KR101960738B1 - Sheet manufacturing method using water base acrylic coating agent and blowing preventing and waterproof method of roof shingle using thereof - Google Patents
Sheet manufacturing method using water base acrylic coating agent and blowing preventing and waterproof method of roof shingle using thereof Download PDFInfo
- Publication number
- KR101960738B1 KR101960738B1 KR1020180094550A KR20180094550A KR101960738B1 KR 101960738 B1 KR101960738 B1 KR 101960738B1 KR 1020180094550 A KR1020180094550 A KR 1020180094550A KR 20180094550 A KR20180094550 A KR 20180094550A KR 101960738 B1 KR101960738 B1 KR 101960738B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- waterproof
- acrylic coating
- sheet
- Prior art date
Abstract
Description
본 발명은 도막 방수제를 이용한 시트 제조방법 및 이를 이용한 지붕 슁글의 날림 방지 및 방수시공공법에 관한 것으로서, 보다 상세하게는 슁글판재층 상층을 커버하는 커버층인 시트가 다이아세톤아크릴아마이드, 메틸렌비스아크릴아마이드, 아크릴아미노메틸프로판설퍼닉에시드, 1-브로모-1-메틸사이클로헥산, 아이소뷰틸사이클로펜탄, 소르비탄스테아레이트, 소르비탄아이소스테아레이트 및 글리세린스테아레이트를 혼합 및 가열한 후 고속으로 강하게 교반하면서 물을 서서히 첨가한 수성 아크릴 도막 방수제에 함침되도록 하여 상기 수성 아크릴 도막 방수제가 접착 기능을 위해 도포된 슁글판재층의 상층을 커버할 때 접착 강도와 방수 성능이 향상되도록 할 수 있는 수성 아크릴 도막 방수제를 이용한 시트 제조방법 및 이를 이용한 지붕 슁글의 날림 방지 및 방수시공공법에 관한 것이다.The present invention relates to a method for producing a sheet using a waterproofing agent for a coating film, and a method for preventing shrinkage of a roof shingle and a waterproofing method using the same. More particularly, the present invention relates to a sheet- Amide, acrylaminomethylpropane sulfone acid, 1-bromo-1-methylcyclohexane, isobutylcyclopentane, sorbitan stearate, sorbitan isostearate and glycerin stearate are mixed and heated, The waterproof acrylic coating film waterproofing agent is impregnated with the aqueous acrylic coating film waterproofing agent gradually added with water to improve the adhesive strength and waterproofing performance when the waterproof acrylic coating film waterproofing agent covers the upper layer of the shrinkable sheet material layer And a roof shingle using the same And a waterproof construction method.
일반적으로, 건축물의 지붕이나 옥상의 콘크리트층은 대기 온도에 따라 수축과 팽창이 반복된다. 이에, 이러한 지붕 외벽면이 그대로 노출되었을 경우 그 만큼 균열 등의 발생 가능성이 높아지게 된다. Generally, the roof of a building or the concrete layer on the roof repeat shrinkage and expansion depending on the atmospheric temperature. Therefore, when the outer surface of the roof is directly exposed, the possibility of occurrence of cracks or the like is increased.
따라서 최근에는 지붕 외벽면 표면에 판재 형태의 슁글판재층을 부착시켜 외부 환경으로부터 지붕 외벽면을 보호하는 시공법이 널리 사용되고 있다.Therefore, recently, a method of protecting the outer wall surface of the roof from the external environment by attaching a shingle plate material in the form of a plate to the surface of the outer wall surface of the roof has been widely used.
여기서, 상기 슁글판재층은 평판 형태의 각 슁글판재 단부가 상호 적층된 상태, 즉, 기와 형태로 덧대어지는 구조가 반복되어 지붕 외벽면 전체를 덮고 있는 상태로 설치된다.Here, the shingle plate layer is installed in a state in which the end portions of the plate-shaped shingle plates are laminated to each other, that is, the structure is padded in a tile shape so as to cover the entire outer surface of the roof.
그런데, 이러한 각 슁글판재는 접착층에 의해 지붕 외벽면에 고정된 상태를 가지기는 하지만, 각 슁글판재 사이에는 별도의 결합 구조가 형성되어 있지 않아 태풍 등과 같은 바람이 강하게 외력을 작용시키는 경우 각 슁글판재가 쉽게 분리되어 사람이나 기타 건물에 충돌하는 현상이 빈번하게 발생된다.However, since each shingle plate member is fixed to the outer wall surface of the roof by the adhesive layer, a separate coupling structure is not formed between each shingle plate member. Therefore, when a strong wind such as a typhoon acts on external force, It easily separates and collides with people or other buildings frequently.
이에, 상기와 같은 문제점을 해결하기 위하여, 등록특허 제10-1041557호 등에 개시된 바와 같이, 상기 슁글판재층에 가로 및 세로 방향으로 슁글판재들 상호간을 고정하는 부직포 재질의 연결층이 개시된 바 있다.In order to solve the above problems, a connecting layer made of a non-woven material for fixing the shingle plates to each other in the transverse and longitudinal directions has been disclosed in Japanese Patent Application No. 10-1041557.
그러나 이러한 경우에도 오랜 시간이 경과시 바람이나 빗물 또는 눈 등에 의해 연결층의 접착 기능이 점차적으로 저하되어 슁글판재층의 날림 방지 및 도막 방수 등의 유지 보수가 실시되어야 하는 문제점이 있고, 이에, 슁글판재층의 날림을 방지하는 접착 기능을 제공하면서도 도막 방수 기능까지 제공하여 유지 보수를 간단히 할 수 있는 방안이 대두되고 있다.However, even in such a case, the adhesive function of the connection layer gradually decreases due to wind, rain, snow or the like when a long period of time has elapsed, so that there is a problem that maintenance such as prevention of skipping of the shingle plate layer and waterproofing of the coating film must be performed. There has been a tendency to provide a coating function to prevent water spillage of the plate material layer while providing a waterproof function of the coating film to simplify the maintenance.
따라서 본 발명의 목적은 슁글판재층 상층을 커버하는 커버층인 시트가 다이아세톤아크릴아마이드, 메틸렌비스아크릴아마이드, 아크릴아미노메틸프로판설퍼닉에시드, 1-브로모-1-메틸사이클로헥산, 아이소뷰틸사이클로펜탄, 소르비탄스테아레이트, 소르비탄아이소스테아레이트 및 글리세린스테아레이트를 혼합 및 가열한 후 고속으로 강하게 교반하면서 물을 서서히 첨가한 수성 아크릴 도막 방수제에 함침되도록 하여 상기 수성 아크릴 도막 방수제가 접착 기능을 위해 도포된 슁글판재층의 상층을 커버할 때 접착 강도와 방수 성능이 향상되도록 할 수 있는 수성 아크릴 도막 방수제를 이용한 시트 제조방법 및 이를 이용한 지붕 슁글의 날림 방지 및 방수시공공법을 제공하는 것이다.SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to provide a method for producing a sheet which is a cover layer covering an upper layer of a shingle plate material, comprising the steps of: (1) dissolving a diacetone acrylamide, methylenebisacrylamide, acrylaminomethylpropane- The water-based acrylic coating film waterproofing agent is impregnated with a water-soluble acrylic coating film water-repellent agent which is added with water and mixed with strong stirring at high speed after mixing and heating pentane, sorbitan stearate, sorbitan isostearate and glycerin stearate, The present invention also provides a method of manufacturing a sheet using a waterproof acrylic waterproofing agent capable of improving adhesion strength and waterproofing performance when covering an upper layer of a coated shingle plate layer, and preventing shrinkage of roof shingle and waterproofing construction method using the same.
한편, 본 발명의 목적은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.Meanwhile, the object of the present invention is not limited to the above-mentioned objects, and other objects not mentioned can be clearly understood by those skilled in the art from the following description.
본 발명에 의하면, 다이아세톤아크릴아마이드 100 중량부에 다이아세톤아크릴아마이드 100 중량부를 기준으로 메틸렌비스아크릴아마이드 70~90 중량부, 아크릴아미노메틸프로판설퍼닉에시드 60~80 중량부, 1-브로모-1-메틸사이클로헥산 50~70 중량부, 아이소뷰틸사이클로펜탄 40~60 중량부, 소르비탄스테아레이트 10~30 중량부, 소르비탄아이소스테아레이트 9~11 중량부 및 글리세린스테아레이트 8~10 중량부가 혼합되어 200℃로 가열된 상태에서 교반된 후 상기 교반된 혼합물에 상기 혼합물 100 중량부를 기준으로 물 50~80 중량부가 첨가되어 수성 아크릴 도막방수제가 제조되는 단계와; 상기 제조된 수성 아크릴 도막방수제에 부직포가 함침되어 도막 방수 시트가 제조되는 단계를 포함하는 수성 아크릴 도막 방수제를 이용한 시트 제조방법이 제공된다.According to the present invention, 100 parts by weight of diacetone acrylamide is mixed with 70 to 90 parts by weight of methylene bisacrylamide, 60 to 80 parts by weight of acrylaminomethylpropane sulfone acid, 1-bromo- 50 to 70 parts by weight of 1-methylcyclohexane, 40 to 60 parts by weight of isobutylcyclopentane, 10 to 30 parts by weight of sorbitan stearate, 9 to 11 parts by weight of sorbitan isostearate and 8 to 10 parts by weight of glycerin stearate Stirring the mixture at 200 DEG C, and adding 50 to 80 parts by weight of water based on 100 parts by weight of the mixture to the stirred mixture to prepare a waterproof acrylic coating film waterproofing agent; And a step of impregnating the non-woven fabric with the water-based acrylic coating film waterproofing agent so as to produce a waterproof coating film.
여기서, 상기 부직포는, 140g/m2 내지 160g/m2 정도의 면밀도를 가지는 것이 바람직하다.Here, the non-woven fabric, it is desirable to have a 140g / m 2 to the surface density of about 160g / m 2.
또한, 본 발명에 의하면, 상기 수성 아크릴 도막 방수제를 이용한 시트 제조방법에 의해 제조된 도막 방수 시트와 수성 아크릴 도막 방수제를 포함하고, 지붕 외벽면 표면에 시공된 슁글판재층의 표면에 전처리 작업이 진행되는 단계와; 상기 슁글판재층의 표면에 상기 수성 아크릴 도막 방수제가 도포 및 시공되어 접착층이 구성되는 단계와; 상기 접착층에 상기 도막 방수 시트가 부착 또는 접착되는 단계를 포함하는 지붕 슁글의 날림 방지 및 방수시공공법이 제공된다.According to the present invention, a pretreatment operation is performed on the surface of the shingle plate layer formed on the surface of the outer wall surface of the roof, including the coating waterproof sheet and the waterproof acrylic coating film waterproofing agent produced by the sheet manufacturing method using the waterproof acrylic waterproofing agent ; Applying and coating the waterproof acrylic acrylate coating on the surface of the shingle plate layer to form an adhesive layer; And a step of attaching or adhering the paint film waterproof sheet to the adhesive layer, and a waterproofing construction method of the roof shingle.
따라서 본 발명에 의하면, 슁글판재층 상층을 커버하는 커버층인 시트가 다이아세톤아크릴아마이드, 메틸렌비스아크릴아마이드, 아크릴아미노메틸프로판설퍼닉에시드, 1-브로모-1-메틸사이클로헥산, 아이소뷰틸사이클로펜탄, 소르비탄스테아레이트, 소르비탄아이소스테아레이트 및 글리세린스테아레이트를 혼합 및 가열한 후 고속으로 강하게 교반하면서 물을 서서히 첨가한 수성 아크릴 도막 방수제에 함침되도록 하여 상기 수성 아크릴 도막 방수제가 접착 기능을 위해 도포된 슁글판재층의 상층을 커버할 때 접착 강도와 방수 성능이 향상되도록 할 수 있다.Therefore, according to the present invention, the sheet which is the cover layer covering the upper layer of the shingle plate layer is made of at least one of diacetone acrylamide, methylene bisacrylamide, acrylaminomethylpropane sulfone acid, The water-based acrylic coating film waterproofing agent is impregnated with a water-soluble acrylic coating film water-repellent agent which is added with water and mixed with strong stirring at high speed after mixing and heating pentane, sorbitan stearate, sorbitan isostearate and glycerin stearate, The adhesive strength and the waterproof performance can be improved when covering the upper layer of the coated shingle plate material layer.
한편, 본 발명의 효과는 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않은 다른 효과들은 청구범위의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.On the other hand, the effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned can be clearly understood by those skilled in the art from the description of the claims.
이하, 본 발명의 실시예에 대하여 상세히 설명하기로 한다. Hereinafter, embodiments of the present invention will be described in detail.
본 발명의 실시예에 따른 수성 아크릴 도막 방수제를 이용한 시트 제조방법은, 다이아세톤아크릴아마이드 100 중량부에 다이아세톤아크릴아마이드 100 중량부를 기준으로 메틸렌비스아크릴아마이드 70~90 중량부, 아크릴아미노메틸프로판설퍼닉에시드 60~80 중량부, 1-브로모-1-메틸사이클로헥산 50~70 중량부, 아이소뷰틸사이클로펜탄 40~60 중량부, 소르비탄스테아레이트 10~30 중량부, 소르비탄아이소스테아레이트 9~11 중량부 및 글리세린스테아레이트 8~10 중량부가 혼합되어 200℃로 가열된 상태에서 20000~23000rpm의 속도로 강하게 교반된 후 상기 교반된 혼합물에 상기 혼합물 100 중량부를 기준으로 물 50~80 중량부가 20~24시간 동안 서서히 첨가되어 수성 아크릴 도막방수제가 제조되는 단계와, 상기 제조된 수성 아크릴 도막방수제에 140g/m2 내지 160g/m2의 두께를 가지는 부직포가 함침되어 도막 방수 시트가 제조되는 단계를 포함한다.In a method for producing a sheet using a waterproof acrylic coating film waterproofing agent according to an embodiment of the present invention, 100 parts by weight of diacetone acrylamide is mixed with 70 to 90 parts by weight of methylene bisacrylamide based on 100 parts by weight of diacetone acrylamide, 60 to 80 parts by weight of peronic acid, 50 to 70 parts by weight of 1-bromo-1-methylcyclohexane, 40 to 60 parts by weight of isobutylcyclopentane, 10 to 30 parts by weight of sorbitan stearate, And 8 to 10 parts by weight of glycerin stearate were mixed at a temperature of 200 ° C. and stirred vigorously at a speed of 20000 to 23000 rpm. To the stirred mixture, 50 to 80 parts by weight of water, based on 100 parts by weight of the mixture, 20 to 24 and the steps are gradually added to the prepared water-based acrylic coating waterproofing agent for a time, an aqueous acrylic coating waterproofing agent prepared above 140g / m 2 to 160g / m 2 thickness of The non-woven fabric having the water-repellent layer is impregnated with the non-woven fabric.
상기 부직포는, 슁글판재층의 상층에 도포된 상기 수성 아크릴 도막방수제에 접착 구성되어 슁글판재층의 날림 방지를 위한 접착 기능과 방수 기능이 제공되도록 하는 고정 및 방수수단으로서, 폴리프로필렌 재질과 140g/m2 내지 160g/m2 정도의 면밀도를 가지는 것이 바람직하다.Wherein the nonwoven fabric is made of a polypropylene material and has a water resistance of 140 g / m < 2 > or less. The nonwoven fabric comprises a waterproof acrylic waterproofing agent applied to an upper layer of a shingle plate layer, preferably it has a surface density of approximately m 2 to 160g / m 2.
여기서, 상기 부직포가 140g/m2를 미만하는 면밀도를 가지는 경우에는 상기 수성 아크릴 도막방수제가 상기 부직포의 내부를 향해 모두 함침되는 높은 투과율로 인하여 상기 부직포의 상측면 표면에 상기 수성 아크릴 도막방수제에 따른 방수층이 소정 두께로 형성되지 못하여 방수층을 이용한 방수 기능이 저하되는 문제점이 있다. 또한, 상기 부직포가 160g/m2를 초과하는 면밀도를 가지는 경우에는 상기 수성 아크릴 도막방수제가 상기 부직포의 일정 깊이로 함침되지 못하게 되는 낮은 투과율로 인하여 재료의 변형률 차이에 따른 균열이 발생하게 되고 이에 내구성과 방수성이 저하되는 문제점이 있다. In the case where the nonwoven fabric has a surface density of less than 140 g / m 2 , the water-based acrylic coating film water repellent agent is impregnated all the way toward the inside of the nonwoven fabric, There is a problem that the waterproof layer is not formed to a predetermined thickness and the waterproof function using the waterproof layer is deteriorated. In addition, when the nonwoven fabric has a surface density exceeding 160 g / m 2 , the waterproofing agent for an aqueous acrylic coating film is cracked due to a difference in strain of the material due to a low transmittance which prevents the nonwoven fabric from being impregnated to a certain depth of the nonwoven fabric. And the water resistance is deteriorated.
이에, 상기 부직포는 상기와 같은 한정된 면밀도를 가지는 것이 바람직하다.Accordingly, it is preferable that the nonwoven fabric has a limited surface area as described above.
상기 수성 아크릴 도막 방수제는, 상기 부직포에 방수층을 제공하여 부직포의 하면이 슁글판재층의 상층에 도포되는 수성 아크릴 도막 방수제 즉, 슁글판재층의 표면에 접착시 접착과 도막 기능이 향상되도록 하는 수단으로서, 다이아세톤아크릴아마이드 100 중량부에 다이아세톤아크릴아마이드 100 중량부를 기준으로 메틸렌비스아크릴아마이드 70~90 중량부, 아크릴아미노메틸프로판설퍼닉에시드 60~80 중량부, 1-브로모-1-메틸사이클로헥산 50~70 중량부, 아이소뷰틸사이클로펜탄 40~60 중량부, 소르비탄스테아레이트 10~30 중량부, 소르비탄아이소스테아레이트 9~11 중량부 및 글리세린스테아레이트 8~10 중량부가 혼합되어 200℃로 가열된 상태에서 20000~23000rpm의 속도로 강하게 교반된 후 상기 교반된 도막방수물에 상기 도막방수물 100 중량부를 기준으로 물 50~80 중량부가 20~24시간 동안 서서히 첨가되어 제조된다.The waterproof acrylic coating film waterproofing agent is a means for providing a waterproof layer on the nonwoven fabric so that the lower surface of the nonwoven fabric is coated on the upper surface of the shrinkable plate layer, , 100 parts by weight of diacetone acrylamide is mixed with 70 to 90 parts by weight of methylenebisacrylamide, 60 to 80 parts by weight of acrylaminomethylpropane sulfone acid, 1-bromo-1-methylcyclohexane 50 to 70 parts by weight of hexane, 40 to 60 parts by weight of isobutylcyclopentane, 10 to 30 parts by weight of sorbitan stearate, 9 to 11 parts by weight of sorbitan isostearate and 8 to 10 parts by weight of glycerin stearate, , The mixture was stirred at a speed of 20,000 to 23,000 rpm, and water was added to the stirred water-repellent layer of the coating film on the basis of 100 parts by weight of the water- 0 to 80 parts by weight for 20 to 24 hours.
상기 다이아세톤아크릴아마이드는, 도막 방수 시공시 방수성과 내마모성을 제공하여 투수비와 흡수비를 낮추고 신장성과 점착성 등을 제공하기 위한 것으로, 빛이나 열 등에 의해 쉽게 중합을 일으켜 혼합물들과의 결합 및 반응이 이루어지도록 한다.The diacetone acrylamide is intended to provide waterproofing and abrasion resistance in waterproofing the coating film to lower permeability and absorption ratio and to provide extensibility and tackiness. The diacetone acrylamide is easily polymerized by light or heat, .
상기 메틸렌비스아크릴아마이드는, 열에 강하고 마찰계수가 극히 낮으며 좋은 내화학성 특징을 통하여 접착 기능과 방수 기능을 통하여 도막 방수 시트의 내구성을 향상시킨다.The methylene bisacrylamide has strong resistance to heat, extremely low coefficient of friction, and good chemical resistance, thereby improving the durability of the waterproof sheet through its adhesive function and waterproof function.
여기서, 상기 메틸렌비스아크릴아마이드는, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 70~90 중량부가 첨가되는데, 상기 90 중량부 보다 많이 첨가되는 경우에는 높은 내화학성으로 인하여 조성물들의 혼합률이 저하되고, 상기 70 중량부 보다 적게 첨가되는 경우에는 접착 및 코팅 기능이 저하되어 내구성까지 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다. Here, the methylene bisacrylamide is added in an amount of 70 to 90 parts by weight based on 100 parts by weight of the diacetone acrylamide. When the amount of the methylene bisacrylamide is more than 90 parts by weight, the mixing ratio of the compositions is lowered due to high chemical resistance If it is added in an amount of less than 70 parts by weight, adhesion and coating function may be deteriorated and durability may be lowered.
상기 아크릴아미노메틸프로판설퍼닉에시드는, 상기 혼합물의 교반시 교반 효율이 향상되도록 한다.The acrylic aminomethyl propane sulfone ester provides an improvement in stirring efficiency when the mixture is stirred.
여기서, 상기 아크릴아미노메틸프로판설퍼닉에시드는, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 60~80 중량부가 첨가되는데, 상기 80 중량부 보다 많이 첨가되는 경우에는 혼합물들의 분산시 입자 크기의 분포도가 커지게 되어 오히려 교반성이 저하되고, 상기 60 중량부보다 적게 첨가되는 경우에는 분산시 입자 크기의 분포도가 작아지게 되어 교반성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.When the amount of the acrylaminomethyl propane sulfuric acid is more than 80 parts by weight based on 100 parts by weight of the diacetone acrylamide, If the amount is less than 60 parts by weight, the degree of dispersion of the particle size during dispersion tends to be small and the agglomeration is deteriorated. Therefore, it is preferable to use the limited weight portion as described above.
상기 1-브로모-1-메틸사이클로헥산은, 상기 혼합물들의 점도 기능을 조절하는 점도조절 및 결합제이다.The 1-bromo-1-methylcyclohexane is a viscosity modifier and binder that modulates the viscosity function of the mixtures.
여기서, 상기 1-브로모-1-메틸사이클로헥산은, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 50~70 중량부가 첨가되는데, 상기 70 중량부 보다 많이 첨가되면 강한 결합력으로 인하여 점도가 증가되어 오히려 교반 혼합이 저하되고, 상기 50 중량부 보다 적게 첨가되면 결합력이 발휘되지 못하여 전반적인 방수성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The 1-bromo-1-methylcyclohexane is added in an amount of 50 to 70 parts by weight based on 100 parts by weight of the diacetone acrylamide. When the amount of the 1-bromo-1-methylcyclohexane is more than 70 parts by weight, If the mixing amount is less than 50 parts by weight, the binding strength is not exhibited and the overall waterproofing property is deteriorated. Therefore, it is preferable to use the limited weight portion as described above.
상기 아이소뷰틸사이클로펜탄은, 상기 도막 방수 시트와 슁글판재층과의 접착 강도를 향상시키는 기능을 제공한다.The isobutylcyclopentane provides a function of improving the adhesion strength between the film waterproof sheet and the shingle plate layer.
여기서, 상기 아이소뷰틸사이클로펜탄은, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 40~60 중량부가 첨가되는데, 상기 60 중량부 보다 많이 첨가되면 도막 방수 시트와 슁글판재층 표면과의 접착력이 증대되지만 다른 혼합물들과의 교반성이 저하되고, 상기 40 중량부 보다 적게 첨가되면 도막 방수 시트와 슁글판재층 표면과의 접착력이 저하되어 슁글판재층의 날림 방지 기능이 제공되지 않는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The isobutylcyclopentane is added in an amount of 40 to 60 parts by weight based on 100 parts by weight of the diacetone acrylamide. If more than 60 parts by weight of the isobutylcyclopentane is added, adhesion between the waterproof sheet and the surface of the shingle plate layer is increased The degree of crosslinking with other mixtures is lowered. When the amount is less than 40 parts by weight, the adhesion between the coating film waterproof sheet and the surface of the shingle plate layer is lowered, and the shrinkage prevention function of the shingle plate layer is not provided. It is preferable to have the same limited weight portion.
상기 소르비탄스테아레이트는, 상기 혼합물들의 교반시 교반성이 향상되도록 계면 활성 기능을 제공한다.The sorbitan stearate provides a surfactant function so that the agitation of the mixtures improves the agitation.
여기서, 상기 소르비탄스테아레이트는, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 10~30 중량부가 첨가되는데, 상기 30 중량부 보다 많이 첨가되면 상기 혼합물들의 결합도가 오히려 저하되어 접착 기능이 저하되고, 상기 10 중량부 보다 적게 첨가되면 상기 혼합물들의 교반성이 크게 저하되어 접착 기능과 도막 기능이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The sorbitan stearate is added in an amount of 10 to 30 parts by weight based on 100 parts by weight of the diacetone acrylamide. If more than 30 parts by weight of the sorbitan stearate is added, the degree of bonding of the mixture is lowered, If less than 10 parts by weight is added, there is a problem that the degree of crosslinking of the mixtures is greatly lowered, thereby lowering the adhesive function and the coating film function.
상기 소르비탄아이소스테아레이트는, 상기 소르비탄스테아레이트와 함께 상기 혼합물들의 교반시 교반성이 향상되도록 하는 기능을 제공한다.The sorbitan isostearate, together with the sorbitan stearate, provides the ability to improve the agitation of the mixtures during stirring.
여기서, 상기 소르비탄아이소스테아레이트는, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 9~11 중량부가 첨가되는데, 상기 11 중량부 보다 많이 첨가되면 상기 혼합물들의 결합도가 오히려 저하되어 접착 기능이 저하되고, 상기 9 중량부 보다 적게 첨가되면 상기 혼합물들의 교반성이 크게 저하되어 접착 기능과 도막 기능이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The sorbitan isostearate is added in an amount of 9 to 11 parts by weight based on 100 parts by weight of the diacetone acrylamide. When the amount of the sorbitan isostearate is more than 11 parts by weight, the degree of bonding of the mixture is lowered, If less than 9 parts by weight is added, there is a problem that the agglomeration of the mixtures is significantly lowered to lower the adhesive function and the coating film function.
상기 글리세린스테아레이트는, 상기 혼합물들의 교반시 유화제 기능을 제공하여 방수층 또는 도막층의 압축 강도를 높이는 효과를 제공한다.The glycerin stearate provides an emulsifier function during stirring of the mixtures to provide an effect of increasing the compressive strength of the waterproof layer or the coating layer.
여기서, 상기 글리세린스테아레이트는, 상기 다이아세톤아크릴아마이드 100 중량부를 기준으로, 8~10 중량부가 첨가되는데, 상기 10 중량부 보다 많이 첨가되면 상기 혼합물들의 결합도가 너무 커지게 되어 오히려 방수층의 외력에 따른 압축 강도가 저하되고, 상기 8 중량부 보다 적게 첨가되면 상기 혼합물들의 결합도가 저하되어 방수층의 발수성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The glycerin stearate is added in an amount of 8 to 10 parts by weight based on 100 parts by weight of the diacetone acrylamide. If the amount of the glycerin stearate is more than 10 parts by weight, the degree of coupling of the mixture becomes too large. And if it is added in an amount of less than 8 parts by weight, the degree of bonding of the mixture may be lowered and the water repellency of the waterproof layer may be deteriorated.
한편, 본 발명에 의하면, 상기 수성 아크릴 도막방수제의 제조시, 상기와 같이 혼합물들이 소정의 중량비를 가지면서 혼합된 후 200℃의 온도로 가열된 상태에서 교반되도록 하고 있는데, 교반온도가 200℃의 온도 보다 낮으면 팽윤율이 저하되고, 교반온도가 200℃의 온도 보다 높으면 과팽윤이 되는 문제점이 있으므로, 상기와 같은 한정된 교반온도를 가지는 것이 좋다.According to the present invention, in the production of the aqueous acrylic coating film waterproofing agent according to the present invention, the mixture is mixed with a predetermined weight ratio as described above, and then stirred in a heated state at a temperature of 200 ° C. If the temperature is lower than the temperature, the swelling rate is lowered. If the stirring temperature is higher than the temperature of 200 ° C, the swelling may occur. Therefore, it is preferable to have the above limited stirring temperature.
또한, 본 발명에 의하면, 상기 수성 아크릴 도막방수제의 제조시, 상기와 같이 혼합물들이 소정의 중량비를 가지면서 혼합된 후 200℃의 온도로 가열된 상태에서 20000~23000rpm의 속도로 강하게 교반되도록 하고 있는데, 교반속도가 상기 범위 보다 낮으면 팽윤율이 저하되고, 교반속도가 상기 범위보다 크면 과팽윤이 되는 문제점이 있으므로, 상기와 같은 한정된 범위의 교반속도를 가지는 것이 좋다.According to the present invention, the water-based acrylic coating film waterproofing agent is mixed with a predetermined weight ratio as described above, and then stirred at 20000 to 23000 rpm in a heated state at 200 ° C If the stirring speed is lower than the above range, the swelling rate is lowered. If the stirring speed is higher than the above range, swelling may occur.
또한, 본 발명에 의하면, 상기와 같이 교반된 도막방수물에 상기 도막방수물 100 중량부를 기준으로 물 50~80 중량부가 20~24시간 동안 서서히 첨가되어 제조되도록 하고 있다.In addition, according to the present invention, 50 to 80 parts by weight of water is gradually added to the water-repellent coating of the present invention by stirring for 20 to 24 hours based on 100 parts by weight of the water-repellent coating.
상기 물은, 상기 도막방수물과 교반시 소정의 점도를 유지시켜 상기 부직포와의 함침시 투과율 등이 조절되도록 하는 기능을 제공한다.The water provides a function of maintaining a predetermined viscosity during stirring with the water repellency of the coating film to control the transmittance or the like upon impregnation with the nonwoven fabric.
여기서, 상기 물은, 상기 도막방수물 100 중량부를 기준으로, 50~80 중량부가 첨가되도록 하고 있는데, 상기 80 중량부 보다 많이 첨가되면 상기 도막방수물의 결합도 및 접착 강도가 약해지게 되어 접착 및 방수 기능이 저하되고, 상기 50 중량부 보다 적게 첨가되면 상기 도막방수물의 결합도 및 접착 강도가 강해져 시공성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.In this case, the water is added in an amount of 50 to 80 parts by weight based on 100 parts by weight of the coating film waterproofing agent. If more than 80 parts by weight of the coating waterproofing agent is added, And if it is added in an amount of less than 50 parts by weight, the bonding strength and adhesive strength of the water repellency of the coating film become strong and the workability is lowered.
한편, 본 발명에 의하면, 상기 수성 아크릴 도막방수제의 제조시, 상기와 같이 도막방수물에 물의 혼합되는 경우 20~24시간 동안 서서히 첨가되면서 교반되도록 하고 있는데, 교반시간 및 첨가시간이 24시간 보다 길면 고증점이 되어 교반성이 저하되고, 교반시간 및 첨가시간이 20시간 보다 짧으면 팽윤율이 저하되는 문제점이 있으므로, 상기와 같은 한정된 교반시간 및 첨가시간을 가지는 것이 바람직하다.According to the present invention, when the waterproofing agent for water-based acrylic coating is water-soluble, water is added to the coating waterproofing agent slowly for 20 to 24 hours. When the stirring time and addition time are longer than 24 hours And the swelling ratio is lowered when the agitation time and the addition time are shorter than 20 hours. Therefore, it is preferable that the agitation time and the addition time are limited as described above.
이하, 본 발명의 실시예에 따른 도막 방수 시트를 이용한 지붕 슁글의 날림 방지 및 방수시공공법에 대해 설명하면 다음과 같다.Hereinafter, the anti-skid and waterproof construction method of the roof shingle using the waterproof sheet according to the present invention will be described as follows.
먼저, 지붕 외벽면 표면에 시공된 슁글판재층의 표면에 청소 및 평탄화 작업 등과 같은 전처리 작업이 진행된다.First, a pretreatment operation such as cleaning and planarizing work is performed on the surface of the shingle plate layer formed on the outer surface of the roof.
이후, 상기 슁글판재층의 표면에 상기 수성 아크릴 도막 방수제가 도포 및 시공되어 접착층이 구성된다.Thereafter, the water-repellent acrylic coating solution is coated on the surface of the shingle plate layer to form an adhesive layer.
이후, 상기 접착층에 상기 수성 아크릴 도막 방수제에 부직포가 함침되어 방수층을 가지는 것을 통해 형성되는 도막 방수 시트가 부착 또는 접착되어 상기 슁글판재층의 슁글판재들의 날림이 방지되고 도막 방수 기능이 제공된다.Thereafter, a coating waterproof sheet formed by impregnating the nonwoven fabric with the waterproof acrylic coating film waterproofing agent and having a waterproof layer is adhered to or adhered to the adhesive layer, thereby preventing shrinking of shingle plates of the shingle plate layer, and a waterproof coating function is provided.
이하, 본 발명의 실시예에 따른 도막 방수 시트를 이용한 지붕 슁글의 날림 방지 및 방수시공공법의 효과를 구체적인 실시예를 통해 설명하기로 한다.Hereinafter, the effects of the anti-skid and waterproofing method of roof shingle using the waterproof sheet according to the present invention will be described with reference to specific embodiments.
이하 실시예는, 본 발명에 따른 도막 방수 시트를 이용한 지붕 슁글의 날림 방지 및 방수시공공법의 성능 등을 평가하기 위한 것으로, 부착강도, 굴곡저항성능, 접합안정성능 등의 시험이 실시되었으며, 이를 시제품 A사와 비교하여 표 1에 그 측정 결과를 비교하여 나타내었다. The following examples are intended to evaluate the performance of the roofing shingle for waterproofing and waterproofing using the waterproof sheet according to the present invention, and tests such as adhesion strength, bending resistance performance and bonding stability performance were conducted. Compared with the prototype A, the measurement results are compared and shown in Table 1.
다이아세톤아크릴아마이드 100 중량부에 다이아세톤아크릴아마이드 100 중량부를 기준으로 메틸렌비스아크릴아마이드 70 중량부, 아크릴아미노메틸프로판설퍼닉에시드 60 중량부, 1-브로모-1-메틸사이클로헥산 50 중량부, 아이소뷰틸사이클로펜탄 40 중량부, 소르비탄스테아레이트 10 중량부, 소르비탄아이소스테아레이트 9 중량부 및 글리세린스테아레이트 8 중량부가 혼합되어 200℃로 가열된 상태에서 20000~23000rpm의 속도로 강하게 교반된 후 상기 교반된 혼합물에 상기 혼합물 100 중량부를 기준으로 물 50 중량부가 20~24시간 동안 서서히 첨가되어 수성 아크릴 도막방수제가 제조되고, 상기 제조된 수성 아크릴 도막방수제에 140g/m2 내지 160g/m2의 두께를 가지는 부직포가 함침되어 도막 방수 시트가 제조된 후, 상기와 같은 지붕 슁글의 날림 방지 및 방수공법이 실시된다.100 parts by weight of diacetone acrylamide was mixed with 70 parts by weight of methylenebisacrylamide, 60 parts by weight of acrylaminomethylpropane sulfone acid, 50 parts by weight of 1-bromo-1-methylcyclohexane, 40 parts by weight of isobutylcyclopentane, 10 parts by weight of sorbitan stearate, 9 parts by weight of sorbitan isostearate and 8 parts by weight of glycerin stearate were mixed with stirring at a speed of 20000 to 23000 rpm while being heated to 200 캜 above was added dropwise a mixture based on the mixture of 100 parts by weight is gradually added during the water 50 parts by weight of 20 ~ 24 hours and produced a water-based acrylic coating film waterproofing agent, to the above prepared water-based acrylic coating repellant 140g / m 2 to 160g / m 2 Waterproof sheet is produced by impregnating a non-woven fabric having a thickness of 10 to 10 mu m, This method is carried out.
다이아세톤아크릴아마이드 100 중량부에 다이아세톤아크릴아마이드 100 중량부를 기준으로 메틸렌비스아크릴아마이드 80 중량부, 아크릴아미노메틸프로판설퍼닉에시드 70 중량부, 1-브로모-1-메틸사이클로헥산 60 중량부, 아이소뷰틸사이클로펜탄 50 중량부, 소르비탄스테아레이트 20 중량부, 소르비탄아이소스테아레이트 10 중량부 및 글리세린스테아레이트 9 중량부가 혼합되어 200℃로 가열된 상태에서 20000~23000rpm의 속도로 강하게 교반된 후 상기 교반된 혼합물에 상기 혼합물 100 중량부를 기준으로 물 60 중량부가 20~24시간 동안 서서히 첨가되어 수성 아크릴 도막방수제가 제조되고, 상기 제조된 수성 아크릴 도막방수제에 140g/m2 내지 160g/m2의 두께를 가지는 부직포가 함침되어 도막 방수 시트가 제조된 후, 상기와 같은 지붕 슁글의 날림 방지 및 방수공법이 실시된다.To 100 parts by weight of diacetone acrylamide were added 80 parts by weight of methylene bisacrylamide, 70 parts by weight of acrylaminomethylpropane sulfone acid, 60 parts by weight of 1-bromo-1-methylcyclohexane, 50 parts by weight of isobutylcyclopentane, 20 parts by weight of sorbitan stearate, 10 parts by weight of sorbitan isostearate and 9 parts by weight of glycerin stearate were mixed with stirring at a speed of 20000 to 23000 rpm while being heated to 200 캜 wherein in the mixture of 100 to a stirred mixture parts by weight basis it is gradually added over the water 60 parts by weight of 20 ~ 24 hours and produced a water-based acrylic coating film waterproofing agent, to the above prepared water-based acrylic coating repellant 140g / m 2 to 160g / m 2 Waterproof sheet is produced by impregnating a non-woven fabric having a thickness of 10 to 10 mu m, This method is carried out.
다이아세톤아크릴아마이드 100 중량부에 다이아세톤아크릴아마이드 100 중량부를 기준으로 메틸렌비스아크릴아마이드 90 중량부, 아크릴아미노메틸프로판설퍼닉에시드 80 중량부, 1-브로모-1-메틸사이클로헥산 70 중량부, 아이소뷰틸사이클로펜탄 60 중량부, 소르비탄스테아레이트 30 중량부, 소르비탄아이소스테아레이트 11 중량부 및 글리세린스테아레이트 10 중량부가 혼합되어 200℃로 가열된 상태에서 20000~23000rpm의 속도로 강하게 교반된 후 상기 교반된 혼합물에 상기 혼합물 100 중량부를 기준으로 물 80 중량부가 20~24시간 동안 서서히 첨가되어 수성 아크릴 도막방수제가 제조되고, 상기 제조된 수성 아크릴 도막방수제에 140g/m2 내지 160g/m2의 두께를 가지는 부직포가 함침되어 도막 방수 시트가 제조된 후, 상기와 같은 지붕 슁글의 날림 방지 및 방수공법이 실시된다.To 100 parts by weight of diacetone acrylamide, 90 parts by weight of methylenebisacrylamide, 80 parts by weight of acrylaminomethylpropane sulfone acid, 70 parts by weight of 1-bromo-1-methylcyclohexane, 60 parts by weight of isobutylcyclopentane, 30 parts by weight of sorbitan stearate, 11 parts by weight of sorbitan isostearate and 10 parts by weight of glycerin stearate were mixed with stirring at a speed of 20000 to 23000 rpm while being heated to 200 캜 wherein in the mixture of 100 to a stirred mixture parts by weight basis it is gradually added over the water 80 parts by weight of 20 ~ 24 hours and produced a water-based acrylic coating film waterproofing agent, to the above prepared water-based acrylic coating repellant 140g / m 2 to 160g / m 2 Waterproof sheet is produced by impregnating a non-woven fabric having a thickness of 10 to 10 mu m, The construction method is implemented.
따라서 본 발명의 실시예에 따른 도막 방수 시트를 이용한 지붕 슁글의 날림 방지 및 방수공법은, 상기 표 1에 나타낸 바와 같이, A사의 제품에 비하여, 부착강도, 굴곡저항성능 및 접합안정성능 등이 현저히 뛰어난 것을 알 수 있다.Therefore, as shown in Table 1, the anti-skid and waterproofing method of the roof shingle using the film waterproof sheet according to the embodiment of the present invention is superior to the product of Company A in adhesion strength, bending resistance performance, You can see what is outstanding.
상술한 본 발명에서는 구체적인 실시예에 관해 설명하였으나, 여러 가지 변형이 본 발명의 범위에서 벗어나지 않고 실시될 수 있다. 따라서 발명의 범위는 설명된 실시예에 의하여 정할 것이 아니고 청구 범위와 청구 범위의 균등한 것에 의해 정해져야 한다. Although the present invention has been described with reference to the specific embodiments, various modifications may be made without departing from the scope of the present invention. Accordingly, the scope of the invention is not to be determined by the embodiments described, but should be determined by equivalents of the claims and the claims.
Claims (3)
상기 제조된 수성 아크릴 도막방수제에 부직포가 함침되어 도막 방수 시트가 제조되는 단계를 포함하는 것을 특징으로 하는 수성 아크릴 도막 방수제를 이용한 시트 제조방법.100 parts by weight of diacetone acrylamide is mixed with 70 to 90 parts by weight of methylene bisacrylamide, 60 to 80 parts by weight of acrylaminomethylpropane sulfone acid, 1-bromo-1-methylcyclohexane 40 to 60 parts by weight of isobutylcyclopentane, 10 to 30 parts by weight of sorbitan stearate, 9 to 11 parts by weight of sorbitan isostearate and 8 to 10 parts by weight of glycerin stearate are mixed at 200 ° C Adding 50 to 80 parts by weight of water based on 100 parts by weight of the mixture to the stirred mixture after stirring in a heated state to produce a waterproof acrylic coating film waterproofing agent;
A method for producing a sheet using a waterproof acrylic coating film waterproofing agent, comprising the steps of: impregnating a nonwoven fabric into the waterproof acrylic coating film waterproofing agent to prepare a waterproof coating film.
140g/m2 내지 160g/m2 정도의 면밀도를 가지는 것을 특징으로 하는 수성 아크릴 도막 방수제를 이용한 시트 제조방법.The nonwoven fabric according to claim 1,
140g / m 2 to 160g / m 2 around a sheet method using a water-based acrylic coating waterproofing agent, characterized in that having a surface density of.
지붕 외벽면 표면에 시공된 슁글판재층의 표면에 전처리 작업이 진행되는 단계와;
상기 슁글판재층의 표면에 상기 수성 아크릴 도막 방수제가 도포 및 시공되어 접착층이 구성되는 단계와;
상기 접착층에 상기 도막 방수 시트가 부착 또는 접착되는 단계를 포함하는 것을 특징으로 하는 지붕 슁글의 날림 방지 및 방수시공공법.A sheet waterproof sheet and a waterproof acrylic coating film waterproofing agent produced by a sheet manufacturing method using the waterproof acrylic waterproofing agent according to claim 1 or 2,
A step of pre-treating the surface of the shingle plate layer formed on the surface of the outer wall surface of the roof;
Applying and coating the waterproof acrylic acrylate coating on the surface of the shingle plate layer to form an adhesive layer;
And a step of adhering or adhering the film waterproof sheet to the adhesive layer.