는데, 이 방짜는 구리 78%와 주석22%의 정확한 비율로 합금하여 만든 최상질의 놋쇠로서 식기, 촛대, 향로, 소반, 대야, 악기, 불구(佛具) 등과 같은 전통적인 민속 공예 재료로 가장 폭 넓게 사용되고 있다.In Korea, there is a unique metal called Bangcha, which is made of the best quality brass alloy made of 78% copper and 22% tin. It is a tableware, a candlestick, an incense burner, a basin, a basin, an instrument, a crutch, etc. It is the most widely used traditional folk craft material.

전통적으로 방짜를 이용하여 제품을 만드는 과정을 보면, 구리와 주석의 합금을 합금한 상태에서 열을 가한 후, 망치로 담금질을 하여 조직이 고른 판을 만들고, 이 판을 쇠망치로 두들겨 그릇이나 악기 등 다양한 제품을 만들게 된다. Traditionally, the process of making a product using a yarn is made of alloys of copper and tin, followed by heat, followed by quenching with a hammer to form a flat plate, and then hammering the plate with an iron hammer to make a bowl or musical instrument. You will make a variety of products.

방짜는 스스로 살균 소독작용을 하기 때문에 식기에 가장 적합하며, 방짜로 만든 식기를 ‘방짜유기’ 또는 ‘놋그릇’이라고 한다.Bangchak is best suited for tableware because it sterilizes itself, and it is called 'bangchak organic' or 'brass bowl'.

예로부터 방짜유기는 스스로 음식을 살균 소독하는 기능을 지니고 있기 때문에 특히 노약자나 어린이, 임산부에게 탁월한 효능이 있는 것으로 알려져 왔다. 즉, 방짜유기는 현대사회에서 가장 중요시하는 웰빙식기로 그 어떤 식기보다도 탁월한 식기라 할 수 있다.Since ancient times, Banggakgi has the function of sterilizing and disinfecting foods on its own, and has been known to be particularly effective for the elderly, children, and pregnant women. In other words, the Bangjak Yugi is the well-being tableware that is most important in the modern society.

그러나 방짜유기는 제작이 어렵고 재료비가 고가이다보니 많은 사람들이 이용하기에는 한계가 있을 뿐만 아니라, 산화하여 녹이 슬면서 아주 해롭다는 파란색의 녹을 발생시키게 되는데 이러한 현상은 사찰 등에서 공양그릇으로 사용하는 경우에 하루 종일 물 또는 음식을 담아 두어야 하는 경우에 더 심하다.However, because the organic cotton is difficult to manufacture and the material cost is high, there are limitations for many people to use, and it causes rust and rust, which causes blue rust, which is very harmful. Worse if you need to keep water or food all day.

이에 본 발명은 전술한 바와 같은 종래의 제반 문제점을 해소하기 위하여 안출된 것으로, 그릇의 안쪽면은 방짜로 형성하고 그릇의 바깥면은 녹이 슬지 않고 가격이 저렴한 스테인레스로 형성함으로써, 방짜가 갖는 웰빙식기로서의 기능을 보유함과 동시에 재료비를 절감할 수 있고 녹이 스는 현상을 최소화할 수 있는 스테인레스 방짜유기 및 그 제조방법을 제공하는데 그 목적이 있다.Accordingly, the present invention has been made to solve the above-mentioned conventional problems, by forming the inner surface of the bowl in the room and the outer surface of the bowl formed of stainless steel, which is inexpensive and inexpensive, well-being tableware Its purpose is to provide a stainless steel organic material and a method of manufacturing the same, which can reduce the material cost and minimize the rusting phenomenon while retaining its function as a metal.

전술한 바와 같은 목적을 달성하기 위해 본 발명에 따른 스테인레스 방짜유기는, 구리와 주석의 합금으로 이루어진 방짜로 제작되며 중심부가 오목하게 함몰되어 그릇의 안쪽면을 형성하는 내면부, 및 스테인레스로 제작되며 중심부가 오목하게 함몰되고 내면부의 바깥면에 밀착된 상태로 고정되어 그릇의 바깥면을 형성하는 외면부를 포함하여 이루어진 것에 기술적 특징이 있다.In order to achieve the object as described above, the stainless steel salt organic body according to the present invention is made of an alloy made of an alloy of copper and tin, and the inner surface portion to form the inner surface of the bowl recessed concave, and made of stainless The technical feature is that the center portion is concave, recessed and fixed in close contact with the outer surface of the inner surface portion to form the outer surface of the bowl.

전술한 구성에 있어서, 내면부의 가장자리는 외면부의 가장자리를 감싸도록 절곡되며, 내면부의 절곡된 가장자리의 내측면에는 외면부의 가장자리 외측면에 형성된 고정홈에 삽입되는 고정돌기가 돌출된다.In the above-described configuration, the edge of the inner surface portion is bent to surround the edge of the outer surface portion, the inner side of the bent edge of the inner surface portion protruding fixing projections are inserted into the fixing groove formed on the outer surface of the edge of the outer surface portion.

전술한 구성에 있어서, 내면부의 가장자리중 절곡되는 부분은 4~6㎜인 것이 바람직하다.In the above-described configuration, it is preferable that the bent portion of the edges of the inner surface portion is 4 to 6 mm.

전술한 구성에 있어서, 외면부의 저면 중심부에는 스테인레스로 제작된 굽이 용접된다.In the above-described configuration, a heel made of stainless is welded to the bottom center of the outer surface portion.

전술한 바와 같은 목적을 달성하기 위해 본 발명에 따른 스테인레스 방짜유기의 제조방법은, 방짜를 가열한 후 단조 또는 압연에 의해 판으로 가공하는 단계, 가공된 방짜판을 원판으로 프레스하는 단계, 스테인레스판을 방짜 원판보다 작은 원판으로 프레스하고 그 저면 가장자리에 고정홈을 파는 단계, 방짜 원판과 스테인 레스 원판을 맞대고 방짜 원판이 안쪽에 위치되도록 그릇 형태로 드로잉하는 단계, 및 방짜 원판을 드로잉하여 형성된 내면부의 가장자리를 바깥쪽으로 접어 스테인레스 원판을 드로잉하여 형성된 외면부의 가장자리를 감싸고 내면부의 일부가 외면부의 고정홈에 삽입되도록 압연하는 단계를 포함하여 이루어지는 것에 기술적 특징이 있다.In order to achieve the object as described above, the manufacturing method of the stainless steel salt organic organic according to the present invention, the step of heating the sheet to the forging or rolling by a plate, the step of pressing the processed sheet to the original plate, stainless plate Press the plate into a smaller plate than the free plate and dig a fixing groove at the bottom edge thereof, face the free plate and the stainless plate, and draw the shape of the plate so that the free plate is located inside, and draw the free plate to There is a technical feature that comprises the step of folding the edge outward to surround the edge of the outer surface formed by drawing a stainless disc and rolling so that a portion of the inner surface is inserted into the fixing groove of the outer surface.

전술한 스테인레스 방짜유기의 제조방법은, 스테인레스판을 절곡하여 굽을 형성하고, 이 굽을 외면부의 저면 중심부에 용접하는 단계를 더 포함하여 이루어진다.The manufacturing method of the above-mentioned stainless steel organic raw material further includes bending a stainless plate to form a heel, and welding the heel to the bottom center of the outer surface portion.

전술한 스테인레스 방짜유기의 제조방법에 있어서, 방짜 원판의 직경을 스테인레스 원판의 직경보다 4~6㎜ 더 크게 형성하는 것이 바람직하다.In the manufacturing method of the above-mentioned stainless steel saltproof organic substance, it is preferable to form the diameter of a saltproof disk 4-4 mm larger than the diameter of a stainless steel disk.

이하, 본 발명에 따른 스테인레스 방짜유기 및 그 제조방법의 바람직한 실시예를 통하여 전술한 바와 같은 구성들의 특징과 그 작용을 보다 상세히 설명하기로 한다.Hereinafter, the characteristics of the above-described components and their functions will be described in more detail with reference to preferred embodiments of the stainless steel organic organic vegetable and its manufacturing method according to the present invention.

첨부된 도면의 도 1은 본 발명의 일 실시예에 따른 스테인레스 방짜유기를 나타낸 단면도이다.Figure 1 of the accompanying drawings is a cross-sectional view showing a stainless steel salt organic according to an embodiment of the present invention.

도 1에 도시된 바와 같이, 본 발명의 일 실시예에 따른 스테인레스 방짜유기(1)는 방짜로 제작되어 그릇의 안쪽면을 형성하는 내면부(10), 및 스테인레스로 제작되며 그릇의 바깥면을 형성하는 외면부(20)을 포함하여 이루어진다.As shown in Figure 1, the stainless steel organic cotton (1) according to an embodiment of the present invention is produced in the room to form the inner surface of the bowl 10, and made of stainless steel and the outer surface of the bowl It comprises an outer surface portion 20 to be formed.

전술한 내면부(10)는 구리 78중량%와 주석 22 중량%를 합금하여 제작된 것으로, 중심부가 오목하게 함몰된 형태로 형성되며, 그 가장자리가 외면부(20)의 가장자리를 감싸도록 절곡된다.The inner surface portion 10 is formed by alloying 78% by weight of copper and 22% by weight of tin. The inner surface portion 10 is formed in a concave shape in the center thereof, and the edge is bent to surround the edge of the outer surface portion 20. .

내면부(10)의 절곡된 가장자리의 내측면에는 후술할 외면부(20)의 고정홈(20a)에 삽입되는 고정돌기(10a)가 돌출된다. 이러한 고정돌기(10a)는 도면에서와 같이 단면이 삼각형상을 이루되 그 정점이 윗쪽으로 치우치게 형성됨으로써, 내면부(10)와 외면부(20)가 견고하게 고정된다.A fixing protrusion 10a inserted into the fixing groove 20a of the outer surface portion 20 to be described later protrudes on the inner side of the bent edge of the inner surface portion 10. The fixing protrusion 10a has a triangular cross section as shown in the drawing, but its peak is formed to be biased upward, so that the inner surface portion 10 and the outer surface portion 20 are firmly fixed.

내면부(10)의 절곡된 가장자리는 4~6㎜가 바람직하며, 5㎜일 때가 가장 바람직하다. 만일, 4㎜ 미만으로 절곡되는 경우에는 접촉면적이 너무 작고 고정돌기(10a)와 고정홈(20a)의 크기 또한 작아야 하기 때문에 고정상태가 양호하지 않으며, 6㎜를 초과할 경우에는 불필요한 접촉면적이 너무 넓어 외관상 좋지 않을 뿐만아니라 절곡된 내면부(10)의 가장자리 단부가 들뜰 염려가 있으며 내면부(10)의 제작비용이 증가하는 단점이 있다.The bent edge of the inner surface portion 10 is preferably 4-6 mm, most preferably 5 mm. If the bending is less than 4 mm, the contact area is too small and the size of the fixing protrusion 10a and the fixing groove 20a must also be small, so that the fixed state is not good. Not only is it too wide in appearance, but there is a concern that the edge end of the bent inner surface portion 10 is raised and the manufacturing cost of the inner surface portion 10 is increased.

이러한 내면부(10)는 구리와 주석의 합금으로 이루어진 방짜의 특성상 자체에 살균 소독기능을 가지고 있기 때문에 음식물에 함유된 각종 세균을 박멸해주어 음식물이 상하는 것을 방지해준다.Since the inner surface portion 10 has a sterilization function in itself due to the characteristics of the room made of an alloy of copper and tin, it prevents food from being damaged by eradicating various bacteria contained in the food.

전술한 외면부(20)는 스테인레스로 제작되며 중심부가 오목하게 함몰되고 내면부(10)의 바깥면에 밀착된 상태로 고정되어 그릇의 바깥면을 형성하는 것으로, 그 가장자리 외측에는 내면부(10)의 고정돌기(10a)가 삽입되는 고정홈(20a)이 형성된다. The outer surface portion 20 is made of stainless steel and is recessed in the center and fixed in a state of being in close contact with the outer surface of the inner surface portion 10 to form the outer surface of the bowl. A fixing groove 20a is inserted into which the fixing protrusion 10a of the) is inserted.

이러한 외면부(20)는 스테인레스의 특성상 녹이 슬지 않기 때문에 세척이 용이할 뿐만 아니라 방짜에 비해 제작비용이 저렴하다.Since the outer surface 20 is not rusted due to the characteristics of stainless steel, it is easy to clean, and the manufacturing cost is lower than that of the room.

첨부된 도 2는 본 발명의 일 실시예에 따른 스테인레스 방짜유기의 제조공정을 나타낸 도면이다.2 is a view illustrating a manufacturing process of a stainless steel organic organic vegetable according to an embodiment of the present invention.

먼저, 구리 78 중량%와 주석 22중량%의 합금으로 이루어진 방짜를 가열한 후 단조 또는 압연에 의해 (a)에서와 같은 사각의 판(11)을 가공한 후, 사각의 판을 (b)에서와 같은 원판형태로 프레스하여 방짜 원판(12)을 제작한다.First, after heating a room composed of an alloy of 78% by weight of copper and 22% by weight of tin, the square plate 11 as in (a) is processed by forging or rolling, and then the square plate is cut in (b). By pressing in the form of a disk such as to prepare a raw disk 12.

한편, 방짜 원판(12)의 제작과는 별도로 스테인레스판을 프레스하여 (c)에서와 같은 원판형태의 스테인레스 원판(21)을 제작한다. 이 때, 스테인레스 원판(21)은 방짜 원판(12)의 직경보다 4~6㎜ 작게 형성한다. 그리고, 스테인레스 원판(21)을 제작한 후에는 그 저면 가장자리에 고정홈(21a)을 형성한다.On the other hand, in addition to the production of the original disk 12, by pressing a stainless plate separately to produce a disk-shaped stainless disk 21 as in (c). At this time, the stainless disc 21 is formed 4-6 mm smaller than the diameter of the spinning disc 12. After the stainless disc 21 is manufactured, the fixing groove 21a is formed at the bottom edge thereof.

전술한 과정을 통해 방짜 원판(11)과 스테인레스 원판(21)의 제작이 완료되면, (d)에서와 같이 방짜 원판(11)과 스테인레스 원판(21)을 맞댄 상태에서 프레스기계 또는 헤라시보리기 등을 이용하여 방짜 원판(11)과 스테인레스 원판(21)을 그릇의 형태로 드로잉한다. 이 때, 방짜 원판(11)이 안쪽에 위치된다. 이러한 드로잉공정을 통해 방짜 원판(11)은 그릇의 내면부(10)를 형성하고 스테인레스 원판(21)은 그릇의 외면부(20)를 형성하게 된다. 참고로, 드로잉공정은 냄비 등을 제작하는 공정에서 통상적으로 이루어지는 것이므로 상세한 설명은 생략한다.When the production of the spinning disk 11 and the stainless disk 21 is completed through the above-described process, as in (d), the press machine or the Herashibori, etc. in a state in which the spinning disk 11 and the stainless disk 21 are returned. Drawing the original disc 11 and the stainless disc 21 in the form of a bowl. At this time, the spinning disk 11 is located inside. Through the drawing process, the spinning disk 11 forms the inner surface portion 10 of the bowl, and the stainless steel plate 21 forms the outer surface portion 20 of the bowl. For reference, the drawing process is usually made in the process of manufacturing a pot, etc., detailed description thereof will be omitted.

드로잉공정이 완료되면, (e)에서와 같이 내면부(10)의 가장자리를 바깥쪽으로 접어 외면부(20)의 가장자리를 감싸고 감싼 부분을 압연하여 내면부(10)의 일부 가 외면부(20)의 고정홈(20a)에 삽입되어 고정돌기(10a)를 형성한다. 이러한 고정돌기(10a)가 고정홈(20a)에 삽입됨으로써 내면부(10)와 외면부(20)가 분리되지 않고 견고히 고정된다. When the drawing process is completed, as shown in (e) to fold the edge of the inner surface portion 10 to the outside to surround the edge of the outer surface portion 20 and to roll the wrapped portion to a part of the inner surface portion 10 is the outer surface portion 20 It is inserted into the fixing groove (20a) of the fixing protrusion (10a) to form. Since the fixing protrusion 10a is inserted into the fixing groove 20a, the inner surface portion 10 and the outer surface portion 20 are firmly fixed without being separated.

첨부된 도면의 도 3은 본 발명의 다른 실시예에 따른 스테인레스 방짜유기를 나타낸 단면도이다. 여기서, 도 1 및 도 2와 동일한 참조부호는 동일기능을 갖는 동일부재이다.Figure 3 of the accompanying drawings is a cross-sectional view showing a stainless steel salt organic according to another embodiment of the present invention. Here, the same reference numerals as those in Figs. 1 and 2 are the same members having the same function.

도 3에 도시된 바와 같이, 본 발명의 다른 실시예에 따른 스테인레스 방짜유기(2)는, 본 발명의 일 실시예에 따른 스테인레스 방짜유기의 외면부(20)의 저면 중심부에 바닥에 대하여 방짜유기를 안정적으로 지지해주는 굽(30)이 더 구비된다.As shown in FIG. 3, the stainless weave organic cotton 2 according to another embodiment of the present invention is a weave organic cotton with respect to the bottom of the bottom center of the outer surface portion 20 of the stainless weft organic cotton organic according to one embodiment of the present invention. Heel 30 is further provided to stably support the.

이러한 굽(30)은 스테인레스판을 절곡하여 형성되며, 용접에 의해 외면부(20)의 저면 중심부에 결합된다.The heel 30 is formed by bending a stainless plate and is coupled to the bottom center of the outer surface portion 20 by welding.

따라서, 제작공정에서도 도 2의 (e)공정후 스테인레스판을 절곡하여 굽을 형성하고, 이 굽을 드로잉된 외면부(20)의 저면 중심부에 용접하는 과정을 더 거치게 된다.Therefore, in the manufacturing process, the stainless plate is bent after the process of FIG. 2E to form a bend, and the bend is further subjected to a process of welding the bottom part of the bottom surface portion 20 of the drawn outer surface portion 20.

이상과 같이 본 발명의 바람직한 실시예들에 따른 스테인레스 방짜유기 및 그 제조방법을 첨부된 도면을 참조로 설명하였으나, 본 발명은 본 명세서에 상세히 설명된 실시예들과 도면에 한정되지 아니하며, 발명의 기술사상 범위 내에서 다양한 변형이 이루어질 수 있다. 예컨대, 방짜를 구성하는 구리와 주석의 성분비는 다 양한 형태로 변경실시 될 수 있으며, 이러한 실시예 역시 본원발명의 권리범위에 포함되는 것으로 보아야 한다.As described above with reference to the accompanying drawings, a stainless steel organic organic and its manufacturing method according to preferred embodiments of the present invention, the present invention is not limited to the embodiments and drawings described in detail herein, of the invention Various modifications may be made within the scope of the technical idea. For example, the component ratios of copper and tin constituting the room can be changed in various forms, such embodiments should be considered to be included in the scope of the invention.

전술한 바와 같이 구성된 본 발명 스테인레스 방짜유기 및 그 제조방법에 따르면, 그릇의 안쪽면은 방짜로 형성하고 그릇의 바깥면은 가격이 저렴하고 녹이 슬지 않는 스테인레스로 형성함으로써, 방짜가 갖는 고유의 특성 즉 살균 소독의 효과를 살리면서 스테인레스가 갖는 특성 즉 녹이 스는 현상을 최소화할 수 있다.According to the present invention stainless steel salt organic cotton and the method of manufacturing the same as described above, the inner surface of the bowl is formed in the room and the outer surface of the bowl is formed of stainless steel that is inexpensive and rustless, that is, the unique characteristics of the While maintaining the effect of disinfection, it is possible to minimize the characteristics of stainless, that is, rust.

또한, 내면부의 가장자리를 바깥쪽으로 절곡하여 외면부의 가장자리를 감싸고 외면부의 가장자리 외측에 형성된 고정홈에 내면부의 절곡된 가장자리로부터 돌출되는 고정돌기가 삽입됨으로서, 내면부와 외면부가 분리되지 않고 견고히 고정될 수 있다.In addition, by bending the edge of the inner surface to the outside to surround the edge of the outer surface and the fixing projection protruding from the bent edge of the inner surface is inserted into the fixing groove formed on the outer edge of the outer surface, the inner surface and the outer surface can be fixed firmly without separation. have.

Claims (7)

구리와 주석의 합금으로 이루어진 방짜로 제작되며 중심부가 오목하게 함몰되어 그릇의 안쪽면을 형성하는 내면부; 및An inner surface portion formed of an alloy made of copper and tin, the inner portion of the bowl being recessed to form an inner surface of the bowl; And 스테인레스로 제작되며 중심부가 오목하게 함몰되고 상기 내면부의 바깥면에 밀착된 상태로 고정되어 그릇의 바깥면을 형성하는 외면부를 포함하여 이루어진 것을 특징으로 하는 스테인레스 방짜유기.Stainless steel organic cotton made of stainless and characterized in that the center portion is concave recessed and fixed in close contact with the outer surface of the inner surface portion to form an outer surface to form the outer surface of the bowl. 제 1 항에 있어서,The method of claim 1, 상기 내면부의 가장자리는 상기 외면부의 가장자리를 감싸도록 절곡되며, 상기 내면부의 절곡된 가장자리의 내측면에는 상기 외면부의 가장자리 외측면에 형성된 고정홈에 삽입되는 고정돌기가 돌출된 것을 특징으로 하는 스테인레스 방짜유기. The edge of the inner surface portion is bent to surround the edge of the outer surface portion, the inner surface of the bent edge of the inner surface portion of the stainless steel organic organic characterized in that the fixing projections are inserted into the fixing groove formed in the outer surface of the outer edge of the outer portion . 제 2 항에 있어서,The method of claim 2, 상기 내면부의 가장자리중 절곡되는 부분은 4~6㎜인 것을 특징으로 하는 스테인레스 방짜유기.Stainless steel woven organic material, characterized in that the bent portion of the edge of the inner surface portion 4 ~ 6mm. 제 1 항 내지 제 3 항중 어느 한 항에 있어서,The method according to any one of claims 1 to 3, 상기 외면부의 저면 중심부에는 스테인레스로 제작된 굽이 용접된 것을 특징 으로 하는 스테인레스 방짜유기.Stainless steel woven organic, characterized in that the heel is made of stainless steel is welded to the center of the bottom surface of the outer surface. 방짜를 가열한 후 단조 또는 압연에 의해 판으로 가공하는 단계;Processing the sheet to form a plate by forging or rolling after heating; 가공된 방짜판을 원판으로 프레스하는 단계;Pressing the machined sheet into a disc; 스테인레스판을 상기 방짜 원판보다 작은 원판으로 프레스하고, 그 저면 가장자리에 고정홈을 파는 단계;Pressing the stainless plate into a disc smaller than the raw disc, and digging a fixing groove at the bottom edge thereof; 상기 방짜 원판과 스테인레스 원판을 맞대고 방짜 원판이 안쪽에 위치되도록 그릇 형태로 드로잉하는 단계; 및Abutting the free disk and the stainless disk and drawing the bowl in such a way that the free disk is positioned inside; And 방짜 원판을 드로잉하여 형성된 내면부의 가장자리를 바깥쪽으로 접어 스테인레스 원판을 드로잉하여 형성된 외면부의 가장자리를 감싸고 내면부의 일부가 외면부의 고정홈에 삽입되도록 압연하는 단계를 포함하여 이루어지는 것을 특징으로 하는 스테인레스 방짜유기 제조방법. Stainless steel organic fabric production comprising the step of folding the edge of the inner surface formed by drawing a spinning disk to the outside to draw a stainless disk to surround the edge of the outer surface formed and rolling a portion of the inner surface is inserted into the fixing groove of the outer surface Way. 제 5 항에 있어서,The method of claim 5, 스테인레스판을 절곡하여 굽을 형성하고, 이 굽을 상기 외면부의 저면 중심부에 용접하는 단계를 더 포함하여 이루어진 것을 특징으로 하는 스테인레스 방짜유기 제조방법.Forming a bend by bending a stainless plate, and further comprising the step of welding the bend to the center of the bottom surface of the outer surface portion stainless steel organic manufacturing method. 제 5 항 또는 제 6 항에 있어서,The method according to claim 5 or 6, 상기 방짜 원판의 직경을 스테인레스 원판의 직경보다 4~6㎜ 더 크게 형성하 는 것을 특징으로 하는 스테인레스 방짜유기 제조방법.Stainless steel organic production method characterized in that the diameter of the spinning disk is formed 4 ~ 6 mm larger than the diameter of the stainless steel disk.
KR1020060048334A 2006-05-29 2006-05-29 Stainless brassware and it's manufacturing method KR20070114578A (en)