KR102225823B1 - Pet toilet sand using pet sand odor remover and its manufacturing method - Google Patents
Pet toilet sand using pet sand odor remover and its manufacturing method Download PDFInfo
- Publication number
- KR102225823B1 KR102225823B1 KR1020200070560A KR20200070560A KR102225823B1 KR 102225823 B1 KR102225823 B1 KR 102225823B1 KR 1020200070560 A KR1020200070560 A KR 1020200070560A KR 20200070560 A KR20200070560 A KR 20200070560A KR 102225823 B1 KR102225823 B1 KR 102225823B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- sand
- capsule
- starch
- Prior art date
Abstract
Description
본 발명은 애완동물용 모래 냄새 제거제를 이용한 애완동물 화장실용 모래 및 그 제조방법에 관한 것으로, 더욱 상세하게는 고양이의 배변, 또는 배뇨로부터 발생하는 냄새를 제거하는 냄새 제거제를 일정 이상의 내압을 형성하도록 구성되는 캡슐에 내포시켜 고양이용 모래에 일정 비율로 첨가함으로써, 배변, 또는 배뇨와의 접촉시 캡슐이 파열되면서 냄새를 제거하는 애완동물용 모래 냄새 제거제를 이용한 애완동물 화장실용 모래 및 그 제조방법에 관한 것이다.The present invention relates to a pet toilet sand using a sand odor remover for pets and a method for manufacturing the same, and more particularly, a odor remover for removing odors generated from feces or urination of a cat to form an internal pressure of a certain level or more. By enclosing it in a capsule and adding it to cat sand at a certain rate, it is used in pet toilet sand and its manufacturing method using a pet sand odor remover that removes odor when the capsule is ruptured when in contact with bowel movement or urination. About.
일반적으로, 애완동물, 특히 고양이의 경우에는 배변이나 배뇨를 위한 화장실과 모래가 별도로 구비되어야만 하고, 화장실 및 모래의 구비시 배변이나 배뇨시 발생하는 냄새를 제거하기 위한 기능성 모래를 사용하거나 별도의 탈취제, 또는 냄새 제거제를 첨가해서 사용하도록 하고 있다. In general, in the case of pets, especially cats, toilets and sand for defecation or urination must be separately provided, and when toilets and sand are provided, functional sand is used to remove odors generated during defecation or urination, or a separate deodorant , Or an odor remover is added.
한편, 고양이용 모래에 사용되는 탈취제, 또는 냄새 제거제의 경우, 통상적으로 고양이용 모래에 함유된 상태로 제조가 이루어지도록 하고 있으며, 일 예로, 대한민국 등록특허 제10-1356232호에는 분말상태의 제올라이트로 이루어진 주원료와, 벤토나이트와 백토로 이루어진 보조원료와, 베이킹소다 및 셀룰로우즈로 이루어진 첨가제가 혼합 및 반죽, 롤링, 건조되어 입상으로 구성된 애완용 모래에 있어서, 상기 주원료는 분말상태의 제올라이트 30중량%에 5중량%의 수분을 혼합 믹싱하여 1~2mm크기를 갖는 입상의 1차원료와, 파쇄된 1~2mm 크기 입자형태의 입상의 제올라이트로 이루어진 2차 원료 40중량%로 혼합 구성되고, 상기 보조원료는 분말상태의 벤토나이트 5중량%와 백토 15중량%로 혼합 구성되며, 상기 첨가제는 베이킹소다 3중량%, 셀룰로우즈 2중량%, 또는 폴리아크릴아미드(polyacrylamide) 5중량%로 혼합 구성하여 제조되는 애완용 모래 및 그 제조방법이 게재된 바 있다. On the other hand, in the case of a deodorant or odor remover used in cat sand, it is generally manufactured in a state contained in cat sand. For example, Korean Patent No. 10-1356232 discloses a powdery zeolite. In the pet sand consisting of a main raw material, an auxiliary raw material composed of bentonite and clay, and an additive composed of baking soda and cellulose are mixed, kneaded, rolled, and dried to form a granular form, the main raw material is in a powdery zeolite 30% by weight. 5% by weight of water is mixed and mixed with a granular one-dimensional material having a size of 1 to 2 mm, and a secondary raw material composed of granular zeolite having a size of 1 to 2 mm, which is crushed, is mixed with 40% by weight of the auxiliary material. Is composed of 5% by weight of powdery bentonite and 15% by weight of clay, and the additive is prepared by mixing 3% by weight of baking soda, 2% by weight of cellulose, or 5% by weight of polyacrylamide. Pet sand and its manufacturing method have been published.
하지만, 전술한 선행기술문헌은 애완동물모래에 흡착성분을 갖는 물질을 혼합하여 탈취성능을 제공하는 것으로 흡착성분의 기공보다 작은 물질에 대한 흡착능력은 제공되지 못하는 문제점이 있다. However, the above-described prior art document provides a deodorizing performance by mixing a material having an adsorption component in pet sand, and thus, there is a problem in that the adsorption capability for a material smaller than the pores of the adsorption component cannot be provided.
또한, 대한민국 등록특허 제10-1728418호에는, 정수슬러지, 애쉬(ASH) 및 석회석을 혼합한 활성슬러지를 가열하여 소성시키고, 상기 소성된 소성물에 양전하물질을 코팅하여 구성되되, 상기 정수슬러지 100중량부에 대해 애쉬 100~200중량부, 석회석 5~20중량부를 혼합하여 활성슬러지를 제조하고, 활성슬러지를 소성 및 탄화시켜 001~5mm의 소성물을 제조하고, 상기 소성물 100중량부에 대해 양전하물질 001~5중량부를 혼합하여 소성물에 양전하물질을 코팅한 구조를 갖는 것을 특징으로 하는 애완동물용 모래탈취제가 게재된 바 있다. In addition, Korean Patent Registration No. 10-1728418 is configured by heating and sintering activated sludge mixed with purified sludge, ash (ASH) and limestone, and coating the calcined material with a positively charged material, and the purified sludge 100 100 to 200 parts by weight of ash and 5 to 20 parts by weight of limestone are mixed to prepare activated sludge, and the activated sludge is calcined and carbonized to prepare a 001 to 5 mm calcined product, and based on 100 parts by weight of the calcined product A sand deodorant for pets, characterized in that it has a structure in which 001 to 5 parts by weight of a positively charged material is mixed and coated with a positively charged material on a fired product, has been published.
그러나, 전술한 선행기술문헌에 의하면, 35~50%의 SiO2, 20~30%의 Al2O3을 포함하는 무기물에 유기물이 일부 포함되는 정수 슬러지를 주성분으로 하는 것이고, 특히 석회석이나 금속 또는 금속산화물이 더 혼합되도록 구성되는 것으로, 이는 고양이와 같은 애완동물의 건강에 심각한 유해성 문제가 있다. However, according to the above-described prior art document, the main component is a purified sludge containing some organic matter in an inorganic material including 35 to 50% SiO 2 and 20 to 30% Al 2 O 3, and in particular, limestone or metal or It is configured to be further mixed with metal oxides, which poses a serious hazard to the health of pets such as cats.
이와 같은 문제점을 해결하기 위하여 본 발명은 전술한 배경기술에 의해서 안출된 것으로, 고양이와 같은 애완동물에게 무해한 성분으로 이루어진 냄새 제거제를 제공하되, 고온의 온도에서 분해되면서 냄새 제거제의 기능성이 소실되는 것을 최소화하여 고양이의 배변, 또는 배뇨로부터 발생하는 냄새의 제거 효율을 극대화할 수 있는 애완동물용 모래 냄새 제거제를 이용한 애완동물 화장실용 모래 및 그 제조방법을 제공하는데 그 목적이 있다.In order to solve such a problem, the present invention is conceived by the above-described background technology, and provides a odor remover made of ingredients that are harmless to pets such as cats, but the functionality of the odor remover is lost as it decomposes at a high temperature. An object thereof is to provide sand for pet toilets and a manufacturing method thereof using a sand odor remover for pets that can maximize the removal efficiency of odors generated from feces or urination of a cat by minimizing it.
또한, 본 발명은 냄새 제거제를 내포액으로 제조한 후, 일정 이상의 내압을 형성하도록 구성되는 캡슐에 내포시켜 고양이용 모래에 일정 비율로 첨가함으로써, 배변, 또는 배뇨와의 접촉시 캡슐이 파열되면서 배변, 또는 배뇨를 용화, 흡수하여 냄새의 제거가 이루어지도록 하는 애완동물용 모래 냄새 제거제를 이용한 애완동물 화장실용 모래 및 그 제조방법을 제공하는데 그 목적이 있다.In addition, in the present invention, after the odor remover is prepared as an inclusion solution, it is enclosed in a capsule configured to form a certain or more internal pressure and added to the cat sand at a certain ratio, so that the capsule is ruptured upon contact with bowel movement or urination. It is an object of the present invention to provide sand for pet toilets and a method of manufacturing the same, using a sand odor remover for pets that solubilizes and absorbs urination to remove odors.
또한, 본 발명은 캡슐의 내압 강도가 0.4~1.0Pa를 이루도록 제조함으로써, 캡슐의 운송 과정 중 외부 충격으로 인한 파열이 발생하는 것을 방지하고, 캡슐의 제품 품질이 저하되는 것을 방지하는 애완동물용 모래 냄새 제거제를 이용한 애완동물 화장실용 모래 및 그 제조방법을 제공하는데 그 목적이 있다.In addition, the present invention prevents the occurrence of rupture due to external impact during the transport process of the capsule by manufacturing the capsule to achieve an internal pressure strength of 0.4 ~ 1.0Pa, and prevents degradation of the product quality of the capsule for pet sand An object thereof is to provide sand for pet toilets and a method of manufacturing the same using an odor remover.
다만, 본 발명의 목적은 이에만 제한되는 것은 아니며, 명시적으로 언급하지 않더라도 과제의 해결수단이나 실시 형태로부터 파악될 수 있는 목적이나 효과도 이에 포함됨은 물론이다. However, the object of the present invention is not limited thereto, and objects or effects that can be grasped from the solutions or embodiments of the problem are also included therein even if not explicitly mentioned.
이와 같은 과제를 달성하기 위한 본 발명의 일 실시예에 따르면, 카라기난 30중량부~82중량부, 젤라틴 5중량부~42중량부, 하이드록시프로필셀룰로스 3중량부~40중량부, 알긴산 나트륨 3중량부~45중량부, 곤약 아교 1중량부~10중량부, 구아검 1중량부~10중량부, 크산탄 1중량부~8중량부 및 글리세린 1중량부~30중량부로 구성되는 캡슐 외피; 및 피톤치드 25 중량부~35중량부, 식물성 에센스 오일로 이루어진 군으로부터 선택되는 적어도 1종의 향료 60중량부~70중량부, 음이온 용액 3중량부~7중량부로 구성되는 내포액;으로 구성되는 애완동물용 모래 냄새 제거제를 제공한다.According to an embodiment of the present invention for achieving such a problem, carrageenan 30 parts by weight to 82 parts by weight, gelatin 5 parts by weight to 42 parts by weight, hydroxypropyl cellulose 3 parts by weight to 40 parts by weight, sodium alginate 3 parts by weight Part to 45 parts by weight, 1 to 10 parts by weight of konjac glue, 1 to 10 parts by weight of guar gum, 1 to 8 parts by weight of xanthan and 1 to 30 parts by weight of glycerin; And phytoncide 25 parts by weight to 35 parts by weight, 60 parts by weight to 70 parts by weight of at least one perfume selected from the group consisting of vegetable essence oil, and an inclusion solution composed of 3 parts by weight to 7 parts by weight of an anion solution; Offer a sand odor remover for animals.
본 발명의 일 실시예에 따르면, 상기 캡슐 외피는, 열화칼슘, 또는 염화 나트륨으로부터 선택되는 적어도 1종의 염화염 1 중량부 ~ 45중량부와 물이 1:5의 질량비로 혼합된 혼합물과 교반된 후, 50℃의 온도로 5분~10분간 가열하여 겔의 형태로 전환되는 것을 특징으로 한다.According to an embodiment of the present invention, the capsule shell is stirred with a mixture of 1 part by weight to 45 parts by weight of at least one chloride salt selected from deteriorated calcium or sodium chloride and water in a mass ratio of 1:5. After that, it is characterized in that it is converted into a gel by heating for 5 to 10 minutes at a temperature of 50°C.
본 발명의 일 실시예에 따르면, 상기 캡슐 외피는 내압 강도가 0.4 ~ 1.0Pa로 형성되는 것을 특징으로 한다.According to an embodiment of the present invention, the capsule shell is characterized in that the internal pressure strength is formed to 0.4 ~ 1.0Pa.
본 발명의 일 실시예에 따르면, 상기 캡슐 외피는 펙틴 1 중량부~15 중량부, 말토덱스트린 1 중량부~20 중량부, 키토산 1 중량부~5중량부를 더 혼합되는 것을 특징으로 한다.According to an embodiment of the present invention, the capsule shell is characterized in that 1 to 15 parts by weight of pectin, 1 to 20 parts by weight of maltodextrin, and 1 to 5 parts by weight of chitosan are further mixed.
본 발명의 일 실시예에 따르면, 상기 캡슐 외피는, 카라기난과 하이드록시프로필메틸셀룰로스의 혼합시 배합 질량비 기준 7:1 내지 3:1로 배합이 이루어지는 것을 특징으로 한다.According to an embodiment of the present invention, the capsule shell is characterized in that the blending is made in a ratio of 7:1 to 3:1 based on a mass ratio of carrageenan and hydroxypropylmethylcellulose.
또한, 본 발명의 다른 일 실시예에 따르면, (a) 피톤치드, 식물성 에센스 오일, 음이온 용액을 포함하는 내포액과, 카라기난, 젤라틴, 하이드록시프로필셀룰로스, 알긴산 나트륨, 곤약 아교, 구아검, 크산탄 및 글리세린을 포함하는 캡슐 외피액 및 염화염 용액을 각각 획득하는 단계; (b) 염화염 용액에 캡슐 외피액을 투입하여 혼합 및 교반하여 액상의 교반물을 제조하고, 상기 액상의 교반물을 50℃의 온도로 5분~10분간 가열하여 전환하는 단계; (c) 전환된 겔 형태의 캡슐 외피의 내부로 내포액을 주입하여 겔 형태의 캡슐을 제조하는 단계; (d) 상기 겔 형태의 캡슐의 내압 강도가 내압 강도가 0.4 ~ 1.0Pa로 형성되도록 건조하는 단계;를 포함하는 애완동물용 모래 냄새 제거제 제조방법을 제공한다.In addition, according to another embodiment of the present invention, (a) phytoncide, vegetable essence oil, an inclusion solution containing an anion solution, carrageenan, gelatin, hydroxypropylcellulose, sodium alginate, konjac glue, guar gum, xanthan And obtaining a capsule shell solution and a chloride salt solution containing glycerin, respectively. (b) adding the capsule shell solution to the chloride solution, mixing and stirring to prepare a liquid agitated product, and converting the liquid agitated product by heating at a temperature of 50° C. for 5 to 10 minutes; (c) preparing a gel-type capsule by injecting an encapsulation solution into the inside of the converted gel-type capsule shell; It provides a method for producing a sand odor removing agent for pets comprising the steps of: (d) drying the gel-type capsule so that the pressure strength of the capsule is formed to have a pressure strength of 0.4 to 1.0Pa.
또한, 본 발명의 다른 일 실시예에 따르면, (a) 콩비지, 전분, 옥수수분, 탄산칼슘, 구아검, 구연산으로 구성된 모래 조성물을 준비하는 단계; (b) 상기 모래 조성물을 1시간~3시간 동안 교반하는 단계; (c) 교반이 완료된 모래용 혼합물을 프레스 성형 방법을 통해 성형하고, 성형이 이루어진 성형물을 건조 및 절단하여 화장실용 모래를 제조하는 단계;를 포함하는 애완동물 화장실용 모래 제조방법을 제공한다.In addition, according to another embodiment of the present invention, (a) preparing a sand composition consisting of soybean curd, starch, corn flour, calcium carbonate, guar gum, citric acid; (b) stirring the sand composition for 1 to 3 hours; (c) molding the mixture for sand after the agitation is completed through a press molding method, and drying and cutting the molded product to produce toilet sand for a pet toilet, including.
본 발명의 다른 일 실시예에 따르면, 상기 애완동물 화장실용 모래 제조방법은, (d) 내압 강도가 0.4 ~ 1.0Pa로 형성되며, 피톤치드, 에센스 및 음이온 용액이 일정 중량부로 혼합된 내포액이 수용되고, 애완동물의 배뇨와의 접촉시 15~20초 이내로 파열되도록 구성되는 겔 형태의 캡슐을 상기 화장실용 모래에 첨가하되, 상기 캡슐 7~15 : 화장실용 모래 2800의 중량비로 첨가하는 단계;를 더 포함하는 것을 특징으로 한다.According to another embodiment of the present invention, the method of manufacturing sand for a pet toilet, (d) has an internal pressure strength of 0.4 to 1.0 Pa, and contains a phytoncide, essence, and anion solution mixed in a predetermined part by weight. And, a gel-type capsule configured to rupture within 15 to 20 seconds upon contact with urination of a pet, but added to the toilet sand, the capsule 7 to 15: adding the toilet sand at a weight ratio of 2800; It characterized in that it further includes.
본 발명의 다른 일 실시예에 따르면, 상기 모래 조성물은, 콩비지 30중량부~50중량부, 전분 20중량부~35중량부, 옥수수분 10중량부~15중량부, 탄산칼슘 3중량부~6중량부, 구아검 2중량부~10중량부, 구연산 1중량부~5중량부로 이루어지는 모래 조성물과, 이 모래 조성물에 더 혼합된 변성 전분 5중량부~10중량부로 구성되는 것을 특징으로 한다.According to another embodiment of the present invention, the sand composition, 30 parts by weight to 50 parts by weight of bean curd, 20 parts by weight to 35 parts by weight of starch, 10 parts by weight to 15 parts by weight of corn flour, 3 parts by weight of calcium carbonate to 6 It is characterized by consisting of a sand composition consisting of parts by weight, 2 to 10 parts by weight of guar gum, and 1 to 5 parts by weight of citric acid, and 5 to 10 parts by weight of modified starch further mixed with the sand composition.
본 발명의 다른 일 실시예에 따르면, 상기 (b) 단계는, 상기 모래 조성물의 교반시, 하이드록시프로필 전분, 인산에스테르나트륨 전분, 옥테닐썩시네이트 전분, 카복시메틸 전분 혹은 전분화녹말로부터 선택된 1종으로 이루어지는 변성전분을 더 투입하여 교반하는것을 특징으로 한다.According to another embodiment of the present invention, step (b) is, when the sand composition is stirred, 1 selected from hydroxypropyl starch, sodium phosphate ester starch, octenyl succinate starch, carboxymethyl starch, or starch starch. It is characterized by further adding and stirring the modified starch consisting of species.
이와 같은 본 발명의 실시예에 의하면, 고양이와 같은 애완동물에게 무해한 성분으로 이루어진 냄새 제거제를 제공하되, 고온의 온도에서 분해되면서 냄새 제거제의 기능성이 소실되는 것을 최소화하여 고양이의 배변, 또는 배뇨로부터 발생하는 냄새의 제거 효율을 극대화할 수 있는 효과가 있다.According to such an embodiment of the present invention, a odor remover made of ingredients harmless to pets such as cats is provided, but it is generated from feces or urination of a cat by minimizing loss of the functionality of the odor remover while decomposing at a high temperature. There is an effect that can maximize the removal efficiency of the odor.
또한, 본 발명의 실시예에 의하면, 냄새 제거제를 내포액으로 제조한 후, 일정 이상의 내압을 형성하도록 구성되는 캡슐에 내포시켜 고양이용 모래에 일정 비율로 첨가함으로써, 배변, 또는 배뇨와의 접촉시에만 캡슐이 파열되면서 배변, 또는 배뇨를 용화, 흡수하여 배변, 또는 배뇨의 냄새를 제거가 이루어짐에 따라 냄새 제거제의 수명을 장시간 유지할 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, after the odor remover is prepared as an inclusion solution, it is enclosed in a capsule configured to form a certain or more internal pressure and added to the cat sand at a certain ratio, so that when it comes into contact with defecation or urination. Only when the capsule is ruptured, the odor of the bowel movement or urination is removed by solubilizing and absorbing the bowel movement or urination, thereby maintaining the life of the odor remover for a long time.
또한, 본 발명의 실시예에 의하면, 캡슐의 내압 강도가 0.4~1.0Pa를 이루도록 제조함으로써, 캡슐의 운송 과정 중 외부 충격으로 인한 파열이 발생하는 것을 방지하고, 캡슐의 제품 품질이 저하되는 것을 방지할 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, by manufacturing the capsule to achieve an internal pressure strength of 0.4 to 1.0 Pa, it prevents rupture due to an external shock during the transportation process of the capsule, and prevents the product quality of the capsule from deteriorating. There is an effect that can be done.
더불어, 본 발명의 다양하면서도 유익한 장점과 효과는 상술한 내용에 한정되지 않으며, 본 발명의 구체적인 실시 형태를 설명하는 과정에서 보다 쉽게 이해될 수 있을 것이다. In addition, various and beneficial advantages and effects of the present invention are not limited to the above description, and may be more easily understood in the course of describing specific embodiments of the present invention.
도 1은 본 발명의 일 실시예에 따른 애완동물용 모래 냄새 제거제의 제조 과정을 나타낸 순서도,
도 2는 본 발명의 일 실시예에 따른 애완동물용 모래 냄새 제거제가 혼합되는 애완동물 화장실용 모래의 제조 과정을 나타낸 순서도,
도 3은 본 발명의 일 실시예에 따른 애완동물용 모래 냄새 제거제가 혼합된 상태의 애완동물 화장실용 모래의 사용 전,후 상태를 나타낸 예시도이다.1 is a flow chart showing a manufacturing process of a sand odor remover for pets according to an embodiment of the present invention,
Figure 2 is a flow chart showing the manufacturing process of the pet toilet sand mixed with a pet sand odor remover according to an embodiment of the present invention,
3 is an exemplary view showing a state before and after the use of the pet toilet sand in a state in which a sand odor remover for pets according to an embodiment of the present invention is mixed.
이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. In addition, in describing the present invention, when it is determined that a detailed description of a related known configuration or function may obscure the subject matter of the present invention, a detailed description thereof will be omitted.
또한, 이하에서 기재된 "포함하다", "구성하다" 또는 "가지다" 등의 용어는, 특별히 반대되는 기재가 없는 한, 해당 구성 요소가 내재될 수 있음을 의미하는 것이므로, 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것으로 해석되어야 하며, 기술적이거나 과학적인 용어를 포함한 모든 용어들은, 다르게 정의되지 않는 한, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가진다. In addition, terms such as "include", "consist of" or "have" described below mean that the corresponding component may be included unless otherwise stated, excluding other components. It should be construed as that it may further include other constituent elements, and all terms including technical or scientific terms are, unless otherwise defined, by those of ordinary skill in the technical field to which the present invention belongs. It has the same meaning as understood.
이하, 첨부된 도면을 참고하여 본 발명의 실시예들을 상세히 설명하도록 한다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도시된 바와 같이, 본 발명의 애완동물용 모래 냄새 제거제는 애완동물이 사용하는 화장실용 모래에 일정량 투입되어 애완동물의 배변, 또는 배뇨(바람직하게는 배뇨)와의 접촉시 파열되면서 내부에 수용되는 내포액에 의해 배변, 또는 배뇨로부서 발생하는 냄새의 제거가 이루어지도록 구성되는 것으로, 카라기난, 젤라틴, 하이드록시프로필셀룰로스, 알긴산 나트륨, 곤약 아교, 구아검, 크산탄 및 글리세린이 일정 중량부로 혼합되는 캡슐 외피와, 캡슐 외피의 내부로 수용되는 피톤치드, 에센스 및 음이온 용액이 일정 중량부로 혼합되는 내포액으로 이루어진다.As shown, the sand odor remover for pets of the present invention is injected in a certain amount into the toilet sand used by the pet, and is ruptured upon contact with the bowel movement or urination (preferably urination) of the pet, and contained therein. A capsule composed of a liquid to remove odors caused by bowel movements or urination, and in which carrageenan, gelatin, hydroxypropylcellulose, sodium alginate, konjac glue, guar gum, xanthan and glycerin are mixed in a certain part by weight It consists of a shell and an encapsulation solution in which a phytoncide, essence, and anion solution accommodated inside the capsule shell are mixed in a certain part by weight.
캡슐 외피는 배변, 또는 배뇨와의 접촉이 이루어질 때, 파열(녹음)이 발생하면서 수용된 내포액의 방출되어 배변, 또는 배뇨로부터 발생하는 냄새의 제거가 이루어지도록 구성된다. The capsule shell is configured such that when contact with bowel movements or urination is made, rupture (recording) occurs and the contained inclusion fluid is released to remove odors generated from bowel movements or urination.
여기서, 캡슐 외피는 카라기난 30중량부~82중량부, 젤라틴 5중량부~42중량부, 하이드록시프로필셀룰로스 3중량부~40중량부, 알긴산 나트륨 3중량부~45중량부, 곤약 아교 1중량부~10중량부, 구아검 1중량부~10중량부, 크산탄 1중량부~8중량부 및 글리세린 1중량부~30중량부로 구성될 수 있다. Here, the capsule shell is carrageenan 30 parts by weight to 82 parts by weight, gelatin 5 parts by weight to 42 parts by weight, hydroxypropyl cellulose 3 parts by weight to 40 parts by weight, sodium alginate 3 parts by weight to 45 parts by weight, konjac glue 1 part by weight It may consist of ~ 10 parts by weight, 1 part by weight to 10 parts by weight of guar gum, 1 part by weight to 8 parts by weight of xanthan, and 1 part by weight to 30 parts by weight of glycerin.
이때, 캡슐 외피는, 카라기난과 하이드록시프로필메틸셀룰로스의 혼합시 배합 질량비 기준 7:1 내지 3:1로 배합이 이루어지도록 할 수 있으나, 이에 한정하는 것은 아니다. At this time, the capsule shell may be blended in a ratio of 7:1 to 3:1 based on the mass ratio of carrageenan and hydroxypropylmethylcellulose, but is not limited thereto.
이는, 캡슐의 외피에 대한 강도가 일정 강도 이상으로 형성되도록 함으로써, 운반시 외부 충격에 의해 캡슐 외피가 임의적으로 파손되어 수용되는 내포액의 유출을 방지하도록 하기 위함이며, 본 발명에서는 캡슐 외피의 내압 강도가 0.4~1.0Pa를 유지할 수 있도록 구성된다.This is to prevent the outflow of the contained liquid contained by the capsule shell being arbitrarily damaged by an external impact during transportation by making the strength of the capsule's outer skin higher than a certain strength.In the present invention, the inner pressure of the capsule shell It is constructed so that the strength can maintain 0.4~1.0Pa.
또한, 캡슐 외피에 포함되는 조성물 중, 알긴산 나트륨의 경우, 3중량부 미만으로 혼합되는 경우에는 배변, 또는 배뇨의 응집성에 대한 효과가 충분히 발휘되기 어렵고, 45중량부를 초과하는 경우에는 다른 조성물과의 혼화성에 문제가 발생할 수 있으며, 함량 증가에 따른 더 이상의 효과 향상을 기대하기 어렵다.In addition, among the compositions contained in the capsule shell, in the case of sodium alginate, when it is mixed with less than 3 parts by weight, the effect on the cohesiveness of bowel movement or urination is difficult to be sufficiently exhibited, and when it exceeds 45 parts by weight, A problem may occur in miscibility, and it is difficult to expect further improvement of the effect according to an increase in the content.
또한, 곤약 아교, 구아검, 크산탄 등은 캡슐 외피의 접착성을 향상시키는 것으로, 곤약 아교는 캡슐 외피를 겔(Gel)의 형태를 이루도록 하며, 크산탄은 구아검과 함께 캡슐 외피를 이루는 조성물들 간의 결합력을 증진시키는 역할을 한다.In addition, konjac glue, guar gum, xanthan, etc. are to improve the adhesion of the capsule shell, and konjac glue makes the capsule shell to form a gel, and xanthan is a composition that forms the capsule shell together with guar gum. It plays a role in enhancing the cohesion between them.
특히, 구아검의 경우, 캡슐 외피의 점착성 및 점도를 증가시키고 유화 안정성을 증진키시는 역할을 하는 것으로, 분자량은 200,000~300,000으로 이루어지는 것을 사용하며, 본 발명에서는 구아검의 혼합량이 1중량부 미만으로 혼합되는 경우, 곤약 아교의 겔 휘발성이 충분하지 못할 수 있고, 10중량부를 초과하는 경우에는 휘발 후 잔량이 많아지면서 캡슐 외피가 충분한 겔 타입의 형태를 이루지 못하는 문제가 있다.In particular, in the case of guar gum, it serves to increase the adhesion and viscosity of the capsule shell and to enhance the emulsion stability, and a molecular weight of 200,000 to 300,000 is used, and in the present invention, the mixed amount of guar gum is less than 1 part by weight. When mixed with, the gel volatility of the konjac glue may not be sufficient, and in the case of exceeding 10 parts by weight, the remaining amount after volatilization increases and the capsule shell does not form a sufficient gel type.
한편, 본 발명의 캡슐 외피에는 열화칼슘, 또는 염화 나트륨으로부터 선택되는 적어도 1종의 염화염이 더 혼합될 수 있다. Meanwhile, at least one chloride salt selected from deteriorated calcium or sodium chloride may be further mixed with the capsule shell of the present invention.
이때, 염화염은 캡슐 외피의 총 중량부에 있어서 1 중량부 ~ 45중량부로 더 혼합될 수 있으며, 1중량부 미만으로 혼합되는 경우, 캡슐 외피의 겔의 강도, 즉 내압 강도가 충분하지 못하여 외형을 유지하기 어려울 뿐만 아니라, 외부 충격에 의해 쉽게 파손될 우려가 있고, 45 중량부를 초과하는 경우 휘발후 잔량이 많아지게 된다.At this time, the chloride salt may be further mixed in 1 part by weight to 45 parts by weight in the total weight part of the capsule shell, and if it is mixed in less than 1 part by weight, the gel strength of the capsule shell, that is, the internal pressure strength, is insufficient In addition to being difficult to maintain, there is a risk of being easily damaged by an external impact, and if it exceeds 45 parts by weight, the residual amount after volatilization increases.
아울러, 본 발명의 캡슐 외피는 내압 강도 뿐만 아니라 외형에 대한 형태 유지를 위해 펙틴, 말토덱스트린 및 키토산이 일정 중량부로 더 혼합될 수 있으며, 본 발명에서는 캡슐 외피의 총 중량부에 있어서 펙틴 1 중량부~15 중량부, 말토덱스트린 1 중량부~20 중량부, 키토산 1 중량부~5중량부를 더 혼합할 수 있다. In addition, in the capsule shell of the present invention, pectin, maltodextrin, and chitosan may be further mixed in a certain part by weight to maintain the shape for the appearance as well as the internal pressure strength, and in the present invention, 1 part by weight of pectin in the total weight part of the capsule shell ~15 parts by weight, 1 part by weight to 20 parts by weight of maltodextrin, and 1 part by weight to 5 parts by weight of chitosan may be further mixed.
이때, 펙틴은 전술한 젤라틴과 반응하여 캠슐 외피가 겔의 형태를 유지할 수 있도록 한다. 이에, 카라기난이나 젤라틴이 혼합되면서 겔 형성이 저하되는 것을 억제시켜 캡슐 외피가 겔 타입의 형태를 안정적으로 유지할 수 있도록 한다. At this time, pectin reacts with the above-described gelatin so that the capsule shell can maintain the shape of the gel. Accordingly, it is possible to stably maintain the gel-type shape of the capsule shell by suppressing deterioration of gel formation as carrageenan or gelatin is mixed.
또한, 말토덱스트린은 캡슐 외피를 이루는 조성물과 키토산의 접착성을 향상시키는 역할을 하며, 키토산은 소정의 강성을 부여하여 캡슐 외피의 외형의 형태가 일정하게 유지될 수 있도록 한다.In addition, maltodextrin serves to improve the adhesion between the composition constituting the capsule shell and chitosan, and chitosan imparts a predetermined stiffness so that the outer shape of the capsule shell can be kept constant.
아울러, 내포액은 캡슐 외피의 내부로 수용되며, 캡슐 외피의 파열시 배변, 또는 배뇨로부서 발생하는 냄새를 제거하는 것으로, 피톤치드 25 중량부~35중량부, 식물성 에센스 오일로 이루어진 군으로부터 선택되는 적어도 1종의 향료 60중량부~70중량부, 음이온 용액 3중량부~7중량부로 구성된다. In addition, the encapsulation liquid is accommodated inside the capsule shell, and removes odors caused by defecation or urination when the capsule shell is ruptured, and at least selected from the group consisting of phytoncide 25 parts by weight to 35 parts by weight, vegetable essence oil. It consists of 60 parts by weight to 70 parts by weight of one perfume and 3 parts by weight to 7 parts by weight of an anion solution.
여기서, 식물성 에센스 오일은, 올리브오일, 피마자오일, 해바라씨오일, 햄프씨드오일, 체리씨드오일, 카르나우바오일, 사탕수수오일, 큐티클오일, 대두오일, 팜오일, 코코넛오일, 포도씨오일, 텀프킨씨드오일, 미강오일, 스위트아몬드오일, 달맞이꽃오일, 홍화오일, 살구씨오일, 세서미오일, 알로에베라오일, 시어오일, 아보카도오일, 헤이즐넛오일, 쿠쿠아넛오일, 라놀린, 보리지오일, 블루베리씨드오일, 아르간오일, 브로콜리씨드오일, 블랙커런트씨드오일, 타조오일, 아몬드오일, 녹차씨오일, 달맞이오일, 로즈힙오일, 로즈힙시드오일, 마카다미아오일, 에뮤오일, 윗점오일, 연꽃오일, 카렌듈라오일, 티마누오일 중 선택된 어느 1종으로 이루어질 수 있다. Here, the vegetable essence oil is olive oil, castor oil, sunflower seed oil, hemp seed oil, cherry seed oil, carnauba oil, sugarcane oil, cuticle oil, soybean oil, palm oil, coconut oil, grape seed oil, tum Pokkin seed oil, bran oil, sweet almond oil, evening primrose oil, safflower oil, apricot seed oil, sesame oil, aloe vera oil, shea oil, avocado oil, hazelnut oil, cuquanut oil, lanolin, barley oil, blueberry seed Oil, argan oil, broccoli seed oil, black currant seed oil, ostrich oil, almond oil, green tea seed oil, evening primrose oil, rose hip oil, rose hip seed oil, macadamia oil, emu oil, high point oil, lotus oil, calendula oil, tea It may be made of any one selected from Manu Oil.
또한, 식물성 에센스 오일은, 라벤다, 티트리, 로즈마리, 케모마일, 페퍼민트, 스피아민트, 애플민트, 유카립투스, 라임블라섬, 세이지, 레몬그라스, 레몬버베나, 로즈힙, 시나몬, 자크로, 스위트펜넬, 진저, 샤프란, 에키나세아, 쟈스민, 캐러웨이, 히비스커스, 마리골드 등으로부터 정제된 에센스 오일 성분으로 이루어질 수 있다. In addition, vegetable essence oils include lavender, tea tree, rosemary, chemomile, peppermint, spearmint, applemint, eucalyptus, lime blossom, sage, lemongrass, lemon verbena, rosehip, cinnamon, jacro, sweet fennel, It may consist of an essence oil component purified from ginger, saffron, echinacea, jasmine, caraway, hibiscus, marigold, and the like.
이와 같이 구성된 본 발명은 전술한 내포액이 수용되는 캡슐 외피와, 이 캡슐 외피가 일정 중량부로 구비되며, 캡슐 외피가 배변, 또는 배요와의 접촉시 파열면서 내포액은 배변, 또는 배뇨의 냄새를 제거하고, 파열된 캡슐 외피는 애완동물 화장실용 모래와의 응축이 이루어지면서 배변, 또는 배뇨와의 접착성에 대한 효과를 향상시키도록 구성될 수 있다. The present invention configured as described above is provided with a capsule shell in which the above-described encapsulation solution is accommodated, and the capsule shell is provided in a certain weight part, and the capsular solution ruptures upon contact with defecation or urination while the encapsulation liquid emits the smell of defecation or urination. The removed and ruptured capsule shell may be configured to improve the effect on adhesion to bowel movement or urination while condensation with sand for pet toilets is achieved.
이와 같이 구성된 본 발명의 내포액이 수용되는 캡슐 외피는 도 1에 도시된 바와 같이, 내포액, 캡슐 외피액 및 염화염 용액을 획득하는 단계(S110), 캡슐 외피액과 염화염 용액 혼합을 혼합 및 교반하는 단계(S120), 교반물을 겔 형태로 전환하는 단계(S130), 겔 형태의 캡슐 외피의 내부로 내포액을 주입하는 단계(S140) 및 내포액이 수용된 캡슐 외피를 건조하는 단계(S150)에 의해 제조된다. As shown in FIG. 1, the capsule shell configured as described above containing the encapsulation solution of the present invention is a step (S110) of obtaining the encapsulation solution, the capsule shell solution, and the chloride solution, mixing the capsule shell solution and the chloride solution And the step of stirring (S120), the step of converting the agitated material into a gel form (S130), the step of injecting the inner envelope liquid into the inside of the capsule shell in the gel form (S140), and the step of drying the capsule shell containing the inner envelope ( S150).
S110 단계는, 피톤치드 25 중량부~35중량부, 식물성 에센스 오일로 이루어진 군으로부터 선택되는 적어도 1종의 향료 60중량부~70중량부, 음이온 용액 3중량부~7중량부로 이루어지는 내포액을 마련한다.Step S110, to prepare an inclusion solution consisting of 25 parts by weight to 35 parts by weight of phytoncide, 60 parts by weight to 70 parts by weight of at least one perfume selected from the group consisting of vegetable essence oil, and 3 parts by weight to 7 parts by weight of an anion solution. .
또한, 카라기난 30중량부~82중량부, 젤라틴 5중량부~42중량부, 하이드록시프로필셀룰로스 3중량부~40중량부, 알긴산 나트륨 3중량부~45중량부, 곤약 아교 1중량부~10중량부, 구아검 1중량부~10중량부, 크산탄 1중량부~8중량부 및 글리세린 1중량부~30중량부로 구성되는 캡슐 외피액과, 이 캡슐 외피액에 더 혼합되는 펙틴 5 중량부~15 중량부, 말토덱스트린 10 중량부~20 중량부, 키토산 2 중량부~5중량부를 각각 개별적으로 마련한다. In addition, 30 to 82 parts by weight of carrageenan, 5 to 42 parts by weight of gelatin, 3 to 40 parts by weight of hydroxypropyl cellulose, 3 to 45 parts by weight of sodium alginate, 1 to 10 parts by weight of konjac glue Parts, a capsule shell liquid consisting of 1 to 10 parts by weight of guar gum, 1 to 8 parts by weight of xanthan and 1 to 30 parts by weight of glycerin, and 5 parts by weight of pectin to be further mixed with the capsule shell liquid 15 parts by weight, 10 parts by weight to 20 parts by weight of maltodextrin, and 2 parts by weight to 5 parts by weight of chitosan are prepared individually.
아울러, 열화칼슘, 또는 염화 나트륨으로부터 선택되는 적어도 1종의 염화염을 캡슐 외피액의 총 중량에 있어서 1 중량부 ~ 45중량부로 마련한다. In addition, at least one chloride salt selected from deteriorated calcium or sodium chloride is provided in an amount of 1 to 45 parts by weight based on the total weight of the capsule shell liquid.
이때, 염화염 용액은 열화칼슘, 또는 염화 나트륨으로부터 선택되는 적어도 1종을 물과 1:5의 질량비로 혼합하고, 8시간 동안 활성화한 후 발생하는 침전물을 제외한 혼합물의 상층부를 별도의 용기로 일정 중량부로 담는다. At this time, in the chloride solution, at least one selected from deteriorated calcium or sodium chloride is mixed with water in a mass ratio of 1:5, and the upper layer of the mixture excluding the precipitate generated after activating for 8 hours is fixed in a separate container. Put it in parts by weight.
S120 단계는, S110 단계에 의해 마련된 염화염 용액에 캡슐 외피액을 투입하여 혼합 및 교반하여 교반물을 제조한다.In step S120, the capsule shell solution is added to the chloride solution prepared by step S110, mixed and stirred to prepare a stirred product.
S130 단계는, S120 단계를 통해 제조된 교반물을 일정 온도로 가열하여 액상의 교반물을 겔 타입으로 전환하는 단계로, 본 발명에서는 액상의 교반물을 50℃의 온도로 5분~10분간 가열하여 전환이 이루어지도록 한다.Step S130 is a step of converting the liquid agitated product to a gel type by heating the agitated product prepared through the step S120 to a constant temperature. In the present invention, the liquid agitated product is heated at a temperature of 50° C. for 5 minutes to 10 minutes. So that the conversion takes place.
S140 단계는, S130 단계에 의해 전환된 겔 형태의 캡슐 외피의 내부로 내포액을 주입하여 겔 형태의 캡슐을 제조하는 단계로, 통상의 주입노즐, 또는 주사기 등과 같은 수단을 통해 캡슐 외피의 내부로 일정량의 내포액을 주입하는 단계이다.Step S140 is a step of injecting the encapsulation solution into the inside of the gel-like capsule shell converted by step S130 to prepare a gel-like capsule, and into the inside of the capsule shell through a means such as a conventional injection nozzle or a syringe. This is the step of injecting a certain amount of inclusion liquid.
S150 단계는, 내포액이 수용된 캡슐을 텀플러와 같은 건조장치를 통해 온도 24℃, 습도 30%~45%의 조건으로 건조시켜 겔 형태의 캡슐의 외면에 대한 소정의 강성이 부여되도록 하는 단계로, 바람직하게는, 캡슐 외피(내포액이 수용된 캡슐)의 내압 강도가 0.4~1.0Pa를 유지할 수 있도록 1시간~3시간 동안 건조한다.Step S150 is a step of drying the capsule containing the encapsulation liquid under conditions of a temperature of 24°C and a humidity of 30% to 45% through a drying device such as a tumbler so that a predetermined stiffness is imparted to the outer surface of the capsule in the form of a gel. , Preferably, it is dried for 1 hour to 3 hours so that the inner pressure strength of the capsule shell (capsule in which the inner liquid is contained) can maintain 0.4 to 1.0 Pa.
한편, 본 발명은 파열된 캡슐 외피(내포액이 수용된 캡슐)가 애완동물 화장실용 모래와의 응축이 이루어지면서 배변, 또는 배뇨와의 접착성에 대한 효과를 향상시키도록 전술한 캡슐 외피와의 접착성이 좋은 애완동물 화장실용 모래를 더 제공할 수 있다. On the other hand, the present invention is the adhesion of the capsule shell described above so that the ruptured capsule shell (capsule in which the inner liquid is contained) is condensed with the sand for the pet toilet and improves the effect on the adhesion to bowel movement or urination. You can provide more sand for this good pet toilet.
이때, 애완동물 화장실용 모래는 도 2에 도시된 바와 같이, 모래 조성물 분쇄단계(S210), 모래 조성물 교반단계(S220), 화장실용 모래 성형단계(S230) 및 캡슐 혼합단계(S240)로 구성된다. At this time, the sand for the pet toilet consists of a sand composition crushing step (S210), a sand composition stirring step (S220), a toilet sand molding step (S230) and a capsule mixing step (S240), as shown in FIG. .
모래 조성물 분쇄단계(S210)는 콩비지 30중량부~50중량부, 전분 20중량부~35중량부, 옥수수분 10중량부~15중량부, 탄산칼슘 3중량부~6중량부, 구아검 2중량부~10중량부, 구연산 1중량부~5중량부로 이루어지는 모래 조성물과, 이 모래 조성물에 더 혼합된 변성 전분 5중량부~10중량부를 준비하고, 이 중 콩비지를 별도로 분쇄기에 투입하여 콩비지의 입자가 10~300메쉬를 형성할 때까지 분쇄하는 단계이다.Sand composition grinding step (S210) is soybean curd 30 parts by weight to 50 parts by weight, starch 20 parts by weight to 35 parts by weight, corn flour 10 parts by weight to 15 parts by weight, calcium carbonate 3 parts by weight to 6 parts by weight, guar gum 2 parts by weight A sand composition consisting of parts by weight of 10 to 10 parts by weight and 1 to 5 parts by weight of citric acid, and 5 to 10 parts by weight of modified starch further mixed with the sand composition are prepared. This is the step of pulverizing until 10 to 300 meshes are formed.
모래 조성물 교반단계(S220)는 준비된 모래 조성물을 교반기에 넣고, 교반기 내 균일하게 교반하는 단계로, 1시간~3시간 동안 교반이 이루어지도록 구성된다. 이때, 전술한 변성전분을 함께 투입하여 교반이 이루어지도록 한다. The sand composition stirring step (S220) is a step of uniformly stirring the prepared sand composition in a stirrer, and is configured to be stirred for 1 hour to 3 hours. At this time, the above-described modified starch is added together to achieve stirring.
여기서, 변성전분은 하이드록시프로필 전분, 인산에스테르나트륨 전분, 옥테닐썩시네이트 전분, 카복시메틸 전분 혹은 전분화녹말로부터 선택된 1종으로 이루어진다.Here, the modified starch is composed of one selected from hydroxypropyl starch, sodium phosphate ester starch, octenyl oxynate starch, carboxymethyl starch, or starch starch.
화장실용 모래 성형단계(S230)는 교반이 완료된 모래용 혼합물을 프레스 성형 방법을 통해 성형하고, 성형이 이루어진 성형물을 건조 및 절단하는 단계이다.The sand molding step for toilet (S230) is a step of molding the mixture for sand, which has been stirred, through a press molding method, and drying and cutting the molded product.
캡슐 혼합단계(S240)는 내포액이 수용된 캡슐 7~15 : 화장실용 모래 2800 의 중량비로 캡슐과 화장실용 모래를 혼합하고, 혼합된 캡슐 및 화장실용 모래의 운송이 이루어지도록 포장하는 단계이다.The capsule mixing step (S240) is a step of mixing the capsule and the toilet sand at a weight ratio of 7 to 15 capsules containing the inclusion liquid: 2800 toilet sand, and packing the mixed capsule and toilet sand to be transported.
이와 같이 구성된 본 발명은 애완동물, 특히 고양이의 배뇨시 내포액이 수용된 캡슐의 내압 압력을 제어하여, 캡슐이 애완동물, 특히 고양이의 배뇨와 접촉하면 파열되면서 고양이의 배뇨로부터 발생하는 냄새를 제거함과 동시에 상기 고양이의 배뇨가 캡슐과 화장실용 모래와 접촉한 후 15~20초 이내로 상기 배뇨를 용화 및 흡수가 이루어지도록 하며, 캡슐의 파열 속도를 높이고, 화장실용 모래의 포장 운송 과정 중 파열되는 것을 차단하여 제품의 품질에 대한 개선된 효과를 제공하는 것이다. The present invention configured as described above controls the internal pressure pressure of the capsule containing the inclusion fluid during urination of a pet, especially a cat, and removes odors generated from urination of the cat as it ruptures when the capsule comes into contact with the urination of a pet, especially a cat. At the same time, the cat's urination is dissolved and absorbed within 15 to 20 seconds after contact with the capsule and the toilet sand, increasing the rupture rate of the capsule, and preventing rupture during the packaging and transportation of toilet sand. This is to provide an improved effect on the quality of the product.
이하, 본 발명을 실시예에 의하여 더욱 상세하게 설명한다. 그러나 하기 실시예는 본 발명을 예시하는 것일 뿐이며, 본 발명의 범위가 하기 실시예에 한정되는 것은 아니며, 하기의 실시 예 및 실험 예는 본 발명을 구체적으로 예시하기 위한 것일 뿐, 본 발명의 권리범위를 제한하는 것이 아님은 당업자에게 있어서 명백한 사실이다. 즉, 본 발명의 단순한 변형 내지 변경은 당업자에 의하여 용이하게 실시될 수 있으며, 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것은 명백한 사실이다.Hereinafter, the present invention will be described in more detail by examples. However, the following examples are only illustrative of the present invention, and the scope of the present invention is not limited to the following examples, and the following examples and experimental examples are only intended to specifically illustrate the present invention, and the rights of the present invention It is obvious to a person skilled in the art that the scope is not limited. That is, simple modifications or changes of the present invention can be easily implemented by those skilled in the art, and it is obvious that all such modifications and changes are included in the scope of the present invention.
실시 예1.Example 1.
캡슐의 외피를 이루는 조성물을 카라기난 40중량부, 젤라틴 25중량부, 하이드록시프로필셀룰로스 25중량부, 알긴산 나트륨 20중량부, 곤약 아교 5중량부, 구아검 6중량부, 크산탄 3중량부, 글리세린 15중량부로 구성하고, 염화염 25중량부로 이루어지는 염화염 용액을 구성하여 캡슐의 내압 강도가 1Pa를 이루도록 제조하였다. The composition forming the outer shell of the capsule is 40 parts by weight of carrageenan, 25 parts by weight of gelatin, 25 parts by weight of hydroxypropylcellulose, 20 parts by weight of sodium alginate, 5 parts by weight of konjac glue, 6 parts by weight of guar gum, 3 parts by weight of xanthan, glycerin A chlorinated salt solution composed of 15 parts by weight and 25 parts by weight of chlorinated salt was prepared so that the internal pressure strength of the capsule was 1 Pa.
이때, 캡슐의 내부에 수용되는 내포액의 조성물은 피톤치드 32중량부, 에센스 65중량부, 음이온 용액 4중량부를 이루도록 구성하였다.At this time, the composition of the encapsulation solution contained in the capsule was configured to form 32 parts by weight of phytoncide, 65 parts by weight of essence, and 4 parts by weight of anion solution.
실시 예2.Example 2.
캡슐의 외피를 이루는 조성물을 카라기난 45중량부, 젤라틴 30중량부, 하이드록시프로필셀룰로스 30중량부, 알긴산 나트륨 30중량부, 곤약 아교 2중량부, 구아검 6중량부, 크산탄 5중량부, 글리세린 15중량부로 구성하고, 염화염 15중량부로 이루어지는 염화염 용액을 구성하여 캡슐의 내압 강도가 0.9Pa를 이루도록 제조하였다. The composition forming the outer shell of the capsule is carrageenan 45 parts by weight, gelatin 30 parts by weight, hydroxypropylcellulose 30 parts by weight, sodium alginate 30 parts by weight, konjac glue 2 parts by weight, guar gum 6 parts by weight, xanthan 5 parts by weight, glycerin A chlorinated salt solution composed of 15 parts by weight and 15 parts by weight of a chlorinated salt was prepared so that the internal pressure strength of the capsule was 0.9 Pa.
이때, 캡슐의 내부에 수용되는 내포액의 조성물은 피톤치드 29중량부, 에센스 68중량부, 음이온 용액 5중량부를 이루도록 구성하였다.At this time, the composition of the encapsulated liquid contained in the capsule was configured to form 29 parts by weight of phytoncide, 68 parts by weight of essence, and 5 parts by weight of an anion solution.
실시 예3.Example 3.
캡슐의 외피를 이루는 조성물을 카라기난 75중량부, 젤라틴 35중량부, 하이드록시프로필셀룰로스 35중량부, 알긴산 나트륨 20중량부, 곤약 아교 6중량부, 구아검 8중량부, 크산탄 6중량부, 글리세린 25중량부로 구성하고, 염화염 15중량부로 이루어지는 염화염 용액을 구성하여 캡슐의 내압 강도가 0.85Pa를 이루도록 제조하였다. The composition forming the outer shell of the capsule is carrageenan 75 parts by weight, gelatin 35 parts by weight, hydroxypropylcellulose 35 parts by weight, sodium alginate 20 parts by weight, konjac glue 6 parts by weight, guar gum 8 parts by weight, xanthan 6 parts by weight, glycerin A chlorinated salt solution composed of 25 parts by weight and 15 parts by weight of chlorinated salt was prepared so that the internal pressure strength of the capsule was 0.85 Pa.
이때, 캡슐의 내부에 수용되는 내포액의 조성물은 피톤치드 25중량부, 에센스 62중량부, 음이온 용액 5중량부를 이루도록 구성하였다.At this time, the composition of the encapsulated liquid contained in the capsule was configured to form 25 parts by weight of phytoncide, 62 parts by weight of the essence, and 5 parts by weight of the anion solution.
실시 예4.Example 4.
캡슐의 외피를 이루는 조성물을 카라기난 82중량부, 젤라틴 38중량부, 하이드록시프로필셀룰로스 18중량부, 알긴산 나트륨 20중량부, 곤약 아교 7중량부, 구아검 2중량부, 크산탄 6중량부, 글리세린 10중량부, 펙틴 12중량부, 말토덱스트린 18중량부, 키토산 4중량부로 구성하고, 염화염 30중량부로 이루어지는 염화염 용액을 구성하여 캡슐의 내압 강도가 0.75Pa를 이루도록 제조하였다. The composition forming the outer shell of the capsule is 82 parts by weight of carrageenan, 38 parts by weight of gelatin, 18 parts by weight of hydroxypropylcellulose, 20 parts by weight of sodium alginate, 7 parts by weight of konjac glue, 2 parts by weight of guar gum, 6 parts by weight of xanthan, glycerin A chloride solution consisting of 10 parts by weight of pectin, 12 parts by weight of pectin, 18 parts by weight of maltodextrin, and 4 parts by weight of chitosan, and 30 parts by weight of chloride was prepared so that the internal pressure strength of the capsule was 0.75 Pa.
이때, 캡슐의 내부에 수용되는 내포액의 조성물은 피톤치드 35중량부, 에센스 70중량부, 음이온 용액 7중량부를 이루도록 구성하였다.At this time, the composition of the encapsulated liquid contained in the capsule was configured to form 35 parts by weight of phytoncide, 70 parts by weight of essence, and 7 parts by weight of an anion solution.
실시 예5.Example 5.
캡슐의 외피를 이루는 조성물을 카라기난 35중량부, 젤라틴 38중량부, 하이드록시프로필셀룰로스 15중량부, 알긴산 나트륨 20중량부, 곤약 아교 1중량부, 구아검 2중량부, 크산탄 2중량부, 글리세린 20중량부, 펙틴 15중량부, 말토덱스트린 12중량부, 키토산 5중량부로 구성하고, 염화염 15중량부로 이루어지는 염화염 용액을 구성하여 캡슐의 내압 강도가 0.35Pa를 이루도록 제조하였다. The composition forming the outer shell of the capsule is carrageenan 35 parts by weight, gelatin 38 parts by weight, hydroxypropylcellulose 15 parts by weight, sodium alginate 20 parts by weight, konjac glue 1 part by weight, guar gum 2 parts by weight, xanthan 2 parts by weight, glycerin A chloride solution consisting of 20 parts by weight of pectin, 15 parts by weight of pectin, 12 parts by weight of maltodextrin, and 5 parts by weight of chitosan, and 15 parts by weight of chloride salt was prepared so that the internal pressure strength of the capsule was 0.35 Pa.
이때, 캡슐의 내부에 수용되는 내포액의 조성물은 피톤치드 35중량부, 에센스 70중량부, 음이온 용액 7중량부를 이루도록 구성하였다.At this time, the composition of the encapsulated liquid contained in the capsule was configured to form 35 parts by weight of phytoncide, 70 parts by weight of essence, and 7 parts by weight of an anion solution.
실시 예6.Example 6.
콩비지 45중량부, 전분 25중량부, 옥수수분 12중량부, 탄산칼슘 5중량부, 구아검 8중량부, 구연산 4중량부의 모래 조성물을 이용하여 애완동물 화장실용 모래를 제조하였다.Sand for pet toilets was prepared using a sand composition of 45 parts by weight of soybean curd, 25 parts by weight of starch, 12 parts by weight of corn flour, 5 parts by weight of calcium carbonate, 8 parts by weight of guar gum, and 4 parts by weight of citric acid.
실시 예7.Example 7.
콩비지 40중량부, 전분30중량부, 옥수수분10중량부, 탄산칼슘6중량부, 구아검4중량부, 구연산5중량부의 비율로 애완동물 화장실용 모래를 제조하였으며, 시?? 예 1~5를 통해 제조된 캡슐을 실시 예7에 의해 제조된 애완동물 화장실용 모래와 각각 혼합하되, 캡슐과 애완동물 화장실용 모래의 중량 비율은 8:2800의 비율로 혼합하였다.Soybean Curd 40 parts by weight, starch 30 parts by weight, corn flour 10 parts by weight, calcium carbonate 6 parts by weight, guar gum 4 parts by weight, citric acid 5 parts by weight was prepared for pet toilet sand. The capsules prepared through Examples 1 to 5 were mixed with the pet toilet sand prepared according to Example 7, respectively, but the weight ratio of the capsule and the pet toilet sand was mixed at a ratio of 8:2800.
또한, 실시 예7에서는 실시 예 1~5를 통해 제조된 캡슐의 배뇨의 냄새 소멸시간 및 운송 파열율에 대한 실험을 실시하였다.In addition, in Example 7, an experiment was conducted on the odor disappearance time and transport rupture rate of urination of the capsules prepared through Examples 1 to 5.
실험 조건으로, 실시 예 1~5를 통해 제조된 캡슐이 혼합된 실시 예7의 화장실용 모래 1kg을 마련하고, 마련된 화장실용 모래에 주사기를 이용하여 고양이의 배뇨 25ml를 주사하여 기록하는 방식으로 실시하였으며, 하기의 표 1에 기재된 T1은, 배뇨의 투입 후 캡슐이 파열되는 시간을 의미하고, T2는 배뇨의 투입, 캡슐이 파열되면서 배뇨의 냄새가 소멸되는 시간을 의미한다.As an experimental condition, 1 kg of toilet sand of Example 7 in which the capsules prepared through Examples 1 to 5 were mixed was prepared, and 25 ml of cat urination was injected into the prepared toilet sand using a syringe and recorded. In Table 1 below, T1 refers to the time when the capsule is ruptured after the injection of urination, and T2 refers to the time at which the odor of urination disappears as the capsule is ruptured and the injection of urination is introduced.
또한, 화장실용 모래 2.8kg에 실시 예7에 의해 제조된 캡슐을 투입, 그 후 포장에 넣고, 1m 높에이서 5번 내던지는 실험을 통해 캡슐의 파열율에 대한 실험을 실시하였으며, 운송 중 파열율이 20%를 넘을 경우, 요구에 부합되지 않는 캡슐로 판단하였다.In addition, the capsule prepared according to Example 7 was put into 2.8 kg of toilet sand, and then put into the packaging, and an experiment was conducted on the rupture rate of the capsule through an experiment of throwing it 5 times at a height of 1 m. If this exceeded 20%, it was judged as a capsule that did not meet the requirements.
표 1에서 볼 수 있듯이, 캡슐의 조성물 중, 곤약 아교를 중량비를 증가시키면, 캡슐의 파열속도를 증가함을 확인할 수 있었다. 그러나 파열되는 시간이 단축할수록 운송과정 중 요동에도 파열이 일어는 문제점이 발생하였고, 실험을 통해 내압강도를 0.4-1Pa를 형성하는 것이 요구에 부합됨을 확인할 수 있었다.As can be seen from Table 1, when the weight ratio of the konjac glue was increased in the composition of the capsule, it was confirmed that the bursting rate of the capsule was increased. However, as the time to rupture was shortened, the problem that rupture occurred even during the vibration during the transportation process occurred, and it was confirmed through an experiment that forming a pressure resistance strength of 0.4-1Pa satisfies the demand.
이에, 실시 예 7의 중량비율로 제조된 화장실용 모래와 통상적으로 이용되는 2종류의 고양이 모래(대비 예1, 2; 질량의 80% 이상의 벤토나이트로 이루어지는 것)에 실시 예4를 통해 제조된 캡슐을 혼합하되, 전술한 비율과 동일한 비율인 8:2800의 중량비율로 혼합하고, 실험 조건 역시 동일한 조건으로 캡슐의 배뇨의 냄새 소멸시간 및 운송 파열율에 대한 실험을 실시하였다.Accordingly, the capsule prepared in Example 4 in the toilet sand prepared in the weight ratio of Example 7 and the two types of cat sand (contrast examples 1 and 2; consisting of 80% or more of bentonite by mass) that are commonly used. However, the mixture was mixed at a weight ratio of 8:2800, which is the same ratio as the above-described ratio, and experiments were conducted on the odor disappearance time and transport rupture rate of urination of the capsule under the same conditions.
전술한 표 2에 나타난 바와 같이, 벤토나이트가 전체 질량의 80%를 이루는 대비 1, 2의 고양이 모래에 비하여 본 발명의 화장실용 모래가 고양이의 배뇨에 대한 냄새 제거 및 화장실용 모래의 융합이 월등함을 알 수 있었으며, 특히 운송시에도 파열이 상대적으로 적게 발생함을 확인할 수 있었다.As shown in Table 2 above, the toilet sand of the present invention is superior to the cat sand of 1 and 2 compared to the cat sand of 1 and 2 compared with bentonite making up 80% of the total mass. It could be seen that, especially during transportation, it was confirmed that relatively little rupture occurred.
실시 예8.Example 8.
실시 예8은 하이드록시프로필 전분, 인산에스테르나트륨 전분, 옥테닐썩시네이트 전분, 카복시메틸 전분, 전분화녹말로부터 선택된 1종, 또는 적어도 2종류 이상 혼합된 혼합 변성 전분이 더 혼합된 화장실용 모래를 제조하고, 제조된 화장실용 모래와 전술한 실시 예2에 의해 제조된 캡슐을 혼합하여 캡슐의 배뇨의 냄새 소멸시간 및 운송 파열율에 대한 실험을 실시하였다.Example 8 is hydroxypropyl starch, sodium phosphate ester starch, octenyl oxynate starch, carboxymethyl starch, one type selected from starched starch, or at least two types of mixed modified starch further mixed with toilet sand And, by mixing the prepared toilet sand and the capsule prepared according to Example 2 described above, an experiment was performed on the odor disappearance time and transport rupture rate of urination of the capsule.
이때, 변성 전분이 더 혼합된 화장실용 모래는 콩비지 35중량부, 전분28중량부, 옥수수분13중량부, 탄산칼슘4중량부, 구아검9중량부, 구연산4중량부, 변성 전분 6중량부로 이루어진다.At this time, the toilet sand in which the modified starch is further mixed is 35 parts by weight of bean curd, 28 parts by weight of starch, 13 parts by weight of corn flour, 4 parts by weight of calcium carbonate, 9 parts by weight of guar gum, 4 parts by weight of citric acid, and 6 parts by weight of modified starch. Done.
또한, 실시 예2의 캡슐과 변성 전분이 더 혼합된 화장실용 모래의 혼합 중량비는 8:2800로 이루어지며, 실험 조건 및 방법 역시 전술한 조건 및 방법과 동일한 조건으로 캡슐의 배뇨의 냄새 소멸시간 및 운송 파열율에 대한 실험을 실시하였다.In addition, the mixing weight ratio of the capsule of Example 2 and the toilet sand in which the modified starch was further mixed was 8:2800, and the experimental conditions and methods were also the same conditions as the above-described conditions and methods, and the odor disappearance time of urination of the capsule and An experiment was conducted on the transport burst rate.
실험 결과, 표 3에 나타난 바와 같이, 변성전분을 더 혼합한 화장실용 모래가 캡슐 외피의 수분 접촉 시 파열 속도를 추진하는 것을 확인할 수 있었으며, 이는 변성전분이 캡슐 외피의 교질을 분산시켜, 배뇨와의 신속한 결합이 이루어지도록 유도하여 배뇨의 냄새를 제거하는 것을 확인할 수 있었다. As a result of the experiment, as shown in Table 3, it was confirmed that the toilet sand further mixed with the modified starch promoted the rupture rate when the capsule shell was in contact with moisture, and this was confirmed that the modified starch dispersed the colloid of the capsule shell, resulting in urination and urination. It was confirmed that the odor of urination was removed by inducing the rapid combination of
이는, 변성전분이 배뇨와 직접 접촉한 후 알칼리성 혹은 산성 체계를 형성시키면서 캡슐 외피를 분해하여 파열율을 더욱 높이는 것을 의미하며, 운송 중 캡슐이 파열되는 운송 중 파열율에 대한 이로운 영향력을 주는 것을 확인할 수 있었다.This means that the modified starch forms an alkaline or acidic system after direct contact with urination and decomposes the capsule shell to further increase the rupture rate.It was confirmed that the capsule rupture during transportation has a beneficial effect on the rupture rate during transportation. Could.
이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The above description is merely illustrative of the technical idea of the present invention, and those of ordinary skill in the art to which the present invention pertains will be able to make various modifications and variations without departing from the essential characteristics of the present invention. Accordingly, the embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain the technical idea, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed by the following claims, and all technical ideas within the scope equivalent thereto should be construed as being included in the scope of the present invention.
Claims (9)
피톤치드 25 중량부~35중량부, 식물성 에센스 오일로 이루어진 군으로부터 선택되는 적어도 1종의 향료 60중량부~70중량부, 음이온 용액 3중량부~7중량부로 구성되는 내포액;으로 구성되되,
상기 캡슐 외피는, 카라기난과 하이드록시프로필메틸셀룰로스의 혼합시 배합 질량비 기준 7:1 내지 3:1로 배합하고,
열화칼슘, 또는 염화 나트륨으로부터 선택되는 적어도 1종의 염화염 1 중량부 ~ 45중량부와 물이 1:5의 질량비로 혼합된 혼합물과 교반된 후, 50℃의 온도로 5분~10분간 가열하여 겔의 형태로 전환되도록 구성되고,
온도 24℃, 습도 30%~45%의 조건으로 건조시켜 내압 강도가 0.4 ~ 1.0Pa로 형성되는 것을 특징으로 하는 애완동물용 모래 냄새 제거제.
Carrageenan 30 to 82 parts by weight, gelatin 5 to 42 parts by weight, hydroxypropyl cellulose 3 to 40 parts by weight, sodium alginate 3 to 45 parts by weight, konjac glue 1 to 10 parts by weight, A capsule shell consisting of 1 part by weight to 10 parts by weight of guar gum, 1 part by weight to 8 parts by weight of xanthan, and 1 part by weight to 30 parts by weight of glycerin, comprising a molecular weight of 200,000 to 300,000; And
Phytoncide 25 parts by weight to 35 parts by weight, 60 parts by weight to 70 parts by weight of at least one flavor selected from the group consisting of vegetable essence oil, an inclusion solution consisting of 3 parts by weight to 7 parts by weight of anion solution; consisting of,
The capsule shell is blended at a mass ratio of 7:1 to 3:1 when carrageenan and hydroxypropylmethylcellulose are mixed,
A mixture of 1 part by weight to 45 parts by weight of at least one chloride salt selected from deteriorated calcium or sodium chloride and water in a mass ratio of 1:5 is stirred and then heated at a temperature of 50℃ for 5 to 10 minutes It is configured to be converted into a gel form,
A sand odor remover for pets, characterized in that it is dried under the conditions of a temperature of 24°C and a humidity of 30% to 45% to have a pressure resistance of 0.4 to 1.0Pa.
상기 캡슐 외피는 펙틴 1 중량부~15 중량부, 말토덱스트린 1 중량부~20 중량부, 키토산 1 중량부~5중량부를 더 혼합되는 것을 특징으로 하는 애완동물용 모래 냄새 제거제.
The method of claim 1,
The capsule shell is a sand odor remover for pets, characterized in that 1 to 15 parts by weight of pectin, 1 to 20 parts by weight of maltodextrin, and 1 to 5 parts by weight of chitosan are further mixed.
(b) 상기 모래 조성물과 변성 전분을 1시간~3시간 동안 교반하는 단계;
(c) 교반이 완료된 모래용 혼합물을 프레스 성형 방법을 통해 성형하고, 성형이 이루어진 성형물을 건조 및 절단하여 화장실용 모래를 제조하는 단계;
(d) 내압 강도가 0.4 ~ 1.0Pa로 형성되며, 피톤치드, 에센스 및 음이온 용액이 일정 중량부로 혼합된 내포액이 수용되고, 애완동물의 배뇨와의 접촉시 15~20초 이내로 파열되도록 구성되는 겔 형태의 캡슐을 상기 화장실용 모래에 첨가하되, 상기 캡슐 7~15 : 화장실용 모래 2800의 중량비로 첨가하는 단계;를 포함하고,
상기 겔 형태의 캡슐은,
카라기난 30중량부~82중량부, 젤라틴 5중량부~42중량부, 하이드록시프로필셀룰로스 3중량부~40중량부, 알긴산 나트륨 3중량부~45중량부, 곤약 아교 1중량부~10중량부, 분자량이 200,000~300,000으로 이루어지는 구아검 1중량부~10중량부, 크산탄 1중량부~8중량부 및 글리세린 1중량부~30중량부로 구성되는 캡슐 외피; 및
피톤치드 25 중량부~35중량부, 식물성 에센스 오일로 이루어진 군으로부터 선택되는 적어도 1종의 향료 60중량부~70중량부, 음이온 용액 3중량부~7중량부로 구성되는 내포액;으로 구성되되,
상기 캡슐 외피는, 카라기난과 하이드록시프로필메틸셀룰로스의 혼합시 배합 질량비 기준 7:1 내지 3:1로 배합하고,
열화칼슘, 또는 염화 나트륨으로부터 선택되는 적어도 1종의 염화염 1 중량부 ~ 45중량부와 물이 1:5의 질량비로 혼합된 혼합물과 교반된 후, 50℃의 온도로 5분~10분간 가열하여 겔의 형태로 전환되도록 구성되고,
온도 24℃, 습도 30%~45%의 조건으로 건조시켜 내압 강도가 0.4 ~ 1.0Pa로 형성되는 것
를 더 포함하는 것을 특징으로 하는 애완동물 화장실용 모래 제조방법.
(a) 30 parts by weight to 50 parts by weight of soybean curd with a particle of 10 to 300 mesh, 20 parts by weight to 35 parts by weight of starch, 10 parts by weight to 15 parts by weight of corn flour, 3 parts by weight to 6 parts by weight of calcium carbonate, A sand composition consisting of 2 parts by weight to 10 parts by weight of guar gum and 1 part by weight to 5 parts by weight of citric acid, and further mixed with the sand composition, hydroxypropyl starch, sodium phosphate ester starch, octenyl succinate starch, carboxymethyl starch or Preparing 5 parts by weight to 10 parts by weight of modified starch consisting of one type selected from starched starch;
(b) stirring the sand composition and the modified starch for 1 to 3 hours;
(c) molding the mixture for sand after the stirring is completed through a press molding method, and drying and cutting the molded product to produce toilet sand;
(d) A gel that has an internal pressure strength of 0.4 to 1.0 Pa, contains an inclusion solution in which phytoncide, essence, and anion solution are mixed in a certain weight part, and is configured to rupture within 15 to 20 seconds when contacting the urine of a pet Including, but adding a capsule of the form to the toilet sand, the capsules 7-15: adding in a weight ratio of 2800 toilet sand; Including,
The gel-type capsule,
Carrageenan 30 to 82 parts by weight, gelatin 5 to 42 parts by weight, hydroxypropyl cellulose 3 to 40 parts by weight, sodium alginate 3 to 45 parts by weight, konjac glue 1 to 10 parts by weight, A capsule shell consisting of 1 part by weight to 10 parts by weight of guar gum, 1 part by weight to 8 parts by weight of xanthan, and 1 part by weight to 30 parts by weight of glycerin, comprising a molecular weight of 200,000 to 300,000; And
Phytoncide 25 parts by weight to 35 parts by weight, 60 parts by weight to 70 parts by weight of at least one flavor selected from the group consisting of vegetable essence oil, an inclusion solution consisting of 3 parts by weight to 7 parts by weight of anion solution; consisting of,
The capsule shell is blended at a mass ratio of 7:1 to 3:1 when carrageenan and hydroxypropylmethylcellulose are mixed,
A mixture of 1 part by weight to 45 parts by weight of at least one chloride salt selected from deteriorated calcium or sodium chloride and water in a mass ratio of 1:5 is stirred and then heated at a temperature of 50℃ for 5 to 10 minutes It is configured to be converted into a gel form,
Drying under the conditions of temperature 24℃ and humidity 30%~45%, and the pressure resistance strength is 0.4~1.0Pa.
Sand manufacturing method for pet toilet, characterized in that it further comprises.