KR102380235B1 - Multifunctional eco-friendly aqueous coating solution composition and coating layer application member applying the same - Google Patents

Multifunctional eco-friendly aqueous coating solution composition and coating layer application member applying the same Download PDF

Info

Publication number
KR102380235B1
KR102380235B1 KR1020210157053A KR20210157053A KR102380235B1 KR 102380235 B1 KR102380235 B1 KR 102380235B1 KR 1020210157053 A KR1020210157053 A KR 1020210157053A KR 20210157053 A KR20210157053 A KR 20210157053A KR 102380235 B1 KR102380235 B1 KR 102380235B1
Authority
KR
South Korea
Prior art keywords
parts
weight
content
acrylic emulsion
solution composition
Prior art date
Application number
KR1020210157053A
Other languages
Korean (ko)
Inventor
최영규
박혁기
박약수
이원종
Original Assignee
주식회사 바위
(주)코리아사이언스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 바위, (주)코리아사이언스 filed Critical 주식회사 바위
Priority to KR1020210157053A priority Critical patent/KR102380235B1/en
Application granted granted Critical
Publication of KR102380235B1 publication Critical patent/KR102380235B1/en

Abstract

A multifunctional eco-friendly aqueous coating liquid composition and a coating layer application member using the same are disclosed. The disclosed aqueous coating liquid composition is an aqueous coating liquid composition for coating an object to be coated and may include a first acrylic emulsion, a second acrylic emulsion, a third acrylic emulsion, an adhesive material, and additives. The first acrylic emulsion may include a mixture of water, ethyl acrylate, methyl methacrylate, methacrylic acid, and potassium persulfate (K_2S_2O_8). The second acrylic emulsion may include a mixture of water, ethyl acrylate, acrylic acid, octadecane sulfonic acid sodium salt, and hydrogen peroxide (H_2O_2). The third acrylic emulsion may include a mixture of water, styrene, butadiene, sodium oleate, potassium persulfate (K_2S_2O_8), sodium phosphate, and dodecyl mercaptan. Accordingly, it is expected that the environmental pollution problem caused by the existing coating agent can be greatly reduced.

Description

다기능성 친환경 수성 코팅액 조성물 및 이를 적용한 코팅층 적용 부재{Multifunctional eco-friendly aqueous coating solution composition and coating layer application member applying the same}Multifunctional eco-friendly aqueous coating solution composition and coating layer application member applying the same}

본 발명은 코팅용 조성물 및 이를 적용한 부재에 관한 것으로, 보다 상세하게는 수성 코팅액 조성물 및 이를 적용하여 형성한 코팅층을 포함하는 부재에 관한 것이다. The present invention relates to a coating composition and a member to which it is applied, and more particularly, to a member including an aqueous coating solution composition and a coating layer formed by applying the same.

종이류(재생종이, 골판지류 포함)로 제조되는 많은 종류의 포장지, 싸개지, 용기 등의 단점은 수분이나 습기에 취약하여 종이가 쉽게 찢어지는 경향이 있고, 용도에 따라 기름(동ㆍ식물류)이나 식초, 커피, 알콜 등에 취약하여 종이가 쉽게 손상되거나 파손되어 내용물이 손상, 유실될 수 있다는 것이다. 이러한 문제점들을 보완하기 위해, 종이에 PE(polyethylene) 필름을 합지하거나 PE 라미네이팅(laminating)을 수행하여 사용하고 있다. The disadvantages of many types of wrapping paper, wrapping paper, and containers manufactured from paper (including recycled paper and corrugated paper) are that they are vulnerable to moisture or moisture, so the paper tends to tear easily, and depending on the use, oil (animals and plants) or It is vulnerable to vinegar, coffee, alcohol, etc., so the paper can be easily damaged or broken, and the contents can be damaged or lost. In order to compensate for these problems, a PE (polyethylene) film is laminated on paper or PE laminating is performed and used.

그런데, PE 필름이 합지되거나 PE 라미네이팅(laminating)이 된 것은 재활용이 되지 않으며 소각시 유해 가스가 방출되거나 매립시 자연 분해가 거의 되지 않아 환경오염의 원인이 되고 있다. 또한, 재활용을 위해 필름을 해리하기 위해서는 많은 비용과 시간이 소요되는 문제가 있다. However, the PE film laminated or PE laminating is not recycled, and harmful gas is emitted during incineration or natural decomposition is hardly performed during landfill, which causes environmental pollution. In addition, there is a problem in that it takes a lot of money and time to dissociate the film for recycling.

한편, 현재 시중에 소개되고 있는 코팅용 발수, 방수제들은 수분이나 습기 방지를 위해 제조된 제품들이 주류를 이루고 있으며, 이러한 제품들은 주로 우레탄(urethane) 등 수지에 왁스(paraffin wax, PE wax 등)와 실리콘(silicone) 화합물들을 혼합하여 제조된다. 그러나, 이러한 제품들은 포장하려는 내용물이 냉동제품일 경우, 저온상태에서 코팅 표면에 크랙(crack)이 발생하여 방수력이 급격히 떨어지는 문제가 있다. 또한, 코팅 도막의 두께를 일정 수준(약 15∼25 ㎛) 이상으로 형성하고 이 두께 수준을 유지시킬 필요가 있다. On the other hand, water repellent and waterproofing agents for coating currently introduced in the market are mainly products manufactured to prevent moisture or moisture. It is prepared by mixing silicone compounds. However, these products have a problem in that, when the contents to be packaged are frozen products, cracks occur on the coating surface in a low temperature state, so that waterproofing power is rapidly reduced. In addition, it is necessary to form the thickness of the coating film to a certain level (about 15 to 25 μm) or more and to maintain this level of thickness.

최근, 환경 보호에 대한 관심이 높아지고 환경 관련 규제들도 늘어나면서 종이류 박스나 포장재(포장지) 관련 분야 등에서 수분(물) 뿐만 아니라 다양한 액상 물질(ex, 기름, 식초, 커피, 알콜 등) 및 오염물질을 견딜 수 있으면서 재활용이 용이하고 친환경적이며 우수한 기능성을 갖는 코팅제의 개발 필요성이 증가하고 있다. Recently, as interest in environmental protection increases and environmental regulations increase, not only moisture (water) but also various liquid substances (ex, oil, vinegar, coffee, alcohol, etc.) and pollutants in paper boxes and packaging materials (packaging paper)-related fields The need for the development of a coating agent that can withstand high temperatures, is easy to recycle, is eco-friendly, and has excellent functionality is increasing.

본 발명이 이루고자 하는 기술적 과제는 피코팅 부재에 적용했을 때 발수성, 방수성, 내오일성, 내산성, 내알콜성이 우수하고 재활용이 용이하며 독성이 없는 다기능성(다목적성) 친환경 수성 코팅액 조성물을 제공하는데 있다. The technical problem to be achieved by the present invention is to provide a multifunctional (multipurpose) eco-friendly aqueous coating solution composition that has excellent water repellency, waterproofness, oil resistance, acid resistance and alcohol resistance, is easy to recycle, and is non-toxic when applied to a member to be coated. there is.

또한, 본 발명이 이루고자 하는 기술적 과제는 상기한 다기능성 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층을 포함하는 코팅층 적용 부재를 제공하는데 있다. In addition, the technical problem to be achieved by the present invention is to provide a coating layer application member including a coating layer formed by applying the above-described multifunctional eco-friendly aqueous coating solution composition.

본 발명이 해결하고자 하는 과제는 이상에서 언급한 과제에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다. The problems to be solved by the present invention are not limited to the problems mentioned above, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.

상기한 과제를 달성하기 위한 본 발명의 실시예들에 따르면, 피코팅물에 코팅하기 위한 수성 코팅액 조성물로서, 물, 에틸 아크릴레이트(ethyl acrylate), 메틸 메타크릴레이트(methyl methacrylate), 메타크릴산(methacrylic acid) 및 과황산칼륨(K2S2O8)의 혼합액을 구비하는 제1 아크릴 에멀젼(acrylic emulsion); 물, 에틸 아크릴레이트(ethyl acrylate), 아크릴산(acrylic acid), 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt) 및 과산화수소(H2O2)의 혼합액을 구비하는 제2 아크릴 에멀젼; 물, 스타이렌(styrene), 부타디엔(butadiene), 올레인산나트륨(sodium oleate), 과황산칼륨(K2S2O8), 인산나트륨(sodium phosphate) 및 도데실메르캅탄(dodecyl mercaptan)의 혼합액을 구비하는 제3 아크릴 에멀젼; 접착성 물질; 및 첨가제;를 포함하는 수성 코팅액 조성물이 제공된다. According to embodiments of the present invention for achieving the above object, as an aqueous coating solution composition for coating an object to be coated, water, ethyl acrylate, methyl methacrylate, methacrylic acid (methacrylic acid) and potassium persulfate (K 2 S 2 O 8 ) A first acrylic emulsion having a mixed solution (acrylic emulsion); a second acrylic emulsion comprising a mixture of water, ethyl acrylate, acrylic acid, octadecane sulfonic acid sodium salt, and hydrogen peroxide (H 2 O 2 ); A mixture of water, styrene, butadiene, sodium oleate, potassium persulfate (K 2 S 2 O 8 ), sodium phosphate, and dodecyl mercaptan A third acrylic emulsion provided; adhesive substances; and additives; is provided.

상기 제1 아크릴 에멀젼에서 물의 함량은 약 100∼120 중량부일 수 있고, 에틸 아크릴레이트(ethyl acrylate)의 함량은 약 50∼70 중량부일 수 있고, 메틸 메타크릴레이트(methyl methacrylate)의 함량은 약 20∼30 중량부일 수 있고, 메타크릴산(methacrylic acid)의 함량은 약 5∼10 중량부일 수 있고, 과황산칼륨(K2S2O8)의 함량은 약 1∼2 중량부일 수 있다. In the first acrylic emulsion, the content of water may be about 100 to 120 parts by weight, the content of ethyl acrylate may be about 50 to 70 parts by weight, and the content of methyl methacrylate is about 20 It may be ∼30 parts by weight, the content of methacrylic acid may be about 5 to 10 parts by weight, and the content of potassium persulfate (K 2 S 2 O 8 ) may be about 1 to 2 parts by weight.

상기 제2 아크릴 에멀젼에서 물의 함량은 약 150∼200 중량부일 수 있고, 에틸 아크릴레이트(ethyl acrylate)의 함량은 약 100∼120 중량부일 수 있고, 아크릴산(acrylic acid)의 함량은 약 80∼100 중량부일 수 있고, 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt)의 함량은 약 8∼10 중량부일 수 있고, 과산화수소(H2O2)의 함량은 약 5∼8 중량부일 수 있다. The content of water in the second acrylic emulsion may be about 150 to 200 parts by weight, the content of ethyl acrylate may be about 100 to 120 parts by weight, and the content of acrylic acid may be about 80 to 100 parts by weight. part, the content of octadecane sulfonic acid sodium salt may be about 8 to 10 parts by weight, and the content of hydrogen peroxide (H 2 O 2 ) may be about 5 to 8 parts by weight.

상기 제3 아크릴 에멀젼에서 물의 함량은 약 80∼100 중량부일 수 있고, 스타이렌(styrene)의 함량은 약 70∼80부 중량부일 수 있고, 부타디엔(butadiene)의 함량은 약 10∼15 중량부일 수 있고, 올레인산나트륨(sodium oleate)의 함량은 약 1∼3 중량부일 수 있고, 과황산칼륨(K2S2O8)의 함량은 약 1∼2 중량부일 수 있고, 인산나트륨(sodium phosphate)의 함량은 약 0.1∼0.3 중량부일 수 있고, 도데실메르캅탄(dodecyl mercaptan)의 함량은 약 0.1∼0.3 중량부일 수 있다. The content of water in the third acrylic emulsion may be about 80 to 100 parts by weight, the content of styrene may be about 70 to 80 parts by weight, and the content of butadiene may be about 10 to 15 parts by weight. And, the content of sodium oleate (sodium oleate) may be about 1 to 3 parts by weight, the content of potassium persulfate (K 2 S 2 O 8 ) may be about 1 to 2 parts by weight, sodium phosphate (sodium phosphate) The content may be about 0.1 to 0.3 parts by weight, and the content of dodecyl mercaptan may be about 0.1 to 0.3 parts by weight.

상기 수성 코팅액 조성물에서 상기 제1 아크릴 에멀젼의 함량은 약 15∼20 중량부일 수 있고, 상기 제2 아크릴 에멀젼의 함량은 약 60∼70 중량부일 수 있고, 상기 제3 아크릴 에멀젼의 함량은 약 10∼15 중량부일 수 있다. In the aqueous coating solution composition, the content of the first acrylic emulsion may be about 15 to 20 parts by weight, the content of the second acrylic emulsion may be about 60 to 70 parts by weight, and the content of the third acrylic emulsion may be about 10 to about 10 parts by weight. 15 parts by weight.

상기 접착성 물질은 메틸 메타크릴레이트(methyl methacrylate)(MMA)를 포함할 수 있다. The adhesive material may include methyl methacrylate (MMA).

상기 첨가제는 탈포제(deformer agent) 및 소포제(antifoaming agent) 중 적어도 하나를 포함할 수 있다. The additive may include at least one of a defoaming agent and an antifoaming agent.

상기 소포제는 폴리디메틸실록산(polydimethylsiloxane)(PDMS)을 포함할 수 있다. The antifoaming agent may include polydimethylsiloxane (PDMS).

본 발명의 다른 실시예들에 따르면, 피코팅 부재; 및 상기 피코팅 부재의 표면에 전술한 수성 코팅액 조성물을 코팅하여 형성한 코팅층;을 포함하는 코팅층 적용 부재가 제공된다. According to other embodiments of the present invention, a member to be coated; and a coating layer formed by coating the above-described aqueous coating solution composition on the surface of the member to be coated.

상기 코팅층은 methacrylic acid copolymer, acrylic acid ester copolymer 및 styrene-butadiene copolymer를 포함할 수 있다. The coating layer may include a methacrylic acid copolymer, an acrylic acid ester copolymer, and a styrene-butadiene copolymer.

상기 피코팅 부재는 종이류, 목재류 또는 패브릭류 등일 수 있다. The member to be coated may be paper, wood, or fabric.

본 발명의 실시예들에 따르면, 피코팅 부재에 적용했을 때 발수성, 방수성, 내오일성, 내산성, 내알콜성이 우수하고 재활용이 용이하며 독성이 없는 다기능성(다목적성) 친환경 수성 코팅액 조성물을 구현할 수 있다. 또한, 본 발명의 실시예들에 따르면, 상기한 다기능성 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층을 포함하는 코팅층 적용 부재를 구현할 수 있다. According to the embodiments of the present invention, when applied to a member to be coated, a multifunctional (multi-purpose) eco-friendly aqueous coating solution composition with excellent water repellency, waterproofness, oil resistance, acid resistance and alcohol resistance, easy recycling, and non-toxic to be implemented. can In addition, according to the embodiments of the present invention, it is possible to implement a coating layer application member including a coating layer formed by applying the above-described multifunctional eco-friendly aqueous coating solution composition.

실시예들에 따른 다기능성 친환경 수성 코팅액 조성물은 우수한 기능성 및 친환경성을 가지므로, 기존의 코팅제(ex, PE 필름 등)를 대체할 수 있고 기존 코팅제에 의한 환경 오염 문제를 크게 줄일 수 있을 것으로 기대된다. Since the multifunctional eco-friendly aqueous coating solution composition according to the embodiments has excellent functionality and eco-friendliness, it is expected that it can replace the existing coating agent (ex, PE film, etc.) and greatly reduce the environmental pollution problem caused by the existing coating agent do.

도 1은 본 발명의 일 실시예에 따른 다기능성(다목적성) 친환경 수성 코팅액 조성물을 설명하기 위한 도면이다.
도 2는 본 발명의 일 실시예에 따른 다기능성(다목적성) 친환경 수성 코팅액 조성물을 제조하는 방법을 설명하기 위한 순서도이다.
도 3은 본 발명의 일 실시예에 따른 것으로, 다기능성(다목적성) 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층(200a)을 포함하는 코팅층 적용 부재를 보여주는 단면도이다.
도 4는 본 발명의 다른 실시예에 따른 것으로, 다기능성(다목적성) 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층(200a, 200b)을 포함하는 코팅층 적용 부재를 보여주는 단면도이다. 1 is a view for explaining a multi-functional (multi-purpose) eco-friendly aqueous coating solution composition according to an embodiment of the present invention.
2 is a flow chart for explaining a method for preparing a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to an embodiment of the present invention.
3 is a cross-sectional view showing a coating layer application member including a coating layer 200a formed by applying a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to an embodiment of the present invention.
4 is a cross-sectional view showing a coating layer application member including coating layers 200a and 200b formed by applying a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to another embodiment of the present invention.

이하, 첨부된 도면들을 참조하여 본 발명의 실시예들을 상세히 설명하기로 한다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

이하에서 설명할 본 발명의 실시예들은 당해 기술 분야에서 통상의 지식을 가진 자에게 본 발명을 더욱 명확하게 설명하기 위하여 제공되는 것이고, 본 발명의 범위가 하기 실시예에 의해 한정되는 것은 아니며, 하기 실시예는 여러 가지 다른 형태로 변형될 수 있다. Examples of the present invention to be described below are provided to more clearly explain the present invention to those of ordinary skill in the art, and the scope of the present invention is not limited by the following examples, The embodiment may be modified in many different forms.

본 명세서에서 사용된 용어는 특정 실시예를 설명하기 위하여 사용되며, 본 발명을 제한하기 위한 것이 아니다. 본 명세서에서 사용되는 단수 형태의 용어는 문맥상 다른 경우를 분명히 지적하는 것이 아니라면, 복수의 형태를 포함할 수 있다. 또한, 본 명세서에서 사용되는 "포함한다(comprise)" 및/또는 "포함하는(comprising)"이라는 용어는 언급한 형상, 단계, 숫자, 동작, 부재, 요소 및/또는 이들 그룹의 존재를 특정하는 것이며, 하나 이상의 다른 형상, 단계, 숫자, 동작, 부재, 요소 및/또는 이들 그룹의 존재 또는 부가를 배제하는 것이 아니다. 또한, 본 명세서에서 사용된 "연결"이라는 용어는 어떤 부재들이 직접적으로 연결된 것을 의미할 뿐만 아니라, 부재들 사이에 다른 부재가 더 개재되어 간접적으로 연결된 것까지 포함하는 개념이다. The terminology used herein is used to describe specific embodiments, not to limit the present invention. As used herein, terms in the singular form may include the plural form unless the context clearly dictates otherwise. Also, as used herein, the terms “comprise” and/or “comprising” refer to a referenced shape, step, number, action, member, element, and/or group that specifies the existence of these groups. and does not exclude the presence or addition of one or more other shapes, steps, numbers, acts, elements, elements, and/or groups thereof. In addition, as used herein, the term “connection” not only means that certain members are directly connected, but also includes indirectly connected members with other members interposed therebetween.

아울러, 본원 명세서에서 어떤 부재가 다른 부재 "상에" 위치하고 있다고 할 때, 이는 어떤 부재가 다른 부재에 접해 있는 경우뿐 아니라 두 부재 사이에 또 다른 부재가 존재하는 경우도 포함한다. 본 명세서에서 사용된 용어 "및/또는"은 해당 열거된 항목 중 어느 하나 및 하나 이상의 모든 조합을 포함한다. 또한, 본원 명세서에서 사용되는 "약", "실질적으로" 등의 정도의 용어는 고유한 제조 및 물질 허용 오차를 감안하여, 그 수치나 정도의 범주 또는 이에 근접한 의미로 사용되고, 본원의 이해를 돕기 위해 제공된 정확하거나 절대적인 수치가 언급된 개시 내용을 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다. In addition, in the present specification, when a member is said to be located "on" another member, this includes not only a case in which a member is in contact with another member but also a case in which another member is present between the two members. As used herein, the term “and/or” includes any one and any combination of one or more of those listed items. In addition, as used herein, terms such as "about", "substantially", etc. are used in the meaning of the range or close to the numerical value or degree, in consideration of inherent manufacturing and material tolerances, and to help the understanding of the present application The exact or absolute figures provided for this purpose are used to prevent the infringer from using the mentioned disclosure unfairly.

이하 첨부된 도면들을 참조하여 본 발명의 실시예들에 대해 상세히 설명한다. 첨부된 도면에 도시된 영역이나 파트들의 사이즈나 두께는 명세서의 명확성 및 설명의 편의성을 위해 다소 과장되어 있을 수 있다. 상세한 설명 전체에 걸쳐 동일한 참조번호는 동일한 구성요소를 나타낸다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. The size or thickness of the regions or parts shown in the accompanying drawings may be slightly exaggerated for clarity and convenience of description. Like reference numerals refer to like elements throughout the detailed description.

도 1은 본 발명의 일 실시예에 따른 다기능성(다목적성) 친환경 수성 코팅액 조성물을 설명하기 위한 도면이다. 1 is a view for explaining a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to an embodiment of the present invention.

도 1을 참조하면, 본 발명의 실시예에 따른 수성 코팅액 조성물은 소정의 피코팅물(피코팅 부재)의 표면에 코팅하여 코팅층을 형성하기 위한 조성물일 수 있다. 상기 수성 코팅액 조성물은 서로 다른 특성을 갖는 제1 아크릴 에멀젼(acrylic emulsion)(10), 제2 아크릴 에멀젼(20) 및 제3 아크릴 에멀젼(30)을 포함할 수 있다. 또한, 상기 수성 코팅액 조성물은 접착성 물질(접착용 물질)(40) 및 첨가제(50)를 더 포함할 수 있다. 제1 내지 제3 아크릴 에멀젼(10, 20, 30)과 접착성 물질(40) 및 첨가제(50)를 혼합하여 상기 수성 코팅액 조성물을 제조할 수 있다. 상기 수성 코팅액 조성물을 구성하기 위한 원료 물질들은 유해하지 않고 독성이 없는 물질로 선택될 수 있다. 또한, 상기 수성 코팅액 조성물은 코팅제로서 요구되는 다양한 물성/기능을 만족시킬 수 있으면서 아울러 생산의 용이성도 확보할 수 있는 제품일 수 있다. 이와 관련해서, 제1 내지 제3 아크릴 에멀젼(10, 20, 30)은 서로 다른 조성을 가질 수 있고, 서로 다른 특성/기능성을 구현할 수 있도록 구성될 수 있다. 이하에서는, 제1 내지 제3 아크릴 에멀젼(10, 20, 30) 각각에 대해서 구체적으로 설명한다. Referring to FIG. 1 , the aqueous coating solution composition according to an embodiment of the present invention may be a composition for forming a coating layer by coating on the surface of a predetermined object to be coated (member to be coated). The aqueous coating solution composition may include a first acrylic emulsion 10 , a second acrylic emulsion 20 , and a third acrylic emulsion 30 having different properties. In addition, the aqueous coating solution composition may further include an adhesive material (adhesive material) 40 and an additive (50). The aqueous coating solution composition may be prepared by mixing the first to third acrylic emulsions 10 , 20 , 30 , the adhesive material 40 and the additive 50 . Raw materials for constituting the aqueous coating solution composition may be selected as non-toxic and non-toxic materials. In addition, the aqueous coating solution composition may be a product that can satisfy various physical properties/functions required as a coating agent and also ensure ease of production. In this regard, the first to third acrylic emulsions 10, 20, and 30 may have different compositions and may be configured to implement different properties/functionalities. Hereinafter, each of the first to third acrylic emulsions 10, 20, and 30 will be described in detail.

제1 아크릴 에멀젼(10)은 물, 에틸 아크릴레이트(ethyl acrylate), 메틸 메타크릴레이트(methyl methacrylate), 메타크릴산(methacrylic acid) 및 과황산칼륨(K2S2O8)의 혼합액을 구비할 수 있다. 제1 아크릴 에멀젼(10)의 상기 혼합액에서, 또는, 제1 아크릴 에멀젼(10)에서 물의 함량은 약 100∼120 중량부일 수 있고, 에틸 아크릴레이트(ethyl acrylate)의 함량은 약 50∼70 중량부일 수 있고, 메틸 메타크릴레이트(methyl methacrylate)의 함량은 약 20∼30 중량부일 수 있고, 메타크릴산(methacrylic acid)의 함량은 약 5∼10 중량부일 수 있으며, 과황산칼륨(K2S2O8)의 함량은 약 1∼2 중량부일 수 있다. 물, 에틸 아크릴레이트(ethyl acrylate), 메틸 메타크릴레이트(methyl methacrylate), 메타크릴산(methacrylic acid) 및 과황산칼륨(K2S2O8)을 혼합하여 중합함으로써 제1 아크릴 에멀젼(10)을 제조할 수 있다. 이때, 상기 원료 물질들이 전술한 함량 조건을 만족할 때, 보다 용이하게 우수한 물성을 갖는 제1 아크릴 에멀젼(10)을 제조할 수 있다. 부가적으로, 상기한 '물'은 증류수일 수 있고, 경우에 따라, 탈이온수일 수도 있다. 이는 본 명세서의 다른 부분에서 사용되는 '물'에 대해서도 동일할 수 있다. The first acrylic emulsion 10 is provided with a mixture of water, ethyl acrylate, methyl methacrylate, methacrylic acid, and potassium persulfate (K 2 S 2 O 8 ) can do. In the mixed solution of the first acrylic emulsion 10, or in the first acrylic emulsion 10, the content of water may be about 100 to 120 parts by weight, and the content of ethyl acrylate is about 50 to 70 parts by weight Can, the content of methyl methacrylate (methyl methacrylate) may be about 20 to 30 parts by weight, the content of methacrylic acid (methacrylic acid) may be about 5 to 10 parts by weight, potassium persulfate (K 2 S 2 O 8 ) The content may be about 1 to 2 parts by weight. Water, ethyl acrylate (ethyl acrylate), methyl methacrylate (methyl methacrylate), methacrylic acid (methacrylic acid) and potassium persulfate (K 2 S 2 O 8 ) by polymerization by mixing the first acrylic emulsion (10) can be manufactured. At this time, when the raw materials satisfy the content conditions described above, the first acrylic emulsion 10 having excellent physical properties can be more easily prepared. Additionally, the above 'water' may be distilled water, and in some cases, deionized water. This may be the same for 'water' used in other parts of this specification.

제1 아크릴 에멀젼(10) 내에 methacrylic acid copolymer (메타크릴산 공중합체)가 형성될 수 있다. 상기 methacrylic acid copolymer는 methacrylic acid - ethyl acrylate copolymer 일 수 있다. 본 명세서에서 제1 아크릴 에멀젼(10)의 상기 혼합액, 즉, 물, 에틸 아크릴레이트, 메틸 메타크릴레이트, 메타크릴산 및 과황산칼륨이 혼합된 상기 혼합액은 methacrylic acid copolymer를 포함하는 것으로 이해될 수 있다. 상기 methacrylic acid copolymer는 코팅제(코팅층)에서 우수한 내열성, 내산성, 내오일성(내유성), 내알콜성을 구현할 수 있는 물질일 수 있다. A methacrylic acid copolymer (methacrylic acid copolymer) may be formed in the first acrylic emulsion 10 . The methacrylic acid copolymer may be a methacrylic acid-ethyl acrylate copolymer. In the present specification, the mixed solution of the first acrylic emulsion 10, that is, the mixed solution in which water, ethyl acrylate, methyl methacrylate, methacrylic acid and potassium persulfate are mixed, may be understood to include a methacrylic acid copolymer. there is. The methacrylic acid copolymer may be a material capable of implementing excellent heat resistance, acid resistance, oil resistance (oil resistance), and alcohol resistance in a coating agent (coating layer).

제2 아크릴 에멀젼(20)은 물, 에틸 아크릴레이트(ethyl acrylate), 아크릴산(acrylic acid), 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt) 및 과산화수소(H2O2)의 혼합액을 구비할 수 있다. 제2 아크릴 에멀젼(20)의 상기 혼합액에서, 또는, 제2 아크릴 에멀젼(20)에서 물의 함량은 약 150∼200 중량부일 수 있고, 에틸 아크릴레이트(ethyl acrylate)의 함량은 약 100∼120 중량부일 수 있고, 아크릴산(acrylic acid)의 함량은 약 80∼100 중량부일 수 있고, 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt)의 함량은 약 8∼10 중량부일 수 있으며, 과산화수소(H2O2)의 함량은 약 5∼8 중량부일 수 있다. 물, 에틸 아크릴레이트(ethyl acrylate), 아크릴산(acrylic acid), 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt) 및 과산화수소(H2O2)를 혼합하여 중합함으로써 제2 아크릴 에멀젼(20)을 제조할 수 있다. 이때, 상기 원료 물질들이 전술한 함량 조건을 만족할 때, 보다 용이하게 우수한 물성을 갖는 제2 아크릴 에멀젼(20)을 제조할 수 있다. The second acrylic emulsion 20 may include a mixture of water, ethyl acrylate, acrylic acid, octadecane sulfonic acid sodium salt, and hydrogen peroxide (H 2 O 2 ). there is. In the mixed solution of the second acrylic emulsion 20, or in the second acrylic emulsion 20, the content of water may be about 150 to 200 parts by weight, and the content of ethyl acrylate is about 100 to 120 parts by weight and the content of acrylic acid may be about 80 to 100 parts by weight, and the content of octadecane sulfonic acid sodium salt may be about 8 to 10 parts by weight, and hydrogen peroxide (H 2 O 2 ) ) may be about 5 to 8 parts by weight. A second acrylic emulsion 20 is prepared by mixing and polymerizing water, ethyl acrylate, acrylic acid, octadecane sulfonic acid sodium salt, and hydrogen peroxide (H 2 O 2 ). can do. At this time, when the raw materials satisfy the content conditions described above, the second acrylic emulsion 20 having excellent physical properties can be more easily prepared.

제2 아크릴 에멀젼(20) 내에 acrylic acid ester copolymer (아크릴산 에스테르 공중합체)가 형성될 수 있다. 본 명세서에서 제2 아크릴 에멀젼(20)의 상기 혼합액, 즉, 물, 에틸 아크릴레이트, 아크릴산, 옥타데칸 설폰산나트륨 및 과산화수소가 혼합된 상기 혼합액은 acrylic acid ester copolymer를 포함하는 것으로 이해될 수 있다. 상기 acrylic acid ester copolymer는 코팅제(코팅층)에서 우수한 내수성 등을 구현할 수 있는 물질일 수 있다. An acrylic acid ester copolymer may be formed in the second acrylic emulsion 20 . In the present specification, the mixed solution of the second acrylic emulsion 20, that is, the mixed solution in which water, ethyl acrylate, acrylic acid, sodium octadecane sulfonate and hydrogen peroxide are mixed, may be understood to include an acrylic acid ester copolymer. The acrylic acid ester copolymer may be a material capable of implementing excellent water resistance in a coating agent (coating layer).

제3 아크릴 에멀젼(30)은 물, 스타이렌(styrene), 부타디엔(butadiene), 올레인산나트륨(sodium oleate), 과황산칼륨(K2S2O8), 인산나트륨(sodium phosphate) 및 도데실메르캅탄(dodecyl mercaptan)의 혼합액을 구비할 수 있다. 제3 아크릴 에멀젼(30)의 상기 혼합액에서, 또는, 제3 아크릴 에멀젼(30)에서 물의 함량은 약 80∼100 중량부일 수 있고, 스타이렌(styrene)의 함량은 약 70∼80부 중량부일 수 있고, 부타디엔(butadiene)의 함량은 약 10∼15 중량부일 수 있고, 올레인산나트륨(sodium oleate)의 함량은 약 1∼3 중량부일 수 있고, 과황산칼륨(K2S2O8)의 함량은 약 1∼2 중량부일 수 있고, 인산나트륨(sodium phosphate)의 함량은 약 0.1∼0.3 중량부일 수 있으며, 도데실메르캅탄(dodecyl mercaptan)의 함량은 약 0.1∼0.3 중량부일 수 있다. 물, 스타이렌(styrene), 부타디엔(butadiene), 올레인산나트륨(sodium oleate), 과황산칼륨(K2S2O8), 인산나트륨(sodium phosphate) 및 도데실메르캅탄(dodecyl mercaptan)을 혼합하여 중합함으로써 제3 아크릴 에멀젼(30)을 제조할 수 있다. 이때, 상기 원료 물질들이 전술한 함량 조건을 만족할 때, 보다 용이하게 우수한 물성을 갖는 제3 아크릴 에멀젼(30)을 제조할 수 있다. The third acrylic emulsion 30 is water, styrene, butadiene, sodium oleate, potassium persulfate (K 2 S 2 O 8 ), sodium phosphate (sodium phosphate), and dodecylmer A mixed solution of dodecyl mercaptan may be provided. In the mixed solution of the third acrylic emulsion 30, or in the third acrylic emulsion 30, the content of water may be about 80 to 100 parts by weight, and the content of styrene may be about 70 to 80 parts by weight. and the content of butadiene may be about 10 to 15 parts by weight, the content of sodium oleate may be about 1 to 3 parts by weight, and the content of potassium persulfate (K 2 S 2 O 8 ) is It may be about 1 to 2 parts by weight, the content of sodium phosphate may be about 0.1 to 0.3 parts by weight, and the content of dodecyl mercaptan may be about 0.1 to 0.3 parts by weight. By mixing water, styrene, butadiene, sodium oleate, potassium persulfate (K 2 S 2 O 8 ), sodium phosphate and dodecyl mercaptan (dodecyl mercaptan) By polymerization, the third acrylic emulsion 30 can be prepared. At this time, when the raw materials satisfy the content conditions described above, the third acrylic emulsion 30 having excellent physical properties can be more easily prepared.

제3 아크릴 에멀젼(30) 내에 styrene-butadiene copolymer (스타이렌-부타디엔 공중합체)가 형성될 수 있다. 본 명세서에서 제3 아크릴 에멀젼(30)의 상기 혼합액, 즉, 물, 스타이렌, 부타디엔, 올레인산나트륨, 과황산칼륨, 인산나트륨 및 도데실메르캅탄이 혼합된 상기 혼합액은 styrene-butadiene copolymer를 포함하는 것으로 이해될 수 있다. 상기 styrene-butadiene copolymer는 코팅제(코팅층)에서 우수한 내광성(light fastness), 내후성(weather resistance), 접착력, 인장력을 구현할 수 있는 물질일 수 있다. A styrene-butadiene copolymer (styrene-butadiene copolymer) may be formed in the third acrylic emulsion 30 . In the present specification, the mixed solution of the third acrylic emulsion 30, that is, water, styrene, butadiene, sodium oleate, potassium persulfate, sodium phosphate and dodecyl mercaptan, is mixed with the mixed solution containing a styrene-butadiene copolymer can be understood as The styrene-butadiene copolymer may be a material capable of implementing excellent light fastness, weather resistance, adhesion, and tensile force in a coating agent (coating layer).

접착성 물질(40)은 메틸 메타크릴레이트(methyl methacrylate)(MMA)이거나 이를 포함할 수 있다. 접착 특성 개선을 위해서는, 접착성 물질(40)이 메틸 메타크릴레이트(methyl methacrylate)(MMA)를 포함하는 것이 바람직할 수 있으나, 경우에 따라, MMA 이외에 다른 물질이 사용될 수도 있다. The adhesive material 40 may be or include methyl methacrylate (MMA). In order to improve the adhesive properties, the adhesive material 40 may preferably include methyl methacrylate (MMA), but in some cases, a material other than MMA may be used.

한편, 첨가제(50)는 탈포제(deformer agent) 및 소포제(antifoaming agent) 중 적어도 하나를 포함할 수 있다. 상기 탈포제는, 예를 들어, 미네랄 오일(mineral oil), 폴리아크릴레이트 기반(polyacrylate base) 탈포제 등을 포함할 수 있다. 상기 소포제는, 예를 들어, 폴리디메틸실록산(polydimethylsiloxane)(PDMS)을 포함할 수 있다. 상기한 탈포제 및 소포제를 사용하는 경우, 코팅층 형성을 위한 도장 작업시 우수한 탈포 및 소포 효과를 얻을 수 있다. Meanwhile, the additive 50 may include at least one of a defoaming agent and an antifoaming agent. The defoaming agent may include, for example, mineral oil, a polyacrylate-based defoaming agent, and the like. The antifoaming agent may include, for example, polydimethylsiloxane (PDMS). In the case of using the above defoaming agent and antifoaming agent, excellent defoaming and defoaming effect can be obtained during the painting operation for forming the coating layer.

본 발명의 실시예에 따른 다기능성 친환경 수성 코팅액 조성물에서 제1 아크릴 에멀젼(10)의 함량은 약 15∼20 중량부일 수 있고, 제2 아크릴 에멀젼(20)의 함량은 약 60∼70 중량부일 수 있고, 제3 아크릴 에멀젼(30)의 함량은 약 10∼15 중량부일 수 있고, 접착성 물질(40)의 함량은 약 3∼5 중량부일 수 있으며, 첨가제(50)의 함량은 약 0.5∼3.5 중량부일 수 있다. 첨가제(50)가 상기 탈포제 및 상기 소포제를 포함하는 경우, 상기 탈포제의 함량은 약 0.5∼1 중량부일 수 있고, 상기 소포제(ex, PDMS)의 함량은 약 1∼2 중량부일 수 있다. 첨가제(50)는 상기 탈포제 및 상기 소포제 이외에 다른 첨가제를 하나 이상 더 포함할 수도 있다. In the multifunctional eco-friendly aqueous coating solution composition according to an embodiment of the present invention, the content of the first acrylic emulsion 10 may be about 15 to 20 parts by weight, and the content of the second acrylic emulsion 20 may be about 60 to 70 parts by weight. and the content of the third acrylic emulsion 30 may be about 10 to 15 parts by weight, the content of the adhesive material 40 may be about 3 to 5 parts by weight, and the content of the additive 50 is about 0.5 to 3.5 It may be parts by weight. When the additive 50 includes the defoaming agent and the antifoaming agent, the content of the defoaming agent may be about 0.5 to 1 parts by weight, and the content of the antifoaming agent (ex, PDMS) may be about 1 to 2 parts by weight. The additive 50 may further include one or more other additives in addition to the defoaming agent and the defoaming agent.

상기 수성 코팅액 조성물에서 제1 아크릴 에멀젼(10)의 함량이 약 15∼20 중량부이고, 제2 아크릴 에멀젼(20)의 함량이 약 60∼70 중량부이고, 제3 아크릴 에멀젼(30)의 함량이 약 10∼15 중량부인 경우, 발수성, 방수성, 내오일성, 내산성, 내알콜성 등을 향상시키고, 다양한 기능성을 확보하는데 유리할 수 있다. 또한, 재활용성 및 친환경성을 개선하는데도 유리할 수 있다. 아울러, 도장 공정의 용이성을 확보하는데도 유리할 수 있다. 따라서, 상기 수성 코팅액 조성물에서 제1 내지 제3 아크릴 에멀젼(10, 20, 30) 각각의 함량 조건을 상기한 범위로 조절하는 것이 바람직할 수 있다. In the aqueous coating solution composition, the content of the first acrylic emulsion 10 is about 15 to 20 parts by weight, the content of the second acrylic emulsion 20 is about 60 to 70 parts by weight, and the content of the third acrylic emulsion 30 is When it is about 10 to 15 parts by weight, it may be advantageous to improve water repellency, waterproofness, oil resistance, acid resistance, alcohol resistance, etc., and to secure various functionalities. In addition, it may be advantageous to improve recyclability and eco-friendliness. In addition, it may be advantageous to secure the easiness of the painting process. Therefore, it may be preferable to adjust the content conditions of each of the first to third acrylic emulsions 10, 20, and 30 in the aqueous coating solution composition within the above-described range.

도 2는 본 발명의 일 실시예에 따른 다기능성(다목적성) 친환경 수성 코팅액 조성물을 제조하는 방법을 설명하기 위한 순서도이다. 2 is a flowchart for explaining a method for preparing a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to an embodiment of the present invention.

도 2를 참조하면, 본 발명의 실시예에 따른 다기능성(다목적성) 친환경 수성 코팅액의 제조 방법은 제1 아크릴 에멀젼을 마련하는 단계(S10), 제2 아크릴 에멀젼을 마련하는 단계(S20) 및 제3 아크릴 에멀젼을 마련하는 단계(S30)를 포함할 수 있다. 또한, 상기 수성 코팅액의 제조 방법은 상기 제1 내지 제3 아크릴 에멀젼과 접착성 물질 및 첨가제를 혼합하는 단계(S40)를 포함할 수 있다. 여기서, S10, S20, S30의 단계 순서는 뒤바뀔 수 있다. 또한, S10, S20, S30의 단계들은 동시에 수행될 수도 있다. Referring to FIG. 2 , the method for preparing a multifunctional (multipurpose) eco-friendly aqueous coating solution according to an embodiment of the present invention includes the steps of preparing a first acrylic emulsion (S10), preparing a second acrylic emulsion (S20) and It may include the step of preparing a third acrylic emulsion (S30). Also, the method for preparing the aqueous coating solution may include mixing the first to third acrylic emulsions with an adhesive material and additives (S40). Here, the order of steps S10, S20, and S30 may be reversed. Also, steps S10, S20, and S30 may be performed simultaneously.

상기 제1 내지 제3 아크릴 에멀젼과 상기 접착성 물질 및 상기 첨가제의 물질 구성 및 제조 방법 등은 도 1을 참조하여 설명한 바와 동일할 수 있다. The material composition and manufacturing method of the first to third acrylic emulsions, the adhesive material, and the additive may be the same as those described with reference to FIG. 1 .

S10 단계에서 물 약 100∼120 중량부, 에틸 아크릴레이트(ethyl acrylate) 약 50∼70 중량부, 메틸 메타크릴레이트(methyl methacrylate) 약 20∼30 중량부, 메타크릴산(methacrylic acid) 약 5∼10 중량부 및 과황산칼륨(K2S2O8) 약 1∼2 중량부를 혼합하여 중합함으로써, 상기 제1 아크릴 에멀젼을 제조할 수 있다. 상기 제1 아크릴 에멀젼 내에 methacrylic acid copolymer (메타크릴산 공중합체)가 형성될 수 있다. 상기 methacrylic acid copolymer는 methacrylic acid - ethyl acrylate copolymer 일 수 있다. In step S10, about 100 to 120 parts by weight of water, about 50 to 70 parts by weight of ethyl acrylate, about 20 to 30 parts by weight of methyl methacrylate, about 5 to about methacrylic acid By mixing 10 parts by weight and about 1 to 2 parts by weight of potassium persulfate (K 2 S 2 O 8 ), the first acrylic emulsion can be prepared. A methacrylic acid copolymer (methacrylic acid copolymer) may be formed in the first acrylic emulsion. The methacrylic acid copolymer may be a methacrylic acid-ethyl acrylate copolymer.

S20 단계에서 물 약 150∼200 중량부, 에틸 아크릴레이트(ethyl acrylate) 100∼120 약 중량부, 아크릴산(acrylic acid) 약 80∼100 중량부, 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt) 약 8∼10 중량부 및 과산화수소(H2O2) 약 5∼8 중량부를 혼합하여 중합함으로써, 상기 제2 아크릴 에멀젼을 제조할 수 있다. 상기 제2 아크릴 에멀젼 내에 acrylic acid ester copolymer (아크릴산 에스테르 공중합체)가 형성될 수 있다. In step S20, about 150-200 parts by weight of water, about 100-120 parts by weight of ethyl acrylate, about 80-100 parts by weight of acrylic acid, about octadecane sulfonic acid sodium salt By mixing 8 to 10 parts by weight and about 5 to 8 parts by weight of hydrogen peroxide (H 2 O 2 ), the second acrylic emulsion can be prepared. An acrylic acid ester copolymer (acrylic acid ester copolymer) may be formed in the second acrylic emulsion.

S30 단계에서 물 약 80∼100 중량부, 스타이렌(styrene) 약 70∼80부 중량부, 부타디엔(butadiene) 약 10∼15 중량부, 올레인산나트륨(sodium oleate) 약 1∼3 중량부, 과황산칼륨(K2S2O8) 약 1∼2 중량부, 인산나트륨(sodium phosphate) 약 0.1∼0.3 중량부 및 도데실메르캅탄(dodecyl mercaptan) 약 0.1∼0.3 중량부를 혼합하여 중합함으로써, 상기 제3 아크릴 에멀젼을 제조할 수 있다. 상기 제3 아크릴 에멀젼 내에 styrene-butadiene copolymer (스타이렌-부타디엔 공중합체)가 형성될 수 있다. In step S30, about 80 to 100 parts by weight of water, about 70 to 80 parts by weight of styrene, about 10 to 15 parts by weight of butadiene, about 1 to 3 parts by weight of sodium oleate, persulfuric acid Potassium (K 2 S 2 O 8 ) about 1 to 2 parts by weight, sodium phosphate (sodium phosphate) about 0.1 to 0.3 parts by weight, and dodecyl mercaptan (dodecyl mercaptan) by polymerization by mixing about 0.1 to 0.3 parts by weight, 3 Acrylic emulsions can be prepared. A styrene-butadiene copolymer (styrene-butadiene copolymer) may be formed in the third acrylic emulsion.

S40 단계에서 상기 제1 아크릴 에멀젼 약 15∼20 중량부, 상기 제2 아크릴 에멀젼 약 60∼70 중량부, 상기 제3 아크릴 에멀젼 약 10∼15 중량부, 상기 접착성 물질 약 3∼5 중량부 및 상기 첨가제 약 0.5∼3.5 중량부를 균일하게 혼합하여 상기 수성 코팅액 조성물을 제조할 수 있다. In step S40, about 15 to 20 parts by weight of the first acrylic emulsion, about 60 to 70 parts by weight of the second acrylic emulsion, about 10 to 15 parts by weight of the third acrylic emulsion, about 3 to 5 parts by weight of the adhesive material and About 0.5 to 3.5 parts by weight of the additive may be uniformly mixed to prepare the aqueous coating solution composition.

상기 접착성 물질은 메틸 메타크릴레이트(methyl methacrylate)(MMA)이거나 이를 포함할 수 있지만, 경우에 따라, MMA 이외에 다른 물질이 사용될 수도 있다. 상기 첨가제(50)는 탈포제(deformer agent) 및 소포제(antifoaming agent) 중 적어도 하나를 포함할 수 있다. 상기 탈포제는, 예를 들어, 미네랄 오일(mineral oil), 폴리아크릴레이트 기반(polyacrylate base) 탈포제 등을 포함할 수 있다. 상기 소포제는, 예를 들어, 폴리디메틸실록산(polydimethylsiloxane)(PDMS)을 포함할 수 있다. 상기 첨가제가 상기 탈포제 및 상기 소포제를 포함하는 경우, 상기 수성 코팅액 조성물에서 상기 탈포제의 함량은 약 0.5∼1 중량부일 수 있고, 상기 소포제(ex, PDMS)의 함량은 약 1∼2 중량부일 수 있다. 상기 첨가제는 상기 탈포제 및 상기 소포제 이외에 다른 첨가제를 하나 이상 더 포함할 수도 있다. The adhesive material may be or include methyl methacrylate (MMA), but in some cases, a material other than MMA may be used. The additive 50 may include at least one of a defoaming agent and an antifoaming agent. The defoaming agent may include, for example, mineral oil, a polyacrylate-based defoaming agent, and the like. The antifoaming agent may include, for example, polydimethylsiloxane (PDMS). When the additive includes the defoaming agent and the antifoaming agent, the content of the defoaming agent in the aqueous coating solution composition may be about 0.5 to 1 parts by weight, and the content of the defoaming agent (ex, PDMS) is about 1 to 2 parts by weight can The additive may further include one or more other additives in addition to the defoaming agent and the defoaming agent.

본 발명의 실시예에 따른 수성 코팅액 조성물은 소정의 피코팅물(피코팅 부재)의 표면 상에 다양한 방식으로 도장될 수 있다. 예를 들어, 스프레이, 롤러, 붓 등을 이용한 다양한 도장 방식으로 도장될 수 있다. 또한, 필요에 따라서, 상기 수성 코팅액 조성물에 물(water)을 추가하여 점도를 조절한 후에 도장 공정을 수행할 수 있다. 따라서, 상기 수성 코팅액 조성물은 점도 조절을 위한 추가적인 물(water)을 더 포함할 수 있다. 소정의 피코팅물(피코팅 부재)의 표면에 상기 수성 코팅액 조성물을 코팅하고 이를 건조 내지 경화함으로써, 코팅층을 형성할 수 있다. 도장(코팅) 방법 및 건조 방법 등은 일반적인 방법을 따를 수 있다. The aqueous coating solution composition according to an embodiment of the present invention may be coated on the surface of a predetermined object to be coated (member to be coated) in various ways. For example, it may be coated by various coating methods using a spray, roller, brush, or the like. In addition, if necessary, the coating process may be performed after adjusting the viscosity by adding water to the aqueous coating solution composition. Accordingly, the aqueous coating solution composition may further include additional water for viscosity control. A coating layer may be formed by coating the aqueous coating solution composition on the surface of a predetermined object to be coated (member to be coated) and drying or curing the composition. A general method may be followed for the coating (coating) method and the drying method.

도 3은 본 발명의 일 실시예에 따른 것으로, 다기능성(다목적성) 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층(200a)을 포함하는 코팅층 적용 부재를 보여주는 단면도이다. 3 is a cross-sectional view showing a coating layer application member including a coating layer 200a formed by applying a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to an embodiment of the present invention.

도 3을 참조하면, 본 발명의 실시예에 따른 코팅층 적용 부재는 피코팅 부재(100) 및 피코팅 부재(100)의 표면에 형성된 코팅층(200a)을 포함할 수 있다. 코팅층(200a)은 도 1 및 도 2를 참조하여 설명한 실시예에 따른 수성 코팅액 조성물을 코팅하여 형성한 것일 수 있다. 코팅층(200a)은 methacrylic acid copolymer, acrylic acid ester copolymer 및 styrene-butadiene copolymer를 포함할 수 있고, 그에 따라, 우수한 내열성, 내산성, 내오일성(내유성), 내알콜성, 내수성, 내광성, 내후성, 접착력, 인장력을 가질 수 있다. 또한, 코팅층(200a)은 우수한 재활용성 및 친환경성을 가질 수 있다. 코팅층(200a)의 두께는, 예를 들어, 약 7∼10 ㎛ 정도일 수 있지만, 이는 예시적인 것이고, 용도 및 적용 분야에 따라 적절한 두께 범위는 달라질 수 있다. Referring to FIG. 3 , the coating layer application member according to the embodiment of the present invention may include a member to be coated 100 and a coating layer 200a formed on the surface of the member 100 to be coated. The coating layer 200a may be formed by coating the aqueous coating solution composition according to the embodiment described with reference to FIGS. 1 and 2 . The coating layer 200a may include a methacrylic acid copolymer, an acrylic acid ester copolymer, and a styrene-butadiene copolymer, and accordingly, excellent heat resistance, acid resistance, oil resistance (oil resistance), alcohol resistance, water resistance, light resistance, weather resistance, adhesion, may have tensile strength. In addition, the coating layer 200a may have excellent recyclability and eco-friendliness. The thickness of the coating layer 200a may be, for example, about 7 to 10 μm, but this is exemplary, and an appropriate thickness range may vary depending on uses and fields of application.

한편, 피코팅 부재(100)는 종이류, 목재류 또는 패브릭류 등일 수 있다. 상기 종이류는 재생종이, 골판지류를 포함하는 모든 종류의 종이를 포함할 수 있고, 박스 형태나 평면 형태(포장지 등), 롤(roll) 형태, 원통 형태 등 다양한 형태를 가질 수 있다. 이러한 종이류의 적어도 일면에 상기한 수성 코팅액 조성물을 코팅하여 코팅층(200a)을 형성함으로써, 다양한 기능성(발수, 방수, 내오일성, 내산성, 내알콜성, 재활용성 등)을 부여할 수 있다. 상기 패브릭류는, 예를 들어, 천막(ex, 산업용 천막 등)과 같은 막 종류나 그 밖에 다양한 천 종류를 포함할 수 있다. 이러한 패브릭류에도 상기한 수성 코팅액 조성물을 코팅하여 코팅층(200a)을 형성할 수 있다. On the other hand, the member to be coated 100 may be paper, wood, fabric, or the like. The paper may include all kinds of paper including recycled paper and corrugated paper, and may have various forms such as a box form or a flat form (such as wrapping paper), a roll form, and a cylindrical form. By coating the above-described aqueous coating solution composition on at least one surface of these papers to form the coating layer 200a, various functionalities (water repellency, waterproofness, oil resistance, acid resistance, alcohol resistance, recyclability, etc.) can be imparted. The fabrics may include, for example, a film type such as a tent (eg, an industrial tent, etc.) or various other types of fabric. The coating layer 200a may be formed by coating the above-described aqueous coating solution composition on these fabrics as well.

도 3의 실시예에서는 피코팅 부재(100)의 일면에만 코팅층(200a)을 형성한 경우를 도시하였지만, 다른 실시예에 따르면, 피코팅 부재(100)의 양면에 코팅층을 형성할 수도 있다. 그 일례가 도 4에 도시되어 있다. 3 illustrates a case in which the coating layer 200a is formed on only one surface of the member 100 to be coated, but according to another embodiment, the coating layer may be formed on both surfaces of the member 100 to be coated. An example thereof is shown in FIG. 4 .

도 4는 본 발명의 다른 실시예에 따른 것으로, 다기능성(다목적성) 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층(200a, 200b)을 포함하는 코팅층 적용 부재를 보여주는 단면도이다. 4 is a cross-sectional view showing a coating layer application member including coating layers 200a and 200b formed by applying a multifunctional (multipurpose) eco-friendly aqueous coating solution composition according to another embodiment of the present invention.

도 4를 참조하면, 본 발명의 실시예에 따른 코팅층 적용 부재는 피코팅 부재(100) 및 피코팅 부재(100)의 양면에 형성된 코팅층(200a, 200b)을 포함할 수 있다. 피코팅 부재(100)의 일면에 형성된 코팅층(200a)은 제1 코팅층(200a)이라 할 수 있고, 피코팅 부재(100)의 타면에 형성된 코팅층(200b)은 제2 코팅층(200b)이라 할 수 있다. 제1 및 제2 코팅층(200a, 200b)은 도 1 및 도 2를 참조하여 설명한 실시예에 따른 수성 코팅액 조성물을 코팅하여 형성한 것일 수 있다. 제1 및 제2 코팅층(200a, 200b)은 methacrylic acid copolymer, acrylic acid ester copolymer 및 styrene-butadiene copolymer를 포함할 수 있다. 제1 및 제2 코팅층(200a, 200b) 각각의 물질, 특성, 두께 등은 도 3에서 설명한 코팅층(200a)과 동일하거나 유사할 수 있다. Referring to FIG. 4 , the coating layer application member according to the embodiment of the present invention may include a member to be coated 100 and coating layers 200a and 200b formed on both surfaces of the member 100 to be coated. The coating layer 200a formed on one surface of the member 100 to be coated may be referred to as a first coating layer 200a, and the coating layer 200b formed on the other surface of the member 100 to be coated may be referred to as a second coating layer 200b. there is. The first and second coating layers 200a and 200b may be formed by coating the aqueous coating solution composition according to the embodiment described with reference to FIGS. 1 and 2 . The first and second coating layers 200a and 200b may include a methacrylic acid copolymer, an acrylic acid ester copolymer, and a styrene-butadiene copolymer. The material, properties, thickness, etc. of each of the first and second coating layers 200a and 200b may be the same as or similar to those of the coating layer 200a described with reference to FIG. 3 .

이상에서 설명한 본 발명의 실시예들에 따르면, 피코팅 부재에 적용했을 때 발수성, 방수성, 내오일성, 내산성, 내알콜성이 우수하고 재활용이 용이하며 독성이 없는 다기능성(다목적성) 친환경 수성 코팅액 조성물을 구현할 수 있다. 또한, 본 발명의 실시예들에 따르면, 상기한 다기능성 친환경 수성 코팅액 조성물을 적용하여 형성한 코팅층을 포함하는 코팅층 적용 부재를 구현할 수 있다. According to the embodiments of the present invention described above, when applied to a member to be coated, a multifunctional (multipurpose) eco-friendly water-based coating solution with excellent water repellency, waterproofness, oil resistance, acid resistance, alcohol resistance, easy recycling, and non-toxicity composition can be implemented. In addition, according to the embodiments of the present invention, it is possible to implement a coating layer application member including a coating layer formed by applying the above-described multifunctional eco-friendly aqueous coating solution composition.

실시예들에 따른 다기능성 친환경 수성 코팅액 조성물은 우수한 기능성 및 친환경성을 가지므로, 기존의 코팅제(ex, PE 필름 등)를 대체할 수 있고 기존 코팅제에 의한 환경 오염 문제를 크게 줄일 수 있을 것으로 기대된다. Since the multifunctional eco-friendly aqueous coating solution composition according to the embodiments has excellent functionality and eco-friendliness, it is expected that it can replace the existing coating agent (ex, PE film, etc.) and greatly reduce the environmental pollution problem caused by the existing coating agent do.

특히, 종이컵 등 다양한 일회용품 등에 상기한 다기능성 친환경 수성 코팅액 조성물이 적용된 경우, 상기 일회용품 등을 재활용하거나 쓰레기로 배출할 때, 기존과 같이 코팅막을 제거할 필요가 없기 때문에, 재활용이 매우 용이할 수 있고 환경 오염 문제를 크게 줄일 수 있을 것으로 기대된다. 또한, 독성이나 유해성이 없거나 거의 없을 수 있으므로, 다양한 분야에 유용하게 적용될 수 있을 것으로 기대된다. In particular, when the above-mentioned multifunctional eco-friendly aqueous coating solution composition is applied to various disposable products such as paper cups, when recycling the disposable products or discharging them as garbage, there is no need to remove the coating film as in the past, so recycling can be very easy. It is expected to greatly reduce the environmental pollution problem. In addition, since there may be little or no toxicity or harmfulness, it is expected to be usefully applied to various fields.

본 명세서에서는 본 발명의 바람직한 실시예에 대하여 개시하였으며, 비록 특정 용어들이 사용되었으나, 이는 단지 본 발명의 기술 내용을 쉽게 설명하고 발명의 이해를 돕기 위한 일반적인 의미에서 사용된 것이지, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예 외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다. 예들 들어, 해당 기술 분야에서 통상의 지식을 가진 자라면, 도 1 내지 도 4를 참조하여 설명한 실시예에 따른 다기능성 친환경 수성 코팅액 조성물과 그 제조 방법 및 상기 다기능성 친환경 수성 코팅액 조성물을 적용한 코팅층 적용 부재는 다양하게 변형될 수 있음을 알 수 있을 것이다. 때문에 발명의 범위는 설명된 실시예에 의하여 정하여 질 것이 아니고 특허 청구범위에 기재된 기술적 사상에 의해 정하여져야 한다. In the present specification, preferred embodiments of the present invention have been disclosed, and although specific terms are used, these are only used in a general sense to easily explain the technical content of the present invention and help the understanding of the present invention, and to limit the scope of the present invention. It is not meant to be limiting. It will be apparent to those of ordinary skill in the art to which the present invention pertains that other modifications based on the technical spirit of the present invention can be implemented in addition to the embodiments disclosed herein. For example, those of ordinary skill in the art will apply the multifunctional eco-friendly aqueous coating solution composition and its manufacturing method according to the embodiment described with reference to FIGS. 1 to 4, and the multifunctional eco-friendly aqueous coating solution coating layer application It will be appreciated that the member may be variously deformed. Therefore, the scope of the invention should not be determined by the described embodiments, but should be determined by the technical idea described in the claims.

* 도면의 주요 부분에 대한 부호설명 *
10 : 제1 아크릴 에멀젼 20 : 제2 아크릴 에멀젼
30 : 제3 아크릴 에멀젼 40 : 접착성 물질
50 : 첨가제 100 : 피코팅 부재
200a, 200b : 코팅층 S10∼S40 : 단계들* Explanation of symbols for the main parts of the drawing *
10: first acrylic emulsion 20: second acrylic emulsion
30: third acrylic emulsion 40: adhesive material
50: additive 100: member to be coated
200a, 200b: coating layer S10 to S40: steps

Claims (11)

피코팅물에 코팅하기 위한 수성 코팅액 조성물로서,
물, 에틸 아크릴레이트(ethyl acrylate), 메틸 메타크릴레이트(methyl methacrylate), 메타크릴산(methacrylic acid) 및 과황산칼륨(K2S2O8)의 혼합액을 구비하는 제1 아크릴 에멀젼(acrylic emulsion);
물, 에틸 아크릴레이트(ethyl acrylate), 아크릴산(acrylic acid), 옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt) 및 과산화수소(H2O2)의 혼합액을 구비하는 제2 아크릴 에멀젼;
물, 스타이렌(styrene), 부타디엔(butadiene), 올레인산나트륨(sodium oleate), 과황산칼륨(K2S2O8), 인산나트륨(sodium phosphate) 및 도데실메르캅탄(dodecyl mercaptan)의 혼합액을 구비하는 제3 아크릴 에멀젼;
접착성 물질; 및
첨가제;를 포함하는, 수성 코팅액 조성물. An aqueous coating solution composition for coating an object to be coated, comprising:
A first acrylic emulsion comprising a mixture of water, ethyl acrylate, methyl methacrylate, methacrylic acid and potassium persulfate (K 2 S 2 O 8 ). );
a second acrylic emulsion comprising a mixture of water, ethyl acrylate, acrylic acid, octadecane sulfonic acid sodium salt, and hydrogen peroxide (H 2 O 2 );
A mixture of water, styrene, butadiene, sodium oleate, potassium persulfate (K 2 S 2 O 8 ), sodium phosphate, and dodecyl mercaptan A third acrylic emulsion provided;
adhesive substances; and
An additive; containing, an aqueous coating solution composition. 제 1 항에 있어서, 상기 제1 아크릴 에멀젼에서,
물의 함량은 100∼120 중량부이고,
에틸 아크릴레이트(ethyl acrylate)의 함량은 50∼70 중량부이고,
메틸 메타크릴레이트(methyl methacrylate)의 함량은 20∼30 중량부이고,
메타크릴산(methacrylic acid)의 함량은 5∼10 중량부이고,
과황산칼륨(K2S2O8)의 함량은 1∼2 중량부인 수성 코팅액 조성물. According to claim 1, wherein in the first acrylic emulsion,
The content of water is 100 to 120 parts by weight,
The content of ethyl acrylate is 50 to 70 parts by weight,
The content of methyl methacrylate is 20 to 30 parts by weight,
The content of methacrylic acid is 5 to 10 parts by weight,
The content of potassium persulfate (K 2 S 2 O 8 ) is 1 to 2 parts by weight of the aqueous coating solution composition. 제 1 항에 있어서, 상기 제2 아크릴 에멀젼에서,
물의 함량은 150∼200 중량부이고,
에틸 아크릴레이트(ethyl acrylate)의 함량은 100∼120 중량부이고,
아크릴산(acrylic acid)의 함량은 80∼100 중량부이고,
옥타데칸 설폰산나트륨(octadecane sulfonic acid sodium salt)의 함량은 8∼10 중량부이고,
과산화수소(H2O2)의 함량은 5∼8 중량부인 수성 코팅액 조성물. The method of claim 1, wherein in the second acrylic emulsion,
The content of water is 150 to 200 parts by weight,
The content of ethyl acrylate is 100 to 120 parts by weight,
The content of acrylic acid is 80 to 100 parts by weight,
The content of octadecane sulfonic acid sodium salt is 8 to 10 parts by weight,
The content of hydrogen peroxide (H 2 O 2 ) is 5 to 8 parts by weight of the aqueous coating solution composition. 제 1 항에 있어서, 상기 제3 아크릴 에멀젼에서,
물의 함량은 80∼100 중량부이고,
스타이렌(styrene)의 함량은 70∼80부 중량부이고,
부타디엔(butadiene)의 함량은 10∼15 중량부이고,
올레인산나트륨(sodium oleate)의 함량은 1∼3 중량부이고,
과황산칼륨(K2S2O8)의 함량은 1∼2 중량부이고,
인산나트륨(sodium phosphate)의 함량은 0.1∼0.3 중량부이고,
도데실메르캅탄(dodecyl mercaptan)의 함량은 0.1∼0.3 중량부인 수성 코팅액 조성물. The method of claim 1, wherein in the third acrylic emulsion,
The content of water is 80 to 100 parts by weight,
The content of styrene is 70 to 80 parts by weight,
The content of butadiene is 10 to 15 parts by weight,
The content of sodium oleate is 1 to 3 parts by weight,
The content of potassium persulfate (K 2 S 2 O 8 ) is 1 to 2 parts by weight,
The content of sodium phosphate is 0.1 to 0.3 parts by weight,
The content of dodecyl mercaptan (dodecyl mercaptan) is an aqueous coating solution composition of 0.1 to 0.3 parts by weight. 제 1 항에 있어서, 상기 수성 코팅액 조성물에서,
상기 제1 아크릴 에멀젼의 함량은 15∼20 중량부이고,
상기 제2 아크릴 에멀젼의 함량은 60∼70 중량부이고,
상기 제3 아크릴 에멀젼의 함량은 10∼15 중량부인 수성 코팅액 조성물. The method of claim 1, wherein in the aqueous coating solution composition,
The content of the first acrylic emulsion is 15 to 20 parts by weight,
The content of the second acrylic emulsion is 60 to 70 parts by weight,
The content of the third acrylic emulsion is 10 to 15 parts by weight of the aqueous coating solution composition. 제 1 항에 있어서,
상기 접착성 물질은 메틸 메타크릴레이트(methyl methacrylate)(MMA)를 포함하는 수성 코팅액 조성물. The method of claim 1,
The adhesive material is an aqueous coating solution composition comprising methyl methacrylate (MMA). 제 1 항에 있어서,
상기 첨가제는 탈포제(deformer agent) 및 소포제(antifoaming agent) 중 적어도 하나를 포함하는 수성 코팅액 조성물. The method of claim 1,
The additive is an aqueous coating solution composition comprising at least one of a defoaming agent and an antifoaming agent. 제 7 항에 있어서,
상기 소포제는 폴리디메틸실록산(polydimethylsiloxane)(PDMS)을 포함하는 수성 코팅액 조성물. 8. The method of claim 7,
The antifoaming agent is an aqueous coating solution composition comprising polydimethylsiloxane (PDMS). 피코팅 부재; 및
상기 피코팅 부재의 표면에 청구항 1 내지 8 중 어느 한 항의 수성 코팅액 조성물을 코팅하여 형성한 코팅층;을 포함하는, 코팅층 적용 부재. a member to be coated; and
A coating layer application member comprising a; a coating layer formed by coating the aqueous coating solution composition of any one of claims 1 to 8 on the surface of the member to be coated. 제 9 항에 있어서,
상기 코팅층은 methacrylic acid copolymer, acrylic acid ester copolymer 및 styrene-butadiene copolymer를 포함하는 코팅층 적용 부재. 10. The method of claim 9,
The coating layer is a coating layer application member comprising a methacrylic acid copolymer, an acrylic acid ester copolymer, and a styrene-butadiene copolymer. 제 9 항에 있어서,
상기 피코팅 부재는 종이류, 목재류 또는 패브릭류인 코팅층 적용 부재. 10. The method of claim 9,
The member to be coated is a member for applying a coating layer of paper, wood or fabric.
KR1020210157053A 2021-11-15 2021-11-15 Multifunctional eco-friendly aqueous coating solution composition and coating layer application member applying the same KR102380235B1 (en)