KR102390538B1 - Multi-purpose insulation paint composition - Google Patents
Multi-purpose insulation paint composition Download PDFInfo
- Publication number
- KR102390538B1 KR102390538B1 KR1020210183038A KR20210183038A KR102390538B1 KR 102390538 B1 KR102390538 B1 KR 102390538B1 KR 1020210183038 A KR1020210183038 A KR 1020210183038A KR 20210183038 A KR20210183038 A KR 20210183038A KR 102390538 B1 KR102390538 B1 KR 102390538B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- water
- agent
- airgel powder
- dispersant
- Prior art date
Abstract
Description
본 발명은 다용도 단열 도료 조성물에 관한 것으로서, 더욱 상세하게는 에어로젤 파우더를 이용하여 조성물을 조성하되 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 하는 한편, 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 함과 동시에 에어로젤 파우더에 부가적으로 방수제를 첨가함으로써 도포대상에 도포한 후 건조된 도막으로서 방수기능과 발수기능을 갖도록 함과 동시에 오랜 기간에 걸쳐 단열효율이 높은 상태로 유지하면서 단열효능의 지속성을 장기화할 수 있도록 한 다용도 단열 도료 조성물에 관한 것이다.The present invention relates to a multi-purpose heat insulating paint composition, and more particularly, the composition is composed using airgel powder, but the hollow (airgel) function is not destroyed when the airgel powder is mixed with an aqueous binder. Mixing for the composition of the composition On the other hand, when mixing the airgel powder with an aqueous binder, the hollow (airgel) function is not destroyed and mixing for the composition of the composition can be made smoothly, and at the same time, a waterproofing agent is additionally added to the airgel powder. It relates to a multipurpose insulating coating composition that has a waterproof function and a water repellent function as a dried coating film after application to an application target by adding it, and at the same time maintains high thermal insulation efficiency over a long period of time and allows the continuity of thermal insulation effect to be prolonged will be.
일반적으로 주택, 아파트, 학교, 공장, 사무실 및 각종 시설물은 대부분 콘크리트와 철(금속)로 되어 있어 뜨거운 여름철에는 태양열과 지열, 복사열 등을 흡수하는 열섬(heat island) 현상으로 인하여 건물과 시설물의 내부온도가 상승하게 된다.In general, houses, apartments, schools, factories, offices, and various facilities are mostly made of concrete and iron (metal). the temperature will rise
이때, 열섬 현상이란 도심의 온도가 대기오염이나 인공열 등의 영향으로 주변지역보다 온도가 높게 나타나는 현상이다.In this case, the heat island phenomenon is a phenomenon in which the temperature of the city center is higher than that of the surrounding area due to the influence of air pollution or artificial heat.
이러한 열섬 현상은 주로 공장의 굴뚝에서 뿜어져 나오는 연기, 자동차 배기가스, 에어컨, 난방기 등의 배출열 등 각종 인공열과 그로 인한 대기오염에서 비롯된다.The heat island phenomenon is mainly caused by various types of artificial heat such as smoke from factory chimneys, exhaust gas from automobiles, air conditioners and heaters, and air pollution caused by them.
이 외에도 아스팔트 및 콘크리트와 같은 인공시설물들이 빛을 흡수하는 효율이 높고 이를 적외선 방사 형태로 다시 외부로 방출하거나 녹지 면적이 점차 감소하여 열섬 현상이 나타나게 된다.In addition, artificial facilities such as asphalt and concrete have high efficiency in absorbing light and emit it back to the outside in the form of infrared radiation, or the green area gradually decreases, resulting in a heat island phenomenon.
따라서, 상기와 같은 열섬현상을 조절하기 위해 냉방기를 가동하여 실내온도를 낮추며, 추운 겨울철에는 반대로 난방기를 가동하여 난방을 하고 있다.Therefore, in order to control the heat island phenomenon as described above, the air conditioner is operated to lower the indoor temperature, and in the cold winter, the heater is operated to heat the room.
이로 인하여 전력비 또는 냉난방 유지비용이 상당 발생하게 되어 이 모든 과정에서 배출되는 이산화탄소 함량이 대기 중에 높아짐으로써 지구온난화 및 이상 기후에까지 영향을 끼쳐오고 있는 실정이다.As a result, electricity costs or heating and cooling maintenance costs are significantly increased, and the carbon dioxide content emitted in all these processes is increased in the atmosphere, which is affecting global warming and abnormal climate.
이에, 선진국에서는 에너지 절감과 지구환경을 보존하기 위하여 에너지 절감 도료에 대하여 에너지 스타 마크 (Energy Star mark) 인증제도를 활용하고 있다.Accordingly, developed countries are using the Energy Star mark certification system for energy-saving paints in order to save energy and preserve the global environment.
냉난방에 따른 비용증가를 억제하고 환경문제를 타개하기 위하여 최근 건축물들은 강제적인 냉난방 시설유지와 최적의 주거환경을 구현하기 위하여 스티로폼, 우레탄 폼 등 여러 가지 종류의 단열재 사용과 주택의 창을 이중창을 설치하고 있다.In order to suppress the cost increase due to heating and cooling and to overcome environmental problems, recent buildings use various types of insulation materials such as styrofoam and urethane foam to maintain compulsory heating and cooling facilities and realize an optimal residential environment, and install double-glazed windows in houses. are doing
그러나 공정상의 번거로움과 단열재가 차지하는 부피와 막대한 비용을 동반하고 있으므로 비효율적이고 경제적인 방법은 아니다.However, it is not an inefficient and economical method because it is accompanied by the inconvenience of the process, the volume occupied by the insulator, and the enormous cost.
더욱이, 기존 단열재만으로는 열 차단 효과가 확실치 못하여 냉난방시 에너지 활용효율을 높이려면 단열재의 두께가 더욱 두꺼워지고 무게가 증가하는 문제점이 있었다.In addition, there is a problem in that the thickness of the insulation material is thicker and the weight is increased in order to increase the energy utilization efficiency during heating and cooling because the heat blocking effect is not certain with the existing insulation material alone.
이에, 비교적 낮은 두께 및 가벼운 무게로 도장재료를 사용하여 열의 축척 및 흡수를 최소화하려는 시도가 있으나 건축물의 외장 도장재로 주로 사용되어 온 우레탄 방수 도료는 시공상의 까다로움과 도막의 들뜸 현상과 외부 열에 대한 차단효과가 낮고, 종래의 단열 도료인 일명, 쿨-루프 (Cool-roof) 페인트는 실내온도를 낮추는 효과는 있으나 기대에 못 미치고, 도료 내 과량의 백색안료인 TiO2 및 유사계열의 광물질 등의 함유로 크랙(crack) 발생, 접착력 저하 등으로 건축물의 수명연장과 에너지절감 측면에서 개선이 필요하다.Therefore, attempts have been made to minimize the accumulation and absorption of heat by using a coating material with a relatively low thickness and light weight, but the urethane waterproofing paint, which has been mainly used as an exterior coating material for buildings, is difficult in construction, The blocking effect is low, and the conventional insulation paint, so-called Cool - roof paint, has an effect of lowering the indoor temperature, but does not meet expectations, Improvements are needed in terms of extending the lifespan of buildings and reducing energy due to cracks and reduced adhesive strength.
더욱이, 종래의 단열 도료로서의 수성도료는 내수성이 좋지를 못하고 통기성이 있어서 오랜 기간이 경과할 경우 단열효율이 떨어지는 현상이 있다.Moreover, the conventional water-based paint as an insulating paint has poor water resistance and breathability.
또한, 종래의 단열 도료에 중공의 에어로젤 파우더를 적용시 에어로젤 파우더의 소수성과 친유성 기능에 의해 수성 바인더가 잘 혼합되지 않으며, 이에 따라 알콜류와 유기용제와 유성 바인더를 혼합 사용하여 단열 소재를 만들었다.In addition, when the hollow airgel powder is applied to the conventional insulating paint, the aqueous binder is not mixed well due to the hydrophobic and lipophilic functions of the airgel powder.
그러나 상기와 같은 경우, 중공의 에어로젤 파우더가 유기계 바인더와 용제로 인하여 중공(에어로젤) 기능이 파괴되면서 중공 기능을 하지 못하여 단열 성능을 떨어뜨리는 현상이 발생하는 문제가 있었다.However, in the above case, there was a problem that the hollow airgel powder did not perform the hollow function as the hollow (airgel) function was destroyed due to the organic binder and the solvent, thereby lowering the thermal insulation performance.
그러므로 도포대상에 도포한 후 건조된 도막으로서 방수기능과 발수기능을 갖도록 함과 동시에 오랜 기간에 걸쳐 단열효율이 높은 상태로 유지하면서 단열효능의 지속성을 장기화할 수 있으며, 아울러 중공의 에어로젤 파우더를 적용하되 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 한 단열 도료 조성물에 대해 연구 및 개발이 요구되는 실정이다.Therefore, as a dried coating film after application to the application target, it has waterproof and water repellent functions, and at the same time, it is possible to prolong the continuity of the insulation effect while maintaining high insulation efficiency over a long period of time. However, there is a need for research and development on an insulating paint composition that allows smooth mixing for the composition of the composition without destroying the hollow (airgel) function.
상기와 같은 문제점을 해결하기 위하여, 본 발명은 에어로젤 파우더를 이용하여 조성물을 조성하되 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 한 다용도 단열 도료 조성물을 제공하는 것을 목적으로 한다.In order to solve the above problems, the present invention uses airgel powder to compose a composition, but when mixing the airgel powder with an aqueous binder, the hollow (airgel) function is not destroyed and the composition of the composition is mixed smoothly. An object of the present invention is to provide a multi-purpose insulating coating composition that allows
본 발명에 따른 기술의 다른 목적은 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 함과 동시에 에어로젤 파우더에 부가적으로 방수제를 첨가함으로써 도포대상에 도포한 후 건조된 도막으로서 방수기능과 발수기능을 갖도록 함과 동시에 오랜 기간에 걸쳐 단열효율이 높은 상태로 유지하면서 단열효능의 지속성을 장기화할 수 있도록 함에 있다.Another object of the technology according to the present invention is to enable smooth mixing for the composition of the composition without destroying the hollow (airgel) function when mixing the airgel powder with an aqueous binder, and at the same time add a waterproofing agent to the airgel powder The purpose of this is to ensure that it has a waterproof and water-repellent function as a dried coating film after application to the application target by adding , and at the same time maintains a high thermal insulation efficiency over a long period of time, while prolonging the continuity of the thermal insulation effect.
본 발명에 따른 기술의 또 다른 목적은 중공 파우더 입자인 에어로젤 파우더를 포함하는 도료 조성물로서, 종래에 철, 티타늄, 알루미늄, 아연 등의 금속 또는 비철금속이 적용되던 단열 도료에 비하여, 낮은 열전도도를 가질 수 있으며, 이를 통하여 단열효율을 현격히 증대시킬 수 있도록 함에 있다.Another object of the technology according to the present invention is a coating composition comprising airgel powder, which is a hollow powder particle, and has lower thermal conductivity compared to heat insulating coatings to which metals such as iron, titanium, aluminum, zinc, or non-ferrous metals are conventionally applied. It is possible to significantly increase the thermal insulation efficiency through this.
전술한 목적을 달성하기 위한 본 발명은 다음과 같다. 즉, 본 발명에 따른 다용도 단열 도료 조성물은 에어로젤 파우더를 포함하는 다용도 단열 도료 조성물로서, Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함한다.The present invention for achieving the above object is as follows. That is, the multipurpose heat insulating coating composition according to the present invention is a multipurpose heat insulating coating composition comprising airgel powder, and includes Di water, a dispersant, an antifoaming agent, a thixotropic agent, a colorant, an airgel powder, a film forming agent, a waterproofing agent, a thickener, and an aqueous binder. .
이때, 상기 다용도 단열 도료 조성물은 탄산칼슘, 탈크를 더 포함하고, 상기 수성 바인더는 수성 아크릴(고형분 함량 50%)로 제공되는 한편, Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 탈크, 수성 아크릴(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 15중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 20중량%, 탈크 5중량%, 수성 아크릴(고형분 함량 50%) 40중량%로 혼합 조성되는 것이 바람직하다.At this time, the multi-purpose insulating paint composition further includes calcium carbonate and talc, and the aqueous binder is provided as aqueous acrylic (solid content 50%), while Di water, dispersant, defoaming agent, thixotropic agent, colorant, airgel powder, film forming The composition of the agent, waterproofing agent, thickener, calcium carbonate, talc, aqueous acrylic (solid content 50%) is 12% by weight of di water, 0.6% by weight of dispersant, 0.1% by weight of defoaming agent, 0.3% by weight of thixotropic agent, 2% by weight of colorant, Airgel powder 15% by weight, film forming agent 1% by weight, waterproofing agent 3% by weight, thickener 1% by weight, calcium carbonate 20% by weight, talc 5% by weight, water-based acrylic (solid content 50%) 40% by weight desirable.
또한, 상기 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편, 상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되는 것이 양호하다.In addition, in the multi-purpose insulating paint composition, the dispersant is provided as a surfactant and aqueous ammonia, while the multi-purpose insulating paint composition is a surfactant provided as a dispersant in Di water to be well dispersed in Di water with respect to the airgel powder and ammonia water to have a pH of 9 or higher, add airgel powder and mix for 8 to 10 minutes at a rotation speed of 800 RPM or less, then water-based acrylic (solid content: 50%) It is preferable that the hollow (airgel) function is not destroyed by mixing and stirring over a period of time at a rotation speed of 1000 RPM or less by adding the remaining components including
더욱이, 상기 탄산칼슘은 20중량%로 제공되되, 350메쉬의 탄산칼슘 10중량% 및 200메쉬의 탄산칼슘 10중량%로 제공되는 한편, 상기 에어로젤 파우더는 입도 80㎛인 에어로젤 파우더로 제공되는 것이 바람직하다.Moreover, the calcium carbonate is provided in 20% by weight, while it is provided as 10% by weight of calcium carbonate of 350 mesh and 10% by weight of calcium carbonate of 200 mesh, the airgel powder is preferably provided as an airgel powder having a particle size of 80㎛ Do.
아울러, 상기 착색제는 지당으로 제공되고, 상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며, 상기 점증제는 셀룰로오즈로 제공되는 것이 양호하다.In addition, it is preferable that the colorant is provided as lipid sugar, the film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate, and the thickener is provided as cellulose.
본 발명에 따른 다용도 단열 도료 조성물의 효과를 설명하면 다음과 같다.The effect of the multipurpose heat insulating coating composition according to the present invention will be described as follows.
첫째, 에어로젤 파우더를 이용하여 조성물을 조성하되 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있다.First, the composition is composed using the airgel powder, but when the airgel powder is mixed with an aqueous binder, the hollow (airgel) function is not destroyed, and mixing for the composition of the composition can be made smoothly.
둘째, 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 함과 동시에 에어로젤 파우더에 부가적으로 방수제를 첨가함으로써 도포대상에 도포한 후 건조된 도막으로서 방수기능과 발수기능을 갖도록 함과 동시에 오랜 기간에 걸쳐 단열효율이 높은 상태로 유지하면서 단열효능의 지속성을 장기화할 수 있다.Second, when mixing with an aqueous binder for airgel powder, the hollow (airgel) function is not destroyed and mixing for the composition of the composition can be made smoothly, and at the same time, it is applied to the application target by adding a waterproofing agent to the airgel powder. As a dried coating film, it has waterproof and water repellent functions, and at the same time, it is possible to prolong the continuity of the insulation effect while maintaining high insulation efficiency over a long period of time.
셋째, 중공 파우더 입자인 에어로젤 파우더를 포함하는 도료 조성물로서, 종래에 철, 티타늄, 알루미늄, 아연 등의 금속 또는 비철금속이 적용되던 단열 도료에 비하여, 낮은 열전도도(thermal conductivity)를 가질 수 있으며, 이를 통하여 단열효율을 현격히 증대시킬 수 있다.Third, as a coating composition comprising airgel powder, which is a hollow powder particle, it may have lower thermal conductivity than conventional heat-insulating paints to which metals such as iron, titanium, aluminum, zinc, or non-ferrous metals have been applied, and this Through this, the thermal insulation efficiency can be significantly increased.
이하, 본 발명에 따른 다용도 단열 도료 조성물의 바람직한 실시예를 상세히 설명한다.Hereinafter, a preferred embodiment of the multipurpose heat insulating coating composition according to the present invention will be described in detail.
본 발명의 바람직한 실시예에 따른 다용도 단열 도료 조성물은 에어로젤 파우더를 포함하며 건축물의 지붕이나 옥상 또는 실내의 보일러, 고무호스 등에 다용도로서 도포시켜 단열시킬 수 있도록 하는 다용도 단열 도료 조성물로서, 이하 표 1을 참고하여 제1실시예 내지 제4실시예에 따른 다용도 단열 도료 조성물을 설명하기로 한다.The multipurpose heat insulating paint composition according to a preferred embodiment of the present invention includes airgel powder and is applied to the roof of a building, roof or indoor boiler, rubber hose, etc. for multiple purposes to insulate it. As shown in Table 1 below With reference, the multi-purpose heat insulating coating composition according to Examples 1 to 4 will be described.
사용량
(중량%)first embodiment
usage
(weight%)
사용량
(중량%)second embodiment
usage
(weight%)
사용량
(중량%)3rd embodiment
usage
(weight%)
사용량
(중량%)4th embodiment
usage
(weight%)
(계면활성제+암모니아수)dispersant
(Surfactant + ammonia water)
(지당)coloring agent
(Gardang)
(2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate)
(Texanol)filmmaker
(2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate)
(Texanol)
(셀룰로오즈)thickener
(Cellulose)
상기 표 1을 참고하면, 본 발명의 제1실시예에 따른 다용도 단열 도료 조성물은 Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함한다.Referring to Table 1, the multipurpose heat insulating coating composition according to the first embodiment of the present invention includes Di water, a dispersant, an antifoaming agent, a thixotropic agent, a colorant, an airgel powder, a film forming agent, a waterproofing agent, a thickener, and an aqueous binder.
이러한 본 발명의 제1실시예에 따른 다용도 단열 도료 조성물은 특히, 탄산칼슘, 탈크를 더 포함하고, 상기 수성 바인더는 수성 아크릴(고형분 함량 50%)로 제공된다.The multi-purpose insulating coating composition according to the first embodiment of the present invention, in particular, further includes calcium carbonate and talc, and the aqueous binder is provided as aqueous acrylic (solid content of 50%).
또한, 상기와 같은 본 발명의 제1실시예에 따른 다용도 단열 도료 조성물에서, Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 탈크, 수성 아크릴(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 15중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 20중량%, 탈크 5중량%, 수성 아크릴(고형분 함량 50%) 40중량%로 혼합 조성된다.In addition, in the multipurpose heat insulating coating composition according to the first embodiment of the present invention as described above, Di water, dispersant, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, calcium carbonate, talc, aqueous acrylic The composition of (solid content 50%) is 12% by weight of Di water, 0.6% by weight of dispersant, 0.1% by weight of antifoaming agent, 0.3% by weight of thixotropic agent, 2% by weight of colorant, 15% by weight of airgel powder, 1% by weight of film forming agent, 3% by weight of waterproofing agent % by weight, thickener 1% by weight, calcium carbonate 20% by weight, talc 5% by weight, aqueous acrylic (solid content 50%) 40% by weight is mixed composition.
상기와 같은 본 발명의 제1실시예에 따른 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편, 상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되는 것이 바람직하다.In the multi-purpose heat-insulating paint composition according to the first embodiment of the present invention as described above, the dispersant is provided with a surfactant and aqueous ammonia, while the multi-purpose heat-insulating paint composition can be well dispersed in Di water with respect to the airgel powder, After adding the surfactant and ammonia water provided as a dispersing agent to Di water so that the pH is 9 or higher, add airgel powder and mix for 8-10 minutes at a rotation speed of 800 RPM or less, and then add Di water, dispersant, and airgel powder. It is preferable that the hollow (airgel) function is not destroyed by adding the remaining components including the aqueous acrylic (solid content of 50%) of the mixture and stirring for a certain period of time at a rotation speed of 1000 RPM or less.
다시 말하면, 상기와 같은 제조과정을 통해 제조됨으로써 본 발명의 제1실시예에서 단열 입자로서 적용되는 에어로젤 파우더에 대해 수성 바인더로 적용되는 수성 아크릴(고형분 함량 50%)과 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있게 되는 것이다.In other words, hollow (airgel) function when mixed with aqueous acrylic (50% solid content) applied as an aqueous binder for the airgel powder applied as heat insulating particles in the first embodiment of the present invention by being manufactured through the manufacturing process as described above It will be possible to smoothly mix for the composition of the composition without being destroyed.
더욱이, 본 발명의 제1실시예에 따른 다용도 단열 도료 조성물에서, 상기 탄산칼슘은 20중량%로 제공되되, 350메쉬의 탄산칼슘 10중량% 및 200메쉬의 탄산칼슘 10중량%로 제공되는 것이 바람직하다.Furthermore, in the multi-purpose heat insulating coating composition according to the first embodiment of the present invention, the calcium carbonate is provided in 20 wt%, preferably 350 mesh 10 wt% calcium carbonate and 200 mesh calcium carbonate 10 wt% Do.
그리고 상기 에어로젤 파우더는 입도 80㎛인 에어로젤 파우더로 제공되는 것이 바람직하고, 상기 착색제는 지당으로 제공됨이 바람직하다.And the airgel powder is preferably provided as an airgel powder having a particle size of 80㎛, and the colorant is preferably provided as a sugar.
또한, 상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되는 것이 바람직한 것이다.In addition, the film forming agent is preferably provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate.
더욱이, 상기와 같은 조막제는 텍사놀(이스트만사)을 사용하거나, 또는 유사제품인 C-12(중국산)와 Dounol DPnB, Butyl Carbitol을 같이 사용할 수도 있는 것이다.Moreover, the film forming agent as described above may use Texanol (Eastman), or C-12 (made in China), Dounol DPnB, and Butyl Carbitol, which are similar products, may be used together.
아울러, 상기 점증제는 셀룰로오즈로 제공되는 것이 바람직하다.In addition, the thickener is preferably provided as cellulose.
전술한 바와 같은 본 발명의 제1실시예에 따른 다용도 단열 도료 조성물은 바인더로서 수성 아크릴에 탄산칼슘을 사용하면서 방수제를 첨가하여 방수 단열재의 강도를 증가시켜 하드하게 만든 제품으로 모체의 변형이 없는 곳, 예컨대 금속재, 콘크리트 등의 하드한 재질의 표면에 도포시켜 사용시 적합한 것이다.As described above, the multi-purpose insulating paint composition according to the first embodiment of the present invention is a product made hard by adding a waterproofing agent while using calcium carbonate in aqueous acrylic as a binder to increase the strength of the waterproofing insulating material. , For example, it is suitable for use by coating it on the surface of a hard material such as metal or concrete.
한편, 상기 표 1을 참고하면, 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물은 Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함한다.On the other hand, referring to Table 1, the multipurpose heat insulating paint composition according to the second embodiment of the present invention includes Di water, a dispersant, an antifoaming agent, a thixotropic agent, a colorant, airgel powder, a film forming agent, a waterproofing agent, a thickener, and an aqueous binder. do.
상기와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물은 탄산칼슘을 더 포함하며, 상기 수성 바인더는 수성 아크릴(고형분 함량 50%)로 제공된다.The multi-purpose insulating coating composition according to the second embodiment of the present invention as described above further includes calcium carbonate, and the aqueous binder is provided as aqueous acrylic (solid content 50%).
또한, 상기와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물에서, Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 수성 아크릴(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 35중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 5중량%, 수성 아크릴(고형분 함량 50%) 40중량%로 혼합 조성된다.In addition, in the multi-purpose insulating coating composition according to the second embodiment of the present invention as described above, Di water, dispersant, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, calcium carbonate, aqueous acrylic (solid content) content 50%) of Di water 12% by weight, dispersant 0.6% by weight, defoaming agent 0.1% by weight, thixotropic agent 0.3% by weight, colorant 2% by weight, airgel powder 35% by weight, film forming agent 1% by weight, waterproofing agent 3% by weight , thickener 1% by weight, calcium carbonate 5% by weight, aqueous acryl (solid content 50%) 40% by weight is mixed composition.
그리고 상기와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편, 상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록 하는 것이 중요하다.And in the multi-purpose heat-insulating paint composition according to the second embodiment of the present invention as described above, the dispersant is provided with a surfactant and aqueous ammonia, while the multi-purpose heat-insulating paint composition can be well dispersed in Di water with respect to the airgel powder. it is important to do
이를 위하여, 다용도 단열 도료 조성물은 Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되는 것이 바람직하다.To this end, the multipurpose insulating paint composition is prepared by adding a surfactant and ammonia water provided as a dispersing agent to Di water to have a pH of 9 or higher, and then mixing the airgel powder for 8 to 10 minutes at a rotation speed of 800 RPM or less while adding it, Di water, dispersing agent, and other components including water-based acrylic (solid content 50%) other than airgel powder are added and mixed and stirred for a certain period of time at a rotation speed of 1000 RPM or less, so that the hollow (airgel) function is not destroyed. it is preferable
다시 말하면, 상기와 같은 제조과정을 통해 제조됨으로써 본 발명의 제2실시예에서 단열 입자로서 적용되는 에어로젤 파우더에 대해 수성 바인더로 적용되는 수성 아크릴(고형분 함량 50%)과 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있게 되는 것이다.In other words, hollow (airgel) function when mixed with aqueous acrylic (solid content 50%) applied as an aqueous binder for the airgel powder applied as heat insulating particles in the second embodiment of the present invention by being manufactured through the manufacturing process as described above It will be possible to smoothly mix for the composition of the composition without being destroyed.
또한, 상기와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물에서, 상기 착색제는 지당으로 제공되고, 상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며, 상기 점증제는 셀룰로오즈로 제공되는 것이 바람직한 것이다.In addition, in the multi-purpose insulating coating composition according to the second embodiment of the present invention as described above, the colorant is provided as lipid sugar, and the film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate, The thickener is preferably provided as cellulose.
그리고 상기와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물에서, 상기 탄산칼슘은 5중량%로 제공되되, 350메쉬의 탄산칼슘 5중량%로 제공되는 것이 바람직하다.And in the multi-purpose heat insulating coating composition according to the second embodiment of the present invention as described above, the calcium carbonate is provided in 5 wt%, it is preferable that the calcium carbonate is provided in 5 wt% of 350 mesh.
더욱이, 상기와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물에서의, 상기 에어로젤 파우더는 35중량%로 제공되되, 입도 80㎛인 에어로젤 파우더 12중량%와 입도 50㎛인 에어로젤 파우더 16중량%와 입도 25㎛인 에어로젤 파우더 7중량%로 제공되는 것이 바람직한 것이다.Furthermore, in the multi-purpose insulating coating composition according to the second embodiment of the present invention as described above, the airgel powder is provided in 35% by weight, 12% by weight of airgel powder having a particle size of 80㎛ and 16% by weight of airgel powder having a particle size of 50㎛ % and it is preferable to provide 7% by weight of airgel powder having a particle size of 25㎛.
전술한 바와 같은 본 발명의 제2실시예에 따른 다용도 단열 도료 조성물은 바인더로서 수성 아크릴에 제1실시예에 비하여 탄산칼슘을 소량(少量) 사용하고 과량(過量)의 에어로젤 파우더를 사용하면서 방수제를 첨가하여 방수 및 발수기능과 단열성을 증대시키고 지속킨 것이다.As described above, in the multipurpose heat insulating paint composition according to the second embodiment of the present invention, a small amount of calcium carbonate is used in aqueous acrylic as a binder, compared to the first embodiment, and an excessive amount of airgel powder is used and a waterproofing agent is applied. It is added to increase and maintain waterproof and water repellent functions and thermal insulation properties.
한편, 상기 표 1을 참고하면, 본 발명의 제3실시예에 따른 다용도 단열 도료 조성물은 Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함한다.On the other hand, referring to Table 1, the multipurpose heat insulating paint composition according to the third embodiment of the present invention contains Di water, a dispersant, an antifoaming agent, a thixotropic agent, a colorant, airgel powder, a film forming agent, a waterproofing agent, a thickener, and an aqueous binder. do.
상기 본 발명의 제3실시예에 따른 다용도 단열 도료 조성물에서의, 수성 바인더는 수성 폴리우레탄(고형분 함량 50%)으로 제공된다.In the multi-purpose insulating coating composition according to the third embodiment of the present invention, the aqueous binder is provided as aqueous polyurethane (solid content of 50%).
또한, 상기와 같은 본 발명의 제3실시예에 따른 다용도 단열 도료 조성물에서, Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 폴리우레탄(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 40중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 수성 폴리우레탄(고형분 함량 50%) 40중량%로 혼합 조성된다.In addition, in the multi-purpose insulating paint composition according to the third embodiment of the present invention as described above, Di water, dispersant, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, aqueous polyurethane (solid content 50 %) is Di water 12% by weight, dispersing agent 0.6% by weight, defoaming agent 0.1% by weight, thixotropic agent 0.3% by weight, colorant 2% by weight, airgel powder 40% by weight, film forming agent 1% by weight, waterproofing agent 3% by weight, thickening agent 1% by weight, water-based polyurethane (solid content 50%) 40% by weight is mixed composition.
본 발명의 제3실시예에 따른 다용도 단열 도료 조성물에서의, 분산제는 계면활성제와 암모니아수로 제공되는 한편, 상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 폴리우레탄(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되는 것이 바람직하다.In the multi-purpose heat-insulating paint composition according to the third embodiment of the present invention, the dispersant is provided with a surfactant and aqueous ammonia, while the multi-purpose heat-insulating paint composition is dissolved in Di water for the airgel powder to be well dispersed in Di water. After adding the surfactant and ammonia water provided as a dispersing agent to a pH of 9 or higher, mixing the airgel powder for 8 to 10 minutes at a rotation speed of 800 RPM or less, then adding water-based poly other than Di water, dispersing agent, and airgel powder It is preferable that the hollow (airgel) function is not destroyed by adding the remaining components including urethane (solid content 50%) and mixing and stirring for a certain time at a rotation speed of 1000 RPM or less.
다시 말하면, 상기와 같은 제조과정을 통해 제조됨으로써 본 발명의 제3실시예에서 단열 입자로서 적용되는 에어로젤 파우더에 대해 수성 바인더로 적용되는 수성 폴리우레탄(고형분 함량 50%)과 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있게 되는 것이다.In other words, hollow (airgel) when mixed with aqueous polyurethane (solid content 50%) applied as an aqueous binder for the airgel powder applied as heat insulating particles in the third embodiment of the present invention by being manufactured through the manufacturing process as described above. It is possible to smoothly mix for the composition of the composition without destroying the function.
또한, 상기 본 발명의 제3실시예에 따른 다용도 단열 도료 조성물에서의, 상기 착색제는 지당으로 제공되고, 상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며, 상기 점증제는 셀룰로오즈로 제공되는 것이 바람직한 것이다.In addition, in the multipurpose heat insulating coating composition according to the third embodiment of the present invention, the colorant is provided as lipid sugar, and the film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate, The thickener is preferably provided as cellulose.
더욱이, 본 발명의 제3실시예에 따른 다용도 단열 도료 조성물에서의, 상기 에어로젤 파우더는 40중량%로 제공되되, 입도 80㎛인 에어로젤 파우더 17중량%와 입도 50㎛인 에어로젤 파우더 16중량%와 입도 25㎛인 에어로젤 파우더 7중량%로 제공되는 것이 바람직하다.Furthermore, in the multipurpose heat insulating coating composition according to the third embodiment of the present invention, the airgel powder is provided in 40% by weight, 17% by weight of airgel powder having a particle size of 80㎛, and 16% by weight of airgel powder having a particle size of 50㎛ It is preferable to provide 7% by weight of the airgel powder of 25㎛.
전술한 바와 같은 본 발명의 제3실시예에 따른 다용도 단열 도료 조성물은 바인더로서 수분산 폴리우레탄을 사용하되, 탄산칼슘을 사용하지 않고 에어로젤 파우더와 방수제를 사용하여 방수기능과 유연성을 갖는 단열도료를 조성하였다.As described above, the multipurpose insulating paint composition according to the third embodiment of the present invention uses water-dispersed polyurethane as a binder, but uses airgel powder and a waterproofing agent without using calcium carbonate. was created.
이러한 방수기능과 유연성을 갖는 단열 도료는 다용도로 사용하되 특히, 고무호스 등의 신축성 재질의 표면에 도포하여 사용하는 것에 적합하며, 이와 같은 신축성 재질의 표면에 도포하여 사용시 유연성에 의해 도포 및 단열 효능이 더욱 안정적으로 구현될 수 있는 것이다.Insulation paints with such waterproof function and flexibility are used for multiple purposes, but are particularly suitable for application on the surface of elastic materials such as rubber hoses. This can be implemented more stably.
한편, 상기 표 1을 참고하면, 본 발명의 제4실시예에 따른 다용도 단열 도료 조성물은 Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함한다.Meanwhile, referring to Table 1, the multipurpose heat insulating paint composition according to the fourth embodiment of the present invention includes Di water, a dispersant, an antifoaming agent, a thixotropic agent, a colorant, airgel powder, a film forming agent, a waterproofing agent, a thickener, and an aqueous binder. do.
상기 제4실시예에 따른 다용도 단열 도료 조성물은 탄산칼슘, 탈크를 더 포함하고, 상기 수성 바인더는 수성 아크릴(고형분 함량 50%)과 수성 폴리우레탄(고형분 함량 50%)로 제공된다.The multi-purpose insulating coating composition according to the fourth embodiment further includes calcium carbonate and talc, and the aqueous binder is provided as aqueous acrylic (solid content 50%) and aqueous polyurethane (solid content 50%).
이러한 본 발명의 제4실시예에 따른 다용도 단열 도료 조성물에서, Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 탈크, 수성 아크릴(고형분 함량 50%), 수성 폴리우레탄(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 15중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 20중량%, 탈크 5중량%, 수성 아크릴(고형분 함량 50%) 20중량%, 수성 폴리우레탄(고형분 함량 50%) 20중량%로 혼합 조성된다.In the multi-purpose insulating paint composition according to the fourth embodiment of the present invention, Di water, dispersant, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, calcium carbonate, talc, aqueous acrylic (solid content 50 %), the composition of aqueous polyurethane (solid content 50%) is Di water 12% by weight, dispersant 0.6% by weight, defoamer 0.1% by weight, thixotropic agent 0.3% by weight, colorant 2% by weight, airgel powder 15% by weight, film forming agent 1% by weight, waterproofing agent 3% by weight, thickener 1% by weight, calcium carbonate 20% by weight, talc 5% by weight, water-based acrylic (50% solid content) 20% by weight, water-based polyurethane (solid content 50%) 20% by weight mixed composition with
상기와 같은 본 발명의 제4실시예에 따른 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편, 상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되는 것이 바람직하다.In the multi-purpose heat-insulating paint composition according to the fourth embodiment of the present invention as described above, the dispersant is provided with a surfactant and aqueous ammonia, while the multi-purpose heat-insulating paint composition can be well dispersed in Di water with respect to the airgel powder, After adding the surfactant and ammonia water provided as a dispersing agent to Di water so that the pH is 9 or higher, add airgel powder and mix for 8-10 minutes at a rotation speed of 800 RPM or less, and then add Di water, dispersant, and airgel powder It is preferable that the hollow (airgel) function is not destroyed by adding the remaining ingredients including the aqueous acrylic (solid content of 50%) of the mixture and stirring for a certain period of time at a rotation speed of 1000 RPM or less.
다시 말하면, 상기와 같은 제조과정을 통해 제조됨으로써 본 발명의 제4실시예에서 단열 입자로서 적용되는 에어로젤 파우더에 대해 수성 바인더로 적용되는 수성 아크릴(고형분 함량 50%)과 수성 폴리우레탄(고형분 함량 50%)의 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있게 되는 것이다.In other words, water-based acrylic (50% solid content) and water-based polyurethane (solid content 50%) applied as an aqueous binder to the airgel powder applied as heat-insulating particles in the fourth embodiment of the present invention by being manufactured through the manufacturing process as described above. %), the hollow (airgel) function is not destroyed when mixing, and mixing for the composition of the composition can be made smoothly.
또한, 상기와 같은 본 발명의 제4실시예에 따른 다용도 단열 도료 조성물에서, 상기 탄산칼슘은 20중량%로 제공되되, 350메쉬의 탄산칼슘 10중량% 및 200메쉬의 탄산칼슘 10중량%로 제공되는 것이 바람직하다.In addition, in the multi-purpose insulating coating composition according to the fourth embodiment of the present invention as described above, the calcium carbonate is provided in 20 wt%, 350 mesh of 10 wt% of calcium carbonate and 200 mesh of 10 wt% of calcium carbonate It is preferable to be
그리고 상기 에어로젤 파우더는 입도 80㎛인 에어로젤 파우더로 제공됨이 바람직한 것이다.And the airgel powder is preferably provided as an airgel powder having a particle size of 80㎛.
아울러, 상기 착색제는 지당으로 제공되고, 상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며, 상기 점증제는 셀룰로오즈로 제공되는 것이 바람직하다.In addition, it is preferable that the colorant is provided as lipid sugar, the film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate, and the thickener is provided as cellulose.
이때, 상기와 같은 조막제는 텍사놀(이스트만사)을 사용하거나, 또는 유사제품인 C-12(중국산)와 Dounol DPnB, Butyl Carbitol을 같이 사용할 수도 있는 것이다.In this case, as the film forming agent, Texanol (Eastman) may be used, or C-12 (made in China), Dounol DPnB, and Butyl Carbitol, which are similar products, may be used together.
전술한 바와 같은 본 발명의 제4실시예에 따른 다용도 단열 도료 조성물은 바인더로서 수분산 폴리우레탄과 수성 아크릴을 동일한 비율로 혼합하고, 탄산칼슘과 에어로젤 파우더를 비슷한 함량을 사용하면서 방수제를 첨가하여 방수기능을 가지면서 향상된 단열기능과 유연성이 일부 구현된 것이다.The multipurpose insulating paint composition according to the fourth embodiment of the present invention as described above is waterproof by mixing water-dispersed polyurethane and water-based acrylic in the same ratio as a binder, and adding a waterproofing agent while using similar amounts of calcium carbonate and airgel powder. Some of the improved insulation and flexibility are realized while having a function.
전술한 바와 같은 본 발명의 실시예들에 따른 다용도 단열 도료 조성물에 의하면, 에어로젤 파우더를 이용하여 조성물을 조성하되 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있다.According to the multi-purpose heat insulating coating composition according to the embodiments of the present invention as described above, the composition is composed using airgel powder, but the hollow (airgel) function of the composition is not destroyed when the airgel powder is mixed with an aqueous binder. Mixing for the composition may be smoothly performed.
또한, 에어로젤 파우더에 대해 수성의 바인더와 혼합시 중공(에어로젤) 기능이 파괴되지 않으면서 조성물의 조성을 위한 혼합이 원활하게 이루어질 수 있도록 함과 동시에 에어로젤 파우더에 부가적으로 방수제를 첨가함으로써 도포대상에 도포한 후 건조된 도막으로서 방수기능과 발수기능을 갖도록 함과 동시에 오랜 기간에 걸쳐 단열효율이 높은 상태로 유지하면서 단열효능의 지속성을 장기화할 수 있게 된다.In addition, when mixing the airgel powder with an aqueous binder, the hollow (airgel) function is not destroyed and mixing for the composition of the composition can be made smoothly, and at the same time, by adding a waterproofing agent to the airgel powder, it is applied to the application target As a dried coating film, it has waterproof and water repellent functions, and at the same time, it is possible to prolong the continuity of the insulation effect while maintaining high insulation efficiency over a long period of time.
더욱이, 중공 파우더 입자인 에어로젤 파우더를 포함하는 도료 조성물로서, 종래에 철, 티타늄, 알루미늄, 아연 등의 금속 또는 비철금속이 적용되던 단열 도료에 비하여, 낮은 열전도도(thermal conductivity)를 가질 수 있으며, 이를 통하여 단열효율을 현격히 증대시킬 수 있는 것이다.Moreover, as a coating composition comprising airgel powder, which is a hollow powder particle, it may have lower thermal conductivity than conventional heat-insulating paints to which metals such as iron, titanium, aluminum, zinc, or non-ferrous metals have been applied, and this Through this, the thermal insulation efficiency can be significantly increased.
이상에서 본 발명의 구체적인 실시예를 상세히 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 본 발명은 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변형의 실시가 가능하며, 이러한 변형은 본 발명의 범위에 포함된다.Although specific embodiments of the present invention have been described in detail above, the present invention is not limited thereto, and various modifications can be made by those skilled in the art to which the present invention pertains. are included within the scope of the present invention.
Claims (10)
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함하되,
상기 다용도 단열 도료 조성물은 탄산칼슘, 탈크를 더 포함하고,
상기 수성 바인더는 수성 아크릴(고형분 함량 50%)로 제공되는 한편,
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 탈크, 수성 아크릴(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 15중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 20중량%, 탈크 5중량%, 수성 아크릴(고형분 함량 50%) 40중량%로 혼합 조성되는 것을 특징으로 하는 다용도 단열 도료 조성물.
As a multi-purpose heat insulating coating composition comprising airgel powder,
Di water, dispersant, antifoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickening agent, water-based binder,
The multipurpose insulating coating composition further comprises calcium carbonate and talc,
The aqueous binder is provided as aqueous acrylic (solid content 50%), while
Di water, dispersing agent, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, calcium carbonate, talc, water-based acrylic (solid content 50%) consisted of 12% by weight of Di water, 0.6% by weight of dispersant, Antifoaming agent 0.1% by weight, thixotropic agent 0.3% by weight, colorant 2% by weight, airgel powder 15% by weight, film forming agent 1% by weight, waterproofing agent 3% by weight, thickener 1% by weight, calcium carbonate 20% by weight, talc 5% by weight, A multipurpose insulating coating composition, characterized in that the composition is mixed with 40% by weight of water-based acrylic (solid content 50%).
상기 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편,
상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되는 것을 특징으로 하는 다용도 단열 도료 조성물.
3. The method of claim 2,
In the multi-purpose insulating coating composition, the dispersant is provided with a surfactant and aqueous ammonia,
The multi-purpose insulating paint composition is added to the di water with a surfactant and ammonia water provided as a dispersant to have a pH of 9 or higher so that the airgel powder can be well dispersed in Di water, and then rotates at 800 RPM or less while adding the airgel powder After mixing at a speed of 8 to 10 minutes, the remaining ingredients including water-based acrylic (50% solid content) other than Di water, dispersant, and airgel powder are added and mixed and stirred over a period of time at a rotation speed of 1000 RPM or less A multi-purpose insulating coating composition, characterized in that it is manufactured so that the hollow (airgel) function is not destroyed.
상기 탄산칼슘은 20중량%로 제공되되, 350메쉬의 탄산칼슘 10중량% 및 200메쉬의 탄산칼슘 10중량%로 제공되는 한편,
상기 에어로젤 파우더는 입도 80㎛인 에어로젤 파우더로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
3. The method of claim 2,
The calcium carbonate is provided in 20% by weight, while it is provided as 10% by weight of calcium carbonate of 350 mesh and 10% by weight of calcium carbonate of 200 mesh,
The airgel powder is a multipurpose insulating coating composition, characterized in that provided as an airgel powder having a particle size of 80㎛.
상기 착색제는 지당으로 제공되고,
상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며,
상기 점증제는 셀룰로오즈로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
3. The method of claim 2,
The colorant is provided as a sugar,
The film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate,
The thickener is a multipurpose insulating coating composition, characterized in that provided in cellulose.
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함하되,
상기 다용도 단열 도료 조성물은 탄산칼슘을 더 포함하고,
상기 수성 바인더는 수성 아크릴(고형분 함량 50%)로 제공되는 한편,
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 수성 아크릴(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 35중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 5중량%, 수성 아크릴(고형분 함량 50%) 40중량%로 혼합 조성되고,
상기 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편,
상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되며,
상기 착색제는 지당으로 제공되고,
상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며,
상기 점증제는 셀룰로오즈로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
As a multi-purpose heat insulating coating composition comprising airgel powder,
Di water, dispersant, antifoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickening agent, water-based binder,
The multi-purpose insulating coating composition further comprises calcium carbonate,
The aqueous binder is provided as aqueous acrylic (solid content 50%), while
Di water, dispersing agent, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, calcium carbonate, water-based acrylic (solid content 50%) consists of 12% by weight of Di water, 0.6% by weight of dispersant, 0.1% of defoaming agent % by weight, thixotropic agent 0.3% by weight, colorant 2% by weight, airgel powder 35% by weight, film forming agent 1% by weight, waterproofing agent 3% by weight, thickener 1% by weight, calcium carbonate 5% by weight, aqueous acrylic (solid content 50%) ) 40% by weight mixed composition,
In the multi-purpose insulating coating composition, the dispersant is provided with a surfactant and aqueous ammonia,
The multi-purpose insulating paint composition is added to the di water with a surfactant and ammonia water provided as a dispersant to have a pH of 9 or higher so that the airgel powder can be well dispersed in Di water, and then rotates at 800 RPM or less while adding the airgel powder After mixing at a speed of 8 to 10 minutes, the remaining ingredients including water-based acrylic (50% solid content) other than Di water, dispersant, and airgel powder are added and mixed and stirred over a period of time at a rotation speed of 1000 RPM or less It is manufactured so that the hollow (airgel) function is not destroyed.
The colorant is provided as a sugar,
The film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate,
The thickener is a multipurpose insulating coating composition, characterized in that provided in cellulose.
상기 탄산칼슘은 5중량%로 제공되되, 350메쉬의 탄산칼슘 5중량%로 제공되는 한편,
상기 에어로젤 파우더는 35중량%로 제공되되, 입도 80㎛인 에어로젤 파우더 12중량%와 입도 50㎛인 에어로젤 파우더 16중량%와 입도 25㎛인 에어로젤 파우더 7중량%로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
7. The method of claim 6,
The calcium carbonate is provided in 5% by weight, while it is provided in 5% by weight of 350 mesh calcium carbonate,
The airgel powder is provided in 35% by weight, 12% by weight of airgel powder having a particle size of 80㎛, 16% by weight of airgel powder having a particle size of 50㎛, and 7% by weight of airgel powder having a particle size of 25㎛ Multipurpose insulating paint, characterized in that it is provided composition.
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함하되,
상기 다용도 단열 도료 조성물에서의, 수성 바인더는 수성 폴리우레탄(고형분 함량 50%)으로 제공되는 한편,
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 폴리우레탄(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 40중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 수성 폴리우레탄(고형분 함량 50%) 40중량%로 혼합 조성되고,
상기 다용도 단열 도료 조성물에서의, 분산제는 계면활성제와 암모니아수로 제공되는 한편,
상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 폴리우레탄(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되며,
상기 착색제는 지당으로 제공되고,
상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며,
상기 점증제는 셀룰로오즈로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
As a multi-purpose heat insulating coating composition comprising airgel powder,
Di water, dispersant, antifoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickening agent, water-based binder,
In the multi-purpose insulating coating composition, the aqueous binder is provided as an aqueous polyurethane (solid content 50%),
Di water, dispersing agent, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickening agent, water-based polyurethane (solid content 50%) consists of 12 wt% of Di water, 0.6 wt% of dispersant, 0.1 wt% of antifoaming agent , 0.3% by weight of thixotropic agent, 2% by weight of colorant, 40% by weight of airgel powder, 1% by weight of film forming agent, 3% by weight of waterproofing agent, 1% by weight of thickener, 40% by weight of water-based polyurethane (solid content 50%) become,
In the multi-purpose insulating coating composition, the dispersant is provided with a surfactant and aqueous ammonia,
The multi-purpose insulating paint composition is added to the di water with a surfactant and ammonia water provided as a dispersant to have a pH of 9 or higher so that the airgel powder can be well dispersed in Di water, and then rotates at 800 RPM or less while adding the airgel powder After mixing at a speed of 8 to 10 minutes, the remaining ingredients including water-based polyurethane (50% solid content) other than Di water, dispersant, and airgel powder are added and mixed over a period of time at a rotation speed of 1000 RPM or less. It is manufactured so that the hollow (airgel) function is not destroyed by stirring,
The colorant is provided as a sugar,
The film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate,
The thickener is a multipurpose insulating coating composition, characterized in that provided in cellulose.
상기 에어로젤 파우더는 40중량%로 제공되되, 입도 80㎛인 에어로젤 파우더 17중량%와 입도 50㎛인 에어로젤 파우더 16중량%와 입도 25㎛인 에어로젤 파우더 7중량%로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
9. The method of claim 8,
The airgel powder is provided in 40% by weight, 17% by weight of airgel powder having a particle size of 80㎛, 16% by weight of airgel powder having a particle size of 50㎛, and 7% by weight of airgel powder having a particle size of 25㎛ Multipurpose insulating paint, characterized in that it is provided composition.
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 수성 바인더를 포함하되,
상기 다용도 단열 도료 조성물은 탄산칼슘, 탈크를 더 포함하고,
상기 수성 바인더는 수성 아크릴(고형분 함량 50%)과 수성 폴리우레탄(고형분 함량 50%)로 제공되는 한편,
Di water, 분산제, 소포제, 요변제, 착색제, 에어로젤 파우더, 조막제, 방수제, 점증제, 탄산칼슘, 탈크, 수성 아크릴(고형분 함량 50%), 수성 폴리우레탄(고형분 함량 50%)의 조성은 Di water 12중량%, 분산제 0.6중량%, 소포제 0.1중량%, 요변제 0.3중량%, 착색제 2중량%, 에어로젤 파우더 15중량%, 조막제 1중량%, 방수제 3중량%, 점증제 1중량%, 탄산칼슘 20중량%, 탈크 5중량%, 수성 아크릴(고형분 함량 50%) 20중량%, 수성 폴리우레탄(고형분 함량 50%) 20중량%로 혼합 조성되고,
상기 다용도 단열 도료 조성물에서, 상기 분산제는 계면활성제와 암모니아수로 제공되는 한편,
상기 다용도 단열 도료 조성물은 상기 에어로젤 파우더에 대해 Di water에 잘 분산될 수 있도록, Di water에 분산제로 제공되는 계면활성제와 암모니아수를 pH 9 이상이 되게 첨가하고 나서 에어로젤 파우더를 투입하면서 800 RPM 이하의 회전속도로 8~10분에 걸쳐 혼합한 후, Di water, 분산제, 에어로젤 파우더 이외의 수성 아크릴(고형분 함량 50%)을 포함하는 나머지 성분들을 첨가하여 1000 RPM 이하의 회전속도로 일정시간에 걸쳐 혼합 교반하여 중공(에어로젤) 기능이 파괴되지 않도록 제조되며,
상기 탄산칼슘은 20중량%로 제공되되, 350메쉬의 탄산칼슘 10중량% 및 200메쉬의 탄산칼슘 10중량%로 제공되는 한편,
상기 에어로젤 파우더는 입도 80㎛인 에어로젤 파우더로 제공되고,
상기 착색제는 지당으로 제공되며,
상기 조막제는 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate로 제공되며,
상기 점증제는 셀룰로오즈로 제공되는 것을 특징으로 하는 다용도 단열 도료 조성물.
As a multi-purpose heat insulating coating composition comprising airgel powder,
Di water, dispersant, antifoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickening agent, water-based binder,
The multipurpose insulating coating composition further comprises calcium carbonate and talc,
The aqueous binder is provided in aqueous acrylic (solids content 50%) and aqueous polyurethane (solids content 50%), while
Di water, dispersing agent, defoaming agent, thixotropic agent, colorant, airgel powder, film forming agent, waterproofing agent, thickener, calcium carbonate, talc, water-based acrylic (50% solid content), water-based polyurethane (solid content 50%) 12% by weight of water, 0.6% by weight of dispersant, 0.1% by weight of antifoaming agent, 0.3% by weight of thixotropic agent, 2% by weight of colorant, 15% by weight of airgel powder, 1% by weight of film forming agent, 3% by weight of waterproofing agent, 1% by weight of thickener, carbonic acid 20% by weight of calcium, 5% by weight of talc, 20% by weight of water-based acrylic (solid content 50%), 20% by weight of water-based polyurethane (50% solid content),
In the multi-purpose insulating coating composition, the dispersant is provided with a surfactant and aqueous ammonia,
The multi-purpose insulating paint composition is added to the di water with a surfactant and ammonia water provided as a dispersant to have a pH of 9 or higher so that the airgel powder can be well dispersed in Di water, and then rotates at 800 RPM or less while adding the airgel powder After mixing at a speed of 8 to 10 minutes, the remaining ingredients including water-based acrylic (50% solid content) other than Di water, dispersant, and airgel powder are added and mixed and stirred over a period of time at a rotation speed of 1000 RPM or less It is manufactured so that the hollow (airgel) function is not destroyed.
The calcium carbonate is provided in 20% by weight, while being provided as 10% by weight of calcium carbonate of 350 mesh and 10% by weight of calcium carbonate of 200 mesh,
The airgel powder is provided as an airgel powder having a particle size of 80㎛,
The colorant is provided as a sugar,
The film forming agent is provided as 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate,
The thickener is a multipurpose insulating coating composition, characterized in that provided in cellulose.