KR20060060938A - Method for manufacturing a finishing materials for indoor and finishing materials manufactured according to the method - Google Patents

Abstract

Disclosed are a method for producing a finish for interior walls having a natural marble appearance and a finish produced thereby. The stone layer is mixed with the aqueous paint of the first color and fine stone particles to cover the surface of the base plate. The marble particle layer is mixed with a water-based paint of the first color, an aqueous paint of the second color, marble particles coarse than the stone particles of the first layer, and a handy coat to sand the surface while exposing a part of the stone powder layer. The gloss layer covers the granite layer and the marble particle layer. Accordingly, after the coating and stirring with water-based paint of the color desired to obtain stone powder, marble particles, handy coat, etc. on the plate, it is possible to manufacture the interior wall finish through the pressing, sanding, polishing process.

Finishing, Wall Finishing, Wood, Marble, Stone, Sanding

Description

METHOD FOR MANUFACTURING A FINISHING MATERIALS FOR INDOOR AND FINISHING MATERIALS MANUFACTURED ACCORDING TO THE METHOD}

1 is a cross-sectional view for explaining the interior wall finishing material according to an embodiment of the present invention.

2A to 2I are cross-sectional views illustrating a method of manufacturing a finishing material for an interior wall having a natural marble appearance according to an embodiment of the present invention.

<Description of the symbols for the main parts of the drawings>

105: base plate 110: stone layer

120: marble particle layer 130: gloss layer

104: blown

The present invention relates to a method for producing a finish and a finish produced thereby, and more particularly, to a method for producing a finish for interior walls having a natural marble appearance and a finish produced thereby.

In general, as a commercial floor or wall finishing material of the building, it is mainly used to polish or pattern by grinding marble or vinyl chloride tiles. In recent years, the use of granite or marble has become commonplace in major commercial buildings such as department stores, office buildings, and large general shopping malls due to the improvement of living standards and the advancement of building materials.

However, these stone products are excellent in durability, but the price is expensive, and since most of them have to rely on imports, development of alternatives considering the price and practical aspects is increasingly required.

On the other hand, to date, high-quality finishes such as natural marble, artificial marble, tiles, and the like can be constructed only by skilled workers, and because of limited size and heavy weight, there were limitations in design with cutting, processing, construction, and technical difficulties.

Therefore, the technical problem of the present invention has been made in view of this point, an object of the present invention is to provide a method of manufacturing a finishing material for interior walls having a natural marble appearance for lighter and lighter in size, and to overcome the limitations of the design.

Another object of the present invention is to provide a finish produced by the above-described method for manufacturing the finish.

In order to realize the above object of the present invention, the interior wall finishing material manufacturing method according to one embodiment, (a) a first mixture of a water-based paint of the desired color to be obtained on the plate, the fine particles of stone and water and stirred with Thick coating to form a first layer; (b) the second layer is applied by intermittently applying a second mixture of agitated marble particles, handy coat, water paint, and water to express different colors and appearance on the resultant of step (b). Forming; (c) tightly applying a third mixture of the marble particles, the handy coat, the water-based paint and water on the resultant of step (b), to form a third layer; (d) placing and pressing the pressing plate on the resultant of step (c); (e) drying the resultant of step (d) for a predetermined time; (f) sanding the dried resultant surface; And (g) applying gloss to the surface of the resultant product by step (f).

It is preferable that the said board | plate material is either MDF and plywood. The stone powder layer is preferably less than 0.5mm in thickness. The stone layer is preferably in an amount of 1 liter per 3.24m ² . It is preferable that the stone powder layer uses a mechanism with an air gun. The second layer is preferably in an amount of 0.5 liter per 3.24m ² . The second layer is preferably formed by a mechanism with an air gun to which the coarse particles are boomed. The third layer is preferably in an amount of 1.5 liters per 3.24m ² . The third layer is preferably performed by a mechanism with an air gun to which the coarse particles are boomed. The pressing plate preferably has a quadrilateral shape of 45kg weight per 3.24m ² . The drying step is preferably dried for 24 hours at a temperature of 15 to 25 degrees Celsius.

It is preferable that the high speed dust collector is attached to the sanding machine. The first thickness is preferably about 1mm. The sanding machine is preferably attached to the cc-150cw paper.

The polishing step is a mixture of 50g marble coat of 3.24m ² marble 250g and 250l of water to apply on the sanding finish surface using a device with an air gun for lacquer coating, after a certain time, cc- It is preferred to include sanding with 1000 cw of paper.

The glossing step is preferably a step of uniformly applying on the surface of the sanding finish using a mechanism to which 0.1l transparent lacquer and 0.2l lacquer thinner per 3.24m ² is attached to the air gun for lacquer coating.

The polishing step is a mixture of 20 g of desired gold, silver, copper powder and 0.3 l of transparent lacquer and 0.6 l of lacquer thinner per 3.24 m ² on the sanded surface using a device equipped with a lacquer air gun. It is preferable that it is a step of applying.

In order to realize the above object of the present invention, the interior wall finishing material according to an embodiment includes a base plate, a stone layer, a marble particle layer, and a glossy layer. The stone powder layer is mixed with an aqueous paint of a first color and fine stone particles to cover the surface of the base plate. The marble particle layer is a water-based paint of the first color, a water-based paint of the second color, marble particles coarse than the stone particles of the first layer, and a handy coat are mixed to expose a part of the stone layer while sanding the surface. Is processed. The gloss layer covers the stone powder layer and the marble particle layer.

Here, the marble particle layer preferably exposes approximately 10% of the entire plane of the stone powder layer when viewed in a plane. The gloss layer is characterized in that the surface is a sand polished marble polish. The gloss layer is another feature of the transparent lacquer layer. The gloss layer is another feature of the lacquer layer that traps one of gold, silver and copper.

According to the method of manufacturing a finishing material for the interior wall and the finished material produced by the same, it is applied by stirring and applying water-based paint of a color desired to obtain stone powder, marble particles, and a handy coat on a sheet of MDF or plywood, and then pressing and sanding. By manufacturing the finishing material through the polishing process, it can be easily cut into a wood saw with the appearance and texture of marble and stone.

Hereinafter, with reference to the accompanying drawings, it will be described in detail the present invention.

1 is a cross-sectional view for explaining the interior wall finishing material according to an embodiment of the present invention.

Referring to Figure 1, the interior wall finish according to an embodiment of the present invention includes a base plate 105, a stone powder layer 110, a marble particle layer 120 and a gloss layer 130.

The stone powder layer 110 is mixed with the water-based paint of the first color and the fine stone particles to cover the surface of the base plate (110).

The marble particle layer 120 may include an aqueous paint of the first color, an aqueous paint of a second color different from the first color, marble particles thicker than the stone particles of the stone powder layer 110, and a handy coat (cotton). Treatment material) is mixed and the surface is sanded while exposing a part of the stone powder layer 110. The stone powder layer 110 exposed while the marble particle layer 120 is not formed is formed to be minutely bumpy, which may represent a natural texture of the stone. In addition, the stone layer 110 having a relatively low height is a region in which a scatter is shot and attached to the wall at the construction of the wall.

The gloss layer 130 covers the marble powder layer 110 and covers the marble particle layer 120 exposed by the stone powder layer 110. Of course, the gloss layer 130 may be omitted.

According to the interior wall finishing material, it is possible to express the marble or stone in the appearance and texture because the water paints of various colors are formed by stirring the powder, marble particles and handy coat, etc. on the base plate, and through the wood saw It can be easily cut so that it can be cut and constructed according to the desired design at the construction site.

In addition, since the base plate is used, the weight is lighter than that of marble or stone, and the marble or stone can be expressed at a lower cost.

In addition, the stone powder layer or the marble particle layer formed on the base plate is a non-combustible material, so that even if an accident such as a fire occurs, the fire may be prevented from expanding through the wall. In addition, it is obvious that the use of the non-flammable material of the gloss layer can prevent the expansion of the fire more efficiently.

Then, a series of manufacturing processes for obtaining the interior wall finishing material according to an embodiment of the present invention will be described in detail with reference to the drawings to be described later.

2A to 2I are cross-sectional views illustrating a method of manufacturing a finishing material for an interior wall having a natural marble appearance according to an embodiment of the present invention.

Referring to FIG. 2A, dirt or contaminants on the surface of the base plate 105 such as MDF or plywood are removed by using a brush or blower 104 or the like. The size and thickness of the MDF or plywood is preferably determined by the size and thickness available in the market, and the specifications can be produced differently according to separate orders and needs. In the drawings, while conveying while supporting the base plate 105 through the roller, it is possible to remove the dust or contaminants while conveying the blower 104.

Next, as shown in FIG. 2B, the air gun attaches the first mixture 108 to which the first color of water-based paint and fine particles of stone powder are stirred with water, as shown in FIG. 2B. It is uniformly applied using the prepared mechanism 109 to form the stone powder layer 110. The stone powder layer 110 is applied thickly so that the lower plate color is not visible in an amount of 1 liter per 3.24 m ² so as to have a thickness of less than 1 mm. In the drawings, while the base plate 105 is supported using a roller, the first coating operation is carried out while being transported. However, the first coating operation may be performed while the mechanism 109 to which the air gun is attached is transferred. have.

Subsequently, as shown in FIG. 2C, the marble particles, the handy coat, and the water-based paint are watered to express a color and appearance different from the color of the stone layer 110 as the second coating operation on the resultant product of FIG. 2B. After stirring to form a second mixture 118 of a desired color, using a mechanism 119 attached to the air gun boom to coarse particles, the amount of 0.5 liter per 3.24m ² is intermittently boom applied to the second mixture layer ( 121). The second mixture layer 121 is preferably boomed so that the area where the stone powder layer 110 is exposed is approximately 20% on a plane. Although the drawing shows that the secondary coating operation is carried out by supporting and transporting the base plate 105 using a roller, the secondary coating operation may be performed while transferring the mechanism 119 to which the air gun is attached. have. The size of the second mixture layer 121 to be applied to the boom is formed in various ways, such as 5mm to 20cm.

Subsequently, as shown in FIG. 2D, the marble particles, the handy coat, and the aqueous paint are agitated with water to form a third mixture 127 of a desired color as shown in FIG. 2D. The third mixture layer 123 is tightly covered to cover the exposed powder layer 110 and the applied second mixture layer 121 in an amount of 1.5 liter per 3.24 m ² using the air gun attached device 128. Apply. In the drawings, while carrying out the third coating operation by transporting while supporting the base plate 105 using a roller, the third coating operation may be performed while transferring the mechanism 129 to which the air gun is attached. have.

Next, as shown in FIG. 2E, the flat pressing plate 129 weighing 45 kg per 3.24 m ² is applied evenly to the plane of the resultant, as shown in FIG. 2D. Accordingly, the fourth mixture in which the second mixture layer 121 of the resultant according to FIG. 1C applied to the bottom and the third mixture layer 123 of the resultant according to FIG. 1D applied to the top are mixed with each other to express natural color and texture. Layer 125 is formed.

The coating layer that does not touch the pressing plate 129, that is, the stone powder layer 110 of the resultant according to FIG. 1B remains as a finely bumpy coating layer, which is a natural texture expression of the stone, and a silkta during wall construction at the construction site. It is an important manufacturing process that hides traces when tackers are attached. In the drawings, the second mixture layer 121 and the third mixture layer 123 are mixed with each other by using the pressing plate 129 to form the fourth mixture layer 125, but a member such as a roller It is also possible to perform the above mixing process using.

Subsequently, as shown in FIG. 2F, the resultant of FIG. 2E is provided to the heating chamber 140 to be dried. It is preferable that the heating chamber 140 is provided with a plurality of dry items. Of course, it can also naturally dry at a temperature of 15-25 degreeC for 24 hours. In a situation where the drying process is not suitable, such as winter, it is preferable to dry using a separate hot air fan.

Subsequently, as shown in FIG. 2G, the resultant dried by FIG. 2F is attached to the circular sanding machine 150 to which the high speed dust collector is attached, thereby attaching cc-150cw paper to a thickness of about 1 mm on the stone layer 110. Sanding process The reason for sanding to a thickness of about 1 mm is to minimize the occurrence of cracks when showing the curved surface without damaging the saw blade for woodworking during the construction of the interior wall finish according to the present invention.

Then, as shown in FIG. 2h, a fourth mixture 151, in which 50 g of marble coats and marbles of 250 l of 3.24 m ² of marble polish, was mixed on the sanded surface to give gloss to the resultant of FIG. 2 g. The fourth mixture layer 130 is applied through a mechanism 153 to which an air gun for lacquer coating is attached.

Subsequently, as shown in FIG. 2I, when the time period of 4 to 5 minutes has elapsed and the fourth mixture layer 130 is cured, a paper wall of cc-1000cw is attached to the sanding machine 160 and sanded. Gives a finish to the dragon finish.

In the above, the sanding treatment was applied after applying the mixture including the marble polish to give the gloss. However, it is obvious that the gloss may be provided through various methods in order to increase the diversity of the interior wall finishing product.

As an example, 0.1l transparent lacquer and 0.2l lacquer thinner per 3.24m ² are mixed on the sanded surface by the process shown in FIG. It is a way to give gloss in a way.

As another example, one of 20 g of desired gold, silver and copper powder per 3.24 m ² on a surface sanded by the process shown in FIG. 2 g to obtain luxurious gold, silver and copper colors in a natural stone texture. The transparent lacquer and the 0.6 l lacquer thinner may be mixed and applied using a mechanism equipped with an air gun for lacquer coating.

As described above, according to the present invention, the stone powder, marble particles, handy coat, water-based paint and the like are stirred with water and coated on a base plate such as MDF or plywood, and then pressed, sanded, and polished. It is possible to produce a finishing material for interior walls having the appearance and texture of natural marble and stone. Accordingly, while exhibiting the luxurious appearance and texture of natural marble or stone, it is possible to finish the construction to the flat or curved surface without being limited by the specification and thickness of the product as intended by the designer and the site builder of the building.

In addition, in the construction site, two processes can be constructed in one process, so the air can be shortened, and by using the production line through mechanization, mass production is possible, and the finishing materials can be supplied to the consumer at a lower price. .

In addition, the stone powder layer or the marble particle layer formed on the base plate is a non-combustible material, so that even if an accident such as a fire occurs, the fire may be prevented from expanding through the wall.

Although described above with reference to the embodiments, those skilled in the art can be variously modified and changed within the scope of the invention without departing from the spirit and scope of the invention described in the claims below. I can understand.

Claims (23)

(a) thickly applying a water-based paint of a desired color on the plate and a first mixture stirred with fine powder of stone and water to form a stone layer; (b) the second layer is applied by intermittently applying a second mixture of agitated marble particles, handy coat, water paint, and water to express different colors and appearance on the resultant of step (b). Forming; (c) tightly applying a third mixture of the marble particles, the handy coat, the water-based paint and water on the resultant of step (b), to form a third layer; (d) placing and pressing the pressing plate on the resultant of step (c); About 10% spread, (e) drying the resultant of step (d) for a predetermined time; (f) sanding the dried resultant surface; And (g) a method of manufacturing the interior wall finishing material comprising the step of giving gloss to the surface of the resultant by the step (f). The method of claim 1, wherein the plate is any one of MDF and plywood. The method of claim 1, wherein the stone layer is less than 0.5mm in thickness, the production method of the interior wall finishing material. The method of claim 1, wherein the stone layer is an amount of 1 liter per 3.24m ² manufacturing method for the interior wall finish. The method of claim 1, wherein the stone layer is a method of manufacturing a wall finishing material for the interior wall, characterized in that using a mechanism with an air gun attached. The method of claim 1, wherein the second layer is present in an amount of 0.5 liters per 3.24m ² . The method of claim 1, wherein the second layer is formed by a mechanism with an air gun attached to which the coarse particles are boomed. The method of claim 1, wherein the third layer is present in an amount of 1.5 liters per 3.24 m ² . The method according to claim 1, wherein the third layer is performed by a device equipped with an air gun to which coarse particles are to be sprayed. The method of claim 1, wherein the pressing plate is a manufacturing method for the interior wall finishing material, characterized in that the quadrilateral flat shape weighing 45kg per 3.24m ² . The method of claim 1, wherein the drying is performed for 24 hours at a temperature of 15 to 25 degrees Celsius. The method of claim 1, wherein the sanding machine is a high-speed dust collector is attached. The method of claim 1, wherein the first thickness is about 1 mm. The method of claim 1, wherein the sanding machine is a cc-150cw paper attached to the manufacturing method of the interior wall finishing material. The method of claim 1, wherein the polishing is, Mixing 50 g of marble coat of 3.24 m ² marble coat with 250 l of water and applying onto a sanded surface using an apparatus equipped with a lacquer air gun; And After a certain time, the manufacturing method of the interior wall finishing material comprising the step of sanding using a paper of cc-1000cw. The method of claim 1, wherein the polishing is, Production of a finishing material for interior walls, characterized in that the step of uniformly applying on the surface of the sanded finish using a mechanism equipped with a lacquer air gun for mixing 0.1l transparent lacquer and 0.2l lacquer thinner per 3.24m ² Way. The method of claim 1, wherein the polishing is, Applying a mixture of 20 g of desired gold, silver, copper powder, and 0.3 l of transparent lacquer and 0.6 l of lacca thinner per 3.24 m ² onto the sanded surface using a device equipped with an air gun for lacquer coating. A method for producing a finishing material for interior walls, characterized in that. An interior wall finish produced by the method of claim 1. Base plate; A stone powder layer of the first color aqueous paint and fine stone particles mixed to cover the surface of the base plate; A marble particle layer whose surface is sanded while exposing a portion of the stone layer by mixing the water-based paint of the first color, the water-based paint of the second color, coarse marble particles than the stone particles of the stone powder layer, and a handy coat; And Finishing material for an interior wall comprising a polished layer covering the stone powder layer and the marble particle layer. 20. The interior wall finish of claim 19, wherein the marble particle layer exposes approximately 10% of the entire plane of the stone powder layer when viewed in a plane. 20. The interior wall finishing material according to claim 19, wherein the polish layer is a sand polished marble polish. The interior wall finishing material according to claim 19, wherein the gloss layer is a transparent lacquer layer. 20. The interior wall finishing material according to claim 19, wherein the gloss layer is a lacquer layer for trapping one of gold, silver and copper.