KR19980041817A - Liquid crystal display using organic insulating film and manufacturing method thereof - Google Patents

Abstract

On the substrate on which the thin film transistor and the storage capacitor electrode are formed, rotationally coated a planarized organic insulating film serving as an interlayer insulating film, forming a pixel electrode, and then partially etching the interlayer insulating film on the thin film transistor and forming an organic black photo on the etched portion. The resist is filled to form a black matrix. A sufficient storage capacity can be ensured by removing the interlayer insulating film on the storage capacitor electrode or by forming a metal layer.

Description

Liquid crystal display using organic insulating film and manufacturing method thereof

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thin film transistor liquid crystal display (hereinafter referred to as TFT-LCD), and more particularly to a TFT-LCD in which a black matrix is formed on a TFT substrate. It is about.

TFT-LCD, widely used as a flat panel display device, is composed of a TFT substrate and a color filter substrate. Black matrices are used to prevent light leakage between adjacent pixels and are usually formed on color filters. However, due to misalignment between the TFT substrate and the color filter substrate, the black matrix has a limit on preventing light leakage. Therefore, in recent years, the method of forming a black matrix on a TFT substrate is used. The manufacturing method of such a TFT substrate is called a black matrix on TFT.

1 is a cross-sectional view of a TFT substrate of a black matrix on TFT type according to the prior art.

As shown in FIG. 1, a gate electrode 2 and a storage capacitor electrode 3 are formed on the transparent insulating substrate 1. The gate insulating film 4 is formed on the gate electrode 2 and the storage capacitor electrode 3. An amorphous silicon layer 5, an etch stop layer 6, and an n ⁺ amorphous silicon layer 7 are sequentially formed on the gate insulating film 4 at a position corresponding to the gate electrode 2. have. A source electrode 8 and a drain electrode 9 are formed on the n ⁺ amorphous silicon layer 7, and the source electrode 8 is connected to a data line (not shown). The gate electrode 2, the gate insulating film 4, the amorphous silicon layer 5, the n ⁺ amorphous silicon layer 7, the source electrode 8 and the drain electrode 9 form a TFT. The protective film 10 is formed on the TFT and the gate insulating film 4, and the black matrix 11 is formed on the protective film 10 formed on the TFT. In the pixel region, a pixel electrode 12 made of indium tin oxide (ITO) is formed on the passivation layer 10, and the pixel electrode 12 is connected to the drain electrode 9 through a contact hole. .

Since the pixel electrode 12 and the data line are adjacent to each other, a coupling capacitance may occur between the pixel electrode 12 and the data line when the liquid crystal display is driven, and the coupling capacitance is an image signal of the liquid crystal display. Distort

In addition, since the black matrix 11 is formed on the TFT, the step difference between the TFT and the pixel electrode becomes large, and thus, the liquid crystal alignment may be defective and light leakage may occur. This light leakage can be solved by increasing the width of the black matrix, but in this case, the aperture ratio is reduced.

Meanwhile, the liquid crystal display device includes a TFT substrate and a color filter substrate, and a substrate spacer is inserted between the two substrates to maintain a constant cell gap, which is a thickness of the liquid crystal layer injected between the two substrates. do. According to the prior art, a method of dispersing a substrate spacer having a constant size on a substrate is mainly used, and the substrate spacer is also sprayed on the pixel electrode 12. However, due to the step in the color filter substrate and the step in the TFT substrate, it is not possible to create a uniform cell spacing, resulting in an uneven thickness of the liquid crystal layer, thereby degrading display characteristics. In addition, due to the shaded area of the substrate spacer scattered on the pixel electrode 12 of the liquid crystal cell, poor liquid crystal alignment and scattering of back light may occur. This misalignment or scattering of back light reduces the transmittance of the liquid crystal cell and generates light leakage.

SUMMARY OF THE INVENTION The present invention has been made to solve this problem, and an object of the present invention is to reduce the coupling capacitance generated between the pixel electrode and the data line, to reduce the poor liquid crystal alignment, and to increase the aperture ratio.

In addition, the gap between the liquid crystal cells is made uniform, and scattering of back light caused by the substrate spacer is suppressed to solve the problem of reduced transmittance and light leakage.

1 is a cross-sectional view showing the structure of a conventional black matrix on TFT substrate,

2 is a plan view showing the structure of a TFT substrate according to the first embodiment of the present invention,

3 is a cross-sectional view taken along line III-III 'of FIG. 2,

4 to 6 are cross-sectional views showing improved structures for compensating for the holding capacitance in the TFT substrate according to the first embodiment of the present invention shown in FIG.

7 is a cross-sectional view showing the structure of a TFT substrate according to the second embodiment of the present invention,

8 is a cross-sectional view showing the structure of a color filter substrate according to an embodiment of the present invention;

9 is a cross-sectional view showing the structure of a liquid crystal cell according to an embodiment of the present invention;

FIG. 10A is a plan view of a portion of the color filter substrate of FIG. 8 in which a substrate spacer is formed;

FIG. 10B is a cross-sectional view taken along the line X-X 'of FIG. 10A,

11A, 12A and 13A are plan views illustrating a method of manufacturing a TFT substrate according to the first embodiment of the present invention,

11B, 12B, and 13B are cross-sectional views taken along the lines XI-XI ′ of FIG. 11A, XII-XII ′ of FIG. 12A, and XIII-XIII ′ of FIG. 13A, respectively.

In order to achieve this problem, in the present invention, an interlayer insulating film is formed of an organic insulating film having a low dielectric constant. The dielectric constant is suitably 2.4 to 3.7, and the organic insulating film is formed flat on the gate line and the data line of the TFT substrate and on the TFT, so that the signal between the pixel electrode formed on the organic insulating film and the data line below the organic insulating film is reduced. It serves to prevent interference.

In addition, a portion of the interlayer insulating film on the TFT and the gate line and the data line is removed to form a groove, and a black matrix of organic black photoresist is flatly filled in the groove.

Herein, the thickness of the organic insulating film is formed to be 2.0 to 4.0 µm in order to sufficiently increase the insulation, and the thickness of the black matrix is preferably 0.5 to 1.7 µm.

In the pixel region, a storage capacitor electrode is formed on the transparent substrate to form a storage capacitor together with the pixel electrode on the interlayer insulating film. In order to prevent the storage capacitance from decreasing due to the interlayer insulating film having a low dielectric constant, the interlayer insulating film on top of the storage capacitor electrode is removed or made thin so that the storage capacitance has a sufficient value.

In addition, as another method for compensating the storage capacitor, a portion of the gate insulating film between the storage capacitor electrode and the pixel electrode is removed to reduce the thickness, or a metal layer connected to the storage capacitor electrode through the contact hole of the gate insulating film exposing the storage capacitor electrode. Can be formed over the gate insulating film, or a metal layer can be formed in contact with the pixel electrode on the gate insulating film above the storage capacitor electrode.

In order to maintain the cell gap between the TFT substrate and the corresponding color filter substrate, a substrate spacer made of an organic insulating film capable of a photolithography process is formed on the color filter substrate. This substrate spacer is formed between the color filters and is located only in the portion corresponding to the TFT of the TFT substrate.

In manufacturing such a TFT substrate, an organic insulating film is coated on the substrate on which the gate line, the data line, the storage capacitor electrode, and the TFT are formed, and the interlayer insulating film on the storage capacitor electrode is etched to reduce the thickness.

Next, an ITO film is deposited and patterned on the interlayer insulating film to form pixel electrodes in the pixel region, and the interlayer insulating film is etched to a predetermined depth using the pixel electrode as a mask, and then the organic black photoresist is formed on the etched portion. To form a flat black matrix.

Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the accompanying drawings, each component is shown differently from the actual ratio as necessary.

A TFT-LCD according to an embodiment of the present invention includes a cell composed of a TFT substrate and a color filter substrate, a liquid crystal injected into the cell, a driving circuit and additional devices.

FIG. 2 is a wiring diagram of the TFT substrate according to the first embodiment of the present invention, and FIG. 3 is a cross-sectional view taken along the line III-III 'of FIG. 2.

As shown in FIG. 2 and FIG. 3, a gate line 21 for transmitting a scan signal from the outside onto a transparent insulating substrate 10 such as glass and parallel to the gate electrode 20 and the gate line 21 which are branches thereof. The storage capacitor electrode 30 is formed, and the gate insulating film 40 covers them. A data line 81 is formed on the gate insulating film 40 to vertically cross the gate line 21 and transmit an image signal from the outside. An amorphous silicon layer 50 is formed on the gate insulating film 40 on the gate electrode 20, and the etch stop layer 60 and the ohmic contact layers 71 and 72 of n ⁺ amorphous silicon are formed thereon. It is. The source electrode 80 and the drain electrode 90 are formed on the ohmic contact layers 71 and 72, respectively, and the source electrode 80 is connected to the data line 81.

Here, the gate electrode 20, the source electrode 80, the drain electrode 90, the gate insulating film 40, the ohmic contact layers 71 and 72, and the amorphous silicon layer 50 form a TFT, and the source electrode 80 ) And the amorphous silicon layer 50 between the drain electrode 90 become the channel portion of the TFT. That is, when a scan signal is applied to the gate electrode 20 through the gate line 21, the thin film transistor is turned on and thus an image signal applied to the source electrode 80 through the data line 81. Is passed through the amorphous silicon layer 50 to the drain electrode.

The interlayer insulating film 100 covers the thin film transistor and the gate insulating film 40 and is formed flat. The interlayer insulating film 100 is made of an organic material having a low dielectric constant of about 2.4 to 3.7, and has a thickness of about 2.0 to 4.0 mu m.

Compared with the case of the silicon nitride film conventionally used as a protective film, the transmittance of the organic insulating film shows a high transmittance similar to that of a thin silicon nitride film even when the film thickness is 10 times or more. Specifically, the transmittance of the organic insulating film of 2.5 μm shows the same transmittance as the silicon nitride film of 0.2 μm in most visible light wavelength ranges.

Dow Chemical's Photo-BCB, BCB, PFCB or JSR's photoresist-based acrylic or polyimide-based or the like may be used as the organic insulating layer, and spin on glass (SOG) may also be used. Since these organic materials are flowable materials, they are spin coated to form an interlayer insulating film evenly.

The interlayer insulating layer 100 may have a smaller thickness on the storage capacitor electrode 30 to form a trench 120 or may be removed to expose the gate insulating layer 40, and the contact hole 130 exposing the drain electrode 90. Has) A pixel electrode 140 made of an ITO film is formed on the interlayer insulating film 100 in the pixel region divided by the gate line 21 and the data line 81. The pixel electrode 140 opens the contact hole 130. It is connected to the drain electrode 90 through the image signal is applied to drive the liquid crystal molecules.

The TFT, which is not covered with the pixel electrode 140, and the interlayer insulating layer 100 on the gate line 21 and the data line 81 are recessed to a certain depth to form a groove, and a black matrix 110 made of an organic black photoresist in the groove. ) Is filled and formed flat. The black matrix 110 may have a thickness of 0.5 to 1.7 μm to have a light density of 2.5 or more, thereby ensuring sufficient light blocking characteristics. The thickness of the black matrix may vary depending on the characteristics of the material forming the black matrix. In particular, the thickness of the black matrix may be reduced by using a material having a high light density. Since the pixel electrode 140 and the interlayer insulating film 100 are connected to each other, the resistance of the black matrix 110 is preferably increased, and the surface resistance is preferably 10 ¹⁰ Ω / □ or more.

As the material forming the black matrix, carbon-based organic materials and pigment-type organic materials may be used. In the case of carbon-based organic materials, the light density is higher. It is preferable to use. Graphite type materials have high light density but low surface resistance, making them unsuitable for black matrix materials.

In this case, the storage capacitor electrode 30 and the pixel electrode 140 serve as storage capacitor batteries. When the thick interlayer insulating layer 100 is formed between the two electrodes 30 and 140, the storage capacitance is reduced, thereby compensating for the compensation capacitor. To this end, the distance between the two electrodes 30 and 140 is reduced by removing the interlayer insulating film 100 between the storage capacitor electrode 30 and the pixel electrode 140 or making the thickness thinner.

Such TFT substrates may have several different forms to compensate for the holding capacitance. 4 to 6 are cross-sectional views showing structures of the TFT substrate improved to compensate for the holding capacitance.

As shown in FIG. 4, the TFT substrate of the first embodiment is formed by etching the gate insulating film 40 to a predetermined depth in addition to the interlayer insulating film 100 on the storage capacitor electrode 30. In this case, in order to etch the gate insulating film 40 to a uniform depth, the upper layer may be removed by forming a double layer having different etching ratios.

In the TFT substrate of the second aspect, as shown in FIG. 5, the metal layer 31 is formed on the gate insulating film 40 on the storage capacitor electrode 30. The metal layer 31 is connected to the storage capacitor electrode 30 through the contact hole 32, and the metal layer 31 is covered with the interlayer insulating film 100.

As shown in FIG. 6, in the third type TFT substrate, the metal layer 31 is formed on the upper gate insulating layer 40 of the storage capacitor electrode 30, and the interlayer insulating layer on the metal layer 31 is removed to thereby remove the pixel electrode. 140 covers the metal layer 31.

As such, since the organic interlayer insulating film 100 having a low dielectric constant is formed between the pixel electrode 140 and the data line 81, the coupling capacitance generated between the pixel electrode 140 and the data line 81 is reduced. As a result, the pixel electrode 140 may be formed to overlap the data line 81 and the gate line 21. Therefore, the aperture ratio of the TFT substrate can be increased by reducing the area occupied by the black matrix 110 and increasing the area occupied by the pixel electrode 140.

In addition, the black matrix 110 is formed on the TFT substrate to suppress photo induced leakage current due to reflection of the back light, and the liquid crystal alignment is performed because the surface of the substrate 10 is flat. The problem of the orientation defect resulting from the step | step difference between the patterns formed in the board | substrate 10 which arises in a process can be solved, and uniform rubbing can be performed. As a result, the light induction current is suppressed, thereby reducing the whitening phenomenon in the display device, and the poor liquid crystal alignment is reduced, thereby suppressing light leakage.

7 is a cross-sectional view of a thin film transistor substrate according to a second exemplary embodiment of the present invention. In the second embodiment of the present invention, an interlayer insulating film is formed on the thin film transistor substrate on which the thin film transistor having the etch-back structure is formed, the interlayer insulating film is formed on the interlayer insulating film on the thin film transistor, and the organic black photo is formed. The resist was filled to form a black matrix.

As shown in FIG. 7, in the TFT substrate according to the second embodiment of the present invention, the gate electrode 20 and the storage capacitor electrode 30 are formed on the transparent insulating substrate 10 such as glass, and the gate insulating film 40 ) Covers them. An amorphous silicon layer 50 is formed on the gate insulating film 40 on the gate electrode 20, and ohmic contact layers 71 and 72 made of n ⁺ amorphous silicon are formed thereon. The source electrode 80 and the drain electrode 90 are formed on the ohmic contact layers 71 and 72, respectively, and the source electrode 80 is connected to a data line (not shown).

The interlayer insulating film 100 is formed to cover the thin film transistor and the gate insulating film 40 and is formed flat. The thickness of the interlayer insulating film 100 is reduced above the storage capacitor electrode 30 to form the trench 120 or to remove the gate insulating film 40. This may be revealed and has a contact hole 130 exposing the drain electrode 90. In the pixel region, a pixel electrode 140 made of an ITO film is formed on the interlayer insulating film 100 and connected to the drain electrode 90 through the contact hole 130.

The interlayer insulating film 100 on the top of the TFT is recessed to a certain depth to form a groove, and the groove is filled with a black matrix 110 made of an organic black photoresist and formed flat.

The type, property, thickness, and the like of the organic insulating film used as the interlayer insulating film and the organic black photoresist constituting the black matrix are similar to those of the first embodiment of the present invention.

In the case of a substrate having a thin film transistor having an etch back structure, the channel portion of the thin film transistor and the organic insulating film are in direct contact with each other, unlike the case of the etch stopper structure.

The TFT substrate according to the second embodiment of the present invention may have another form for compensating for the holding capacitance as in the first embodiment. TFT substrates having this other form are similar to the improved structures of the TFT substrate according to the first embodiment of the present invention except for the structure of the thin film transistor.

8 illustrates a cross-sectional structure of a color filter substrate according to an exemplary embodiment of the present invention. As shown in FIG. 8, in the color filter substrate, the color filter 160 is formed on the transparent insulating substrate 150, the passivation layer 170 is formed on the color filter 160, and the common electrode is formed on the passivation layer 170. 180 is formed.

9 illustrates a cross-sectional structure of a liquid crystal cell according to an embodiment of the present invention. In order to maintain the cell gap between the TFT substrate and the color filter substrate, a columnar substrate spacer 190 is formed on the color filter substrate. The substrate spacer 190 is formed of an organic insulating film capable of a photographic process, and is placed on the channel portion of the TFT in the TFT substrate. In this case, since the upper portion of the TFT channel is a flattened film having a constant thickness, the TFT is not damaged even if the substrate spacer 190 is formed thereon.

FIG. 10A is a plan view of the color filter substrate on which the substrate spacer 190 is formed, and FIG. 10B is a cross sectional view taken along the line X-X 'of FIG. 10A and 10B, R, G, and B represent red, green, and blue color filters, respectively. This color filter 160 has a concave portion (a) as shown in FIG. 10A in the middle and a substrate spacer is formed in this portion.

In the color filter substrate, since the substrate spacer 190 is formed of an organic insulating layer capable of performing a photolithography process, it is easy to control the cell gap and form the substrate spacer 190 at a desired position. Therefore, the substrate spacer is not formed on the color filter 160 corresponding to the pixel electrode of the TFT substrate, but formed only on the portion corresponding to the TFT channel of the TFT substrate, thereby reducing cell gap defects due to the step difference. As the spacer 190 is positioned in the opening, problems of light leakage and transmittance reduction may be prevented. In addition, unlike conventional substrates in which R, G, and B color filters are all formed in a single thickness to maintain a constant cell gap, even if each of the R, G, and B color filters is formed to have a different thickness, a constant cell It is easy to adjust the color coordinate and transmittance of the color filter because it does not affect the spacing.

Since the substrate spacer 190 has a constant height, a shadow area may be generated thereby. In general, such shaded areas cause poor liquid crystal alignment in the rubbing process. However, since the shaded area in this case is formed to be narrower than the channel portion of the TFT and is covered by the black matrix, display defects due to alignment film coating and rubbing defects can be reduced.

Hereinafter, a method of manufacturing a TFT-LCD according to an embodiment of the present invention will be described with reference to the drawings.

11A, 12A, and 13A are plan views illustrating a method of manufacturing a TFT substrate according to an embodiment of the present invention, and FIGS. 11B, 12B, and 13B are XI-XI ′ of FIG. 11A and XII-XII of FIG. 12A, respectively. And cross-sectional views taken along lines XIII-XIII of FIG. 13A.

As shown in FIGS. 11A and 11B, a metal layer having a thickness of about 3,000 Å is deposited and patterned on the transparent insulating substrate 10 to form the gate electrode 20, the gate line 21, and the storage capacitor electrode 30. Subsequently, a gate insulating film 40 formed of silicon nitride or the like, an amorphous silicon layer, and a silicon nitride film are sequentially formed on the substrate 10 by chemical vapor deposition. At this time, the thickness of the gate insulating film is about 3,000-6,000 Pa, the thickness of the amorphous silicon layer is 500-1,000 Pa, and the thickness of the silicon nitride film used as the etch stop layer is 1,000-2,000 Pa. Next, a photoresist is deposited on the silicon nitride film and then exposed from the backside of the substrate 10 to form a photoresist pattern. The nitride film is etched using the photoresist as a mask to form an etch stop layer 60. A heavily doped n ⁺ amorphous silicon layer is then deposited and etched together with the amorphous silicon layer. Next, a source electrode 80, a drain electrode 90, and a data line 81 are formed by depositing and patterning a metal having a thickness of about 3,000 에 on the substrate 10, and using n ⁺ amorphous silicon layer as a mask. The ohmic contacts 71 and 72 are etched. The gate electrode 20, the source electrode 80, the drain electrode 90, the gate insulating film 40, the ohmic contact layers 71 and 72 and the amorphous silicon layer 50 form a TFT.

Next, as shown in FIGS. 12A and 12B, an interlayer insulating film 100 made of an organic insulating film having a low dielectric constant and a high light transmittance is formed on the substrate 10. The interlayer insulating film 100 is formed and planarized by a rotation coating method. Most preferably, the interlayer insulating film 100 has a dielectric constant of about 2.4 to 3.7 and a thickness of about 2.0 to 4.0 μm. A portion of the interlayer insulating layer 100 is etched to form contact holes 130 on the drain electrode 90 and to form a trench 120 on the storage capacitor electrode 30. At this time, the process of forming the contact hole is formed by using a general photolithography process, it can be formed by a dry etching method using O ₂ , SF ₆ , CF ₄ and the like. If the organic material used is a photo definable material, a pattern may be formed only by exposing and developing using a mask without applying a separate photoresist.

Next, as shown in FIGS. 13A and 13B, the ITO film is deposited and patterned on the substrate 10 to pattern the pixel electrodes 140 in individual pixel regions defined by the intersection of the gate lines 21 and the data lines 81. To form.

Next, as shown in FIGS. 2 and 3, the interlayer insulating film 100 is etched to a predetermined depth using the pixel electrode 140 as a mask, and the organic black photoresist is filled in the etched portion to form the black matrix 110. ) Is formed flat. At this time, the preferred etching depth is 0.5-1.7 mu m, and the surface resistance of the organic black photoresist has a value of 10 ¹⁰ Ω / □ or more. The black matrix 110 formed as described above has a light density of 2.5 or more.

Such TFT substrates may have several different forms in order to increase the holding capacitance. 4 to 6, a method of manufacturing a TFT substrate having different storage capacitor electrodes will be described.

In the TFT substrate of FIG. 4, as shown in FIG. 4, after etching the interlayer insulating film 100 to form the trench 120, a portion of the gate insulating film 40 on the storage capacitor electrode 30 is dry-etched. Etch using Therefore, the thickness of the gate insulating layer 40 on the storage capacitor electrode 30 is reduced, thereby increasing the storage capacitance. In this case, in order to etch to a uniform depth of the gate insulating film 40, it may be formed as a double layer having different etching ratios and only the upper layer may be removed.

In the TFT substrate of the second aspect, as shown in FIG. 5, a portion of the gate insulating film 40 is etched to form a contact hole 32 on the storage capacitor electrode 30. Next, when the source electrode 80 is formed, the metal layer 31 is formed on the storage capacitor electrode 30. The metal layer 31 is connected to the storage capacitor electrode 30 through the contact hole 32.

In the TFT substrate of the third form, as shown in FIG. 6, the metal layer 31 is formed on the storage capacitor electrode 30 when the source electrode 80 is formed. In this case, the metal layer 31 is connected to the pixel electrode 140 formed later.

On the other hand, with reference to Figure 8 will be described a method of manufacturing a color filter substrate according to an embodiment of the present invention. As shown in FIG. 8, the color resist is coated on the transparent substrate 150 and the color filter 160 is formed through a photolithography process. This color filter 160 may be partially removed to provide sufficient area for the substrate spacer to be formed. The passivation layer 170 is formed on the color filter 160, and the common electrode 180 is formed on the passivation layer 170 using the ITO layer.

Next, as shown in FIG. 9, an organic insulating layer is coated on the substrate 150, and a columnar substrate spacer 190 is formed through a photolithography process. The substrate spacer 190 lies only in the channel portion of the TFT in the above-described TFT substrate.

The TFT substrate and the color filter substrate are combined to form a liquid crystal cell, and a liquid crystal is injected therein and an additional circuit is attached to form a TFT-LCD.

As described above, in the TFT-LCD according to the present invention, a flattened black matrix on TFT substrate was formed using an interlayer insulating film made of an organic insulating film having a low dielectric constant. Therefore, the light induction current can be reduced by removing the reflection of the back light generated when the black matrix is formed on the color filter substrate. In addition, since the black matrix is formed using the pixel electrode pattern, the aperture ratio may be maximized, and the alignment defect due to the step between the patterns formed on the substrate may be reduced in the liquid crystal alignment process.

On the other hand, since the substrate spacer is formed of an organic insulating layer capable of a photolithography process, the substrate spacer is not formed on the color filter so that a cell gap defect due to the step of the color filter can be reduced, and the color coordinates of the color filter Transmittance adjustment is easy. In addition, since the substrate spacer exists only in the TFT channel portion, it is possible to prevent problems of light leakage and transmittance reduction caused by the substrate spacer positioned in the opening, and since the shaded area of the substrate spacer is smaller than the area of the TFT channel portion, the alignment layer Defects in the display due to poor application and rubbing can be reduced.

As a result, the TFT-LCD according to the present invention may have characteristics of high opening ratio, low power consumption, high contrast ratio and whitening reduction.

Claims (32)

Transparent insulation substrate, A thin film transistor formed on the substrate and comprising a gate electrode, a drain electrode, a source electrode, a gate insulating film, and a semiconductor layer; An interlayer insulating film covering the thin film transistor, having a groove on the thin film transistor, made of an organic insulating film, and having a constant height, and A black matrix filled in the groove Thin film transistor substrate. In claim 1, The interlayer insulating film has a first contact hole exposing the drain electrode, And a pixel electrode connected to the drain electrode through the first contact hole and formed on the interlayer insulating layer. Thin film transistor substrate. In claim 2, And a storage capacitor electrode formed on the substrate to be separated from the gate electrode and positioned below the pixel electrode with the gate insulating layer interposed therebetween. Thin film transistor substrate. In claim 3, The dielectric constant of the interlayer insulating film is 2.4-3.7 Thin film transistor substrate. In claim 3, The thickness of the interlayer insulating film is 2.0-4.0 ㎛ Thin film transistor substrate. In claim 3, The black matrix has a thickness of 0.5 to 1.7 μm or more. Thin film transistor substrate. In claim 3, The black matrix is formed of an organic black photoresist Thin film transistor substrate. In claim 7, The surface resistance of the organic black photoresist is 10 ¹⁰ Ω / □ or more Thin film transistor substrate. In claim 3, The interlayer insulating film covers the gate insulating film on the storage capacitor electrode. Thin film transistor substrate. In claim 9, The gate insulating film has a second contact hole exposing the storage capacitor electrode, And a metal layer formed on the gate insulating layer on the storage capacitor electrode and covered by the interlayer insulating layer and connected to the storage capacitor electrode through the second contact hole. Thin film transistor substrate. In claim 9, The interlayer insulating film on the storage capacitor electrode is thinner than other portions. Thin film transistor substrate In claim 3, The gate insulating film on the storage capacitor electrode is thinner than other portions. Thin film transistor substrate. In claim 12, The gate insulating layer is formed of a double layer made of a material having a different etching selectivity. Thin film transistor substrate. In claim 3, And a metal layer formed on the storage capacitor electrode and connected to the pixel electrode. Thin film transistor substrate. A transparent insulating substrate, a thin film transistor formed on the substrate, the thin film transistor comprising a gate electrode, a drain electrode, a source electrode, a gate insulating film and a semiconductor layer, and covering the thin film transistor flatly, having a groove on the thin film transistor, and formed of an organic insulating film. An interlayer insulating film, a black matrix filled in the grooves, and the interlayer insulating film having a first contact hole for exposing the drain electrode and connected to the drain electrode through the first contact hole and formed on the interlayer insulating film. A thin film transistor substrate including a pixel electrode, A color filter substrate comprising a transparent insulating substrate, a color filter formed on the substrate, and a common electrode formed on the color filter, and A substrate spacer formed between the thin film transistor substrate and the color filter substrate; Thin film transistor liquid crystal display. The method of claim 15, The substrate spacer is made of an organic insulating film Thin film transistor liquid crystal display. The method of claim 15, The substrate spacer is present on top of the thin film transistor Thin film transistor liquid crystal display. Forming a gate line and a gate electrode which is a branch of the gate line on the transparent insulating substrate, Forming a gate insulating film, Forming a semiconductor layer, Forming a data pattern including a data line intersecting the gate line, a source electrode and a drain electrode which are branches of the data line; Coating the interlayer insulating film evenly with the organic insulating film, Etching the interlayer insulating film to form a first contact hole exposing the drain electrode; Forming a pixel electrode on the pixel region which is divided into the gate line and the data line on the interlayer insulating layer; Etching a portion of the interlayer insulating film using the pixel electrode as a mask, and Forming a black matrix on the portion where the interlayer insulating layer is etched. Method of manufacturing a thin film transistor substrate. The method of claim 18, The interlayer insulating film has a dielectric constant of 2.4 to 3.7 Method of manufacturing a thin film transistor substrate. The method of claim 18, The thickness of the interlayer insulating film is formed to 2.0 to 4.0 ㎛ Method of manufacturing a thin film transistor substrate. The method of claim 18, The thickness of the black matrix is formed to 0.5 ~ 1.7㎛ Method of manufacturing a thin film transistor substrate. The method of claim 18, The black matrix is formed of an organic black photoresist Method of manufacturing a thin film transistor substrate. The method of claim 22, The organic black photoresist has a surface resistance of 10 ¹⁰ Ω / □ or more Method of manufacturing a thin film transistor substrate. The method of claim 18, Forming a storage capacitor electrode in the pixel area when forming the gate line; Method of manufacturing a thin film transistor substrate. The method of claim 24, Etching the interlayer insulating film over the storage capacitor electrode; Method of manufacturing a thin film transistor liquid crystal display device. The method of claim 25, Etching the gate insulating film on the storage capacitor electrode to a predetermined depth. Method of manufacturing a thin film transistor substrate. The method of claim 25, The gate insulating layer is formed of a double layer using a material having a different etching selectivity, Removing only the upper layer of the bilayer Method of manufacturing a thin film transistor substrate. The method of claim 24, Forming a metal layer on the gate insulating film on the storage capacitor electrode when the data line is formed, and Etching the interlayer insulating film to form a second contact hole exposing the metal layer; The pixel electrode is connected to the metal layer through the second contact hole. Method of manufacturing a thin film transistor substrate. The method of claim 24, Etching the gate insulating film to form a second contact hole exposing the storage capacitor electrode; and Forming a metal layer on the gate insulating layer to be connected to the storage capacitor electrode through the second contact hole when the data line is formed; Method of manufacturing a thin film transistor substrate. Coating the insulating interlayer with the organic insulating film on the transparent first insulating substrate on which the thin film transistor is formed, Forming a pixel electrode on the interlayer insulating layer; Etching a portion of the interlayer insulating layer using the pixel electrode as a mask to form a groove; Forming a black matrix in the groove, Forming a color filter on the transparent second insulating substrate, Forming a common electrode on an entire surface of the second insulating substrate on which the color filter is formed; and Forming a substrate spacer on the common electrode between the color filter substrates; Method of manufacturing a thin film transistor liquid crystal display device. The method of claim 30, The substrate spacer is formed of an organic insulating film Method of manufacturing a thin film transistor liquid crystal display device. The method of claim 30, Coupling the thin film transistor substrate and the color filter substrate such that the substrate spacer is positioned over the thin film transistor; Method of manufacturing a thin film transistor liquid crystal display device.