KR102622700B1 - 차폐력 향상 및 엠보가공에 의한 색상 발현이 가능한 위생재 부직포용 복합섬유 - Google Patents
차폐력 향상 및 엠보가공에 의한 색상 발현이 가능한 위생재 부직포용 복합섬유 Download PDFInfo
- Publication number
- KR102622700B1 KR102622700B1 KR1020210157810A KR20210157810A KR102622700B1 KR 102622700 B1 KR102622700 B1 KR 102622700B1 KR 1020210157810 A KR1020210157810 A KR 1020210157810A KR 20210157810 A KR20210157810 A KR 20210157810A KR 102622700 B1 KR102622700 B1 KR 102622700B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight ratio
- composite fiber
- dye
- tio2
- resin
- Prior art date
Abstract
본 발명은 위생재 부직포용 복합섬유에 있어서, 상기 복합섬유의 코어부는 폴리에스테르계 수지 95~99중량비 및 염료 1~5 중량비로 구성되고, 제2성분의 시스부는 폴리에스테르계 수지보다 융점이 20 ℃ 이상 낮은 폴리올레핀계 수지 95~99.5중량비 및 이산화티타늄(TiO2) 0.5~5 중량비로 구성되되,상기 이산화티타늄(TiO2) 대 염료의 중량비는 3:1~7:1이고, 상기 폴리에스테르계 수지는 방향족 디카르본산과 글리콜의 축중합물로, 폴리에틸렌 테레프탈레이트, 폴리에틸렌 2,6-디나프탈레이트, 폴리프로필렌 테레프탈레이트, 폴리부틸렌 테레프탈레이트, 폴리에틸렌 이소프탈레이트, 또는 이들의 혼합물이고, 상기 올레핀계 수지는 고밀도 폴리에틸렌, 저밀도 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌 공중합체, 또는 이들의 혼합물인 것에 특징이 있는 위생재 부직포용 복합섬유를 제공한다.
Description
본 발명은 차폐력 향상 및 엠보가공에 의한 색상 발현이 가능한 위생재 부직포용 복합섬유에 관한 것으로, 부직포용 복합섬유의 시스부에 실리카 소광제 및 코어부에 염료를 첨가하여 엠보 가공시 열에 의한 색상 발현이 되는 복합섬유에 대한 발명이다.
직물밀도 10∼45g/㎡의 저밀도 부직포는 종이기저귀, 위생냅킨 등의 표면재료로 사용된다. 부직포의 용도가 다양화됨에 따라, 부직포에 요구되는 특성 또한 엄격하게 되고, 부드러운 촉감을 유지하면서 고강도를 보유하는 부직포에 대한 요구가 있어 왔다.
이러한 요구에 부응하기 위하여 미세하고 열접착성이 있으며, 저융점 성분이 충분한 열접착강도를 제공할 뿐만 아니라 유연성을 부여하는 복합섬유가 필요하게 된다.
종래 폴리에틸렌, 폴리프로필렌 등의 폴리올레핀계 성분을 저융점성분으로 하고 통상의 폴리에틸렌테레프탈레이트 등의 폴리에스테르 및 폴리프로필렌 등의 폴리올레핀계 성분을 고융점성분으로 하는 시스-코아형 또는 사이드 바이 사이드형 복합섬유는 기존에 많이 알려져 있다.
예를 들어, 미국특허 5,866,488호에는 제1성분이 폴리에틸렌으로 되고 제2성분이 폴리에스테르로 되며, 상기 폴리에틸렌은 길이방향으로 섬유 표면의 적어도 일부를 연속적으로 점유하며 그 분자쇄에 1.5개/탄소수 1000 이하의 메틸 분기를 가지고, 밀도가 0.940∼0.965g/㎤, Q값(중량평균분자량/수평균분자량)이 4.8 이하인 열융착성 복합섬유가 제시된다.
또한 미국특허 제5,798,305호에는 폴리프로필렌 또는 폴리프로필렌으로 되는 고융점 성분과 폴리에틸렌으로 되는 저융점 성분으로 이루어지며, 폴리에틸렌이 섬유방향으로 섬유표면의 적어도 일부를 연속적으로 형성하며 분자쇄에 0∼1.5 메틸분기/탄소수 1000을 가지고, 밀도가 0.950∼0.965g/㎤, Q값(중량평균분자량/수평균분자)이 4.5 이하인 핫멜트접착성 복합섬유가 제시된다.
또한 생리대 및 기저귀와 같은 위생재료에 사용되는 부직포의 성능이 다양화되면서 고신축, 고벌키, 고흡수/발수성과 같은 기능이 강조되고 있다. 이와 더불어 제품에 대한 미적 디자인 또는 브랜드의 고급화를 위해 코팅이나 프린팅을 이용하여 외부에 추가가공을 진행시킬 수 있으나, 본 발명은 제품에 대한 엠보싱 가공으로 압력차이에 의한 색상발현될 수 있는 기술개발을 하게 되었다.
본 발명인 위생재 부직포용 복합섬유는 코어부의 염료색을 외부에서 선택적으로 확인할 수 있도록 부분 차폐성을 강화하기 위해 발명된 것으로, 복합섬유의 염료가 혼합된 코어부 및 차폐제인 이산화티타늄(TiO2)을 함유한 시스부로 구성된 복합섬유에 엠보싱 가공에 의해 부분적인 색상발현이 가능한 복합섬유를 제공하는 것을 목적으로 한다.
상기와 같은 문제점을 해결하기 위해 본 발명은 위생재 부직포용 복합섬유에 있어서, 상기 복합섬유의 코어부는 폴리에스테르계 수지 95~99중량비 및 염료 1~5 중량비로 구성되고, 제2성분의 시스부는 폴리에스테르계 수지보다 융점이 20 ℃ 이상 낮은 폴리올레핀계 수지 95~99.5중량비 및 이산화티타늄(TiO2) 0.5~5 중량비로 구성되되,상기 이산화티타늄(TiO2) 대 염료의 중량비는 3:1~7:1이고, 상기 폴리에스테르계 수지는 방향족 디카르본산과 글리콜의 축중합물로, 폴리에틸렌 테레프탈레이트, 폴리에틸렌 2,6-디나프탈레이트, 폴리프로필렌 테레프탈레이트, 폴리부틸렌 테레프탈레이트, 폴리에틸렌 이소프탈레이트, 또는 이들의 혼합물이고, 상기 올레핀계 수지는 고밀도 폴리에틸렌, 저밀도 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌 공중합체, 또는 이들의 혼합물인 것에 특징이 있는 위생재 부직포용 복합섬유를 제공한다.
또한 본 발명은 위생재 부직포용 복합섬유에 있어서, 상기 복합섬유의 코어부는 폴리프로필렌 수지 95~99중량비 및 염료 1~5 중량비로 구성되고, 제2성분의 시스부는 폴리에스테르계 수지보다 융점이 20 ℃ 이상 낮은 폴리올레핀계 수지 95~99.5중량비 및 이산화티타늄(TiO2) 0.5~5 중량비로 구성되되, 상기 이산화티타늄(TiO2) 대 염료의 중량비는 3:1~7:1이고, 상기 프로필렌 단독중합체, 프로필렌을 주성분으로 하는 에틸렌, 부텐-1 또는 4-메틸 펜텐-1 등과의 공중합체, 또는 이들의 혼합물이고, 상기 올레핀계 수지는 고밀도 폴리에틸렌, 저밀도 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌 공중합체, 또는 이들의 혼합물인 것에 특징이 있는 위생재 부직포용 복합섬유를 제공한다.
본 발명인 위생재 부직포용 복합섬유는 코어부의 염료색을 외부에서 선택적으로 확인할 수 있도록 부분 차폐성을 강화하기 위해 발명된 것으로, 복합섬유의 염료가 혼합된 코어부 및 차폐제인 이산화티타늄(TiO2)을 함유한 시스부로 구성된 복합섬유에 엠보싱 가공에 의해 부분적인 색상발현이 가능한 복합섬유를 제공하여 제품의 외관에 대한 디자인적인 효과를 제공할 수 있다.
이하 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. 우선, 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.
본 명세서에서 사용되는 정도의 용어 '약', '실질적으로' 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.
본 명세서에서 사용되는 정도의 용어 약, 실질적으로 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.
본 발명은 위생재 부직포용 복합섬유에 관한 것으로, 상기 복합섬유의 코어부는 폴리에스테르계 수지 95~99중량비 및 염료 1~5 중량비로 구성되고, 제2성분의 시스부는 폴리에스테르계 수지보다 융점이 20 ℃ 이상 낮은 폴리올레핀계 수지 95~99.5중량비 및 이산화티타늄(TiO2) 0.5~5 중량비로 구성된다. 이때 상기 이산화티타늄(TiO2) 대 염료의 중량비는 3:1~7:1가 바람직하다.
염료는 섬유에 혼합사용가능한 것은 모두 사용가능하며, 이에 대한 제한은 없다. 예를 들면, Cibacron Red FR, Cibacron Blue FR, Cibacron Yellow F4G, Cibacron Navy 등도 사용가능하다.
이산화타타늄(TiO2)은 무기계 자외선 차단제로 많이 사용되고 있는 소재 중 하나로 이산화티탄은 굴절이 높아 빛을 산란시키는 효과가 우수하며 입자가 미세하여 백색도, 은폐력, 착색력 등의 광학적 성질이 우수하다.
폴리에스테르계 수지는 방향족 디카르본산과 글리콜의 축중합물로, 방향족 디카르본산으로는 테레프탈산, 이소프탈산, 프탈산, 나프탈렌디카르본산 등을 사용할 수 있고, 글리콜로는 에틸렌글리콜, 1,3-프로판디올, 14-부탄디올 등을 사용할 수 있다.
상기 폴리에스테르계 수지는 방향족 디카르본산과 글리콜의 축중합물로, 폴리에틸렌 테레프탈레이트, 폴리에틸렌 2,6-디나프탈레이트, 폴리프로필렌테레프탈레이트, 폴리부틸렌 테레프탈레이트, 폴리에틸렌이소프탈레이트, 또는 이들의 혼합물이 바람직하게 사용된다. 바람직하게는 폴리에틸렌 테레프탈레이트를 사용할 수 있다. 폴리에스테르계 수지는 ASTM D2857에 준하여 측정한 고유점도(IV)가 050 내지 080 dL/g인 것이 바람직하다.
올레핀계 수지는 열접착시 용융되는 부분으로 폴리에스테르계 수지보다 융점이 20 ℃ 이상 낮은 올레핀계 수지를 사용하는 것이 바람직하다. 올레핀계 수지는 고밀도 폴리에틸렌(HDPE), 중밀도 폴리에틸렌(MDPE), 저밀도 폴리에틸렌(LDPE), 폴리프로필렌, 에틸렌-프로필렌 공중합체 또는 이들의 혼합물이다. 바람직하게는 고밀도 폴리에틸렌(HDPE)을 사용할 수 있다. 올레핀계 수지의 유동흐름지수(MI, Melting Index)는 특별히 제한되지 않지만,
바람직하게는 1 내지 100 g/10분, 더욱 바람직하게는 5 내지 40 g/10분이다.
본 발명에 따른 다른 구체예의 부직포 바인더용 열접착형 복합섬유는 제1성분으로 폴리프로필렌 수지 및 제2성분으로 폴리올레핀계 수지로 이루어지고, 5~30 %의 중공율을 갖는 것을 특징으로 하는 탄성과 벌키성이 우수한 중공형태의 부직포 바인더용 열접착형 복합섬유에 관한 것이다.
상기 폴리프로필렌 수지는 폴리프로필렌은 프로필렌을 주성분으로 하는 결정성 중합체의 총칭이며, 이중에는 프로필렌 단독중합체 뿐만 아니라, 프로필렌을 주성분으로 하는 에틸렌, 부텐-1 또는 4-메틸 펜텐-1 등과의 공중합체, 또는 이들의 혼합물이 바람직하게 사용될 수 있다. 바람직하게는 호모 폴리프로필렌을 사용할 수 있다.
폴리프로필렌 수지의 동흐름지수(MI, Melting Index)는 특별히 제한되지 않지만, 바람직하게는 1 내지 100 g/10분, 더욱 바람직하게는 10 내지 40 g/10분이다.
본 발명의 부직포 바인더용 열접착형 복합섬유는 제1성분이 30∼70 중량% 및 제2성분이 70∼30 중량%로 이루어지는 것이 바람직하다.
이하 본 발명에 따른 위생재 부직포용 이형단면 열접착 복합섬유를 제조하기 위한 방법의 실시예를 나타내지만, 본 발명이 실시예로 한정되는 것은 아니다.
실시예 1
제1성분(코어부) 조성물로서 고유점도가 0.64 dL/g인 폴리에틸렌 테레프탈레이트 99.5wt%에 블루염료 0.5wt% 함유하고, 제2성분(시스부) 조성물로서 저융점 폴리에틸렌 수지(HDPE 또는 PE) 98wt% 및 TiO2를 2.0wt% 함유한 제2성분 조성물 50중량%를 압출기에 투입하여 용융하였다.
용융된 제1성분 및 제2성분 조성물을 통상의 시스-코어 소프트 복합방사장치로 유입한 후 800 m/분의 방사속도로 방사하였다. 폴리에틸렌 테레프탈레이트의 유리전이온도 이상의 온도에서 방사된 복함섬유를 3.0~4.0배 연신배향하고, 크림프를 부여하여 38~64 mm로 절단하여 본 발명에 따른 복합섬유를 제조하였다. 이후 부직포로 만든 후 엠보싱 가공을 하였다.
실시예 2
실시예 1과 동일하게 제조하되, 제2성분 코어부에 폴리프로필렌으로 하였다.
비교예 1
실시예 1과 동일하게 제조하되, 제2성분 시스부에 차폐제(TiO2)를 첨가하지 않았다.
비교예 2
실시예 1과 동일하게 제조하되, 제2성분 시스부에 차폐제(TiO2) 1.0w%, 제1성분 코어부에 염료 0.5w%로 첨가하였다.
비교예 3
실시예 1과 동일하게 제조하되, 제2성분 시스부에 차폐제(TiO2) 4w%, 제1성분 코어부에 염료 0.5w%로 첨가하였다.
◈ 실시예 및 비교예의 물성 평가
1. 물성평가 방법
* 차폐성(색차계)
5x5cm(25cm2) 면적의 시료의 일면에 파란색 물감을 5cc 떨어뜨린 후 1분 후
색차계를 이용하여 L,a,b 값을 측정하였다.
| 구분 | 실시예1 | 실시예 2 | 비교예1 | 비교예2 | 비교예3 | |
| Sheath부 (제2성분) |
비중 | 50w% | 50w% | 50w% | 50w% | 50w% |
| Resin | HDPE 또는 PE | HDPE 또는 PE | HDPE 또는 PE | HDPE 또는 PE | HDPE 또는 PE | |
| 첨가제 | TiO2 2w% | TiO2 2w% | - | TiO2 1w% | TiO2 4w% | |
| Core부 (제1성분) |
비중 | 50w% | 50w% | 50w% | 50w% | 50w% |
| Resin | PET | PP | PET | PET | PET | |
| 첨가제 | Blue 염료 0.5w% | Blue 염료 0.5w% | Blue 염료 0.5w% | Blue 염료 0.5w% | Blue 염료 0.5w% | |
| 색차 | L | 95.6 | 95.8 | 95.5 | 95.1 | 96.5 |
| a | -0.3 | -0.2 | -0.3 | -0.2 | -0.6 | |
| b | 2.8 | 2.7 | 2.7 | 2.5 | 3.6 | |
| 엠보 공정 후 부직포 | 색상 발현 | 색상 발현 | 전체 색상 Blue | 전체 색상 약간 Blue |
Blue 생삭 발현 안됨 |
|
상기 표1과 같이 코어부와 시스부의 중량비가 1 대 1일 경우 첨가된 염료 대 TiO2의 중량비가 1: 4인 실시예 1,2의 색상발현이 의미가 있으며, 비교예 1은 시스부에 차폐제가 없어 코어부의 염료 색이 그대로 전체색상으로 나타나고, 비교예 2는 염료 대 TiO2의 중량비가 1: 2로 차폐제 함량이 낮아 시스부의 차폐성이 낮아 엠보싱 부분 이외에도 약간의 색상이 발현되고, 비교예 3은 염료 대 TiO2의 중량비가 1: 8로 차폐력이 너무 커서 엠보 공정 후에도 염료색의 발현이 어렵다.
이상에서 설명한 바와 같은 본 설명의 특징 및 기타의 장점은 후술되는 실시예로부터 보다 명백하게 될 것이며, 하기 실시예는 예시적인 목적으로 기재될 뿐 본 발명의 보호범위를 한정하거나 제한하는 것으로 해석될 수 없다.
Claims (2)
- 위생재 부직포용 복합섬유에 있어서,
상기 복합섬유의 코어부는 폴리에스테르계 수지 95~99중량비 및 염료 1~5 중량비로 구성되고,
제2성분의 시스부는 폴리에스테르계 수지보다 융점이 20 ℃ 이상 낮은 폴리올레핀계 수지 95~99.5중량비 및 이산화티타늄(TiO2) 0.5~5 중량비로 구성되되,
상기 이산화티타늄(TiO2) 대 염료의 중량비는 3:1~7:1이고,
상기 폴리에스테르계 수지는 방향족 디카르본산과 글리콜의 축중합물로, 폴리에틸렌 테레프탈레이트, 폴리에틸렌 2,6-디나프탈레이트, 폴리프로필렌 테레프탈레이트, 폴리부틸렌 테레프탈레이트, 폴리에틸렌 이소프탈레이트, 또는 이들의 혼합물이고, 상기 폴리올레핀계 수지는 고밀도 폴리에틸렌, 저밀도 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌 공중합체, 또는 이들의 혼합물로 유동흐름지수(MI, Melting Index)은 5 내지 40 g/10분인 것에 특징이 있는 위생재 부직포용 복합섬유를 이용하여,
5x5cm(25cm2) 면적의 시료의 일면에 파란색 물감을 5cc 떨어뜨린 후 1분 후색차계의 L값이 95.6, a값이 -0.3, b값이 2.8인 것으로,
상기 코어부의 염료색을 외부에서 선택적으로 확인할 수 있도록 부분 차폐성을 강화하고, 복합섬유의 염료가 혼합된 코어부 및 차폐제인 이산화티타늄(TiO2)을 함유한 시스부로 구성된 복합섬유에 엠보싱 가공에 의해 부분적인 색상발현이 가능한 복합섬유를 제공하여 제품의 외관에 대한 디자인적인 효과에 특징이 있는
차폐력 향상 및 엠보가공에 의한 색상 발현이 가능한 위생재 부직포용 복합섬유.
- 위생재 부직포용 복합섬유에 있어서,
상기 복합섬유의 코어부는 폴리프로필렌 수지 95~99중량비 및 염료 1~5 중량비로 구성되고,
제2성분의 시스부는 상기 폴리프로필렌 수지보다 융점이 20 ℃ 이상 낮은 폴리올레핀계 수지 95~99.5중량비 및 이산화티타늄(TiO2) 0.5~5 중량비로 구성되되,
상기 이산화티타늄(TiO2) 대 염료의 중량비는 3:1~7:1이고,
상기 폴리프로필렌 수지는 프로필렌 단독중합체이고, 상기 폴리올레핀계 수지는 고밀도 폴리에틸렌, 저밀도 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌 공중합체, 또는 이들의 혼합물로 유동흐름지수(MI, Melting Index)은 5 내지 40 g/10분인 것에 특징이 있는 위생재 부직포용 복합섬유를 이용하여,
5x5cm(25cm2) 면적의 시료의 일면에 파란색 물감을 5cc 떨어뜨린 후 1분 후색차계의 L값이 95.6, a값이 -0.3, b값이 2.8인 것으로,
상기 코어부의 염료색을 외부에서 선택적으로 확인할 수 있도록 부분 차폐성을 강화하고, 복합섬유의 염료가 혼합된 코어부 및 차폐제인 이산화티타늄(TiO2)을 함유한 시스부로 구성된 복합섬유에 엠보싱 가공에 의해 부분적인 색상발현이 가능한 복합섬유를 제공하여 제품의 외관에 대한 디자인적인 효과에 특징이 있는
차폐력 향상 및 엠보가공에 의한 색상 발현이 가능한 위생재 부직포용 복합섬유.