KR101240293B1 - Oriental lacquer applied stent and manufacturing method therefor - Google Patents

Oriental lacquer applied stent and manufacturing method therefor Download PDF

Info

Publication number
KR101240293B1
KR101240293B1 KR1020110029770A KR20110029770A KR101240293B1 KR 101240293 B1 KR101240293 B1 KR 101240293B1 KR 1020110029770 A KR1020110029770 A KR 1020110029770A KR 20110029770 A KR20110029770 A KR 20110029770A KR 101240293 B1 KR101240293 B1 KR 101240293B1
Authority
KR
South Korea
Prior art keywords
lacquer
stent
stent body
medium
manufacturing
Prior art date
Application number
KR1020110029770A
Other languages
Korean (ko)
Other versions
KR20120111345A (en
Inventor
전용복
Original Assignee
전용복
(주)바로크씨앤에프
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 전용복, (주)바로크씨앤에프 filed Critical 전용복
Priority to KR1020110029770A priority Critical patent/KR101240293B1/en
Publication of KR20120111345A publication Critical patent/KR20120111345A/en
Application granted granted Critical
Publication of KR101240293B1 publication Critical patent/KR101240293B1/en

Abstract

본 발명은 옻에 의해 살균력이 부여되어 스텐트에 의한 감염우려가 없고, 천연재료인 옻을 사용함으로서 인체에 무해하며, 또한, 스텐트에 적용된 옻이 탈리될 우려도 없어서 위생적이면서도 안전성이 우수한 옻이 적용된 스텐트 및 그 제조방법에 관한 것으로서, 방사상으로 팽창되는 망상의 원통체인 스텐트바디(10)와, 상기 스텐트바디(10)의 표면에 전체적 또는 부분적으로 형성된 옻층(20)을 포함하여 이루어진 것을 특징으로 한다.In the present invention, sterilization power is given by the lacquer, there is no concern about infection by the stent, and it is harmless to the human body by using the natural lacquer, and there is no fear that the lacquer applied to the stent is detached, so that the lacquer having excellent hygiene and safety is applied. A stent and a method for manufacturing the same, characterized in that it comprises a stent body (10), which is a radially expandable cylindrical body, and a lacquer layer (20) formed in whole or in part on the surface of the stent body (10). .

Description

옻이 적용된 스텐트 및 그 제조방법{Oriental lacquer applied stent and manufacturing method therefor}Lacquer applied stent and manufacturing method thereof {Oriental lacquer applied stent and manufacturing method therefor}

본 발명은 옻이 적용된 스텐트 및 그 제조방법에 관한 것으로서, 옻에 의해 살균력이 부여되어 스텐트에 의한 감염우려가 없고, 천연재료인 옻을 사용함으로서 인체에 무해하며, 또한, 스텐트에 적용된 옻이 탈리될 우려도 없어서 위생적이면서도 안전성이 우수한 옻이 적용된 스텐트 및 그 제조방법에 관한 것이다.
The present invention relates to a stent to which lacquer is applied and a method of manufacturing the same, which is endowed with bactericidal power and is not susceptible to infection by the stent. The present invention relates to a stent to which lacquer is applied which is hygienic and excellent in safety, and a method of manufacturing the same.

옻은 천연수재의 일종으로서 오래 전부터 우리 조상들이 이용하고 있는 도장 재료 중의 하나이다. 이러한 옻은 내산성, 내식성이 우수하며, 내열성, 방수성, 방부성 및 방충성도 우수한 것으로 알려져 있다. 뿐만 아니라, 옻은 전자파를 흡수하며, 항균, 살균성도 가지고, 원적외선도 방사된다. Lacquer is a kind of natural wood, one of the painting materials that our ancestors have been using for a long time. Such lacquer is known to be excellent in acid resistance, corrosion resistance, heat resistance, waterproofing, antiseptic and insect repellent. In addition, lacquer absorbs electromagnetic waves, has antibacterial and bactericidal properties, and emits far infrared rays.

또한, 동의보감과 방약합편에는 마른 옻은 성질이 따뜻하고, 어혈을 풀어준다고 기록되어 있으며, 최근에는 옻의 우루시올이 항암효과를 가지는 것으로 보고되고 있다. In addition, dry lacquer has been recorded in Dongbobom and medicinal plywood, which is warm in nature and releases blood, and recently, urushiol of lacquer has been reported to have anticancer effect.

한편, 의료용 스텐트는 질병이나 외상, 수술 등으로 인하여 통로가 협착된 인체 내강(內腔)의 환부를 원래의 상태로 확장하기 위한 목적으로 사용된다. 이러한 스텐트는 초탄성 형상기억합금 와이어나 스텐인레스 와이어를 교차되게 엮어서 제조된 원형의 금속망으로 이루어지는데, 인체에 삽입되어 반경반향으로 확경되면서 협착된 부위를 원래의 상태로 확장시킨다. On the other hand, the medical stent is used for the purpose of expanding the affected part of the human lumen (i) where the passage is narrowed due to disease, trauma, surgery and the like. The stent is made of a circular metal mesh fabricated by interlacing superelastic shape memory alloy wires or stainless steel wires. The stent is inserted into a human body and is enlarged in a radial direction to expand the constricted portion to its original state.

이러한 스텐트는 인체에 삽입되는 것이므로 스텐트를 통해 감염의 위험이 없어야 한다. 따라서 스텐트를 인체에 시술하기 전에 스텐트를 멸균처리하기는 하나, 스텐트에 의해 감염되는 사례가 발생되고 있으며, 스텐트에 의해 염증이 발생되기도 한다.
Since the stent is inserted into the human body, there should be no risk of infection through the stent. Therefore, although the stent is sterilized before the stent is put on the human body, there are cases of infection by the stent, and inflammation may be caused by the stent.

본 발명은 상기의 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 천연재료인 옻에 의해 살균력이 부여되므로 스텐트에 의한 감염우려가 없을 뿐만 아니라 인체에도 무해하며, 옻에 의한 추가적인 효과도 얻을 수 있고, 또한, 스텐트에 옻이 견고하게 부착되어 옻이 탈리될 우려도 없어서 위생적이면서도 안전성이 우수한 옻이 적용된 스텐트 및 그 제조방법을 제공하는 것이다.
The present invention is to solve the above problems, the object of the present invention is because the bactericidal power is given by the natural material of lacquer is not only harmful to the stent, but also harmless to the human body, it is possible to obtain additional effects by the lacquer In addition, it is to provide a stent and a method of manufacturing the same is applied lacquer is excellent hygiene and safety because there is no fear that the lacquer is firmly attached to the stent to remove the lacquer.

본 발명에 일 특징에 따르면, 방사상으로 팽창되는 망상의 원통체인 스텐트바디(10)와, 상기 스텐트바디(10)의 표면에 전체적 또는 부분적으로 형성된 옻층(20)을 포함하여 이루어진 것을 특징으로 하는 옻이 적용된 스텐트(30)가 제공된다.
According to one feature of the present invention, a lacquer characterized in that it comprises a stent body (10), which is a radially expanded network cylinder, and a lacquer layer (20) formed in whole or in part on the surface of the stent body (10) This applied stent 30 is provided.

본 발명의 다른 특징에 따르면, 상기 옻층(20)에는 은분말이 부착 또는 함유된 것을 특징으로 하는 옻이 적용된 스텐트(30)가 제공된다.
According to another feature of the invention, the lacquer layer 20 is provided with a stent 30 is applied lacquer, characterized in that the silver powder is attached or contained.

본 발명의 또 다른 특징에 따르면, 금속와이어를 교차시켜 방사상으로 팽창되도록 형성된 원통체형상의 스텐트바디(10)를 준비하는 스텐트바디준비단계와, According to another feature of the present invention, the stent body preparing step of preparing a cylindrical stent body 10 formed to cross the metal wire to be expanded radially,

요철면이 형성된 매개물(2)의 요철면에 옻을 칠하는 매개물옻칠단계와, A medium lacquer step of lacquering the uneven surface of the medium (2) on which the uneven surface is formed,

상기 스텐트바디(10)를 상기 매개물(2)에 접촉시켜 매개물(2)에 칠해진 옻을 스텐트바디(10)에 묻혀서 전이시키는 옻전이단계와, A lacquer transition step in which the stent body 10 is contacted with the medium 2 to bury the lacquer coated on the medium 2 on the stent body 10 to transfer the stent body 10;

옻이 전이된 상기 스텐트바디(10)를 가열하여 스텐트바디(10)에 전이된 옻을 경화시키는 경화단계를 포함하여 이루어진 것을 특징으로 하는 옻이 적용된 스텐트 제조방법이 제공된다.
Provided is a method for producing a stent with lacquer, comprising a curing step of curing the lacquer transferred to the stent body 10 by heating the stent body 10 to which the lacquer is transferred.

본 발명의 또 다른 특징에 따르면, 상기 옻전이단계 전에 상기 스텐트바디(10)를 옻액에 침지시키는 옻액침지단계가 추가된 것을 특징으로 하는 옻이 적용된 스텐트 제조방법이 제공된다.
According to another feature of the present invention, a lacquer applied stent manufacturing method is provided, characterized in that the lacquer immersion step of immersing the stent body 10 in the lacquer liquid before the lacquer transition step.

본 발명의 또 다른 특징에 따르면, 상기 경화단계에서는 스텐트바디(10)를 길이방향으로 신축시키면서 경화시키는 것을 특징으로 하는 옻이 적용된 스텐트 제조방법이 제공된다.
According to another feature of the present invention, in the curing step is provided a stent manufacturing method is applied lacquer, characterized in that while curing the stent body 10 in the longitudinal direction.

이상과 같은 구성을 가지는 본 발명은 스텐트(30)에 옻층(20)이 형성되어 옻에 의한 살균력이 부여된다. 따라서 본 발명에 의한 스텐트(30)는 인체에 시술 후 감염위험에 없다. 또한, 천연소재인 옻이 사용되기 때문에 인체에 무해할 뿐만 아니라 옻의 응혈방지기능과, 항암기능 등에 의한 효과도 얻을 수 있다. 특히, 옻의 응혈방지기능에 의해 스텐트(30)에 피가 응고되어 부착되는 방지되므로, 스텐트(30)에 혈액이 응고되어 부착됨에 따른 문제발생 가능성이 저하된다. In the present invention having the above configuration, a lacquer layer 20 is formed on the stent 30 to impart sterilizing power by lacquer. Therefore, the stent 30 according to the present invention is not at risk of infection after the procedure in the human body. In addition, since natural lacquer is used, not only is it harmless to the human body, but also anticoagulant and anticancer effect can be obtained. In particular, since the blood is prevented from coagulating and adhered to the stent 30 by the anticoagulant function of lacquer, the possibility of a problem due to coagulation and attachment of blood to the stent 30 is reduced.

특히, 본 발명은 스텐트바디(10)에 직접 옻을 칠하지 않고 매개물을 통해 스텐트에 옻을 부착시키는 간접적인 방법으로 스텐트바디(10)에 옻을 부착시킴으로써, 스텐트바디(10)에 부분적으로 옻층(20)이 형성되도록 한다. 스텐트바디(10) 전체에 연속적인 옻층(20)이 형성되면, 스텐트가 변형되는 과정에서 옻층(20)에 크랙이 발생되어 옻이 쪼개지면서 스텐트바디(10)에서 탈리될 우려가 높은데, 전술한 바와 같이, 매개물을 통해 스텐트바디(10)에 부분적인 옻층(20)을 형성함으로써 이러한 문제의 발생소지를 없앤 것이다. In particular, the present invention by attaching the lacquer to the stent body 10 in an indirect way to attach the lacquer to the stent through the medium without applying lacquer directly to the stent body (10), partially to the stent body (10) 20) is formed. If a continuous lacquer layer 20 is formed on the entire stent body 10, cracks are generated in the lactating layer 20 during the process of deforming the stent, and there is a high possibility of detachment from the stent body 10 due to splitting of the lacquer. As such, by forming a partial lacquer layer 20 on the stent body 10 through the medium, this problem is eliminated.

또한, 본 발명은 스텐트바디(10)에 옻을 부착시키기 전에 스텐트바디(10)를 옻액에 침지시켜 옻액이 스텐트바디(10) 표면으로 침투되도록 함으로써, 이후 과정에서 옻과 스텐트바디의 부착성을 향상시키고, 아울러 옻을 고온경화시킴으로써, 옻과 스텐트바디(10)의 부착성이 한층 더 향상되도록 한다. 뿐만 아니라 옻을 경화시키는 과정에서 스텐트바디(10)를 신축시키면서 고온경화시킴으로써, 스텐트의 변형을 옻이 수용하여 경화되도록 하는데, 이 또한, 스텐트(30)가 인체에 시술되어 변형되는 과정에서 옻이 탈리되는 것을 방지하기 위한 것이다. In addition, the present invention is to immerse the stent body 10 in the lacquer liquid before adhering the lacquer to the stent body 10 so that the lacquer liquid penetrates into the surface of the stent body 10, the adhesion between the lacquer and the stent body in the subsequent process In addition, by further curing the lacquer at a high temperature, the adhesion between the lacquer and the stent body 10 is further improved. In addition, by curing the stent body (10) at high temperature while curing the lacquer, the deformation of the stent is accommodated by the lacquer to be cured. Also, in the process of deforming the stent (30) to the human body, This is to prevent detachment.

또, 옻층에 은분말이 부착되거나 함유되면 옻의 살균력에 은의 살균력이 더해져서 스텐트의 살균력이 한층 더 향상된다.
Moreover, when silver powder adheres or contains in a lacquer layer, the sterilizing power of silver is added to the sterilizing power of a lacquer, and the sterilizing power of a stent is further improved.

도 1은 본 발명의 일 실시예에 의한 스텐트의 정면도
도 2는 본 발명의 상기 스텐트의 제조공정도
1 is a front view of a stent according to an embodiment of the present invention
Figure 2 is a manufacturing process of the stent of the present invention

이하에서 도면을 참조하여 본 발명의 바람직한 실시예를 설명한다. 도 1은 본 발명의 일 실시예에 따른 스텐트를 보인 것이다. Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings. 1 shows a stent according to an embodiment of the present invention.

도시된 바와 같이, 본 발명은 인체 시술용 스텐트(30)로서, 스텐트바디(10)와, 이 스텐트바디(10)의 표면에 형성된 옻층(20)을 포함하여 이루어진다. As shown, the present invention comprises a stent body 10, the stent body 10, and a lacquer layer 20 formed on the surface of the stent body 10.

상기 스텐트바디(10)는 초탄성 형상기억합금 와이어나 스텐인레스 와이어를 교차되게 엮어서 마름모형상의 중공을 가지는 원통형 금속망으로 이루어진다. 이러한 스텐트바디(10)를 길이방향으로 신장시키면 폭이 축경되고, 길이방향으로 신장시키는 외력을 제거하면 폭이 초기의 상태로 확경된다. The stent body 10 is made of a cylindrical metal mesh having a rhombus hollow by interweaving superelastic shape memory alloy wire or stainless steel wire. When the stent body 10 is elongated in the longitudinal direction, the width is reduced, and when the stent body 10 is removed, the width is reduced to the initial state.

이러한 스텐트바디(10)의 표면에는 옻층(20)이 형성된다. 상기 옻층(20)은 스텐트바디(10) 전체에 연속적으로 형성될 수도 있으나, 바람직하게는 스텐트바디(10)에 부분적으로 형성된다. 옻층(20)이 스텐트바디(10) 전체에 연속적으로 형성되면 스텐트가 신축 변형되는 과정에서 옻층(20)에 크랙이 발생되고 스텐트바디(10)와 옻층(20)의 변형력 차이에 의해 옻이 스텐트바디(10)에서 탈리될 가능성이 상승되는데, 옻층(20)이 부분적으로 형성되면 이러한 우려가 저하된다. The lacquer layer 20 is formed on the surface of the stent body 10. The lacquer layer 20 may be continuously formed throughout the stent body 10, but is preferably partially formed in the stent body 10. When the lacquer layer 20 is continuously formed in the entire stent body 10, cracks are generated in the lacquer layer 20 during the process of stretching and deforming the stent, and lacquer stents are caused by the difference in the deformation force between the stent body 10 and the lacquer layer 20. The likelihood of detachment from the body 10 is increased, and this concern is lowered if the lacquer layer 20 is partially formed.

바람직하게는 이러한 옻층(20)은 7~8㎛ 정도의 두께로 형성된다.Preferably such lacquer layer 20 is formed to a thickness of about 7 ~ 8㎛.

이와 같이 스텐트바디(10)에 옻층(20)이 형성되면, 옻에 의해 스텐트에 살균력이 부여될 뿐만 아니라 옻이 응혈방지기능에 의해 스텐트에 묻은 피가 응고되어 이에 따라 추가적인 문제가 발생되는 것이 방지되며, 옻에 함유된 우루시올에 의한 항암효과도 얻을 수 있다. 또한, 스텐트 시술부위에 염증이 발생되는 것이 방지되고, 염증이 발생되더라도 옻에서 방사되는 원적외선이나 기타 옻의 효능에 의해 염증치료가 촉진된다.When the lacquer layer 20 is formed on the stent body 10 as described above, sterilization power is applied to the stent by the lacquer, and the blood is solidified on the stent by the anticoagulant function, thereby preventing additional problems from occurring. Also, anticancer effect by urushiol contained in the lacquer can be obtained. In addition, inflammation is prevented from occurring in the stent site, and inflammation is promoted by the effect of far-infrared rays or other lacquer radiated from the lacquer even when the inflammation occurs.

이러한 구성을 갖는 본 발명은 다음과 같은 방법으로 제조된다. This invention which has such a structure is manufactured by the following method.

먼저, 스텐트바디(10)를 준비한 후, 세척하여 표면에 묻은 이물질을 제거한다. 이어서 스텐트바디(10)를 72시간 정도 옻액에 침지시킨다. 스텐트바디(10)를 옻액에 침지시켜 두면, 옻액이 스텐트바디(10) 표면에 침투되어 후술하는 과정에서 스텐트바디(10)에 전이된 옻과 스텐트바디(10)의 접착력이 향상된다.First, after preparing the stent body 10, by washing to remove the foreign matter on the surface. Subsequently, the stent body 10 is immersed in lacquer liquid for about 72 hours. When the stent body 10 is immersed in the lacquer liquid, the adhesion of the lacquer and the stent body 10 transferred to the stent body 10 in the process described later, the lacquer liquid penetrates the surface of the stent body 10.

한편, 이와는 별도로 요철면을 갖는 매개물(2)을 준비하고, 매개물(2)의 요철면에 옻을 칠하여 옻층(4)을 형성한다. 요철면을 갖는 매개물(2)로는 직물이나 편물과 같은 천이나, 종이, 또는 요철면을 갖도록 성형된 사출물 등이 사용된다. 바람직하게는 매개물로는 천이 사용되는데, 특히 바람직하게는 실크가 사용된다.On the other hand, separately, the intermediate 2 having the uneven surface is prepared, and lacquer is applied to the uneven surface of the intermediate 2 to form the lacquer layer 4. As the medium 2 having an uneven surface, a cloth such as woven or knitted fabric, a paper, or an injection molded molded to have an uneven surface is used. Preferably, cloth is used as the medium, particularly preferably silk.

이어서 매개물(2)에 칠해진 옻층(4)이 경화되기 전에 상기 스텐트바디(10)를 매개물(2)에 접촉시켜 매개물(2)에 칠해진 옻을 스텐트바디(10)에 전이시킨다. 구체적으로는 스텐트바디(10)를 매개물 표면에 굴린다. 이와 같이 하면 매개물(2)에 칠해진 옻이 스텐트바디(10)에 묻어서 전이되는데, 매개물(2)의 옻이 칠해진 면이 고른 평면이 아니고 요철면이기 때문에 스텐트바디(10)에 고르게 옻이 묻지 못하고, 부분적으로 묻게 되어 부분적인 옻층(20)이 형성된다. Then, before the lacquer layer 4 painted on the medium 2 is cured, the stent body 10 is contacted with the medium 2 to transfer the lacquer painted on the medium 2 to the stent body 10. Specifically, the stent body 10 is rolled on the medium surface. In this way, the lacquer coated on the medium 2 is buried and transferred to the stent body 10. Since the lacquered surface of the medium 2 is not an even plane but an uneven surface, lacquer is not evenly applied to the stent body 10. Partially buried, the partial lacquer layer 20 is formed.

이와 같이 처리한 다음, 옻이 묻은 스텐트바디(10)를 가열하여 옻을 경화시킨다. 옻을 자연경화시킬 수도 있으나, 이와 같이 하면, 경화에 상당히 장시간이 소요되어 생산성이 저하된다. 따라서 옻을 가열하여 고온에서 경화시키면 경화시간이 단축되어 생산성이 향상될 뿐만 아니라 옻과 스텐트바디(10)의 부착력도 향상된다. 바람직하게는 280~300℃에서 25~30분 정도 경화시킨다. After this treatment, the lacquered stent body 10 is heated to cure the lacquer. Although lacquer can also be hardened naturally, in this case, it will take a very long time to harden and productivity will fall. Therefore, when heating and curing the lacquer at a high temperature, the curing time is shortened to improve productivity as well as to improve adhesion of the lacquer and the stent body 10. Preferably it hardens about 25 to 30 minutes at 280-300 degreeC.

바람직하게는 스텐트바디(10)를 신축시키면서 경화시킨다. 이는 스텐트바디(10)의 변형력을 옻이 수용하여 경화됨으로써, 스텐트(30)가 인체에 시술되어 변형되더라도 옻이 탈락되지 않도록 하기 위한 것이며, 아울러 상대적으로 약하게 부착된 옻을 미리 탈락시키기 위한 것이다. Preferably, the stent body 10 is cured while stretching. This is to prevent the lacquer from falling off even if the stent 30 is deformed and cured by the lacquer to accommodate the deformation force of the stent body 10, and also to pre-drop the relatively weakly attached lacquer in advance.

한편, 필요에 따라서는 옻층(20)에 은분말을 부착 또는 함유시킬 수도 있다. 이는 옻의 살균력에 은의 살균력이 더해져서 스텐트(30)가 한층 더 우수한 살균력을 갖도록 하기 위한 것인데, 매개물에 은분말이 함유된 옻을 칠하여 옻층(20)에 은이 함유되도록 하거나 또는 옻층(20)에 은분말을 부착시킬 수도 있다. 이 경우에는 옻을 스텐트바디(10)에 전이시킨 다음, 스텐트바디(10)에 은분말을 묻혀서 경화시킨다. In addition, silver powder may be adhered or contained in the lacquer layer 20 as needed. This is to add the sterilization power of the silver to the sterilization power of the lacquer so that the stent 30 has a more excellent sterilizing power, by applying lacquer containing silver powder to the medium so that the lacquer layer 20 contains silver or silver powder in the lacquer layer 20 You can also attach a horse. In this case, the lacquer is transferred to the stent body 10, and then hardened by applying a silver powder to the stent body 10.

Claims (5)

삭제delete 삭제delete 금속와이어를 교차시켜 방사상으로 팽창되도록 형성된 원통체형상의 스텐트바디(10)를 준비하는 스텐트바디준비단계와,
요철면이 형성된 매개물(2)의 요철면에 옻을 칠하는 매개물옻칠단계와,
상기 스텐트바디(10)를 상기 매개물(2)에 접촉시켜 매개물(2)에 칠해진 옻을 스텐트바디(10)에 묻혀서 전이시키는 옻전이단계와,
옻이 전이된 상기 스텐트바디(10)를 가열하여 스텐트바디(10)에 전이된 옻을 경화시키는 경화단계를 포함하여 이루어진 것을 특징으로 하는 옻이 적용된 스텐트 제조방법.
A stent body preparation step of preparing a cylindrical stent body (10) formed so as to cross the metal wire and expand radially,
A medium lacquer step of lacquering the uneven surface of the medium (2) on which the uneven surface is formed,
A lacquer transition step in which the stent body 10 is contacted with the medium 2 to bury the lacquer coated on the medium 2 on the stent body 10 to transfer the stent body 10;
Lacquer applied stent manufacturing method characterized in that it comprises a curing step of curing the lacquer transferred to the stent body (10) by heating the stent body (10).
제3항에 있어서, 상기 옻전이단계 전에 상기 스텐트바디(10)를 옻액에 침지시키는 옻액침지단계가 추가된 것을 특징으로 하는 옻이 적용된 스텐트 제조방법. 4. The method of claim 3, wherein a lacquer immersion step of immersing the stent body (10) in a lacquer solution is added before the lacquer transition step. 제3항에 있어서, 상기 경화단계에서는 스텐트바디(10)를 길이방향으로 신축시키면서 경화시키는 것을 특징으로 하는 옻이 적용된 스텐트 제조방법.4. The method of claim 3, wherein in the curing step, the stent body 10 is stretched and cured while stretching in the longitudinal direction.
KR1020110029770A 2011-03-31 2011-03-31 Oriental lacquer applied stent and manufacturing method therefor KR101240293B1 (en)