KR102237697B1 - Method for manufacturing trap nets of sink and the trap nets - Google Patents

Method for manufacturing trap nets of sink and the trap nets Download PDF

Info

Publication number
KR102237697B1
KR102237697B1 KR1020190143931A KR20190143931A KR102237697B1 KR 102237697 B1 KR102237697 B1 KR 102237697B1 KR 1020190143931 A KR1020190143931 A KR 1020190143931A KR 20190143931 A KR20190143931 A KR 20190143931A KR 102237697 B1 KR102237697 B1 KR 102237697B1
Authority
KR
South Korea
Prior art keywords
sewing
pla
manufacturing
knitted fabric
drain trap
Prior art date
Application number
KR1020190143931A
Other languages
Korean (ko)
Inventor
이문희
Original Assignee
이문희
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이문희 filed Critical 이문희
Priority to KR1020190143931A priority Critical patent/KR102237697B1/en
Application granted granted Critical
Publication of KR102237697B1 publication Critical patent/KR102237697B1/en

Abstract

Disclosed is a method for manufacturing a filter for a sink drain trap. The method for manufacturing a filter for a sink drain trap comprises: a step of manufacturing PLA monofilaments by melting and spinning PLA resin at a temperature of 165-175 degrees; a step of manufacturing PLA multifilaments of 35d/12f by a spin draw yarn process for PLA monofilaments; a step of performing circular knitting with a tubular mesh having a diameter of 80-150 mm by using the PLA multifilaments through a circular knitting device; a step of adding a sewing reinforcement piece having a certain width at certain intervals on the outside of a circular knitted fabric; a step of sewing the circular knitted fabric at a position in which the sewing reinforcement piece is added by using the PLA multi-filaments; and a step of cutting the circular knitted fabric at a position spaced at constant intervals from a sewing line based on the sewing line formed by the sewing step. The filter can be treated with food waste.

Description

싱크대 배수 트랩용 거름망 제조방법 및 그 방법에 의해서 제조된 싱크대 배수 트랩용 거름망{Method for manufacturing trap nets of sink and the trap nets}TECHNICAL FIELD [Method for manufacturing trap nets of sink and the trap nets]

이 발명은 싱크대 배수 트랩용 거름망 제조방법에 관한 것으로, 보다 상세하게는 싱크대 배수 트랩에 설치하여 싱크대 사용 시에 발생하는 음식물 찌거기를 걸러 음식물 쓰레기와 함께 간편하게 처리할 수 있도록 하는 싱크대 배수 트랩용 거름망을 제조하는 방법에 관한 것이다.The present invention relates to a method for manufacturing a strainer for a sink drainage trap, and more specifically, a sieve for a sink drain trap that can be installed in a sink drain trap to filter food waste generated when using the sink and easily dispose of it together with food waste. It relates to a method of manufacturing.

싱크대에는 싱크대의 사용 시에 발생하는 음식물 찌거기를 포함한 이물질 및 식기류가 배수구로 빠지는 것을 방지하기 위한 배수 트랩이 설치된다. 싱크대 배수 트랩은 금속 또는 합성수지로 제작되며, 대부분은 전체적으로는 원통형을 이루되 바닥면과 측면 상에는 일정 간격을 두고 다수의 작은 배수구멍이 관통 형성된 구조로 이루어진다. 따라서, 설거지를 하는 과정 등에서 배수구멍보다 상대적으로 작은크기의 음식물 찌꺼기는 물과 함께 배수가 되지만, 배구구멍에 비하여 크기가 큰 음식물 찌꺼기들은 배수 트랩에 걸리게 된다.A drain trap is installed in the sink to prevent foreign matter including food waste and tableware from falling out of the drain when the sink is used. The sink drain trap is made of metal or synthetic resin, and most of them have a cylindrical shape, but have a structure in which a number of small drainage holes are formed through the bottom and sides at a certain distance. Accordingly, in the process of washing dishes, food wastes of a size relatively smaller than the drainage hole are drained together with water, but food wastes having a size larger than the volleyball hole are caught in the drainage trap.

한편, 싱크대 배수 트랩에 걸린 음식물 찌꺼기는 음식물 쓰레기와 함께 폐기 처리하게 되지만, 배수 트랩에 걸린 음식물 찌꺼기를 처리하는 데에는 손이 많이 가게 된다. 특히, 설거지 후 배수 트랩을 깨끗하게 세척하지 않으면 세균 번식의 원인이 되는 등 위생적인 측면에서도 여러 문제점이 있었다.On the other hand, the food waste caught in the sink drain trap is disposed of together with the food waste, but it takes a lot of hands to dispose of the food waste caught in the drain trap. In particular, there have been several problems in terms of hygiene, such as if the drainage trap is not cleaned cleanly after washing dishes, it may cause the propagation of bacteria.

이와 같은 어려움을 극복하고자 대한민국특허청 등록실용신안공보 제20-0255888호, 대한민국특허청 등록실용신안공보 제20-0262320호 등에 개시된 예와 같은 형태의 싱크대 배수 트랩용 거름망이 제안되기도 하였다. 그러나 예의 싱크대 배수 트랩용 거름망은 음식물 찌꺼기를 거르는 측면에서는 효과가 있었으나, 대부분이 합성수지 소재로 1회용으로 제작됨으로써 음식물 쓰레기와 함께 처리하지 못하고 합성수지재의 거름망과 음식물 찌꺼기를 다시 분리 처리해야 하는 불편함이 있었다.In order to overcome such difficulties, a strainer for sink drain traps in the same form as disclosed in Korean Patent Office Utility Model Publication No. 20-0255888 and Korean Patent Office Utility Model Publication No. 20-0262320 has been proposed. However, the filter screen for sink drainage traps in the old days was effective in filtering food waste, but most of them were made of synthetic resin for single use, so they could not be disposed of together with food waste. there was.

대한민국특허청 등록실용신안공보 제-0255888호Korean Intellectual Property Office Registration Utility Model Publication No.-0255888 대한민국특허청 등록실용신안공보 제-0262320호Korean Intellectual Property Office Registration Utility Model Publication No.-0262320

이 발명은 전술한 바와 같은 문제점을 해결하기 위해서 안출된 것으로, 싱크대 배수 트랩에 설치하여 싱크대 사용 시에 발생하는 음식물 찌거기를 걸러 음식물 쓰레기와 함께 간편하게 처리할 수 있도록 하는 싱크대 배수 트랩용 거름망 제조방법을 제공하는 데 목적이 있다.The present invention was conceived to solve the above-described problems, and a method for manufacturing a strainer for a sink drain trap that can be installed in a sink drain trap to filter food waste generated when using the sink and easily dispose of it together with food waste. It has a purpose to provide.

이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망 제조방법은 PLA 수지를 165~175℃ 온도 조건에서 용융 방사하여 PLA 모노 필라멘트를 제조하는 단계; PLA 모노 필라멘트를 Spin Draw Yarn 공정으로 35d/12f의 PLA 멀티 필라멘트를 제조하는 단계; 환편기를 통해 PLA 멀티 필라멘트를 사용하여 지름이 80~150㎜의 통형태의 망으로 환편직하는 단계; 환편직된 편물의 외부에 일정 간격을 두고 일정 폭을 갖는 재봉 보강편을 덧대는 단계; PLA 멀티 필라멘트를 사용하여 재봉 보강편이 덧대어진 위치의 환편직된 편물을 재봉하는 단계; 및 재봉단계에 의해 형성된 재봉선을 기준으로 재봉선으로부터 일정 간격 떨어진 위치의 환편직된 편물을 재단하는 단계; 를 포함하여 이루어질 수 있다.The method of manufacturing a strainer for a sink drain trap according to an embodiment of the present invention comprises the steps of manufacturing a PLA monofilament by melt-spinning a PLA resin at a temperature of 165 to 175°C; Preparing a PLA multifilament of 35d/12f using a PLA monofilament by a Spin Draw Yarn process; Using PLA multifilaments through a circular knitting machine, circular knitting into a tubular network having a diameter of 80 to 150 mm; Adding a sewing reinforcement piece having a predetermined width at a predetermined interval on the outside of the circular knitted fabric; Sewing the circular knitted fabric at the position where the sewing reinforcement piece is padded using PLA multifilament; And cutting a circular knitted fabric at a predetermined distance from the sewing line based on the sewing line formed by the sewing step. It can be made, including.

이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망 제조방법에서 재봉 보강편은 동물성 콜라겐(collagen), 동물성 콜라겐 100 중량부에 대하여 30~35 중량부의 글리세린(glycerin) 및 27.5~22.5 중량부의 셀룰로오스(cellulose)를 혼합하고, 60~80℃ 범위 내의 온도에서 박막의 형태로 성형될 수 있다.In the method of manufacturing a strainer for a sink drain trap according to an embodiment of the present invention, the sewing reinforcement piece is animal collagen, 30 to 35 parts by weight of glycerin and 27.5 to 22.5 parts by weight of cellulose based on 100 parts by weight of animal collagen. ) Can be mixed and formed in the form of a thin film at a temperature within the range of 60 to 80°C.

이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망은 옥수수 전분에서 추출된 원료로 이루어지며 생분해성 수지로 알려져 있는 PLA 수지와 콜라겐 성분으로 제조됨으로써 설거지 과정에서 발생한 음식물 찌꺼기와 분리하지 않고 함께 처리해도 되는 장점이 있다.The strainer for sink drainage trap according to an embodiment of the present invention is made of raw materials extracted from corn starch, and is made of PLA resin and collagen, which are known as biodegradable resins, so that they can be treated together without separating them from food waste generated during the washing process. There is an advantage.

도1은 이 발명의 일 실시예에 따른 싱크대 배수 트랩용 거름망 제조방법을 설명하기 위한 도면.
도2는 이 발명의 일 실시 예에 의해서 제조된 싱크대 배수 트랩용 거름망의 구성을 설명하기 위한 도면.
도3은 이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망의 사용 상태를 보인 도면.1 is a view for explaining a method of manufacturing a strainer for a sink drain trap according to an embodiment of the present invention.
2 is a view for explaining the configuration of a strainer for a sink drain trap manufactured according to an embodiment of the present invention.
3 is a view showing a state of use of a strainer for a sink drain trap according to an embodiment of the present invention.

이하에서는 이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망 제조방법에 대하여 첨부된 도면을 참조하면서 보다 구체적으로 설명하기로 한다.Hereinafter, a method of manufacturing a strainer for a sink drain trap according to an embodiment of the present invention will be described in more detail with reference to the accompanying drawings.

도1은 이 발명의 일 실시예에 따른 싱크대 배수 트랩용 거름망 제조방법을 설명하기 위한 도면이고, 도2는 이 발명의 일 실시 예에 의해서 제조된 싱크대 배수 트랩용 거름망의 구성을 설명하기 위한 도면이다. 도면 중에 표시되는 도면부호 100은 이 발명의 실시 예에 의해 제조된 싱크대 배수 트랩용 거름망을 지시하는 것이다.FIG. 1 is a view for explaining a method of manufacturing a strainer for a sink drain trap according to an embodiment of the present invention, and FIG. 2 is a view for explaining the configuration of a sieve for a sink drain trap manufactured according to an embodiment of the present invention. to be. Reference numeral 100 indicated in the drawings denotes a strainer for a sink drain trap manufactured according to an embodiment of the present invention.

이 출원의 일 실시 예에 따른 싱크대 배수 트랩용 거름망(100, 이하 거름망으로 약칭할 수 있음)은 도2에서 보이는 바와 같이 일정 간격과 일정 크기의 눈이 형성되도록 환편직된 통상의 편물 하부를 재봉한 구조로 이루어진다. 특히, 이 발명의 실시 예에 따른 거름망(100)는 도면에서 보이는 바와 같이 망상으로 환편직된 편물(110)의 개방된 하부에 재봉 보강편(120)을 덧댄 후 재봉하여 하부는 막힌 구조를 이루게 된다. 이 발명의 실시 예에 따른 거름망(100)은 환편직된 편물(110)이 일정 크기의 눈이 일정 간격으로 형성된 망상으로 형성됨으로써 물과 눈 크기 이상의 물질은 통과하지만, 눈 크기 이상의 물질은 걸러지게 되는 구성으로 이루어진다.The filter screen for sink drainage trap (100, hereinafter may be abbreviated as a filter screen) according to an embodiment of this application sews the lower part of a circular knitted fabric so that eyes of a certain interval and a certain size are formed as shown in FIG. It consists of one structure. In particular, the strainer 100 according to the embodiment of the present invention is formed by adding a sewing reinforcement piece 120 to the open lower part of the knitted fabric 110 circularly knitted in a mesh shape as shown in the drawing, and then sewing the lower part to form a closed structure. do. The strainer 100 according to the embodiment of the present invention is a circular knitted fabric 110 formed in a network in which eyes of a predetermined size are formed at regular intervals, so that water and materials larger than the eye size pass, but materials larger than the eye size are filtered. It consists of a configuration.

전술한 환편직된 편물(110)은 친환경 소재로 알려져 있는 PLA(Ploy Latic Acid) 수지로 편직된다. 이하에서는 PLA 수지로 거름망(100)을 제조하는 공정에 대하여 설명한다.The circular knitted fabric 110 described above is knitted with PLA (Ploy Latic Acid) resin, which is known as an eco-friendly material. Hereinafter, a process of manufacturing the strainer 100 using PLA resin will be described.

환편물의 편직을 위한 실의 제조는 PLA 모노 필라멘트 제조 공정과 PLA 멀티 필라멘트 제조 공정으로 구분 형성된다.The production of yarn for knitting circular knitted fabrics is divided into a PLA monofilament manufacturing process and a PLA multifilament manufacturing process.

우선, PLA 수지를 165~175℃의 온도 조건에서 용융 방사하는 공정을 통해서 매우 가는 두께의 PLA 모노 필라멘트를 제조한다. 이렇게 형성된 매우 가는 두께의 PLA 모노 필라멘트 가닥들은 Spin Draw Yarn 공정을 통해서 35d/12f의 PLA 멀티 필라멘트로 제조된다.First, a PLA monofilament having a very thin thickness is manufactured through a process of melt spinning a PLA resin at a temperature of 165 to 175°C. The very thin PLA monofilament strands thus formed are manufactured into 35d/12f PLA multifilaments through the Spin Draw Yarn process.

위의 공정에서 제조된 PLA 멀티 필라멘트 가닥들을 환편기를 사용한 환편 공정에 의해서 지름이 80~150mm 범위 내의 통형상의 망으로 환편직된다. 이렇게 환편직된 편물(110)에는 일정 간격을 두고 일정한 크기의 눈이 형성된다. 이때 눈의 크기는 1mm 이내로 형성되는 것이 바람직하다.The PLA multifilament strands manufactured in the above process are circularly knitted into a cylindrical net within the range of 80-150mm in diameter by a circular knitting process using a circular knitting machine. In this circular knitted fabric 110, eyes of a certain size are formed at regular intervals. At this time, the size of the eye is preferably formed within 1mm.

환편직된 편물(110)은 다음 공정을 위해서 와인더에 의해서 접힌 상태로 감길 수 있다.The circular knitted fabric 110 may be wound in a folded state by a winder for the next process.

한편, 전술한 바와 같이 통상으로 환편직된 편물(110)은 싱크대 배수 트랩의 크기에 맞게 150~200mm 범위 내의 길이로 재단이 되고, 재단된 한쪽은 재봉 공정에 의해서 마감된다. 재단 공정과 재봉 공정은 생산공정에서 그 순서가 변경될 수 있다. 즉, 재단 이후에 재봉이 이루어질 수도 있고, 재봉 이루에 해당 위치가 재단될 수도 있다.On the other hand, as described above, the generally circular knitted fabric 110 is cut to a length within the range of 150 to 200 mm to fit the size of the sink drain trap, and one cut is finished by a sewing process. The order of the cutting process and sewing process may be changed during the production process. That is, sewing may be performed after cutting, or a corresponding position may be cut on the sewing edge.

한편, 재봉 공정이 예상되는 위치에는 도2에서 보이는 바와 같이 재봉 보강편(120)이 덧대어지고, 재봉 공정에 의해서 재봉 보강편(120)과 환편직된 편물(110)은 재봉이 됨에 따라 재봉선이 형성된다. 재봉 공정에서 사용되는 재봉실(130)로는 앞서 설명한 PLA 멀티 필라멘트가 사용된다.On the other hand, as shown in Fig. 2, the sewing reinforcement piece 120 is padded at the position where the sewing process is expected, and the sewing reinforcement piece 120 and the circular knitted fabric 110 are sewn according to the sewing line. Is formed. As the sewing thread 130 used in the sewing process, the PLA multifilament described above is used.

그리고 재봉선을 기준으로 재봉선으로부터 일정 간격 떨어진 위치의 환편직된 편물을 재단함으로써 하단은 재봉 보강편(120)과 재봉실(130)에 의해서 막히고, 상단은 개방된 주머니 형태의 거름망(100)이 완성될 수 있다.And by cutting the circular knitted fabric at a certain distance from the sewing line based on the sewing line, the lower end is blocked by the sewing reinforcement piece 120 and the sewing thread 130, and the upper end is an open pocket-shaped strainer 100 to be completed. I can.

특히, 거름망(100)의 하단을 재봉하는 과정에서 덧대어지는 재봉 보강편(120)은 콜라겐을 주성분으로 하며 글리세린과 셀룰로오스가 혼합된 소재가 박막 형태로 제조된 것이 사용될 수 있다. 재봉 보강편으로 사용되는 박막 소재의 성분은 동물성 콜라겐(collagen), 동물성 콜라겐 100 중량부에 대하여 30~35 중량부의 글리세린(glycerin) 및 27.5~22.5 중량부의 셀룰로오스(cellulose)로 이루어지고, 60~80℃ 범위 내의 온도에서 박막의 형태로 성형되고 상온에서 경화된 것이 사용될 수 있다.In particular, the sewing reinforcement piece 120, which is padded in the process of sewing the lower end of the strainer 100, is made of collagen as a main component, and a material in which glycerin and cellulose are mixed may be used in the form of a thin film. The ingredients of the thin film material used as the sewing reinforcement are made of animal collagen, 30 to 35 parts by weight of glycerin and 27.5 to 22.5 parts by weight of cellulose based on 100 parts by weight of animal collagen, and 60 to 80 It is molded in the form of a thin film at a temperature within the range of ℃ and cured at room temperature may be used.

즉, 이 발명의 실시 예에 따른 거름망(100)은 생분해성 수지인 PLA 수지로부터 형성된 PLA 멀티 필라멘트로 환편직된 편물(110)과 주성분이 콜라겐인 재봉 보강편(120)으로 구성이 된다. 따라서 음식물 찌꺼기를 처리하는 과정에서, 거름망(100)과 음식물 찌꺼기를 서로 분리하여 처리하지 않고 함께 처리해도 무방할 수 있게 된다.That is, the strainer 100 according to an embodiment of the present invention is composed of a knitted fabric 110 circularly knitted with PLA multifilaments formed from PLA resin, which is a biodegradable resin, and a sewing reinforcing piece 120 whose main component is collagen. Therefore, in the process of treating the food waste, the sieve 100 and the food waste may be treated together without being separated from each other and treated.

도3은 이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망의 사용 상태를 보인 도면이다.3 is a view showing a state of use of a strainer for a sink drain trap according to an embodiment of the present invention.

도3에서 보이는 바와 같이 싱크대(200)로부터 배수 트랩(210)을 들어 올린 후, 배수 트랩(210)의 상단부에 이 발명의 실시 예에 따른 거름망(100)의 상단이 걸리도록 함으로써, 싱크대(200)에서 설거지 등을 하는 과정에서 발생하는 음식물 찌꺼기 등 오물은 거름망(100) 내부에 쌓이게 된다.After lifting the drain trap 210 from the sink 200 as shown in FIG. 3, the upper end of the sieve 100 according to the embodiment of the present invention is caught on the upper end of the drain trap 210, so that the sink 200 In the process of washing dishes in ), dirt, such as food waste, accumulates inside the sieve 100.

앞서 설명하였듯이, 이 발명의 실시 예에 따른 거름망은 PLA 수지와 콜라겐 성분으로 구성됨으로써, 음식물 찌꺼기와 함께 처리할 수 있게 된다. 즉, 플라스틱 소재로 제조되었던 기존의 싱크대 거름망 제품과는 달리 음식물 찌꺼기와 분리하지 않고 한꺼번에 처리할 수 있는 장점이 있게 된다.As described above, the strainer according to the embodiment of the present invention is composed of PLA resin and collagen, so that it can be treated with food waste. In other words, unlike conventional sink sieve products made of plastic materials, there is an advantage of being able to treat them all at once without separating them from food waste.

이상에서는 첨부된 도면들을 참조하면서 이 발명의 실시 예에 따른 싱크대 배수 트랩용 거름망 제조방법에 대하여 설명하였다. 이러한 실시예는 이 발명의 특허청구범위에 기재된 기술 사상에 포함되는 것이다. 또한, 이러한 실시 예들은 예시적인 것에 불과한 것으로, 이 발명의 특허청구범위를 해석함에 있어 한정 해석해서는 아니 된다.In the above, a method of manufacturing a strainer for a sink drain trap according to an embodiment of the present invention has been described with reference to the accompanying drawings. These embodiments are included in the technical idea described in the claims of this invention. In addition, these embodiments are only illustrative, and should not be construed as limiting in interpreting the claims of the present invention.

100 : 싱크대 배수 트랩용 거름망
110 : 환편직된 편물
120 : 재봉 보강편
130 : 재봉실
200 : 싱크대
210 : 배수 트랩100: strainer for sink drain trap
110: circular knitted fabric
120: sewing reinforcement piece
130: sewing thread
200: sink
210: drain trap

Claims (3)

PLA 수지를 165~175℃ 온도 조건에서 용융 방사하여 PLA 모노 필라멘트를 제조하는 단계;
상기 PLA 모노 필라멘트를 Spin Draw Yarn 공정으로 35d/12f의 PLA 멀티 필라멘트를 제조하는 단계;
환편기에서 상기 PLA 멀티 필라멘트를 사용하여 지름이 80~150㎜의 통형태의 망으로 환편직하는 단계;
상기 단계에서 길이가 긴 통형태의 망으로 환편직된 편물의 외부에 일정 간격을 두고 일정 폭을 갖는 재봉 보강편을 덧대는 단계;
상기 PLA 멀티 필라멘트를 사용하여 상기 재봉 보강편이 덧대어진 위치의 상기 환편직된 편물을 재봉하는 단계; 및
상기 단계에서 재봉에 의해 형성된 재봉선을 기준으로 상기 재봉선으로부터 일정 간격 떨어진 위치의 환편직된 편물을 재단하는 단계; 를 포함하여 이루어지는 것을 특징으로 하는 싱크대 배수 트랩용 거름망 제조방법.
Melt-spinning the PLA resin at a temperature of 165 to 175°C to prepare a PLA monofilament;
Preparing a 35d/12f PLA multifilament from the PLA monofilament by a Spin Draw Yarn process;
Using the PLA multi-filament in a circular knitting machine, circular knitting into a tubular network having a diameter of 80 to 150 mm;
Adding a sewing reinforcement piece having a predetermined width at a predetermined interval to the outside of the circular knitted fabric with a long cylindrical net in the step;
Sewing the circular knitted fabric at the position where the sewing reinforcement piece is padded using the PLA multifilament; And
Cutting a circular knitted fabric at a predetermined distance from the sewing line based on the sewing line formed by sewing in the step; A method for manufacturing a strainer for a sink drain trap, characterized in that comprising a.
 제1항에 있어서,
상기 재봉 보강편은,
동물성 콜라겐(collagen), 상기 동물성 콜라겐 100 중량부에 대하여 30~35 중량부의 글리세린(glycerin) 및 27.5~22.5 중량부의 셀룰로오스(cellulose)를 혼합하고, 60~80℃ 범위 내의 온도에서 박막의 형태로 성형된 것을 특징으로 하는 싱크대 배수 트랩용 거름망 제조방법.
The method of claim 1,
The sewing reinforcement piece,
Animal collagen, 30 to 35 parts by weight of glycerin and 27.5 to 22.5 parts by weight of cellulose are mixed with respect to 100 parts by weight of animal collagen, and formed into a thin film at a temperature within the range of 60 to 80°C. A method for manufacturing a strainer for a sink drain trap, characterized in that.
 제1항 또는 제2항의 방법에 의해서 제조된 싱크대 배수 트랩용 거름망.
A strainer for a sink drain trap manufactured by the method of claim 1 or 2.
KR1020190143931A 2019-11-12 2019-11-12 Method for manufacturing trap nets of sink and the trap nets KR102237697B1 (en)