KR20060117629A - Functional water paint - Google Patents
Functional water paint Download PDFInfo
- Publication number
- KR20060117629A KR20060117629A KR1020050040041A KR20050040041A KR20060117629A KR 20060117629 A KR20060117629 A KR 20060117629A KR 1020050040041 A KR1020050040041 A KR 1020050040041A KR 20050040041 A KR20050040041 A KR 20050040041A KR 20060117629 A KR20060117629 A KR 20060117629A
- Authority
- KR
- South Korea
- Prior art keywords
- water
- paint
- weight
- parts
- titanium oxide
- Prior art date
Abstract
Description
본 발명은 자정 기능이 있는 기능성 수성도료에 관한 것으로, 더 자세하게는 광촉매제인 아나타제형 산화티탄과 수성 접착제 및 물을 기존 조성으로 하며, 분말상의 태백, 운모, 규조토, 안료 등과 같은 도료 구성물과, 소포제, 증조제 등과 같은 보조제를 필요에 따라 적어도 1종 이상씩 선택적으로 첨가함으로써, 일반 수성도료와 동등한 수준의 초기 도장 품질을 가지면서도, 산화티탄의 광촉매작용에 의한 자기 청결성, 내곰팡이성, 멸균성 및 공기 정화성을 갖도록 한 기능성 수성도료에 관한 것이다.The present invention relates to a functional aqueous coating having a self-cleaning function, and more particularly, to anatase-type titanium oxide, an aqueous adhesive, and water, which are photocatalysts, and a paint composition such as powdery white milk, mica, diatomaceous earth, and pigment, and an antifoaming agent. By selectively adding at least one auxiliary agent such as a thickener, etc. as necessary, it has an initial coating quality equivalent to that of a general water-based paint, and is self-cleaning, mold-resistant, and sterile by photocatalytic action of titanium oxide. And it relates to a functional water-based paint to have air purification.
산업혁명 이후 산업 기술의 발전과 함께 과거에 비하여 생화수준의 괄목할만한 향상이 이루어졌으나, 그 역작용으로서, 오히려 대기 오염은 심각해지고 있으며, 대도시의 경우에는, 자동차에서 배출되는 배가스에 의한 대기 오염이 가중되고 있고, 근래에는 봄철마다 되풀이되는 중국으로부터의 황사 및 황사와 함께 실려오는 중국 내의 각종 산업 오염물까지 증가하고 있는 실정이다.After the Industrial Revolution, with the development of industrial technology, remarkable improvement of the level of biodiversity has been made compared to the past, but in reverse, air pollution is becoming serious, and in the case of large cities, air pollution by the exhaust gas emitted from automobiles is increased. In recent years, there has been an increasing number of industrial pollutants in China, which are accompanied by yellow dust and yellow dust from China, which are repeated every spring.
그러나, 생활수준의 향상과 더불어 미관에 대한 판단 기준과 주변 환경에 대 한 기대 수준이 올라감에 따라 건축물의 내·외벽 오염에 대하여 더욱 민감해지고 있는 바, 대기의 오염 정도가 커짐에 따라 건축물의 내·외 미관 향상과 청결을 위한 비용이 현저히 증가하고 있다.However, with the improvement of living standards, the standard of aesthetics and the expectation of surrounding environment have increased, so it is becoming more sensitive to contamination of interior and exterior walls of buildings. · The cost for improving aesthetics and cleanliness is increasing significantly.
오늘날 각종 건축물의 내·외벽면의 마감은 크게 두 가지 종류로 구분될 수 있는 바, 그 하나는, 유리, 가공석재, 표면처리 강재 등 도료에 의한 별도의 도색이 필요 없는 마감재가 사용되는 경우이고, 다른 하나는, 대부분의 아파트와 같이 철근 콘크리트 구조물로 건축된 후 벽면에 대한 도색으로 마감되는 경우로서, 도색되는 건축물에 대하여 좀더 살펴 보면 다음과 같다.Today, the interior and exterior walls of various buildings can be divided into two types, one of which is a case in which finishing materials that do not need to be painted by paint, such as glass, processed stone, and surface-treated steel, are used. The other is the case of building with reinforced concrete structure like most apartments and finishing with painting on the wall.
각종 건축물의 내·외 벽면 도색에 사용되는 도료는 일반적으로 유성도료가 아닌 수성도료가 주로 사용되고 있으며, 수성도료로 도색된 건축물의 내·외 벽면은 시간이 흐름에 따라 도료 자체의 경시 열화에 의한 황변과, 전술한 대기 오염 등에 의해 최초 도색하였을 때의 색감을 잃어버리면서 각종 오염물에 의해 더렵혀짐으로써 그 미관을 해치게 된다.In general, paints used for interior and exterior wall painting of various buildings are mainly water-based paints, not oil-based paints.In the interior and exterior wall of buildings painted with water-based paints, due to deterioration of the paint itself with time, The yellow color and the color of the first paint due to the air pollution described above are lost, and are contaminated by various pollutants, thereby deteriorating the aesthetics.
상기와 같은 건축물 벽면의 오염은, 건축물의 가치까지도 떨어뜨리게 되기 때문에, 건축물 특히, 아파트나 사무실 빌딩 등과 같은 대형 건축물은 일정한 주기로 벽면에 대한 청소와 새로운 도색이 반복적으로 실시되고 있으나, 건축물에 대한 도색 작업은 비용이 상당하기 때문에 경제적인 부담이 되고 있다.As the contamination of the building wall as described above also lowers the value of the building, the building, in particular, large buildings such as apartments and office buildings have been repeatedly cleaned and newly painted on the wall at regular intervals. The work is costly because of the considerable cost.
더욱이, 도색 작업 중 흩날리는 도료에 의한 주변 환경의 2차적인 오염과 주변의 피해를 야기시켜 이웃끼리 분쟁이 발생될 수 있는 여지도 있는 바, 표면 오염도가 낮은 도료를 사용함으로써 도색 주기를 연장하여 재도색에 따른 비용의 절감 을 꾀하여야 하나, 현재의 일반적인 도료로는 큰 소득이 없는 실정이다.Moreover, the secondary paint may cause secondary pollution of the surrounding environment and surrounding damage caused by paints scattered during painting, which may cause disputes between neighbors. The cost of painting should be reduced, but the current general paint does not have a big income.
또한, 각종 오염물 등에 의한 건축물 외벽면의 단순 오염 뿐 아니라, 실내 벽면의 경우에는 기름, 연기, 과일, 야채 등의 각종 오염물의 부착과 함께 그러한 오염물이 부패하여 악취를 발생시키기도 하고, 공팡이나 유해 세균 등이 번식하게 됨으로써, 미관을 해침은 물론 건강에도 악영향을 끼칠 수 있게 된다.In addition to the simple contamination of the exterior walls of buildings with various contaminants, in addition to the attachment of various contaminants such as oil, smoke, fruits, and vegetables, indoor contaminants may decompose such contaminants and cause odors. By the reproduction of the back, not only can hurt the aesthetics but also adversely affect health.
따라서, 상기와 같은 문제점을 해결하기 위하여 항균성 도료가 개발되기도 하였으나, 그러한 도료에 함유된 곰팡이 방지제나 살균제 자체가 독성을 가지고 있기 때문에 그 사용량이 제한되는 단점이 있으며, 곰팡이 방지제와 살균제가 유해 세균을 죽일 수는 있으나, 유해 세균이 남긴 독소를 완전히 제거하지 못하기 때문에 여전히 오염과 건강 상의 문제가 남아 있게 된다.Therefore, in order to solve the above problems, antimicrobial paints have been developed, but since the antifungal or fungicides contained in such paints are toxic, their usage is limited. It can kill, but it still does not completely eliminate the toxins left by harmful bacteria, leaving contamination and health problems.
또한, 공기 중에 있는 질산화물(NOx), 일산화탄소(COx), 이산화유황(SO2) 등과 같은 각종 오염물이 검축물의 실내 유입되어 건강에 악영향을 미칠 수도 있으나, 고가의 공기 정화기를 사용하는 외에 마땅한 대처 방안이 없는 실정이다.In addition, various contaminants such as nitrogen oxides (NOx), carbon monoxide (COx), and sulfur dioxide (SO 2 ) in the air may adversely affect health due to the inflow of the indoors of the specimens. There is no situation.
본 발명은, 수성도료를 사용하여 이루어지는 도색 작업에 의해 내·외 벽면이 마감되는 종래 건축물의 내·외벽면 오염에 따른 제반 문제점들을 해결하기 위하여 창안된 것으로, 도색 주기를 현저히 연장하여 그 비용을 절감할 수 있을 뿐만 이니라, 오염시 오염물을 분해하여 제거되도록 하는 동시에 실내 환경을 포함한 주변 환경의 공기 정화까지도 가능한 기능성 수성도료를 제공함에 본 발명의 목적이 있다.The present invention has been made to solve various problems caused by the contamination of the interior and exterior walls of a conventional building, in which the interior and exterior walls are finished by the painting work using water-based paint, and significantly extends the cost of painting. It is an object of the present invention to provide a functional water-based paint that can not only reduce, but also decompose and remove contaminants during pollution, and at the same time, purify the air of the surrounding environment including the indoor environment.
본 발명의 상기 목적은 광촉매제로 알려져 있는 산화티탄에 의하여 달성된다.This object of the present invention is achieved by a titanium oxide known as a photocatalyst.
본 발명의 수성도료는 광촉매제인 아나타제형 산화티탄 10∼46wt%와, 수용성 접착제 26∼35wt% 및 물 29∼64wt%로 조성되며, 필요에 따라 분말상 도료 구성물과 보조제가 첨가되는 바, 각각의 성분들을 살펴 보면 다음과 같다.The aqueous paint of the present invention is composed of 10 to 46 wt% of an anatase type titanium oxide, a photocatalyst, 26 to 35 wt% of a water-soluble adhesive, and 29 to 64 wt% of water, and a powdery paint composition and an auxiliary agent are added as necessary. Looking at them as follows.
본 발명 수성도료의 핵심 구성 요소인 상기 산화티탄은, 빛을 받아 화학반응을 촉진시키는 광촉매제로서, 산화티탄은 자외선에 반응하여 대기, 물, 토양 등의 환경에 존재하는 유해 물질을 이산화탄소와 물로 산화 분해하는 기능을 가지고 있으며, 물체의 표면에 코팅될 경우 그 표면에 초친수성을 부여함으로서 자정 능력을 갖도록 하는 물질로서, 그 함량이 10wt%에 미치지 못하면 상기의 효과가 충분치 못하고, 46wt%를 초과하게 되면 제조 단가가 비싸질 뿐 아니라 도료로서의 특성이 떨어지게 된다.The titanium oxide, which is a key component of the aqueous coating of the present invention, is a photocatalyst which receives a light and promotes a chemical reaction. The titanium oxide reacts with ultraviolet rays to convert carbon dioxide and water into harmful substances present in the environment such as air, water, and soil. It has a function of oxidative decomposition, and when coated on the surface of an object, it gives superhydrophilicity to the surface to have self-cleaning ability.If the content is less than 10wt%, the above effect is not sufficient and exceeds 46wt%. This will not only increase the manufacturing cost but also degrade the properties as a paint.
그리고, 상기의 산화티탄은 입경 100nm 이하의 분말이 사용되는 바, 입경이 작을수록 분산도 측면에서 더욱 바람직하며, 100nm를 초과하는 경우에는 도료 내부에서의 분산도가 떨어져 산화티탄에 의한 표면 특성 불균일을 초래할 수 있을 뿐 아니라, 도료층 표면의 평활도를 떨어뜨릴 수 있게 됨으로써 도료층 표면 품질을 떨어뜨리게 된다.In addition, the above-mentioned titanium oxide powder having a particle size of 100 nm or less is used, and the smaller the particle size, the more preferable in terms of dispersion degree. In addition to this, the smoothness of the surface of the paint layer may be reduced, thereby degrading the paint layer surface quality.
수용성 접착제는, 적절한 도막 접착력을 얻기 위한 요소로서, 그 함량이 26wt%에 미치지 못하면 도막 접착력이 부족하게 되어 도막의 내구성이 떨어지게 되며, 35wt%를 초과하게 되면 접착력 향상은 미미하면서 산화티탄 또는 물의 함량을 떨어뜨려 산화티탄에 의한 광촉매 특성 저하를 초래하게 되거나, 조성물 전체의 분산도를 떨어뜨리게 된다.The water-soluble adhesive is an element for obtaining proper coating strength. If the content is less than 26wt%, the coating thickness is insufficient and the durability of the coating becomes poor. When the water content exceeds 35wt%, the adhesion strength is minimal but the content of titanium oxide or water is insignificant. This results in a decrease in the photocatalytic properties due to titanium oxide, or to reduce the dispersion of the entire composition.
상기의 수용성 접착제로는, 수용성 수지, 폴리머 라텍스, 실리콘 수용액 또는 그 들의 복합물이 선택될 수 있는 바, 예를 들면, 아크릴산 에스테르계 라텍스, 에폭시수지계 라텍스, 유기 실리콘을 변성시킨 아크릴산 에스테르계 라텍스, 규소 교질 수용액 등을 들 수 있으며, 이들 중의 하나 또는 그 이상을 혼합하여 사용할 수 있다.As the water-soluble adhesive, a water-soluble resin, a polymer latex, an aqueous solution of silicone or a composite thereof may be selected. For example, an acrylic ester latex, an epoxy resin latex, an acrylic ester latex modified with an organic silicone, silicon Colloidal aqueous solution etc. can be mentioned, One or more of these can be mixed and used.
그리고, 물은 상기 산화티탄과 수용성 접착제에 대한 용제의 역할을 하게 되는 바, 산화티탄과 수용성 접착제를 각각의 함량 범위로 조절한 후 100wt%에 부족한 만큼 혼합된다.Then, water is used as a solvent for the titanium oxide and the water-soluble adhesive bar, after adjusting the titanium oxide and the water-soluble adhesive in each content range is mixed as insufficient in 100wt%.
상기와 같이, 산화티탄, 수용성 접착제 및 물의 3원 성분계로 구성되는 본 발명의 수성도료를 기본 조성으로 하여, 별도의 도료 구성물과 보조제가 추가적으로 첨가될 수 있는 바, 이를 살펴 보면 다음과 같다.As described above, with the aqueous coating of the present invention composed of a three-component system of titanium oxide, a water-soluble adhesive, and water as a basic composition, a separate paint component and an auxiliary agent may be additionally added.
도료 구성물은, 사용 용도에 따라 필요로 되는 도료의 특성을 개선하기 위한 분말상의 성분으로서, 분말의 입도는 작을 수록 좋으며, 가능하면 1200메쉬 이상의 입도가 바람직하고, 태백, 고령토, 산화아연, 탄산칼슘, 탄산규소, 활석, 몬모릴로나이트, 운모, 규소 석회석, 규조토 등 중 하나 또는 2종 이상을 조합하여 사용할 수 있으며, 그 함량은 상기 기본 조성의 3원 성분계 수성도료 100중량부에 대하여 5∼20중량부의 비율로 첨가하는 것이 바람직하다.The paint constituent is a powder component for improving the properties of the paint required according to the intended use. The smaller the particle size of the powder is, the better the particle size of 1200 mesh or more is possible, and Taebaek, Kaolin, Zinc Oxide and Calcium Carbonate. , Silicon carbonate, talc, montmorillonite, mica, silicon limestone, diatomaceous earth, etc. can be used in combination of one or two or more, the content is 5 to 20 parts by weight based on 100 parts by weight of the three-component aqueous coating of the basic composition It is preferable to add in ratio.
이때, 상기 도료 구성물의 첨가량이 5중량부에 미치지 못하면 그 효과를 거의 얻을 수 없으며, 20중량부를 초과하게 되면 물의 상대적인 함량 부족에 의한 각 성분들의 분산도 저하 경향이 나타날 수 있게 된다.At this time, if the addition amount of the paint constituent is less than 5 parts by weight, the effect is hardly obtained, and if it exceeds 20 parts by weight, the dispersion degree of each component may be lowered due to the lack of relative content of water.
그리고, 도료 구성물의 하나로서, 필요에 따라 각종 색상을 얻을 수 있도록 산화철, 톨루엔 아믹, 프탈로시아닌, 울트라마린 등의 수성 착색 안료가 추가 사용될 수도 있으며, 안료를 사용하는 경우, 상기 도료 구성물 함량 범위 내에서 사용되도록 한다.In addition, as one of the paint constituents, an aqueous coloring pigment such as iron oxide, toluene amic, phthalocyanine, and ultramarine may be additionally used to obtain various colors as needed, and in the case of using the pigment, within the paint constituent content range To be used.
또한, 상기와 같이 구성되는 다성분계 조성물은, 제조, 운반, 보관 및 시공 과정에서 다양한 문제가 발생될 수 있기 때문에 분산제, 평활제, 소포제, 증조제, 방부제, 산화방지제, 가소제, pH 조절제, 도막 형성제 등과 같은 별도의 보조제가 적어도 하나 이상 사용될 수 있는 바, 각 보조제의 역할을 살펴 보면 다음과 같다.In addition, the multi-component composition is configured as described above, because a variety of problems can occur during the manufacturing, transport, storage and construction process, dispersant, leveling agent, defoamer, thickener, preservative, antioxidant, plasticizer, pH adjuster, coating film At least one additional adjuvant, such as a forming agent, may be used. Looking at the role of each adjuvant as follows.
분산제는, 수용성 접착제 내에서 분말상의 광촉매제와 도료 구성물을 효과적으로 분산시키는 작용을 하고, 평활제는, 피복된 도료의 표면 평활성을 개선시켜 주며, 소포제는, 도료의 생산, 가공, 사용 중 발생될 수 있는 기포 발생을 방지하여 주게 된다.Dispersants serve to effectively disperse powdery photocatalysts and paint constituents in water-soluble adhesives, smoothers improve surface smoothness of coated paints, and antifoams can be produced during the production, processing and use of paints. It prevents the occurrence of bubbles.
그리고, 증조제는, 도료의 점도를 조절함으로써 도료의 생산, 보관 및 시공과정 중에서 조밀도 증가, 침전 방지, 안정 작용 및 도료의 유변 성능을 개선시켜 주는 작용을 하며, 방부제는, 도료의 보관, 운송 과정 중 부패하거나 변질되는 것 을 방지하여 주고, 산화방지제는, 도료가 산화되는 것을 방지한다.In addition, the thickener adjusts the viscosity of the paint to increase density, prevent precipitation, stabilize and improve the rheological performance of the paint during the production, storage, and construction of the paint. It prevents decay and deterioration during transportation, and antioxidants prevent the paint from oxidizing.
증소제는, 도료의 유연성을 유지시켜 주고, pH 조절제는 도료의 pH를 조절하여 도료 체계의 안정성을 유지하는 역할을 하며, 도막 형성제는, 도막 형성과 함께 동결 방지 기능에 의해 비교적 넓은 온도 범위 내에서 도막이 형성되도록 도와주는 작용을 하게 된다.The thickener maintains the flexibility of the paint, the pH adjuster adjusts the pH of the paint to maintain the stability of the paint system, and the film forming agent has a relatively wide temperature range by a freeze protection function with the film formation. It helps to form a coating film in the inside.
그리고, 상기와 같은 보조제는 필요에 따라 1종 이상이 사용될 수 있으나, 각 보조제의 함량은 상기 기본 조성의 3원 성분계 수성도료 100중량부에 대하여 5wt%를 초과하지 않도록 하는 것이 바람직하며, 그 이상 첨가되는 경우 효과는 일정하면서 제조 원가만이 상승하게 된다.In addition, one or more of the above auxiliary agents may be used as necessary, but the content of each auxiliary agent is preferably not to exceed 5wt% with respect to 100 parts by weight of the three-component aqueous coating of the basic composition, and more When added, the effect is constant while only manufacturing costs rise.
상기와 같은 조성의 본 발명 수성도료의 특성을 다음의 실시예를 통하여 설명하면 다음과 같다.The characteristics of the aqueous coating of the present invention having the above composition will be described through the following examples.
실시예 1Example 1
입경이 10∼80nm 범위의 아나타제형 산화티탄 30wt%와, 수성 접착제로서 아크릴산 에스테르계 라텍스 35wt%와, 물 35wt% 의 혼합물 100중량부에,30 wt% of anatase type titanium oxide in the range of 10 to 80 nm, 35 wt% of acrylic ester latex and 35 wt% of water as an aqueous adhesive,
분말상 도료 구성물로서 탄산칼슘 3중량부와, 활석 2중량부 및3 parts by weight of calcium carbonate, 2 parts by weight of talc and
보조제로서 분산제 1중량부, 소포제 0.3중량부, 증조제 3중량부, 방부제0.2중량부, 습윤제 0.3중량부, 평활제 2중량부, 도막 형성제 2중량부를 혼합하였으며, 전체 조성물의 pH 를 9 로 조절하였다.1 part by weight of dispersant, 0.3 part by weight of antifoam, 3 parts by weight of thickener, 0.2 part by weight of preservative, 0.3 part by weight of wetting agent, 2 parts by weight of leveling agent, and 2 parts by weight of film forming agent were mixed. Adjusted.
실시예2Example 2
입경이 20∼100nm인 아나타제형 산화티탄 10wt%와, 수성 접착제인 폴리비닐 아세테이트 에멀젼 30wt%와, 물 60wt% 의 혼합물 100중량부에,10 wt% of anatase titanium oxide having a particle diameter of 20 to 100 nm, 30 wt% of a polyvinyl acetate emulsion as an aqueous adhesive, and 100 wt% of a mixture of 60 wt% of water,
분말상 도료 구성물로서 태백분 7.5중량부와, 탄산칼슘 8중량부와, 활석 3중량부 및 몬모릴로나이트 3중량부 및7.5 parts by weight of Taebaek powder, 8 parts by weight of calcium carbonate, 3 parts by weight of talc, 3 parts by weight of montmorillonite, and the like
보조제로서 분산제 0.6중량부, 소포제 0.3중량부, 증조제 0.3중량부, 방부제0.2중량부, 습윤제 0.3중량부, 평활제 1중량부, 도막 형성제 2중량부를 혼합하였으며, 전체 조성물의 pH 를 9 로 조절하였다.0.6 parts by weight of a dispersant, 0.3 parts by weight of an antifoaming agent, 0.3 parts by weight of a thickener, 0.2 parts by weight of a preservative, 0.3 parts by weight of a wetting agent, 1 part by weight of a leveling agent, and 2 parts by weight of a film-forming agent were mixed. Adjusted.
실시예 3Example 3
입경이 5∼60nm인 아나타제형 산화티탄 46wt%와, 수성 접착제인 유기 실리콘 변성 아크릴산 에스테르계 라텍스 32wt%와, 물 24wt% 의 혼합물 100중량부에,46 wt% of anatase titanium oxide having a particle diameter of 5 to 60 nm, 32 wt% of an organic silicone-modified acrylic ester latex as an aqueous adhesive, and 100 wt% of a mixture of 24 wt% of water,
분말상 도료 구성물로서 규조토 1중량부 및1 part by weight of diatomaceous earth as a powder paint composition and
보조제로서 분산제 1중량부, 소포제 0.3중량부, 증조제 0.3중량부, 방부제0.2중량부, 습윤제 0.3중량부, 평활제 1중량부, 도막 형성제 2중량부를 혼합하였으며, 전체 조성물의 pH 를 9 로 조절하였다.1 part by weight of dispersant, 0.3 part by weight of antifoam, 0.3 part by weight of thickener, 0.2 part by weight of preservative, 0.3 part by weight of wetting agent, 1 part by weight of leveling agent, and 2 parts by weight of film forming agent were mixed. Adjusted.
실시예 4Example 4
입경이 20∼100nm인 아나타제형 산화티탄 29wt%와, 수성 접착제인 에폭시수지계 라텍스 26wt%와, 물 45wt% 를 혼합하였다.29 wt% of anatase titanium oxide having a particle diameter of 20 to 100 nm, 26 wt% of an epoxy resin latex as an aqueous adhesive, and 45 wt% of water were mixed.
상기의 실시예 1 내지 4 와 조성된 본 발명의 수성도료와 일반 수성도료를 사용하여 비교한 결과, 도색 시공 초기 단계의 표면 품질은 서로 비슷하였으나, 도색된 각 도료층 표면에 기름과 먼지를 섞어 인위적으로 부착시킨 기름때의 경우 본 발명의 수성도료층 표면은 햇빛의 자외선 또는 인위적인 자외선에에 의한 산화티탄의 광촉매작용으로 자연적인 비바람이나 인공적인 간단한 물세척으로 세척이 가능하였던 반면에, 일반 수성도료층 표면은 별도의 세척제를 사용하야야만 하였다.As a result of using the water-based paints and general water-based paints of the present invention prepared with Examples 1 to 4 above, the surface quality of the initial stages of painting was similar, but oil and dust were mixed on the surface of each painted layer. In the case of artificially adhering oil, the surface of the aqueous coating layer of the present invention was cleaned by natural weather or artificial simple water washing due to the photocatalytic action of titanium oxide caused by ultraviolet or artificial ultraviolet rays of sunlight. The layer surface had to use a separate cleaning agent.
그리고, 음식물 찌꺼기를 부착한 결과, 일반 수성도료층 표면에서는 부패가 진행되었으나, 본 발명의 수성도료층 표면에서는 그러한 현상이 발생되지 않았다.And, as a result of adhering food waste, decay progressed on the surface of the general aqueous coating layer, but such a phenomenon did not occur on the surface of the aqueous coating layer of the present invention.
이상에서 살펴본 바와 같이, 본 발명의 수성도료는 일반 수성도료와 대등한 수준의 초기 도장 표면 품질을 가지고 있으면서, 자기 청결 및 곰팡이 방지 기능을 가지고 있기 때문에 도장 주기를 연장하여 재도장에 따른 비용 절감을 꾀할 수 있으며, 특히, 자기 청결 기능으로 주방의 환경 개선 및 청결 관리를 손쉽게 하여 준다.As described above, the water-based paint of the present invention has a level of initial paint surface comparable to that of the general water-based paint, and has a self-cleaning and mildew prevention function, thereby reducing the cost of repainting by extending the coating cycle. In particular, the self-cleaning function facilitates the improvement of the kitchen environment and the cleanliness of the kitchen.
그리고, 곰팡이 방지 기능과 함께 벽면에 접촉된 공기 중의 각종 유기 기체 및 NOx, CO, SO2 등의 유기 물질을 분해, 제거하여 주기 때문에, 아파트와 같은 대형 건축물의 실내 환경 정화는 물로느 그러한 건축물 주변의 대기의 정화에도 상당한 도움이 될 수 있을 것으로 기대된다.In addition, since it decomposes and removes various organic gases such as NOx, CO, and SO 2 in the air in contact with the wall with a fungus prevention function, the indoor environment purification of a large building such as an apartment is performed by water. It is expected to be of great help to clean up the atmosphere.
Claims (6)