JP2002220319A - Adhesive sheet for cosmetic - Google Patents
Adhesive sheet for cosmeticInfo
- Publication number
- JP2002220319A JP2002220319A JP2001016828A JP2001016828A JP2002220319A JP 2002220319 A JP2002220319 A JP 2002220319A JP 2001016828 A JP2001016828 A JP 2001016828A JP 2001016828 A JP2001016828 A JP 2001016828A JP 2002220319 A JP2002220319 A JP 2002220319A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- cosmetic
- adhesive sheet
- acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は化粧用粘着シートに
関し、詳しくは額や眉間、目尻などに生じる皺部分に貼
付して物理的に皺を伸ばすことによって、皮膚面のたる
みを取り除き、皺を除去することを目的とする化粧用粘
着シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cosmetic pressure-sensitive adhesive sheet, and more particularly, removes slack on a skin surface by sticking to a wrinkle formed on a forehead, a space between eyebrows, the corners of the eyes and the like to physically remove wrinkles. The present invention relates to a cosmetic adhesive sheet intended to be removed.
【０００２】[0002]
【従来の技術】美容に関する関心は従来から絶えること
がなく、女性にとっては永遠の課題でもある。その中で
も、加齢に伴い顔面に生じる皺を除去する方法について
は、従来から多くの方法が提案されている。2. Description of the Related Art Interest in beauty has always been present and is an eternal issue for women. Above all, many methods have been proposed for removing wrinkles generated on the face with aging.
【０００３】例えば、最も確実に皺を除去する方法とし
ては、美容整形手術による物理的除去方法があり、皺が
生じた部分を引っ張って強制的に皺を伸ばし、弛んだ皺
を切除するという方法である。しかしながら、この方法
は手術にて行うために、痛みを伴うと共に傷口が残るこ
ともあり、また、施術費用も高いので、決して最良の方
法とは云いがたいものである。[0003] For example, the most reliable method of removing wrinkles is a physical removal method using cosmetic surgery, in which a wrinkled portion is pulled to forcibly stretch the wrinkles and the loose wrinkles are removed. It is. However, since this method is performed by surgery, it may be painful and leave a wound, and the operation cost is high. Therefore, this method is far from the best method.
【０００４】また、美容院やエステティックサロンのよ
うな専門店で顔面マッサージを行う方法もある。この方
法はマッサージによって顔面の皮膚の血行を良くし、新
陳代謝を高めて皮膚の血行を良好にして弛みを少なくす
るものであって、一般的には皺の発生を抑制しようとす
るものであり、マッサージを用いて一旦生じた皺を除去
するのは極めて困難なものである。There is also a method of performing a face massage at a specialty store such as a beauty salon or an aesthetic salon. This method improves the blood circulation of the skin of the face by massage, enhances the metabolism, improves the blood circulation of the skin and reduces looseness, and is generally intended to suppress the occurrence of wrinkles, It is extremely difficult to remove wrinkles once formed using massage.
【０００５】さらに、近年では皮膚の弛みを少なくする
ために、ビタミンＥなどの有効成分を含有させた栄養ク
リームを塗布し、リフトアップ効果を狙った製品も開発
されている。これらの製品も弛みを防止することを主目
的としているので、一旦生じた皺を除去することは困難
である。Further, in recent years, products for applying a nutritional cream containing an active ingredient such as vitamin E to reduce the loosening of the skin have been developed in order to achieve a lift-up effect. Since these products also have a main purpose of preventing loosening, it is difficult to remove wrinkles once formed.
【０００６】また、皮膜形成性の化粧パッククリームや
化粧パックシートによって、顔の汚れを除去したり、潤
いを与える方法も美容法としては一般的であるが、これ
らの方法でも皺を除去することは困難である。[0006] It is also a common cosmetic method to remove facial stains and moisturize with a film-forming cosmetic pack cream or cosmetic pack sheet, but these methods also remove wrinkles. It is difficult.
【０００７】上記の各方法においてクリームや乳液を用
いた方法では、手指を汚す、塗布操作が煩わしい、など
の問題がある。さらに、皮膜形成性の化粧パッククリー
ムや化粧パックシートでは、クリームが乾燥して皮膜化
するまで数分〜十数分間待つ必要があるので精神的な苦
痛を伴い、パックシートを用いる場合には、皮膚面を予
め水や化粧水で濡らすか、シートに水や化粧するを塗布
して使用しなければならず、決して取扱性の良好なもの
とは云えない。[0007] The methods using creams or emulsions in the above-mentioned methods have problems such as soiling of fingers and troublesome application operation. Furthermore, in the case of a film-forming cosmetic pack cream or a cosmetic pack sheet, it is necessary to wait several minutes to several tens of minutes until the cream dries and turns into a film. The skin surface must be wetted with water or lotion in advance, or water or makeup must be applied to the sheet before use, and it cannot be said that it has good handleability.
【０００８】また、これら顔用の美容製品は、決して皮
膚面にダメージを与えるものであってはならず、製品化
に当たっては、皮膚刺激性がないように細心の注意を払
わなければならないのである。In addition, these facial beauty products must not cause any damage to the skin surface, and in commercialization, great care must be taken so as not to cause skin irritation. .
【０００９】[0009]
【発明が解決しようとする課題】そこで、本発明は、上
記従来技術の問題点を解決するためになされたものであ
って、極めて簡単な操作で皮膚面に適用することがで
き、しかも皮膚刺激をほとんど生起することなく、物理
的に皺を除去する方法を検討した結果、特定の粘着剤層
を有する粘着シートを用いることによって、従来にない
全く新しい皺除去シートが得られることを見い出し、本
発明を完成するに至った。SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems of the prior art, and can be applied to the skin surface by an extremely simple operation. As a result of studying a method for physically removing wrinkles without causing any wrinkles, it was found that an entirely new wrinkle removal sheet could be obtained by using a pressure-sensitive adhesive sheet having a specific pressure-sensitive adhesive layer. The invention has been completed.
【００１０】[0010]
【課題を解決するための手段】即ち、本発明は、可撓性
を有するシート状基材の片面に粘着剤層が形成されてな
る粘着シートであって、粘着剤層がアクリル系粘着剤、
有機液状成分およびポリペプチドを含有すると共に、架
橋処理が施されていることを特徴とする化粧用粘着シー
トを提供するものである。That is, the present invention relates to a pressure-sensitive adhesive sheet comprising a flexible sheet-like substrate having a pressure-sensitive adhesive layer formed on one surface thereof, wherein the pressure-sensitive adhesive layer comprises an acrylic pressure-sensitive adhesive;
An object of the present invention is to provide a cosmetic adhesive sheet containing an organic liquid component and a polypeptide and having been subjected to a crosslinking treatment.
【００１１】[0011]
【発明の実施の形態】本発明の化粧用粘着シートに用い
るシート状基材は、粘着剤層を保持するための機能を有
すると共に、皮膚面の曲面に適合するために適度な可撓
性を有するものが用いられる。具体的には、酢酸セルロ
ース、エチルセルロースなどのセルロース系フィルム
や、ポリエチレンテレフタレートなどのポリエステル系
フィルム、ポリエチレン、ポリプロピレン、エチレン／
プロピレン共重合体などのポリオレフィン系フィル
ム、、酢酸ビニル−塩化ビニル共重合体、軟質ポリ塩化
ビニル、ポリウレタン、ポリ塩化ビニリデン、エチレン
−酢酸ビニル共重合体、サーリン、ポリテトラフルオロ
エチレンなどの単独フィルムやこれらの積層フィルム、
各種金属箔、金属蒸着フィルムなどを用いることができ
る。また、これらの材料からなる繊維から作られた織布
や不織布などの布帛、抄紙なども用いることができる。
また、上記シート状基材のうち、柔軟性や肌触り性、透
湿性などの点からは、紙基材や不織布などの多孔質構造
を有する基材を用いることが好ましい。BEST MODE FOR CARRYING OUT THE INVENTION The sheet-like base material used for the cosmetic pressure-sensitive adhesive sheet of the present invention has a function of holding a pressure-sensitive adhesive layer and has an appropriate flexibility to conform to the curved surface of the skin surface. Is used. Specifically, cellulose films such as cellulose acetate and ethyl cellulose, polyester films such as polyethylene terephthalate, polyethylene, polypropylene, ethylene /
Polyolefin-based films such as propylene copolymer, vinyl acetate-vinyl chloride copolymer, flexible polyvinyl chloride, polyurethane, polyvinylidene chloride, ethylene-vinyl acetate copolymer, Surlyn, polytetrafluoroethylene, etc. These laminated films,
Various metal foils, metal-deposited films, and the like can be used. In addition, fabrics such as woven fabrics and nonwoven fabrics made of fibers made of these materials, papermaking, and the like can also be used.
In addition, among the above-mentioned sheet-like base materials, it is preferable to use a base material having a porous structure such as a paper base material or a nonwoven fabric from the viewpoint of flexibility, softness, moisture permeability and the like.
【００１２】上記した本発明に用いるシート状基材は、
プラスチックシートからなる基材の場合には、０．５〜
５００μｍ、好ましくは２〜３００μｍ、特に好ましく
は５〜１５０μｍの厚みを有するものを採用することが
好ましく、紙や不織布などの多孔質基材の場合には、１
〜１００ｇ／ｍ2 、好ましくは１０〜９０ｇ／ｍ2 、特
に好ましくは１５〜６０ｇ／ｍ2 の目付量の基材を採用
することが好ましい。The sheet-like base material used in the present invention is
In the case of a substrate made of a plastic sheet, 0.5 to
It is preferable to employ a material having a thickness of 500 μm, preferably 2 to 300 μm, particularly preferably 5 to 150 μm.
It is preferable to employ a substrate having a basis weight of １００100 g / m 2 , preferably 10-90 g / m 2 , particularly preferably 15-60 g / m 2 .
【００１３】本発明の化粧用粘着シートにおいて、上記
シート状基材の片面に形成される粘着剤層は、皮膚面に
簡単に密着して皮膚面を物理的に粘着固定すると共に、
貼付中には皮膚刺激性がなく、また、皮膚面から剥離す
る際には皮膚面に痛みや角質損傷などを与えずに簡単に
剥離できるような適度な皮膚接着性を有するものを用い
る。[0013] In the cosmetic pressure-sensitive adhesive sheet of the present invention, the pressure-sensitive adhesive layer formed on one surface of the sheet-like base material easily adheres to the skin surface to physically and firmly fix the skin surface,
A material having no skin irritation during application and having an appropriate skin adhesive property that can be easily peeled off without causing pain or keratin damage to the skin surface when peeled from the skin surface is used.
【００１４】具体的には、所謂、乾燥状態の粘着剤を用
いるのではなく、有機液状成分を含有させて粘着剤層に
適度な潤いと柔軟性を与え、さらに、架橋処理を施すこ
とによって、内部凝集力を補強したものが用いられる。
つまり、有機液状成分を含有させることにより、粘着剤
層全体が柔軟になって、皮膚面に貼付した際の密着、固
定性が向上する。しかも、有機液状成分を含有させてい
るので、貼付している皮膚面に適度な潤い感を与えるこ
とができるのである。Specifically, instead of using a so-called dry pressure-sensitive adhesive, an organic liquid component is contained to give the pressure-sensitive adhesive layer an appropriate amount of moisture and flexibility. What strengthened internal cohesion is used.
That is, by containing the organic liquid component, the entire pressure-sensitive adhesive layer becomes flexible, and the adhesion and fixability when applied to the skin surface are improved. In addition, since the organic liquid component is contained, an appropriate moist feeling can be given to the skin surface to which the adhesive is applied.
【００１５】上記のような粘着剤層を形成するための粘
着剤としては、有機液状成分と適度に相溶し、粘着剤層
中に有機液状成分をブルーミングさせずに安定的に保持
することができるものであれば、限定されるものではな
く、粘着特性の調整のしやすさや有機液状成分との優れ
た相溶性の点から、本発明においてはアクリル系粘着剤
を用いる。As the pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer as described above, the pressure-sensitive adhesive is suitably compatible with the organic liquid component and stably holds the organic liquid component in the pressure-sensitive adhesive layer without blooming. It is not limited as long as it can be used, and an acrylic pressure-sensitive adhesive is used in the present invention from the viewpoint of easy adjustment of pressure-sensitive properties and excellent compatibility with an organic liquid component.
【００１６】このようなアクリル系粘着剤のうち、皮膚
面に対する接着性確保の点から、主成分単量体として
（メタ）アクリル酸アルキルエステルを用いたものが好
ましく、また、粘着剤層の内部凝集力を向上させるため
に、側鎖にカルボキシル基を有する単量体との共重合体
を用いることが好ましい。さらに、側鎖にカルボキシル
基を有する単量体を共重合した粘着剤は、分子内に酸性
基となるカルボキシル基を有するので、粘着剤層に適度
な内部凝集力を付与し、皮膚面に接着した場合に優れた
皮膚接着性を発揮するが、共重合量が多いと皮膚刺激性
を発現する原因となる恐れがある。従って、このような
場合には、カルボキシル基の一部もしくは全部を中和し
ておくことが好ましい。Among such acrylic pressure-sensitive adhesives, those using (meth) acrylic acid alkyl ester as a main component monomer are preferable from the viewpoint of ensuring adhesiveness to the skin surface. In order to improve cohesion, it is preferable to use a copolymer with a monomer having a carboxyl group in a side chain. Furthermore, the pressure-sensitive adhesive obtained by copolymerizing a monomer having a carboxyl group in the side chain has a carboxyl group that becomes an acidic group in the molecule, so that the pressure-sensitive adhesive layer has an appropriate internal cohesive force and adheres to the skin surface In this case, excellent skin adhesion is exhibited, but a large amount of copolymer may cause skin irritation. Therefore, in such a case, it is preferable to neutralize a part or all of the carboxyl groups.
【００１７】本発明において上記アクリル系粘着剤を調
製するために用いられる（メタ）アクリル酸アルキルエ
ステルとしては、アルキル基の炭素数が２〜１８、好ま
しくは４〜１５の（メタ）アクリル酸アルキルエステル
が好ましく、具体的には（メタ）アクリル酸のエチルエ
ステル、プロピルエステル、ブチルエステル、ペンチル
エステル、ヘキシルエステル、ヘプチルエステル、オク
チルエステル、ノニルエステル、デシルエステル、ドデ
シルエステル、ウンデシルエステル、トリデシルエステ
ルなどを一種もしくは二種以上用いることができる。ま
た、これらのエステルは直鎖状であっても、分岐鎖状で
もよいものである。In the present invention, the alkyl (meth) acrylate used for preparing the acrylic pressure-sensitive adhesive includes an alkyl (meth) acrylate having an alkyl group having 2 to 18, preferably 4 to 15 carbon atoms. Esters are preferred, and specifically, ethyl ester, propyl ester, butyl ester, pentyl ester, hexyl ester, heptyl ester, octyl ester, nonyl ester, decyl ester, dodecyl ester, undecyl ester, tridecyl of (meth) acrylic acid Ester or the like can be used alone or in combination of two or more. These esters may be linear or branched.
【００１８】また、側鎖にカルボキシル基を有する単量
体としては、アクリル酸、メタクリル酸、イタコン酸、
クロトン酸、マレイン酸、無水マレイン酸などの単量体
を用いることができ、こられのうち、皮膚接着力や凝集
力の向上などの粘着特性を向上させるために、アクリル
酸やメタクリル酸を用いることが好ましい。これらの単
量体はアクリル系粘着剤を調製するための全単量体混合
物中に３〜５０重量％、好ましくは５〜４０重量％配合
することがよい。The monomers having a carboxyl group in the side chain include acrylic acid, methacrylic acid, itaconic acid,
Monomers such as crotonic acid, maleic acid, and maleic anhydride can be used, and among them, acrylic acid or methacrylic acid is used to improve the adhesive properties such as improvement of skin adhesion and cohesion. Is preferred. These monomers may be blended in an amount of 3 to 50% by weight, preferably 5 to 40% by weight, in the total monomer mixture for preparing the acrylic pressure-sensitive adhesive.
【００１９】なお、本発明において用いられるアクリル
系粘着剤には、上記単量体以外に、粘着特性を阻害しな
い範囲であれば、他の共重合体単量体を共重合させるこ
とができる。具体的には、スチレンスルホン酸、アリル
スルホン酸、スルホプロピル（メタ）アクリレート、
（メタ）アクリロイルオキシナフタレンスルホン酸、ア
クリルアミドメチルプロパンスルホン酸などのスルホキ
シル基含有単量体、ヒドロキシエチル （メタ）アクリ
レート、ヒドロキシプロピル（メタ）アクリレートなど
のヒドロキシル基含有単量体、（メタ）アクリルアミ
ド、ジメチル（メタ）アクリルアミド、Ｎ−ブチル（メ
タ）アクリルアミド、Ｎ−メチロール（メタ）アクリル
アミド、Ｎ−メチロールプロパン（メタ）アクリルアミ
ドなどのアミド基含有単量体、アミノエチル（メタ）ア
クリレート、ジメチルアミノエチル（メタ）アクリレー
ト、ｔｅｒｔ−ブチルアミノエチル（メタ）アクリレー
トなどのアミノ基含有単量体、メトキシエチル（メタ）
アクリレート、エトキシエチル（メタ）アクリレートな
どのアルコキシアルキル基含有単量体、メトキシエチレ
ングリコール（メタ）アクリレート、テトラヒドロフル
フリル（メタ）アクリレート、メトキシジエチレングリ
コール（メタ）アクリレート、メトキシポリエチレング
リコール（メタ）アクリレート、メトキシポリプロピレ
ングリコール（メタ）アクリレートなどのアルコキシ基
含有単量体、（メタ）アクリロニトリル、酢酸ビニル、
プロピオン酸ビニル、ビニルピロリドンなどのビニル系
単量体などを一種もしくは二種以上用いることができ
る。これらのうち、架橋処理の際の架橋点の調整や粘着
特性の調整のしやすさの点から、カルボキシル基含有単
量体やヒドロキシル基含有単量体、アルコキシル基やエ
ーテル基を含有する単量体を用いることが好ましい。The acrylic pressure-sensitive adhesive used in the present invention may be copolymerized with other copolymer monomers other than the above monomers, as long as the pressure-sensitive adhesive properties are not impaired. Specifically, styrenesulfonic acid, allylsulfonic acid, sulfopropyl (meth) acrylate,
(Meth) acryloyloxynaphthalenesulfonic acid, sulfoxyl group-containing monomers such as acrylamidomethylpropanesulfonic acid, hydroxyethyl (meth) acrylate, hydroxyl group-containing monomers such as hydroxypropyl (meth) acrylate, (meth) acrylamide, Amide group-containing monomers such as dimethyl (meth) acrylamide, N-butyl (meth) acrylamide, N-methylol (meth) acrylamide, N-methylolpropane (meth) acrylamide, aminoethyl (meth) acrylate, dimethylaminoethyl ( Amino group-containing monomers such as meth) acrylate and tert-butylaminoethyl (meth) acrylate, and methoxyethyl (meth)
Alkoxyalkyl group-containing monomers such as acrylate and ethoxyethyl (meth) acrylate, methoxyethylene glycol (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, methoxydiethylene glycol (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, and methoxy Alkoxy group-containing monomers such as polypropylene glycol (meth) acrylate, (meth) acrylonitrile, vinyl acetate,
One or more vinyl monomers such as vinyl propionate and vinyl pyrrolidone can be used. Among these, a carboxyl group-containing monomer or a hydroxyl group-containing monomer, a monomer containing an alkoxyl group or an ether group, from the viewpoint of easy adjustment of a crosslinking point and an adhesive property at the time of a crosslinking treatment. It is preferred to use a body.
【００２０】また、上記のように側鎖にカルボキシル基
を有する単量体を用いた場合には、カルボキシル基によ
る酸性を中和する目的で、アンモニアや、トリエタノー
ルアミンなどのアミン類、水酸化ナトリウムや水酸化カ
リウムなどのアルカリ金属の水酸化物を所定量配合して
カルボキシル基の一部もしくは全部を中和処理すること
が好ましい。When a monomer having a carboxyl group in the side chain is used as described above, ammonia, amines such as triethanolamine, hydroxylamine, etc. are used to neutralize the acidity due to the carboxyl group. It is preferable to mix a predetermined amount of an alkali metal hydroxide such as sodium or potassium hydroxide to neutralize a part or all of the carboxyl groups.
【００２１】さらに、上記本発明における粘着剤層に
は、有機液状成分としてエステル化物を用いることが好
ましい。エステル化物はアクリル系共重合体との相溶性
が良好であり、粘着剤層に柔らかくし皮膚面に対してソ
フトに接触して密着性が向上するので、本発明の代表的
用途である顔面の皺伸ばし用途には最適である。Further, in the pressure-sensitive adhesive layer in the present invention, it is preferable to use an esterified compound as an organic liquid component. Since the esterified product has good compatibility with the acrylic copolymer, and softens the pressure-sensitive adhesive layer and softly contacts the skin surface to improve the adhesion, the facial application which is a typical application of the present invention is used. Ideal for wrinkle reduction applications.
【００２２】上記エステル化物としては、代表的には炭
素数８〜２０の一塩基酸または多塩基酸と炭素数１４〜
２０の分岐アルコールとのエステル化物、および／また
は炭素数１４〜２０の不飽和脂肪酸または不飽和分岐酸
と４価以下のアルコールとのエステル化物が用いられるAs the esterified product, typically, a monobasic acid or polybasic acid having 8 to 20 carbon atoms and 14 to 14 carbon atoms are used.
An esterified product of a branched alcohol having 20 and / or an unsaturated fatty acid or an unsaturated branched acid having 14 to 20 carbon atoms and an alcohol having a valency of 4 or less is used.
【００２３】前者のエステル化物としての炭素数８〜２
０の一塩基酸または多塩基酸と炭素数１４〜２０の分岐
アルコールとのエステル化物は、粘着剤層に均一に溶解
して粘着剤層が皮膚面へ密着する濡れ性を向上させる成
分である。炭素数が上記範囲外であると、該エステル化
物による上記作用が充分に発揮しにくくなるだけでな
く、アクリル系共重合体との相溶性が悪くなり、ブルー
ミング現象を生じることがある。The former esterified product having 8 to 2 carbon atoms
The esterified product of 0 monobasic acid or polybasic acid and a branched alcohol having 14 to 20 carbon atoms is a component that uniformly dissolves in the pressure-sensitive adhesive layer and improves the wettability in which the pressure-sensitive adhesive layer adheres to the skin surface. . If the number of carbons is outside the above range, not only the above effects of the esterified product will not be sufficiently exerted, but also the compatibility with the acrylic copolymer will be deteriorated, and a blooming phenomenon may occur.
【００２４】このような前者のエステル化物としては、
具体的にはラウリン酸イソステアリル、ミリスチン酸イ
ソセチル、ミリスチン酸オクチルドデシル、パルミチン
酸イソステアリル、ステアリン酸イソセチル、オレイン
酸オクチルドデシル、アジピン酸ジイソステアリル、セ
バシン酸ジイソセチル、トリメリット酸トリオレイル、
トリメリット酸トリイソセチルなどを一種もしくは二種
以上配合することができる。As the former esterified product,
Specifically, isostearyl laurate, isocetyl myristate, octyldodecyl myristate, isostearyl palmitate, isocetyl stearate, octyldodecyl oleate, diisostearyl adipate, diisocetyl sebacate, trioleyl trimellitate,
One or two or more triisocetyl trimellitates can be blended.
【００２５】また、後者のエステル化物としての炭素数
１４〜２０の不飽和脂肪酸または不飽和分岐酸と４価以
下のアルコールとのエステル化物は、粘着剤層に均一に
溶解して皮膚面に対する粘着剤層の密着性を向上させる
成分である。炭素数が上記範囲外であると、該エステル
化物による上記作用が充分に発揮しにくくなるだけでな
く、アクリル系共重合体との相溶性が悪くなり、ブルー
ミング現象を生じる場合がある。The latter esterified product of an unsaturated fatty acid or unsaturated branched acid having 14 to 20 carbon atoms and an alcohol having a valency of 4 or less as an esterified product is uniformly dissolved in the adhesive layer and adhered to the skin surface. It is a component that improves the adhesiveness of the agent layer. If the number of carbons is outside the above range, not only the above-mentioned effects of the esterified product will not be sufficiently exerted, but also the compatibility with the acrylic copolymer will deteriorate, and a blooming phenomenon may occur.
【００２６】このような後者のエステル化物としては、
具体的には、ミリストレイン酸、オレイン酸、リノール
酸、リノレン酸、イソパルミチン酸、イソステアリン酸
などの不飽和脂肪酸または不飽和分岐酸に、エチレング
リコールやプロピレングリコール、グリセリン、トリメ
チロールプロパン、ペンタエリスリトール、ソルビタン
などの４価以下のアルコールとからなるエステル化物を
一種もしくは二種以上配合することができる。As the latter esterified product,
Specifically, unsaturated fatty acids or unsaturated branched acids such as myristoleic acid, oleic acid, linoleic acid, linolenic acid, isopalmitic acid, isostearic acid, ethylene glycol, propylene glycol, glycerin, trimethylolpropane, pentaerythritol , Or one or two or more esterified compounds composed of an alcohol having a valency of 4 or less such as sorbitan.
【００２７】上記二種類のエステル化物はそれぞれ単独
もしくは組み合わせて、後述する架橋処理が施されたア
クリル系共重合体に配合した場合、その配合量はアクリ
ル系共重合体１００重量部に対して、エステル化物の総
量が３０〜１００重量部、好ましくは３０〜８０重量部
の範囲になるように調製する。エステル化物の配合量が
３０重量％に満たない場合には、皮膚面に対する粘着剤
層の濡れ性が不充分になる恐れがあり、また、１００重
量部を超える配合量では、エステル化物が粘着剤層から
ブルーミングして皮膚面を汚染する場合がある。When the above two types of esterified compounds are used alone or in combination with each other in an acrylic copolymer which has been subjected to a cross-linking treatment described below, the compounding amount is based on 100 parts by weight of the acrylic copolymer. The total amount of the esterified product is adjusted to 30 to 100 parts by weight, preferably 30 to 80 parts by weight. When the amount of the esterified compound is less than 30% by weight, the wettability of the pressure-sensitive adhesive layer to the skin surface may be insufficient. May bloom from the layer and contaminate the skin surface.
【００２８】なお、上記エステル化物は不飽和結合を有
するので、大気中の酸素によって酸化劣化して物性変化
を起こし、所望の特性を発揮しない恐れがあり、このよ
うな場合には自体公知の酸化防止剤を粘着剤層中に配合
しておくことが好ましい。Since the above-mentioned ester has an unsaturated bond, it may be oxidized and degraded by atmospheric oxygen to cause a change in physical properties, thereby failing to exhibit desired properties. It is preferable that an inhibitor is incorporated in the pressure-sensitive adhesive layer.
【００２９】また、本発明においては前記した粘着剤層
中にポリペプチドを含有させる。ポリペプチドは貼付す
る皮膚面を保湿するために重要な作用を有するものであ
り、貼付した皮膚面に充分な潤いを与えると共に、皺伸
ばし作用を助長する働きをすると考えられる。In the present invention, the pressure-sensitive adhesive layer contains a polypeptide. The polypeptide has an important function for moisturizing the skin surface to be applied, and is considered to provide sufficient moisture to the applied skin surface and promote a wrinkle-growing action.
【００３０】このようなポリペプチドとしては、ペプチ
ド結合を有するものであればポリアミノ酸やタンパク質
など特に限定されるものではないが、保湿効果を充分に
発揮させるためにはコラーゲンタンパク質を用いること
が好ましい。また、コラーゲンタンパク質は、その構造
状の特徴から、イオン結合や水素結合、ファン・デル・
ワールス力によって皮膚面に収着して保湿効果を発揮す
るのであるが、耐熱性に乏しく、加熱すると変性してゼ
ラチンに分解することが知られている。The polypeptide is not particularly limited as long as it has a peptide bond, such as a polyamino acid and a protein, but it is preferable to use a collagen protein in order to sufficiently exert a moisturizing effect. . Collagen proteins are characterized by their ionic and hydrogen bonds, van der
It is sorbed on the skin surface by the Waals force and exerts a moisturizing effect, but has poor heat resistance and is known to be denatured and decomposed into gelatin when heated.
【００３１】一般に、粘着シートの製造工程で粘着剤溶
液の塗布、乾燥を行う工程があり、加熱操作が必要とな
るので、コラーゲンタンパク質を配合していると、ゼラ
チンに分解し、特に、粘着剤層の表層部に存在していた
コラーゲンタンパク質がゼラチン化して粘着力の低下を
引き起こすようになる。このように本発明の化粧用粘着
シートが加熱製造もしくは加熱保存される可能性のある
場合には、コラーゲンタンパク質を加水分解して、重量
平均分子量を４００〜４０００、好ましくは５００〜２
０００程度になるように分子鎖を分断したものを用いる
ことが好ましい。このように加水分解されたコラーゲン
タンパク質は、コラーゲンタンパク質が本来有する保湿
機能を低下させずに、耐熱性を付加することができ、皮
膚接着力の低下を招くことがないのである。In general, there is a step of applying and drying a pressure-sensitive adhesive solution in the process of producing a pressure-sensitive adhesive sheet, and a heating operation is required. Collagen proteins existing in the surface layer of the layer are gelatinized and cause a decrease in adhesive strength. As described above, when the cosmetic pressure-sensitive adhesive sheet of the present invention may be heated or stored by heating, the collagen protein is hydrolyzed to have a weight average molecular weight of 400 to 4,000, preferably 500 to 2,000.
It is preferable to use one obtained by dividing the molecular chain so as to be about 000. The collagen protein hydrolyzed in this manner can add heat resistance without lowering the moisturizing function inherent to the collagen protein, and does not cause a decrease in skin adhesive strength.
【００３２】上記したポリペプチドは粘着剤層の主構成
成分であるアクリル系粘着剤１００重量部当たり、０．
１〜３０重量部、好ましくは０．１〜２０重量部の範囲
で含有させる。ポリペプチドの含有量が０．１重量部に
満たない場合には、充分な保湿性を皮膚面に与えること
ができず、所望する効果を発揮できない恐れがある。一
方ポリペプチドの含有量が３０重量部を超えると、ポリ
ペプチドと共に含有させている有機液状成分が粘着剤層
中から押し出されるようにして滲出し、皮膚接着性の低
下を招く恐れが生じる。The above-mentioned polypeptide is used in an amount of 0.1 to 100 parts by weight of the acrylic pressure-sensitive adhesive which is a main component of the pressure-sensitive adhesive layer.
It is contained in an amount of 1 to 30 parts by weight, preferably 0.1 to 20 parts by weight. When the content of the polypeptide is less than 0.1 part by weight, sufficient moisturizing property cannot be given to the skin surface, and a desired effect may not be exhibited. On the other hand, when the content of the polypeptide exceeds 30 parts by weight, the organic liquid component contained together with the polypeptide is extruded from the pressure-sensitive adhesive layer so as to be exuded, which may cause a decrease in skin adhesion.
【００３３】上記ポリペプチドは粘着剤層中に均一に混
合、分散されなければならないが、上記したアクリル系
粘着剤は一般的に疎水性が高いので、親水性物質である
ポリペプチドはそのままでは均一に混合、分散しがた
い。そこで、本発明では前記したように、カルボキシル
基を中和する際に用いる中和剤を水溶液の状態でアクリ
ル系粘着剤溶液中に添加し、必要に応じて水を追加添加
してポリペプチドを溶解混合することが好ましい。The above-mentioned polypeptide must be uniformly mixed and dispersed in the pressure-sensitive adhesive layer. However, since the above-mentioned acrylic pressure-sensitive adhesive is generally highly hydrophobic, the polypeptide which is a hydrophilic substance is uniform as it is. Difficult to mix and disperse. Therefore, in the present invention, as described above, a neutralizing agent used for neutralizing a carboxyl group is added to an acrylic pressure-sensitive adhesive solution in the form of an aqueous solution, and water is added as necessary to add a polypeptide. It is preferred to dissolve and mix.
【００３４】なお、ポリペプチドの添加に際しても、そ
のまま添加するのではなく、水溶液の状態で添加するこ
とによって、混合、分散性が向上するので好ましい。こ
のように粘着剤層を形成する場合、アクリル系粘着剤溶
液に水を混合して含水粘着剤溶液を調製し、最終的に乾
燥させて無水状態の粘着剤層を形成するのである。含水
粘着剤溶液中の含水量としては、０．１〜５０重量％、
好ましくは１〜５０重量％の範囲に調整することが、ポ
リペプチドの溶解性や均一な粘着剤溶液の調製のために
好ましいものである。In addition, when the polypeptide is added, it is preferable to add the polypeptide in the form of an aqueous solution instead of adding it as it is because the mixing and dispersibility are improved. In forming the pressure-sensitive adhesive layer in this way, water is mixed with the acrylic pressure-sensitive adhesive solution to prepare a water-containing pressure-sensitive adhesive solution, and finally dried to form an anhydrous pressure-sensitive adhesive layer. The water content in the water-containing pressure-sensitive adhesive solution is 0.1 to 50% by weight,
Adjustment to a range of preferably 1 to 50% by weight is preferable for solubility of the polypeptide and preparation of a uniform pressure-sensitive adhesive solution.
【００３５】本発明における粘着剤層には、上記したよ
うに有機液状成分およびポリペプチドを必須成分として
含有させるが、粘着剤層が可塑化されて内部凝集力が低
下しすぎることがあるので、架橋処理を施して粘着剤層
に適度な保形性を付与することが重要である。The pressure-sensitive adhesive layer of the present invention contains an organic liquid component and a polypeptide as essential components as described above. However, since the pressure-sensitive adhesive layer is sometimes plasticized, the internal cohesive force is excessively reduced. It is important to give a suitable shape-retaining property to the pressure-sensitive adhesive layer by performing a crosslinking treatment.
【００３６】粘着剤層を架橋する方法としては、有機過
酸化物やイソシアネート化合物、有機金属塩、金属アル
コラート化合物、、金属キレート化合物、エポキシ系化
合物、一級アミノ系化合物などの架橋剤を用いた化学的
架橋や、電離性放射線を照射してなる物理的架橋を行う
ことができるが、架橋度合いの調整のし易さや配合しや
すさ、ポットライフの点から、有機過酸化物、多官能性
イソシアネート化合物、エポキシ系化合物、金属キレー
ト化合物や金属アルコラート化合物を用いた化学的架橋
処理を施すことが好ましい。これらのうち、特に好まし
くは多官能性イソシアネート化合物やエポキシ系化合物
である。As a method for crosslinking the pressure-sensitive adhesive layer, a chemical using a crosslinking agent such as an organic peroxide, an isocyanate compound, an organic metal salt, a metal alcoholate compound, a metal chelate compound, an epoxy compound or a primary amino compound is used. Cross-linking and physical cross-linking by irradiation with ionizing radiation can be performed.However, from the viewpoints of easy adjustment of the degree of cross-linking, ease of compounding, and pot life, organic peroxides and polyfunctional isocyanates It is preferable to carry out a chemical crosslinking treatment using a compound, an epoxy compound, a metal chelate compound or a metal alcoholate compound. Among these, a polyfunctional isocyanate compound and an epoxy compound are particularly preferable.
【００３７】上記のようにして粘着剤層を架橋処理する
ことによって、粘着剤層中のアクリル系共重合体は溶剤
に対して不溶化される。粘着剤層に適度な内部凝集力を
付与するには、アクリル系共重合体の１５〜８０重量
％、好ましくは３５〜６５重量％を不溶化するように架
橋処理することによって、前述した有機液状成分を比較
的多量に含有させても、凝集力の低下を生じず、適度な
皮膚接着性を維持できるのである。By subjecting the pressure-sensitive adhesive layer to a cross-linking treatment as described above, the acrylic copolymer in the pressure-sensitive adhesive layer is insolubilized in a solvent. In order to impart an appropriate internal cohesion to the pressure-sensitive adhesive layer, the above-mentioned organic liquid component is subjected to a crosslinking treatment so as to insolubilize 15 to 80% by weight, preferably 35 to 65% by weight of the acrylic copolymer. Even when a relatively large amount of is contained, a reduction in cohesive force does not occur and an appropriate skin adhesion can be maintained.
【００３８】本発明の化粧用粘着シートは、上記の構成
からなるものであるが、必要に応じて粘着剤層中に、粘
着付与剤や充填剤、顔料、染料などの着色剤、酸化防止
剤などの添加剤を適宜配合することができる。The cosmetic pressure-sensitive adhesive sheet of the present invention has the above-mentioned constitution. If necessary, the pressure-sensitive adhesive layer may contain a tackifier, a filler, a coloring agent such as a pigment or a dye, and an antioxidant. Such additives as can be appropriately compounded.
【００３９】また、本発明の化粧用粘着シートは、三角
形状や正方形状、長方形状、台形状などの形状を基本に
して、額や眉間、目尻などの貼付すべき皮膚面の形状に
合わせて適宜変形させて打ち抜き、シート状にすること
ができる。また、一枚ずつを打ち抜くこともできるが、
長尺状のシートとしてミシン目を設けることで、必要な
大きさや長さに応じて一枚ずつのシートに切り取って使
用できるようにしておくことができる。The cosmetic pressure-sensitive adhesive sheet of the present invention has a triangular shape, a square shape, a rectangular shape, a trapezoidal shape, or the like, and is adapted to the shape of the skin surface to be affixed, such as the forehead, the space between the eyebrows, and the outer corner of the eye. It can be appropriately deformed and punched to form a sheet. You can also punch one by one,
By providing perforations as long sheets, the sheets can be cut into individual sheets according to the required size and length so that they can be used.
【００４０】なお、本発明の化粧用粘着シートにおける
粘着剤層には、その露出表面に表面にシリコーン処理や
フッ素処理などの剥離処理を施したセパレータにて被
覆、仮着して、使用するまで粘着剤層の汚染を防止する
ことができる。また、一枚のセパレータ上に複数枚のシ
ートを併着しておくこともできることは云うまでもな
い。The pressure-sensitive adhesive layer in the cosmetic pressure-sensitive adhesive sheet of the present invention is covered with a separator having its exposed surface subjected to a release treatment such as silicone treatment or fluorine treatment, temporarily attached, and used until it is used. The contamination of the pressure-sensitive adhesive layer can be prevented. Needless to say, a plurality of sheets can be attached together on one separator.
【００４１】[0041]
【発明の効果】本発明の化粧用粘着シートは、以上のよ
うな構成からなるので、額や眉間、目尻などの皺のある
皮膚面に貼付しておくだけで、皮膚刺激をほとんど起こ
すことなく、簡単に皮膚面へ潤いを与えることができ、
しかも繰り返し使用することによって、徐々に物理的な
作用が働き、皺の除去に効果を発揮するようになる。ま
た、特定のゲル状粘着剤を用いているので、皮膚面に対
して極めてソフトに貼着しており、剥離に際しても皮膚
の角質層にダメージを与えることがないのである。The cosmetic pressure-sensitive adhesive sheet of the present invention has the above-mentioned structure, so that it can be applied only to a wrinkled skin surface such as the forehead, eyebrows, and outer corners of the eye, and hardly causes skin irritation. , Can easily moisturize the skin surface,
In addition, by using repeatedly, a physical action gradually works, and the effect of removing wrinkles is exerted. In addition, since a specific gel-like adhesive is used, it is extremely softly adhered to the skin surface, and does not damage the stratum corneum of the skin when peeled off.
【００４２】[0042]
【実施例】以下に本発明の実施例を示し、さらに具体的
に説明するが、本発明はこれらに限定されるものではな
く、本発明の技術的思想を逸脱しない範囲内で種々の応
用が可能である。なお、以下の文中で「部」とあるのは
「重量部」を意味し、「％」とあるのは「重量％」を意
味する。EXAMPLES Examples of the present invention will be described below in more detail, but the present invention is not limited thereto, and various applications can be made without departing from the technical concept of the present invention. It is possible. In the following text, “parts” means “parts by weight”, and “%” means “% by weight”.
【００４３】実施例１ ２−エチルヘキシルアクリレート９５部、アクリル酸５
部からなる単量体混合物を、酢酸エチルを重合溶媒とし
て溶液重合を行い、アクリル系共重合体を調製した。Example 1 95 parts of 2-ethylhexyl acrylate, 5 of acrylic acid
The monomer mixture consisting of 1 part was subjected to solution polymerization using ethyl acetate as a polymerization solvent to prepare an acrylic copolymer.
【００４４】得られたアクリル系共重合体溶液の固形分
１００部に、２５％アンモニア水を１０部添加し、トリ
オレイン酸ソルビタン５０部、加水分解コラーゲンタン
パク質（成和化成社製、商品名Ｗ−４２ＣＰ、重量平均
分子量１０００）０．５部、架橋剤としてのトリグリシ
ジルイソシアヌレート（日産化学社製、商品名ＴＥＰＩ
Ｃ−Ｇ）０．１５部を配合して、さらに水を添加して含
水率１５％の粘着剤溶液を調製した。（アクリル系共重
合体の中和度５０％）To 100 parts of the solid content of the obtained acrylic copolymer solution, 10 parts of 25% aqueous ammonia was added, 50 parts of sorbitan trioleate, 50 parts of hydrolyzed collagen protein (trade name: W, manufactured by Seiwa Chemical Co., Ltd.) -42CP, weight average molecular weight 1000) 0.5 part, triglycidyl isocyanurate as a crosslinking agent (manufactured by Nissan Chemical Industries, trade name TEPI)
CG) was added, and water was further added to prepare an adhesive solution having a water content of 15%. (50% neutralization degree of acrylic copolymer)
【００４５】次いで、得られた含水粘着剤溶液を、片面
にシリコーン処理を施したセパレータの処理面に、乾燥
後の厚みが４５μｍとなるように塗布し、１３０℃で５
分間乾燥して酢酸エチルおよび水を除去して、粘着剤層
を形成した。Next, the obtained water-containing pressure-sensitive adhesive solution was applied to a treated surface of a separator having one surface subjected to silicone treatment so that the thickness after drying was 45 μm,
After drying for minutes, ethyl acetate and water were removed to form an adhesive layer.
【００４６】次に、得られた粘着剤層の表面に、ポリエ
ステル製の不織布（目付量２５ｇ／ｍ2 ）を貼り合わせ
て粘着シートを作製し、６０℃で３日間加温して熟成
し、本発明の化粧用粘着シートを作製した。Next, a polyester non-woven fabric (having a basis weight of 25 g / m 2 ) was attached to the surface of the obtained pressure-sensitive adhesive layer to prepare a pressure-sensitive adhesive sheet, which was heated at 60 ° C. for 3 days and aged. The cosmetic pressure-sensitive adhesive sheet of the present invention was produced.
【００４７】比較例１ 実施例１において、加水分解コラーゲンタンパク質を配
合しなかった以外は、実施例１と同様にして化粧用粘着
シートを作製した。Comparative Example 1 A cosmetic adhesive sheet was prepared in the same manner as in Example 1 except that the hydrolyzed collagen protein was not blended.
【００４８】比較例２ 実施例１において、架橋剤を配合しなかった以外は、実
施例１と同様にして化粧用粘着シートを作製した。Comparative Example 2 A cosmetic pressure-sensitive adhesive sheet was prepared in the same manner as in Example 1, except that the crosslinking agent was not used.
【００４９】比較例３ 実施例１において、トリオレイン酸ソルビタンを配合し
なかった以外は、実施例１と同様にして、化粧用粘着シ
ートを作製した。Comparative Example 3 A cosmetic pressure-sensitive adhesive sheet was prepared in the same manner as in Example 1, except that sorbitan trioleate was not used.
【００５０】実施例２ ２−エチルヘキシルアクリレート９５部、アクリル酸５
部からなる単量体混合物を、酢酸エチルを重合溶媒とし
て溶液重合を行い、アクリル系共重合体を調製した。Example 2 95 parts of 2-ethylhexyl acrylate, 5 of acrylic acid
The monomer mixture consisting of 1 part was subjected to solution polymerization using ethyl acetate as a polymerization solvent to prepare an acrylic copolymer.
【００５１】得られたアクリル系共重合体溶液の固形分
１００部に、２５％アンモニア水を２０部添加し、トリ
オレイン酸ソルビタン５０部、加水分解コラーゲンタン
パク質（成和化成社製、商品名Ｗ−ＮＥ、重量平均分子
量７００）０．５部、架橋剤としてのトリグリシジルイ
ソシアヌレート（日産化学社製、商品名ＴＥＰＩＣ−
Ｇ）０．２部を配合して、さらに水を添加して含水率３
０％の粘着剤溶液を調製した。（アクリル系共重合体の
中和度１００％）To 100 parts of the solid content of the obtained acrylic copolymer solution, 20 parts of 25% aqueous ammonia was added, and 50 parts of sorbitan trioleate and hydrolyzed collagen protein (trade name: W, manufactured by Seiwa Chemical Co., Ltd.) -NE, 0.5 part by weight average molecular weight 700), triglycidyl isocyanurate as a crosslinking agent (manufactured by Nissan Chemical Industries, trade name TEPIC-
G) 0.2 part was blended, and water was further added to make the water content 3
A 0% adhesive solution was prepared. (100% neutralization degree of acrylic copolymer)
【００５２】次いで、得られた含水粘着剤溶液を、片面
にシリコーン処理を施したセパレータの処理面に、乾燥
後の厚みが６０μｍとなるように塗布し、１３０℃で５
分間乾燥して酢酸エチルおよび水を除去して、粘着剤層
を形成した。Then, the obtained water-containing pressure-sensitive adhesive solution was applied to the treated surface of a separator having one surface subjected to silicone treatment so that the thickness after drying was 60 μm,
After drying for minutes, ethyl acetate and water were removed to form an adhesive layer.
【００５３】次に、得られた粘着剤層の表面に、ポリエ
ステルフィルム（厚さ１００μｍ）を貼り合わせて粘着
シートを作製し、６０℃で３日間加温して熟成し、本発
明の化粧用粘着シートを作製した。Next, a polyester film (thickness: 100 μm) was bonded to the surface of the obtained pressure-sensitive adhesive layer to prepare a pressure-sensitive adhesive sheet, which was heated at 60 ° C. for 3 days to be aged, and the cosmetic sheet of the present invention was aged. An adhesive sheet was produced.
【００５４】実施例３ 実施例１におけるトリオレイン酸ソルビタン５０部を、
ミリスチン酸オクチルドデシル８０部に代えた以外は、
実施例１と同様にして本発明の化粧用粘着シートを作製
した。Example 3 50 parts of sorbitan trioleate in Example 1 was used.
With the exception of replacing it with 80 parts of octyldodecyl myristate,
In the same manner as in Example 1, a cosmetic pressure-sensitive adhesive sheet of the present invention was produced.
【００５５】実施例４ 実施例１において調製したアクリル系共重合体を、イソ
ノニルアクリレート９３部、アクリル酸７部を共重合し
て得られるアクリル系共重合体に代えた以外は、実施例
１と同様にして本発明の化粧用粘着シートを作製した。Example 4 Example 1 was repeated except that the acrylic copolymer prepared in Example 1 was replaced with an acrylic copolymer obtained by copolymerizing 93 parts of isononyl acrylate and 7 parts of acrylic acid. In the same manner as in the above, a cosmetic pressure-sensitive adhesive sheet of the present invention was produced.
【００５６】上記各実施例および比較例にて得られた化
粧用粘着シートについて、アクリル系重合体の不溶化率
（ゲル分率）、皮膚接着力、皮膚刺激性、糊残り、保湿
性、皺除去性（つっぱり感）を、以下の方法によって評
価し、その結果を表１にまとめた。With respect to the cosmetic pressure-sensitive adhesive sheets obtained in the above Examples and Comparative Examples, the acrylic polymer insolubilization rate (gel fraction), skin adhesion, skin irritation, adhesive residue, moisture retention, wrinkle removal The properties (tension) were evaluated by the following methods, and the results are summarized in Table 1.
【００５７】＜不溶化率＞各実施例および比較例にて作
製した粘着シートから、粘着剤層を約１ｇサンプリング
し、正確にその重量（Ｗ0 ）を測定した。次いで、各サ
ンプルを酢酸エチル中に４日間浸漬し、酢酸エチル可溶
分を抽出した。残渣としての不溶分（ゲル分）を濾別、
乾燥してその重量（Ｗ1 ）を測定した。不溶化率（ゲル
分率）の算出は、以下の式によって行った。<Insolubilization Ratio> About 1 g of the pressure-sensitive adhesive layer was sampled from the pressure-sensitive adhesive sheets prepared in Examples and Comparative Examples, and its weight (W 0 ) was measured accurately. Next, each sample was immersed in ethyl acetate for 4 days to extract ethyl acetate-soluble components. The insoluble matter (gel content) as a residue is separated by filtration,
After drying, the weight (W 1 ) was measured. The insolubilization rate (gel fraction) was calculated by the following equation.
【００５８】[0058]
【数１】 (Equation 1)
【００５９】＜皮膚接着力＞各実施例および比較例にて
作製した粘着シートを、幅１９ｍｍに裁断し、エタノー
ルで拭ったボランティアの額部に貼付し、１時間経過後
に、９０度方向に速度３００ｍｍ／分の速さで剥離し、
その際の接着力を測定した。<Skin Adhesive Strength> The pressure-sensitive adhesive sheets prepared in Examples and Comparative Examples were cut to a width of 19 mm, and adhered to volunteers' foreheads wiped with ethanol. Peel at a speed of 300 mm / min,
The adhesive force at that time was measured.
【００６０】＜皮膚刺激性＞上記皮膚接着力試験におい
て１時間貼付後、剥離した際に、以下の判定基準によっ
て、皮膚刺激性を評価した。 〇：僅かに痛みを感じるか、もしくは苦痛に感じない程
度の刺激がある。 △：やや苦痛に感じる痛みがある。 ×：苦痛に感じる痛みがある。 ××：非常に強い痛みを感じる。<Skin irritation> The skin irritation was evaluated according to the following criterion when peeled for 1 hour after application in the skin adhesion test. 〇: There is slight irritation, or slight irritation. Δ: Pain felt somewhat painful. ×: Pain felt painful. XX: Very strong pain is felt.
【００６１】＜糊残り＞上記皮膚接着力試験において１
時間貼付後、剥離した際に、以下の判定基準によって、
貼付した皮膚面への糊残りを評価した。 〇：糊残りが全くない。 △：端部に糊残りを生じる。 ×：１／３以上の面積に糊残りを生じる。<Glue residue> In the above skin adhesion test, 1
After the time pasting, when peeled, by the following criteria,
The adhesive residue on the adhered skin surface was evaluated. 〇: No adhesive residue at all. Δ: Adhesive residue occurs at the end. ×: Adhesive residue occurs in an area of 1/3 or more.
【００６２】＜保湿性＞上記皮膚接着力試験において１
時間貼付して剥離したのちの保湿感を際に、以下の判定
基準によって評価した。なお、市販の化粧パック用クリ
ームを用い、上記試験と同様にボランティアの額部に塗
布したものを対照例とした。判定基準は以下の通りであ
る。 ○：清涼感がある。 △：僅かに清涼感がある。 ×：ほとんど清涼感がない。 ××：清涼感を感じず、皮膚面がべとつく。<Humidity> In the above skin adhesion test, 1
The moisturizing sensation after sticking and peeling for a time was evaluated according to the following criteria. In addition, the thing applied to the forehead part of the volunteer similarly to the said test using the cream for commercial cosmetic packs was set as the control example. The criteria are as follows. ：: Refreshing feeling. Δ: Slight cooling feeling. ×: Almost no refreshing feeling. ××: The skin surface is not sticky without feeling cool.
【００６３】＜皺除去性（つっぱり感）＞上記皮膚接着
力試験において、１時間貼付して剥離した後、１時間経
過後の貼付部位のつっぱり感を、以下の判定基準によっ
て評価した。なお、対照例として市販の化粧パック用ク
リームを用いて、上記試験と同様にボランティアの額部
に塗布した。 ○：つっぱり感がある。 △：僅かにつっぱり感がある。 ×：ほとんどつっぱり感を感じない。<Wrinkle Removability (Tightness)> In the above-mentioned skin adhesion test, after one hour of application and peeling, one hour after the application, the tightness of the application site was evaluated according to the following criteria. As a control, a commercially available cream for a cosmetic pack was applied to the volunteer's forehead in the same manner as in the above test. ：: There is a sense of tightness. Δ: Slightly tight feeling. ×: Almost no feeling of tightness.
【００６４】[0064]
【表１】 [Table 1]
Claims (8)
着剤層が形成されてなる粘着シートであって、粘着剤層
がアクリル系粘着剤、有機液状成分およびポリペプチド
を含有すると共に、架橋処理が施されていることを特徴
とする化粧用粘着シート。1. A pressure-sensitive adhesive sheet comprising a flexible sheet-like substrate having a pressure-sensitive adhesive layer formed on one surface thereof, wherein the pressure-sensitive adhesive layer contains an acrylic pressure-sensitive adhesive, an organic liquid component and a polypeptide. A cosmetic pressure-sensitive adhesive sheet, which has been subjected to a crosslinking treatment.
である請求項１記載の化粧用粘着シート。2. The cosmetic pressure-sensitive adhesive sheet according to claim 1, wherein the sheet-like substrate is a paper substrate or a nonwoven fabric.
酸アクリルエステルと、側鎖にカルボキシル基を有する
単量体とを含む単量体混合物を共重合してなり、カルボ
キシル基の一部もしくは全部が中和されている粘着剤で
ある請求項１記載の化粧用粘着シート。3. An acrylic pressure-sensitive adhesive obtained by copolymerizing a monomer mixture containing a (meth) acrylic acid acrylic ester and a monomer having a carboxyl group in a side chain, wherein a part of the carboxyl group or 2. The cosmetic pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive is entirely neutralized.
が不溶化されている請求項１記載の化粧用粘着シート。4. 15 to 80% by weight of the acrylic copolymer
The cosmetic pressure-sensitive adhesive sheet according to claim 1, wherein is insolubilized.
基酸または多塩基酸と炭素数１４〜２０の分岐アルコー
ルとのエステル化物、および／または炭素数１４〜２０
の不飽和脂肪酸または不飽和分岐酸と４価以下のアルコ
ールとのエステル化物である請求項１記載の化粧用粘着
シート。5. The organic liquid component is an esterified product of a monobasic acid or polybasic acid having 8 to 20 carbon atoms and a branched alcohol having 14 to 20 carbon atoms, and / or 14 to 20 carbon atoms.
The cosmetic pressure-sensitive adhesive sheet according to claim 1, which is an esterified product of the unsaturated fatty acid or unsaturated branched acid of the above and an alcohol having a valency of 4 or less.
ンタンパク質である請求項１記載の化粧用粘着シート。6. The cosmetic pressure-sensitive adhesive sheet according to claim 1, wherein the polypeptide is a hydrolyzed collagen protein.
重量平均分子量が４００〜４０００である請求項６記載
の化粧用粘着シート。7. The cosmetic pressure-sensitive adhesive sheet according to claim 6, wherein the weight-average molecular weight of the hydrolyzed collagen protein is 400 to 4000.
徴とする請求項１〜７の何れか１項に記載の化粧用粘着
シート。8. The cosmetic pressure-sensitive adhesive sheet according to claim 1, wherein the surface to be stuck is a wrinkle portion.