KR20020014284A - Method for manufacturing building materials and interior finishing materials using a gypsum - Google Patents

Method for manufacturing building materials and interior finishing materials using a gypsum Download PDF

Info

Publication number
KR20020014284A
KR20020014284A KR1020000047476A KR20000047476A KR20020014284A KR 20020014284 A KR20020014284 A KR 20020014284A KR 1020000047476 A KR1020000047476 A KR 1020000047476A KR 20000047476 A KR20000047476 A KR 20000047476A KR 20020014284 A KR20020014284 A KR 20020014284A
Authority
KR
South Korea
Prior art keywords
gypsum
mixing
plaster
manufacturing
mass
Prior art date
Application number
KR1020000047476A
Other languages
Korean (ko)
Other versions
KR100385343B1 (en
Inventor
허권
이종각
이종경
이순우
Original Assignee
허권
이순우
이종경
이종각
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 허권, 이순우, 이종경, 이종각 filed Critical 허권
Priority to KR10-2000-0047476A priority Critical patent/KR100385343B1/en
Publication of KR20020014284A publication Critical patent/KR20020014284A/en
Application granted granted Critical
Publication of KR100385343B1 publication Critical patent/KR100385343B1/en

Abstract

PURPOSE: A manufacturing method of construction materials and interior finishing materials using plaster is provided to prevent smell or strong alkaline toxicity of concrete from contacting the human body directly and to have effects on deodorizing or controlling moisture by mixing plaster with porous elvan or a germanium oxide. CONSTITUTION: A manufacturing method of construction materials and interior finishing materials using plaster comprises the steps of: manufacturing a plaster admixture by mixing plaster and natural materials of an appointed quantity in proportion to the quantity of the plaster; manufacturing a mixed liquor by mixing water, sulfate of aluminum oxide, high-range water reducing agent and cellulose of an appointed quantity in proportion to the quantity of the plaster; after mixing and kneading the manufactured plaster admixture and the mixed liquor, molding in a mold form having an appointed shape within the time limit of 3 minutes to 1 hour or forming directly to a wall or a floor; and drying the shaped product or the formation surface for 2-48 hours.

Description

석고를 이용한 건축 자재 및 내부 시공 재료의 제조방법{Method for manufacturing building materials and interior finishing materials using a gypsum}Method for manufacturing building materials and interior finishing materials using a gypsum}

본 발명은 석고를 이용한 건축자재 및 내부 시공 재료를 제조하는 방법에 관한 것으로, 보다 상세하게는 석고와 천연물을 혼합하여 응결 성형함으로써 석고를 결합재로 사용한 내부 시공재료를 제조할 수 있으며, 응결된 석고가 황토나 콘크리트와는 달리 표면에 분진을 가지고 있고, 강도면에서도 비교적 큰 값을 가지므로 테니스 코트 등에 적용될 수 있는 건축자재 및 내부 시공 재료를 제조하는 방법에 관한 것이다.The present invention relates to a method for manufacturing building materials and internal construction materials using gypsum, and more specifically, it is possible to manufacture internal construction materials using gypsum as a binder by condensation molding by mixing gypsum and natural products, and condensed gypsum. Unlike ocher or concrete, it has a dust on the surface and has a relatively large value in terms of strength, and thus relates to a method of manufacturing building materials and internal construction materials that can be applied to a tennis court.

일반적으로, 석고는 천연석고와 산업체 부산물인 화학석고로 나눌 수 있다. 천연 석고는 현재 국내에서는 수입에 의존하고 있으나 화학석고는 국내에서 많이 생산되고 있다. 천연석고의 주산지는 주로 미국, 캐나다, 프랑스 러시아 등이며 석고는 결정수의 결합 형태에 따라 이수석고 반수석고, 무수석고로 구분되는데 천연 석고의 경우 무수석고와 이수석고로 얻어진다. 화학석고 역시 불산 석고를 제외한 인산부산석고, 배연탈황석고, 및 티탄석고는 이수석고로 얻어지며 불산 석고는 무수석고로 얻어진다.In general, gypsum can be divided into natural gypsum and chemical gypsum, an industrial by-product. Natural gypsum currently depends on imports in Korea, but chemical gypsum is produced in Korea. Natural gypsum is mainly produced in the United States, Canada, France, Russia, etc. Gypsum is divided into dihydrate gypsum and half gypsum and anhydrous gypsum. Chemical gypsum is also obtained from phosphate gypsum, flue gas desulfurization gypsum, and titanium gypsum, except for hydrofluoric acid gypsum.

한편 예로부터 우리 나라의 전통적인 건축자재로는 돌과 흙이 주로 사용되어 왔다. 흙은 자체온도 조절능력이 뛰어나고 원적외선을 방출하며 각종 박테리아가 기생할 수 있고 점성을 가질 수 있으므로 결합재로 사용되어 왔었다. 그러나 결합력이 약하고 물에 접촉되었을 때 쉽게 유실되므로 사용에 제한적일 수밖에 없었다.On the other hand, stone and soil have been mainly used as traditional building materials in our country. Soil has been used as a binder because it has excellent temperature control, emits far-infrared rays, and can be parasitic and viscous. However, the binding force was weak and easily lost when contacted with water, which was limited to use.

돌은 난방을 위한 구들이나 벽체 등에 사용되었다. 돌이 충분히 열을 받아 원적외선을 방출할 때 인체에 많은 치료효과가 있다고 알려져 있다. 그러나 최근의 여러 복잡한 생활 양상에 따라 많은 현대식 건축물이 필요하여 콘크리트를 이용한 건축물이 대량으로 건립되게 되었다. 그러나 이런 대량의 콘크리트 건축 구조물은 화학적 작용에 의해 인체에 많은 역작용을 일으키고 있다. 특히 콘크리트가 갖는 독성에 의한 것이다. 콘크리트는 액성이 강한 알칼리성이며 콘크리트가 건조될 때 암모니아와 소량의 알데히드(aldehyde)가 방출되는 것으로 알려져 있다. 따라서 콘크리트로 건설된 구조물에 들어갔을 때 매캐한 냄새가 나기도 하며 심하면 신축된 집이나 구조물에서는 1년 이상 두통과 현기증 또는 알레르기를 일으킬 수 있다. 최근 이와 같은 부작용을 줄여 보고자 황토 페인트를 벽면에 칠하기도 하고, 콘크리트가 아닌 마감재를 이용하여 최대한 콘크리트 독을 해소하고자 노력하고 있다. 우리나라는 4계가 뚜렷하고 계절별로 온도차가 심하므로 방바닥을 가열하여 난방한다. 과거에는 돌과 흙을 바닥재로 사용하였으나 최근 콘크리트를 사용하므로 콘크리트 독에 완전히 노출된 상태라고 할 수 있다.Stone was used for heating spheres and walls. It is known that when the stone is heated enough to emit far infrared rays, there are many therapeutic effects on the human body. However, according to the recent complicated life patterns, many modern buildings are required, and concrete-based buildings have been built in large quantities. However, these mass concrete building structures are causing a lot of adverse reactions to the human body by chemical action. Especially due to the toxicity of concrete. It is known that concrete has a strong liquidity and releases ammonia and a small amount of aldehyde when the concrete is dried. Therefore, when entering a concrete structure, it may have a smoky smell, and even a newly built house or structure may cause headaches, dizziness or allergies for more than a year. Recently, in order to reduce such side effects, ocher paint may be painted on walls, and efforts are made to resolve the concrete poison as much as possible by using a non-concrete finish. In Korea, the four systems are distinct and the temperature difference is severe according to the season. In the past, stone and soil were used as flooring materials. However, since concrete is recently used, it is completely exposed to concrete docks.

이와 같은 콘크리트 독에 직접 노출되지 않게 하기 위해서는 콘크리트를 황토 등으로 도포하는 것이 좋은 방법이며, 이런 노력의 하나로 석고보드 등을 들 수 있으나 석고보드의 경우 인장력을 높이기 위하여 암면이나 기타 유해한 물질이 사용되는 경우가 종종 있으며 시공에 있어서도 벽면에 덧붙여 마감하는 재료로만 이용되고 있는 문제점이 있다.In order to prevent direct exposure to the concrete dock, it is a good idea to apply concrete with ocher, etc. One such effort is gypsum board, but in the case of gypsum board, rock wool or other harmful substances are used to increase tensile strength. Sometimes there is a problem that is used only as a material for finishing the wall in addition to the construction.

본 발명은 상기와 같이 벽체를 제품화된 석고보드만을 사용하여야하는 문제점이나 방바닥 등을 직접 시공할 수 없는 문제점 등을 해결하기 위하여 발명된 것으로, 석고에 천연물인 맥반석이나 게르마늄산화물을 첨가하고 또는 이들 둘을 같이 혼합하여 황산반토를 용해한 물에 반죽하여 직접 시공하여 내부 시공재료로 사용하거나 일정한 거푸집을 이용하여 성형함으로써 건축자재로 활용하는 방법을 제공한다.The present invention has been invented to solve the problem of using only the gypsum board made of the wall product as described above, or the problem of not being able to directly install a floor, and the like, adding a natural product of ganban stone or germanium oxide to the gypsum or both. And kneading together in water dissolved in alumina sulfate to construct directly and use it as an internal construction material or by using a certain formwork to provide a method of utilizing as a building material.

이를 위하여 방바닥이나 벽체를 석고로 도포하되 석고 내에 맥반석, 게르마늄산화물 등의 천연 다공성 물질을 첨가하고 인장 강도를 높이기 위하여 천연 cellulose를 0.5mm∼2mm의 섬유로 된 것을 혼용하는 방법을 사용하였다. 한편 시공시 작업성을 높이고 도포된 면의 석고 구조가 치밀한 구조를 갖도록 유동성을 높이는 유동화제를 사용하였다. 유동화제는 멜라민 설폰산의 알데히드 축합물이나 나프탈렌 설폰산의 알데히드 축합물을 사용하였다. 검은 색을 나타내기 위하여 철의 산화물인 마그네타이트를 사용할 수 있고, 푸른색을 나타내기 위하여 푸른색의 염료를 사용할 수 있다. 이와 같은 염료나 산화물을 사용하여도 콘크리트에서와는 달리 강도에 큰 영향이 없는 것으로 나타났다. 시공시 강도 발현시간을 조절하기 위하여 황산반토를 소량 사용한다. 앞에서 얻은 여러 혼합물을 물과 반죽하여 직접 벽체나 방바닥, 또는 테니스 코트 면을 시공할 수도 있으나 반죽된 몰탈을 거푸집이나 형틀에 성형시켜 타일이나 보도 블럭을 시공하는 것처럼 시공할 수도 있다.For this purpose, the floor or wall was coated with gypsum, but natural porous cellulose, such as ganbanite and germanium oxide, was added to the gypsum and natural cellulose mixed with 0.5mm ~ 2mm fiber was used to increase tensile strength. On the other hand, a fluidizing agent was used to increase workability during construction and to increase fluidity so that the gypsum structure of the coated surface has a dense structure. As the fluidizing agent, an aldehyde condensate of melamine sulfonic acid or an aldehyde condensate of naphthalene sulfonic acid was used. Magnetite, an oxide of iron, may be used to represent black, and a blue dye may be used to represent blue. The use of these dyes and oxides did not appear to have a significant effect on strength, unlike in concrete. A small amount of alumina sulfate is used to control the strength development time during construction. You can knead several of the mixtures previously obtained with water to build walls, floors, or tennis courts directly, but you can also apply kneaded mortar to your formwork or mold to build tiles or sidewalk blocks.

도 1은 본 발명에 따른 석고를 이용한 건축 자재 및 내부 시공 재료의 제조방법을 보여주기 위한 순서도이다.1 is a flow chart illustrating a method of manufacturing a building material and the internal construction material using gypsum according to the present invention.

상기와 같은 본 발명의 목적을 달성하기 위해서 본 발명은,In order to achieve the object of the present invention as described above, the present invention,

석고와 석고 질량에 비례한 일정량의 천연물질을 혼합하여 석고 혼합물을 제조하는 단계;Preparing a gypsum mixture by mixing gypsum with an amount of natural material proportional to the gypsum mass;

석고 질량에 비례한 일정량의 물에 석고 질량에 비례한 일정량의 황산반토, 유동화제 및 섬유소(cellulose)를 혼합하여 혼합액을 제조하는 단계;Preparing a mixed solution by mixing a predetermined amount of water proportional to the gypsum mass with a predetermined amount of alumina sulfate, a fluidizing agent and cellulose in proportion to the gypsum mass;

제조된 석고 혼합물과 혼합액을 혼합하여 반죽한 후 3 분∼1시간의 시간 범위내에서 일정 형상을 갖는 거푸집에서 성형하거나 또는 벽체 및 바닥면에 직접 시공하는 단계;Mixing and kneading the prepared gypsum mixture and the mixed solution and then molding in a mold having a predetermined shape within a time range of 3 minutes to 1 hour, or directly applying to a wall and a bottom surface;

성형된 제품이나 시공된 면을 2 ∼ 48 시간 동안 건조시키는 단계를 포함한다.Drying the molded article or the constructed side for 2 to 48 hours.

본 발명에 따른 석고에 천연물인 맥반석이나 게르마늄산화물을 첨가하고 또는 이들 둘을 같이 혼합하여 황산반토를 용해한 물에 반죽하여 직접 시공하거나 일정한 거푸집을 이용하여 성형함으로써 건축자재로 활용하는 방법은 콘크리트 독을인체와 직접 접촉하지 않도록 할 수 있다. 또한 석고에 원적외선을 발산할 수 있는 다공성의 맥반석을 첨가하므로써 흡취 또는 습도조절 등의 효과를 동시에 얻을 수 있다.The method of using as a building material by adding a natural product of ganban stone or germanium oxide to the gypsum according to the present invention, or mixing them together and kneading them in water dissolved in alumina sulphate, or constructing them by using a regular formwork is a concrete dock. You can avoid direct contact with the human body. In addition, by adding a porous ganban stone that can emit far infrared rays to the gypsum can be obtained at the same time, such as absorption or humidity control.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하면 다음과 같다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

첨부된 도 1은 본 발명에 따른 석고에 천연물인 맥반석이나 게르마늄산화물을 첨가하고 또는 이들 둘을 같이 혼합하여 황산반토를 용해한 물에 반죽하여 직접 시공하거나 일정한 거푸집을 이용하여 성형함으로써 건축자재로 활용하는 방법을 보여주기 위한 순서도이다.1 is attached to the gypsum according to the present invention by adding a natural product of ganban stone or germanium oxide or mixing them together and kneading in water dissolved in alumina alumina to be applied directly or molded using a regular formwork to utilize as a building material This is a flowchart to show how.

도 1에 도시한 바와 같이, 본 발명은 석고에 천연물인 맥반석이나 게르마늄산화물을 첨가하고 또는 이들 둘을 같이 혼합하여 황산반토를 용해한 물에 반죽하여 시공재료로 이용하거나, 석고 반죽을 일정한 거푸집을 이용하여 성형함으로써 건축자재로 활용하게 된다.As shown in FIG. 1, the present invention adds natural ganban stone or germanium oxide to gypsum or mixes them together to knead alumina sulphate-dissolved water to use as a construction material, or to use a plaster mold as a formwork. It is used as a building material by molding.

이를 위하여 먼저 석고에 일정량의 맥반석이나 게르마늄산화물등 천연물질을 석고와 혼합하여 석고 혼합물을 제조한다. 이후에 물에 일정량의 황산반토, 유동화제 및 섬유소(cellulose)를 혼합하여 혼합액을 제조한다.For this purpose, a gypsum mixture is prepared by first mixing gypsum or germanium oxide with a certain amount of gypsum. Thereafter, a predetermined amount of alumina sulfate, a fluidizing agent, and cellulose are mixed with water to prepare a mixed solution.

바람직하게 석고 혼합물은 순수한 석고에 천연 물질을 맥반석이나 게르마늄산화물을 하나 또는 그 이상을 석고 질량의 0∼80%를 칭량하여 이를 석고 분말과 혼합하여 제조하며, 혼합액은 석고 질량의 30∼70% 정도의 물(水)에 멜라민 설폰산의 알데히드 축합물이나 나프탈렌 설폰산의 알데히드 축합물의 유동화제를 석고 질량의 0.3∼2% 정도 첨가하고, 황산반토를 석고 질량의 0.5∼20% 정도 첨가하여 제조한다. 혼합액에는 인장강도를 높이기 위하여 석고 질량의 0∼10%의 cellulose 섬유를 물에 더 첨가시켜 반죽할 수도 있다.Preferably, the gypsum mixture is prepared by mixing gypsum powder or natural substance with one or more of gypsum or germanium oxide in pure gypsum and weighing it with 0 to 80% of the gypsum mass and mixing it with gypsum powder, and the mixture is about 30 to 70% of the gypsum mass. The fluidizing agent of an aldehyde condensate of melamine sulfonic acid or an aldehyde condensate of naphthalene sulfonic acid is added to water of about 0.3 to 2% of the gypsum mass, and alumina sulfate is added to about 0.5 to 20% of the gypsum mass. . The mixed solution may be kneaded by further adding 0-10% of cellulose fibers to the water to increase tensile strength.

이와 같이 제조된 석고 혼합물과 혼합액을 혼합하여 반죽한 후 3 분∼1시간의 시간 범위 내에서 일정 형상을 갖는 거푸집에서 성형하여 건축자재를 제조하거나 또는 석고 혼합물과 혼합액을 혼합한 반죽을 방바닥이나 벽체를 직접 시공하는 내부 시공재료로 이용된다. 이후에 거푸집등을 통하여 성형된 제품 즉, 건축자재나 내부 시공재료로 시공된 면을 2 - 48 시간 동안 건조시킨다.After kneading by mixing the gypsum mixture and the mixed solution prepared in this way, the building material is manufactured by molding in a mold having a certain shape within a time range of 3 minutes to 1 hour, or a dough or a mixture of the gypsum mixture and the mixed solution is coated on the floor or wall. It is used as an internal construction material for direct construction. Thereafter, the molded product, ie, the surface of the building material or the internal construction material, is dried for 2 to 48 hours.

이상에서와 같이 본 발명에 따른 석고를 이용하여 내장 마감재 및 바닥 마감재를 제조하는 방법은 석고를 결합재로 이용하고 여기에 다공성의 물질을 혼합시켜 콘크리트의 독소가 인체에 직접 접촉하지 않도록 할 수 있는 할 수 있으므로 건강에 좋은 영향을 미칠 수 있다.As described above, the method for manufacturing the interior finishing material and the floor finishing material using the gypsum according to the present invention is to use the gypsum as a binder and to mix the porous material therein so that the toxins in the concrete do not directly contact the human body. It can have a good effect on your health.

또한, 본 발명에 따른 석고를 이용한 건축 자재의 제조방법중 예를 들어 테니스 코트의 바닥면을 시공하는 방법은 바닥면이 콘크리트로 시공된 면과는 달리 관절이나 무릎 등에 무리를 주지 않을 뿐 아니라 테니스 공의 튀김현상도 진흙으로 시공된 면과 유사하고 바닥면이 빗물 등에 저항성이 크므로 내구성도 크게 증진될 것으로 기대된다.In addition, in the method of manufacturing the floor surface of the tennis court, for example, the manufacturing method of the building material using plaster according to the present invention, unlike the surface of the floor is constructed of concrete, not only do not impart a joint or knee, but also tennis The frying phenomenon of the ball is similar to that of mud and the bottom surface is highly resistant to rain, so durability is expected to be greatly improved.

이상에서 설명한 바와 같이, 본 발명에 따른 석고를 이용한 건축 자재 및 내부 시공재료의 제조방법은 석고에 천연물인 맥반석이나 게르마늄산화물을 첨가하고또는 이들 둘을 같이 혼합하여 황산반토를 용해한 물에 반죽하여 직접 시공하거나 일정한 거푸집을 이용하여 성형함으로써 콘크리트 독이 인체와 직접 접촉하지 않도록 할 수 있으며, 석고에 원적외선을 발산할 수 있는 다공성의 맥반석을 첨가하므로써 흡취 또는 습도조절 등의 효과를 동시에 얻을 수 있으므로, 훌륭한 내장 마감재 및 바닥 마감재가 된다.As described above, the manufacturing method of the building material and the interior construction material using the gypsum according to the present invention is added to the gypsum by dissolving alumina sulfate in water by adding a natural machstone or germanium oxide to the gypsum or by mixing them together It is possible to prevent the concrete dock from coming into direct contact with the human body by constructing it or by using a regular formwork, and by adding porous elvan stones that can emit far infrared rays to the gypsum, it is possible to obtain effects such as absorption or humidity control at the same time. Finishes and floor finishes.

또한, 석고를 이용한 건축 자재는 콘크리트로 시공된 면과는 달리 충격 흡수성이 뛰어나 관절이나 무릎 등에 무리를 주지 않을 뿐 아니라 바닥면이 빗물 등에 저항성이 크므로 내구성도 크게 증진되므로 테니스코트 등에 사용하기가 적합하다.In addition, unlike the concrete construction surface, gypsum building materials are excellent in shock absorption and do not stress the joints or knees. Suitable.

상술한 바와 같이 본 발명은 상기 실시예에 한정되지 않고, 본 발명의 기술적 요지를 벗어나지 않는 범위내에서 당업자에 의해 다양하게 변형시켜 실시할 수 있다.As described above, the present invention is not limited to the above embodiments, and various modifications can be made by those skilled in the art without departing from the technical gist of the present invention.

Claims (4)

ⅰ)석고와 상기 석고 질량에 비례한 일정량의 천연물질을 혼합하여 석고 혼합물을 제조하는 단계;Iii) preparing a gypsum mixture by mixing gypsum with an amount of natural material proportional to the gypsum mass; ⅱ)상기 석고 질량에 비례한 일정량의 물에 상기 석고 질량에 비례한 일정량의 황산반토, 유동화제 및 섬유소(cellulose)를 혼합하여 혼합액을 제조하는 단계;Ii) mixing a predetermined amount of water in proportion to the gypsum mass with a predetermined amount of alumina sulfate, a fluidizing agent and cellulose in proportion to the gypsum mass to prepare a mixed solution; ⅲ)상기 단계에서 제조된 석고 혼합물과 혼합액을 혼합하여 반죽한 후 3 분∼1시간의 시간 범위내에서 일정 형상을 갖는 거푸집에서 성형하거나 또는 벽체 및 바닥면에 직접 시공하는 단계;Iii) mixing and mixing the gypsum mixture prepared in the above step with the mixed solution and then molding in a mold having a certain shape within a time range of 3 minutes to 1 hour, or constructing directly on a wall and a bottom surface; ⅳ)성형된 제품이나 시공된 면을 2 - 48 시간 동안 건조시키는 단계를 포함하는 석고를 이용한 건축 자재 및 내부 시공재료의 제조방법.Iii) a method of manufacturing building materials and internal construction materials using gypsum comprising the step of drying the molded product or the constructed surface for 2 to 48 hours. 제 1항에 있어서, 상기 ⅰ단계는 석고분말과 상기 석고 분말의 전체 질량 0-80%의 범위내에서 천연 산화물이나 맥반석, 옥석을 투입하고 이를 혼합하는 단계인 것을 특징으로 하는 석고를 이용한 건축 자재 및 내부 시공재료의 제조방법.The gypsum building material according to claim 1, wherein the step (b) is a step of injecting natural oxide, elvan, and gemstones into the gypsum powder and the gypsum powder in the range of 0-80% of the total mass and mixing them. And a method of manufacturing the internal construction material. 제 1항에 있어서, 상기 ⅱ단계는 상기 석고 질량의 30∼70% 정도의 물에 황산반토를 상기 석고 질량의 0.5 - 20%의 범위내에서 용해하고 석고가 응결된 후 인장강도를 보완하고 동결융해에 대한 저항성을 갖도록 상기 석고 질량의 0∼10%의범위내에서 0.5∼2mm의 섬유소(cellulose)를 혼합하는 단계인 것을 특징으로 하는 석고를 이용한 건축 자재 및 내부 시공재료의 제조방법.The method of claim 1, wherein the step ii is to dissolve alumina sulfate in water of about 30 to 70% of the gypsum mass within the range of 0.5 to 20% of the gypsum mass, and to supplement the tensile strength and freeze after the gypsum is solidified A method of manufacturing a building material and internal construction material using gypsum, characterized in that the step of mixing the cellulose of 0.5 to 2mm in the range of 0 to 10% of the gypsum mass to have resistance to melting. 제 1항에 있어서, 상기 ⅰ단계의 천연물질은 다공성의 원적외선 방출량이 비교적 큰 맥반석, 옥석, 게르마늄산화물중 하나 또는 하나 이상의 혼합물인 것을 특징으로 하는 석고를 이용한 건축 자재 및 내부 시공재료의 제조방법.The method of claim 1, wherein the natural material of step ⅰ is a gypsum stone, jade stone, germanium oxide or a mixture of one or more of the far-infrared emission of the porous is relatively large.
KR10-2000-0047476A 2000-08-17 2000-08-17 Method for manufacturing building materials and interior finishing materials using a gypsum KR100385343B1 (en)