KR19990033108A - Process for preparing catalyst for dehydrogenation - Google Patents
Process for preparing catalyst for dehydrogenation Download PDFInfo
- Publication number
- KR19990033108A KR19990033108A KR1019970054365A KR19970054365A KR19990033108A KR 19990033108 A KR19990033108 A KR 19990033108A KR 1019970054365 A KR1019970054365 A KR 1019970054365A KR 19970054365 A KR19970054365 A KR 19970054365A KR 19990033108 A KR19990033108 A KR 19990033108A
- Authority
- KR
- South Korea
- Prior art keywords
- catalyst
- dehydrogenation
- reaction
- particles
- alumina
- Prior art date
Abstract
본 발명은 탈수소 반응용 촉매의 제조방법에 관한 것으로, 노말파라핀을 탈수소하여 노말올레핀을 제조함에 있어서, 드로핑과 1차 숙성단계에서 비중 0.86 - 0.87, 동점도가 10 - 30 cSt 인 유동 파라핀을 현탁매개체로 사용함으로써 입자 내에 지름이 1 μm 이상인 기공을 갖는 대기공 알루미나 입자를 촉매 지지체로 사용함을 특징으로 하며, 본 발명에 의한 촉매는 탈수소촉매의 반응안정성을 향상시키게 된다.The present invention relates to a method for preparing a catalyst for the dehydrogenation reaction. In the production of normal olefins by dehydrogenation of normal paraffins, suspended paraffins having a specific gravity of 0.86-0.87 and a kinematic viscosity of 10-30 cSt in the dropping and primary aging stages are prepared. By using as a medium, it is characterized in that the air support alumina particles having pores with a diameter of 1 μm or more in the particles as a catalyst support, the catalyst according to the invention improves the reaction stability of the dehydrogenation catalyst.
Description
본 발명은 탈수소 반응용 촉매의 제조방법에 관한 것으로, 보다 상세하게로는 대기공 구형 알루미나 입자를 촉매지지체로 사용하며 높은 활성과 선택도 및 반응안정성을 갖는 탈수소 반응용 촉매의 제조방법에 관한 것이다.The present invention relates to a method for preparing a catalyst for dehydrogenation reaction, and more particularly, to a method for preparing a catalyst for dehydrogenation reaction using atmospheric sphere alumina particles as a catalyst support and having high activity, selectivity and reaction stability. .
알루미나는 그 자체로서 촉매역활을 수행하거나 또는 촉매의 지지체로서 사용될 수 있으며, 이때 알루미나의 물리적 특성을 이를 이용하여 제조된 촉매의 물리적 안정성, 즉 운반 및 공정수행중에 필요한 기계적 강도 및 내마모성 뿐만 아니라 촉매의 반응성 즉, 활성도, 선택도, 반응안정성 등에도 큰 영향을 미친다. 또한 알루미나 입자 내에 대기공이 있는 구조를 가질 경우, 반응물 및 생성물의 흐름을 원활하게 해주어서 결과적으로 반응성을 향상시키는 우수한 효과를 가질 수 있게 된다.Alumina can act as a catalyst on its own or can be used as a support for a catalyst, wherein the physical properties of the alumina can be used to determine the physical stability, i.e. the mechanical strength and abrasion resistance necessary during transport and process, of the catalyst. The reactivity, that is, activity, selectivity, reaction stability, and the like have a great influence. In addition, when the structure has the air hole in the alumina particles, it is possible to smooth the flow of the reactants and products, as a result can have an excellent effect of improving the reactivity.
이러한 촉매를 이용하여 탈수화된 탄화수소는 정밀화학제품의 기초원료, 고분자재료의 기초원료 및 고성능 휘발유의 제조를 위한 첨가제의 원료 등으로 그 수요가 계속 증가하고 있는 경제성이 높은 화합물이다.Hydrocarbons dehydrated using such catalysts are highly economical compounds, which are in increasing demand as basic raw materials for fine chemicals, basic raw materials for polymer materials, and raw materials for additives for producing high performance gasoline.
노말파라핀을 탈수소하여 노말올레핀으로 전환하는 방법은 이미 공지되어 있는 것으로써, 그 방법은 수소와 노말파라핀을 탈수소촉매와 접촉시키고 대기업 혹은 그 이상의 고온으로 반응시키는 것이다. 이 반응에 이용되는 탈수소촉매는 백금 또는 기타 Ⅷ B 족 귀금속원소에 속하는 금속을 알루미나, 실리카, 실리카-알루미나 등에 함침시킨 것이다.Dehydrogenation of normal paraffins to convert them to normal olefins is well known, which involves contacting hydrogen and normal paraffins with a dehydrogenation catalyst and reacting at large temperatures or higher. The dehydrogenation catalyst used in this reaction is impregnated with alumina, silica, silica-alumina or the like belonging to platinum or other metals belonging to Group VIII precious metal elements.
그러나 상기와 같은 반응에서는 탈수소화반응 이외에 열분해반응, 이성질화반응, 고리화반응 등의 부반응과 목적생성물인 모노올레핀이 더욱 더 탈수화반응되어 디올레핀이 생성되는 등으로 인하여, 촉매의 이용 효율을 감소시키고 촉매의 비활성화를 가속화시킴으로써 결과적으로 촉매 수명의 단축을 야기할 수 있다. 동시에 상업적 규모의 공정에 적용할 경우 원료의 낭비 및 후단분리공정에 대한 과도한 무리를 일으킬 수 있다.However, in the above reaction, in addition to dehydrogenation reaction, side reactions such as pyrolysis reaction, isomerization reaction and cyclization reaction, and monoolefin, which is a target product, are further dehydrated to produce diolefin. Reducing and accelerating catalyst deactivation may result in shortening of catalyst life. At the same time, application to commercial scale processes can lead to waste of raw materials and excessive strain on the post-separation process.
따라서 노말파라핀의 노말올레핀으로의 선택도를 향상시키고 촉매의 비활성화를 감소시킴으로서, 탈수소반응용 촉매의 반응안정성과 사용수명을 연장시키기 위하여, 백금 또는 기타 Ⅷ B족 귀금속 원소에 한가지 이상의 금속성분을 결합시킨 촉매조성물의 첨가 및 대체가 제안되어 왔다.Therefore, by improving the selectivity of normal paraffins to normal olefins and reducing the deactivation of the catalyst, in order to extend the reaction stability and the service life of the catalyst for dehydrogenation, one or more metal components are combined with platinum or other Group B noble metal elements. The addition and replacement of the catalyst composition has been proposed.
영국특허 1,497,297호에는 갈륨, 인듐, 탈륨 중에서 최소한 한 가지 이상의 원소를 선택하여 백금 및 알칼리금속과 함께 알루미나에 함침시킨 촉매를 제안하였으며, 미국특허 4,551,574호에서는 백금, 주석, 인듐과 알칼리 또는 알칼리토금속을 알루미나에 함침시킨 촉매조성물에 대해 기술하고 있다. 또한, 미국특허 4,762,960호에서는 백금, 주석, 게르마늄, 레늄 및 알칼리 또는 알칼리토금속을 옥사이드 지지체에 함침시킨 탈수소촉매 제조방법에 관해 기술하고 있으며, 미국특허 4,800,674호에서는 백금, 팔라듐, 이리듐, 오스뮴 및 Ⅳ A족 원소를 공침시킨 탈수소 촉매조성물에 대해서 제안하고 있다.British Patent No. 1,497,297 proposes a catalyst in which alumina is impregnated with platinum and alkali metals by selecting at least one element from gallium, indium and thallium, and US Patent 4,551,574 proposes platinum, tin, indium and alkali or alkaline earth metals. A catalyst composition impregnated with alumina is described. In addition, US Pat. No. 4,762,960 describes a method for preparing a dehydrogenation catalyst in which platinum, tin, germanium, rhenium, and alkali or alkaline earth metals are impregnated in an oxide support, and US Pat. A dehydrogenation catalyst composition in which a group element is co-precipitated is proposed.
그러나, 상기와 같이 단순한 조성물의 추가 및 대체에 의해 제조된 촉매들은 노말파라핀의 탈수소화반응에 대한 반응활성 및 유용한 반응생성물의 선택도의 증진에는 효과를 나타내었으나, 촉매의 비활성화가 빠르게 진행되어 반응안정성의 측면에서는 만족스럽지 못한 것이었다.However, the catalysts prepared by the addition and replacement of simple compositions as described above had an effect on the reaction activity and the selectivity of useful reaction products for the dehydrogenation of normal paraffins, but the deactivation of the catalyst proceeded rapidly. In terms of stability, it was not satisfactory.
본 발명의 목적은 반응물인 노말파라핀과 생성물인 노말올레핀의 입자내에서의 흐름이 원활하도록 하여 결국, 촉매의 반응안정성을 향상시킬 수 있는 구형 알루미나 입자의 제조방법을 제공하는 것이다.It is an object of the present invention to provide a method for producing spherical alumina particles that can smoothly flow in particles of a reactant normal paraffin and a product normal olefin, thereby improving the reaction stability of the catalyst.
본 발명은 노말파라핀을 탈수소하여 노말올레핀을 제조함에 있어서, 드로핑과 1차 숙성단계에서 비중 0.86 - 0.87, 동점도가 10 - 30 cSt 인 유동 파라핀을 사용함으로써 입자 내에 지름이 1μm 이상인 기공을 갖는 대기공 알루미나 입자를 촉매 지지체로 사용함을 특징으로 한다.In the present invention, in the preparation of normal olefins by dehydrogenation of normal paraffins, an atmosphere having pores having a diameter of 1 μm or more in a particle by using flowing paraffin having a specific gravity of 0.86-0.87 and a kinematic viscosity of 10-30 cSt in a dropping and primary aging step It is characterized by using co-alumina particles as the catalyst support.
이하, 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.
구형알루미나 입자의 제조는 오일-드로핑 방법 즉,알루미늄금속을 산용액에 용해시켜 제조된 알루미나 하이드로졸과 최종적으로는 제조과정에서 암모니아로 가수분해될 약염기를 혼합한 후, 현탁매개체인 불수용성(不水容性)액체에 드로핑하여 구형의 알루미나 하이드로겔을 형성한 후, 이 구형의 겔을 숙성한 후 세척, 건조, 소성과정을 거쳐서 최종적으로 구형 알루미나 입자를 제조하게 된다.Spherical alumina particles are prepared by the oil-dropping method, i.e., alumina hydrosol prepared by dissolving aluminum metal in an acid solution and a weak base to be hydrolyzed with ammonia during the preparation process. After dropping in a liquid to form a spherical alumina hydrogel, the spherical alumina hydrogel is aged and then washed, dried and calcined to finally produce spherical alumina particles.
본 발명에서는 대기공의 기공구조를 가지는 구형 알루미나 입자를 제조하기 위하여 알루미나 하이드로졸과 약염기의 혼합물이 드로핑되는 현탁매개체로서 특정 비중과 동점도를 가지는 유동파라핀을 도입하고 이를 통과하면서 생성된 알루미나 하이드로겔 입자도 상기 특정 유동파라핀내에서 1차 숙성과정을 거친 후에 수산화암모니움 수용액에서의 2차 숙성과정으로 옮겨가도록 함으로써 대기공의 기공구조를 갖는 구형 알루미나 입자를 제조하였다.In the present invention, in order to prepare spherical alumina particles having a pore structure of air pores, alumina hydrogel produced by introducing a flowing paraffin having a specific specific gravity and kinematic viscosity as a suspension medium in which a mixture of alumina hydrosol and a weak base is dropped and passing through the same. Spherical alumina particles having a pore structure of atmospheric pores were prepared by allowing the particles to undergo a first aging process in the specific flow paraffin and then to a second aging process in an aqueous ammonium hydroxide solution.
드로핑과정에서 사용되는 현탁매개체는, 수용성인 알루미나하이드로졸과 약염기의 혼합물에 대해 불용성이고 물보다 표면장력이 커서, 드로핑된 혼합물 방울이 그 자체의 부피에서 가장 작은 표면적을 가지는 구조인 구형으로 성형되도록 해주는 역할을 할 수 있어야 한다.The suspending medium used in the dropping process is formed into a spherical structure in which the drop of the dropped mixture has the smallest surface area in its volume because it is insoluble in water-soluble mixtures of alumina hydrosol and weak base and has a higher surface tension than water. It should be able to play a role.
숙성과정에서는 현탁매개체내에서 알루미나하이드로겔이 100∼110℃의 온도로 24∼48시간동안 머무르며 이때 알루미나하이드로겔내의 약염기가 가수분해되면서 서서히 세공구조를 형성하게 해주어야 한다. 즉, 본 발명은 드로핑과 숙성과정에서 상기와 같은 역할을 수행할 수 있도록 비중이 0.86 - 0.87이고, 동점도가 10 - 30cSt 인 유동파라핀을 현택매개체로 사용함으로써 알루미나 입자내에 기공지름이 1μm상인 대기공의 세공구조를 가지도록 한다.In the aging process, the alumina hydrogel stays in the suspension medium at a temperature of 100 to 110 ° C. for 24 to 48 hours. At this time, the weak base in the alumina hydrogel is hydrolyzed to gradually form the pore structure. That is, the present invention uses a liquid paraffin having a specific gravity of 0.86-0.87 and a kinematic viscosity of 10-30 cSt as a suspension medium to perform the above roles in the dropping and aging process, the atmosphere having a pore diameter of 1 μm in the alumina particles. Have a pore structure.
한편, 동점도가 제시된 범위를 벗어날 경우 비록 비중이 제시된 범위내에 있더라도 대기공의 세공구조를 형성할 수 없다.On the other hand, if the kinematic viscosity is outside the range presented, even if the specific gravity is within the range can not form the pore structure of the air hole.
본 발명의 실시예는 다음과 같으며, 여기에 사용된 대기공 지름의 유무판정은 전자현미경(SEM)을 사용하여 1,000배 확대된 사진의 판독에 의하여 결정하였도, 비중 및 동점도 측정은 한국공업규격 2002(KS M 2002), 한국공업규격 2015(KS M 2014)에 의거하여 측정하였다.Examples of the present invention are as follows, and the determination of the presence or absence of the air hole diameter used here is determined by reading a photograph magnified 1,000 times by using an electron microscope (SEM), specific gravity and kinematic viscosity measurement is Korean Industrial Standard The measurements were made in accordance with 2002 (KS M 2002) and Korean Industrial Standard 2015 (KS M 2014).
<실시예 1><Example 1>
순도 99.7% 그래뉼형태 알루미늄 금속 10g을 순수 45.3㎖가 담긴 반응기에 투여하고 상온에서 혼합한 다음, 35% 황산 22.6㎖를 반응기에 12시간동안에 걸쳐서 매우 서서히 투여하였다. 발생되는 수소가스는 계속 배출시키면서 물재킷을 사용하여 90℃가 넘지 않도록 냉각시켰으며, 3시간 경과 후 부터는 맨틀을 이용한 가열을 적절히 조절하여 90℃를 계속 유지하여 24시간 경과시켜 알루미늄 수용액 약 50㎖을 얻었다.10 g of purity 99.7% granular aluminum metal was administered to a reactor containing 45.3 ml of pure water, mixed at room temperature, and then 22.6 ml of 35% sulfuric acid was administered to the reactor very slowly over 12 hours. The generated hydrogen gas was continuously discharged and cooled to not exceed 90 ℃ by using the water jacket.After 3 hours, the heating using the mantle was properly adjusted to maintain 90 ℃ for 24 hours. Got.
상온으로 냉각시킨 반응기에 다이알릴아민 9.3g을 순수 23.9㎖에 용해시킨 약염기수용액을 제조한 후, 투여하고 강하게 교반하면서 혼합하여 약 90㎖의 알루미나하이드로졸을 얻었다.A weak base solution in which 9.3 g of diallylamine was dissolved in 23.9 mL of pure water was prepared in a reactor cooled to room temperature, and then administered and mixed with vigorous stirring to obtain about 90 mL of alumina hydrosol.
비중 0.8687, 동점도 14.15 cSt 인 유동 파라핀을 현타매개체로서 지름 5㎝, 길이 10㎝의 유리관에 채우고 온도를 95℃로 유지하면서, 액위 4㎝위에서부터 Nozzle를 통하여 상기와 같이 제조된 알루미나하이드로졸을 드로핑하여 구형의 알루미나하이드로겔을 생성시켰다.Alumina hydrosols prepared as described above were drawn through a nozzle from 4 cm above the liquid level while filling the liquid tube with a specific gravity of 0.8687 and a kinematic viscosity of 14.15 cSt in a glass tube 5 cm in diameter and 10 cm in length as a suspension medium and maintaining the temperature at 95 ° C. To produce spherical alumina hydrogel.
유리관 밑바닥에 축적된 알루미나 하이드로겔을 추출하여 동일한 유동파라핀이 충진된 오일조에 옮기고 107℃, 15시간 동안 1차 숙성시켰다. 1차숙성된 알루미나하이드로겔을 오일조에서 추출하여 93℃, 25중량%의 수산화암모니움수용액 400㎖에 투입하고 8시간동안 2차 숙성을 진행시켰다.The alumina hydrogel accumulated in the bottom of the glass tube was extracted and transferred to the oil bath filled with the same liquid paraffin, and aged for 15 hours at 107 ° C. The first aged alumina hydrogel was extracted in an oil bath and poured into 400 ml of 25% by weight aqueous ammonium hydroxide solution, followed by secondary aging for 8 hours.
120℃에서 12시간동안 건조한 후, 630℃에서 3시간동안 소성하여 구형 알루미나 입자가 최종적으로 완성하여 입자의 전단면에 대한 전자현미경 촬영에 의하여 1μm이상의 지름을 가지는 기공의 유무를 확인하였다.After drying at 120 ° C. for 12 hours, calcining at 630 ° C. for 3 hours, the spherical alumina particles were finally finished, and the presence of pores having a diameter of 1 μm or more was confirmed by electron microscopy of the shear surface of the particles.
이렇게 제조된 구형 알루미나에 염화백금산 수용액과 염산을 각각 3.0부피%로 섞은 후 혼합수용액에 함침한 다음, 180℃의 건조공기에서 1시간 건조시킨 후, 400℃에서 2시간 소성시켰다. 백금이 함침된 알루미나 입자에 질산칼륨수용액과 염산을 각각 4.0부피%를 섞은 혼합수용액을 함침한 후, 150℃, 건조공기에서 2시간 건조시킨 다음, 650℃에서 2시간 소성시켜 최종 탈수화 촉매를 얻었다.Spherical alumina solution and hydrochloric acid were mixed in 3.0 vol% of the spherical alumina thus prepared, impregnated in a mixed aqueous solution, and then dried in a dry air at 180 ° C. for 1 hour, and then calcined at 400 ° C. for 2 hours. The impregnated alumina particles with platinum were impregnated with a mixed aqueous solution containing 4.0% by volume of potassium nitrate solution and hydrochloric acid, and then dried at 150 ° C. in dry air for 2 hours, and then calcined at 650 ° C. for 2 hours to obtain a final dehydration catalyst. Got it.
촉매의 성능평가를 위해 650℃에서 4시간 동안 수소로 환원한 후, 수소 및 프로판의 혼합기체를 유입시켜 탈수소반응 실험을 실시하였다. 반응조건은 프로판의 액체공간속도는 5hr-1, 수소와 프로판의 혼합몰비는 1 였으며, 반응압력은 1.5기압, 반응온도는 630℃ 등온으로 유지하였다. 반응전후의 기체 조성은 반응장치에 연결된 기체분석기에 의해 분석되어 프로판 전환율과 프로필렌 선택도를 구하고, 반응시간 20시간 경과 후의 전환율과 선택도로부터 반응안정성을 평가하였다.In order to evaluate the performance of the catalyst, it was reduced to hydrogen at 650 ° C. for 4 hours, and then a dehydrogenation experiment was conducted by introducing a mixed gas of hydrogen and propane. In the reaction conditions, the liquid space velocity of propane was 5hr −1 , the mixing molar ratio of hydrogen and propane was 1, the reaction pressure was 1.5 atm, and the reaction temperature was maintained at 630 ° C isothermal. The gas composition before and after the reaction was analyzed by a gas analyzer connected to the reactor to obtain propane conversion and propylene selectivity, and the reaction stability was evaluated from the conversion rate and selectivity after 20 hours of reaction time.
<비교예 1>Comparative Example 1
드포핑이 이루어지고 이어서 1차 숙성이 진행되는 현택매개체로서 케로젠을 사용하는 것을 제외하고는 실시예 1과 동일한 방법으로 구형 알루미나 입자를 제조, 분석하고 반응평가를 실시하였다.Spherical alumina particles were prepared and analyzed in the same manner as in Example 1, except that kerosene was used as a suspending medium in which depopping was carried out, followed by primary aging.
<비교예 2>Comparative Example 2
드로핑이 이루어지고 이어서 1차 숙성이 진행되는 현택매개체로서 비중 0.8699, 동점도 77.02 cSt 인 유동파라핀을 사용하는 것을 제외하고는 실시예 1과 동일한 방법으로 구형알루미나 입자를 제조, 분석하고 반응평가를 실시하였다.Spherical alumina particles were prepared and analyzed in the same manner as in Example 1 except for using a liquid paraffin having a specific gravity of 0.8699 and a kinematic viscosity of 77.02 cSt as a dropping medium followed by first aging. It was.
상기와 같은 방법으로 제조된 구형 알루미나 입자의 분석결과와 반응평가 결과를 아래 표에 나타내었다.The analysis results and the reaction evaluation results of the spherical alumina particles prepared by the above method are shown in the table below.
본 발명은 상기와 같은 현탁매개체를 이용한 드로핑 및 숙성과정을 거쳐 제조된 구형알루미나 입자는 기공구조가 충분히 구축될 수 있기 때문에 지름이 1μm 이상인 대기공의 세공구조를 가질 수 없고, 이에 따라 반응물인 노말파라핀과 생성물인 노말올레핀의 입자내에서의 흐름이 원활하도록 하여 이를 촉매지지체로 사용하여 제조됨으로써 탈수소촉매의 반응안정성을 향상시키게 된다.According to the present invention, the spherical alumina particles prepared through the dropping and aging process using the suspension medium as described above cannot have the pore structure of air pores having a diameter of 1 μm or more because the pore structure can be sufficiently built, and thus the reactants are The flow of the normal paraffin and the product normal olefin in the particle is smoothly produced by using it as a catalyst support to improve the reaction stability of the dehydrogenation catalyst.
Claims (1)