KR102000540B1 - Glue composition and detachable beauty tool using the same - Google Patents

Glue composition and detachable beauty tool using the same Download PDF

Info

Publication number
KR102000540B1
KR102000540B1 KR1020180089704A KR20180089704A KR102000540B1 KR 102000540 B1 KR102000540 B1 KR 102000540B1 KR 1020180089704 A KR1020180089704 A KR 1020180089704A KR 20180089704 A KR20180089704 A KR 20180089704A KR 102000540 B1 KR102000540 B1 KR 102000540B1
Authority
KR
South Korea
Prior art keywords
weight
parts
coating layer
glue coating
glue
Prior art date
Application number
KR1020180089704A
Other languages
Korean (ko)
Inventor
박찬인
Original Assignee
박찬인
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박찬인 filed Critical 박찬인
Priority to KR1020180089704A priority Critical patent/KR102000540B1/en
Application granted granted Critical
Publication of KR102000540B1 publication Critical patent/KR102000540B1/en

Abstract

The present invention relates to a glue composition and a detachable beauty tool using the same. The beauty tool comprises: a beauty tool body; and a glue coating layer disposed directly on the beauty tool body. In addition, in an initial state, the glue coating layer is in a dried state without adhesive force, and the glue coating layer has the adhesive force in the state where water is provided to the glue coating layer.

Description

글루 조성물 및 이를 이용한 탈부착식 미용 도구{GLUE COMPOSITION AND DETACHABLE BEAUTY TOOL USING THE SAME}GLUE COMPOSITION AND DETACHABLE BEAUTY TOOL USING THE SAME}

본 발명은 글루 조성물 및 이를 이용한 탈부착식 미용 도구에 관한 것으로서, 보다 상세하게는 우수한 접착력을 가지면서도 반복 사용에도 접착력 저하가 최소화된 글루 조성물 및 이를 이용한 탈부착식 미용 도구에 관한 것이다.The present invention relates to a glue composition and a detachable cosmetic tool using the same, and more particularly, to a glue composition and a detachable cosmetic tool using the same, which has excellent adhesion and minimizes a decrease in adhesion even in repeated use.

속눈썹(eyelash)은 눈의 가장자리에 나 있는 길이 10mm 정도의 경모(硬毛)로, 위아래의 눈꺼풀에 군생하여 먼지 등의 이물로부터 인간의 안구를 보호하는 역할을 한다. 뿐만 아니라 풍성하고 진한 속눈썹은 인간의 눈을 더욱 돋보이게 할 수 있다. 이러한 미용 상의 이유로 인조 속눈썹(artificial eyelash) 또는 가속눈썹이라 불리우는 미용 도구가 개발된 바 있다.Eyelashes are 10mm long hairs on the edges of the eyes, which grow on the upper and lower eyelids to protect the human eye from foreign objects such as dust. In addition, rich and dark eyelashes can make the human eye stand out. For these cosmetic reasons, a beauty tool called artificial eyelash or accelerated eyelash has been developed.

인조 속눈썹은 인조 모발 내지는 사람의 모발로 만들어진 속눈썹 형상의 미용 도구를 의미한다. 일반적으로 인조 속눈썹은 인간의 속눈썹이 난 안검(eye-lid)에 상응하는 긴 호형의 모주(毛柱)와 상기 모주에 결합된 다수의 속눈썹 세모(細毛)를 포함하여 인간의 속눈썹과 같은 형상을 모사하도록 구성되어 있다. 상기 인조 속눈썹은 접착제 또는 접착 테이프 등의 접착 부재를 이용하여 긴 호형의 모주를 안검에 직접 부착하여 사용하는 실정이다. False eyelashes means an eyelash-shaped beauty tool made of artificial hair or human hair. Generally, false eyelashes have the shape of a human eyelash including a long arc hairline corresponding to the eye-lid of a human eyelash and a plurality of eyelash hairs coupled to the hairline. It is configured to simulate. The false eyelashes are used by directly attaching a long arc-shaped column to the eyelid using an adhesive member such as an adhesive or an adhesive tape.

사용자의 안검과 인조 속눈썹을 고정시키는 접착 부재의 접착능은 매우 중요한 요소가 될 수 있다. 예를 들어, 접착 부재의 접착력이 지나치게 강하면 인조 속눈썹을 분리할 때에 사용자에게 통증을 유발하거나, 사용자의 자연 속눈썹을 훼손시킬 수 있어 적절하지 못하다. 뿐만 아니라, 인조 속눈썹을 고정하기 위한 접착 부재는 사용자의 피부에 직접 부착되기 때문에 접착 부재의 접착력이 지나치게 강할 경우 사용자의 피로를 유발하거나 사용자의 피부에 유해한 영향을 줄 수 있다.Adhesion of the adhesive member for fixing the user's eyelid and false eyelashes may be a very important factor. For example, if the adhesive force of the adhesive member is too strong, it may cause pain to the user when separating the false eyelashes, or damage the user's natural eyelashes, which is not appropriate. In addition, since the adhesive member for fixing the artificial eyelashes is directly attached to the skin of the user, if the adhesive force of the adhesive member is too strong, it may cause fatigue of the user or harmful effects on the skin of the user.

반면, 접착 부재의 접착력이 충분하지 못하면 인조 속눈썹 자체의 자중에 의해 인조 속눈썹의 고정이 충분한 시간동안 지속되지 못하거나, 사용자의 눈물 등의 이물에 의해 접착력이 저하되는 문제가 있다. On the other hand, if the adhesive force of the adhesive member is not sufficient, the fixing of the artificial eyelashes by the self-weight of the artificial eyelashes itself does not last for a sufficient time, or there is a problem that the adhesive strength is lowered by foreign objects such as tears of the user.

또한 종래의 접착 부재는 사용자의 피부로부터 탈착될 경우 접착력을 대부분 상실하여 인조 속눈썹의 재사용이 곤란하며, 한번 탈착된 인조 속눈썹을 재사용하기 위해서는 접착제를 다시 도포하여 사용자의 안검에 부착해야 하기 때문에 그 사용이 번거롭다. 이러한 이유 때문에 사용자는 하루에도 수 개의 인조 속눈썹을 사용해야 하는 실정이다.In addition, the conventional adhesive member loses most of the adhesive strength when it is detached from the user's skin, so it is difficult to reuse the artificial eyelashes, and in order to reuse the artificial eyelashes once removed, the adhesive must be reapplied and attached to the user's eyelids. This is cumbersome For this reason, users need to use several false eyelashes a day.

이에 본 발명이 해결하고자 하는 과제는 쉽게 탈부착이 가능하고, 수 회의 재사용이 가능한 탈부착식 미용 도구를 제공하는 것이다.The problem to be solved by the present invention is to provide a detachable cosmetic tools that can be easily removable, can be reused several times.

본 발명이 해결하고자 하는 다른 과제는 쉽게 탈부착이 가능하고, 수 회의 재사용이 가능한 탈부착식 미용 도구를 준비하기 위한 글루 조성물을 제공하는 것이다.Another problem to be solved by the present invention is to provide a glue composition for preparing a detachable cosmetic tools that can be easily removable, can be reused several times.

본 발명의 과제들은 이상에서 언급한 기술적 과제로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The objects of the present invention are not limited to the above-mentioned technical problem, and other technical problems not mentioned will be clearly understood by those skilled in the art from the following description.

상기 과제를 해결하기 위한 본 발명의 일 실시예에 따른 탈부착식 미용 도구는, 미용 도구 바디 및 상기 미용 도구 바디 상에 직접 배치된 글루 코팅층을 포함하는 탈부착식 미용 도구로서, 초기 상태에서, 상기 글루 코팅층은 점착력을 갖지 않고 건조된 상태이고, 상기 글루 코팅층에 수분이 제공된 상태에서, 상기 글루 코팅층은 점착력을 갖는다.Detachable beauty tools according to an embodiment of the present invention for solving the above problems, as a removable beauty tools including a beauty coating body and a glue coating layer disposed directly on the beauty tools body, in the initial state, the glue The coating layer is in a dry state without adhesiveness, and in a state in which water is provided to the glue coating layer, the glue coating layer has adhesive force.

상기 미용 도구 바디는, 호형의 모주 및 상기 모주로부터 돌출된 다수의 세모를 포함하고, 상기 미용 도구는 인조 속눈썹일 수 있다.The cosmetic tool body may include an arc-shaped hairline and a plurality of hairs protruding from the hairline, and the hairdressing tool may be an artificial eyelash.

또, 상기 글루 코팅층은, 100 중량부의 고분자 단백질 물질; 60 중량부 이상 80 중량부 이하의 저분자 다당류 물질; 15 중량부 이상 25 중량부 이하의 고분자 다당류 물질; 및 90 중량부 이상 110 중량부 이하의 알코올성 물질을 포함할 수 있다.In addition, the glue coating layer, 100 parts by weight of a polymer protein material; At least 60 parts by weight and at most 80 parts by weight of low molecular weight polysaccharide material; 15 parts by weight to 25 parts by weight of a polymer polysaccharide material; And 90 parts by weight or more and 110 parts by weight or less of alcoholic material.

또한, 상기 고분자 단백질 물질은 젤라틴을 포함하고, 상기 저분자 다당류 물질은 덱스트린을 포함하며, 상기 고분자 다당류 물질은 아라비아 검 또는 잔탄 검을 포함하고, 상기 알코올성 물질은 글리세롤을 포함할 수 있다.In addition, the high molecular protein material may include gelatin, the low molecular weight polysaccharide material may include dextrin, the high molecular weight polysaccharide material may include gum arabic or xanthan gum, and the alcoholic material may include glycerol.

또는, 상기 글루 코팅층은, 100 중량부의 아크릴레이트계 화합물; 20 중량부 이상 30 중량부 이하의 폴리비닐알코올계 화합물 또는 우레탄계 화합물; 및 1.0 중량부 이상 5.0 중량부 이하의 가용화제를 포함할 수 있다.Alternatively, the glue coating layer, 100 parts by weight of the acrylate compound; 20 parts by weight or more and 30 parts by weight or less of a polyvinyl alcohol compound or a urethane compound; And 1.0 part by weight or more and 5.0 parts by weight or less.

상기 다른 과제를 해결하기 위한 본 발명의 일 실시예에 따른 글루 조성물은 100 중량부의 고분자 단백질 물질; 60 중량부 이상 80 중량부 이하의 저분자 다당류 물질; 15 중량부 이상 25 중량부 이하의 고분자 다당류 물질; 및 90 중량부 이상 110 중량부 이하의 알코올성 물질을 포함한다.Glue composition according to an embodiment of the present invention for solving the other problem is 100 parts by weight of a polymer protein material; At least 60 parts by weight and at most 80 parts by weight of low molecular weight polysaccharide material; 15 parts by weight to 25 parts by weight of a polymer polysaccharide material; And at least 90 parts by weight and at most 110 parts by weight of alcoholic material.

상기 글루 조성물은 1.0 중량부 이상 5.0 중량부 이하의 올리브 리퀴드를 더 포함할 수 있다.The glue composition may further include an olive liquid of 1.0 parts by weight or more and 5.0 parts by weight or less.

상기 다른 과제를 해결하기 위한 본 발명의 다른 실시예에 따른 글루 조성물은 100 중량부의 아크릴레이트계 화합물; 20 중량부 이상 30 중량부 이하의 폴리비닐알코올계 화합물 또는 우레탄계 화합물; 및 1.0 중량부 이상 5.0 중량부 이하의 가용화제를 포함한다.Glue composition according to another embodiment of the present invention for solving the other problems is 100 parts by weight of the acrylate compound; 20 parts by weight or more and 30 parts by weight or less of a polyvinyl alcohol compound or a urethane compound; And 1.0 part by weight or more and 5.0 parts by weight or less.

기타 실시예의 구체적인 사항들은 상세한 설명에 포함되어 있다.Specific details of other embodiments are included in the detailed description.

본 발명의 실시예들에 따르면 탈부착이 가능하고 사용자에게 우수한 착용감을 줄 수 있는 미용 도구를 제공할 수 있다.According to embodiments of the present invention it is possible to provide a beauty tool that can be detachable and give an excellent fit to the user.

본 발명의 실시예들에 따른 효과는 이상에서 예시된 내용에 의해 제한되지 않으며, 더욱 다양한 효과들이 본 명세서 내에 포함되어 있다.Effects according to embodiments of the present invention are not limited by the contents exemplified above, and more various effects are included in the present specification.

도 1은 본 발명의 일 실시예에 따른 탈부착식 미용 도구를 나타낸 도면이다.
도 2는 도 1의 점선 영역을 확대한 확대도이다.1 is a view showing a removable beauty tool according to an embodiment of the present invention.
FIG. 2 is an enlarged view illustrating the dotted line region of FIG. 1.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.Advantages and features of the present invention and methods for achieving them will be apparent with reference to the embodiments described below in detail with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but may be implemented in various forms, and only the embodiments are provided to make the disclosure of the present invention complete, and those of ordinary skill in the art to which the present invention pertains. It is provided to fully inform the scope of the invention, and the invention is defined only by the scope of the claims.

공간적으로 상대적인 용어인 '아래(below)', '아래(beneath)', '하부(lower)', '위(above)', '상부(upper)' 등은 도면에 도시되어 있는 바와 같이 하나의 소자 또는 구성 요소들과 다른 소자 또는 구성 요소들과의 상관관계를 용이하게 기술하기 위해 사용될 수 있다. 공간적으로 상대적인 용어는 도면에 도시되어 있는 방향에 더하여 사용시 소자의 서로 다른 방향을 포함하는 용어로 이해되어야 한다. 예를 들면, 도면에 도시되어 있는 소자를 뒤집을 경우, 다른 소자의 '아래(below 또는 beneath)'로 기술된 소자는 다른 소자의 '위(above)'에 놓일 수 있다. 따라서, 예시적인 용어인 '아래'는 아래와 위의 방향을 모두 포함할 수 있다.The spatially relative terms 'below', 'beneath', 'lower', 'above', 'upper' and the like are shown in FIG. It may be used to easily describe the correlation of a device or components with other devices or components. Spatially relative terms should be understood to include terms that differ in the direction of use of the device in addition to the directions shown in the figures. For example, when the device shown in the figure is inverted, a device described as 'below or beneath' of another device may be placed above the other device. Thus, the exemplary term 'below' may include both directions below and above.

본 명세서에서 사용된 용어는 실시예들을 설명하기 위한 것이며 본 발명을 제한하고자 하는 것은 아니다. 본 명세서에서, '및/또는'은 언급된 아이템들의 각각 및 하나 이상의 모든 조합을 포함한다. 또, 단수형은 문구에서 특별히 언급하지 않는 한 복수형도 포함한다. 명세서에서 사용되는 '포함한다(comprises)' 및/또는 '포함하는(comprising)'은 언급된 구성요소 외에 하나 이상의 다른 구성요소의 존재 또는 추가를 배제하지 않는다. '내지'를 사용하여 나타낸 수치 범위는 그 앞과 뒤에 기재된 값을 각각 하한과 상한으로서 포함하는 수치 범위를 나타낸다. '약' 또는 '대략'은 그 뒤에 기재된 값 또는 수치 범위의 20% 이내의 값 또는 수치 범위를 의미한다.The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. In this specification, 'and / or' includes each and all combinations of one or more of the items mentioned. In addition, the singular also includes the plural unless specifically stated in the text. As used herein, 'comprises' and / or 'comprising' does not exclude the presence or addition of one or more other components in addition to the mentioned components. Numerical ranges shown using 'to' indicate numerical ranges including the values described before and after the lower limit and the upper limit, respectively. "About" or "approximately" means a value or numerical range within 20% of the value or numerical range described thereafter.

다른 정의가 없다면, 본 명세서에서 사용되는 모든 용어(기술 및 과학적 용어를 포함)는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 공통적으로 이해될 수 있는 의미로 사용될 수 있을 것이다. 또 일반적으로 사용되는 사전에 정의되어 있는 용어들은 명백하게 특별히 정의되어 있지 않는 한 이상적으로 또는 과도하게 해석되지 않는다.Unless otherwise defined, all terms (including technical and scientific terms) used in the present specification may be used in a sense that can be commonly understood by those skilled in the art. In addition, the terms defined in the commonly used dictionaries are not ideally or excessively interpreted unless they are specifically defined clearly.

이하, 본 발명의 실시예들에 대하여 상세하게 설명한다.Hereinafter, embodiments of the present invention will be described in detail.

본 발명의 일 실시예에 따른 글루 조성물은 고분자 단백질 물질, 저분자 다당류 물질, 고분자 다당류 물질 및 알코올성 물질을 포함할 수 있다.Glue composition according to an embodiment of the present invention may include a high molecular protein material, a low molecular polysaccharide material, a high molecular polysaccharide material and an alcoholic material.

상기 고분자 단백질 물질의 예로는 젤라틴을 들 수 있다. 동물성 단백질 고분자인 젤라틴은 수분의 존재 하에서 졸(sol) 상태를 가지고, 피착물의 표면으로부터 내부로 침투할 수 있다. 그리고 피착물의 내부로 침투하여 수분이 제거되면 겔(gel)화하여 물리적 접착과 동시에 분자 내의 아미노기, 카르복실기, 수산기 등에 의한 화학적 결합이 발생할 수 있다. 본 발명이 이에 제한되는 것은 아니나, 젤라틴은 동물의 가죽, 힘줄, 창자, 뼈 등을 고아 그 액체를 고형화한 동물성 아교(阿膠)로부터 추출될 수 있다. 젤라틴은 항원성이 없어 본 실시예에 따른 글루 조성물이 인간의 피부 내지는 모발에 부착되더라도 습진, 가려움, 피부질환, 통증 등의 부작용을 나타내지 않을 수 있다.Examples of the high molecular protein material include gelatin. Gelatin, an animal protein polymer, has a sol state in the presence of moisture and can penetrate internally from the surface of the adherend. In addition, when water is removed by penetrating the inside of the adherend, a gel may be formed to form a physical bond and chemical bonding may occur by amino groups, carboxyl groups, and hydroxyl groups in the molecule. Although the present invention is not limited thereto, gelatin may be extracted from animal glue obtained by solidifying the liquid of animal skin, tendons, intestines, bones, and the like. Gelatin is not antigenic, even if the glue composition according to this embodiment is attached to human skin or hair may not exhibit side effects such as eczema, itching, skin diseases, pain.

또, 상기 저분자 다당류 물질의 예로는 덱스트린을 들 수 있다. 일반적으로 덱스트린은 녹말보다 분자량이 작은 다당류를 지칭한다. 예를 들어, 덱스트린은 (C6H10O5)n으로 표현될 수 있다. 본 발명이 이에 제한되는 것은 아니나, 덱스트린은 일반 전분으로부터 추출되거나, 또는 상기 일반 전분을 산화 처리한 산화 전분(oxidized starch), 상기 일반 전분을 산처리한 산 처리 전분(acid thinning starch), 가교 전분(cross-linked starch) 등의 변성 전분(modified starch)으로부터 추출될 수 있다.Moreover, dextrin is mentioned as an example of the said low molecular weight polysaccharide substance. Dextrin generally refers to polysaccharides having a lower molecular weight than starch. For example, dextrin may be represented by (C 6 H 10 O 5 ) n. Although the present invention is not limited thereto, dextrin is extracted from normal starch, or oxidized starch (oxidized starch) oxidized the general starch, acid-treated starch (acid thinning starch), crosslinked starch It can be extracted from modified starch, such as (cross-linked starch).

상기 덱스트린은 전술한 고분자 단백질 물질과 혼합되어 글루 조성물 내에서 초기 접착력을 발휘하고, 글루 조성물의 점도 안정성을 향상시킬 수 있다. 또, 글루 조성물의 충분한 도포 시간을 확보할 수 있어 글루 조성물의 응집 현상을 방지할 수 있다.The dextrin may be mixed with the aforementioned high molecular protein material to exert initial adhesion in the glue composition, and may improve viscosity stability of the glue composition. Moreover, sufficient application time of a glue composition can be ensured and the aggregation phenomenon of a glue composition can be prevented.

글루 조성물 내의 저분자 다당류 물질의 함량은 상기 고분자 단백질 물질의 함량 보다 작을 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 젤라틴 100 중량부에 대해 상기 덱스트린을 약 60 중량부 이상 약 80 중량부 이하, 또는 약 65 중량부 이상 약 70 중량부 이하의 범위로 포함할 수 있다. 덱스트린의 함량이 60 중량부 미만이면 글루 조성물의 도포 시에 응집 현상이 발생할 수 있다. 또, 덱스트린의 함량이 80 중량부를 초과하면 접착력의 저하가 발생할 수 있다.The content of low molecular polysaccharide material in the glue composition may be less than the content of the polymeric protein material. In an exemplary embodiment, the glue composition may include the dextrin in a range of about 60 parts by weight to about 80 parts by weight, or about 65 parts by weight to about 70 parts by weight based on 100 parts by weight of the gelatin. If the content of dextrin is less than 60 parts by weight, aggregation may occur during application of the glue composition. In addition, when the content of dextrin exceeds 80 parts by weight, a decrease in adhesive force may occur.

상기 고분자 다당류 물질은 식물성 고분자일 수 있다. 상기 고분자 다당류 물질은 검(gum) 물질을 포함할 수 있다. 검 물질은 탄성을 가질 수 있다. 검 물질의 예로는 아라비아 검(gum Arabic), 가티 검(gum ghatti), 카라야 검(karaya gum), 구아 검(guar gumx), 트라가칸트 검(tragacanth gum), 로커스트빈 검(locust bean gum), 잔탄 검(xanthan gum) 중 하나 이상을 포함할 수 있다. 글루 조성물의 접착력 향상 측면에서 아라비아 검 및/또는 잔탄 검이 바람직할 수 있다.The polymer polysaccharide material may be a vegetable polymer. The polymer polysaccharide material may include a gum material. The gum material may be elastic. Examples of gum substances include gum Arabic, gum ghatti, karaya gum, guar gumx, tragacanth gum, and locust bean gum. ), And one or more of xanthan gum. Arabian gum and / or xanthan gum may be preferred in view of improving adhesion of the glue composition.

상기 아라비아 검 및 잔탄 검은 유기 바인더로 기능하여 글루 조성물의 접착력 향상에 기여하고, 글루 조성물의 점도를 증가시킬 수 있다. 또, 본 실시예에 따른 글루 조성물을 코팅하는 경우에, 상기 아라비아 검 및 잔탄 검은 글루 코팅층의 탄성을 증가시킬 수 있다. 본 발명이 이에 제한되는 것은 아니나 본 실시예에 따른 글루 조성물을 이용한 미용 도구를 인간의 안검에 부착하는 경우에 인간의 눈물 등의 이물에 의해 글루의 산도가 변화할 수 있다. 그러나 아라비아 검 및 잔탄 검은 글루의 산도가 변화하는 경우에도 우수한 접착력을 유지할 수 있다.The gum arabic and xanthan gum can serve as an organic binder to contribute to improving the adhesive strength of the glue composition, it is possible to increase the viscosity of the glue composition. In addition, when coating the glue composition according to the present embodiment, it is possible to increase the elasticity of the gum arabic gum and xanthan gum coating layer. Although the present invention is not limited thereto, the acidity of the glue may be changed by foreign matters such as tears of the human body when the cosmetic tool using the glue composition according to the present embodiment is attached to the human eyelid. However, good adhesion can be maintained even when the acidity of the gum arabic and xanthan gum is changed.

글루 조성물 내의 고분자 다당류 물질의 함량은 상기 저분자 다당류 물질의 함량 보다 작을 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 젤라틴 100 중량부에 대해 상기 아라비아 검 및 잔탄 검을 약 15 중량부 이상 약 25 중량부 이하, 또는 약 18 중량부 이상 22 중량부 이하의 범위로 포함할 수 있다. 아라비아 검 및 잔탄 검의 함량이 15 중량부 미만이면 글루 조성물을 이용한 글루 코팅층의 탄성이 저하될 수 있다. 또, 아라비아 검 및 잔탄 검의 함량이 25 중량부를 초과하면 글루 조성물의 과도한 점성 증가로 인해 글루 조성물을 이용하여 고른 도포가 곤란할 수 있다.The content of the polymer polysaccharide material in the glue composition may be less than the content of the low molecular polysaccharide material. In an exemplary embodiment, the glue composition may include the gum arabic and xanthan gum in an amount of about 15 parts by weight to about 25 parts by weight, or about 18 parts by weight to 22 parts by weight based on 100 parts by weight of the gelatin. . If the content of gum arabic and xanthan gum is less than 15 parts by weight, the elasticity of the glue coating layer using the glue composition may decrease. In addition, when the content of gum arabic and xanthan gum exceeds 25 parts by weight, even application of the glue composition may be difficult due to excessive increase in viscosity of the glue composition.

또, 상기 알코올성 물질의 예로는 글리세롤을 들 수 있다. 글리세롤은 C3H5(OH)3으로 표현되는 지방족 3가 알코올성 물질이다. 상기 글리세롤은 전술한 고분자 단백질 물질 및 저분자 다당류 물질과 혼합되어 글루 조성물의 점도 안정성을 향상시킬 수 있다. 또, 본 실시예에 따른 글루 조성물이 건조되어 용매가 증발한 후에 글루 코팅층의 표면을 안정한 상태로 유지시킬 수 있다. 이를 통해 본 실시예에 따른 글루 조성물을 이용하여 미용 도구를 제조하는 경우에 반복적인 부착과 탈착에도 불구하고 우수한 접착력을 유지하도록 할 수 있다. 몇몇 실시예에서, 알코올성 물질은 글리세롤 및 디프로필렌글리콜을 모두 포함할 수도 있다. 글리세롤에 더하여 흡습성을 갖는 디프로필렌글리콜을 더 첨가함으로써 반복적인 부착과 탈착에도 불구하고 더욱 우수한 접착력을 유지하도록 할 수 있다.Moreover, glycerol is mentioned as an example of the said alcoholic substance. Glycerol is an aliphatic trihydric alcoholic substance represented by C 3 H 5 (OH) 3 . The glycerol may be mixed with the aforementioned high molecular protein material and low molecular weight polysaccharide material to improve viscosity stability of the glue composition. In addition, after the glue composition according to the present embodiment is dried to evaporate the solvent, the surface of the glue coating layer may be maintained in a stable state. Through this, in the case of manufacturing a beauty tool using the glue composition according to the present embodiment it can be maintained to maintain excellent adhesion despite repeated attachment and detachment. In some embodiments, the alcoholic material may include both glycerol and dipropylene glycol. In addition to glycerol, further addition of hygroscopic dipropylene glycol can be made to maintain better adhesion despite repeated attachment and desorption.

글루 조성물 내의 알코올성 물질의 함량은 상기 저분자 다당류 물질의 함량 보다 클 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 젤라틴 100 중량부에 대해 글리세롤을 약 90 중량부 이상 약 110 중량부 이하, 또는 약 95 중량부 이상 약 105 중량부 이하의 범위로 포함할 수 있다. 글리세롤의 함량이 90 중량부 미만이면 글루 조성물의 건조 후 글루 코팅층의 표면에 점착성이 잔존할 수 있다. 또, 글리세롤의 함량이 110 중량부를 초과하면 글루 조성물의 접착력이 저하될 수 있다.The content of alcoholic material in the glue composition may be greater than the content of the low molecular polysaccharide material. In an exemplary embodiment, the glue composition may include about 90 parts by weight or more and about 110 parts by weight or less, or about 95 parts by weight or more and about 105 parts by weight or less based on 100 parts by weight of the gelatin. If the content of glycerol is less than 90 parts by weight, the adhesive may remain on the surface of the glue coating layer after drying the glue composition. In addition, when the content of glycerol exceeds 110 parts by weight, the adhesive strength of the glue composition may be lowered.

몇몇 실시예에서, 글루 조성물은 트윈 60, 트윈 80, 올리브 리퀴드 등의 가용화제(solubilizing agent) 또는 유화제(emulsifying agent)를 더 포함할 수 있다. 가용화제는 글루 조성물 내의 고분자 단백질 물질, 저분자 다당류 물질, 고분자 다당류 물질 및/또는 알코올성 물질 간의 분산을 유도할 수 있고, 글루 조성물의 도포성을 향상시킬 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 젤라틴 100 중량부에 대해 가용화제를 약 1.0 중량부 이상 5.0 중량부 이하, 또는 약 3.0 중량부 이상 4.0 중량부 이하의 범위로 포함할 수 있다. 가용화제가 상기 범위 내로 포함될 경우 접착력의 저하 없이 가용화제의 기능을 발휘할 수 있다.In some embodiments, the glue composition may further comprise solubilizing agents or emulsifying agents, such as Tween 60, Tween 80, Olive Liquid, and the like. The solubilizer may induce dispersion between the high molecular protein material, the low molecular polysaccharide material, the high molecular polysaccharide material, and / or the alcoholic material in the glue composition, and may improve the applicability of the glue composition. In an exemplary embodiment, the glue composition may include about 1.0 part by weight to 5.0 parts by weight, or about 3.0 parts by weight or more and 4.0 parts by weight or less based on 100 parts by weight of the gelatin. When the solubilizer is included in the above range it can exhibit the function of the solubilizer without a decrease in the adhesive force.

또, 몇몇 실시예에서, 글루 조성물은 용매를 더 포함할 수 있다. 용매는 전술한 고분자 단백질 물질, 저분자 다당류 물질, 고분자 다당류 물질 및 알코올성 물질의 분산과 용해가 가능하면 특별히 제한되지 않으나, 예를 들어 용매는 증류수 등일 수 있다. 본 발명이 이에 제한되는 것은 아니나, 글루 조성물 내의 용매의 함량은 상기 젤라틴 100 중량부에 대해 약 40 중량부 이상 약 60 중량부 이하, 또는 약 50 중량부일 수 있다.In addition, in some embodiments, the glue composition may further comprise a solvent. The solvent is not particularly limited as long as it can disperse and dissolve the aforementioned high molecular protein material, low molecular polysaccharide material, high molecular polysaccharide material, and alcoholic material. For example, the solvent may be distilled water or the like. Although the present invention is not limited thereto, the content of the solvent in the glue composition may be about 40 parts by weight to about 60 parts by weight, or about 50 parts by weight based on 100 parts by weight of the gelatin.

비제한적인 일례로, 본 실시예에 따른 글루 조성물은 약 28 중량% 내지 약 32 중량%의 젤라틴, 약 18 중량% 내지 약 22 중량%의 덱스트린, 약 5 중량% 내지 약 8 중량%의 잔탄 검, 약 28 중량% 내지 약 32 중량%의 글리세롤 및 잔량의 증류수를 포함할 수 있다.In one non-limiting example, the glue composition according to this embodiment comprises about 28% to about 32% gelatin, about 18% to about 22% dextrin, about 5% to about 8% xanthan gum. , About 28% to about 32% by weight of glycerol and the balance of distilled water.

본 실시예에 따른 글루 조성물은 코팅이 용이한 점도와 보존 안정성을 가지면서도 우수한 접착력을 가질 수 있다. 또한, 글루 조성물을 코팅 및 건조시킬 경우, 글루 코팅층 표면이 점착력을 갖지 않고 건조된 상태를 유지할 수 있다. 그리고 글루 코팅층이 수분과 접촉할 경우 비로소 접착력이 발생할 수 있다. 따라서 본 실시예에 따른 글루 조성물을 이용한 글루 코팅층을 미용 도구에 활용할 경우 휴대와 사용이 용이한 효과가 있다. 뿐만 아니라, 상기 미용 도구를 반복적으로 장착 및 탈착하는 경우에도 글루 코팅층의 접착력 저하를 최소화할 수 있다.Glue composition according to the present embodiment may have an excellent adhesive strength while having easy viscosity and storage stability of the coating. In addition, when coating and drying the glue composition, the surface of the glue coating layer may be kept dry without having an adhesive force. In addition, adhesive force may occur when the glue coating layer comes into contact with moisture. Therefore, when the glue coating layer using the glue composition according to the present embodiment is used in a beauty tool, it is easy to carry and use. In addition, even when repeatedly mounting and detaching the cosmetic tools can be reduced the adhesive strength of the glue coating layer.

이하, 다른 실시예들에 대하여 설명한다. Hereinafter, other embodiments will be described.

본 발명의 다른 실시예에 따른 글루 조성물은 아크릴레이트계 화합물, 폴리비닐알코올계 화합물 및 가용화제를 포함할 수 있다.Glue composition according to another embodiment of the present invention may include an acrylate compound, a polyvinyl alcohol compound and a solubilizer.

상기 아크릴레이트계 화합물은 에스테르 결합을 갖는 화합물이면 특별히 제한되지 않는다. 상기 아크릴레이트계 화합물은 수분의 존재 하에서 고분자 화합물을 형성하며 접착력을 가질 수 있다. 특히, 본 실시예에 따른 글루 조성물이 건조되어 용매가 증발한 후에 글루 코팅층의 표면이 점착력을 갖지 않고, 글루 코팅층이 수분과 접촉할 경우 비로소 접착력이 발생할 수 있다.The acrylate compound is not particularly limited as long as it is a compound having an ester bond. The acrylate compound may form a high molecular compound in the presence of water and may have an adhesive force. In particular, after the glue composition according to the present embodiment is dried to evaporate the solvent, the surface of the glue coating layer does not have adhesive force, and the adhesive force may occur only when the glue coating layer contacts water.

또, 상기 폴리비닐알코올계 화합물은 전술한 아크릴레이트계 화합물과 함께 혼합되어 글루 조성물 내에서 접착력을 발휘할 수 있다. 또, 폴리비닐알코올계 화합물은 극성 용매에 대한 분산성이 우수한 장점이 있다. 폴리비닐알코올계 화합물은 분자 내 다수의 수산기를 가지고 있어 화학적 결합에 기여할 뿐만 아니라 아크릴레이트계 화합물과의 반응이 용이하다. 몇몇 실시예에서, 글루 조성물은 아크릴레이트계 화합물과 폴리비닐알코올계 화합물의 중합체 형태의 분자를 더 포함할 수도 있다.In addition, the polyvinyl alcohol-based compound may be mixed with the acrylate-based compound described above to exert the adhesive force in the glue composition. In addition, the polyvinyl alcohol-based compound has an advantage of excellent dispersibility in polar solvents. Polyvinyl alcohol-based compounds have a number of hydroxyl groups in the molecule not only contribute to the chemical bonding but also easy to react with the acrylate-based compound. In some embodiments, the glue composition may further comprise molecules in the form of polymers of acrylate-based compounds and polyvinyl alcohol-based compounds.

또, 본 실시예에 따른 글루 조성물을 코팅하는 경우에, 상기 폴리비닐알코올계 화합물은 글루 코팅층의 탄성을 증가시킬 수 있다. 이를 통해 글루 조성물 및 이를 이용한 글루 코팅층이 우수한 접착력을 가짐과 동시에 사용자가 탈착을 원하는 경우 사용자의 피부 내지는 모발에 손상 없이도 탈착을 용이하게 할 수 있다. 뿐만 아니라, 본 실시예에 따른 글루 조성물을 이용하여 미용 도구를 제조하는 경우에 반복적인 부착과 탈착에도 불구하고 우수한 접착력을 유지하도록 할 수 있다.In addition, when coating the glue composition according to the present embodiment, the polyvinyl alcohol-based compound may increase the elasticity of the glue coating layer. Through this, the glue composition and the glue coating layer using the same have an excellent adhesive force and can be easily detached without damaging the user's skin or hair if the user wants to detach. In addition, in the case of manufacturing a cosmetic tool using the glue composition according to the present embodiment can be maintained to maintain excellent adhesion despite repeated attachment and detachment.

글루 조성물 내의 폴리비닐알코올계 화합물의 함량은 상기 아크릴레이트계 화합물의 함량 보다 작을 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 아크릴레이트계 화합물 100 중량부에 대해 상기 폴리비닐알코올계 화합물을 약 20 중량부 이상 약 30 중량부 이하, 또는 약 24 중량부 이상 약 26 중량부 이하의 범위로 포함할 수 있다. 폴리비닐알코올계 화합물의 함량이 20 중량부 미만이면 글루 코팅층에 충분한 탄성을 부여할 수 없어 탈착이 곤란할 수 있다. 또, 폴리비닐알코올계 화합물의 함량이 30 중량부를 초과하면 글루 조성물이 충분한 접착력을 갖지 못할 수 있다.The content of the polyvinyl alcohol compound in the glue composition may be smaller than the content of the acrylate compound. In an exemplary embodiment, the glue composition has a range of about 20 parts by weight to about 30 parts by weight, or about 24 parts by weight to about 26 parts by weight of the polyvinyl alcohol compound based on 100 parts by weight of the acrylate compound. It can be included as. When the content of the polyvinyl alcohol-based compound is less than 20 parts by weight, sufficient elasticity may not be imparted to the glue coating layer, and thus desorption may be difficult. In addition, when the content of the polyvinyl alcohol-based compound exceeds 30 parts by weight, the glue composition may not have sufficient adhesive strength.

상기 가용화제의 예로는 트윈 60, 트윈 80, 또는 올리브 리퀴드 등을 들 수 있다. 가용화제는 글루 조성물 내의 아크릴레이트계 화합물과 폴리비닐알코올계 화합물 간의 분산을 유도할 수 있고, 글루 조성물의 도포성을 향상시킬 수 있다.Examples of the solubilizer include tween 60, tween 80, or olive liquid. The solubilizer can induce dispersion between the acrylate compound and the polyvinyl alcohol compound in the glue composition, and can improve the applicability of the glue composition.

글루 조성물 내의 가용화제의 함량은 상기 폴리비닐알코올계 화합물의 함량 보다 작을 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 아크릴레이트계 화합물 100 중량부에 대해 가용화제를 약 1.0 중량부 이상 5.0 중량부 이하, 또는 약 3.0 중량부 이상 4.0 중량부 이하의 범위로 포함할 수 있다. 가용화제가 상기 범위 내로 포함될 경우 접착력의 저하 없이 가용화제의 기능을 발휘할 수 있다.The content of the solubilizer in the glue composition may be less than the content of the polyvinyl alcohol-based compound. In an exemplary embodiment, the glue composition may include about 1.0 part by weight to 5.0 parts by weight, or about 3.0 parts by weight or more and 4.0 parts by weight or less based on 100 parts by weight of the acrylate compound. When the solubilizer is included in the above range it can exhibit the function of the solubilizer without a decrease in the adhesive force.

몇몇 실시예에서, 글루 조성물은 디프로필렌글리콜을 더 포함할 수 있다. 흡습성을 갖는 디프로필렌글리콜을 더 포함함으로써 반복적인 부착과 탈착에도 불구하고 우수한 접착력을 유지하도록 할 수 있다.In some embodiments, the glue composition may further comprise dipropylene glycol. By further including the hygroscopic dipropylene glycol it is possible to maintain excellent adhesion despite repeated attachment and desorption.

또, 몇몇 실시예에서, 글루 조성물은 용매를 더 포함할 수 있다. 용매는 전술한 고분자 아크릴레이트계 화합물, 폴리비닐알코올계 화합물 및 가용화제의 분산과 용해가 가능하면 특별히 제한되지 않으나, 예를 들어 용매는 증류수 등일 수 있다. 본 발명이 이에 제한되는 것은 아니나, 글루 조성물 내의 용매의 함량은 상기 아크릴레이트계 화합물 100 중량부에 대해 약 40 중량부 이상 약 60 중량부 이하, 또는 약 50 중량부일 수 있다.In addition, in some embodiments, the glue composition may further comprise a solvent. The solvent is not particularly limited as long as it can disperse and dissolve the above-described polymer acrylate compound, polyvinyl alcohol compound, and solubilizing agent, for example, the solvent may be distilled water or the like. Although the present invention is not limited thereto, the content of the solvent in the glue composition may be about 40 parts by weight to about 60 parts by weight, or about 50 parts by weight based on 100 parts by weight of the acrylate compound.

비제한적인 일례로, 본 실시예에 따른 글루 조성물은 약 75 중량% 내지 약 80 중량%의 아크릴레이트계 화합물 및 약 18 중량% 내지 약 22 중량%의 폴리비닐알코올계 화합물을 포함하고, 약 1 중량% 내지 약 4 중량%의 올리브 리퀴드를 더 포함할 수 있다.In one non-limiting example, the glue composition according to this embodiment comprises about 75% to about 80% by weight of the acrylate compound and about 18% to about 22% by weight of the polyvinyl alcohol compound, about 1 It may further comprise up to about 4% by weight olive liquid.

본 실시예에 따른 글루 조성물은 코팅이 용이한 점도와 보존 안정성을 가지면서도 우수한 접착력을 가질 수 있다. 또한, 글루 조성물을 코팅 및 건조시킬 경우, 글루 코팅층 표면이 점착력을 갖지 않고 건조된 상태를 유지할 수 있다. 그리고 글루 코팅층이 수분과 접촉할 경우 비로소 접착력이 발생할 수 있다. 따라서 본 실시예에 따른 글루 조성물을 이용한 글루 코팅층을 미용 도구에 활용할 경우 휴대와 사용이 용이한 효과가 있다. 뿐만 아니라, 상기 미용 도구를 반복적으로 장착 및 탈착하는 경우에도 글루 코팅층의 접착력 저하를 최소화할 수 있다.Glue composition according to the present embodiment may have an excellent adhesive strength while having easy viscosity and storage stability of the coating. In addition, when coating and drying the glue composition, the surface of the glue coating layer may be kept dry without having an adhesive force. In addition, adhesive force may occur when the glue coating layer comes into contact with moisture. Therefore, when the glue coating layer using the glue composition according to the present embodiment is used in a beauty tool, it is easy to carry and use. In addition, even when repeatedly mounting and detaching the cosmetic tools can be reduced the adhesive strength of the glue coating layer.

본 발명의 또 다른 실시예에 따른 글루 조성물은 아크릴레이트계 화합물, 우레탄계 화합물 및 가용화제를 포함할 수 있다. 본 실시예에 따른 아크릴레이트계 화합물 및 가용화제의 기능과 함량 등에 대해서는 앞서 설명한 바 있으므로 중복되는 설명은 생략한다.Glue composition according to another embodiment of the present invention may include an acrylate compound, a urethane compound and a solubilizer. Since the functions and contents of the acrylate compound and the solubilizer according to the present embodiment have been described above, redundant descriptions are omitted.

우레탄계 화합물은 전술한 아크릴레이트계 화합물과 함께 혼합되어 글루 조성물 내에서 접착력을 발휘할 수 있다. 몇몇 실시예에서, 글루 조성물은 아크릴레이트계 화합물과 우레탄계 화합물의 중합체 형태의 분자를 더 포함할 수도 있다. 본 실시예에 따른 글루 조성물을 코팅하는 경우에, 상기 우레탄계 화합물은 글루 코팅층의 탄성을 증가시킬 수 있다. 이를 통해 글루 조성물 및 이를 이용한 글루 코팅층이 우수한 접착력을 가짐과 동시에 사용자가 탈착을 원하는 경우 사용자의 피부 내지는 모발에 손상 없이도 탈착을 용이하게 할 수 있다. 뿐만 아니라, 본 실시예에 따른 글루 조성물을 이용하여 미용 도구를 제조하는 경우에 반복적인 부착과 탈착에도 불구하고 우수한 접착력을 유지하도록 할 수 있다.The urethane compound may be mixed with the acrylate compound described above to exert the adhesive force in the glue composition. In some embodiments, the glue composition may further comprise molecules in the form of polymers of acrylate based compounds and urethane based compounds. In the case of coating the glue composition according to the present embodiment, the urethane-based compound may increase the elasticity of the glue coating layer. Through this, the glue composition and the glue coating layer using the same have an excellent adhesive force and can be easily detached without damaging the user's skin or hair if the user wants to detach. In addition, in the case of manufacturing a cosmetic tool using the glue composition according to the present embodiment can be maintained to maintain excellent adhesion despite repeated attachment and detachment.

글루 조성물 내의 우레탄계 화합물의 함량은 상기 아크릴레이트계 화합물의 함량 보다 작을 수 있다. 예시적인 실시예에서, 글루 조성물은 상기 아크릴레이트계 화합물 100 중량부에 대해 상기 우레탄계 화합물을 약 20 중량부 이상 약 30 중량부 이하, 또는 약 24 중량부 이상 약 26 중량부 이하의 범위로 포함할 수 있다. 우레탄계 화합물의 함량이 20 중량부 미만이면 글루 코팅층에 충분한 탄성을 부여할 수 없어 탈착이 곤란할 수 있다. 또, 우레탄계 화합물의 함량이 30 중량부를 초과하면 글루 조성물이 충분한 접착력을 갖지 못할 수 있다.The content of the urethane compound in the glue composition may be smaller than the content of the acrylate compound. In an exemplary embodiment, the glue composition may include the urethane-based compound in a range of about 20 parts by weight to about 30 parts by weight, or about 24 parts by weight to about 26 parts by weight with respect to 100 parts by weight of the acrylate compound. Can be. When the content of the urethane-based compound is less than 20 parts by weight, sufficient elasticity may not be imparted to the glue coating layer, and thus desorption may be difficult. In addition, when the content of the urethane-based compound exceeds 30 parts by weight, the glue composition may not have sufficient adhesive force.

몇몇 실시예에서, 글루 조성물은 디프로필렌글리콜을 더 포함할 수 있다. 흡습성을 갖는 디프로필렌글리콜을 더 포함함으로써 반복적인 부착과 탈착에도 불구하고 우수한 접착력을 유지하도록 할 수 있다.In some embodiments, the glue composition may further comprise dipropylene glycol. By further including the hygroscopic dipropylene glycol it is possible to maintain excellent adhesion despite repeated attachment and desorption.

또, 몇몇 실시예에서, 글루 조성물은 용매를 더 포함할 수 있다. 용매는 전술한 고분자 아크릴레이트계 화합물, 우레탄계 화합물 및 가용화제의 분산과 용해가 가능하면 특별히 제한되지 않으나, 예를 들어 용매는 증류수 등일 수 있다. 본 발명이 이에 제한되는 것은 아니나, 글루 조성물 내의 용매의 함량은 상기 아크릴레이트계 화합물 100 중량부에 대해 약 40 중량부 이상 약 60 중량부 이하, 또는 약 50 중량부일 수 있다.In addition, in some embodiments, the glue composition may further comprise a solvent. The solvent is not particularly limited as long as it can disperse and dissolve the above-described polymer acrylate compound, urethane compound, and solubilizing agent, for example, the solvent may be distilled water or the like. Although the present invention is not limited thereto, the content of the solvent in the glue composition may be about 40 parts by weight to about 60 parts by weight, or about 50 parts by weight based on 100 parts by weight of the acrylate compound.

비제한적인 일례로, 본 실시예에 따른 글루 조성물은 약 75 중량% 내지 약 80 중량%의 아크릴레이트계 화합물 및 약 18 중량% 내지 약 22 중량%의 우레탄계 화합물을 포함하고, 약 1 중량% 내지 약 4 중량%의 올리브 리퀴드를 더 포함할 수 있다.In one non-limiting example, the glue composition according to this embodiment comprises from about 75% to about 80% by weight of an acrylate compound and from about 18% to about 22% by weight of a urethane compound, from about 1% to about It may further comprise about 4% by weight olive liquid.

이하, 첨부된 도면을 참조하여 본 발명에 따른 미용 도구에 대하여 설명한다.Hereinafter, with reference to the accompanying drawings will be described a beauty tool according to the present invention.

도 1은 본 발명의 일 실시예에 따른 탈부착식 미용 도구를 나타낸 도면이다. 도 2는 도 1의 점선 영역을 확대한 확대도이다.1 is a view showing a removable beauty tool according to an embodiment of the present invention. FIG. 2 is an enlarged view illustrating the dotted line region of FIG. 1.

도 1 및 도 2를 참조하면, 본 실시예에 따른 탈부착식 미용 도구(1)는 미용 도구 바디(10) 및 미용 도구 바디(10) 상에 배치된 글루 코팅층(20)을 포함할 수 있다.1 and 2, the detachable cosmetic tool 1 according to the present embodiment may include a cosmetic tool body 10 and a glue coating layer 20 disposed on the cosmetic tool body 10.

도 1 등은 미용 도구의 예로 인조 속눈썹을 예시하고 있으나 본 발명이 이에 제한되는 것은 아니며, 미용 도구는 가발, 인조 손톱/발톱, 장신구 등일 수도 있다.1 and the like, but the artificial eyelashes are illustrated as an example of a beauty tool, but the present invention is not limited thereto, and the beauty tool may be a wig, artificial nails / claws, or jewelry.

예시적인 실시예에서, 미용 도구 바디(10)는 모주(毛柱)(11)와 모주(11)에 결합된 다수의 속눈썹 세모(細毛)(12)를 포함하는 인조 속눈썹일 수 있다. 모주(11) 및 세모(12)는 물리적 경계를 갖지 않고 일체로 이루어지거나, 또는 모주(11) 및 세모(12)는 별도로 제조된 후 접착 부재 등을 통해 결합되거나, 또는 모주(11) 및 세모(12)는 별도로 제조된 후 물리적으로 결합된 상태일 수도 있다.In an exemplary embodiment, the cosmetic tool body 10 may be an artificial eyelash that includes a hair 11 and a plurality of eyelash hairs 12 coupled to the hair 11. The main column 11 and the tricot 12 are integrally formed without having a physical boundary, or the main column 11 and the tricot 12 are separately manufactured and then bonded through an adhesive member or the like, or the main column 11 and the triangular 12 may be separately manufactured and then physically coupled.

미용 도구(1)가 인조 속눈썹인 예시적인 실시예에서, 모주(11)는 인간의 속눈썹이 난 안검(eye-lid)에 상응하는 긴 호형일 수 있다. 모주(11)는 유연성을 가지고 사용자의 안검 형상에 따라 변형될 수 있다. 모주(11)는 폴리에틸렌테레프탈레이트(PET), 폴레에스테르(PE), 나일론(nylon), 폴리프로필렌(PP) 또는 폴리비닐클로라이드(PVC) 등의 합성 섬유를 포함하여 이루어지거나, 인간 또는 동물의 털로부터 유래한 천연 섬유를 포함하여 이루어질 수 있다.In an exemplary embodiment in which the cosmetic tool 1 is an artificial eyelash, the hairline 11 may be a long arc corresponding to the eye-lid of a human eyelash. The main column 11 may be deformed according to the shape of the user's eyelid with flexibility. The main column 11 includes synthetic fibers such as polyethylene terephthalate (PET), polyester (PE), nylon (nylon), polypropylene (PP) or polyvinyl chloride (PVC), or human or animal hair. It may comprise natural fibers derived from.

또, 미용 도구(1)가 인조 속눈썹인 예시적인 실시예에서, 다수의 세모(12)들은 모주(11)의 연장 방향과 상이한 방향으로 돌출된 형상일 수 있다. 세모(12)의 평균 굵기는 모주(11)에 비해 얇을 수 있으나 본 발명이 이에 제한되는 것은 아니다. 세모(12)는 인간의 속눈썹들을 모사하도록 구성될 수 있다. 세모(12)는 모주(11)와 동일하거나 상이한 재질로 이루어질 수 있다. 즉, 세모(12)는 폴리에틸렌테레프탈레이트(PET), 폴레에스테르(PE), 나일론(nylon), 폴리프로필렌(PP) 또는 폴리비닐클로라이드(PVC) 등의 합성 섬유를 포함하여 이루어지거나, 인간 또는 동물의 털로부터 유래한 천연 섬유를 포함하여 이루어질 수 있다.In addition, in the exemplary embodiment in which the cosmetic tool 1 is an artificial eyelash, the plurality of hairs 12 may be shaped to protrude in a direction different from the direction in which the hairline 11 extends. The average thickness of the three hairs 12 may be thinner than the mother line 11, but the present invention is not limited thereto. The hair triangle 12 may be configured to simulate human eyelashes. The three hairs 12 may be made of the same or different material as the mother line 11. That is, the hairs 12 are made of synthetic fibers such as polyethylene terephthalate (PET), polyester (PE), nylon (nylon), polypropylene (PP) or polyvinyl chloride (PVC), or human or animal It may comprise a natural fiber derived from the hair of.

다수의 세모(12)들은 서로 다른 길이를 가질 수 있다. 즉, 어느 세모(12)는 인접한 다른 세모(12)와 다른 돌출 길이를 가질 수 있고, 이를 통해 인간의 속눈썹과 보다 유사한 형태를 모사할 수 있다. 몇몇 실시예에서, 다수의 세모(12)들은 소정의 커얼(curl)을 가질 수 있다. 또, 다수의 세모(12)들은 모두 동일한 방향으로의 커얼을 가질 수 있다. 이를 통해 인간의 속눈썹과 보다 유사한 형태를 모사할 수 있다.The multiple triangles 12 may have different lengths. That is, some hairs 12 may have a protruding length different from other hairs 12 adjacent to each other, thereby simulating a shape more similar to human eyelashes. In some embodiments, the plurality of triangles 12 may have a certain curl. In addition, the plurality of triangles 12 may all have curl in the same direction. This allows you to simulate a shape more similar to human eyelashes.

예시적인 실시예에서, 미용 도구 바디(10) 상에는 글루 코팅층(20)이 배치될 수 있다. 예를 들어, 모주(11) 및/또는 세모(12) 표면 상에는 직접 글루 코팅층(20)이 배치될 수 있다. 도 1은 글루 코팅층(20)이 모주(11) 상에만 배치된 경우를 예시하고 있으나, 본 발명이 이에 제한되는 것은 아니다. 다른 실시예에서, 글루 코팅층(20)은 세모(12)와 접촉할 수도 있다.In an exemplary embodiment, the glue coating layer 20 may be disposed on the cosmetic tool body 10. For example, the glue coating layer 20 may be disposed directly on the surface of the master column 11 and / or hairs 12. 1 illustrates a case where the glue coating layer 20 is disposed only on the mother column 11, but the present invention is not limited thereto. In other embodiments, the glue coating layer 20 may be in contact with the hairs 12.

글루 코팅층(20)은 전술한 본 발명의 일 실시예에 따른 글루 조성물이 미용 도구 바디(10) 상에 코팅 및 건조 내지는 경화되어 형성된 층일 수 있다. 예시적인 실시예에서, 건조된 상태의 글루 코팅층(20)은 고분자 단백질 물질, 저분자 다당류 물질, 고분자 다당류 물질 및 알코올성 물질을 포함하고, 가용화제 또는 유화제를 더 포함할 수 있다. The glue coating layer 20 may be a layer formed by coating and drying or curing the glue composition according to the above-described embodiment of the present invention on the cosmetic tool body 10. In an exemplary embodiment, the dried glue coating layer 20 may include a high molecular protein material, a low molecular polysaccharide material, a high molecular polysaccharide material, and an alcoholic material, and further include a solubilizer or an emulsifier.

글루 코팅층(20) 내의 저분자 다당류 물질의 함량은 상기 고분자 단백질 물질의 함량 보다 작을 수 있다. 예를 들어, 글루 코팅층(20)은 상기 고분자 단백질 100 중량부에 대해 저분자 다당류 물질을 약 60 중량부 이상 약 80 중량부 이하, 또는 약 65 중량부 이상 약 70 중량부 이하의 범위로 포함할 수 있다. 또, 글루 코팅층(20) 내의 고분자 다당류 물질의 함량은 상기 저분자 다당류 물질의 함량 보다 작을 수 있다. 예를 들어, 글루 코팅층(20)은 고분자 단백질 물질 100 중량부에 대해 고분자 다당류 물질을 약 15 중량부 이상 약 25 중량부 이하, 또는 약 18 중량부 이상 22 중량부 이하의 범위로 포함할 수 있다. 또한, 글루 코팅층(20) 내의 알코올성 물질의 함량은 상기 저분자 다당류 물질의 함량 보다 클 수 있다. 예를 들어, 글루 코팅층(20)은 고분자 단백질 100 중량부에 대해 알코올성 물질을 약 90 중량부 이상 약 110 중량부 이하, 또는 약 95 중량부 이상 약 105 중량부 이하의 범위로 포함할 수 있다. 각 성분의 구체적인 기능에 대해서는 앞서 설명한 바 있으므로 중복되는 설명은 생략한다.The content of the low molecular weight polysaccharide material in the glue coating layer 20 may be smaller than the content of the high molecular protein material. For example, the glue coating layer 20 may include about 60 parts by weight to about 80 parts by weight, or about 65 parts by weight to about 70 parts by weight of the low molecular polysaccharide material with respect to 100 parts by weight of the polymer protein. have. In addition, the content of the polymer polysaccharide material in the glue coating layer 20 may be smaller than the content of the low molecular polysaccharide material. For example, the glue coating layer 20 may include a polymer polysaccharide material in a range of about 15 parts by weight to about 25 parts by weight, or about 18 parts by weight to 22 parts by weight based on 100 parts by weight of the polymer protein material. . In addition, the content of the alcoholic material in the glue coating layer 20 may be greater than the content of the low molecular weight polysaccharide material. For example, the glue coating layer 20 may include an alcoholic material in a range of about 90 parts by weight to about 110 parts by weight, or about 95 parts by weight to about 105 parts by weight based on 100 parts by weight of the polymer protein. Since specific functions of each component have been described above, redundant descriptions are omitted.

본 실시예에 따른 탈부착식 미용 도구(1)의 글루 코팅층(20)은 초기 상태에서 점착력을 실질적으로 갖지 않을 수 있다. 즉, 초기 상태에서 글루 코팅층(20)은 끈적이지 않고 건조된 상태를 유지할 수 있다. 본 명세서에서, 초기 상태라 함은 수분이 제공되지 않고 실온 조건에서의 상태를 의미한다. 예를 들어, 초기 상태는 25℃의 상대습도 약 50% 이하의 상태, 또는 상대습도 약 40% 이하의 상태, 또는 상대습도 약 30% 이하의 상태를 의미할 수 있다. 다시 말해서, 초기 상태에서 탈부착식 미용 도구(1)의 글루 코팅층(20)을 피착물을 향하도록 하여 가압하더라도 미용 도구(1)와 피착물은 부착되지 않을 수 있다. 또, 초기 상태에서 글루 코팅층(20)의 촉감은 거칠거나 매끄러울 수 있다. The glue coating layer 20 of the removable beauty tool 1 according to the present embodiment may have substantially no adhesive force in an initial state. That is, in the initial state, the glue coating layer 20 may remain dry and not sticky. In the present specification, the initial state means a state at room temperature without providing moisture. For example, the initial state may mean a state of about 50% or less of relative humidity at 25 ° C., or a state of about 40% or less of relative humidity, or a state of about 30% or less of relative humidity. In other words, even if the glue coating layer 20 of the detachable cosmetic tool 1 is pressed toward the adherend in the initial state, the cosmetic tool 1 and the adherend may not be attached. In addition, in the initial state, the touch of the glue coating layer 20 may be rough or smooth.

또, 본 실시예에 따른 탈부착식 미용 도구(1)의 글루 코팅층(20)에 수분이 제공될 경우 글루 코팅층(20)은 접착력을 나타낼 수 있다. 즉, 글루 코팅층(20)이 수분과 접촉한 후에 탈부착식 미용 도구(1)의 글루 코팅층(20)을 피착물을 향하도록 하여 가압할 경우 미용 도구(1)와 피착물은 서로 부착될 수 있다. 다시 말해서, 적정량의 수분이 제공된 상태에서 글루 코팅층(20)은 접착력을 가지며, 미용 도구(1)를 사용자의 피부 내지는 모발에 부착할 수 있다. 비제한적인 일례로, 글루 코팅층(20)은 단위 면적당 약 15.0g/cm2 이상 30.0g/cm2 이하의 수분이 제공되면 사용자의 안검에 부착될 수 있을 정도의 접착력을 나타낼 수 있다.In addition, when moisture is provided to the glue coating layer 20 of the detachable cosmetic tool 1 according to the present embodiment, the glue coating layer 20 may exhibit adhesive strength. That is, after the glue coating layer 20 is in contact with moisture, when the glue coating layer 20 of the removable beauty tool 1 is pressed toward the adherend, the beauty tool 1 and the adherend may be attached to each other. . In other words, the glue coating layer 20 has an adhesive force in a state where an appropriate amount of moisture is provided, and the cosmetic tool 1 may be attached to the skin or hair of the user. As a non-limiting example, the glue coating layer 20 may exhibit an adhesive strength that can be attached to the user's eyelid when water of about 15.0 g / cm 2 or more and 30.0 g / cm 2 or less is provided per unit area.

본 실시예에 따른 탈부착식 미용 도구(1)는 글루 코팅층(20)을 포함하여 사용자에 의한 별도의 접착 부재 등의 도포 없이도 간편하게 부착이 가능하다. 또, 초기 상태에서 글루 코팅층(20)은 점착력을 갖지 않기 때문에 탈부착식 미용 도구(1)의 휴대와 보관이 용이한 장점이 있으며, 수분을 제공하는 것만으로 글루 코팅층(20)이 접착력을 나타낼 수 있어 사용이 간편하다. 즉, 사용자는 접착제 패키지 등 없이도 탈부착식 미용 도구(1) 패키지만을 휴대한 상태로 일상 생활이 가능하며, 탈부착식 미용 도구(1)의 부착을 원할 경우 주변에서 쉽게 구할 수 있는 물을 글루 코팅층(20)에 묻힌 후 바로 부착이 가능하다. 또, 사용자가 미용 도구(1)를 부착한 상태로 생활하다가 어떠한 이유로 미용 도구(1)가 탈착된 경우에도 별도의 접착제 없이 물을 글루 코팅층(20)에 재차 묻힌 후 손쉽게 부착이 가능하다.The detachable cosmetic tool 1 according to the present embodiment may be attached easily without the application of a separate adhesive member by the user, including the glue coating layer 20. In addition, in the initial state, since the adhesive coating layer 20 does not have adhesive strength, there is an advantage in that the removable beauty tool 1 is easy to carry and store, and the adhesive coating layer 20 may exhibit adhesive force only by providing moisture. Easy to use That is, the user can carry out daily life with only the removable beauty tool (1) package without the adhesive package, etc., if you want to attach the removable beauty tool (1) glue coating layer (water can be obtained easily around) It can be attached immediately after buried in 20). In addition, even when the user lives with the beauty tool 1 attached, for some reason, the beauty tool 1 is detached and then easily attached to the glue coating layer 20 without any additional adhesive.

또한 글루 코팅층(20)이 충분한 탄성을 나타내어 미용 도구(1)를 장시간 부착하고 있더라도 사용자의 피로감을 최소화할 수 있으며, 사용자의 피부 내지는 자연 속눈썹을 훼손하지 않고도 탈착이 용이한 효과가 있다. 뿐만 아니라, 인조 속눈썹의 반복적인 장착과 탈착에도 불구하고 글루 코팅층(20)은 지속적으로 접착성을 내재하고 있기 때문에 수 회의 재사용이 가능한 장점이 있다.In addition, even if the glue coating layer 20 exhibits sufficient elasticity, even if the beauty tool 1 is attached for a long time, the fatigue of the user can be minimized, and the detachment can be easily performed without damaging the user's skin or natural eyelashes. In addition, despite the repeated mounting and detachment of the artificial eyelashes, the glue coating layer 20 has an advantage that can be reused several times because it is inherently adhesive.

이하, 다른 실시예들에 대하여 설명한다. Hereinafter, other embodiments will be described.

본 발명의 다른 실시예에 따른 탈부착식 미용 도구는 글루 코팅층이 아크릴레이트계 화합물, 폴리비닐알코올계 화합물 및 가용화제를 포함하는 점이 도 1 등에서 설명한 탈부착식 미용 도구(1)와 상이한 점이다.The detachable cosmetic tool according to another embodiment of the present invention is different from the detachable cosmetic tool 1 described in FIG. 1 in that the glue coating layer includes an acrylate compound, a polyvinyl alcohol compound, and a solubilizer.

글루 코팅층은 전술한 본 발명의 다른 실시예에 따른 글루 조성물이 미용 도구 바디 상에 코팅 및 건조 내지는 경화되어 형성된 층일 수 있다. 예시적인 실시예에서, 건조된 상태의 글루 코팅층은 아크릴레이트계 화합물, 폴리비닐알코올계 화합물 및 가용화제를 포함하고, 디프로필렌글리콜을 더 포함할 수 있다.The glue coating layer may be a layer formed by coating and drying or curing the glue composition according to another embodiment of the present invention described above. In an exemplary embodiment, the dried glue coating layer may include an acrylate compound, a polyvinyl alcohol compound, and a solubilizer, and further include dipropylene glycol.

글루 코팅층 내의 폴리비닐알코올계 화합물의 함량은 상기 아크릴레이트계 화합물의 함량 보다 작을 수 있다. 예를 들어, 글루 코팅층은 상기 아크릴레이트계 화합물 100 중량부에 대해 상기 폴리비닐알코올계 화합물을 약 20 중량부 이상 약 30 중량부 이하, 또는 약 24 중량부 이상 약 26 중량부 이하의 범위로 포함할 수 있다. 또, 글루 코팅층 내의 가용화제의 함량은 상기 폴리비닐알코올계 화합물의 함량 보다 작을 수 있다. 예를 들어, 글루 코팅층은 상기 아크릴레이트계 화합물 100 중량부에 대해 가용화제를 약 1.0 중량부 이상 5.0 중량부 이하, 또는 약 3.0 중량부 이상 4.0 중량부 이하의 범위로 포함할 수 있다. 각 성분의 구체적인 기능에 대해서는 앞서 설명한 바 있으므로 중복되는 설명은 생략한다.The content of the polyvinyl alcohol compound in the glue coating layer may be smaller than the content of the acrylate compound. For example, the glue coating layer may include about 20 parts by weight to about 30 parts by weight, or about 24 parts by weight to about 26 parts by weight of the polyvinyl alcohol compound based on 100 parts by weight of the acrylate compound. can do. In addition, the content of the solubilizer in the glue coating layer may be less than the content of the polyvinyl alcohol-based compound. For example, the glue coating layer may include a solubilizer in a range of about 1.0 parts by weight to 5.0 parts by weight, or about 3.0 parts by weight to 4.0 parts by weight based on 100 parts by weight of the acrylate compound. Since specific functions of each component have been described above, redundant descriptions are omitted.

본 실시예에 따른 탈부착식 미용 도구의 글루 코팅층은 초기 상태에서 점착력을 갖지 않을 수 있다. 또, 본 실시예에 따른 탈부착식 미용 도구의 글루 코팅층에 수분이 제공될 경우 글루 코팅층은 접착력을 나타낼 수 있다. 초기 상태와 수분이 제공된 상태에서의 글루 코팅층의 기능에 대해서는 도 1 등과 함께 설명한 바 있으므로 중복되는 설명은 생략한다.The glue coating layer of the detachable cosmetic tool according to this embodiment may not have an adhesive force in an initial state. In addition, when moisture is provided to the glue coating layer of the removable beauty tool according to the present embodiment, the glue coating layer may exhibit adhesive force. Since the function of the glue coating layer in the initial state and the moisture provided state has been described with reference to FIG. 1 and the like, the overlapping description will be omitted.

본 발명의 또 다른 실시예에 따른 탈부착식 미용 도구는 글루 코팅층이 아크릴레이트계 화합물, 우레탄계 화합물 및 가용화제를 포함하는 점이 도 1 등에서 설명한 탈부착식 미용 도구(1)와 상이한 점이다.The detachable cosmetic tool according to another embodiment of the present invention is different from the detachable cosmetic tool 1 described in FIG. 1 in that the glue coating layer includes an acrylate compound, a urethane compound, and a solubilizer.

글루 코팅층은 전술한 본 발명의 또 다른 실시예에 따른 글루 조성물이 미용 도구 바디 상에 코팅 및 건조 내지는 경화되어 형성된 층일 수 있다. 예시적인 실시예에서, 건조된 상태의 글루 코팅층은 아크릴레이트계 화합물, 우레탄계 화합물 및 가용화제를 포함하고, 디프로필렌글리콜을 더 포함할 수 있다.The glue coating layer may be a layer formed by coating and drying or curing the glue composition according to another embodiment of the present invention described above. In an exemplary embodiment, the dried glue coating layer may include an acrylate compound, a urethane compound, and a solubilizer, and further include dipropylene glycol.

글루 코팅층 내의 우레탄계 화합물의 함량은 상기 아크릴레이트계 화합물의 함량 보다 작을 수 있다. 예를 들어, 글루 코팅층은 상기 아크릴레이트계 화합물 100 중량부에 대해 상기 우레탄계 화합물을 약 20 중량부 이상 약 30 중량부 이하, 또는 약 24 중량부 이상 약 26 중량부 이하의 범위로 포함할 수 있다. 또, 글루 코팅층 내의 가용화제의 함량은 상기 우레탄계 화합물의 함량 보다 작을 수 있다. 예를 들어, 글루 코팅층은 상기 아크릴레이트계 화합물 100 중량부에 대해 가용화제를 약 1.0 중량부 이상 5.0 중량부 이하, 또는 약 3.0 중량부 이상 4.0 중량부 이하의 범위로 포함할 수 있다. 각 성분의 구체적인 기능에 대해서는 앞서 설명한 바 있으므로 중복되는 설명은 생략한다.The content of the urethane compound in the glue coating layer may be smaller than the content of the acrylate compound. For example, the glue coating layer may include the urethane-based compound in a range of about 20 parts by weight to about 30 parts by weight, or about 24 parts by weight to about 26 parts by weight based on 100 parts by weight of the acrylate compound. . In addition, the content of the solubilizer in the glue coating layer may be less than the content of the urethane-based compound. For example, the glue coating layer may include a solubilizer in a range of about 1.0 parts by weight to 5.0 parts by weight, or about 3.0 parts by weight to 4.0 parts by weight based on 100 parts by weight of the acrylate compound. Since specific functions of each component have been described above, redundant descriptions are omitted.

본 실시예에 따른 탈부착식 미용 도구의 글루 코팅층은 초기 상태에서 점착력을 갖지 않을 수 있다. 또, 본 실시예에 따른 탈부착식 미용 도구의 글루 코팅층에 수분이 제공될 경우 글루 코팅층은 접착력을 나타낼 수 있다. 초기 상태와 수분이 제공된 상태에서의 글루 코팅층의 기능에 대해서는 도 1 등과 함께 설명한 바 있으므로 중복되는 설명은 생략한다.The glue coating layer of the detachable cosmetic tool according to this embodiment may not have an adhesive force in an initial state. In addition, when moisture is provided to the glue coating layer of the removable beauty tool according to the present embodiment, the glue coating layer may exhibit adhesive force. Since the function of the glue coating layer in the initial state and the moisture provided state has been described with reference to FIG. 1 and the like, the overlapping description will be omitted.

이하, 제조예 및 비교예를 더 참조하여 본 발명에 대해 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail with reference to Production Examples and Comparative Examples.

<제조예 1><Manufacture example 1>

젤라틴과 덱스트린, 글리세롤 및 증류수를 혼합하고 가열하며 1시간 동안 교반하였다. 그리고 잔탄 검을 더 첨가하여 글루 조성물을 제조하였다. 이 때 젤라틴, 덱스트린, 잔탄 검 및 글리세롤의 혼합 중량비는 30:20:6:30 이었다.Gelatin, dextrin, glycerol and distilled water were mixed, heated and stirred for 1 hour. Xanthan gum was further added to prepare a glue composition. At this time, the mixing weight ratio of gelatin, dextrin, xanthan gum and glycerol was 30: 20: 6: 30.

그 다음 폴리에틸렌 기재 표면에 제조된 글루 조성물을 도포하고 가열 건조하여 글루 코팅층이 형성된 탈부착식 인조 속눈썹을 제조하였다.Then, a glue composition prepared on the polyethylene substrate surface was applied and heat dried to prepare a detachable artificial eyelash having a glue coating layer formed thereon.

<제조예 2><Manufacture example 2>

아크릴레이트와 폴리비닐알코올 및 증류수를 혼합하고 가열하며 1시간 동안 교반하였다. 그리고 올리브 리퀴드를 더 첨가하여 글루 조성물을 제조하였다. 이 때 아크릴레이트, 폴리비닐알코올 및 올리브 리퀴드의 혼합 중량비는 77:20:3 이었다.The acrylate, polyvinyl alcohol and distilled water were mixed, heated and stirred for 1 hour. And olive liquid was further added to prepare a glue composition. At this time, the mixed weight ratio of acrylate, polyvinyl alcohol and olive liquid was 77: 20: 3.

그 다음 폴리에틸렌 기재 표면에 제조된 글루 조성물을 도포하고 가열 건조하여 글루 코팅층이 형성된 탈부착식 인조 속눈썹을 제조하였다.Then, a glue composition prepared on the polyethylene substrate surface was applied and heat dried to prepare a detachable artificial eyelash having a glue coating layer formed thereon.

<비교예 1-1><Comparative Example 1-1>

젤라틴, 덱스트린, 잔탄 검 및 글리세롤의 혼합 중량비를 30:15:6:40으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 글루 조성물을 제조하고, 글루 코팅층이 형성된 인조 속눈썹을 제조하였다.Glue composition was prepared in the same manner as in Preparation Example 1, except that the mixing weight ratio of gelatin, dextrin, xanthan gum and glycerol was 30: 15: 6: 40, to prepare artificial eyelashes having a glue coating layer.

<비교예 1-2><Comparative Example 1-2>

젤라틴, 덱스트린, 잔탄 검 및 글리세롤의 혼합 중량비를 30:20:10:35으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 글루 조성물을 제조하고, 글루 코팅층이 형성된 인조 속눈썹을 제조하였다.Glue composition was prepared in the same manner as in Preparation Example 1, except that the mixing weight ratio of gelatin, dextrin, xanthan gum and glycerol was 30: 20: 10: 35, to prepare artificial eyelashes having a glue coating layer.

<비교예 1-3><Comparative Example 1-3>

젤라틴, 덱스트린, 잔탄 검 및 글리세롤의 혼합 중량비를 20:20:6:30으로 한 것을 제외하고는 제조예 1과 동일한 방법으로 글루 조성물을 제조하고, 글루 코팅층이 형성된 인조 속눈썹을 제조하였다.Glue composition was prepared in the same manner as in Preparation Example 1, except that the mixing weight ratio of gelatin, dextrin, xanthan gum and glycerol was 20: 20: 6: 30, to prepare artificial eyelashes having a glue coating layer.

<비교예 2-1><Comparative Example 2-1>

아크릴레이트, 폴리비닐알코올 및 올리브 리퀴드의 혼합 중량비를 77:27:1으로 한 것을 제외하고는 제조예 2와 동일한 방법으로 글루 조성물을 제조하고, 글루 코팅층이 형성된 인조 속눈썹을 제조하였다.A glue composition was prepared in the same manner as in Preparation Example 2, except that the mixing weight ratio of acrylate, polyvinyl alcohol, and olive liquid was 77: 27: 1, and an artificial eyelash having a glue coating layer was prepared.

<비교예 2-2><Comparative Example 2-2>

아크릴레이트, 폴리비닐알코올 및 올리브 리퀴드의 혼합 중량비를 77:15:6으로 한 것을 제외하고는 제조예 2와 동일한 방법으로 글루 조성물을 제조하고, 글루 코팅층이 형성된 인조 속눈썹을 제조하였다.A glue composition was prepared in the same manner as in Preparation Example 2, except that the mixing weight ratio of acrylate, polyvinyl alcohol, and olive liquid was 77: 15: 6, and an artificial eyelash having a glue coating layer was prepared.

제조예 1과 제조예 2 및 비교예들에 따른 글루 조성물을 이용한 글루 코팅층 및 이를 이용한 인조 속눈썹을 비교한 결과를 하기 표 1에 나타내었다.The results of comparing the glue coating layer using the glue composition according to Preparation Example 1 and Preparation Example 2 and Comparative Examples and the artificial eyelashes using the same are shown in Table 1 below.

제조예 1Preparation Example 1 비교예 1-1Comparative Example 1-1 비교예 1-2Comparative Example 1-2 비교예 1-3Comparative Example 1-3 제조예 2Preparation Example 2 비교예 2-1Comparative Example 2-1 비교예 2-2Comparative Example 2-2 성분ingredient 젤라틴gelatin 3030 3030 3030 2020 -- -- -- 덱스트린dextrin 2020 1515 2020 2020 -- -- -- 잔탄 검Xanthan sword 66 66 1010 66 -- -- -- 글리세롤Glycerol 3030 4040 3535 3030 -- -- -- 아크릴레이트Acrylate -- -- -- -- 7777 7777 7777 폴리비닐알코올Polyvinyl alcohol -- -- -- -- 2020 2727 1515 올리브 리퀴드Olive Liquid -- -- -- -- 33 1One 66 응집현상Coagulation ×× △△ ○○ ○○ ×× ○○ ×× 도포성Applicability 우수Great 양호Good 불량Bad 보통usually 우수Great 보통usually 양호Good 글루 코팅층 상태Glue Coating State 끈적임 없음No stickiness 끈적임 없음No stickiness 끈적임Sticky 끈적임Sticky 끈적임 없음No stickiness 끈적임Sticky 끈적임Sticky 접착력Adhesion 우수Great 우수Great 양호Good 불량Bad 우수Great 불량Bad 우수Great 재사용 회수Reuse Recovery 10회 이상10 times or more 2회Episode 2 4회4 times -- 10회 이상10 times or more 1회1 time 3회3rd time

이상에서 본 발명의 실시예를 중심으로 설명하였으나 이는 단지 예시일 뿐 본 발명을 한정하는 것이 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 본 발명의 실시예의 본질적인 특성을 벗어나지 않는 범위에서 이상에 예시되지 않은 여러 가지의 변형과 응용이 가능함을 알 수 있을 것이다. 예를 들어, 본 발명의 실시예에 구체적으로 나타난 각 구성 요소는 변형하여 실시할 수 있다. 그리고 이러한 변형과 응용에 관계된 차이점들은 첨부된 청구 범위에서 규정하는 본 발명의 범위에 포함되는 것으로 해석되어야 할 것이다.Although described above with reference to the embodiments of the present invention, which is merely an example and not limiting the present invention, those skilled in the art to which the present invention pertains without departing from the essential characteristics of the embodiments of the present invention. It will be appreciated that various modifications and applications are not possible. For example, each component specifically shown in the embodiment of the present invention may be modified. And differences relating to such modifications and applications will have to be construed as being included in the scope of the invention defined in the appended claims.

Claims (8)

미용 도구 바디 및 상기 미용 도구 바디 상에 직접 배치된 글루 코팅층을 포함하는 탈부착식 미용 도구를 포함하는 미용 도구 패키지로서,
상기 미용 도구 패키지의 초기 상태에서, 상기 미용 도구의 상기 글루 코팅층은 점착력을 갖지 않고 건조된 상태이고,
상기 초기 상태에서 상기 글루 코팅층은 건조된 상태를 유지하다가,
상기 글루 코팅층이 수분과 접촉한 후에 상기 글루 코팅층은 점착력을 나타내고,
상기 글루 코팅층은,
100 중량부의 고분자 단백질 물질로서, 젤라틴으로 이루어진 고분자 단백질 물질; 60 중량부 이상 80 중량부 이하의 저분자 다당류 물질로서, 덱스트린으로 이루어진 저분자 다당류 물질; 15 중량부 이상 25 중량부 이하의 고분자 다당류 물질로서, 잔탄 검으로 이루어진 고분자 다당류 물질; 및 90 중량부 이상 110 중량부 이하의 알코올성 물질로서, 글리세롤로 이루어진 알코올성 물질을 포함하는, 미용 도구 패키지.A cosmetic tool package comprising a cosmetic tool body and a removable cosmetic tool comprising a glue coating layer disposed directly on the cosmetic tool body,
In the initial state of the beauty tool package, the glue coating layer of the beauty tool is in a dry state without adhesive force,
In the initial state, the glue coating layer is kept dry,
After the glue coating layer is in contact with moisture, the glue coating layer exhibits adhesive force,
The glue coating layer,
100 parts by weight of a polymer protein material, the polymer protein material consisting of gelatin; 60 to 80 parts by weight of the low molecular polysaccharide material, comprising: a low molecular polysaccharide material consisting of dextrin; 15 to 25 parts by weight of a polymer polysaccharide material, the polymer polysaccharide material consisting of xanthan gum; And 90 parts by weight or more and 110 parts by weight or less of alcoholic material, comprising an alcoholic material consisting of glycerol. 제1항에 있어서,
상기 미용 도구 바디는, 호형의 모주 및 상기 모주로부터 돌출된 다수의 세모를 포함하고,
상기 미용 도구는 인조 속눈썹인, 미용 도구 패키지.The method of claim 1,
The beauty instrument body includes an arc-shaped hairline and a plurality of hairs protruding from the hairline,
The beauty tool is an artificial eyelash, beauty tool package. 삭제delete 삭제delete 미용 도구 바디 및 상기 미용 도구 바디 상에 직접 배치된 글루 코팅층을 포함하는 탈부착식 미용 도구를 포함하는 미용 도구 패키지로서,
상기 미용 도구 패키지의 초기 상태에서, 상기 미용 도구의 상기 글루 코팅층은 점착력을 갖지 않고 건조된 상태이고,
상기 초기 상태에서 상기 글루 코팅층은 건조된 상태를 유지하다가,
상기 글루 코팅층이 수분과 접촉한 후에 상기 글루 코팅층은 점착력을 나타내고,
상기 글루 코팅층은,
100 중량부의 아크릴레이트계 화합물;
20 중량부 이상 30 중량부 이하의 폴리비닐알코올계 화합물; 및
1.0 중량부 이상 5.0 중량부 이하의 가용화제로서, 올리브 리퀴드를 포함하는 가용화제를 포함하는, 미용 도구 패키지.A cosmetic tool package comprising a cosmetic tool body and a removable cosmetic tool comprising a glue coating layer disposed directly on the cosmetic tool body,
In the initial state of the beauty tool package, the glue coating layer of the beauty tool is in a dry state without adhesive force,
In the initial state, the glue coating layer is kept dry,
After the glue coating layer is in contact with moisture, the glue coating layer exhibits adhesive force,
The glue coating layer,
100 parts by weight of an acrylate compound;
20 parts by weight or more and 30 parts by weight or less of a polyvinyl alcohol compound; And
A cosmetic instrument package comprising a solubilizer comprising 1.0 parts by weight to 5.0 parts by weight of a solubilizer comprising olive liquid. 100 중량부의 고분자 단백질 물질로서, 젤라틴으로 이루어진 고분자 단백질 물질; 60 중량부 이상 80 중량부 이하의 저분자 다당류 물질로서, 덱스트린으로 이루어진 저분자 다당류 물질; 18 중량부 이상 22 중량부 이하의 고분자 다당류 물질로서, 잔탄 검으로 이루어진 고분자 다당류 물질; 및 95 중량부 이상 105 중량부 이하의 글리세롤을 포함하는 글루 조성물100 parts by weight of a polymer protein material, the polymer protein material consisting of gelatin; 60 to 80 parts by weight of the low molecular polysaccharide material, comprising: a low molecular polysaccharide material consisting of dextrin; 18 to 22 parts by weight of a polymer polysaccharide material, the polymer polysaccharide material consisting of xanthan gum; And at least 95 parts by weight and at most 105 parts by weight of glycerol. 제6항에 있어서,
1.0 중량부 이상 5.0 중량부 이하의 올리브 리퀴드를 더 포함하는 글루 조성물.The method of claim 6,
A glue composition further comprising 1.0 part by weight to 5.0 parts by weight of olive liquid. 삭제delete
KR1020180089704A 2018-08-01 2018-08-01 Glue composition and detachable beauty tool using the same KR102000540B1 (en)