KR101946065B1 - Double-sided adhesive tape having improved reworkability - Google Patents

Double-sided adhesive tape having improved reworkability Download PDF

Info

Publication number
KR101946065B1
KR101946065B1 KR1020110080096A KR20110080096A KR101946065B1 KR 101946065 B1 KR101946065 B1 KR 101946065B1 KR 1020110080096 A KR1020110080096 A KR 1020110080096A KR 20110080096 A KR20110080096 A KR 20110080096A KR 101946065 B1 KR101946065 B1 KR 101946065B1
Authority
KR
South Korea
Prior art keywords
adhesive layer
double
adhesive tape
sheet
adhesive
Prior art date
Application number
KR1020110080096A
Other languages
Korean (ko)
Other versions
KR20120089990A (en
Inventor
원종섭
Original Assignee
쓰리엠 이노베이티브 프로퍼티즈 캄파니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 쓰리엠 이노베이티브 프로퍼티즈 캄파니 filed Critical 쓰리엠 이노베이티브 프로퍼티즈 캄파니
Priority to PCT/US2011/067537 priority Critical patent/WO2012092342A2/en
Priority to CN201180058676.0A priority patent/CN103249793B/en
Priority to JP2013547639A priority patent/JP6005060B2/en
Priority to TW100149831A priority patent/TWI532813B/en
Publication of KR20120089990A publication Critical patent/KR20120089990A/en
Application granted granted Critical
Publication of KR101946065B1 publication Critical patent/KR101946065B1/en

Abstract

본 발명은 접착면에 대하여 수평으로 작용하는 힘에 의하여 용이하게 박리되어 재작업성이 우수한 양면 점착 테이프에 대한 것으로서, 다층으로 이루어진 점착시트의 층들 중 어느 한 층이 용이하게 박리되어 용이하게 제거할 수 있는 양면 점착 테이프에 대한 것이다. The present invention relates to a double-sided pressure-sensitive adhesive tape which is easily peeled off by a force acting horizontally on an adhesive surface and is excellent in reworkability, and is characterized in that any one of the layers of the pressure- For a double-sided adhesive tape.

Description

재작업성이 향상된 양면 점착 테이프{DOUBLE-SIDED ADHESIVE TAPE HAVING IMPROVED REWORKABILITY}{DOUBLE-SIDED ADHESIVE TAPE HAVING IMPROVED REWORKABILITY}

본 발명은 재작업성이 향상된 양면 점착 테이프에 대한 것으로서, 구체적으로는, 접착면에 수평한 방향으로 힘을 가할 경우 상기 양면 점착 테이프를 이루는 층 중 하나의 층이 용이하게 박리되어, 재작업성이 향상된 양면 점착 테이프에 대한 것이다.The present invention relates to a double-sided pressure-sensitive adhesive tape having improved reworkability. More specifically, when a force is applied to a bonding surface in a horizontal direction, one layer of the double-sided pressure-sensitive adhesive tape is easily peeled off, This is for an improved double-sided adhesive tape.

전자기기 등의 제품의 제조공정에서는 접착을 위하여 다양한 종류의 점착제 또는 점착 테이프를 사용한다. 이러한 제품의 제조공정에서 불량이 발생하는 경우, 그 제품을 폐기하기도 하지만 그 제품을 구성요소별로 분리하여 재작업을 하기도 한다.In the production process of products such as electronic devices, various kinds of adhesive or adhesive tape are used for adhesion. If a defect occurs in the manufacturing process of such a product, the product may be discarded, but the product may be divided into components and reworked.

특히 최근 전자기기 등이 고기능화, 고급화 되면서, 상기 전자기기를 구성하는 각각의 구성 부품들도 고기능화, 고급화되고 그에 따라 가격도 고가가 되고 있는 실정이다. 이러한 전자제품의 제조공정에서 불량이 발생할 경우, 그 제품을 그대로 폐기한다면 자원소모와 환경오염의 문제뿐만 아니라 경제적 손실도 크게 된다.Particularly, as electronic devices and the like have become more sophisticated and advanced in recent years, the respective constituent parts constituting the above-described electronic devices are becoming more sophisticated and more advanced, and accordingly, their prices are becoming higher. If a defect occurs in the manufacturing process of such an electronic product, if the product is discarded as it is, economic loss as well as resource consumption and environmental pollution become serious.

이러한 고가의 전자기기 구성부품의 일례로서 터치 패널이 있다. 상기 터치패널(touch panel)은 디스플레이 패널의 표면에 장착되어 사용자의 손가락, 터치 펜 등의 물리적 접촉을 전기적 신호로 변환하여 출력하는 장치로서, 액정표시장치(liquid crystal display), 플라즈마 디스플레이 패널(plasma display panel), EL(electro-luminescence) 소자, 유기발광소자 등에 응용되고 있다.As an example of such expensive electronic component parts, there is a touch panel. The touch panel is mounted on a surface of a display panel and converts physical contact of a user's finger, touch pen, etc. into an electrical signal and outputs the electrical signal. The touch panel includes a liquid crystal display, a plasma display panel display panels, EL (electro-luminescence) devices, organic light emitting devices, and the like.

이러한 터치 패널은 구성이 정교하고 가격 또한 고가이다. 그런데 상기 터치 패널을 디스플레이 패널에 부착하거나 또는 터치 패드에 보호용 커버 윈도우(cover window)를 부착하는 작업공정에서 먼지 등에 의한 오염이 발생하거나 또는 배치위치 오차 등의 불량이 발생하는 경우가 생긴다. 상기와 같은 불량이 발생하였다고 하여 불량이 발생한 제품을 폐기한다면 이는 경제적으로 큰 손실이다. 따라서, 경제적 손실을 줄이기 위해서는 불량이 생기면 상기 터치패널을 디스플레이 패널 또는 커버 윈도우와 분리하여 다시 사용할 수 있어야 한다. 상기와 같은 재사용의 필요성은 터치 패널뿐만 아니라 다른 부품에서도 마찬가지이다.Such a touch panel is elaborate in configuration and is expensive. However, in the work process of attaching the touch panel to the display panel or attaching a protective window to the touch pad, contamination due to dust or the like may occur, or defects such as placement position errors may occur. If the defective product is discarded due to the defective product, it is economically disadvantageous. Therefore, in order to reduce the economic loss, when the failure occurs, the touch panel must be separated from the display panel or the cover window and used again. The necessity of such reuse is the same not only in the touch panel but also in other parts.

그런데, 상기 제품의 제조과정에서 터치패널은 상대재인 디스플레이 패널이나 커버 윈도우와 매우 강고하게 접착되어 있기 때문에, 상기 터치패널이 잘 분리되지 않거나, 분리되는 과정에서 상기 터치패널이 손상될 수 있다. 만약, 터치 패널이 분리되지 않거나, 분리과정에서 손상되게 되면 고가의 성능에 이상이 없었던 고가의 터치패널을 사용하지 못하게 되는 손실을 입게 된다. 한편, 손상 없이 터치 패널이 분리된다고 하더라도 분리된 터치 패널에 접착제의 잔존물이 존재하게 되면 분리된 터치 패널을 재사용하기 어려워진다.However, since the touch panel is strongly adhered to the display panel or the cover window, which is a counterpart, during the manufacturing process of the product, the touch panel may not be well separated or may be damaged during the separation process. If the touch panel is not detached or damaged during the detachment process, the expensive touch panel, which has no abnormality in performance, is damaged. On the other hand, even if the touch panel is detached without being damaged, it is difficult to reuse the detached touch panel if residual adhesive of the adhesive is present on the separated touch panel.

이와 같이, 전자기기와 그 구성 부품들이 더욱 정교해지고 고가화되고 있는 시점에서, 제조단가의 절약과 작업성 측면에서 볼 때, 조립과정에서 비록 불량이 발생하더라도 구성 부품만은 안전하게 재사용하여 재작업할 수 있도록 하는 것이 매우 절실하게 요구되고 있다.As described above, when electronic devices and their constituent parts become more sophisticated and higher in price, in view of the reduction in manufacturing cost and workability, only the component parts can be safely reused and reworked It is very urgently required.

본 발명은 구성 부품을 서로 안정적으로 부착시킬 수 있으면서도 또한 필요한 경우에는 용이하게 박리되어 재작업성을 향상시킬 수 있는 점착 테이프를 제공하는 것을 목적으로 한다.It is an object of the present invention to provide a pressure-sensitive adhesive tape capable of stably attaching component parts to each other and, when necessary, peeling off easily to improve reworkability.

본 발명은 또한, 다층으로 이루어진 점착 테이프에서 특정의 층이 용이하게 박리될 수 있도록 하여, 상기 점착 테이프를 이용하여 부품을 조립하는 과정에서 불량이 발생하더라도 상기 부품을 서로 용이하게 분리할 수 있도록 하는 점착 테이프를 제공하는 것을 목적으로 한다.The present invention also provides a pressure sensitive adhesive tape that allows a specific layer to be readily peeled off from a multi-layer adhesive tape so that the components can be easily separated from each other even if a failure occurs during assembly of the component using the adhesive tape And to provide an adhesive tape.

본 발명은 또한 상기 점착 테이프를 이용하여 제조된 디스플레이 장치를 제공하는 것을 목적으로 한다.Another object of the present invention is to provide a display device manufactured using the adhesive tape.

본 발명은 필름형태의 시트; 상기 시트의 일면에 배치된 제 1 점착층; 및 상기 시트의 타면에 배치된 제 2 점착층을 포함하는 양면 점착 테이프를 제공한다.The present invention relates to a sheet in the form of a film; A first adhesive layer disposed on one side of the sheet; And a second adhesive layer disposed on the other side of the sheet.

상기 양면 점착 테이프에서 상기 제 2 점착층의 전단강도(Shear Strength)는, 상기 양면 점착 테이프를 이용하여 SUS(스테인리스 스틸) 패널에 알루미늄 스트립을 부착하고 60℃의 온도에서 cross-head 속도가 10 mm/min인 조건일 때 0.05 내지 16 Kg/in2의 범위이다. 상기 양면 점착 테이프의 접착면에 대하여 수평이지만 방향이 서로 상반되는 힘을 각각 SUS(스테인리스 스틸) 패널과 알루미늄 스트립에 가하면서 응력(stress)과 변형율(strain)을 측정하여, 이때 발생하는 최대 응력을 전단강도(shear strength)라 한다(도 7 및 도 8 참조).In the double-sided adhesive tape, the shear strength of the second adhesive layer was measured by attaching an aluminum strip to a stainless steel (SUS) panel using the double-faced adhesive tape and measuring the cross-head speed at 10 mm / min in the range of 0.05 to 16 Kg / in 2 when the condition. Stress and strain are measured while applying a force, which is horizontal but opposite in direction to the adhesive surface of the double-faced pressure-sensitive adhesive tape, to the SUS (stainless steel) panel and the aluminum strip, Shear strength "(see Figs. 7 and 8).

상기 제 2 점착층의 전단강도가 0.05Kg/in2 보다 작아지게 되면 사용 중 충격 등에 의하여 제 2 점착층이 박리될 우려가 있어 사용상 불편이 생길 수 있다. 한편, 상기 제 2 점착층의 전단강도가 16 Kg/in2 이하라면 박리성이 뛰어나 충분한 재작업성을 가질 수 있지만, 16 Kg/in2 보다 크게 되면 박리가 쉽지않아 재작업이 용이하지 않게 된다. 이에 제 2 점착층의 전단강도를 상기와 같이 한정한다. Wherein the shear strength of the second adhesive layer is 0.05 kg / in 2 The second adhesive layer may peel off due to impact or the like during use, which may cause inconveniences in use. On the other hand, when the shear strength of the second adhesive layer is 16 Kg / in 2 The peelability is excellent and sufficient reworkability can be obtained. However, if it is larger than 16 Kg / in 2 , peeling is not easy and reworking is not easy. The shear strength of the second adhesive layer is limited as described above.

본 발명의 일례에 따르면 선택성을 높이기 위하여 상기 전단강도를 보다 한정하여, 상기 설명한 조건에서 0.08 내지 10 Kg/in2로 할 수 있다. 전단강도가 10 Kg/in2 이하라면 재작업성이 보다 더 용이할 것이다. 보다 바람직하게는 0.08 내지 4 Kg/in2 범위일 수 있다. According to an embodiment of the present invention, the shear strength may be further limited to 0.08 to 10 Kg / in 2 under the above-described conditions in order to increase the selectivity. If the shear strength is less than 10 Kg / in 2, reworkability will be easier. And more preferably 0.08 to 4 Kg / in 2 .

본 발명의 일례에 따르면, 상기 제 1 점착층의 전단강도는 상기 제 2 점착층의 전단강도보다 크다.According to an embodiment of the present invention, the shear strength of the first adhesive layer is larger than the shear strength of the second adhesive layer.

본 발명의 다른 일례에 따르면, 재작업을 용이하게 하기 위하여 상기 제 2 점착층은, 60℃의 온도에서 4.5 in2의 면적에 1Kg의 하중이 인가될 때의 분리시간이 20초 이상이고, 3Kg의 하중이 인가될 때의 분리시간이 600분 이하일 수 있으며, 바람직하게는 1Kg의 하중이 인가될 때의 분리시간이 30초 이상이고, 3Kg의 하중이 인가될 때의 분리시간이 300분 이하가 되도록 조정할 수 있다.According to another embodiment of the present invention, in order to facilitate rework, the second adhesive layer has a separation time of 20 seconds or more when a load of 1 kg is applied to an area of 4.5 in 2 at a temperature of 60 ° C, The separation time when a load of 1 kg is applied is 30 seconds or more and the separation time when a load of 3 Kg is applied is 300 minutes or less .

분리시간은 도 9에서 보는 바와 같이 측정할 수 있다. 도 9에서 보는 바와 같이, 본 발명에 따른 양면 점착 테이프를 이용하여 PMMA/PC 플레이트를 SUS(스테인레스 스틸) 패널에 부착한 후 상기 PMMA/PC 플레이트에 1Kg 이상의 하중을 인가하여 상기 양면 점착 테이프에 의하여 부착되었던 PMMA/PC 플레이트와 SUS 패널이 분리되는 시간을 측정한다.The separation time can be measured as shown in FIG. As shown in FIG. 9, a PMMA / PC plate was attached to a stainless steel (SUS) panel using a double-faced adhesive tape according to the present invention, and a load of 1 kg or more was applied to the PMMA / Measure the time at which the attached PMMA / PC plate and the SUS panel are separated.

상기 제2 점착층의 분리시간이 전술한 범위에 해당되는 경우, 사용 중 충격 등에 의하여 제 2 점착층이 박리될 가능성이 없어 사용이 더 편리하며, 재작업이 용이하다.When the separation time of the second adhesive layer falls within the above-mentioned range, there is no possibility that the second adhesive layer peels off due to impact or the like during use, so that the use is more convenient and rework is easy.

이때 선택성을 높이기 위하여 60℃의 온도에서 4.5 in2의 면적에 1Kg의 하중이 인가될 때의 분리시간이 30초 이상이고, 3Kg의 하중이 인가될 때의 분리시간이 300분 이하가 되도록 조정할 수 있다. 제2점착층의 분리시간이 상기 설명된 범위에 해당되는 경우 재작업이 보다 용이할 것이다.In order to increase the selectivity, it is possible to adjust the separation time when the load of 1 kg is applied to the area of 4.5 in 2 at the temperature of 60 ° C. to be 30 seconds or more, and the separation time when the load of 3 Kg is applied to be 300 minutes or less have. If the separation time of the second adhesive layer falls within the range described above, reworking will be easier.

본 발명의 일례에 따르면 상기 제 2 점착층은 점착성 고분자에 의하여 형성될 수 있다. 제 2 점착층을 형성하여 상기와 같은 전단강도를 갖게 되거나 또는 상기와 같은 분리시간을 가질 수 있게 된다면 상기 제 2 점착층을 형성하는 고분자의 종류나 분자량 등은 특별히 한정되지 않는다. 예를 들어 분자량 10,000 내지 300,000 정도의 고분자를 사용할 수도 있고, 그 이상 또는 그 이하의 분자량을 갖는 고분자를 사용할 수도 있을 것이다. 상기 제 2 점착층을 형성하기 위한 물질로서 필요에 따라서 상대적으로 저분자량의 점착성 고분자를 사용할 수 있고, 상대적으로 고분자량의 점착성 고분자를 사용할 수도 있는데, 이는 사용자의 선택에 따라 달라질 것이다.According to an embodiment of the present invention, the second adhesive layer may be formed of a sticky polymer. The type and molecular weight of the polymer forming the second adhesive layer are not particularly limited as long as the second adhesive layer has the shear strength as described above or can have the separation time as described above. For example, a polymer having a molecular weight of about 10,000 to 300,000 may be used, or a polymer having a molecular weight of more than or equal to that may be used. As a material for forming the second adhesive layer, a relatively low molecular weight adhesive polymer may be used as needed, and a relatively high molecular weight adhesive polymer may be used, which will vary depending on the user's selection.

본 발명에 의한 양면 점착 테이프를 사용하는 작업공정에서 재작업이 필요한 경우, 접착면에 대하여 수평방향으로 상반되는 힘을 작용할 경우 제 2 점착층이 박리되어 본 발명에 의한 양면 점착 테이프를 매개로 서로 부착되어 있던 부품들이 용이하게 분리될 수 있다. 그에 따라, 재작업성을 높일 수 있다.When rework is required in a work process using the double-sided adhesive tape according to the present invention, when a force opposing to the adhesive surface in a horizontal direction acts on the second adhesive layer, the second adhesive layer peels off, The attached parts can be easily separated. Accordingly, reworkability can be improved.

본 발명의 일례에 따르면, 상기 필름형태의 시트는 투명한 재료에 의하여 제조되는데, 아크릴계 수지, 폴리에스테르 수지, 폴리카보네이트 수지, 노르보넨계 수지, 올레핀 중합체 및 TAC (triacetyl cellulose)로 이루어진 군에서 선택된 재료에 의하여 만들어질 수 있다. 본 발명의 일례에 따르면, 특히 폴리에스테르 수지의 일종으로서 광투과율이 높은 폴리에틸렌 테레프탈레이트(PET)를 적절하게 사용할 수 있다.According to one example of the present invention, the sheet in the form of a film is made of a transparent material, and is made of a material selected from the group consisting of an acrylic resin, a polyester resin, a polycarbonate resin, a norbornene resin, an olefin polymer and TAC (triacetyl cellulose) Lt; / RTI > According to one embodiment of the present invention, polyethylene terephthalate (PET) having a high light transmittance can be suitably used as a kind of polyester resin in particular.

본 발명의 일례에 따르면, 상기 필름형태의 시트의 두께는 5 내지 약 100㎛ 정도로 조정할 수 있다. 필름형태의 시트의 두께가 상기와 같을 경우, 소형 및 대형 디스플레이 전자기기에 용이하게 적용될 수 있다. According to an example of the present invention, the thickness of the sheet in film form can be adjusted to about 5 to about 100 mu m. When the thickness of the film-like sheet is the same as above, it can be easily applied to small and large display electronic devices.

본 발명의 일례에 따르면 상기 제 1 점착층(110)와 제 2 점착층(120)의 두께는 각각 5 내지 약 500㎛ 범위 내로 조정할 수 있다. 상기 정도의 두께라면, 부착시키고자 하는 대상물품, 예컨대 전자부품을 점착시키기에 충분한 점착력을 나타낼 수 있을 것이다. According to an embodiment of the present invention, the thicknesses of the first adhesive layer 110 and the second adhesive layer 120 can be adjusted within a range of 5 to 500 mu m, respectively. If the thickness is as large as the above, it may exhibit a sufficient adhesive force for adhering an object to be attached, for example, an electronic component.

본 발명의 일례에 따르면 상기 제 2 점착층은 점착성 고분자 조성물에 의하여 형성될 수 있다. 상기 제 2 점착층을 형성하기 위한 점착성 고분자 조성물은 모노머 및 중합개시제를 포함하며, 여기에 더하여 연쇄전달제(chain transfer agent), 중합억제제, 및 저분자량 첨가제(수평균 분자량이 10,000 이하) 및 경화제 중 적어도 하나를 추가로 포함할 수 있다. 이때 점착제 고분자 조성물의 추가 성분으로 포함되는 경화제의 함량은, 상기 경화제의 종류에 따라 상이할 수 있다. According to an embodiment of the present invention, the second adhesive layer may be formed by the adhesive polymer composition. The adhesive polymer composition for forming the second adhesive layer includes a monomer and a polymerization initiator, and in addition, a chain transfer agent, a polymerization inhibitor, and a low molecular weight additive (number average molecular weight of 10,000 or less) At least one of < / RTI > The content of the curing agent contained as an additional component of the pressure-sensitive adhesive polymer composition may vary depending on the kind of the curing agent.

본 발명의 다른 일례에 따르면, 상기 제 2 점착층에서 필름형태의 시트가 배치된 면의 반대면에는 보조필름 시트가 추가로 배치될 수 있는데, 상기 보조필름 시트에는 제 3 점착층이 배치된다. 여기서, 상기 제 3 점착층의 전단강도는 상기 제 2 점착층의 전단강도보다 크도록 조정한다.According to another embodiment of the present invention, an auxiliary film sheet may be additionally disposed on a surface opposite to a surface on which the film-shaped sheet is disposed in the second adhesive layer, and a third adhesive layer is disposed on the auxiliary film sheet. Here, the shear strength of the third adhesive layer is adjusted to be larger than the shear strength of the second adhesive layer.

본 발명에 의한 양면 점착 테이프는 광 투과성이 우수한 투명한 테이프이다. 본 발명의 일례에 따르면 상기 양면 점착 테이프의 광투과율은 90% 이상인 것이 바람직하다.The double-sided pressure-sensitive adhesive tape according to the present invention is a transparent tape excellent in light transmittance. According to one embodiment of the present invention, the double-sided pressure-sensitive adhesive tape preferably has a light transmittance of 90% or more.

본 발명은 또한, 상기 양면 점착테이프를 사용하는 디스플레이 장치를 제공한다. 본 발명의 일례에 따른 디스플레이 장치는, 디스플레이 패널; 상기 디스플레이 패널의 표시면에 배치된 양면 점착 테이프; 및 상기 양면 점착 테이프에 배치된 투명 플레이트;를 포함한다. 여기서 상기 양면 점착 테이프는 본 발명에 따른 재작업성이 우수한 양면 점착 테이프이다. The present invention also provides a display device using the double-sided pressure-sensitive adhesive tape. A display device according to an example of the present invention includes: a display panel; A double-sided adhesive tape disposed on a display surface of the display panel; And a transparent plate disposed on the double-sided adhesive tape. Here, the double-sided pressure-sensitive adhesive tape is a double-sided pressure-sensitive adhesive tape excellent in reworkability according to the present invention.

본 발명의 일례에 따르면, 상기 투명 플레이트는 전자기기의 커버 윈도우 일 수 있으며, 또한 상기 투명 플레이트가 터치패널인 것도 가능하다. 본 발명의 일례에 따르면, 상기 투명 플레이트는 디스플레이 패널에 부착된 터치패널의 전면에 배치되는 커버 윈도우일 수 있다. According to an embodiment of the present invention, the transparent plate may be a cover window of an electronic device, and the transparent plate may be a touch panel. According to an example of the present invention, the transparent plate may be a cover window disposed on the front surface of the touch panel attached to the display panel.

본 발명에 따른 양면 점착 테이프는 피착제와의 젖음성이 좋아 양호한 접착력을 보이기 때문에 통상의 사용상태에서는 벗겨질 염려가 없지만, 접착면에 대하여 평행한 방향으로 미는 힘을 작용시키면 제 2 점착층이 피착제로부터 용이하게 분리될 수 있다. 또한 분리된 후의 점착층 물질 잔사의 제거가 용이하여 상기 양면 점착 테이를 사용하는 경우 재작업성이 우수하다.Since the double-sided pressure-sensitive adhesive tape according to the present invention has good wettability with the adherend and exhibits a good adhesive force, there is no fear that the double-sided pressure-sensitive adhesive tape will peel off under normal use. However, if a pressing force is applied in a direction parallel to the adhesive surface, It can be easily separated from zero. In addition, when the double-sided pressure-sensitive adhesive tape is used, the re-workability is excellent because it is easy to remove the adhesive layer material residue after separation.

본 발명에 의한 양면 점착 테이프는 투명하기 때문에 디스플레이 장치의 표시면에 유용하게 적용될 수 있는데, 특히 고가의 터치패널이나 커버 윈도우와 같은 투명 플레이트를 디스플레이 패널의 표시부에 접착 고정시키는 데에 유용하게 사용될 수 있다. 상기 양면 점착 테이프을 이용하여 투명 플레이트를 디스플레이 패널의 표시부에 접착시키는 경우, 상기 양면 점착 테이프의 제 2 점착층이 박리가 용이하여 재작업성이 우수하기 때문에 제조과정에서 불량이 발생하더라도 고가의 구성 부품을 재사용할 수 있게 된다.The double-sided pressure-sensitive adhesive tape according to the present invention can be advantageously applied to a display surface of a display device because it is transparent. Especially, it can be used to fix a transparent plate such as an expensive touch panel or a cover window to a display portion of a display panel have. When the transparent plate is adhered to the display portion of the display panel using the double-sided adhesive tape, since the second adhesive layer of the double-sided adhesive tape is easily peeled off and the reworkability is excellent, Can be reused.

도 1은 본 발명의 일례에 따른 양면 점착 테이프(100)의 구조를 도식적으로 표현한 것이다.
도 2는 도 1에 의한 양면 점착 테이프(100)를 이용하여 투명 플레이트(310)를 디스플레이 패널(320)의 표면에 부착시킨 상태를 도식적으로 표현한 것이다.
도 3는 도 2에서 사용된 양면 점착 테이프(100)에 대하여 접착면에 수평방향으로 힘을 작용시켜 제 2 점착층을 박리시킨 모습을 보여주는 도면이다.
도 4은 본 발명의 다른 일례에 따른 양면 점착 테이프(200)의 구조를 도식적으로 표현한 것이다.
도 5는 도 4에 의한 양면 점착 테이프(200)를 이용하여 투명 플레이트(310)를 디스플레이 패널(320)의 표면에 부착시킨 상태를 도식적으로 표현한 것이다.
도 6은 도 5에서 사용된 양면 점착 테이프(200)에 대하여 접착면에 수평방향으로 힘을 작용시켜 제 2 점착층을 박리시키는 모습을 보여주는 도면이다.
도 7은 전단 응력을 측정하기 위한 구성을 보여주는 도면이다.
도 8은 전단강도 측정을 위하여 도 7에 의한 알루미늄 스트립과 SUS패널에 수평방향의 힘을 인가하면서 측정한 응력-변형율(stress-strain) 그래프를 보여주는 도면이다.
도 9는 분리시간을 측정하기 위한 구성을 보여주는 도면이다.1 is a schematic representation of the structure of a double-faced pressure-sensitive adhesive tape 100 according to an example of the present invention.
FIG. 2 is a schematic representation of a state in which the transparent plate 310 is attached to the surface of the display panel 320 using the double-sided adhesive tape 100 shown in FIG.
3 is a view showing a state in which the second adhesive layer is peeled off by applying a force to the adhesive surface in the horizontal direction with respect to the double-sided adhesive tape 100 used in Fig.
4 is a schematic representation of the structure of the double-faced pressure-sensitive adhesive tape 200 according to another example of the present invention.
5 is a schematic representation of a state in which the transparent plate 310 is attached to the surface of the display panel 320 using the double-sided adhesive tape 200 according to FIG.
6 is a view showing a state in which the second adhesive layer is peeled off by applying a force to the adhesive surface in the horizontal direction with respect to the double-sided adhesive tape 200 used in Fig.
7 is a view showing a configuration for measuring shear stress.
8 is a graph showing a stress-strain graph measured while applying a horizontal force to the aluminum strip and the SUS panel according to FIG. 7 for measuring the shear strength.
9 is a view showing a configuration for measuring a separation time.

이하, 도면을 참고하여 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail with reference to the drawings.

도 1은 본 발명의 일례에 따른 양면 점착 테이프(100)의 구조를 보여준다.1 shows a structure of a double-faced pressure-sensitive adhesive tape 100 according to an example of the present invention.

본 발명의 일례에 의한 양면 점착 테이프(100)는 필름형태의 시트(101), 상기 시트의 일면에 배치된 제 1 점착층(110), 상기 시트의 타면에 배치된 제 2 점착층(120)을 포함한다.A double-sided adhesive tape 100 according to an exemplary embodiment of the present invention includes a sheet 101 in the form of a film, a first adhesive layer 110 disposed on one side of the sheet, a second adhesive layer 120 disposed on the other side of the sheet, .

상기 필름형태의 시트(101)로서 필름형태의 플라스틱 재료가 사용될 수 있다. 이러한 플라스틱 재료의 예로서, 폴리메틸 메타크릴레이트(PMMA)와 같은 아크릴계 수지, 폴리에틸렌 테레프탈레이트(PET)와 같은 폴리에스테르, 폴리카보네이트, 노르보넨계 수지, 올레핀 중합체, TAC(triacetyl cellulose) 등이 있다. 상기 플라스틱 재료는 단독으로 또는 2종 이상을 조합하여 사용할 수 있다. As the film-like sheet 101, a plastic material in the form of a film can be used. Examples of such plastic materials include acrylic resins such as polymethyl methacrylate (PMMA), polyesters such as polyethylene terephthalate (PET), polycarbonate, norbornene resins, olefin polymers, and triacetyl cellulose (TAC) . These plastic materials may be used alone or in combination of two or more.

이러한 플라스틱 필름 중에서도, 쉽게 구할 수 있으면서도 고투명성을 갖는 PET 필름 등을 용이하게 사용할 수 있다. Among these plastic films, a PET film or the like which is easily obtainable and has high transparency can be easily used.

본 발명의 일례에 따른 상기 필름형태의 시트(101)는 광투과율이 90% 이상인 것을 사용할 수 있다.The sheet 101 in the form of a film according to an example of the present invention may have a light transmittance of 90% or more.

상기 필름형태의 시트(101)의 두께는 특별히 한정되지 않는다. 본 발명의 일례에 따르면, 상기 필름형태의 시트(101)의 두께는 약 5 ㎛ 내지 약 100 ㎛의 범위로 선택될 수 있으며, 필요에 따라서는 10 ㎛ 내지 50 ㎛의 범위로 할 수도 있다.The thickness of the film sheet 101 is not particularly limited. According to one example of the present invention, the thickness of the film-like sheet 101 may be selected in the range of about 5 占 퐉 to about 100 占 퐉, and may be in the range of 10 占 퐉 to 50 占 퐉, if necessary.

상기 필름형태의 시트(101)의 일면에는 제 1 점착층이 배치된다. 본 발명의 일례에 따르면 상기 제 1 점착층(110)은 점착성 고분자에 의하여 형성될 수 있다.A first adhesive layer is disposed on one side of the sheet 101 in the form of a film. According to an embodiment of the present invention, the first adhesive layer 110 may be formed of a sticky polymer.

상기 제 1 점착층(110)을 형성하기 위한 점착성 고분자는 일반적으로 디스플레이용 부품의 부착에 통상적으로 사용되는 점착성 고분자를 사용할 수 있는데, 스플레이의 시인성을 저하시키지 않을 정도의 투명성을 가져야 한다. 이러한 점착성 고분자로서 예를 들어, 아크릴계 점착성 고분자, 실리콘계 점착성 고분자, 폴리에스테르계 점착성 고분자, 고무계 점착성 고분자 또는 폴리우레탄계 점착성 고분자 등의 공지 또는 관용의 감압성 점착성 고분자가 있다. 상기 점착성 고분자는 단독으로 또는 2종 이상 조합하여 사용할 수도 있다. 제 1 점착층(110) 형성을 위한 점착성 고분자로서, 예를 들어 아크릴계 고분자를 사용할 수 있는데, C1 -18의 (메타)아크릴레이트가 모노머 성분 총량에 대하여 50 중량% 이상인 것을 사용할 수 있다. As the adhesive polymer for forming the first adhesive layer 110, a sticky polymer commonly used for attaching display components may be used, and transparency should be such that the visibility of the splay is not deteriorated. As such a sticking polymer, there is known or commonly used pressure-sensitive adhesive polymer such as acrylic adhesive polymer, silicone adhesive polymer, polyester adhesive polymer, rubber adhesive polymer or polyurethane adhesive polymer. These adhesive polymers may be used alone or in combination of two or more. As the adhesive polymer for forming the first adhesive layer 110, for example, an acrylic polymer may be used, and (meth) acrylate of C 1 -18 may be used in an amount of 50% by weight or more based on the total amount of the monomer components.

본 발명의 일례에 따르면 제 1 점착층(110)은 현재 시판되어 있는 통상의 광학용 점착제(Optical Clean Adhesive; OCA)에 의하여 형성될 수 있다. 상기 제 1 점착층(110)은 투명해야 하는데 광투과율이 90% 이상 정도가 되고, 투명플레이트(310)를 디스플레이 기판(320)의 표시부에 안정적으로 부착시킬 수 있을 정도의 접착력만 가지고 있다면 접착력이나 그 종류에 특별한 제한이 있는 것은 아니다.According to an embodiment of the present invention, the first adhesive layer 110 may be formed by a commercially available optical clean adhesive (OCA). The first adhesive layer 110 should be transparent and have a light transmittance of about 90% or more. If the transparent plate 310 has an adhesive strength sufficient to stably attach the transparent plate 310 to the display portion of the display substrate 320, There is no particular restriction on the kind.

상기 제 1 점착층을 형성하기 위한 점착성 고분자와 제 2 점착층을 형성하기 위한 점착성 고분자는 그 종류가 동일계열 또는 유사계열일 수도 있지만, 그 조성과 분자량까지 서로 동일한 것은 아니다. The adhesive polymer for forming the first adhesive layer and the adhesive polymer for forming the second adhesive layer may be of the same or similar series, but their composition and molecular weight are not the same.

상기 제 1 점착층의 전단강도(Shear Strength)는 1 Kg/in2 이상으로 할 수 있다. 보다 강한 접착을 위해서는 제 1 점착층의 전단강도를 3 Kg/in2 이상으로 할 수도 있다. The shear strength of the first adhesive layer may be 1 Kg / in 2 or more. For a stronger adhesion, the shear strength of the first adhesive layer may be 3 Kg / in 2 or more.

전단 강도의 측정은 상기에서와 마찬가지로, 도 7에서 보는 바와 같이 양면 점착 테이프를 이용하여 SUS(스테인리스 스틸) 패널에 알루미늄 스트립을 부착하여 측정하는데, 60℃의 온도에서 상기 양면 점착 테이프의 접착면에 대하여 수평이지만 방향이 서로 상반되는 힘을 각각 SUS 패널과 알루미늄 스트립에 가하되 상기 알루미늄 스트립을 SUS패널로부터 분리시키기 위한 수단의 cross-head 속도를 10 mm/min인 조건으로 하여 측정한다. 상기 서로 상반되는 힘이 가해지는 동안, 도 8에서 보는 바와 같이 응력(stress)과 변형율(strain)을 측정하여, 이때 발생하는 최대 응력을 전단강도(shear strength)라 한다(도 8 참조) (실험조건 Between Al strip and SUS panel, cross-head speed: 10 mm/min).The shear strength was measured by attaching an aluminum strip to a stainless steel (SUS) panel using a double-sided adhesive tape as shown in Fig. 7, and measuring the shear strength at the bonding surface of the double- And a force which is horizontal but opposite in direction to each other is applied to the SUS panel and the aluminum strip, and the cross-head speed of the means for separating the aluminum strip from the SUS panel is measured under the condition of 10 mm / min. As shown in FIG. 8, stress and strain are measured while opposing forces are applied, and the maximum stress generated at this time is referred to as shear strength (see FIG. 8) Conditions Between Al strip and SUS panel, cross-head speed: 10 mm / min).

상기 제 1 점착층을 형성하기 위한 고분자는 그 분자량이 특별히 제한되는 것은 아니며, 적게는 10,000에서부터 크게는 1,000,000 이상까지도 가능하다.The molecular weight of the polymer for forming the first adhesive layer is not particularly limited, and may range from 10,000 to as high as 1,000,000 or more.

상기 필름형태의 시트(101)에서, 상기 제 1 점착층이 배치되지 않은 타면에는 제 2 점착층(120)이 형성된다. 상기 제 2 점착층은 박리층으로서, 접착면에 수평방향으로 힘을 작용시킬 경우 용이하게 박리되어, 본 발명에 의한 양면 점착 테이프를 사용하여 제조되는 제품의 재작업성을 향상시킨다.In the film-like sheet 101, a second adhesive layer 120 is formed on the other surface on which the first adhesive layer is not disposed. The second adhesive layer is a peeling layer which is easily peeled off when a force is applied to the adhesive surface in the horizontal direction to improve the reworkability of a product manufactured using the double-faced adhesive tape according to the present invention.

본 발명의 일례에 따르면, 상기 제 2 점착층(120) 역시 점착성 고분자에 의하여 형성될 수 있다. 상기 제 2 점착층을 형성하기 위한 점착성 고분자는, 모노머 및 중합개시제를 포함하며, 아울러 연쇄전달제(chain transfer agent), 중합억제제(retardant), 저분자량 첨가제 및 경화제 중 적어도 하나를 추가로 포함하는 점착성 고분자 조성물에 의하여 형성될 수 있다.According to an embodiment of the present invention, the second adhesive layer 120 may also be formed of a sticky polymer. Wherein the adhesive polymer for forming the second adhesive layer comprises a monomer and a polymerization initiator and further comprises at least one of a chain transfer agent, a polymerization inhibitor, a low molecular weight additive and a curing agent Can be formed by a sticky polymer composition.

상기 제 2 점착층을 형성하기 위한 점착성 고분자는 디스플레이의 시인성을 크게 저하시키지 않을 정도의 투명성을 가져야 한다. 이러한 점착성 고분자로서 예를 들어, 아크릴계 점착성 고분자, 실리콘계 점착성 고분자, 폴리에스테르계 점착성 고분자, 고무계 점착성 고분자 또는 폴리우레탄계 점착성 고분자 등의 공지 또는 관용의 감압성 점착성 고분자가 있다. 상기 점착성 고분자는 단독으로 또는 2종 이상 조합하여 사용할 수도 있다. 상기 제 2 점착층을 형성하기 위한 점착성 고분자는 상기 제 1 점착층을 형성하기 위한 점착성 고분자와 그 종류가 동일계열이거나 또는 유사계열일 수 있지만, 그 조성과 또는 분자량까지 동일한 것은 아니다.The adhesive polymer for forming the second adhesive layer should have transparency such that the visibility of the display is not significantly deteriorated. As such a sticking polymer, there is known or commonly used pressure-sensitive adhesive polymer such as acrylic adhesive polymer, silicone adhesive polymer, polyester adhesive polymer, rubber adhesive polymer or polyurethane adhesive polymer. These adhesive polymers may be used alone or in combination of two or more. The adhesive polymer for forming the second adhesive layer may be of the same type or similar type as the adhesive polymer for forming the first adhesive layer, but the composition and the molecular weight are not the same.

본 발명의 일례에 따르면 상기 상기 제 2 점착층을 형성하는 점착성 고분자로서 아크릴계 점착성 고분자를 사용할 수 있다.According to an embodiment of the present invention, an acrylic adhesive polymer may be used as the adhesive polymer forming the second adhesive layer.

이러한 아크릴계 점착성 고분자로서 예를 들어, 탄소수 1 내지 18의 (메트)아크릴산 알킬 에스테르, 즉, C1 -18의 아크릴레이트 계열의 화합물을 모노머의 주성분으로 함유하는 아크릴계 고분자를 사용할 수 있다. 상기 C1 -18의 아크릴레이트 계열과 다른 모노머를 함께 포함하는 공중합체를 사용할 수도 있음은 물론이다. As such an acrylic adhesive polymer, for example, an acrylic polymer containing a (meth) acrylic acid alkyl ester having 1 to 18 carbon atoms, that is, an acrylate-based compound of C 1 -18 as a main component of a monomer can be used. It is needless to say that a copolymer including the above-mentioned C 1 -18 acrylate series and other monomers may also be used.

상기 C1 -18의 아크릴레이트 계열의 모노머와 함께 사용될 수 있는 공중합성 모노머의 구체적인 예로는, 각종 작용기를 갖는 공중합성 모노머, 스티렌계 모노머, α-올레핀계 모노머, 비닐 에스테르, 시아노기 함유 모노머, 아미드기 함유 모노머, 하이드록실기 함유 모노머, 산기(acidic group) 함유 모노머, 에폭시기 함유 모노머, 아미노기 함유 모노머, 카복실기 함유 모노머 등이 있다. Specific examples of the copolymerizable monomers that can be used together with the above-mentioned C 1 -18 acrylate monomers include copolymerizable monomers having various functional groups, styrene monomers, -olefin monomers, vinyl esters, cyano group-containing monomers, An amide group-containing monomer, a hydroxyl group-containing monomer, an acidic group-containing monomer, an epoxy group-containing monomer, an amino group-containing monomer, and a carboxyl group-containing monomer.

한편 아크릴계 점착성 고분자의 개질용 모노머로 알려진 각종 모노머도 사용될 수 있는데, 본 발명의 일례에 따르면 IBXA로 알려진 이소보닐아크릴레이트를 사용할 수 있다.On the other hand, various monomers known as modifying monomers for acrylic adhesive polymers can also be used. According to one example of the present invention, isobornyl acrylate known as IBXA can be used.

상기 아크릴계 점착성 고분자를 제조하는 방법은 공지의 방법을 적용할 수 있다. 예를 들면 용액 중합 방법, 에멀젼 중합방법, 자기 중합 방법, 또는 광 개시제를 사용하는 광중합 방법 등을 사용할 수 있다. A known method can be applied to the acrylic adhesive polymer. For example, a solution polymerization method, an emulsion polymerization method, a self polymerization method, or a photopolymerization method using a photoinitiator can be used.

본 발명의 일례에 따르면, 중합 개시제로서 광개시제를 사용하는 광중합 방법을 적용할 수 있다. 이러한 광중합개시제로서 이가큐어(Irgacure) 계열의 광중합 개시제를 사용할 수 있다.According to one example of the present invention, a photopolymerization method using a photoinitiator as a polymerization initiator can be applied. As such a photopolymerization initiator, an Irgacure series photopolymerization initiator may be used.

또한 필요한 경우 가교제를 사용할 수도 있는데 공지된 것들을 사용할 수 있다. 특히, 다작용성 아크릴레이트 또는 메타크릴레이트, 다작용성 멜라민 화합물, 다작용성 에폭시 화합물 또는 다작용성 이소시아네이트 화합물 등을 사용할 수 있다. 상기 가교제의 종류에 특별한 제한이 있는 것은 아니며, 상기 가교제는 단독으로 또는 2종 이상 조합하여 사용될 수 있다.If necessary, crosslinking agents may also be used, and known ones can be used. In particular, polyfunctional acrylates or methacrylates, polyfunctional melamine compounds, polyfunctional epoxy compounds or polyfunctional isocyanate compounds can be used. The type of the crosslinking agent is not particularly limited, and the crosslinking agent may be used alone or in combination of two or more.

아울러 상기 점착성 고분자에는 필요에 따라 각종 첨가제를 함유할 수 있는데, 예를 들어, 관용의 점착부여 수지, 가소제, 충전제, 착색제, 자외선 흡수제, 계면활성제 등 공지된 각종 첨가제를 첨가할 수 있다. 그러나 이들 첨가제가 첨가되더라도 상기 점착성 고분자 수지의 투명성 및 무색성을 훼손해서는 안된다.The adhesive polymer may contain various additives as required. For example, various known additives such as a tackifier resin for general use, a plasticizer, a filler, a colorant, an ultraviolet absorber, and a surfactant may be added. However, even if these additives are added, transparency and colorlessness of the adhesive polymer resin should not be impaired.

또한, 상기 점착성 고분자를 형성하기 위한 조성물은 연쇄전달제(chain transfer agent), 중합억제제(retardant), 저분자량 첨가제 및 경화제 중 적어도 하나를 더 포함할 수 있다.In addition, the composition for forming the adhesive polymer may further include at least one of a chain transfer agent, a polymerization inhibitor, a low molecular weight additive, and a curing agent.

상기 연쇄전달제(chain transfer agent)에는 적어도 하나의 약한 화학결합(chemical bonding)이 존재하여 연쇄전달반응(chain transfer reaction)을 유도한다. 상기 연쇄전달반응에 의하여 최종 생성되는 고분자의 평균 분자량이 낮아지기 때문에 상기 연쇄전달제는 분자량 조절제라고도 한다. 본 발명에서는 연쇄전달제를 사용함으로써 제 2 점착층(120)을 형성하는 점착성 고분자의 분자량을 낮추어 제 2 점착층의 전단강도(shear strength)를 조절할 수 있다. 본 발명의 일례에 따르면, 상기 연쇄전달제로서 IOTG (Isooctyl thioglycolate)를 사용할 수 있다.At least one weak chemical bond is present in the chain transfer agent to induce a chain transfer reaction. Since the average molecular weight of the polymer finally produced by the chain transfer reaction is lowered, the chain transfer agent is also referred to as a molecular weight modifier. In the present invention, by using a chain transfer agent, the shear strength of the second adhesive layer can be controlled by lowering the molecular weight of the adhesive polymer forming the second adhesive layer 120. According to one embodiment of the present invention, IOTG (Isooctyl thioglycolate) may be used as the chain transfer agent.

상기 중합억제제(retardant)는 중합 반응을 지연시켜 고분자의 분자량을 낮출 수 있다. 본 발명의 일례에 따르면, 상기 중합억제제의 일례로서 AMS(Alpha-methyl styrene)를 사용할 수 있다.The polymerization inhibitor may retard the polymerization reaction and lower the molecular weight of the polymer. According to one embodiment of the present invention, AMS (Alpha-methyl styrene) may be used as an example of the polymerization inhibitor.

상기 저분자량 첨가제는 고분자 조성물에 첨가되어, 제조된 고분자의 평균 분자량을 낮추거나, 또는 평균 분자량에는 큰 영향을 주지 않더라도 고분자 내에 부분적으로 저분자량 부분이 존재하게 하여 점착력 또는 전단 강도를 낮추는 역할을 한다. 본 발명의 일례에 따르면 상기 저분자량 첨가제의 수평균 분자량은 10000 이하가 되도록 한다. 상기 저분자량 첨가제로서는 상업적으로 시판되는 제품을 사용할 수 있다. 본 발명의 상기 저분자량 첨가제의 일례에 따르면 Joncyl(BASF사) 계열의 제품을 사용할 수 있다. The low molecular weight additive is added to the polymer composition to lower the average molecular weight of the prepared polymer or to lower the adhesive force or the shear strength by allowing a low molecular weight portion to be partially present in the polymer even if the average molecular weight is not greatly affected . According to an embodiment of the present invention, the number average molecular weight of the low molecular weight additive is set to 10,000 or less. As the low molecular weight additive, commercially available products may be used. According to one example of the low molecular weight additive of the present invention, Joncyl (BASF) series products can be used.

상기 경화제는 고분자 조성물에 첨가되어 경화반응을 일으키는 물질로서, 기본적으로 고분자 조성물의 응집력을 확보할 수 있으며, 경화반응에 의해 형성되는 제2 점착층의 표면 손상을 억제할 수 있다. 상기 경화제로는 상업적으로 시판되는 제품을 사용할 수 있으며, 일례를 들면 HDD (SK Cytec specialties사) 계열의 제품을 사용할 수 있다. The curing agent is added to the polymer composition to cause a curing reaction. Basically, the cohesive force of the polymer composition can be secured and the surface damage of the second adhesive layer formed by the curing reaction can be suppressed. As the curing agent, a commercially available product can be used. For example, a product of HDD (SK Cytec specialties) can be used.

본 발명에 따른 양면 점착 테이프는 상기 제 2 점착층의 전단강도를 약화시켜 재작업성을 향상시키는데, 상기 전단강도는 상기 연쇄전달제, 중합억제제 및 저분자량 첨가제에 의하여 약화시킬 수 있다. 상기 연쇄전달제, 중합억제제 및 저분자량 첨가제는 한 종류만 사용할 수도 있고, 2종 이상을 혼합하여 사용할 수도 있다. 본 발명의 일례에 따르면 모노머의 중량 100 중량부에 대하여 상기 연쇄전달제는 0.03 내지 5 중량부만큼 포함될 수 있고, 중합억제제는 0.01 내지 0.5 중량부만큼 포함될 수 있고, 저분자량 첨가제는 1 내지 50 중량부 포함될 수 있다. 상기 함량은 사용하는 모노머의 종류에 따라 달라질 수 있다. 본 발명의 또 다른 일례에 따르면, 경화제의 함량은 모노머의 중량 100 중량부에 대하여 0 중량부를 초과하되, 0.07 중량부 이하로 포함될 수 있다.The double-sided adhesive tape according to the present invention weakens the shear strength of the second adhesive layer to improve reworkability, and the shear strength can be weakened by the chain transfer agent, polymerization inhibitor and low molecular weight additive. The chain transfer agent, polymerization inhibitor and low molecular weight additive may be used alone or in combination of two or more. According to an embodiment of the present invention, the chain transfer agent may be contained in an amount of 0.03 to 5 parts by weight based on 100 parts by weight of the monomer, 0.01 to 0.5 parts by weight of the polymerization inhibitor may be included, and 1 to 50 parts by weight May be included. The content may vary depending on the kind of the monomer used. According to another embodiment of the present invention, the content of the curing agent is more than 0 part by weight, but not more than 0.07 part by weight based on 100 parts by weight of the monomer.

본 발명의 일례에 따르면, 상기 상기 제 2 점착층(120)의 전단강도는 제 1 점착층(110)의 전단강도 보다 작다. 그렇기 때문에 재작업이 필요한 경우, 접착면에 대하여 수평방향으로 서로 상반되는 힘을 가하면 제 2 점착층이 박리되어 본 발명에 의한 양면 점착 테이프를 매개로 서로 부착되어 있던 부품들이 용이하게 분리될 수 있다.According to an embodiment of the present invention, the shear strength of the second adhesive layer 120 is smaller than the shear strength of the first adhesive layer 110. Therefore, when a re-work is required, if a force opposing each other in the horizontal direction with respect to the adhesive surface is applied, the second adhesive layer is peeled off and the components attached to each other through the double-faced adhesive tape according to the present invention can be easily separated .

상기 제 2 점착층(120)의 전단강도(Shear Strength)는 0.05 내지 16 Kg/in2 의 범위로서 16 Kg/in2 이하의 범위이다. 상기 전단 강도는 구체적으로, 알루미늄 스트립을 SUS 패널에 부착하고, 60℃의 온도에서 cross-head 속도가 10mm/min인 조건일 때 측정한 값을 기준으로 한다(실험조건 Between Al strip and SUS panel, cross-head speed: 10 mm/min).The shear strength of the second adhesive layer 120 is in the range of 0.05 to 16 Kg / in 2 and not more than 16 Kg / in 2 . Specifically, the shear strength is measured by attaching an aluminum strip to an SUS panel and measuring the temperature at a temperature of 60 ° C at a crosshead speed of 10 mm / min (experimental conditions Between Al strip and SUS panel, cross-head speed: 10 mm / min).

상기 전단강도는 16 Kg/in2 이하의 범위에서 적절하게 조정될 수 있는데, 본 발명에 의한 양면 점착 테이프가 사용되는 용도에 따라 달라질 수 있다. 예를 들어, 비교적 소형의 기기라고 할 수 있는 모바일 기기에 적용되는 경우 접착강도가 대형의 디스플레이 장치에 적용되는 만큼 크지 않아도 되는 바, 상기 양면 점착 테이프의 전단강도는 60℃의 온도에서 10 Kg/in2 이하, 즉, 0.08 내지 10 Kg/in2 가 되도록 할 수 있다. 여기서 모바일 기기는 통상적으로 알려진 기기로서, 핸드폰, 스파트폰, PMP, 네비게이션, MP3 플레이어, 태블릿 PC 등이 있으며, 넷북이나 노트북도 포함될 수 있다. The shear strength is 16 Kg / in 2 And can be varied depending on the application in which the double-sided pressure-sensitive adhesive tape according to the present invention is used. For example, when applied to a mobile device such as a relatively small device, the adhesive strength may not be as large as that applied to a large display device. The shear strength of the double-faced adhesive tape is preferably 10 Kg / in 2 0.08 to 10 Kg / in < 2 > . Here, mobile devices are commonly known devices such as a mobile phone, a SPOT phone, a PMP, a navigation device, an MP3 player, a tablet PC, and the like, and may include a netbook or a notebook.

재작업성을 용이하게 하기 위하여 상기 제 2 점착층은, 점착제를 이용하여 PMMA/PC와 플레이트를 접착한 후 60℃의 온도에서 4.5in2의 면적에 1 Kg의 하중을 인가했을 때의 분리시간이 20초 이상이고, 3Kg의 하중이 인가될 때의 분리시간이 600분 이하가 되도록 조정할 수도 있다.In order to facilitate re-workability, the second adhesive layer is formed by bonding a PMMA / PC plate with a pressure-sensitive adhesive, separating the plate at a temperature of 60 ° C at an area of 4.5 in 2 and applying a load of 1 kg, Is 20 seconds or more, and the separation time when a load of 3 kg is applied is 600 minutes or less.

상기 분리시간은 본 발명에 의한 양면 점착 테이프가 사용되는 용도에 따라 적절하게 조정될 수 있다. 예를 들어, 비교적 소형의 기기라고 할 수 있는 모바일 기기에 적용되는 경우 접착강도가 대형의 디스플레이 장치에 적용되는 만큼 크지 않아도 되는 바, 상기 양면 점착 테이프는, 60℃의 온도에서 4.5 in2의 면적에 1 Kg의 하중이 인가될 때의 분리시간이 30초 이상이고, 3Kg의 하중이 인가될 때의 분리시간이 300분 이하가 되도록 조정할 수 있다. The separation time can be suitably adjusted according to the application in which the double-faced adhesive tape according to the present invention is used. For example, when applied to a mobile device such as a relatively small device, the adhesive strength may not be as large as that applied to a large display device. The double-sided adhesive tape has an area of 4.5 in 2 The separation time when a load of 1 kg is applied is 30 seconds or more and the separation time when a load of 3 Kg is applied is 300 minutes or less.

본 발명의 일례에 따른 양면 점착 테이프(100)의 제 2 점착층(120)은, 도 2에서 보는 바와 같이 투명 플레이트(310)를 디스플레이 패널(320)의 표시부에 부착시키는 데 적용될 수 있는데, 재작업이 필요한 경우 도 3에서 보는 바와 같이 비교적 용이하게 박리되어야 한다.The second adhesive layer 120 of the double-sided adhesive tape 100 according to an example of the present invention can be applied to attach the transparent plate 310 to the display portion of the display panel 320 as shown in FIG. If work is required, it should be comparatively easily peeled as shown in Fig.

참고로, 도 2에서 제 1 점착층(110)이 투명 플레이트(310)에 부착되고 제 2 점착층(120) 디스플레이 패널(320)의 표시면에 부착되었는데, 반대로 제 1 점착층이 디스플레이 패널의 표시면에 부착되고 제 2 점착층은 투명 플레이트에 부착될 수도 있다.2, the first adhesive layer 110 is attached to the transparent plate 310 and the second adhesive layer 120 is attached to the display surface of the display panel 320. In contrast, And the second adhesive layer may be attached to the transparent plate.

본 발명의 일례에 따르면 상기와 같이 제 2 점착층을 형성할 때, 상대적으로 저분자량인 점착성 고분자를 이용함으로써 재작업성을 높일 수도 있고, 평균 분자량이 낮지는 않지만 일정량의 저분자량 첨가제가 포함된 점착성 고분자를 사용할 수도 있다. 적용용도 및 사용자의 선택에 따라 분자량 10,000 내지 300,000 정도의 고분자를 사용할 수도 있고, 그 이상 또는 그 이하의 분자량을 갖는 고분자를 사용할 수도 있을 것이다.According to an embodiment of the present invention, when the second adhesive layer is formed as described above, the reworkability can be improved by using the adhesive polymer having a relatively low molecular weight, and the reworkability can be improved by using a small amount of low molecular weight additive A sticky polymer may also be used. Depending on the application and the user's choice, a polymer having a molecular weight of about 10,000 to 300,000 may be used, or a polymer having a molecular weight of more than or equal to the molecular weight may be used.

본 발명에 따른 양면 점착 테이프를 제조하는 방법의 일례로는, 제 1 점착성 고분자를 시럽상태로 만들어 필름형태의 시트(101)의 일면에 배치하고 광경화시켜 제 1 점착층(110)을 형성하고, 제 2 점착성 고분자를 시럽상태로 만들어 필름형태의 시트(101)의 타면에 배치하고 광경화시켜 제 2 점착층(120)을 형성하는 방법이 있다. 여기서 제 1 점착층을 형성하는 순서와 제 2 점착층을 형성하는 순서는 바뀌어도 상관이 없으며, 제 1 점착층과 제 2 점착층을 동시에 형성할 수도 있다.One example of a method for producing a double-sided adhesive tape according to the present invention is to form a first adhesive layer 110 in a syrup state by placing the first adhesive polymer on a surface of a sheet 101 in the form of a film and photo- , The second adhesive polymer is syrupy placed on the other side of the sheet 101 in the form of a film, and the second adhesive layer 120 is formed by photo-curing. Here, the order of forming the first adhesive layer and the order of forming the second adhesive layer may be changed, and the first adhesive layer and the second adhesive layer may be simultaneously formed.

필요한 경우 제 1 점착층의 노출면과 제 2 점착층의 노출면 중 어느 한 곳에 이형지 또는 라이너를 배치할 수도 있다.If necessary, a release paper or a liner may be disposed on either the exposed surface of the first adhesive layer or the exposed surface of the second adhesive layer.

상기 제 1 점착층(110) 및 제 2 점착층(120)은 필요한 점착력을 부여할 수만 있다면 그 두께는 특별히 제한되지 않는다. 예를 들어, 상기 제 1 점착층(110) 및 제 2 점착층(120)의 두께는 모두 약 5 내지 약 500㎛가 가능하며, 필요에 따라서는 약 100 내지 약 400㎛의 두께를 가질 수 있다.The thickness of the first adhesive layer 110 and the second adhesive layer 120 is not particularly limited as long as it can impart necessary adhesive force. For example, the first adhesive layer 110 and the second adhesive layer 120 may all have a thickness of about 5 to about 500 탆, and may have a thickness of about 100 to about 400 탆, if necessary .

또한 본 발명의 일례에 따른 양면 점착 테이프는 가시광 파장 영역에서의 광투과율(JIS K7361)이 90% 이상이 되도록 할 수 있다.The double-faced pressure-sensitive adhesive tape according to an example of the present invention can have a light transmittance (JIS K7361) of 90% or more in a visible light wavelength region.

본 발명에 있어서, 상기 양면 점착 테이프는 본 발명의 효과를 손상시키지 않기만 하면 추가적인 층을 더 포함할 수 있다.In the present invention, the double-sided pressure-sensitive adhesive tape may further include additional layers as long as the effect of the present invention is not impaired.

일례로, 도 4에 도시된 양면 점착 테이프(200)는, 도 1에 따른 양면 점착 테이프의 제 2 점착층(120)에 보조필름 시트(102)가 더 배치되어 있으며, 상기 보조필름 시트(102)에는 제 3 점착층(130)이 배치되어 있는 구조이다.For example, in the double-sided adhesive tape 200 shown in Fig. 4, the auxiliary film sheet 102 is further disposed on the second adhesive layer 120 of the double-sided adhesive tape according to Fig. 1, The third adhesive layer 130 is disposed.

여기서 보조필름 시트(102)의 재료 및 두께 등은 상기 필름형태의 시트(101)와 동일할 수 있다. 또한 제 3 점착층(130)은 제 1 점착층(110)과 동일할 수 있다.Here, the material, the thickness, and the like of the auxiliary film sheet 102 may be the same as the sheet 101 in the film form. The third adhesive layer 130 may be the same as the first adhesive layer 110.

본 발명은 또한, 상기 양면 점착테이프(100, 200)를 사용하는 디스플레이 장치를 제공한다. 본 발명의 일례에 따른 디스플레이 장치는, 디스플레이 패널(320); 상기 디스플레이 패널의 표시면에 배치된 양면 점착 테이프(100, 200); 및 상기 양면 점착 테이프에 배치된 투명 플레이트(310);를 포함한다(도 2 및 도 5).The present invention also provides a display device using the double-faced pressure-sensitive adhesive tape (100, 200). A display device according to an exemplary embodiment of the present invention includes a display panel 320; A double-sided adhesive tape (100, 200) disposed on a display surface of the display panel; And a transparent plate 310 disposed on the double-sided adhesive tape (FIGS. 2 and 5).

구체적으로, 도 2에 도시된 본 발명의 일례에 따르면 상기 양면 점착 테이프(100)의 제 2 점착층(120)을 디스플레이 패널(320)의 표시부에 접착하고 제 1 점착층(110)을 투명 플레이트(310)에 접착한 구조이다. 도 5에서는 본 발명의 다른 일례에 따른 양면 점착 테이프(200)의 제 3 점착층(130)을 디스플레이 패널(320)의 표시부에 접착하고 제 1 점착층(110)을 투명플레이트(310)에 접착한 구조이다.2, the second adhesive layer 120 of the double-sided adhesive tape 100 is adhered to the display portion of the display panel 320, and the first adhesive layer 110 is adhered to the transparent plate 100. [ (310). 5, the third adhesive layer 130 of the double-sided adhesive tape 200 according to another embodiment of the present invention is adhered to the display portion of the display panel 320 and the first adhesive layer 110 is adhered to the transparent plate 310 It is one structure.

본 발명의 일례에 따르면 상기 투명 플레이트(310)는 전자기기의 커버 윈도우 또는 플레이트가 터치패널일 수 있다. According to an exemplary embodiment of the present invention, the transparent plate 310 may be a touch panel of a cover window or a plate of an electronic device.

본 발명의 다른 일례에 따르면, 상기 투명 플레이트는 디스플레이 패널에 부착된 터치패널의 전면에 배치되는 커버 윈도우일 수 있다. 즉, 상기 터치패널의 전면에 커버 윈도우를 부착하는 경우에도 본 발명에 의한 양면 점착 테이프를 사용할 수 있다.According to another embodiment of the present invention, the transparent plate may be a cover window disposed on a front surface of a touch panel attached to the display panel. That is, even when the cover window is attached to the front surface of the touch panel, the double-sided adhesive tape according to the present invention can be used.

본 발명에 따른 양면 점착 테이프는 바람직하게는, 상기 디스플레이 패널의 표시전면에 접착시킬 수 있다.The double-sided adhesive tape according to the present invention is preferably adhered to the display front surface of the display panel.

이와 같이 본 발명에 따른 양면 점착 테이프(100, 200)는 터치패널이나 커버 윈도우와 같은 투명 플레이트(310)를 디스플레이 패널(320)의 표시부에 접착 고정시키는 데에 유용하게 사용될 수 있다. 또는, 터치패널의 전면 표시부에 커버 윈도우를 부착할 때도 상기 양면 점착 테이프(100, 200)를 사용할 수 있다.As described above, the double-faced pressure-sensitive adhesive tape 100, 200 according to the present invention can be advantageously used to adhesively fix the transparent plate 310 such as a touch panel or a cover window to the display portion of the display panel 320. Alternatively, the double-sided adhesive tape 100, 200 may be used to attach the cover window to the front display portion of the touch panel.

상기 양면 점착 테이프는 도 3 및 도 6에서 보는 바와 같이, 투명 플레이트(310)와 디스플레이 패널(320)에 대하여, 접착면에 대하여 수평인 방향으로 상반된 힘, 예컨대 전단력(shear force)을 가할 경우 제 2 점착층이 용이하게 박리되기 때문에 재작업성이 우수하다.As shown in FIGS. 3 and 6, the double-faced pressure-sensitive adhesive tape is applied to the transparent plate 310 and the display panel 320 in the case of applying opposing forces, for example shear force, 2 Since the adhesive layer is easily peeled off, the reworkability is excellent.

본 발명에 따른 상기 양면 점착 테이프(100, 200)의 제 2 점착층(120)은 피착제와의 젖음성이 좋아 양호한 접착력을 보이기 때문에 통상의 사용상태에서는 벗겨질 염려가 없지만, 접착면에 대하여 수평방향으로 힘을 작용시키면 용이하게 분리되며 또한 분리된 후의 점착층 물질 잔사의 제거가 용이하다. 그 결과 상기 분리된 디스플레이 패널(320)과 투명 플레이트(310)를 재사용할 수 있기 때문에 이들을 폐기하지 않아도 된다. 따라서, 불필요한 낭비를 줄여 제조 비용을 절감할 수 있다.Since the second adhesive layer 120 of the double-faced pressure-sensitive adhesive tape 100 or 200 according to the present invention has good wettability with the adherend and exhibits a good adhesive strength, there is no fear of peeling off under normal use, And it is easy to remove the adhesive layer material residue after separation. As a result, since the separated display panel 320 and the transparent plate 310 can be reused, they need not be discarded. Therefore, unnecessary waste can be reduced, and the manufacturing cost can be reduced.

본 발명에 따른 디스플레이 패널은 그 종류가 특별히 제한되지 않는다. 예를 들어, 액정 표시장치, CRT 브라운관, 플라즈마 디스플레이, 유기발광소자 디스플레이 등이 있다.
The kind of the display panel according to the present invention is not particularly limited. For example, there are a liquid crystal display, a CRT cathode ray tube, a plasma display, and an organic light emitting diode display.

이하 실시예 및 비교예를 통하여 본 발명을 보다 구체적으로 설명한다.Hereinafter, the present invention will be described more specifically by way of examples and comparative examples.

<비교제조예 1 내지 4 및 실시예 1 내지 25><Comparative Production Examples 1 to 4 and Examples 1 to 25>

필름형태의 시트(101)로서 25㎛ 두께를 갖는 PET 필름을 사용하였다. 광학점착체(OCA; Optically Clear Adhesive)로서 사용되는 3M사의 "Optically Clear Adhesive 8146"를 상기 시트(101)의 일면에 100㎛ 두께로 적층하여 제 1 점착층(110)을 형성하였다.A PET film having a thickness of 25 mu m was used as the sheet 101 in film form. A first adhesive layer 110 was formed by laminating 3M's "Optically Clear Adhesive 8146", which is used as an OCA (Optically Clear Adhesive), to a thickness of 100 μm on one side of the sheet 101.

제 2 점착층(120)을 형성하기 위한 점착성 고분자를 제조하기 위하여, 먼저 광중합 방법에 따라 하기 표 1의 조성으로 비교예 및 실시예에 따른 점착성 고분자를 제조하였다. 하기 표 1에서 함량은 모노머들의 전체 중량을 100 중량부로 했을 때의 상대적인 중량을 나타낸다. 모노머로는 아크릴계 모노머를 2종 혼합하여 사용하였다. To prepare the adhesive polymer for forming the second adhesive layer 120, the adhesive polymer according to the comparative examples and the examples were prepared according to the photopolymerization method with the composition shown in Table 1 below. In the following Table 1, the content represents the relative weight when the total weight of the monomers is 100 parts by weight. As the monomer, two kinds of acrylic monomers were used in combination.

시료
sample
제1모노머The first monomer 제2모노머The second monomer 광개시제Photoinitiator 연쇄전달제Chain transfer agent 중합억제제Polymerization inhibitor 저분자량 첨가제Low molecular weight additive 경화제Hardener 2-EHA2-EHA IBXAIBXA Irgacure 651Irgacure 651 IOTGIOTG AMSAMS Joncryl 962Joncryl 962 HDDAHDDA 실시예 1Example 1 5050 5050 0.30.3 0.050.05 -- -- -- 실시예 2Example 2 5050 5050 0.30.3 0.10.1 -- -- -- 실시예 3Example 3 5050 5050 0.30.3 0.20.2 -- -- -- 실시예 4Example 4 5050 5050 0.30.3 0.30.3 -- -- -- 실시예 5Example 5 5050 5050 0.30.3 0.40.4 -- -- -- 실시예 6Example 6 5050 5050 0.30.3 0.50.5 -- -- -- 실시예 7Example 7 5050 5050 0.30.3 1One -- -- -- 실시예 8Example 8 4545 5555 0.30.3 0.30.3 -- -- -- 실시예 9Example 9 6060 4040 0.30.3 0.30.3 -- -- -- 실시예 10Example 10 7070 3030 0.30.3 0.30.3 -- -- -- 실시예 11Example 11 5050 5050 0.30.3 -- 0.20.2 -- -- 실시예 12Example 12 5050 5050 0.30.3 -- 0.150.15 -- -- 실시예 13Example 13 5050 5050 0.30.3 -- 0.10.1 -- -- 실시예 14Example 14 5050 5050 0.30.3 -- 0.050.05 -- -- 실시예 15Example 15 5050 5050 0.30.3 -- -- 55 -- 실시예 16Example 16 5050 5050 0.30.3 -- -- 1010 -- 실시예 17Example 17 5050 5050 0.30.3 -- -- 1515 -- 실시예 18Example 18 5050 5050 0.30.3 -- -- 2020 -- 실시예 19Example 19 5050 5050 0.30.3 00 -- -- -- 실시예 20Example 20 5050 5050 0.30.3 0.020.02 -- -- -- 실시예 21Example 21 6060 4040 0.30.3 -- -- -- -- 실시예 22Example 22 6060 4040 0.150.15 -- -- -- -- 실시예 23Example 23 6060 4040 0.150.15 -- -- -- 0.020.02 실시예 24Example 24 6060 4040 0.150.15 -- -- -- 0.050.05 실시예 25Example 25 6060 4040 0.150.15 -- -- -- 0.070.07 비교예 1Comparative Example 1 6060 4040 0.150.15 -- -- -- 0.10.1 비교예 2Comparative Example 2 6060 4040 0.150.15 -- -- -- 0.120.12 비교예 3Comparative Example 3 6060 4040 0.150.15 -- -- -- 0.150.15 비교예 4Comparative Example 4 6060 4040 0.150.15 -- -- -- 0.200.20

상기 표 1에서 사용된 물질에 대한 정보는 하기 표 2에 기재된 바와 같다.The information on the materials used in Table 1 is as shown in Table 2 below.

명칭 designation 타입type 등급Rating 제공업체Provider 비고Remarks 2-EHA2-EHA 모노머Monomer -- LG ChemicalLG Chemical 2-ethlyhexyl acrylate2-ethlyhexyl acrylate IBXAIBXA 모노머Monomer -- Osaka Organic ChemicalOsaka Organic Chemical Isobornyl arcrylateIsobornyl arcrylate Irgacure 651Irgacure 651 Photo initiatorPhoto initiator -- BASFBASF 2,2-Dimethoxy-1,2-diphenylethan-1-one2,2-Dimethoxy-1,2-diphenylethan-1-one IOTGIOTG Chain transfer agentChain transfer agent PurePure TCI
(Tokyo Chemical Industry)TCI
(Tokyo Chemical Industry) Isooctyl thioglycolateIsooctyl thioglycolate AMSAMS 모노머Monomer PurePure Sigma AldrichSigma Aldrich Alpha methly styreneAlpha methly styrene Joncryl 963Joncryl 963 Acryl polyolAcryl polyol BASFBASF -- HDDAHDDA 경화제Hardener -- SK Cytec specialtiesSK Cytec specialties Hexandiol diacrylateHexandiol diacrylate

상기 2 종류의 모노머에 광개시제를 혼합하고, 질소 분위기 하에서 UV를 조사하여 부분 중합을 실시하였다. 상기 UV 조사 조건은 아래 표 3과 같다. 상기 부분 중합의 결과 시럽 상태의 예비중합 조성물을 얻었다.The photoinitiators were mixed with the two kinds of monomers, and partial polymerization was carried out by irradiating UV in a nitrogen atmosphere. The UV irradiation conditions are shown in Table 3 below. As a result of the partial polymerization, a syrupy prepolymerized composition was obtained.

UV IntensityUV Intensity N2 Purging timeN 2 Purging time Delta TDelta T Final ViscosityFinal Viscosity 0.3 mW/cm2 0.3 mW / cm 2 15 min15 min 6 ℃6 ℃ 1000~2000cps1000 to 2000 cps

이어 상기 시럽 상태의 예비중합 조성물에 나머지 성분들을 혼합하고, 나이프 코팅 방법에 의하여 상기 시럽 상태의 예비 중합 조성물을 실리콘으로 코팅된 두장의 PET 이형지 사이에 도포하였다. 상기 도포된 물질에 대하여 낮은 에너지의 UV를 조사하였다. UV 조사는 아래 표 4에서 보는 바와 같이 4 단계의 영역에서 이루어 졌다. 상기 UV 조사에 의하여 50㎛ 두께의 제 2 점착층 (120) 물질을 얻었다.Then, the remaining components were mixed in the syrup-like prepolymerized composition, and the syrupy prepolymerized composition was applied between two silicone-coated PET release papers by a knife coating method. The applied material was irradiated with low energy UV. The UV irradiation was made in the area of the 4-step as shown in Table 4 below. The second adhesive layer 120 material having a thickness of 50 mu m was obtained by the UV irradiation.

Zone 1Zone 1 Zone 2Zone 2 Zone 3Zone 3 Zone 4Zone 4 Intensity(mW/cm2)Intensity (mW / cm 2 ) 3.03.0 5.05.0 6.06.0 6.06.0 Residence time(s)Residence time (s) 4545 4545 4545 4545

상기 제조된 제 2 점착층 물질을 상기 필름형태의 시트(101)에 도포하여 제 2 점착층(120)을 형성함으로써 양면 점착 테이프를 제조한 후 이들을 각각 비교예 1 내지 4 및 실시예 1 내지 25라고 하였다.
The thus-prepared second adhesive layer material was applied to the film-form sheet 101 to form a second adhesive layer 120 to obtain double-faced pressure-sensitive adhesive tapes, which were then respectively packed into Comparative Examples 1 to 4 and Examples 1 to 25 .

<평가><Evaluation>

상기 비교예 1 내지 4 및 실시예 1 내지 25에서 제조에 사용된 점착성 고분자에 대하여 분자량을 측정하고, 60℃에서의 분리시간 및 전단강도를 측정하였다. The molecular weight of the adhesive polymer used in the preparation of Comparative Examples 1 to 4 and Examples 1 to 25 was measured and the separation time and shear strength at 60 ° C were measured.

전단강도(Shear Strength)는 Al 스트립과 SUS 패널 사이에 점착제를 배치한 후 10mm/min의 cross-head speed로 측정하였다.Shear Strength was measured by placing a pressure-sensitive adhesive between the Al strip and the SUS panel followed by a cross-head speed of 10 mm / min.

구체적으로, 상기 양면 점착 테이프를 1"x1"로 잘라 샘플을 만들어서 60℃의 온도에서 전단강도를 측정하였다.Specifically, the double-faced pressure-sensitive adhesive tape was cut into 1 " x 1 " samples to measure the shear strength at a temperature of 60 캜.

도 7에서 보는 바와 같이, 상기 샘플의 제 2 점착층(120)이 Al 스트립에 접착하도록 상기 샘플을 Al 스트립에 적층하였다. 상기 Al의 두께는 1.3mm, 폭은 28mm 이다. 상기 샘플의 타면을 SUS 패널 (SUS: 0.8mm x 75mm x 75mm)에 접착시켰다. 이때 제 1 점착층(110)이 SUS 패널에 접착되었다. 상기 SUS 패널은 스테인리스 스틸 패널을 의미한다.As shown in FIG. 7, the sample was laminated on the Al strip so that the second adhesive layer 120 of the sample adhered to the Al strip. The thickness of the Al is 1.3 mm and the width is 28 mm. The other side of the sample was bonded to an SUS panel (SUS: 0.8 mm x 75 mm x 75 mm). At this time, the first adhesive layer 110 was bonded to the SUS panel. The SUS panel means a stainless steel panel.

상기 적층된 샘플은 60℃, 1Mpa 에서 20분간 유지되면서 접착(auto clave)이 이루어졌다. 상기 적층된 샘플을 60℃의 대류챔버(air convection chamber; provided by Instron)에 배치하고, 상기 양면 점착 테이프의 접착면에 대하여 수평이지만 방향이 서로 상반되는 힘을 10mm/min의 cross-head speed로 각각 SUS(스테인리스 스틸) 패널과 알루미늄 스트립에 가하였다. 상기 상반되는 힘을 가하면서, 10분간 응력-변형율(stress-strain) 커브를 측정하여, 최대 응력을 전단강도로 하였다(도 8 참조).The laminated sample was held at 60 DEG C and 1 Mpa for 20 minutes to perform an auto clave. The laminated sample was placed in an air convection chamber (provided by Instron) at 60 ° C, and a force was applied to the adhesive surface of the double-sided adhesive tape at a cross-head speed of 10 mm / min Were added to SUS (stainless steel) panels and aluminum strips, respectively. The stress-strain curve was measured for 10 minutes while applying the opposite force, and the maximum stress was the shear strength (see FIG. 8).

분리 시간은 60℃의 온도에서 도 9에서와 같이 측정하였다. The separation time was measured at a temperature of 60 DEG C as in FIG.

구체적으로, 상기 양면 점착 테이프를 47mm x 62mm의 크기(면적 4.5 inch2)로 잘라서 샘플을 만들었다. 상기 샘플의 제 2 점착층(120)이 PMMA/PC 플레이트와 접착하도록 적층하였다. 여기서 상기 PMMA/PC 플레이트는 Luplion® MR58(from MGC filsheet Co., Ltd) 이며, 크기는 52mm x 70mm x 0.8mm(두께) 이다. 또한 상기 샘플의 제 1 점착층이 SUS 패널(SUS: 0.8mm x 75mm x 75mm)과 접착되도록 적층하였다.Specifically, the double-faced pressure-sensitive adhesive tape was cut into a size of 47 mm x 62 mm (area 4.5 inch 2 ) to prepare a sample. And the second adhesive layer 120 of the sample was laminated so as to adhere to the PMMA / PC plate. The PMMA / PC plate is a Luplion (R) MR58 (from MGC Filsheet Co., Ltd.), and the size is 52mm x 70mm x 0.8mm (thickness). Further, the first adhesive layer of the sample was laminated so as to be bonded to an SUS panel (SUS: 0.8 mm x 75 mm x 75 mm).

상기 적층된 샘플은 60℃, 1Mpa 에서 20분간 유지되면서 접착(auto clave)이 이루어졌다. 이어 상기 적층된 샘플을 60℃의 대류챔버(air convection chamber; provided by Instron)에 배치하고 상기 1Kg 또는 3Kg의 하중을 각각 상기 PMMA/PC 플레이트에 인가한 후 분리 시간을 측정하였다. 이때 1Kg의 하중을 인가하여 제2점착층이 분리되지 않을 경우, 3Kg의 하중으로 변경하여 분리시간을 측정하였다.The laminated sample was held at 60 DEG C and 1 Mpa for 20 minutes to perform an auto clave. The laminated sample was placed in an air convection chamber (provided by Instron) at 60 ° C, and the load of 1 Kg or 3 Kg was applied to the PMMA / PC plate, respectively, and the separation time was measured. At this time, when the 1 Kg load was applied and the second adhesive layer could not be separated, the load was changed to 3 Kg and the separation time was measured.

그 결과를 표 5 및 표 6에 각각 기재하였다. The results are shown in Table 5 and Table 6, respectively.

분리시간 (min) (1kgf 인가 기준)Separation time (min) (Based on 1kgf application) 전단강도 (kgf/in2)Shear strength (kgf / in 2 ) 실시예 1Example 1 9090 22 실시예 2Example 2 3535 1.51.5 실시예 3Example 3 1919 0.90.9 실시예 4Example 4 1313 0.70.7 실시예 5Example 5 99 0.80.8 실시예 6Example 6 88 0.50.5 실시예 7Example 7 44 0.30.3 실시예 8Example 8 21.521.5 1.21.2 실시예 9Example 9 1.51.5 0.250.25 실시예 10Example 10 0.50.5 0.080.08 실시예 11Example 11 28.128.1 1.31.3 실시예 12Example 12 34.734.7 1.31.3 실시예 13Example 13 47.547.5 1.61.6 실시예 14Example 14 80.980.9 1.81.8 실시예 15Example 15 46.746.7 1.61.6 실시예 16Example 16 1515 1One 실시예 17Example 17 10.910.9 0.80.8 실시예 18Example 18 33 0.40.4 실시예 19Example 19 377377 33 실시예 20Example 20 220220 2.52.5 실시예 21Example 21 306306 2.12.1

분리시간 (min)Separation time (min) 전단강도 (kgf/in2)Shear strength (kgf / in 2 ) 실시예 22Example 22 808 (1kgf)808 (1kgf) 38.6 (3kgf)38.6 (3kgf) 2.62.6 실시예 23Example 23 1420 (1kgf)1420 (1kgf) 49.7 (3kgf)49.7 (3kgf) 3.13.1 실시예 24Example 24 분리되지 않음(1kgf)Not separated (1kgf) 228 (3kgf)228 (3kgf) 11.111.1 실시예 25Example 25 분리되지 않음(1kgf)Not separated (1kgf) 520.5 (3kgf)520.5 (3kgf) 15.415.4 비교예 1Comparative Example 1 분리되지 않음(1kgf)Not separated (1kgf) 분리되지 않음 (3kgf)Not detached (3kgf) 18.918.9 비교예 2Comparative Example 2 분리되지 않음(1kgf)Not separated (1kgf) 분리되지 않음 (3kgf)Not detached (3kgf) 20.220.2 비교예 3Comparative Example 3 분리되지 않음(1kgf)Not separated (1kgf) 분리되지 않음 (3kgf)Not detached (3kgf) 19.919.9 비교예 4Comparative Example 4 분리되지 않음(1kgf)Not separated (1kgf) 분리되지 않음 (3kgf)Not detached (3kgf) 19.319.3

상기에서 표 5와 표 6에서 보는 바와 같이, 연쇄전달제(chain transfer agent), 중합억제제, 저분자량 첨가제, 및 경화제 중 적어도 하나를 적당량 포함하는 경우 제 2 점착층(120)의 전단강도가 낮고 분리시간도 적어져, 접착면에 대하여 수평인 방향으로 힘을 가할 경우 제 2 점착층이 용이하게 분리될 수 있다.As shown in Table 5 and Table 6 above, when an appropriate amount of at least one of a chain transfer agent, a polymerization inhibitor, a low molecular weight additive, and a curing agent is contained in an appropriate amount, the shear strength of the second adhesive layer 120 is low The separation time is reduced, and when the force is applied in the horizontal direction with respect to the adhesive surface, the second adhesive layer can be easily separated.

특히 본원 실시예 1 내지 25는, PMMA/PC 플레이트와 제2 점착층을 인위적으로 분리시, 이들의 원래 형태를 유지하면서 떨어지는 응집파괴(cohesion failure)가 일어나는 반면, 비교예 1 내지 4에서는 PMMA/PC 플레이트와 제2 점착층을 서로 손상시키며 떨어지는 접착 파괴(adhesion failure)가 발생하였다. 따라서 본 발명의 양면 점착 테이프는 구성 부품을 서로 안정적으로 부착시킬 수 있으면서도, 또한 필요한 경우 용이하게 박리되어 재작업성을 향상시킬 수 있음을 알 수 있다. Particularly, in Examples 1 to 25 of the present invention, when the PMMA / PC plate and the second adhesive layer were artificially separated, cohesion failure occurred while maintaining their original shape, whereas in Comparative Examples 1 to 4, PMMA / The PC plate and the second adhesive layer were damaged with each other, and a falling adhesion failure occurred. Therefore, it can be seen that the double-sided pressure-sensitive adhesive tape of the present invention can stably attach the constituent parts to each other, and can easily peel off if necessary to improve reworkability.

100: 양면 점착 테이프 101: 필름형태의 시트
102: 보조필름시트 110: 제 1 점착층
120: 제 2 점착층 130: 제3 점착층
310: 투명플레이트 320: 디스플레이 패널100: double-sided adhesive tape 101: sheet in film form
102: auxiliary film sheet 110: first adhesive layer
120: second adhesive layer 130: third adhesive layer
310: transparent plate 320: display panel

Claims (16)

필름형태의 시트;
상기 시트의 일면에 배치된 제 1 점착층; 및
상기 시트의 타면에 배치된 제 2 점착층을 포함하며;
여기서, 상기 제 2 점착층의 전단강도(Shear Strength)는, 60℃의 온도에서 알루미늄 스트립 및 SUS 패널을 사용한 cross-head 속도가 10mm/min인 조건일 때 0.05 내지 16 Kg/in2이고,
상기 제 1 점착층의 전단강도는 상기 제 2 점착층의 전단강도보다 같거나 큰 것을 특징으로 하는 양면 점착 테이프.Sheet in film form;
A first adhesive layer disposed on one side of the sheet; And
And a second adhesive layer disposed on the other side of the sheet;
Here, the shear strength of the second adhesive layer is 0.05 to 16 Kg / in 2 at a cross-head speed of 10 mm / min using an aluminum strip and an SUS panel at a temperature of 60 ° C,
Wherein the shear strength of the first adhesive layer is greater than or equal to the shear strength of the second adhesive layer. 삭제delete 제 1항에 있어서, 상기 제 2 점착층은, 60℃의 온도에서 PMMA/PC 플레이트와 SUS 패널을 사용한 4.5 in2의 면적에 1Kg의 하중이 인가 될 때의 분리시간이 20초 이상이고, 3Kg의 하중이 인가될 때의 분리시간이 600분 이하인 것을 특징으로 하는 양면 점착 테이프.The method according to claim 1, wherein the second adhesive layer has a separation time of 20 seconds or more when a load of 1 kg is applied to an area of 4.5 in 2 using a PMMA / PC plate and a SUS panel at a temperature of 60 캜, Sensitive adhesive tape according to claim 1, wherein a separation time when a load of the adhesive tape is applied is 600 minutes or less. 제 1항에 있어서, 상기 필름형태의 시트는 아크릴계 수지, 폴리에스테르 수지, 폴리카보네이트 수지, 노르보넨계 수지, 올레핀 중합체 및 TAC(triacetyl cellulose)로 이루어진 군에서 선택되는 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 1, wherein the film-form sheet is selected from the group consisting of an acrylic resin, a polyester resin, a polycarbonate resin, a norbornene resin, an olefin polymer, and TAC (triacetyl cellulose). 제 1항에 있어서, 상기 필름형태의 시트는 폴리에틸렌 테레프탈레이트(PET)인 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 1, wherein the film-like sheet is polyethylene terephthalate (PET). 제 1항에 있어서, 상기 필름형태의 시트의 두께는 5 ㎛ 내지 100 ㎛ 인 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 1, wherein the film-shaped sheet has a thickness of 5 to 100 탆. 제 1항에 있어서, 상기 필름형태의 시트의 광 투과율은 90% 이상인 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 1, wherein the film-form sheet has a light transmittance of 90% or more. 제 1항에 있어서, 제 1 점착층과 제 2 점착층의 두께는 각각 5 ㎛ 내지 500 ㎛ 범위 내에 있는 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 1, wherein the thicknesses of the first adhesive layer and the second adhesive layer are in the range of 5 탆 to 500 탆, respectively. 제 1항에 있어서, 상기 제 2 점착층은 점착성 고분자 조성물에 의하여 형성되는데,
상기 점착성 고분자 조성물은 모노머, 및 중합개시제를 포함하며, 연쇄전달제(chain transfer agent), 중합억제제(retardant), 및 저분자량 첨가제 및 경화제 중 적어도 하나를 추가로 포함하는 것을 특징으로 하는 양면 점착 테이프.The method of claim 1, wherein the second adhesive layer is formed of a sticky polymer composition,
Wherein the adhesive polymer composition comprises a monomer and a polymerization initiator and further comprises at least one of a chain transfer agent, a polymerization inhibitor, and a low molecular weight additive and a curing agent. . 제 9항에 있어서, 모노머 100 중량부에 대하여, 상기 연쇄전달제 0.03 내지 5 중량부, 중합억제제 0.01 내지 0.5 중량부 및 저분자량 첨가제 1 내지 50 중량부 중 적어도 하나를 포함하는 것을 특징으로 하는 양면 점착 테이프.10. The composition of claim 9, wherein the composition comprises at least one of 0.03 to 5 parts by weight of the chain transfer agent, 0.01 to 0.5 parts by weight of a polymerization inhibitor, and 1 to 50 parts by weight of a low molecular weight additive, based on 100 parts by weight of the monomer Adhesive tape. 제 1항에 있어서, 상기 제 2 점착층에서 필름형태의 시트가 배치된 면의 반대면에는 보조필름 시트가 추가로 배치되어 있으며, 상기 보조필름 시트에는 제 3 점착층이 배치되어 있는 것을 특징으로 하는 양면 점착 테이프.The method according to claim 1, wherein an auxiliary film sheet is additionally disposed on a surface opposite to a surface on which the film-shaped sheet is disposed in the second adhesive layer, and a third adhesive layer is disposed on the auxiliary film sheet Double-sided adhesive tape. 제 11항에 있어서, 상기 제 3 점착층의 전단강도는 상기 제 2 점착층의 전단강도보다 큰 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 11, wherein the shear strength of the third adhesive layer is larger than the shear strength of the second adhesive layer. 제 1항에 있어서, 광투과율이 90% 이상인 것을 특징으로 하는 양면 점착 테이프.The double-faced pressure-sensitive adhesive tape according to claim 1, wherein the light transmittance is 90% or more. 디스플레이 패널;
상기 디스플레이 패널의 디스플레이 표시면에 배치된 양면 점착 테이프; 및
상기 양면 점착 테이프에 배치된 투명 플레이트를 포함하며,
상기 양면 점착 테이프는 제1항, 제3항 내지 제13항 중 어느 한 항에 의한 것임을 특징으로 하는 디스플레이 장치.A display panel;
A double-sided adhesive tape disposed on a display screen of the display panel; And
And a transparent plate disposed on the double-sided adhesive tape,
Wherein the double-sided adhesive tape is according to any one of claims 1 to 13. 제14항에 있어서, 상기 투명 플레이트는 전자기기의 커버 윈도우인 것을 특징으로 하는 디스플레이 장치.15. The display device according to claim 14, wherein the transparent plate is a cover window of an electronic device. 제14항에 있어서, 상기 투명 플레이트는 터치패널인 것을 특징으로 하는 디스플레이 장치.15. The display device according to claim 14, wherein the transparent plate is a touch panel.
KR1020110080096A 2010-12-31 2011-08-11 Double-sided adhesive tape having improved reworkability KR101946065B1 (en)