KR20070002364A - Interlining for clothing having function of anion emission - Google Patents

Interlining for clothing having function of anion emission Download PDF

Info

Publication number
KR20070002364A
KR20070002364A KR1020050057862A KR20050057862A KR20070002364A KR 20070002364 A KR20070002364 A KR 20070002364A KR 1020050057862 A KR1020050057862 A KR 1020050057862A KR 20050057862 A KR20050057862 A KR 20050057862A KR 20070002364 A KR20070002364 A KR 20070002364A
Authority
KR
South Korea
Prior art keywords
anion
weight
wick
clothing
anion emission
Prior art date
Application number
KR1020050057862A
Other languages
Korean (ko)
Inventor
김춘근
Original Assignee
김춘근
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김춘근 filed Critical 김춘근
Priority to KR1020050057862A priority Critical patent/KR20070002364A/en
Publication of KR20070002364A publication Critical patent/KR20070002364A/en

Abstract

The interlining for clothing having an anion emission function is provided to prevent the lowering of hardness due to the frequent washing. An anion coating layer(20) is manufactured by mixing the anion emission materials(22) such as tourmaline, charcoal, yellow soil and elvan with high efficiency as the specific ratio after crushing. The size of the crushed anion emission materials is 0.2-0.6 mm, preferably. The anion emission materials and the liquid adhesive(24) are mixed with a specific ratio of 45-60 wt % and 30-40 wt %. The water of 10-15 wt % is injected, preferably. Polyurethane resin and silicon group adhesive are used as the liquid adhesive, preferably, in order to maintain the flexibility.

Description

음이온 방출기능을 갖는 의류용 심지{Interlining for clothing having function of anion emission}Interlining for clothing having function of anion emission

도 1은 본 발명에 따라 음이온 방출기능을 갖는 심지를 적용시킨 의류의 요부 절결 사시도.Figure 1 is a perspective view of the main portion of the garment is applied wick with anion release function according to the present invention.

도 2는 본 발명의 음이온 방출기능을 갖는 의류에 적용된 심지의 단면도,Figure 2 is a cross-sectional view of the wick applied to the garment having anion release function of the present invention,

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10 : 바탕재 20 : 음이온코팅층10: base material 20: anion coating layer

22 : 음이온방출물질 24 : 액상접착제22: anion emitting material 24: liquid adhesive

30 : 접착층 40 : 겉감30: adhesive layer 40: outer

본 발명은 음이온이 방출기능을 갖는 의류용 심지에 관한 것으로, 보다 상세하게는 음이온을 방출하여 인체의 건강증진 및 쾌적한 생활에 기여하며 의류의 청결도 유지되어 위생적인 음이온 방출기능을 갖는 의류용 심지에 관한 것이다.The present invention relates to a wick for clothes having an anion release function, more specifically to the discharge of anion contributes to the health and comfortable life of the human body and to maintain the cleanliness of the clothing to the sanitary anion wick It is about.

일반적으로 의류용 심지는 와이셔츠의 칼라나 소매 또는 정장 자켓의 칼라, 가슴부분이나 등부분에서 겉감의 내부에 위치하여 의류의 형태를 유지하고 착용감 을 높여주는 기능을 하며, 이는 일정한 형태를 유지를 위해 경도가 있으며 세탁이 용이한 면, 마 등과 같은 천연섬유 또는 합성섬유의 직포나 부직포를 그 재료로 한다.In general, the wick for clothing is located inside the outer skin at the collar of the shirt, the sleeve or the collar of the suit jacket, the chest or the back to maintain the shape of the garment and enhance the fit. The material is made of woven or non-woven fabric of natural or synthetic fibers such as cotton, hemp, etc., which have hardness and are easy to wash.

이와 같은 의류용 심지는 통상적으로 의류의 겉감 내부에 놓여 봉합되므로 세탁 시 의류와 함께 세탁되는데, 반복적인 세탁에 의해 그 경도가 저하되기 쉬워 의류의 형태가 변형되는 경우가 많았다.Such wicks for garments are usually placed inside the outer fabric of the garment and are sewn together to be washed together with the garment during washing, and the hardness of the garment tends to be deteriorated by repeated washing.

따라서 본 발명의 심지에 적용시키고자 하는 음이온은 공기 중의 먼지에 대한 분해작용, 탈취작용 및 항균작용을 하며, 인체에 대해서는 세포활성화, 혈액정화와 혈액순환촉진, 면역력 증가 및 자율신경조절 등의 작용을 한다. 나아가 음이온은 피로회복을 촉진시키고 β-엔돌핀을 활성화시켜 기분을 상쾌하게 하며, 체내의 이온밸런스를 유지시켜 통증을 완화시키고 알레르기 체질을 개선시키는 것과 같은 건강 및 정신활동에 도움을 주는 기능을 갖고 있다.Therefore, the anion to be applied to the wick of the present invention is decomposed, deodorized and antibacterial to the dust in the air, the body activation, blood purification and blood circulation, immune immunity and autonomic nerve control, etc. Do it. Furthermore, negative ions have functions to promote fatigue and activate β-endorphin to refresh mood, maintain ionic balance in the body, relieve pain and improve allergic predisposition, such as health. .

본 발명은 전술한 바와 같은 음이온의 특성에 착안하여 개발된 것으로, 음이온방출물질들을 특정 비율로 혼합한 후 의류용 심지에 결합함으로서 인체에 유익한 음이온이 장기간 방사되어 인체의 건강과 쾌적함을 증진시키고, 음이온의 먼지 분해작용, 탈취작용 및 항균작용에 의해 의류의 오염도가 감소되므로 잦은 세탁으로 인한 경도저하를 방지할 수 있는 음이온 방출기능을 갖는 의류용 심지를 제공함에 그 목적이 있다.The present invention was developed in view of the characteristics of the negative ions as described above, by mixing the negative ions release material in a specific ratio and bound to the wick for clothing, the negative ions beneficial to the human body is radiated for a long time to promote the health and comfort of the human body, It is an object of the present invention to provide a wick for clothing having an anion release function that can prevent the deterioration of hardness due to frequent washing, since the contamination of clothing is reduced by dust decomposition, deodorization and antibacterial action of the anion.

상기의 목적을 달성하기 위한 본 발명의 음이온 방출기능을 갖는 의류용 심지는 토르말린 45-60중량%, 숯 12-17중량%, 황토 10-15중량%, 맥반석 11-16중량% 및 옥 7-13중량%를 분쇄 및 혼합한 음이온방출물질 45-60중량%에 액상접착제 30-40중량%을 투입하고 물 10-15중량%를 가하여 혼합한 후, 저면에 접착층이 형성된 직포 또는 부직포의 바탕재 상면에 도포하여 음이온코팅층을 형성한 다음, 상기 음이온방출물질이 도포된 바탕재를 170-180℃의 온도에서 15-18분간 건조시켜 제품 형성된다. 특히 상기 음이온방출물질의 입자는 0.2-0.6mm의 크기로 구성됨을 특징으로 한다.Clothing wick with anion release function of the present invention for achieving the above object 45-60% by weight tourmaline, 12-17% by weight charcoal, 10-15% by ocher, 11-16% by weight of ganban stone and jade 7- 30-40% by weight of a liquid adhesive was added to 45-60% by weight of the anion-releasing material, which was ground and mixed with 13% by weight, mixed with 10-15% by weight of water, and then the base material of the woven or nonwoven fabric having an adhesive layer formed on the bottom surface thereof. After coating on the upper surface to form an anion coating layer, the base material coated with the anion-emitting material is dried for 15-18 minutes at a temperature of 170-180 ℃ to form a product. In particular, the particles of the anion-emitting material is characterized in that consisting of 0.2-0.6mm in size.

이하, 본 발명의 구성을 첨부한 도면을 참조하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings, the configuration of the present invention will be described in detail.

본 발명의 의류용 심지를 구성하는 음이온코팅층(20)은 토르말린, 숯, 황토, 맥반석 및 옥과 같은 고효율의 음이온방출물질(22)들을 분쇄한 후 특정비율로 혼합함으로서, 각 물질들의 상호작용에 의해 음이온 발생율이 극대화되어 인체에 유익한 작용을 하게 된다. 이와 같은 음이온방출물질(22)들은 그 상호작용이 효율적으로 이루어지기 위해 입자의 크기가 0.2-0.6mm의 크기가 되도록 분쇄시키는 것이 바람직하다.The anion coating layer 20 constituting the garment wick of the present invention is pulverized high-efficiency anion-emitting material 22, such as tourmaline, charcoal, loess, elvan and jade, and then mixed in a specific ratio, by interaction of each material The anion generation rate is maximized to have a beneficial effect on the human body. Such anion-releasing material 22 is preferably pulverized so that the particle size is 0.2-0.6mm in order to make the interaction efficiently.

또한 음이온방출물질(22)과 액상접착제(24)는 특정비율인 45-60중량% 및 30-40중량%의 비율로 혼합되는데, 이는 음이온방출물질(22)의 혼합량이 증가하면 방출되는 음이온의 양은 증가하지만 음이온방출물질(22)이 음이온코팅층(20)에서 분리되기 쉬운 반면, 상기 음이온방출물질(22)의 혼합량이 감소하면 방출되는 음이온방출물질(22)이 음이온코팅층(20)에서 쉽게 분리되지는 않으나, 방출되는 음이온의 양이 감소하기 때문에 상기와 같은 음이온방출물질(22)과 액상접착제(24)의 비율로 혼합하는 것이 바람직하다.In addition, the anion-releasing material 22 and the liquid adhesive 24 are mixed at a specific ratio of 45-60% by weight and 30-40% by weight, which increases the amount of anion released when the amount of the anion-releasing material 22 is increased. While the amount is increased, the anion-releasing material 22 is easily separated from the anion-coating layer 20, while the amount of anion-releasing material 22 released is easily separated from the anion-coating layer 20 when the mixing amount of the anion-emitting material 22 is reduced. However, since the amount of anion released is reduced, it is preferable to mix the anion-releasing material 22 and the liquid adhesive 24 as described above.

이때 물은 10-15중량%를 투입하는 것이 바람직하며, 이는 상기 음이온방출물질 혼합물이 바탕재(10) 상면에 도포되기 용이한 점성을 가지면서 심지가 적당한 유연성을 가질 수 있을 정도의 양에 해당된다.At this time, it is preferable to add 10-15% by weight of water, which corresponds to the amount of the wick can have a moderate flexibility while the viscosity of the anion-emitting material mixture is easy to be applied to the upper surface of the base material (10) do.

또한 음이온방출물질(22)과 혼합되는 액상접착제(24)는 접착력을 가지면서 심지의 유연성을 유지할 수 있도록 폴리우레탄계 수지 및 실리콘계 접착제가 이용되는 것이 바람직하다.In addition, the liquid adhesive 24 mixed with the anion-releasing material 22 is preferably a polyurethane-based resin and a silicone-based adhesive to maintain the flexibility of the wick while having an adhesive force.

이와 같이 혼합 형성된 음이온방출물질 혼합물은 도 1 및 도 2에 보이는 바와 같이 바탕재(10) 상면에 도포되어 음이온코팅층(20)을 형성하게 되는데, 음이온방출물질 혼합물을 바탕재(10) 상면에 도포하는 방식은 분무방식, 로울러 압착방식 또는 스크린 접착방식과 같은 통상의 방법이 적용되게 된다.The mixed anion-emitting material mixture formed as described above is applied to the upper surface of the base material 10 as shown in FIGS. 1 and 2 to form an anion coating layer 20. Anion-emitting material mixture is applied to the upper surface of the base material 10. The method of spraying, roller compacting or screen bonding is applied to conventional methods.

한편, 바탕재(10)는 폴리에스테르 또는 폴리아크릴 섬유 등과 같이 섬유의 굵기가 있으며 저렴한 재질로 제직 또는 접합된 것을 이용하는데, 따라서 음이온방출물질 혼합물이 바탕재(10)의 섬유 사이의 공간으로 침투하기 용이하여 보다 많은 양의 음이온방출물질(22)이 코팅되므로 음이온 방출량의 증대를 기대할 수 있다.On the other hand, the base material 10 is used as the thickness of the fiber, such as polyester or polyacrylic fiber, weaved or bonded with an inexpensive material, so that the anion-emitting material mixture penetrates into the space between the fibers of the base material 10 It is easy to do so because a larger amount of anion-releasing material 22 is coated can be expected to increase the amount of anion release.

이때 도 1 및 도 2에 보이는 바와 같이, 바탕재(10)의 저면에는 심지가 의류의 겉감(40) 내부에 위치될 때 고정될 수 있도록 접착제가 도포된 접착층(30)이 형성되어 있다.At this time, as shown in Figures 1 and 2, the bottom surface of the base material 10 is formed with an adhesive layer 30 is coated with an adhesive to be fixed when the wick is positioned inside the outer cloth 40 of the garment.

<실시예><Example>

우선, 토르말린 60중량%, 숯 12중량%, 황토 10중량%, 맥반석 11중량% 및 옥 7중량%로 이루어진 음이온방출물질(22)을 분쇄기에 넣어 분쇄한 후, 체에 걸러 그 입자의 크기가 0.5mm 되도록 하였다. 상기 분말화된 음이온방출물질(22) 55중량%에 액상 폴리우레탄 접착제 35중량%를 투입하고 물 10중량%를 가하면서 균일하게 혼합하였다.First, the anion-releasing material (22) consisting of 60% by weight tourmaline, 12% by weight charcoal, 10% by weight loess, 11% by weight elvan and 7% by weight jade is put into a grinder, and pulverized. 0.5 mm. To 55% by weight of the powdered anion-releasing material (22) was added 35% by weight of the liquid polyurethane adhesive and uniformly mixed while adding 10% by weight of water.

계속해서 저면에 접착층(30)이 있으며 와이셔츠 칼라 부분에 삽입되는 통상의 심지를 제조대 위해 놓고, 일정한 점도로 혼합된 상기 음이온방출물질 혼합물을 분무기로 도포하여 음이온코팅층(20)을 형성하였다.Subsequently, there is an adhesive layer 30 on the bottom surface and a conventional wick inserted into a shirt collar portion is placed for manufacturing, and the anion-coating material mixture mixed at a constant viscosity is applied by a sprayer to form an anion coating layer 20.

마지막으로 상기의 음이온코팅층(20)이 심지 상면에 접착 및 고정되도록 180℃의 온도에서 15분간 건조시켜 심지를 완성하였다.Finally, the anion coating layer 20 was dried at a temperature of 180 ° C. for 15 minutes to bond and fix the upper surface of the wick to complete the wick.

상기의 실시예를 통해 의류용 심지가 결합된 와이셔츠를 착용해 본 결과, 칼라 부분의 오염도가 기존의 셔츠보다 감소되었으며 피로감이 덜하고 쾌적함을 느낄 수 있었다. 이는 심지에 코팅된 음이온방출물질(22)로부터 방사되는 음이온의 생체에너지 활성화작용, 혈액순환 촉진작용, 먼지분해작용, 탈취 및 항균작용에 따른 결과로 볼 수 있다.As a result of wearing a shirt combined with a wick for clothing through the above embodiment, the degree of contamination of the collar portion was reduced than that of the existing shirt, and the fatigue and the comfort could be felt. This can be seen as a result of the bioenergy activation action, blood circulation promoting action, dust decomposition action, deodorization and antibacterial action of the anion radiated from the anion-emitting material 22 coated on the wick.

또한 실험에 의하면 와이셔츠 칼라에서 500-1,500개/cc의 음이온이 방출되었으며, 이는 숲과 같은 자연 상태에서 방출되는 음이온 방출량에 해당되는 것으로 뛰어난 음이온 방출효과를 확인할 수 있었으며, 그 지속력도 통상 3년간 유지되는 것으로 나타났다.In addition, according to the experiment, 500-1,500 / cc of negative ions were released from the shirt collar, which corresponds to the amount of negative ions released from the natural state such as forests. Appeared to be maintained.

이상에서 설명한 바와 같이 본 발명의 음이온 방출기능을 갖는 의류용 심지에 의하면, 심지의 상면에 특정비율로 분쇄 및 혼합된 음이온방출물질과 액상 접착제가 특정비율로 혼합된 음이온코팅층이 형성되어 인체의 혈액순환을 좋게 하고 생체에너지를 활성화하며 항균 및 탈취작용을 하므로 인체의 질병을 예방하고 건강을 증진시킬 수 있다.As described above, according to the wick for clothes having an anion-releasing function of the present invention, an anion coating layer in which the anion-releasing material and liquid adhesive are mixed and pulverized in a specific ratio is formed on the upper surface of the wick so that the blood of the human body is formed. It improves circulation, activates bioenergy, and acts as an antibacterial and deodorant, which can prevent diseases of the human body and promote health.

또한 음이온코팅층의 먼지분해작용, 항균작용 및 탈취작용에 의해 의류의 칼라와 소매 등의 오염을 줄이므로, 쾌적한 생활이 가능하며 세탁의 횟수를 줄어들게 하여 심지의 경도가 쉽게 저하되는 것을 방지할 수 있는 것과 같은 효과가 제공될 수 있다.In addition, by reducing dust, antibacterial and deodorizing effect of the anion coating layer, clothing color and sleeves can be contaminated, thus enabling a comfortable life and reducing the number of washings, thus preventing the hardness of the wick from being easily degraded. The same effect can be provided.

Claims (2)

토르말린 45-60중량%, 숯 12-17중량%, 황토 10-15중량%, 맥반석 11-16중량% 및 옥 7-13중량%를 분쇄 및 혼합한 음이온방출물질(22) 45-60중량%에 액상접착제(24) 30-40중량%을 투입하고 물 10-15중량%를 가하여 혼합한 후, 저면에 접착층(30)이 형성된 직포 또는 부직포의 바탕재(10) 상면에 도포하여 음이온코팅층(20)을 형성한 다음, 상기 음이온방출물질(22)이 도포된 바탕재(10)를 170-180℃의 온도에서 15-18분간 건조시켜 구성됨을 특징으로 하는 음이온 방출기능을 갖는 의류용 심지.45-60% by weight of anion-releasing material (22), pulverized and mixed 45-60% by weight tourmaline, 12-17% by weight charcoal, 10-15% by ocher, 11-16% by weight elvan and 7-13% by jade 30-40% by weight of the liquid adhesive agent 24 was added thereto, 10-15% by weight of water was added thereto, mixed, and then applied to the upper surface of the base material 10 of the woven or nonwoven fabric having the adhesive layer 30 formed thereon. 20) After forming, the base material (10) coated with the anion-releasing material (22) is a wick for clothes having an anion-releasing function, characterized in that it is configured to dry for 15-18 minutes at a temperature of 170-180 ℃. 제 1항에 있어서,The method of claim 1, 상기 음이온방출물질(22)은 그 입자가 0.2-0.6mm의 크기로 구성된 것을 특징으로 하는 음이온 방출기능을 갖는 의류용 심지.The anion-releasing material 22 is a wick for clothes having anion-releasing function, characterized in that the particles are composed of a size of 0.2-0.6mm.
KR1020050057862A 2005-06-30 2005-06-30 Interlining for clothing having function of anion emission KR20070002364A (en)