KR20010020709A - Reinforced wood bat - Google Patents

Abstract

PURPOSE: A reinforced wood bat is provided to endow the appearance and the characteristics similar to those of existing wood bats, to improve the resistance against breaking and damage due to batting, and to reduce the cost of manufacturing by adopting a simple method. CONSTITUTION: One or more continuous layers(14) made of sleeves formed in a net shape from high-strength fibers by use of a mounting tube are affixed to approximately the overall outer surface of a wood core(12) made slightly smaller than a normal wood bat, so as to form a preformed bat assembly. A thermally compressible plastic tube is put over the preformed bat assembly and thermally compressed to form a mold, into which a setting resin is injected and set to form a reinforced wood bat(10).

Description

Reinforced Wood Bats {REINFORCED WOOD BAT}

The present invention generally relates to a wooden bat reinforced with an outer surface for hitting a ball such as a baseball and a soft ball, and a manufacturing method thereof. More specifically, the present invention is a coating of a composite material comprising high strength fibers and resins and covered with a thin layer on the outer surface of a wooden core, with a solid reinforced outer periphery from the knob or lower end to the upper or outer end. ) Wood batting and manufacturing method. The fiber strand of the fuselage portion of the reinforced bat is in the form of a net oriented diagonally, and the fiber strand of the handle portion is more in the form of a net oriented in the longitudinal direction of the bat.

Baseball bats and softball bats have been made of wood since the beginning of organized baseball games and baseball leagues. Wood bats were manufactured using conventional lathe processing techniques and their standard outline dimensions were developed along with the standard weight properties for wood bats. In addition, hollow aluminum bats have been developed and used by many young athletes, and certain regulations relating to particular leagues and age groups require hollow aluminum bats. In addition, hollow plastic bats have been developed for use in practice and training in younger age groups. Typically, such plastic batts are used with lightweight hollow plastic balls, rubber balls and the like.

U.S. Pat. 4,844,460, 5,114,144 and Canadian Patent No. 962291 show a variety of developed batting bats.

The main disadvantage of solid wood bats is that they are relatively expensive and often break when used. Thus, over the past few years, the weight, size, strength, stiffness, and flexibility within acceptable weight and size parameters are suitable for exerting good performance characteristics, but not only standard solid wood bats, but also extruded aluminum bats. Many attempts have been made to develop longer-lasting reinforced wooden bats. For example, the diameters of certified wooden bats do not exceed 2.75 inches.

As one of these prior attempts, in a wooden bat disclosed in US Pat. No. 3,129,003 to Wheeler et al., The fiberglass sleeve is pressed against the handle portion of the wooden bat and the plastic coating It is applied to the sleeve to fix the sleeve in place. In Baum, U. S. Patent No. 5,114, 144, a knitted or woven fabric layer of high strength fibers impregnated with resin is attached to a bat-shaped central core made of foamed plastic or extruded aluminum. The resin forms a monolith while attaching the outer layer of resin-coated wood planks and placing the composite in the split mold to pressurize the split mold together. US Pat. No. 3,598,410 to Costopoulos discloses a wood bat consisting of a plurality of individual thin layers wound spirally in a surface groove and having high tensile multi-fiber filaments. Finally, US Pat. No. 5,301,940 to Seki discloses resin injection techniques for attaching continuous reinforcing fibers and molding materials to the outer surface of bat cores made using soluble materials or foamed resins.

However, none of the prior art patents disclose a reinforced wooden bat of the features of the present invention. In particular, the prior art does not disclose a reinforced solid wood bat comprising a continuous sleeve made of high strength fiber resin and bonded over almost the entire outer surface of the wood bat. In addition, the prior art does not disclose a combination scheme in which the braided sleeve is attached to the solid wood core in two or more layers covering almost the entire outer surface of the bat. In addition, the prior art provides a high-strength composite sleeve that adheres to the surface of the shaved wood core and the shaved wood core to slightly smaller dimensions in order to ensure that the finished bat is restored to the standard dimension size specified for the original wood bat. Does not disclose a combination method of forming a standard size of a predetermined wooden bat.

It is an object of the present invention to include a wooden bat core and high strength fibers whose shape and arrangement are the same as conventional wooden bats but whose dimensions are slightly smaller than conventional wooden bats of standard size and adhere over almost the entire outer surface of the wooden core. It is to provide a reinforced wooden bat for hitting a ball, such as baseball, softball, consisting of a thin layer of reinforced composite material, the outer dimensions of which form a finished product batter that is the same as a conventional wooden bat of standard size.

Another object of the present invention is to provide a high strength fiber impregnated with a transparent curable resin that interacts with a wooden core to exhibit the same appearance and impact properties as a conventional wooden bat, while significantly reducing breakage and damage due to contact with the hitting ball. It is to provide a reinforced wood bat as described in the above object, wherein a continuous layer of one or more fabric sleeves consisting of strands forms a thin layer of reinforcing composite. Indeed, testing of the endurance life of the bat of the present invention revealed no bats in fact broken.

It is a further object of the present invention to provide a reinforced wood bat as described in the above object, wherein a continuous layer of two or more reinforcing braid sleeves made of fiberglass strands is glued over almost the entire outer surface of the wood core.

Another object of the invention is that the high strength fiberglass strands are oriented in a diagonal net of + 45 ° / -45 ° in the fuselage section striking the ball in the longitudinal direction or 0 ° in the handle section and in the fuselage section of the bat. It is an object of the present invention to provide the reinforced wooden bat described in the above-described object, wherein the impact property is improved in the handle portion at break resistance.

It is a further object of the present invention that the support extensions formed in the lathe machining support the work of attaching fiberglass strands on a wooden core to orient it and the lamination of the reinforcement composite laminate to the wooden core. To provide a wooden bat.

Another object of the present invention is the reinforced wooden bat described in the above-mentioned object, which improves the operation of bonding the reinforcing composite to the wooden core by cutting the longitudinally extending groove symmetrically along the circumference of the handle portion of the bat. To provide.

Yet another object of the present invention is to form a wooden core in the shape of a bat with a slightly smaller outline size and to place a continuous layer of one or more fiberglass sleeves over substantially the entire core to form a preformed bat assembly. It is to provide a method for producing a reinforced wooden bat of the method. The preformed bat assembly is then placed in a mold, the curable resin applied to the layer of the fiberglass sleeve, and the resin cured so that the fiberglass layer adheres to the outer surface of the bat core to form a thin layer, the conventional dimensions of which You will form a reinforced wooden bat of the finished product that exactly matches your wooden bat.

Another object of the present invention is to form a wooden core to include a support extension in lathe processing extending longitudinally from its respective end in a conventional manner, and using the attachment tube and the support extension as a handle to A method of making a reinforced wooden bat using a preformed bat assembly in such a way that the two or more layers of fiberglass braided sleeves spread over almost the entire outer surface of the wooden core. The fiberglass sleeve is then impregnated with a curable resin, and the resin is cured to form a thin layer of reinforcement sleeve to adhere firmly to the wood core, thereby forming an integral bat structure.

Yet another object of the present invention is to adhere a mold for applying an epoxy resin suitable for a preformed bat assembly in which glass fibers are located on the surface of a wooden bat core, to closely fit a high shrink plastic tube to the preformed bat assembly. By simultaneously stretching and heat shrinking to form a tubular plastic mold, while injecting curable resin into the tubular mold and applying head pressure to form a hollow tube extension for wetting the glass fibers prior to curing. In another aspect, there is provided a method for producing a reinforced wooden bat formed from a high heat shrink tube.

Another object of the present invention is to pour the epoxy resin into the hollow tube extension of the tubular plastic mold, and then insert a heat absorber into the hollow tube extension, thereby attenuating the exothermic reaction of the epoxy resin and preliminarily before curing the resin. SUMMARY OF THE INVENTION It is to provide a method of making a reinforced wooden bat according to the above object in such a way that the glass fibers of the molded bat assembly can be wetted over a sufficient time.

Yet another object of the present invention is to invert the tubular plastic mold containing the preformed bat assembly with the glass fiber wetted with epoxy resin upside down and hold it by a mounting tool that supports the bat directly underneath the knob. It is to provide a method of making a reinforced wooden bat according to the aforementioned two objectives just prior to the manner in which the resin and glass fibers are better filled at the interface of the handle / knob.

It is yet another object of the present invention to provide a plurality of circular grooves in the fuselage portion by further adding resin to the fuselage end of the bat to help extend the life of the bat. The grooves have transverse transitions or chamfered edges on their inner and outer sides.

1 is an elevational view of the reinforced wooden bat of the present invention in which the barrel portion of the bat is cut away to show the composite laminate on the wooden core,

2 is an elevational view of the wooden core of the present invention with broken lines indicating the circular size of a conventional standard size wooden bat,

3 is an elevational view of the preformed bat assembly of the present invention with two layers of suitable fiberglass braid sleeves spread over the entire wood core;

4 is an enlarged perspective view of a knob and handle portion of the preformed bat assembly shown in FIG. 3;

5 is an enlarged perspective view of the fuselage or outer end of the preformed bat assembly shown in FIG.

6 is a partial cross-sectional view of the body or tip of the bat showing that the tip of the bat is substantially covered by a thin layer of reinforced composite;

7 is a partial cross-sectional view of the handle end of a bat showing that the knob of the bat is substantially covered by a thin layer of reinforcement composite,

8 is an enlarged front view of a portion of a braided sleeve according to the present invention in the form of a suitable braid;

9 is a partial cross-sectional side view showing an attachment tube according to the present invention, with a wooden core ready to be inserted for receiving a first layer of fiberglass sleeve;

10 shows attachment with the first layer of fiberglass sleeve snugly fitted on the outer surface of the wooden core by rubbing the support extension at the outer leading end of the bat so that the wooden core is again ready to receive the second layer. Partial cross-sectional side view showing a wooden core fully inserted into the tube,

FIG. 11 is another partial cross sectional side view similar to FIGS. 9 and 10 showing that the wood core is removed from the attachment tube so that the second layer of fiberglass sleeve is attached on the outer surface;

12 is a plan view of a lower half mold in which a bat assembly preformed with a wooden core and glass fibers is disposed to apply a curable resin thin layer former;

FIG. 13 is a schematic side view of two conventional half molds and their cavities showing a coupling relationship between a mold and an inlet for injecting a preformed bat assembly and a curable resin into the mold to impregnate the sleeve layer;

14 is an end elevation view of the lower half mold and preformed bat assembly shown in FIG. 12;

15 is a schematic side view of an apparatus for simultaneously elongating and retracting a high shrink thermoplastic tube while forming a tubular plastic mold;

FIG. 16 schematically shows an apparatus for wetting the fiberglass layer as the epoxy resin moves downward over a preformed bat assembly in a tubular plastic mold, with an ash heat absorber at a location in the resin. Side View,

FIG. 17 is a schematic side view of an apparatus for supporting a preformed bat assembly in a tubular plastic mold and a layer of fiber wetted with epoxy resin by a mounting hole directly below the knob of the bat;

FIG. 18 is an elevational view of a wooden core of a modified bat of FIG. 2, ie a bat with a large number of circular grooves in its fuselage, showing the circular size of a conventional standard sized wooden bat.

FIG. 19 is an elevational view of a wooden core of a bat modified from the bat of FIG. 18 with broken lines indicating the circular size of a conventional standard sized wooden bat, ie a bat with a plurality of circular grooves with chamfered edges in the fuselage; FIG.

<Description of the code | symbol about the principal part of drawing>

10: reinforced wooden bat

12: wood core

14: composite thin layer

16, 17: handle portion

18, 21: knob

19, 20: fuselage part

28 support extension

32: preformed bat assembly

34: fiberglass sleeve

40, 42: fiberglass strand

50: attachment pipe

64: lower half mold

66: upper half mold

68: joint

70: injection hole

72: tubular mold

74: hollow tube

80 spout

82: high shrink tube

84: radiant heater

86: epoxy resin

102: circular groove

110: longitudinal groove

206: chamfered outer edges

207: Chamfered Inner Corner

According to the present invention, solid wood cores cut in shape the same as wood batts are made with dimensions that are slightly smaller than the standard dimension sizes specified for conventional wood batts. The wood core is manufactured leaving the support extension in the lathe as it is. The wood core is then coated with one or more layers of continuous flexible fabric sleeve, suitably fiberglass braided sleeves, formed of strands of high strength fibers, to form a preformed bat assembly. Each layer of fabric sleeve fits snugly over almost the entire outer surface of the wood core during formation of the preformed bat assembly such that its strands are aligned along the handle portion of the bat to significantly increase the longitudinal strength of the braid. do. Next, an appropriate curable resin, suitably self-curing epoxy resin at or near room temperature, is applied to the layer of high strength fiber sleeves of the preformed bat assembly and cured so that the layer of sleeve is the same as specified for the wooden batt. A thin layer of sized dimensions adheres to the core.

In a suitable embodiment of the invention, the diameter of the fiberglass braided sleeve or other flexible fabric sleeve is formed almost uniformly. The uniform inner diameter of the sleeve is slightly smaller than the diameter of the core in the fuselage portion and considerably larger than the diameter of the core in the handle portion. In addition, the sleeve may expand in diameter when subjected to radial force, and may contract in diameter when subjected to longitudinal tension or torsion. Suitable is that the strands of the sleeve are aligned in an orientation of approximately + 45 ° / -45 ° with respect to the longitudinal axis of the sleeve.

Thus, if a layer of sleeve is attached on the core, the sleeve is slightly expanded on the core of the fuselage portion, thereby causing the strands to exhibit increased orientation at angles greater than + 45 ° / -45 °. On the other hand, if a layer of each sleeve is placed at a predetermined position around the outer periphery of the wooden core, the core can be twisted or rotated relative to the sleeve, thereby placing the sleeve under longitudinal tension. In this manner, the sleeve is retracted to fit snugly around the outer end or top of the bat. Likewise, the strand of the handle portion is also tensioned or twisted so that the sleeve is compressed to fit snugly around the handle portion of the bat. Importantly, the orientation of the fiber strands along the handle portion is changed by the stretching and contraction of the braided sleeve around the handle portion of the wooden core. Indeed, when using braided sleeves, the fabric strands have been shown to inevitably interlock, exhibiting an orientation closer to the bat's longitudinal axis at the handle portion. By being oriented and fixed further in this longitudinal direction, the tensile strength of the braided sleeve is significantly increased along the longitudinal axis of the handle. Otherwise, the handle is the weakest part. When the layer of the sleeve is formed into a thin layer and adhered to the core by the curable resin, the orientation of such a good strand is maintained as it is in the bat. This arrangement significantly improves the strength characteristics of the bat.

The present invention also includes a unique method for producing the novel wooden bats described above. In general, the method of the present invention begins with the formation of solid wood bat cores from standard bat billets using conventional bat making equipment such as lathes and the like. However, in the case of the present invention, in order to accommodate the layer of fiberglass sleeve, the wood core is tapered over its entire surface to a slightly smaller dimension than that defined for a standard wood bat. Moreover, the support extension part or support stud in lathe process is left as it is.

Then, to support the application of the curable resin according to the invention, a plurality of longitudinal grooves are cut symmetrically along the perimeter of the wooden core along the handle portion. Suitable is to treat the wood core so that air is released from the wood and apply a resin primer to the core surface. Next, a hollow attachment tube is used to attach one or more layers of continuous fiberglass braided sleeves onto the wooden core to form a preformed bat assembly. Suitable is to attach a layer of two fiberglass sleeves. This operation is performed in accordance with the invention by placing the sleeve on the outer side of the attachment tube with one end of the sleeve closing the front of the open inlet of the attachment tube.

The end of the handle side of the wood core is pushed into the open end of the attachment canal while restraining the movement of the braided sleeve as it moves off the outer surface of the attachment canal and onto the core. By this suppression, the sleeve is placed under longitudinal tension as it is moved onto the handle portion of the core and the braided sleeve is stretched to fit snugly on the handle portion. Once the core is completely inside the attachment tube, the core is rotated using the support extension of the end of the fuselage side as a handle. By this rotational action, the sleeve contracts on the outer end of the core and comes into contact with the circular base of the support extension, which is the point where the support extension and the end of the body side of the bat meet.

By shrinking the sleeve around the outer end of the core, the core can be pulled out of the attachment canal without loosening or detaching the sleeve and simultaneously withdrawing the core a second layer of fiberglass sleeve over the first layer. Can be distributed. In this case, tension is applied to the end of the second layer extending on the knob so that the second layer contracts on the core and the handle portion of the first layer. By doing so, the preformed bat assembly is ready for subsequent processing.

Suitable molding techniques in accordance with the present invention include the step of thermally contracting a conventional high shrink plastic tube to fit snugly in a preformed bat assembly. In this case, the constricted tube is used as a mold for bonding a layer of the fiberglass sleeve to the core in a thin layer by the curable resin. In addition, the tube may be provided with an appropriate tubular extension at the end of the fuselage which will be used as a container for storing and retaining the resin as it is wetted into the fiberglass sleeve before it is cured when it is slowly fed into the tubular mold. It is suitable to shrink. Since there is a difference between the diameter of the handle portion of the bat and the diameter of the fuselage portion, the method of shrinking the plastic mold tube on the preformed bat assembly not only heats and shrinks the plastic mold tube during the heat shrink process, At the same time, it was proved necessary to stretch. This stretching operation was found to be necessary to allow the mold tube to fully contract around the handle portion of the preformed bat assembly.

The curable resin is then slowly fed into a tubular mold, suitably through a shrink wrap tube extension to wet the layer of fiberglass sleeve. It is also preferable to insert an elongate ash wood piece into the resin inside the tube so as to act as a heat absorber. It is also suitable to apply air pressure to allow the resin to wet the layer of fiberglass sleeve of the bat assembly preformed within a suitable time.

After wetting the layer of fiberglass sleeve, the preformed bat assembly in the tubular plastic mold may be turned upside down and held by a mount that supports the bat directly underneath the knob. By doing so, the uncured resin and glass fibers are better filled at the interface of the knob / knob. Once the resin has cured, the tubular plastic mold and the heat shrink wrap are removed. The support extensions are then cut and the ends of the exposed bat are closed. Next, sand is applied to the handle or the handle is sanded to give a rough feel.

The above and other objects and advantages of the present invention will be apparent from the detailed construction and operation of the present invention described and claimed in more detail below with reference to the accompanying drawings which are a part of the present specification. Overall, like parts of the accompanying drawings are referred to by the same reference numerals.

In describing suitable embodiments of the invention as illustrated in the accompanying drawings, certain terms are used for clarity, but the invention is limited to the specific embodiments shown and described and such selected terms. It is not. It is to be understood that each specific term includes all technical equivalents that function in a similar manner to accomplish a similar purpose.

Referring to FIG. 1, the reinforced bat of the present invention is generally indicated at 10 and includes a wooden core 12 and a composite thin layer 14. The composite thin layer 14 is formed of one or more continuous layers of flexible fabric sleeves covering almost the entire outer surface of the wooden core 12. The woven sleeve consists of high strength fibers, suitably glass fibers, also known as fiberglass, and is preferably formed in the form of woven braids. The braided sleeve is impregnated with a curable resin such that the reinforcing layer is laminated to adhere to the outer surface of the wooden core 12.

In addition, the bat 10 is fabricated to conform to the standard dimensional and standard physical properties of a conventional wooden bat. More specifically, conventional wood batts are manufactured in various standard lengths, combining standard weight characteristics, standard outer diameters, and tapered shape characteristics. The bat 10 is made to follow such standard characteristics. Like a conventional wooden bat, the bat 10 includes a handle portion 16 having a knob 18 at one end thereof, the handle portion 16 being tapered outwardly to the leading end or the outer end. It is incorporated into the fuselage portion 20 which terminates at 22.

The wood core 12 is formed in the same manner as the conventional way in a wooden bat using conventional lathe operations, and includes a handle portion 17, a fuselage portion 19 and a knob 21 at the end of the handle portion. do. However, as shown in FIG. 2, the wooden core 12 is formed with an outer dimension that is slightly smaller than that of a conventional wooden bat. The dashed line indicated by reference numeral 24 in FIG. 2 defines the outline of a conventional wooden bat, which indicates that the wooden core 12 is formed with a slightly smaller outline dimension than the dimensions of a conventional standard size wooden bat. have. When the thin layer 14 is bonded to the wooden core 12, the outer dimension of the reinforced wooden bat 10 of the finished product is the same as that of a conventional wooden bat of standard size. A suitable one is that by turning the wood core the standard wooden batt shrinks approximately 1/10 inch from the dimension over its entire length. Thus, for a standard wooden bat with a diameter of about 2.50 inches, it is suitable that the diameter at the fuselage portion 19 of the wooden core 1 is about 2.35-2.40 inches.

In addition, when shaving the wood core 12 in lathe machining, as shown in FIG. 2, the longitudinally extending support of a specific dimension is formed in the lathe machining and extends axially from each end of the core 12. The wood core 12 is formed so that the part or studs 26, 28 are left. The extension or stud 28 at the outer end is formed to be large enough to be used as a handle in the manufacture of the bat 10. The extension 28 is suitably about 1 inch in diameter and about 2-3 inches in length. The extension 26 at the end of the knob side may be slightly smaller, about 3/4 inch in diameter and about 1/2 inch in length. The wood core 12 is cut along the longitudinal groove 30 along the handle portion 17. These grooves are used to assist in wetting or impregnating a layer of fiberglass sleeve along the handle portion of the core. In addition, these grooves are symmetrically disposed along the circumference of the handle and preferably extend at least about 15 inches along the length of the bat from a point less than about 1 1/2 inches to the knob. The groove 30 can be of any effective size and shape. It has proved satisfactory to form four grooves, 0.06 inches by 0.06 inches, symmetrically spaced along the perimeter of the handle.

The preformed bat assembly is shown in FIG. 3 and indicated generally at 32. This assembly 32 is formed by coating almost the entire outer surface of the wooden core 12 with one or more continuous layers of flexible fabric sleeves, generally designated 34. Suitably two successive layers of fiberglass braided sleeves fit snugly on the core 12, which are indicated at 36 and 38 in FIGS. 6 and 7. Although two continuous layers are suitable, one continuous layer may be sufficient, or three or more layers may be used depending on the density of the fiberglass strands and the weave tightness of the braid or sleeve.

The diameter of the sleeve 34 is generally constant, and the sleeve 34 is braided such that the strands are generally perpendicular to each other and at an angle of approximately 45 ° or + 45 ° / -45 ° relative to the longitudinal axis of the core 12. Or formed. In the present invention, the orientation of the strand of 0 ° is parallel to the longitudinal axis of the wood core 12 or bat 10, and the orientation of 90 ° is axially in the plane perpendicular to the longitudinal axis. Or placed around the bat. Strands oriented at + 45 ° or −45 ° are disposed at an angle of 45 ° with respect to the longitudinal axis of the core or bat, and the plane of + 45 ° is perpendicular to the plane of −45 °.

A suitable orientation of strands of + 45 ° / -45 ° is that the strands 40, 42 are perpendicular to each other and oriented approximately + 45 ° / -45 ° with respect to the longitudinal axis of the sleeve 34, as shown in FIG. 8. Is illustrated. These strands 40, 42 are shown as solid lines in FIGS. 3, 4, and 5 for simplicity of the drawings. The shape of a suitable fiberglass sleeve 34 for a bat with a fuselage of 2.50 inches in diameter is about 2.25 inches whose inner diameter is slightly smaller than the maximum diameter of the core 12. Suitably a braid of about 2.35-2.40 inches. Suitable braids weigh about 26.5 feet per pound and 9 ounces per square yard, respectively, and are manufactured and marketed by A & P Technology of Covington, Kentucky.

Although braided sleeves made of fiberglass pieces or strands are suitable constructions of the sleeves 34 for forming the layers 36 and 38 of the present invention, within the scope of the present invention, fiberglass strands and / or other high strength fiber strands. Woven sleeves or knit sleeves may also be used. In addition, the woven sleeve or the knitted sleeve may or may not include a seam in the longitudinal direction. Thus, in the present invention, the term "sleeve" is intended to include not only suitable braided sleeves, but also any fabrics, knits, and other fabrics that can be made of continuous flexible sleeves made of fiberglass and / or other high strength fibers. will be.

As noted above, the inner diameter of a suitable fiberglass sleeve 34 is slightly smaller than the outer diameter of the fuselage portion 19 of the wooden core 12. Thus, the sleeve 34 expands slightly as it is pulled onto the fuselage portion 19. As such, the sleeve 34 and the body 19 are brought into close contact with each other so that the overall + 45 ° / -45 ° orientation of the fiberglass strands 40 and 42 is maintained as the original, or the core 12 Slightly increased along the fuselage portion 19. The overall + 45 ° / -45 ° or greater orientation in this fuselage portion 19 is illustrated at 46 in the preformed bat assembly 32 of FIG. 3 and in the enlarged partial view of FIG. 5.

On the other hand, the sleeve is not normally tightly fitted to the core either at the leading end 54 of the core or along the handle portion 17. By rotating the core, the sleeve 34 is retracted on the core 12 of the tip 54. Shrinkage of the sleeve 34 at the tip 54 is illustrated in FIG. 5 of the accompanying drawings. 5 shows that the base 44 of the support extension 28 covers the entire surface of the tip 54 except the point where the core 12 extends axially from the tip 54. You will find it. As such, it is uniquely performed in accordance with the present invention that the layer of sleeve fits snugly around the top of the tip 54 and around the base 44 of the extension 28, but the tip of the core is substantially It can also be carried out in any way that covers.

On the other hand, by applying tension to the braided sleeve 34 on the handle portion 17 of the core, the sleeve is extended in the longitudinal direction on the handle portion. By elongation of this sleeve, the fiber strands 40, 42 are oriented more longitudinally than at the handle portion, as indicated at 48 in FIGS. 3 and 4. Thus the angle at which the fiber strands 40, 42 are oriented more longitudinally than at the handle portion is considerably smaller than the normal + 45 ° / -45 ° orientation of the braid as shown in FIG. 8. Thus, it is seen herein to use one or more continuous layers of braided sleeves of glass fibers or other high strength fibers that are suitably oriented at + 45 ° / -45 ° and whose inner diameter is less than or equal to the diameter of the fuselage portion of the wooden core. It has proved to be quite advantageous in producing thin coated coating batts of the invention. More specifically, when the braided sleeve is attached to the wooden core, the larger fuselage diameter causes the glass fiber strands to cross the original + 45 ° / -45 ° orientation by + 45 ° / -45 °. Extends in an orientation equal to or slightly larger than. Subsequently, as the layers 36, 38 of the sleeve are fitted on the core and stretched and retracted on the handle portion of the core, the strands are oriented significantly longitudinally in an orientation significantly smaller than an angle of + 45 ° / -45 °. . By changing the orientation of the strands toward the 0 ° orientation in this manner, the strength of the strands in the longitudinal direction is significantly increased, thereby increasing the reinforcing effect of the glass fibers in the handle portion of the bat. In addition, by stretching and contracting the braided sleeve, the strands of the handle portions are fixed substantially with respect to each other, further increasing the strength in the longitudinal direction of the strands. Suitable orientation of the strands in the handle portion of the bat when an interlocking effect occurs is between about + 20 ° / -20 ° and about + 25 ° / -25 °.

In the present invention, a continuous layer of suitable fiberglass braided sleeves can be easily and quickly attached over almost the entire outer surface of the core 12 by the use of hollow attachment tubes in the fabrication of preformed bat assemblies. This method is schematically illustrated in FIGS. 9, 10 and 11, in which the attachment tube is indicated generally by the reference numeral 50. The layers of the sleeve are suitably attached in two layers to form two or more layers by selecting the length of the sleeve to a sufficient length. In this case, the sleeve 34 is disposed on the outer side of the attachment pipe 50, and the inner diameter of the sleeve 34 is of a size slightly smaller than the maximum diameter of the wood core. As the attachment tube, any rigid plastic tube formed with a predetermined inner diameter can be used, but a transparent plastic tube is suitable. Before and after the sleeve 34 is placed on the attachment pipe 50, the adjacent ends are tightly tightened with tape or the like as shown in FIG. In this way, the sleeve 34 and the attachment pipe are ready to receive the wooden core 12. As shown in FIG.

While restraining the movement of the sleeve 34 on the outer side of the attachment tube 50, the end 17 of the handle side of the wood core 12 is pushed into the tied and tightened end 52 of the sleeve 34, so that the sleeve Is forcibly moved into the attachment pipe 50. Thereby, as the bat is pushed into the attachment tube 50, the sleeve 34 moves out of the outer surface of the attachment tube 50 under tension and onto the bat. As a result of the tension applied to the sleeve in the longitudinal direction, the sleeve tends to shrink on the handle portion 17 of the core, so that the strand is oriented in the longitudinal direction as desired. When the core 12 completely enters the attachment pipe 50, the core is rotated using the support extension 28 at the end of the fuselage side as a handle. By this rotational or torsional action, the sleeve 34 contracts on the outer end 54 of the wooden core 12. The core is engaged until the sleeve is retracted to engage the circular base 44 of the support extension 28, which is the point where the support extension 28 and the outer end or tip of the core meet and fully cover the remainder of the end 54 of the core. Rotate In this way, the first layer 36 of the sleeve 34 is positioned at a predetermined position on the core 12.

The amount of rotation of the core 12 to sufficiently cover the entirety of the end portion 54 of the core up to the base 44 of the support extension 28 depends on the characteristics of the sleeve, including density, weave tightness, and the like. If a suitable fiberglass braid sleeve as described above is used, the core only needs to be rotated 1.5 revolutions to sufficiently retract the sleeve 34 around the end 54 of the core. As the sleeve is contracted to the base 44 in this manner, the core can be pulled out of the attachment pipe without loosening or detaching the sleeve, and thus the core 12 is withdrawn from the attachment pipe 50 without the core 12 being pulled out. A second layer 38 of fiberglass sleeve 34 may be distributed over (12). Thus, it is possible to attach the two continuous layers 36, 38 of the high-strength sleeve 34 over almost the entire outer surface of the core 12 quickly and easily without separating them from each other. In fact, the second layer 38 is simply folded back on the first layer 36. Additional layers may likewise be attached one or two layers simply by repeating the above-described method. In addition, the tubular sleeve can be continuously supplied to the attachment pipe 50 from the end where it is not attached.

Withdrawing the wood core 12 from the attachment tube 50, the sleeve 34 is cut off leaving a portion extending a few inches past the support extension 26 at the end of the core. Then, as described above, the sleeve is pulled around the handle portion 17 of the core to orient the strands 40, 42 of the layer 38 of the sleeve in the orientation of the desired fixing effect relative to the handle portion 16 of the bat. To do so, the end 41 of the layer 38 of the sleeve is tensioned with respect to the core 12. This tensioning operation can be easily performed by rotating the core with the support extension 28 as a handle while keeping the outer end 41 of the layer 38 of the sleeve fixed. Further, the sleeve tube is pulled tightly to the base of the knob 21 and pulled down around the end of the knob side. This operation places a small piece of plastic PVC pipe 39 on the end 41 and studs 26 of the layer 38 and then tightens the braid end while moving the PVC pipe toward the base of the knob 21. It is easily done by pulling it. Next, the ends 41 of the braid layer 38 are folded overlapped and taped (not shown). If desired, additional tension may be applied to the outer layer 38 by tightening the tube 39 more tightly on the base of the knob 21. In this way, the pre-formed bat assembly 32 is completed.

The layers 36, 38 of the sleeve 34 are tightly glued over the entire outer surface of the core 12 with a suitable curable resin during formation of the bat 10. Any curable resin can be used that adheres the fiberglass layer tightly to the wooden core but does not show cracks, breaks or fractures when subjected to impacts from ball strikes or other causes. In addition, transparent resins are suitable because the reinforced bat of the present invention is intended to have approximately the same appearance as a standard wooden bat. Thus, curable resins for use in the present invention are selected to obtain transparency, fracture toughness, impact properties, interlayer adhesion, interfacial adhesion and high lateral energy dispersion coefficient.

Suitable resins for use in the present invention are thermosetting epoxy resins that self cure at or near room temperature. The epoxy component is suitably a 2,2 '-(1,3-phenylene) bis-2-oxazoline (2,2'-(1,3-phenylene) bis-2-oxazoline) system. Other bifunctional and multifunctional epoxy resins with or without monofunctional diluents may also be used. Suitable converters or curing agents for use in forming thermosetting epoxy resins include multifunctional primary and secondary amines, Lewis acids, Lewis bases, dibasic carboxylic acids and anhydrides, and the like. Suitable curing agents include alkyl amines such as diethylenetriamine, triethlenetetramine, metaxylenediamine, α-aminoethyl piperazine and the like. Polyoxypropyleneamines, amidoamines, polyamides and cycloaliphatic polyamines may also be used as all or as mixtures of conversion agents. The mixing ratio is approximately the stoichiometric ratio (except Lewis acids and Lewis bases) composed of one active amine hydrogen for each epoxy group. In addition to the epoxy component and the amine curing agent component, it is suitable to incorporate a third component which precipitates during curing and forms a discontinuous second phase. This second phase is suitably a small elastomeric sphere-like tissue that is less than about 1 micron in diameter and is encapsulated and adhered to a continuous epoxy phase. This second phase improves fracture toughness, impact resistance, and improves the composite's resistance to premature delamination. Suitable resin materials are manufactured and marketed by Applied Polymeric Inc. of Benicia, California.

To assist in adhering a suitable epoxy resin to the wood batt core, it is suitable to apply a primer to the wood batt core prior to attaching the layer of fiberglass sleeve. Suitable primer compositions are epoxy resin emulsions that exhibit low toxicity, low cost, long shelf life, good wood permeability, Tg &gt; 60 ° C., and low viscosity. Particularly effective is the use of a suitable coalescing and penetrating solvent with a monocomponent thermoplastic epoxy having a molecular weight of 30,000. Epoxy containing two components, the component B of which contains a mixture of alkyl amines, amidoamines, and emulsifying surfactants will produce satisfactory results, but the two components and limited shelf life are limited. It is not so suitable because of the fact. Still other examples of primer compositions include resorcinol formaldehyde, urea formaldehyde and polyethylenimine hydroxymethylated resorcinol. Suitable primers are also made and commercially available from Applied Polymeric Inc.

6 and 7 show a close adhesion and thin layer formation relationship between the layer of composite sleeve 14 and the surface of the wooden core 12 forming the reinforced batt. As shown, the layers 36, 38 of the sleeve 34 are at the outer end 22 corresponding to the point at which the support extensions 26, 28 in the lathe are removed from the finish of the bat 10. Except for the portion 56 and the portion 58 at the base of the knob 18 are coated over almost the entire outer surface of the bat 10. In addition, according to the present invention, reinforcement of the knob 18 is unnecessary. Thus, the reinforcement layers 36, 38 can be cut at the point 60 at which the knob 18 merges with the bottom of the handle portion 16. In this case, the extension 26 is cut in contact with the base of the knob 18 at the end of the bat. Thus, according to the invention, the reinforcing layer of the fiberglass is continuously coated over almost the entire outer surface of the bat 10 from the point at which the knob is incorporated into the handle 16 to the outer leading portion 56 of the bat. . This uninterrupted continuous coating corresponds to more than 99% of the total outer surface of the bat without the knob 18.

Conventional methods for laminating and bonding a layer of fiberglass sleeve to a wooden core are illustrated in FIGS. 12, 13 and 14. The preformed bat assembly 32 is disposed within a mold 62 comprising a lower half mold 64 and an upper half mold 66, in which case each half mold 64, 66 is a preformed bat. Each comprising a portion corresponding to one half of a cavity 68 that houses the assembly 32. The components of the mold are conventional, and when the mold is closed, a suitable thermosetting or thermoplastic resin, which can be cured by heat, is injected through the inlet 70 to fill the cavity 68 and the layer 36 of the fiberglass sleeve 38) is sufficiently impregnated with resin. Heat and pressure are then applied to the preformed bat assembly 32 including the cavity of the mold and the layers 36 and 38 impregnated with the resin. In this case, the resin is melted and fused to thinly bond the sleeve layer to the wooden core, and the fiberglass strand of the handle portion 16 is held in the above-mentioned suitable orientation as indicated by reference numeral 48, and the fuselage portion The fiberglass strand of (14) is heated to a temperature which keeps the mesh in the diagonal direction as indicated by 46. One known resin injection molding technique is the method disclosed in Seki's U.S. Patent No. 5,301,940 described above, except that the shape of the mold must be changed to accommodate the end support extensions 26, 28. There is.

It is also part of the present invention to use a novel method for applying and curing an epoxy resin, such as the suitable epoxy resins described above, to secure the layer of fiberglass sleeve to the wooden core. However, in using a suitable epoxy resin, a primer, such as the suitable epoxy primer described above, must be applied to the wooden core 12 prior to the attachment of the layer of fiberglass sleeve. Suitable is to apply the resin primer after heating the wood core to about 110 ° F. This heating not only serves to release air from the wood core, but also assists the primer infiltrating the wood. When heating is complete, the wooden core is immersed in the epoxy primer composition. It is suitable to once again immerse the wood core in the primer composition after drying. However, heating is not performed in the case of the second immersion. This completes the application of the primer to the wooden core to accommodate the epoxy resin during the curing and molding operations.

In the present invention, a unique molding technique has been found that allows a thin layer of fiberglass sleeve to be adhered to a wooden core to facilitate the faster and cheaper technique than conventional processes. Such suitable molding techniques include the process of heat shrinking a conventional plastic tube to closely fit a preformed bat assembly, and using the heat shrink tube as a mold for applying and curing the epoxy resin. The molding technique described above will now be described with reference to FIGS. 15, 16, and 17, which are exemplary views in which tubular plastic molds are generally designated at 72.

To form the required tubular mold 72, an appropriately sized hollow tube 74 is placed on the support extension 28 at the end of the fuselage side of the bat assembly 32. The hollow tube 74 includes an elongate tube portion 76 and a short tube portion 78 that is dimensioned to fit on the extension 28. The diameter of the tubular part 8 on the extension 28 is smaller than the diameter of the tubular part 76. The elongated tubular portion 76 forms an open spout 80 of the mold 72, while the short tubular portion 78 is connected from the spout 80 to a mold surrounding the preformed bat assembly. A circular opening 81 (see Fig. 16) is formed. In general, a 1 1/2 inch hollow tube of about 20 inches in length and made of cardboard has been found to be satisfactory for use as the tube portion 76. The short tubular portion 78 can be easily attached to the inside of the tubular portion 76 made of cardboard. The base of the tube 74 is placed on a suitable stand (not shown) that supports the tube 74 in an upright vertical position. The preformed bat assembly 32 is then supported on the tube 74 by inserting the support extension 28 into the tube portion 78.

Next, a high shrink tube 82, about 4 inches wide when unfolded, is attached over the entire surface across the preformed bat assembly and tube 74. Thin PVC high shrink tubes have been found to be satisfactory for use as high shrink tubes 82. Subsequently, the high shrink tube 82 is shrunk by using an annular radiant heater 84 or the like so as to closely adhere to the layer of the fiberglass sleeve. Suitably, the radiant heater 84 is automatically moved upwardly, starting from the bottom of the tube 82 and through the preformed bat assembly 32 starting from the outer end. As shown in FIG. 15, the annular radiant heater 84 significantly extends into the handle portion 17 past the fuselage portion 19 of the tube 74 and the preformed bat assembly 32 above the assembled structure. It is moved. As also shown, the high shrink tube 82 is retracted to fit snugly against the tube 74 and the preformed bat assembly 32. As the high shrink tube 82 is retracted on the tube 74 and the preformed bat assembly 32, it provides a suitable opening for the air inside the tube 82 to be released. When the radiant heater passes completely through the assembled structure, the tube 82 contracts and fits around the end portion 18 on the knob side, and then the long length tube extension opened to the end portion 54 on the fuselage side. The hollow tube 74 is removed leaving the preformed bat assembly 32 enclosed within a heat shrinkable plastic sheath forming the provided tubular plastic mold 72.

Since there is a significant difference between the diameter of the handle portion 16 of the bat and the diameter of the fuselage portion 20, the plastic mold tube must be simultaneously removed during the heat shrink process to shrink the mold tube on the handle portion of the preformed bat assembly. Elongation and heating proved to be necessary. It has been found that doing so is desirable to sufficiently shrink the mold tube in the handle portion of the bat. Such simultaneous stretching of the tube in the handle portion 16 of the bat during the heat shrink process can be performed by any suitable technique. However, one simple method is to release the support of the tube 74 when the annular radiant heater 84 rises to about three quarters of its upward path, ie to support the preformed bat assembly assembled thereon. So that the preformed bat assembly 32 and the tube 74 freely hang with respect to the remaining portion of the tube 82 supported from the top, along with the corresponding portion of the tube 82 heat-shrunk on its outer surface. That's how. By gravity acting on the unshrunk tube 82 as such, the unshrinkable tube is elongated at the same time as it is heat shrinked on the handle portion by the radiant heater.

With the tube 74 removed from the tube extension 85, the preformed bat assembly 32 in the tubular plastic mold is now ready to receive a suitable epoxy resin 86. Move the assembled components to an ambient temperature environment. The epoxy resin composition is then mixed and poured into the hollow tube extension 85 through the open spout 80. When using a suitable epoxy resin, it was found that about 7 ounces of mixed resin would be sufficient. It is suitable to insert an elongate piece of ash wood about 1 inch by 1 inch in cross section and 14 inches in length so as to act as a heat absorber. Such ash wood acts to attenuate the exothermic reaction of the epoxy resin, thereby increasing the action time or "retention time" of the resin. The open end 80 of the hollow tube extension 85 is then placed and fixed on the collecting fixture 90 to pressurize air pressure into the tube extension and tubular plastic mold. By applying head pressure in this manner, the fiberglass sleeve of the preformed bat assembly is wetted in a timely manner without the resin prematurely curing. It is suitable to apply an air pressure of about 10 psi so that a suitable epoxy resin is supported such that within 30 to 40 minutes the resin separates from the opening 92 of the mold at the end of the handle side of the assembly 32. Passed across the entire length of the preformed bat assembly 32 and the tubular plastic mold 72. As shown in FIG. 16, the epoxy resin wets approximately the upper quarter of the preformed bat assembly 32 at the height indicated at 94. Thus, the method of pressurizing a tubular plastic mold is one form of the composite manufacturing method known in the art under the name of "Resin Transfer Molding."

Ambient temperatures of about 80-82 ° F. proved to be optimal temperatures for applying and curing the epoxy resin. Any temperature lower than this temperature undesirably increases the viscosity of the resin, making the wetting time too long. In addition, significantly higher ambient temperatures than such temperatures also cause undesirable exothermic reactions of the resin, making the formed bats unusable.

After the preformed bat assembly 32 is wetted, the assembly 32 is turned upside down and held by a mount 96 supporting the bat directly underneath the knob 18 (see FIG. 17). By doing so, the uncured resin and fiberglass are better filled at the interface of the knob / knob. Suitably, the mounting holes 96 are molded and heated to a temperature above 200 ° F. to form a permanent ring between the top of the knob of the bat 10 and the base of the handle portion 16. As such, the step of holding the assembly 32 upside down can be omitted if the layer of fiberglass sleeve is effectively saturated during the resin transfer molding step described above.

After approximately 1 1/2 to 2 hours of curing the epoxy resin, the tubular mold 72 constituting the heat shrink wrap is removed. In addition, the support extensions 26 and 28 are cut and the ends of the exposed bat are finished. Then, sand is applied to the handle or the handle is sanded to give the handle a rough feel.

While suitable embodiments have been described using one or more layers of flexible fabric sleeves made of high strength fibers or fibers, fabric sleeves made of other high tensile strength fibers such as Kevlar, Spectra, carbon, nylon, etc. It may also be used in the present invention. Also, within the scope of the present invention, one or more pieces or strands of such other high strength fibers may be braided, woven, knitted, or formed with a fiberglass strand or piece into a flexible sleeve. Thus, the invention is not intended to be limited to sleeves consisting solely of braided or unbraided glass fibers.

In addition, the particular wood forming the wood core 12 may be an optional problem. Typically, high quality ash wood is used to produce a quality wood bat, and such ash wood may also be used in the present invention. However, considering the surprising reinforcement performance of the inventive fiberglass sleeve 14 coated with a thin layer, lower ash wood can also be used as the wood core 12.

Finally, FIGS. 18 and 19 show bats 100 and 200 according to a variant, respectively. The bat 100 of FIG. 18 includes a plurality of circular grooves 102 in the bat. As shown, there are 15 grooves that are approximately 3/16 inches wide and approximately 0.100 ± 0.010 inches deep. A strip portion of the fuselage approximately 3/16 inches wide is between each pair of grooves. The longitudinal groove 110 is also shown. Another corresponding groove 110 is on the opposite side of bat 100. The two grooves 110 are approximately 1/32 inches in width and the same depth as the grooves 102. The groove 102 functions similarly to extract air from the groove 102 when resin flows from the fuselage end toward the knob end, similar to the four grooves 30 in the handle end. Since the fabric layer is not close at the fuselage end and the flow of resin is faster at the fuselage end, compared to the four grooves 30 in the handle end with the closer fabric layer and the slower resin flow, only two grooves ( Only 110 is considered necessary at the end of the fuselage.

The bat 200 of FIG. 19 includes a plurality of grooves 202 at the fuselage ends that are similar to the grooves 102 of the bat 100. However, the groove 202 includes chamfered outer 206 and inner 207 edges. When the bat is cut along the longitudinal axis, the groove 202 has a shape like a sine wave (bat 100 in FIG. 18 has a shape like a square wave in the same cross section). Drawing a line along the fuselage surface, the top of the strip between each pair of grooves 202 touches the line. The bat 200 is shown without the longitudinal grooves 110 of the bat 100. Since it takes the form of a sinusoidal waveform, each channel does not have to force air out of the groove 202. In addition, the incoming resin more easily fills the grooves 202. However, the groove 110 may be formed as necessary.

Bat 100 and bat 200 are manufactured in the same manner as bat 10 described above. There is more resin at the fuselage end just to help extend the life of the trees in the batting area of the bat. In the bat 100 and bat 200, 100 of the applied polymer CR-58 epoxy is mixed and 28 of the applied polymer HB-3 curing agent. 100 grams of the mixture is used in a batting mold, with approximately 80-90 grams actually flowing through the bat.

The foregoing description has been considered as illustrative of the principles of the invention and those skilled in the art will make numerous other modifications and variations to the invention. Accordingly, there is no intention to limit the invention to the construction and operation as shown and described. All suitable modifications and equivalents may be classified as falling within the scope of the present invention as set forth.

In the reinforced wooden bat of the present invention, the strands are batted while the one or more continuous layers of flexible fabric sleeves formed of strands of high strength fibers are fitted snugly over almost the entire outer surface of the wood core to form a preformed bat assembly. By being oriented and fixed closer to the bat's longitudinal axis along the handle portion of, the tensile strength of the braided sleeve along the handle's longitudinal axis is significantly increased. In addition, when the layer of the sleeve is formed into a thin layer by the curable resin and adhered to the core, the orientation of such a good strand is maintained as it is in the bat. Therefore, such an arrangement significantly improves the strength characteristics of the bat of the present invention.

In addition, in the method of making the wooden bat of the present invention, a continuous layer of suitable fiberglass braided sleeves is readily and quickly attached over almost the entire outer surface of the core by the use of hollow attachment tubes in the fabrication of preformed bat assemblies. Can be. In addition, the method of the present invention is very economical because it includes a unique molding technique that allows a thin layer of fiberglass sleeve to be adhered to the wooden core in a faster and cheaper way than conventional processes. As well as can be practiced simply.

Claims (20)

Reinforced wood bats of the same dimensions as wood bats of standard size, A wooden core, including handle and fuselage portions, which form elongated members of outer dimensions slightly smaller than the outer dimensions of standard sized wooden batts, and a thin layer of the outer surface of the wooden core, impregnated with a curable resin One or more continuous layers of sleeves of reinforcing fibers covering the at least one continuous layer, wherein the one or more continuous layers of the sleeves have an outer dimension of the wooden core to a final dimension of a reinforced wooden bat substantially equal to the outer dimensions of the standard size wooden bat. Reinforced wood bat, characterized in that the increasing thickness. 2. The reinforced wooden bat of claim 1, wherein said sleeve consists of strands of said fiber. 2. The reinforced wooden bat according to claim 1, wherein the majority of the fibers consist of glass fibers. The reinforced wooden bat of claim 2, wherein the fiber strand is oriented at about + 45 ° / -45 ° in the fuselage portion of the bat. 5. The reinforced wooden bat of claim 4, wherein the fiber strand is oriented at an angle substantially smaller than + 45 ° / −45 ° at the handle portion of the bat. 6. The wooden bat of claim 5, wherein the oriented fiber strand is substantially fixed at the handle portion of the bat. The reinforced wooden bat of claim 1, wherein the handle portion of the wood core includes a plurality of longitudinally extending grooves spaced symmetrically with respect to the handle portion of the bat. 4. The reinforced wooden bat of claim 3, wherein the glass fiber sleeves are each provided in two continuous layers covering substantially the entire outer surface of the wooden core. 9. A reinforced wooden bat according to claim 8, wherein the two continuous layers are also continuous to each other with their outer layers overlying on the inner layer. The reinforced wooden bat of claim 1, wherein at least one layer covers more than 99% of the total outer surface of the wood core from the base to the outer end of the handle portion of the bat. The reinforced wooden bat of claim 1, wherein the bat includes a knob at the end of the handle portion, and wherein the two or more layers each cover most of the knob. 2. The reinforced wooden bat of claim 1, wherein said batt comprises a plurality of circular grooves at said fuselage ends. 13. The reinforced wooden bat according to claim 12, wherein the groove and the body have transverse transitions. 13. The reinforced wooden bat according to claim 12, wherein the groove and the fuselage have transitional portions of chamfered edges. The reinforced wooden bat of claim 1, wherein the outer surface of the wood core is impregnated with an emulsion primer adhered by the curable resin during the coating of one or more layers of the sleeve to the wood core in a thin layer. A preformed bat assembly for forming a wood bat reinforced using curable resin, A wooden core comprising a handle portion and a fuselage portion forming a stretched wooden member substantially in the shape of a bat and having longitudinal studs extending axially from its lower and upper ends, and substantially the entire outer surface of the wooden core; And at least one layer of a sleeve of reinforcing fibers covering the at least one preformed bat assembly. The preformed bat assembly of claim 16, wherein the stud is removed upon finishing the reinforced wood bat. 17. The preformed bat of claim 16, wherein at least one layer of the sleeve each covers more than 99% of the entire outer surface of the wood core from the base of the handle of the bat to the outer tip thereof. Assembly. Reinforced wood bats of the same dimensions as wood bats of standard size, Solid wood cores, including handle portions and fuselage portions, which form elongated solid wood members of outer dimensions slightly smaller than the outer dimensions of standard size wooden batts, and impregnated with curable resin to form a thin layer on almost the entire outer surface of the wooden cores. A reinforcement tree comprising at least one continuous layer of sleeves of reinforcing fiber strands covering the outer surface, wherein the at least one continuous layer of sleeves substantially equals the outer dimension of the wooden core to the outer dimension of the standard size wooden bat. A thickness that increases to the final dimension of the bat, wherein the fiber strand is oriented approximately + 45 ° / -45 ° in the fuselage portion of the bat, and the fiber strand is + 45 ° / -45 in the handle portion of the bat Oriented at a substantially smaller angle than °, the handle portion of the wooden core is the perimeter of the handle portion of the bat For the reinforced wooden bat comprises a plurality of grooves extending in the longitudinal direction and spaced symmetrically. 20. The reinforced wooden bat of claim 19, wherein said batt comprises a plurality of grooves at said fuselage ends.