KR102176530B1 - Double-sided tape for attaching component and method of manufacturing the same - Google Patents

Double-sided tape for attaching component and method of manufacturing the same Download PDF

Info

Publication number
KR102176530B1
KR102176530B1 KR1020190030458A KR20190030458A KR102176530B1 KR 102176530 B1 KR102176530 B1 KR 102176530B1 KR 1020190030458 A KR1020190030458 A KR 1020190030458A KR 20190030458 A KR20190030458 A KR 20190030458A KR 102176530 B1 KR102176530 B1 KR 102176530B1
Authority
KR
South Korea
Prior art keywords
polyurethane
weight
parts
double
sided tape
Prior art date
Application number
KR1020190030458A
Other languages
Korean (ko)
Other versions
KR20200110932A (en
Inventor
김범진
Original Assignee
주식회사 가야
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 가야 filed Critical 주식회사 가야
Priority to KR1020190030458A priority Critical patent/KR102176530B1/en
Publication of KR20200110932A publication Critical patent/KR20200110932A/en
Application granted granted Critical
Publication of KR102176530B1 publication Critical patent/KR102176530B1/en

Abstract

본 발명에서는 폴리우레탄 기재층, 상기 폴리우레탄 기재층의 일면에 형성된 제 1 점착층 및 상기 폴리우레탄 기재층의 타면에 형성된 제 2 점착층을 포함하되, 상기 폴리우레탄 기재층은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물로 형성되며, 상기 제 1 점착층 및 상기 제 2 점착층은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는 점착 조성물로 형성됨에 따라, 두께가 얇으면서도 접착성, 내구성이 우수한 양면테이프를 제공한다. 또한, 상기와 같은 양면테이프를 보다 간단하게 제조할 수 있는 양면테이프의 제조방법을 제공한다.In the present invention, a polyurethane base layer, a first adhesive layer formed on one surface of the polyurethane base layer, and a second adhesive layer formed on the other surface of the polyurethane base layer, wherein the polyurethane base layer is polyurethane, methylethyl It is formed of a polyurethane composition containing ketone and dimethylformamide, and the first adhesive layer and the second adhesive layer are formed of an adhesive composition containing a vinyl chloride-vinyl acetate copolymer, ethyl acetate, and an organic solvent. , Provides a double-sided tape with excellent adhesion and durability while being thin. In addition, it provides a method of manufacturing a double-sided tape that can more simply manufacture the double-sided tape as described above.

Description

양면테이프 및 이의 제조방법{DOUBLE-SIDED TAPE FOR ATTACHING COMPONENT AND METHOD OF MANUFACTURING THE SAME}Double-sided tape and its manufacturing method {DOUBLE-SIDED TAPE FOR ATTACHING COMPONENT AND METHOD OF MANUFACTURING THE SAME}

본 발명은 양면테이프 및 이의 제조방법에 관한 것이다. 바람직하게는, 전가기기의 부품 부착용 양면테이프 및 이의 제조방법에 관한 것이다.The present invention relates to a double-sided tape and a method of manufacturing the same. Preferably, it relates to a double-sided tape for attaching parts of an electric appliance and a manufacturing method thereof.

양면테이프는 필름 또는 발포폼 형태의 기재 양면에 점착층이 형성된 것으로, 두 개의 고체면이 접착될 수 있도록 한다. 특히, 양면테이프는 액정 패널, 플라즈마 디스플레이 패널, 유기 EL 패널 등의 디스플레이 패널, 내부 칩 등 전자기기를 구성하는 부품 간의 접착을 위해 활용되고 있다.Double-sided tape is a film or foam-type substrate with adhesive layers formed on both sides of the substrate, so that the two solid surfaces can be bonded. In particular, double-sided tapes are used for bonding between components constituting electronic devices such as liquid crystal panels, plasma display panels, display panels such as organic EL panels, and internal chips.

일례로, 대한민국 등록특허 제10-1914376호에서는 순차적으로 적층된 40 ~ 90 마이크로미터 두께의 제 1 점착층, 25 ~ 150 마이크로미터 두께의 기재층, 120 ~ 3000 마이크로미터 두께의 발포폼층, 10 ~ 50 마이크로미터 두께의 스킨층 및 40 ~ 90 마이크로미터 두께의 제 2 점착층을 포함하는 양면 점착 테이프에 대해 개시하고 있다. For example, in Korean Patent Registration No. 10-1914376, a first adhesive layer having a thickness of 40 to 90 micrometers, a base layer having a thickness of 25 to 150 micrometers, a foam layer having a thickness of 120 to 3000 micrometers, 10 to which are sequentially stacked. Disclosed is a double-sided adhesive tape comprising a skin layer having a thickness of 50 micrometers and a second adhesive layer having a thickness of 40 to 90 micrometers.

한편, 상기 등록특허에 개시된 바와 같이, 종래의 양면테이프는 접착성을 향상시키면서도 양면테이프의 내구성을 향상시키기 위해, 점착층과 기재층 또는 발포폼층의 두께를 40 마이크로미터 이상으로 형성하였다.On the other hand, as disclosed in the registered patent, in order to improve the durability of the double-sided tape while improving the adhesion of the conventional double-sided tape, the thickness of the adhesive layer and the base layer or foam layer was formed to be 40 micrometers or more.

그러나, 상기된 바와 같이, 양면테이프의 두께가 두꺼워질 경우에는 두께 또는 너비가 마이크로 수준인 소형 부품에는 적용이 어려운 문제가 있었다. 반면, 양면테이프의 두께를 현저히 줄일 경우에는 접착 성능이 현저히 저하되고 내구성이 저하되어 양면테이프로서의 활용도가 낮아지는 문제가 있었다.However, as described above, when the thickness of the double-sided tape becomes thick, there is a problem that it is difficult to apply to small parts having a thickness or width of a micro level. On the other hand, when the thickness of the double-sided tape is remarkably reduced, there is a problem that the adhesion performance is significantly reduced and the durability is reduced, and the utilization as a double-sided tape is reduced.

또한, 상기된 바와 같은 종래의 양면테이프는 제 1 이형지에 점착 조성물을 도포한 뒤 상기 점착 조성물 상에 필름 또는 발포폼 형태의 기재의 일면을 부착하는 단계, 및 제 2 이형지에 점착 조성물을 도포한 뒤 이를 상기 기재의 타면에 부착하는 단계에 따라 통상 제조된다. 그러나, 이와 같은 경우 양면테이프를 제조하는 공정이 복잡할 뿐 아니라 필름 또는 발포폼 형태의 기재와 점착층 간의 접착성이 낮아 두 증 간의 분리가 발생되는 문제가 있었다.In addition, in the conventional double-sided tape as described above, the step of attaching one side of a substrate in the form of a film or foam on the adhesive composition after applying the adhesive composition to the first release paper, and applying the adhesive composition to the second release paper It is usually manufactured according to the step of attaching it to the other side of the substrate. However, in this case, not only the process of manufacturing the double-sided tape is complicated, but also the adhesiveness between the substrate in the form of a film or foam and the adhesive layer is low, causing separation between the two layers.

이에 따라, 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수할 뿐 아니라 간단한 공정으로 제조될 수 있는, 양면테이프에 대한 개발이 요구되고 있다.Accordingly, there is a need for development of a double-sided tape, which is thin and has excellent properties such as adhesion and durability, and can be manufactured by a simple process.

대한민국 등록특허 제10-1914376호Korean Patent Registration No. 10-1914376

본 발명의 목적은 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수한, 양면테이프를 제공하는 데에 있다.An object of the present invention is to provide a double-sided tape having excellent properties such as adhesion and durability while having a thin thickness.

본 발명의 또 다른 목적은 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수한 양면테이프를 간단한 공정으로 단 시간 내에 제조할 수 있는, 양면테이프의 제조방법을 제공하는 데에 있다.Another object of the present invention is to provide a method of manufacturing a double-sided tape, which can manufacture a double-sided tape having a thin thickness and excellent properties such as adhesion and durability in a short time through a simple process.

본 발명의 목적은 상기된 바와 같은 기술적 과제로 한정되지 않으며, 이하의 설명으로부터 또 다른 기술적 과제가 도출될 수 있다. The object of the present invention is not limited to the technical problem as described above, and another technical problem may be derived from the following description.

상기 목적을 달성하기 위하여, 본 발명은 폴리우레탄 기재층; 상기 폴리우레탄 기재층의 일면에 형성된 제 1 점착층; 및 상기 폴리우레탄 기재층의 타면에 형성된 제 2 점착층을 포함하되, 상기 폴리우레탄 기재층은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물로 형성되며, 상기 제 1 점착층 및 상기 제 2 점착층은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는 점착 조성물로 형성되는, 양면테이프를 제공한다.In order to achieve the above object, the present invention is a polyurethane base layer; A first adhesive layer formed on one surface of the polyurethane substrate layer; And a second adhesive layer formed on the other surface of the polyurethane substrate layer, wherein the polyurethane substrate layer is formed of a polyurethane composition comprising polyurethane, methyl ethyl ketone and dimethyl formamide, and the first adhesive layer And the second adhesive layer provides a double-sided tape formed of an adhesive composition comprising a vinyl chloride-vinyl acetate copolymer, ethyl acetate and an organic solvent.

상기 폴리우레탄 조성물은 상기 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤 1 ~ 25 중량부 및 상기 다이메틸폼아마이드 150 ~ 250 중량부를 포함할 수 있다. The polyurethane composition may include 1 to 25 parts by weight of the methyl ethyl ketone and 150 to 250 parts by weight of the dimethyl formamide based on 100 parts by weight of the polyurethane .

상기 폴리우레탄 조성물은 점도가 4,000 ~ 5,000 cps 일 수 있다.The polyurethane composition may have a viscosity of 4,000 to 5,000 cps.

상기 점착 조성물은 상기 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 상기 에틸 아세테이트 30 ~ 65 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함할 수 있다.The adhesive composition may include 30 to 65 parts by weight of ethyl acetate and 40 to 100 parts by weight of the organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer.

상기 점착 조성물은 상기 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 폴리아크릴아마이드 1 ~ 10 중량부를 더 포함할 수 있다.The adhesive composition may further include 1 to 10 parts by weight of polyacrylamide based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer.

상기 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 200,000 일 수 있다.The polyacrylamide may have a number average molecular weight of 10,000 to 200,000.

상기 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드를 포함할 수 있다.The polyacrylamide may include polyacrylamide having a number average molecular weight of 10,000 to 50,000 and polyacrylamide having a number average molecular weight of 100,000 to 150,000.

상기 점착 조성물은 점도가 3,000 ~ 4,000 cps 일 수 있다.The adhesive composition may have a viscosity of 3,000 to 4,000 cps.

상기 유기용매는 메탄올, 에탄올, 톨루엔, 메틸에틸케톤 및 다이메틸폼아마이드로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The organic solvent may include at least one selected from the group consisting of methanol, ethanol, toluene, methylethylketone, and dimethylformamide.

상기 목적을 달성하기 위해, 본 발명은 폴리우레탄 기재층, 상기 폴리우레탄 기재층의 일면에 형성된 제 1 점착층 및 상기 폴리우레탄 기재층의 타면에 형성된 제 2 점착층을 포함하는 양면테이프의 제조방법에 있어서, 상기 폴리우레탄 기재층 형성용 폴리우레탄 조성물과 상기 제 1 점착층 및 상기 제 2 점착층 형성용 점착 조성물을 준비하는 제 1 단계; 및 이형지 상에 상기 폴리우레탄 조성물과 상기 점착 조성물을 도포하고 경화하여 제 1 점착층, 폴리우레탄 기재층 및 제 2 점착층의 순차로 적층된 양면테이프를 형성하는 제 2 단계;를 포함하고, 상기 폴리우레탄 조성물은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하며, 상기 점착 조성물은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는, 양면테이프의 제조방법을 제공한다.In order to achieve the above object, the present invention is a method for producing a double-sided tape comprising a polyurethane base layer, a first adhesive layer formed on one surface of the polyurethane base layer, and a second adhesive layer formed on the other surface of the polyurethane base layer In the above, the first step of preparing the polyurethane composition for forming the polyurethane base layer and the adhesive composition for forming the first adhesive layer and the second adhesive layer; And a second step of applying and curing the polyurethane composition and the adhesive composition on a release paper to form a double-sided tape sequentially stacked with a first adhesive layer, a polyurethane base layer, and a second adhesive layer. The polyurethane composition includes polyurethane, methyl ethyl ketone, and dimethyl formamide, and the adhesive composition includes a vinyl chloride-vinyl acetate copolymer, ethyl acetate and an organic solvent, and provides a method for producing a double-sided tape.

본 발명의 양면테이프는 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수할 수 있다. 특히, 본 발명의 양면테이프는 폴리우레탄 기재층과 폴리우레탄 기재층의 양면의 점착층을 포함하여, 총 10 마이크로미터 이내의 두께를 가질 수 있어, 소형 부품의 적용에 유리할 수 있다.The double-sided tape of the present invention may have excellent properties such as adhesion and durability while having a thin thickness. In particular, the double-sided tape of the present invention, including the adhesive layer on both sides of the polyurethane base layer and the polyurethane base layer, may have a thickness within a total of 10 micrometers, and thus may be advantageous for application of small parts.

본 발명의 제조방법에 따르면, 종래와 달리 폴리우레탄 조성물과 점착 조성물로 제 1 점착층, 폴리우레탄 기재층 및 제 2 점착층을 동시에 형성함으로써, 간단한 공정으로도 두께가 얇고 접착성, 내구성 등의 특성이 우수한 양면테이프를 제조할 수 있다.According to the manufacturing method of the present invention, unlike the prior art, by simultaneously forming a first adhesive layer, a polyurethane base layer, and a second adhesive layer with a polyurethane composition and an adhesive composition, the thickness is thin and adhesiveness, durability, etc. Double-sided tapes with excellent properties can be manufactured.

도 1은 본 발명의 일 실시예에 따른 양면테이프의 단면도이다.1 is a cross-sectional view of a double-sided tape according to an embodiment of the present invention.

아래에서는 첨부한 도면을 참조하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예를 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those of ordinary skill in the art can easily implement the present invention. However, the present invention may be implemented in various different forms and is not limited to the embodiments described herein. In the drawings, parts not related to the description are omitted in order to clearly describe the present invention.

본 발명의 명세서 및 청구범위에 사용된 용어 또는 단어는 통상적이거나 사전적인 의미로 한정 해석되지 아니하며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms or words used in the specification and claims of the present invention are not limitedly interpreted in a conventional or dictionary meaning, and the inventor can appropriately define the concept of the term in order to describe his own invention in the best way. Based on the principle, it should be interpreted as a meaning and concept consistent with the technical idea of the present invention.

본 발명의 명세서 전체에 있어서, 어떤 부분이 어떤 구성 요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. In the entire specification of the present invention, when a certain part "includes" a certain component, it means that other components may be further included rather than excluding other components unless otherwise stated. .

본 발명의 명세서 전체에 있어서, "A 및/또는 B"는, A 또는 B, 또는 A 및 B를 의미한다.In the entire specification of the present invention, "A and/or B" means A or B, or A and B.

이하에서 본 발명을 구체적으로 설명하였으나, 본 발명이 이에 제한되는 것은 아니다.Hereinafter, the present invention has been described in detail, but the present invention is not limited thereto.

본 발명에서는 양면테이프를 제공한다.In the present invention, a double-sided tape is provided.

본 발명의 일 실시예에서는 폴리우레탄 기재층(10), 상기 폴리우레탄 기재층(10)의 일면에 형성된 제 1 점착층(20), 및 상기 폴리우레탄 기재층(10)의 타면에 형성된 제 2 점착층(30)을 포함하되, 상기 폴리우레탄 기재층(10)은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물로 형성되며, 상기 제 1 점착층(20) 및 상기 제 2 점착층(30)은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는 점착 조성물로 형성됨에 따라, 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수한 양면테이프를 제공한다.In an embodiment of the present invention, a polyurethane base layer 10, a first adhesive layer 20 formed on one surface of the polyurethane base layer 10, and a second adhesive layer formed on the other surface of the polyurethane base layer 10 Including an adhesive layer 30, wherein the polyurethane base layer 10 is formed of a polyurethane composition containing polyurethane, methyl ethyl ketone, and dimethylformamide, the first adhesive layer 20 and the agent 2 As the adhesive layer 30 is formed of an adhesive composition including a vinyl chloride-vinyl acetate copolymer, ethyl acetate, and an organic solvent, a double-sided tape having excellent properties such as adhesion and durability while having a thin thickness is provided.

바람직하게, 본 실시예의 양면테이프는 종래와 달리 상기 폴리우레탄 조성물과 상기 점착 조성물을 이용하여 제조되되, 복수 개의 슬롯다이노즐을 통해 점착 조성물, 폴리우레탄 조성물 및 점착 조성물의 순서로 적층되도록 분사되어 3 개의 층을 이루도록 한 후 이를 건조하여, 형성된 것일 수 있다. 이에 따라, 본 실시예의 양면테이프는 종래 보다 간단한 공정으로 얇은 두께를 가지면서도 접착성, 내구성 등의 특성이 우수할 수 있다. Preferably, the double-sided tape of this embodiment is manufactured using the polyurethane composition and the adhesive composition unlike the conventional one, but is sprayed so that the adhesive composition, the polyurethane composition, and the adhesive composition are stacked in order through a plurality of slot die nozzles. It may be formed by drying them after forming a layer of dogs. Accordingly, the double-sided tape of the present embodiment may have a thinner thickness through a simpler process than the conventional one, but may have excellent properties such as adhesion and durability.

도 1은 본 실시예에 따른 양면테이프의 단면도로서, 도 1에 도시된 바와 같이, 본 실시예의 양면테이프는 폴리우레탄 기재층(10)과 상기 폴리우레탄 기재층(10)의 일면과 타면에 각각 점착층이 형성된 형태로 형성되며, 상기 점착층은 이형지(40)에 의해 외부와의 접촉이 차단된 형태로 형성될 수 있다.1 is a cross-sectional view of the double-sided tape according to this embodiment, as shown in FIG. 1, the double-sided tape of this embodiment is on one side and the other side of the polyurethane base layer 10 and the polyurethane base layer 10, respectively. It is formed in a form in which an adhesive layer is formed, and the adhesive layer may be formed in a form in which contact with the outside is blocked by the release paper 40.

폴리우레탄 기재층(10)은 제 1 점착층(20) 및 제 2 점착층(30)이 지지되는 기본 기재로서, 본 실시예의 폴리우레탄 기재층(10)은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물로 형성된다. 이때, 본 실시예의 폴리우레탄 기재층(10)이 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물로 형성된다는 것은, 도포 내지 분사된 폴리우레탄 조성물이 건조 또는 경화되면서 폴리우레탄 기재층(10)을 형성한다는 것을 의미할 수 있다. 상기 폴리우레탄은 알코올기와 아이소사이안산기의 결합으로 형성된 우레탄결합으로 결합된 고분자 화합물이라면, 특별히 제한되지 않는다.The polyurethane substrate layer 10 is a basic substrate on which the first adhesive layer 20 and the second adhesive layer 30 are supported, and the polyurethane substrate layer 10 of this embodiment is polyurethane, methyl ethyl ketone, and dimethyl It is formed of a polyurethane composition containing formamide. At this time, the polyurethane substrate layer 10 of the present embodiment is formed of a polyurethane composition containing polyurethane, methyl ethyl ketone and dimethyl formamide, the polyurethane substrate applied or sprayed while drying or curing It may mean that the layer 10 is formed. The polyurethane is not particularly limited as long as it is a polymer compound bonded by a urethane bond formed by a bond between an alcohol group and an isocyanic acid group.

또한, 본 실시예에서는 기존의 폴리에틸렌 테레프탈레이트 필름 등을 대체하여 폴리우레탄 조성물로 폴리우레탄 기재층(10)을 형성함으로써, 인장강도는 높되 신장율이 낮아, 우수한 강도 및 낮은 변형 정도의 특성을 가지는 기재를 제공할 수 있다. In addition, in this embodiment, by forming the polyurethane substrate layer 10 with a polyurethane composition by replacing the existing polyethylene terephthalate film, etc., a substrate having high tensile strength but low elongation, excellent strength and low degree of deformation. Can provide.

폴리우레탄 조성물은 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤 1 ~ 25 중량부를 포함할 수 있다. 만약, 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤을 1 중량부 미만으로 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 높아지는 문제가 있을 수 있다. 반면, 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤 25 중량부를 초과하여 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 낮아지며, 양면테이프의 내구성이 현저히 저하되는 문제가 있을 수 있다.The polyurethane composition may include 1 to 25 parts by weight of the methyl ethyl ketone based on 100 parts by weight of polyurethane. If less than 1 part by weight of the methyl ethyl ketone is included with respect to 100 parts by weight of polyurethane, there may be a problem that the viscosity of the polyurethane composition is excessively increased. On the other hand, when it contains more than 25 parts by weight of the methyl ethyl ketone with respect to 100 parts by weight of polyurethane, the viscosity of the polyurethane composition may be too low, and durability of the double-sided tape may be significantly reduced.

폴리우레탄 조성물은 폴리우레탄 100 중량부에 대해 상기 다이메틸폼아마이드 150 ~ 250 중량부를 포함할 수 있다. 만약, 폴리우레탄 조성물이 폴리우레탄 100 중량부에 대해 상기 다이메틸폼아마이드를 150 중량부 미만으로 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 높아지는 문제가 있을 수 있다. 반면, 폴리우레탄 100 중량부에 대해 상기 다이메틸폼아마이드를 250 중량부를 초과하여 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 낮아지며, 양면테이프의 내구성이 현저히 저하되는 문제가 있을 수 있다.The polyurethane composition may include 150 to 250 parts by weight of the dimethylformamide based on 100 parts by weight of polyurethane. If the polyurethane composition contains less than 150 parts by weight of the dimethylformamide relative to 100 parts by weight of the polyurethane, there may be a problem that the viscosity of the polyurethane composition is too high. On the other hand, when the dimethyl formamide is included in excess of 250 parts by weight based on 100 parts by weight of polyurethane, the viscosity of the polyurethane composition may be too low, and durability of the double-sided tape may be significantly reduced.

본 실시예의 폴리우레탄 조성물은 폴리우레탄 100 중량부에 대해 메틸에틸케톤 1 ~ 25 중량부 및 다이메틸폼아마이드 150 ~ 250 중량부를 포함할 때, 점도가 4,000 ~ 5,000 cps 로 형성될 수 있다. 또한, 본 실시예의 폴리우레탄 조성물은 전체 총 중량 중 고형분이 20 ~ 30 중량%일 수 있다.When the polyurethane composition of the present embodiment contains 1 to 25 parts by weight of methyl ethyl ketone and 150 to 250 parts by weight of dimethyl formamide based on 100 parts by weight of polyurethane, the viscosity may be 4,000 to 5,000 cps. In addition, the polyurethane composition of the present embodiment may have a solid content of 20 to 30% by weight of the total total weight.

제 1 점착층(20) 및 제 2 점착층(30)은 도 1에 도시된 바와 같이 폴리우레탄 기재층(10)의 일면에 형성되며, 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는 점착 조성물로 형성될 수 있다. 이때, 본 실시예의 제 1 점착층(20) 또는 제 2 점착층(30)이 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는 점착 조성물로 형성된다는 것은, 도포 내지 분사된 점착 조성물이 건조 또는 경화되면서 점착층을 형성함을 의미하는 것일 수 있다.The first adhesive layer 20 and the second adhesive layer 30 are formed on one surface of the polyurethane base layer 10 as shown in FIG. 1, and contain a vinyl chloride-vinyl acetate copolymer, ethyl acetate, and an organic solvent. It may be formed of an adhesive composition comprising. At this time, the first adhesive layer 20 or the second adhesive layer 30 of the present embodiment is formed of an adhesive composition comprising a vinyl chloride-vinyl acetate copolymer, ethyl acetate and an organic solvent, the applied or sprayed adhesive composition The drying or curing may mean forming an adhesive layer.

점착 조성물은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하되, 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함할 수 있다.The adhesive composition includes a vinyl chloride-vinyl acetate copolymer, ethyl acetate and an organic solvent, but contains 30 to 65 parts by weight of ethyl acetate and 40 to 100 parts by weight of the organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. I can.

점착 조성물은 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부를 포함할 수 있다. 만약, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트를 30 중량부 미만으로 포함할 경우에는 접착성이 낮은 문제가 있을 수 있다. 반면, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 65 중량부를 초과하여 포함할 경우에는 점착 조성물의 점도가 낮아지고, 접착성이 낮아지는 문제가 있을 수 있다.The adhesive composition may include 30 to 65 parts by weight of ethyl acetate based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. If the adhesive composition contains less than 30 parts by weight of ethyl acetate based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, there may be a problem of low adhesion. On the other hand, when the adhesive composition contains more than 65 parts by weight of ethyl acetate based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, there may be a problem in that the viscosity of the adhesive composition is lowered and adhesiveness is lowered.

점착 조성물은 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 유기용매를 40 ~ 100 중량부로 포함할 수 있다. 만약, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 유기용매를 40 중량부 미만으로 포함할 경우에는 점착 조성물의 점도가 낮아지고, 양면테이프의 접착 성능이 저하되는 문제가 있을 수 있다. 반면, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 유기용매 100 중량부를 초과하여 포함할 경우에는 점착 조성물의 점도가 낮아지고, 양면테이프의 접착 성능이 저하되는 문제가 있을 수 있다.The adhesive composition may include 40 to 100 parts by weight of an organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. If the adhesive composition contains less than 40 parts by weight of an organic solvent with respect to 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, there may be a problem that the viscosity of the adhesive composition decreases and the adhesive performance of the double-sided tape decreases. . On the other hand, when the adhesive composition contains more than 100 parts by weight of the organic solvent with respect to 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, the viscosity of the adhesive composition may be lowered, and the adhesive performance of the double-sided tape may be deteriorated.

상기 유기용매는 메탄올, 에탄올, 톨루엔, 메틸에틸케톤 및 다이메틸폼아마이드로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The organic solvent may include at least one selected from the group consisting of methanol, ethanol, toluene, methylethylketone, and dimethylformamide.

바람직하게, 상기 유기용매는 메탄올 및 톨루엔을 포함할 수 있다.Preferably, the organic solvent may include methanol and toluene.

더욱 바람직하게, 상기 유기용매는 메탄올 및 톨루엔을 1 : 1 ~ 12 의 중량비로 포함할 수 있다.More preferably, the organic solvent may contain methanol and toluene in a weight ratio of 1:1 to 12.

본 실시예의 점착 조성물은 상기 점착 조성물은 상기 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 폴리아크릴아마이드 1 ~ 10 중량부를 더 포함할 수 있다. 본 실시예의 점착 조성물은 폴리아크릴아마이드의 피막 성능에 의해 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)이 각각의 계면에서 서로 혼합되지 않고 분리된 층으로 형성될 수 있도록 하면서도 접착 성능을 더욱 향상시킬 수 있다.The adhesive composition of the present embodiment may further include 1 to 10 parts by weight of polyacrylamide based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. The adhesive composition of this embodiment is a layer in which the first adhesive layer 20, the polyurethane base layer 10, and the second adhesive layer 30 are not mixed with each other at each interface by the film performance of polyacrylamide. While being able to be formed, the adhesion performance can be further improved.

본 실시예의 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 200,000 인 것일 수 있다.The polyacrylamide of this embodiment may have a number average molecular weight of 10,000 to 200,000.

바람직하게, 본 실시예의 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드를 포함할 수 있다.Preferably, the polyacrylamide of this embodiment may include a polyacrylamide having a number average molecular weight of 10,000 to 50,000 and a polyacrylamide having a number average molecular weight of 100,000 to 150,000.

더욱 바람직하게, 본 실시예의 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드 1 : 1.5 ~ 4 의 중량비로 포함할 수 있다.More preferably, the polyacrylamide of the present embodiment may include polyacrylamide having a number average molecular weight of 10,000 to 50,000 and polyacrylamide having a number average molecular weight of 100,000 to 150,000 in a weight ratio of 1: 1.5 to 4.

특히, 본 실시예에서는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드 1 : 1.5 ~ 4 의 중량비로 포함할 때, 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수한 양면 테이프를 제공할 수 있다. Particularly, in this embodiment, when the number average molecular weight is 10,000 to 50,000 polyacrylamide and the number average molecular weight of 100,000 to 150,000 polyacrylamide 1: 1.5 to 4 when included in a weight ratio, adhesion, durability, etc. It is possible to provide a double-sided tape having excellent properties.

본 실시예에 따라, 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함하거나, 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부, 상기 유기용매 40 ~ 100 중량부 및 상기 폴리아크릴아마이드 1 ~ 10 중량부를 포함하는 점착 조성물은, 점도가 3,000 ~ 4,000 cps 일 수 있다. 또한, 상기 점착 조성물의 고형분은 40 ~ 50 중량%일 수 있다.According to the present embodiment, ethyl acetate 30 to 65 parts by weight and 40 to 100 parts by weight of the organic solvent are included with respect to 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, or ethyl for 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. The adhesive composition including 30 to 65 parts by weight of acetate, 40 to 100 parts by weight of the organic solvent, and 1 to 10 parts by weight of the polyacrylamide may have a viscosity of 3,000 to 4,000 cps. In addition, the solid content of the adhesive composition may be 40 to 50% by weight.

또한, 본 발명에서는 양면테이프의 제조방법을 제공한다.In addition, the present invention provides a method of manufacturing a double-sided tape.

본 발명의 일 실시예에서는 폴리우레탄 기재층(10), 상기 폴리우레탄 기재층(10)의 일면에 형성된 제 1 점착층(20) 및 상기 폴리우레탄 기재층(10)의 타면에 형성된 제 2 점착층(30)을 포함하는 양면테이프의 제조방법에 있어서, 상기 폴리우레탄 기재층(10) 형성용 폴리우레탄 조성물과 상기 제 1 점착층(20) 및 상기 제 2 점착층(30) 형성용 점착 조성물을 준비하는 제 1 단계 및 이형지(40) 상에 상기 폴리우레탄 조성물과 상기 점착 조성물을 도포하고 경화하여 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)의 순차로 적층된 양면테이프를 형성하는 제 2 단계를 포함하고, 상기 폴리우레탄 조성물은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하며, 상기 점착 조성물은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는, 양면테이프의 제조방법을 제공한다.In an embodiment of the present invention, a polyurethane base layer 10, a first adhesive layer 20 formed on one surface of the polyurethane base layer 10, and a second adhesive formed on the other surface of the polyurethane base layer 10 In the method of manufacturing a double-sided tape including a layer 30, the polyurethane composition for forming the polyurethane base layer 10 and the adhesive composition for forming the first adhesive layer 20 and the second adhesive layer 30 In the first step of preparing and applying and curing the polyurethane composition and the adhesive composition on a release paper 40, the first adhesive layer 20, the polyurethane base layer 10, and the second adhesive layer 30 Including a second step of forming a double-sided tape stacked in sequence, the polyurethane composition comprises polyurethane, methyl ethyl ketone and dimethyl formamide, the adhesive composition is vinyl chloride-vinyl acetate copolymer, ethyl acetate And it provides a method of manufacturing a double-sided tape containing an organic solvent.

(1)폴리우레탄 기재층(10) 형성용 폴리우레탄 조성물과 상기 제 1 점착층(20) 및 상기 제 2 점착층(30) 형성용 점착 조성물을 준비하는 제 1 단계(1) a first step of preparing a polyurethane composition for forming a polyurethane base layer 10 and an adhesive composition for forming the first adhesive layer 20 and the second adhesive layer 30

본 실시예의 제 1 단계에서는 폴리우레탄 기재층(10)의 형성을 위한 폴리우레탄 조성물과 상기 제 1 점착층(20) 및 상기 제 2 점착층(30)의 형성을 위한 점착 조성물을 각각 준비할 수 있다.In the first step of this embodiment, a polyurethane composition for forming a polyurethane base layer 10 and an adhesive composition for forming the first adhesive layer 20 and the second adhesive layer 30 may be prepared, respectively. have.

본 실시예의 제 1 단계에서는 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물을 제조할 수 있다. In the first step of this embodiment, a polyurethane composition including polyurethane, methyl ethyl ketone and dimethyl formamide may be prepared.

예를 들어, 본 실시예의 제 1 단계에서는 반응 용기 내에 상기 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 적정 비율로 혼합한 후 이를 교반함으로써, 균일한 조성의 폴리우레탄 조성물을 제조할 수 있다. 상기 폴리우레탄은 알코올기와 아이소사이안산기의 결합으로 형성된 우레탄결합으로 결합된 고분자 화합물이라면, 특별히 제한되지 않는다.For example, in the first step of the present embodiment, the polyurethane, methyl ethyl ketone, and dimethyl formamide are mixed in an appropriate ratio in a reaction vessel and then stirred to prepare a polyurethane composition having a uniform composition. The polyurethane is not particularly limited as long as it is a polymer compound bonded by a urethane bond formed by a bond between an alcohol group and an isocyanic acid group.

폴리우레탄 조성물은 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤 1 ~ 25 중량부를 포함할 수 있다. 만약, 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤을 1 중량부 미만으로 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 높아지는 문제가 있을 수 있다. 반면, 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤 25 중량부를 초과하여 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 낮아지며, 양면테이프의 내구성이 현저히 저하되는 문제가 있을 수 있다.The polyurethane composition may include 1 to 25 parts by weight of the methyl ethyl ketone based on 100 parts by weight of polyurethane. If less than 1 part by weight of the methyl ethyl ketone is included with respect to 100 parts by weight of polyurethane, there may be a problem that the viscosity of the polyurethane composition is excessively increased. On the other hand, when it contains more than 25 parts by weight of the methyl ethyl ketone with respect to 100 parts by weight of polyurethane, the viscosity of the polyurethane composition may be too low, and durability of the double-sided tape may be significantly reduced.

폴리우레탄 조성물은 폴리우레탄 100 중량부에 대해 상기 다이메틸폼아마이드 150 ~ 250 중량부를 포함할 수 있다. 만약, 폴리우레탄 조성물이 폴리우레탄 100 중량부에 대해 상기 다이메틸폼아마이드를 150 중량부 미만으로 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 높아지는 문제가 있을 수 있다. 반면, 폴리우레탄 100 중량부에 대해 상기 다이메틸폼아마이드를 250 중량부를 초과하여 포함할 경우에는 폴리우레탄 조성물의 점도가 지나치게 낮아지며, 양면테이프의 내구성이 현저히 저하되는 문제가 있을 수 있다.The polyurethane composition may include 150 to 250 parts by weight of the dimethylformamide based on 100 parts by weight of polyurethane. If the polyurethane composition contains less than 150 parts by weight of the dimethylformamide relative to 100 parts by weight of the polyurethane, there may be a problem that the viscosity of the polyurethane composition is too high. On the other hand, when the dimethyl formamide is included in excess of 250 parts by weight based on 100 parts by weight of polyurethane, the viscosity of the polyurethane composition may be too low, and durability of the double-sided tape may be significantly reduced.

본 실시예의 폴리우레탄 조성물은 폴리우레탄 100 중량부에 대해 메틸에틸케톤 1 ~ 25 중량부 및 다이메틸폼아마이드 150 ~ 250 중량부를 포함할 때, 점도가 4,000 ~ 5,000 cps 로 형성될 수 있다. 또한, 본 실시예의 폴리우레탄 조성물은 전체 총 중량 중 고형분이 20 ~ 30 중량%일 수 있다.When the polyurethane composition of the present embodiment contains 1 to 25 parts by weight of methyl ethyl ketone and 150 to 250 parts by weight of dimethyl formamide based on 100 parts by weight of polyurethane, the viscosity may be 4,000 to 5,000 cps. In addition, the polyurethane composition of the present embodiment may have a solid content of 20 to 30% by weight of the total total weight.

본 실시예에서는 기존의 폴리에틸렌 테레프탈레이트 필름 등을 대체하여 폴리우레탄 조성물로 폴리우레탄 기재층(10)을 형성함으로써, 인장강도는 높되 신장율이 낮아, 우수한 강도 및 낮은 변형 정도의 특성을 가지는 기재를 제공할 수 있다. In this embodiment, by forming the polyurethane substrate layer 10 with a polyurethane composition by replacing the existing polyethylene terephthalate film, etc., the tensile strength is high but the elongation is low, thereby providing a substrate having excellent strength and low degree of deformation characteristics. can do.

또한, 본 실시예의 제 1 단계에서는 폴리우레탄 기재층(10)의 양면에 점착층을 형성하기 위한, 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하는 점착 조성물을 제조할 수 있다. 예를 들어, 제 1 단계에서는 반응 용기 내에 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 적정 비율로 혼합한 후 이를 교반함으로써, 균일한 조성의 점착 조성물을 제조할 수 있다.In addition, in the first step of the present embodiment, an adhesive composition including a vinyl chloride-vinyl acetate copolymer, ethyl acetate and an organic solvent may be prepared for forming an adhesive layer on both surfaces of the polyurethane base layer 10. For example, in the first step, a vinyl chloride-vinyl acetate copolymer, ethyl acetate, and an organic solvent are mixed in an appropriate ratio in a reaction vessel and then stirred to prepare an adhesive composition having a uniform composition.

점착 조성물은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트 및 유기용매를 포함하되, 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함할 수 있다. The adhesive composition includes a vinyl chloride-vinyl acetate copolymer, ethyl acetate and an organic solvent, but contains 30 to 65 parts by weight of ethyl acetate and 40 to 100 parts by weight of the organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. I can.

점착 조성물은 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부를 포함할 수 있다. 만약, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트를 30 중량부 미만으로 포함할 경우에는 접착성이 낮은 문제가 있을 수 있다. 반면, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 65 중량부를 초과하여 포함할 경우에는 점착 조성물의 점도가 낮아지고, 접착성이 낮아지는 문제가 있을 수 있다.The adhesive composition may include 30 to 65 parts by weight of ethyl acetate based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. If the adhesive composition contains less than 30 parts by weight of ethyl acetate based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, there may be a problem of low adhesion. On the other hand, when the adhesive composition contains more than 65 parts by weight of ethyl acetate based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, there may be a problem in that the viscosity of the adhesive composition is lowered and adhesiveness is lowered.

점착 조성물은 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 유기용매를 40 ~ 100 중량부로 포함할 수 있다. 만약, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 유기용매를 40 중량부 미만으로 포함할 경우에는 점착 조성물의 점도가 낮아지고, 양면테이프의 접착 성능이 저하되는 문제가 있을 수 있다. 반면, 점착 조성물이 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 유기용매 100 중량부를 초과하여 포함할 경우에는 점착 조성물의 점도가 낮아지고, 양면테이프의 접착 성능이 저하되는 문제가 있을 수 있다.The adhesive composition may include 40 to 100 parts by weight of an organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. If the adhesive composition contains less than 40 parts by weight of an organic solvent with respect to 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, there may be a problem that the viscosity of the adhesive composition decreases and the adhesive performance of the double-sided tape decreases. . On the other hand, when the adhesive composition contains more than 100 parts by weight of the organic solvent with respect to 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, the viscosity of the adhesive composition may be lowered, and the adhesive performance of the double-sided tape may be deteriorated.

상기 유기용매는 메탄올, 에탄올, 톨루엔, 메틸에틸케톤 및 다이메틸폼아마이드로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The organic solvent may include at least one selected from the group consisting of methanol, ethanol, toluene, methylethylketone, and dimethylformamide.

바람직하게, 상기 유기용매는 메탄올 및 톨루엔을 포함할 수 있다.Preferably, the organic solvent may include methanol and toluene.

더욱 바람직하게, 상기 유기용매는 메탄올 및 톨루엔을 1 : 1 ~ 12 의 중량비로 포함할 수 있다.More preferably, the organic solvent may contain methanol and toluene in a weight ratio of 1:1 to 12.

본 실시예의 점착 조성물은 상기 점착 조성물은 상기 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 폴리아크릴아마이드 1 ~ 10 중량부를 더 포함할 수 있다. 본 실시예의 점착 조성물은 폴리아크릴아마이드의 피막 성능에 의해 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)이 각각의 계면에서 서로 혼합되지 않고 분리된 층으로 형성될 수 있도록 하면서도 점착 성능을 더욱 향상시킬 수 있다.The adhesive composition of the present embodiment may further include 1 to 10 parts by weight of polyacrylamide based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. The adhesive composition of this embodiment is a layer in which the first adhesive layer 20, the polyurethane base layer 10, and the second adhesive layer 30 are not mixed with each other at each interface by the film performance of polyacrylamide. While it can be formed, the adhesion performance can be further improved.

본 실시예의 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 200,000 인 것일 수 있다.The polyacrylamide of this embodiment may have a number average molecular weight of 10,000 to 200,000.

바람직하게, 본 실시예의 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드를 포함할 수 있다.Preferably, the polyacrylamide of this embodiment may include a polyacrylamide having a number average molecular weight of 10,000 to 50,000 and a polyacrylamide having a number average molecular weight of 100,000 to 150,000.

더욱 바람직하게, 본 실시예의 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드 1 : 1.5 ~ 4 의 중량비로 포함할 수 있다.More preferably, the polyacrylamide of the present embodiment may include polyacrylamide having a number average molecular weight of 10,000 to 50,000 and polyacrylamide having a number average molecular weight of 100,000 to 150,000 in a weight ratio of 1: 1.5 to 4.

특히, 본 실시예에서는 수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드 1 : 1.5 ~ 4 의 중량비로 포함할 때, 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수한 양면 테이프를 제공할 수 있다. Particularly, in this embodiment, when the number average molecular weight is 10,000 to 50,000 polyacrylamide and the number average molecular weight of 100,000 to 150,000 polyacrylamide 1: 1.5 to 4 when included in a weight ratio, adhesion, durability, etc. It is possible to provide a double-sided tape having excellent properties.

본 실시예에 따라, 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함하거나, 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 에틸 아세테이트 30 ~ 65 중량부, 상기 유기용매 40 ~ 100 중량부 및 상기 폴리아크릴아마이드 1 ~ 10 중량부를 포함하는 점착 조성물은, 점도가 3,000 ~ 4,000 cps 일 수 있다. 또한, 상기 점착 조성물의 고형분은 40 ~ 50 중량%일 수 있다.According to the present embodiment, ethyl acetate 30 to 65 parts by weight and 40 to 100 parts by weight of the organic solvent are included with respect to 100 parts by weight of the vinyl chloride-vinyl acetate copolymer, or ethyl for 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. The adhesive composition including 30 to 65 parts by weight of acetate, 40 to 100 parts by weight of the organic solvent, and 1 to 10 parts by weight of the polyacrylamide may have a viscosity of 3,000 to 4,000 cps. In addition, the solid content of the adhesive composition may be 40 to 50% by weight.

상기에 따라 제조된 폴리우레탄 조성물 및 점착 조성물에는 도포 내지 분사의 용이성을 향상시키기 위해, 적량의 유기용매가 더 혼합될 수 있다. 상기 유기용매는 메탄올, 에탄올, 톨루엔, 메틸에틸케톤 및 다이메틸폼아마이드로 이루어진 군에서 선택되는 하나 이상일 수 있으나, 이에 제한되지 않는다.In order to improve the ease of application or spraying, the polyurethane composition and the adhesive composition prepared according to the above may be further mixed with an appropriate amount of an organic solvent. The organic solvent may be one or more selected from the group consisting of methanol, ethanol, toluene, methylethylketone, and dimethylformamide, but is not limited thereto.

본 실시예의 양면테이프에서 상기 폴리우레탄 조성물은 점도가 4,000 ~ 5,000 cps 이며, 상기 점착 조성물은 점도가 3,000 ~ 4,000 cps 으로 형성됨에 따라, 두 개의 조성물은 점도 차이에 있어 서로 혼합되지 않고, 각각이 층을 이룰 수 있다.In the double-sided tape of this example, the polyurethane composition has a viscosity of 4,000 to 5,000 cps, and the adhesive composition has a viscosity of 3,000 to 4,000 cps, so that the two compositions are not mixed with each other due to the difference in viscosity, and each layer Can be achieved.

(2)이형지(40) 상에 상기 폴리우레탄 조성물과 상기 점착 조성물을 도포하고 경화하여 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)의 순차로 적층된 양면테이프를 형성하는 제 2 단계(2) The polyurethane composition and the adhesive composition are applied and cured on a release paper 40 to sequentially stack the first adhesive layer 20, the polyurethane base layer 10, and the second adhesive layer 30. The second step of forming double-sided tape

본 실시예의 제 2 단계에서는 이형지(40) 상에 상기 제 1 단계에서 제조된 폴리우레탄 조성물과 상기 제 1 단계에서 제조된 점착 조성물을 도포하고 경화하여 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)의 순차로 적층된 양면테이프를 형성할 수 있다. 상기된 바와 같이 본 실시예에 따르는 폴리우레탄 조성물과 점착 조성물은 서로 상이한 점도 및 고형분 함량 조건을 가지는 바, 두 개의 조성물은 점도와 비중의 차이로 인해 서로 혼합되지 않고 분리된 상태로 존재할 수 있다.In the second step of the present embodiment, the polyurethane composition prepared in the first step and the adhesive composition prepared in the first step are applied and cured on a release paper 40 to provide the first adhesive layer 20 and the polyurethane base layer. (10) and the second adhesive layer 30 may be sequentially stacked to form a double-sided tape. As described above, the polyurethane composition and the adhesive composition according to the present embodiment have different viscosity and solid content conditions from each other, and the two compositions may exist in a separate state without being mixed with each other due to the difference in viscosity and specific gravity.

바람직하게, 본 실시예의 제 2 단계에서는 슬롯다이로 각 조성물을 분사 내지 도포함으로써, 양면테이프를 형성할 수 있다.Preferably, in the second step of this embodiment, a double-sided tape can be formed by spraying or applying each composition with a slot die.

더욱 바람직하게, 본 실시예의 제 2 단계에서는 3 개의 슬롯다이를 이용하며, 3 개의 슬롯다이노즐을 통해 점착 조성물, 폴리우레탄 조성물 및 점착 조성물이 순차적으로 적층된 형태로 도포될 수 있도록 각각의 조성물을 분사한 후 이를 건조시킴으로써, 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)의 순차로 적층된 양면테이프를 형성할 수 있다.More preferably, in the second step of this embodiment, three slot dies are used, and each composition is applied so that the adhesive composition, the polyurethane composition, and the adhesive composition are sequentially stacked through the three slot die nozzles. By drying it after spraying, it is possible to form a double-sided tape in which the first adhesive layer 20, the polyurethane base layer 10, and the second adhesive layer 30 are sequentially stacked.

예를 들어, 상기 건조는 하부 이형지(40) 상에 3 개의 슬롯다이노즐을 통해 점착 조성물, 폴리우레탄 조성물 및 점착 조성물을 순차적으로 적층된 형태로 도포한 다음, 건조기를 통과시킴으로써, 상기 조성물들을 경화시킬 수 있다. 이때, 건조기는 내부에 6 개의 온도 구간을 가질 수 있으며, 건조기의 입구부터 출구 사이에, 각각이 순차적으로 60 ℃, 75 ℃, 85 ℃, 100 ℃, 110 ℃ 및 100 ℃로 이루어진 것일 수 있다.For example, in the drying, the adhesive composition, the polyurethane composition and the adhesive composition are sequentially stacked on the lower release paper 40 through three slot die nozzles, and then the compositions are cured by passing through a dryer. I can make it. At this time, the dryer may have six temperature zones therein, and between the inlet and the outlet of the dryer, each may be sequentially composed of 60 ℃, 75 ℃, 85 ℃, 100 ℃, 110 ℃ and 100 ℃.

특히, 본 실시예에서는 상기와 같이 내부 온도가 구간별로 상이한 건조기를 통해 각각의 조성물을 건조 및 경화시킴으로써, 이형지(40)와 각 조성물 간의 분리 또는 들뜸을 방지하고, 각 조성물이 경화되는 과정에서 기포가 과도하게 형성되지 않되 내부와 외부가 균일하게 경화되도록 할 수 있다.In particular, in this embodiment, by drying and curing each composition through a dryer having a different internal temperature for each section as described above, separation or lifting between the release paper 40 and each composition is prevented, and bubbles are formed in the process of curing each composition. Is not formed excessively, but the inside and outside can be uniformly cured.

이에 따라, 제 1 이형지(40)에 점착 조성물을 도포한 뒤 필름 또는 발포폼 형태의 기재의 일면을 부착하는 단계 및 제 2 이형지(40)에 점착 조성물을 도포한 뒤 상기 기재의 타면에 부착하는 단계를 포함하는 종래의 양면테이프 제조공정과 달리, 본 실시예에서는 점착 조성물, 폴리우레탄 조성물 및 점착 조성물이 순차적으로 적층된 형태로 도포될 수 있도록 각각의 조성물을 분사한 후 이를 건조시킴으로써, 제 1 점착층(20), 폴리우레탄 기재층(10) 및 제 2 점착층(30)의 순차로 적층된 양면테이프를 형성함에 따라, 보다 간단한 공정으로 양면테이프를 제조할 수 있고, 기재층과 점착층 간의 결합력이 우수하여 각 층 간의 분리 현상이 발생되지 않으며, 두께가 얇으면서도 접착성, 내구성 등의 특성이 우수할 수 있다.Accordingly, after applying the adhesive composition to the first release paper 40, attaching one side of the substrate in the form of a film or foam, and applying the adhesive composition to the second release paper 40 and then attaching the adhesive composition to the other side of the substrate. Unlike the conventional double-sided tape manufacturing process including the step, in this embodiment, the adhesive composition, the polyurethane composition, and the adhesive composition are sprayed and dried so that the adhesive composition can be sequentially applied in a stacked form, By forming the double-sided tape sequentially stacked with the adhesive layer 20, the polyurethane base layer 10, and the second adhesive layer 30, a double-sided tape can be manufactured in a simpler process, and the base layer and the adhesive layer Since the bonding between the layers is excellent, separation between layers does not occur, and characteristics such as adhesion and durability may be excellent even though the thickness is thin.

이하 실시예, 비교예, 및 실험예를 통하여 본 발명의 양면테이프 및 이의 제조방법에 대해 구체적으로 설명하기로 한다. 이들 실시예는 단지 본 발명을 예시하기 위한 것이므로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다.Hereinafter, the double-sided tape of the present invention and a method of manufacturing the same will be described in detail through Examples, Comparative Examples, and Experimental Examples. Since these examples are for illustrative purposes only, the scope of the present invention is not to be construed as being limited by these examples.

[ 실시예 ][Example]

실시예 1 내지 4Examples 1 to 4

표 1[단위 : 중량부] 및 표 2[단위 : 중량부]와 같은 조성의 폴리우레탄 조성물 및 점착 조성물을 각각 제조하였다.A polyurethane composition and an adhesive composition having the same composition as Table 1 [unit: parts by weight] and Table 2 [unit: parts by weight] were prepared, respectively.

이어서, 슬롯다이노즐 3개를 인접하게 배치한 후, 하부 이형지 상에 슬롯다이노즐을 통해 점착 조성물, 폴리우레탄 조성물 및 점착 조성물의 순으로 적층되도록 각각의 조성물을 7 kg/min의 속도로 분사한 다음, 건조기를 통과하도록 하면서 경화시켜, 하부 이형지 상에 제 2 점착층, 폴리우레탄 기재층 및 제 1 점착층을 형성하였다.Then, after placing three slot die nozzles adjacent to each other, each composition was sprayed at a rate of 7 kg/min so that the adhesive composition, the polyurethane composition, and the adhesive composition were sequentially stacked on the lower release paper through the slot die nozzle. Then, it was cured while passing through a dryer to form a second adhesive layer, a polyurethane base layer, and a first adhesive layer on the lower release paper.

이때, 건조기는 건조기의 입구부터 출구까지 총 6 개의 온도 구간을 가지도록 형성된 것이며, 각각이 순차적으로 60 ℃, 75 ℃, 85 ℃, 100 ℃, 110 ℃ 및 100 ℃로 이루어진다.At this time, the dryer is formed to have a total of six temperature ranges from the inlet to the outlet of the dryer, each of which is sequentially composed of 60 ℃, 75 ℃, 85 ℃, 100 ℃, 110 ℃ and 100 ℃.

이 후, 제 1 점착층 상에 상부 이형지를 적층함으로써, 도 1에 도시된 바와 같은 단면을 가지는 양면테이프를 제조하였다.Thereafter, by laminating the upper release paper on the first adhesive layer, a double-sided tape having a cross-section as shown in FIG. 1 was manufactured.

이때, 제 1 점착층 및 제 2 접착층은 약 3 마이크로미터의 두께로 형성되었으며, 폴리우레탄 기재층은 4 마이크로미터의 두께로 형성되어, 이형지를 제외한 양면테이프의 두께는 약 10 마이크로미터로 형성되었다.At this time, the first adhesive layer and the second adhesive layer were formed to a thickness of about 3 micrometers, and the polyurethane base layer was formed to a thickness of 4 micrometers, and the thickness of the double-sided tape excluding the release paper was formed to about 10 micrometers. .

실시예 1 내지 4Examples 1 to 4 폴리우레탄Polyurethane 100100 메틸에틸케톤Methyl ethyl ketone 1515 다이메틸폼아마이드Dimethylformamide 200200

실시예 1Example 1 실시예 2Example 2 실시예3Example 3 실시예4Example 4 염화비닐-비닐아세테이트 공중합체Vinyl chloride-vinyl acetate copolymer 100100 100100 100100 100100 에틸 아세테이트Ethyl acetate 4040 4040 4040 4040 유기용매Organic solvent 메탄올Methanol 66 66 66 66 톨루엔toluene 7272 7272 7272 7272 폴리아크릴아마이드Polyacrylamide -- 0.50.5 55 1515 *폴리아크릴아마이드 : 수평균 분자량이 40,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 140,000 ~ 150,000 인 폴리아크릴아마이드 1 : 2*Polyacrylamide: Polyacrylamide with a number average molecular weight of 40,000 ~ 50,000 and polyacrylamide with a number average molecular weight of 140,000 ~ 150,000 1: 2

실시예 5Example 5

폴리아크릴아마이드 : 수평균 분자량이 40,000 ~ 50,000 인 폴리아크릴아마이드만을 사용한 것을 제외하고는, 실시예 2와 동일하게 제조하였다. Polyacrylamide: It was prepared in the same manner as in Example 2, except that only polyacrylamide having a number average molecular weight of 40,000 to 50,000 was used.

실시예 6Example 6

수평균 분자량이 140,000 ~ 150,000 인 폴리아크릴아마이드만을 사용한 것을 제외하고는, 실시예 2와 동일하게 제조하였다. It was prepared in the same manner as in Example 2, except that only polyacrylamide having a number average molecular weight of 140,000 to 150,000 was used.

[ 비교예 ][Comparative Example]

비교예 1 내지 4Comparative Examples 1 to 4

표 3[단위 : 중량부]과 같은 조성으로 폴리우레탄 조성물을 제조한 것을 제외하고는, 실시예 1과 동일하게 제조하였다.It was prepared in the same manner as in Example 1, except that a polyurethane composition was prepared in the same composition as Table 3 [unit: parts by weight].

비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 폴리우레탄Polyurethane 100100 100100 100100 100100 메틸에틸케톤Methyl ethyl ketone 0.50.5 3030 1515 1515 다이메틸폼아마이드Dimethylformamide 200200 200200 140140 260260

비교예 5 내지 8Comparative Examples 5 to 8

표 4[단위 : 중량부]와 같은 조성으로 점착 조성물을 제조한 것을 제외하고는, 실시예 1과 동일하게 제조하였다.It was prepared in the same manner as in Example 1, except that the adhesive composition was prepared in the same composition as Table 4 [unit: parts by weight].

비교예 5Comparative Example 5 비교예 6Comparative Example 6 비교예7Comparative Example 7 비교예8Comparative Example 8 염화비닐-비닐아세테이트 공중합체Vinyl chloride-vinyl acetate copolymer 100100 100100 100100 100100 에틸 아세테이트Ethyl acetate 2525 7070 4040 4040 유기용매Organic solvent 메탄올Methanol 66 66 66 66 톨루엔toluene 7272 7272 2929 9999

[ 실험예 ][Experimental Example]

실험예 1 : 점도 측정Experimental Example 1: Viscosity Measurement

실시예 1 내지 6 및 비교예 1 내지 8에 따르는 폴리우레탄 조성물 및 점착 조성물의 점도를 측정하고, 그 결과를 표 5에 나타내었다.The viscosity of the polyurethane compositions and adhesive compositions according to Examples 1 to 6 and Comparative Examples 1 to 8 were measured, and the results are shown in Table 5.

이때, 점도는 브룩필드(Brookfield) 점도계를 이용하여, 약 25 ℃에서 측정되었다.At this time, the viscosity was measured at about 25 °C using a Brookfield viscometer.

폴리우레탄 조성물의 점도(cps)Viscosity of polyurethane composition (cps) 점착 조성물의 점도(cps)Viscosity of adhesive composition (cps) 실시예1Example 1 4,5004,500 3,2003,200 실시예2Example 2 4,5004,500 3,5003,500 실시예3Example 3 4,5004,500 3,0003,000 실시예4Example 4 4,5004,500 3,7003,700 실시예5Example 5 4,5004,500 3,0003,000 실시예6Example 6 4,5004,500 3,9003,900 비교예1Comparative Example 1 5,5005,500 3,2003,200 비교예2Comparative Example 2 3,5003,500 3,2003,200 비교예3Comparative Example 3 6,0006,000 3,2003,200 비교예4Comparative Example 4 3,2003,200 3,2003,200 비교예5Comparative Example 5 4,5004,500 4,2004,200 비교예6Comparative Example 6 4,5004,500 2,2002,200 비교예7Comparative Example 7 4,5004,500 4,6004,600 비교예8Comparative Example 8 4,5004,500 2,2002,200

표 5를 보면, 본 실시예에 따를 경우 폴리우레탄 조성물은 4,000 ~ 5,000 cps 의 점도를 가지며, 점착 조성물은 3,000 ~ 4,000 cps 의 점도를 가짐을 알 수 있다.Referring to Table 5, it can be seen that the polyurethane composition has a viscosity of 4,000 to 5,000 cps, and the adhesive composition has a viscosity of 3,000 to 4,000 cps according to this example.

실험예 2 : 접착성 평가Experimental Example 2: Evaluation of adhesion

실시예 1의 양면테이프를 25 마이크로미터 두께의 폴리에틸렌 테레프탈레이트 필름(PET)에 적층시킨 후, 이를 폭 25 mm, 길이 200 mm의 시편으로 제조하였다. 시편을 3 mm 두께의 폴리카보네이트판(PC 판)에 부착한 후, 핸드롤러(2 kg)로 기포를 제거함으로써, 부착 고정하였다. 이 후, 만능재료시험기(영국 LLODY 15K)를 이용하여 180 °로 접착성을 평가하고, 그 결과를 표 6에 나타내었다.After laminating the double-sided tape of Example 1 on a 25 micrometer thick polyethylene terephthalate film (PET), it was prepared as a specimen having a width of 25 mm and a length of 200 mm. After attaching the specimen to a 3 mm thick polycarbonate plate (PC plate), air bubbles were removed with a hand roller (2 kg) to fix the attachment. Thereafter, the adhesion was evaluated at 180° using a universal testing machine (LLODY 15K, UK), and the results are shown in Table 6.

또한, 실시예 1과 동일한 방법으로 실시예 2 내지 6 및 비교예 1 내지 8의 접착성을 평가한 후, 그 결과를 표 6에 나타내었다.In addition, after evaluating the adhesion of Examples 2 to 6 and Comparative Examples 1 to 8 in the same manner as in Example 1, the results are shown in Table 6.

접착성(g/25mm)Adhesiveness (g/25mm) 접착성(g/25mm)Adhesiveness (g/25mm) 실시예1Example 1 10001000 비교예1Comparative Example 1 800800 실시예2Example 2 14001400 비교예2Comparative Example 2 750750 실시예3Example 3 10501050 비교예3Comparative Example 3 810810 실시예4Example 4 12001200 비교예4Comparative Example 4 730730 실시예5Example 5 10001000 비교예5Comparative Example 5 420420 실시예6Example 6 10001000 비교예6Comparative Example 6 350350 비교예7Comparative Example 7 410410 비교예8Comparative Example 8 320320

표 6을 보면, 본 실시예에 따를 경우 접착성이 현저히 향상됨을 확인할 수 있다.Referring to Table 6, it can be seen that adhesion is remarkably improved when the present embodiment is followed.

실험예 3 : 내구성 평가Experimental Example 3: Durability evaluation

실시예 1의 양면테이프를 폴리카보네이트 판넬의 일면에 적층시켜 시편을 제조하였다. 이를 약 80 ℃의 오븐에서 약 300 시간 동안 보관한 후, 외형에서 나타나는 변화를 관찰하고, 그 결과를 하기 기준에 따라 평가하여 표 7에 나타내었다.The double-sided tape of Example 1 was laminated on one side of a polycarbonate panel to prepare a specimen. After storing this in an oven at about 80° C. for about 300 hours, changes in appearance were observed, and the results were evaluated according to the following criteria, and are shown in Table 7.

○ : 고온 처리 후, 폴리카보네이트 판넬로부터 양면테이프의 들뜸, 기포 및 박리가 발생되지 않고, 외형에 변형이 없는 경우○: After high-temperature treatment, the double-sided tape from the polycarbonate panel is not lifted, bubbled, or peeled off, and there is no deformation in the appearance.

△ : 고온 처리 후, 폴리카보네이트 판넬로부터 양면테이프의 일부분에서 들뜸, 기포 및 박리가 일부 발생된 경우△: After high-temperature treatment, in the case of partial lifting, air bubbles, and peeling from a part of the double-sided tape from the polycarbonate panel

× : 고온 처리 후, 폴리카보네이트 판넬로부터 양면테이프의 전면에서 들뜸, 기포 및 박리가 발생된 경우×: After high-temperature treatment, when lifting, air bubbles, and peeling occur on the front surface of the double-sided tape from the polycarbonate panel

또한, 실시예 1과 동일한 방법으로 실시예 2 내지 6 및 비교예 1 내지 8의 고온 내구성을 평가하여 In addition, by evaluating the high temperature durability of Examples 2 to 6 and Comparative Examples 1 to 8 in the same manner as in Example 1

고온 내구성High temperature durability 고온 내구성High temperature durability 실시예1Example 1 △△ 비교예1Comparative Example 1 ×× 실시예2Example 2 ○○ 비교예2Comparative Example 2 ×× 실시예3Example 3 ○○ 비교예3Comparative Example 3 ×× 실시예4Example 4 ○○ 비교예4Comparative Example 4 ×× 실시예5Example 5 △△ 비교예5Comparative Example 5 ×× 실시예6Example 6 △△ 비교예6Comparative Example 6 ×× 비교예7Comparative Example 7 ×× 비교예8Comparative Example 8 ××

표 7을 보면, 본 실시예에 따를 경우 고온 내구성이 우수함을 확인할 수 있다.Referring to Table 7, it can be seen that according to the present embodiment, high temperature durability is excellent.

실험예 4 : 폴리우레탄 기재층의 특성 평가Experimental Example 4: Evaluation of the properties of the polyurethane substrate layer

실시예 1 및 비교예 1 내지 4 각각의 폴리우레탄 조성물을 이용하여 4 마이크로미터 두께를 가지는 폴리우레탄 기재층을 형성한 다음 이의 인장강도(단위 : N/mm2) 및 신장률(%)을 평가하여, 그 결과를 표 8에 나타내었다.After forming a polyurethane base layer having a thickness of 4 micrometers using each of the polyurethane compositions of Example 1 and Comparative Examples 1 to 4, the tensile strength (unit: N/mm 2 ) and elongation (%) were evaluated. , The results are shown in Table 8.

이때, 인장강도 및 신장률은 ASTM D882에 따라 평가하였다.At this time, the tensile strength and elongation were evaluated according to ASTM D882.

인장강도The tensile strength 신장률Elongation 실시예1Example 1 4646 380380 비교예1Comparative Example 1 3535 470470 비교예2Comparative Example 2 3030 460460 비교예3Comparative Example 3 3232 465465 비교예4Comparative Example 4 3333 480480

표 8을 보면, 본 실시예에 따를 경우 인장 강도는 높고, 신율은 낮은 특성을 가지는 바, 테이프 기재로서의 특성은 우수할 수 있다.Referring to Table 8, according to the present embodiment, the tensile strength is high and the elongation is low, and the characteristics as a tape base material may be excellent.

전술한 바와 같이, 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 기술을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.As described above, the description of the present invention is for illustrative purposes only, and those of ordinary skill in the art to which the present invention pertains can easily be modified into other specific forms without changing the technical spirit or essential features of the present invention. You can understand. Therefore, the embodiments described above are illustrative in all respects and should be understood as non-limiting. For example, each component described as a single type may be implemented in a distributed manner, and similarly, components described as being distributed may also be implemented in a combined form.

본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is indicated by the claims to be described later rather than the detailed description, and all changes or modified forms derived from the meaning and scope of the claims and their equivalent concepts should be interpreted as being included in the scope of the present invention. do.

10 : 폴리우레탄 기재층
20 : 제 1 점착층
30 : 제 2 점착층
40 : 이형지10: polyurethane base layer
20: first adhesive layer
30: second adhesive layer
40: Hyungji Lee

Claims (10)

폴리우레탄 기재층;
상기 폴리우레탄 기재층의 일면에 형성된 제 1 점착층; 및
상기 폴리우레탄 기재층의 타면에 형성된 제 2 점착층을 포함하되,
상기 폴리우레탄 기재층은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하는 폴리우레탄 조성물로 형성되며,
상기 제 1 점착층 및 상기 제 2 점착층은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트, 폴리아크릴아마이드 및 유기용매를 포함하는 점착 조성물로 형성되고,
상기 점착 조성물은 상기 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 상기 에틸 아세테이트 30 ~ 65 중량부, 상기 폴리아크릴아마이드 1 ~ 10 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함하는 것을 특징으로 하는, 양면테이프.
Polyurethane base layer;
A first adhesive layer formed on one surface of the polyurethane substrate layer; And
Including a second adhesive layer formed on the other surface of the polyurethane base layer,
The polyurethane base layer is formed of a polyurethane composition comprising polyurethane, methyl ethyl ketone and dimethyl formamide,
The first adhesive layer and the second adhesive layer are formed of an adhesive composition comprising a vinyl chloride-vinyl acetate copolymer, ethyl acetate, polyacrylamide, and an organic solvent,
The adhesive composition comprises 30 to 65 parts by weight of the ethyl acetate, 1 to 10 parts by weight of the polyacrylamide, and 40 to 100 parts by weight of the organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. , Double-sided tape.
 제 1 항에 있어서,
상기 폴리우레탄 조성물은
상기 폴리우레탄 100 중량부에 대해 상기 메틸에틸케톤 1 ~ 25 중량부 및 상기 다이메틸폼아마이드 150 ~ 250 중량부를 포함하는 것을 특징으로 하는, 양면테이프.
The method of claim 1,
The polyurethane composition is
A double-sided tape comprising 1 to 25 parts by weight of the methyl ethyl ketone and 150 to 250 parts by weight of the dimethyl formamide based on 100 parts by weight of the polyurethane.
 제 1 항에 있어서,
상기 폴리우레탄 조성물은
점도가 4,000 ~ 5,000 cps 인 것을 특징으로 하는, 양면테이프.
The method of claim 1,
The polyurethane composition is
Double-sided tape, characterized in that the viscosity is 4,000 ~ 5,000 cps.
 삭제delete 삭제delete 제 1 항에 있어서,
상기 폴리아크릴아마이드는 수평균 분자량이 10,000 ~ 200,000 인 것을 특징으로 하는, 양면테이프.
The method of claim 1,
The polyacrylamide is a double-sided tape, characterized in that the number average molecular weight is 10,000 to 200,000.
 제 6 항에 있어서,
상기 폴리아크릴아마이드는
수평균 분자량이 10,000 ~ 50,000 인 폴리아크릴아마이드 및 수평균 분자량이 100,000 ~ 150,000 인 폴리아크릴아마이드를 포함하는 것을 특징으로 하는, 양면테이프.
The method of claim 6,
The polyacrylamide is
A double-sided tape, characterized in that it comprises a polyacrylamide having a number average molecular weight of 10,000 to 50,000 and a polyacrylamide having a number average molecular weight of 100,000 to 150,000.
 제 1 항에 있어서,
상기 점착 조성물은
점도가 3,000 ~ 4,000 cps 인 것을 특징으로 하는, 양면테이프.
The method of claim 1,
The adhesive composition is
Double-sided tape, characterized in that the viscosity is 3,000 ~ 4,000 cps.
 제 1 항에 있어서,
상기 유기용매는
메탄올, 에탄올, 톨루엔, 메틸에틸케톤 및 다이메틸폼아마이드로 이루어진 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는, 양면테이프.
The method of claim 1,
The organic solvent is
Methanol, ethanol, toluene, methyl ethyl ketone and dimethyl formamide, characterized in that it comprises at least one selected from the group consisting of, double-sided tape.
 폴리우레탄 기재층, 상기 폴리우레탄 기재층의 일면에 형성된 제 1 점착층 및 상기 폴리우레탄 기재층의 타면에 형성된 제 2 점착층을 포함하는 양면테이프의 제조방법에 있어서,
상기 폴리우레탄 기재층 형성용 폴리우레탄 조성물과 상기 제 1 점착층 및 상기 제 2 점착층 형성용 점착 조성물을 준비하는 제 1 단계; 및
이형지 상에 상기 폴리우레탄 조성물과 상기 점착 조성물을 도포하고 경화하여 제 1 점착층, 폴리우레탄 기재층 및 제 2 점착층의 순차로 적층된 양면테이프를 형성하는 제 2 단계;를 포함하고,
상기 폴리우레탄 조성물은 폴리우레탄, 메틸에틸케톤 및 다이메틸폼아마이드를 포함하며,
상기 점착 조성물은 염화비닐-비닐아세테이트 공중합체, 에틸 아세테이트, 폴리아크릴아마이드 및 유기용매를 포함하되,
상기 점착 조성물은 상기 염화비닐-비닐아세테이트 공중합체 100 중량부에 대해 상기 에틸 아세테이트 30 ~ 65 중량부, 상기 폴리아크릴아마이드 1 ~ 10 중량부 및 상기 유기용매 40 ~ 100 중량부를 포함하는 것을 특징으로 하는, 양면테이프의 제조방법.In the method of manufacturing a double-sided tape comprising a polyurethane base layer, a first adhesive layer formed on one surface of the polyurethane base layer, and a second adhesive layer formed on the other surface of the polyurethane base layer,
A first step of preparing a polyurethane composition for forming the polyurethane base layer and an adhesive composition for forming the first adhesive layer and the second adhesive layer; And
A second step of applying and curing the polyurethane composition and the adhesive composition on a release paper to form a double-sided tape sequentially stacked with a first adhesive layer, a polyurethane base layer, and a second adhesive layer; Including,
The polyurethane composition includes polyurethane, methyl ethyl ketone and dimethyl formamide,
The adhesive composition includes a vinyl chloride-vinyl acetate copolymer, ethyl acetate, polyacrylamide, and an organic solvent,
The adhesive composition comprises 30 to 65 parts by weight of the ethyl acetate, 1 to 10 parts by weight of the polyacrylamide, and 40 to 100 parts by weight of the organic solvent based on 100 parts by weight of the vinyl chloride-vinyl acetate copolymer. , Method of manufacturing double-sided tape.
KR1020190030458A 2019-03-18 2019-03-18 Double-sided tape for attaching component and method of manufacturing the same KR102176530B1 (en)