KR102132765B1 - The method of making sublimation cut sticker and its method of making using the variable temperature and the transfer method of this cut sticker - Google Patents

The method of making sublimation cut sticker and its method of making using the variable temperature and the transfer method of this cut sticker Download PDF

Info

Publication number
KR102132765B1
KR102132765B1 KR1020190063252A KR20190063252A KR102132765B1 KR 102132765 B1 KR102132765 B1 KR 102132765B1 KR 1020190063252 A KR1020190063252 A KR 1020190063252A KR 20190063252 A KR20190063252 A KR 20190063252A KR 102132765 B1 KR102132765 B1 KR 102132765B1
Authority
KR
South Korea
Prior art keywords
coating layer
sublimation
layer
sticker
temperature
Prior art date
Application number
KR1020190063252A
Other languages
Korean (ko)
Inventor
최윤범
Original Assignee
최윤범
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최윤범 filed Critical 최윤범
Priority to KR1020190063252A priority Critical patent/KR102132765B1/en
Application granted granted Critical
Publication of KR102132765B1 publication Critical patent/KR102132765B1/en

Abstract

The present invention relates to a sublimation transfer cut sticker using thermochromic properties, which is attached to clothes, a cup, and the like to enable a user to form a desired picture, letter, number, and figure and changes color thereof indoors or outdoors in accordance with a temperature change, and a manufacturing method and a transfer method thereof. According to the present invention, the sublimation transfer cut sticker using thermochromic properties comprises: a mixture coating layer (102); a white urethane skin resin coating layer (104) formed on the upper surface of the mixture coating layer (102); a hot melt adhesive layer (106) formed on the upper surface of the white urethane skin resin coating layer (104); a silicone adhesive layer (108) formed on the lower surface of the mixture coating layer (102); and a PET film layer (110) attached to the lower surface of the silicone adhesive layer (108), wherein the mixture coating layer (102) is formed by mixing a transparent liquid white urethane skin resin and thermochromic black pigment.

Description

변온을 이용한 승화전사 컷팅스티커 및 그 제조방법과 이 컷팅스티커의 전사방법{The method of making sublimation cut sticker and its method of making using the variable temperature and the transfer method of this cut sticker}The sublimation cut sticker and its method of making using the variable temperature and the transfer method of this cut sticker}

본 발명은 스티커에 관한 것으로, 보다 상세하게는 의류 또는 컵 등에 부착되어 실외 또는 실내의 온도변화에 따라 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출하는 변온을 이용한 승화전사 컷팅스티커 및 그 제조방법과 이 컷팅스티커의 전사방법에 관한 것이다.The present invention relates to a sticker, and more specifically, a sublimation transcription cutting sticker using a temperature that is attached to clothing or a cup, etc. and changes color according to temperature changes in the outdoor or indoor to express a picture, letter, number, or figure desired by the user. It relates to a manufacturing method and a method of transferring the cutting sticker.

옷에 장식용 스티커를 부착하여 장식하기도 한다. 장식용 스티커는 흔히, 저면에 핫멜트접착제가 도포된 장식필름을 원하는 이미지 형상으로 재단하여 제조된 것과, 스팡글이나 보석들을 부착하여 제조된 것이 있다.It is also decorated by attaching decorative stickers on clothes. Decorative stickers are often manufactured by cutting a decorative film coated with a hot melt adhesive on the bottom to a desired image shape, or by attaching spangles or jewelry.

이 중 장식필름을 원하는 이미지 형상으로 재단하여 제조된 스티커는 도 1에 도시된 바와 같이, 비교적 넓은 면적을 가지는데, 이러한 스티커(2)를 옷에 부착하면, 스티커(2)에 의해 옷의 유연성이 저하되어 뻣뻣한 느낌을 주는 등 착용감이 저하되는 단점이 있다.Among these, the sticker produced by cutting the decorative film into a desired image shape has a relatively large area, as shown in FIG. 1. When this sticker 2 is attached to clothes, the flexibility of the clothes by the sticker 2 There is a disadvantage that the wearing feeling is reduced, such as giving a stiff feeling by being lowered.

그리고, 스팡글을 부착하여 제조된 장식스티커는 도 2에 도시된 바와 같이, 원하는 형상을 형성하도록 작은 크기의 스팡글(4)이 이웃되게 부착되어 제조된다.In addition, the decorative sticker manufactured by attaching the spangles is manufactured by attaching the spangles 4 of small size to be adjacent to form a desired shape, as shown in FIG. 2.

이러한 스티커는 전술한 스티커와 달리 옷의 유연성을 저하시키는 등의 문제점은 없으나, 스팡글(4)을 부착하여 이미지를 형성하는 것이므로 세밀한 형상을 형성하기 곤란할 뿐만 아니라 스팡글(4)들을 배열 부착시키기 위한 고가의 복잡한 장비가 필요한 단점이 있다.Unlike the sticker described above, such a sticker does not have a problem such as deteriorating the flexibility of clothes, but since it forms an image by attaching the spangles 4, it is difficult to form a detailed shape and the spangles 4 are arranged and attached. It has the disadvantage of requiring expensive and complex equipment.

상기 문제점을 해결하기 위해, 2008년 12월 09일자 출원번호 제10-2008-0124795호(발명의 명칭 : 패션용 장식스티커 및 그 제조방법과 이 장식스티커가 부착된 의류)로 특허청에 출원된 바 있으며, 청구범위는 " 청구항 1. 저면에 핫멜트접착제층(12)이 형성된 장식필름원단(10)을 원하는 형상으로 재단하여 장식패치(20)를 만드는 과정과, 상기 장식패치(20)를 베이스시트(30) 상면에 부착하는 과정과, 상기 장식패치(20)를 세절하여 장식패치(20)를 다수개의 세절편(22)으로 분할하는 과정과, 저면에 점착제층(42)이 형성된 픽업필름(40)을 상기 베이스In order to solve the above problems, filed with the Korean Intellectual Property Office on December 09, 2008 with application number 10-2008-0124795 (invention name: decorative sticker for fashion and its manufacturing method and clothing to which the decorative sticker is attached) Claim 1 is a process of making a decorative patch 20 by cutting a decorative film fabric 10 having a hot melt adhesive layer 12 on a bottom surface into a desired shape, and a base sheet of the decorative patch 20. (30) The process of attaching to the upper surface, the process of dividing the decorative patch 20 into pieces and dividing the decorative patch 20 into a plurality of small pieces 22, and a pickup film having an adhesive layer 42 formed on the bottom surface ( 40) above base

시트(30) 상면에 부착하는 과정과, 상기 베이스시트(30)를 제거하는 과정을 포함하여 이루어진 것을 특징으로 하는 패션용 장식스티커의 제조방법. 청구항 2. 제1항에 있어서, 상기 베이스시트(30)는 스폰지로 이루어진 것을 특징으로 하는 패션용 장식스티커의 제조방법. 청구항 3. 제1항 또는 제2항에 있어서, 상기 장식패치(20)를 세절편(22)으로 분할하는 과정에서는 열선으로 장식패치(20)를 분할하여 세절편(22) 사이에 열선에 의해 용융되어 제거된 블랭크라인(24)이 형성된 것을 특징으로 하는 패션용 장식스티커의 제조방법. 청구항 4. 저면에 점착제층(42)이 형성된 픽업필름(40)과, 저면에 핫멜트접착제층(12)이 형성된 장식필름원단(10)을 재단하여 이루어져서 상기 픽업필름(40)의 저면에 부착된 장식패치(20)와, 상기 장식패치(20)와 픽업필름(40)의 저면을 커버하는 박리지(50)를 포함하며, 상기 장식패치(20)는 다수개의 세절편(22)으로 분할된 것을 특징으로 하는 패션용 장식스티커. 청구항 5. 저면에 핫멜트접착제층(12)이 형성된 장식패치(20)가 상기 핫멜트접착제층(12)에 의해 부착된 의류로서, 상기 장식패치(20)는 다수개의 세절편(22)으로 분할된 것을 특징으로 하는 의류. " 이다.A method of manufacturing a decorative sticker for fashion, comprising a process of attaching to the top surface of the sheet 30 and removing the base sheet 30. 2. The method of claim 1, wherein the base sheet (30) is made of a sponge. 3. The method according to claim 1 or 2, wherein in the process of dividing the decorative patch (20) into three pieces (22), the decorative patch (20) is divided into hot wires by means of a hot wire between the three pieces (22). Method of manufacturing a decorative sticker for fashion, characterized in that the blank line 24 is removed by melting. 4. The pick-up film 40 with an adhesive layer 42 formed on the bottom surface and a decorative film fabric 10 with a hot-melt adhesive layer 12 formed on the bottom surface are cut and attached to the bottom surface of the pickup film 40. It includes a decorative patch 20, the decorative patch 20 and a release paper 50 covering the bottom surface of the pickup film 40, the decorative patch 20 is divided into a plurality of small pieces (22) Fashion decorative sticker, characterized in that. 5. The garment patch (12) having a hot melt adhesive layer (12) formed on the bottom surface is a garment attached by the hot melt adhesive layer (12), wherein the decorative patch (20) is divided into a plurality of cut pieces (22). Clothing characterized in that. " to be.

그러나, 상기 종래의 패션용 장식스티커 및 그 제조방법과 이 장식스티커가 부착된 의류는 실외 또는 실내의 온도변화에 따라 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출하지 못하는 문제점이 있었다.However, the conventional fashion decorative sticker and its manufacturing method and the clothing to which the decorative sticker is attached discolor according to the temperature change of the outdoor or indoor, so that there is a problem that a user cannot express a picture, letter, number, or figure desired by the user.

따라서, 본 발명은 상기한 종래 기술에 따른 제반 문제점을 해결하기 위하여 개량발명된 것으로서, 본 발명의 목적은 의류 또는 컵 등에 부착되어 실외 또는 실내의 온도변화에 따라 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출하는 변온을 이용한 승화전사 컷팅스티커 및 그 제조방법과 이 컷팅스티커의 전사방법을 제공하는 데 있다.Accordingly, the present invention has been improved to solve all the problems according to the prior art described above, and the object of the present invention is attached to a garment or cup, etc. to change color according to the temperature change of the outdoor or indoor picture or text desired by the user, It is to provide a sublimation transfer cutting sticker using a variable temperature expressing numbers and figures, a manufacturing method thereof, and a transfer method of the cutting sticker.

그러나 본 발명의 목적은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the object of the present invention is not limited to the above-mentioned object, other objects not mentioned will be clearly understood by those skilled in the art from the following description.

상기한 목적을 달성하기 위한 본 발명에 따른 변온을 이용한 승화전사 컷팅스티커는,Sublimation transcription cutting sticker using the temperature change according to the present invention for achieving the above object,

혼합물도포층(102)과;A mixture coating layer 102;

상기 혼합물도포층(102)의 상면에 형성된 우레탄스킨백색수지도포층(104)과;A urethane skin white resin coating layer 104 formed on the upper surface of the mixture coating layer 102;

상기 우레탄스킨백색수지도포층(104)의 상면에 형성된 핫멜트접착제층(106)과;A hot melt adhesive layer 106 formed on an upper surface of the urethane skin white resin coating layer 104;

상기 혼합물도포층(102)의 저면에 형성된 실리콘접착제층(108)과;A silicone adhesive layer 108 formed on the bottom surface of the mixture coating layer 102;

상기 실리콘접착제층(108)의 저면에 부착된 패트(Pet)필름층(110)을 포함하되,It includes a plastic (Pet) film layer 110 attached to the bottom surface of the silicone adhesive layer 108,

상기 혼합물도포층(102)은 우레탄스킨투명수지액상과 변온검정색안료가 혼합되어 있다.The mixture coating layer 102 is a mixture of a urethane skin transparent resin liquid and a temperature-changing black pigment.

그리고, 상기한 목적을 달성하기 위한 본 발명에 따른 변온을 이용한 승화전사 스티커의 제조방법은,And, a method of manufacturing a sublimation warrior sticker using the temperature change according to the present invention for achieving the above object,

100중량부의 우레탄스킨투명수지액상을 교반기에 투입시킨 후, 상기 교반기에 20중량부의 변온검정색안료를 투입시키고, 교반기를 3분 동작시킨 후, 교반기로부터 100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료가 혼합된 혼합액상물을 얻는 제1단계와;After adding 100 parts by weight of the urethane skin transparent resin liquid phase to the stirrer, 20 parts by weight of the temperature-changing black pigment was added to the stirrer, and after operating the stirrer for 3 minutes, 100 parts by weight of the urethane skin transparent resin liquid phase and 20 parts by weight of the stirrer. A first step of obtaining a mixed liquid substance in which a constant temperature black pigment is mixed;

상기 제1단계 후, 얻어진 혼합액상물을 컨베이어로부터 일정간격을 두고 상측에 설치되어 있는 콤마나이프에 투입시킨 후, 콤마나이프를 동작시켜 콤마나이프에 투입된 혼합액상물을 컨베이어에 위치되어 있는 합지필름(200)의 상면에 1차적으로 도포시켜 우레탄스킨투명수지액상과 변온검정색안료가 혼합되어 있는 혼합물도포층(102)을 얻는 제2단계와;After the first step, the obtained mixed liquid material is put at a predetermined interval from the conveyor into the comman knife installed on the upper side, and then the comb knife is operated to mix the liquid liquid material introduced into the comma knife on the conveyor film ( A second step of firstly applying to the upper surface of 200) to obtain a mixture coating layer 102 in which a urethane skin transparent resin liquid phase and a temperature-changing black pigment are mixed;

상기 제2단계 후, 합지필름(200), 혼합물도포층(102)을 열챔버로 보내어 혼합물도포층(102)에 포함되어 있는 용재를 기화시키고, 열챔버로부터 합지필름(200), 용재가 기화된 혼합물도포층(102)을 얻는 제3단계와;After the second step, the lamination film 200 and the mixture coating layer 102 are sent to a heat chamber to vaporize the solvent contained in the mixture coating layer 102, and the lamination film 200 and the solvent are vaporized from the heat chamber. A third step of obtaining the mixed mixture coating layer 102;

상기 제3단계 후, 우레탄스킨백색수지액상을 위치시키고 우레탄스킨백색수지액상을 혼합물도포층(102)의 상면에 2차적으로 도포시켜 우레탄스킨백색수지도포층(104)을 얻는 제4단계와;After the third step, a fourth step of obtaining a urethane skin white resin coating layer 104 by secondly applying the urethane skin white resin liquid phase to the upper surface of the mixture coating layer 102;

상기 제4단계 후, 핫멜트접착제를 위치시키고 핫멜트접착제를 우레탄스킨백색수지도포층(104)의 상면에 도포시켜 핫멜트접착제층(106)을 얻는 제5단계와;After the fourth step, a fifth step of obtaining a hot melt adhesive layer 106 by placing the hot melt adhesive and applying the hot melt adhesive to the upper surface of the urethane skin white resin coating layer 104;

상기 제5단계 후, 합지필름(200)을 제거시키고 실리콘접착제를 위치시킨 후, 실리콘접착제를 혼합물도포층(102)의 저면에 도포시켜 실리콘접착제층(108)을 얻는 제6단계와;After the fifth step, a sixth step of removing the laminated film 200 and positioning the silicone adhesive, and then applying the silicone adhesive to the bottom surface of the mixture coating layer 102 to obtain a silicone adhesive layer 108;

상기 제6단계 후, 패트필름을 위치시키고 패트필름을 실리콘접착제층(108)의 저면에 부착시켜 패트필름층(110)을 얻는 제7단계를 포함한다.After the sixth step, a seventh step of positioning the plastic film and attaching the plastic film to the bottom surface of the silicone adhesive layer 108 to obtain the plastic film layer 110.

그리고, 상기한 목적을 달성하기 위한 본 발명에 따른 변온을 이용한 승화전사 컷팅스티커의 전사방법은,And, the transfer method of the sublimation transcription cutting sticker using the temperature change according to the present invention for achieving the above object,

이형지의 상면에 의류(300)를 위치시킨 후, 상기 의류(300)의 상면에 혼합물도포층(102), 우레탄스킨백색수지도포층(104), 핫멜트접착제층(106), 실리콘접착제층(108), 패트필름층(110)을 포함한 변온을 이용한 승화전사 스티커(100)를 위치시키되, 의류(300)의 상면에 핫멜트접착제층(106)이 접촉되도록 하는 제1단계와;After placing the garment 300 on the upper surface of the release paper, the mixture coating layer 102, the urethane skin white resin coating layer 104, the hot melt adhesive layer 106, the silicone adhesive layer 108 on the upper surface of the garment 300 ), a first step of positioning the sublimation transfer sticker 100 using the temperature of the change, including the plastic film layer 110, so that the hot melt adhesive layer 106 contacts the upper surface of the garment 300;

상기 제1단계 후, 패트필름층(110)의 저면에 이형지를 위치시키고 열가압부로 이형지를 165℃로 7초 동안 1차 가압시키는 제2단계와;After the first step, a second step of placing the release paper on the bottom surface of the plastic film layer 110 and first pressurizing the release paper at 165° C. for 7 seconds with a heat pressing part;

상기 제2단계 후, 이형지를 제거시킴과 아울러 패트필름층(110)을 제거시킨 후, 사용자가 원하는 그림이나 문자, 숫자, 도형이 도안되어 있는 승화지(400)를 실리콘접착제층(108)의 저면에 위치시키되, 실리콘접착제층(108)의 저면에 승화지(400)의 도안 즉, 정면이 접촉되도록 하는 제3단계와;After the second step, after removing the release paper and removing the plastic film layer 110, a picture, letter, number, or figure desired by the user is printed on the sublimated paper 400 of the silicone adhesive layer 108. A third step of being placed on the bottom surface, such that the design of the sublimation paper 400 is brought into contact with the bottom surface of the silicon adhesive layer 108, that is, the front surface is in contact;

상기 제3단계 후, 승화지(400)의 배면에 이형지를 위치시키고 열가압부로 이형지를 190℃로 30초 동안 2차 가압시켜 승화지(400)의 도안이 변온을 이용한 승화전사 스티커(100)에 전사시키는 제4단계를 포함한다.After the third step, the release paper is placed on the back of the sublimation paper 400, and the release paper is second pressurized to 190° C. for 30 seconds by a heat pressing part, so that the design of the sublimation paper 400 uses sublimation transfer sticker 100 It includes a fourth step of transferring.

이상에서 상술한 바와 같이 본 발명에 따른 변온을 이용한 승화전사 컷팅스티커 및 그 제조방법과 이 컷팅스티커의 전사방법은 의류 또는 컵 등에 부착되어 실외 또는 실내의 온도변화에 따라 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출함으로써, 심미감을 주는 효과가 있다.As described above, the sublimation transfer cutting sticker using the temperature according to the present invention and its manufacturing method and the transfer method of the cutting sticker are attached to clothes or cups, etc., and discolored according to the temperature change in the outdoor or indoor, so that the user can obtain the desired picture or By expressing letters, numbers, and shapes, it has the effect of giving an aesthetic sense.

도 1 내지 도 2는 종래 의류용 스티커를 도시한 도면,
도 3은 본 발명에 따른 제1실시예의 변온을 이용한 승화전사 컷팅스티커를 도시한 도면,
도 4는 도 3의 제1실시예의 변온을 이용한 승화전사 컷팅스티커의 확대 단면도,
도 5는 도 3의 제1실시예의 변온을 이용한 승화전사 컷팅스티커의 제조방법을 개략적으로 도시한 도면,
도 6a 내지 도 6f는 도 3의 제1실시예의 변온을 이용한 승화전사 컷팅스티커의 전사방법을 개략적으로 도시한 도면,
도 7은 본 발명에 따른 제2실시예의 변온을 이용한 승화전사 컷팅스티커를 도시한 도면,
도 8은 도 7의 제2실시예의 변온을 이용한 승화전사 컷팅스티커의 확대 단면도,
도 9는 도 7의 제2실시예의 변온을 이용한 승화전사 컷팅스티커의 제조방법을 개략적으로 도시한 도면,
도 10a 내지 도 10f는 도 7의 제2실시예의 변온을 이용한 승화전사 컷팅스티커의 전사방법을 개략적으로 도시한 도면,
도 11a 내지 도 11d는 도 7의 제2실시예의 변온을 이용한 승화전사 컷팅스티커를 컵의 외면에 부착한 사용 상태를 나타낸 도면이다.1 to 2 is a view showing a conventional clothing sticker,
Figure 3 is a view showing a sublimation transcription cutting sticker using the temperature of the first embodiment according to the present invention,
Figure 4 is an enlarged cross-sectional view of the sublimation transcription cutting sticker using the temperature of the first embodiment of Figure 3,
5 is a view schematically showing a method of manufacturing a sublimation transcription cutting sticker using the temperature of the first embodiment of FIG. 3,
6A to 6F are views schematically showing a method of transferring a sublimation transcription cutting sticker using the temperature of the first embodiment of FIG. 3,
7 is a view showing a sublimation transcription cutting sticker using the temperature of the second embodiment according to the present invention,
Figure 8 is an enlarged cross-sectional view of the sublimation transcription cutting sticker using the temperature of the second embodiment of Figure 7,
9 is a view schematically showing a method of manufacturing a sublimation transcription cutting sticker using the temperature of the second embodiment of FIG. 7,
10A to 10F are views schematically showing a method of transferring a sublimation transcription cutting sticker using the temperature of the second embodiment of FIG. 7;
11A to 11D are views showing a use state in which a sublimation transcription cutting sticker using the temperature of the second embodiment of FIG. 7 is attached to the outer surface of the cup.

이하, 본 발명에 따른 변온을 이용한 승화전사 컷팅스티커 및 그 제조방법과 이 컷팅스티커의 전사방법의 바람직한 실시 예를 설명한다.Hereinafter, a preferred embodiment of a sublimation transfer cutting sticker using the variable temperature according to the present invention and a manufacturing method thereof and a transfer method of the cutting sticker will be described.

하기에서 본 발명을 설명함에 있어서, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다.In the following description of the present invention, when it is determined that a detailed description of related known functions or configurations may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted.

도 3은 본 발명에 따른 제1실시예의 변온을 이용한 승화전사 컷팅스티커를 도시한 도면이고, 도 4는 도 3의 제1실시예의 변온을 이용한 승화전사 컷팅스티커의 확대 단면도이다.3 is a view showing a sublimation transcription cutting sticker using the temperature of the first embodiment according to the present invention, and FIG. 4 is an enlarged cross-sectional view of the sublimation transcription cutting sticker using the temperature of the first embodiment of FIG. 3.

도 3 내지 도 4에 도시된 바와 같이, 본 발명에 따른 제1실시예의 변온을 이용한 승화전사 컷팅스티커(100)는,3 to 4, the sublimation transcription cutting sticker 100 using the temperature of the first embodiment according to the present invention,

혼합물도포층(102)과;A mixture coating layer 102;

상기 혼합물도포층(102)의 상면에 형성된 우레탄스킨백색수지도포층(104)과;A urethane skin white resin coating layer 104 formed on the upper surface of the mixture coating layer 102;

상기 우레탄스킨백색수지도포층(104)의 상면에 형성된 핫멜트접착제층(106)과;A hot melt adhesive layer 106 formed on an upper surface of the urethane skin white resin coating layer 104;

상기 혼합물도포층(102)의 저면에 형성된 실리콘접착제층(108)과;A silicone adhesive layer 108 formed on the bottom surface of the mixture coating layer 102;

상기 실리콘접착제층(108)의 저면에 부착된 패트(Pet)필름층(110)을 포함한다.It includes a plastic (Pet) film layer 110 attached to the bottom surface of the silicone adhesive layer 108.

여기서, 상기 혼합물도포층(102)은 우레탄스킨투명수지액상과 변온검정색안료가 혼합되어 도포된 것이다.Here, the mixture coating layer 102 is a mixture of a urethane skin transparent resin liquid and a temperature-changing black pigment.

상기 우레탄스킨백색수지도포층(104)은 우레탄스킨백색수지액상이 도포된 것이다.The urethane skin white resin coating layer 104 is applied with a urethane skin white resin liquid phase.

상기와 같이 포함된 제1실시예의 변온을 이용한 승화전사 컷팅스티커(100)의 제조방법을 도 5를 참조하여 설명하면 다음과 같다.The manufacturing method of the sublimation transcription cutting sticker 100 using the temperature of the first embodiment included as described above will be described with reference to FIG. 5 as follows.

먼저, 100중량부의 우레탄스킨투명수지액상을 교반기(도시는 생략함)에 투입시킨다.First, 100 parts by weight of a urethane skin transparent resin liquid phase is introduced into a stirrer (not shown).

그리고, 상기 교반기에 20중량부의 변온검정색안료를 투입시키고, 교반기를 3분 동작시킨 후, 교반기로부터 100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료가 혼합된 혼합액상물을 얻는다.Then, 20 parts by weight of the temperature-changing black pigment was added to the stirrer, and after the stirrer was operated for 3 minutes, 100 parts by weight of the urethane skin transparent resin liquid and 20 parts by weight of the temperature-changing black pigment were obtained from the stirrer.

그리고, 상기 얻어진 혼합액상물을 컨베이어(도시는 생략함)로부터 일정간격을 두고 상측에 설치되어 있는 콤마나이프(도시는 생략함)에 투입시킨다.Then, the obtained mixed liquid material is placed at a predetermined interval from a conveyor (not shown) into a comma knife (not shown) installed on the upper side.

그리고, 상기 콤마나이프를 동작시켜 콤마나이프에 투입된 혼합액상물(100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료가 혼합된 것)을 컨베이어에 위치되어 있는 합지필름(200)의 상면에 1차적으로 도포시켜 혼합물도포층(102)을 얻는다.Then, by operating the comma knife, the mixed liquid material (100 parts by weight of a urethane skin transparent resin liquid and 20 parts by weight of a temperature-sensitive black pigment) mixed in the comma knife is placed on the top surface of the lamination film 200 located on the conveyor. It is applied primarily to obtain a mixture coating layer (102).

그리고, 상기 합지필름(200), 혼합물도포층(102)을 열챔버(도시는 생략함)로 보내어 혼합물도포층(102)에 포함되어 있는 용재를 기화시키고, 상기 열챔버로부터 합지필름(200), 용재가 기화된 혼합물도포층(102)을 얻는다.Then, the lamination film 200, the mixture coating layer 102 is sent to a heat chamber (not shown) to vaporize the solvent contained in the mixture coating layer 102, and the lamination film 200 from the heat chamber , A mixture coating layer 102 in which the solvent is vaporized is obtained.

그리고, 우레탄스킨백색수지액상을 위치시킨 후, 상기 우레탄스킨백색수지액상을 혼합물도포층(102)의 상면에 2차적으로 도포시켜 우레탄스킨백색수지도포층(104)을 얻는다.Then, after placing the urethane skin white resin liquid phase, the urethane skin white resin liquid phase is secondarily applied to the upper surface of the mixture coating layer 102 to obtain the urethane skin white resin coating layer 104.

그리고, 핫멜트접착제를 위치시킨 후, 상기 핫멜트접착제를 우레탄스킨백색수지도포층(104)의 상면에 도포시켜 핫멜트접착제층(106)을 얻는다.Then, after positioning the hot melt adhesive, the hot melt adhesive is applied to the upper surface of the urethane skin white resin coating layer 104 to obtain the hot melt adhesive layer 106.

그리고, 상기 합지필름(200)을 제거시키고 실리콘접착제를 위치시킨 후, 실리콘접착제를 혼합물도포층(102)의 저면에 도포시켜 실리콘접착제층(108)을 얻는다.Then, after removing the laminated film 200 and positioning the silicone adhesive, the silicone adhesive is applied to the bottom surface of the mixture coating layer 102 to obtain the silicone adhesive layer 108.

그리고, 패트(Pet)필름을 위치시킨 후, 상기 패트필름을 실리콘접착제층(108)의 저면에 부착시켜 패트필름층(110)을 얻는다.Then, after placing the PET film, the PET film is attached to the bottom surface of the silicone adhesive layer 108 to obtain the PET film 110.

상기와 같이 제조된 제1실시예의 변온을 이용한 승화전사 컷팅스티커의 전사방법을 도 6a 내지 도 6e를 참조하여 설명하면 다음과 같다.The transfer method of the sublimation transfer cutting sticker using the temperature of the first embodiment prepared as described above will be described with reference to FIGS. 6A to 6E.

먼저, 의류(300)를 위치시킨 후, 도 6a에 도시된 바와 같이, 상기 의류(300)의 상면에 혼합물도포층(102), 우레탄스킨백색수지도포층(104), 핫멜트접착제층(106), 실리콘접착제층(108), 패트필름층(110)을 포함한 변온을 이용한 승화전사 스티커(100)를 위치시키되, 의류(300)의 상면에 핫멜트접착제층(106)이 접촉되도록 한다.First, after positioning the garment 300, as shown in Figure 6a, the mixture coating layer 102, the urethane skin white resin coating layer 104, hot melt adhesive layer 106 on the upper surface of the garment 300 , Placing the sublimation transfer sticker 100 using the temperature including the silicone adhesive layer 108 and the plastic film layer 110, so that the hot melt adhesive layer 106 is in contact with the top surface of the clothing (300).

그리고, 상기 패트필름층(110)의 저면에 이형지(도시는 생략함)를 위치시킨 후, 열가압부(도시는 생략함)로 이형지를 165℃로 7초 동안 1차 가압시킨다. 이때, 도 6b에 도시된 바와 같이, 의류(300)의 상면에 변온을 이용한 승화전사 컷팅스티커(100)가 부착됨과 동시에 변색된다.Then, after placing a release paper (not shown) on the bottom surface of the plastic film layer 110, the release paper is first pressurized at 165°C for 7 seconds with a heat press (not shown). At this time, as shown in FIG. 6B, the sublimation warrior cutting sticker 100 using the temperature change is attached to the upper surface of the garment 300 and discolored at the same time.

그리고, 상기 이형지를 제거시킴과 아울러 도 6c에 도시된 바와 같이, 패트필름층(110)을 제거시킨 후, 사용자가 원하는 그림이나 문자, 숫자, 도형이 도안되어 있는 승화지(400)를 실리콘접착제층(108)의 저면에 위치시키되, 도 6d에 도시된 바와 같이, 실리콘접착제층(108)의 저면에 승화지(400)의 도안 즉, 정면이 접촉되도록 한다,In addition, after removing the release paper, as shown in FIG. 6C, after removing the plastic film layer 110, a silicone adhesive is applied to the sublimation paper 400 in which a picture, letter, number, or figure desired by the user is designed. Located on the bottom surface of the layer 108, as shown in Figure 6d, the bottom surface of the silicone adhesive layer 108, so that the design of the sublimation paper 400, that is, the front contact,

그리고, 상기 승화지(400)의 배면에 이형지를 위치시킨 후, 열가압부로 이형지를 190℃로 30초 동안 2차 가압시킨다. 이때, 승화지(400)의 도안이 변온을 이용한 승화전사 스티커(100)에 전사된다(도 6e참조).Then, after placing the release paper on the back surface of the sublimation paper 400, the release paper is secondarily pressurized at 190°C for 30 seconds with a heat press. At this time, the pattern of the sublimation paper 400 is transferred to the sublimation transcription sticker 100 using the temperature change (see FIG. 6E ).

그리고, 상기 이형지를 제거시키고 도 6e에 도시된 바와 같이, 승화지(400)를 제거시킨 후, 냉각시킨다. 상기 냉각에 따라, 도 6f에 도시된 바와 같이, 의류에 부착된 변온을 이용한 승화전사 스티커(100)는 검정색으로 변색된다.Then, after removing the release paper and removing the sublimation paper 400, as shown in FIG. 6E, it is cooled. According to the cooling, as shown in FIG. 6F, the sublimation warrior sticker 100 using the temperature of affix attached to the garment is discolored in black.

한편, 검정색으로 변색된 변온을 이용한 승화전사 컷팅스티커(100)는 실외 또는 실내에서 온도변화에 따라 흰색으로 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출시킨다.On the other hand, the sublimation transcription cutting sticker 100 using the temperature discolored in black discolors to white according to the temperature change in the outdoor or indoor to express the picture, letters, numbers, or shapes desired by the user.

도 7은 본 발명에 따른 제2실시예의 변온을 이용한 승화전사 컷팅스티커를 도시한 도면이고, 도 8은 도 7의 제2실시예의 변온을 이용한 승화전사 컷팅스티커의 확대 단면도이다.7 is a view showing a sublimation transcription cutting sticker using the temperature of the second embodiment according to the present invention, and FIG. 8 is an enlarged cross-sectional view of the sublimation transcription cutting sticker using the temperature of the second embodiment of FIG. 7.

도 7 내지 도 8에 도시된 바와 같이, 본 발명에 따른 제2실시예의 변온을 이용한 승화전사 컷팅스티커(100)는,7 to 8, the sublimation transcription cutting sticker 100 using the temperature change of the second embodiment according to the present invention,

혼합물도포층(102)과;A mixture coating layer 102;

상기 혼합물도포층(102)의 상면에 형성된 우레탄스킨백색수지도포층(104)과;A urethane skin white resin coating layer 104 formed on the upper surface of the mixture coating layer 102;

상기 우레탄스킨백색수지도포층(104)의 상면에 형성된 핫멜트접착제층(106)과;A hot melt adhesive layer 106 formed on an upper surface of the urethane skin white resin coating layer 104;

상기 핫멜트접착제층(106)의 상면에 형성된 유성점착제층(112)과;An oily adhesive layer 112 formed on an upper surface of the hot melt adhesive layer 106;

상기 유성 실리콘접착제층(112)의 상면에 부착된 패트필름층(110)을 포함한다.And a plastic film layer 110 attached to the top surface of the oily silicone adhesive layer 112.

여기서, 상기 혼합물도포층(102)은 우레탄스킨투명수지액상과 변온검정색안료가 혼합되어 도포된 것이다.Here, the mixture coating layer 102 is a mixture of a urethane skin transparent resin liquid and a temperature-changing black pigment.

상기 우레탄스킨백색수지도포층(104)은 우레탄스킨백색수지액상이 도포된 것이다.The urethane skin white resin coating layer 104 is applied with a urethane skin white resin liquid phase.

상기와 같이 포함된 제2실시예의 변온을 이용한 승화전사 컷팅스티커(100)의 제조방법을 도 9를 참조하여 설명하면 다음과 같다.The manufacturing method of the sublimation transcription cutting sticker 100 using the temperature of the second embodiment included as described above will be described with reference to FIG. 9 as follows.

먼저, 100중량부의 우레탄스킨투명수지액상을 교반기(도시는 생략함)에 투입시킨다.First, 100 parts by weight of a urethane skin transparent resin liquid phase is introduced into a stirrer (not shown).

그리고, 상기 교반기에 20중량부의 변온검정색안료를 투입시키고, 교반기를 3분 동작시킨 후, 교반기로부터 100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료가 혼합된 혼합액상물을 얻는다.Then, 20 parts by weight of the temperature-changing black pigment was added to the stirrer, and after the stirrer was operated for 3 minutes, 100 parts by weight of the urethane skin transparent resin liquid and 20 parts by weight of the temperature-changing black pigment were obtained from the stirrer.

그리고, 상기 얻어진 혼합액상물을 컨베이어(도시는 생략함)로부터 일정간격을 두고 상측에 설치되어 있는 콤마나이프(도시는 생략함)에 투입시킨다.Then, the obtained mixed liquid material is placed at a predetermined interval from a conveyor (not shown) into a comma knife (not shown) installed on the upper side.

그리고, 상기 콤마나이프를 동작시켜 콤마나이프에 투입된 혼합액상물(100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료)을 컨베이어에 위치되어 있는 합지필름(200)의 상면에 1차적으로 도포시켜 혼합물도포층(102)을 얻는다.Then, by operating the comma knife, the mixed liquid material (100 parts by weight of urethane skin transparent resin and 20 parts by weight of the temperature-changing black pigment) added to the comma knife is primarily applied to the top surface of the lamination film 200 located on the conveyor. To obtain a mixture coating layer 102.

그리고, 상기 합지필름(200), 혼합물도포층(102)을 열챔버(도시는 생략함)로 보내어 혼합물도포층(102)에 포함되어 있는 용재를 기화시키고, 상기 열챔버로부터 합지필름(200), 용재가 기화된 혼합물도포층(102)을 얻는다.Then, the lamination film 200, the mixture coating layer 102 is sent to a heat chamber (not shown) to vaporize the solvent contained in the mixture coating layer 102, and the lamination film 200 from the heat chamber , A mixture coating layer 102 in which the solvent is vaporized is obtained.

그리고, 우레탄스킨백색수지액상을 위치시킨 후, 상기 우레탄스킨백색수지액상을 혼합물도포층(102)의 상면에 2차적으로 도포시켜 우레탄스킨백색수지도포층(104)을 얻는다.Then, after placing the urethane skin white resin liquid phase, the urethane skin white resin liquid phase is secondarily applied to the upper surface of the mixture coating layer 102 to obtain the urethane skin white resin coating layer 104.

그리고, 핫멜트접착제를 위치시킨 후, 상기 핫멜트접착제를 우레탄스킨백색수지도포층(104)의 상면에 도포시켜 핫멜트접착제층(106)을 얻는다.Then, after positioning the hot melt adhesive, the hot melt adhesive is applied to the upper surface of the urethane skin white resin coating layer 104 to obtain the hot melt adhesive layer 106.

그리고, 상기 합지필름(200)을 제거시키고 유성점착제를 위치시킨 후, 유성점착제를 핫멜트접착제층(106)의 상면에 도포시켜 유성점착제층(112)을 얻는다.Then, after removing the laminated film 200 and positioning the oily adhesive, the oily adhesive is applied to the top surface of the hot melt adhesive layer 106 to obtain the oily adhesive layer 112.

그리고, 패트(Pet)필름을 위치시킨 후, 상기 패트필름을 유성점착제층(112)의 상면에 부착시켜 패트필름층(110)을 얻는다.Then, after positioning the PET film, the PET film is attached to the top surface of the oily adhesive layer 112 to obtain the PET film layer 110.

상기와 같이 제조된 제2실시예의 변온을 이용한 승화전사 컷팅스티커의 전사방법을 도 10a 내지 도 10f를 참조하여 설명하면 다음과 같다.The transfer method of the sublimation transfer cutting sticker using the temperature of the second embodiment prepared as described above will be described with reference to FIGS. 10A to 10F.

먼저, 이형지(도시는 생략함)를 위치시킨 후, 도 10a에 도시된 바와 같이, 상기 이형지의 상면에 혼합물도포층(102), 우레탄스킨백색수지도포층(104), 핫멜트접착제층(106), 유성점착제층(112), 패트필름층(110)을 포함한 변온을 이용한 승화전사 스티커(100)를 위치시키되, 이형지의 상면에 패트필름층(110)이 접촉되도록 한다.First, after placing the release paper (not shown), as shown in FIG. 10A, the mixture coating layer 102, the urethane skin white resin coating layer 104, the hot melt adhesive layer 106 on the upper surface of the release paper , Placing the sublimation transfer sticker 100 using the temperature including the oily adhesive layer 112, the plastic film layer 110, so that the plastic film layer 110 is in contact with the top surface of the release paper.

그리고, 상기 사용자가 원하는 그림이나 문자, 숫자, 도형이 도안되어 있는 승화지(400)를 혼합물도포층(102)의 상면에 위치시키되, 도 10b에 도시된 바와 같이, 혼합물도포층(102)의 상면에 승화지(400)의 도안 즉, 정면이 접촉되도록 한다,Then, the sublimation paper 400 on which a picture, letter, number, or figure desired by the user is designed is placed on the upper surface of the mixture coating layer 102, but as shown in FIG. 10B, the mixture coating layer 102 The pattern of the sublimation paper 400 on the upper surface, that is, to make the front contact,

그리고, 상기 도 10c에 도시된 바와 같이, 승화지(400)의 배면에 이형지를 위치시킨 후, 열가압부로 이형지를 190℃로 30초 동안 가압시킨다. 이때, 승화지(400)의 도안이 변온을 이용한 승화전사 컷팅스티커(100)에 전사된다(도 10e참조).And, as shown in Figure 10c, after placing the release paper on the back surface of the sublimation paper 400, the release paper is pressed at 190° C. for 30 seconds with a heat press. At this time, the pattern of the sublimation paper 400 is transferred to the sublimation transcription cutting sticker 100 using the temperature (see FIG. 10E ).

그리고, 상기 도 10d에 도시된 바와 같이, 이형지를 제거시킨 후, 냉각시킨다. 상기 냉각에 따라, 도 10f에 도시된 바와 같이, 변온을 이용한 승화전사 스티커(100)는 검정색으로 변색된다.Then, as shown in FIG. 10D, the release paper is removed and then cooled. According to the cooling, as shown in FIG. 10F, the sublimation transcription sticker 100 using the change of temperature is discolored in black.

한편, 상기 패트필름층(110)을 제거시킨 후, 컵(도시는 생략함) 등의 물건 외면에 변온을 이용한 승화전사 스티커(100)를 접착시키되, 컵의 외면에 유성점착제층(112)이 부착되도록 한다.On the other hand, after removing the plastic film layer 110, a sublimation transfer sticker 100 using a temperature change is attached to an outer surface of an object such as a cup (not shown), but an oily adhesive layer 112 is applied to the outer surface of the cup. To be attached.

그리고, 검정색으로 변색된 변온을 이용한 승화전사 컷팅스티커(100)는 실외 또는 실내에서 온도변화에 따라 흰색으로 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출시킨다.In addition, the sublimation transcription cutting sticker 100 using the temperature discolored in black discolors to white according to the temperature change in the outdoor or indoor to express a picture, letter, number, or figure desired by the user.

도 11a 내지 도 11d는 도 7의 제2실시예의 변온을 이용한 승화전사 컷팅스티커를 컵의 외면에 부착한 사용 상태를 나타낸 도면으로,11A to 11D are views showing a use state in which the sublimation warrior cutting sticker using the temperature of the second embodiment of FIG. 7 is attached to the outer surface of the cup;

검정색으로 변색된 변온을 이용한 승화전사 컷팅스티커(100)는 실외 또는 실내에서 온도변화에 따라 빨간색으로 변색하여 사용자가 원하는 그림이나 문자, 숫자, 도형을 표출시킨다.The sublimation transcription cutting sticker 100 using the temperature discolored in black discolors in red according to the temperature change in the outdoor or indoor to display the picture, letters, numbers, or shapes desired by the user.

상기 발명의 상세한 설명은 단지 본 발명의 예시적인 것으로서, 이는 단지 본 발명을 설명하기 위한 목적에서 사용된 것이지 의미 한정이나 특허청구범위에 기재된 본 발명의 범위를 제한하기 위하여 사용된 것은 아니다.The detailed description of the invention is merely exemplary of the present invention, which is used for the purpose of describing the present invention only, and is not used to limit the scope of the present invention as defined in the claims or claims.

그러므로 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. 따라서 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다.Therefore, those skilled in the art will understand that various modifications and other equivalent embodiments are possible therefrom. Therefore, the true technical protection scope of the present invention should be determined by the technical spirit of the appended claims.

100 : 변온을 이용한 승화전사 컷팅스키커
102 : 혼합물도포층
104 : 우레탄스킨백색수지도포층
106 : 핫멜트접착제층
108 : 실리콘접착제층
110 : 패트필름층
112 : 유성점착제층
200 : 합지필름
300 : 의류
400 : 승화지100: sublimation warrior cutting skiker using variable temperature
102: mixture coating layer
104: urethane skin white resin coating layer
106: hot melt adhesive layer
108: silicone adhesive layer
110: plastic film layer
112: oily adhesive layer
200: laminated film
300: clothing
400: sublimation paper

Claims (6)

100중량부의 우레탄스킨투명수지액상을 교반기에 투입시킨 후, 상기 교반기에 20중량부의 변온검정색안료를 투입시키고, 교반기를 3분 동작시킨 후, 교반기로부터 100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료가 혼합된 혼합액상물을 얻는 제1단계와;
상기 제1단계 후, 얻어진 혼합액상물을 컨베이어로부터 일정간격을 두고 상측에 설치되어 있는 콤마나이프에 투입시킨 후, 콤마나이프를 동작시켜 콤마나이프에 투입된 혼합액상물을 컨베이어에 위치되어 있는 합지필름(200)의 상면에 1차적으로 도포시켜 우레탄스킨투명수지액상과 변온검정색안료가 혼합되어 있는 혼합물도포층(102)을 얻는 제2단계와;
상기 제2단계 후, 합지필름(200), 혼합물도포층(102)을 열챔버로 보내어 혼합물도포층(102)에 포함되어 있는 용재를 기화시키고, 열챔버로부터 합지필름(200), 용재가 기화된 혼합물도포층(102)을 얻는 제3단계와;
상기 제3단계 후, 우레탄스킨백색수지액상을 위치시키고 우레탄스킨백색수지액상을 혼합물도포층(102)의 상면에 2차적으로 도포시켜 우레탄스킨백색수지도포층(104)을 얻는 제4단계와;
상기 제4단계 후, 핫멜트접착제를 위치시키고 핫멜트접착제를 우레탄스킨백색수지도포층(104)의 상면에 도포시켜 핫멜트접착제층(106)을 얻는 제5단계와;
상기 제5단계 후, 합지필름(200)을 제거시키고 실리콘접착제를 위치시킨 후, 실리콘접착제를 혼합물도포층(102)의 저면에 도포시켜 실리콘접착제층(108)을 얻는 제6단계와;
상기 제6단계 후, 패트필름을 위치시키고 패트필름을 실리콘접착제층(108)의 저면에 부착시켜 패트필름층(110)을 얻는 제7단계를 포함한 것을 특징으로 하는 변온을 이용한 승화전사 컷팅스티커의 제조방법.
After adding 100 parts by weight of the urethane skin transparent resin liquid phase to the stirrer, 20 parts by weight of the temperature-changing black pigment was added to the stirrer, and after operating the stirrer for 3 minutes, 100 parts by weight of the urethane skin transparent resin liquid phase and 20 parts by weight of the stirrer. A first step of obtaining a mixed liquid substance in which a constant temperature black pigment is mixed;
After the first step, the obtained mixed liquid material is put at a predetermined interval from the conveyor into the comman knife installed on the upper side, and then the comb knife is operated to mix the liquid liquid material introduced into the comma knife on the conveyor film ( A second step of firstly applying to the upper surface of 200) to obtain a mixture coating layer 102 in which a urethane skin transparent resin liquid phase and a temperature-changing black pigment are mixed;
After the second step, the lamination film 200 and the mixture coating layer 102 are sent to a heat chamber to vaporize the solvent contained in the mixture coating layer 102, and the lamination film 200 and the solvent are vaporized from the heat chamber. A third step of obtaining the mixed mixture coating layer 102;
After the third step, a fourth step of positioning the urethane skin white resin liquid phase and secondarily applying the urethane skin white resin liquid phase to the upper surface of the mixture coating layer 102 to obtain a urethane skin white resin coating layer 104;
After the fourth step, a fifth step of obtaining a hot melt adhesive layer 106 by placing the hot melt adhesive and applying the hot melt adhesive to the upper surface of the urethane skin white resin coating layer 104;
After the fifth step, a sixth step of removing the laminated film 200 and positioning the silicone adhesive, and then applying the silicone adhesive to the bottom surface of the mixture coating layer 102 to obtain a silicone adhesive layer 108;
After the sixth step, including the seventh step of positioning the plastic film and attaching the plastic film to the bottom surface of the silicone adhesive layer 108 to obtain the plastic film layer 110, the sublimation transfer cutting sticker using temperature. Manufacturing method.
이형지의 상면에 의류(300)를 위치시킨 후, 상기 의류(300)의 상면에 혼합물도포층(102), 우레탄스킨백색수지도포층(104), 핫멜트접착제층(106), 실리콘접착제층(108), 패트필름층(110)을 포함한 변온을 이용한 승화전사 스티커(100)를 위치시키되, 의류(300)의 상면에 핫멜트접착제층(106)이 접촉되도록 하는 제1단계와;
상기 제1단계 후, 패트필름층(110)의 저면에 이형지를 위치시키고 열가압부로 이형지를 165℃로 7초 동안 1차 가압시키는 제2단계와;
상기 제2단계 후, 이형지를 제거시킴과 아울러 패트필름층(110)을 제거시킨 후, 사용자가 원하는 그림이나 문자, 숫자, 도형이 도안되어 있는 승화지(400)를 실리콘접착제층(108)의 저면에 위치시키되, 실리콘접착제층(108)의 저면에 승화지(400)의 도안 즉, 정면이 접촉되도록 하는 제3단계와;
상기 제3단계 후, 승화지(400)의 배면에 이형지를 위치시키고 열가압부로 이형지를 190℃로 30초 동안 2차 가압시켜 승화지(400)의 도안이 변온을 이용한 승화전사 스티커(100)에 전사시키는 제4단계를 포함한 것을 특징으로 하는 변온을 이용한 승화전사 컷팅스티커의 전사방법.
After placing the garment 300 on the upper surface of the release paper, the mixture coating layer 102, the urethane skin white resin coating layer 104, the hot melt adhesive layer 106, the silicone adhesive layer 108 on the upper surface of the garment 300 ), a first step of positioning the sublimation transfer sticker 100 using the temperature of the change, including the plastic film layer 110, so that the hot melt adhesive layer 106 contacts the upper surface of the garment 300;
After the first step, a second step of placing the release paper on the bottom surface of the plastic film layer 110 and first pressurizing the release paper at 165° C. for 7 seconds with a heat pressing part;
After the second step, after removing the release paper and removing the plastic film layer 110, a picture, letter, number, or figure desired by the user is printed on the sublimated paper 400 of the silicone adhesive layer 108. A third step of being placed on the bottom surface, such that the design of the sublimation paper 400 is brought into contact with the bottom surface of the silicon adhesive layer 108, that is, the front surface is in contact;
After the third step, the release paper is placed on the back of the sublimation paper 400, and the release paper is second pressurized to 190° C. for 30 seconds by a heat pressing part, so that the design of the sublimation paper 400 uses sublimation transfer sticker 100 Transfer method of the sublimation transcription cutting sticker using a temperature, characterized in that it comprises a fourth step of transferring.
100중량부의 우레탄스킨투명수지액상을 교반기에 투입시킨 후, 상기 교반기에 20중량부의 변온검정색안료를 투입시키고, 교반기를 3분 동작시킨 후, 교반기로부터 100중량부의 우레탄스킨투명수지액상과 20중량부의 변온검정색안료가 혼합된 혼합액상물을 얻는 제1단계와;
상기 제1단계 후, 얻어진 혼합액상물을 컨베이어로부터 일정간격을 두고 상측에 설치되어 있는 콤마나이프에 투입시킨 후, 콤마나이프를 동작시켜 콤마나이프에 투입된 혼합액상물을 컨베이어에 위치되어 있는 합지필름(200)의 상면에 1차적으로 도포시켜 우레탄스킨투명수지액상과 변온검정색안료가 혼합되어 있는 혼합물도포층(102)을 얻는 제2단계와;
상기 제2단계 후, 합지필름(200), 혼합물도포층(102)을 열챔버로 보내어 혼합물도포층(102)에 포함되어 있는 용재를 기화시키고, 열챔버로부터 합지필름(200), 용재가 기화된 혼합물도포층(102)을 얻는 제3단계와;
상기 제3단계 후, 우레탄스킨백색수지액상을 위치시키고 우레탄스킨백색수지액상을 혼합물도포층(102)의 상면에 2차적으로 도포시켜 우레탄스킨백색수지도포층(104)을 얻는 제4단계와;
상기 제4단계 후, 핫멜트접착제를 위치시키고 핫멜트접착제를 우레탄스킨백색수지도포층(104)의 상면에 도포시켜 핫멜트접착제층(106)을 얻는 제5단계와;
상기 제5단계 후, 합지필름(200)을 제거시키고 유성점착제를 위치시킨 후, 유성점착제를 핫멜트접착제층(106)의 상면에 도포시켜 유성점착제층(112)을 얻는 제6단계와;
상기 제6단계 후, 패트(Pet)필름을 위치시키고 패트필름을 유성점착제층(112)의 상면에 부착시켜 패트필름층(110)을 얻는 제7단계를 포함한 것을 특징으로 하는 변온을 이용한 승화전사 컷팅스티커의 제조방법.
After adding 100 parts by weight of the urethane skin transparent resin liquid phase to the stirrer, 20 parts by weight of the temperature-changing black pigment was added to the stirrer, and after operating the stirrer for 3 minutes, 100 parts by weight of the urethane skin transparent resin liquid phase and 20 parts by weight of the stirrer. A first step of obtaining a mixed liquid substance in which a constant temperature black pigment is mixed;
After the first step, the obtained mixed liquid material is placed at a predetermined interval from the conveyor, and then put into a comma knife installed on the upper side, and then the comb knife is operated to put the mixed liquid material introduced into the comma knife into a laminated film located on the conveyor ( A second step of firstly applying to the upper surface of 200) to obtain a mixture coating layer 102 in which a urethane skin transparent resin liquid phase and a temperature-changing black pigment are mixed;
After the second step, the lamination film 200 and the mixture coating layer 102 are sent to a heat chamber to vaporize the solvent contained in the mixture coating layer 102, and the lamination film 200 and the solvent are vaporized from the heat chamber. A third step of obtaining the mixed mixture coating layer 102;
After the third step, a fourth step of obtaining a urethane skin white resin coating layer 104 by secondly applying the urethane skin white resin liquid phase to the upper surface of the mixture coating layer 102;
After the fourth step, a fifth step of obtaining a hot-melt adhesive layer 106 by placing the hot-melt adhesive and applying the hot-melt adhesive to the upper surface of the urethane skin white resin coating layer 104;
After the fifth step, after removing the laminated film 200 and positioning the oily adhesive, a sixth step of obtaining an oily adhesive layer 112 by applying the oily adhesive to the top surface of the hot melt adhesive layer 106;
After the sixth step, a sublimation warrior using a variable temperature, comprising a seventh step of positioning the PET film and attaching the PET film to the top surface of the oil-based adhesive layer 112 to obtain the PET film layer 110. Method for manufacturing cutting sticker.
이형지를 위치시킨 후, 상기 이형지의 상면에 혼합물도포층(102), 우레탄스킨백색수지도포층(104), 핫멜트접착제층(106), 유성점착제층(112), 패트필름층(110)을 포함한 변온을 이용한 승화전사 스티커(100)를 위치시키되, 이형지의 상면에 패트필름층(110)이 접촉되도록 하는 제1단계와;
상기 제1단계 후 사용자가 원하는 그림이나 문자, 숫자, 도형이 도안되어 있는 승화지(400)를 혼합물도포층(102)의 상면에 위치시키되, 혼합물도포층(102)의 상면에 승화지(400)의 도안 즉, 정면이 접촉되도록 하는 제2단계와;
상기 제2단계 후, 승화지(400)의 배면에 이형지를 위치시키고 열가압부로 이형지를 190℃로 30초 동안 가압시켜 승화지(400)의 도안이 변온을 이용한 승화전사 스티커(100)에 전사시키는 제3단계를 포함한 것을 특징으로 하는 변온을 이용한 승화전사 컷팅스티커의 전사방법.
After placing the release paper, the mixture coating layer 102, the urethane skin white resin coating layer 104, the hot melt adhesive layer 106, the oily adhesive layer 112, the plastic film layer 110 on the upper surface of the release paper A first step of positioning a sublimation transcript sticker 100 using variable temperature and allowing the plastic film layer 110 to contact the top surface of the release paper;
After the first step, the sublimation paper 400 on which the user desires a picture, letter, number, or figure is designed is placed on the upper surface of the mixture coating layer 102, but the sublimation paper 400 is placed on the upper surface of the mixture coating layer 102. ), that is, the second step of making the front contact;
After the second step, the release paper is placed on the back surface of the sublimation paper 400, and the release paper is pressed to 190° C. for 30 seconds by a heat pressing part, so that the design of the sublimation paper 400 is transferred to the sublimation transcription sticker 100 using temperature. A transfer method of a sublimation transcription cutting sticker using a constant temperature, characterized in that it comprises a third step.
삭제delete 삭제delete
KR1020190063252A 2019-05-29 2019-05-29 The method of making sublimation cut sticker and its method of making using the variable temperature and the transfer method of this cut sticker KR102132765B1 (en)