KR200343191Y1 - Wood for furniture and/or building - Google Patents
Wood for furniture and/or building Download PDFInfo
- Publication number
- KR200343191Y1 KR200343191Y1 KR20-2003-0037008U KR20030037008U KR200343191Y1 KR 200343191 Y1 KR200343191 Y1 KR 200343191Y1 KR 20030037008 U KR20030037008 U KR 20030037008U KR 200343191 Y1 KR200343191 Y1 KR 200343191Y1
- Authority
- KR
- South Korea
- Prior art keywords
- paint
- wood
- layer
- chlorite
- stain
- Prior art date
Abstract
본 고안은 가구 및/또는 건축용 목재에 관한 것으로서, 더 상세하게는 클로라이트(Chlorite)와 일라이트(Illite)로 이루어진 클로라이트 분말을 도료에 첨가하여 목재소지에 도포함으로서 나무무늬를 그대로 유지하면서 도료에서 발생하는 인체 유해가스를 중화시켜 건강에 유익한 환경을 제공하는 가구 및/또는 건축용 목재에 관한 것이다.The present invention relates to wood for furniture and / or construction, and more particularly, chlorite powder made of chlorite and illite, and added to the paint to coat the wood material while maintaining the wood pattern as it is. The present invention relates to furniture and / or building timber that neutralizes the harmful gases generated in the environment and provides a healthful environment.
본 고안에 따른 목재는 목재소지와, 상기 목재소지의 적어도 일면에 클로라이트와 일라이트 두가지 광물이 동일 맥상에서 동시에 혼합 생성되는 클로라이트 분말이 첨가된 스테인을 도포하여 형성된 스테인층과, 상기 스테인층 표면에 클로라이트 분말이 첨가된 도료를 도포하여 형성된 도료층으로 이루어진다.The wood according to the present invention is a stained layer formed by applying a stain to the wood base, and the chlorite powder is added to the chlorite and illite two minerals on the same vein at least on one surface of the wood base, and the stain layer It consists of the coating layer formed by apply | coating the paint which added chlorite powder to the surface.
Description
본 고안은 가구 및/또는 건축용 목재에 관한 것으로서, 더 상세하게는 클로라이트와 일라이트로 이루어진 클로라이트 분말을 도료에 첨가하여 목재소지에 도포함으로서 나무무늬를 그대로 유지하면서 도료에서 발생하는 인체 유해가스를 중화시켜 건강에 유익한 환경을 제공하는 가구 및/또는 건축용 목재에 관한 것이다.The present invention relates to wood for furniture and / or construction, and more particularly, harmful chlorine gas generated from paints by adding chlorite powder composed of chlorite and illite to the paint and being applied to the wood material while maintaining the wood pattern as it is. It relates to furniture and / or building timber that neutralizes them to provide a healthful environment.
주지하다시피 목재는 인간의 주위환경과 밀접한 가구나 건축 내외장재 등에 널리 사용되어 왔다.As is well known, wood has been widely used in furniture and interior and exterior materials, which are closely related to the human environment.
가구는 사람이 사용하기 편리하도록 옷장이나 이불장, 책상, 문갑 등 다양한 형태로 제작되어 가정이나 사무실에 위치된다.The furniture is made in various forms such as a wardrobe, a quilt, a desk, a lock, and is placed in a home or an office for the convenience of a person.
상기한 가구나 건축용 목재는 미생물에 의한 분해에 의해 수명이 단축될 우려가 있어 그 표면을 일정한 도료로서 도장 처리한다.The furniture and building timbers mentioned above may be shortened by microorganisms for their lifespan, and the surfaces thereof are treated with a constant paint.
종래에는 상기한 도료로 신나, 우레탄, 락카 등을 일정한 함량비로 배합한 도료가 이용되었으며, 이 도료를 붓, 롤러 또는 스프레이를 이용해서 목재의 표면에 도포하면 목재 표면에 도료층이 형성되어 미생물에 의한 분해 문제를 해결하면서 천연 그대로의 나무무늬를 살릴 수 있다.Conventionally, paints containing a thinner, urethane, lacquer, etc. in a specific content ratio have been used. When the paint is applied to a surface of wood by using a brush, roller, or spray, a paint layer is formed on the surface of the wood and is applied to microorganisms. While solving the problem of decomposition by the natural wood texture can be saved.
그러나 종래 기술에 따른 목재용 도료는 신나, 우레탄, 락카와 같이 인체에 유해한 인공 화합물로만 조성되므로 도포 작업후에 인체에 악영향을 주게 되는 문제점이 있었다.However, since the paint for wood according to the prior art is composed only of artificial compounds harmful to the human body, such as thinner, urethane, lacquer, there was a problem that adversely affect the human body after the application.
즉, 휘발성 유기화합물인 도료에서 인체에 유해한 가스를 발생하고 발암물질을 방출하여 인체의 건강에 나쁜 영향을 미친다.That is, volatile organic compounds generate harmful gases to the human body and release carcinogens, which adversely affects the health of the human body.
이러한 문제점을 감안하여, 공개번호 특1998-083689호에는 원적외선 방사 항균 온돌 목재 마루판 및 그 제조방법이 개시되어 있고, 공개번호 특2001-0073862호에는 가구용 도료 및 이를 이용한 가구 도장방법이 개시되어 있다.In view of such a problem, Korean Laid-Open Publication No. 1998-083689 discloses a far-infrared radiation antibacterial ondol wood floorboard and a method for manufacturing the same. In Korean Laid-Open Publication No. 2001-0073862, a paint for furniture and a method of painting a furniture using the same are disclosed.
상기 전자의 마루판은 Al2O3, SiO2, Fe2O3, ZrO3 분말과 같은 원적외선 방사 바이오 세라믹 분말과 구리, 아연, 은 등의 금속 산화물과 같은 무기 항균제 분말을 5-10중량% 포함하는 우레탄 도료를 합판의 표면에 10-20g/m2의 도포량으로 도포하여 제조된다.The former floorboard is Al2O3, SiO2, Fe2O3, ZrO3 10-20 g / m urethane paint containing 5-10% by weight of far-infrared radiation bioceramic powder such as powder and inorganic antimicrobial powder such as metal oxides such as copper, zinc and silver on the surface of plywood2It is prepared by applying in an application amount of.
상기 후자의 가구 도장방법은 가구의 형태로 가공 조립된 제품의 표면을 샌드 페이퍼로써 곱게 연마하고, 상기 연마된 제품의 표면에 황토, 참숯, 물이 적절히 혼합되어 있는 도료를 수시로 흔들어 주면서 균일하게 분사하며, 도료층이 건조된 후에는 다시 그 표면을 샌드 페이퍼로써 곱게 연마하고, 상기 연마된 제품의 표면에 휘발성이 강한 식물성 알코올을 3회 정도 분사하여 마무리한다.In the latter furniture coating method, the surface of the product processed and assembled in the form of furniture is finely ground with sand paper, and the surface of the polished product is sprayed uniformly while frequently shaking the paint in which ocher, charcoal and water are properly mixed. After the paint layer is dried, the surface is polished finely with sand paper, and the surface of the polished product is sprayed three times with strong volatile vegetable alcohol to finish.
이 경우 바이오 세라믹 분말이나 황토 등에서 나오는 원적외선으로 신체 기능의 활성화를 얻을 수 있으나 도료를 1회만 도포하기 때문에 도료의 원래 목적인 나무무늬를 살리거나 미생물에 의한 분해 문제를 살리는 데에는 어려움이 있었다.In this case, it is possible to obtain the activation of the body function by far infrared rays from the bio-ceramic powder or loess. However, since the coating is applied only once, it is difficult to save the wood pattern or the problem of decomposition by microorganisms.
본 고안은 상술한 문제점을 해결하기 위하여 안출된 것으로서, 본 고안의 주 목적은 목재의 표면에 인체에 유익한 클로라이트 분말을 도료에 첨가해서 수회 도포함으로써 미생물에 의한 분해 문제를 해결하고 나무무늬를 그대로 살릴 수 있는 가구 및/또는 건축용 목재를 제공하는데 있다.The present invention is devised to solve the above problems, the main purpose of the present invention is to solve the problem of decomposition by microorganisms by adding chlorite powder, which is beneficial to the human body, on the surface of wood to the paint and apply it several times to keep the wood pattern To provide sustainable furniture and / or construction timber.
본 고안은 다른 목적은, 도료에 포함된 클로라이트 분말의 탈취, 항균 및 원적외선 방사 효과를 이용해 도료에서 발생하는 인체유해가스를 차단하거나 감소시켜 인체에 유익한 환경을 제공할 수 있는 가구 및/또는 건축용 목재를 제공하는데 있다.Another object of the present invention is to provide furniture and / or construction that can provide a beneficial environment for the human body by blocking or reducing the harmful gas generated from the paint by using the deodorizing, antibacterial and far-infrared radiation effect of the chlorite powder contained in the paint To provide wood.
상술한 목적을 달성하기 위하여 본 고안은 목재로 이루어진 소지와, 상기 목재소지의 적어도 일면에 클로라이트와 일라이트 두가지 광물이 동일 맥상에서 동시에 혼합 생성되는 클로라이트 분말이 첨가된 스테인을 도포하여 형성된 스테인층과, 상기 스테인층 표면에 클로라이트 분말이 첨가된 도료를 도포하여 형성된 도료층이 구비됨을 특징으로 하는 가구 및/또는 건축용 목재를 제공하고자 한다.In order to achieve the above object, the present invention is a stain formed by applying a stain made of wood and chlorite powder on which at least one surface of chlorite and illite are mixed and formed at the same vein at least on one surface of the wood body. A layer and a paint layer formed by applying a paint to which the chlorite powder is added to a surface of the stain layer are provided.
여기서, 상기 도료층은 스테인층의 표면에 클로라이트 분말이 첨가된 샌딩(sanding)도료를 도포하여 형성된 샌딩 도료층과, 샌딩 도료층의 표면에 클로라이트 분말이 첨가된 중도도료를 도포하여 형성된 중도 도료층과, 중도 도료층의 표면에 클로라이트 분말이 첨가된 상도도료를 도포하여 형성된 상도 도료층으로 이루어진 것이 바람직하다.Here, the paint layer is a sanding paint layer formed by applying a sanding paint with the chlorite powder added to the surface of the stain layer, and a medium paint formed by applying a middle paint with the chlorite powder added to the surface of the sanding paint layer It is preferable that it consists of a coating layer and the top coat layer formed by apply | coating the top coat which added chlorite powder to the surface of the intermediate coat layer.
도 1은 본 고안에 따른 건축용 목재의 사시도이다.1 is a perspective view of a building timber according to the present invention.
도 2는 도 1의 I-I선 단면도이다.FIG. 2 is a cross-sectional view taken along line II of FIG. 1.
도 3은 본 고안의 일실시예에 따른 건축용 목재의 제조공정도이다.Figure 3 is a manufacturing process of the building timber according to an embodiment of the present invention.
도 4는 도 3에 나타낸 도료층 형성공정의 상세 공정도이다.4 is a detailed process chart of the coating layer forming step shown in FIG. 3.
도 5는 본 고안에 적용되는 클로라이트 분말의 탈취효과를 나타내는 시험성적서이다.5 is a test report showing the deodorizing effect of the chlorite powder applied to the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
10 : 목재소지 20 : 스테인층10: wood 20: stain layer
30 : 도료층 32 : 샌딩 도료층30: paint layer 32: sanding paint layer
34 : 중도 도료층 36 : 상도 도료층34: middle paint layer 36: top coat layer
먼저 본 고안의 이해를 돕기 위해 클로라이트(Chlorite)와 일라이트(Illite)로 이루어진 클로라이트 분말(Chlorite Powder)과 그 물리학적 성질에 관해 설명한다.First, chlorite powder composed of chlorite and illite and its physical properties will be described in order to help the present invention.
상기 클로라이트 분말은 접촉, 영수, 변성, 점토질 광물로서 클로라이트와 일라이트 두가지 광물이 동일 맥상에서 동시에 혼합 생성된다.The chlorite powder is a contact, an aqueous solution, a modified, clay mineral, chlorite and illite two minerals are simultaneously mixed in the same vein.
상기 클로라이트 분말은 광물학적인 구조가 인편상 점토질 구조를 갖으며,주성분은 SiO2, Al203, K2O, Mg0, Fe2O3로서 황백색, 녹색의 합성광물로 아래와 같은 물리학적 성질을 갖는다.The chlorite powder has a flaky clay structure with a mineralogical structure, and main components are SiO 2 , Al 2 O 3 , K 2 O, Mg0, and Fe 2 O 3, which are yellowish white and green synthetic minerals. Has
상온에서 3∼25 마이크론(㎛) 파장의 원적외선을 89∼92% 방사하고, 도 5에 나타낸 바와 같이 탈취력이 매우 강하다(95%).89-92% of far-infrared rays having a wavelength of 3 to 25 microns (µm) are emitted at room temperature, and as shown in Fig. 5, the deodorizing power is very strong (95%).
상기 원적외선은 세포 활성과 생체에 활력을 불어넣는 가시광선으로 체온 상승과 미세혈관 확장, 세포조직 재생능력 증가, 노화현상을 억제하는 효능이 있다.The far-infrared ray is a visible light that energizes cell activity and the living body, and has an effect of suppressing an increase in body temperature, microvascular expansion, increased tissue regeneration capacity, and aging phenomenon.
또한 클로라이트 분말은 수중에서 물 분자를 활성화시켜 용존산소를 3배이상 확보하고, 산소 응집력이 강하며, 또 수중에서 (-)2가 전하를 가지며 용수중의 유기질 이온을 흡착한다.In addition, chlorite powder activates water molecules in water to secure more than three times of dissolved oxygen, has strong oxygen cohesion, has negative charge in water, and adsorbs organic ions in water.
도한 상기 클로라이트 분말은 자체 함수기능으로 보습효과가 크고 직사 자외선을 방지하며 활도가 높다.In addition, the chlorite powder has a high moisturizing effect due to its own water function, prevents direct ultraviolet rays, and has high activity.
강력한 음이온을 발산하고(건식 분말상태: 141∼500 ion/cc) 균감소율인 항균도가 99.9%로 높다.It emits strong anions (dry powder state: 141 to 500 ion / cc) and has a high antimicrobial degree of 99.9%.
상기 음이온을 충분히 공급받으면 나트륨과 칼슘의 이온화량이 늘어나면서 체질도 알칼리성으로 바뀌어 두통이나 근육통, 피로감이 완화되고 질병에 대한 저항력이 높아진다.When the anion is sufficiently supplied, the amount of ionization of sodium and calcium increases and the constitution also becomes alkaline, thereby reducing headache, muscle pain, fatigue, and increasing resistance to disease.
이하 본 고안의 실시예에 대하여 첨부된 도면을 참고로 그 구성 및 작용을 설명하기로 한다.Hereinafter, the configuration and operation of the embodiments of the present invention will be described with reference to the accompanying drawings.
도 1은 본 고안에 따른 건축용 목재의 사시도이다.1 is a perspective view of a building timber according to the present invention.
도 2는 도 1의 I-I선 단면도이다.FIG. 2 is a cross-sectional view taken along line II of FIG. 1.
목재수지(10)의 적어도 일면에 스테인층(20)과 도료층(30)이 형성된다.A stain layer 20 and a paint layer 30 are formed on at least one surface of the wood resin 10.
도 1이나 도 2에 나타낸 스테인층(20)이나 각 도료층(32,34,36)의 두께는 본 고안의 이해를 돕기 위해 높게 도시한 것일 뿐 실제 각 층의 두께는 100㎛ 내외로 얇은 막(film)이다.The thickness of the stain layer 20 or the paint layers 32, 34, 36 shown in FIG. 1 or FIG. 2 is only high for the purpose of understanding the present invention, but the thickness of each layer is about 100 μm. (film).
상기 스테인층(20)은 목재수지(10)의 적어도 일면에 클로라이트 분말이 첨가된 스테인이 도포되어 형성된다.The stain layer 20 is formed by applying a stain to which chlorite powder is added to at least one surface of the wood resin 10.
이때 목재소지로는 원목, 집성목, 합판, 무늬목과 MDF, PB, 플라이우드(Plywood) 등이 이용된다.At this time, wood materials, solid wood, plywood, veneer and MDF, PB, plywood (Plywood) is used.
상기 스테인(stain)은 목재소지(10)의 바탕에 스며들어서 색을 내게 하기 위한 재료(착색제)로서, 용제의 종류에 따라 알코올 스테인, 오일 스테인, 수성 스테인 등이 사용된다.The stain (stain) is a material (coloring agent) for impregnating the base of the wood substrate 10 to give a color, alcohol stain, oil stain, aqueous stain and the like are used according to the type of solvent.
상기 도료층(film)(30)은 스테인층(20)의 표면에 클로라이트 분말이 첨가된 도료가 도포되어 형성된다.The paint layer 30 is formed by applying a paint to which the chlorite powder is added to the surface of the stain layer 20.
상기 도료(coating)는 표면의 보호, 겉모양, 모양의 변화 등을 목적으로 하여 사용하는 우레탄, 렉카 재료의 일종으로, 유동상태에서 표면에 바른 후 해당 건조 방법에 따라 건조하면 고체의 연속적인 얇은 막이 형성되어 도료층(30)을 형성한다.The coating (coating) is a kind of urethane, Lekka material used for the purpose of protecting the surface, appearance, shape change, etc., when applied to the surface in the fluid state and dried according to the drying method, a continuous thin thin A film is formed to form the paint layer 30.
본 고안에서 상기 도료층(30)은 하도의 샌딩 도료층(32), 중도 도료층(34), 상도 도료층(36)으로 이루어진다.In the present invention, the paint layer 30 includes a sanding paint layer 32, a middle paint layer 34, and a top coat layer 36.
하도 공정으로 사용되는 샌딩(sanding)도료는 목재소지에 투명 래커 도장을 할 때 적합한 액상, 반투명, 휘발 건조성의 도료로서, 상기 샌딩 도료에 클로라이트 분말을 첨가하여 스테인층(20)의 표면에 고르게 도포해서 건조시켜 샌딩 도료층(32)이 형성된다.The sanding paint used in the undercoating process is a liquid, translucent, volatilized and dry paint suitable for the application of transparent lacquer to wood substrates. The sanding paint is added to the surface of the stain layer 20 by adding chlorite powder. It is apply | coated and dried and the sanding coating layer 32 is formed.
상기 샌딩 도료층(32)은 니트로셀룰로오스를 주요 도료층 형성요소로 하여 자연 건조되어 형성되고 연마하기 쉽다.The sanding paint layer 32 is naturally dried by nitrocellulose as a main paint layer forming element, and is easily formed and polished.
중도도료(intermediate coat, barrier coat)는 도료를 거듭 칠하여 도장 마무리할 때의 중간칠에 사용하는 도료로서, 상기 중도도료에 클로라이트 분말을 첨가하여 샌딩 도료층(32)의 표면에 고르게 도포해서 건조시켜 중도 도료층(34)이 형성된다.Intermediate coat (intermediate coat, barrier coat) is a paint used for the intermediate coating when the coating finish by repeatedly coating the paint, by applying chlorite powder to the intermediate paint and evenly applied to the surface of the sanding paint layer 32 and dried The intermediate paint layer 34 is formed.
상기 중도 도료층(34)은 샌딩 도료층(32)과 상도 도료층(36)의 중간에서 양자에 대한 부착성과 내구성을 향상시키며, 하부의 샌딩 도료층(32)이 편평하지 못할 때 이를 보완한다.The intermediate paint layer 34 improves adhesion and durability to both of the sanding paint layer 32 and the top coat layer 36, and compensates when the sanding paint layer 32 is not flat. .
상도도료(top coat)는 도료를 여러번 칠하여 도장 마무리를 할 때 상도로 사용되는 도료로서, 상기 상도도료에 클로라이트 분말을 첨가하여 중도 도료층(34)의 표면에 고르게 도포해서 건조시켜 상도 도료층(36)이 형성된다.A top coat is a paint used as a top coat when the paint finishes by painting several times. The top coat is added with chlorite powder to the top coat to be evenly applied to the surface of the middle paint layer 34, and then dried. 36 is formed.
도 3은 본 고안의 일실시예에 따른 건축용 목재의 제조공정도이다.Figure 3 is a manufacturing process of the building timber according to an embodiment of the present invention.
도 4는 도 3에 나타낸 도료층 형성공정의 상세 공정도이다.4 is a detailed process chart of the coating layer forming step shown in FIG. 3.
먼저 원목이나 MDF와 같은 목재소지(10) 표면의 거친 부분은 연마하여 평활하게 하고, 표면의 기름기나 오염물 및 연마분은 깨끗이 제거하여 건조하는 표면처리 공정을 실행한다(S300).First, the rough part of the surface of the wood base 10 such as solid wood or MDF is polished and smoothed, and the surface oily or contaminants and the abrasive powder are removed and dried to perform a surface treatment process (S300).
표면처리가 끝난 후, 클로라이트 분말을 물에 혼합하여 표면처리가 끝난 목재소지(10)의 적어도 일면에 붓, 롤러 또는 스프레이를 이용하여 직접 도포하여 상온에서 건조한다(S310).After the surface treatment is finished, the chlorite powder is mixed with water and directly applied to at least one surface of the surface-treated wood substrate 10 using a brush, roller or spray to dry at room temperature (S310).
이때 물에 혼합된 클로라이트 분말은 목재소지(10)의 내부로 스며들어 목재소지의 표면에 도막을 형성하지 않게 된다.At this time, the chlorite powder mixed with water does not penetrate into the interior of the wood substrate 10 so as not to form a coating film on the surface of the wood substrate.
다음, 목재소지(10)의 표면을 연마하여 평활하고 청결하게 한 상태에서 수성, 유성 또는 오일 스테인에 클로라이트 분말을 2∼12중량%로 첨가해서 충분히 교반한 후 표면에 붓, 롤러 또는 스페레이를 이용해서 두께 80∼120㎛가 되게끔 1회 이상 도포하여 상온에서 스테인도료의 경화시간만큼 건조함으로써 스테인층(20)이 형성된다(S320).Next, the surface of the wood substrate 10 is ground and smooth and clean, and the chlorite powder is added in an amount of 2 to 12% by weight to an aqueous, oily or oil stain and sufficiently stirred, followed by a brush, a roller or a sprey on the surface. By applying to at least one time to become a thickness of 80 ~ 120㎛ by using to dry the curing time of the stain paint at room temperature to form a stain layer 20 (S320).
이때 1회에 지나치게 두꺼운 스테인층(20)의 도포를 피하고, 2회 이상 도포하는 경우 재도포는 1회 도포후 상온에서 스테인도료의 최소 후속도포가능시간이 경과한 후에 행한다.At this time, the application of the stain layer 20 that is too thick at a time is avoided, and in the case of applying the coating twice or more times, the reapplication is performed after the minimum subsequent coatable time of the stain coating at room temperature after one application.
스테인층(20)의 표면에 클로라이트 분말이 첨가된 도료를 도포하고 건조해서 도료층(30)을 형성하되(S330), 도 4와 같은 공정으로 다수의 도료층(32,34,36)을 형성한다.Applying the paint with the chlorite powder added to the surface of the stain layer 20 to form a coating layer 30 by drying (S330), a plurality of paint layers (32, 34, 36) by the process as shown in FIG. Form.
도 4에서 스테인층(20) 표면을 연마하여 평활하고 청결하게 한 상태에서(S331), 하도 공정으로 샌딩도료에 클로라이트 분말을 2∼12중량%로 첨가해서 충분히 교반한 후, 표면에 붓, 롤러 또는 스프레이를 이용해서 두께 80∼120㎛가 되게끔 1회 이상 도포하여 상온에서 샌딩도료의 경화시간만큼 건조함으로써 니트로셀룰로오스를 주요 도료층 형성요소로 하는 샌딩 도료층(32)이 형성된다(S332).In FIG. 4, the surface of the stained layer 20 was polished to make it smooth and clean (S331). After adding chlorite powder to the sanding paint at 2 to 12% by weight in the undercoat process, the mixture was sufficiently stirred and then brushed on the surface. A sanding coating layer 32 having nitrocellulose as a main coating layer forming element is formed by applying the roller or spray one or more times so as to have a thickness of 80 to 120 μm and drying at room temperature by the curing time of the sanding coating (S332). ).
이때 1회에 지나치게 두꺼운 샌딩 도료층(32)의 도포를 피하고, 2회 이상 도포하는 경우 재도포는 1회 도포후 상온에서 샌딩도료의 최소 후속도포가능시간이 경과한 후에 행한다.At this time, the application of the sanding paint layer 32 that is too thick at a time is avoided, and in the case of applying two or more times, re-coating is performed after the minimum subsequent coating time of the sanding paint has elapsed at room temperature after one time of application.
다음 샌딩 도료층(32)을 연마하여 평활하고 청결하게 한 상태에서(S333), 중도도료에 클로라이트 분말을 2∼12중량%로 첨가해서 충분히 교반한 후, 표면에 붓, 롤러 또는 스프레이를 이용해서 두께 80∼120㎛가 되게끔 도포하여 상온에서 중도도료의 경화시간만큼 건조함으로써 무늬가 형성되는 중도 도료층(34)이 형성된다(S334).Next, the sanding paint layer 32 was polished to be smooth and clean (S333). After adding chlorite powder in an amount of 2 to 12% by weight to the middle paint, the mixture was sufficiently stirred, and then a brush, roller, or spray was applied to the surface. Then, the coating is applied so as to have a thickness of 80 to 120 μm and dried at a room temperature for the curing time of the intermediate coating to form a middle coating layer 34 in which a pattern is formed (S334).
이때 1회에 지나치게 두꺼운 중도 도료층(34)의 도포를 피하고, 2회 이상 도포하는 경우 재도포는 1회 도포후 상온에서 중도도료의 최소 후속도포가능시간이 경과한 후에 행한다.At this time, the application of too thick intermediate coating layer 34 is avoided at once, and in the case of applying twice or more times, reapplication is performed after the minimum possible coatable time of intermediate coating at room temperature after one application.
다음 중도 도료층(34)을 연마하여 평활하고 청결하게 한 상태에서(S335), 상도도료에 클로라이트 분말을 2∼12중량%로 첨가해서 충분히 교반한 후, 표면에 붓, 롤러 또는 스프레이를 이용해서 두께 80∼120㎛가 되게끔 2회 도포하여 상온에서 상도도료의 경화시간만큼 건조함으로써 상도 도료층(36)이 형성된다(S336).Next, in the state of polishing the intermediate paint layer 34 to make it smooth and clean (S335), 2 to 12% by weight of chlorite powder is added to the top coat, and then sufficiently stirred, using a brush, roller or spray on the surface. By coating twice so as to have a thickness of 80 to 120㎛ and dried by the curing time of the top coat at room temperature, the top coat layer 36 is formed (S336).
이때 1회에 지나치게 두꺼운 상도 도료층(36)의 도포를 피하고, 2회 이상 도포하는 경우 재도포는 1회 도포후 상온에서 상도도료의 최소 후속도포가능시간이경과한 후에 행한다.At this time, the application of the too thick top coat layer 36 is avoided at once, and in the case of applying the coat twice or more times, reapplication is performed after the minimum subsequent coatable time of the top coat has elapsed at room temperature after one coat.
이와 같은 공정으로 목재소지(10)의 적어도 일면에 스테인층(20), 샌딩 도료층(32), 중도 도료층(34), 상도 도료층(36)이 차례로 형성된다.In this process, a stain layer 20, a sanding paint layer 32, a middle paint layer 34, and a top coat layer 36 are sequentially formed on at least one surface of the wood substrate 10.
상기 도 3의 실시예에서는 각 공정마다 도료에 클로라이트 분말을 첨가하여 목재소지(10)에 도포하였으나 목재의 사용 위치 및 용도에 따라 하나 이상의 공정에서 클로라이트 분말을 첨가하지 않고 도료만 도포할 수 있다.In the embodiment of FIG. 3, the chlorite powder is added to the paint for each process and applied to the wood substrate 10. However, only the paint may be applied without adding the chlorite powder in at least one process depending on the location and use of the wood. have.
이상에서와 같이 클로라이트 분말이 첨가된 도료를 목재소지(10)에 도포하여 가구나 건축용 내외장재로 사용하면, 클로라이트 분말이 도료의 독성을 차단하고 감소시켜 인체에 유해한 가스의 발생을 중화시켜 준다.As described above, when the paint containing the chlorite powder is applied to the wood base 10 and used as interior or exterior materials for furniture or construction, the chlorite powder blocks and reduces the toxicity of the paint to neutralize the generation of harmful gases to the human body.
또한 도료를 칠하는 원래의 목적인 미생물에 의한 분해 문제를 해결하면서 천연 그대로의 나무무늬를 살릴 수 있다.In addition, while solving the problem of decomposition by microorganisms, the original purpose of painting, it is possible to save the natural wood pattern.
또한, 클로라이트 분말의 항균, 항곰팡이 기능으로 건강하고 쾌적한 주거환경을 제공하고, 강력한 탈취 효과로 실내의 공기를 정화시켜 주며 원적외선 방사와 음이온 방출로 인체의 혈액순환을 촉진시킨다.In addition, the antibacterial and antifungal function of chlorite powder provides a healthy and comfortable living environment, and it cleanses the indoor air by its powerful deodorizing effect and promotes blood circulation of the human body by emitting far infrared rays and anions.
본 고안은 상기에 설명되고 도면에 예시된 것에 의해 한정되는 것은 아니며 특허청구 범위내에서 다양한 변형 및 변용예가 가능한 것임은 물론이다.The present invention is not limited to the above described and illustrated in the drawings, of course, various modifications and variations are possible within the scope of the claims.
상술한 바와 같이 목재 소지와 목재 소지의 일면에 클로라이트 분말이 첨가된 스테인을 도포하여 생성된 스테인층과, 스테인층에 클로라이트 분말이 첨가된 도료를 첨가하여 생성된 도료층을 포함하여 구성된 본 고안에 따른 목재는 다음과같은 효과를 제공한다.As described above, the present invention includes a stain layer formed by applying a stain to which chlorite powder is added to the wood substrate and one surface of the wood substrate, and a paint layer generated by adding a paint to which the chlorite powder is added to the stain layer. The wood according to the design offers the following effects:
첫째, 목재의 표면에 인체에 유익한 클로라이트 분말을 도료에 첨가해서 수회 도포함으로써 미생물에 의한 분해 문제를 해결하고 나무무늬를 그대로 살릴 수 있다.First, by adding chlorite powder, which is beneficial to the human body, to the paint on the surface of the wood several times, the problem of decomposition by microorganisms can be solved and the wood pattern can be saved as it is.
둘째, 도료에 포함된 클로라이트 분말의 탈취, 항균 및 원적외선 방사 효과를 이용해 도료에서 발생하는 인체유해가스를 차단하거나 감소시켜 인체에 유익한 환경을 제공할 수 있다.Second, by using the deodorizing, antibacterial and far-infrared radiation effect of the chlorite powder contained in the paint can block or reduce the harmful gas generated in the paint can provide a beneficial environment for the human body.
Claims (2)