KR102083764B1 - Composite plate that is improved adsorption performance of antimicrobial, antifungal, and harmful substances - Google Patents
Composite plate that is improved adsorption performance of antimicrobial, antifungal, and harmful substances Download PDFInfo
- Publication number
- KR102083764B1 KR102083764B1 KR1020190105518A KR20190105518A KR102083764B1 KR 102083764 B1 KR102083764 B1 KR 102083764B1 KR 1020190105518 A KR1020190105518 A KR 1020190105518A KR 20190105518 A KR20190105518 A KR 20190105518A KR 102083764 B1 KR102083764 B1 KR 102083764B1
- Authority
- KR
- South Korea
- Prior art keywords
- powder
- pvc
- parts
- weight
- mixture
- Prior art date
Abstract
Description
본 발명은 건축물등의 마감재로 사용되는 조개분말을 함유한 복합 판재에 관한 것으로, 보다 상세하게는 종래의 아파트와 같은 주거용이나 사무실과 같은 상업용 건축물 마감재 시공시, 바닥재, 벽재, 천정재 등에 사용되는 조개분말을 함유한 복합 판재로서, 특정한 처리가 된 조개분말을 일정 비율로 사용함으로써, 친환경적이면서 우수한 항균 및 항곰팡이 효과를 나타내며, 내열성/내한성, 단열성, 방음성이 우수하고, 탈취효과를 가지며 더불어 준 불연성이고, 유해가스를 배출하지 않는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재에 관한 것이다.The present invention relates to a composite plate containing a shell powder used as a finishing material for buildings, and more particularly used in the construction of commercial building finishes such as residential or office, such as apartments, flooring, walls, ceilings, etc. As a composite plate containing clam powder, by using a certain ratio of clam powder treated in a certain ratio, it is environmentally friendly and shows excellent antibacterial and antifungal effects, excellent heat resistance / cold resistance, heat insulation, sound insulation, deodorizing effect and The present invention relates to a composite plate which is incombustible and does not emit harmful gases and has improved antibacterial, antifungal and harmful substance adsorption performance.
통상적으로 건축물의 바닥이나 벽체를 장식하거나 미려하게 마감하기 위하여 다양화된 마감재 패널을 사용하는데, 이러한 마감재 패널들은 목재, 합판, MDF, HDF, PB, PVC 중에서 선택된 재질이나 혹은 이들의 혼합물 또는 다양한 화합물질의 재질로 이루어지며, 또한 마감재 패널 상호 간의 조립을 용이하게 하거나 시공성을 향상시키기 위해 마감재 패널의 측면에 특정한 기계적 체결요소를 구비하거나 접착제 등의 보조적인 고정 장치를 사용하고 있으며, 이러한 마감재들의 소재들 중에서 목질 섬유판(MDF, HDF)을 기재로 하고, 상부에 무늬가 인쇄된 모양지층과 모양지층의 보호를 위하여 산화알루미늄이 적층된 이른바 라미네이트 판재가 사용되고 있다. 이와 같은 라미네이트 판재는 내마모성, 내구성 등이 우수하고, 미려한 무늬를 표현하고 평활한 평면을 유지하는데 적합하여 오랫동안 건축자재 시장에서 소비자들로부터 가장 많은 관심을 받아 왔다. Typically, a variety of finish panels are used to decorate or beautifully decorate the floor or wall of a building, which may be selected from wood, plywood, MDF, HDF, PB, PVC, or mixtures of these or various compounds. It is made of quality materials and also has a special mechanical fastening element on the side of the finish panel or uses an auxiliary fixing device such as an adhesive to facilitate assembly between the finish panels or improve workability. Among them, so-called laminate boards are used, in which wood fiber boards (MDF, HDF) are used as a base material, and aluminum oxide is laminated for protection of the pattern paper layer on which the pattern is printed and the pattern paper layer. Such laminate boards have been attracting the most attention from consumers in the building materials market for a long time because they are excellent in abrasion resistance and durability, and are suitable for expressing a beautiful pattern and maintaining a flat plane.
그런데, 상기 마감재의 기재를 형성하는 HDF는 아무리 밀도가 높아도 목질 섬유와 목질 섬유를 결합시키기 위하여 통상적으로 사용하는 수지들은 근본적으로 수분의 침투를 저지할 수가 없는 단점이 있어, 마감재를 연결한 틈 혹은 마감재의 측면 사이로 수분이 침투하면 목질 섬유로 이루어진 판넬의 기재가 부풀어 본래의 형상을 상실하고 마감재의 외형이 변하는 문제점이 있을 뿐만아니라, 이러한 문제점을 최소화하기 위해 사용되는 접착제 등의 성분으로 되는 포름알데히드, 톨루엔 등과 같은 유해화학 물질을 사용하는 문제점이 있었다. By the way, the HDF forming the base material of the finishing material, no matter how dense, the resins commonly used to combine wood fibers and wood fibers can not fundamentally prevent the penetration of moisture, the gap connecting the finish material or If moisture penetrates between the sides of the finishing material, the base material of the panel made of wood fiber swells and loses its original shape, and the appearance of the finishing material changes, as well as formaldehyde, which is a component such as an adhesive used to minimize such problems. There was a problem using hazardous chemicals such as toluene and the like.
따라서, 이러한 문제점을 해결하기 위해, 대한민국 특허등록번호 제10-1722537호(특허문헌 1)에서는 WPC(Wood Plastic Compotision)계 친환경 소재를 제공하기 위한 것으로, "층간소음을 감소시키고 보행감을 향상시키도록 코르크 재질로 형성되는 흡음층; 상기 흡음층 상면에 적층되고, 상기 흡음층의 물성을 보강하고 균형과 강도를 높여주며 긴밀하게 적층되도록 접착력을 구비하는 제1 패드층; 상기 제1 패드층 상면에 적층되고, 물에 대한 내성이 있는 방수재질로 형성되는 방수보드층; 상기 방수보드층 상면에 적층되고, 상기 방수보드층의 물성을 보강하고 균형과 강도를 높여주며 긴밀하게 적층되도록 접착력을 구비하는 제2 패드층; 상기 제2 패드층 상면에 적층되고, 상면에는 나무 질감 및 무늬 연출이 가능한 표면장식층; 상기 표면 장식층 상면에 적층되고, 상기 표면 장식층 상면에 연출되는 나무 질감 및 무늬를 표현하고, 외부 충격 및 방수가 가능하도록 투명 시트형태로 형성되는 표면보호층;을 포함하여 바닥재 보드가 서로 연접하여 형성되되, 상기 흡음층은 상기 제1 패드층과 긴밀한 접착을 위해 상면에 다수개의 격자 홈을 형성하는 것을 특징으로 하는 다기능 마루 바닥재"를 개시하고 있다.Therefore, to solve this problem, Korean Patent Registration No. 10-1722537 (Patent Document 1) is to provide a WPC (Wood Plastic Compotision) -based eco-friendly material, "to reduce the noise between floors and improve the feeling of walking A sound absorbing layer formed of a cork material, a first pad layer laminated on an upper surface of the sound absorbing layer, the first pad layer having an adhesive force to reinforce the physical properties of the sound absorbing layer, increasing balance and strength, and closely stacking the upper surface of the first pad layer; A waterproof board layer laminated and formed of a waterproof material resistant to water, laminated on an upper surface of the waterproof board layer, reinforcing physical properties of the waterproof board layer, improving balance and strength, and providing adhesion to be closely stacked; A second pad layer laminated on an upper surface of the second pad layer, a surface decoration layer on which a wood texture and a pattern are produced, and laminated on an upper surface of the surface decoration layer A surface protection layer is formed in the form of a transparent sheet so as to represent the texture and pattern of the wood to be produced on the upper surface of the decorative surface layer, and the flooring board is formed in contact with each other, including the sound-absorbing layer The multi-functional flooring flooring "is characterized in that a plurality of lattice grooves are formed on the upper surface for close adhesion with the first pad layer.
한편, WPC계 판재는 많은 장점에도 불구하고 상기와 같이 수분에 취약하다는 문제가 있으며, 따라서 이를 보완하기 위한 물질로서 SPC(Solid Plastic Composite 또는 Stone Plastic Composite)계 바닥재 원료가 제안되었는데, 이는 천연 석회암 분말과 폴리비닐염화물로 구성되어 친환경적이다. 또한, 수축 팽창율 시험을 위한 6시간 80℃ 시험 결과에서 WPC 바닥재의 경우 0.40% 였지만 SPC계의 경우 0.06% 미만이며, 내구성이 좋고 내화성이 우수하고, 열전달 효율이 우수하다는 장점이 있다. On the other hand, WPC-based plate material has a problem that it is vulnerable to moisture as described above in spite of many advantages, so SPC (Solid Plastic Composite or Stone Plastic Composite) -based flooring material has been proposed as a material to compensate for this, which is a natural limestone powder It is composed of polyvinyl chloride and environmentally friendly. In addition, 6 hours 80 ℃ test results for shrinkage expansion rate test was 0.40% in the case of WPC flooring, but less than 0.06% in the SPC system, has the advantages of good durability, excellent fire resistance, and excellent heat transfer efficiency.
다른 한편, 일반인에게 주거용 건축물의 건축 자재로 황토 판재도 제안되어 왔는데, 황토는 많은 량의 원적외선을 방사하여 생체내의 분자를 자극하여 활성화시킴으로써 생체를 보온하고, 체내 독소인 과산화지질을 중화시키고, 생물체 내에서 부패한 세포를 분해시키는 효능을 가지고 있다는 과학적으로 입증된 황토의 효능을 이용하는 것으로서, 최근에는 황토를 건축물 마감재로 사용하려는 시도가 상기 설명한 바와 같은 다양한 분야에서 다양하게 이루어지고 있다.On the other hand, ocher boards have been proposed to the general public as building materials for residential buildings, which emits large amounts of far-infrared rays to stimulate and activate molecules in the body, thereby warming the body, neutralizing lipid peroxide, a toxin in the body, and In order to use the efficacy of scientifically proven loess, which has the effect of decomposing decayed cells within, recent attempts to use loess as a building finishing material have been made in various fields as described above.
그러나 이와 같은 통상적인 황토 제품은 시공 후에 갈라짐 현상이 많이 발생하여 시공 면에서 쉽게 떨어져 나갈 뿐만 아니라 시공이 불편한 등의 단점이 있어 이에 대한 해결책으로 황토와 백시멘트 또는 황토와 수지 접착제와 혼합된 제품들을 사용하고 있는데, 이러한 제품들은 결국 인체에 유해한 벤젠, 톨로엔, 클로로포름, 아세톤, 포름알데히드 등의 발암물질을 배출시켜 바람직하지 않다. However, such a common ocher product has many disadvantages such as easy separation from the construction surface after construction, and it is inconvenient to install. As a solution to this, ocher and back cement or products mixed with ocher and resin adhesive are used. In the end, these products release undesirable carcinogens such as benzene, toloene, chloroform, acetone and formaldehyde, which are harmful to humans.
따라서, 이러한 문제점을 해결하기 위한 제안이 다수 있는데, 예를 들면, 대한민국 특허등록번호 제10-1811857호(특허문헌 3)에서는, "황토층; 바다머드 및 생강 추출액을 포함하는 머드 내부층; 및 바다머드 및 조개 패각 입자를 포함하는 머드 표면층; 이 순차적으로 적층된 바다머드를 이용한 적층체"의 구성을 개시하고, 이러한 구성의 적층체는 다양한 건강 증진 효과들이 인체에 효과적으로 흡수 및 적용될 수 있는 장점이 있으며, 우수한 방열 특성을 가져 연료비를 최소화할 수 있는 효과가 있다고 개시하고 있다.Therefore, there are a number of proposals to solve this problem, for example, Korean Patent Registration No. 10-1811857 (Patent Document 3), "ocher layer; mud inner layer containing sea mud and ginger extract; and sea Mud surface layer comprising mud and shell shell particles; the laminate using the sequentially laminated sea mud ", the laminate of this configuration has the advantage that various health promoting effects can be effectively absorbed and applied to the human body In addition, it has been disclosed that there is an effect that can minimize the fuel cost by having excellent heat dissipation characteristics.
그런데, 상기한 특허문헌들에 개시된 발명을 포함하여, 종래의 방법들은 통상적으로 수지들을 사용하여 제조되는 패널은 포름할데하이드의 방출을 피할 수가 없거나, 소재의 특성상 편평도를 유지하는데 불리하거나, 내마모성, 내구성 등의 물성이 떨어지거나, 미세한 크랙이 잘 발생하는 등의 강도가 약하다는 등의 각각의 문제점을 안고 있었다.By the way, including the invention disclosed in the above-mentioned patent documents, conventional methods are usually disadvantageous to maintain the flatness due to the nature of the material, or the panel produced by using the resin can not avoid the release of formaldehyde, Each of them had problems such as poor physical properties such as durability and poor cracking.
따라서, 본 발명자는 상기한 바와 같이 종래에 제안된 각종 바닥재의 문제점을 해결할 수 있는 방법에 대해 예의 연구한 결과, 특정한 처리가 된 조개분말을 일정 비율로 사용하므로 친환경성이고, 우수한 항균작용효과를 나타내며, 내열성, 내한성, 단열성, 방음성이 우수하고, 탈취효과를 가지며 더불어 준 불연성이고 유해가스를 배출을 최소화하는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 조개분말을 함유한 복합 판재의 구성과 그 제조방법을 밝혀내어 본 발명을 완성하게 되었다.Therefore, the present inventors earnestly researched how to solve the problems of the conventionally proposed various flooring as described above, because the use of a specific treated shell powder at a certain ratio is environmentally friendly, excellent antibacterial effect It is composed of composite plate containing clam powder with excellent heat resistance, cold resistance, heat insulation, sound insulation, deodorizing effect, quasi-incombustibility and improved antibacterial, anti-fungal, and adsorption of harmful substances. The manufacturing method was discovered and the present invention was completed.
따라서, 본 발명은 상기한 종래의 실정을 감안하여 상기 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 내열성, 내한성, 단열성, 방음성이 우수하면서, 환경 친화적이면서 항균 및 항곰팡이 작용효과와 탈취효과가 우수하여 건축물 등의 마감재로 사용될 수 있는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재를 제공하기 위한 것이다.Therefore, the present invention is to solve the above problems in view of the above-mentioned conventional situation, the object of the present invention is excellent in heat resistance, cold resistance, heat insulation, sound insulation, environmentally friendly, antibacterial and anti-fungal action and deodorizing effect It is excellent to provide a composite board that improves the antibacterial, anti-fungal, harmful substances adsorption performance that can be used as a finishing material for buildings.
본 발명의 다른 목적은 상기한 특성과 더불어 난연성이면서 또한 유해가스를 배출하지 않는 건축물 등의 마감재로 사용될 수 있는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재를 제공하기 위한 것이다.Another object of the present invention is to provide a composite plate with improved antibacterial, anti-fungal, harmful substance adsorption performance that can be used as a finishing material, such as a flame retardant and does not emit harmful gases in addition to the above characteristics.
본 발명은 또한 상기한 명확한 목적 이외에 이러한 목적 및 본 명세서의 전반적인 기술로부터 이 분야의 통상인에 의해 용이하게 도출될 수 있는 다른 목적을 달성함을 그 목적으로 할 수 있다.The present invention may also be directed to achieving these and other objects which can be readily derived by one of ordinary skill in the art from the general description herein.
이와 같은 목적을 달성하기 위한 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재는, 탄산칼슘(CaCO3) 분말을 주재로 함유하고, 상기 주재에 부가하여 조개 분말, 벤토나이트 (bentonite), 운모 (mica), 고령토 (kaolin), 옥분, 및 (i)PVC(Poly Vinyl Chloride) 레진 분말, (ii)폴리유산 (poly lactic acid; PLA), (iii)PVC(Poly Vinyl Chloride) 레진 분말 및 폴리유산 (poly lactic acid; PLA) 혼합물 중에서 선택되는 하나의 물질을 포함하여 구성된 것임을 특징으로 한다.In order to achieve the above object, the composite plate having improved antibacterial, anti-fungal and harmful substance adsorption performance includes calcium carbonate (CaCO3) powder as a main material, and in addition to the main material, shell powder, bentonite, mica ( mica, kaolin, jade, and (i) Poly Vinyl Chloride resin powder, (ii) poly lactic acid (PLA), (iii) Poly Vinyl Chloride resin powder and polylactic acid (poly lactic acid; PLA) is characterized in that it comprises a material selected from the mixture.
또한, 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재는, 탄산칼슘(CaCO3)분말 55 내지 65 중량부와 조개분말 25 내지 35 중량부를 각각 고속 혼합기에서 균질하게 배합한 후, 상기 배합물에 벤토나이트 (bentonite), 운모 (mica) 및 고령토 (kaolin)를 각각 2 내지 3 중량부로 공급하여 혼합하고, 상기 혼합물에 옥분을 0.5 내지 1.5 중량부의 범위로 혼합하고, 상기 혼합물에 대해 7 내지 10 중량부 비율의 범위 내에서 (i)PVC(Poly Vinyl Chloride) 레진 분말, (ii)폴리유산 (poly lactic acid; PLA), (iii)PVC(Poly Vinyl Chloride) 레진 분말 및 폴리유산 (poly lactic acid; PLA) 혼합물 중에서 선택되는 하나의 물질을 공급하여 배합하고 반죽하고, 상기 배합하여 얻은 반죽물을 소정 형상의 압출기를 이용하여 판재로 압출 성형하여 제조되는 것을 특징으로 한다.In addition, the composite plate with improved antibacterial, anti-fungal, harmful substance adsorption performance, after mixing 55 to 65 parts by weight of calcium carbonate (CaCO3) powder and 25 to 35 parts by weight of shellfish powder, respectively, in a high-speed mixer, Bentonite, mica and kaolin are fed at 2 to 3 parts by weight, respectively, mixed with the mixture, 0.5 to 1.5 parts by weight of octane, and 7 to 10 parts by weight of the mixture. (I) Poly Vinyl Chloride Resin Powder, (ii) Poly Lactic Acid (PLA), (iii) Poly Vinyl Chloride Resin Powder and Poly Lactic Acid (PLA) 1) A material selected from the mixture is supplied, compounded and kneaded, and the obtained kneaded product is manufactured by extrusion molding into a plate using an extruder having a predetermined shape.
상술한 바와 같이 구성되는 본 발명에 따른 항균, 항곰팡이, 유해물질 흡착성능을 개선한 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재는 특정한 처리가 된 조개분말을 일정 비율로 사용하여 제조된 마감재를 제공함으로써, 친환경적이면서 설치공간을 쾌적한 실내공간으로 유지시켜줄 수 있습니다.Antimicrobial, anti-mold, and harmful substances according to the present invention constituted as described above, antibacterial, anti-mold, improved composite material improved the adsorption of harmful substances produced by using a specific ratio of shellfish powder treated By providing a finished material, it is possible to keep the installation space eco-friendly and comfortable.
또한, 내열성, 내한성, 단열성 및 방음성이 우수하고, 탈취효과를 가지며 더불어 준 난연성이고 유해가스를 최소화시킬 수 있어, 종래의 바닥재에 있어서의 제반 문제점을 해결하였다. In addition, it is excellent in heat resistance, cold resistance, heat insulation and soundproofing, has a deodorizing effect and can be quasi-flammable and minimize the harmful gas, thereby solving all the problems in the conventional flooring.
도 1은 본 발명의 바람직한 실시형태에 따른 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재의 제조 공정을 보여주는 플로우 챠트이다.1 is a flow chart showing a manufacturing process of a composite plate with improved antibacterial, antifungal, harmful substance adsorption performance according to a preferred embodiment of the present invention.
본 발명은 그 기술적 사상 또는 주요한 특징으로부터 벗어남이 없이 다른 여러 가지 형태로 실시될 수 있다. 따라서, 본 발명의 실시예들은 모든 점에서 단순한 예시에 지나지 않으며 한정적으로 해석되어서는 안된다.The invention can be embodied in many different forms without departing from the spirit or main features thereof. Accordingly, the embodiments of the present invention are merely examples in all respects and should not be construed as limiting.
제 1, 제 2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. Terms such as first and second may be used to describe various components, but the components should not be limited by the terms.
상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. The terms are used only for the purpose of distinguishing one component from another.
예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제 1 구성요소는 제 2 구성요소로 명명될 수 있고, 유사하게 제 2 구성요소도 제 1 구성요소로 명명될 수 있다. For example, without departing from the scope of the present invention, the first component may be referred to as the second component, and similarly, the second component may also be referred to as the first component.
어떤 구성요소가 다른 구성요소에 "연결되어" 있다거나 "접속되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. When a component is said to be "connected" or "connected" to another component, it may be directly connected to or connected to that other component, but it may be understood that another component may be present in the middle. Should be.
반면에, 어떤 구성요소가 다른 구성요소에 "직접 연결되어" 있다거나 "직접 접속되어" 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.On the other hand, when a component is said to be "directly connected" or "directly connected" to another component, it should be understood that there is no other component in between.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting of the present invention. Singular expressions include plural expressions unless the context clearly indicates otherwise.
본 출원에서, "포함하다" 또는 "구비하다", "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.In this application, the terms "comprise", "comprise", "have", etc., are intended to indicate that there is a feature, number, step, operation, component, part, or combination thereof described in the specification, one Or other features or numbers, steps, operations, components, components or combinations thereof, or those in combination thereof should not be excluded in advance.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art.
일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Terms such as those defined in the commonly used dictionaries should be construed as having meanings consistent with the meanings in the context of the related art, and shall not be construed in ideal or excessively formal meanings unless expressly defined in this application. Do not.
이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 본 발명의 가장 바람직한 실시형태를 첨부된 도면을 참조로 하여 상세히 설명하기로 한다.DETAILED DESCRIPTION Hereinafter, the most preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. .
도 1은 본 발명의 바람직한 실시형태에 따른 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재의 제조 공정을 보여주는 플로우 챠트이고, 도 2는 본 발명의 바람직한 실시형태에 따라 제조된 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재에 대한 시험결과를 나타내는 시험성적서의 사본이다.1 is a flow chart showing the manufacturing process of the composite plate improved the antibacterial, anti-fungal, harmful substances adsorptive performance according to a preferred embodiment of the present invention, Figure 2 is an antibacterial, anti-fungal prepared according to a preferred embodiment of the present invention This is a copy of the test report showing the test results for composite plates with improved mold and harmful substance adsorption performance.
도 1에 도시된 바와 같이, 본 발명의 바람직한 실시형태에 따른 본 발명의 건축물 등의 마감재에서 사용될 수 있는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재는, 탄산칼슘(CaCO3) 분말을 주재로 함유하고, 상기 주재에 부가하여 조개 분말, 벤토나이트 (bentonite), 운모 (mica), 고령토 (kaolin), 옥분 및 PVC(Poly Vinyl Chloride) 레진 분말로 구성될 수 있다.As shown in Figure 1, the composite plate improved the antibacterial, anti-fungal, harmful substances adsorption performance that can be used in the finishing material of the building of the present invention according to a preferred embodiment of the present invention, calcium carbonate (CaCO3) powder It is contained as a main material, and in addition to the main material, it may be composed of clam powder, bentonite, mica, kaolin, jade powder and poly vinyl chloride (PVC) resin powder.
이렇게 구성되는 본 발명의 건축물 등의 마감재에서 사용될 수 있는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재의 제조방법은, 탄산칼슘(CaCO3)분말 55 내지 65 중량부와 조개분말 25 내지 35 중량부를 각각 고속 혼합기에서 균질하게 배합하는 배합단계; 상기 배합단계의 배합물에 벤토나이트 (bentonite), 운모 (mica) 및 고령토 (kaolin)를 각각 2 내지 3 중량부로 공급하여 혼합하는 혼합단계; 상기 혼합단계에서 얻어진 혼합물에 옥분을 0.5 내지 1.5 중량부의 범위로 부가 후 혼합하는 옥분 혼합 단계; 상기 옥분 혼합 단계를 통해 얻어진 혼합물에 대해 7 내지 10 중량부 비율의 범위 내에서 PVC(Poly Vinyl Chloride) 레진 분말을 공급하여 배합하고 반죽하는 반죽단계; 상기 반죽단계에서 얻은 PVC(Poly Vinyl Chloride) 레진 분말이 혼합된 조개분말 혼합물을 소정 형상의 압출기를 이용하여 판재로 압출 성형하는 성형단계; 및 성형 공정에서 얻어진 판재를 소정 규격으로 절단하는 절단단계를 포함하여 이루어진다.The manufacturing method of the composite plate improved the antibacterial, anti-fungal, harmful substances adsorption performance that can be used in the finishing materials of the building and the like of the present invention is composed of 55 to 65 parts by weight of calcium carbonate (CaCO3) powder and 25 to 35 shellfish powder A blending step of uniformly blending the parts by weight in a high speed mixer respectively; A mixing step of supplying bentonite, mica, and kaolin to 2 to 3 parts by weight, respectively, to the blend of the blending step; Oxygen mixing step of mixing after adding the jade powder in the range of 0.5 to 1.5 parts by weight to the mixture obtained in the mixing step; A kneading step of supplying, blending and kneading the PVC (Poly Vinyl Chloride) resin powder within a range of 7 to 10 parts by weight with respect to the mixture obtained through the mixing of the jade powder; A molding step of extruding the clam powder mixture in which the PVC (poly vinyl chloride) resin powder obtained in the kneading step is mixed into a plate using an extruder having a predetermined shape; And a cutting step of cutting the sheet material obtained in the molding process to a predetermined standard.
본 발명의 다른 바람직한 실시형태에 따르면, PVC(Poly Vinyl Chloride) 레진 분말을 배합할때 일정량의 PVC 안정제를 사용하는 것이 바람직하다.According to another preferred embodiment of the present invention, it is preferable to use a certain amount of PVC stabilizer when compounding the PVC (Poly Vinyl Chloride) resin powder.
여기서, PVC 안정제는 완성된 제품의 사용기간 중 수지의 물리적, 화학적 성질을 유지하도록 도와주는 화합물이다. 플라스틱의 혼합 및 제조 등의 조작은 고온에서 이루어지기 때문에 첨가제의 보호 없이는 심하게 분해된다. 가격이 저렴하고 가공성이 우수해 범용 플라스틱으로 다양한 용도에서 사용되고 있는 PVC는 열에 약한 단점이 있어 이를 보완하기 위해 열안정제가 사용되고 있다. 열안정제는 형태에 따라 분말, 액상, PASTE, GRANULE 안정제로 분류되며 성상에 의해 Cd/Ba/Zn계, Cd/Ba계, Ba/Zn계, Ca/Zn계, Na/Zn계, Sn계, Pb계, Cd계, Zn계로 나눌 수 있다. Here, PVC stabilizers are compounds that help to maintain the physical and chemical properties of the resin during the life of the finished product. Since operations such as mixing and manufacturing of plastics are performed at high temperatures, they are severely decomposed without the protection of additives. PVC, which is used for various purposes as a general purpose plastic because of its low price and excellent processability, has a weak disadvantage in heat, and heat stabilizers are used to compensate for this. Thermal stabilizers are classified into powder, liquid, PASTE, and GRANULE stabilizers according to their form and are characterized by Cd / Ba / Zn based, Cd / Ba based, Ba / Zn based, Ca / Zn based, Na / Zn based, Sn based, It can be divided into Pb system, Cd system and Zn system.
본 발명의 바람직한 실시형태에 따라 부가되는 상기 벤토나이트, 운모 및 고령토를 각각 2 내지 3 중량부로 하는 것이 가장 바람직한데 이 범위를 벗어나면 천연소재 느낌을 부여하기 어려울 뿐만 아니라 성형성, 강도 등을 저해하는 문제점이 있어 바람직하지 않다.Most preferably, the bentonite, mica and kaolin added according to a preferred embodiment of the present invention are 2 to 3 parts by weight, respectively. Outside of this range, it is difficult to impart a feeling of natural material but also impairs moldability, strength and the like. There is a problem, which is not desirable.
본 발명의 다른 바람직한 실시형태에 따르면, 상기 옥분은 쌀과 서속(黍粟, 기장과 조)을 3:2로 배합한 후 분쇄하여 얻어진 분말에 옥돌가루를 10 중량부 미만의 비율로 부가하여 얻어진 것으로, 이러한 옥분을 본 발명에 따른 비율로 함유함으로써 표면의 미려한 색상이 보다 고급스럽게 나타나고, 이에 부가하여 구성성분 간의 결속을 강화하여 마감재를 한층 고급스럽게 하면서 강도를 증진시키는 작용효과를 제공할 수 있다.According to another preferred embodiment of the present invention, the jade powder is obtained by mixing rice and sorghum (속, millet and crude) in a ratio of 3: 2, and then adding jade powder at a ratio of less than 10 parts by weight to the powder obtained by grinding. By containing such jade powder in a ratio according to the present invention, the beautiful color of the surface appears more luxuriously, and in addition, it is possible to enhance the binding between the components to provide an effect of enhancing the strength while further enhancing the finish. .
본 발명의 또 다른 바람직한 실시형태에 따르면, 상기 조개분말은 조개껍질을 1,700 내지 1,900℃의 온도에서 소성한 후 그라인딩한 것을 사용하고, 더욱 바람직하게는 상기 조개분말은 조개껍질을 1,700 내지 1,900℃의 온도에서 소성하고 그라인딩한 후 체질하여 0.07 내지 0.20mm 입자 사이즈의 조개분말만을 분별하여 사용할 수 있다. According to another preferred embodiment of the present invention, the shell powder is used by grinding the shell after firing at a temperature of 1,700 to 1,900 ℃, more preferably the shell powder of the shell shell 1,700 to 1,900 ℃ After sintering and grinding at the temperature, the sieved may be used to fractionate only shell powder having a particle size of 0.07 to 0.20 mm.
만일 조개껍질의 소성 온도가 상기 온도를 벗어나 너무 높으면 강도가 급격히 저하하고 반대로 너무 낮으면 제조된 제품의 질감이 현저히 떨어져 바람직하지 않다. 또한, 본 발명에 따라 사용될 수 있는 조개껍질은 특정한 것에 한정되지 않고 어떠한 것이라도 사용될 수 있다.If the firing temperature of the shell is too high outside the above temperature, the strength is sharply lowered. On the contrary, if the firing temperature of the clam shell is too low, the texture of the manufactured product is significantly lowered, which is undesirable. In addition, the clam shell which can be used according to the present invention is not limited to a specific one, and any one may be used.
또한, 조개껍질 분말의 입자 사이즈가 0.07mm 이하로 되면 너무 미분으로 되어 원하는 강도를 얻기 힘들며, 0.20mm 이상으로 되면 접촉 촉감이 떨어져 바람직하지 않다.In addition, when the particle size of the clam shell powder is 0.07 mm or less, it becomes too fine to obtain a desired strength, and when it is 0.20 mm or more, the contact feel is poor, which is not preferable.
본 발명의 또 다른 바람직한 실시형태에 따르면, 상기 옥분 혼합 단계를 통해 얻어진 혼합물에 대해 7 내지 10 중량부 비율의 범위 내에서 PVC(Poly Vinyl Chloride) 레진 분말을 공급하여 배합하고 반죽하는 반죽단계에서, 상기 PVC(Poly Vinyl Chloride) 레진 분말 대신에 또는 이와 함께 폴리유산 (poly lactic acid; PLA)을 사용할 수 있다.According to another preferred embodiment of the present invention, in the kneading step of supplying, blending and kneading a PVC (Poly Vinyl Chloride) resin powder in a range of 7 to 10 parts by weight with respect to the mixture obtained through the mixing of the jade powder, Polylactic acid (PLA) may be used instead of or in conjunction with the polyvinyl chloride resin powder.
본 발명에 따라 사용되는 폴리유산 수지는 락타이드 또는 락트산의 열가소성 폴리에스테르로서, 옥수수, 감자 등의 재생 가능한 식물 자원에서 추출한 전분을 발효시켜 제조되는 락트산을 중합시켜 제조될 수 있는 것으로, PVC(Poly Vinyl Chloride) 레진 분말과 같은 작용효과를 나타낸다. The polylactic acid resin used according to the present invention is a thermoplastic polyester of lactide or lactic acid, and may be prepared by polymerizing lactic acid produced by fermenting starch extracted from renewable plant resources such as corn and potatoes. Vinyl Chloride) has the same effect as resin powder.
이와 같이 본 발명에 따라 사용되는 PVC(Poly Vinyl Chloride) 레진 분말과 폴리유산 수지는 사용 또는 폐기 과정에서 이산화탄소 등의 환경 유해 물질의 배출량이 다른 석유계 소재에 비해 월등히 적고, 폐기 시에도 자연 환경 하에서 용이하게 분해될 수 있는 친환경적인 특성을 가진다.As described above, polyvinyl chloride resin and polylactic acid resin (PVC) resins and polylactic acid resins used according to the present invention have significantly lower emissions of environmentally harmful substances such as carbon dioxide during use or disposal, compared to other petroleum-based materials. It has environmentally friendly properties that can be easily decomposed.
본 발명의 또 다른 바람직한 실시형태에 따르면, 상기 본 발명의 성형단계는 이 기술분야의 통상인에게 공지된 일반적인 공정에 의해 달성될 수 있는데, 예를 들어 본 발명의 성형단계는 압출 성형단계로 구성될 수 있는데, 이는 얻어진 혼합물을 가열시킨 후 압출기를 이용하여 용이하게 원하는 판재형상으로 성형하는 것이 가능하다.According to another preferred embodiment of the present invention, the molding step of the present invention can be achieved by a general process known to those skilled in the art, for example, the molding step of the present invention is composed of an extrusion molding step This can be accomplished by heating the resulting mixture and then easily shaping it into the desired plate shape using an extruder.
더욱이, 본 발명의 또 다른 바람직한 실시형태에 따르면, 상기 본 발명의 절단단계 또한 이 기술분야의 통상인에게 공지된 일반적인 공정에 의해 달성될 수 있으며, 특정한 방식에 한정되지 않는다.Moreover, according to another preferred embodiment of the present invention, the cutting step of the present invention may also be accomplished by a general process known to those skilled in the art, and is not limited to a specific manner.
이하, 본 발명을 바람직한 실시예에 의해 보다 자세히 설명하지만, 본 발명이 이들 예시된 실시예에 한정되는 것이 아님은 물론이다.Hereinafter, the present invention will be described in more detail with reference to preferred embodiments, but the present invention is not limited to these illustrated embodiments.
실시예 1Example 1
조개껍질을 1,800℃에서 1시간 소성하고 분쇄한 후 체질하여 0.07 내지 0.20mm 입자 사이즈의 조개분말 30kg과 탄산칼슘(CaCO3) 분말 60kg을 고속 혼합기에서 균질하게 배합하고, 여기에 벤토나이트 2kg, 운모 2kg 및 고령토 2kg을 동시에 공급하여 혼합하였다. The shell is calcined at 1,800 ° C. for 1 hour, pulverized and sieved, and 30 kg of clam powder with a particle size of 0.07 to 0.20 mm and 60 kg of calcium carbonate (CaCO 3) are homogeneously blended in a high-speed mixer, and 2 kg of bentonite, 2 kg of mica and 2 kg of kaolin were fed simultaneously and mixed.
그런 다음, 상기 얻어진 혼합물에 옥분을 1kg을 부가 후, 약 10분간 혼합한 후 PVC(Poly Vinyl Chloride) 레진 분말 6kg과 PVC 안정제 1kg을 공급하여 배합하고 반죽하였다. Then, 1 kg of jade was added to the mixture, and then mixed for about 10 minutes. Then, 6 kg of PVC (Poly Vinyl Chloride) resin powder and 1 kg of PVC stabilizer were supplied, mixed, and kneaded.
그런 다음 반죽단계에서 얻은 PVC 레진이 혼합된 조개분말 반죽물을 일정한 형상의 압출기를 이용하여 판재 형태로 압출 성형하고, 소정 규격으로 절단하여 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재를 얻었다.Then, the shell material dough mixed with the PVC resin obtained in the kneading step is extruded into a plate shape using an extruder having a predetermined shape, and cut into a predetermined size to produce a composite plate that improves the antibacterial, antifungal and harmful substance adsorption performance. Got it.
실시예 2Example 2
조개껍질을 1,800℃에서 1시간 소성하고 분쇄한 후 체질하여 0.07 내지 0.20mm 입자 사이즈의 조개분말 30kg과 탄산칼슘(CaCO3) 분말 60kg을 고속 혼합기에서 균질하게 배합하고, 여기에 벤토나이트 2kg, 운모 2kg 및 고령토 2kg을 동시에 공급하여 혼합하였다. The shell is calcined at 1,800 ° C. for 1 hour, pulverized and sieved, and 30 kg of clam powder having a particle size of 0.07 to 0.20 mm and 60 kg of calcium carbonate (CaCO 3) are homogeneously mixed in a high-speed mixer, and 2 kg of bentonite, 2 kg of mica and 2 kg of kaolin were fed simultaneously and mixed.
그런 다음, 상기 얻어진 혼합물에 옥분을 1kg을 부가 후, 약 10분간 혼합한 후 폴리유산 6kg, PVC 안정제 1kg을 공급하여 배합하고 반죽하였다. Then, 1 kg of jade was added to the mixture, and then mixed for about 10 minutes. Then, 6 kg of polylactic acid and 1 kg of a PVC stabilizer were supplied, mixed and kneaded.
그런 다음 반죽단계에서 얻은 PVC 레진이 혼합된 조개분말 반죽물을 일정한 형상의 압출기를 이용하여 판재 형태로 압출 성형하고, 소정 규격으로 절단하여 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재를 얻었다.Then, the shell material dough mixed with the PVC resin obtained in the kneading step is extruded into a plate shape using an extruder having a predetermined shape, and cut into a predetermined size to produce a composite plate that improves the antibacterial, antifungal and harmful substance adsorption performance. Got it.
실시예 3Example 3
조개껍질을 1,800℃에서 1시간 소성하고 분쇄한 후 체질하여 0.07 내지 0.20mm 입자 사이즈의 조개분말 30kg과 탄산칼슘(CaCO3) 분말 60kg을 고속 혼합기에서 균질하게 배합하고, 여기에 벤토나이트 2kg, 운모 2kg 및 고령토 2kg을 동시에 공급하여 혼합하였다. The shell is calcined at 1,800 ° C. for 1 hour, pulverized and sieved, and 30 kg of clam powder with a particle size of 0.07 to 0.20 mm and 60 kg of calcium carbonate (CaCO 3) are homogeneously blended in a high-speed mixer, and 2 kg of bentonite, 2 kg of mica and 2 kg of kaolin were fed simultaneously and mixed.
그런 다음, 상기 얻어진 혼합물에 옥분을 1kg을 부가 후, 약 10분간 혼합한 후 PVC(Poly Vinyl Chloride) 레진 분말 6kg을 공급하여 배합하고 반죽하였다. Then, 1 kg of jade was added to the obtained mixture, followed by mixing for about 10 minutes, and then fed with 6 kg of PVC (Poly Vinyl Chloride) resin powder to mix and knead.
그런 다음 반죽단계에서 얻은 PVC 레진이 혼합된 조개분말 반죽물을 일정한 형상의 압출기를 이용하여 판재 형태로 압출 성형하고, 소정 규격으로 절단하여 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재를 얻었다.Then, the shell material dough mixed with the PVC resin obtained in the kneading step is extruded into a plate shape using an extruder having a predetermined shape, and cut into a predetermined size to produce a composite plate that improves the antibacterial, antifungal and harmful substance adsorption performance. Got it.
비교예 1Comparative Example 1
상기 실시예 1에서 탄산칼슘(CaCO3) 분말을 사용하지 않는 것을 제외하고는 실시예 1과 동일하게 실시하여 복합 판재를 얻었다.Except not using the calcium carbonate (CaCO3) powder in Example 1 was carried out in the same manner as in Example 1 to obtain a composite plate.
비교예 2Comparative Example 2
상기 실시예 1에서 벤토나이트를 사용하지 않는 것을 제외하고는 실시예 1과 동일하게 실시하여 복합 판재를 얻었다.Except not using the bentonite in Example 1 was carried out in the same manner as in Example 1 to obtain a composite plate.
비교예 3Comparative Example 3
상기 실시예 1에서 운모를 사용하지 않는 것을 제외하고는 실시예 1과 동일하게 실시하여 복합 판재를 얻었다.Except not using mica in Example 1, it was carried out in the same manner as in Example 1 to obtain a composite plate.
비교예 4Comparative Example 4
상기 실시예 1에서 고령토를 사용하지 않는 것을 제외하고는 실시예 1과 동일하게 실시하여 복합 판재를 얻었다.Except not using kaolin in Example 1 was carried out in the same manner as in Example 1 to obtain a composite plate.
본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 상기 설명된 구현예에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.The invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth above, but various modifications and improvements of those skilled in the art using the basic concepts of the invention as defined in the following claims are also within the scope of the present invention. It belongs to.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
Claims (5)
상기 옥분은 쌀과 서속(黍粟, 기장과 조)을 3:2로 배합한 후 분쇄하여 얻어진 분말에 옥돌가루를 10 중량부 미만의 비율로 부가하여 얻어지는 것임을 특징으로 하는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재.
Containing calcium carbonate (CaCO3) powder as a main material, in addition to the main material, clam powder, bentonite, mica, kaolin, jade powder, and (i) Polyvinyl Chloride resin powder, (ii) a polylactic acid (PLA), (iii) a polyvinyl chloride (PVC) resin powder and a polylactic acid (PLA) mixture.
The jade powder is obtained by adding jade powder in a ratio of less than 10 parts by weight to a powder obtained by pulverizing after mixing rice and seosok (기, millet and crude) in a 3: 2 antibacterial, anti-fungal, harmful Composite plate with improved material adsorption performance.
상기 PVC(Poly Vinyl Chloride) 레진 분말의 배합시 일정량의 PVC 안정제를 사용하며, 상기 PVC 안정제는 분말, 액상, PASTE, GRANULE 안정제 중에서 선택되는 임의의 하나의 물질인 것을 특징으로 하는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재.
The method of claim 1,
When the PVC (Poly Vinyl Chloride) resin powder is mixed with a certain amount of PVC stabilizer, the PVC stabilizer is an antibacterial, anti-mildew, characterized in that any one selected from powder, liquid, PASTE, GRANULE stabilizer, Composite plate with improved adsorption of harmful substances.
상기 옥분은 쌀과 서속(黍粟, 기장과 조)을 3:2로 배합한 후 분쇄하여 얻어진 분말에 옥돌가루를 10 중량부 미만의 비율로 부가하여 얻어지는 것을 특징으로 하는 항균, 항곰팡이, 유해물질 흡착성능을 개선한 복합 판재.55 to 65 parts by weight of calcium carbonate (CaCO3) powder and 25 to 35 parts by weight of shellfish powder are respectively homogeneously blended in a high speed mixer, and then bentonite, mica and kaolin are respectively added to the mixture in 2 to 3 parts. 3 parts by weight of the mixture is mixed, mixed with jade powder in the range of 0.5 to 1.5 parts by weight, and (i) Poly Vinyl Chloride (PVC) resin powder in the range of 7 to 10 parts by weight of the mixture, ( ii) polylactic acid (PLA), (iii) polyvinyl chloride (PVC) resin powder and polylactic acid (PLA), a material selected from a mixture of the mixture is supplied, compounded and kneaded, the formulation The dough is obtained is produced by extrusion molding into a plate using an extruder of a predetermined shape,
The jade powder is obtained by adding jade powder in a ratio of less than 10 parts by weight to a powder obtained by pulverizing after mixing rice and seosok (黍 粟, millet and crude) in a 3: 2 antibacterial, anti-fungal, harmful Composite plate with improved material adsorption performance.