Abstract

PURPOSE: Luminous button capable of effectively preventing traffic accidents, identifying persons in clothes with the button at night, and exhibiting various luminous colors by combination of different luminous materials to derive a new fashion trend is provided. CONSTITUTION: The button is prepared by a process comprising introducing synthetic resin and luminous materials after uniformly admixing them into a centrifugal sheet production device; preparing a solid resin sheet by rotating the device; and punching and cutting the sheet into button blanks. The composition of the luminous material is 1-10wt.% to 100 parts by weight of the synthetic resin.

Description

Method for producing luminous buttons {Method for producing luminous button}

본 발명은 야광단추의 제조에 관한 것으로서, 보다 구체적으로는 보다 개선된 야광특성을 갖는 야광단추를 보다 향상된 생산성으로 제조할 수 있는 방법에 관한 것이다.The present invention relates to the manufacture of a luminous button, and more particularly, to a method for producing a luminous button having improved luminous properties with improved productivity.

일반적으로, 야광단추는 의류에 부착하여 야간 운전중인 운전자가 상기한 의류를 착용한 자를 보다 용이하게 인지할 수 있도록 하거나 의류에 장식효과를 부여하기 위한 것으로, 종래 야광단추는 대한민국 등록실용신안공보 제 20-0179656호 등에 제안된 바와 같이 단추 표면에 야광지를 부착하고 투명 접착제로 코팅하는 것에 의해 제조되어 왔다.In general, the luminous button is attached to the clothing so that the driver driving at night can easily recognize the person who wears the above-mentioned clothing or give a decorative effect to the clothing. 20-0179656 and the like have been produced by attaching a luminous paper to the button surface and coating with a transparent adhesive.

그러나, 이와 같은 종래의 야광단추는 단추 하나에 하나의 야광지를 붙이고 투명코팅을 하여 제조하기 때문에 제조 공정이 복잡하고 많은 작업량을 필요로 하므로 생산성이 불량할 뿐만 아니라 단추의 한쪽 면에서만 야광을 발하게 되므로 야간 운전자가 이러한 야광단추를 인지하는데 다소 어려움이 있는 것이다.However, since the conventional luminous buttons are manufactured by attaching one luminous paper to one button and applying a transparent coating, the manufacturing process is complicated and requires a large amount of work, so that not only the productivity is poor but also luminous is emitted from only one side of the button. It is rather difficult for a night driver to recognize these luminous buttons.

따라서 본 발명이 이루고자 하는 기술적 과제는 종래의 것에 비해 우수한 야광특성을 갖는 야광단추를 보다 향상된 생산성으로 제조할 수 있도록 하는 데에 있다.Therefore, the technical problem to be achieved by the present invention is to be able to manufacture a light-emitting button having excellent luminous properties compared to the conventional one with improved productivity.

상기한 과제를 해결한 본 발명에 의하면 단추제조용 합성수지와 야광 또는 축광물질을 혼합하여 단추 블랭크로 성형한 후 통상의 방법으로 면삭 가공하여 단추모양을 부여하는 것을 특징으로 하는 야광단추의 제조방법이 제공된다.According to the present invention to solve the above problems is a method of manufacturing a luminous button, characterized in that the button manufacturing by mixing the synthetic resin and the luminous or photoluminescent material for the button manufacturing to form a button blank and then surface-treated by a conventional method. do.

이하 본 발명을 보다 상세하게 설명하기로 한다.Hereinafter, the present invention will be described in more detail.

본 발명에 있어서, 단추 제조용 합성수지와 야광 또는 축광물질(이하, 양자를 "야광물질"이라 통칭한다.)의 배합비율은 사용되는 합성수지와 야광물질의 종류에 따라 다를 수 있으나, 일반적으로 합성수지 100중량부당 야광물질 1∼10중량부 정도가 적당하다. 야광물질의 함량이 너무 적으면 충분한 야광특성을 발현시키기에 부적합하며, 야광물질의 함량이 너무 많으면 야광물질이 고가이므로 야광단추의 원가측면에서 바람직하지 않을 뿐만 아니라 단추의 물성이 불량하게 될 수도 있다.In the present invention, the blending ratio of the synthetic resin for button production and luminous or photoluminescent material (hereinafter, both are referred to as "glow material") may vary depending on the type of synthetic resin and luminous material used, but generally 100 weight of synthetic resin About 1-10 weight part of unjust luminous substances are suitable. Too low content of luminous material is not suitable for expressing sufficient luminous properties. Too high luminous material content is expensive because it is expensive and may not be desirable in terms of the cost of the luminous buttons. .

본 발명에서 야광물질은 축광성 또는 자외선 흡수에 수반하여 발광성을 가지는 야광성 또는 형광물질로서, 이러한 야광물질로는 다양한 색상의 것이 당 분야에 잘 알려져 있으며, 야광물질은 수지와 혼련할 수 있는 것이면 그 종류에 관계없이 적용할 수 있고, 서로 다른 색상의 야광물질들을 혼합하여 사용할 수도 있으며, 이러한 경우 젊은 층 대상의 외출복이나 언더웨어 등의 다양한 패션효과를 부여할 수 있는 효과도 얻을 수 있다. 야광물질의 예를 들면 알루민산스트론튬, 황화아연 등이 있다.In the present invention, the luminous material is a luminous or fluorescent material having luminescence accompanied with photoluminescence or ultraviolet absorption. As the luminous material, various colors are well known in the art, and the luminous material may be mixed with a resin. Regardless of its type, it can be applied, and it is also possible to use a mixture of luminous materials of different colors, and in this case, it is also possible to obtain an effect that can give various fashion effects such as going out and underwear for young people. Examples of the luminous material include strontium aluminate, zinc sulfide and the like.

또한 본 발명은 단추 제조에 사용되는 모든 종류의 합성수지를 사용할 수 있으며, 이러한 합성 수지들 중에서도 특히 바람직한 것은 폴리에스테르이다.In addition, the present invention can use all kinds of synthetic resins used in the manufacture of buttons, polyester is particularly preferred among these synthetic resins.

특별히 제한하기 위한 것은 아니지만 단추제조용 합성수지와 야광물질을 혼합하여 단추블랭크를 성형하는 데에는 다음과 같은 방법을 이용하는 것이 바람직하다.Although not particularly limited, it is preferable to use the following method to form a button blank by mixing a synthetic resin for button production and a luminous material.

우선 액체상태의 단추제조용 합성수지와 야광물질을 믹서에 투입하여 균일하게 혼합한다. 이때, 적당량의 경화제, 촉진제 등의 첨가제를 함께 투입하여 함께 혼합하는 것이 바람직하다. 얻어진 혼합물은 대략 30∼40℃의 온도로 가온한 후 원심력을 이용한 시트제조기에 투입한다. 원심력을 이용한 시트제조기에 투입된 원료를 회전시키면 시트제조기 내측면에 밀착되어 액체의 상태에서 서서히 연질 고체상태의 시트가 형성된다. 이와 같이 연질 고체상태로 변한 수지 시트를 시트제조기에서 분리해낸 후 소정 크기로 펀칭 하여 단추블랭크를 제조한다.First, the synthetic resin for manufacturing buttons and the luminous material in the liquid state are added to the mixer and mixed uniformly. At this time, it is preferable to add an appropriate amount of additives such as a curing agent and an accelerator together and mix them together. The obtained mixture is heated to a temperature of approximately 30 to 40 ° C. and then introduced into a sheet maker using centrifugal force. When the raw material introduced into the sheet maker using the centrifugal force is rotated, the raw material is brought into close contact with the inner side of the sheet maker, thereby gradually forming a soft solid sheet in the liquid state. Thus, the resin sheet changed into a soft solid state is separated from the sheet maker, and then punched to a predetermined size to produce a button blank.

이와 같이 제조된 단추블랭크는 건조시킨 후에 통상의 방법으로 면삭 가공하여 단추모양을 부여하게 된다.The button blanks thus prepared are dried and then surface-treated in a conventional manner to impart a button shape.

이하, 본 발명을 바람직한 실시예를 들어 설명하기로 한다. 단, 본 발명은 하기 실시예로 제한되는 것은 아니다.Hereinafter, the present invention will be described with reference to preferred embodiments. However, the present invention is not limited to the following examples.

[실시예]EXAMPLE

폴리에스테르 100중량부, 야광물질로서 알루민산스트론튬 5중량부, 촉진제로서 코발트나프텐산 1중량부 및 경화제로서 메틸에틸케톤퍼옥사이드 1.2 중량부를 믹서로 혼합하고 열통에서 33℃로 가온한 후 30℃로 설정된 원심분리형 시트제조기에 투입하고 1시간 정도 회전시켜 연질 고체상태의 시트를 얻었다. 이 시트를 시트기에 분리해낸 후 펀칭 하여 단추블랭크를 제조하고, 이를 상온에서 잘 건조한 다음 면삭 가공하여 단추를 제조하였다. 제조된 단추는 모든 방향에서, 즉 전면에 걸쳐 우수한 야광특성을 나타냈다.100 parts by weight of polyester, 5 parts by weight of strontium aluminate as luminous material, 1 part by weight of cobalt naphthenic acid as accelerator and 1.2 parts by weight of methyl ethyl ketone peroxide as a curing agent were mixed with a mixer, heated to 33 ° C. in a hot tub, and then heated to 30 ° C. It put into the set centrifugal type sheet maker, it rotated about 1 hour, and the sheet of the soft solid state was obtained. The sheet was separated from the sheet machine and punched to prepare a button blank, which was then dried well at room temperature and then surface-treated to prepare a button. The buttons produced showed excellent luminous properties in all directions, ie over the entire surface.

이상 설명한 바와 같이 본 발명에 의하면 야광특성이 향상된 야광단추를 보다 단순화된 공정 및 높은 생산성으로 제조하는 것이 가능하게 되며, 이와 같이제조되는 본 발명의 야광단추는 교통사고의 방지효과가 우수하고, 등산복 및 낚시 복에 적용할 경우 야영시 식별의 효과가 있으며, 여러 색상의 야광물질을 혼합하여 다양한 칼라의 야광특성을 발현할 수 있어 젊은 층을 대상으로 한 의류나, 언더웨어 등에 적용할 경우 새로운 패션효과를 부여할 수 있는 등의 장점이 있는 것이다.As described above, according to the present invention, it is possible to manufacture a luminous button having improved luminous properties with a simpler process and higher productivity. The luminous button of the present invention manufactured as described above is excellent in preventing traffic accidents and climbing clothes. When applied to fishing and fishing clothes, there is an effect of identification when camping, and it is possible to express various luminous properties of various colors by mixing luminous materials of various colors, and when applied to clothing or underwear for young people, a new fashion effect It can be given such advantages.

Claims

In the manufacture of luminous buttons;

Liquid button manufacturing synthetic resin and luminous material are uniformly mixed, put into a sheet maker using centrifugal force and rotated to obtain a soft solid resin sheet, and punched to a predetermined size to prepare a button blank. To give a button shape,

A method for producing a luminous button, characterized in that the compounding ratio of the synthetic resin for producing buttons and the luminous material is 1 to 10 parts by weight of luminous material per 100 parts by weight of the synthetic resin.