KR102331819B1 - Lacquer printed film, base material with the film and method for producing the film - Google Patents

Lacquer printed film, base material with the film and method for producing the film Download PDF

Info

Publication number
KR102331819B1
KR102331819B1 KR1020190143291A KR20190143291A KR102331819B1 KR 102331819 B1 KR102331819 B1 KR 102331819B1 KR 1020190143291 A KR1020190143291 A KR 1020190143291A KR 20190143291 A KR20190143291 A KR 20190143291A KR 102331819 B1 KR102331819 B1 KR 102331819B1
Authority
KR
South Korea
Prior art keywords
lacquer
film
printed
base material
flexible film
Prior art date
Application number
KR1020190143291A
Other languages
Korean (ko)
Other versions
KR20210056614A (en
Inventor
허동규
Original Assignee
(주)머티리얼앤디자인
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)머티리얼앤디자인 filed Critical (주)머티리얼앤디자인
Priority to KR1020190143291A priority Critical patent/KR102331819B1/en
Publication of KR20210056614A publication Critical patent/KR20210056614A/en
Application granted granted Critical
Publication of KR102331819B1 publication Critical patent/KR102331819B1/en

Abstract

본 발명은 옻이 인쇄된 필름 및 그 필름이 부착된 모재 및 그 필름의 제조방법에 관한 것으로서, 정제된 옻칠을 가용성 필름 상에 인쇄함으로써 옻이 인쇄된 필름을 제공하는 옻이 인쇄된 필름 및 그 필름이 부착된 모재 및 그 필름의 제조방법에 관한 것이다. The present invention relates to a film printed with lacquer, a base material to which the film is attached, and a method for manufacturing the film, wherein the film and the film printed with lacquer to provide a film with lacquer by printing purified lacquer on a soluble film It relates to a base material to which a film is attached and a method for manufacturing the film.

Description

옻이 인쇄된 필름 및 그 필름이 부착된 모재 및 그 필름의 제조방법{LACQUER PRINTED FILM, BASE MATERIAL WITH THE FILM AND METHOD FOR PRODUCING THE FILM}Lacquer printed film, base material to which the film is attached, and method for manufacturing the film

본 발명은 가요성 필름 상에 정제된 옻칠이 인쇄된 옻이 인쇄된 필름 및 그 필름이 부착된 모재 및 그 필름의 제조방법에 관한 것이다.The present invention relates to a film on which purified lacquer is printed on a flexible film, a film on which the lacquer is printed, a base material to which the film is attached, and a method for manufacturing the film.

옻나무의 표피에 상처를 내면 회백색의 칠액이 나오는데, 칠액은 그대로 또는 가공된 액상옻으로 각종 생활제품의 외면에 도포 및 건조('옻칠'이라 함)되어 사용된다. 칠액은 향균성, 탈취성 및 내구성이 우수하여 제품에 옻칠할 경우 제품의 보전성이 향상된다.When the epidermis of lacquer is injured, a grayish-white lacquer solution is released. The lacquer solution is used as it is or is processed liquid lacquer, applied and dried (called 'lacquer') on the exterior of various household products. The lacquer solution has excellent antibacterial properties, deodorization properties and durability.

이러한 옻칠은 오래전부터 장롱, 상, 그릇 등의 일상생활용품의 제조뿐만 아니라, 문화유산을 제조하는 과정에도 옻칠이 사용되었다. 옻칠에 대한 우수한 특성은 이미 널리 알려져 다양하게 활용되고 있다.Lacquer lacquer has been used not only for the manufacture of daily necessities such as wardrobes, tables, and bowls, but also for the production of cultural heritage from a long time ago. The excellent properties of lacquer are already widely known and are being used in various ways.

이러한 옻칠을 코팅하는 방법으로는 한국등록특허 제10-1935521호(이하, '특허문헌 1'이라 함)에 기재된 것이 공지되어 있다.As a method of coating such lacquer, the one described in Korean Patent No. 10-1935521 (hereinafter referred to as 'Patent Document 1') is known.

특허문헌 1의 경우 금속 재질의 커틀러리의 표면에 옻칠을 직접 도포하여 코팅층을 형성하고 있다.In the case of Patent Document 1, a coating layer is formed by directly applying lacquer on the surface of a metal cutlery.

하지만, 특허문헌 1의 경우 금속 재질이 평면이 아닌 곡선이거나 절곡된 부분에 붓 등을 사용하여 옻칠을 할 경우 건조되는 과정에서 균열이 발생하는 문제점이 있다. However, in the case of Patent Document 1, when lacquering using a brush or the like on a curved or bent metal material rather than a flat surface, there is a problem in that cracks occur during drying.

또한, 금속 재질에 옻칠을 한 후 칠액을 건조하기 위해서는 고온의 열을 가하여 건조시키거나 장시간 자연 건조 시켜야 하는데, 장시간 자연 건조할 경우 내부까지 완전히 건조 되지 않아 제품을 사용하는 사용자가 옻에 의한 알러지가 유발할 수 있다. 또한, 고온의 열을 가할 경우 옻칠의 효능을 상실하는 문제점이 있다. In addition, in order to dry the lacquer solution after lacquering the metal material, it must be dried by applying high-temperature heat or naturally dried for a long time. can cause In addition, there is a problem in that the efficacy of the lacquer is lost when high-temperature heat is applied.

한국등록특허 제10-1935521호Korean Patent No. 10-1935521

본 발명은 전술한 문제를 해결하기 위해 안출된 것으로, 가요성 필름에 정제된 옻칠을 인쇄하여 필름의 형태로 형성함으로써 옻칠을 충분히 건조시켜 제품에 부착하여 사용할 수 있는 옻이 인쇄된 필름 및 그 필름이 부착된 모재 및 그 필름의 제조방법을 제공하는 것을 목적으로 한다. The present invention has been devised to solve the above-mentioned problems, and by printing purified lacquer on a flexible film and forming the film in the form of a film, the lacquer-printed film and the film can be used by attaching the lacquer to the product by drying the lacquer sufficiently. An object of the present invention is to provide an attached base material and a method for manufacturing the film.

본 발명의 일 특징에 따른 옻이 인쇄된 필름의 제조방법은, 가요성 필름을 준비하는 단계; 및 상기 가요성 필름 상에 정제된 옻칠을 인쇄하는 단계;를 포함하는 것을 특징한다. According to one aspect of the present invention, there is provided a method for manufacturing a film printed with lacquer, comprising the steps of: preparing a flexible film; and printing purified lacquer on the flexible film.

또한, 상기 옻이 인쇄된 필름을 모재에 부착하는 단계를 포함하는 것을 특징으로 한다. In addition, it characterized in that it comprises the step of attaching the lacquer printed film to the base material.

본 발명의 일 특징에 따른 옻이 인쇄된 필름은, 가요성 필름; 및 상기 가요성 필름 상에 인쇄되는 정제된 옻칠;을 포함하는 것을 특징으로 한다.The lacquer printed film according to one aspect of the present invention includes a flexible film; and a refined lacquer lacquer printed on the flexible film.

본 발명의 일 특징에 따른 옻이 인쇄된 필름이 부착된 모재는, 모재; 상기 모재에 접찹되는 가요성 필름; 및 상기 가요성 필름상에 인쇄되는 정제된 옻칠;을 포함하는 것을 특징으로 한다.The base material to which the lacquer printed film according to one aspect of the present invention is attached includes: a base material; a flexible film bonded to the base material; and a refined lacquer lacquer printed on the flexible film.

이상에서 설명한 바와 같은 본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름 및 그 필름이 부착된 모재 및 그 필름의 제조방법은 다음과 같은 효과가 있다.The lacquer printed film, the base material to which the film is attached, and the method for manufacturing the film according to the preferred embodiment of the present invention as described above have the following effects.

가용성 필름에 정제된 옻칠을 인쇄하여 충분히 건조시킨 후 필름의 형태로 제작하여 모재에 부착함으로써 누구나 손쉽게 사용할 수 있다는 효과가 있다. By printing purified lacquer on a soluble film and drying it sufficiently, it is produced in the form of a film and attached to the base material, so that anyone can use it easily.

또한, 정제된 옻칠을 필름의 형태로 제작 및 옻이 인쇄된 필름을 모재에 부착할 때, 열을 이용하지 않고 인쇄 및 부착함으로써 옻의 효능을 유지할 수 있다. In addition, when the refined lacquer lacquer is produced in the form of a film and the lacquer printed film is attached to the base material, the efficacy of lacquer can be maintained by printing and attaching without using heat.

또한, 가요성 필름 상에 프라이머층을 형성한 후 정제된 옻칠을 인쇄함으로써 가요성 필름이 휘거나 구겨지더라도 정제된 옻칠이 쉽게 박리되지 않는 효과가 있다. In addition, since the purified lacquer is printed after forming a primer layer on the flexible film, even if the flexible film is bent or crumpled, the purified lacquer is not easily peeled off.

도 1은 본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름의 제조방법.
도 2는 본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름의 사시도.
도 3은 가요성 필름에 프라이머층이 형성된 모습을 나타낸 도.
도 4는 본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름의 단면도.
도 5는 모재에 UV경화층이 형성된 모습을 나타낸 도.
도6 는 옻이 인쇄된 필름이 부착된 모재의 단면도.1 is a method of manufacturing a film printed with lacquer according to a preferred embodiment of the present invention.
Figure 2 is a perspective view of a film printed with lacquer according to a preferred embodiment of the present invention.
3 is a view showing a state in which a primer layer is formed on a flexible film.
4 is a cross-sectional view of a film printed with lacquer according to a preferred embodiment of the present invention.
5 is a view showing a state in which a UV curing layer is formed on the base material.
6 is a cross-sectional view of the base material to which the lacquer printed film is attached.

이하의 내용은 단지 발명의 원리를 예시한다. 그러므로 당업자는 비록 본 명세서에 명확히 설명되거나 도시되지 않았지만 발명의 원리를 구현하고 발명의 개념과 범위에 포함된 다양한 장치를 발명할 수 있는 것이다. 또한, 본 명세서에 열거된 모든 조건부 용어 및 실시 예들은 원칙적으로, 발명의 개념이 이해되도록 하기 위한 목적으로만 명백히 의도되고, 이와 같이 특별히 열거된 실시 예들 및 상태들에 제한적이지 않는 것으로 이해되어야 한다.The following is merely illustrative of the principles of the invention. Therefore, those skilled in the art can devise various devices that, although not explicitly described or shown herein, embody the principles of the invention and are included in the spirit and scope of the invention. In addition, it should be understood that all conditional terms and examples listed herein are, in principle, expressly intended only for the purpose of understanding the inventive concept and are not limited to the specifically enumerated embodiments and states as such. .

상술한 목적, 특징 및 장점은 첨부된 도면과 관련한 다음의 상세한 설명을 통하여 보다 분명해질 것이며, 그에 따라 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명의 기술적 사상을 용이하게 실시할 수 있을 것이다. The above-described objects, features and advantages will become more apparent through the following detailed description in relation to the accompanying drawings, and accordingly, those of ordinary skill in the art to which the invention pertains will be able to easily practice the technical idea of the invention. .

이하, 도 1 내지 도 5을 참고하여 본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름(10) 및 그 필름(10)이 부착된 모재(10) 및 그 필름(10)의 제조방법에 대해 설명한다. Hereinafter, with reference to FIGS. 1 to 5 , the lacquer printed film 10 and the base material 10 to which the film 10 is attached, and a method of manufacturing the film 10 according to a preferred embodiment of the present invention Explain.

본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름(10)은 가요성 필름(120) 및 가요성 필름 상에 인쇄되는 정제된 옻칠(100)을 포함할 수 있다.The film 10 on which the lacquer is printed according to a preferred embodiment of the present invention may include the flexible film 120 and the refined lacquer 100 printed on the flexible film.

가요성 필름(120)은 변형이 자유로운 재질로 이루어질 수 있으며, 가요성 필름(120)은 상부에 프라이머층(110)이 형성될 수 있다. The flexible film 120 may be made of a material freely deformable, and the flexible film 120 may have a primer layer 110 formed thereon.

도 3에 도시된 바와 같이, 가요성 필름(120)은 상부에 프라이머층(110)이 형성될 수 있다. 프라이머층(110)은 가요성 필름(120)과 정제된 옻칠(100) 사이에 형성될 수 있는 것이다. 프라이머층(110)은 정제된 옻칠(100)이 건조될 때 일어날 수 있는 가요성 필름(120)의 변형을 최소화 하는 역할을 한다. 3 , the flexible film 120 may have a primer layer 110 formed thereon. The primer layer 110 may be formed between the flexible film 120 and the refined lacquer 100 . The primer layer 110 serves to minimize deformation of the flexible film 120 that may occur when the refined lacquer 100 is dried.

구체적으로, 도 4에 도시된 바와 같이, 정제된 옻칠(100)은 프라이머층(110)이 형성된 가요성 필름(120) 상에 인쇄될 수 있다. Specifically, as shown in FIG. 4 , the refined lacquer 100 may be printed on the flexible film 120 on which the primer layer 110 is formed.

가요성 필름(120) 상에 인쇄된 정제된 옻칠(100)은 일정시간 건조 시킨 후 사용되는데, 정제된 옻칠(100)이 건조될 때 정제된 옻칠(100)의 내부의 수분이 증발되면서 증발된 체적만큼 수축되는 건조수축 현상이 일어날 수 있다. The purified lacquer 100 printed on the flexible film 120 is used after drying for a certain period of time. Drying shrinkage that shrinks by volume may occur.

건조수축 현상이 일어날 때, 가요성 필름(120)과 정제된 옻칠(100) 사이에 프라이머층(110)이 형성이 되어있지 않다면, 정제된 옻칠(100)이 건조되면서 일어나는 건조수축 현상에 의해 가요성 필름(120) 또한 함께 수축되면서 가요성 필름(120)의 형상이 변화될 수 있다. When the drying shrinkage phenomenon occurs, if the primer layer 110 is not formed between the flexible film 120 and the refined lacquer 100, it becomes flexible due to the drying shrinkage phenomenon that occurs while the refined lacquer 100 is dried. As the flexible film 120 is also contracted together, the shape of the flexible film 120 may be changed.

따라서, 가요성 필름(120)과 정제된 옻칠(110) 사이에 프라이머층(110)을 형성함으로써 정제된 옻칠(100)이 건조 시 발생할 수 있는 가요성 필름(120)의 형상 변형을 최소화 할 수 있는 것이다. 프라이머층(110)은 가요성 필름(120)과 정제된 옻칠(100) 사이에 형성되어 정제된 옻칠(100)이 건조 시 발생하는 건조수축 현상을 완충시켜주는 역할을 하는 것이다. Accordingly, by forming the primer layer 110 between the flexible film 120 and the refined lacquer 110, the shape deformation of the flexible film 120 that may occur when the refined lacquer 100 is dried can be minimized. there will be The primer layer 110 is formed between the flexible film 120 and the refined lacquer 100, and serves to buffer the drying shrinkage that occurs when the refined lacquer 100 is dried.

프라이머층(110)은 우레탄 계열의 재질로 형성하는 것이 바람직하다.The primer layer 110 is preferably formed of a urethane-based material.

정제된 옻칠(100)은 실크 스크린 인쇄 기법을 이용해 가요성 필름(120) 상에 인쇄될 수 있다. 이때, 실크 스크린 인쇄기법은 70℃ 미만의 환경에서 이루어지는 것이 바람직하다.The refined lacquer 100 may be printed on the flexible film 120 using a silk screen printing technique. At this time, it is preferable that the silk screen printing technique be performed in an environment of less than 70°C.

실크 스크린 인쇄 기법은 열을 가하지 않고 가요성 필름(120) 상에 정제된 옻칠(100)을 인쇄할 수 있다. 따라서, 정제된 옻칠(100)은 가요성 필름(120)에 인쇄되더라도 탈취 및 살균 기능을 유지할 수 있게 되는 것이다. The silk screen printing technique can print the refined lacquer 100 on the flexible film 120 without applying heat. Accordingly, the refined lacquer 100 can maintain deodorization and sterilization functions even when printed on the flexible film 120 .

옻이 인쇄된 필름(10)은 냉장고 선반, 김치 냉장고 선반 및 식료품 보관대 등에 부착될 수 있다. 옻이 인쇄된 필름(10)을 부착함으로써 식료품에 의해 발생되는 냄새를 탈취하는 효과와 식료품 보관 시 각종 박테리아 등의 번식을 억제시키는 살균효과 또한 기대할 수 있다.The lacquered film 10 may be attached to a refrigerator shelf, a kimchi refrigerator shelf, a food storage stand, and the like. By attaching the lacquer-printed film 10, an effect of deodorizing odors generated by foodstuffs and a sterilizing effect of suppressing the propagation of various bacteria during storage of foodstuffs can also be expected.

이하, 도 3 내지 도 4를 이용하여 본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름(10)의 제조방법에 대해 설명한다.Hereinafter, a method of manufacturing the lacquer printed film 10 according to a preferred embodiment of the present invention will be described with reference to FIGS. 3 to 4 .

옻이 인쇄된 필름(10)의 제조방법은 가요성 필름(120)을 준비하는 준비단계(S1) 및 가요성 필름(120) 상에 정제된 옻칠(100)을 인쇄하는 인쇄단계(S3)를 포함할 수 있다. The manufacturing method of the lacquer-printed film 10 includes a preparation step (S1) of preparing the flexible film 120 and a printing step (S3) of printing the purified lacquer 100 on the flexible film 120. may include

준비단계(S1)는 정제된 옻칠(100)이 인쇄될 가요성 필름(120)을 준비하는 단계이다. 가요성 필름(120)이 준비되면, 가요성 필름(120) 상에 정제된 옻칠을 인쇄하는 인쇄단계(S3)가 실행되는데, 이때, 가요성 필름(120)의 표면에 프라이머층(110)을 형성하는 프라이머층 형성단계(S2)가 먼저 실행될 수 있다.The preparation step (S1) is a step of preparing the flexible film 120 on which the refined lacquer 100 will be printed. When the flexible film 120 is prepared, a printing step (S3) of printing the purified lacquer on the flexible film 120 is performed. At this time, a primer layer 110 is applied to the surface of the flexible film 120. A primer layer forming step (S2) to form may be performed first.

프라이머층 형성단계(S2)는 가요성 필름(120) 상부에 프라이머층(110)을 형성하는 단계이다.The primer layer forming step S2 is a step of forming the primer layer 110 on the flexible film 120 .

프라이머층 형성단계(S2)는 가요성 필름(120) 상에 정제된 옻칠(100)이 인쇄되기 전에 가요성 필름(120)에 프라이머층(110)을 형성함으로써, 정제된 옻칠(100)이 인쇄된 후 나타날 수 있는 건조 수축에 의한 변형을 완충시켜주는 완충역할을 하게 되는 것이다.In the primer layer forming step (S2), the purified lacquer 100 is printed by forming the primer layer 110 on the flexible film 120 before the purified lacquer 100 is printed on the flexible film 120 . It will serve as a buffer that buffers the deformation caused by drying shrinkage that may occur after drying.

가요성 필름(120)에 프라이머층(110)이 형성되면, 가요성 필름(120)의 표면에 정제된 옻칠(100)을 인쇄하는 인쇄단계(S3)가 실행될 수 있다. When the primer layer 110 is formed on the flexible film 120 , a printing step S3 of printing the purified lacquer 100 on the surface of the flexible film 120 may be performed.

인쇄단계(S3)는 옻 나무에서 추출 후 정제시킨 정제된 옻칠(100)을 가요성 필름(120)에 인쇄하는 단계이다. 인쇄단계(S3)는 실크 스크린 인쇄기법을 이용하여 가요성 필름(120)에 정제된 옻칠(100)을 인쇄할 수 있다. The printing step (S3) is a step of printing the purified lacquer 100, which is extracted and refined from the lacquer tree, on the flexible film 120. In the printing step (S3), the refined lacquer 100 may be printed on the flexible film 120 using a silk screen printing technique.

실크 스크린 기법은 비단 및 화학섬유 등의 천을 팽팽하게 하여 가요성 필름(120)의 상부에 스크린의 형태로 고정하게 된다. 이후 고정된 비단 및 화학섬유의 상부에 정제된 옻칠(100)을 부어 넣은 후 정제된 옻칠(100)이 비단 및 화학섬유의 상부에서 하부로 투과되도록 밀대 또는 롤러를 이용하여 인쇄한다. 투과된 정제된 옻칠(100)은 가요성 필름(120) 상에 인쇄함으로써 옻이 인쇄된 필름(10)이 제작되는 것이다.In the silk screen technique, a fabric such as silk or chemical fiber is taut and fixed on the flexible film 120 in the form of a screen. After that, the purified lacquer 100 is poured on the fixed silk and chemical fibers, and then the refined lacquer 100 is printed using a pusher or roller so that the purified lacquer 100 is transmitted from the top to the bottom of the silk and chemical fibers. The transmitted purified lacquer 100 is printed on the flexible film 120 to produce the lacquer-printed film 10 .

옻이 인쇄된 필름(10)의 제작이 완료되면, 옻이 인쇄된 필름(10)을 모재(200)에 부착하는 부착단계(S4)가 실행될 수 있다.When the production of the lacquer-printed film 10 is completed, an attaching step (S4) of attaching the lacquer-printed film 10 to the base material 200 may be performed.

부착단계(S4)는 옻이 인쇄된 필름(10)과 모재(200)를 부착하는 단계이다. 옻이 인쇄된 필름(10)과 모재(200)는 UV접착제를 이용하여 부착할 수 있다. The attaching step ( S4 ) is a step of attaching the lacquer printed film 10 and the base material 200 . The lacquer-printed film 10 and the base material 200 may be attached using a UV adhesive.

모재(200)의 상면에 UV접착제를 도포한 후 옻이 인쇄된 필름(10)을 부착하게 되는데, 이때, 옻이 인쇄된 필름(10)의 하면과 모재(200)의 상면이 맞닿도록 부착하게 된다. 옻이 인쇄된 필름(10)과 모재(200)가 부착되면, UV를 조사하여 UV접착제를 경화시키고, 경화가 완료되면 UV경화층(130)이 형성됨으로써 옻이 인쇄된 필름(10)과 모재(200)가 완전이 접합될 수 있는 것이다. 따라서, 모재(200)와 가요성 필름(120) 사이에 UV경화층(130)이 형성될 수 있다.After UV adhesive is applied to the upper surface of the base material 200, the lacquer printed film 10 is attached. At this time, the lower surface of the lacquer printed film 10 and the upper surface of the base material 200 are attached to contact do. When the lacquer-printed film 10 and the base material 200 are attached, UV is irradiated to cure the UV adhesive, and when curing is completed, a UV curing layer 130 is formed, thereby forming the lacquer-printed film 10 and the base material. (200) can be completely joined. Accordingly, the UV curing layer 130 may be formed between the base material 200 and the flexible film 120 .

이처럼, 옻이 인쇄된 필름이 부착된 모재(20)는 모재(200)와 모재에 접착되는 가요성 필름(120)과 가요성 필름(120) 상에 인쇄되는 정제된 옻칠(100)을 포함하여 형성될 수 있다. 즉, 옻이 인쇄된 필름이 부착된 모재(20)는 상부에서부터 정제된 옻칠(100), 프라이머층(110), 가요성 필름(120), UV경화층(130) 및 모재(200) 순으로 적층되는 것이다. 모재(200)는 유리, 목재 등의 재질로 이루어질 수 있다.As such, the base material 20 to which the lacquer printed film is attached includes the base material 200, the flexible film 120 adhered to the base material, and the purified lacquer 100 printed on the flexible film 120. can be formed. That is, the base material 20 to which the lacquer-printed film is attached is the lacquer 100, the primer layer 110, the flexible film 120, the UV curing layer 130, and the base material 200 refined from the top in this order. will be stacked. The base material 200 may be made of a material such as glass or wood.

본 발명의 바람직한 실시 예에 따른 옻이 인쇄된 필름(10)은 정제된 옻칠(100)을 가요성 필름(120) 상에 인쇄하여 필름의 형태로 제작하여 정제된 옻칠(100)이 충분히 건조된 후 사용함으로써 전문가가 아니더라도 손쉽게 사용할 수 있다.The film 10 on which the lacquer is printed according to a preferred embodiment of the present invention is manufactured in the form of a film by printing the purified lacquer 100 on the flexible film 120, so that the purified lacquer 100 is sufficiently dried. It can be used easily even by non-professionals by using it afterward.

구체적으로, 옻나무 추출물은 추출물의 성분 중 하나인 우루시올에 의해 사용자에 알러지를 유발시킬 수 있다. 정제된 옻칠(100)은 충분한 건조가 이루어지면 우루시올에 의한 알러지 유발을 최소화할 수 있다. 즉, 정제된 옻칠(100)을 직접 모재(200)에 도포할 경우, 도포 및 건조시키는 과정에서 알러지가 유발될 수 있다는 위험이 있다. 따라서, 가요성 필름(120)에 정제된 옻칠(100)을 인쇄하여 충분히 건조시킨 후 필름의 형태로 제작하여 모재(200)에 부착시킴으로써 누구나 손쉽게 사용할 수 있다는 효과가 있다. Specifically, the sumac extract may cause an allergy in the user by urushiol, which is one of the components of the extract. When the refined lacquer 100 is sufficiently dried, the allergy caused by urushiol can be minimized. That is, when the refined lacquer 100 is directly applied to the base material 200 , there is a risk that an allergy may be induced in the process of application and drying. Therefore, by printing the purified lacquer 100 on the flexible film 120 and drying it sufficiently, it is manufactured in the form of a film and attached to the base material 200 , thereby enabling anyone to easily use it.

또한, 정제된 옻칠(100)을 필름의 형태로 제작 및 옻이 인쇄된 필름(10)을 모재(200)에 부착할 때, 열을 이용하지 않고 인쇄 및 부착함으로써 옻의 효능을 유지할 수 있다. In addition, when the refined lacquer 100 is manufactured in the form of a film and the lacquer-printed film 10 is attached to the base material 200, the efficacy of the lacquer can be maintained by printing and attaching it without using heat.

정제된 옻칠(100)은 탈취기능과 더불어 세균 증식을 억제하는 효능을 가진다. The purified lacquer 100 has a deodorizing function and an effect of inhibiting bacterial growth.

blankblank #1#One

BACTERIA-1

BACTERIA-1 AT BEGINNINGAT BEGINNING 1.5×104 1.5×10 4 1.5×104 1.5×10 4 AFTER 24hAFTER 24h 2.6×104 2.6×10 4 <0.63<0.63 VALUE OF ANTI-MICROBIAL ACTIVITYVALUE OF ANTI-MICROBIAL ACTIVITY -- 4.64.6

BACTERIA-2

BACTERIA-2 AT BEGINNINGAT BEGINNING 1.4×104 1.4×10 4 1.4×104 1.4×10 4 AFTER 24hAFTER 24h 1.1×106 1.1×10 6 1.6×103 1.6×10 3 VALUE OF ANTI-MICROBIAL ACTIVITYVALUE OF ANTI-MICROBIAL ACTIVITY -- 2.82.8

표 1은 정제된 옻칠(100)이 도포된 필름(#1)과 도포되지 않은 필름(blank)에 박테리아를 증식시킨 후 같은 조건에서 24시간이 지난 후 각각의 필름에 박테리아의 개체 수를 관찰한 실험의 결과를 나타낸 것이다. Table 1 shows that the number of bacteria was observed on each film after 24 hours under the same conditions after the bacteria were grown on the film (#1) and the film (blank) not coated with purified lacquer 100. It shows the results of the experiment.

표 1에 명시된 바와 같이, 정제된 옻칠(100)이 도포된 필름에서의 박테리아의 개체수는 줄어든 반면, 정제된 옻칠(100)이 도포되지 않은 필름에서는 박테리아의 개체수가 증가한 것을 알 수 있다. As shown in Table 1, it can be seen that the number of bacteria in the film to which the purified lacquer 100 is applied is decreased, whereas the number of bacteria is increased in the film to which the purified lacquer 100 is not applied.

정제된 옻칠(100)은 70℃ 이상의 열을 받을 경우, 이와 같은 효능을 상실하게 된다. 따라서, 열을 사용하지 않는 인쇄 방법과 부착방법 즉, 실크 스크린 인쇄 방법 및 UV접착제를 경화시켜 부착시키는 방법을 사용하여 정제된 옻칠(100)을 가요성 필름(120) 상에 인쇄하고 옻이 인쇄된 필름(10)을 모재(200)에 부착함으로써 정제된 옻칠(100)의 효능을 유지할 수 있는 것이다.When the refined lacquer 100 is subjected to heat of 70° C. or higher, such efficacy is lost. Therefore, the purified lacquer 100 is printed on the flexible film 120 and the lacquer is printed using a printing method and attachment method that does not use heat, that is, a silk screen printing method and a method of curing and attaching a UV adhesive. It is possible to maintain the efficacy of the refined lacquer 100 by attaching the film 10 to the base material 200 .

또한, 가요성 필름(120) 상에 정제된 옻칠(100)을 인쇄하거나, 옻이 부착된 필름(10)을 모재(20)에 부착 시 열을 가하게 되면, 높은 열에 의해 가요성 필름(120)의 형상이 변화될 수 있다. 가요성 필름(120)이 열에 의해 변형되면, 가요성 필름(120) 상에 인쇄된 정제된 옻칠(100)의 형상 또한 변형될 수 있을 뿐만 아니라, 정제된 옻칠(100)이 가요성 필름(120) 상에서 박리될 수 있다. 따라서, 열을 사용하지 않는 인쇄 방법과 부착방법을 사용함으로써 정제된 옻칠(100)의 형상 및 가요성 필름(120)의 형상 변화 및 박리를 방지함과 동시에 정제된 옻칠(100)의 기능인 탈취 및 향균기능 또한 유지할 수 있는 것이다.In addition, when the refined lacquer 100 is printed on the flexible film 120 or heat is applied when the lacquered film 10 is attached to the base material 20, the flexible film 120 is caused by high heat. shape may be changed. When the flexible film 120 is deformed by heat, the shape of the refined lacquer 100 printed on the flexible film 120 may also be deformed, and the refined lacquer 100 may be transformed into the flexible film 120 . ) can be peeled off. Therefore, by using a printing method and an attachment method that do not use heat, the shape of the refined lacquer 100 and the shape change and peeling of the flexible film 120 are prevented, and at the same time, deodorization and deodorization, which are the functions of the refined lacquer 100, are used. The antibacterial function can also be maintained.

또한, 가요성 필름(120) 상에 프라이머층(110)을 형성한 후 정제된 옻칠(100)을 인쇄함으로써 가요성 필름(120)이 휘거나 구겨지더라도 정제된 옻칠(100)이 쉽게 박리되지 않는 효과가 있다. In addition, by printing the purified lacquer 100 after forming the primer layer 110 on the flexible film 120, even if the flexible film 120 is bent or crumpled, the purified lacquer 100 is not easily peeled off. has no effect.

전술한 바와 같이, 본 발명의 바람직한 실시 예를 참조하여 설명하였지만, 해당기술분야의 당업자는 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 또는 변형하여 실시할 수 있다.As described above, although described with reference to preferred embodiments of the present invention, those skilled in the art can variously modify or modify the present invention within the scope without departing from the spirit and scope of the present invention as set forth in the following claims. can be carried out.

10: 옻이 인쇄된 필름 20: 옻이 인쇄된 필름이 부착된 모재
100: 정제된 옻칠 110: 프라이며층
120: 가요성 필름 130: UV경화층
200: 모재
S1: 준비단계 S2: 프라이머층 형성단계
S3: 인쇄단계 S4: 부착단계10: Lacquer printed film 20: Base material with lacquered printed film attached
100: refined lacquer 110: fry and layer
120: flexible film 130: UV cured layer
200: base material
S1: Preparation step S2: Primer layer forming step
S3: printing step S4: attaching step

Claims (4)

가요성 필름을 준비하는 단계;
상기 가요성 필름의 표면에 프라이머층을 형성하는 단계;
상기 프라이머층이 형성된 가요성 필름의 표면에 실크 스크린 인쇄 기법을 이용하여 정제된 옻칠을 인쇄하는 단계; 및
UV 접착제가 도포된 모재의 상면에 상기 옻이 인쇄된 필름을 부착하는 단계;를 포함하는 것을 특징으로 하는 옻이 인쇄된 필름이 부착된 모재의 제조방법.

preparing a flexible film;
forming a primer layer on the surface of the flexible film;
printing purified lacquer on the surface of the flexible film on which the primer layer is formed using a silk screen printing technique; and
A method of manufacturing a base material to which the lacquer printed film is attached, comprising the step of attaching the lacquer printed film to the upper surface of the base material to which the UV adhesive is applied.

 삭제delete 삭제delete 삭제delete
KR1020190143291A 2019-11-11 2019-11-11 Lacquer printed film, base material with the film and method for producing the film KR102331819B1 (en)