KR20050000627A - Method for heat treatment in gasnitriding - Google Patents
Method for heat treatment in gasnitriding Download PDFInfo
- Publication number
- KR20050000627A KR20050000627A KR1020030041091A KR20030041091A KR20050000627A KR 20050000627 A KR20050000627 A KR 20050000627A KR 1020030041091 A KR1020030041091 A KR 1020030041091A KR 20030041091 A KR20030041091 A KR 20030041091A KR 20050000627 A KR20050000627 A KR 20050000627A
- Authority
- KR
- South Korea
- Prior art keywords
- nitriding
- heat treatment
- metal products
- heat
- gas
- Prior art date
Abstract
Description
본 발명은 가스질화의 열처리 방법에 관한 것으로서, 상세하게는 철강 제품의 표면을 경화함에 있어 추가적인 설비의 증설 없이 양산시 안정적인 품질과 생산성을 유지할 수 있는 가스질화의 열처리 방법에 관한 것이다.The present invention relates to a heat treatment method of gas nitriding, and more particularly, to a heat treatment method of gas nitriding that can maintain stable quality and productivity during mass production without additional equipment in hardening the surface of steel products.
통상적으로 철강의 표면경화법에는 강 표면의 화학성분을 변화시켜 경화하는화학적 표면경화법과 강 표면의 화학성분을 변화시키지 않고 담금질만으로 경화하는 물리적 표면경화법이 있다. 전자의 경우에는 침탄, 질화, 침황, 침붕 등이 있으며, 후자의 경우에는 유도가열 담금질, 화염 담금질 등이 있다.In general, there are chemical surface hardening methods for hardening by changing the chemical composition of the steel surface and physical surface hardening method for hardening only by quenching without changing the chemical composition of the steel surface. In the former case, there are carburizing, nitriding, nitriding, and cupping. In the latter case, there are induction heating quenching and flame quenching.
이때 질화에 의한 표면열처리는 최초 염욕질화로부터 가스질화, 진공가스질화, 플라즈마 질화로 발전되어 왔다. 염욕질화의 경우에는 오염물질의 처리가 수반되고, 표면에 다공의 백색층으로 인하여 수명증가에 한계가 있다. 그리고 가스질화는 금속표면에 질소를 침투시켜서 표면을 경화하는 공법으로 높은 표면경도, 내마모성, 흠집에 대한 저항성(antigalling), 피로수명증진, 내식성(스테인레스의 경우는 예외), 내열성, 열에 의한 표면연화 저항성 등을 얻을 수 있다.At this time, the surface heat treatment by nitriding has been developed from the initial salt bath nitriding to gas nitriding, vacuum gas nitriding, and plasma nitriding. In case of salt bath nitriding, treatment of contaminants is involved, and life expectancy is limited due to the porous white layer on the surface. In addition, gas nitriding is a method of hardening the surface by infiltrating nitrogen into the metal surface, which has high surface hardness, abrasion resistance, antigalling resistance, fatigue life, corrosion resistance (except in the case of stainless steel), heat resistance, heat softening by heat. Resistance and the like can be obtained.
특히 가스질화 공법에는 체적변화가 수반되는 담금질이 없고, 상대적으로 낮은 처리온도가 적용되기 때문에 침탄 또는 기타의 일반적인 경화에 비해 조직변형이 적어 양산함에 있어 안정적인 품질을 유지하기에는 적절한 방식이다. 다만, 가스질화에 있어서도 표면에 15㎛ 이상의 백색층이 형성되므로 이에 따른 금형의 표면박리 등의 문제를 처리하기 위한 방안이 필요하다. 물론, 이를 위해 과도한 설비의 증설이 수반되거나 양산에 제한이 있어서는 곤란하므로 이러한 제한을 극복하는 가스질화의 열처리방밥이 절실한 실정이나 아직까지는 이에 대한 대책이 거의 없는 것이 작금의 현실이다.In particular, the gas nitriding method has no volumetric quenching, and relatively low treatment temperature is applied, which is less suitable for carburizing or other general hardening, and thus is suitable for maintaining stable quality in mass production. However, even in gas nitriding, since a white layer having a thickness of 15 μm or more is formed on the surface, a method for dealing with problems such as surface peeling of the mold is required. Of course, it is difficult for this to be accompanied by excessive expansion of equipment or limitation in mass production, so the heat treatment of gaseous nitriding that overcomes these limitations is urgently needed, but there are few measures for this.
따라서 본 발명은 상기한 점에 착안하여 안출한 것으로서, 보다 구체적으로는 가스질화로 철강 제품의 표면을 경화함에 있어 추가적인 설비의 증설 없이 공정제어만으로 양산시 안정적인 품질과 생산성을 유지할 수 있는 가스질화의 열처리 방법을 제공하는 것을 그 목적으로 한다.Therefore, the present invention has been made in view of the above point, and more specifically, in the hardening of the surface of steel products by gas nitriding, the gas nitrification heat treatment method which can maintain stable quality and productivity during mass production only by process control without additional equipment. To provide that purpose.
도 1은 질화처리과정의 일단을 보여주는 예시도,1 is an exemplary view showing one end of a nitriding treatment process;
도 2는 종래의 공정을 간략하게 나타내는 도표,2 is a diagram briefly showing a conventional process,
도 3은 종래의 공정에 의한 제품조직의 확대사진,Figure 3 is an enlarged photograph of the product structure by the conventional process,
도 4는 종래의 공정에 따른 경도변화를 나타내는 그래프,4 is a graph showing a change in hardness according to a conventional process,
도 5는 본 발명의 공정을 간략하게 나타내는 도표,5 is a diagram briefly showing a process of the present invention;
도 6은 본 발명의 공정에 따른 경도변화를 나타내는 그래프,6 is a graph showing the change in hardness according to the process of the present invention,
도 7은 본 발명의 공정에 의한 제품조직의 확대사진.Figure 7 is an enlarged photograph of the product structure by the process of the present invention.
* 도면의 주요 부분에 대한 부호 설명 *Explanation of symbols on the main parts of the drawings
W: 백선층 N: 질화층W: ringworm layer N: nitride layer
이러한 목적을 달성하기 위해 본 발명은 금속제품을 가스질화하는 방법에 있어서, 소정의 온도를 유지한 상태로 제1설정시간 동안 열처리하는 제1단계와, 상기 제1단계보다 승온한 상태로 제2설정시간 동안 열처리하는 제2단계와, 서냉하면서 약 120℃ 내외의 온도범위에서 금속제품을 장출하는 제3단계를 거치도록 함을 특징으로 한다.In order to achieve the above object, the present invention provides a method of gas-nitriding a metal product, comprising: a first step of heat treatment for a first predetermined time while maintaining a predetermined temperature; And a third step of heat-treating for a predetermined time and a third step of unloading the metal product in a temperature range of about 120 ° C. while slow cooling.
이때, 상기 제1단계는 약 510℃내외의 온도를 유지한 상태로 약 30시간 동안 열처리하고, 상기 제2단계는 약 530℃내외의 온도를 유지한 상태로 약 52시간 동안 열처리한다.In this case, the first step is heat treated for about 30 hours while maintaining a temperature of about 510 ℃, and the second step is heat treated for about 52 hours while maintaining a temperature of about 530 ℃.
이하, 첨부된 도면을 참조하여 본 발명에 따른 바람직한 실시예를 상세하게 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 1에 나타내는 바와 같이 통상의 가스질화 공정은 금속제품을 질화통에 넣고 질소가스 분위기에서 열처리를 수행한다. 그리고 도 2처럼 NH3가스는 금속의 A1변태점(723℃) 이하의 온도인 500~550℃에서 2NH3←3H2+ 2N 과 같이 해리되고, 이때 발생된 발생기 질소(N)가 금속표면의 미소성분인 Al, Cr, Mo, Ti 등과 화합하여 Al-N, Cr-N등과 같은 질화물을 만든다. 이와 같이 가스질화 공정은 고경도의 표면을 얻기 위한 별도의 소입(燒入) 공정을 필요로 하지 않으며, 특히 낮은 온도에서처리되므로 변형이 적어 정밀도를 유지해야 하는 제품에 적합한 표면경화법이다.As shown in FIG. 1, in a typical gas nitriding process, a metal product is placed in a nitriding tank and heat treated in a nitrogen gas atmosphere. And NH 3 gas is dissociated as 2NH 3 ← 3H 2 + 2N at 500 ~ 550 ℃, the temperature below the metal A 1 transformation point (723 ℃) as shown in Figure 2 , the generator nitrogen (N) generated at this time is Nitrides such as Al-N, Cr-N, etc. are made by combining with Al, Cr, Mo, Ti, and the like. As such, the gas nitriding process does not require a separate quenching process to obtain a hard surface, and is a surface hardening method suitable for a product that needs to maintain precision due to low deformation since it is processed at a low temperature.
다만, 상기한 가스질화 공정은 도 3의 확대사진(배율 500배)처럼 질화층(N)과 백선층(W)이 필연적으로 생기는데, 이 때 종래의 기술편에서 설명한 바와 같이 백선층(W)의 박리문제를 해결하는 것이 무엇보다 중요하다. 즉, 상기한 백선층(W)에는 질소가스의 확산(탈락)으로 인한 기공이 많이 분포되어 있는데, 제품의 특성에 따라 백선층(화합물층)이 필요하기도 하지만 거의 대부분의 경우에는 연속공정에서 연마가공해서 절삭하는 후속공정이 수반되어야 한다. 더욱이 유압 펌핑유니트의 플란저와 같이 고압의 조건하에서 작동을 하는 부품의 표면에 백선층(W)이 두텁게 존재할 경우에는 백선층(W)에 존재하는 수많은 기공 때문에 크랙이 발생할 우려가 많아 성장 및 소착, 탈락 등의 원인이 될 가능성이 크다. 이럴 때 시멘타이트 조직인 백선층(w)의 강도가 너무 높아서 가공비가 과다하게 소요되는 점을 개선하는 것이 본 발명의 과제라 할 수 있다.However, in the gas nitridation process, the nitride layer N and the white wire layer W inevitably occur as shown in the enlarged photograph (500 times magnification) of FIG. 3, at which time the white wire layer W as described in the related art. It is important to solve the problem of peeling. In other words, the white wire layer (W) has a lot of pores due to the diffusion (falling) of nitrogen gas, depending on the characteristics of the product may require a white wire layer (compound layer), but in most cases grinding process in a continuous process This is followed by a subsequent process of cutting. Furthermore, if thick white wire layer (W) is present on the surface of a component operating under high pressure conditions, such as a plunger of a hydraulic pumping unit, there is a risk of cracks due to numerous pores in the white wire layer (W). It is likely to cause dropouts. In this case, it is a problem of the present invention to improve the point that the strength of the white wire layer (w), which is a cementite structure, is excessively high so that the processing cost is excessively required.
본 발명에 따르면, 소정의 온도를 유지한 상태로 제1설정시간 동안 열처리하는 제1단계와, 상기 제1단계보다 승온한 상태로 제2설정시간 동안 열처리하는 제2단계와, 서냉하면서 약 120℃ 내외의 온도범위에서 금속제품을 장출하는 제3단계를 구비한다. 그런데 펌프의 핵심부라고 할 수 있는 플란저(plunger) 부품을 질화처리하는 종래의 경우를 보면, 도 2와 같은 1단의 질화공정을 적용하는 결과를 보여 주고 있다. 즉, 플란저(plunger) 부품을 질화처리하는 종래의 경우를 보면, 도 3처럼 질화층(N)의 깊이가 0.39mm인 반면, 화합물층인 백선층(W)의 깊이가 17~18㎛로 나타나는데, 참고적으로 플란저의 표면으로부터의 깊이 변화에 따른 경도를 수치적으로 표기하면 표 1 및 도 4와 같다.According to the present invention, a first step of heat-treating for a first predetermined time while maintaining a predetermined temperature, a second step of heat-treating for a second predetermined time with a temperature higher than the first step, and about 120 while slowly cooling And a third step of discharging the metal product in the temperature range of about ℃. However, the conventional case of nitriding a plunger part, which is a core part of a pump, shows a result of applying a nitriding process of one stage as shown in FIG. That is, in the conventional case of nitriding a plunger part, as shown in FIG. 3, the depth of the nitride layer N is 0.39 mm, while the depth of the white wire layer W, which is a compound layer, is 17-18 μm. For reference, the hardness according to the change in depth from the surface of the plunger is numerically expressed as Table 1 and FIG. 4.
한편, 본 발명은 종래의 질화처리공정을 보다 구체적으로 구분하여 처리하되, 제1단계의 공정에서는 약 510℃ 내외의 온도를 유지한 상태로 30시간 동안 열처리하고, 제2단계의 공정에서는 약 530℃ 내외의 온도를 유지한 상태로 52시간 동안 열처리한다. 따라서 본 발명에는 종전과 동일하게 제작된 플란저의 금속제품을 도 5와 같은 2단질화 공정으로 열처리함을 주된 특징으로 삼는다. 그리고 상기한 바와 같이 약 510℃~530℃ 내외의 온도범위에서 2단계 형태로 질화처리를 행함에 있어서 Al+Ni 혼합 기체가스와 암모니아(NH3)를 종래와 동일한 비율로 혼합한 기체가스를 질화통 내부로 투입하면서 열처리를 행하게 된다. 그런 다음, 적절한 냉각을 거치되, 약 120℃ 내외의 온도범위에서 제품을 장출하는 점은 종래와 동일하다.In the present invention, the conventional nitriding treatment process is classified in more detail, but the heat treatment is performed for 30 hours while maintaining the temperature of about 510 ° C. in the first step, and about 530 in the second step. Heat treatment for 52 hours while maintaining a temperature of about ℃. Therefore, the main feature of the present invention is to heat-treat the metal product of the plunger manufactured in the same manner as before in the two-stage nitriding process as shown in FIG. As described above, in performing the nitriding treatment in the form of two stages in the temperature range of about 510 ° C. to 530 ° C., the gaseous mixture of Al + Ni mixed gas gas and ammonia (NH 3) in the same ratio as in the prior art The heat treatment is performed while feeding into the inside. Then, through appropriate cooling, the point of loading the product in the temperature range of about 120 ℃ is the same as the conventional.
이와 같은 본 발명의 2단계 열처리는 진공설비 등의 추가적인 설비 없이 열풍장치를 제어하는 것만으로도 용이하게 본 발명의 목적달성이 가능하다. 그리고 이것은 기존에 설치된 제어패널(도시 생략)에서 타이머의 설정을 변경하는 것으로 충분하다.Such two-stage heat treatment of the present invention can easily achieve the object of the present invention simply by controlling the hot air device without additional equipment such as vacuum equipment. And this is enough to change the setting of the timer in the existing control panel (not shown).
아울러 본 발명에 따른 금속제품의 경도변화는 표 2 및 도 6과 같으며, 전술한 종래의 표 1과 비교하여 볼 때 전반적으로 경도가 향상됨을 알 수 있다.In addition, the hardness change of the metal product according to the present invention is shown in Table 2 and Figure 6, it can be seen that the overall hardness is improved compared to the conventional Table 1 described above.
그리고 본 발명에 의해 제조된 금속제품의 표면을 500배율로 확대한 도 7의 사진을 판독하여 보면, 백선층(W)의 깊이는 12~13㎛ 이하로 감소된다. 따라서 백선층의 깊이가 감소되는 만큼 연삭에 의한 후가공 시간을 절약할 수 있어 생산성이 향상된다. 더욱이 경화층의 깊이는 0.46mm 내외로 나타나므로 종래에 비해 표면경화에 의한 물성 개선이 크게 기대된다.And when reading the photograph of FIG. 7 which enlarged the surface of the metal product manufactured by this invention at 500 magnification, the depth of the white wire layer W is reduced to 12-13 micrometers or less. Therefore, as the depth of the white wire layer is reduced, it is possible to save post-processing time by grinding, thereby improving productivity. In addition, since the depth of the cured layer is about 0.46 mm, physical property improvement due to surface hardening is expected to be significantly higher than in the related art.
또한, 본 발명에서 백선층이 얇아지는 이유는 복잡한 이론전개보다는 수많은 반복시험에 의한 시행착오에 의존하지만 백선층의 형성이 질화시간과 관련이 있다는 결론에 도달한다. 즉, 질화시간이 길어지면 표면의 백선층에 충만된 질소가스가 탈락하여 기공이 형성되는데, 이 기공사이로 탄소가 침투하여 결국 탄소조직이 확산되고, 이것이 시멘타이트 조직으로 바뀌어 백선층이 형성된다. 그리고 질화처리에 실질적으로 소요되는 시간을 대비하여 보면, 종래에는 1단질화에서 약 72시간 유지되는 반면, 본 발명에서는 2단질화의 총 82시간 중 약 530℃내외의 온도에서 약 52시간 유지됨으로 인해 질화시간이 크게 단축됨을 알 수 있다.In addition, the reason for the thinning of the ringworm layer in the present invention depends on trial and error by numerous repeated tests rather than complex theoretical development, but it is concluded that the formation of ringworm layer is related to the nitriding time. In other words, when the nitriding time is long, the nitrogen gas filled in the white wire layer on the surface is eliminated and pores are formed. The pores penetrate the carbon and eventually the carbon structure is diffused, which is converted into cementite structure to form the white wire layer. In contrast to the time required for the nitriding treatment, conventionally, it is maintained for about 72 hours at 1-molecularization, whereas in the present invention, it is maintained at about 52 hours at about 530 ° C. of the total 82 hours of 2-mole-nitration. It can be seen that the nitriding time is greatly reduced.
또한 통상의 질화처리 온도를 저온(예컨대, 520℃)으로 유지하는 경우, 질소의 확산 속도가 낮아져 질화 경화 깊이가 감소하기 때문에 깊은 질화처리를 할 수 없으며 소재의 어닐링 효과가 줄어든다는 점도 감안해야 한다. 이외에도 전술한 경도나 경화 깊이 등의 요소는 본 발명의 온도 및 시간조건 외에 가스공급량, 가스혼합성분비, 투입 금속제품의 조직상태 등의 여타 공정조건에 의하여 달라질 수 있음은 물론이다.In addition, when the normal nitriding temperature is maintained at a low temperature (for example, 520 ° C.), it is also necessary to take into consideration that deep nitriding cannot be performed and the annealing effect of the material is reduced because the diffusion rate of nitrogen is lowered and the nitriding hardening depth is reduced. . In addition, the above-described factors such as hardness and hardening depth may be changed by other process conditions such as gas supply amount, gas mixture component ratio, and texture state of the input metal product in addition to the temperature and time conditions of the present invention.
상기한 구성 및 작용에 따르면, 본 발명은 가스질화로 철강 제품의 표면을 경화함에 있어 추가적인 설비의 증설 없이 공정제어만으로 양산시 안정적인 품질과 생산성을 유지할 수 있는, 유용한 효과가 있다.According to the above configuration and operation, the present invention has a useful effect in maintaining the stable quality and productivity during mass production only by the process control without additional equipment in curing the surface of the steel product by gas nitriding.
본 발명은 기재된 실시예에 한정되는 것은 아니고, 본 발명의 사상 및 범위를 벗어나지 않고 다양하게 수정 및 변형할 수 있음은 이 기술의 분야에서 통상의 지식을 가진 자에게 자명하며, 따라서 그러한 변형예 또는 수정예들은 본 발명의 특허청구범위에 속한다 해야 할 것이다.It is apparent to those skilled in the art that the present invention is not limited to the described embodiments and that various modifications and variations can be made without departing from the spirit and scope of the present invention, and therefore such modifications or Modifications should be within the scope of the claims of the present invention.
Claims (3)