KR20040100817A - Method and device for manufacturing remicon using powder mixer - Google Patents

Method and device for manufacturing remicon using powder mixer Download PDF

Info

Publication number
KR20040100817A
KR20040100817A KR1020030065350A KR20030065350A KR20040100817A KR 20040100817 A KR20040100817 A KR 20040100817A KR 1020030065350 A KR1020030065350 A KR 1020030065350A KR 20030065350 A KR20030065350 A KR 20030065350A KR 20040100817 A KR20040100817 A KR 20040100817A
Authority
KR
South Korea
Prior art keywords
mixer
concrete
cement
mixed
ready
Prior art date
Application number
KR1020030065350A
Other languages
Korean (ko)
Inventor
김병모
Original Assignee
기초소재 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 기초소재 주식회사 filed Critical 기초소재 주식회사
Priority to KR1020030065350A priority Critical patent/KR20040100817A/en
Publication of KR20040100817A publication Critical patent/KR20040100817A/en

Abstract

PURPOSE: Provided is a method for manufacturing ready mix concrete to equally compound aggregates, water, mixing materials and cement in a concrete mixer, to prevent material separation phenomenon due to difference of specific gravity, and thus to produce ready mix concrete having good quality. CONSTITUTION: The method for manufacturing ready mix concrete comprises a metering process for metering an amounts of aggregates in reservoirs(10,11), cements and mixing materials in reservoirs(12,13,14) and mixture in respective metering bins(20-25), and a first compounding process for compounding the above raw materials in a concrete mixer(30). The ready mix concrete manufacturing method further comprises a second compounding process for compounding the cement and mixing materials beforehand in a separate powder mixer(50) between the metering process and the first compounding process.

Description

분체믹서를 이용한 레미콘 제조방법 및 제조장치{Method and device for manufacturing remicon using powder mixer}Method and device for manufacturing remicon using powder mixer {Method and device for manufacturing remicon using powder mixer}

본 발명은 분체믹서를 이용한 레미콘 제조방법 및 제조장치에 관한 것으로서, 더욱 상세하게는 시멘트, 골재, 물, 혼합재, 혼화재 등의 원료를 콘크리트 믹서에서 배합시켜 레미콘을 제조함에 있어서, 상기 시멘트와 혼합재 등의 분체원료만을 미리 분체믹서에서 배합시킨 후, 콘크리트 믹서에서 나머지 원료와 함께 배합시킴으로써, 각각의 원료들의 배합을 균일하게 이루어지도록 하며, 원료의 비중차에 의한 재료분리 현상을 획기적으로 방지할 수 있는 분체믹서를 이용한 레미콘 제조방법 및 제조장치에 관한 것이다.The present invention relates to a ready-mixed concrete manufacturing method and manufacturing apparatus using a powder mixer, and more specifically, in preparing a ready-mixed concrete by mixing raw materials such as cement, aggregate, water, mixed materials, admixtures, etc. By mixing only the powder raw material in the powder mixer in advance, and then mixing it with the remaining raw materials in the concrete mixer, the mixing of each raw material is made uniform, and can prevent the material separation phenomenon due to the specific gravity difference of the raw materials It relates to a ready-mixed concrete manufacturing method and apparatus using a powder mixer.

일반적으로, 레미콘(remicon)이란 Ready Mixed Concrete의 약자로서, 각 제품별로 조골재 최대치수, 호칭강도, 슬럼프 등에 따라 100여개 이상의 많은 규격이 있다.In general, the ready-mix concrete (remicon) is an abbreviation of Ready Mixed Concrete, and each product has more than 100 specifications based on the maximum aggregate size, nominal strength, slump, and the like.

상기 조골재 최대치수란 사용하는 조골재 중 가장 큰 조골재의 지름이 지정된 규격을 넘지 않는 것으로 19mm, 25mm, 40mm 등으로 대별되며, 25mm이하 규격은 철근콘크리트에, 40mm 이상은 주로 무근(無筋)콘크리트에 사용된다.The maximum size of the coarse aggregate is the diameter of the largest coarse aggregate used does not exceed the specified specifications, and is roughly divided into 19mm, 25mm, 40mm, etc., the size of 25mm or less in reinforced concrete, 40mm or more mainly in non-concrete concrete Used.

또한, 상기 호칭강도는 타설 28일의 압축강도를 기준으로 하여 100kgf/㎠ 이상의 고강도 콘크리트에 이르기까지 다양하게 존재하며, 상기 슬럼프는 콘크리트의 반죽질기를 지칭하는 것으로서, 수치가 높을수록 유동성이 많은 부드러운 콘크리트를 의미하며, 일반적으로 5cm부터 21cm까지 사용된다.In addition, the nominal strength is present in a variety of high strength concrete of 100kgf / ㎠ or more on the basis of the compressive strength of 28 days pour, the slump refers to the dough kneading of concrete, the higher the value the more fluidity smooth Refers to concrete and is generally used from 5cm to 21cm.

이러한 레미콘은 콘크리트 건축물(아파트 등) 또는 교량, 도로 및 터널공사의 기초 자재로 사용되도록 완벽한 콘크리트 제조설비를 갖춘 공장에서 시멘트, 골재(모래, 자갈), 물, 혼화재 그리고, 혼합재의 재료를 이용하여 KSF4009에 규정된 제조방법 및 품질검사 등에 준하여 콘크리트 믹서에서 배합비율에 맞춰 배합시키게 된다.These ready-mixed concrete can be used with cement, aggregate (sand, gravel), water, admixture, and mixed materials in concrete buildings (apartments, etc.) or in factories with complete concrete manufacturing facilities to be used as foundation materials for bridges, roads and tunnel construction. In accordance with the manufacturing method and quality inspection, etc. specified in KSF4009, the concrete mixer is blended according to the mixing ratio.

이후, 어느 정도 콘크리트 혼합물을 배합시킨 다음에 믹서트럭으로 운반하고, 공사현장까지 운반하는 과정에서 상기 믹서트럭의 믹서드럼에 담긴 레미콘의 응고를 방지하기 위하여 일정한 속도로 상기 믹서드럼을 회전시켜 나머지마저 배합시키게 되는데, 이러한 제조방법으로 제조된 것을 슈링크 믹스트 콘크리트(shrink mixed concrete)라고 하며, 처음부터 믹서트럭 속에서 운반하면서 완전히 배합시킨 것을 트랜싯 믹스트 콘크리트(transit mixed concrete)라고 한다.Thereafter, the concrete mixture is blended to some extent and then transported to the mixer truck, and the mixer drum is rotated at a constant speed in order to prevent solidification of the ready mixed concrete contained in the mixer drum of the mixer truck during the transport to the construction site. It is to be blended, which is produced by such a manufacturing method is called shrink mixed concrete, and from the start, it is called transit mixed concrete that is completely mixed while transporting in a mixer truck.

여기서, 상기 콘크리트 믹서(30)는 구동원에 의해 구동되어 원료를 원활하게 배합시키는 블레이드수단이 구비되어 있으며, 상기 믹서트럭(40)은 도 4에 도시된 바와 같이, 믹서드럼(41)의 후부에 깔때기 형상의 호퍼(42)가 설치되어 있어 이것을 통해 콘크리트를 투입할 수 있고, 믹서드럼(41)의 하부에 반원단면 형상의 슈트(43)가 설치되어 믹서드럼(41)에 의해 일정한 농도로 배합된 콘크리트를 원거리에 있는 건설현장 등의 해당장소에 공급할 수 있도록 구성되어 있다.Here, the concrete mixer 30 is provided by a blade means for smoothly blending the raw material is driven by a drive source, the mixer truck 40 is shown in the rear of the mixer drum 41, as shown in FIG. A funnel-shaped hopper 42 is provided so that concrete can be introduced therethrough, and a semi-circular cross-section chute 43 is installed at the bottom of the mixer drum 41 to be blended at a constant concentration by the mixer drum 41. It is configured to supply the concrete to the relevant place such as construction site at a long distance.

여기서, 미설명부호 10 ~ 14는 원료를 저장하여 두는 저장소를 나타내고, 20 ~ 25는 상기 원료를 계량하여 콘크리트 믹서(30)에 투입하기 위한 계량빈을 나타낸다.Here, reference numerals 10 to 14 denote storage bins for storing the raw materials, and 20 to 25 denote weighing bins for measuring the raw materials and injecting them into the concrete mixer 30.

한편, 도 4는 종래의 레미콘을 제조함에 있어서, 원료의 배합과정 및 제조공정을 나타내는 것으로서, 첨부도면을 참조하여 간단하게 설명하면, 콘크리트의 고강도화를 위한 상기 혼합재로는 슬래그 파우더(slag powder), 플라이 애쉬(fly ash) 등이 있으며, 이것을 시멘트, 골재, 물, 혼화재(감수제, 지연제, 조강제) 등과 배합시켜 상기 콘크리트 믹서(30)에 투입하고, 일정시간 동안에 일정한 농도로 배합시켜 제조한 레미콘을 믹서트럭(40)을 이용하여 건설 현장 등으로 공급될 수 있도록 한다.On the other hand, Figure 4 shows the mixing process and manufacturing process of the raw material in the manufacture of the conventional ready-mixed concrete, simply described with reference to the accompanying drawings, the mixture for the high strength of the concrete slag powder (slag powder), Fly ash (fly ash) and the like, which is blended with cement, aggregate, water, admixture (reducing agent, retardant, crude) and the like to the concrete mixer 30, prepared by mixing at a constant concentration for a certain time. The ready-mixed concrete can be supplied to a construction site using the mixer truck 40.

그런데, 이와 같은 종래의 레미콘을 제조함에 있어서, 상기 원료들이 함께 콘크리트 믹서(30)에 투입되면 상기 시멘트와 혼합재는 상기 골재, 물, 그리고, 혼화재 등과 같이 배합되는데, 이때 상기 시멘트와 혼합재보다 크기가 큰 골재 등이 균일한 배합을 방해하고, 비중차에 의해 재료분리 현상이 일어나 특정 혼합재가 한쪽으로 쏠리는 문제점이 발생하였다.By the way, in manufacturing such a conventional ready-mixed concrete, when the raw materials are put together in the concrete mixer 30, the cement and the mixed material is combined with the aggregate, water, and mixed material, etc., where the size is larger than the cement and mixed material Large aggregates and the like hinder uniform mixing, and material separation occurs due to specific gravity difference, which causes a problem in that a specific mixture is oriented to one side.

따라서, 본 발명은 상기와 같은 문제점을 해결하기 위해 발명한 것으로서, 레미콘을 제조함에 있어서, 상기 레미콘의 원료인 시멘트와 혼합재를 따로 분체믹서에서 배합시킨 다음에 일정시간이 경과한 후, 콘크리트 믹서에 골재, 물, 혼화재 등의 나머지 원료와 함께 배합시킴으로써, 각각의 원료들이 균일하게 배합되도록 하고, 원료의 비중차에 의한 재료분리 현상을 차단하여 우수한 레미콘을 생산할 수 있는 새로운 레미콘 제조방법 및 제조장치를 제공하는데 그 목적이 있다.Therefore, the present invention has been invented to solve the above problems, in the production of ready-mixed concrete, after mixing a cement and a mixed material as the raw material of the ready-mixed separately in a powder mixer, after a predetermined time has passed to the concrete mixer By mixing with the remaining raw materials such as aggregate, water, admixture, etc., each raw material is uniformly blended, and a new ready-mixed concrete manufacturing method and apparatus for producing excellent ready-mixed concrete can be produced by blocking material separation phenomenon due to specific gravity difference of raw materials. The purpose is to provide.

도 1은 본 발명에 따른 레미콘 제조장치에 의한 원료의 배합과정을 나타내는 구성도,1 is a block diagram showing the mixing process of the raw material by the ready-mixed concrete manufacturing apparatus according to the present invention,

도 2는 본 발명에 따른 분체믹서를 이용한 레미콘 제조과정을 나타내는 블록도,2 is a block diagram showing a ready-mixed concrete manufacturing process using a powder mixer according to the present invention;

도 3은 본 발명에 따른 분체믹서를 나타내는 도면,3 is a view showing a powder mixer according to the present invention;

도 4는 종래의 레미콘 제조장치에 의한 원료의 배합과정을 나타내는 구성도이다.Figure 4 is a block diagram showing the mixing process of the raw material by the conventional ready-mixed concrete manufacturing apparatus.

〈도면의 주요 부분에 대한 부호의 설명〉<Explanation of symbols for main parts of drawing>

10 ~ 14 : 저장소 20 ~ 25 : 계량빈10 ~ 14: storage 20 ~ 25: weighing bin

30 : 콘크리트 믹서 40 : 믹서트럭30: concrete mixer 40: mixer truck

41 : 믹서드럼 42 : 호퍼41: mixer drum 42: hopper

43 : 슈트 50 : 분체믹서43: suit 50: powder mixer

51 : 하우징 52a,52b : 교반날개51 housing 52a, 52b stirring blade

53a,53b : 고정프레임 54 : 구동모터53a, 53b: fixed frame 54: drive motor

55 : 회전축 56 : 동력전달수단55: rotation shaft 56: power transmission means

이하, 상기와 같은 목적을 달성하기 위한 본 발명의 특징에 대해 설명하면 다음과 같다.Hereinafter, the features of the present invention for achieving the above object are as follows.

본 발명은 골재 저장소(10,11)에서의 골재와, 시멘트 및 혼합재 저장소(12,13,14)에서의 시멘트 및 혼합재와, 혼화재를 각각의 계량빈(20 ∼ 25)에서 일정량 계량하는 제1공정과;The present invention provides a first method for weighing aggregates in aggregate reservoirs 10, 11, cement and mixtures in cement and mixture reservoirs 12, 13, 14, and admixtures in respective metering bins 20 to 25. Process;

상기 원료를 콘크리트 믹서(30)에서 배합시키는 제2공정을 포함하여 이루어지는 레미콘 제조방법에 있어서,In the ready-mixed concrete manufacturing method comprising a second step of blending the raw material in the concrete mixer 30,

상기 제1공정 및 제2공정 사이에, 상기 시멘트와 혼합재를 별도의 분체믹서(50)에서 미리 배합시키는 공정을 더 포함하는 것을 특징으로 한다.Between the first step and the second step, characterized in that it further comprises the step of pre-mixing the cement and the mixture in a separate powder mixer (50).

또한, 모래, 자갈 등의 골재와, 시멘트 및 혼합재를 각각 저장하는 저장소(10 ∼ 14)와; 혼화재를 포함하여 상기 골재, 시멘트 그리고, 혼합재를 일정량 계량하는 계량빈(20 ∼ 25)과; 상기 원료를 투입하여 일정한 시간동안에 일정한 농도로 배합시키는 콘크리트 믹서(30)를 포함하여 이루어진 레미콘 제조장치에 있어서,Further, aggregates such as sand and gravel, and reservoirs 10 to 14 for storing cement and mixed materials, respectively; A metering bin (20 to 25) for measuring a predetermined amount of the aggregate, cement, and mixed material including a mixed material; In the ready-mixed concrete manufacturing apparatus comprising a concrete mixer 30 to add the raw material to a certain concentration for a certain time,

상기 계량빈(20 ~ 25)의 원료를 콘크리트 믹서(30)에 투입하기 전에 상기 시멘트와 혼합재만을 미리 배합시키는 분체믹서(50)가 더 포함된 것을 특징으로 한다.Before the raw material of the metering bin (20 ~ 25) to the concrete mixer 30 is characterized in that it further comprises a powder mixer 50 for pre-mixing only the cement and the mixture.

특히, 상기 분체믹서(50)는 용기형태의 하우징(51)과, 시멘트 및 혼합재를 교반시켜 믹싱하는 직경이 서로 다른 2중 나선구조의 교반날개(52a,52b)와, 상기 교반날개(52a,52b)를 구동시키는 구동모터(54)와, 상기 구동모터(54)의 동력을 상기 교반날개(52a,52b)가 장착된 회전축(55)에 전달시키는 동력전달수단(56)을 포함하여 구성된 것을 특징으로 한다.In particular, the powder mixer 50 is a container-shaped housing 51, the stirring blades (52a, 52b) of the two-helical structure having a different diameter for stirring and mixing the cement and the mixture, and the stirring blade (52a, And a power transmission means 56 for transmitting the drive motor 54 for driving 52b) and the power of the drive motor 54 to the rotating shaft 55 on which the stirring blades 52a and 52b are mounted. It features.

상기 교반날개(52a,52b)에는 회전축(55)과 일정간격을 두고 수직으로 연결고정된 고정프레임(53a,53b)이 형성된 것을 특징으로 한다.The stirring blades (52a, 52b) is characterized in that the fixed frame (53a, 53b) is fixed to the vertically connected to the rotation axis 55 at a predetermined interval.

이하, 첨부도면을 참조하여 본 발명의 구성에 대해 상세하게 설명하면 다음과 같다.Hereinafter, the configuration of the present invention with reference to the accompanying drawings in detail.

도 1은 본 발명에 따른 분체믹서를 이용한 레미콘 제조장치에 의해 원료의 배합과정을 나타내는 구성도이고, 도 2는 본 발명에 따른 분체믹서를 이용한 레미콘 제조과정을 나타내는 블록도이다.1 is a block diagram showing the mixing process of the raw material by the ready-mixed concrete manufacturing apparatus using a powder mixer according to the present invention, Figure 2 is a block diagram showing a ready-mixed concrete manufacturing process using a powder mixer according to the present invention.

본 발명은 시멘트, 골재, 물, 혼합재, 혼화재 등의 원료를 콘크리트 믹서(30)에서 일정한 시간동안에 일정한 농도로 배합시켜 레미콘을 제조함에 있어서, 상기 시멘트와 혼합재 등의 분체원료만을 미리 분체믹서(50)에서 배합시킨 후, 콘크리트 믹서(30)에서 나머지 혼합물과 함께 배합시키는 제조방법으로서, 도 1에 도시된 바와 같이, 모래, 자갈 등이 저장된 골재 저장소(10,11)에서의 골재를 계량빈(20,21)에서 일정량 계량하고, 시멘트 및 혼합재 저장소(12,13,14)에서 각각의 시멘트 및 혼합재 즉, 플라이 애쉬(fly ash)와, 슬래그 파우더(slag powder)를 계량빈(22,23,24)에서 일정량 계량하는 한편, 탁월한 감수효과를 갖는 감수(減水)제와, 콘크리트의 응고를 지연시키는 지연제 및 혼합물의 강도를 조기에 증진시키는 조강제와, 물 등과 같은 혼화재를 계량빈(25)에서 일정량 계량하여 콘크리트 믹서(30)에서 배합을 시키게 된다.In the present invention, when preparing a ready-mixed concrete by mixing the raw materials, such as cement, aggregate, water, mixed materials, admixtures, etc. at a constant concentration for a predetermined time in the concrete mixer 30, only the powder raw materials such as cement and mixed materials in advance powder mixer (50). After mixing in the), as a manufacturing method for mixing with the remaining mixture in the concrete mixer 30, as shown in Figure 1, the aggregates in the aggregate storage (10, 11) stored sand, gravel, etc. 20, 21, and the cement and mixture reservoir (12, 13, 14), each of the cement and mixture, that is, fly ash (slag ash) and slag powder (slag powder) in the measuring bin (22, 23, 24), while weighing a certain amount, the water-reducing agent having an excellent water-resisting effect, a retarder for delaying the solidification of concrete and a coarse-grained material for early improvement of the strength of the mixture, and a mixed material such as water are weighed in the bin (25). ) The amount metered thereby the mixing in a concrete mixer (30).

이때, 상기 시멘트 및 혼합재 등과 같이 미세분체로 이루어진 혼합물은 따로 분리시켜 미리 배합시키게 되는 바, 상기 콘크리트 믹서(30)와 같은 용도를 갖는 분체믹서(50)에서 1차로 배합시키게 된다.At this time, the mixture made of fine powder, such as the cement and the mixing material is separated separately to be mixed in advance, it is to be primarily blended in the powder mixer 50 having the same purpose as the concrete mixer (30).

이때, 상기 저장소(10 ~ 14)에 저장된 원료를 일정량 계량하여 계량빈(20 ~ 25)에 담을 수 있도록 그 원료가 유동되는 라인에 조절수단이 구비되어 있는 것이 바람직하다.At this time, it is preferable that the adjusting means is provided in a line through which the raw material flows so that the raw material stored in the reservoirs 10 to 14 can be weighed in a certain amount and contained in the measuring bins 20 to 25.

한편, 상기 분체믹서(50)는 시멘트 및 혼합재를 담아두기 용이하도록 형성된 용기형태의 하우징(51)과, 시멘트 및 혼합재를 교반시켜 믹싱하는 직경이 서로 다른 2중 나선구조의 교반날개(52a,52b)와, 상기 교반날개(52a,52b)를 구동시키는 구동모터(54)와, 상기 구동모터(54)의 동력을 상기 교반날개(52a,52b)가 장착된 회전축(55)에 전달시키는 동력전달수단(56) 즉, 벨트 또는 체인 등을 포함하여 구성되어 있다.On the other hand, the powder mixer 50 is a container-shaped housing 51 formed so as to easily hold the cement and the mixed material, and the stirring blades 52a and 52b of the double spiral structure having different diameters by mixing the cement and the mixed material by stirring. ), A drive motor 54 for driving the stirring blades 52a and 52b, and a power transmission for transmitting the power of the drive motor 54 to the rotating shaft 55 on which the stirring blades 52a and 52b are mounted. Means 56, i.e., a belt or a chain.

이때, 상기 교반날개(52a,52b)에는 상기 교만날개(52a,52b)가 흔들림없이 일정하게 회전가능하도록 회전축(55)과 일정간격을 두고 수직으로 연결 고정된 다수개의 고정프레임(53a,53b)이 고정되어 있다.At this time, the stirring blades (52a, 52b) the arrogant blades (52a, 52b) a plurality of fixed frames (53a, 53b) connected vertically fixed at regular intervals with the rotation shaft (55) to be able to rotate constantly without shaking Is fixed.

이와 같이, 분체로 이루어진 시멘트와 혼합제를 따로 분리하여 미리 배합시키는 이유는 시멘트와 각각의 혼합재가 완전하게 배합되기 전에 골재와 물 등을 배합시키게 되면, 각각의 원료들이 균일하게 배합되지 않는 동시에, 원료들의 비중차에 의해 재료분리 현상이 발생하여 특정 혼합재가 한쪽으로 쏠리는 문제점을 방지하기 위함이다.As such, the reason for separating and mixing the cement and the powder composed of powder separately in advance is that when the aggregate and the water are mixed before the cement and the respective mixture are completely blended, the raw materials are not uniformly blended, and This is to prevent a problem that a specific mixture is oriented to one side due to the material separation phenomenon caused by the difference in specific gravity.

따라서, 상술한 바와 같이, 시멘트와 혼합재를 1차로 분체믹서(50)에서 미리 완전하게 배합시킨 다음에 그 배합된 원료를 나머지 원료와 함께 콘크리트 믹서(30)에서 2차로 배합시키게 된다.Therefore, as described above, the cement and the mixture are first blended completely in the powder mixer 50 in advance, and then the blended raw materials are secondarily mixed in the concrete mixer 30 together with the remaining raw materials.

이때, 상기 시멘트와 혼합재가 혼합된 혼합물에 상기 골조, 물 그리고, 혼화재 등을 배합시키게 되면, 그 골조, 물 그리고, 혼화재 등이 골고루 균일하게 상기 혼합물에 배합하게 되어 균일한 혼합물을 이루게 되며, 재료분리 현상이 발생하지 않아 특정 혼합재의 쏠림 현상도 또한, 발생하지 않게 된다.In this case, when the framework, water, and a blending material are blended into the mixture of the cement and the mixing material, the framework, water, and the mixing material are evenly blended into the mixture to form a uniform mixture. Separation does not occur such that the pulling of certain mixtures does not occur.

상기와 같이 일정한 시간동안에 일정한 농도로 배합되어 제조된 레미콘을 믹서트럭(40)의 믹서드럼(41)에 저장하고, 그 저장상태에서 원거리의 건설현장으로 운반하게 된다.The ready-mixed ready-mixed concrete mixed at a constant concentration for a predetermined time as described above is stored in the mixer drum 41 of the mixer truck 40, and transported to the construction site of the remote in the storage state.

이때, 상기 레미콘이 응고되지 않도록 믹서드럼(41)을 일정한 속도로 회전시키면서 그 레미콘을 교반시키게 된다.At this time, the ready-mixed concrete mixer is stirred while rotating the mixer drum 41 at a constant speed so that the ready-mixed concrete is not solidified.

따라서, 이와 같이 본 발명에 따른 분체믹서를 이용한 레미콘을 제조함에 있어서, 레미콘 생산공장에서 레미콘을 제조 시에 시멘트 및 혼합재 등과 같은 분체원료는 분체믹서(50)에서 우선 1차로 배합시키고, 그런 다음에 배합된 분체원료를 골조, 물, 혼화재 등과 함께 콘크리트 믹서(30)에서 다시 배합시켜 콘크리트 혼합물이 균일하게 배합될 수 있도록 함으로써, 레미콘의 품질을 향상시키고, 그로인한 불량 레미콘의 사용을 억제하여 부실시공을 방지할 수 있는 새로운 레미콘 제조방법 및 제조장치를 제공할 수 있게 되는 것이다.Therefore, in manufacturing the ready-mixed concrete using the powder mixer according to the present invention, when preparing the ready-mixed concrete in the ready-mixed concrete production plant, powder raw materials such as cement and mixed materials are first blended in the powder mixer 50 first, and then By mixing the blended powder raw materials together with the framework, water, admixture in the concrete mixer 30 so that the concrete mixture can be uniformly blended, the quality of ready-mixed concrete can be improved, and the use of poor ready-mixed concrete is thereby suppressed. Will be able to provide a new ready-mixed concrete manufacturing method and manufacturing apparatus that can prevent.

상술한 바와 같이, 본 발명에 따른 분체믹서를 이용한 레미콘 제조방법 및 제조장치에 의하면, 시멘트 및 혼합재 등과 같은 분체원료를 미리 분체믹서에서 배합시키고 난 후, 콘크리트 믹서에 나머지 혼합물과 배합시킴으로써, 각각의 원료들의 배합을 균일하게 이루어지도록 하며, 원료의 비중차에 의한 재료분리 현상을 획기적으로 차단하므로, 그로인해 불량 레미콘의 사용을 억제가능하여 부실시공을 획기적으로 방지할 수 있는 효과가 있다.As described above, according to the ready-mixed concrete manufacturing method and manufacturing apparatus using the powder mixer according to the present invention, by mixing the powder raw materials such as cement and mixed materials in a powder mixer in advance, and by mixing with the remaining mixture in the concrete mixer, Since the mixing of the raw materials is made uniform, and the material separation phenomenon due to the specific gravity difference of the raw materials is significantly blocked, there is an effect that can prevent the use of defective ready-mixed concrete, thereby preventing the secondary holes.

Claims (4)

골재 저장소(10,11)에서의 골재와, 시멘트 및 혼합재 저장소(12,13,14)에서의 시멘트 및 혼합재와, 혼화재를 각각의 계량빈(20 ~ 25)에서 일정량 계량하는 제1공정과;A first step of weighing a certain amount of aggregate in the aggregate reservoirs 10, 11, cement and mixtures in the cement and mixture reservoirs 12, 13, 14, and admixture in each metering bin 20-25; 상기 원료를 콘크리트 믹서(30)에서 배합시키는 제2공정을 포함하여 이루어지는 레미콘 제조방법에 있어서,In the ready-mixed concrete manufacturing method comprising a second step of blending the raw material in the concrete mixer 30, 상기 제1공정 및 제2공정 사이에, 상기 시멘트와 혼합재를 별도의 분체믹서(50)에서 미리 배합시키는 공정을 더 포함하는 것을 특징으로 하는 분체믹서를 이용한 레미콘 제조방법.Between the first step and the second step, the method for producing ready-mixed concrete using a powder mixer, characterized in that further comprising the step of pre-mixing the cement and the mixture in a separate powder mixer (50). 모래, 자갈 등의 골재와, 시멘트 및 혼합재를 각각 저장하는 저장소(10 ~ 14)와; 혼화재를 포함하여 상기 골재, 시멘트 그리고, 혼합재를 일정량 계량하는 계량빈(20 ~ 25)과; 상기 원료를 투입하여 일정한 시간동안에 일정한 농도로 배합시키는 콘크리트 믹서(30)를 포함하여 이루어진 레미콘 제조장치에 있어서,Aggregates such as sand and gravel, and reservoirs 10 to 14 for storing cement and mixed materials, respectively; A metering bin (20 to 25) for measuring a certain amount of the aggregate, cement, and mixed material, including a mixed material; In the ready-mixed concrete manufacturing apparatus comprising a concrete mixer 30 to add the raw material to a certain concentration for a certain time, 상기 계량빈(20 ~ 25)의 원료를 콘크리트 믹서(30)에 투입하기 전에 상기 시멘트와 혼합재만을 미리 배합시키는 분체믹서(50)가 더 포함된 것을 특징으로 하는 분체믹서를 이용한 레미콘 제조장치.Before the raw material of the metering bin (20 ~ 25) to the concrete mixer 30, the powder mixer (50) for mixing only the cement and the mixed material in advance is characterized in that it further comprises a powder mixer. 제2항에 있어서, 상기 분체믹서(50)는 용기형태의 하우징(51)과, 시멘트 및혼합재를 교반시켜 믹싱하는 직경이 서로 다른 2중 나선구조의 교반날개(52a,52b)와, 상기 교반날개(52a,52b)를 구동시키는 구동모터(54)와, 상기 구동모터(54)의 동력을 상기 교반날개(52a,52b)가 장착된 회전축(55)에 전달시키는 동력전달수단(56)을 포함하여 구성된 것을 특징으로 하는 분체믹서를 이용한 레미콘 제조장치.The method of claim 2, wherein the powder mixer 50 is a container-like housing 51, the stirring blades (52a, 52b) of a double spiral structure having different diameters by mixing and mixing the cement and the mixture, and the stirring A drive motor 54 for driving the blades 52a and 52b, and a power transmission means 56 for transmitting the power of the drive motor 54 to the rotary shaft 55 on which the stirring blades 52a and 52b are mounted. Ready-mixed concrete manufacturing apparatus using a powder mixer, characterized in that configured to include. 제3항에 있어서, 상기 교반날개(52a,52b)에는 회전축(55)과 일정간격을 두고 수직으로 연결 고정된 고정프레임(53a,53b)이 형성된 것을 특징으로 하는 분체믹서를 이용한 레미콘 제조장치.According to claim 3, The stirring blades (52a, 52b) Ready-mixed concrete manufacturing apparatus using a powder mixer, characterized in that the fixed frame (53a, 53b) is connected to the vertically fixed at a predetermined interval with the rotating shaft (55).
KR1020030065350A 2003-09-19 2003-09-19 Method and device for manufacturing remicon using powder mixer KR20040100817A (en)