KR102280236B1 - Multi functional cutting board - Google Patents
Multi functional cutting board Download PDFInfo
- Publication number
- KR102280236B1 KR102280236B1 KR1020210014931A KR20210014931A KR102280236B1 KR 102280236 B1 KR102280236 B1 KR 102280236B1 KR 1020210014931 A KR1020210014931 A KR 1020210014931A KR 20210014931 A KR20210014931 A KR 20210014931A KR 102280236 B1 KR102280236 B1 KR 102280236B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- cutting board
- multifunctional
- far
- Prior art date
Abstract
Description
본 발명은 도마에 원적외선 발산 기능과 칼날 등을 수납 할 수 있는 수납부를 형성시킴으로써, 도마로부터 발산되는 원적외선에 의해 상기 도마 뿐만 아니라 수납부에 수납되는 칼날 등에 대한 항균 및 탈취 기능을 구현할 수 있도록 하며, 이로 인해 도마 및 칼날 등을 항상 위생적이고 청결한 상태로 유지할 수 있도록 하는 다기능 도마에 관한 것이다.The present invention provides an antibacterial and deodorizing function for not only the cutting board but also the blade accommodated in the storage unit by the far infrared rays emitted from the cutting board by forming a far-infrared emitting function and a storage unit that can accommodate a blade, etc. on the cutting board, Due to this, it relates to a multifunctional cutting board that allows the cutting board and the blade to be always maintained in a sanitary and clean state.
일반적으로 도마는 칼로 음식 재료를 절단할 수 있도록 판 형상으로 이루어진 부재로써, 도마의 상부에 놓여진 음식 재료를 지지하여 절단 작업을 용이하게 하는 역할을 한다.In general, a cutting board is a member made of a plate shape to cut the food material with a knife, and serves to support the food material placed on the top of the cutting board to facilitate the cutting operation.
이러한 도마는 항상 습기와 각종 잔류 음식물에 노출됨에 따라 각종 세균의 번식 및 서식이 활발히 이루어지며 이로 인해 비위생적인 문제점이 있다.As such a cutting board is always exposed to moisture and various kinds of residual food, various kinds of bacteria are actively reproduced and inhabited, which causes unsanitary problems.
또한, 상기 도마 뿐만 아니라 도마와 함께 사용되는 칼 등의 경우에도 상기와 같은 습기와 음식물에 지속적으로 접촉함에 따라 비위생적이다.In addition, not only the cutting board but also the knife used together with the cutting board is unsanitary as it continuously comes into contact with moisture and food as described above.
이를 해결하기 위하여, 특허문헌 1 및 2 등에서와 같이 각종 주방용품에 대한 탈취나 살균을 수행하는 장치가 사용되고 있으나, 이러한 장치의 사용은 다음과 같은 문제점이 있다.In order to solve this problem, a device for deodorizing or sterilizing various kitchen appliances as in Patent Documents 1 and 2 is used, but the use of such a device has the following problems.
첫째, 상기와 같은 주방용품 탈취 및 살균 장치는 장치 자체의 크기가 커서 주방 공간을 불필요하게 차지하는 등 주방의 공간 활용성을 미비하게 하는 문제점이 있었다.First, the device for deodorizing and sterilizing kitchenware as described above has a problem in that the size of the device itself is large and thus the space utilization of the kitchen is insufficient, such as occupying the kitchen space unnecessarily.
둘째, 상기와 같은 주방용품 탈취 및 살균 장치는 통상 전기로 구동됨에 따라 전력 낭비 및 소음 발생의 원인이 되는 문제점이 있었다.Second, the deodorizing and sterilizing apparatus for kitchenware as described above has a problem of causing power wastage and noise generation as it is normally driven by electricity.
셋째, 상기와 같은 주방용품 탈취 및 살균 장치는 가격이 비교적 고가이며, 가격 대비 탈취나 살균 기능이 미비한 문제점이 있었다.Third, the deodorizing and sterilizing device for kitchenware as described above is relatively expensive, and there is a problem in that the deodorization or sterilization function is insufficient compared to the price.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 도마에 원적외선 발산 기능과 칼날 등을 수납 할 수 있는 수납부를 형성시킴으로써, 도마로부터 발산되는 원적외선에 의해 상기 도마 뿐만 아니라 수납부에 수납되는 칼날 등에 대한 항균 및 탈취 기능을 구현할 수 있도록 하며, 이로 인해 별도의 장치를 구입하지 않고도 도마 및 칼날 등을 항상 위생적이고 청결한 상태로 유지할 수 있도록 함을 과제로 한다.The present invention is to solve the above problems, and by forming a receiving part that can accommodate a far-infrared emitting function and a blade, etc. on the cutting board, by far infrared rays emitted from the cutting board, not only the cutting board but also the blade stored in the storage unit. It makes it possible to implement antibacterial and deodorizing functions, and for this reason, it is a task to keep cutting boards and knives in a sanitary and clean state without purchasing a separate device.
본 발명은 다기능 도마에 있어서, 수지 100 중량부에 대하여, 목초액 2 ~ 10 중량부, 마그네슘 0.5 ~ 9 중량부, 제올라이트 0.1 ~ 5 중량부, 광물 1.5 ~ 5.5 중량부, 은 용액 0.04 ~ 5 중량부, 이산화티타늄(TiO2) 0.01 ~ 0.04 중량부, 아연 0.1 ~ 0.2 중량부 및 전분 0.1 ~ 0.5 중량부를 혼합하여 이루어지는 것을 특징으로 하는 다기능 도마를 과제의 해결 수단으로 한다.The present invention is a multifunctional chopping board, based on 100 parts by weight of the resin, 2 to 10 parts by weight of wood vinegar, 0.5 to 9 parts by weight of magnesium, 0.1 to 5 parts by weight of zeolite, 1.5 to 5.5 parts by weight of minerals, 0.04 to 5 parts by weight of silver solution , titanium dioxide (TiO 2 ) 0.01 to 0.04 parts by weight, 0.1 to 0.2 parts by weight of zinc, and 0.1 to 0.5 parts by weight of starch.
여기서 상기 수지는 실리콘 또는 폴리우레탄을 사용하고, 상기 은 용액은 실버 콜로이드(silver colloidal) 35 ~ 60 중량%, 세라믹 20 ~ 30 중량% 및 알루미늄 20 ~ 35 중량%를 혼합하여 이루어지며, 상기 광물은 흑운모, 토르말린, 칠보석, 황토, 견운모, 자수정, 생광석, 실리카, 죽탄, 의왕석, 귀양석, 흑요석 또는 맥반석 중에서 단독 또는 2종 이상 병용하여 사용하고, 한편, 상기 마그네슘, 제올라이트, 광물, 이산화티타늄, 아연, 세라믹, 알루미늄은 입도 0.1 ~ 100㎛의 미분말 형태로 적용되는 것이 바람직하다.Here, the resin uses silicone or polyurethane, and the silver solution is made by mixing 35 to 60% by weight of silver colloidal, 20 to 30% by weight of ceramic, and 20 to 35% by weight of aluminum, and the mineral is It is used alone or in combination of two or more of biotite, tourmaline, cloisonne, ocher, sericite, amethyst, raw ore, silica, bamboo charcoal, Uiwangseok, guiyangseok, obsidian, or elvan, on the other hand, the magnesium, zeolite, mineral, dioxide Titanium, zinc, ceramic, and aluminum are preferably applied in the form of fine powder having a particle size of 0.1 to 100 μm.
한편, 상기 다기능 도마는 몸체(10); 및 상기 몸체(10)의 일단에 형성되는 수납부(20);를 포함하여 구성되는 것이 바람직하다.On the other hand, the multi-function chopping board body (10); and a receiving
본 발명은 도마에 원적외선 발산 기능과 칼날 등을 수납 할 수 있는 수납부를 형성시킴으로써, 도마로부터 발산되는 원적외선에 의해 상기 도마 뿐만 아니라 수납부에 수납되는 칼날 등에 대한 항균 및 탈취 기능을 구현할 수 있도록 하며, 이로 인해 별도의 장치를 구입하지 않고도 도마 및 칼날 등을 항상 위생적이고 청결한 상태로 유지할 수 있는 효과가 있다.The present invention provides an antibacterial and deodorizing function for not only the cutting board but also the blade accommodated in the storage unit by the far infrared rays emitted from the cutting board by forming a far-infrared emitting function and a storage unit that can accommodate a blade, etc. on the cutting board, For this reason, there is an effect that the cutting board and the blade can always be maintained in a sanitary and clean state without purchasing a separate device.
도 1은 본 발명에 따른 다기능 도마를 나타낸 사시도
도 2는 본 발명에 따른 다기능 도마에 칼날이 삽입된 상태를 나타낸 단면도1 is a perspective view showing a multifunctional chopping board according to the present invention;
Figure 2 is a cross-sectional view showing a state in which the blade is inserted into the multifunctional cutting board according to the present invention
상기의 효과를 달성하기 위한 본 발명은 다기능 도마에 관한 것으로서, 본 발명의 기술적 구성을 이해하는데 필요한 부분만이 설명되며 그 이외 부분의 설명은 본 발명의 요지를 흩트리지 않도록 생략될 것이라는 것을 유의하여야 한다.It should be noted that the present invention for achieving the above effect relates to a multifunctional cutting board, and only the parts necessary for understanding the technical configuration of the present invention will be described, and the description of other parts will be omitted so as not to obscure the gist of the present invention. do.
이하, 첨부된 도면을 참조하여 본 발명에 따른 다기능 도마를 상세히 설명하면 다음과 같다.Hereinafter, a multifunctional cutting board according to the present invention will be described in detail with reference to the accompanying drawings.
도 1 및 도 2에 도시된 바와 같이, 본 발명에 따른 다기능 도마는 음식물을 지지하여 절단작업을 용이하게 하는 몸체(10)가 구비되고, 상기 몸체(10)의 일단에 칼날을 수납 할 수 있는 수납부(20)가 형성된다. 한편, 사용 편의성 등을 고려하여 상기 도마에는 엠보(embo) 형태의 돌기가 형성될 수도 있고, 또한 상기 수납부(20)의 내부에는 칼갈이 커터나 물구멍 등을 더 형성시킬 수도 있다.1 and 2, the multifunctional chopping board according to the present invention is provided with a
즉, 본 발명에 따른 다기능 도마는 칼날 등의 수납 기능과 더불어 도마에 원적외선 발산 기능을 부여함으로써, 도마로부터 발산되는 원적외선에 의해 도마 뿐만 아니라 수납부에 수납되는 칼날 등에 대한 항균 및 탈취 기능을 구현할 수 있도록 한다.That is, the multifunctional cutting board according to the present invention provides a far-infrared emitting function to the cutting board in addition to the storage function of the blade, so that the antibacterial and deodorizing function can be implemented for not only the cutting board but also the knife stored in the storage unit by the far-infrared radiation emitted from the cutting board. let it be
상기와 같이 원적외선 발산 성능과 이를 통해 항균 및 탈취 성능을 구현하기 위해 본 발명에 따른 다기능 도마는 수지 100 중량부에 대하여, 목초액 2 ~ 10 중량부, 마그네슘 0.5 ~ 9 중량부, 제올라이트 0.1 ~ 5 중량부, 광물 1.5 ~ 5.5 중량부, 은 용액 0.04 ~ 5 중량부, 이산화티타늄(TiO2) 0.01 ~ 0.04 중량부, 아연 0.1 ~ 0.2 중량부 및 전분 0.1 ~ 0.5 중량부를 혼합하여 이루어진다.As described above, in order to implement far-infrared emitting performance and antibacterial and deodorizing performance through this, the multifunctional cutting board according to the present invention is based on 100 parts by weight of resin, 2 to 10 parts by weight of wood vinegar, 0.5 to 9 parts by weight of magnesium, 0.1 to 5 parts by weight of zeolite. parts, minerals 1.5 to 5.5 parts by weight, silver solution 0.04 to 5 parts by weight, titanium dioxide (TiO 2 ) 0.01 to 0.04 parts by weight, zinc 0.1 to 0.2 parts by weight, and starch 0.1 to 0.5 parts by weight.
상기 수지는 이미 공지된 다양한 합성수지나 플라스틱 등을 사용할 수 있으며, 예로 실리콘이나 폴리우레탄 등을 적용할 수 있다.As the resin, various known synthetic resins or plastics may be used, and for example, silicone or polyurethane may be applied.
상기 목초액은 비특허문헌 1에서와 같이, 살균 성능이 있는 공지된 물질로써 본 발명에서는 이미 공지된 참나무 목초액(oak vinegar) 등의 사용이 가능하며, 그 함량이 2 중량부 미만일 경우 살균 성능이 미비해질 우려가 있으며, 10 중량부를 초과할 경우 제품 원가가 상승하여 비경제적일 우려가 있다.As in Non-Patent Document 1, the wood vinegar is a known substance having sterilization performance, and in the present invention, known oak vinegar, etc. can be used, and when the content is less than 2 parts by weight, the sterilization performance is insufficient. If it exceeds 10 parts by weight, the cost of the product increases, which may be uneconomical.
아울러, 상기 목초액은 상기와 같이 도마의 성형 시 혼합되어 성형될 수도 있고, 또는 도마의 외면에 코팅될 수도 있다.In addition, the wood vinegar may be mixed and molded during the molding of the cutting board as described above, or may be coated on the outer surface of the cutting board.
상기 마그네슘은 비중이 1.738로써, 경량금속인 알루미늄 무게의 2/3 이하로 공업용으로 사용되는 금속 중에서 최경량 소재이고, 특히 상기와 같이 실용금속 중에서 가장 가벼운 금속이면서 인체에 무해한 소재이며, 그 함량이 0.5 중량부 미만일 경우 도마가 제대로 제조되지 못할 우려가 있으며, 9 중량부를 초과할 경우 제품 원가가 상승하여 비경제적일 우려가 있다.Magnesium has a specific gravity of 1.738, less than 2/3 of the weight of aluminum, which is a lightweight metal, and is the lightest material among metals used for industrial purposes. In particular, as described above, magnesium is the lightest metal among practical metals and harmless to the human body, and its content is 0.5 If it is less than 9 parts by weight, there is a fear that the cutting board may not be properly manufactured, and if it exceeds 9 parts by weight, the product cost increases and thus it may be uneconomical.
상기 제올라이트는 각종 악취 등의 흡착기능이 있다고 알려진 공지된 물질이며, 그 함량이 0.1 중량부 미만일 경우 탈취 성능이 미비해질 우려가 있으며, 5 중량부를 초과할 경우 제품 원가가 상승하여 비경제적일 우려가 있다.The zeolite is a known material known to have an adsorption function for various odors, and if the content is less than 0.1 parts by weight, the deodorization performance may be insufficient, and if it exceeds 5 parts by weight, the product cost increases and there is a risk of being uneconomical there is.
상기 광물은 원적외선을 발산하는 천연광물로써 흑운모, 토르말린, 칠보석, 황토, 견운모, 자수정, 생광석, 실리카, 죽탄, 의왕석, 귀양석, 흑요석 또는 맥반석 중에서 단독 또는 2종 이상 병용하여 사용하며, 그 함량이 1.5 중량부 미만일 경우 원적외선 발산효과가 미비해질 우려가 있으며, 5.5 중량부를 초과할 경우 사용량 대비 상기 기능의 증가율이 미비하여 비경제적일 우려가 있다.The mineral is a natural mineral that emits far-infrared rays, and is used alone or in combination of two or more of biotite, tourmaline, cloisonne, ocher, sericite, amethyst, raw ore, silica, bamboo charcoal, Uiwang-seok, guiyang-seok, obsidian or elvan, If the content is less than 1.5 parts by weight, there is a fear that the far-infrared emitting effect may be insufficient, and if it exceeds 5.5 parts by weight, the increase rate of the function compared to the amount used is insufficient and there is a fear that it is uneconomical.
상기 은 용액은 탈취 및 살균 기능을 더욱 향상시키기 위해 첨가되는 것으로, 실버 콜로이드(silver colloidal) 35 ~ 60 중량%, 세라믹 20 ~ 30 중량% 및 알루미늄 20 ~ 35 중량%를 혼합 및 건조한 것으로 액상으로 이루어진다.The silver solution is added to further improve the deodorization and sterilization function, and is made by mixing and drying 35 to 60% by weight of silver colloidal, 20 to 30% by weight of ceramic, and 20 to 35% by weight of aluminum, and is made of a liquid. .
상기 실버 콜로이드는 2 ~ 500nm 범위의 크기를 갖는 은 입자들이 녹아있는 콜로이드상 물질로 이미 다양한 제품이 공개된 공지의 물질이다. 본 발명에서 사용되는 실버 콜로이드는 특정 제품에 한정하지 않고 이미 공지된 다양한 제품을 선택적으로 적용할 수 있다.The silver colloid is a colloidal material in which silver particles having a size in the range of 2 to 500 nm are melted, and is a known material for which various products have already been disclosed. The silver colloid used in the present invention is not limited to a specific product, and various known products can be selectively applied.
그리고 상기 세라믹은 알루미나, 실리콘 나이트라이드, 지르코니아, 실리콘 카바이드, 패각 등의 세라믹 중에서 단독 또는 2종 이상 병용하여 사용할 수 있다.The ceramic may be used alone or in combination of two or more of ceramics such as alumina, silicon nitride, zirconia, silicon carbide, and shell.
또한 알루미늄 역시 이미 공지된 다양한 알루미늄의 적용이 가능하며, 상기 각 물질의 함량이 상기 범위를 벗어날 경우 탈취 및 항균기능이 제대로 구현되지 않을 우려가 있다.In addition, aluminum can also be applied to a variety of known aluminum, and when the content of each material is out of the above range, there is a fear that the deodorizing and antibacterial functions may not be properly implemented.
한편, 상기와 같이 이루어지는 은 용액의 혼합량이 0.04 중량부 미만일 경우 상기 효과가 미비해질 우려가 있으며, 5 중량부를 초과할 경우, 사용량 대비 탈취 및 항균기능의 향상효율이 미비하여 비경제적일 우려가 있다.On the other hand, if the mixing amount of the silver solution made as described above is less than 0.04 parts by weight, the effect may be insignificant, and if it exceeds 5 parts by weight, the improvement efficiency of deodorization and antibacterial functions compared to the amount used is insufficient, and there is a risk of being uneconomical. .
상기 이산화티타늄(TiO2)은 상기 각 물질들이 상호 분리되지 않고 혼합될 수 있는 안정제의 기능을 할 뿐만 아니라, 빛에 의한 산화환원력을 바탕으로 도마의 악취를 흡착하여 분해하기 위해 첨가되는 것으로, 그 사용량이 0.01 중량부 미만일 경우 상기 효과가 미비해질 우려가 있고, 0.04 중량부를 초과할 경우 도마의 물성을 저하시킬 우려가 있다.The titanium dioxide (TiO 2 ) not only functions as a stabilizer for the materials to be mixed without being separated from each other, but also adsorbs and decomposes the odor of the cutting board based on the redox power by light. When the amount used is less than 0.01 parts by weight, there is a fear that the above effect is insignificant, and when it exceeds 0.04 parts by weight, there is a risk of lowering the physical properties of the cutting board.
상기 아연은 가공성을 높이는 작용을 하며, 아연의 혼합량이 0.1 중량부 미만이 될 경우에는 가공성이 저하할 우려가 있고, 아연의 혼합량이 0.2 중량부를 초과할 경우에는 연성이 현저하게 저하되어 제조 후 부식균열을 일으킬 우려가 있다.The zinc acts to increase workability, and when the amount of zinc mixed is less than 0.1 parts by weight, there is a risk of deterioration of workability, and when the mixing amount of zinc exceeds 0.2 parts by weight, ductility is remarkably reduced and corrosion after manufacturing There is a risk of causing cracks.
상기 전분은 바인더(binder) 기능을 하는 것으로, 그 사용량이 0.1 중량부 미만일 경우 상기 효과가 미비해질 우려가 있고, 0.5 중량부를 초과할 경우 도마의 물성을 저하시킬 우려가 있다.The starch functions as a binder, and when the amount used is less than 0.1 parts by weight, the effect may be insignificant, and when it exceeds 0.5 parts by weight, there is a risk of lowering the physical properties of the cutting board.
한편, 상기 마그네슘, 제올라이트, 광물, 이산화티타늄, 아연, 세라믹, 알루미늄은 분말화하여 적용되는 것이 바람직하며, 분말 입자크기는 특별히 한정하지 않고 다양한 입자크기를 적용할 수 있으며 일 예로 입도 0.1 ~ 100㎛ 정도의 미분말 형태로 적용할 수 있다.On the other hand, the magnesium, zeolite, mineral, titanium dioxide, zinc, ceramic, and aluminum are preferably applied by powdering, and the powder particle size is not particularly limited and various particle sizes can be applied. For example, a particle size of 0.1 ~ 100㎛ It can be applied in the form of fine powder.
이하 본 발명의 구성을 아래 실시예에 의거하여 더욱 상세히 설명하겠는 바 본 발명이 하기의 실시예에 의해서만 반드시 한정되는 것은 아니다.Hereinafter, the configuration of the present invention will be described in more detail based on the following examples, but the present invention is not necessarily limited only by the following examples.
1. 은 용액의 제조1. Preparation of silver solution
(제조예 1)(Production Example 1)
실버 콜로이드 60 중량%, 세라믹(알루미나) 20 중량% 및 알루미늄 20 중량%로 이루어진 은 용액을 제조하였다.A silver solution consisting of 60% by weight of colloidal silver, 20% by weight of ceramic (alumina) and 20% by weight of aluminum was prepared.
(제조예 2)(Production Example 2)
실버 콜로이드 35 중량%, 세라믹(알루미나) 30 중량% 및 알루미늄 35 중량%로 이루어진 은 용액을 제조하였다.A silver solution consisting of 35% by weight of colloidal silver, 30% by weight of ceramic (alumina) and 35% by weight of aluminum was prepared.
2. 도마의 제조2. Manufacturing of cutting board
(실시예 1)(Example 1)
실리콘 100 중량부에 대하여, 목초액 2 중량부, 마그네슘 0.5 중량부, 제올라이트 0.1 중량부, 광물(흑운모) 1.5 중량부, 제조예 1에 따른 은 용액 0.04 중량부, 이산화티타늄 0.01 중량부, 상기 아연 0.1 중량부 및 전분 0.1 중량부를 혼합하고, 도마 사출 성형기를 이용하여 사출성하여 제조하였다.Based on 100 parts by weight of silicon, 2 parts by weight of wood vinegar, 0.5 parts by weight of magnesium, 0.1 parts by weight of zeolite, 1.5 parts by weight of minerals (biotite), 0.04 parts by weight of the silver solution according to Preparation Example 1, 0.01 parts by weight of titanium dioxide, 0.1 parts by weight of the zinc It was prepared by mixing parts by weight and 0.1 parts by weight of starch, and injection molding using a cutting board injection molding machine.
(실시예 2)(Example 2)
폴리우레탄 100 중량부에 대하여, 목초액 10 중량부, 마그네슘 9 중량부, 제올라이트 5 중량부, 광물(토르말린) 5.5 중량부, 제조예 2에 따른 은 용액 5 중량부, 이산화티타늄 0.04 중량부, 상기 아연 0.2 중량부 및 전분 0.5 중량부를 혼합하고, 도마 사출 성형기를 이용하여 사출성형하여 제조하였다.Based on 100 parts by weight of polyurethane, 10 parts by weight of wood vinegar, 9 parts by weight of magnesium, 5 parts by weight of zeolite, 5.5 parts by weight of mineral (tourmaline), 5 parts by weight of the silver solution according to Preparation Example 2, 0.04 parts by weight of titanium dioxide, the zinc 0.2 parts by weight and 0.5 parts by weight of starch were mixed, and injection molding was performed using a cutting board injection molding machine.
(비교예 1)(Comparative Example 1)
실리콘 100 중량부를 도마 사출 성형기를 이용하여 사출성형하여 제조하였다.100 parts by weight of silicone was prepared by injection molding using a cutting board injection molding machine.
(비교예 2)(Comparative Example 2)
폴리우레탄 100 중량부를 도마 사출 성형기를 이용하여 사출성형하여 제조하였다.100 parts by weight of polyurethane was prepared by injection molding using a cutting board injection molding machine.
2. 원적외선 발산 성능 및 살균성 평가2. Far-infrared emission performance and sterilization evaluation
(1) 원적외선 방사 성능(1) Far-infrared radiation performance
KFIA-FI-1005에 기준하여 측정하되, FT-IR Spectrometer을 이용한 BLACK BODY 대비 측정으로써 실내온도 37℃에서 측정하였으며, 그 결과는 아래 [표 1]와 같다.Measured based on KFIA-FI-1005, compared to BLACK BODY using FT-IR Spectrometer and measured at room temperature of 37℃, and the results are shown in [Table 1] below.
(5 ~ 20㎛)emissivity
(5 ~ 20㎛)
원적외선
방사되지 않음
far infrared
not radiated
원적외선
방사되지 않음
far infrared
not radiated
(W/m2·㎛, 37℃)radiant energy
(W/m 2 μm, 37°C)
상기 [표 1]에서와 같이 본 발명의 실시예 1, 2에 따른 다기능 도마는 원적외선 방사효율이 우수함을 알 수 있다.As shown in [Table 1], it can be seen that the multifunctional cutting board according to Examples 1 and 2 of the present invention has excellent far-infrared radiation efficiency.
(2) 살균 성능(2) Sterilization performance
JIS Z 2801에 기준하여 측정하되, 표준필름은 Stomacher 400 POLY-BAG을 사용하였고, 시험균액을 35±1℃, 90% R.H.에서 24시간 정치 배양 후 균수를 측정하였으며, 균주는 Staphy lococcus aureus ATCC 6538P(균주 1)와 Escherichia coli ATCC 8739(균주 2)를 사용하였고, 그 결과는 아래 [표 2]와 같다.Measured based on JIS Z 2801, but Stomacher 400 POLY-BAG was used for the standard film, and the number of bacteria was measured after stationary incubation for 24 hours at 35±1℃, 90% RH, and the strain was Staphy lococcus aureus ATCC 6538P. (Strain 1) and Escherichia coli ATCC 8739 (Strain 2) were used, and the results are shown in [Table 2] below.
균주 1
strain 1
(세균수/cm2)Initial number of bacteria
(Bacteria/cm 2 )
(log)antibacterial activity
(log)
균주 2
strain 2
(세균수/cm2)Initial number of bacteria
(Bacteria/cm 2 )
(log)antibacterial activity
(log)
상기 [표 2]에서와 같이 본 발명의 실시예 1, 2에 따른 다기능 도마는 살균기능이 우수함을 알 수 있다.As shown in [Table 2], it can be seen that the multifunctional cutting board according to Examples 1 and 2 of the present invention has excellent sterilization function.
(3) 탈취 성능(3) Deodorization performance
탈취 성능을 평가하기 위해 암모니아 제거율을 시험하였으며, 구체적으로는 상기 실시예 및 비교예에 따른 다기능 도마를 용기 내에 위치시키고 암모니아 가스를 주입한 후 가스 검지관을 이용하여 2시간 후 암모니아 제거율을 측정(시험규격 : KFIA-FI-1004)하였고, 그 결과를 아래의 [표 3]에 나타내었다.In order to evaluate the deodorization performance, the ammonia removal rate was tested, and specifically, the multifunctional chopping board according to the above Examples and Comparative Examples was placed in the container, ammonia gas was injected, and the ammonia removal rate was measured after 2 hours using a gas detection tube ( Test standard: KFIA-FI-1004), and the results are shown in [Table 3] below.
Example
One
2
comparative example
One
2
상기 [표 3]에서와 같이 본 발명의 실시예 1, 2에 따른 다기능 도마는 탈취 성능이 우수함을 알 수 있다.As shown in [Table 3], it can be seen that the multifunctional cutting board according to Examples 1 and 2 of the present invention has excellent deodorization performance.
상술한 바와 같이, 본 발명에 따른 다기능 도마는 상기의 바람직한 실시 예를 통해 설명하고, 그 우수성을 확인하였지만 해당 기술 분야의 당업자라면 하기의 특허 청구 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.As described above, the multifunctional cutting board according to the present invention has been described through the above preferred embodiment, and its excellence has been confirmed, but those skilled in the art will not depart from the spirit and scope of the present invention described in the claims below. It will be understood that various modifications and variations of the present invention may be made therein.
10 : 몸체 20 : 수납부10: body 20: accommodating part
Claims (3)
수지 100 중량부에 대하여, 목초액 2 ~ 10 중량부, 마그네슘 0.5 ~ 9 중량부, 제올라이트 0.1 ~ 5 중량부, 광물 1.5 ~ 5.5 중량부, 은 용액 0.04 ~ 5 중량부, 이산화티타늄(TiO2) 0.01 ~ 0.04 중량부, 아연 0.1 ~ 0.2 중량부 및 전분 0.1 ~ 0.5 중량부를 혼합하여 이루어지는 것을 특징으로 하는, 다기능 도마.
In the multifunctional cutting board,
Based on 100 parts by weight of the resin, 2 to 10 parts by weight of wood vinegar, 0.5 to 9 parts by weight of magnesium, 0.1 to 5 parts by weight of zeolite, 1.5 to 5.5 parts by weight of minerals, 0.04 to 5 parts by weight of silver solution, titanium dioxide (TiO 2 ) 0.01 - 0.04 parts by weight, zinc 0.1 to 0.2 parts by weight, and starch, characterized in that made by mixing 0.1 to 0.5 parts by weight, a multifunctional cutting board.
상기 수지는 실리콘 또는 폴리우레탄을 사용하고,
상기 은 용액은 실버 콜로이드(silver colloidal) 35 ~ 60 중량%, 세라믹 20 ~ 30 중량% 및 알루미늄 20 ~ 35 중량%를 혼합하여 이루어지며,
상기 광물은 흑운모, 토르말린, 칠보석, 황토, 견운모, 자수정, 생광석, 실리카, 죽탄, 의왕석, 귀양석, 흑요석 또는 맥반석 중에서 단독 또는 2종 이상 병용하여 사용하고,
한편, 상기 마그네슘, 제올라이트, 광물, 이산화티타늄, 아연, 세라믹, 알루미늄은 입도 0.1 ~ 100㎛의 미분말 형태로 적용되는 것을 특징으로 하는, 다기능 도마.
The method of claim 1,
The resin uses silicone or polyurethane,
The silver solution is made by mixing 35 to 60% by weight of silver colloidal, 20 to 30% by weight of ceramic, and 20 to 35% by weight of aluminum,
The mineral is used alone or in combination of two or more of biotite, tourmaline, chil-jewel, ocher, sericite, amethyst, raw ore, silica, bamboo charcoal, Uiwang-seok, guiyang-seok, obsidian or elvan,
On the other hand, the magnesium, zeolite, mineral, titanium dioxide, zinc, ceramic, aluminum is a multi-functional cutting board, characterized in that applied in the form of fine powder having a particle size of 0.1 ~ 100㎛.
상기 다기능 도마는,
몸체(10); 및
상기 몸체(10)의 일단에 형성되는 수납부(20);를 포함하여 구성되는 것을 특징으로 하는, 다기능 도마.The method of claim 1,
The multifunctional chopping board,
body 10; and
A multifunctional chopping board, characterized in that it comprises; a receiving portion (20) formed at one end of the body (10).