KR102458029B1 - Sofa with antibacterial function and manufacturing method thereof - Google Patents
Sofa with antibacterial function and manufacturing method thereof Download PDFInfo
- Publication number
- KR102458029B1 KR102458029B1 KR1020220084739A KR20220084739A KR102458029B1 KR 102458029 B1 KR102458029 B1 KR 102458029B1 KR 1020220084739 A KR1020220084739 A KR 1020220084739A KR 20220084739 A KR20220084739 A KR 20220084739A KR 102458029 B1 KR102458029 B1 KR 102458029B1
- Authority
- KR
- South Korea
- Prior art keywords
- sofa
- manufacturing
- antibacterial
- covering fabric
- antibacterial function
- Prior art date
Abstract
Description
본 발명은 항균 기능을 구비한 소파 및 그의 제조방법에 관한 것으로서, 좀더 세부적으로 말하자면 소파 커버링 원단에 직접 항균 처리를 함으로써 오염되기 쉬운 환경에서 소파 표면에 부착되는 세균과 바이러스를 사멸시켜서 항균 효과를 나타낼 수 있도록 하며, 비프탈레이트계 가소제를 사용함으로써 인체 유해성을 제거하고, 보호제를 사용하여 내구성을 향상시키고, 고분자 결합제를 사용하여 기계적 물성을 유지할 수 있도록 하는, 항균 기능을 구비한 소파 및 그의 제조방법에 관한 것이다.The present invention relates to a sofa having an antibacterial function and a method for manufacturing the same, and more specifically, by directly applying an antibacterial treatment to a sofa covering fabric, it can kill bacteria and viruses attached to the surface of the sofa in an environment prone to contamination, thereby exhibiting an antibacterial effect. A sofa having an antibacterial function and a method for manufacturing the same, which removes harmfulness to the human body by using a nonphthalate-based plasticizer, improves durability by using a protective agent, and maintains mechanical properties by using a polymer binder it's about
일반적으로, 소파는 일반사람들이 앉아 휴식을 취하는 휴식용 의자이며, 보통 의자의 앉는 자리를 길게 한 형으로 2 내지 4인용의 크기가 보통이나 2인용과 1인용을 2 내지 3개 맞춘 것도 있으며, 이러한 소파는 사용자가 안정된 자세로 편안한 휴식을 도모하기 위한 수단으로 사용되어 왔다.In general, a sofa is a resting chair where ordinary people sit and take a rest, and it is a type with a long seat, usually for 2 to 4 people, but there are also 2 or 3 sets of 2 people and 1 person, Such a sofa has been used as a means for a user to promote a comfortable rest in a stable posture.
또한, 소파는 등받이 및 쿠션받이로 이루어진 프레임에 각각 올려져 조립되는 시트백 및 시트쿠션과, 이 시트쿠션 양측에 위치되는 팔걸이로 이루어지는데, 이러한 소파는 소파에 앉은 사람의 몸무게에 의한 압력을 견디는 쿠션재의 탄성력과 압력이 해제되어 쿠션재가 원상태로 복원되는 복원력이 함께 작용할 수 있다.In addition, the sofa consists of a seat back and a seat cushion assembled by being mounted on a frame made of a backrest and a cushion support, respectively, and armrests positioned on both sides of the seat cushion, such a sofa is a cushioning material that withstands pressure due to the weight of a person sitting on the sofa The elastic force and pressure of the cushion material are released and the restoring force that restores the cushioning material to its original state can act together.
소파는 등을 기대는 등받이 부분과 앉는 방석부재가 일체로 되어 있는 경우도 있고 등받이 부분과 방석부재가 분리되어 있는 경우도 있으며, 거실이나 실내 등의 공간에 맞게 적절히 배치하여 사용되고 있다.In the case of a sofa, the backrest part on which the back rests and the seat cushion member are integrally formed, or the backrest part and the cushion member are separated in some cases.
이러한 소파는 가정, 사무실, 업소 등과 같이 다양한 장소에서 사용되고 있는데, 최근에 COVID-19로 인하여 전염병에 대한 경각심이 높아진 관계로 소파의 항균 처리에 대한 수요가 높아지고 있다. These sofas are used in various places such as homes, offices, businesses, etc. Recently, the demand for antibacterial treatment of sofas is increasing due to increased awareness of infectious diseases due to COVID-19.
이러한 소파의 항균 처리에 관한 기술로서, 소파 프레임의 표면에 항균필름을 접착하여 소파를 구성함으로써, 항균성, 항취성 및 소취성이 우수하여 위생적으로 사용 가능하고, 코팅성 및 접착성이 뛰어나 쉽게 박리되거나 손상되지 않도록 하는 기술이 대한민국 등록특허공보 등록번호 10-2267226(공고일자 2021년 06월 22일)의 "항균성 소파"에서 개시된바 있다.As a technology related to the antibacterial treatment of the sofa, by attaching an antibacterial film to the surface of the sofa frame to configure the sofa, it can be used hygienically due to excellent antibacterial, anti-odor and deodorizing properties, and easy peeling due to excellent coating and adhesion A technology to prevent it from being damaged or damaged has been disclosed in "Antibacterial Sofa" of Republic of Korea Patent Publication No. 10-2267226 (announcement date June 22, 2021).
그러나, 상기한 등록번호 10-2267226를 포함한 종래의 소파는 소파 프레임에 항균 처리를 하기 때문에 항균효율이 높지 않은 문제점이 있다.However, the conventional sofa including the registration number 10-2267226 has a problem in that the antibacterial efficiency is not high because the sofa frame is subjected to antibacterial treatment.
본 발명의 목적은 상기한 바와 같은 종래의 문제점을 해결하기 위한 것으로서, 소파 커버링 원단에 직접 항균 처리를 함으로써 오염되기 쉬운 환경에서 표면에 부착되는 세균과 바이러스를 사멸시켜서 항균 효과를 높일 수 있도록 하는, 항균 기능을 구비한 소파 및 그의 제조방법을 제공하는 데 있다. An object of the present invention is to solve the problems of the prior art as described above, and to kill bacteria and viruses attached to the surface in an environment prone to contamination by directly antibacterial treatment on the sofa covering fabric to increase the antibacterial effect, To provide a sofa having an antibacterial function and a method for manufacturing the same.
본 발명의 다른 목적은, 비프탈레이트계 가소제를 사용함으로써 인체 유해성을 제거하고, 보호제를 사용하여 내구성을 향상시키고, 고분자 결합제를 사용하여 기계적 물성을 유지할 수 있도록 하는, 항균 기능을 구비한 소파 및 그의 제조방법을 제공하는 데 있다. Another object of the present invention is to remove harmfulness to the human body by using a non-phthalate-based plasticizer, improve durability by using a protective agent, and maintain mechanical properties by using a polymer binder, a sofa having an antibacterial function and its To provide a manufacturing method.
상기한 목적을 달성하기 위한 수단으로서 본 발명의 구성은, 소파 프레임을 제조하는 단계와, 소파 커버링원단을 준비하는 단계와, 알코올기를 가지는 항균물질과, 주석산 염을 1~4 : 1의 몰비율로 공융혼합한 후, 산화아연을 더하여 항균성 공융 혼합물을 제조하는 단계와, 다이아이소노닐 프탈산(Diisononyl phthalate)을 수소반응(hydrogenation)시켜서 비프탈레이트계 가소제를 제조하는 단계와, PVC 수지에 항균성 공융 혼합물과 가소제와 보호제와 고분자 결합제를 혼합하여 코팅제를 제조하는 단계와, 소파 커버링원단에 코팅제를 도포하는 단계와, 코팅제가 도포된 소파 커버링원단을 건조시키는 단계와, 건조가 완료된 소파 커버링원단을 재단하는 단계와, 재단되어 있는 소파 커버링원단을 재봉하는 단계와, 소파 프레임에 소파 커버링원단을 커버링하는 단계를 포함하여 이루어지면 바람직하다.As a means for achieving the above object, the configuration of the present invention comprises a step of manufacturing a sofa frame, a step of preparing a sofa covering fabric, an antibacterial substance having an alcohol group, and a tartrate salt in a molar ratio of 1-4: 1 After eutectic mixing, adding zinc oxide to prepare an antimicrobial eutectic mixture, hydrogenation of diisononyl phthalate to produce a nonphthalate plasticizer, and antimicrobial eutectic mixture to PVC resin Mixing a plasticizer, a protective agent, and a polymer binder to prepare a coating agent, applying a coating agent to the sofa covering fabric, drying the sofa covering fabric coated with the coating agent, and cutting the sofa covering fabric after drying It is preferable to include the step of sewing the cut sofa covering fabric, and the step of covering the sofa covering fabric on the sofa frame.
본 발명의 구성은, 상기 항균물질은, 멘톨, 프로폴리스, 및 플라보노이드의 그룹으로부터 선택되는 1가지 이상을 사용하지면 바람직하다.In the configuration of the present invention, the antibacterial substance is preferably at least one selected from the group consisting of menthol, propolis, and flavonoids.
본 발명의 구성은, 상기 가소제는 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르를 제조하여 사용하면 바람직하다.In the constitution of the present invention, the plasticizer is preferably used by preparing 1-2 cyclohexane dicarboxylic acid diisononyl ester.
본 발명의 구성은, 상기 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르는 밀도 0.944 ~ 0.954 g/cm3, 점도 44 ~ 60 mPa*s인 것을 사용하면 바람직하다.In the configuration of the present invention, the 1-2 cyclohexane dicarboxylic acid diisononyl ester preferably has a density of 0.944 to 0.954 g/cm 3 and a viscosity of 44 to 60 mPa*s.
본 발명의 구성은, 상기 보호제는 금속 인산염을 사용하면 바람직하다.As for the structure of this invention, when the said protective agent uses a metal phosphate, it is preferable.
본 발명의 구성은, 상기 금속인산염은 인산아연(zinc phosphate)을 사용하면 바람직하다.In the configuration of the present invention, the metal phosphate is preferably zinc phosphate.
본 발명의 구성은, 상기 금속 인산염은 입자 크기가 0.5 내지 10 μm인 것을 사용하면 바람직하다.In the configuration of the present invention, it is preferable to use the metal phosphate having a particle size of 0.5 to 10 μm.
본 발명의 구성은, 상기 고분자 결합제는 알키드 폴리우레탄(alkyd polyurethane), 폴리비닐 부티랄(polyvinyl butyral) 중에서 선택되는 하나 이상을 포함하면 바람직하다.In the configuration of the present invention, the polymer binder preferably includes at least one selected from alkyd polyurethane and polyvinyl butyral.
본 발명은, 소파 커버링 원단에 직접 항균 처리를 함으로써 오염되기 쉬운 환경에서 소파 표면에 부착되는 세균과 바이러스를 사멸시켜서 항균 효과를 나타낼 수 있도록 하며, 비프탈레이트계 가소제를 사용함으로써 인체 유해성을 제거하고, 보호제를 사용하여 내구성을 향상시키고, 고분자 결합제를 사용하여 기계적 물성을 유지할 수 있도록 하는, 효과를 갖는다.The present invention provides an antibacterial effect by killing bacteria and viruses adhering to the surface of the sofa in an environment prone to contamination by directly applying antibacterial treatment to the sofa covering fabric, and by using a nonphthalate-based plasticizer, it removes harmfulness to the human body, It has an effect of improving durability by using a protective agent and maintaining mechanical properties by using a polymer binder.
도 1은 본 발명의 일 실시예에 따른 항균 기능을 구비한 소파의 제조방법의 공정 순서도이다.1 is a process flowchart of a method of manufacturing a sofa having an antibacterial function according to an embodiment of the present invention.
이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 본 발명의 바람직한 실시예를 첨부된 도면을 참조로 하여 상세히 설명하기로 한다. 본 발명의 목적, 작용, 효과를 포함하여 기타 다른 목적들, 특징점들, 그리고 동작상의 이점들이 바람직한 실시예의 설명에 의해 보다 명확해질 것이다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings in order to describe in detail enough that those of ordinary skill in the art can easily practice the present invention. Other objects, features, and operational advantages, including the object, action, effect, and other objects of the present invention will become clearer by the description of the preferred embodiment.
참고로, 여기에서 개시되는 실시예는 여러가지 실시가능한 예중에서 당업자의 이해를 돕기 위하여 가장 바람직한 실시예를 선정하여 제시한 것일 뿐, 본 발명의 기술적 사상이 반드시 제시된 실시예에만 의해서 한정되거나 제한되는 것은 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위내에서 균등물 내지 대체물들을 포함하는 다양한 변화와 부가 및 변경이 가능하다.For reference, the embodiments disclosed herein are only presented by selecting and presenting the most preferred embodiments to help those skilled in the art from among various possible implementations, and the technical spirit of the present invention is not necessarily limited or limited only by the presented embodiments. No, various changes, additions, and modifications including equivalents or substitutes are possible without departing from the technical spirit of the present invention.
또한, 본원의 명세서 및 청구범위에 사용된 용어나 단어의 표현은, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 정의된 것으로서, 통상적이거나 사전적인 의미로만 한정해서 해석되어서는 아니되며, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 일예로서, 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한 복수의 표현을 포함한다.In addition, the terms or expressions used in the specification and claims of the present application are defined on the basis of the principle that the inventor can appropriately define the concept of the term in order to best describe his invention. , should not be construed as being limited only to the conventional or dictionary meaning, but should be interpreted as meaning and concept consistent with the technical spirit of the present invention. As an example, the singular expression includes the plural expression unless the context clearly dictates otherwise.
도 1은 본 발명의 일 실시예에 따른 항균 기능을 구비한 소파의 제조방법의 공정 순서도이다.1 is a process flowchart of a method of manufacturing a sofa having an antibacterial function according to an embodiment of the present invention.
도 1에 도시되어 있는 바와 같이, 본 발명의 일 실시예에 따른 항균 기능을 구비한 소파의 제조방법은, 소파 프레임을 제조하는 단계(S10)와, 소파 커버링원단을 준비하는 단계(S20)와, 알코올기를 가지는 항균물질과, 주석산 염을 1~4 : 1의 몰비율로 공융혼합한 후, 산화아연을 더하여 항균성 공융 혼합물을 제조하는 단계(S30)와, 비프탈레이트계 가소제를 제조하는 단계(S40)와, PVC 수지에 항균성 공융 혼합물과 가소제와 보호제와 고분자 결합제를 혼합하여 코팅제를 제조하는 단계(S50)와, 소파 커버링원단에 코팅제를 도포하는 단계(S60)와, 코팅제가 도포된 소파 커버링원단을 건조시키는 단계(S70)와, 건조가 완료된 소파 커버링원단을 재단하는 단계(S80)와, 재단되어 있는 소파 커버링원단을 재봉하는 단계(S90)와, 소파 프레임에 소파 커버링원단을 커버링하는 단계(S100)를 포함하여 이루어진다.As shown in Fig. 1, the method of manufacturing a sofa having an antibacterial function according to an embodiment of the present invention includes manufacturing a sofa frame (S10), and preparing a sofa covering fabric (S20) and , an antibacterial material having an alcohol group and a tartaric acid salt in a molar ratio of 1 to 4: 1, followed by adding zinc oxide to prepare an antimicrobial eutectic mixture (S30), and preparing a nonphthalate-based plasticizer ( S40) and mixing an antimicrobial eutectic mixture, a plasticizer, a protective agent, and a polymer binder in a PVC resin to prepare a coating (S50), and applying a coating agent to the sofa covering fabric (S60), and a sofa covering with a coating agent applied Steps of drying the fabric (S70), cutting the drying finished sofa covering fabric (S80), sewing the cut sofa covering fabric (S90), and covering the sofa covering fabric on the sofa frame (S100) is included.
상기 항균성 공융혼합물은 다음의 화학시 1과 같이 알코올기를 가지는 항균물질과, 다음의 화학식 2와 같은 주석산 염을 1~4 : 1의 몰비율로 공융혼합한 후, 산화아연을 더하여 제조한다.The antimicrobial eutectic mixture is prepared by eutectic mixing an antibacterial material having an alcohol group as shown in 1 in the following chemistry and a tartrate salt as shown in Chemical Formula 2 in a molar ratio of 1-4: 1, and then adding zinc oxide.
[화학식 1][Formula 1]
[화학식 2][Formula 2]
상기 항균물질은, 멘톨, 프로폴리스, 및 플라보노이드의 그룹으로부터 선택되는 1가지 이상을 사용할 수 있다.The antibacterial material may be one or more selected from the group of menthol, propolis, and flavonoids.
일반적으로 사용되는 주석산은 물에 대한 용해도가 낮아 수지에 혼입할 경우 고농도로 적용되기 어려워 제형에 제한이 있으므로, 주석산 염 형태로 항균물질과 이온결합을 유도하여 용해도 및 안정성을 개선할 수 있다. Since tartaric acid generally used has low solubility in water, it is difficult to apply it at high concentration when incorporated into a resin, so there is a limitation in formulation.
상기 화학식 1의 알코올기를 가지는 항균물질과, 화학식 2의 주석산 염의 각 몰비율에서의 이온결합을 하기 반응식에 나타내었다.The ionic bond at each molar ratio of the antibacterial material having an alcohol group of Formula 1 and the tartaric acid salt of Formula 2 is shown in the following reaction formula.
[반응식 1] 항균물질:주석산 염 (1:1)[Scheme 1] Antibacterial substance: tartrate (1:1)
[반응식 2] 항균물질:주석산 염 (2:1)[Scheme 2] Antibacterial substance: tartrate (2:1)
[반응식 3] 항균물질:주석산 염 (3:1)[Scheme 3] Antibacterial substance: tartrate (3:1)
[반응식 4] 항균물질:주석산 염 (4:1)[Scheme 4] Antibacterial substance: tartrate (4:1)
상기 항균물질과 주석산 염은 특정 작용기의 부분 전하에 의한 쌍극자간 결합으로 인해 공융혼합물을 형성할 수 있고, 이들의 화학 구조를 통해 상기 범위의 몰비에서 항균성 공융혼합물을 형성할 수 있다.The antibacterial substance and the tartrate salt may form a eutectic mixture due to the dipole bond due to the partial charge of a specific functional group, and through their chemical structure, an antimicrobial eutectic mixture may be formed at a molar ratio in the above range.
상기 주석산 염의 몰비율이 1을 초과하면 항균물질과 이온결합을 하지 못하고 남는 주석산 염 분자들이 물에 대한 용해도를 초과하여 저온에서 석출될 수 있다.When the molar ratio of the tartrate exceeds 1, the tartrate molecules remaining without ionic bonding with the antibacterial material may be precipitated at a low temperature in excess of solubility in water.
상기 항균성 공융혼합물은 침전물이 없는 투명상을 갖는다.The antimicrobial eutectic has a clear phase without precipitates.
상기 가소제는, 다음의 반응식 5와 같이 다이아이소노닐 프탈산(Diisononyl phthalate)을 수소반응(hydrogenation)시킴으로서 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르를 제조하여 사용한다.The plasticizer is used by preparing 1-2 cyclohexane dicarboxylic acid diisononyl ester by hydrogenation of diisononyl phthalate as shown in Scheme 5 below.
[반응식 5][Scheme 5]
상기 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르는 밀도 0.944 ~ 0.954 g/cm3, 점도 44 ~ 60 mPa*s인 것을 사용한다.The 1-2 cyclohexane dicarboxylic acid diisononyl ester uses a density of 0.944 to 0.954 g/cm 3 , and a viscosity of 44 to 60 mPa*s.
상기 보호제는, 하나 이상의 금속 인산염(metal phosphates)을 포함하고, 입자 형태로 평균 크기는 0.5 내지 10 μm인 것을 사용한다.The protective agent includes one or more metal phosphates, and has an average size of 0.5 to 10 μm in the form of particles.
상기 금속 인산염은 인산아연(zinc phosphate)을 사용한다.The metal phosphate is zinc phosphate.
상기 금속 인산염은 입자 크기가 0.5 내지 10 μm인 경우에 가소제와 혼합시 단단한 응집 혼합물을 형성함으로써 코팅층의 부식을 방지하여 내구성을 향상시키는데 도움을 준다.When the metal phosphate has a particle size of 0.5 to 10 μm, it helps to improve durability by preventing corrosion of the coating layer by forming a hard cohesive mixture when mixed with a plasticizer.
상기 고분자 결합제는 알키드 폴리우레탄(alkyd polyurethane), 폴리비닐 부티랄(polyvinyl butyral) 중에서 선택되는 하나 이상을 포함한다.The polymer binder includes at least one selected from alkyd polyurethane and polyvinyl butyral.
상기 고분자 결합제는 상기 가소제 및 보호제를 운반하여 결합시키는 역할을 하며, 혼합 과정에서 발생하는 전단력을 방지할 뿐만 아니라 보호제 내에 있는 인산염의 부하를 감소시켜 가소제 및 보호제의 표면 특성이 크게 변하지 않고 우수한 기계적 물성을 유지할 수 있도록 한다.The polymer binder serves to transport and bind the plasticizer and the protective agent, and not only prevents the shear force generated during the mixing process, but also reduces the load of phosphate in the protective agent, so that the surface properties of the plasticizer and the protective agent are not significantly changed and excellent mechanical properties to be able to maintain
상기한 구성에 의한, 본 발명의 일실시예에 따른 항균 기능을 구비한 소파 및 그의 제조방법의 작용은 다음과 같다.According to the above configuration, the operation of the sofa and its manufacturing method having an antibacterial function according to an embodiment of the present invention is as follows.
먼저, 소파 프레임을 제조한다(S10).First, a sofa frame is manufactured (S10).
다음에, 소파 커버링원단을 준비한다(S20). 소파 원단으로서는 천연가죽, 인조가죽, 파샤, 패브릭, 사무드, 세르텍스, 라무스, 플로킹 등이 있다.Next, prepare a sofa covering fabric (S20). Sofa fabrics include natural leather, artificial leather, pasha, fabric, samud, certex, ramus, and flocking.
이어서, 알코올기를 가지는 항균물질과, 주석산 염을 1~4 : 1의 몰비율로 공융혼합한 후, 산화아연을 더하여 항균성 공융 혼합물을 제조한다(S30).Next, an antibacterial substance having an alcohol group and a tartrate salt are eutectic-mixed in a molar ratio of 1-4: 1, and then zinc oxide is added to prepare an antimicrobial eutectic mixture (S30).
다음에, 다이아이소노닐 프탈산(Diisononyl phthalate)을 수소반응(hydrogenation)시킴으로써 비프탈레이트계 가소제로서 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르를 제조한다(S40).Next, diisononyl phthalate is hydrogenated to prepare 1-2 cyclohexane dicarboxylic acid diisononyl ester as a non-phthalate-based plasticizer (S40).
상기 가소제는 석유자원에서 합성되는 기존의 환경호르몬 유발물질을 발생시키지 않으면서도, PVC 수지 조성물에 혼합함으로써 가소제 본연의 성능인 PVC의 유연성을 증가시켜서 가공성을 용이하게 할 수 있다.The plasticizer can facilitate processability by increasing the flexibility of PVC, which is the original performance of the plasticizer, by mixing it with the PVC resin composition without generating the existing environmental hormone-inducing substances synthesized from petroleum resources.
이어서, PVC 수지에 상기 항균성 공융 혼합물 및 상기 가소제, 그리고 보호제와 고분자 결합제를 혼합하여 코팅제를 제조한다(S50).Then, a coating agent is prepared by mixing the antimicrobial eutectic mixture, the plasticizer, and the protective agent and the polymer binder in the PVC resin (S50).
다음에, 소파 커버링원단에 코팅제를 도포함으로써 코팅층을 형성한다(S60). 이 경우에 소파 커버링원단의 재질에 따라 소파 커버링원단 전체를 코팅할 수도 있고, 소파 커버링원단을 부분적으로 코팅할 수도 있다. Next, a coating layer is formed by applying a coating agent to the sofa covering fabric (S60). In this case, depending on the material of the sofa covering fabric, the entire sofa covering fabric may be coated, or the sofa covering fabric may be partially coated.
이어서, 코팅제가 도포된 소파 커버링원단을 건조시킨다(S70).Then, the sofa covering fabric coated with the coating agent is dried (S70).
다음에, 건조가 완료된 소파 커버링원단을 재단한다(S80).Next, the drying finished sofa covering fabric is cut (S80).
이어서, 재단되어 있는 소파 커버링원단을 재봉한다(S90).Then, the cut sofa covering fabric is sewn (S90).
다음에, 소파 프레임에 소파 커버링원단을 커버링함으로써 소파를 제작한(S100).Next, the sofa was manufactured by covering the sofa covering fabric on the sofa frame (S100).
Claims (9)
소파 커버링원단을 준비하는 단계와,
알코올기를 가지는 항균물질과, 주석산 염을 1~4 : 1의 몰비율로 공융혼합한 후, 산화아연을 더하여 항균성 공융 혼합물을 제조하는 단계와,
다이아이소노닐 프탈산(Diisononyl phthalate)을 수소반응(hydrogenation)시켜서 비프탈레이트계 가소제를 제조하는 단계와,
PVC 수지에 항균성 공융 혼합물과 가소제와 보호제와 고분자 결합제를 혼합하여 코팅제를 제조하는 단계와,
소파 커버링원단에 코팅제를 도포하는 단계와,
코팅제가 도포된 소파 커버링원단을 건조시키는 단계와,
건조가 완료된 소파 커버링원단을 재단하는 단계와,
재단되어 있는 소파 커버링원단을 재봉하는 단계와,
소파 프레임에 소파 커버링원단을 커버링하는 단계를 포함하여 이루어지는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. manufacturing a sofa frame;
A step of preparing a sofa covering fabric,
Preparing an antimicrobial eutectic mixture by eutectic mixing an antibacterial substance having an alcohol group and a tartrate salt in a molar ratio of 1-4: 1, and then adding zinc oxide;
preparing a non-phthalate-based plasticizer by hydrogenation of diisononyl phthalate ;
Preparing a coating agent by mixing an antimicrobial eutectic mixture, a plasticizer, a protective agent, and a polymer binder in PVC resin;
Applying a coating agent to the sofa covering fabric;
Drying the sofa covering fabric to which the coating agent is applied;
Cutting the sofa covering fabric after drying is completed;
A step of sewing the cut sofa covering fabric,
Method of manufacturing a sofa with an antibacterial function, characterized in that it comprises the step of covering the sofa covering fabric on the sofa frame.
상기 항균물질은, 멘톨, 프로폴리스, 및 플라보노이드의 그룹으로부터 선택되는 1가지 이상을 사용하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. The method of claim 1,
The antibacterial material, menthol, propolis, and a method of manufacturing a sofa having an antibacterial function, characterized in that using at least one selected from the group of flavonoids.
상기 가소제는 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르를 제조하여 사용하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. The method of claim 1,
The plasticizer is a method of manufacturing a sofa having an antibacterial function, characterized in that used to prepare 1-2 cyclohexane dicarboxylic acid diisononyl ester.
상기 1-2 사이클로헥산 디카르복실산 다이아이소노닐 에스테르는 밀도 0.944 ~ 0.954 g/cm3, 점도 44 ~ 60 mPa*s인 것을 사용하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. 4. The method of claim 3,
The 1-2 cyclohexane dicarboxylic acid diisononyl ester is a method of manufacturing a sofa having an antibacterial function, characterized in that it uses a density of 0.944 ~ 0.954 g / cm 3 , and a viscosity of 44 ~ 60 mPa *s.
상기 보호제는 금속 인산염을 사용하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. The method of claim 1,
The method of manufacturing a sofa having an antibacterial function, characterized in that the protective agent uses a metal phosphate.
상기 금속인산염은 인산아연(zinc phosphate)을 사용하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. 6. The method of claim 5,
The metal phosphate is a method of manufacturing a sofa having an antibacterial function, characterized in that using zinc phosphate.
상기 금속 인산염은 입자 크기가 0.5 내지 10 μm인 것을 사용하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법. 6. The method of claim 5,
The metal phosphate is a method of manufacturing a sofa with an antibacterial function, characterized in that using a particle size of 0.5 to 10 μm.
상기 고분자 결합제는 알키드 폴리우레탄(alkyd polyurethane), 폴리비닐 부티랄(polyvinyl butyral) 중에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는 항균 기능을 구비한 소파의 제조방법.The method of claim 1,
The polymer binder is an alkyd polyurethane (alkyd polyurethane), polyvinyl butyral (polyvinyl butyral) manufacturing method of a sofa having an antibacterial function, characterized in that it comprises at least one selected from the group consisting of.
A sofa with an antibacterial function, characterized in that manufactured according to any one of claims 1 to 8.