KR102259294B1 - Leaflet applied reusable adhesive and method manufacturing the same - Google Patents

Leaflet applied reusable adhesive and method manufacturing the same Download PDF

Info

Publication number
KR102259294B1
KR102259294B1 KR1020190111152A KR20190111152A KR102259294B1 KR 102259294 B1 KR102259294 B1 KR 102259294B1 KR 1020190111152 A KR1020190111152 A KR 1020190111152A KR 20190111152 A KR20190111152 A KR 20190111152A KR 102259294 B1 KR102259294 B1 KR 102259294B1
Authority
KR
South Korea
Prior art keywords
pressure
sensitive adhesive
weight
acrylic copolymer
crosslinking agent
Prior art date
Application number
KR1020190111152A
Other languages
Korean (ko)
Other versions
KR20210029908A (en
Inventor
최문성
Original Assignee
최문성
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최문성 filed Critical 최문성
Priority to KR1020190111152A priority Critical patent/KR102259294B1/en
Publication of KR20210029908A publication Critical patent/KR20210029908A/en
Application granted granted Critical
Publication of KR102259294B1 publication Critical patent/KR102259294B1/en

Abstract

캔버스천 또는 텐트천으로 이루어지며, 상면에는 광고 내용이 인쇄되는 인쇄층, 인쇄층의 하면에 배치되며, 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 제조되는 점착제층 및 이형층으로 이루어진 광고지 및 그 제조 방법이 개시되어 있다.A flyer made of a canvas cloth or tent cloth, and a print layer on which advertisement content is printed on the upper surface, and placed on the lower surface of the printing layer, and composed of a pressure-sensitive adhesive layer and a release layer prepared by mixing an acrylic copolymer, a reaction solvent, a crosslinking agent and a crosslinking accelerator. And a manufacturing method thereof is disclosed.

Description

재사용이 가능한 점착제가 도포된 광고지 및 이의 제조방법{Leaflet applied reusable adhesive and method manufacturing the same}Leaflet applied reusable adhesive and method manufacturing the same}

본 발명은 재사용이 가능한 점착제가 도포된 광고지 및 이의 제조방법에 관한 것으로, 보다 상세하게는 캔버스천 또는 텐트천을 이용하여 색상 표현력 및 점착성이 뛰어나고, 재사용하더라도 점착력이 유지되어 계속하여 탈부착이 가능한 광고지 및 그 제조방법에 관한 것이다.The present invention relates to a flyer coated with a reusable adhesive and a method for manufacturing the same, and more particularly, excellent color expression and adhesiveness by using a canvas cloth or tent cloth, and a flyer that can be continuously attached and detached by maintaining adhesive strength even if reused, and It relates to the manufacturing method.

광고지의 경우, 점착 테이프 등을 이용하여 벽 또는 일정 장소에 붙이는 것이 일반적이다. 이런 경우, 미관을 해치기 때문에 광고지의 뒷면에 점착제가 도포되어 나온다.In the case of a flyer, it is common to attach it to a wall or a certain place using an adhesive tape or the like. In this case, the adhesive is applied to the back side of the flyer because it spoils the aesthetics.

이때, 점착제의 경우, 점착력이 우수한 경우에는 견고하게 붙이는 장점은 있지만, 이를 떼는 경우, 벽의 벽지 등을 손상시키거나, 점착제의 잔여물이 붙어 있게 되는 경우가 많고, 광고지의 경우 찢어지는 경우도 발생하게 된다. 이 경우, 손상된 표면을 수리하거나, 잔여물을 제거하는 부수적인 작업이 필요하고, 찢어지는 경우에는 재사용이 어렵게 되는 문제점이 있다. 점착력이 약한 경우에는 잘 부착되지 않고, 계속하여 부착 시 점착력이 유지되지가 않는다.At this time, in the case of adhesive, if the adhesive strength is excellent, it has the advantage of sticking firmly, but when it is removed, it damages the wallpaper of the wall, or the residue of the adhesive is often attached, and in the case of flyers, there are cases where it is torn. Will occur. In this case, there is a problem in that it is necessary to repair the damaged surface or a side work of removing the residue, and if it is torn, reuse is difficult. If the adhesive strength is weak, it does not adhere well, and the adhesive strength is not maintained when continuing to adhere.

따라서, 높은 점착력을 가지며, 탈거하더라도 점착력을 유지하여 재사용이 가능한 점착제 조성물 및 이를 이용한 광고지 개발이 절실히 요구되고 있는 실정이다. Accordingly, there is an urgent need to develop a pressure-sensitive adhesive composition that has high adhesive strength and can be reused by maintaining the adhesive force even if removed and a flyer using the same.

본 발명은 상기한 문제점을 해결하기 위한 것으로, 본 발명은 점착력이 우수하고, 반복하여 부착 및 탈거를 하더라도 점착력이 유지되는 점착제가 도포된 광고지 및 이의 제조 방법을 제공하는 것이다.The present invention is to solve the above problems, the present invention is excellent in adhesion, to provide a pressure-sensitive adhesive coated flyer and a method of manufacturing the same that maintains the adhesion even if repeatedly attached and removed.

상기 기술적 과제를 해결하기 위한 본 발명의 일 실시예에 따라, 재사용이 가능한 점착제가 도포된 광고지는 캔버스천 또는 텐트천으로 이루어지며, 상면에는 광고 내용이 인쇄되는 0.3 내지 0.8 mm 두께를 갖는 인쇄층; 상기 인쇄층의 하면에 배치되며, 50 내지 70μm 두께를 갖는 점착제층; 및 상기 점착제층의 하면에 배치되며, 0.1 mm 내지 0.2 mm 두께를 가지는 이형층을 포함하고, 상기 점착제층에서의 점착제는 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 제조되고, 상기 아크릴계 공중합체는 연질 타입 단량체인 부틸아크릴레이트 및 경질 타입 단량체인 메틸메타크릴레이트를 중합하여 형성되고, 상기 반응 용제로는 에틸아세테이트, 부틸아세테이트, 톨루엔, 자일렌, 아세톤, 메틸에틸케톤 중 하나가 사용되며, 상기 가교제는 이소시아네이트계 가교제이고, 상기 가교 촉진제는 디메틸시클로헥실아민, 트리에틸아민, 디부틸주석 디라우레이트, 초산칼륨 중에서 하나가 사용되고, 상기 점착제는 상기 점착제 총량 기준으로 상기 아크릴계 공중합체는 35 내지 55 중량%, 상기 반응 용제는 15 내지 30 중량%, 상기 가교제는 11 내지 26 중량%, 상기 가교촉진제는 3 내지 9 중량%를 함유하고, 상기 아크릴계 공중합체는 상기 아크릴계 공중합체 총량 기준으로 상기 연질 타입의 단량체는 11 내지 25중량%, 상기 경질 타입의 단량체는 75 내지 89중량%를 함유한다. According to an embodiment of the present invention for solving the above technical problem, a reusable adhesive is applied advertisement paper made of a canvas cloth or a tent cloth, and a printing layer having a thickness of 0.3 to 0.8 mm on which advertisement contents are printed on an upper surface; A pressure-sensitive adhesive layer disposed on the lower surface of the printing layer and having a thickness of 50 to 70 μm; And a release layer disposed on a lower surface of the pressure-sensitive adhesive layer and having a thickness of 0.1 mm to 0.2 mm, wherein the pressure-sensitive adhesive in the pressure-sensitive adhesive layer is prepared by mixing an acrylic copolymer, a reaction solvent, a crosslinking agent and a crosslinking accelerator, and the acrylic The copolymer is formed by polymerizing butyl acrylate as a soft type monomer and methyl methacrylate as a hard type monomer, and as the reaction solvent, one of ethyl acetate, butyl acetate, toluene, xylene, acetone, and methyl ethyl ketone is used. In addition, the crosslinking agent is an isocyanate-based crosslinking agent, the crosslinking accelerator is one of dimethylcyclohexylamine, triethylamine, dibutyltin dilaurate, and potassium acetate, and the adhesive is based on the total amount of the adhesive 35 to 55% by weight, the reaction solvent is 15 to 30% by weight, the crosslinking agent contains 11 to 26% by weight, the crosslinking accelerator contains 3 to 9% by weight, and the acrylic copolymer is based on the total amount of the acrylic copolymer The soft type monomer contains 11 to 25% by weight, and the hard type monomer contains 75 to 89% by weight.

상기 기술적 과제를 해결하기 위한 본 발명의 다른 실시예에 따라, 재사용이 가능한 점착제가 도포된 광고지를 제조하는 방법은 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 점착제를 생성하는 단계; 상기 점착제를 캔버스천 또는 텐트천에 광고가 인쇄된 인쇄층의 하면에 도포하는 단계; 상기 점착제가 도포된 인쇄층을 건조하는 단계; 상기 상기 인쇄층에 도포된 점착제에 이형지를 부착하는 단계; 및 상기 이형지가 부착된 광고지를 숙성시키는 단계를 포함하고, 상기 아크릴계 공중합체는 연질 타입 단량체인 부틸아크릴레이트 및 경질 타입 단량체인 메틸메타크릴레이트를 중합하여 형성되고, 상기 반응 용제로는 에틸아세테이트, 부틸아세테이트, 톨루엔, 자일렌, 아세톤, 메틸에틸케톤 중 하나가 사용되며, 상기 가교제는 이소시아네이트계 가교제이고, 상기 가교 촉진제는 디메틸시클로헥실아민, 트리에틸아민, 디부틸주석 디라우레이트, 초산칼륨 중에서 하나가 사용되고, 상기 점착제는 상기 점착제 총량 기준으로 상기 아크릴계 공중합체는 35 내지 55 중량%, 상기 반응 용제는 15 내지 30 중량%, 상기 가교제는 11 내지 26 중량%, 상기 가교촉진제는 3 내지 9 중량%를 함유하고, 상기 아크릴계 공중합체는 상기 아크릴계 공중합체 총량 기준으로 상기 연질 타입의 단량체는 11 내지 25중량%, 상기 경질 타입의 단량체는 75 내지 89중량%를 함유한다.According to another embodiment of the present invention for solving the above technical problem, a method of manufacturing a flyer coated with a reusable adhesive includes the steps of creating an adhesive by mixing an acrylic copolymer, a reaction solvent, a crosslinking agent, and a crosslinking accelerator; Applying the pressure-sensitive adhesive to a lower surface of a printed layer on which an advertisement is printed on a canvas cloth or tent cloth; Drying the printed layer to which the pressure-sensitive adhesive is applied; Attaching a release paper to the pressure-sensitive adhesive applied to the printing layer; And aging the flyer to which the release paper is attached, wherein the acrylic copolymer is formed by polymerizing butyl acrylate as a soft type monomer and methyl methacrylate as a hard type monomer, and as the reaction solvent, ethyl acetate, One of butyl acetate, toluene, xylene, acetone, and methyl ethyl ketone is used, the cross-linking agent is an isocyanate-based cross-linking agent, and the cross-linking accelerator is from dimethylcyclohexylamine, triethylamine, dibutyltin dilaurate, and potassium acetate. One is used, and the adhesive is 35 to 55% by weight of the acrylic copolymer, 15 to 30% by weight of the reaction solvent, 11 to 26% by weight of the crosslinking agent, and 3 to 9% by weight of the crosslinking accelerator based on the total amount of the adhesive. %, and the acrylic copolymer contains 11 to 25% by weight of the soft type monomer and 75 to 89% by weight of the hard type monomer based on the total amount of the acrylic copolymer.

본 발명에 의하면, 인쇄지 또는 인쇄층에 캔버스천 또는 텐트천이 이용됨으로써, 색상 표현력이 우수하여 효과가 높은 광고지를 제공할 수가 있다.According to the present invention, by using canvas cloth or tent cloth for printing paper or printing layer, it is possible to provide a flyer with excellent color expression and high effect.

또한, 본 발명에 의하면, 점착력이 우수하고, 반복적으로 사용하더라도 점착력을 유지하는 점착제가 도포된 광고지를 제공할 수가 있다.In addition, according to the present invention, it is possible to provide a flyer coated with a pressure-sensitive adhesive that has excellent adhesion and maintains adhesion even if it is repeatedly used.

도 1은 본 발명의 일 실시예에 따른 재사용이 가능한 점착제가 도포된 광고지의 단면도를 나타내는 도면이다.
도 2는 본 발명의 일 실시예에 따른 광고가 인쇄된 인쇄층의 일면을 나타내는 도면이다.
도 3은 본 발명의 일 실시예에 따른 재사용이 가능한 점착제가 도포된 광고지를 제조하는 방법에 관한 흐름도를 나타내는 도면이다.1 is a view showing a cross-sectional view of a flyer coated with a reusable adhesive according to an embodiment of the present invention.
2 is a view showing one side of a printed layer on which an advertisement is printed according to an embodiment of the present invention.
3 is a view showing a flow chart of a method of manufacturing a flyer coated with a reusable adhesive according to an embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 따라 상세히 설명하기로 한다.Hereinafter, with reference to the accompanying drawings will be described in detail according to a preferred embodiment of the present invention.

도 1은 본 발명의 일 실시예에 따른 재사용이 가능한 점착제가 도포된 광고지의 단면도를 나타내는 도면이다.1 is a view showing a cross-sectional view of a flyer coated with a reusable adhesive according to an embodiment of the present invention.

도 1을 참조하면, 재사용이 가능한 점착제가 도포된 광고지(100)는 인쇄층(10), 점착제층(20) 및 이형층(30)을 포함한다.Referring to FIG. 1, a flyer 100 coated with a reusable adhesive includes a printing layer 10, an adhesive layer 20, and a release layer 30.

인쇄층(10)은 캔버스천 또는 텐트천으로 이루어지고, 인쇄층(10)의 일면에 광고 문구 또는 광고 이미지가 인쇄되어 형성된다. 인쇄층(30)의 두께는 0.3 내지 0.8 mm[밀리미터]이며, 바람직하게는, 0.6 mm이다.The printing layer 10 is made of a canvas cloth or tent cloth, and is formed by printing an advertisement phrase or an advertisement image on one surface of the printing layer 10. The thickness of the printing layer 30 is 0.3 to 0.8 mm [millimeter], preferably 0.6 mm.

캔버스천은 유화를 그릴 때 사용되는 특수천의 일종으로, 면, 마직물 또는 화학섬유로 이루어진다. 조직은 굵은 변수실을 스고, 편직 또는 사직으로 짜여 진다.Canvas cloth is a type of special cloth used when painting oil paintings, and is made of cotton, hemp cloth, or chemical fiber. The organization is woven through a thick variable thread and woven into a knitting or yarn.

텐트천(포토천)은 두꺼워서 구김이 적고 잉크흡수량이 많아 색상 표현력이 높아, 고급 광고 또는 인테리어용으로 사용된다. 또한, 흡수성이 뛰어나 출력 시 번지지 아니하며, 별도의 코팅 작업 없이 어느 정도의 내수성을 가진다. 텐트천은 위의 캔버스천보다 저렴한 천으로 본 발명에서 바람직하게는 텐트천이 사용될 수 있다.Tent cloth (photo cloth) is thick, so it has less wrinkles and has high color expression due to its high ink absorption, so it is used for high-end advertisements or interiors. In addition, it has excellent water absorption, does not bleed during printing, and has a certain degree of water resistance without a separate coating operation. Tent cloth is a cloth cheaper than the above canvas cloth, and preferably tent cloth may be used in the present invention.

캔버스천 또는 텐트천의 표면은 일반 필름과 같이 매끄러운 것이 아니라, 천 질감을 갖기 때문에, 점착제를 모든 표면에 고르게 점착되지 않거나, 모든 표면이 부착되는 것이 아니기 때문에 더욱 용이하게 떼어져 재반복하여 사용할 수 있는 효과가 있다. 또한, 흡수성이 뛰어나 일반 필름 또는 종이에 인쇄하는 것보다 색상 표현력이 높아 광고 효과가 높다고 할 것이다.The surface of the canvas or tent cloth is not as smooth as a general film, but because it has a cloth texture, the adhesive is not evenly adhered to all surfaces, or not all surfaces are adhered, so it can be removed more easily and used repeatedly. It works. In addition, it is highly absorbent and has higher color expression than printing on ordinary film or paper, so it is said that the advertising effect is high.

도 2는 본 발명의 일 실시예에 따른 광고가 인쇄된 인쇄층의 일면을 나타내는 도면이다.2 is a view showing one side of a printed layer on which an advertisement is printed according to an embodiment of the present invention.

점착제(Adhesive)층(20)에서, 점착제는 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 제조된다.In the adhesive layer 20, the adhesive is prepared by mixing an acrylic copolymer, a reaction solvent, a crosslinking agent, and a crosslinking accelerator.

점착제층(20)의 두께는 50 내지 70μm이며, 바람직하게는, 60μm이다. 점착제는 60 μm의 두께로 인쇄층(10)의 타면에 균일하게 도포된다.The thickness of the pressure-sensitive adhesive layer 20 is 50 to 70 μm, preferably 60 μm. The adhesive is uniformly applied to the other surface of the printing layer 10 with a thickness of 60 μm.

점착제는 점착제 총량 기준으로 아크릴계 공중합체는 35 내지 55 중량%, 반응 용제는 15 내지 30 중량%, 가교제는 11 내지 26 중량% 및 가교 촉진제는 3 내지 9 중량%를 함유한다.The pressure-sensitive adhesive contains 35 to 55% by weight of the acrylic copolymer, 15 to 30% by weight of the reaction solvent, 11 to 26% by weight of the crosslinking agent, and 3 to 9% by weight of the crosslinking accelerator based on the total amount of the pressure-sensitive adhesive.

아크릴계 공중합체는 주사용 단량체를 사용하여 중합하여 합성된다. 아크릴계 공중합체는 주사용 단량체인 부틸아크릴레이트(Butyl acrylate), 메틸메타크릴레이트(Methyl Methacrylate), 에틸아크릴레이트(Ethyl acrylate), 에틸헥실 아크릴레이트(Ethylhexyl Acrylate) 및 하이드록시에틸 메타크릴레이트(Hydroxyethyl Methacrylate) 중에서 2종을 중합하여 형성한다.The acrylic copolymer is synthesized by polymerization using a monomer for injection. Acrylic copolymers are injectable monomers such as butyl acrylate, methyl methacrylate, ethyl acrylate, ethylhexyl acrylate, and hydroxyethyl methacrylate. It is formed by polymerizing two kinds of methacrylate).

구체적으로, 아크릴계 공중합체는 유리전이온도(Tg)가 0℃ 이하인 연질 타입의 단량체인 부틸아크릴레이트(Butyl acrylate), 에틸아크릴레이트(Ethyl acrylate) 및 에틸헥실 아크릴레이트(Ethylhexyl Acrylate) 중에서 1종 및 유리전이온도(Tg)가 0℃ 이상인 경질 타입의 단량체인 메틸메타크릴레이트(Methyl Methacrylate) 및 하이드록시에틸 메타크릴레이트(Hydroxyethyl Methacrylate) 중에서 1종을 중합하여 형성한다. 여기에서, 연질 타입의 단량체는 점착제의 점착성을 향상시키는 기능을 하고, 경질 타입의 단량체는 점착제의 응집력을 향상시키는 기능을 한다.Specifically, the acrylic copolymer is one of butyl acrylate, ethyl acrylate, and ethylhexyl acrylate, which are soft-type monomers having a glass transition temperature (Tg) of 0° C. or less, and It is formed by polymerizing one of methyl methacrylate and hydroxyethyl methacrylate, which are hard-type monomers having a glass transition temperature (Tg) of 0°C or higher. Here, the soft type monomer functions to improve the adhesion of the pressure-sensitive adhesive, and the hard type monomer functions to improve the cohesiveness of the pressure-sensitive adhesive.

본 발명의 일 실시예에 있어서, 아크릴계 공중합체 총량 기준으로 연질 타입의 단량체는 11 내지 25중량%, 경질 타입의 단량체는 75 내지 89중량%를 함유한다. 인쇄층(10)의 재질이 캔버스천 또는 텐트천이기 때문에, 점착제의 경우, 응집력이 더 중요한 요소이기 때문에 경질 타입의 단량체가 연질 타입에 비하여 많이 사용된다.In one embodiment of the present invention, the soft type monomer contains 11 to 25% by weight, and the hard type monomer contains 75 to 89% by weight based on the total amount of the acrylic copolymer. Since the material of the printing layer 10 is a canvas cloth or tent cloth, in the case of a pressure-sensitive adhesive, since cohesion is a more important factor, a hard type monomer is used more than a soft type.

합성된 아크릴계를 액체 상태로 유지시키기 위하여 반응 용제가 같이 사용된다. 반응 용제로는 에틸아세테이트(Ethyl Acetate), 부틸아세테이트(Butyl Acetate), 톨루엔(toluene), 자일렌(xylene), 아세톤 (acetone), 메틸에틸케톤(Methylethylketone), 부틸칼비톨 아세테이트 중 하나 또는 그 이상이 사용된다. In order to keep the synthesized acrylic system in a liquid state, a reaction solvent is used together. As the reaction solvent, one or more of ethyl acetate, butyl acetate, toluene, xylene, acetone, methylethylketone, and butylcarbitol acetate Is used.

아크릴계 공중합체 부분의 가교를 위하여, 그리고, 점착제의 분자량을 높여 초기 접착력 및 응집력을 조절 할 수 있도록 가교제를 적당하게 혼용한다. 바람직하게는 가교제로 이소시아네이트계가 사용된다. 이소시아네이트계는 반응온도, 속도 및 점착력 조절이 용이한 장점이 있다. 가교제의 경우, 적은 경우에는 아크릴 공중합체들을 부분 가교가 제대로 이루어지지 않을 수 있고, 많은 경우에는 점착제층의 접착력 및 전단박리력 저하의 우려가 있어, 본 발명의 일 실시예에서, 가교제는 점착제 총량 기준으로 11 내지 26 중량%를 함유한다.For crosslinking of the acrylic copolymer part, and to increase the molecular weight of the pressure-sensitive adhesive to control initial adhesion and cohesion, a crosslinking agent is appropriately mixed. Preferably, an isocyanate type is used as a crosslinking agent. The isocyanate system has the advantage of being easy to control the reaction temperature, speed and adhesion. In the case of a crosslinking agent, in the case of a small amount, partial crosslinking of the acrylic copolymers may not be performed properly, and in many cases, there is a concern of lowering the adhesion and shear peeling power of the pressure-sensitive adhesive layer. In one embodiment of the present invention, the crosslinking agent is the total amount of the pressure-sensitive adhesive. It contains 11 to 26% by weight on a basis.

점착제에는 반응속도를 빠르게 하고 부분 가교를 촉진시키는 가교촉진제가 더 첨가될 수 있다. 가교촉진제로는 점착제 총량 기준으로 3 내지 9 중량%를 첨가하는 것이 바람직하다. A crosslinking accelerator for accelerating the reaction rate and promoting partial crosslinking may be further added to the pressure-sensitive adhesive. As a crosslinking accelerator, it is preferable to add 3 to 9% by weight based on the total amount of the adhesive.

본 발명의 일 실시예에 있어서, 가교촉진제는 구체적으로 디메틸시클로헥실아민(Dimethylcyclohexylamine), 트리에틸아민(Triethylamine), 디부틸주석 디라우레이트(Dibutyltin dilaurate), 초산칼륨(Potassium acetate) 중에서 1종 또는 그 이상을 선택하여 사용할 수 있다.In one embodiment of the present invention, the crosslinking accelerator is specifically one of dimethylcyclohexylamine, triethylamine, dibutyltin dilaurate, potassium acetate, or You can choose and use more than that.

이형층(30)은 점착제층(20)을 보호하는 것으로서, 점착제층(20) 하면에 착탈 가능하게 구비된다. 사용 시에는 점착제층(20)으로부터 제거한 뒤 사용된다.The release layer 30 protects the pressure-sensitive adhesive layer 20 and is detachably provided on the lower surface of the pressure-sensitive adhesive layer 20. In use, it is removed from the pressure-sensitive adhesive layer 20 and then used.

이형층(30)에는 이형지가 이용되며, 이형지는 densified kraft 종이, polycoated kraft 종이, clay coated kraft 종이, lay flat 종이 또는 PET 재질의 필름 이형지가 있다. 이형층(30)의 두께는 0.1 mm 내지 0.2 mm이며, 바람직하게는, 0.15 mm이다.Release paper is used for the release layer 30, and the release paper includes densified kraft paper, polycoated kraft paper, clay coated kraft paper, lay flat paper, or film release paper of PET material. The thickness of the release layer 30 is 0.1 mm to 0.2 mm, preferably 0.15 mm.

도 3은 본 발명의 일 실시예에 따른 재사용이 가능한 점착제가 도포된 광고지를 제조하는 방법에 관한 흐름도를 나타내는 도면이다.3 is a view showing a flow chart of a method of manufacturing a flyer coated with a reusable adhesive according to an embodiment of the present invention.

도 3을 참조하면, 단계 310에서, 아크릴계 공중합체, 반응 용제, 가교제 및 가교 촉진제를 이용하여 점착제를 제조한다.Referring to FIG. 3, in step 310, a pressure-sensitive adhesive is prepared using an acrylic copolymer, a reaction solvent, a crosslinking agent, and a crosslinking accelerator.

점착제는 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 제조된다.The pressure-sensitive adhesive is prepared by mixing an acrylic copolymer, a reaction solvent, a crosslinking agent, and a crosslinking accelerator.

점착제가 형성된 점착제층의 두께는 50 내지 70μm이며, 바람직하게는, 60μm이다. 점착제는 60 μm의 두께로 인쇄층(10)의 타면에 균일하게 도포된다.The thickness of the pressure-sensitive adhesive layer on which the pressure-sensitive adhesive is formed is 50 to 70 μm, preferably 60 μm. The adhesive is uniformly applied to the other surface of the printing layer 10 with a thickness of 60 μm.

점착제는 점착제 총량 기준으로 아크릴계 공중합체는 35 내지 55 중량%, 반응 용제는 15 내지 30 중량%, 가교제는 11 내지 26 중량% 및 가교 촉진제는 3 내지 9 중량%를 함유한다.The pressure-sensitive adhesive contains 35 to 55% by weight of the acrylic copolymer, 15 to 30% by weight of the reaction solvent, 11 to 26% by weight of the crosslinking agent, and 3 to 9% by weight of the crosslinking accelerator based on the total amount of the pressure-sensitive adhesive.

아크릴계 공중합체는 주사용 단량체를 사용하여 중합하여 합성된다. 아크릴계 공중합체는 주사용 단량체인 부틸아크릴레이트, 메틸메타크릴레이트, 에틸아크릴레이트, 에틸헥실 아크릴레이트 및 하이드록시에틸 메타크릴레이트 중에서 2종을 중합하여 형성한다. 구체적으로, 아크릴계 공중합체는 유리전이온도가 0℃ 이하인 연질 타입의 단량체인 부틸아크릴레이트, 에틸아크릴레이트 및 에틸헥실 아크릴레이트 중에서 1종 및 유리전이온도가 0℃ 이상인 경질 타입의 단량체인 메틸메타크릴레이트 및 하이드록시에틸 메타크릴레이트 중에서 1종을 중합하여 형성한다. 여기에서, 연질 타입의 단량체는 점착제의 점착성을 향상시키는 기능을 하고, 경질 타입의 단량체는 점착제의 응집력을 향상시키는 기능을 한다.The acrylic copolymer is synthesized by polymerization using a monomer for injection. The acrylic copolymer is formed by polymerizing two of butyl acrylate, methyl methacrylate, ethyl acrylate, ethylhexyl acrylate and hydroxyethyl methacrylate, which are injectable monomers. Specifically, the acrylic copolymer is one of butyl acrylate, ethyl acrylate, and ethylhexyl acrylate, which are soft-type monomers with a glass transition temperature of 0°C or less, and methyl methacryl, a hard-type monomer with a glass transition temperature of 0°C or higher. It is formed by polymerizing one of hydroxyethyl methacrylate and hydroxyethyl methacrylate. Here, the soft type monomer functions to improve the adhesion of the pressure-sensitive adhesive, and the hard type monomer functions to improve the cohesiveness of the pressure-sensitive adhesive.

본 발명의 일 실시예에 있어서, 아크릴계 공중합체 총량 기준으로 연질 타입의 단량체는 11 내지 25중량%, 경질 타입의 단량체는 75 내지 89중량%를 함유한다. 인쇄층의 재질이 캔버스천 또는 텐트천이기 때문에, 점착제의 경우, 응집력이 더 중요한 요소이기 때문에 경질 타입의 단량체가 연질 타입에 비하여 많이 사용된다.In one embodiment of the present invention, the soft type monomer contains 11 to 25% by weight, and the hard type monomer contains 75 to 89% by weight based on the total amount of the acrylic copolymer. Since the material of the printed layer is canvas or tent cloth, in the case of a pressure-sensitive adhesive, since cohesion is a more important factor, hard-type monomers are more commonly used than soft-type monomers.

반응 용제로는 에틸아세테이트, 부틸아세테이트, 톨루엔, 자일렌, 아세톤, 메틸에틸케톤, 부틸칼비톨 아세테이트 중 하나 또는 그 이상이 사용된다. As the reaction solvent, one or more of ethyl acetate, butyl acetate, toluene, xylene, acetone, methyl ethyl ketone, and butyl carbitol acetate is used.

가교제로 이소시아네이트계가 사용된다. An isocyanate type is used as a crosslinking agent.

점착제에는 반응속도를 빠르게 하고 부분 가교를 촉진시키는 가교촉진제가 더 첨가될 수 있다. A crosslinking accelerator for accelerating the reaction rate and promoting partial crosslinking may be further added to the pressure-sensitive adhesive.

본 발명의 일 실시예에 있어서, 가교촉진제는 구체적으로 디메틸시클로헥실아민, 트리에틸아민, 디부틸주석 디라우레이트, 초산칼륨 중에서 1종 또는 그 이상을 선택하여 사용할 수 있다.In one embodiment of the present invention, the crosslinking accelerator may specifically be used by selecting one or more of dimethylcyclohexylamine, triethylamine, dibutyltin dilaurate, and potassium acetate.

단계 320에서, 인쇄층의 하면에 점착제를 도포한다. 인쇄층은 캔버스천 또는 텐트천으로 이루어지고, 인쇄층의 일면에 광고 문구 또는 광고 이미지가 인쇄되어 형성된다. 인쇄층의 두께는 0.3 내지 0.8 mm이며, 바람직하게는, 0.6 mm이다.In step 320, a pressure-sensitive adhesive is applied to the lower surface of the printing layer. The printing layer is made of canvas cloth or tent cloth, and is formed by printing an advertisement phrase or advertisement image on one side of the printing layer. The thickness of the printing layer is 0.3 to 0.8 mm, preferably 0.6 mm.

캔버스천은 유화를 그릴 때 사용되는 특수천의 일종으로, 면, 마직물 또는 화학섬유로 이루어진다. 조직은 굵은 변수실을 스고, 편직 또는 사직으로 짜여 진다. 텐트천(포토천)은 두꺼워서 구김이 적고 잉크흡수량이 많아 색상 표현력이 높아, 고급 광고 또는 인테리어용으로 사용된다. 또한, 흡수성이 뛰어나 출력 시 번지지 아니하며, 별도의 코팅 작업 없이 어느 정도의 내수성을 가진다. 텐트천은 위의 캔버스천보다 저렴한 천으로 본 발명에서 바람직하게는 텐트천이 사용될 수 있다.Canvas cloth is a type of special cloth used when painting oil paintings, and is made of cotton, hemp cloth, or chemical fiber. The organization is woven through a thick variable thread and woven into a knitting or yarn. Tent cloth (photo cloth) is thick, so it has less wrinkles and has high color expression due to its high ink absorption, so it is used for high-end advertisements or interiors. In addition, it has excellent water absorption, does not bleed during printing, and has a certain degree of water resistance without a separate coating operation. Tent cloth is a cloth cheaper than the above canvas cloth, and preferably tent cloth may be used in the present invention.

캔버스천 또는 텐트천의 표면은 일반 필름과 같이 매끄러운 것이 아니라, 천 질감을 갖기 때문에, 점착제를 모든 표면에 고르게 점착되지 않거나, 모든 표면이 부착되는 것이 아니기 때문에 더욱 용이하게 떼어져 재반복하여 사용할 수 있는 효과가 있다. 또한, 흡수성이 뛰어나 일반 필름 또는 종이에 인쇄하는 것보다 색상 표현력이 높아 광고 효과가 높다고 할 것이다.The surface of the canvas or tent cloth is not as smooth as a general film, but because it has a cloth texture, the adhesive is not evenly adhered to all surfaces, or not all surfaces are adhered, so it can be removed more easily and used repeatedly. It works. In addition, it is highly absorbent and has higher color expression than printing on ordinary film or paper, so it is said that the advertising effect is high.

단계 330에서, 점착제가 도포된 인쇄층을 90℃ 내지 95℃의 상태에서, 10분 동안 건조시킨다.In step 330, the printed layer to which the pressure-sensitive adhesive is applied is dried for 10 minutes in a state of 90°C to 95°C.

단계 340에서, 건조된 점착제층에 이형지를 부착한 후, 소정의 압력을 가하여 이형지층을 형성한다. 이형지는 densified kraft 종이, polycoated kraft 종이, clay coated kraft 종이, lay flat 종이 또는 PET 재질의 필름 이형지가 있다. 이형층(30)의 두께는 0.1 mm 내지 0.2 mm이고, 0.15mm이 바람직하다.In step 340, after attaching the release paper to the dried pressure-sensitive adhesive layer, a predetermined pressure is applied to form the release paper layer. Release papers include densified kraft paper, polycoated kraft paper, clay coated kraft paper, lay flat paper or PET film release paper. The thickness of the release layer 30 is 0.1 mm to 0.2 mm, preferably 0.15 mm.

단계 350에서, 45℃ 내지 50℃의 온도에서, 24시간 숙성시킨다. 필요한 경우, 숙성 단계 후에 적당한 크기로 절단하여 광고지를 완성한다.In step 350, it is aged for 24 hours at a temperature of 45°C to 50°C. If necessary, after the aging step, cut into suitable size to complete the flyer.

이상에서 본 발명의 바람직한 실시예에 대해 도시하고 설명하였으나, 본 발명은 상술한 특정의 바람직한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위 내에 있게 된다.Although the preferred embodiments of the present invention have been illustrated and described above, the present invention is not limited to the specific preferred embodiments described above, and without departing from the gist of the present invention claimed in the claims, in the technical field to which the present invention pertains. Anyone of ordinary skill in the art can implement various modifications, as well as such modifications will be within the scope of the claims.

100: 재사용이 가능한 점착제가 도포된 광고지
10: 인쇄층
20: 점착제층
30: 이형층100: flyer with reusable adhesive
10: printed layer
20: adhesive layer
30: release layer

Claims (2)

캔버스천 또는 텐트천으로 이루어지며, 상면에는 광고 내용이 인쇄되는 0.3 내지 0.8 mm 두께를 갖는 인쇄층;
상기 인쇄층의 하면에 배치되며, 50 내지 70μm 두께를 갖는 점착제층; 및
상기 점착제층의 하면에 배치되며, 0.1 mm 내지 0.2 mm 두께를 가지는 이형층을 포함하고,
상기 점착제층에서의 점착제는 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 제조되고,
상기 아크릴계 공중합체는 연질 타입 단량체인 부틸아크릴레이트 및 경질 타입 단량체인 메틸메타크릴레이트를 중합하여 형성되고,
상기 반응 용제로는 에틸아세테이트, 부틸아세테이트, 톨루엔, 자일렌, 아세톤, 메틸에틸케톤 중 하나가 사용되며,
상기 가교제는 이소시아네이트계 가교제이고,
상기 가교 촉진제는 디메틸시클로헥실아민, 트리에틸아민, 디부틸주석 디라우레이트, 초산칼륨 중에서 하나가 사용되고,
상기 점착제는 상기 점착제 총량 기준으로 상기 아크릴계 공중합체는 35 내지 55 중량%, 상기 반응 용제는 15 내지 30 중량%, 상기 가교제는 11 내지 26 중량%, 상기 가교촉진제는 3 내지 9 중량%를 함유하고,
상기 아크릴계 공중합체는 상기 아크릴계 공중합체 총량 기준으로 상기 연질 타입의 단량체는 11 내지 25중량%, 상기 경질 타입의 단량체는 75 내지 89중량%를 함유하는 것을 특징으로 하는 재사용이 가능한 점착제가 도포된 광고지.A printing layer made of canvas cloth or tent cloth and having a thickness of 0.3 to 0.8 mm on which advertisement contents are printed on the upper surface;
A pressure-sensitive adhesive layer disposed on the lower surface of the printing layer and having a thickness of 50 to 70 μm; And
It is disposed on the lower surface of the pressure-sensitive adhesive layer, and includes a release layer having a thickness of 0.1 mm to 0.2 mm,
The pressure-sensitive adhesive in the pressure-sensitive adhesive layer is prepared by mixing an acrylic copolymer, a reaction solvent, a crosslinking agent and a crosslinking accelerator,
The acrylic copolymer is formed by polymerizing butyl acrylate as a soft type monomer and methyl methacrylate as a hard type monomer,
As the reaction solvent, one of ethyl acetate, butyl acetate, toluene, xylene, acetone, and methyl ethyl ketone is used,
The crosslinking agent is an isocyanate-based crosslinking agent,
The crosslinking accelerator is one of dimethylcyclohexylamine, triethylamine, dibutyltin dilaurate, and potassium acetate,
The pressure-sensitive adhesive contains 35 to 55% by weight of the acrylic copolymer, 15 to 30% by weight of the reaction solvent, 11 to 26% by weight of the crosslinking agent, and 3 to 9% by weight of the crosslinking accelerator based on the total amount of the pressure-sensitive adhesive. ,
The acrylic copolymer contains 11 to 25% by weight of the soft type monomer and 75 to 89% by weight of the hard type monomer based on the total amount of the acrylic copolymer. . 아크릴계 공중합체, 반응 용제, 가교제 및 가교촉진제를 혼합하여 점착제를 생성하는 단계;
상기 점착제를 캔버스천 또는 텐트천에 광고가 인쇄된 인쇄층의 하면에 도포하는 단계;
상기 점착제가 도포된 인쇄층을 건조하는 단계;
상기 상기 인쇄층에 도포된 점착제에 이형지를 부착하는 단계; 및
상기 이형지가 부착된 광고지를 숙성시키는 단계를 포함하고,
상기 아크릴계 공중합체는 연질 타입 단량체인 부틸아크릴레이트 및 경질 타입 단량체인 메틸메타크릴레이트를 중합하여 형성되고,
상기 반응 용제로는 에틸아세테이트, 부틸아세테이트, 톨루엔, 자일렌, 아세톤, 메틸에틸케톤 중 하나가 사용되며,
상기 가교제는 이소시아네이트계 가교제이고,
상기 가교 촉진제는 디메틸시클로헥실아민, 트리에틸아민, 디부틸주석 디라우레이트, 초산칼륨 중에서 하나가 사용되고,
상기 점착제는 상기 점착제 총량 기준으로 상기 아크릴계 공중합체는 35 내지 55 중량%, 상기 반응 용제는 15 내지 30 중량%, 상기 가교제는 11 내지 26 중량%, 상기 가교촉진제는 3 내지 9 중량%를 함유하고,
상기 아크릴계 공중합체는 상기 아크릴계 공중합체 총량 기준으로 상기 연질 타입의 단량체는 11 내지 25중량%, 상기 경질 타입의 단량체는 75 내지 89중량%를 함유하는 것을 특징으로 하는 재사용이 가능한 점착제가 도포된 광고지를 제조하는 방법.Mixing an acrylic copolymer, a reaction solvent, a crosslinking agent, and a crosslinking accelerator to produce a pressure-sensitive adhesive;
Applying the pressure-sensitive adhesive to a lower surface of a printed layer on which an advertisement is printed on a canvas cloth or tent cloth;
Drying the printed layer to which the pressure-sensitive adhesive is applied;
Attaching a release paper to the pressure-sensitive adhesive applied to the printing layer; And
Including the step of aging the flyer to which the release paper is attached,
The acrylic copolymer is formed by polymerizing butyl acrylate as a soft type monomer and methyl methacrylate as a hard type monomer,
As the reaction solvent, one of ethyl acetate, butyl acetate, toluene, xylene, acetone, and methyl ethyl ketone is used,
The crosslinking agent is an isocyanate-based crosslinking agent,
The crosslinking accelerator is one of dimethylcyclohexylamine, triethylamine, dibutyltin dilaurate, and potassium acetate,
The pressure-sensitive adhesive contains 35 to 55% by weight of the acrylic copolymer, 15 to 30% by weight of the reaction solvent, 11 to 26% by weight of the crosslinking agent, and 3 to 9% by weight of the crosslinking accelerator based on the total amount of the pressure-sensitive adhesive. ,
The acrylic copolymer contains 11 to 25% by weight of the soft type monomer and 75 to 89% by weight of the hard type monomer based on the total amount of the acrylic copolymer. How to manufacture.
KR1020190111152A 2019-09-08 2019-09-08 Leaflet applied reusable adhesive and method manufacturing the same KR102259294B1 (en)