KR102617043B1 - 공동주택 건축물의 친환경 상수관 제조방법 - Google Patents
공동주택 건축물의 친환경 상수관 제조방법 Download PDFInfo
- Publication number
- KR102617043B1 KR102617043B1 KR1020220171173A KR20220171173A KR102617043B1 KR 102617043 B1 KR102617043 B1 KR 102617043B1 KR 1020220171173 A KR1020220171173 A KR 1020220171173A KR 20220171173 A KR20220171173 A KR 20220171173A KR 102617043 B1 KR102617043 B1 KR 102617043B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- eco
- water
- core material
- Prior art date
Abstract
본 발명은 공동주택 건축물의 친환경 상수관 제조방법에 관한 것으로, 보다 상세하게는 계면분리가 일어나지 않으면서 수생생물의 성장을 억제하고, 원활한 상수의 흐름을 유도할 수 있도록 개선된 공동주택 건축물의 친환경 상수관 제조방법에 관한 것이다.
Description
본 발명은 건축 기술 분야 중 공동주택 건축물의 친환경 상수관 제조방법에 관한 것으로, 보다 상세하게는 계면분리가 일어나지 않으면서 수생생물의 성장을 억제하고, 원활한 상수의 흐름을 유도할 수 있도록 개선된 공동주택 건축물의 친환경 상수관 제조방법에 관한 것이다.
일반적으로 식수를 공급하는 수도관은 주철관 또는 아연관 등의 금속관을 사용하고 있으며, 이러한 금속관은 오랜 기간 사용할 경우 관의 내벽에 발생하는 녹으로 인하여 내벽이 부식되고 녹은 식수에 혼입되어 식수를 오염시킴으로써 식수를 위생적으로 공급하는데 많을 문제점을 발생시키고 있을 뿐 아니라 금속관은 설치작업 및 운반시에 과중한 무게로 인하여 작업성이 나쁘다.
상기와 같은 문제점은 금속관보다 강도면에서 약한 합성수지제 수도관의 내충격성을 개선한 올레핀계의 고밀도폴리에틸렌(HDPE) 및 폴리염화비닐(PVC)수지로 제조된 수도관으로 대체하여 사용함으로써 해결할 수 있으나, 합성수지제 수도관 역시 물을 저속으로 흘리거나 장기 체류하는 경우에는 대장균과 같은 유해 미생물의 번식으로 인하여 악취를 발생시켜 불쾌감을 주거나 심한 경우 설사, 장염, 식중독을 일으킬 수 있으므로 합성수지제로 수도관을 제작할 때 항균성을 부여하는 기술들이 개발되어 있다.
하지만, 상수의 흐름성을 저해하지 않으면서 수생생물의 번식을 막고, 청결한 깨끗한 물을 공급할 수 있는 상수관의 제조 필요성은 여전하다고 볼 수 있다.
즉, 현재 개시되고 있는 상수관을 기능을 더욱 더 개량할 기술들이 지속적으로 개발되어야 할 것이다.
특히, 현재 개시되고 있는 대부분의 기술들은 코팅층을 형성하는 것이 대부분인데, 코팅층의 경우에는 오래 사용시 벗겨지거나 계면 분리에 의해 탈락되는 경우가 많아 효과를 지속시키는데 한계가 있다. 즉, 반영구적인 사용이 어렵다.
본 발명은 이상과 같은 문제점등을 해결하고자 안출된 것으로서, 계면분리가 일어나지 않으면서 수생생물의 성장을 억제하고, 원활한 상수의 흐름을 유도할 수 있도록 개선된 공동주택 건축물의 친환경 상수관 제조방법을 제공함에 있다.
본 발명은 상기한 목적을 달성하기 위한 수단으로, 상수관을 만들기 위한 원료를 조성하는 제1단계; 상기 제1단계에서 조성된 원료를 이중다이스에 주입하여 이중압출하는 제2단계; 이중압출된 압출관의 외표면을 방식처리하는 제3단계; 상기 제3단계 후 규격별로 커팅하여 제품화하는 제4단계;를 포함하는 공동주택 건축물의 친환경 상수관 제조방법에 있어서; 상기 제1단계에서 원료조성은 코어재와 쉘재로 각각 나뉘어 이루어지며, 상기 제2단계에서 이중압출은 코어재와 쉘재가 각각 다른 통로로 투입된 후 압출되어 쉘재가 코어재를 완전히 감싸 밀봉하는 형태로 이루어진 것을 특징으로 하는 공동주택 건축물의 친환경 상수관 제조방법을 제공한다.
이때, 상기 코어재는 저밀도폴리에틸렌(LDPE) 100중량부에 대해, 편백유 5중량부, 글루타싸이온 5중량부, 10㎛ 입도의 참숯분말 3.5중량부를 혼합하여 조성되며; 상기 쉘재는 고밀도폴리에틸렌(HDPE) 100중량부에 대해, 삼인산칼슘 15중량부, 10㎛ 입도의 제올라이트분말 10중량부, 메틸실리코네이트 5.5중량부, 히드록시프롤린 5.5중량부, 탄산바륨 3.5중량부를 혼합하여 조성된 것에도 그 특징이 있다.
본 발명에 따르면, 계면분리가 일어나지 않으면서 수생생물의 성장을 억제하고, 원활한 상수의 흐름을 유도할 수 있도록 개선된 효과가 있다.
도 1은 본 발명에 따른 방법을 설명하는 플로우챠트이다.
이하에서는, 첨부도면을 참고하여 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.
본 발명 설명에 앞서, 이하의 특정한 구조 내지 기능적 설명들은 단지 본 발명의 개념에 따른 실시예를 설명하기 위한 목적으로 예시된 것으로, 본 발명의 개념에 따른 실시예들은 다양한 형태로 실시될 수 있으며, 본 명세서에 설명된 실시예들에 한정되는 것으로 해석되어서는 아니된다.
도 1에 도시된 바와 같이, 본 발명에 따른 공동주택 건축물의 친환경 상수관 제조방법은 상수관을 만들기 위한 원료를 조성하는 제1단계; 상기 제1단계에서 조성된 원료를 이중다이스에 주입하여 이중압출하는 제2단계; 이중압출된 압출관의 외표면을 방식처리하는 제3단계; 상기 제3단계 후 규격별로 커팅하여 제품화하는 제4단계;를 포함한다.
이때, 상기 제1단계에서 원료조성은 코어재와 쉘재로 각각 나뉘어 이루어지며, 상기 제2단계에서 이중압출은 코어재와 쉘재가 각각 다른 통로로 투입된 후 압출되어 쉘재가 코어재를 완전히 감싸 밀봉하는 형태로 이루어진다.
아울러, 상기 코어재는 저밀도폴리에틸렌(LDPE) 100중량부에 대해, 편백유 5중량부, 글루타싸이온 5중량부, 10㎛ 입도의 참숯분말 3.5중량부를 혼합하여 조성된다.
이 경우, 편백유는 편백나무에서 추출한 오일로 천연 항균기능을 수행하기 위해 첨가된다.
그리고, 글루타싸이온은 글루탐산, 시스테인, 글라이신 세개의 펩티드로 구성되어 산화와 환원의 순환이 반복되면서 독성 과산화물을 제거하는 특성을 갖는다.
또한, 참숯은 물질을 따뜻하게 하는 힘을 방사하여 인체의 혈액순환을 원활하게 돕는 원적외선 방출특성, 복원력이 뛰어나고 무한정 전자공급을 통해 산화방지 및 환원하는 특성, 부패균의 발생을 억제하여 악취를 흡착하고 냄새를 제거하는 특성을 제공하기 위해 첨가된다.
이러한 코어재는 쉘재에 의해 밀봉되며, 쉘재의 극미세 공극을 통해 극미량씩 용출되면서 상수를 정화하고, 항균하는데 극미량씩 용출되기 때문에 상수관의 수명을 다할 때 까지 반영구적으로 사용할 수 있다.
한편, 상기 쉘재는 고밀도폴리에틸렌(HDPE) 100중량부에 대해, 삼인산칼슘 15중량부, 10㎛ 입도의 제올라이트분말 10중량부, 메틸실리코네이트 5.5중량부, 히드록시프롤린 5.5중량부, 탄산바륨 3.5중량부를 혼합하여 조성된다.
여기에서, 삼인산칼슘은 항균기능을 강화시키고, 수중 미생물의 성작을 억제하기 위해 첨가된다.
또한, 제올라이트분말은 수생생물의 성장을 차단하고, 물이끼가 생기지 않도록 하기 위해 첨가된다.
뿐만 아니라, 메틸실리코네이트는 강한 발수력을 제공하면서 오염되지 않도록 표면을 평활하게 유지하는 방오 기능도 확보하게 된다.
아울러, 히드록시프롤린(hydroxyproline)은 압출성형품의 표면 크랙발생을 억제하고, 갈라짐 방지, 내부식화를 강화시킨다.
그리고, 탄산바륨은 응집을 촉진하여 경화성을 좋게 하고, 매끄러운 표면을 형성하도록 유도하여 성형성과 가공성을 증대시킬 뿐만 아니라, 자외선을 흡수하지 않아 산화방지, 변색방지에도 기여한다.
다른 한편, 본 발명에서는 상기 코어재를 형성할 때 저밀도폴리에틸렌(LDPE) 100중량부에 대해, 기능성 가공액 30중량부, 설포라판 10중량부를 더 첨가할 수 있다.
이 경우, 상기 기능성 가공액은 오존수 100중량부에 대해 메틸이소치아졸리논 10중량부, 망간아세테이트 15중량부, 사과껍질 추출액 10중량부가 혼합되어 구성된다.
여기에서, 상기 오존수는 무성코로나방전 방식으로 오존을 발생시키는 오존발생기를 이용하여 생성된 오존에 물을 1:5의 비율로 혼합하여 이루어지며, 이러한 오존수는 항산화 및 항균(살균) 특성이 매우 뛰어난 것으로 보고되어 있다.
다만, 오존 가스 자체는 인체에 유해하지만, 이를 물에 녹여 오존수로 만들게 되면 안전하게 사용할 수 있는데, 이러한 오존수는 암치료, 치과치료, 식품안전 및 수질정화에 다양한 방식을 활용되고 있음이 알려져 있다.
그리고, 메틸이소치아졸리논(2-methyl-4-isothiazoline-3-one)은 살균, 분해력을 증대시키면서 분산력을 높이기 위해 첨가된다.
이때, 망간아세테이트는 사방형의 결정성 분말로 분해되어 망간산화물을 형성할 때 서서히 산화되면서 유기물 분해, 라디칼 반응 촉진 효과를 높이는 작용을 위해 첨가된다.
또한, 사과껍질 추출액은 특히 납을 포함한 중금속 성분 제거에 효과를 보이는 것으로 보고되어 있다.
그리고, 설포라판은 강한 항균성에 의한 수인성 전염병(예. 결막염), 특히 물에서 발생하는 눈병을 일으키는 원인균의 활성을 억제하는데 유용하다.
다른 한편, 본 발명에서는 상기 쉘재를 형성할 때 고밀도폴리에틸렌(HDPE) 100중량부에 대해, 테르페노이드 10중량부, 질석 5중량부, P-페닐아조아닐린 5중량부, 디메틸폴리실록산 15중량부를 더 첨가할 수 있다.
뿐만 아니라, 테르페노이드는 물때를 분해하여 물때가 고착되는 것을 방지하고,
또한, 질석(Vermiculite)은 운모와 같은 결정구조를 가지는 단사정계에 속하는 광물로 버미큘라이트라고도 하며, 양이온 교환능력이 크다.
아울러, P-페닐아조아닐린은 소수화에 따른 발수특성은 물론 방수, 방습 특성을 강화시킨다.
특히, 디메틸폴리실록산은 열에 강한 실록산 결합(Si-O-Si)과 유기질의 메틸기로 구성되어 있어 소포성, 내열성, 열산화 안정성, 내화학성과 발수성을 증대시킨다.
또다른 한편, 상기 제3단계에서 이루어지는 압출관의 외표면에 대한 방식처리는 스프레이코팅 방식으로 이루어지며, 코팅되는 코팅액은 고밀도폴리에틸렌 100중량부에 대해, 리그닌설폰산염 10중량부, 구아검 15중량부, 붕사 5중량부, 에틸렌디아민테트라아세트산 5중량부 및 물 50중량부를 혼합하여 이루어진다.
이때, 리그닌설폰산염은 수화열에 의한 균열을 방지하고 응결경화를 조절하게 된다.
그리고, 구아검은 점탄성이 높아 조성물의 접착력을 높이도록 하이드로겔화시키는 주요 구성으로서, 붕사와 반응하여 하이드로겔화 속도를 조절하게 된다. 이 경우, 상기 구아검과 붕사는 3:1의 중량비를 가져야 한다.
또한, 에틸렌디아민테트라아세트산(Ethylenediaminetetraacetic acid)는 산화에 의한 산패를 막고 중성화를 억제하여 채움재의 성형 후 내식성을 강화시키기 위해 첨가된다.
이와 같은 방법으로 상수관을 제조하게 되면 반영구적인 항균성과 물때가 잘 끼지 않는 특성을 가져 깨끗한 물을 공급할 수 있게 된다.
Claims (2)
- 삭제
- 상수관을 만들기 위한 원료를 조성하는 제1단계; 상기 제1단계에서 조성된 원료를 이중다이스에 주입하여 이중압출하는 제2단계; 이중압출된 압출관의 외표면을 방식처리하는 제3단계; 상기 제3단계 후 규격별로 커팅하여 제품화하는 제4단계;를 포함하고,
상기 제1단계에서 원료조성은 코어재와 쉘재로 각각 나뉘어 이루어지며, 상기 제2단계에서 이중압출은 코어재와 쉘재가 각각 다른 통로로 투입된 후 압출되어 쉘재가 코어재를 완전히 감싸 밀봉하는 형태로 이루어진 것을 특징으로 하는 공동주택 건축물의 친환경 상수관 제조방법에 있어서,
상기 코어재는 저밀도폴리에틸렌(LDPE) 100중량부에 대해, 편백유 5중량부, 글루타싸이온 5중량부, 10㎛ 입도의 참숯분말 3.5중량부를 혼합하여 조성되며;
상기 쉘재는 고밀도폴리에틸렌(HDPE) 100중량부에 대해, 삼인산칼슘 15중량부, 10㎛ 입도의 제올라이트분말 10중량부, 메틸실리코네이트 5.5중량부, 히드록시프롤린 5.5중량부, 탄산바륨 3.5중량부를 혼합하여 조성된 것을 특징으로 하는 공동주택 건축물의 친환경 상수관 제조방법.