KR101969654B1 - Velvet woven fabric having excellent anti-static property and appearance - Google Patents
Velvet woven fabric having excellent anti-static property and appearance Download PDFInfo
- Publication number
- KR101969654B1 KR101969654B1 KR1020170160143A KR20170160143A KR101969654B1 KR 101969654 B1 KR101969654 B1 KR 101969654B1 KR 1020170160143 A KR1020170160143 A KR 1020170160143A KR 20170160143 A KR20170160143 A KR 20170160143A KR 101969654 B1 KR101969654 B1 KR 101969654B1
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- fabric
- pile
- denier
- polyester
- Prior art date
Abstract
Description
본 발명은 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물에 관한 것으로서, 파일사의 기립된 상태를 최대한 유지하여 벨벳 직물 특유의 고급스런 표면효과를 나타내고, 외관이 손상되는 것을 억제하여 풍부한 표면 효과를 발현하며, 또한 지조직의 경사와 위사를 카본 블랙을 포함하는 폴리에스테르 원착사를 이용함으로써 제전성이 우수한 벨벳 직물에 관한 것이다.The present invention relates to a velvet fabric excellent in antistatic property and having a beautiful appearance, which exhibits a luxurious surface effect peculiar to a velvet fabric by maintaining the standing state of the pile yarn as much as possible, And also to a velvet fabric excellent in antistaticity by using polyester yarns containing a carbon black in the warp and weft of the ground structure.
일반적으로 벨벳 직물은 지조직에 형성된 파일조직의 중앙부를 컷팅함으로써 원단의 일면에 파일(잔털)이 형성되도록 한 직물을 지칭하는 것으로, 이러한 벨벳 직물은 표면의 촉감이나 질감이 좋아서 의복지로 많이 선호되고 있다. 통상 벨벳 직물은 표면의 조직감이 드러나지 않게 하고 파일에 방향성을 형성하여 약간의 광택감을 부여함으로써 풍성한 표면 효과를 발현시킬 수 있고, 색상을 다양하게 할 수 있을 뿐만 아니라 파일 길이 및 직조방법에 따라서 표면에 다양한 조직감을 부여할 수 있어서 주로 여성 및 남성용 의복과 모자, 쇼올 외에도 실내장식, 시트커버, 봉제완구용으로 널리 이용된다.Generally, a velvet fabric refers to a fabric which is formed by cutting a central portion of a pile fabric formed on a pile fabric so that a pile (fine hair) is formed on one side of the fabric. Such a velvet fabric is preferred as a garment have. In general, velvet fabrics are capable of manifesting a rich surface effect by making the texture of the surface not to be exposed and forming a directionality in the pile to give a slight glossiness, and in addition to being able to vary the color, It is widely used for interior decoration, seat cover and stuffed toys in addition to women's and men's clothes, hats and shawls because it can give various texture.
일반적인 벨벳 직물의 제직과정을 살펴보면, 경사와 위사의 교차에 의해서 지조직을 형성하고, 파일사가 상기 지조직을 왕복하여 파일조직을 형성시키킨 후, 상기 파일 조직의 중앙부를 절단하는 과정을 거쳐 제조된다. In general, a weaving process of a velvet fabric is described as follows. That is, a paper tissue is formed by the intersection of warp and weft, a pile is formed by reciprocating the pile tissue to form a pile tissue, do.
벨벳 직물은 파일에 방향성을 부여하여 약간의 광택감을 나타내고 파일의 끝단과 측면의 빛 반사도의 차이에 의해 명암이 표현되며, 포근함과 미려함을 제공하여 풍부한 표면효과를 발현하고 색상을 다양하게 할 수 있을 뿐만 아니라 파일길이 및 직조방법에 따라서 표면에 다양한 조직감을 부여할 수 있어서 고급의 직물로서 취급되어 왔다.The velvet fabric gives a directionality to the pile to give a slight luster, and the light and shade are expressed by the difference of the light reflectance of the end and the side of the pile, and the pile and the beauty are provided to manifest the abundant surface effect, In addition, depending on the length of the pile and the method of weaving, various textures can be imparted to the surface, which has been treated as a high-grade fabric.
그런데 상기와 같은 벨벳 직물의 파일조직은 외력을 받으면 형태가 무너지기 쉬워 일정한 방향을 유지하기 어렵고, 외력이 반복하여 가해지면 외력이 제거된 후에도 파일이 원래의 형태로 되돌아가지 못하여 벨벳 직물의 외관이 손상되는 문제가 있다.However, when the external force is applied to the velvet fabric, the shape of the velvet fabric tends to collapse, and it is difficult to maintain a constant direction. If the external force is repeatedly applied, the file can not be returned to its original shape even after the external force is removed. There is a problem that is damaged.
상기와 같은 문제를 해결하기 위하여, 한국등록특허공보 제0737975호에는 벨벳 직물 지조직의 경사 및 위사에 합성섬유 장섬유 또는 합섬 단독 또는 합섬과 천연섬유의 혼방 단섬유를 사용하고, 파일사에 단사섬도 1데니어 이하인 합성섬유 멀티필라멘트를 사용하며, 상기 파일사는 가연 후 연사 또는 사이징하여 제직에 투입하는 장섬유 벨벳 직물의 제조방법이 개시되어 있다.In order to solve the above problems, Korean Patent Registration No. 0737975 discloses a method of using a synthetic fiber long fiber or synthetic fiber alone or a mixed fiber of natural fiber and synthetic fiber for a warp and weft of a velvet fabric, A synthetic fiber multifilament having a fineness of 1 denier or less is used, and the filament yarn is subjected to twisting, twisting or sizing to put into a weaving machine.
상기 발명의 장섬유 벨벳 직물은 합성섬유 멀티필라멘트사를 지조직의 경사와 위사, 파일사로 사용함으로써 장섬유사 특유의 우수한 드레이프성, 탄력성, 인장강도를 발현하고, 파일사로서 합섬 초극세사를 사용하여 소프트한 촉감을 부여하며, 파일사는 가연 후 연사 또는 사이징 함으로써 EASY-CARE성을 부여한다. 그런데 상기 발명에 의하면 벨벳 직물의 외관손상을 방지하고 부드러운 촉감을 유지하기 위하여 파일사를 가연후 연사 또는 사이징하는 과정을 거쳐야 함으로써 벨벳 직물 특유의 광택감, 포근함, 미려함 등의 표면 효과가 감소하는 단점이 있다.The long fiber velvety fabric of the present invention is characterized in that synthetic fiber multifilament yarns are used as warp yarns, weft yarns and pile yarns of a terry structure to exhibit excellent drape, elasticity and tensile strength peculiar to long fiber yarns, Soft texture, and the filer gives EASY-CARE property by twisting after burning or sizing. However, according to the above-described invention, since the pile yarn is subjected to the process of twisting, twisting, and sizing in order to prevent damage to the outer surface of the velvet fabric and to maintain soft touch, the surface effect such as luster, whiteness and beauty unique to the velvet fabric is reduced have.
또한, 한국등록특허공보 제0919467호에는 경사로서 나일론 에어텍스쳐링 가공사를 사용하고, 위사로서 폴리트리메틸렌테레프탈레이트 멀티필라멘트의 코어사와 나일론 멀티필라멘트와 폴리에틸렌테레프탈레이트 멀티필라멘트 및 폴리트리메틸렌테레프탈레이트 멀티필라멘트 중에서 선택된 1종의 멀티필라멘트들로 이루어진 이펙트사가 에어텍스쳐링 가공된 복합 에어텍스쳐링 가공사를 사용하여 데님조 합성섬유 직물을 제직하는 방안이 제시되었다. 상기와 같은 구성을 갖는 직물은 드라이한 촉감 및 양호한 볼륨감을 나타내고, 천연섬유의 방적사를 사용하여 제직된 직물과 유사한 촉감과 외관을 제공한다. 그러나 상기 직물은 코어사와 이펙트사가 상이하여 제조과정이 복잡하며, 또한 상기 직물을 벨벳 직물의 지조직용 원단으로 적용할 경우 지조직이 외부로 노출되어도 지조직을 구성하는 상기 에어텍스쳐링 가공사의 특성으로 인하여 벨벳 직물의 외관 훼손을 어느 정도 방지할 수 있으나, 합성섬유를 에어텍스쳐링 가공하면 원사에 비해 강도가 저하되고 상기 에어텍스쳐링 가공사는 신축성이 커서 지조직용 원단의 형태안정성이 낮으므로 벨벳 직물의 사용에 따라 파일의 기립상태가 쉽게 무너져 벨벳 직물 본래의 고급스럽고 미려한 외관이 손상되는 문제가 있다. 또한 상기와 같은 지조직을 갖는 벨벳 직물의 경우에는 흡수율이 낮아 습도가 낮은 게절에 마찰에 의해 정전기가 발생하여 사용자에게 불쾌감을 부여하며, 작업현장에서 화재 또는 폭발사고 등을 일으키는 문제가 있다.Korean Patent Registration No. 0919467 discloses a nylon air texturing yarn as a warp yarn, a core yarn of polytrimethylene terephthalate multifilament as a weft yarn, a nylon multifilament yarn and a polyethylene terephthalate multifilament yarn and a polytrimethylene terephthalate multifilament yarn A method of weaving denim synthetic fiber fabrics using a composite air texturing yarn in which an effect yarn consisting of one selected multifilament yarn is air-textured has been proposed. Fabrics having such a configuration exhibit a dry feel and a good volume feel and provide a tactile appearance and appearance similar to fabrics woven using yarns of natural fibers. However, since the fabric is different from the core yarn and the effect yarn, the fabrication process is complicated. Further, when the fabric is applied to the fabric for the fabric of the velvet fabric, the fabric is exposed to the outside, It is possible to prevent some damage to the appearance of the velvet fabric. However, since the air-texturing process of the synthetic fiber causes the strength to be lower than that of the yarn, and the air-texturing process yarn has a large elasticity, There is a problem that the standing state of the file is easily collapsed to deteriorate the luxurious and beautiful appearance inherent in the velvet fabric. In addition, in the case of the velvet fabric having the above-mentioned ground structure, there is a problem that static electricity is generated due to friction in a low moisture level due to a low water absorption rate, giving an uncomfortable feeling to a user, and causing fire or explosion accident at a work site.
본 발명이 해결하고자 하는 과제는 파일의 기립된 상태를 최대한 유지하여 벨벳 직물 특유의 고급스런 표면효과를 나타내고 외관이 손상되는 것을 억제하여, 풍부한 표면효과를 발현하며, 또한 제전성이 우수하여 정전기 발생이 억제되는 벨벳 직물을 제공하는 것이다. 그러나 이러한 과제는 예시적인 것으로, 이에 의해 본 발명의 범위가 한정되는 것은 아니다.A problem to be solved by the present invention is to maintain a standing state of a file as much as possible to exhibit a luxurious surface effect peculiar to the velvet fabric and suppressing damage to the appearance, exhibiting a rich surface effect, To provide a restrained velvet fabric. However, these problems are exemplary and do not limit the scope of the present invention.
상기 과제를 해결하기 위한 본 발명의 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물은 지조직의 경사 및 위사 중 어느 하나 이상은 폴리에스테르 원착사로 구성되고, 상기 파일사는 아세테이트사로 구성되는 것이 바람직하다. 또한 상기 지조직의 경사는 70~160 데니어이며,, 지조직의 위사는 50 데니어 이상인 것이 바람직하다. 그리고 상기 폴리에스테르 원착사는 원사내 카본 함량이 0.5 내지 2.0 중량%이며, 상기 폴리에스테르 원착사의 강도는 3 g/d 이상인 것이 바람직하다.. 특히 상기 지조직에서 경사의 밀도는 22 本/인치 이상이며, 위사의 밀도는 46本/인치 이상이며, 상기 파일사의 섬도는 120~300 데니어이며, 상기 파일사는 후염사 또는 원착사인 것이 바람직하다. In order to attain the above object, the present invention provides a velvet fabric excellent in antistatic property and having a beautiful appearance, wherein at least one of the warp and weft of the ground structure is made of polyester yarn, and the yarn is preferably composed of acetate yarn. Further, the slope of the ground structure is 70 to 160 denier, and the grain size of the ground structure is preferably 50 denier or more. The polyester base yarn preferably has a carbon content in the yarn of 0.5 to 2.0 wt%, and the strength of the polyester base yarn is preferably 3 g / d or more. In particular, the density of the warp yarns in the base fabric is 22 / , The density of the weft yarn is 46 yarns / inch or more, the fineness of the filament yarn is 120 to 300 denier, and the filament yarn is preferably afterglow or original yarn.
본 발명에 따른 벨벳 직물은 폴리에스테르 원착사로 지조직을 제직함으로써 파일의 촉감이 부드러우면서 기립성이 높고 종광을 안정된 장력으로 당겨주므로 파일의 길이가 일정하며, 파일 본수를 증가시키지 않고도 표면밀도를 크게 하여 지조직을 외부로 드러나지 않도록 함으로써 벨벳 직물 특유의 광택감, 포근함, 미려함 등의 풍부한 표면효과를 발현할 수 있다. 특히 상기 지조직의 경사 및 위사 중 어느 하나 이상에 원사 내부에 카본 블랙을 포함함으로써, 합성섬유로 제조되는 본 발명의 벨벳 직물의 대전방지성을 부여함으로써 정전기의 발생을 방지하는 제전성을 부여할 수 있다. The velvet fabric according to the present invention is made by weaving a polyester terraced yarn with a smooth texture of the pile, so that the tactile feeling of the pile is high and the standing is high, and the pile is pulled with a stable tension. Therefore, the length of the pile is constant, So that it is possible to manifest a rich surface effect such as glossiness, warmth, and beauty unique to the velvet fabric. In particular, by incorporating carbon black in the yarn in at least one of the warp and weft of the ground structure, the antistatic property of the inventive velvet fabric made of synthetic fibers is imparted to impart antistatic properties for preventing the generation of static electricity .
도 1은 벨벳 직물의 개략적인 구성을 확대하여 나타낸 단면도이며,
도 2는 본 발명의 일실시예에 따라 제조된 벨벳 직물의 측면도(a) 및 파일사의 표면 사진(b)이다.1 is an enlarged cross-sectional view showing a schematic configuration of a velvet fabric,
2 is a side view (a) of a velvet fabric made according to one embodiment of the present invention and a surface photograph (b) of a pile yarn.
이하, 첨부된 도면들을 참조하여 본 발명의 실험예를 상세히 설명하면 다음과 같다. 그러나 본 발명은 이하에서 개시되는 실험예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 수 있는 것으로, 이하의 실험예는 본 발명의 개시가 완전하도록 하며, 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다. 또한 설명의 편의를 위하여 도면에서는 구성 요소들이 그 크기가 과장 또는 축소될 수 있다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. It should be understood, however, that the invention is not limited to the disclosed exemplary embodiments, but is capable of other various forms of implementation. The following examples are intended to be illustrative of the present invention, Is provided to fully inform the user. Also, for convenience of explanation, the components may be exaggerated or reduced in size.
이하, 본 발명에 따른 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물에 대하여 첨부된 도면에 의거하여 구체적으로 설명하기로 한다. 본 발명에 첨부된 도 1은 벨벳 직물의 개략적인 구성을 확대하여 나타낸 단면도이며, 도 2는 본 발명의 일실시예에 따라 제조된 벨벳 직물의 측면도(a) 및 파일사의 표면 사진(b)이다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a velvet fabric having an excellent antistatic property and a beautiful appearance according to the present invention will be described in detail with reference to the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a side view (a) of a fabric made in accordance with one embodiment of the present invention, and Figure 2 (b) is a surface photograph of a pile yarn; Figure 1 is an enlarged cross- .
벨벳 직물은 도 1에 도시된 바와 같이 위사(10)와 경사(20)로 이루어진 지조직(30)에 일정한 길이의 파일조직(40)이 형성되는 구조로서, 외부로 드러나는 파일조직이 벨벳 직물의 특성을 결정하는 중요한 역할을 한다.The velvet fabric is a structure in which a
이러한 벨벳 직물의 고급스런 특성을 유지하기 위하여는 파일의 기립된 상태를 유지하는 것과 지조직이 파일로 가려져서 외부로 드러나지 않도록 하는 것이 중요하고, 파일의 기립성을 증가시키기 위하여 파일 원사를 강도가 높은 섬유로 구성하면 촉감이 뻣뻣해지는 문제가 있으며, 지조직을 파일로 가리도록 하기 위하여 파일 본수를 증가시킬 경우 이에 따른 제조원가의 상승과 함께 촉감 또한 부드럽지 않게 된다.In order to maintain the luxurious characteristics of such a velvet fabric, it is important to maintain the standing state of the file and to prevent the paper organization from being exposed to the outside by the file. In order to increase the standing of the file, If the fibers are made of a stiff material, there is a problem that the tactile feeling becomes stiff. When the number of the file is increased in order to cover the paper tissue with the pile, the manufacturing cost is increased and the tactile feeling is not smooth.
본 발명의 일실시예에 따른 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물은 지조직과 파일사로 구성되며, 상기 지조직의 경사 및 위사 중 어느 하나 이상은 폴리에스테르 원착사로 구성되고,A velvet fabric excellent in antistatic property and having an excellent appearance according to an embodiment of the present invention is composed of a papermaker's fabric and pile fabric, wherein at least one of the warp and weft of the papermaker's fabric is made of polyester yarn,
상기 파일사는 아세테이트사로 구성되는 것이 바람직하다. 즉, 본 발명의 일실시예에 따른 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물의 지조직의 경사 및 위사 증 어느 하나 이상은 폴리에스테르 원착사로 구성된다.The pile yarn is preferably composed of acetate yarn. That is, at least one of the warp and weft of the ground structure of the velvet fabric having excellent antistatic property and excellent appearance according to one embodiment of the present invention is composed of polyester yarn.
상기 폴리에스테르 원착사는 우수한 특성으로 인하여 의류용, 인테리어용, 산업자재 등의 분야에 널리 이용되고 있으며, 다양한 제품으로 제조시에 종래의 백색 원사를 제직, 수세, 염색, 히트 세트 및 마무리 처리 등의 공정을 거치게 된다. 그러나, 폴리에스테르 섬유는 염색이 용이하지 아니하므로, 상기 폴리에스테르 섬유가 분산 염료를 흡수하기 위해서는 소정 압력 하에서 고온을 필요로 한다. 이같이 백색의 폴리에스테르 원사를 사용한 가공 공정은 복잡한 여러 단계를 거치므로 제조 비용의 상승과 별도의 염색 공정에 의한 염액 폐수의 처리 비용 증가와 폐수에 의한 환경 문제 등의 문제가 야기될 수 있는 단점이 있다.Due to its excellent properties, the polyester base yarn is widely used in fields such as clothing, interior use, industrial materials, and the like. In producing various products, conventional white yarn is used for weaving, washing, dyeing, heat setting, Process. However, since the polyester fiber is not easy to dye, the polyester fiber needs a high temperature under a predetermined pressure to absorb the disperse dye. Since the processing process using white polyester yarn involves complicated steps, there are disadvantages such as an increase in manufacturing cost, an increase in the processing cost of the salt wastewater by a separate dyeing process, and an environmental problem caused by the wastewater have.
상기와 같은 폴리에스테르 백색 원사의 가공 공정상 문제를 해결하기 위하여 폴리에스테르의 중합반응 동안 또는 중합반응으로부터 섬유 형성까지의 어느 단계에서 섬유 자체에 착색제 등을 혼합하여 섬유를 제조하는 방법이 시도되었다. 상기와 같이 착색제 등을 혼합하여 제조한 섬유를 원착사라 하며, 주로 카본 블랙을 직접 첨가하여 폴리에스테르 원착사를 제조하게 된다. In order to solve the problems in the processing of the polyester white yarn as described above, attempts have been made to produce fibers by mixing a coloring agent or the like in the fibers themselves during the polymerization reaction of the polyester, or at any stage from the polymerization reaction to the fiber formation. The fibers prepared by mixing the colorant and the like as described above are called original yarns, and carbonaceous black is directly added to produce the polyester yarns.
본 발명의 일실시예에 의하면 상기와 같이 폴리에스테르 원착사를 벨벳 직물을 제조하기 위한 지조직의 경사로 사용되는 경우에는 섬도가 70 내지 160 데니어인 것이 바람직하며, 위사로 사용되는 경우에는 50 데니어 이상인 것이 바람직하다. According to an embodiment of the present invention, when the polyester circular knitting yarn is used as a slant of a paper structure for producing a velvet fabric, the fineness is preferably 70 to 160 denier, and when used as a weft yarn, .
상기와 같이 폴리에스테르 원착사를 경사 및/또는 위사로 사용하여 벨벳 직물의 지조직을 제직할 때, 경사가 파일의 기립성을 향상시키면서 표면밀도를 조밀하게 형성이 가능하며, 또한 우수한 제전성을 얻을 수 있다. 즉, 경사의 섬도가 70 데니어 미만이면 굴곡강도가 낮아서 외력이 반복됨에 따라 쉽게 굴곡되어 파일조직 외관이 손상되기 쉽고, 160 데니어를 초과하면 벨벳 직물의 장점인 부드러운 촉감이 사라지게 된다. 또한 위사의 섬도가 50 데니어 미만인 경우에는 파일사의 직립성이 부족하게 되어 벨벳 직물의 외관이 불량하게 된다. As described above, when weaving the base fabric of the velvet fabric using the polyester spinning yarn as the warp and / or weft, the warp yarn can densely form the surface density while improving the standing property of the pile, Can be obtained. That is, when the fineness of the warp yarn is less than 70 denier, the bending strength is low and the external force is repeated, so that it is easily bent and the outer appearance of the pile fabric is liable to be damaged, and when it exceeds 160 denier, Also, when the fineness of the weft yarn is less than 50 denier, the uprightness of the filament yarn becomes insufficient and the appearance of the velvet fabric becomes poor.
상기와 같은 조건을 갖는 폴리에스테르 원착사를 이용하여 형성된 지조직을 이용한 벨벳 직물은 각진 형상으로 변형되어도 파일이 각진 부위를 충분히 피복 할 수 있어서 각진 부위에서도 벨벳직물의 미려한 외관을 유지하는 것이 가능하다. Even if the velvet fabric using the ground structure formed using the polyester yarn having the above-mentioned conditions is deformed into the angular shape, the pile can sufficiently cover the angled portion, so that it is possible to maintain the beautiful appearance of the velvet fabric at the angled portion .
상기 폴리에스테르 원착사는 제조시 원사내 카본 블랙의 함량을 0.5 내지 2.0 중량%으로 제조하는 것이 바람직하다. 상기 카본 블랙의 함량이 0.5 중량% 미만일 경우에는 원착사 자체로 색상 발현이 어렵고, 2.0 중량%을 초과하는 경우에는 상기 카본 블랙의 추가함에 따라 더 이상 색상 발현의 효과가 나타나지 않는다. 또한 2.0 중량%를 초과하는 경우에는 카본 블랙이 이물질로 작용하여 사절 등의 방사 작업성이 저하되는 문제점이 발생하게 된다. The polyester base yarn is preferably produced in an amount of 0.5 to 2.0% by weight in terms of the carbon black content in the yarn. When the content of the carbon black is less than 0.5% by weight, color reproduction is difficult to achieve by itself. When the content of the carbon black exceeds 2.0% by weight, the effect of color development is not exhibited. On the other hand, when the amount exceeds 2.0% by weight, carbon black acts as a foreign substance, which lowers the spinning workability of yarn and the like.
또한, 상기 폴리에스테르 원착사의 제조시 연신배율은 5.5 내지 6.4가 바람직하다. 연신비가 5.5 미만일 경우에는 배향도가 낮아서 강도발현이 어려우며, 6.4를 초과할 경우에는 과연신의 수준이 되어 단사절이 발생하면서 작업성이 저하되거나 완전사절이 발생하게 된다. 또한, 본 발명에서는 연신공정에서 고데트 롤러의 온도를 210 내지 250 ℃로 조절하는 것이 바람직하다. 상기 고데트 롤러의 온도가 210 ℃ 미만에서는 열적효과가 충분하지 못하여 이완효율이 떨어져 원하는 수축율을 얻을 수 없으며, 250 ℃를 초과하는 경우에는 열분해에 의한 원사 강도 저하 및 롤러상 타르 발생이 증가하여 작업성이 저하된다.In addition, the stretch magnification in the production of the polyester base yarn is preferably 5.5 to 6.4. When the stretching ratio is less than 5.5, the degree of orientation is low and the strength is difficult to manifest. If the stretching ratio is more than 6.4, the workability is lowered or the complete embossing occurs due to the occurrence of single threading. Further, in the present invention, it is preferable to control the temperature of the high-defect roller in the stretching step to 210 to 250 ° C. If the temperature of the high deterioration roller is less than 210 ° C, the thermal efficiency is insufficient and the relaxation efficiency is low to obtain a desired shrinkage ratio. When the temperature exceeds 250 ° C, the yarn strength is lowered due to pyrolysis and the tar- The property is deteriorated.
상기와 같이 제조되는 폴리에스테르 원착사의 강도는 3 g/d 이상인 것이 바람직하다. 즉, 상기 폴리에스테르 원착사의 강도가 3 g/d 미만인 경우에는 원사의 강도가 낮아서 외력이 반복됨에 따라 쉽게 굴곡되어 파일조직 외관이 손상되기 쉽다. 따라서 사용시 벨벳 직물의 고급스런 느낌이 감소하므로, 본 발명에서 사용되는 폴리에스테르 원착사는 강도는 3 g/d 이상인 것이 바람직하다.The strength of the polyester base yarn produced as described above is preferably 3 g / d or more. That is, when the strength of the polyester base yarn is less than 3 g / d, the strength of the yarn is low and the external force is repeated, so that it is easily bent and the appearance of the pile fabric is liable to be damaged. Therefore, the feeling of luxury of the velvet fabric is reduced during use, so that the polyester base yarn used in the present invention preferably has a strength of 3 g / d or more.
상기와 같이 폴리에스테르 원착사를 이용하여 지조직을 제직한 후, 파일사를 형성하여 본 발명의 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물을 제조할 수 있다. 이 때 상기 벨벳 직물은 도 1에 도시된 바와 같이 위사(a)와 경사(b)로 이루어진 지조직에 일정한 길이의 파일조직(d)이 형성되는 구조로서, 외부로 드러나는 파일조직이 벨벳직물의 특성을 결정하는 중요한 역할을 한다. 상기 지조직은 제직시 경사의 밀도는 22 本/인치 이상이며, 위사의 밀도는 46本/인치 이상인 것이 바람직하다 As described above, a polyester fabric is used to weave a ground structure, and then a pile yarn is formed, whereby a velvet fabric having an excellent antistatic property and a beautiful appearance of the present invention can be produced. In this case, as shown in FIG. 1, the velvet fabric has a structure in which a file structure d having a predetermined length is formed in a paper structure composed of a warp yarn a and a warp yarn b, It plays an important role in determining the characteristics. It is preferable that the density of the warp yarns is 22 yarns / inch or more and the density of weft yarns is 46 yarns / inch or more when weaving
상기와 같이 지조직의 경위사 밀도의 범위를 갖는 지조직의 경우에 파일을 견고한 상태로 형성이 가능하며, 또한 파일의 직립성이 가장 우수하다. 또한 상기와 같은 조건을 갖는 지조직으로 제조된 벨벳 직물의 경우에 광택감, 포근함, 미려함 등의 표면 효과가 가장 우수한 것으로 나타난다. As described above, in the case of the ground structure having the range of the warp yarn density of the ground structure, the file can be formed in a solid state and the uprightness of the file is the most excellent. In addition, in the case of the velvet fabric made from the ground structure having the above-mentioned conditions, the surface effect such as glossiness, warmth, and beauty is the most excellent.
통상적으로 벨벳 직물은 지조직과 파일사를 교대로 직조하고 제직 후에 절모(切毛)하여 컷 파일(cut pile)로 하거나 절모를 하지 않고 고리 모양의 루프(loop)를 표면에 치밀하게 나타나도록 제조하는 방법, 또는 경사와 위사의 교차에 의해 상, 하측 지조직의 이중직으로 제직되는 과정에 파일사가 상,하측 지조직으로 왕복하여 파일조직을 형성하고 파일조직의 중간을 절단하여 두 장의 직물이 되도록 함으로써 잘린 파일조직이 파일이 되어 직물의 표면에 나타나도록 하는 방법을 거쳐 벨벳 직물을 완성하게 된다. In general, velvet fabrics are made by alternately weaving ground tissues and pile yarns and cutting them into cut piles after weaving, so that annular loops are densely formed on the surface Or by the intersection of warp and weft, the pile yarn is made to reciprocate to the upper and lower side tissues in the process of weaving with the double yarns of the upper and lower side tissues to form the pile structure and cut the middle part of the pile structure to be two pile fabrics So that the cut file organization becomes a file and appears on the surface of the fabric, thereby completing the velvet fabric.
본 발명의 일실시예에 따른 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물은 상기와 같이 제조된 지조직에 파일사를 직조하여 벨벳 직물을 제조하게 된다. 그리고 상기 파일사로 사용되는 아세테이트사는 단면이 날카롭지 않고 둥글기 때문에 촉감이 부드럽고, 또한 단면형태가 주름 잡혀 있어서 단면이 원형인 나일론과 폴리에스테르보다 피복성이 우수한 이점이 있다. 본 발명에서 사용되는 파일사는 섬도가 120 데니어 내지 300 데니어 이며, 3 g/d 미만의 강도를 갖는 아세테이트사가 바람직하다. 상기와 같은 아세테이트사를 파일사로 사용한 경우에 상기 파일사의 직립성이 우수하며, 특히 지조직이 외부로 쉽게 드러나지 않고, 또한 각진 부위에서 지조직이 일부 드러나는 경우에도 고급스러운 광택 특성으로 인하여 벨벳 직물의 미려한 외관을 유지할 수 있다. A velvet fabric having excellent antistatic properties and excellent appearance according to an embodiment of the present invention is produced by weaving pile yarn on the fabric obtained as described above. The acetate yarn used as the filament yarn is advantageous in that the acetate yarn is superior in nylon and polyester having a circular cross section because the cross section of the acetate yarn is not sharper and rounded and therefore has a soft touch and a corrugated cross section. The pile used in the present invention is preferably an acetate yarn having a fineness of 120 denier to 300 denier and a strength of less than 3 g / d. When the acetate yarn as described above is used as a pile yarn, the pliability of the pile yarn is excellent. In particular, even when the pile fabric is not easily exposed to the outside and part of the pile fabric is exposed at the angled part, The appearance can be maintained.
상기 파일사로 사용되는 아세테이트사는 후염사 또는 원착사를 이용할 수 있다. 즉, 통상의 제조방법으로 원사를 제조한 후 염색공정을 수행하여 착색하는 후염사와, 제조시 카본 블랙을 첨가하여 착색하는 원착사 모두 사용이 가능하다. 특히 파일사로 원착사를 사용하는 경우에는 폴리에스테르 원착사를 사용한 지조직과 함께 벨벳 직물의 대전방지성을 더욱 향상시킬 수 있다. The acetate yarn used as the filament yarn may be a post-yarn yarn or a circular yarn. Namely, it is possible to use both a post-dyeing yarn obtained by coloring a yarn after a yarn is manufactured by a conventional production method, and a colored yarn which is colored by adding carbon black at the time of production. In particular, in the case of using a filament yarn as the filament yarn, the antistatic property of the velvet fabric can be further improved together with the fabric using the polyester yarn.
또한 상기 벨벳 직물의 제조시 상기 파일사의 밀도는 200,000 내지 500,000 데니어/인치2 인 것이 바람직하다. 상기 파일사의 밀도는 벨벳 직물의 단위면적에 존재하는 파일사의 총섬도를 의미한다. 즉, 파일사를 섬도가 작은 가는 실을 사용함으로써, 파일 본수를 증가시켜 파일사의 밀도를 증가시키게 되면, 유사 스웨이드 감촉을 갖는 매끄럽고 아름다운 표면, 큰 파일 밀도 및 심오한 광택을 갖는 벨벳 직물을 얻을 수 있다. 즉, 파일 사의 밀도가 200,000 데니어/인치2 미만인 경우에는 벨벳 직물의 부드러운 촉감이 감소하고, 500,000 데니어/인치2 를 초과하는 경우에는 파일사 사이에 골이 형성되고 외력에 의해 파일의 직립형태가 쉽게 무너지는 단점이 있다. 따라서 본 발명의 파일사의 밀도는 200,000 내지 500,000 데니어/인치2 인 것이 가장 바람직하다.It is also preferred that the pile yarns have a density of 200,000 to 500,000 denier / inch 2 in the production of the velvet fabric. The density of the pile yarn means the total fineness of the pile yarn existing in the unit area of the velvet fabric. That is, by increasing the density of the filament yarn by increasing the number of files by using a filament yarn having a small fineness, a velvet fabric having smooth and beautiful surface, large file density and profound luster with a pseudo suede feel can be obtained . That is, when the density of the filament yarn is less than 200,000 denier / inch 2, the soft touch of the velvet fabric is reduced. When the filament yarn density exceeds 500,000 denier / inch 2 , a valley is formed between the filament yarns, There is a drawback that it collapses. Therefore, it's density file of the present invention is from 200,000 to 500,000 denier / inch 2 is most preferred.
상기와 같이 제조된 본 발명의 일실시예에 따른 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물은 지조직에 사용된 카본 블랙을 포함하는 폴리에스테르 원착사에 의해 제전성이 부여될 수 있다. The velvet fabric having excellent antistatic properties and excellent appearance according to an embodiment of the present invention manufactured as described above can be imparted with antistatic property by the polyester raw material including carbon black used in the ground tissue.
본 발명의 지조직에 사용된 카본 블랙을 포함하는 폴리에스테르 원착사는 영구적인 대전방지능을 가지며, 넓은 영역에서의 도전성을 가진다.The polyester base yarn including the carbon black used in the paper structure of the present invention has a permanent antistatic function and has a wide range of conductivity.
폴리에스테르와 같은 고분자 소재를 표면저항을 낮추어 대전방지 기능을 갖게 하는 방법으로는 대전방지제를 표면에 도포하는 방법 또는 카본 블랙 등의 대전방지용 첨가제를 ?O합시 첨가하는 방법 또는 전도성 고분자의 층을 표면에 형성시키는 방법 등이 알려져 있다. 폴리에스테르 수지의 표면에 도포되는 외부형 대전방지제는 초기 대전방지성은 우수하지만 상대습도가 높은 환경에서는 내구성이 유지되지 못하는 문제점이 있으며, 내부형 대전방지제는 플라스틱 성형시 다른 첨가제와 함께 사용될 수 있어서 작업이 간편할 뿐만 아니라 성형 후에도 표면으로 대전방지제가 계속적으로 스며나와 대전방지층을 형성하기 때문에 높은 상대습도 하에서도 내구성을 보유할 수 있다는 장점이 있는 반면, 그 첨가량이 많을 경우 인장강도 등과 같은 기계적 특성을 현저히 저하시키게 되는 문제점이 있다.Examples of a method of lowering the surface resistance of a polymer material such as polyester to provide an antistatic function include a method of applying an antistatic agent to the surface or a method of adding an antistatic additive such as carbon black to a surface of a conductive polymer, And the like are known. The external antistatic agent applied on the surface of the polyester resin is excellent in initial antistatic property but has a problem that durability can not be maintained in an environment of high relative humidity and the internal antistatic agent can be used together with other additives in plastic molding, The antistatic agent continuously penetrates into the surface even after molding to form an antistatic layer. Therefore, it is advantageous to have durability even under a high relative humidity. On the other hand, when the amount of the antistatic agent is high, mechanical properties such as tensile strength There is a problem that is significantly deteriorated.
상기와 같이 지조직을 구성하는 경사 및/또는 위사에 카본 블랙을 포함하는 폴리에스테르 원착사를 사용하므로써, 이를 이용한 벨벳 직물에 영구적인 대전방지성을 부여할 수 있게 된다. 이 때 상기 폴리에스테르 원착사는 원사내 카본 함량이 0.5 내지 2.0 중량%인 것이 바람직하다. 위에서 살핀 바와 같이, 상기 카본 블랙의 함량이 0.5 중량% 미만일 경우에는 원착사 자체로 색상 발현이 어렵고, 2.0 중량%을 초과하는 경우에는 상기 카본 블랙의 추가함에 따라 더 이상 색상 발현의 효과가 나타나지 않는다. 또한 2.0 중량%를 초과하는 경우에는 카본 블랙이 이물질로 작용하여 사절 등의 방사 작업성이 저하되는 문제점이 발생하게 된다. As described above, by using a polyester raw material containing carbon black in the warp and / or weft constituting the ground structure, permanent antistatic property can be imparted to the velvet fabric using the same. At this time, the polyester base yarn preferably has a carbon content in the yarn of 0.5 to 2.0 wt%. As can be seen from the above, when the content of the carbon black is less than 0.5% by weight, color reproduction is difficult to achieve by itself, and when it exceeds 2.0% by weight, the effect of further color development is not exhibited due to the addition of the carbon black . On the other hand, when the amount exceeds 2.0% by weight, carbon black acts as a foreign substance, which lowers the spinning workability of yarn and the like.
상기와 같은 일련의 공정을 거쳐 본 발명의 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물을 제조할 수 있게 된다. Through the above-described series of processes, it is possible to produce a velvet fabric having an excellent antistatic property and a beautiful appearance of the present invention.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시한다. 그러나 하기의 실시예는 본 발명을 보다 쉽게 이해하기 위하여 제공되는 것일 뿐 본 발명이 하기의 실시예에 한정되는 것은 아니다.Hereinafter, preferred embodiments of the present invention will be described in order to facilitate understanding of the present invention. However, the following examples are provided only for the purpose of easier understanding of the present invention, and the present invention is not limited to the following examples.
[실시예 1][Example 1]
카본 블랙 1 중량%를 포함하는 150 데니어인 폴리에스테르 원착사를 경사로 이용하고, 위사로는 50 데니어의 레귤러 폴리에스터를 사용하여 경사밀도 30本/inch, 위사밀도 50本/inch의 평직으로 제직하여 지조직을 제직하였다. 상기와 같이 제직된 지조직에 150 데니어인 아세테이트사를 파일사로 이용하여 상기 파일사의 밀도가 200,000 데니어/인치2 인 벨벳 직물을 완성하여 시험편으로 사용하였다. A polyester knitted fabric having a denier of 150 denier containing 1% by weight of carbon black was used as a warp, and a weft yarn was weaved using a regular denier polyester of 50 denier at a warp density of 30 yarns / inch and a weft density of 50 yarns / inch The organization of the paper was made. The velvet fabric having a denier of 200,000 denier / inch 2 was used as the test piece by using acetate yarn of 150 denier as pile yarn to the ground tissue as described above.
[실시예 2][Example 2]
카본 블랙 1 중량%를 포함하는 50 데니어인 폴리에스테르 원착사를 위사로 이용하고, 경사로는 150 데니어의 레귤러 폴리에스터를 사용하여 경사밀도 30本/inch, 위사밀도 50本/inch의 평직으로 제직하여 지조직을 제직하였다. 상기와 같이 제직된 지조직에 150 데니어인 아세테이트사를 파일사로 이용하여 상기 파일사의 밀도가 350,000 데니어/인치2 인 벨벳 직물을 완성하여 시험편으로 사용하였다. A 50 denier polyester raw material containing 1% by weight of carbon black was used as a weft yarn and a weft yarn was weighed in a plain weave having a weft density of 30 yarns / inch and a weft density of 50 yarns / inch using a regular polyester of 150 denier The organization of the paper was made. The velvet fabric having a denier of 350,000 denier / inch 2 was used as a test piece by using acetate yarn of 150 denier as pile yarn to the woven paper tissue as described above.
[실시예 3][Example 3]
카본 블랙 1 중량%를 포함하는 150 데니어인 폴리에스테르 원착사를 경사로 이용하고, 위사로는 카본 블랙 1 중량%를 포함하는 50 데니어인 폴리에스테르 원착사를 사용하여 경사밀도 30本/inch, 위사밀도 50本/inch의 평직으로 제직하여 지조직을 제직하였다. 상기와 같이 제직된 지조직에 150 데니어인 아세테이트사를 파일사로 이용하여 상기 파일사의 밀도가 500,000 데니어/인치2 인 벨벳 직물을 완성하여 시험편으로 사용하였다. A polyester knitted fabric having a denier of 150 denier containing 1% by weight of carbon black was used as a warp, and a polyester denier having a denier of 50 denier containing 1% by weight of carbon black was used, And woven in a plain weave of 50 lines / inch to weave the ground tissue. The velvet fabric having a density of 500,000 denier / inch 2 of the pile yarn was used as a test piece by using acetate yarn of 150 denier as pile yarn to the ground tissue as described above.
[비교예 1][Comparative Example 1]
카본 블랙을 포함하지 않는 150 데니어인 폴리에스테르 원착사를 경사로 사용한 점을 제외하고, 나머지 조건은 실시예 1과 동일하게 벨벳 직물을 제조하여 시험편으로 사용하였다. A velvet fabric was prepared in the same manner as in Example 1 except that a polyester denier having no carbon black was used as a warp yarn.
[비교예 2][Comparative Example 2]
카본 블랙을 포함하지 않는 50 데니어인 폴리에스테르 원착사를 위사로 사용한 점을 제외하고, 나머지 조건은 실시예 2와 동일하게 벨벳 직물을 제조하여 시험편으로 사용하였다. A velvet fabric was prepared and used as test pieces in the same manner as in Example 2, except that a 50 denier polyester yarn without carbon black was used as a weft yarn.
[비교예 3][Comparative Example 3]
카본 블랙을 포함하지 않는 150 데니어인 폴리에스테르 원착사를 경사로 사용하고, 카본 블랙을 포함하지 않는 50 데니어인 폴리에스테르 원착사를 위사로 사용한 점을 제외하고, 나머지 조건은 실시예 3과 동일하게 벨벳 직물을 제조하여 시험편으로 사용하였다The remaining conditions were the same as in Example 3, except that a polyester knitted fabric of 150 denier without carbon black was used as the warp, and a 50 denier polyester knitted fabric containing no carbon black was used as the weft yarn. Fabrics were prepared and used as test specimens
상기 실시예 1 내지 3 및 비교예 1 내지 3의 시험편에 대하여 마찰포로는 KS K 0905에 규정된 나일론 포를 사용하고, 23±2℃, 55±2%의 항온·항습의 조건하에서 KS K 0555 B법에 의거하여 마찰 대전압을 측정하였다. 즉, KS K 0905에 규정된 나일폰 포를 마찰포로서 일반 세제로 세탁한 후에 건조시키고 5 cm X 5 cm의 크기로 절단하여 준비하고, 다음에 상기 <실시예 1 내지 3> 및 <비교예 1 내지 3>의 시험편을 60초 동안 회전 마찰시키고 Rotary Static Tester를 사용하여 마찰 대전압을 측정하였다. 그리고 그 결과를 아래의 표 1에 나타내었다With respect to the test pieces of Examples 1 to 3 and Comparative Examples 1 to 3, the friction prison was a nylon cloth defined in KS K 0905, and under the conditions of constant temperature and humidity of 23 ± 2 ° C and 55 ± 2%, KS K 0555 The friction voltage was measured according to the B method. That is, the nylon foil as defined in KS K 0905 was washed with a general detergent as a frictional cloth, dried and cut into a size of 5 cm × 5 cm. Then, the above <Examples 1 to 3> and <Comparative Example 1 to 3 > were subjected to rotational rubbing for 60 seconds and the friction voltage was measured using a Rotary Static Tester. The results are shown in Table 1 below
상기 표 1을 살펴보면, 초기 마찰 대전압의 경우에 실시예 1의 시험편의 경우에 마찰 대전압이 161 V로 측정되었으며, 실시예 2의 시험편의 경우에 마찰 대전압이 178 V로 측정되었다. 특히 경사 및 위사를 모두 폴리에스테르 원착사를 사용한 실시예 3의 시험편의 경우에는 마찰 대전압이 123 V로 측정되었다. Referring to Table 1, in the case of the initial frictional electrification voltage, the frictional electrification voltage was measured at 161 V in the case of the test piece of Example 1, and in the case of the test piece of Example 2, the frictional electrification voltage was measured at 178V. In particular, in the case of the test piece of Example 3 in which both the warp and the weft were made of the polyester encapsulant, the frictional electrification voltage was measured to be 123 V. [
이에 반하여 본 발명의 일실시예에 따른 폴리에스테르 원착사를 사용하지 않은 비교예 1 내지 3의 시험편의 경우에는 마찰 대전압이 968 V 내지 1,045 V로 측정되었다. 상기 <표 1>은 본 발명의 일실시예에 따른 벨벳 직물의 마찰 대전압이 본 발명의 폴리에스테르 원착사를 사용하지 않은 비교예의 시험편 대비 현저하게 감소되는 것을 보여주고 있다.On the contrary, in the case of the test pieces of Comparative Examples 1 to 3 in which polyester precursor was not used according to an embodiment of the present invention, the frictional electrification voltage was measured from 968 V to 1,045 V. Table 1 above shows that the frictional electrification voltage of the velvet fabric according to an embodiment of the present invention is significantly reduced as compared with the test piece of the comparative example not using the polyester encasing of the present invention.
특히, 실시예 1 내지 3의 시험편을 세탁조건 KS K ISO 6330에 의거하여 세탁온도 40±3 ℃, 빨랫줄 건조 방법으로 20회 세탁후 마찰 대전압을 평가한 결과를 살펴보면, 실시예 1 내지 3의 시험편의 경우에는 모두 초기의 마찰 대전압과 유사한 마찰 대전압을 나타내는 것을 알 수 있다. 즉, 본 발명의 벨벳 직물은 세탁 후에도 측정된 마찰 대전압이 지속적으로 유지되고 있어, 세탁 내구성이 우수하며, 영구적인 대전 방지성이 있는 것을 확인 할 수 있다.In particular, the test pieces of Examples 1 to 3 were evaluated for the rubbing voltage by washing at a washing temperature of 40 ± 3 ° C and a
본 발명은 도면에 도시된 실험예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 다른 실험예가 가능하다는 점을 이해할 것이다. 따라서 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의하여 정해져야 할 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the scope of the present invention. Accordingly, the true scope of the present invention should be determined by the technical idea of the appended claims.
10 : 위사, 20 : 경사, 30 : 지조직, 40 : 파일조직,10: weft, 20: slope, 30: ground structure, 40: file structure,
Claims (8)
상기 지조직의 경사 및 위사 중 어느 하나 이상은 연신 배율이 5.5 ~ 6.4인 폴리에스테르 원착사로 구성되되,
상기 경사는 70~160 데니어이고, 위사는 50 데니어 이상이며,
상기 경사의 밀도는 22 本/인치 이상이며, 상기 위사의 밀도는 46本/인치 이상이며,
상기 파일사는 120~300 데니어인 아세테이트사로 구성되되,
상기 파일사의 밀도는 200,000 내지 500,000 데니어/인치2 인 것을 특징으로 하는 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물.
A velvety fabric comprising a tissue and a filament yarn,
Wherein at least one of the warp and weft of the ground structure is composed of a polyester yarn having a draw ratio of 5.5 to 6.4,
The warp is 70 to 160 denier, the warp yarn is 50 denier or more,
The density of the warp yarns is 22 yarns / inch or more, the density of the weft yarns is 46 yarns / inch or more,
The pile yarn is composed of acetate yarns having a denier of 120 to 300,
The file's density is from 200,000 to 500,000 denier / inch 2, the antistatic properties are velvet fabric having excellent and beautiful appearance, characterized in that.
상기 폴리에스테르 원착사는 원사내 카본 함량이 0.5 내지 2.0 중량%인 것을 특징으로 하는 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물.
The method according to claim 1,
Characterized in that the polyester original yarn has a carbon content in the yarn of 0.5 to 2.0 wt%, and has a good antistatic property and a beautiful appearance.
상기 파일사는 후염사 또는 원착사인 것을 특징으로 하는 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물.
The method according to claim 1,
Characterized in that the pile yarn is a post-warp yarn or an original yarn yarn.
상기 폴리에스테르 원착사의 강도는 3 g/d 이상인 것을 특징으로 하는 제전성이 우수하고 미려한 외관을 갖는 벨벳 직물.
The method according to claim 1,
Wherein the polyester base yarn has a strength of 3 g / d or more.