KR101941262B1 - Self-adhesion type asphalt waterproofing sheet, manufacturing method therof and complex waterproof method using thereof - Google Patents
Self-adhesion type asphalt waterproofing sheet, manufacturing method therof and complex waterproof method using thereof Download PDFInfo
- Publication number
- KR101941262B1 KR101941262B1 KR1020180113592A KR20180113592A KR101941262B1 KR 101941262 B1 KR101941262 B1 KR 101941262B1 KR 1020180113592 A KR1020180113592 A KR 1020180113592A KR 20180113592 A KR20180113592 A KR 20180113592A KR 101941262 B1 KR101941262 B1 KR 101941262B1
- Authority
- KR
- South Korea
- Prior art keywords
- asphalt
- weight
- parts
- self
- mixed
- Prior art date
Abstract
Description
본 발명은 자착식 아스팔트 방수시트, 그 제조방법 및 이를 이용한 복합 방수시공방법에 관한 것으로서, 보다 상세하게는 스트레이트아스팔트와 브로운아스팔트 복합물에 쇼듐라우릴설페이트, 쇼듐스테아레이트, 쇼듐 2-뷰틸아세토아세테이트, 2-뷰틸아세토아세틱에시드, 디하이드록시아세톤포스페이트, 탄산칼슘, 디옥틸프탈레이트, 디뷰틸프탈레이트 등을 혼합하여 아스팔트 컴파운드 조성물을 제조하고 부직포가 일면에 부착된 PET 필름의 타면에 상기 아스팔트 컴파운드 조성물을 도포하여 시공 온도의 영향을 받지 않아 동절기에도 아스팔트나 콘크리트에 부착시 접착 강도가 저하되지 않도록 할 수 있는 노출형 자착식 아스팔트 방수시트, 그 제조방법 및 이를 이용한 복합 방수시공방법에 관한 것이다. The present invention relates to a water-repellent asphalt waterproof sheet, a method for producing the waterproof sheet, and a composite waterproofing method using the same. More particularly, the present invention relates to a waterproof sheet comprising chondrionyl sulfate, , 2-butylacetoacetic acid, dihydroxyacetonephosphate, calcium carbonate, dioctyl phthalate, dibutyl phthalate and the like are mixed to prepare an asphalt compound composition and the asphalt compound composition The present invention relates to an asphalt-type waterproof sheet, and more particularly, to a method for manufacturing an asphalt waterproof sheet, and a composite waterproofing method using the asphalt waterproof sheet.
일반적으로, 다양한 건축물 또는 구조물에는 빗물 또는 지하수가 침투하여 콘크리트 강도의 저하, 온도변화에 의한 물의 체적변화에 따른 공극 균열의 발생, 시간의 경과에 따른 균열의 확대로 인해 그 건축물 또는 구조물의 안전을 저해하거나 그 수명이 단축되는 것을 방지하기 위해 다양한 방수공법이 실행되고 있다.Generally, various buildings or structures are exposed to rainwater or groundwater, resulting in deterioration of concrete strength, occurrence of pore cracks due to changes in water volume due to temperature changes, and expansion of cracks over time. Various waterproofing methods are being implemented to prevent the water from being damaged or its life being shortened.
이와 같은 건축물 또는 구조물에서는 개질 아스팔트, 고무계 등 다양한 재료들이 사용되고 있으며 또한 다양한 분야에서 변형적으로 사용되고 있다. 이와 같이 콘크리트 건축물 또는 구조물에 적용되는 방수재로서 아스팔트 3겹 8층 방수(블로운 아스팔트), 시트식방수재, 클로로프렌 고무계 방수재, 규산 알카리계 액상 방수재(침투식방수재)가 있다.In such buildings or structures, various materials such as modified asphalt and rubber are used, and they are also used in various fields in a variety of fields. As such waterproofing materials applied to concrete structures or structures, there are asphalt three layer 8 layer waterproofing (blown asphalt), sheet type waterproofing material, chloroprene rubber waterproofing material and silicate alkali waterproofing liquid material (infiltration waterproofing material).
한편, 최근에는 적용의 편리성 및 사용의 편의성으로 인해 다양한 시트형 방수재가 널리 사용 및 연구되고 있다. 이와 같은 방수시트는 대부분 자착식으로 형성되어 있어 그 사용의 편리성이 증대되고 있다. 이와 같은 자착식 방수시트의 하나의 종래예가 특허 제10-1116662호에 공지되어 있다. In recent years, various sheet-like waterproofing materials have been widely used and studied due to convenience of application and ease of use. Most of such waterproof sheets are formed by injection molding, and the convenience of use is increased. One conventional example of such a waterproofing sheet is known from Japanese Patent No. 10-1116662.
그 특허 제10-1116662호에 개시된 고분자 합성고무 및 폐플라스틱의 중합과 극성이 부여된 자착식 방수시트는, 저밀도 폴리에틸렌수지(LLDPE) 55중량% ~ 70중량%와, 폐열가소성수지 20중량% ~ 40중량%와, SBS수지(Polystyrene Polybutadiene Polystyrene) 0.5중량% ~ 5중량%로 조성된 열가소성 필름방수층과; 상기 필름방수층 하부에 조성되며, 폐타이어 10중량% ~ 60중량%, 폐플라스틱 10중량% ~ 45중량%, 폐놀류의 산화방지제 0.5중량% ~ 5중량%, 방향족아민류의 노화방지제 0.5중량% ~ 5중량%, 합성고무 10중량% ~ 50중량%, 유기산 0.5중량% ~ 5중량%, 무기산 0.5중량% ~ 5중량%로 중합된 1차 화합물을 마련하고, 상기 1차 화합물 10중량% ~ 30중량%와, 스The polymerized synthetic rubber and the polarized water-impervious waterproofing sheet disclosed in Japanese Patent No. 10-1116662 are prepared by mixing 55% by weight to 70% by weight of a low density polyethylene resin (LLDPE), 20% by weight of a waste thermoplastic resin, A thermoplastic film waterproofing layer composed of 40% by weight of an acrylic resin and 0.5% by weight to 5% by weight of an SBS resin (Polystyrene Polybutadiene Polystyrene); Wherein the antifogging agent is composed of 10 wt% to 60 wt% of waste tire, 10 wt% to 45 wt% of waste plastic, 0.5 wt% to 5 wt% of antioxidant of pulp and paper, 0.5 wt% The first compound is polymerized in an amount of 5 to 5% by weight, synthetic rubber in an amount of 10 to 50% by weight, organic acid in an amount of 0.5 to 5% by weight and inorganic acid in an amount of 0.5 to 5% % By weight,
트레이트 아스팔트 30중량% ~ 70중량%, 불론아스팔트 2중량% ~10중량%, 석유화학수지 3중량% ~ 20중량%, 터펜페놀수지 1중량% ~ 5중량%, 나프텐계 2중량% ~ 20중량%, 파라핀계 1중량% ~ 15중량%, 왁스 1중량% ~ 15중량%, 폴리부텐 1중량% ~ 10중량%, 충진제 3중량% ~ 15중량%, SBS수지(Polystyrene Polybutadiene Polystyrene) 1중량% ~ 10중량%로 조성된 방수점착층과; 상기 방수점착층 하부면에 부착되는 박리지로 구성되어 있다. 30 wt% to 70 wt% of asphalt, 2 wt% to 10 wt% of asphalt, 3 wt% to 20 wt% of petrochemical resin, 1 wt% to 5 wt% of terpene phenol resin, 2 wt% to 20 wt% 1 to 15% by weight of paraffin wax, 1 to 15% by weight of wax, 1 to 10% by weight of polybutene and 3 to 15% by weight of a filler, 1 weight of SBS resin (Polystyrene Polybutadiene Polystyrene) % To 10% by weight of water-repellent adhesive layer; And a release paper adhering to the lower surface of the waterproof adhesive layer.
이 같은 구성의 고분자 합성고무 및 폐플라스틱의 중합과 극성이 부여된 자착식 방수시트는 중합온도, 수지, 투입순서, 투입시간의 제법에 따라 분자량, 연화점, 인장력이 우수한 폴리머를 중합시키고, 이 폴리머를 방수 점착층에 적용될 수 있게 함으로써, 아스팔트와 다른 수지와의 결합력이 증대되고, 피착면(아스팔트 또는 시멘트)에도 부착이 잘될 수 있으며, 점착방수층은, 자착력이 강력하고, 신장률이 뛰어나, 불규칙한 피착면이나 습기가 잔류된 피착면에도 그 부착력이 우수함으로써, 들뜸현상이나 바탕면의 거동에 대한 순응력이 우수하여 탁월한 방수성이보장되는 효과를 제공한다.The polymer synthetic rubber and the waterproofing sheet having polarity imparted with polarity are polymerized with a polymer having excellent molecular weight, softening point and tensile strength according to the production method of the polymerization temperature, the resin, the charging order and the charging time, (Asphalt or cement), the adhesive waterproof layer can be applied to the waterproof adhesive layer, and the bonding strength between the asphalt and the other resin is increased and the adhesive waterproof layer is stronger in self-bonding strength and excellent in elongation, The adhesive force is excellent even on the adherend surface or the adhered surface on which moisture is retained, thereby providing an excellent watertightness due to excellent net stress against lifting and surface behavior.
다른 하나의 종래예로서 특허공개 10-2012-0069189호에 개시된 고무화 아스팔트계 자착식 방수/방근시트는, 아스팔트, 스티렌계 블록 공중합체, 파라핀계 점탄성 오일 및 석유수지 및 폴리부텐을 포함하는 방수층; 및 상기방수층 상에 적층된 고밀도 폴리에틸렌층을 포함하며, 여기에서 상기 방수층은 아스팔트 30 내지 70중량%, 스티렌계 블록 공중합체 1 내지 30중량%, 파라핀계 점탄성 합성오일 0.5 내지 20중량%의 중량비로 구성되어 있다.As another conventional example, the rubberized asphalt-based waterproofing / weatherproof sheet disclosed in the patent publication 10-2012-0069189 includes a waterproof layer containing asphalt, styrenic block copolymer, paraffinic viscoelastic oil and petroleum resin and polybutene ; And a high density polyethylene layer laminated on the waterproof layer, wherein the waterproof layer is composed of 30 to 70% by weight of asphalt, 1 to 30% by weight of a styrenic block copolymer, and 0.5 to 20% by weight of a paraffinic viscoelastic synthetic oil Consists of.
이 같은 구성에 따라 균열 추종성, 저온유연성이 우수하며 콘크리트 구조물의 바탕면이나, 방수시트간의 이음부의 접착방법이 토치 등에 의한 열융착 또는 접착제를 사용하는 접착방법이 아닌 방수재 자체가 보유하고 있는 접척성을 이용하여 부착하는 비융착/비가열형 접착공법으로 기존 시트 방수공법에서 누수하자 빈도가 가장 높은 접합부에 대한 누수 문제를 근본적으로 해결할 수 있는 효과를 제공한다.According to this structure, it is excellent in crack followability and low temperature flexibility, and the bonding method of the joint between the base sheet of the concrete structure and the waterproof sheet is not a bonding method using a heat welding or an adhesive using a torch, , It is possible to fundamentally solve the leakage problem of the joint having the highest frequency of leakage in the existing sheet waterproofing method.
또 다른 종래의 자착식 방수시트가 일본 특개소 제57-98559호, 일본 특개소 제57-139143호, 미국 특허 제4,485,201호, 한국 등록특허 제0332632호, 한국 등록특허 제0388810호, 한국 등록특허 제0569694호, 한국 등록특허 제0701822호, 한국 등록특허 제0671412호, 한국 등록특허 제0726350호, 한국 공개특허 제2009-0090532호, 한국 공개특허 제2009-0056756호에 개시되어 있다.Another conventional self-adhesive waterproof sheet is disclosed in Japanese Patent Laid-Open Nos. 57-98559, 57-139143, 4,485,201, Korean Patent No. 0332632, Korean Patent No. 0388810, Korean Registered Patent Korean Patent No. 0701822, Korean Patent No. 0671412, Korean Patent No. 0726350, Korean Patent Publication No. 2009-0090532, Korean Patent Publication No. 2009-0056756.
그러나 상기와 같은 각각의 자착식 방수시트들은 다소의 문제점이 초래되는 것으로 나타났다. 먼저, 중량이 과도하여 설치 및 사용이 용이하지 않을 뿐 아니라 건축물 또는 구조물에 안전성을 저하시키는 문제점이 있다.However, each of the self-adhesive waterproof sheets described above has been found to cause some problems. First, it is not easy to install and use heavy weight, and there is a problem that safety is lowered in a building or a structure.
그리고 방수시트의 표면이 거칠고 매끄럽지 못하여 설치후 시간이 경과함에 따라 해충, 곤충 등이 기생하거나 군집하여 그 방수시트를 손상시킬 수 있으며, 또한 낮은 햇빛 반사율로 인해 지붕이나 옥상에 시공하는 경우 열기가 흡수되어 적용성이 저하되는 문제점이 있다.And the surface of the waterproof sheet is not smooth and smooth, so that insects and insects may parasitize or collapse due to passage of time after the installation, and the waterproof sheet may be damaged. Also, when the roof is installed on the roof or roof due to low sunlight reflectance, So that the applicability is deteriorated.
또한, 강도가 상대적으로 취약하여 수명성 및 유지성이 저하되는 문제점이 있다.In addition, there is a problem that strength and maintainability are deteriorated due to relatively low strength.
따라서 본 발명의 목적은 스트레이트아스팔트와 브로운아스팔트 복합물에 쇼듐라우릴설페이트, 쇼듐스테아레이트, 쇼듐 2-뷰틸아세토아세테이트, 2-뷰틸아세토아세틱에시드, 디하이드록시아세톤포스페이트, 탄산칼슘, 디옥틸프탈레이트, 디뷰틸프탈레이트 등을 혼합하여 아스팔트 컴파운드 조성물을 제조하고 부직포가 일면에 부착된 PET 필름의 타면에 상기 아스팔트 컴파운드 조성물을 도포하여 시공 온도의 영향을 받지 않아 동절기에도 아스팔트나 콘크리트에 부착시 접착 강도가 저하되지 않도록 할 수 있는 노출형 자착식 아스팔트 방수시트, 그 제조방법 및 이를 이용한 복합 방수시공방법을 제공하는 것이다.Accordingly, an object of the present invention is to provide a process for producing a mixture of straight asphalt and bronze asphalt complex, which comprises adding to a mixture of chondroitin sulfate, sodium dodecyl sulfate, sodium dodecyl phthalate, sodium dodecyl phthalate, dihydroxyacetone phosphate, And dibutyl phthalate to prepare an asphalt compound composition. The asphalt compound composition is applied to the other side of the PET film adhered to one side of the nonwoven fabric and is not affected by the application temperature. Therefore, when adhered to asphalt or concrete in winter, And to provide a method of manufacturing the same and a composite waterproofing method using the asphaltic waterproof sheet.
한편, 본 발명의 목적은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.Meanwhile, the object of the present invention is not limited to the above-mentioned objects, and other objects not mentioned can be clearly understood by those skilled in the art from the following description.
본 발명에 의하면, 부직포가 일면에 부착된 PET 필름의 타면에 아스팔트 컴파운드 조성물이 도포되어 구성되며, 아스팔트 컴파운드 조성물은, 스트레이트아스팔트와 브로운아스팔트가 혼합된 아스팔트 복합물에 쇼듐라우릴설페이트, 쇼듐스테아레이트, 쇼듐 2-뷰틸아세토아세테이트, 2-뷰틸아세토아세틱에시드, 디하이드록시아세톤포스페이트, 탄산칼슘, 디옥틸프탈레이트 및 디뷰틸프탈레이트가 혼합되어 구성되는 자착식 아스팔트 방수시트가 제공된다.According to the present invention, an asphalt compound composition is formed by applying an asphalt compound composition on the other surface of a PET film having a nonwoven fabric attached on one surface thereof. The asphalt compound composition is prepared by mixing together asphalt complexes in which straight asphalt and bronze asphalt are mixed with chondriauryl sulfate, There is provided a water-insoluble asphalt waterproof sheet comprising a mixture of sodium hydroxide, potassium hydroxide, sodium hydroxide, sodium hydroxide, sodium hydroxide, sodium hydroxide, sodium hydroxide, sodium hydroxide,
또한, 본 발명에 의하면, 스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에 상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 60-80 중량부, 쇼듐스테아레이트 50-70 중량부, 쇼듐 2-뷰틸아세토아세테이트 40-60 중량부, 2-뷰틸아세토아세틱에시드 30-50 중량부, 디하이드록시아세톤포스페이트 20-40 중량부, 탄산칼슘 10-30 중량부, 디옥틸프탈레이트 5-15 중량부 및 디뷰틸프탈레이트 3-5 중량부가 혼합된 아스팔트 컴파운드 조성물이 제조되는 단계와; 상기 아스팔트 컴파운드 조성물이 부직포가 일면에 부착된 PET 필름의 타면에 도포되는 단계를 포함하는 자착식 아스팔트 방수시트의 제조방법이 제공된다.According to the present invention, the asphalt composite in which the straight asphalt and the bronze asphalt are mixed in a volume ratio of 7: 3 is mixed with 60 to 80 parts by weight of chondroitin sulfate, 50 to 70 parts by weight of sodium stearate 40 to 60 parts by weight of sodium 2-hydroxyacetoacetate, 30 to 50 parts by weight of 2-hydroxyacetoacetic acid, 20 to 40 parts by weight of dihydroxyacetone phosphate, 10 to 30 parts by weight of calcium carbonate, -15 parts by weight of dibutyl phthalate and 3-5 parts by weight of dibutyl phthalate are prepared; Wherein the asphalt compound composition is applied to the other side of the PET film attached to one surface of the nonwoven fabric.
또한, 본 발명에 의하면, 상기 자착식 아스팔트 방수시트 제조방법에 의해 제조된 자착식 아스팔트 방수시트를 포함하고, 콘크리트층 표면에 전처리 작업이 진행되는 단계와; 상기 자착식 아스팔트 방수시트가 상기 콘크리트층 표면에 부착되는 단계와; 상기 자착식 아스팔트 방수시트의 상부에 도막방수제가 도포되는 단계를 포함하는 자착식 아스팔트 방수시트를 이용한 복합 방수시공방법이 제공된다.According to another aspect of the present invention, there is provided a method for manufacturing a waterproofing asphalt waterproofing sheet, comprising the steps of: pre-treating a surface of a concrete layer, Attaching the self-adhesive asphalt waterproof sheet to the surface of the concrete layer; And a coating waterproofing agent is applied on the top of the self-adhering asphalt waterproofing sheet.
따라서 본 발명에 의하면, 스트레이트아스팔트와 브로운아스팔트 복합물에 쇼듐라우릴설페이트, 쇼듐스테아레이트, 쇼듐 2-뷰틸아세토아세테이트, 2-뷰틸아세토아세틱에시드, 디하이드록시아세톤포스페이트, 탄산칼슘, 디옥틸프탈레이트, 디뷰틸프탈레이트 등을 혼합하여 아스팔트 컴파운드 조성물을 제조하고 부직포가 일면에 부착된 PET 필름의 타면에 상기 아스팔트 컴파운드 조성물을 도포하여 시공 온도의 영향을 받지 않아 동절기에도 아스팔트나 콘크리트에 부착시 접착 강도가 저하되지 않도록 할 수 있는 노출형 자착식 아스팔트 방수시트, 그 제조방법 및 이를 이용한 복합 방수시공방법을 제공할 수 있다.Therefore, according to the present invention, it is possible to provide an asphalt-based asphalt-based asphalt-containing asphalt composition, which is characterized in that it contains chondroitin sulfate, And dibutyl phthalate to prepare an asphalt compound composition. The asphalt compound composition is applied to the other side of the PET film adhered to one side of the nonwoven fabric and is not affected by the application temperature. Therefore, when adhered to asphalt or concrete in winter, The present invention can provide an exposed type self-adhering asphalt waterproof sheet which can be prevented from deteriorating, and a composite waterproofing method using the same.
한편, 본 발명의 효과는 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않은 다른 효과들은 청구범위의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.On the other hand, the effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned can be clearly understood by those skilled in the art from the description of the claims.
이하, 본 발명의 실시예에 대하여 상세히 설명하기로 한다. Hereinafter, embodiments of the present invention will be described in detail.
먼저, 본 발명의 실시예에 따른 자착식 아스팔트 방수시트는, PET 필름의 일면에 부직포가 부착되고 타면에 아스팔트 컴파운드 조성물이 도포되어 구성된다.First, a self-adhering asphalt waterproof sheet according to an embodiment of the present invention comprises a non-woven fabric on one side of a PET film and an asphalt compound composition on the other side.
여기서, 아스팔트 컴파운드 조성물은, 스트레이트아스팔트와 브로운아스팔트가 혼합된 아스팔트 복합물에 쇼듐라우릴설페이트, 쇼듐스테아레이트, 쇼듐 2-뷰틸아세토아세테이트, 2-뷰틸아세토아세틱에시드, 디하이드록시아세톤포스페이트, 탄산칼슘, 디옥틸프탈레이트 및 디뷰틸프탈레이트가 혼합되어 구성되며, 보다 바람직하게는, 스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에 상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 60-80 중량부, 쇼듐스테아레이트 50-70 중량부, 쇼듐 2-뷰틸아세토아세테이트 40-60 중량부, 2-뷰틸아세토아세틱에시드 30-50 중량부, 디하이드록시아세톤포스페이트 20-40 중량부, 탄산칼슘 10-30 중량부, 디옥틸프탈레이트 5-15 중량부 및 디뷰틸프탈레이트 3-5 중량부가 혼합되어 제조된다.Here, the asphalt compound composition is a mixture of asphalt complexes in which a mixture of straight asphalt and brown asphalt is admixed with at least one selected from the group consisting of chondria lauryl sulfate, sodium stearate, sodium 2-butylacetoacetate, 2-butylacetoacetic acid, dihydroxyacetone phosphate, Calcium, dioctyl phthalate and dibutyl phthalate are mixed. More preferably, the asphalt composite in which the straight asphalt and the bronze asphalt are mixed in a volume ratio of 7: 3 is mixed with 100 parts by weight of the asphalt composite, 60-80 parts by weight, 60-70 parts by weight of sodium dodecyl acetoacetate, 30-50 parts by weight of 2-butylacetoacetic acid, 20-40 parts by weight of dihydroxyacetone phosphate, 10-30 parts by weight of calcium carbonate, 5-15 parts by weight of dioctyl phthalate and 3-5 parts by weight of dibutyl phthalate It is prepared.
또한, 본 발명의 실시예에 따른 자착식 아스팔트 방수시트의 제조방법은, 스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에 상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 60-80 중량부, 쇼듐스테아레이트 50-70 중량부, 쇼듐 2-뷰틸아세토아세테이트 40-60 중량부, 2-뷰틸아세토아세틱에시드 30-50 중량부, 디하이드록시아세톤포스페이트 20-40 중량부, 탄산칼슘 10-30 중량부, 디옥틸프탈레이트 5-15 중량부 및 디뷰틸프탈레이트 3-5 중량부가 혼합된 아스팔트 컴파운드 조성물이 제조되는 단계와, 상기 아스팔트 컴파운드 조성물이 부직포가 일면에 부착된 PET 필름의 타면에 도포되는 단계를 포함한다.The method for manufacturing a self-adhering asphalt waterproof sheet according to an embodiment of the present invention is characterized in that asphalt composite in which the ratio of straight asphalt and blown asphalt is mixed at a volume ratio of 7: 3 is added to 100 parts by weight of the asphalt composite, 40 to 60 parts by weight of sodium 2-butylacetoacetate, 30 to 50 parts by weight of 2-butylacetoacetic acid, 20 to 40 parts by weight of dihydroxyacetone phosphate, 10 to 30 parts by weight of calcium carbonate, 5 to 15 parts by weight of dioctyl phthalate and 3 to 5 parts by weight of dibutyl phthalate are mixed, and the asphalt compound composition is mixed with the PET film On the other surface.
여기서, 상기 아스팔트 컴파운드 조성물은, 상기 부직포가 일면에 부착된 PET 필름의 타면에 접착 방수층을 제공하여 PET 필름의 하면이 콘크리트층의 상층 표면에 구성시 접착과 도막 기능이 향상되도록 한다.Here, the asphalt compound composition provides an adhesive waterproof layer on the other side of the PET film attached to one surface of the nonwoven fabric, so that the lower surface of the PET film is improved in adhesion and film function when it is formed on the upper surface of the concrete layer.
상기 스트레이트아스팔트는, 방수성능을 제공하고 일예로, KS F 4052 방수공사용 아스팔트가 사용될 수 있으며, 그 중 3종 또는 5종이 사용될 수 있는데 본 발명에서는 침입도가 80~100 mm 인 5종을 사용하는 것이 바람직하며, 3종의 경우 아스팔트에 레진이나 오일함량이 높아 내한성은 우수하나 점착 성능이 5종에 비해 높아 시트 제조시 시트간 접합이 이루어질 수 있다. 이에, 상대적으로 점착성이 낮은 5종을 사용하는 것이 바람직하다.The straight asphalt provides waterproof performance. For example, KS F 4052 asphalt for waterproofing construction can be used. Three or five types of asphalt can be used. In the present invention, five types of penetration depths of 80 to 100 mm are used And 3 kinds of asphalt are high in resin and oil content and excellent in cold resistance but higher than 5 kinds of adhesive performance, so that sheet-to-sheet bonding can be made in sheet production. Therefore, it is preferable to use five species having relatively low adhesiveness.
여기서, 상기 스트레이트아스팔트는, 브로운아스팔트와 혼합시 7의 부피비를 가지는데, 7 부피비를 초과하는 경우에는 점착 성능이 너무 커지게 되어 콘크리트층에 작업을 위해 이면필름이 제거되는 경우 PET 필름에 도포된 아스팔트 컴파운드 조성물간 접합이 이루어져 작업 효율이 저하되는 문제점이 있고, 7 부피비를 미만하는 경우에는 오히려 콘크리트층과의 접착성과 방수 기능이 저하되는 문제점이 있다. In the case where the asphalt is mixed with the bronze asphalt, the straight asphalt has a volume ratio of 7. When the volume ratio exceeds 7, the adhesive property becomes too large, and when the backing film is removed for work on the concrete layer, There is a problem in that work efficiency is lowered due to bonding between the asphalt compound compositions. When the volume ratio is less than 7, adhesion and adhesion to concrete layer deteriorate.
상기 브로운아스팔트는, 석유 아스팔트에 공기를 취입하여 산화중합시켜 만든 탄성력이 큰 아스팔트로 만든 것으로서, 스트레이트 아스팔트에 비해 아스팔텐(asphaltene)의 함유량이 적고 페트롤렌(petrolene)의 함유량이 적어 내열성 및 가소성이 크며 내충격성이 강하고, 감온성이 적은 특징을 갖는다. 또한, 탄성, 내충격성, 방수성, 방습성, 방청성, 방수성 및 전기 절연성이 우수하고, 변성이 적은 성질을 가지고 있다. The above-mentioned bronze asphalt is made of asphalt having high elasticity, which is formed by oxidizing and polymerizing air through petroleum asphalt. It has less asphaltene content than petroleum asphalt and less petroleene content than straight asphalt so that heat resistance and plasticity Has a high impact resistance and low temperature sensitivity. Also, it has excellent properties of elasticity, impact resistance, waterproofness, moisture-proofing property, rust-proofing property, waterproof property and electric insulation property, and has little modification property.
여기서, 상기 브로운아스팔트는, 스트레이트아스팔트와 혼합시 3의 부피비를 가지는데, 3 부피비를 초과하는 경우에는 건조가 잘 되지 않아 시공후 특히 하절기에 태양열에 녹아 끈적거리는 현상과 동절기에 층분리 및 균열이 발생하는 문제점이 있고, 3 부피비를 미만하는 경우에는 방수성 및 접착성이 크게 저하되어 시공성 및 작업성이 저하되는 문제점이 있다. The above mentioned asphalt has a volume ratio of 3 when it is mixed with straight asphalt. When it exceeds 3 volume ratio, the dry asphalt is not well dried, so that it becomes sticky after the construction, especially in summer, And when the volume ratio is less than 3, the water resistance and adhesiveness are significantly lowered, and the workability and workability are deteriorated.
이에, 상기 아스팔트 복합물은, 스트레이트아스팔트와 브로운아스팔트가 상기와 같은 한정된 부피비를 가지는 것을 통하여, 향상된 탄성, 내충격성, 방수성, 접착성, 절연성, 시공성 및 작업성 등의 효과가 제공되도록 하는 것이 바람직하다.It is desirable that the above-mentioned asphalt composite is provided with the effects of improved elasticity, impact resistance, waterproof property, adhesiveness, insulation property, workability, and workability through the above-mentioned limited volume ratio of straight asphalt and blown asphalt Do.
상기 쇼듐라우릴설페이트는, 아스팔트 컴파운드 조성물의 제조시, 상기 첨가물들의 교반성능을 향상과 접착력을 향상시키는 계면활성 및 침투 기능을 제공하여 시공시 방수성과 내마모성을 제공하여 투수비와 흡수비를 낮추고 신정성과 점착성 등을 제공한다.Saidium lauryl sulfate provides a water-repellent and abrasion-resistant property during the production of the asphalt compound composition by providing a surfactant and penetration function that improves the agitation performance of the additives and improves the adhesion, thereby lowering the permeability and absorption ratio, And tackiness.
여기서, 상기 쇼듐라이릴설페이트는, 상기 아스팔트 복합물 100 중량부를 기준으로 60-80 중량부가 첨가되는데, 80 중량부 보다 많이 첨가되는 경우에는 높은 내화학성으로 인하여 조성물들의 혼합률이 저하되고, 60 중량부 보다 적게 첨가되는 경우에는 접착 및 코팅 기능이 저하되어 내구성까지 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다. When the amount of the sulfated lysyl sulfate is more than 80 parts by weight, the mixing ratio of the compositions is lowered due to the high chemical resistance, and when 60 parts by weight In the case where the amount of addition is less, there is a problem that adhesion and coating function are lowered and durability is lowered. Therefore, it is preferable to have a limited weight portion as described above.
상기 쇼듐스테아레이트는, 아스팔트 컴파운드 조성물의 제조시, 상기 첨가물의 교반 효율이 향상되도록 한다.The above-mentioned schodium stearate enables the stirring efficiency of the additive to be improved in the production of the asphalt compound composition.
여기서, 상기 쇼듐스테아레이트는, 상기 아스팔트 복합물 100 중량부를 기준으로 50-70 중량부가 첨가되는데, 70 중량부 보다 많이 첨가되는 경우에는 혼합물들의 분산시 입자 크기의 분포도가 커지게 되어 오히려 교반성이 저하되고, 50 중량부보다 적게 첨가되는 경우에는 분산시 입자 크기의 분포도가 작아지게 되어 교반성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.When the amount of the additive is more than 70 parts by weight, the distribution of the particle size during the dispersion of the mixture increases, and the degree of agglomeration decreases. If less than 50 parts by weight is added, there is a problem that the degree of dispersion of the particle size during dispersion tends to be small and the degree of agglomeration is deteriorated.
상기 쇼듐 2-뷰틸아세토아세테이트는, 아스팔트 컴파운드 조성물의 제조시, 조성물의 점도 기능을 조절하는 점도조절 및 결합제이다.The above-mentioned isothiocyanatoacetic acid is a viscosity modifier and a binder for controlling the viscosity function of the composition in the production of an asphalt compound composition.
여기서, 상기 쇼듐 2-뷰틸아세토아세테이트는, 상기 아스팔트 복합물 100 중량부를 기준으로 40-60 중량부가 첨가되는데, 60 중량부 보다 많이 첨가되면 강한 결합력으로 인하여 점도가 증가되어 오히려 교반 혼합이 저하되고, 40 중량부 보다 적게 첨가되면 결합력이 발휘되지 못하여 전반적인 방수성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The addition of more than 60 parts by weight of the above-mentioned amorphous 2-butylacetoacetate, on the basis of 100 parts by weight of the asphalt composite, increases the viscosity due to the strong binding force, If it is added in an amount less than 1 part by weight, a bonding force can not be exerted and the overall waterproofing property is deteriorated.
상기 2-뷰틸아세토아세틱에시드는, 상기 PET 필름과 콘크리트층과의 접착 강도를 향상시키는 기능을 제공한다.The 2-butyl acetoacetic acid provides a function of improving the adhesion strength between the PET film and the concrete layer.
여기서, 상기 2-뷰틸아세토아세틱에시드는, 상기 아스팔트 복합물 100 중량부를 기준으로 30-50 중량부가 첨가되는데, 50 중량부 보다 많이 첨가되면 PET 필름과 콘크리트층 표면과의 접착력이 증대되지만 다른 혼합물들과의 교반성이 저하되고, 30 중량부 보다 적게 첨가되면 PET 필름과 콘크리트층 표면과의 접착력이 저하되어 PET 필름의 시공 온도의 영향을 받지 않도록 하는 접착 기능이 제공되지 않는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.The amount of 2-butylacetoacetic acid is 30-50 parts by weight based on 100 parts by weight of the asphalt composite. When the amount is more than 50 parts by weight, adhesion between the PET film and the surface of the concrete layer is increased. However, And if it is added in an amount of less than 30 parts by weight, the adhesion between the PET film and the surface of the concrete layer is lowered and the adhesive function of not being affected by the temperature of the PET film is not provided. It is preferable to have the same limited weight portion.
상기 디하이드록시아세톤포스페이트는, 아스팔트 컴파운드 조성물의 제조시, 상기 혼합물들의 교반시 교반성이 향상되도록 계면 활성 기능을 제공한다. The dihydroxyacetone phosphate provides a surfactant function in the preparation of the asphalt compound composition such that the agitation of the mixtures improves agitation.
여기서, 상기 디하이드록시아세톤포스페이트는, 상기 아스팔트 복합물 100 중량부를 기준으로 20-40 중량부가 첨가되는데, 40 중량부 보다 많이 첨가되면 상기 혼합물들의 결합도가 오히려 저하되어 접착 기능이 저하되고, 20 중량부 보다 적게 첨가되면 상기 혼합물들의 교반성이 크게 저하되어 접착 기능과 도막 기능이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.When the amount of the dihydroxyacetone phosphate is more than 40 parts by weight, the degree of bonding of the mixture is lowered to lower the adhesive function, and when 20 parts by weight of the dihydroxyacetone phosphate is added, , There is a problem that the agglomeration of the above-mentioned mixtures is significantly lowered, and the adhesive function and the coating film function are deteriorated. Therefore, it is preferable to have the above limited weight portion.
상기 탄산칼슘은, 아스팔트 컴파운드 조성물을 통한 방수층 또는 접착층의 두께를 확보하기 위한 것으로, 인장강도와 신장률 등의 특성을 제공한다.The calcium carbonate is used for securing the thickness of the waterproof layer or the adhesive layer through the asphalt compound composition and provides properties such as tensile strength and elongation.
여기서, 탄산칼슘은, 상기 아스팔트 복합물 100 중량부를 기준으로 10-30 중량부가 첨가되는데, 30 중량부 보다 많이 첨가되면 다른 첨가물과의 균일한 혼합이 이루어지지 않아 물성이 저하되는 문제점이 있고, 10 중량부 보다 적게 첨가되면 도막의 두께 확보가 어려워 흡착성, 인장강도 및 신장률의 특성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.Here, the calcium carbonate is added in an amount of 10-30 parts by weight based on 100 parts by weight of the asphalt composite. If it is added in an amount of more than 30 parts by weight, the calcium carbonate is not uniformly mixed with other additives, , There is a problem that it is difficult to secure the thickness of the coating film and the characteristics of the adsorption property, the tensile strength and the elongation percentage are lowered. Therefore, it is preferable to have the above limited weight portion.
상기 디옥틸프탈레이트는, 아스팔트 컴파운드 조성물을 통한 방수층 또는 접착층의 연성 및 안정성을 향상시키는 가소제 기능을 제공한다.The dioctyl phthalate provides a plasticizer function that improves the ductility and stability of the waterproof layer or adhesive layer through the asphalt compound composition.
여기서, 상기 디옥틸프탈레이트는, 상기 아스팔트 복합물 100 중량부를 기준으로 5-15 중량부가 첨가되는데, 15 중량부 보다 많이 첨가되면 상기 혼합물들의 연성과 안정성이 오히려 저하되어 접착 기능이 저하되고, 5 중량부 보다 적게 첨가되면 상기 혼합물들의 교반성이 크게 저하되어 접착 기능과 도막 기능이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.If the amount of the dioctyl phthalate added is more than 15 parts by weight, the ductility and stability of the mixture deteriorate to lower the adhesive function, and when the amount of the dioctyl phthalate is less than 5 parts by weight When the amount is less than the above range, the degree of crosslinking of the above-mentioned mixtures is greatly lowered, and the adhesive function and the film function are deteriorated.
상기 디뷰틸프탈레이트는, 아스팔트 컴파운드 조성물의 혼합시 유화제 기능을 제공하여 방수층 또는 도막층의 압축 강도를 높이는 효과를 제공한다.The dibutyl phthalate provides an emulsifier function during mixing of the asphalt compound composition to provide an effect of increasing the compressive strength of the waterproof layer or the coating layer.
여기서, 디뷰틸프탈레이트는, 상기 아스팔트 복합물 100 중량부를 기준으로 3-5 중량부가 첨가되는데, 5 중량부 보다 많이 첨가되면 상기 혼합물들의 결합도가 너무 커지게 되어 오히려 방수층의 외력에 따른 압축 강도가 저하되고, 3 중량부 보다 적게 첨가되면 상기 혼합물들의 결합도가 저하되어 방수층의 발수성이 저하되는 문제점이 있으므로, 상기와 같은 한정된 중량부를 가지는 것이 좋다.If more than 5 parts by weight of dibutyl phthalate is added, the degree of coupling of the mixtures becomes too large, so that the compressive strength of the waterproof layer is lowered due to the external force of the waterproof layer. If less than 3 parts by weight is added, there is a problem that the water repellency of the waterproof layer is deteriorated because the degree of bonding of the mixtures is lowered.
또한, 본 발명의 실시예에 따른 자착식 아스팔트 방수시트를 이용한 방수시공방법에 대해 설명하면 다음과 같다.The waterproofing method using the self-adhering asphalt waterproof sheet according to the embodiment of the present invention will be described as follows.
먼저, 콘크리트층 표면에 청소 및 평탄화 작업 등과 같은 전처리 작업이 진행된다.First, the surface of the concrete layer is subjected to pre-treatment such as cleaning and planarization.
이후, 상기와 같은 제조방법에 의해 제조된 자착식 아스팔트 방수시트가 콘크리트층 표면에 접착된다.Thereafter, the self-adhering asphalt waterproof sheet produced by the above-described manufacturing method is adhered to the surface of the concrete layer.
이후, 상기 자착식 아스팔트 방수시트의 상부 즉, 방수시트의 부직포에 우레탄 도막방수제가 도포된다.Thereafter, the urethane coating waterproofing agent is applied to the upper portion of the above-mentioned water-repellent asphalt waterproof sheet, that is, the nonwoven fabric of the waterproof sheet.
여기서, 상기 우레탄 도막방수제는, 공지의 구성을 가질 수 있으므로, 상세한 설명은 생략하기로 한다.Here, the urethane coating water repellent agent may have a known constitution, and a detailed description thereof will be omitted.
이하, 본 발명의 실시예에 따른 자착식 아스팔트 방수시트의 효과를 구체적인 실시예를 통해 설명하기로 한다.Hereinafter, the effects of the self-adhering asphalt waterproof sheet according to the embodiment of the present invention will be described with reference to specific embodiments.
이하 실시예는, 본 발명에 따른 자착식 아스팔트 방수시트를 이용하여 우레탄 도막방수제와의 복합 시공 성능 등을 평가하기 위한 것으로, 인장강도, 신장률, 인열성능, 굴곡저항성능, 접합안정성능, 부착성능, 내움푹패임성능 및 내피로성능 등의 시험이 실시되었으며, 이를 시제품 A사와 비교하여 표 1에 그 측정 결과를 비교하여 나타내었다. The following examples are for evaluating the combined construction performance with a waterproofing agent for urethane coatings using the self-adhering asphalt waterproof sheet according to the present invention, and the tensile strength, elongation, tearing performance, flexural resistance performance, , Internal denting performance, and endothelial performance. The results are compared with those of the prototype A, and the results are shown in Table 1.
스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에 상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 80 중량부, 쇼듐스테아레이트 70 중량부, 쇼듐 2-뷰틸아세토아세테이트 60 중량부, 2-뷰틸아세토아세틱에시드 50 중량부, 디하이드록시아세톤포스페이트 40 중량부, 탄산칼슘 30 중량부, 디옥틸프탈레이트 15 중량부 및 디뷰틸프탈레이트 5 중량부가 혼합된 아스팔트 컴파운드 조성물이 제조되고, 상기 아스팔트 컴파운드 조성물이 부직포가 일면에 부착된 PET 필름의 타면에 도포되어 자착식 아스팔트 방수시트가 제도된 후, 상기와 같은 우레탄 도막방수제와의 복합 방수 공법이 실시된다. 80 parts by weight of chondroitin sulfate, 70 parts by weight of sodium stearate, and 60 parts by weight of sodium 2-butylacetoacetate, based on 100 parts by weight of the asphalt composite, were mixed in an asphalt composite in which the straight asphalt and the brown asphalt were mixed in a volume ratio of 7: , 50 parts by weight of 2-butylacetoacetic acid, 40 parts by weight of dihydroxyacetone phosphate, 30 parts by weight of calcium carbonate, 15 parts by weight of dioctyl phthalate and 5 parts by weight of dibutyl phthalate were mixed to prepare an asphalt compound composition The asphalt compound composition is coated on the other side of the PET film attached to one side of the nonwoven fabric to form a self-adhesive asphalt waterproof sheet, followed by a combined waterproofing method with the urethane film waterproofing agent as described above.
스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에 상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 70 중량부, 쇼듐스테아레이트 60 중량부, 쇼듐 2-뷰틸아세토아세테이트 50 중량부, 2-뷰틸아세토아세틱에시드 40 중량부, 디하이드록시아세톤포스페이트 30 중량부, 탄산칼슘 20 중량부, 디옥틸프탈레이트 10 중량부 및 디뷰틸프탈레이트 4 중량부가 혼합된 아스팔트 컴파운드 조성물이 제조되고, 상기 아스팔트 컴파운드 조성물이 부직포가 일면에 부착된 PET 필름의 타면에 도포되어 자착식 아스팔트 방수시트가 제도된 후, 상기와 같은 우레탄 도막방수제와의 복합 방수 공법이 실시된다. 70 parts by weight of chondriauryl sulfate, 60 parts by weight of sodium stearate and 50 parts by weight of sodium 2-butylacetoacetate were mixed with 100 parts by weight of the asphalt composite in an amount of 7: 3 by volume of straight asphalt and 7: , 40 parts by weight of 2-butyl acetoacetic acid, 30 parts by weight of dihydroxyacetone phosphate, 20 parts by weight of calcium carbonate, 10 parts by weight of dioctyl phthalate and 4 parts by weight of dibutyl phthalate were mixed, The asphalt compound composition is coated on the other side of the PET film attached to one side of the nonwoven fabric to form a self-adhesive asphalt waterproof sheet, followed by a combined waterproofing method with the urethane film waterproofing agent as described above.
스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에 상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 60 중량부, 쇼듐스테아레이트 50 중량부, 쇼듐 2-뷰틸아세토아세테이트 40 중량부, 2-뷰틸아세토아세틱에시드 30 중량부, 디하이드록시아세톤포스페이트 20 중량부, 탄산칼슘 10 중량부, 디옥틸프탈레이트 5 중량부 및 디뷰틸프탈레이트 3 중량부가 혼합된 아스팔트 컴파운드 조성물이 제조되고, 상기 아스팔트 컴파운드 조성물이 부직포가 일면에 부착된 PET 필름의 타면에 도포되어 자착식 아스팔트 방수시트가 제도된 후, 상기와 같은 우레탄 도막방수제와의 복합 방수 공법이 실시된다. 60 parts by weight of chondriauryl sulfate, 50 parts by weight of sodium stearate and 40 parts by weight of sodium 2-butylacetoacetate were mixed with 100 parts by weight of the asphalt composite in a ratio of 7: 3 by volume of straight asphalt and 7: , 30 parts by weight of 2-butylacetoacetic acid, 20 parts by weight of dihydroxyacetone phosphate, 10 parts by weight of calcium carbonate, 5 parts by weight of dioctyl phthalate and 3 parts by weight of dibutyl phthalate were mixed to prepare an asphalt compound composition The asphalt compound composition is coated on the other side of the PET film attached to one side of the nonwoven fabric to form a self-adhesive asphalt waterproof sheet, followed by a combined waterproofing method with the urethane film waterproofing agent as described above.
따라서 본 발명의 실시예에 따른 자착식 아스팔트 방수시트를 이용한 복합 방수 공법은, 상기 표 1에 나타낸 바와 같이, A사의 제품의 경우 10℃와 25℃에서의 부착성능이 차이가 많이 발생되는 것에 비해 본 발명의 실시예들은 유사하게 측정되어 시공 온도 조건에서의 영향이 거의 발생되지 않음을 알 수 있고, 그 외의 측정항목에서도 A사의 제품에 비해 우수한 특성을 가지는 것을 알 수 있다.Therefore, in the combined waterproofing method using the self-adhesive asphalt waterproof sheet according to the embodiment of the present invention, as shown in Table 1, the adhesion performance at 10 ° C and 25 ° C is significantly different for the products of Company A It can be seen that the embodiments of the present invention are measured similarly and almost no influence is exerted under the construction temperature condition.
상술한 본 발명에서는 구체적인 실시예에 관해 설명하였으나, 여러 가지 변형이 본 발명의 범위에서 벗어나지 않고 실시될 수 있다. 따라서 발명의 범위는 설명된 실시예에 의하여 정할 것이 아니고 청구 범위와 청구 범위의 균등한 것에 의해 정해져야 한다. Although the present invention has been described with reference to the specific embodiments, various modifications may be made without departing from the scope of the present invention. Accordingly, the scope of the invention is not to be determined by the embodiments described, but should be determined by equivalents of the claims and the claims.
Claims (4)
아스팔트 컴파운드 조성물은,
스트레이트아스팔트와 브로운아스팔트가 혼합된 아스팔트 복합물에 쇼듐라우릴설페이트, 쇼듐스테아레이트, 쇼듐 2-뷰틸아세토아세테이트, 2-뷰틸아세토아세틱에시드, 디하이드록시아세톤포스페이트, 탄산칼슘, 디옥틸프탈레이트 및 디뷰틸프탈레이트가 혼합되어 구성되는 것을 특징으로 하는 시공 온도의 영향을 받지 않는 자착식 노출형 아스팔트 방수시트.The asphalt composite composition is applied to the other surface of the PET film having the nonwoven fabric bonded on one surface thereof,
The asphalt compound composition,
Asphalt complexes comprising a mixture of straight asphalt and brown asphalt may be mixed with at least one selected from the group consisting of chondria lauryl sulfate, sodium stearate, sodium 2-butylacetoacetate, 2-butylacetoacetic acid, dihydroxyacetone phosphate, calcium carbonate, dioctyl phthalate and di Wherein the waterproof sheet is formed of a mixture of water and butyl phthalate.
스트레이트아스팔트와 브로운아스팔트가 7:3의 부피비로 혼합된 아스팔트 복합물에,
상기 아스팔트 복합물 100 중량부를 기준으로 쇼듐라우릴설페이트 60-80 중량부, 쇼듐스테아레이트 50-70 중량부, 쇼듐 2-뷰틸아세토아세테이트 40-60 중량부, 2-뷰틸아세토아세틱에시드 30-50 중량부, 디하이드록시아세톤포스페이트 20-40 중량부, 탄산칼슘 10-30 중량부, 디옥틸프탈레이트 5-15 중량부 및 디뷰틸프탈레이트 3-5 중량부가 혼합되는 것을 특징으로 하는 시공 온도의 영향을 받지 않는 자착식 노출형 아스팔트 방수시트.The asphalt composite composition of claim 1,
In an asphalt composite having straight asphalt and brown asphalt mixed at a volume ratio of 7: 3,
60 to 80 parts by weight of chondroitin sulfate, 50 to 70 parts by weight of sodium stearate, 40 to 60 parts by weight of sodium 2-butylacetoacetate, and 30 to 50 parts by weight of 2-butylacetoacetic acid based on 100 parts by weight of the asphalt composite 20 to 40 parts by weight of dihydroxyacetone phosphate, 10 to 30 parts by weight of calcium carbonate, 5 to 15 parts by weight of dioctyl phthalate and 3-5 parts by weight of dibutyl phthalate. Non-fraying exposed asphalt waterproof sheet.
상기 아스팔트 컴파운드 조성물이 부직포가 일면에 부착된 PET 필름의 타면에 도포되는 단계를 포함하는 것을 특징으로 하는 시공 온도의 영향을 받지 않는 자착식 노출형 아스팔트 방수시트의 제조방법. In an asphalt composite in which the straight asphalt and the bronze asphalt are mixed in a volume ratio of 7: 3, 60 to 80 parts by weight of chondroitin sulfate, 50 to 70 parts by weight of sodium stearate, 30-50 parts by weight of 2-butylacetoacetic acid, 20-40 parts by weight of dihydroxyacetone phosphate, 10-30 parts by weight of calcium carbonate, 5-15 parts by weight of dioctyl phthalate, Preparing an asphalt compound composition mixed with 3-5 parts by weight of phthalate;
Wherein the asphalt compound composition is applied to the other side of the PET film attached to one surface of the nonwoven fabric.
콘크리트층 표면에 전처리 작업이 진행되는 단계와;
상기 자착식 아스팔트 방수시트가 상기 콘크리트층 표면에 부착되는 단계와;
상기 자착식 노출형 아스팔트 방수시트의 상부에 도막방수제가 도포되는 단계를 포함하는 것을 특징으로 하는 시공 온도의 영향을 받지 않는 자착식 노출형 아스팔트 방수시트를 이용한 복합 방수시공방법.A waterproof sheet as claimed in any one of claims 1 to 3,
A step of pre-treating the surface of the concrete layer;
Attaching the self-adhesive asphalt waterproof sheet to the surface of the concrete layer;
And applying a coating waterproofing agent to the top of the self-extinguishing type asphalt waterproofing sheet, wherein the waterproofing agent is applied to an upper portion of the self-supporting type asphalt waterproofing sheet.