KR102318566B1 - Method of manufacturing formwark tie for building and formwark tie for building manufactured by using the same - Google Patents

Method of manufacturing formwark tie for building and formwark tie for building manufactured by using the same Download PDF

Info

Publication number
KR102318566B1
KR102318566B1 KR1020200092857A KR20200092857A KR102318566B1 KR 102318566 B1 KR102318566 B1 KR 102318566B1 KR 1020200092857 A KR1020200092857 A KR 1020200092857A KR 20200092857 A KR20200092857 A KR 20200092857A KR 102318566 B1 KR102318566 B1 KR 102318566B1
Authority
KR
South Korea
Prior art keywords
form tie
construction
tie
reinforcing fiber
laminate
Prior art date
Application number
KR1020200092857A
Other languages
Korean (ko)
Inventor
강규채
Original Assignee
(주) 태광아이티씨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 태광아이티씨 filed Critical (주) 태광아이티씨
Priority to KR1020200092857A priority Critical patent/KR102318566B1/en
Application granted granted Critical
Publication of KR102318566B1 publication Critical patent/KR102318566B1/en

Abstract

The present invention provides a method for manufacturing a form tie for building. A method for manufacturing a form tie for building according to the present invention comprises the steps of: preparing reinforcing fiber arrays; preparing a matrix type prepreg by impregnating the reinforcing fiber arrays with a resin; preparing a laminate by laminating a plurality of prepregs; and forming a laminate by applying heat to the laminate and compressing a mold. Although weight reduction has been realized, the form tie for building manufactured by the manufacturing method shows high strength properties, and exhibits outstanding formability and workability due to an integrated structure thereof.

Description

건축용 폼타이의 제조방법 이에 의하여 제조된 건축용 폼타이{METHOD OF MANUFACTURING FORMWARK TIE FOR BUILDING AND FORMWARK TIE FOR BUILDING MANUFACTURED BY USING THE SAME} Architectural form tie manufactured by the manufacturing method

본 기술은 건축 시공시 사용되는 구조용 부품 분야의 기술로서, 구체적으로는 콘크리트 내벽과 외벽을 연결하는 구조용 부품인 폼타이의에 제조기술에 관한 것이다. This technology is a technology in the field of structural parts used during construction, and more specifically, it relates to a manufacturing technology of a form tie, a structural part that connects the concrete inner wall and the outer wall.

통상적으로 폼타이라는 건축용 부품은 콘크리트 시공에서 거푸집을 정확한 치수로 시공하기 위하여 사용하는 조임용 부품이다. 거푸집의 일정한 간격을 유지시키는 세퍼레이터의 역할도 수행하는 각종 철선, 꺽쇠, 볼트 등을 통틀어 포함하는 부품 용어이기도 하다. Typically, a building part called a form tie is a fastening part used to construct a formwork with accurate dimensions in concrete construction. It is also a term for parts that includes various iron wires, clamps, bolts, etc. that also play the role of a separator that maintains a constant interval of the formwork.

도 1은 종래 폼타이의 사용예를 설명하기 위한 예시 도면이다. 도 1을 참조하면, 도 1에서 사각 테두리 내의 부품이 폼타이에 대응한다. 도 1에서 보는 바와 같이 폼타이는 벽체 간의 거리유지 및 고정을 위하여 사용되며, 도 1에서 보는 바와 같이 벽체를 관통하는 구조의 폼타이가 일반적이며, 이와 다르게 관통하지 않는 형태의 폼타이도 사용되고 있다. 1 is an exemplary view for explaining an example of using a conventional form tie. Referring to FIG. 1 , in FIG. 1 , a component within a rectangular frame corresponds to a form tie. As shown in FIG. 1, the form tie is used for maintaining and fixing the distance between the walls, and as shown in FIG. 1, a form tie having a structure that penetrates the wall is common, and a form tie of a form that does not penetrate differently is also used. .

이와 같이 상기 폼타이는 벽체간의 형태 유지 및 내구성 측면에서 매우 중요한 건축용 부품이며, 폼타이의 강도 및 치수 정확성은 건축물의 골격의 품질을 좌우하는 중요 인자로 작용한다. As such, the form tie is a very important building component in terms of maintaining the shape and durability between the walls, and the strength and dimensional accuracy of the form tie act as important factors influencing the quality of the skeleton of the building.

따라서 상기 폼타이는 시공 후 파손, 변형 등 시공 분량이 발생하지 않도록 높은 인장강도를 가져야 하며 중단열 벽면체 시공 후, 폼타이의 변형, 부식으로 인한 건축물 안정성 저하 방지를 위하여 높은 굴곡 강도도 요구된다. 나아가 상기 폼타이 제조 기술분야에서는 건축물 시공 비용 절감을 위하여 원가 절감 및 경량화 이슈도 최근에는 중요하게 대두되고 있다.Therefore, the form tie must have high tensile strength so that the amount of construction such as breakage and deformation does not occur after construction, and high flexural strength is also required to prevent deterioration of the building stability due to deformation and corrosion of the form tie after the construction of the middle and middle row wall body. . Furthermore, in the field of the form tie manufacturing technology, cost reduction and weight reduction issues have recently emerged as important in order to reduce building construction costs.

도 2는 각각 국내형 폼타이와 외국형 폼타이를 예시한 도면이다. 도 2를 참조하면, 국내 기술의 폼타이로서는 폼타이 양 끝단에 철근을 장입하여 내외부 벽면을 연결하는 타입이 주료 개발되어 있다. 이러한 폼타이는 철근 사용을 통하여 단가 및 시공비용을 절감할 수 있고 사출 성형으로 대량 생산이 가능한 장점을 갖기 때문이다. 그러나 상기 국내형 폼타이는 철근 사용으로 부식에 취약하고 외국 제품에 비하여 상대적으로 단열성이 취약한 측면이 있다. 나아가 철근의 높은 비중으로 인하여 벽면 무게가 증가되는 문제점이 있다. 2 is a view illustrating a domestic type form tie and a foreign type form tie, respectively. Referring to FIG. 2 , as a form tie of domestic technology, a type in which reinforcing bars are charged at both ends of the form tie to connect the inner and outer walls have been mainly developed. This is because the form tie can reduce unit cost and construction cost through the use of reinforcing bars, and has the advantage of being able to mass-produce by injection molding. However, the domestic form tie is vulnerable to corrosion due to the use of reinforcing bars and has relatively weak insulation properties compared to foreign products. Furthermore, there is a problem in that the weight of the wall increases due to the high specific gravity of the reinforcing bars.

한편, 외국의 폼타이 제품의 경우 철근을 사용하지 않고 폼타이를 벽면에 시공하여 연결하는 제품이 개발되어 있다. 이러한 외국 제품의 경우, 고강도 플라스틱을 사용하므로 정밀 가공이 유리하고, 벽면 경량화를 통한 운송비용 절감이 가능하다. 그러나 이러한 외국형 폼타이의 경우에도, 아직까지 강도 문제로 인한 깨짐, 부러짐 등 시공불량이 발생하는 경우가 많고 폼타이의 고단가로 인하여 높은 시공비용이 발생하는 문제도 있다. 나아가 일러한 타입의 폼타이는 정밀가공이 요구되므로 대량 생산이 어려운 측면이 있다. On the other hand, in the case of foreign form tie products, products that connect the form tie to the wall without using reinforcing bars have been developed. For these foreign products, since high-strength plastic is used, precision processing is advantageous, and transportation costs can be reduced by reducing the weight of the wall. However, even in the case of such foreign form ties, there are still many cases where construction defects such as cracks and breakages occur due to strength problems, and there is a problem in that high construction costs occur due to the high unit price of the form ties. Furthermore, since these types of form ties require precision processing, mass production is difficult.

본 발명은 전술한 종래 국내외 폼타이의 문제점을 해결하기 위하여 안출된 발명으로서, 폼타이 형상 가공이 용이하여 대량생산이 가능하고, 기계적 물성이 우수한 건축용 폼타이의 제조방법을 제공하는 것을 목적으로 한다. The present invention is an invention devised to solve the problems of the aforementioned conventional domestic and foreign form ties, and it is an object of the present invention to provide a method of manufacturing a form tie for construction that is easy to process and mass-produces, and has excellent mechanical properties. .

또한, 본 발명은 상기 방법으로 제조되고, 부식의 우려가 낮고 인장강도 및 굴곡강도 등의 기계적 특성이 우수하며 나아가 경량화가 실현되어 작업성이 매우 우수한 건축용 폼타이를 제공하는 것을 목적으로 한다. In addition, an object of the present invention is to provide a form tie for construction that is manufactured by the above method, has a low risk of corrosion, has excellent mechanical properties such as tensile strength and flexural strength, and is also lightweight and has excellent workability.

본 발명의 일 실시예에 따른 건축용 폼타이의 제조방법은 강화섬유 어레이를 준비하는 단계; 상기 강화섬유 어레이에 수지를 함침시켜 매트릭스 형태의 프리프레그를 준비하는 단계; 복수의 프리프레그를 라미네이트하여 적층체를 준비하는 단계; 및 상기 적층체에 열을 가하고 금형을 압착하여 성형하는 단계를 포함한다. A method of manufacturing a form tie for construction according to an embodiment of the present invention comprises the steps of preparing a reinforcing fiber array; preparing a matrix-type prepreg by impregnating the reinforcing fiber array with a resin; preparing a laminate by laminating a plurality of prepregs; and applying heat to the laminate and compressing the mold to form the laminate.

상기 강화섬유 어레이는 강화섬유의 단섬유 간에 직교하도록 직조된 직조체일 수 있다. The reinforcing fiber array may be a woven body woven to be orthogonal between the short fibers of the reinforcing fiber.

상기 강화섬유로서는 유리 섬유, 아라미드 섬유, 카본 섬유, SiC 섬유 등이 사용될 수 있다. As the reinforcing fiber, glass fiber, aramid fiber, carbon fiber, SiC fiber, etc. may be used.

상기 적층체는 각각의 프리프레그의 강화섬유 배열이 서로 동일하게 마주보도록 적층되어 형성될 수도 있고, 각각의 프리프레그의 강화섬유 배열이 서로 경사지도록 적층되어 형성될 수도 있다. The laminate may be formed by stacking the reinforcing fiber arrangement of each prepreg to face each other identically, or may be formed by stacking the reinforcing fiber arrangement of each prepreg to be inclined to each other.

한편, 상기 적층체는 강화섬유의 종류가 서로 다른 이종의 프리프레그들을 포함할 수도 있다. Meanwhile, the laminate may include heterogeneous prepregs having different types of reinforcing fibers.

함침되는 수지로서는 에폭시계 수지가 사용되는 것이 바람직하다. It is preferable that an epoxy resin is used as resin to be impregnated.

상기 프리프레그는 함치 수지 100 중량부에 대하여 강화섬유 어레이를 30 내지 70 중량부로 포함할 수 있다. The prepreg may include 30 to 70 parts by weight of the reinforcing fiber array based on 100 parts by weight of the impregnated resin.

본 발명의 일 실시예에 따른 건축용 폼타이는 전술한 방법으로 제조되고, 길이방향으로 연장된 막대 형상을 간는 건축용 폼타이로서, 중앙부의 폭이 최대이고 양 말단에 가까워질 수록 폭이 일정하게 좁아지고, 표면에 복수의 요철을 갖는 일체형 구조체이다. A form tie for construction according to an embodiment of the present invention is manufactured by the above-described method, and as a form tie for construction having a rod shape extending in the longitudinal direction, the width of the central portion is the maximum and the width is constantly narrow as it approaches both ends. It is an integrated structure having a plurality of irregularities on its surface.

상기 건축용 폼타이는 인장강도 및 굴곡강도가 각각 적어도 300 MPa이며, 상기 길이방향에 수직한 방향의 단면이 원형일 수 있다. The building form tie may have a tensile strength and a flexural strength of at least 300 MPa, respectively, and a cross section in a direction perpendicular to the longitudinal direction may be circular.

본 발명에 따른 건축용 폼타이는 일체형 구조이고, 프레스 금형 방식 등 압착식 성형 방식에 의하여 이루어지므로 제조 과정이 단순하고 대량생산에 용이한 장점을 갖는다. The form tie for construction according to the present invention has an integrated structure and is made by a compression molding method such as a press mold method, so that the manufacturing process is simple and has the advantage of easy mass production.

상기 폼타이는 인장강도 및 굴곡강도 등의 기계적 물성이 우수하고, 경량화가 실현되어 작업성이 매우 우수하며, 부품 운송 비용 등을 절감하여 전체적인 부품 단가를 저감할 수 있다. The form tie has excellent mechanical properties such as tensile strength and flexural strength, and is very excellent in workability by realizing weight reduction, and it is possible to reduce the overall unit cost of parts by reducing parts transportation costs.

또한, 상기 폼타이는 강화섬유 플라스틱으로 이루어져 있어 벽체간 열교환을 억제하므로 제조되는 벽체의 단열성을 향상시킬 수 있다. In addition, since the form tie is made of reinforced fiber plastic to suppress heat exchange between the walls, it is possible to improve the insulation properties of the manufactured wall.

결국, 본 발명에 따른 폼타이는 시공의 경제성 뿐만 아니라 건축물의 안정성을 현저히 향상시킬 수 있다. As a result, the form tie according to the present invention can significantly improve the stability of the building as well as the economical efficiency of construction.

도 1은 종래 폼타이의 사용예를 설명하기 위한 예시 도면이다.
도 2는 각각 국내형 폼타이와 외국형 폼타이를 예시한 도면이다.
도 3은 본 발명의 일 실시예에 따른 건축용 폼타이의 제조방법을 개념적으로 도시한 순서도이다.
도 4는 본 발명의 일 실시예에 따른 프리프레그의 강화섬유 직조 형상을 예시한 도면이다.
도 5는 본 발명의 일 실시예에 따른 건축용 폼타이를 개념적으로 도시한 도면이다. 1 is an exemplary view for explaining an example of using a conventional form tie.
2 is a view illustrating a domestic type form tie and a foreign type form tie, respectively.
3 is a flowchart conceptually illustrating a method of manufacturing a form tie for construction according to an embodiment of the present invention.
4 is a view illustrating the shape of the reinforcing fiber weaving of the prepreg according to an embodiment of the present invention.
5 is a view conceptually illustrating a form tie for construction according to an embodiment of the present invention.

이하 첨부된 도면을 참조하여, 본 발명의 일 실시예에 따른 건축용 폼타이의 제조방법 및 제조된 건축용 폼타이에 대하여 자세하게 설명하도록 한다. 그러나 하기 설명들은 본 발명의 기술사상을 구체화하여 설명하기 위한 예시적인 설명들이며, 본 발명은 아래 설명들로부터 유추될 수 있는 다양한 변형 실시예들을 포함할 수 있음은 자명하다. 아울러, 본 발명의 기술사상은 오직 후술하는 청구범위에 의하여 해석되고 제한될 수 있을 뿐, 하기 설명들에 의하여 본 발명의 기술사상이 제한되는 것은 아니다. Hereinafter, with reference to the accompanying drawings, a method for manufacturing a form tie for construction according to an embodiment of the present invention and the manufactured form tie for construction will be described in detail. However, the following descriptions are exemplary descriptions for concretely explaining the technical idea of the present invention, and it is obvious that the present invention may include various modified embodiments that can be inferred from the descriptions below. In addition, the technical spirit of the present invention can only be interpreted and limited by the following claims, and the technical spirit of the present invention is not limited by the following description.

도 3은 본 발명의 일 실시예에 따른 건축용 폼타이의 제조방법을 개념적으로 도시한 순서도이다. 3 is a flowchart conceptually illustrating a method of manufacturing a form tie for construction according to an embodiment of the present invention.

건축용 폼타이의 제조방법(S10은 순차적으로 강화섬유 어레이 준비단계(S110), 프리프레그 준비단계(S120), 라미네이트 단계(S130) 및 프레스 성형단계(S140)를 포함한다. The manufacturing method (S10) of the form tie for construction sequentially includes a reinforcing fiber array preparation step (S110), a prepreg preparation step (S120), a lamination step (S130) and a press forming step (S140).

강화섬유 어레이 준비단계(S110)는 수지에 의하여 함침시켜 프리프레그를 준비하는 단계(S120) 이전에 프리프레그를 이루는 강화섬유의 배열을 결정짓는 단계이다. 상기 강화섬유는 단섬유끼리 직교 방향으로 직조하여 형성될 수 있다. 이와 다르게, 직조가 아닌 단섬유들의 평행 배열 등 다양한 방식의 배열이 가능하고, 경우에 따라서는 부직포 형태의 강화섬유도 고려할 수 있다. 그러나 기계적 강도만을 고려했을 때는 직조 형태의 강화섬유 어레이가 유리하고 직조의 형태도 직교하는 방식의 직조가 유리한 것으로 테스트 결과 확인되었다.The reinforcing fiber array preparation step (S110) is a step of determining the arrangement of the reinforcing fibers constituting the prepreg before the step (S120) of preparing the prepreg by impregnating it with a resin. The reinforcing fibers may be formed by weaving short fibers in an orthogonal direction. Alternatively, various arrangements such as parallel arrangement of short fibers rather than weaving are possible, and in some cases, reinforcing fibers in the form of non-woven fabrics may also be considered. However, when only the mechanical strength is considered, the test results confirmed that the woven reinforcing fiber array is advantageous and the weaving of the orthogonal weave is advantageous.

도 4는 본 발명의 일 실시예에 따른 프리프레그의 강화섬유 직조 형상을 예시한 도면이다.4 is a view illustrating the shape of the reinforcing fiber weaving of the prepreg according to an embodiment of the present invention.

도 4를 참조하면, 직교 방식으로 직조된 강화섬유의 경우에도 도 4에서 보는 바와 같이 세부적으로 다양한 직조 형태를 포함할 수 있다. 즉, 십자형의 대칭적 직조 조직을 갖는 강화섬유, 단위 형태가 'ㄱ'자인 직조 조직을 갖는 강화섬유 등 다양한 직조 형태가 가능하다. 이러한 직조 형태는 최종 제조되는 폼타이의 물성과 기능에 영향을 미칠 수 있는 중요 인자로서 기능할 수 있으며, 향후 더욱 다양한 변형의 직조 형태에 대한 물성과의 상관 관계를 규명할 필요가 있다. Referring to FIG. 4 , even in the case of reinforcing fibers woven in an orthogonal manner, as shown in FIG. 4 , various weaving forms may be included in detail. That is, various weaving forms are possible, such as a reinforcing fiber having a cross-shaped symmetrical weave, and a reinforcing fiber having a woven structure in the shape of 'a'. This weaving form can function as an important factor that can affect the properties and functions of the final manufactured form tie, and it is necessary to investigate the correlation between the physical properties of the weaving form of more various modifications in the future.

한편, 상기 강화섬유로는 다양한 공지된 섬유들이 사용될 수 있다. 상기 강화섬유로는 유리 섬유, 아라미드 섬유, 카본 섬유 SiC 섬유 등 다양한 섬유가 사용될 수 있으며, 경우에 따라서는 하나의 강화섬유 어레이에 복수의 강화섬유가 포함될 수도 있다. Meanwhile, various known fibers may be used as the reinforcing fibers. As the reinforcing fiber, various fibers such as glass fiber, aramid fiber, carbon fiber SiC fiber, etc. may be used, and in some cases, a plurality of reinforcing fibers may be included in one reinforcing fiber array.

위와 같이, 강화섬유 어레이가 준비되면, 상기 강화섬유 어레이에 수지를 함침시켜 매트릭스 형태의 프리프레그를 준비한다(S120). 상기 프리프레그는 성형체의 부피를 결정하는 기본 단위 유닛으로 기능한다. As above, when the reinforcing fiber array is prepared, the prepreg in the form of a matrix is prepared by impregnating the reinforcing fiber array with a resin (S120). The prepreg functions as a basic unit that determines the volume of the molded body.

본 실시예에서, 상기 강화섬유 어레이에 함침되는 수지로는 에폭시계 수지가 사용된다. 에폭시계 수지의 경우 강화섬유의 강도 유지 및 라미네이트 단계(S130)에서의 열 압착 작업성이 우수하다. In this embodiment, an epoxy-based resin is used as the resin impregnated into the reinforcing fiber array. In the case of the epoxy-based resin, it is excellent in maintaining the strength of the reinforcing fibers and thermal compression workability in the lamination step (S130).

함침 방식은 크게 제한되지 않는다. 예를 들어, 강화섬유 어레이를 수지 용액에 함침시켜 매트릭스를 구현할 수도 있고, 이와 다르게 강화섬유 어레이에 수지를 도포 또는 스프레이 방식으로 함침시킬 수도 있다. 이러한 함침 방식은 강화섬유 어레이으 형태 안정성을 고려하여 다양하게 변경될 수 있다. The impregnation method is not significantly limited. For example, a matrix may be implemented by impregnating the reinforcing fiber array in a resin solution, or alternatively, the reinforcing fiber array may be impregnated with a resin by coating or spraying. This impregnation method may be variously changed in consideration of the shape stability of the reinforcing fiber array.

한편, 상기 수지는 수지 100 중량부 대비, 강화섬유가 30 내지 70 중량부가 되도록 함침되는 것이 바람직하다. 한편, 상기 수지에는 성형성 및 강도 특성 등을 고려하여 다양한 첨가제가 포함될 수도 있다. 예를 들어, 강도 향상을 위하여 현무암을 열처리 후 분말화한 세라믹 분말이 미량 포함될 수 있다. 테스트 결과, 현무암 유래 세라믹 분말의 첨가시 상당한 강도 향상이 이루어지는 것으로 확인되었다. On the other hand, the resin is preferably impregnated so that the reinforcing fiber is 30 to 70 parts by weight relative to 100 parts by weight of the resin. Meanwhile, various additives may be included in the resin in consideration of moldability and strength characteristics. For example, a trace amount of ceramic powder obtained by heat-treating basalt and then pulverizing it may be included in order to improve strength. As a result of the test, it was confirmed that a significant improvement in strength was achieved when the basalt-derived ceramic powder was added.

위와 같이 매트릭스 형태의 프리프레그가 준비되면, 상기 복수의 프리프레그들을 적층하여 적층체를 준비한다(S130). 상기 적층체는 프리프레그의 두께, 제조되는 폼타이의 스케일을 고려하여 복수의 프리프레그들을 라미네이트하는 단계(S130)를 거쳐 이루어진다. 상기 프리프레그들은 수~수십 개가 사용될 수 있다. When the matrix-type prepreg is prepared as described above, a laminate is prepared by stacking the plurality of prepregs (S130). The laminate is made by laminating a plurality of prepregs in consideration of the thickness of the prepreg and the scale of the manufactured form tie ( S130 ). Several to tens of the prepregs may be used.

한편, 상기 적층체는 동일한 강화섬유를 포함하는 동일한 프리프레그들의 라미네이트를 통하여 형성될 수도 있고, 서로 이종의 강화섬유를 포함하는 이종의 프리프레그들 라미네이트하여 형성될 수도 있다. Meanwhile, the laminate may be formed by laminating the same prepregs containing the same reinforcing fibers, or may be formed by laminating different prepregs containing different types of reinforcing fibers with each other.

중요한 점은 최총 제조되는 폼타이의 표면, 내부 등의 영역별 물성을 고려하여, 해당 프리프레그가 폼타이의 어떠한 영역을 구성하는지 사전 예측하여 적층 순서를 결정하는 것이다. 이러한 이종의 프리프레그들의 적층을 통하여, 최종 제조되는 일체형 폼타이의 강도특성을 영역별로 다르게 설정할 수 있으며, 이는 특수한 폼타이의 제조를 가능하게 하는 기술적 기반이 될 수 있다. An important point is to determine the stacking order by predicting in advance which area of the form tie the corresponding prepreg will constitute in consideration of the physical properties of each area, such as the surface and the inside of the final manufactured form tie. Through the lamination of these heterogeneous prepregs, the strength characteristics of the finally manufactured integrated form tie can be set differently for each area, which can be a technical basis for manufacturing a special form tie.

상기 프리프레들은 나름의 직조 방향을 가지고 있다. 상기 라미네이트 단계(S130)에서 적층되는 복수의 프리프레그들은 동일한 직조 방향으로 대응되도록 적층될 수도 있으나, 이와 다르게 프리프레그간 서로 직조방향이나 배열 방향이 교차되거나 경사를 이루도록 적층될 수도 있다. The prepregs have their own weaving direction. The plurality of prepregs stacked in the lamination step ( S130 ) may be stacked to correspond in the same weaving direction, but alternatively, the prepregs may be stacked so that the weaving directions or arrangement directions intersect each other or make an inclination.

적층체를 이루는 프리프레그들의 강화섬유 어레이들이 오버랩 됨에 따라 형성되는 멀티 어레이는 위에서 보았을 때, 0~90°사이의 다양한 교차를 형성할 수 있으며, 이러한 다양성의 변수는 폼타이 물성을 다각화 할 수 있는 중요 기술인자로 작용할 수 있다. A multi-array formed by overlapping reinforcing fiber arrays of prepregs constituting a laminate can form a variety of intersections between 0 and 90° when viewed from above. It can act as an important technical factor.

적층체가 준비되면, 열을 가하면서 미리 설계된 특정 형상의 금형을 압착함으로써 적층체를 성형하는 단계(S140)가 이루어진다. 이로써, 본 발명의 일 실시예에 따른 건축용 폼타이가 제조될 수 있다. 본 실시예에서, 상기 성형은, 프레스 금형 방식으로 이루어지며, 1회의 압착 성형만으로 폼타이가 형성될 수 있다. 본 발명의 폼타이는 후술하겠으나 일체형으로 이루어져 있기 때문에, 이처럼 성형 공정이 단순화될 수 있다. When the laminate is prepared, a step (S140) of molding the laminate is performed by pressing a mold of a pre-designed specific shape while applying heat. Thus, the form tie for construction according to an embodiment of the present invention can be manufactured. In this embodiment, the molding is made in a press mold method, and a form tie may be formed only by one compression molding. Although the form tie of the present invention will be described later, since it is made of an integral body, the forming process can be simplified as described above.

상기 가해지는 열의 온도는 함침된 수지 특성과 깊은 연관을 가지며, 적어도 함치 수지가, 가해지는 열에 의하여 적어도 일부 용융되어 프리프레그간의 융착을 가능하게 하는 범위에서 설정되어야 한다. The temperature of the applied heat is closely related to the properties of the impregnated resin, and at least the impregnated resin is at least partially melted by the applied heat, and should be set in a range that enables fusion between the prepregs.

이하에서는, 위의 방법으로 제조될 수 있는 건축용 폼타이의 일 실시예를 설명하도록 한다. Hereinafter, an embodiment of a form tie for construction that can be manufactured by the above method will be described.

도 5는 본 발명의 일 실시예에 따른 건축용 폼타이를 개념적으로 도시한 도면이다. 5 is a view conceptually illustrating a form tie for construction according to an embodiment of the present invention.

도 5를 참조하면, 본 실시예에 따른 건축용 폼타이(100)는 전체적으로 길이방향을 따라 연장된 막대 형상의 구조체이다. 도 5에서 보는 바와 같이 폼타이(100)의 중앙 부위는 볼록한 구조를 가지며, 상기 중앙부위를 기준으로 양 말단(120)까지 대칭적인 구조를 갖는다. 또한, 중앙부위에서 말단까지 이어지는 부위는 점차 폭이 일정하게 좁아지는 구조를 갖는다. 한편, 본 실시예에서 상기 폼타이는 길이방향으 단면이 원형인 원기둥 형상을 갖는다. 그러나 이와 다르게 각형인 폼타이도 경우에 따라서는 필요할 수 있다. Referring to FIG. 5 , the building form tie 100 according to the present embodiment is a bar-shaped structure extending along the longitudinal direction as a whole. As shown in FIG. 5 , the central portion of the form tie 100 has a convex structure, and has a symmetrical structure to both ends 120 with respect to the central portion. In addition, the portion extending from the central portion to the end has a structure in which the width is gradually narrowed. On the other hand, in this embodiment, the form tie has a cylindrical shape having a circular cross section in the longitudinal direction. However, unlike this, a prismatic form tie may also be required in some cases.

한편, 상기 폼타이(100)는 적어도 일 영역에 요철(110)을 포함하며, 이러한 요철은 홈 형상을 포함한다. 이러한 홈 형상의 요철(110)은 폼타이(100)를 둘러싸는 시멘트 등과의 결합 특성을 증가시켜 전체적으로 시공된 폼타이(100)의 고정력을 증가시킨다. On the other hand, the form tie 100 includes an unevenness 110 in at least one area, and the unevenness includes a groove shape. The groove-shaped unevenness 110 increases the bonding characteristics with cement surrounding the form tie 100 to increase the fixing force of the overall constructed form tie 100 .

양 말단(120)의 중앙부위는 오목하게 형성되어 있으며, 이는 다른 연결부품과의 결합 특성을 고려하여 고려된 구조이다. The central portion of both ends 120 is concave, which is a structure considered in consideration of coupling characteristics with other connecting parts.

전술한 바와 같이, 상기 폼타이(100)은 전체적으로 동일한 프리프레그의 성형으로 이루어질 수도 있으나, 표면부터 내부로 갈수로 서로 이질적인 프리프레그로 이루어질 수도 있다. 이러한 이질성은 강화섬유의 이질성, 또는 함침되는 수지의 이질성 등으로부터 기인할 수 있다. As described above, the form tie 100 may be formed of the same prepreg as a whole, but may be formed of prepregs that are different from each other as they go from the surface to the inside. Such heterogeneity may be due to the heterogeneity of the reinforcing fibers or the heterogeneity of the impregnated resin.

결국, 상기 폼타이(100)는 요구되는 물성, 적용되는 건출물의 특수성, 적용되는 부위의 특수성 등 다양한 변화를 고려하여 상기한 변수 인자들을 고려하여 맞춤형으로 설계될 수 있을 것이다. As a result, the form tie 100 may be custom designed in consideration of the aforementioned variable factors in consideration of various changes, such as required physical properties, the specificity of the building to be applied, and the specificity of the part to be applied.

상기 폼타이(100)는 기본적으로 강화섬유 플라스틱으로 이루어져 있어 경량화를 실현할 수 있으며, 경량의 재질로 이루어짐에도 우수한 강도특성을 나타낼 수 있다. 실험결과, 표 1에서 보는 바와 같은 물성치를 확인하였다. Since the form tie 100 is basically made of reinforced fiber plastic, it is possible to realize weight reduction, and can exhibit excellent strength characteristics even though it is made of a lightweight material. As a result of the experiment, the physical properties as shown in Table 1 were confirmed.

성능지표performance indicator 성능Performance 측정기관measuring institution 인장강도(Mpa)Tensile strength (Mpa) 300 이상300 or more 한국건설생활환경시험연구원Korea Construction Living Environment Testing Institute 굴곡강도(Mpa)Flexural strength (Mpa) 300 이상300 or more 상동same as above 차수공차(mm)Order tolerance (mm) ±0.2±0.2 상동same as above

이상에서 설명한 바에 따라, 본 발명에 따른 폼타이는 외국제품을 대체하여 다양한 건출물에 적용됨으로써, 시공 단가를 낮추면서도 건축물의 안정성을 획기적으로 개선할 수 있을 것으로 기대하고 있다. As described above, it is expected that the form tie according to the present invention can be applied to various buildings by replacing foreign products, thereby reducing the construction cost and dramatically improving the stability of the building.

Claims (11)

단섬유 간에 직교하도록 직조된 직조체인 강화섬유 어레이를 준비하는 단계;
상기 강화섬유 어레이에 수지를 함침시켜 매트릭스 형태의 프리프레그를 준비하는 단계;
복수의 프리프레그를 라미네이트하여 적층체를 준비하는 단계; 및
상기 적층체에 열을 가하고 금형을 압착하여 성형하는 단계를 포함하는 방법으로 제조되고,
길이방향으로 연장된 막대 형상을 갖고,
중앙부의 폭이 최대이고 양 말단에 가까워질 수록 폭이 일정하게 좁아지며,
표면에 복수의 요철을 가지며 일체형으로 이루어진 건축용 폼타이.
Preparing a reinforcing fiber array, which is a woven fabric woven orthogonally between short fibers;
preparing a matrix-type prepreg by impregnating the reinforcing fiber array with a resin;
preparing a laminate by laminating a plurality of prepregs; and
Manufactured by a method comprising the step of applying heat to the laminate and molding by pressing a mold,
It has a rod shape extending in the longitudinal direction,
The width of the central part is maximum, and the width becomes narrower as it approaches both ends.
A form tie for construction that has a plurality of irregularities on the surface and is made of one piece.
 삭제delete 제1항에 있어서,
상기 강화섬유는 유리 섬유, 아라미드 섬유, 카본 섬유 및 SiC 섬유로 이루어진 군으로부터 선택된 적어도 하나의 섬유를 포함하는 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
The reinforcing fiber is a form tie for construction, characterized in that it comprises at least one fiber selected from the group consisting of glass fiber, aramid fiber, carbon fiber and SiC fiber.
 제1항에 있어서,
상기 복수의 프리프레그는 각각의 프리프레그의 강화섬유 배열이 서로 동일하게 마주보도록 적층되는 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
The plurality of prepregs is a form tie for construction, characterized in that the reinforcing fiber arrangement of each prepreg is laminated to face each other identically.
 제1항에 있어서,
상기 복수의 프리프레그는 각각의 프리프레그의 강화섬유 배열이 서로 경사지도록 적층되는 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
The plurality of prepregs is a form tie for construction, characterized in that the stacking so that the reinforcing fiber arrangement of each prepreg is inclined to each other.
 제1항에 있어서,
상기 적층체는 강화섬유의 종류가 서로 다른 이종의 프리프레그들을 포함하는 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
The laminate is a form tie for construction, characterized in that it includes prepregs of different types of reinforcing fibers.
 제1항에 있어서,
상기 수지는 에폭시계 수지를 포함하는 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
The resin is a form tie for construction, characterized in that it comprises an epoxy-based resin.
 제1항에 있어서,
상기 프리프레그는,
수지 100 중량부; 및
강화섬유 어레이 30 내지 70 중량부를 포함하는 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
The prepreg is
100 parts by weight of resin; and
Form tie for construction, characterized in that it comprises 30 to 70 parts by weight of the reinforcing fiber array.
 삭제delete 제1항에 있어서,
인장강도 및 굴곡강도가 각각 적어도 300 MPa인 것을 특징으로 하는 건축용 폼타이.
According to claim 1,
A form tie for construction, characterized in that the tensile strength and the flexural strength are each at least 300 MPa.
 제1항에 있어서,
상기 길이방향에 수직한 방향의 단면이 원형인 것을 특징으로 하는 건축용 폼타이.
















According to claim 1,
A form tie for construction, characterized in that the cross section in the direction perpendicular to the longitudinal direction is circular.
KR1020200092857A 2020-07-27 2020-07-27 Method of manufacturing formwark tie for building and formwark tie for building manufactured by using the same KR102318566B1 (en)