KR20030018284A - Admixture prescription of ocher paint and preparation method - Google Patents

Abstract

PURPOSE: A yellow soil paint composition and its preparation method are provided, which is improved in adhesive strength and coating property and is used to paint the wall of yellow soil. CONSTITUTION: The yellow soil paint composition comprises the yellow soil deposit; and organic synthetic emulsion polysol. Preferably the yellow soil paint composition comprises 8 wt% of polysol 126; 12 wt% of polysol 506; 30 wt% of the yellow soil deposit; and 50 wt% of water.

Description

Prescription and preparation method for admixture of ocher paint

It is an object of the present invention to develop a natural ocher paint with natural ocher color with only natural pure ocher without mixing chemical pigment pigments using natural ocher.

Therefore, the present invention relates to an ocher paint admixture and a manufacturing method which are developed to produce environmentally friendly building materials and to be effectively used for human health promotion that does not inhibit far infrared rays emitted from an inorganic oxide of ocher.

Therefore, our ancestors have learned the usefulness of far-infrared rays and ceramics emitted from inorganic oxides of ocher. It has developed a culture of housing and has enriched our living and eating habits by making containers of earthenware and ceramics to store food and grains.

However, to this day, most of the urban people live in cement-concrete buildings, and the walls, ceilings, and floors are exposed to cold, chill, and moisture.

Therefore, in recent years, as the interest in health has increased, the construction of Hanok using ocher has been actively spreading, but since there is no paint that can complement aesthetic appearance after barking ocher houses, ocher bricks are stacked or plastered and painted. There was a inconvenience not to do. In addition, since the paint or oil paint lacks the adhesion or absorption in the ocher, the life is short and the color is discolored.

It is an object of the present invention to develop a novel method of manufacturing which improves the problems of admixtures and manufacturing methods of ocher paints using the conventional ocher monomaterials described above.

The present invention having the above object is to prevent the strength and cracking or peeling of the ocher brick construction layer by applying the ocher paint to the exterior and inner walls of the modern house as well as the hanok house to extend the life of the building and to complement the aesthetics The intended purpose of the present invention is to be achieved.

1 is the ocher paint admixture and the prescription of the present invention

Figure 2 is a side cross-sectional view of the manufacturing process related to the invention

※ Explanation of code for main part of Figure 2 drawing

(1) crushers (2) ocher sap extractors (3) sediment extractors

(4) paint mixer (5) packing machine

1 is an admixture formulation to be mixed with the ocher paint of the present invention, in which admixtures of (1), (2), (3) and (4) are mixed in accordance with the percentage of prescription.

Thus, the method of mixing the ocher paint admixture by the mixing ratio of the method of manufacturing the cross-sectional view showing the second embodiment of the manufacturing method in the order of (5), (6), (7), (8), and (9) The process is as follows.

According to the present invention, in Fig. 2 (5) the loess is pulverized in the crusher (6) the loess and water are mixed in the loess sap extractor to obtain the loess sap (7) and then sent to the sediment extractor to extract the fine loess sediment. The ocher sediments thus obtained were mixed in the mixer of (8) in accordance with the percentages of (1), (2), (3) and (4) in the prescription for the first degree ocher admixture, and then the packing process was carried out in the packaging machine of (9). It is characterized by the method of manufacturing in place.

Therefore, the ocher paint according to the present invention does not use chemical pigments at all and extracts only the fine ocher sediment as the color of the natural ocher essence, so as to prepare the ocher paint. It is characterized by the fact that it does not occur at all by the discoloration, and it is sufficient to help the strength of the ocher brick, to remove cracks, to beautify aesthetics, and to extend the life.

Claims (2)

Admixtures and prescriptions of ocher paints in Figs. 1 (1), (2), (3) and (4) Manufacturing method manufactured according to the admixture of FIG. 1 and the percentage of prescription in FIG. 1 by the process of FIG. 2 (5), (6), (7), (8), and (9)