KR102298842B1 - Coating method using water-based coating material with excellent compatability with solvelt-based coating film and eco-friendly heavy duty coating film manufactured therefrom - Google Patents

Coating method using water-based coating material with excellent compatability with solvelt-based coating film and eco-friendly heavy duty coating film manufactured therefrom Download PDF

Info

Publication number
KR102298842B1
KR102298842B1 KR1020200162210A KR20200162210A KR102298842B1 KR 102298842 B1 KR102298842 B1 KR 102298842B1 KR 1020200162210 A KR1020200162210 A KR 1020200162210A KR 20200162210 A KR20200162210 A KR 20200162210A KR 102298842 B1 KR102298842 B1 KR 102298842B1
Authority
KR
South Korea
Prior art keywords
water
soluble
oil
coating film
weight
Prior art date
Application number
KR1020200162210A
Other languages
Korean (ko)
Inventor
김현일
김상민
김진용
Original Assignee
삼화페인트공업주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼화페인트공업주식회사 filed Critical 삼화페인트공업주식회사
Priority to KR1020200162210A priority Critical patent/KR102298842B1/en
Application granted granted Critical
Publication of KR102298842B1 publication Critical patent/KR102298842B1/en

Abstract

The present invention provides a coating method using a water-soluble coating material having excellent affinity with an oil-based coating film, and an eco-friendly heavy duty coating film manufactured therefrom. The coating method includes: a step 1 of painting or painting an oil-based coating; a step 2 of surface-treating the painted oil-based coating film; a step 3 of forming an epoxy primer by coating the water-soluble epoxy primer composition (A) on the surface-treated oil-based coating film; and a step 4 of coating the water-soluble urethane topcoat composition (B) on the epoxy undercoat. By coating a water-soluble anti-rust coating material with excellent affinity with an oil-based coating film without removing the existing oil-based coating film, process shortening, cost reduction, work efficiency, environmental friendliness, adhesion and rust prevention are excellent.

Description

유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법 및 이로부터 제조된 친환경 중방식 도막{COATING METHOD USING WATER-BASED COATING MATERIAL WITH EXCELLENT COMPATABILITY WITH SOLVELT-BASED COATING FILM AND ECO-FRIENDLY HEAVY DUTY COATING FILM MANUFACTURED THEREFROM}A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film and an eco-friendly medium-duty coating film manufactured therefrom

본 발명은 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법 및 이로부터 제조된 친환경 중방식 도막에 관한 것으로, 보다 상세하게는 기존 유성 도막을 제거하지 않고 유성 도막과 친화력이 우수한 수용성 방청 도장재를 도장함으로써 공정 단축, 비용 절감, 작업 효율 상승, 및 환경 친화성이 우수하고, 부착력과 방청성이 뛰어난 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법 및 이로부터 제조된 친환경 중방식 도막에 관한 것이다. The present invention relates to a coating method using a water-soluble coating material having excellent affinity with an oil-based coating film and an eco-friendly medium-corrosion coating film manufactured therefrom, and more particularly, to an oil-based coating film and a water-soluble rust preventive coating material excellent in affinity with an oil-based coating film without removing the existing oil-based coating film It relates to a coating method using an oil-based coating film having excellent process shortening, cost reduction, work efficiency increase, and environmental friendliness, excellent adhesion and rust prevention, and a water-soluble coating material having excellent affinity, and an eco-friendly heavy-duty coating film manufactured therefrom.

도장업계에 친환경 관련 법규들이 대두됨에 따라 점점 더 적은 양의 유기용제를 포함하는 유성 도장재들이 증가하고 있으며, 나아가 수용성 도장재 제품들의 수요가 증가하고 있다. As eco-friendly laws and regulations emerge in the coating industry, oil-based coating materials containing less and less organic solvents are increasing, and further, the demand for water-soluble coating materials is increasing.

기존 유성 도장재들의 경우 철재에 일반적으로 도장되는 도료이며, 에폭시 타입, 우레탄 타입, 알키드 타입, 아크릴 타입 등이 적용되고 있다.Existing oil-based paints are paints that are generally applied to steel, and epoxy type, urethane type, alkyd type, acrylic type, etc. are being applied.

이렇게 유성 도장재로 도장된 도막은 장기간 대기에 노출 시 도막 노화가 발생되어 보수도장이 요구된다. 이때, 유성 도막의 경우에는 동일한 타입의 유성 도장재를 적용하기도, 하지만 내구성을 증진시키기 위하여 다른 타입의 유성 도장재를 적용하기도 한다.When exposed to the atmosphere for a long period of time, the coating film painted with oil-based coating material deteriorates and requires repair. In this case, in the case of an oil-based coating film, the same type of oil-based coating material is applied, but a different type of oil-based coating material is also applied to improve durability.

일례로, 알키드 유성 도막의 내구성 증진을 위하여 우레탄 도장재를 마감 도장하는 경우가 있다. 특히, 일액형 타입의 알키드 구도막 위 우레탄 도장을 위하여는 특수 에폭시 마스틱계 도장재를 적용할 수 있다. 에폭시 마스틱계도장재는 고고형분 제품이기에 다소 친환경적인 부분이 있으나, 점도가 높아 보수 도장시 유기용제 희석을 통한 작업성 확보가 요구되는 경우가 많다. 결국 희석율이 높아질수록 휘발성 유기화합물(VOC)은 증가하게 되며, 환경적으로 작업자들의 건강에 위협을 줄 수 있다.For example, in order to improve the durability of the alkyd oil-based coating film, there is a case where the urethane coating material is finished. In particular, for the urethane coating on the one-component type alkyd old coating film, a special epoxy mastic coating material can be applied. Epoxy mastic coating materials are somewhat eco-friendly as they are high-solids products, but due to their high viscosity, it is often required to secure workability by diluting organic solvents during repair and painting. As a result, the higher the dilution rate, the more volatile organic compounds (VOCs) increase, which can threaten the health of workers in an environment.

또한, 일액형 알키드 구도막의 특성상 보수 도장 되는 도장재의 유기용제의 함량이 높아 질수록 구도막을 녹이는 부분이 증가하여 상용성이 떨어지고 주름이 발생하는 경우가 있다.In addition, due to the characteristics of the one-component alkyd old coating film, the higher the content of the organic solvent in the coating material to be repaired, the more the part that melts the old coating film increases, resulting in poor compatibility and wrinkling in some cases.

유성 구도막 상부에 유성 도장재로 보수도장을 실시할 경우 일반적으로 동력공구 세정(SSPC-SP3)에 준하는 표면처리로 들뜬 구도막과 녹을 제거하고, 정상적인 구도막에 대해서는 수공구 세정(SSPC-SP2)에 준하는 표면처리를 한다.In the case of performing repair painting with oil-based paint on the upper part of the oil-based paint film, the surface treatment equivalent to the power tool cleaning (SSPC-SP3) is generally used to remove the excited old paint film and rust, and for the normal paint film, the surface treatment equivalent to the hand tool cleaning (SSPC-SP2) do

그러나, 여전히 유성 도장재를 사용하므로 유성 타입의 보수 도장은 친환경 정책과는 멀어지는 부분이 있다.However, since oil-based coating materials are still used, oil-based repair coatings are far from eco-friendly policies.

따라서, 최근 대두되고 있는 친환경 정책에 따라 적용되는 유성 구도막에 수용성 도료로 보수 도장하려고 하고 있다.Therefore, in accordance with the recently emerging eco-friendly policy, oil-based old coatings are being repaired and painted with water-soluble paints.

그러나, 수용성 도장재를 유성 구도막에 적용하기 위해서는 일반적으로 유성과 수용성의 친화력이 떨어지는 부분이 있어 전체적으로 기존 도막을 제거하는 블라스트 세정(SSPC-SP5, SSPC-SP6, SPC-SP10)을 통한 표면처리 후 보수도장이 진행되어야 한다.However, in order to apply a water-soluble coating material to an oil-based paint film, there is a part that generally has a poor affinity for oil and water solubility. Painting should proceed.

그러므로, 수용성 도장재를 적용하기 위하여 필수적으로 진행되는 표면처리는 비용상승, 공사기간 증가, 도장 공정 증가 등 다양한 부분에서 비효율성을 야기시키며, 이로 인하여 불가피하게 유성 도장재로 재도장하는 경우가 증가하고 있다.Therefore, the necessary surface treatment to apply water-soluble coating materials causes inefficiencies in various areas such as cost increase, construction period increase, and coating process increase, and consequently, the case of repainting with oil-based coating material is increasing inevitably. .

이러한 부분들로 인하여 블라스트 세정하지 않고, 동력공구 세정(SSPC-SP3) 또는 수공구 세정(SSPC-SP2)과 같은 간단한 표면처리 후에 유성 구도막에 적용할 수 있는 친화력 있는 수용성 도장재를 이용한 도장 공법의 요구가 증가하고 있다.Due to these parts, without blast cleaning, there is a demand for a coating method using a water-soluble, friendly coating material that can be applied to an oil-based paint film after simple surface treatment such as power tool cleaning (SSPC-SP3) or hand tool cleaning (SSPC-SP2). is increasing

수용성 도장재는 유기용제를 함유하지 않아 알키드 타입 및 아크릴 타입의 도장재와 같은 일액형 구도막을 녹일 위험도 없을뿐더러 적용되는 용제가 물인 만큼 매우 친환경적이다.Water-soluble coating materials do not contain organic solvents, so there is no risk of dissolving one-component coatings such as alkyd and acrylic coating materials, and it is very eco-friendly as the applied solvent is water.

또한, 중방식 도장의 경우 공장 도장과 현장 도장으로 이루어지고, 공장 도장의 경우에는 도장 구역, 배기 장치 등이 명확히 갖추어져 있는 공간이기 때문에 유성 도장재로 도장하는 것은 큰 문제가 없다. 하지만, 이렇게 유성 도장재가 도장된 부재가 현장으로 이동되어 후속 상도 도장 및 보수 도장의 현장 도장이 이루어지는 경우, 도장 시설 및 배기 장치가 미흡하게 설치되어 있는 경우가 많으므로, 문제가 발생할 수 있다.In addition, in the case of heavy-duty coating, it consists of factory coating and on-site coating, and in the case of factory coating, there is no big problem in coating with oil-based coating materials because the coating area and exhaust device are clearly provided. However, when the member coated with the oil-based coating material is moved to the site and the on-site painting of the subsequent top coat and repair painting is performed, the painting facility and the exhaust system are often insufficiently installed, so a problem may occur.

이에 친환경적인 수용성 도장재로 현장 도장하는 것이 작업자의 안전 및 환경적인 측면에서 필요하나, 유성 도막과 수용성 도장재의 친화력이 문제가 되어 유성으로 도장되는 상황이다.Therefore, on-site painting with an eco-friendly water-soluble coating material is necessary in terms of worker safety and environment, but the affinity between the oil-based coating film and the water-soluble coating material is a problem, so it is painted with oil.

따라서, 이러한 부분들로 인하여 유성 도막과 친화력이 우수한 수용성 도장재를 사용한 친환경 도장 공법이 매우 필요한 상황이다.Therefore, due to these parts, an eco-friendly coating method using a water-soluble coating material having excellent affinity with an oil-based coating film is very necessary.

대한민국 등록특허 제10-1170794호 (특허등록일: 2012년07월27일)Republic of Korea Patent Registration No. 10-1170794 (Patent registration date: July 27, 2012)

따라서, 본 발명은 유성 도장재의 유기 용제 휘발에 의해 발생하는 작업자 안전 및 환경적인 측면에서의 문제점을 유성 도막과 친화력이 우수하고 물을 용매로 사용하는 수용성 도장재로 도장하여 해소하는 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법을 제공하는 데 있다. Therefore, the present invention has an affinity with an oil-based coating film that solves the problems in worker safety and environmental aspects caused by the organic solvent volatilization of the oil-based coating material by coating it with a water-soluble coating material that has excellent affinity with the oil-based coating film and uses water as a solvent. An object of the present invention is to provide a coating method using an excellent water-soluble coating material.

또한, 본 발명은 기존 유성 도막을 제거하지 않고 유성 도막과 친화력이 우수한 수용성 도장재를 적용함으로써 공정 단축, 비용 절감, 작업 효율 상승, 및 환경 친화성이 우수한 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법을 제공하는 데 있다.In addition, the present invention does not remove the existing oil-based coating film and applies a water-soluble coating material having excellent affinity with an oil-based coating film, thereby shortening the process, reducing costs, increasing work efficiency, and coating using a water-soluble coating material having excellent affinity with an oil-based coating film excellent in environmental friendliness It is to provide a technique.

또한, 본 발명은 방청성이 월등한 친환경 중방식 도막을 제공하는 데 있다.In addition, the present invention is to provide an eco-friendly medium-corrosive coating film having excellent rust prevention properties.

본 발명이 해결하고자 하는 과제는 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 이하의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problems to be solved by the present invention are not limited to the problems mentioned above, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.

상기 과제를 해결하기 위해, 본 발명의 일 측면에 따르면, In order to solve the above problems, according to an aspect of the present invention,

유성 도막을 도장하거나 도장되어 있는 1 단계;Step 1 of painting or painting an oil-based coating;

도장된 유성 도막을 표면처리하는 2 단계;A second step of surface-treating the painted oil-based coating film;

수용성 에폭시 하도 조성물(A)을 표면처리된 유성 도막에 도장하여 에폭시 하도를 형성하는 3 단계; 및Step 3 of coating the water-soluble epoxy primer composition (A) on the surface-treated oil-based coating film to form an epoxy primer; and

수용성 우레탄 상도 조성물(B)을 상기 에폭시 하도에 도장하는 4 단계;를 포함하는Including a; 4 step of coating the water-soluble urethane topcoat composition (B) on the epoxy undercoat

유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법을 제공한다.A coating method using a water-soluble coating material having excellent affinity with an oil-based coating film is provided.

또한, 상기 유성 도막은 아크릴 타입, 알키드 타입, 에폭시 타입, 무기질 타입, 및 우레탄 타입의 유성 도막으로 이루어진 군에서 선택된 하나 이상일 수 있다.In addition, the oil-based coating film may be at least one selected from the group consisting of an acrylic type, an alkyd type, an epoxy type, an inorganic type, and a urethane type oil-based coating film.

또한, 상기 표면처리는 동력공구 세정(SSPC-SP3), 수공구 세정(SSPC-SP2), 용제 세정(SSPC-SP1), 블라스트 세정(SSPC-SP5, SSPC-SP6, SSPC-SP10), 수세척(SSPC-SP12), 및 세정하지 않음으로 이루어진 군에서 선택된 하나 이상일 수 있다.In addition, the surface treatment is power tool cleaning (SSPC-SP3), hand tool cleaning (SSPC-SP2), solvent cleaning (SSPC-SP1), blast cleaning (SSPC-SP5, SSPC-SP6, SSPC-SP10), water washing ( SSPC-SP12), and no cleaning.

여기서, 상기 수용성 에폭시 하도 조성물(A)은 Here, the water-soluble epoxy primer composition (A) is

수용성 에폭시 수지 10 내지 50중량부, 방청안료 5 내지 30중량부, 편상 안료 1 내지 20중량부, 특수 방청 첨가제 0.1 내지 2중량부, 및 수용성 에폭시 경화제 50 내지 90중량부를 함유하는 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, 0.1 to 2 parts by weight of a special antirust additive, and 50 to 90 parts by weight of a water-soluble epoxy curing agent.

하도 형성용 수용성 에폭시 도료 조성물일 수 있다.It may be a water-soluble epoxy paint composition for forming an undercoat.

그리고, 상기 하도 형성용 수용성 에폭시 도료 조성물에서,And, in the water-soluble epoxy paint composition for forming an undercoat,

상기 수용성 에폭시 수지는 자기유화성 에폭시(Self-emulsifiable Epoxy), 액상 에폭시 에멀젼(Liquid based epoxy emulsion), 반고상 에폭시 에멀젼(Semisolid based epoxy emulsion), 고상 에폭시 수지(Solid based epoxy emulsion), 및 페놀노볼락계 에멀젼(phenol novolac based emulsion)으로 이루어진 군에서 선택된 하나 이상일 수 있다.The water-soluble epoxy resin is self-emulsifiable epoxy, liquid based epoxy emulsion, semisolid based epoxy emulsion, solid based epoxy emulsion, and phenolo. It may be at least one selected from the group consisting of phenol novolac based emulsion.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물에서,In addition, in the water-soluble epoxy paint composition for forming an undercoat,

상기 방청안료는 징크포스페이트(Zinc phosphate), 마그네슘포스페이트(Magnesium phosphate), 칼슘하이드로젠포스페이트(Calcium hydrogen phosphate), 스트론튬 알루미늄 폴리포스페이트 하이드레이트(Strontium aluminium polyphosphate hydrate), 칼슘 알루미늄 폴리포스페이트 실리케이트 하이드레이트(Calcium aluminium polyphosphate silicate hydrate), 징크 알루미늄 오르토포스페이트(Zinc aluminium orthophosphate), 징크 오르토포스페이트 하이드레이트(Zinc orthophosphate hydrate), 징크 몰리브데늄 오르토포스페이트 하이드레이트(Zinc molybdenum orthophosphate hydrate), 및 징크 알루미늄 폴리포스페이트 하이드레이트(Zinc aluminium polyphosphate hydrate)로 이루어진 군에서 선택된 하나일 수 있다.The rust preventive pigment is zinc phosphate, magnesium phosphate, calcium hydrogen phosphate, strontium aluminum polyphosphate hydrate, calcium aluminum polyphosphate silicate hydrate. silicate hydrate), zinc aluminum orthophosphate, zinc orthophosphate hydrate, zinc molybdenum orthophosphate hydrate, and zinc aluminum polyphosphate hydrate (Zinc aluminium) It may be one selected from the group consisting of.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물에서, In addition, in the water-soluble epoxy paint composition for forming an undercoat,

상기 편상안료(barrier pigment)는 마이카(Mica), 운모상 산화철(MIO, micaceous iron oxide), 글라스 플레이크(Glass flake), 및 알루미늄 플레이크(Aluminum flake)로 이루어진 군에서 선택된 하나 이상일 수 있다.The barrier pigment may be at least one selected from the group consisting of mica, micaceous iron oxide (MIO), glass flake, and aluminum flake.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물에서,In addition, in the water-soluble epoxy paint composition for forming an undercoat,

상기 특수 방청 첨가제는 소듐나이트라이트(Sodium nitrite), 포타슘나이트라이트(Potassium nitrite), 리튬나이트라이트(Lithium nitrite), 소듐벤조에이트(Sodium benzoate), 티아졸(Thiazole), 이미다졸(Imidazole), 및 벤조트리아졸(Benzotriazole)로 이루어진 군에서 선택된 하나 이상일 수 있다.The special anti-rust additive is sodium nitrite, potassium nitrite, lithium nitrite, sodium benzoate, thiazole, imidazole, and It may be at least one selected from the group consisting of benzotriazole.

그리고, 상기 하도 형성용 수용성 에폭시 도료 조성물에서,And, in the water-soluble epoxy paint composition for forming an undercoat,

상기 수용성 에폭시 경화제는 페날카민(Phenalkamine), 폴리아미드(Polyamide), 폴리아민(Polyamine), 폴리아미도아민(Polyamidoamine), 및 알리파틱 아민(Aliphatic amine)으로 이루어진 군에서 선택된 하나 이상일 수 있다.The water-soluble epoxy curing agent may be at least one selected from the group consisting of phenalkamine, polyamide, polyamine, polyamidoamine, and aliphatic amine.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물은,In addition, the water-soluble epoxy paint composition for forming the undercoat,

(i) 수용성 에폭시 수지 10 내지 50 중량부, 방청안료 5 내지 30 중량부, 편상안료 1 내지 20 중량부, 특수 방청 첨가제 0.1 내지 2 중량부를 함유하는 주제부; 및(i) a main part containing 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, and 0.1 to 2 parts by weight of a special antirust additive; and

(ii) 수용성 에폭시 경화제 50 내지 90 중량부를 함유하는 경화제부;를 포함할 수 있다.(ii) a curing agent part containing 50 to 90 parts by weight of a water-soluble epoxy curing agent; may be included.

여기서, 상기 하도 형성용 수용성 에폭시 도료 조성물의 Here, the water-soluble epoxy paint composition for forming the undercoat

상기 (i) 주제부 및 (ii) 경화제부는 1:0.05 ~ 0.3의 중량비로 사용될 수 있다.The (i) main part and (ii) curing agent part may be used in a weight ratio of 1:0.05 to 0.3.

또한, 상기 수용성 우레탄 상도 조성물(B)은In addition, the water-soluble urethane topcoat composition (B) is

수산기-함유 폴리아크릴 수지 20 내지 70중량부, 체질안료 1 내지 30중량부, 수용성 우레탄 경화제 40 내지 90중량부, 및 필름 형성 보조제 15 내지 35중량부를 함유하는, 20 to 70 parts by weight of a hydroxyl group-containing polyacrylic resin, 1 to 30 parts by weight of an extender, 40 to 90 parts by weight of a water-soluble urethane curing agent, and 15 to 35 parts by weight of a film forming aid,

상도 형성용 수용성 우레탄 도료 조성물일 수 있다.It may be a water-soluble urethane paint composition for forming a top coat.

그리고, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,And, in the water-soluble urethane paint composition for forming the top coat,

상기 수산기-함유 폴리아크릴 수지는 20 내지 70 중량부를 포함할 수 있다.The hydroxyl group-containing polyacrylic resin may include 20 to 70 parts by weight.

또한, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,In addition, in the water-soluble urethane paint composition for forming the top coat,

상기 체질안료는 황산바륨, 활석, 실리카, 장석 및 탄산칼슘으로 이루어진 군에서 선택된 하나 이상일 수 있다.The extender pigment may be at least one selected from the group consisting of barium sulfate, talc, silica, feldspar and calcium carbonate.

그리고, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,And, in the water-soluble urethane paint composition for forming the top coat,

상기 수용성 우레탄 경화제는 친수성기를 불포함한 TDI(Toluene Diisocyanate), MDI(Methylene Diphenyl Diisocyanate), HDI(Hexamethylene Diisocyanate), HDI(Hexamethylene Diisocyanate) 뷰렛, IPDI(Isophorone Diisocyanate), TDI 삼량체, HDI 삼량체 및 친수성기를 포함한 TDI(Toluene Diisocyanate), MDI(Methylene Diphenyl Diisocyanate), HDI(Hexamethylene Diisocyanate), HDI(Hexamethylene Diisocyanate) 뷰렛, IPDI(Isophorone Diisocyanate), TDI 삼량체, 및 HDI 삼량체로 이루어진 군에서 선택된 하나 이상일 수 있다.The water-soluble urethane curing agent contains a hydrophilic group-free TDI (Toluene Diisocyanate), MDI (Methylene Diphenyl Diisocyanate), HDI (Hexamethylene Diisocyanate), HDI (Hexamethylene Diisocyanate) burette, IPDI (Isophorone Diisocyanate), TDI trimer, HDI trimer and hydrophilic group It may be one or more selected from the group consisting of TDI (Toluene Diisocyanate), MDI (Methylene Diphenyl Diisocyanate), HDI (Hexamethylene Diisocyanate), HDI (Hexamethylene Diisocyanate) burette, IPDI (Isophorone Diisocyanate), TDI trimer, and HDI trimer including .

여기서, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,Here, in the water-soluble urethane paint composition for forming the top coat,

상기 필름 형성 보조제는 PMA(propylene glycol methyl ether acetate), PGDA(Propylene Glycol Diacetate), 부틸아세테이트, 및 에틸아세테이트로 이루어진 군에서 선택된 하나 이상일 수 있다.The film forming aid may be at least one selected from the group consisting of propylene glycol methyl ether acetate (PMA), propylene glycol diacetate (PGDA), butyl acetate, and ethyl acetate.

그리고, 상기 상도 형성용 수용성 우레탄 도료 조성물은,And, the water-soluble urethane paint composition for forming the top coat,

(iii) 상기 수산기-함유 폴리아크릴 수지 20 내지 70 중량부 및 상기 체질안료 1 내지 30 중량부를 함유하는 주제부; 및(iii) a main part containing 20 to 70 parts by weight of the hydroxyl group-containing polyacrylic resin and 1 to 30 parts by weight of the extender; and

(iv) 상기 수용성 우레탄 경화제 40 내지 90 중량부 및 상기 필름 형성 보조제 15 내지 35 중량부를 함유하는 경화제부;를 포함할 수 있다.(iv) a curing agent part containing 40 to 90 parts by weight of the water-soluble urethane curing agent and 15 to 35 parts by weight of the film forming aid; may include.

또한, 상기 상도 형성용 수용성 우레탄 도료 조성물의In addition, the water-soluble urethane paint composition for forming the top coat

상기 (iii) 주제부 및 (iv) 경화제부는 1:0.05 ~ 0.3의 중량비로 사용될 수 있다.The (iii) main part and (iv) curing agent part may be used in a weight ratio of 1:0.05 to 0.3.

본 발명의 다른 측면에 따르면,According to another aspect of the present invention,

상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법으로 제조된 Manufactured by a coating method using a water-soluble coating material having excellent affinity with the oil-based coating film

표면 처리된 유성 도막, 수용성 에폭시 하도 조성물(A)로 도장된 에폭시 하도, 및 수용성 우레탄 상도 조성물(B)로 도장된 우레탄 상도를 포함하는,Containing a surface-treated oil-based coating film, an epoxy primer coated with a water-soluble epoxy primer composition (A), and a urethane topcoat coated with a water-soluble urethane topcoat composition (B),

친환경 중방식 도막을 제공한다.It provides an eco-friendly medium-proof coating film.

본 발명에 따르면, 기존 유성 도막 제거가 불필요하고, 유성 도막의 표면처리를 간단히 수행한 후 보수 도장하는 유성 도막과 친화력이 우수한 수용성 도장재를 적용한 도장 공법을 제공하므로 공정이 단축되고, 비용이 절감되고, 작업 효율이 향상되며, 환경 친화성이 우수하다.According to the present invention, there is no need to remove the existing oil-based coating film, and a coating method is provided using an oil-based coating film that is repaired after performing simple surface treatment of the oil-based coating film and a water-soluble coating material having excellent affinity, thereby shortening the process and reducing costs. , work efficiency is improved, and environmental friendliness is excellent.

또한, 본 발명은 유성 도막 상부에 주름이 생성되지 않는 수성 도막을 형성하는 보수 도장 공법인 유성 도막과 친화력이 우수한 수용성 도장재를 적용한 도장 공법을 제공하므로 도장 품질이 우수하다.In addition, the present invention provides a coating method in which a water-soluble coating material excellent in affinity with an oil-based coating film is applied, which is a repair coating method for forming a water-based coating film that does not generate wrinkles on the upper part of the oil-based coating film, so that the coating quality is excellent.

또한, 본 발명은 유성 도막 상부에 중방식 페인트인 유성 도막과 친화력이 우수한 수용성 도장재를 적용한 도장 공법을 제공하므로 중방식 도장 성능이 월등하다.In addition, since the present invention provides a coating method in which a water-soluble coating material having excellent affinity with an oil-based coating film, which is a heavy-duty paint, is applied to the upper portion of the oil-based coating film, the medium coating performance is superior.

또한, 본 발명의 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법 시 유성 도막에 간단한 표면처리하여도 유성 도막과 중방식 도막이 우수한 부착성 및 내구성을 가지면서 이를 장기간 유지할 수 있다.In addition, during the coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention, even if the oil-based coating film is subjected to a simple surface treatment, the oil-based coating film and the heavy-duty coating film have excellent adhesion and durability, and can be maintained for a long period of time.

본 발명의 효과는 상기한 효과로 한정되는 것은 아니며, 본 발명의 상세한 설명 또는 특허청구범위에 기재된 발명의 구성으로부터 추론 가능한 모든 효과를 포함하는 것으로 이해되어야 한다.It should be understood that the effects of the present invention are not limited to the above-described effects, and include all effects that can be inferred from the configuration of the invention described in the detailed description or claims of the present invention.

도 1은 본 발명의 일 실시예에 따른 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법의 공정흐름도이다. 1 is a process flow diagram of a coating method using an oil-based coating film and a water-soluble coating material having excellent affinity according to an embodiment of the present invention.

이하 첨부된 도면을 참조하면서 본 발명에 따른 바람직한 실시예를 상세히 설명하기로 한다.Hereinafter, preferred embodiments according to the present invention will be described in detail with reference to the accompanying drawings.

본 발명의 이점 및 특징, 그리고 그것을 달성하는 방법은 첨부된 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다.Advantages and features of the present invention, and a method of achieving the same, will become apparent with reference to the embodiments described below in detail in conjunction with the accompanying drawings.

그러나 본 발명은 이하에 개시되는 실시예들에 의해 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.However, the present invention is not limited by the embodiments disclosed below, but will be implemented in a variety of different forms, and only these embodiments allow the disclosure of the present invention to be complete, and common knowledge in the art to which the present invention pertains It is provided to fully inform those who have the scope of the invention, and the present invention is only defined by the scope of the claims.

또한, 본 발명을 설명함에 있어 관련된 공지 기술 등이 본 발명의 요지를 흐리게 할 수 있다고 판단되는 경우 그에 관한 자세한 설명은 생략하기로 한다.In addition, in the description of the present invention, if it is determined that related known technologies may obscure the gist of the present invention, detailed description thereof will be omitted.

이하, 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.

유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film

본 발명은 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법을 제공한다. The present invention provides a coating method using a water-soluble coating material having excellent affinity with an oil-based coating film.

본 발명의 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법은 The coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention is

유성 도막을 도장하거나 도장되어 있는 1 단계;Step 1 of painting or painting an oil-based coating;

도장된 유성 도막을 표면처리하는 2 단계;A second step of surface-treating the painted oil-based coating film;

수용성 에폭시 하도 조성물(A)을 표면처리된 유성 도막에 도장하여 에폭시 하도를 형성하는 3 단계; 및Step 3 of coating the water-soluble epoxy primer composition (A) on the surface-treated oil-based coating film to form an epoxy primer; and

수용성 우레탄 상도 조성물(B)을 상기 에폭시 하도에 도장하는 4 단계;를 포함한다.4 step of coating the water-soluble urethane topcoat composition (B) on the epoxy undercoat; includes.

여기서, 상기 유성 도막은 아크릴 타입, 알키드 타입, 에폭시 타입, 무기질 타입, 및 우레탄 타입의 유성 도막으로 이루어진 군에서 선택된 하나 이상일 수 있다.Here, the oil-based coating film may be at least one selected from the group consisting of an acrylic type, an alkyd type, an epoxy type, an inorganic type, and a urethane type oil-based coating film.

그리고, 상기 유성 도막의 피도면은 철강재, 콘크리트, 타일, 아연재, 목재 및 세라믹재로 이루어진 군에서 선택된 되어 하나 이상일 수 있다.In addition, the target surface of the oil-based coating film may be at least one selected from the group consisting of steel, concrete, tile, zinc, wood, and ceramic material.

또한, 상기 표면처리는 동력공구 세정(SSPC-SP3), 수공구 세정(SSPC-SP2), 용제 세정(SSPC-SP1), 블라스트 세정(SSPC-SP5, SSPC-SP6, SSPC-SP10), 수세척(SSPC-SP12), 및 세정하지 않음으로 이루어진 군에서 선택된 하나 이상일 수 있다.In addition, the surface treatment is power tool cleaning (SSPC-SP3), hand tool cleaning (SSPC-SP2), solvent cleaning (SSPC-SP1), blast cleaning (SSPC-SP5, SSPC-SP6, SSPC-SP10), water washing ( SSPC-SP12), and no cleaning.

여기서, SSPC(The Society for Protective Coatings) 기준은 미국 철강구조물 도장협의회의 도장 바탕 처리방법 기준이다.Here, the SSPC (The Society for Protective Coatings) standard is the standard for coating background treatment of the American Steel Structure Coatings Council.

상기 동력공구 세정(SSPC-SP3)은 들뜬녹, 흑피, 도막 등을 동력공구(그라인더)로써 지시하는 만큼 제거한다.The power tool cleaning (SSPC-SP3) removes loose rust, mill scale, coating film, etc. as instructed by a power tool (grinder).

상기 수공구 세정(SSPC-SP2)은 스크랩프, 샌드페이퍼, 와이어 브러쉬 등의 수공구로써 제거할 수 있는 녹, 흑피, 도막을 지시하는 만큼 제거한다.The hand tool cleaning (SSPC-SP2) removes rust, mill scale, and coating film that can be removed with a hand tool such as scrap, sandpaper, or wire brush as instructed.

상기 용제 세정(SSPC-SP1)은 용제, 증기, 알칼리, 에멀젼 및 수증기에 의한 세정으로 유분, 그리스, 먼지, 오염물 등을 제거한다.The solvent cleaning (SSPC-SP1) removes oil, grease, dust, contaminants, etc. by cleaning with a solvent, steam, alkali, emulsion and water vapor.

여기서, 상기 블라스트 세정(SSPC-SP5, SSPC-SP6, SSPC-SP10)은 SSPC-SP5, SSPC-SP6, 또는 SSPC-SP10의 각 세정방법에 의해 녹, 흑피, 도막 및 기타 이물질을 분리 제거하는 세정 방법이다.Here, the blast cleaning (SSPC-SP5, SSPC-SP6, SSPC-SP10) is a cleaning that separates and removes rust, mill scale, paint film and other foreign substances by each cleaning method of SSPC-SP5, SSPC-SP6, or SSPC-SP10 way.

상기 블라스트 세정(SSPC-SP5)은 나금속 블라스트 세정(White Metal Blast Cleaning)으로, 모래, 그리트(Grit) 및 쇼트(Shot)를 사용하여 휠 또는 노즐에 의한 블라스트 세정, 건식 혹은 습식으로 눈에 띄는 모든 녹, 흑피, 도막 및 기타 이물질을 100 % 제거한다.The blast cleaning (SSPC-SP5) is a bare metal blast cleaning (White Metal Blast Cleaning), using sand, grit, and shot to blast cleaning by a wheel or nozzle, Remove 100% of all rust, mill scale, paint film and other foreign matter.

또한, 상기 블라스트 세정(SSPC-SP6)은 일반 블라스트 세정(Commercial Blast Cleaning)으로, 비교적 심한 부식환경에 놓여지는 피도물인 식별 가능한 이물질, 잔유물의 2/3 이상을 블라스트(분리 제거) 세정하는 것이다.In addition, the blast cleaning (SSPC-SP6) is a general blast cleaning (Commercial Blast Cleaning), and blast (separate removal) cleaning of more than 2/3 of identifiable foreign substances and residues, which are objects to be coated, placed in a relatively severe corrosive environment.

또한, 상기 블라스트 세정(SSPC-SP10)은 준나금속 블라스트세정(Near White Blast Cleaning)으로, 식별 가능한 이물질, 잔유물의 95 % 이상까지 완전 나금속세정에 가까운 블라스트 세정하는 것이다.In addition, the blast cleaning (SSPC-SP10) is a near white blast cleaning, which is a blast cleaning close to complete bare metal cleaning up to 95% or more of identifiable foreign substances and residues.

그리고, 수세척(SSPC-SP12)은 연마제 분사 세정 공법을 적용하기 곤 란하거나 용해성 염의 오염이 심각할 경우에 주로 사용되는 공법으로 초고압수로 표면의 이물질 및 오염물을 제거 하는 워터 제팅(water jetting)을 의미한다.And, water washing (SSPC-SP12) is a method mainly used when it is difficult to apply the abrasive spray cleaning method or when contamination of soluble salts is serious. means

그리고, 상기 수용성 에폭시 하도 조성물(A)은 And, the water-soluble epoxy primer composition (A) is

수용성 에폭시 수지 10 내지 50중량부, 방청안료 5 내지 30중량부, 편상 안료 1 내지 20중량부, 특수 방청 첨가제 0.1 내지 2중량부, 및 수용성 에폭시 경화제 50 내지 90중량부를 함유하는 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, 0.1 to 2 parts by weight of a special antirust additive, and 50 to 90 parts by weight of a water-soluble epoxy curing agent.

하도 형성용 수용성 에폭시 도료 조성물일 수 있다.It may be a water-soluble epoxy paint composition for forming an undercoat.

또한, 상기 수용성 우레탄 상도 조성물(B)은In addition, the water-soluble urethane topcoat composition (B) is

수산기-함유 폴리아크릴 수지 20 내지 70중량부, 체질안료 1 내지 30중량부, 수용성 우레탄 경화제 40 내지 90중량부, 및 필름 형성 보조제 15 내지 35중량부를 함유하는, 20 to 70 parts by weight of a hydroxyl group-containing polyacrylic resin, 1 to 30 parts by weight of an extender, 40 to 90 parts by weight of a water-soluble urethane curing agent, and 15 to 35 parts by weight of a film forming aid,

상도 형성용 수용성 우레탄 도료 조성물일 수 있다.It may be a water-soluble urethane paint composition for forming a top coat.

본 발명의 상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법은 유성 도막과 친화력이 우수한 친환경 수용성 시스템을 도장재로 적용함으로써 친환경적이며, 휘발성 유기화합물(VOC)이 낮은 도장 공법이다.The coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention is an environmentally friendly and low volatile organic compound (VOC) coating method by applying an eco-friendly water-soluble system having excellent affinity with the oil-based coating film as a coating material.

또한, 본 발명의 상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법은 유성 도막에 친화력이 우수한 수용성 도료 도장 시 유성도료로 도장한 것과 동등한 부착력을 제공하기 때문에 친환경적인 장점 외에도 부착력이 우수하다.In addition, the coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention provides adhesion equivalent to that of the oil-based coating when painting the water-soluble paint having excellent affinity to the oil-based coating film.

또한, 본 발명의 상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법은 유성 도막 상부에 수용성 도장재를 적용하기 위하여 전체적으로 기존 도막을 제거하는 블라스트 세정(SSPC-SP5, SSPC-SP6, SSPC-SP10) 공정을 일반적인 표면처리인 동력공구세정(SSPC-SP3) 및 수공구세정(SSPC-SP2) 정도의 간단한 표면처리로 변경할 수 있어 비용절감, 공사기간 단축, 도장 공정 효율성 상승, 환경 친화성을 기대할 수 있다.In addition, the coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention is blast cleaning (SSPC-SP5, SSPC-SP6, SSPC-SP10) that removes the existing coating film as a whole in order to apply the water-soluble coating material on top of the oil-based coating film. The process can be changed to a simple surface treatment such as power tool cleaning (SSPC-SP3) and hand tool cleaning (SSPC-SP2), which are general surface treatments, so you can expect cost savings, shortened construction period, increased painting process efficiency, and environmental friendliness. .

또한, 본 발명의 상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법은 일액형 알키드 도막에 대하여 보수할 경우에는 에폭시 유성 도장재의 작업성과 휘발성 유기화합물(VOC)의 단점에 대해서 친환경 보수 도장 공법으로 대체하여 제공할 수 있다. In addition, the coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention is an eco-friendly repair coating method for the workability of the epoxy-based coating material and the disadvantages of volatile organic compounds (VOC) when repairing the one-component alkyd coating film. may be provided as a substitute.

그리고, 본 발명의 상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법은 일액형 아크릴타입의 도막 등에 대해서도 아크릴 도막 제거 없이 보수 도장할 수 있는 방법을 제공한다In addition, the coating method using the water-soluble coating material having excellent affinity with the oil-based coating film of the present invention provides a method for repairing and painting even a one-component acrylic type coating film without removing the acrylic coating film.

이하, 도 1을 참조하여 본 발명의 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법을 상세히 설명한다.Hereinafter, a coating method using a water-soluble coating material having excellent affinity with the oil-based coating film of the present invention will be described in detail with reference to FIG. 1 .

도 1은 본 발명의 일 실시예에 따른 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법의 공정흐름도이다. 1 is a process flow diagram of a coating method using an oil-based coating film and a water-soluble coating material having excellent affinity according to an embodiment of the present invention.

도 1을 참조하면, 먼저, 유성 도막을 도장하거나 도장되어 있는 1 단계(S110)를 거쳐,Referring to FIG. 1 , first, an oil-based coating film is painted or through a first step (S110) of being painted,

도장된 유성 도막을 표면처리하는 2 단계(S120)에서 동력공구세정(SSPC-SP3), 수공구세정(SSPC-SP2), 용제 세정(SSPC-SP1), 블라스트세정(SSPC-SP5, SSPC-SP6, SSPC-SP10), 수세척(SSPC-SP12), 및 미실시로 이루어진 군에서 선택된 하나 이상의 표면처리를 수행한 후, Power tool cleaning (SSPC-SP3), hand tool cleaning (SSPC-SP2), solvent cleaning (SSPC-SP1), blast cleaning (SSPC-SP5, SSPC-SP6, After performing at least one surface treatment selected from the group consisting of SSPC-SP10), water washing (SSPC-SP12), and not performing,

수용성 에폭시 하도 조성물(A)을 표면처리된 유성 도막에 도장하여 에폭시 하도를 형성하는 3 단계(S130)과 Step 3 (S130) of forming an epoxy primer by coating the water-soluble epoxy primer composition (A) on the surface-treated oil-based coating film;

수용성 우레탄 상도 조성물(B)을 상기 에폭시 하도에 도장하는 4 단계(S140)를 거쳐 유성 도막 상부에 수성 도막을 주름 및 부착 부실현상 등의 도막결함 발생 없이 형성하는 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법을 수행한다.A water-soluble coating material excellent in affinity with an oil-based coating film that forms a water-based coating film on the upper part of the oil-based coating film without occurrence of coating film defects such as wrinkles and poor adhesion through the fourth step (S140) of coating the water-soluble urethane topcoat composition (B) on the epoxy undercoat Perform the painting method used.

이때, 상기 수용성 에폭시 하도 조성물(A)은 At this time, the water-soluble epoxy primer composition (A) is

수용성 에폭시 수지 10 내지 50중량부, 방청안료 5 내지 30중량부, 편상 안료 1 내지 20중량부, 특수 방청 첨가제 0.1 내지 2중량부, 및 수용성 에폭시 경화제 50 내지 90중량부를 함유하는 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, 0.1 to 2 parts by weight of a special antirust additive, and 50 to 90 parts by weight of a water-soluble epoxy curing agent.

하도 형성용 수용성 에폭시 도료 조성물일 수 있다. It may be a water-soluble epoxy paint composition for forming an undercoat.

여기서, 상기 수용성 에폭시 수지들은 다습한 조건에서도 도장이 가능하므로 하도 형성용 수지로 사용될 수 있다.Here, the water-soluble epoxy resins can be used as a resin for forming a primer because coating is possible even in humid conditions.

그리고, 상기 하도 형성용 수용성 에폭시 도료 조성물에서,And, in the water-soluble epoxy paint composition for forming an undercoat,

상기 수용성 에폭시 수지는 자기유화성 에폭시(Self-emulsifiable Epoxy), 액상 에폭시 에멀젼(Liquid based epoxy emulsion), 반고상 에폭시 에멀젼(Semisolid based epoxy emulsion), 고상 에폭시 수지(Solid based epoxy emulsion), 및 페놀노볼락계 에멀젼(phenol novolac based emulsion)으로 이루어진 군에서 선택된 하나 이상일 수 있다. The water-soluble epoxy resin is self-emulsifiable epoxy, liquid based epoxy emulsion, semisolid based epoxy emulsion, solid based epoxy emulsion, and phenolo. It may be at least one selected from the group consisting of phenol novolac based emulsion.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물에서,In addition, in the water-soluble epoxy paint composition for forming an undercoat,

상기 방청안료는 화학적 또는 전기화학적 방법에 의해 금속의 부식을 방지할 수 있는 안료로서, 징크포스페이트(Zinc phosphate), 마그네슘포스페이트(Magnesium phosphate), 칼슘하이드로젠포스페이트(Calcium hydrogen phosphate), 스트론튬 알루미늄 폴리포스페이트 하이드레이트(Strontium aluminium polyphosphate hydrate), 칼슘 알루미늄 폴리포스페이트 실리케이트 하이드레이트(Calcium aluminium polyphosphate silicate hydrate), 징크 알루미늄 오르토포스페이트(Zinc aluminium orthophosphate), 징크 오르토포스페이트 하이드레이트(Zinc orthophosphate hydrate), 징크 몰리브데늄 오르토포스페이트 하이드레이트(Zinc molybdenum orthophosphate hydrate), 및 징크 알루미늄 폴리포스페이트 하이드레이트(Zinc aluminium polyphosphate hydrate)로 이루어진 군에서 선택된 하나일 수 있다.The rust preventive pigment is a pigment capable of preventing corrosion of metal by a chemical or electrochemical method, and includes zinc phosphate, magnesium phosphate, calcium hydrogen phosphate, and strontium aluminum polyphosphate. Strontium aluminum polyphosphate hydrate, calcium aluminum polyphosphate silicate hydrate, zinc aluminum orthophosphate, zinc orthophosphate hydrate, zinc molybdenum orthophosphate Zinc molybdenum orthophosphate hydrate), and zinc aluminum polyphosphate hydrate (Zinc aluminum polyphosphate hydrate) may be one selected from the group consisting of.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물에서, In addition, in the water-soluble epoxy paint composition for forming an undercoat,

상기 편상안료(barrier pigment)는 편상의 구조로 페인트 필름을 통한 수분 침투를 효과적으로 지연시킬 수 있는 안료로서, 마이카(Mica), 운모상 산화철(MIO, micaceous iron oxide), 글라스 플레이크(Glass flake), 및 알루미늄 플레이크(Aluminum flake)로 이루어진 군에서 선택된 하나 이상일 수 있다. The barrier pigment is a pigment that can effectively delay moisture penetration through the paint film with a flake-like structure, and includes mica, micaceous iron oxide (MIO), glass flake, And it may be at least one selected from the group consisting of aluminum flakes.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물에서, In addition, in the water-soluble epoxy paint composition for forming an undercoat,

상기 특수 방청 첨가제는 소듐나이트라이트(Sodium nitrite), 포타슘나이트라이트(Potassium nitrite), 리튬나이트라이트(Lithium nitrite), 소듐벤조에이트(Sodium benzoate), 티아졸(Thiazole), 이미다졸(Imidazole), 및 벤조트리아졸(Benzotriazole)로 이루어진 군에서 선택된 하나 이상일 수 있다.The special anti-rust additive is sodium nitrite, potassium nitrite, lithium nitrite, sodium benzoate, thiazole, imidazole, and It may be at least one selected from the group consisting of benzotriazole.

여기서, 특수 방청 첨가제는 철재의 부식을 방지하기 위해 첨가되는 데,Here, a special anti-rust additive is added to prevent corrosion of steel,

소듐, 포타슘 등과 같은 알칼리금속은 높은 이온화 경향성을 바탕으로 음극 방식으로 철재의 부식을 방지하며, 아질산염은 양극 억제제로서 양극 반응을 억제함으로써 철재 표면을 부동태화시켜 철재의 부식을 방지한다. 아질산염은 6 이하에서의 낮은 pH에서는 과산화질소와 산화질소를 발생시켜 효과가 없으며, 적용량이 낮을 경우에는 효과가 미비하며, 적용량이 높을 경우 질산염이 생성되며, 이로 인하여 오히려 부식방지 성능이 떨어질 수 있다.Alkali metals such as sodium and potassium prevent corrosion of iron materials in a cathodic manner based on their high ionization tendency, and nitrite as an anode inhibitor inhibits the anode reaction to passivate the surface of iron materials to prevent corrosion of iron materials. At low pH below 6, nitrite has no effect by generating nitric peroxide and nitric oxide, and when the applied amount is low, the effect is insignificant, and when the applied amount is high, nitrate is generated, which can lead to a decrease in corrosion prevention performance. .

이때, 특수 방청 첨가제를 0.1 내지 2 중량부, 바람직하게는 0.1 내지 1중량부의 양으로 사용할 수 있으며, 상기 범위로 사용할 때 다습한 조건에서의 습식 부식을 최소화하여 녹발생을 방지하는데 효과가 있다.In this case, the special anti-rust additive may be used in an amount of 0.1 to 2 parts by weight, preferably 0.1 to 1 part by weight, and when used in the above range, it is effective in preventing rust by minimizing wet corrosion in humid conditions.

상기 하도 형성용 수용성 에폭시 도료 조성물에 상기 특수 방청 첨가제뿐만 아니라 상기 방청안료를 함께 적용함으로써 방청 성능을 추가 보완하여 장기적으로 부식을 방지할 수 있다.By applying the special anti-rust additive as well as the anti-rust pigment to the water-soluble epoxy paint composition for forming the undercoat, the anti-rust performance can be further supplemented to prevent corrosion in the long term.

그리고, 상기 하도 형성용 수용성 에폭시 도료 조성물에서, And, in the water-soluble epoxy paint composition for forming an undercoat,

상기 수용성 에폭시 경화제는 페날카민(Phenalkamine), 폴리아미드(Polyamide), 폴리아민(Polyamine), 폴리아미도아민(Polyamidoamine), 및 알리파틱 아민(Aliphatic amine)으로 이루어진 군에서 선택된 하나 이상일 수 있다. The water-soluble epoxy curing agent may be at least one selected from the group consisting of phenalkamine, polyamide, polyamine, polyamidoamine, and aliphatic amine.

또한, 상기 하도 형성용 수용성 에폭시 도료 조성물은, In addition, the water-soluble epoxy paint composition for forming the undercoat,

(i) 수용성 에폭시 수지 10 내지 50 중량부, 방청안료 5 내지 30 중량부, 편상안료 1 내지 20 중량부, 특수 방청 첨가제 0.1 내지 2 중량부를 함유하는 주제부; 및(i) a main part containing 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, and 0.1 to 2 parts by weight of a special antirust additive; and

(ii) 수용성 에폭시 경화제 50 내지 90 중량부를 함유하는 경화제부;를 포함할 수 있다.(ii) a curing agent part containing 50 to 90 parts by weight of a water-soluble epoxy curing agent; may be included.

여기서, 상기 하도 형성용 수용성 에폭시 도료 조성물의 Here, the water-soluble epoxy paint composition for forming the undercoat

상기 (i) 주제부 및 (ii) 경화제부는 1:0.05 ~ 0.3의 중량비로 사용될 수 있다.The (i) main part and (ii) curing agent part may be used in a weight ratio of 1:0.05 to 0.3.

또한, 상기 수용성 우레탄 상도 조성물(B)은In addition, the water-soluble urethane topcoat composition (B) is

수산기-함유 폴리아크릴 수지 20 내지 70중량부, 체질안료 1 내지 30중량부, 수용성 우레탄 경화제 40 내지 90중량부, 및 필름 형성 보조제 15 내지 35중량부를 함유하는, 20 to 70 parts by weight of a hydroxyl group-containing polyacrylic resin, 1 to 30 parts by weight of an extender, 40 to 90 parts by weight of a water-soluble urethane curing agent, and 15 to 35 parts by weight of a film forming aid,

상도 형성용 수용성 우레탄 도료 조성물일 수 있다.It may be a water-soluble urethane paint composition for forming a top coat.

여기서, 상도는 수려한 미관 및 외부 노출의 특성상 우수한 내후성을 보유하여야 하며, 본 발명에서는 수성 타입의 우레탄 도료가 적용되고 있다.Here, the top coat must have excellent weather resistance due to the beautiful appearance and characteristics of external exposure, and in the present invention, a water-based type urethane paint is applied.

본 발명에 따른 상도 형성용 수용성 우레탄 수지는 1회의 도장으로도 40㎛ 이상의 도막을 형성할 수 있고, 2회의 도장으로는 대략 80㎛ 정도의 두꺼운 도막을 형성하는 것이 바람직할 수 있다.The water-soluble urethane resin for forming a top coat according to the present invention can form a coating film of 40 µm or more with one coat, and it may be preferable to form a thick coat of about 80 µm with two coats.

본 발명의 수용성 우레탄 도료 조성물로 된 우레탄 상도는 마이크로폼(Micro foam)을 제어하여 광택 저하 및 외관 불량이 발생되는 기포 및 팝핑(Popping) 현상을 줄이고 후도막으로 도장이 가능하다.The urethane topcoat made of the water-soluble urethane coating composition of the present invention can control micro-foam to reduce the bubble and popping phenomenon that causes gloss deterioration and poor appearance, and can be coated with a thick film.

또한, 상기 상도 형성용 수용성 우레탄 도료 조성물에서, In addition, in the water-soluble urethane paint composition for forming the top coat,

상기 수산기-함유 폴리아크릴 수지는 20 내지 70 중량부를 포함할 수 있다.The hydroxyl group-containing polyacrylic resin may include 20 to 70 parts by weight.

그리고, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,And, in the water-soluble urethane paint composition for forming the top coat,

상기 체질안료는 황산바륨, 활석, 실리카, 장석 및 탄산칼슘으로 이루어진 군에서 선택된 하나 이상일 수 있다.The extender pigment may be at least one selected from the group consisting of barium sulfate, talc, silica, feldspar and calcium carbonate.

또한, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,In addition, in the water-soluble urethane paint composition for forming the top coat,

상기 수용성 우레탄 경화제는 친수성기를 불포함한 TDI(Toluene Diisocyanate), MDI(Methylene Diphenyl Diisocyanate), HDI(Hexamethylene Diisocyanate), HDI(Hexamethylene Diisocyanate) 뷰렛, IPDI(Isophorone Diisocyanate), TDI 삼량체, HDI 삼량체 및 친수성기를 포함한 TDI(Toluene Diisocyanate), MDI(Methylene Diphenyl Diisocyanate), HDI(Hexamethylene Diisocyanate), HDI(Hexamethylene Diisocyanate) 뷰렛, IPDI(Isophorone Diisocyanate), TDI 삼량체, 및 HDI 삼량체로 이루어진 군에서 선택된 하나 이상일 수 있다.The water-soluble urethane curing agent contains a hydrophilic group-free TDI (Toluene Diisocyanate), MDI (Methylene Diphenyl Diisocyanate), HDI (Hexamethylene Diisocyanate), HDI (Hexamethylene Diisocyanate) burette, IPDI (Isophorone Diisocyanate), TDI trimer, HDI trimer and hydrophilic group It may be one or more selected from the group consisting of TDI (Toluene Diisocyanate), MDI (Methylene Diphenyl Diisocyanate), HDI (Hexamethylene Diisocyanate), HDI (Hexamethylene Diisocyanate) burette, IPDI (Isophorone Diisocyanate), TDI trimer, and HDI trimer including .

본 발명에 있어서, 수용성 우레탄 경화제는 친수성기를 포함한 이소시아네이트와 친수성기를 불포함한 이소시아네이트의 혼합 사용을 통하여 이루어진다. In the present invention, the water-soluble urethane curing agent is made through the mixed use of an isocyanate containing a hydrophilic group and an isocyanate not containing a hydrophilic group.

친수성기를 포함한 이소시아네이트의 경우, 이소시아네이트기(NCO)가 물과 반응하여 이산화탄소 가스를 발생하는 것을 친수성기가 사전에 물분자와 결합함으로써 방지한다. In the case of an isocyanate including a hydrophilic group, the isocyanate group (NCO) reacts with water to generate carbon dioxide gas, thereby preventing the hydrophilic group from bonding with a water molecule in advance.

친수성기를 불포함한 이소시아네이트는 친수성기를 포함한 이소시아네이트보다 반응속도가 느리기 때문에 반응속도를 제어하여 추후 물분자들이 빠져나올 수 있는 시간을 부여하며 기포 및 팝핑(Popping) 현상을 감소시킨다.Since the isocyanate without a hydrophilic group has a slower reaction rate than the isocyanate containing a hydrophilic group, the reaction rate is controlled to give time for water molecules to escape later, and bubbles and popping are reduced.

친수성기를 포함한 이소시아네이트와 친수성기를 불포함한 이소시아네이트의 경우 혼합 비율이 기포 및 팝핑(Popping) 현상에 크게 영향을 미치므로, 1:0.3 ~ 0.9의 중량비로 혼합하여 사용한다.In the case of the isocyanate containing a hydrophilic group and the isocyanate without a hydrophilic group, the mixing ratio greatly affects the bubble and popping phenomenon, so it is used by mixing it in a weight ratio of 1:0.3 to 0.9.

또한, 상기 상도 형성용 수용성 우레탄 도료 조성물에서,In addition, in the water-soluble urethane paint composition for forming the top coat,

상기 필름 형성 보조제는 PMA(propylene glycol methyl ether acetate), PGDA(Propylene Glycol Diacetate), 부틸아세테이트, 및 에틸아세테이트로 이루어진 군에서 선택된 하나 이상일 수 있다.The film forming aid may be at least one selected from the group consisting of propylene glycol methyl ether acetate (PMA), propylene glycol diacetate (PGDA), butyl acetate, and ethyl acetate.

여기서, 상기 필름 형성 보조제는 수지에 대한 용해력이 우수한 것을 사용할 수 있고, 이에 의해, 도막의 평활성 및 기포 및 팝핑 제어를 추구할 수 있다.Here, the film forming aid may be used to have excellent solubility in resin, thereby pursuing smoothness of the coating film and control of foaming and popping.

그리고, 상기 상도 형성용 수용성 우레탄 도료 조성물은,And, the water-soluble urethane paint composition for forming the top coat,

(iii) 상기 수산기-함유 폴리아크릴 수지 20 내지 70 중량부 및 상기 체질안료 1 내지 30 중량부를 함유하는 주제부; 및(iii) a main part containing 20 to 70 parts by weight of the hydroxyl group-containing polyacrylic resin and 1 to 30 parts by weight of the extender; and

(iv) 상기 수용성 우레탄 경화제 40 내지 90 중량부 및 상기 필름 형성 보조제 15 내지 35 중량부를 함유하는 경화제부;를 포함할 수 있다.(iv) a curing agent part containing 40 to 90 parts by weight of the water-soluble urethane curing agent and 15 to 35 parts by weight of the film forming aid; may include.

또한, 상기 상도 형성용 수용성 우레탄 도료 조성물의In addition, the water-soluble urethane paint composition for forming the top coat

상기 (iii) 주제부 및 (iv) 경화제부는 1:0.05 ~ 0.3의 중량비로 사용될 수 있다.The (iii) main part and (iv) curing agent part may be used in a weight ratio of 1:0.05 to 0.3.

친환경 중방식 도막Eco-friendly medium-proof coating film

본 발명은 상기 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법으로 제조된 The present invention is prepared by a coating method using a water-soluble coating material having excellent affinity with the oil-based coating film.

표면 처리된 유성 도막, 수용성 에폭시 하도 조성물(A)로 도장된 에폭시 하도, 및 수용성 우레탄 상도 조성물(B)로 도장된 우레탄 상도를 포함하는,Containing a surface-treated oil-based coating film, an epoxy primer coated with a water-soluble epoxy primer composition (A), and a urethane topcoat coated with a water-soluble urethane topcoat composition (B),

친환경 중방식 도막을 제공한다.It provides an eco-friendly medium-proof coating film.

여기서, 상기 표면 처리된 유성 도막은 아크릴 타입, 알키드 타입, 에폭시 타입, 무기질 타입, 및 우레탄 타입의 유성 도막으로 이루어진 군에서 선택된 하나 이상일 수 있다.Here, the surface-treated oil-based coating film may be at least one selected from the group consisting of an acrylic-type, alkyd-type, epoxy-type, inorganic-type, and urethane-type oil-based coating film.

또한, 본 발명의 일 실시예에 따르면, 상기 수용성 에폭시 하도는 30 ㎛ ~ 300 ㎛의 건조 두께를 가질 수 있고; 상기 수용성 우레탄 상도는 20 ㎛ ~ 100 ㎛의 건조 두께를 가질 수 있고, 또한 상기 친환경 중방식 도막은 50 ㎛ ~ 400 ㎛의 건조 두께를 가질 수 있다.In addition, according to an embodiment of the present invention, the water-soluble epoxy primer may have a dry thickness of 30 μm to 300 μm; The water-soluble urethane topcoat may have a dry thickness of 20 µm to 100 µm, and the eco-friendly medium-proof coating film may have a dry thickness of 50 µm to 400 µm.

본 발명의 일 실시예에 따르면, 상기 수용성 에폭시 하도 및 수용성 우레탄 상도는 각각 2회 이상 설치될 수 있다. 이때, 각각의 도막은 완전히 또는 적절히 건조된 다음에 다음 도막을 설치할 수 있다. 상기 도막의 적절한 건조는 손으로 누르거나 가볍게 문지를 때, 자국이 남거나 묻어나지 않는 정도를 의미할 수 있다.According to an embodiment of the present invention, the water-soluble epoxy undercoat and the water-soluble urethane top coat may be installed two or more times, respectively. At this time, after each coating film is completely or properly dried, the next coating film can be installed. Proper drying of the coating film may mean a degree to which marks are not left or smeared when pressed by hand or lightly rubbed.

본 발명의 일 실시예에 따르면, 상기 수용성 에폭시 하도 및 수용성 우레탄 상도 사이에, 하도 형성용 수용성 에폭시 도료 조성물로부터 형성된 중도를 더 포함할 수 있다.According to an embodiment of the present invention, between the water-soluble epoxy primer and the water-soluble urethane topcoat, a middle layer formed from a water-soluble epoxy paint composition for forming a primer may be further included.

상기 하도와 중도는 실질적으로 동일한 에폭시 도료 조성물을 2회 도포하는 것으로서, 구체적으로는, 하도 형성용 수용성 에폭시 도료 조성물을 먼저 도포하여 수용성 에폭시 하도를 형성시키고, 필요에 따라 수용성 에폭시 하도를 완전히 또는 적절히 건조시킨 다음, 하도 형성용 수용성 에폭시 도료 조성물을 한번 더 도포하여 중도를 형성시킴으로써 수행될 수 있다. 하도 및 중도의 두께는 특별히 제한되지 않으나, 상술한 범위에서 선택될 수 있다.The undercoat and the intermediate coat are two coats of substantially the same epoxy paint composition. Specifically, the water-soluble epoxy paint composition for forming an undercoat is first applied to form a water-soluble epoxy undercoat, and, if necessary, the water-soluble epoxy undercoat is completely or properly applied. After drying, the water-soluble epoxy paint composition for forming an undercoat is applied once more to form a middle coat. The thickness of the lower coat and the middle coat is not particularly limited, but may be selected from the above-mentioned range.

본 발명의 친화경 중방식 도막의 하나의 이점에 따르면, 하도 형성용 수용성 에폭시 도료 조성물로부터 형성된 수용성 에폭시 하도는 다습한 환경에서 우수한 내수성 및 방청성을 나타내며, 상도 형성용 수용성 우레탄 도료 조성물로부터 형성된 수용성 우레탄 상도는 우수한 기계적 물성을 나타낸다. According to one advantage of the affinity medium anticorrosion coating film of the present invention, the water-soluble epoxy primer formed from the water-soluble epoxy paint composition for forming a base coat exhibits excellent water resistance and rust resistance in a humid environment, and a water-soluble urethane formed from the water-soluble urethane paint composition for forming a top coat. The top coat shows excellent mechanical properties.

이러한 수용성 에폭시 하도 및 수용성 우레탄 상도는 서로 물성 및 기능을 보완함으로써, 다습한 환경에서 우수한 내수성 및 방청성을 나타내며, 이러한 물성을 장기간 유지할 수 있는 우수한 내구성을 또한 나타낸다.These water-soluble epoxy primers and water-soluble urethane topcoats complement each other in physical properties and functions, thereby exhibiting excellent water resistance and rust prevention in a humid environment, and also exhibiting excellent durability to maintain these properties for a long period of time.

이하에서, 실시예를 통하여 본 발명을 보다 상세히 설명한다. 그러나, 하기의 실시예는 본 발명을 더욱 구체적으로 설명하기 위한 것으로서, 본 발명의 범위가 하기의 실시예에 의하여 한정되는 것은 아니다. 하기의 실시예는 본 발명의 범위 내에서 당업자에 의해 적절히 수정, 변경될 수 있다.Hereinafter, the present invention will be described in more detail through examples. However, the following examples are provided to explain the present invention in more detail, and the scope of the present invention is not limited by the following examples. The following examples can be appropriately modified and changed by those skilled in the art within the scope of the present invention.

<준비예><Preparation example>

유성 알키드계 도료인 KS 6020 종 2급 도료를 도장한 강재를 준비하였다.A steel material coated with KS 6020 class 2 paint, which is an oil-based alkyd paint, was prepared.

<실시예> 및 <시험예><Example> and <Test Example>

<실시예 1> 수용성 에폭시 도료 조성물(A-1)의 제조<Example 1> Preparation of water-soluble epoxy paint composition (A-1)

수용성 에폭시 수지(국도화학, KEM-134-60) 300 g, 습윤분산제(BYKChemie,Disperbyk-199) 5 g, 소포제(BYK-Chemie, BYK-021) 5 g, 증점제(DOW, Acrysol SCT-275) 10 g, 방청안료(SIGMA, Zinc phosphate) 140g, 특수 방청 첨가제(ALFA, Potassium nitrite) 2 g, 티타늄 다이옥사이드(Dupont, Ti pure R-706) 150 g, 물 208 g, 편상안료(Avention, Super Grade Mica Powder) 100 g 및 구상안료(SAC, S-SIL 5) 80 g을 배합용기에 투입한 다음, 고속교반기를 이용하여 1,500 rpm ~ 1,800 rpm으로 1 시간 이상 분산 교반하여 에폭시 주제부를 제조하였다.Water-soluble epoxy resin (Kukdo Chemical, KEM-134-60) 300 g, wetting and dispersing agent (BYKChemie, Disperbyk-199) 5 g, defoaming agent (BYK-Chemie, BYK-021) 5 g, thickener (DOW, Acrysol SCT-275) 10 g, anti-rust pigment (SIGMA, zinc phosphate) 140 g, special anti-rust additive (ALFA, Potassium nitrite) 2 g, titanium dioxide (Dupont, Ti pure R-706) 150 g, water 208 g, flake pigment (Avention, Super Grade) Mica Powder) 100 g and spherical pigment (SAC, S-SIL 5) 80 g were put into a mixing container, and then dispersed and stirred at 1,500 rpm to 1,800 rpm for 1 hour or more using a high-speed stirrer to prepare an epoxy main part.

다음으로, 수용성 경화제 수지(국도화학, KH-748) 750 g, 물 250 g을 배합용기에 투입한 다음, 고속교반기를 이용하여 1,500 rpm으로 30 분 이상 분산 교반하여 에폭시 경화제부를 제조하였다.Next, 750 g of a water-soluble curing agent resin (Kukdo Chemical, KH-748) and 250 g of water were put into a mixing container, and then dispersed and stirred at 1,500 rpm for 30 minutes or more using a high-speed stirrer to prepare an epoxy curing agent part.

상기 제조된 에폭시 주제부 및 에폭시 경화제부를 1:0.2의 중량비로 혼합하여 1,500 rpm으로 5분간 교반하여 하기 표 1과 같이 수용성 에폭시 도료 조성물(A-1)을 제조하였다.The prepared epoxy main part and the epoxy curing agent part were mixed in a weight ratio of 1:0.2 and stirred at 1,500 rpm for 5 minutes to prepare a water-soluble epoxy paint composition (A-1) as shown in Table 1 below.

<실시예 2> 수용성 에폭시 도료 조성물(A-2)의 제조<Example 2> Preparation of water-soluble epoxy paint composition (A-2)

실시예 1에서와 유사하게 진행하여, 수용성 에폭시 주제부에서 특수 방청 첨가제(ALFA, Potassium nitrite) 15 g 및 물 195 g을 사용하는 것을 제외하고는, 다른 성분들을 모두 동일하게 사용하여, 수용성 에폭시 주제부 및 수용성 에폭시 경화제부를 제조하였다.Proceeding similarly to Example 1, except for using 15 g of a special anti-rust additive (ALFA, Potassium nitrite) and 195 g of water in the water-soluble epoxy main part, using all other components the same, A part and a water-soluble epoxy curing agent part were prepared.

또한, 실시예 1에서와 동일하게, 상기 수용성 에폭시 주제부 및 수용성 에폭시 경화제부로부터 하기 표 1과 같이 수용성 에폭시 도료 조성물(A-2)을 제조하였다.In addition, in the same manner as in Example 1, a water-soluble epoxy paint composition (A-2) was prepared from the water-soluble epoxy main part and the water-soluble epoxy curing agent part as shown in Table 1 below.

<실시예 3> 수용성 우레탄 도료 조성물(B-1)의 제조<Example 3> Preparation of water-soluble urethane coating composition (B-1)

물 100 g, 습윤분산제(BYK-Chemie, Disperbyk-199) 5 g, 소포제(BYK-Chemie, BYK-021) 5 g, 티타늄 다이옥사이드(Dupont, Ti pure R-706) 170 g, 체질안료(대명케미칼, 황산바륨) 80 g을 균일하게 혼합하고 볼밀로 약 2 시간 연화하는 연화공정을 진행하였다.Water 100 g, wetting and dispersing agent (BYK-Chemie, Disperbyk-199) 5 g, defoaming agent (BYK-Chemie, BYK-021) 5 g, titanium dioxide (Dupont, Ti pure R-706) 170 g, extender pigment (Daemyung Chemical) , barium sulfate) was uniformly mixed with 80 g and a softening process was performed with a ball mill for about 2 hours.

연화공정 후, 상기의 연화물 360 g에 수산기-함유 폴리아크릴 수지(Covestro, Bayhydrol A2470) 550 g, 증점제(DOW, Acrysol SCT-275) 20 g, 물 70 g을 후첨하여 약 1 시간 배합하는 공정을 진행하였다. After the softening process, a process of post-addition of 550 g of hydroxyl-containing polyacrylic resin (Covestro, Bayhydrol A2470), 20 g of thickener (DOW, Acrysol SCT-275), and 70 g of water to 360 g of the softened product for about 1 hour. proceeded.

경화제부는 친수성기-포함 이소시아네이트 화합물(Covestro, Bayhydur ultra 2487/1) 400 g, 친수성기-불포함 이소시아네이트 화합물(Tosoh, Coronate HXR) 400 g, 필름 형성 보조제(Dow, Dowanol PMA) 200 g을 배합용기에 투입한 다음, 고속교반기를 이용하여 1,500 rpm으로 30 분 이상 교반하여 분산시켰다.In the curing agent part, 400 g of a hydrophilic group-containing isocyanate compound (Covestro, Bayhydur ultra 2487/1), 400 g of a hydrophilic group-free isocyanate compound (Tosoh, Coronate HXR), and 200 g of a film forming aid (Dow, Dowanol PMA) were added to the mixing container. Next, using a high-speed stirrer, the mixture was dispersed by stirring at 1,500 rpm for 30 minutes or more.

상기 제조된 수용성 우레탄 주제부 및 수용성 우레탄 경화제부를 대략 1:0.2의 중량비로 혼합하여 1,500 rpm으로 5 분간 교반하여 하기 표 2와 같이 수용성 우레탄 도료 조성물(B-1)을 제조하였다.The water-soluble urethane main part and the water-soluble urethane curing agent prepared above were mixed in a weight ratio of about 1:0.2 and stirred at 1,500 rpm for 5 minutes to prepare a water-soluble urethane coating composition (B-1) as shown in Table 2 below.

<실시예 4> 수용성 우레탄 도료 조성물(B-2)의 제조<Example 4> Preparation of water-soluble urethane coating composition (B-2)

주제부는 실시예 3에서와 동일하게 제조하였다. The main part was prepared in the same manner as in Example 3.

경화제부는, 친수성기-포함 이소시아네이트 화합물(Covestro, Bayhydur ultra 2487/1)을 과량(600 g)으로, 친수성-불포함 이소시아네이트 화합물(Tosoh, Coronate HXR)을 소량(200 g)으로 사용하지만 필름 형성 보조제(Dow, Dowanol PMA) 200 g을 함께 사용하여, 실시예 3에서와 동일하게 제조하였다. The curing agent part uses an excess (600 g) of a hydrophilic group-containing isocyanate compound (Covestro, Bayhydur ultra 2487/1) and a small amount (200 g) of a hydrophilic-free isocyanate compound (Tosoh, Coronate HXR), but a film forming aid (Dow) , Dowanol PMA) was used together with 200 g, and prepared in the same manner as in Example 3.

상기 제조된 우레탄 주제부 및 우레탄 경화제부를 대략 1:0.2의 중량비로 혼합하여 1,500 rpm으로 5 분간 교반하여 하기 표 2와 같이 수용성 우레탄 도료 조성물(B-2)을 제조하였다.The prepared urethane main part and the urethane curing agent part were mixed in a weight ratio of about 1:0.2 and stirred at 1,500 rpm for 5 minutes to prepare a water-soluble urethane coating composition (B-2) as shown in Table 2 below.

구분division 실시예 1Example 1 실시예 2Example 2 수용성 에폭시 주제부water soluble epoxy 수용성 에폭시 수지water-soluble epoxy resin 300300 300300 습윤분산제wetting and dispersing agent 55 55 소포제antifoam 55 55 증점제thickener 1010 1010 방청안료anti-rust pigment 140140 140140 특수방청 첨가제Special anti-rust additive 22 1515 티타니아 다이옥사이드titania dioxide 150150 150150 물water 208208 195195 편상안료flake pigment 100100 100100 구상안료spherical pigment 8080 8080 수용성 에폭시 경화제부Water-soluble epoxy curing agent part 수용성 경화제 수지Water-soluble hardener resin 750750 750750 물water 250250 250250

구분division 실시예 3Example 3 실시예 4Example 4 수용성 우레탄
주제부water soluble urethane
subject part 연화공정softening process 물water 100100 100100 습윤분산제wetting and dispersing agent 55 55 소포제antifoam 55 55 티타늄 다이옥사이드titanium dioxide 170170 170170 체질안료body pigment 8080 8080 후첨 배합공정Post-addition compounding process 수산기-함유 폴리아크릴 수지Hydroxyl group-containing polyacrylic resin 550550 550550 증점제thickener 2020 2020 물water 7070 7070 수용성 우레탄 경화제부Water-soluble urethane curing agent part 친수성-포함 이소시아네이트 화합물Hydrophilic-comprising isocyanate compounds 400400 600600 친수성-불포함 이소시아네이트 화합물Hydrophilic-Free Isocyanate Compounds 400400 200200 필름 형성 보조제film forming aid 200200 200200

<비교예 1> 에폭시 마스틱계 유성 도료<Comparative Example 1> Epoxy mastic based oil paint

유성 도료로 에폭시 마스틱계 제품은 제조사 삼화페인트의 슈퍼폭시 360 제품을 선정하였다.As an oil-based paint, the Super Foxy 360 product of Samhwa Paint was selected for the epoxy mastic-based product.

<비교예 2> 우레탄 유성 도료<Comparative Example 2> Urethane oil-based paint

유성 도료로 우레탄 상도 제품은 제조사 삼화페인트의 슈퍼탄 300BG 제품을 선정하였다.As an oil-based paint, Supertan 300BG of Samhwa Paint was selected for the urethane topcoat product.

<시험예> KS M 6020 유성도료 1종 조합도료 2급 위 재도장성 평가<Test Example> KS M 6020 Oil-Based Paint Type 1 Combination Paint Grade 2 Repaintability Evaluation

상기 실시예 1 내지 실시예 4와 비교예 1 내지 비교예 2를 유성 알키드계 도료인 KS M 6020 유성도료 1종 조합도료 2급에 준하는 제조사 삼화페인트의 KS M 6020 유성도료 1종 조합페인트 2급이 도장된 강재 시험편에 재도장 간격 별 도장 후 표 3과 같이 외관을 평가하였다. 또한, 재도장 간격 48 시간 후 외관 사진을 표 4에 나타내었다. The above Examples 1 to 4 and Comparative Examples 1 to 2 were used as an oil-based alkyd-based paint, KS M 6020 oil-based paint 1 type combination paint 2nd grade KS M 6020 oil-based paint 1 type combination paint 2nd grade of Samhwa Paints Appearance was evaluated as shown in Table 3 after repainting for each repainting interval on this coated steel test piece. In addition, a photograph of the appearance after 48 hours of repainting is shown in Table 4.

실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 비교예1Comparative Example 1 비교예2Comparative Example 2 5시간5 hours ◎◎ ◎◎ ◎◎ ◎◎ XX XX 24시간24 hours ◎◎ ◎◎ ◎◎ ◎◎ XX XX 48시간48 hours ◎◎ ◎◎ ◎◎ ◎◎ △△ XX

◎ (우수), ○ (양호), △(보통), X (불량) ◎ (Excellent), ○ (Good), △ (Normal), X (Poor)

실시예1Example 1 실시예2Example 2 실시예3Example 3 48 시간 후
외관 사진after 48 hours
Exterior Photo

Figure 112020128185438-pat00001
Figure 112020128185438-pat00001
Figure 112020128185438-pat00002
Figure 112020128185438-pat00002
Figure 112020128185438-pat00003
Figure 112020128185438-pat00003
 실시예4Example 4 비교예1Comparative Example 1 비교예2Comparative Example 2 48 시간 후
외관 사진after 48 hours
Exterior Photo
Figure 112020128185438-pat00004
Figure 112020128185438-pat00004
Figure 112020128185438-pat00005
Figure 112020128185438-pat00005
Figure 112020128185438-pat00006
Figure 112020128185438-pat00006

상기 표 3 및 표 4에서와 같이, 유성 알키드계 도료인 KS M 6020 유성도료 1종 조합도료 2급이 도장된 강재의 유성 도막에 후속으로 실시예 1 내지 실시예 4와 비교예 1 및 비교예 2의 각 도료를 상기 유성 도막을 제거하지 않고 도장한 후 외관 평가한 결과, 실시예 1 내지 실시예 4의 경우 주름 및 부풀음이 없었고 표면 형상이 매끈하고 미려하였으므로, 비교예 1 및 비교예 2 보다 도막 형상이 우수함을 확인할 수 있었다. As shown in Tables 3 and 4 above, Examples 1 to 4 and Comparative Examples 1 and Comparative Examples were subsequently applied to the oil-based coating film of steel coated with KS M 6020 oil-based alkyd-based paint, first-class combination paint, second grade. As a result of evaluating the appearance of each paint of 2 without removing the oil-based coating film, in Examples 1 to 4, there were no wrinkles and swelling, and the surface shape was smooth and beautiful, so compared to Comparative Examples 1 and 2 It was confirmed that the coating film shape was excellent.

지금까지 본 발명에 따른 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법 및 이로부터 제조된 친환경 중방식 도막에 관한 구체적인 실시예에 관하여 설명하였으나, 본 발명의 범위에서 벗어나지 않는 한도 내에서는 여러 가지 실시 변형이 가능함은 자명하다.Specific examples of the coating method using the water-soluble coating material having excellent affinity with the oil-based coating film according to the present invention and the eco-friendly heavy-duty coating film manufactured therefrom have been described. It is obvious that transformation is possible.

그러므로 본 발명의 범위는 설명된 실시예에 국한되어 정해져서는 안 되며, 후술하는 특허청구범위뿐만 아니라 이 특허청구범위와 균등한 것들에 의해 정해져야 한다.Therefore, the scope of the present invention should not be limited to the described embodiments, but should be defined by the following claims as well as the claims and equivalents.

즉, 전술된 실시예는 모든 면에서 예시적인 것이며, 한정적인 것이 아닌 것으로 이해되어야 하며, 본 발명의 범위는 상세한 설명보다는 후술될 특허청구범위에 의하여 나타내어지고, 그 특허청구범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.That is, it should be understood that the above-described embodiments are illustrative in all respects and not restrictive, and the scope of the present invention is indicated by the claims to be described later rather than the detailed description, and the meaning and scope of the claims; All changes or modifications derived from the concept of equivalents thereof should be construed as being included in the scope of the present invention.

Claims (19)

유성 도막을 도장하거나 도장되어 있는 1 단계;
도장된 유성 도막을 제거하지 않고, 동력공구 세정(SSPC-SP3), 수공구 세정(SSPC-SP2), 용제 세정(SSPC-SP1), 및 세정하지 않음으로 이루어진 군에서 선택된 하나 이상으로 표면처리하는 2 단계;
수용성 에폭시 하도 조성물(A)을 표면처리된 유성 도막에 도장하여 에폭시 하도를 형성하는 3 단계; 및
수용성 우레탄 상도 조성물(B)을 상기 에폭시 하도에 도장하는 4 단계;를 포함하고,
상기 수용성 에폭시 하도 조성물(A)은 수용성 에폭시 수지 10 내지 50 중량부, 방청안료 5 내지 30 중량부, 편상 안료 1 내지 20 중량부, 특수 방청 첨가제 0.1 내지 2 중량부, 및 수용성 에폭시 경화 제 50 내지 90 중량부를 함유하는 하도 형성용 수용성 에폭시 도료 조성물이며,
상기 특수 방청 첨가제는 소듐나이트라이트(Sodium nitrite), 포타슘나이트 라이트(Potassium nitrite), 리튬나이트라이트(Lithium nitrite), 티아졸(Thiazole), 이미다졸(Imidazole), 및 벤조트리아졸(Benzotriazole)로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
Step 1 of painting or painting an oil-based coating;
Surface treatment with one or more selected from the group consisting of power tool cleaning (SSPC-SP3), hand tool cleaning (SSPC-SP2), solvent cleaning (SSPC-SP1), and no cleaning without removing the painted oil-based coating 2 step;
Step 3 of coating the water-soluble epoxy primer composition (A) on the surface-treated oil-based coating film to form an epoxy primer; and
4 step of coating the water-soluble urethane topcoat composition (B) on the epoxy undercoat;
The water-soluble epoxy primer composition (A) contains 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, 0.1 to 2 parts by weight of a special antirust additive, and 50 to 50 parts by weight of a water-soluble epoxy curing agent. It is a water-soluble epoxy paint composition for forming an undercoat containing 90 parts by weight,
The special anti-rust additive is made of sodium nitrite, potassium nitrite, lithium nitrite, thiazole, imidazole, and benzotriazole. Characterized in that at least one selected from the group,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제1항에 있어서,
상기 유성 도막은 아크릴 타입, 알키드 타입, 에폭시 타입, 무기질 타입, 및 우레탄 타입의 유성 도막으로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
According to claim 1,
The oil-based coating film is characterized in that at least one selected from the group consisting of an acrylic type, an alkyd type, an epoxy type, an inorganic type, and a urethane type oil-based coating film
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 삭제delete 삭제delete 제1항에 있어서,
상기 수용성 우레탄 상도 조성물(B)은
수산기-함유 폴리아크릴 수지 20 내지 70중량부, 체질안료 1 내지 30중량부, 수용성 우레탄 경화제 40 내지 90중량부, 및 필름 형성 보조제 15 내지 35중량부를 함유하는,
상도 형성용 수용성 우레탄 도료 조성물인 것을 특징으로 하는
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
According to claim 1,
The water-soluble urethane topcoat composition (B) is
20 to 70 parts by weight of a hydroxyl group-containing polyacrylic resin, 1 to 30 parts by weight of an extender, 40 to 90 parts by weight of a water-soluble urethane curing agent, and 15 to 35 parts by weight of a film forming aid,
It is characterized in that it is a water-soluble urethane paint composition for forming a top coat.
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 1 항에 있어서,
상기 하도 형성용 수용성 에폭시 도료 조성물에서,
상기 수용성 에폭시 수지는 자기유화성 에폭시(Self-emulsifiable Epoxy), 액상 에폭시 에멀젼(Liquid based epoxy emulsion), 반고상 에폭시 에멀젼(Semisolid based epoxy emulsion), 고상 에폭시 수지(Solid based epoxy emulsion), 및 페놀노볼락계 에멀젼(phenol novolac based emulsion)으로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
The method of claim 1,
In the water-soluble epoxy paint composition for forming an undercoat,
The water-soluble epoxy resin is a self-emulsifiable epoxy, a liquid based epoxy emulsion, a semisolid based epoxy emulsion, a solid based epoxy emulsion, and a phenolo. Characterized in that at least one selected from the group consisting of a rock-based emulsion (phenol novolac based emulsion),
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 1 항에 있어서,
상기 하도 형성용 수용성 에폭시 도료 조성물에서,
상기 방청안료는 징크포스페이트(Zinc phosphate), 마그네슘포스페이트(Magnesium phosphate), 칼슘하이드로젠포스페이트(Calcium hydrogen phosphate), 스트론튬 알루미늄 폴리포스페이트 하이드레이트(Strontium aluminium polyphosphate hydrate), 칼슘 알루미늄 폴리포스페이트 실리케이트 하이드레이트(Calcium aluminium polyphosphate silicate hydrate), 징크 알루미늄 오르토포스페이트(Zinc aluminium orthophosphate), 징크 오르토포스페이트 하이드레이트(Zinc orthophosphate hydrate), 징크 몰리브데늄 오르토포스페이트 하이드레이트(Zinc molybdenum orthophosphate hydrate), 및 징크 알루미늄 폴리포스페이트 하이드레이트(Zinc aluminium polyphosphate hydrate)로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
The method of claim 1,
In the water-soluble epoxy paint composition for forming an undercoat,
The rust preventive pigment is zinc phosphate, magnesium phosphate, calcium hydrogen phosphate, strontium aluminum polyphosphate hydrate, calcium aluminum polyphosphate silicate hydrate. silicate hydrate), zinc aluminum orthophosphate, zinc orthophosphate hydrate, zinc molybdenum orthophosphate hydrate, and zinc aluminum polyphosphate hydrate (Zinc aluminium) Characterized in that at least one selected from the group consisting of
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 1 항에 있어서,
상기 하도 형성용 수용성 에폭시 도료 조성물에서,
상기 편상안료(barrier pigment)는 마이카(Mica), 운모상 산화철(MIO, micaceous iron oxide), 글라스 플레이크(Glass flake), 및 알루미늄 플레이크(Aluminum flake)로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
The method of claim 1,
In the water-soluble epoxy paint composition for forming an undercoat,
The flake pigment (barrier pigment) is characterized in that at least one selected from the group consisting of mica (Mica), mica-like iron oxide (MIO, micaceous iron oxide), glass flake, and aluminum flake (Aluminum flake),
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 삭제delete 제 1 항에 있어서,
상기 하도 형성용 수용성 에폭시 도료 조성물에서,
상기 수용성 에폭시 경화제는 페날카민(Phenalkamine), 폴리아미드(Polyamide), 폴리아민(Polyamine), 폴리아미도아민(Polyamidoamine), 및 알리파틱 아민(Aliphatic amine)으로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
The method of claim 1,
In the water-soluble epoxy paint composition for forming an undercoat,
The water-soluble epoxy curing agent is characterized in that at least one selected from the group consisting of phenalkamine, polyamide, polyamine, polyamidoamine, and aliphatic amine,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 1 항에 있어서,
상기 하도 형성용 수용성 에폭시 도료 조성물은,
(i) 수용성 에폭시 수지 10 내지 50 중량부, 방청안료 5 내지 30 중량부, 편상안료 1 내지 20 중량부, 특수 방청 첨가제 0.1 내지 2 중량부를 함유하는 주제부; 및
(ii) 수용성 에폭시 경화제 50 내지 90 중량부를 함유하는 경화제부;를 포함하는 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
The method of claim 1,
The water-soluble epoxy paint composition for forming an undercoat comprises:
(i) a main part containing 10 to 50 parts by weight of a water-soluble epoxy resin, 5 to 30 parts by weight of a rust preventive pigment, 1 to 20 parts by weight of a flake pigment, and 0.1 to 2 parts by weight of a special antirust additive; and
(ii) a curing agent part containing 50 to 90 parts by weight of a water-soluble epoxy curing agent;
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 11 항에 있어서,
상기 하도 형성용 수용성 에폭시 도료 조성물의
상기 (i) 주제부 및 (ii) 경화제부는 1:0.05 ~ 0.3의 중량비로 사용되는 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
12. The method of claim 11,
of the water-soluble epoxy paint composition for forming the undercoat
The (i) main part and (ii) curing agent part are used in a weight ratio of 1:0.05 to 0.3,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 삭제delete 제 5 항에 있어서,
상기 상도 형성용 수용성 우레탄 도료 조성물에서,
상기 체질안료는 황산바륨, 활석, 실리카, 장석 및 탄산칼슘으로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
6. The method of claim 5,
In the water-soluble urethane paint composition for forming the top coat,
The extender pigment is characterized in that at least one selected from the group consisting of barium sulfate, talc, silica, feldspar and calcium carbonate,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 5 항에 있어서,
상기 상도 형성용 수용성 우레탄 도료 조성물에서,
상기 수용성 우레탄 경화제는 친수성기를 불포함한 TDI(Toluene Diisocyanate), MDI(Methylene Diphenyl Diisocyanate), HDI(Hexamethylene Diisocyanate), HDI(Hexamethylene Diisocyanate) 뷰렛, IPDI(Isophorone Diisocyanate), TDI 삼량체, HDI 삼량체 및 친수성기를 포함한 TDI(Toluene Diisocyanate), MDI(Methylene Diphenyl Diisocyanate), HDI(Hexamethylene Diisocyanate), HDI(Hexamethylene Diisocyanate) 뷰렛, IPDI(Isophorone Diisocyanate), TDI 삼량체, 및 HDI 삼량체로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
6. The method of claim 5,
In the water-soluble urethane paint composition for forming the top coat,
The water-soluble urethane curing agent contains a hydrophilic group-free TDI (Toluene Diisocyanate), MDI (Methylene Diphenyl Diisocyanate), HDI (Hexamethylene Diisocyanate), HDI (Hexamethylene Diisocyanate) burette, IPDI (Isophorone Diisocyanate), TDI trimer, HDI trimer and hydrophilic group It is characterized in that at least one selected from the group consisting of TDI (Toluene Diisocyanate), MDI (Methylene Diphenyl Diisocyanate), HDI (Hexamethylene Diisocyanate), HDI (Hexamethylene Diisocyanate) burette, IPDI (Isophorone Diisocyanate), TDI trimer, and HDI trimer including to do,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 5 항에 있어서,
상기 상도 형성용 수용성 우레탄 도료 조성물에서,
상기 필름 형성 보조제는 PMA(propylene glycol methyl ether acetate), PGDA(Propylene Glycol Diacetate), 부틸아세테이트, 및 에틸아세테이트로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
6. The method of claim 5,
In the water-soluble urethane paint composition for forming the top coat,
The film forming aid is characterized in that at least one selected from the group consisting of propylene glycol methyl ether acetate (PMA), propylene glycol diacetate (PGDA), butyl acetate, and ethyl acetate,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 5 항에 있어서,
상기 상도 형성용 수용성 우레탄 도료 조성물은,
(iii) 상기 수산기-함유 폴리아크릴 수지 20 내지 70 중량부 및 상기 체질안료 1 내지 30 중량부를 함유하는 주제부; 및
(iv) 상기 수용성 우레탄 경화제 40 내지 90 중량부 및 상기 필름 형성 보조제 15 내지 35 중량부를 함유하는 경화제부;를 포함하는 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
6. The method of claim 5,
The water-soluble urethane paint composition for forming the top coat comprises:
(iii) a main part containing 20 to 70 parts by weight of the hydroxyl group-containing polyacrylic resin and 1 to 30 parts by weight of the extender; and
(iv) a curing agent part containing 40 to 90 parts by weight of the water-soluble urethane curing agent and 15 to 35 parts by weight of the film forming aid;
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 17 항에 있어서,
상기 상도 형성용 수용성 우레탄 도료 조성물의
상기 (iii) 주제부 및 (iv) 경화제부는 1:0.05 ~ 0.3의 중량비로 사용되는 것을 특징으로 하는,
유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법.
18. The method of claim 17,
of the water-soluble urethane paint composition for forming the top coat
The (iii) main part and (iv) curing agent part are used in a weight ratio of 1:0.05 to 0.3,
A coating method using a water-soluble coating material with excellent affinity with an oil-based coating film.
 제 1 항에 따른 유성 도막과 친화력이 우수한 수용성 도장재를 이용한 도장 공법으로 제조된
표면 처리된 유성 도막, 수용성 에폭시 하도 조성물(A)로 도장된 에폭시 하도, 및 수용성 우레탄 상도 조성물(B)로 도장된 우레탄 상도를 포함하는,
친환경 중방식 도막.




The oil-based coating film according to claim 1 and a water-soluble coating material that has excellent affinity for
Containing a surface-treated oil-based coating film, an epoxy primer coated with a water-soluble epoxy primer composition (A), and a urethane topcoat coated with a water-soluble urethane topcoat composition (B),
Eco-friendly medium-proof coating film.
KR1020200162210A 2020-11-27 2020-11-27 Coating method using water-based coating material with excellent compatability with solvelt-based coating film and eco-friendly heavy duty coating film manufactured therefrom KR102298842B1 (en)