KR101935742B1 - Manufacture method of lawn grass protecting mat - Google Patents

Manufacture method of lawn grass protecting mat Download PDF

Info

Publication number
KR101935742B1
KR101935742B1 KR1020180091345A KR20180091345A KR101935742B1 KR 101935742 B1 KR101935742 B1 KR 101935742B1 KR 1020180091345 A KR1020180091345 A KR 1020180091345A KR 20180091345 A KR20180091345 A KR 20180091345A KR 101935742 B1 KR101935742 B1 KR 101935742B1
Authority
KR
South Korea
Prior art keywords
weight
grass
parts
protection mat
lawn
Prior art date
Application number
KR1020180091345A
Other languages
Korean (ko)
Inventor
윤안식
제해득
박다솜
Original Assignee
제해득
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 제해득 filed Critical 제해득
Priority to KR1020180091345A priority Critical patent/KR101935742B1/en
Application granted granted Critical
Publication of KR101935742B1 publication Critical patent/KR101935742B1/en

Abstract

The present invention relates to a manufacturing method of a grass protection mat which is for use of protecting grass and consists of a plastic material. The manufacturing method of a grass protection mat comprises the step of: (A) producing a composition for the grass protection mat; and (B) producing the grass protection mat, and has properties such as abrasion resistance, dimensional stability, tensile strength and the like.

Description

잔디보호매트 제조방법{MANUFACTURE METHOD OF LAWN GRASS PROTECTING MAT}TECHNICAL FIELD [0001] The present invention relates to a grass protection mat,

본 발명은 잔디보호매트의 제조방법에 관한 것으로서, 더욱 상세하게는 폴리프로필렌계 합성수지를 주재료로 하여 제조되며 잔디의 식생공간을 확보함과 더불어 내구성 등 성능을 향상시킬 수 있도록 함은 물론 사용수명을 높일 수 있도록 하고 잔디보호매트로서 지녀야 할 품질기준을 만족시킬 수 있도록 한 잔디보호매트 제조방법에 관한 것이다.More particularly, the present invention relates to a method for manufacturing a grass protection mat, and more particularly, to a method for manufacturing a grass protection mat, which is manufactured using polypropylene-based synthetic resin as a main material and secures a vegetation space for lawn, And to a method for manufacturing a grass protection mat that can satisfy a quality standard to be possessed as a grass protection mat.

일반적으로 골프장, 공원, 잔디광장, 잔디구장, 학교, 잔디녹화공간, 연약지반, 산책로 등 잔디생육지역에서 생육되는 잔디는 다수의 이용자나 차량 등에 의해 지속적인 밟힘이 이루어지므로 손상되기 쉬우며, 손상된 잔디의 개보수를 위해서는 비용이 상당하게 소요된다.Generally, grasses grown in a grass growing area such as a golf course, a park, a lawn square, a grass field, a school, a lawn recording space, a soft ground, a walking path, etc. are susceptible to damage due to continuous stepping by a large number of users and vehicles, The cost of renovation is considerable.

이에, 최근에는 다수의 이용자나 차량 등의 잦은 통행으로 인해 잔디가 손상되는 것을 방지하도록 잔디보호매트를 깔아 배치하는 방식으로 잔디를 보호하고 있다.Recently, a grass protection mat is laid out to protect the lawn from being damaged due to frequent passage of a large number of users and vehicles.

이와 같이, 잔디생육지역에 설치되어 잔디의 보호에 사용되는 종래 잔디보호매트는 대부분이 잔디통과공간이 형성되는 바디부와, 상기 바디부의 하부에 구비되어 바디부에 가해지는 하중을 지지 및 완충하도록 하는 탄성력을 갖는 완충부재를 포함하는 구성으로 이루어진다.As described above, the conventional grass protection mat, which is installed in the grass growing area and used for protecting the lawn, is provided with a body part in which most of the lawn passage space is formed and a lower part provided under the body part to support and buffer the load applied to the body part. And a cushioning member having an elastic force.

하지만, 종래 잔디보호매트는 표면 균열이나 갈라짐은 물론 뒤틀리거나 변형되고 때로는 쉽게 파손되고 절단되는 등 내구성이 떨어지는 문제점이 있어 개선이 요구되고 있는 실정에 있다.However, the conventional lawn mats have problems in that they are not durably deformed as they are twisted or deformed as well as surface cracks and cracks, and sometimes are easily broken and cut.

또한 잔디보호매트로서 지녀야 할 품질기준을 만족시키지 못하는 제품들이 사용되기도 하며, 종래 잔디보호매트는 미끄럽고 치수 변경이 발생함은 물론 저온에서 쉽게 취화(embrittlement)되어 크랙이 발생하는 등의 문제점이 있었다.Also, products which do not satisfy the quality standards to be used as the grass protection mat are used. In addition, the conventional grass protection mat is slippery, has a problem of dimensional change, and is easily embrittlement at low temperature to cause cracks.

한편, 종래 잔디보호매트 관련 선행기술문헌에 있어 국내등록특허 제10-1755568호나 제10-1769737호 등을 비롯한 대다수의 개시된 잔디보호매트들은 잔디 보호를 위한 구조적인 형상에만 주안점을 두고 개발하는 유형들을 보여주고 있다.In the prior art related to the grass protection mat in the related art, most of the lawn protection mats disclosed in Korean Patent No. 10-1755568, No. 10-1769737, etc., .

대한민국 등록특허공보 제10-1755658호Korean Patent Registration No. 10-1755658 대한민국 등록특허공보 제10-1769737호Korean Patent Publication No. 10-1769737

본 발명은 상술한 종래의 문제점을 해소 및 이를 감안하여 안출된 것으로서, 폴리프로필렌계 합성수지를 주재료로 하여 제조되는 플라스틱재 잔디보호매트를 제공하되 잔디의 생육공간을 확보함과 더불어 내구성 등 성능을 향상시킬 수 있도록 하고 사용수명을 높일 수 있도록 한 잔디보호매트 제조방법을 제공하는데 그 목적이 있다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made to solve the above-mentioned problems of the prior art and to provide a plastic lawn protection mat manufactured using polypropylene-based synthetic resin as a main material, The present invention provides a method of manufacturing a grass protection mat, which can increase the service life of the grass protection mat.

본 발명은 폴리프로필렌계 합성수지를 비롯한 첨가원료의 적합한 조성과 물성을 이용하여 내마모성, 치수안정성, 인장강도, 미끄럼 방지 및 자외선 차단 등의 성능을 확보 및 기능성을 구비할 수 있도록 하며, 뒤틀림이나 변형 및 파손과 절단 등의 단점을 개선함과 더불어 잔디보호매트로서 지녀야 할 기계적 물성 등의 품질기준을 만족시킬 수 있도록 한 잔디보호매트 제조방법을 제공하는데 그 목적이 있다.The present invention uses a suitable composition and physical properties of a polypropylene-based synthetic resin to make it possible to ensure performance such as abrasion resistance, dimensional stability, tensile strength, anti-slip and ultraviolet shielding, It is an object of the present invention to provide a grass protection mat manufacturing method which can improve the disadvantages such as breakage and cutting, and satisfy the quality standards such as mechanical properties to be possessed as a grass protection mat.

상기의 목적을 달성하기 위한 본 발명에 따른 잔디보호매트 제조방법은, 잔디의 식생 구역상에 설치되어 식생되는 잔디를 보호하는데 사용하기 위한 용도이고, 플라스틱 재질로 이루어지는 잔디보호매트 제조방법에 있어서, (A) 뒤틀림, 변형, 파손 및 절단되는 단점을 개선함과 더불어 성능을 향상시킬 수 있도록 하기 위해 폴리프로필렌 수지를 주재료로 하는 잔디보호매트용 조성물을 제조하는 단계; (B) 상기 잔디보호매트용 조성물을 사출 성형함에 의해 사각 격자배열구조에 의한 잔디식생공간을 확보한 식생부를 포함하는 잔디보호매트로 제조하는 단계; 를 포함하되, 상기 (A)단계에서는 폴리프로필렌 수지 50중량부에 대해서 무수말레인산으로 개질된 알파-올레핀 공중합체 5 내지 30중량부, 무수말레인산으로 개질된 스티렌계 블록 공중합체 1 내지 25중량부를 포함하는 혼합 조성으로 하여 펠렛으로 제조하는 단계; 및 폴리프로필렌 수지 50중량부에 대해서 기능성 첨가제 3 내지 140중량부를 포함하는 혼합 조성으로 하여 마스터배치를 제조하는 단계; 를 포함하고, 상기 (B)단계에서는 상기 펠렛과 마스터배치를 용융 혼합 및 사출하는 단계; 및 상기 사출되는 잔디보호매트 조성물에 대해 일정 형태를 갖는 판상형의 잔디보호매트로 성형하는 단계; 를 포함하는 것을 특징으로 한다.According to another aspect of the present invention, there is provided a method for manufacturing a grass protection mat comprising the steps of: (A) preparing a composition for a lawn protective mat using polypropylene resin as a main material in order to improve defects such as twisting, deformation, breakage and cutting, and to improve performance; (B) fabricating a grass protection mat including a vegetation part securing a grass vegetation space by a rectangular grid arrangement structure by injection molding the composition for lawn protection mat; 5 to 30 parts by weight of an alpha-olefin copolymer modified with maleic anhydride, and 1 to 25 parts by weight of a styrene block copolymer modified with maleic anhydride are contained in 50 parts by weight of the polypropylene resin in the step (A) To form a pellet; And 3 to 140 parts by weight of a functional additive to 50 parts by weight of a polypropylene resin; Mixing the pellet and the master batch in the step (B); And shaping the grass protection mat into a sheet-like grass protection mat having a predetermined shape with respect to the grass protection mat composition; And a control unit.

여기에서, 상기 펠렛과 마스터배치를 용융 혼합 및 사출하는 단계에서는 사출기본체의 내부로 고음압용 초음파 펄스를 인가함으로써 사출기본체 내 형성되는 압력을 감소시켜 부하를 최소화함과 더불어 분산성을 높여줄 수 있도록 하며 용융 혼합 및 사출효율을 높일 수 있도록 처리할 수 있다.Here, in the step of melt mixing and injecting the pellet and the master batch, by applying an ultrasonic pulse for high sound pressure to the interior of the injector body, the pressure formed in the injector body is reduced to minimize the load and increase the dispersibility And can be processed to increase melt mixing and injection efficiency.

여기에서, 상기 무수말레인산으로 개질된 알파-올레핀계 공중합체는 분자량 48000~100000이고 밀도 0.9~0.925g/㎤이며 용융지수 10~25g/10min인 무수말레인산 1~10중량%를 첨가하여 그래프팅 반응에 의한 개질을 수행한 것으로서, 유리전이온도가 0℃ 이하이고 결정화도가 35% 이하이며; 상기 알파 올레핀계 공중합체는 에틸렌-옥텐 공중합체, 에틸렌 부텐 공중합체, 에틸렌 비닐알코올 공중합체, 에틸렌 초산비닐 공중합체 중에서 선택된 어느 1군으로 구성할 수 있다.Here, the alpha-olefin-based copolymer modified with maleic anhydride has a molecular weight of 48,000 to 100,000, a density of 0.9 to 0.925 g / cm 3, and a melt index of 10 to 25 g / 10 min to 1 to 10% by weight of maleic anhydride, , Wherein the glass transition temperature is 0 占 폚 or less and the crystallinity is 35% or less; The alpha olefin-based copolymer may be composed of any one group selected from ethylene-octene copolymer, ethylene butene copolymer, ethylene vinyl alcohol copolymer and ethylene-vinyl acetate copolymer.

여기에서, 상기 무수말레인산으로 개질된 스티렌계 블록 공중합체는 분자량 48000~100000이고 밀도 0.9~0.925g/㎤이며 용융지수 10~25g/10min인 무수말레인산 1~5중량%를 첨가하여 그래프팅 반응에 의한 개질을 수행한 것으로서, 유리전이온도가 110~150℃이고 결정화도가 60~85%이며; 상기 스티렌계 블록 공중합체는 스티렌-부타디엔-스티렌(SBS), 스티렌-에틸렌-부타디엔-스티렌(SEBS), 스티렌-에틸렌-프로필렌-스티렌(SEPS), 스티렌-이소프로필렌-스티렌(SIS) 중에서 선택된 어느 1군일 수 있다.Here, the styrene block copolymer modified with maleic anhydride has a molecular weight of 48,000 to 100,000, a density of 0.9 to 0.925 g / cm 3 and a melt index of 10 to 25 g / 10 min, and 1 to 5% by weight of maleic anhydride is added to the grafting reaction. Wherein the glass transition temperature is from 110 to 150 DEG C and the crystallinity is from 60 to 85%; The styrenic block copolymer may be any one selected from styrene-butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEBS), styrene-ethylene-propylene-styrene (SEPS), and styrene- Group.

여기에서, 상기 폴리프로필렌 수지는 폴리프로필렌 단일중합체, 폴리프로필렌 랜덤 공중합체, 폴리프로필렌 블록 공중합체, 폴리프로필렌과 폴리에틸렌의 화합물 중에서 선택된 어느 1군이며; 중량평균분자량 80000~1000000이고 용융지수 10~100g/10mim일 수 있다.Here, the polypropylene resin is any one group selected from the group consisting of a polypropylene homopolymer, a polypropylene random copolymer, a polypropylene block copolymer, a polypropylene and a polyethylene; A weight average molecular weight of 80000 to 1000000 and a melt index of 10 to 100 g / 10 mm.

여기에서, 상기 기능성 첨가제는, 치수안정제, 미끄럼방지제, 자외선차단제, 무기난연제 중에서 선택된 적어도 1군 이상이 사용될 수 있다.The functional additive may be at least one selected from the group consisting of a dimension stabilizer, an anti-slip agent, an ultraviolet screening agent, and an inorganic flame retardant.

여기에서, 상기 치수안정제는 몬모릴로나이트, 벤토나이트, 마이카, 버미큘라이트, 울라스토나이트 중에서 선택된 어느 1군 이상을 사용하되, 폴리프로필렌 수지 100중량부에 대해서 10~40중량부를 첨가할 수 있다.Here, any one or more selected from the group consisting of montmorillonite, bentonite, mica, vermiculite and wollastonite may be used as the dimension stabilizer, and 10 to 40 parts by weight may be added to 100 parts by weight of the polypropylene resin.

여기에서, 상기 미끄럼방지제는 미끄럼방지와 더불어 내오존성, 내마모성, 내후성, 내열성, 내한성의 기능을 확보하도록 스티렌부타디엔, 폴리우레탄, 니트릴, 부틸, 부타디엔, 에틸렌프로필렌의 고무계 재질 중에서 선택된 어느 1군 이상을 사용하되, 폴리프로필렌수지 100중량부에 대해서 5~20중량부를 첨가할 수 있다.Here, the antiskid agent is preferably at least one selected from the group consisting of styrene butadiene, polyurethane, nitrile, butyl, butadiene, and ethylene propylene rubber materials in order to ensure the functions of ozone resistance, abrasion resistance, weather resistance, But may be added in an amount of 5 to 20 parts by weight based on 100 parts by weight of the polypropylene resin.

여기에서, 상기 자외선차단제는 이산화티타늄, 산화아연, 호모살레이트, 아보벤젠, 옥틸메톡시신나메이트, 에칠헥실메톡시신나메이트, 옥시녹세이트, 옥토크릴, 옥시벤존 중에서 선택된 어느 1군 이상을 사용하되, 폴리프로필렌수지 100중량부에 대해서 5~25중량부를 첨가할 수 있다.The ultraviolet light blocking agent may be at least one selected from titanium dioxide, zinc oxide, homosalate, avobenzene, octylmethoxycinnamate, ethylhexylmethoxycinnamate, oxynosate, octocryl and oxybenzone 5 to 25 parts by weight based on 100 parts by weight of the polypropylene resin may be added.

여기에서, 상기 소음 조절제는 압축 탄성 및 복원력이 가능하도록 알루미늄 실리케이트 원형 중공체를 사용하되, 폴리프로필렌수지 100중량부에 대해서 3~20중량부를 첨가할 수 있다.Here, the noise control agent is an aluminum silicate circular hollow body so as to be capable of compressive elasticity and restoring force, and 3 to 20 parts by weight may be added to 100 parts by weight of the polypropylene resin.

여기에서, 상기 잔디보호매트는, 연속되는 사각 격자배열구조로 이루어지는 베이스프레임틀; 상기 베이스프레임틀이 갖는 격자들 사이에 형성되고 잔디통과공간을 형성하는 잔디식생공간; 상기 베이스프레임틀의 하부에서 하측방향으로 돌출되고 상부에서 가해지는 하중에 대해 완충기능을 발휘하도록 구비 및 간격 배열되는 제1완충돌부; 상기 베이스프레임틀의 하부에서 하측방향으로 돌출되고 상기 제1완충돌부와 함께 상부에서 가해지는 하중에 대해 완충기능을 발휘하도록 구비 및 간격 배열되는 제2완충돌부; 상기 베이스프레임틀의 외곽에 구비되고 이웃하는 두 측면 상에 외측방향으로 돌출되어 잔디보호매트간의 연결에 사용되는 고리형 연결부; 상기 베이스프레임틀의 네 모서리 부분 내측에 고정핀 등의 고정부재 삽입에 의한 지면 고정력을 제공하는데 사용되는 핀고정부; 상기 베이스프레임틀의 상부에서 상측방향으로 돌출되고 잔디줄기 형태로 촘촘하게 배치되는 잔디보호돌부;를 포함하도록 구성할 수 있다.Here, the grass protection mat may include: a base frame frame having a continuous rectangular grid arrangement; A grass vegetation space formed between the lattices of the base frame frame and forming a grass passage space; A first full collision portion protruding downward from a lower portion of the base frame frame and arranged and spaced apart to exert a buffer function against a load applied at an upper portion thereof; A second full collision portion protruding downward from a lower portion of the base frame frame and arranged and spaced apart to exert a buffer function against a load applied at an upper portion together with the first full collision portion; An annular connecting portion provided on an outer periphery of the base frame frame and protruding outwardly on two adjacent sides to be used for connection between the lawn protection mats; A pinching portion used to provide a ground fixing force by inserting fixing members such as fixing pins into four corner portions of the base frame frame; And a grass protrusion protruding upward from an upper portion of the base frame frame and closely arranged in the form of a grass stem.

여기에서, 상기 베이스프레임틀은 전체적으로 사각형상의 몸체를 갖되 사각형을 이루는 단위격자가 반복 배열되는 구성으로서, 상기 사각형 단위격자마다 서로 이격되는 이중 프레임틀 구조로 형성하여 잔디의 통과가 가능하도록 구비되며; 상기 이중 프레임틀의 각 상면에서 잔디보호돌부를 이중 구조로 돌출 형성하며; 상기 제1완충돌부는 사각 배열구조를 갖도록 간격 배치하되, 내부가 비어있고 원형 둘레의 외주연을 갖는 원통몸체로서, 상기 원통몸체의 비어있는 내부에 십자형 구조의 연결지지부가 연결 구비되며; 상기 제2완충돌부는 원기둥의 형태로 이루어지고, 상기 제1완충돌부에 이웃하여 사방 배치 및 상기 제1완충돌부의 간격 배치되는 사이사이에 돌출 형성되는 구성을 갖게 할 수 있다.Here, the base frame frame may have a rectangular frame body, and a rectangular unitary grid may be repeatedly arranged. The base frame frame may have a double frame structure spaced apart from each other for each rectangular unit grid, A grass protection protrusion protruding from each upper surface of the double frame frame in a double structure; Wherein the first free end collision portion is spaced apart from the first free end portion to have a rectangular array structure, the hollow cylindrical body having an outer periphery and an outer periphery with a circular periphery, the hollow support portion having a cross- The second full impact portion may have a cylindrical shape and may protrude from the space between the first full impact portion and the first full impact portion adjacent to the first full impact portion.

본 발명에 따르면, 폴리프로필렌계 합성수지를 주재료로 하여 제조되는 플라스틱재 잔디보호매트를 제공할 수 있으며, 잔디의 생육공간을 확보함과 더불어 내구성 등 성능을 향상시킬 수 있음은 물론 사용수명을 높일 수 있는 잔디보호매트를 제조할 수 있다.According to the present invention, it is possible to provide a plastic lawn protecting mat manufactured using polypropylene-based synthetic resin as a main material, to secure a space for growing grass, to improve performance such as durability, A grass protection mat can be manufactured.

본 발명은 폴리프로필렌계 합성수지를 비롯한 첨가원료의 적합한 조성과 물성을 이용하여 내마모성, 치수안정성, 인장강도, 미끄럼 방지 및 자외선 차단 등의 성능을 확보 및 유용한 기능성을 구비할 수 있으며, 뒤틀림이나 변형 및 파손과 절단 등의 단점을 개선할 수 있고 잔디보호매트로서 가져야 할 기계적 물성 등의 품질기준을 만족시킬 수 있으며 중금속 함량이 기준치 이하인 우수한 품질을 갖는 잔디보호매트를 제조할 수 있다.The present invention can provide functionalities such as abrasion resistance, dimensional stability, tensile strength, anti-slip and ultraviolet shielding, and useful functionality by using appropriate composition and physical properties of additives such as polypropylene-based synthetic resin, It is possible to improve the disadvantages such as breakage and cutting and to satisfy the quality standards such as the mechanical properties to be provided as the lawn protection mat and to produce the lawn protection mat having the excellent quality with the heavy metal content below the standard value.

도 1 및 도 2는 본 발명의 실시예에 따른 잔디보호매트 제조방법을 설명하기 위해 나타낸 제조공정도이다.
도 3 및 도 4는 본 발명의 실시예에 따른 잔디보호매트 제조방법에 의해 제조된 잔디보호매트를 나타낸 사시도이다.
도 5 및 도 6은 본 발명의 실시예에 따른 잔디보호매트 제조방법에 의해 제조된 샘플링 제품을 나타낸 사진이다.
FIG. 1 and FIG. 2 are manufacturing process diagrams illustrating a method for manufacturing a grass protection mat according to an embodiment of the present invention.
3 and 4 are perspective views illustrating a grass protection mat manufactured by the method for manufacturing a grass protection mat according to an embodiment of the present invention.
5 and 6 are photographs showing a sampling product manufactured by the method of manufacturing the grass protection mat according to the embodiment of the present invention.

본 발명에 대해 첨부한 도면을 참조하여 바람직한 실시예를 설명하면 다음과 같으며, 이와 같은 상세한 설명을 통해서 본 발명의 목적과 구성 및 그에 따른 특징들을 보다 잘 이해할 수 있게 될 것이다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. The present invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings.

본 발명의 실시예에 따른 잔디보호매트의 제조방법은 잔디의 식생 구역상에 설치되어 식생되는 잔디를 보호하는데 사용하기 위한 것으로서, 도 1에 나타낸 바와 같이, 크게는 잔디보호매트용 조성물 제조단계(S100)와 사출성형단계(S200)를 포함하는 구성으로 이루어진다.The method for manufacturing a lawn protection mat according to an embodiment of the present invention is used for protecting a lawn that is installed on a vegetation area of a lawn so as to protect the lawn. As shown in Fig. 1, S100) and an injection molding step (S200).

상기 잔디보호매트용 조성물 제조단계(S100)는 폴리프로필렌 수지를 주재료로 하는 잔디보호매트용 조성물을 제조하는 단계로서, 도 2에서 보여주는 바와 같이 폴리프로필렌 수지 50중량부에 대해서 무수말레인산으로 개질된 알파-올레핀 공중합체 5 내지 30중량부, 무수말레인산으로 개질된 스티렌계 블록 공중합체 1 내지 25중량부를 포함하는 혼합 조성으로 하여 펠렛으로 제조하는 펠렛제조단계(S110)와, 폴리프로필렌 수지 50중량부에 대해서 기능성 첨가제 3 내지 140중량부를 포함하는 혼합 조성으로 하여 마스터배치를 제조하는 마스터배치 제조단계(S120)로 세분화할 수 있다.As shown in FIG. 2, 50 parts by weight of polypropylene resin is mixed with 50 parts by weight of maleic anhydride-modified maleic anhydride modified alpha 5 to 30 parts by weight of an olefin copolymer, and 1 to 25 parts by weight of a styrene block copolymer modified with maleic anhydride; and a step (S110) of producing a pellet by pelletization, And a master batch production step (S120) of preparing a master batch using a mixed composition comprising 3 to 140 parts by weight of a functional additive.

이때, 상기 기능성 첨가제는 치수안정제, 미끄럼방지제, 자외선차단제, 소음조절제, 열산화방지제 중에서 선택된 어느 1군 이상이 첨가되어 기능성을 구비하는데 사용될 수 있다.At this time, the functional additive may be added to at least one group selected from a dimension stabilizer, an anti-slip agent, an ultraviolet screener, a noise control agent, and a thermal oxidation inhibitor to provide functionality.

상기 주재료로 사용되는 폴리프로필렌 수지는 잔디보호매트를 성형하기 위한 베이스 수지로 사용되고, 기본적으로 높은 기계적 강도와 내열성 및 내구성을 갖는 것으로서, 폴리프로필렌 랜덤 공중합체, 폴리프로필렌 블록 공중합체, 폴리프로필렌과 폴리에틸렌의 화합물 중에서 선택된 어느 1군이 사용될 수 있다.The polypropylene resin used as the main material is used as a base resin for molding a grass protection mat and basically has high mechanical strength, heat resistance and durability, and includes a polypropylene random copolymer, a polypropylene block copolymer, a polypropylene and a polyethylene May be used.

이때, 충격강도와 강성 및 외부 압력에 견디는 외압 특성이 우수한 물성을 갖는 폴리프로필렌 블록 공중합체를 사용하는 것이 더욱 바람직하다 할 수 있다.At this time, it is more preferable to use a polypropylene block copolymer having physical properties excellent in impact strength, stiffness, and external pressure characteristics to withstand external pressure.

여기에서, 폴리프로필렌 랜덤 공중합체는 구조가 유연하고 내구성이 우수한 물성을 활용할 수 있다.Here, the polypropylene random copolymer can utilize physical properties that are flexible in structure and excellent in durability.

여기에서, 상기 폴리프로필렌 수지는 중량평균분자량 80000~1000000이고 용융지수 10~100g/10mim인 것일 수 있다.Here, the polypropylene resin may have a weight average molecular weight of 80000 to 1000000 and a melt index of 10 to 100 g / 10 mm.

여기에서, 상기 중량평균분자량에 있어 최저치 미만일 경우 다른 원료들과의 중합성이 저하될 뿐만 아니라 사출 성형되는 잔디보호매트의 기계적 물성이 저하되며, 최대치를 초과할 경우 용융점도가 높아져 사출 성형성 및 치수 안정성이 떨어질 수 있다.If the weight average molecular weight is less than the lower limit, the polymerizable property with other raw materials is deteriorated and the mechanical properties of the lawn mats to be injection-molded deteriorate. When the maximum value is exceeded, the melt viscosity increases, Dimensional stability may be deteriorated.

상기 용융지수는 230℃ 및 216kg 하중에서 가지는 수치로서, 최저치 미만일 경우 유동성이 약해 사출 성형시 압출을 어렵게 하면서 매트의 형태 유지를 어렵게 하며, 최대치를 초과하는 경우 유동성이 너무 커서 사출 성형성이 오히려 저하될 수 있다.The melt index is a numerical value at a temperature of 230 ° C and 216 kg. When the melt index is below the minimum value, the fluidity is weak, which makes it difficult to maintain the shape of the mat while extrusion is difficult during injection molding. .

이하에서 언급되는 용융지수 또한 특별한 기재가 없는 이상 230℃ 및 216kg 하중에서 가지는 수치라 할 수 있다.The melt index mentioned below is also a numerical value at 230 캜 and 216 kg load unless there is a special substrate.

본 발명에 있어 상기 무수말레인산으로 개질된 알파-올레핀계 공중합체를 통해서는 폴리프로필렌의 저온에서의 내충격성과 유연성을 보완할 수 있다.In the present invention, the alpha-olefin-based copolymer modified with maleic anhydride can complement the impact resistance and flexibility at low temperature of polypropylene.

이때, 상기 무수말레인산으로 개질된 알파-올레핀계 공중합체는 그 함량이 폴리프로필렌 수지 100중량부(총 사용량 기준)에 대하여 5 내지 30 중량부일 때 저온에서의 우수한 내충격성, 유연성, 가공성 및 기계적 강도를 기대할 수 있다.When the content of the alpha-olefin-based copolymer modified with maleic anhydride is 5 to 30 parts by weight based on 100 parts by weight of the polypropylene resin (based on the total amount used), excellent impact resistance, flexibility, processability and mechanical strength Can be expected.

여기에서, 상기 무수말레인산으로 개질된 알파-올레핀계 공중합체에 대해 5중량부 미만일 경우 저온에서의 내충격성과 유연성을 개선하는 효과를 기대하기 어려우며, 30중량부를 초과할 경우 잔디보호매트로서의 가공성 및 기계적 강도를 기대하기 어렵다.If the amount of the alpha-olefin-based copolymer modified with maleic anhydride is less than 5 parts by weight, it is difficult to expect an effect of improving the impact resistance and flexibility at low temperatures. If the amount exceeds 30 parts by weight, Strength is hard to expect.

여기에서, 상기 무수말레인산으로 개질된 알파-올레핀계 공중합체는 그래프트 반응 및 개질 효과를 높이기 위해 분자량 48000~100000이고 밀도 0.9~0.925g/㎤이며 용융지수 10~25g/10min인 무수말레인산 1~10중량%를 첨가하여 그래프팅 반응에 의한 개질을 수행하는 것이 바람직하며, 개질에 의한 인장특성 등의 물성을 증대시킬 수 있음은 물론 폴리프로필렌 수지와의 상용성을 개선할 수 있다.The α-olefin-based copolymer modified with maleic anhydride may have a molecular weight of 48,000 to 100,000, a density of 0.9 to 0.925 g / cm 3, a melt index of 10 to 25 g / 10 min, and a maleic anhydride value of 1 to 10 It is preferable to carry out the modification by the grafting reaction by adding the weight%, and it is possible not only to increase physical properties such as tensile properties by modification, but also to improve the compatibility with the polypropylene resin.

여기에서, 상기 알파 올레핀계 공중합체는 에틸렌-옥텐 공중합체, 에틸렌 부텐 공중합체, 에틸렌 비닐알코올 공중합체, 에틸렌 초산비닐 공중합체 중에서 선택된 어느 1군일 수 있다.Here, the alpha olefin-based copolymer may be any one selected from the group consisting of an ethylene-octene copolymer, an ethylene butene copolymer, an ethylene vinyl alcohol copolymer, and an ethylene-vinyl acetate copolymer.

또한, 상기 무수말레인산으로 개질된 알파-올레핀계 공중합체는 유리전이온도가 0℃ 이하이고 결정화도가 35% 이하인 것이 바람직하며, 잔디보호매트의 저온에서의 내충격성과 유연성이 보완되는 효과를 높일 수 있다.Also, the α-olefin-based copolymer modified with maleic anhydride preferably has a glass transition temperature of 0 ° C. or less and a crystallinity of 35% or less, and can improve the impact resistance and flexibility at low temperature of the lawn protection mat .

만일, 유리전이온도가 0℃를 초과하는 경우 저온에서의 내충격성에 대한 보완 효과를 기대하기 어려우며, 결정화도가 30%를 초과하는 경우 유연성에 대한 보완 효과를 기대하기 어렵다.If the glass transition temperature is higher than 0 ° C, it is difficult to expect a complementary effect on the impact resistance at low temperatures. If the crystallinity exceeds 30%, it is difficult to expect a complementary effect on flexibility.

여기에서, 저온에서의 내충격성은 유리전이온도가 0℃ 이하이기만 하면 저온에서도 알파-올레핀계 공중합체가 고무같은 상태를 유지하여 내충격성 보완 효과를 기대할 수 있으므로 유리전이온도의 하한은 특별히 한정하지 않는다 할 것이며, 결정화도가 30% 이하이면 70% 이상의 비결정부분에 의한 유연성 보완 효과를 기대할 수 있으므로 결정화도의 하한은 특별히 한정하지 않는다 할 것이다.Here, the impact resistance at low temperature is not particularly limited so long as the glass transition temperature is not higher than 0 占 폚, since the α-olefin-based copolymer maintains the rubbery state even at a low temperature to anticipate the impact resistance complementary effect When the degree of crystallinity is 30% or less, the complementary effect of the amorphous portion due to the amorphous portion of 70% or more can be expected. Therefore, the lower limit of the degree of crystallinity is not particularly limited.

본 발명에 있어 상기 무수말레인산으로 개질된 스티렌계 블록 공중합체를 통해서는 마찰특성, 충격흡수성, 치수안정성, UV 및 오존 저항성, 고온 및 저온 내구성(고온 및 저온에서의 내크랙성) 등의 물성을 유지하면서도 잔디보호매트의 접착성을 개선시킬 수 있다. 이는 스티렌계 블록 공중합체의 일부분인 고무성분 때문에 잔디보호매트의 물성이 향상되는 것으로 판단되며, 스티렌계 블록 공중합체가 무수말레인산으로 개질되면 인장특성 등을 개선할 수 있고 폴리프로필렌 수지와의 상용성이 상승되기 때문에 잔디보호매트의 표면 접착성이 개선되는 것으로 판단된다.The styrenic block copolymer modified with maleic anhydride in the present invention has properties such as friction characteristics, impact absorbability, dimensional stability, UV and ozone resistance, and high temperature and low temperature durability (crack resistance at high and low temperatures) The adhesion of the lawn mats can be improved. It is considered that the physical properties of the lawn mats are improved due to the rubber component, which is a part of the styrenic block copolymer. When the styrenic block copolymer is modified with maleic anhydride, the tensile properties and the like can be improved and compatibility with the polypropylene resin It is considered that the surface adhesion of the lawn mats is improved.

이때, 상기 무수말레인산으로 개질된 스티렌계 블록 공중합체는 그 함량이 폴리프로필렌수지 100 중량부(총 사용량 기준)에 대하여 1 내지 25중량부일 때, 잔디보호매트의 마찰특성, 충격흡수성, 치수안정성, UV 및 오존 저항성, 고온 및 저온 내구성(고온 및 저온에서의 내크랙성) 등의 물성을 유지할 수 있다. At this time, when the content of the styrene block copolymer modified with maleic anhydride is 1 to 25 parts by weight based on 100 parts by weight (based on the total amount used) of the polypropylene resin, the friction modulus, impact absorbability, dimensional stability, UV and ozone resistance, and high-temperature and low-temperature durability (crack resistance at high and low temperatures).

여기에서, 상기 무수말레인산으로 개질된 스티렌계 블록 공중합체에 대해 함량이 1중량부 미만이면 강도 보강을 기대하기 어려우며, 25중량부를 초과하는 경우 잔디보호매트로서의 성형성 및 가공성을 기대하기 어렵다.If the content of the styrene block copolymer modified with maleic anhydride is less than 1 part by weight, it is difficult to expect strength reinforcement. If the content is more than 25 parts by weight, it is difficult to expect moldability and processability as a grass protection mat.

여기에서, 상기 무수말레인산으로 개질된 스티렌계 블록 공중합체는 그래프트 반응 및 개질 효과를 높이기 위해 분자량 48000~100000이고 밀도 0.9~0.925g/㎤이며 용융지수 10~25g/10min인 무수말레인산 1~5중량%를 첨가하여 그래프팅 반응에 의한 개질을 수행하는 것이 바람직하며, 개질에 의한 인장특성 등의 물성을 증대시킬 수 있음은 물론 폴리프로필렌 수지와의 상용성을 개선할 수 있다.Here, the styrene block copolymer modified with maleic anhydride preferably has a molecular weight of 48,000 to 100,000, a density of 0.9 to 0.925 g / cm 3 and a melt index of 10 to 25 g / 10 min to 1 to 5 weight of maleic anhydride % Is added to perform the modification by the grafting reaction. It is possible not only to increase physical properties such as tensile properties by modification, but also to improve the compatibility with the polypropylene resin.

여기에서, 상기 스티렌계 블록 공중합체는 스티렌-부타다이엔-스티렌(SBS), 스티렌-에틸렌-부타디엔-스티렌(SEBS), 스티렌-에틸렌-프로필렌-스티렌(SEPS), 스티렌-이소프로필렌-스티렌(SIS) 중에서 선택된 어느 1군일 수 있다.Here, the styrenic block copolymer may be at least one selected from the group consisting of styrene-butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEBS), styrene-ethylene-propylene-styrene (SEPS), styrene- SIS). ≪ / RTI >

또한, 상기 무수말레인산으로 개질된 스티렌계 블록 공중합체는 유리전이온도가 110~150℃이고 결정화도가 60~85%인 것이 바람직한데, 잔디보호매트에 대한 강도와 사출 성형성이 보완되는 효과를 높일 수 있다.The styrene-based block copolymer modified with maleic anhydride preferably has a glass transition temperature of 110 to 150 ° C and a crystallinity of 60 to 85%. It is preferable that the strength and the injection moldability of the grass protection mat are complemented .

만일, 유리전이온도가 110℃ 미만일 경우 사출 성형시 잔디보호매트의 불량 발생이 많아지고 150℃를 초과하는 경우 접착성이 너무 높아 강도가 떨어지는 문제가 발생되며, 결정화도가 60% 미만일 경우 매트로서의 일정 이상의 강도를 만족시킬 수 없고 85%를 초과하는 경우 성형성이 저하됨과 더불어 강도가 너무 커지므로 유연성이 결여되는 문제가 발생될 수 있다.If the glass transition temperature is less than 110 캜, the occurrence of defects in the grass protection mat increases during injection molding. If the glass transition temperature is higher than 150 캜, the adhesiveness is too high to lower the strength. When the crystallinity is less than 60% The strength can not be satisfied. When it exceeds 85%, the moldability is deteriorated and the strength becomes too large, resulting in a problem that flexibility is lacking.

또한, 본 발명에서는 기능성 향상 및 구비를 위해 첨가되는 기능성 첨가제에 있어, 상기 치수안정제는 폴리프로필렌의 사출 성형시 큰 열팽창율로 인한 잔디보호매트의 변형을 방지할 수 있도록 한 것으로서, 몬모릴로나이트, 벤토나이트, 버미큘라이트, 울라스토나이트 등의 무기충전제 중에서 선택된 어느 1군 이상을 사용할 수 있으며, 치수안정효과가 우수하도록 폴리프로필렌 수지 100중량부(총 사용량 기준)에 대해서 10~40중량부를 첨가할 수 있다.Further, in the present invention, in the functional additive added for the purpose of improving the functionality, the dimensional stabilizer is to prevent the deformation of the grass protection mat due to a large thermal expansion rate during the injection molding of polypropylene. The montmorillonite, bentonite, And inorganic fillers such as polyvinyl alcohol, vermiculite, and wollastonite may be used, and 10 to 40 parts by weight may be added to 100 parts by weight of the polypropylene resin (based on the total amount used) so as to obtain excellent dimensional stability.

여기에서, 치수안정제에 대해 10중량부 미만일 경우 치수안정 효과를 기대하기 어려우며, 40중량부를 초과할 경우 잔디보호매트로서의 가공성 및 기계적 강도를 기대하기 어렵고 불량율이 높을 수 있다.If the amount is less than 10 parts by weight, it is difficult to expect a dimensional stabilizing effect. When the amount exceeds 40 parts by weight, workability and mechanical strength as a grass protection mat can not be expected, and a defective ratio may be high.

상기 미끄럼방지제는 잔디보호매트에 대한 미끄럼방지기능을 발휘케 함과 더불어 내오존성, 내마모성, 내후성, 내열성, 내한성의 기능을 확보하도록 스티렌부타디엔, 폴리우레탄, 니트릴, 부틸, 부타디엔, 에틸렌프로필렌의 고무계 재질 중에서 선택된 어느 1군 이상을 사용할 수 있으며, 폴리프로필렌수지 100중량부(총 사용량 기준)에 대해서 5~20중량부를 첨가할 수 있다.The anti-slip agent is a rubber-based material of styrene butadiene, polyurethane, nitrile, butyl, butadiene, and ethylene propylene so as to secure the functions of ozone resistance, abrasion resistance, weather resistance, heat resistance and cold resistance, , And 5 to 20 parts by weight based on 100 parts by weight of the polypropylene resin (based on the total amount used) may be added.

이때, 상기 미끄럼방지제는 사출 성형되는 잔디보호매트의 표면 평활성을 저해하지 않도록 하기 위해 0.1~10㎛의 입자 크기의 것을 사용하면서 우수한 미끄럼방지 효과를 위해 밀도가 1.15~1.35g/㎤인 것을 사용함이 바람직하다.In order to prevent the surface smoothness of the lawn mats to be injection-molded, the anti-slip agent has a particle size of 0.1 to 10 탆 and has a density of 1.15 to 1.35 g / cm 3 for an excellent slip prevention effect. desirable.

여기에서, 미끄럼방지제에 대해 5중량부 미만일 경우 미끄럼방지 효과를 기대하기 어려우며, 20중량부를 초과할 경우 중금속 함량이 높아질 수 있다.When the amount of the antistatic agent is less than 5 parts by weight, it is difficult to expect a slip effect. When the amount exceeds 20 parts by weight, the heavy metal content may be increased.

여기에서, 상기 스티렌부타디엔을 사용하는 경우 내열성과 내마모성 및 내노화성의 물성을 기대할 수 있고, 폴리우레탄은 내오존성과 내마모성을 기대할 수 있고, 니트릴은 내마모성 및 내약품성을 기대할 수 있고, 부틸은 내후성 및 내마찰성을 기대할 수 있고, 부타디엔은 내마모성과 내굴곡성 및 내한성을 기대할 수 있으며, 에틸렌프로필렌은 내구성과 내열성 및 내후성을 기대할 수 있다.When the above-mentioned styrene butadiene is used, physical properties such as heat resistance, abrasion resistance and aging resistance can be expected. Polyurethane can be expected to have ozone resistance and abrasion resistance. Nitrile can be expected to have abrasion resistance and chemical resistance. And frictional resistance can be expected. Butadiene can be expected to have abrasion resistance, flexural resistance and cold resistance, and ethylene propylene can be expected to have durability, heat resistance and weatherability.

상기 자외선차단제는 물리적 차단제인 이산화티타늄이나 산화아연을 사용함이 바람직하며, 이는 자외선 차단을 통해 잔디보호매트가 변색되는 것을 유용하게 방지할 수 있다.The ultraviolet screening agent is preferably titanium dioxide or zinc oxide, which is a physical blocking agent, and can effectively prevent the discoloration of the grass protection mat through ultraviolet ray shielding.

하지만, 특별히 이에 국한되지 않는다 할 것으로서, 호모살레이트, 아보벤젠, 옥틸메톡시신나메이트, 에칠헥실메톡시신나메이트, 옥시녹세이트, 옥토크릴, 옥시벤존 등의 화학적 차단제 중에서 선택된 어느 1군 이상을 사용할 수도 있다.However, it should be understood that any one or more selected from chemical blocking agents such as homosalate, avobenzene, octylmethoxycinnamate, ethylhexylmethoxycinnamate, oxynosate, octocryl, oxybenzone, It can also be used.

상기 이산화티타늄이나 산화아연을 첨가하는 경우에는 자외선 차단 효과를 높이기 위해 0.01~10㎛의 입자 크기가 사용될 수 있다.When titanium dioxide or zinc oxide is added, a particle size of 0.01 to 10 mu m can be used to enhance the ultraviolet blocking effect.

여기에서, 상기 자외선차단제는 폴리프로필렌수지 100중량부(총 사용량 기준)에 대해서 5~25중량부를 첨가함이 바람직한데, 5중량부 미만일 경우 자외선 차단기능을 발휘하기 어려우며, 25중량부를 초과하는 경우 잔디보호매트에서의 백색성이 짙어질 수 있어 색상 변화가 발생될 수 있다.The ultraviolet screening agent is preferably added in an amount of 5 to 25 parts by weight based on 100 parts by weight of the polypropylene resin (based on the total amount used). When the amount is less than 5 parts by weight, the ultraviolet screening function is difficult to exhibit. When the amount is more than 25 parts by weight The whiteness in the lawn protection mat may become thick and color change may occur.

상기 소음조절제는 압축 탄성 및 복원력이 가능하도록 알루미늄 실리케이트 원형 중공체를 사용하며, 폴리프로필렌수지 100중량부에 대해서 3~20중량부를 첨가할 수 있는데, 3중량부 미만일 경우 소음 조절효과를 기대할 수 없으며, 20중량부를 초과할 경우 잔디보호매트에 대한 기계적 강도가 커지므로 오히려 압축 탄성을 기대할 수 없게 된다.The noise control agent uses an aluminum silicate circular hollow body so as to be capable of compressive elasticity and restoring force, and can be added in an amount of 3 to 20 parts by weight based on 100 parts by weight of the polypropylene resin. If the amount is less than 3 parts by weight, noise control effect can not be expected If the amount is more than 20 parts by weight, the mechanical strength of the grass protection mat increases, so that the compression elasticity can not be expected.

이때, 상기 소음조절제는 우수한 소음조절 효과를 발휘하도록 30~80㎛의 입자 크기 및 8~10기압의 내압축성을 갖는 것일 수 있다.At this time, the noise control agent may have a particle size of 30 to 80 mu m and a compressibility of 8 to 10 atm to exert an excellent noise control effect.

상기 열산화방지제는 사출 성형 가공시 고온에 의한 수지의 열산화를 방지할 수 있도록 하는 것으로서, 폴리프로필렌수지 100중량부(총 사용량 기준)에 대하여 1 내지 5중량부를 첨가하여 사용할 수 있으며, 1중량부 미만일 경우 열산화 방지효과를 기대하기 어렵고 잔디보호매트의 충격강도 및 인장강도를 저하시킬 수 있으며, 5중량부를 초과할 경우 가공성 및 사출 성형성을 저해할 수 있다.The thermal oxidation inhibitor is capable of preventing thermal oxidation of the resin due to high temperature during injection molding, and may be used in an amount of 1 to 5 parts by weight based on 100 parts by weight of the polypropylene resin (based on the total amount used) The effect of preventing thermal oxidation can not be expected and the impact strength and tensile strength of the grass protection mat can be lowered. If the amount is more than 5 parts by weight, workability and injection moldability can be deteriorated.

이때, 상기 열산화방지제로는 테트라키스[메틸렌-3(3,5-디-티-부틸-4-하이드록시페닐)프로피오네이트]메탄, 옥타데실-3-(3,5-디-티-부틸-4-하이드록시페닐)프로피오네이트, 2,2'-메틸렌비스(4-메틸-6-티-부틸페놀), 2,6-디-티-부틸-4-메틸페놀 중에서 선택된 어느 1군 이상이 사용될 수 있다.As the thermal oxidation inhibitor, tetrakis [methylene-3 (3,5-di-tert-butyl-4-hydroxyphenyl) propionate] methane, octadecyl-3- (3,5- -Butyl-4-hydroxyphenyl) propionate, 2,2'-methylenebis (4-methyl-6-thi-butylphenol), and 2,6- More than one group may be used.

더불어, 본 발명에서는 잔디보호매트(1)에 대해 난연성을 보강하도록 폴리황화암모늄, 폴리클로로포스페이트, 폴리인산암모늄, 폴리황화멜라민, 멜라민 피로포스페이트, 피페라진 폴리포스페이트, 트리페닐 포스페이트 중에서 선택된 어느 1군 이상의 무기계 난연제를 더 포함하는 구성을 갖게 할 수 있으며, 우수한 난연 효과를 기대할 수 있도록 폴리프로필렌 수지 100중량부(총 사용량 기준)에 대해서 무기계 난연제 10~30중량부를 첨가하는 것이 바람직하다 할 수 있다.In addition, in the present invention, any one group selected from among ammonium polysulfide, ammonium polyphosphate, ammonium polyphosphate, melamine pyrophosphate, piperazine polyphosphate, and triphenyl phosphate to reinforce the flame retardancy of the grass protection mat And 10 to 30 parts by weight of an inorganic flame retardant may be added to 100 parts by weight of the polypropylene resin (based on the total amount used) so that an excellent flame retardant effect can be expected.

상기 사출성형단계(S200)는 상기 잔디보호매트용 조성물을 이용하여 사출 성형함에 의해 판상형의 매트로 제조하는 단계로서, 도 2에서 보여주는 바와 같이 상기 펠렛과 마스터배치를 용융 혼합 및 사출하는 사출단계(S210)와, 상기 사출되는 잔디보호매트용 조성물에 대해 일정 형태를 갖는 판상형의 잔디보호매트로 성형하는 성형단계(S220)로 세분화할 수 있다.The injection molding step (S200) is a step of preparing a plate-like mat by injection molding using the composition for lawn protective mat. The injection molding step (S200) comprises an injection step of melting and mixing the pellet and the master batch S210), and a forming step (S220) of molding the composition for the lawn mats protective mat into a plate-like lawn protection mat having a certain shape.

상기 사출단계(S210)에서는 상기한 조성으로 이루어지는 잔디보호매트용 조성물을 용융 혼합 및 사출을 수행하는 사출기본체의 내부로 고음압용 초음파 펄스를 인가함으로써 사출기본체 내 형성되는 압력을 감소시켜 부하를 최소화함과 더불어 분산성을 높여줄 수 있도록 하면서 용융 혼합 및 사출 효율을 향상시킬 수 있도록 처리할 수 있다.In the injection step S210, by applying an ultrasonic pulse for high sound pressure to the inside of the injector main body for performing the melt mixing and injection of the composition for the lawn protective mat of the above composition, the pressure formed in the injector main body is reduced to minimize the load It is possible to improve the melt mixing and injection efficiency while improving the dispersibility.

상기 성형단계(S220)에서는 도 3 및 도 4에 나타낸 바와 같이, 잔디 상에 설치하기 위한 잔디보호매트(1)에 대해 식생부(100)를 포함하는 판상 구조를 갖는 매트형 몸체로 구비된다.In the forming step S220, as shown in FIGS. 3 and 4, a mat-shaped body having a plate-like structure including the vegetation part 100 is provided to the grass protection mat 1 to be installed on the grass.

상기 잔디보호매트(1)는 도시한 바와 같이, 사출 성형에 의해 이루어지는 것으로서, 잔디의 식생을 가능하게 하면서 이를 이용자나 차량으로부터 보호하기 위한 식생부(100)를 포함한다.As shown in the drawing, the grass protection mat 1 is formed by injection molding, and includes a vegetation part 100 for protecting the lawn vegetation from users and vehicles.

이때, 상기 식생부(100)는 연속되는 사각 격자배열구조로 이루어지는 베이스프레임틀(110)과, 상기 베이스프레임틀(110)이 갖는 격자들 사이에 형성되고 잔디통과공간을 형성하는 잔디식생공간(120)과, 상기 베이스프레임틀(110)의 하부에서 하측방향으로 돌출되고 상부에서 가해지는 하중에 대해 완충기능을 발휘하도록 구비 및 간격 배열되는 제1완충돌부(130)와, 상기 베이스프레임틀(110)의 하부에서 하측방향으로 돌출되고 상기 제1완충돌부(130)와 함께 상부에서 가해지는 하중에 대해 완충기능을 발휘하도록 구비 및 간격 배열되는 제2완충돌부(140)와, 상기 베이스프레임틀(110)의 외곽에 구비되고 이웃하는 두 측면 상에 외측방향으로 돌출되어 잔디보호매트(1)간의 연결에 사용되는 고리형 연결부(150)와, 상기 베이스프레임틀(110)의 네 모서리 부분 내측에 고정핀 등의 고정부재 삽입에 의한 지면 고정력을 제공하는데 사용되는 핀고정부(160)와, 상기 베이스프레임틀(110)의 상부에서 상측방향으로 돌출되고 잔디줄기 형태로 촘촘하게 배치되는 잔디보호돌부(200)를 포함하는 구성을 갖게 할 수 있다.The vegetation part 100 includes a base frame frame 110 having a continuous rectangular grid arrangement structure and a grass vegetation space formed between the grids of the base frame frame 110 and forming a grass passing space A first full impact portion 130 protruding downward from a lower portion of the base frame frame 110 and arranged and spaced apart to exert a damping function against a load applied at an upper portion of the base frame frame 110, A second full impact portion 140 protruding downward from a lower portion of the first full impact portion 130 and arranged and spaced apart to exert a buffer function against a load applied to the first full impact portion 130 at an upper portion thereof, An annular connecting portion 150 provided at an outer periphery of the base frame frame 110 and protruding outwardly on two adjacent side surfaces to be used for connection between the lawn protection mat 1 and an annular connecting portion 150, Inside the corner part And a grass protection protrusion 200 protruding upward from the upper part of the base frame frame 110 and closely arranged in the form of a grass stem, ) Can be provided.

이때, 상기 베이스프레임틀(100)은 전체적으로 사각형상의 몸체를 갖되 사각형을 이루는 단위격자가 반복 배열되는 구성이며, 상기 사각형 단위격자마다 서로 이격되는 이중 프레임틀 구조로 형성하여 잔디의 관통 배치가 가능하도록 구비되고, 상기 이중 프레임틀의 각 상면에서 잔디보호돌부(200)를 이중 구조로 돌출 형성하는 구성을 갖게 할 수 있다.At this time, the base frame frame 100 has a rectangular frame body, and a rectangular unitary grid is repeatedly arranged. The rectangular frame frame 100 is formed of a double frame frame structure that is spaced apart from each square unit grid, And the grass protection protrusions 200 protrude from the upper surface of the double frame frame in a double structure.

여기에서, 상기 잔디보호돌부(200)는 잔디보호기능과 더불어 미끄러짐을 방지하는 구조적인 역할을 수행한다 할 수 있다.Here, the lawn guard protrusion 200 may play a structural role to prevent slipping in addition to the lawn protecting function.

상기 제1완충돌부(130)는 사각 배열구조를 갖도록 간격 배치되는 것으로서, 내부가 비어있고 원형 둘레의 외주연을 갖는 원통몸체로서, 상기 원통몸체의 비어있는 내부에 십자형 구조의 연결지지부가 연결 구비되는 구성을 갖게 할 수 있다.The first impingement portion 130 is spaced apart from the first impingement portion 130 so as to have a rectangular arrangement, and is a cylindrical body having an inner periphery and an outer periphery of a circular periphery, and a cross- So that it is possible to have a configuration.

상기 제2완충돌부(140)는 원기둥의 형태로 이루어지고, 상기 제1완충돌부(130)에 이웃하여 사방 배치 및 상기 제1완충돌부(130)의 간격 배치되는 사이사이에 돌출되는 구성을 갖게 할 수 있다.The second full impact portion 140 is formed in the shape of a cylinder and protrudes between the four sides disposed next to the first full impact portion 130 and the interval between the first full impact portions 130 Configuration.

이에 따라, 본 발명에서는 상술한 조성으로 이루어지고 사출 성형을 통해 상술한 구조를 갖는 판상의 잔디보호매트(1)를 용이하게 제조할 수 있고, 잔디 상에 간단하게 설치하여 다수의 이용자나 차량으로부터 잔디를 보호하는데 사용할 수 있다.Accordingly, in the present invention, the plate-like grass protection mat 1 having the above-described composition and having the above-described structure can be easily manufactured through injection molding, and it can be easily installed on the lawn, Can be used to protect grass.

또한, 본 발명에 따른 잔디보호매트(1)는 중금속에 대한 함량을 기준치 이하로 낮추면서 우수한 성능을 확보함은 물론 우수한 기능성을 발휘할 수 있는 잔디보호매트(1)를 제공할 수 있다.In addition, the grass protection mat 1 according to the present invention can provide a grass protection mat 1 that can exhibit excellent performance while exhibiting excellent functionality while lowering the content of heavy metals to below a standard value.

도 5 및 도 6은 본 발명의 실시예에 따른 잔디보호매트 제조방법에 의해 제조된 샘플링 제품을 나타낸 사진으로서, 본 발명의 이해를 돕기 위해 첨부하였다.FIG. 5 and FIG. 6 are photographs showing a sampling product manufactured by the method of manufacturing the grass protection mat according to the embodiment of the present invention, and are attached to facilitate understanding of the present invention.

이하, 본 발명에 따른 실시예를 통하여 보다 구체적으로 설명하기로 한다, 다만, 하기 실시예 및 비교예는 본 발명을 예시 및 비교를 위한 것일 뿐, 본 발명의 보호범위를 한정하는 것은 아니라 할 것이다.Hereinafter, the present invention will be described in more detail with reference to the following examples. However, the following examples and comparative examples are for illustrative and comparative purposes only and do not limit the scope of protection of the present invention .

하기 표 1에 나타낸 성분 및 배합비로 잔디보호매트용 조성물을 제조하였으며, 이러한 잔디보호매트용 조성물을 사출성형기에 투입하여 사출 성형함으로써 잔디보호매트를 제조하였다.A composition for lawn protection mats was prepared at the components and mixing ratios shown in Table 1 below. The lawn protection mat was prepared by injection molding the composition for lawn protection mats into an injection molding machine.

구체적으로, 잔디보호매트용 조성물에 대해서는 폴리프로필렌 일정량(총 사용량의 50%)에 무수말레인산으로 개질된 알파-올레핀 공중합체와 무수말레인산으로 개질된 스티렌계 블록 공중합체를 혼합하되 펠렛으로 만들고, 폴리프로필렌 일정량(총 사용량의 나머지 50%)에 기능성 첨가제를 혼합하되 마스터배치로 만들었다.Specifically, for the composition for lawn protection mat, pellets were prepared by mixing pellets of an alpha-olefin copolymer modified with maleic anhydride and a styrenic block copolymer modified with maleic anhydride in a predetermined amount of polypropylene (50% of the total amount used) The functional additives were mixed in a certain amount of propylene (the remaining 50% of the total amount used) and made into a master batch.

이때, 폴리프로필렌은 총 사용량 대비 펠렛 제조시 50% 분량을 사용하고, 마스터배치 제조시 나머지 50% 분량을 사용하였으며, 기타 첨가재료의 투입량을 사용범위 내에서 하기 표 1에 나타낸 바와 같이 조절하였다.At this time, 50% of the polypropylene was used for preparing the pellet, and the remaining 50% was used for preparing the masterbatch. The amount of the other ingredients added was controlled as shown in Table 1 below.

이렇게 제조된 잔디보호매트용 조성물을 이용하여 사출 성형함에 의해 잔디보호매트를 제조하였다.A grass protection mat was prepared by injection molding using the composition for lawn protection mat.

여기에서, 폴리프로필렌 수지는 폴리프로필렌 블록 공중합체, 무수말레인산으로 개질된 알파-올레핀계 공중합체는 무수말레인산과 에틸렌-옥텐 공중합체, 무수말레인산으로 개질된 스티렌계 블록 공중합체는 무수말레인산과 스티렌-부타디엔-스티렌(SBS), 치수안정제는 몬모릴로나이트, 미끄럼방지제는 스티렌부타디엔, 자외선차단제는 이산화티타늄, 소음조절제는 알루미늄 실리케이트 원형 중공체, 열산화방지제는 테트라키스메탄을 사용하였으며, 단지 비교예에서는 무수말레인산에 의한 개질방식을 적용하지 않았다.Here, the polypropylene resin is a polypropylene block copolymer, the alpha-olefin copolymer modified with maleic anhydride is a maleic anhydride and the ethylene-octene copolymer, and the styrene block copolymer modified with maleic anhydride is maleic anhydride and styrene- Butadiene-styrene (SBS), the dimension stabilizer montmorillonite, the anti-slip agent styrene butadiene, the ultraviolet screening agent titanium dioxide, the noise control agent aluminum silicate circular hollow body and the thermal oxidation inhibitor tetrakismethane. The reforming method by the above method is not applied.

하기 표 1에서 괄호 안의 수치는 알파-올레핀계 공중합체와 스티렌계 블록 공중합체에 개질제로 사용된 무수말레인산의 총 중량 대비 첨가함량(중량%)을 나타낸 것이다.The numerical values in parentheses in the following Table 1 show the content (wt.%) Added to the total weight of maleic anhydride used as a modifier in the alpha-olefin copolymer and the styrene block copolymer.

구분division 조성(중량부)Composition (parts by weight) 폴리프로필렌Polypropylene 알파-올레핀
공중합체
Alpha-olefin
Copolymer
스티렌계 블록
공중합체
Styrenic block
Copolymer
치수
안정제
size
stabilizator
미끄럼방지제Anti-slip agent 자외선차단제Sunscreen 소음
조절제
noise
Modulator
열산화방지제Thermal antioxidant
무수말레인산 개질Maleic anhydride modification 무수말레인산비개질Maleic anhydride unmodified 무수말레인산 개질Maleic anhydride modification 무수말레인산비개질Maleic anhydride unmodified 실시예1Example 1 100100 20(5)20 (5) 15(3)15 (3) 2020 1515 1010 55 33 실시예2Example 2 100100 20(5)20 (5) 15(3)15 (3) 2020 1515 1010 55 33 실시예3Example 3 100100 25(10)25 (10) 20(5)20 (5) 2525 2020 1515 1010 55 실시예4Example 4 100100 25(10)25 (10) 20(5)20 (5) 2525 2525 2020 55 55 비교예1Comparative Example 1 100100 2525 2020 2525 2020 1515 1010 55 비교예2Comparative Example 2 100100 2020 1515 55 55 55 55 55

(실험예)(Experimental Example)

상기 실시예 및 비교예에 의해 제조된 잔디보호매트에 대해 성능 평가를 실시하였으며, 표 2에 그 결과치를 나타내었다.The performance of the lawn mats manufactured by the above examples and comparative examples was evaluated, and the results are shown in Table 2.

1. 비카트연화점 시험1. Vicat softening test

상기 실시예 및 비교예에 의해 제조된 잔디보호매트에 대해 각각 시험편을 제조하였으며, 이에 대해 KTL M 106-2017에 기준한 방식으로 평가하였다.Test specimens were prepared for the lawn mats prepared according to the above examples and comparative examples, and the test specimens were evaluated in a manner based on KTL M 106-2017.

비교예에 비해 실시예들이 갖는 비카트연화점이 더 높게 나타남을 보여주고 있다.The Vickart softening point of the Examples is higher than that of the Comparative Examples.

2. 미끄럼저항 시험2. Slip resistance test

상기 실시예 및 비교예에 의해 제조된 바닥재에 대해 EN 14877에 기준한 방식으로 평가하였으며, 건조시와 습윤시로 나누어 평가하였다.The flooring prepared according to the above Examples and Comparative Examples was evaluated in accordance with the method according to EN 14877, and evaluated by dividing into dryness and wetness.

미끄럼방지제의 사용여부에 따라 제품이 갖는 미끄럼 저항에 차이가 발생함을 보여주고 있다.It is shown that there is a difference in the sliding resistance of the product depending on whether or not the anti-slip agent is used.

3. 치수안정성 시험3. Dimensional stability test

상기 실시예 및 비교예에 의해 제조된 바닥재에 대해 KS F 3888-1에 기준한 방식으로 평가하였다.The flooring prepared according to the above examples and comparative examples was evaluated in a manner based on KS F 3888-1.

상기 실시예 및 비교예에 있어서는 치수안정제의 사용여부에 따라 제품이 갖는 치수 안정성에 차이가 있음을 보여주고 있다.In the above Examples and Comparative Examples, there is a difference in the dimensional stability of the product depending on whether a dimension stabilizer is used or not.

4. 내마모성 시험4. Abrasion resistance test

상기 실시예 및 비교예에 의해 제조된 바닥재에 대해 시험편을 제조하였으며, KS M ISO 5470-1에 기준한 방식으로 평가하였다.Test pieces were prepared for the flooring prepared according to the above examples and comparative examples and evaluated in a manner based on KS M ISO 5470-1.

비교예에 비해 실시예들이 갖는 내마모성이 더욱 우수하게 나타남을 보여주고 있다.The abrasion resistance of the examples is more excellent than that of the comparative examples.

5. 인장강도 및 신장률 시험5. Tensile strength and elongation test

상기 실시예 및 비교예에 의해 제조된 각각의 잔디보호매트에 대해 KS M 3006에 기준한 방식으로 평가하였다.The respective lawn mats prepared according to the above examples and comparative examples were evaluated in a manner based on KS M 3006.

비교예에 비해 실시예들이 갖는 인장강도 및 신장률이 더욱 높게 나타남을 보여주고 있다.The tensile strength and elongation percentage of Examples are higher than those of Comparative Examples.

6. 압축 및 강도 시험6. Compression and Strength Test

상기 실시예 및 비교예에 의해 제조된 각각의 잔디보호매트에 대해 제품 사용상태(50cm×50cm)로 하여 1500N/0.01㎡의 하중을 가하여 변형과 파손 및 절단 상태를 확인하였다.Each of the lawn mats manufactured by the above examples and comparative examples was subjected to a load of 1500 N / 0.01 m 2 under a condition of using the product (50 cm × 50 cm), thereby confirming deformation, breakage and cutting conditions.

실시예들은 식생부를 갖는 잔디보호매트에 있어 변형이나 파손 및 절단이 없었는데, 비교예에서는 잔디보호매트의 식생부에 있어 파손 및 절단이 발생되어 품질에 차이가 있었다.In the examples, there was no deformation, breakage and cutting in the grass protection mat with vegetation part, but in the comparative example, the vegetation part of the grass protection mat was broken and cut, and the quality was different.

구분division 비카트
연화점(℃)
Bicart
Softening point (℃)
미끄럼저항
(BPN)
Slip resistance
(BPN)
치수안정성
(mm)
Dimensional stability
(mm)
내마모성
(mg)
Abrasion resistance
(mg)
신장율
(%)
Elongation rate
(%)
인장강도
(MPa)
The tensile strength
(MPa)
실시예1Example 1 7272 건조dry 8080 1.51.5 1818 3232 0.90.9 습윤Wet 6161 실시예2Example 2 7171 건조dry 8282 1.31.3 1717 3232 1.01.0 습윤Wet 6363 실시예3Example 3 6868 건조dry 8585 1.11.1 1515 3333 1.21.2 습윤Wet 6666 실시예4Example 4 6969 건조dry 8888 1.11.1 1515 3232 1.21.2 습윤Wet 6969 비교예1Comparative Example 1 6565 건조dry 8080 2.02.0 2121 2828 0.60.6 습윤Wet 5050 비교예2Comparative Example 2 6464 건조dry 7070 3.23.2 3232 2525 0.60.6 습윤Wet 4545

상기 표 2를 통해서는 본 발명에 따라 제조되는 잔디보호매트가 우수한 성능을 확보함은 물론 기계적 특성에 의한 품질기준을 만족함을 보여주고 있다.Table 2 shows that the lawn mats manufactured according to the present invention have excellent performance and satisfy the quality standards based on mechanical properties.

7. 중금속 시험7. Heavy metal test

상기 실시예 및 비교예에 의해 제조된 각각의 잔디보호매트에 대해 KTL M 106-2017에 기준한 방식으로 평가하였으며, 표 3에 그 결과치를 나타내었다.The respective lawn mats prepared according to the above examples and comparative examples were evaluated in a manner based on KTL M 106-2017, and the results are shown in Table 3.

구분division 납(mg/kg)Lead (mg / kg) 카드뮴(mg/kg)Cadmium (mg / kg) 수은(mg/kg)Mercury (mg / kg) 6가 크롬(mg/kg)Hexavalent chromium (mg / kg) 실시예1Example 1 5858 3232 1818 1818 실시예2Example 2 6060 3636 2020 1919 실시예3Example 3 6262 4343 2222 2121 실시예4Example 4 6161 4242 2222 2020 비교예1Comparative Example 1 5252 4040 1717 1818 비교예2Comparative Example 2 5050 3838 1616 1616

상기 표 3을 통해서는 본 발명에 따라 제조되는 잔디보호매트에 있어 중금속 함량이 기준치 미만을 나타내고 있음을 확인할 수 있다.It can be seen from Table 3 that the heavy metal content of the grass protection mat manufactured according to the present invention is less than the standard value.

예로서, 잔디보호매트의 완제품에 대한 기준치는 납 90 이하, 카드뮴 50 이하, 수은 25 이하, 6가 크롬 25 이하의 품질기준을 만족하면 된다.For example, the reference value for finished products of lawn protection mat may satisfy the quality standard of lead 90 or less, cadmium 50 or less, mercury 25 or less, hexavalent chromium 25 or less.

이에 따라, 본 발명에서는 폴리프로필렌계 합성수지를 주재료로 하여 제조되는 플라스틱재 잔디보호매트를 제공하되 잔디의 생육공간을 확보함과 더불어 내구성을 높이는 등 성능을 향상시킴과 더불어 품질기준을 만족시킬 수 있는 우수한 품질의 잔디보호매트를 제조할 수 있다.Accordingly, it is an object of the present invention to provide a plastic lawn protecting mat manufactured using polypropylene-based synthetic resin as a main material, to secure a space for lawn growth and to improve durability and performance, It is possible to produce a grass protection mat of excellent quality.

이상에서 설명한 실시예는 본 발명의 바람직한 실시예를 설명한 것에 불과하고 이러한 실시예에 극히 한정되는 것은 아니며, 본 발명의 기술적 사상과 청구범위 내에서 이 기술분야의 당해업자에 의하여 다양한 수정과 변형 및 단계의 치환 등이 이루어질 수 있다 할 것이며, 이는 본 발명의 기술적 범위에 속한다 할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the inventions. And the like can be made, and it will be within the technical scope of the present invention.

S100: 잔디보호매트용 조성물 제조단계
S110: 펠릿 제조단계
S120: 마스터배치 제조단계
S200: 사출성형단계
S210: 용융 혼합 및 사출단계
S220: 성형단계
S100: Preparation of composition for grass protection mat
S110: pellet manufacturing step
S120: master batch manufacturing step
S200: injection molding step
S210: melt mixing and injection step
S220: molding step

Claims (11)

잔디의 식생 구역상에 설치되어 식생되는 잔디를 보호하는데 사용하기 위한 용도이고 플라스틱 재질로 이루어지며, (A) 뒤틀림, 변형, 파손 및 절단되는 단점을 개선함과 더불어 성능을 향상시킬 수 있도록 하기 위해 폴리프로필렌 수지를 주재료로 하는 잔디보호매트용 조성물을 제조하는 단계; (B) 상기 잔디보호매트용 조성물을 사출 성형함에 의해 사각 격자배열구조에 의한 잔디식생공간을 확보한 식생부를 포함하는 잔디보호매트로 제조하는 단계;를 포함하는 잔디보호매트 제조방법에 있어서,
상기 (A)단계에서는 폴리프로필렌 수지 50중량부에 대해서 저온에서의 우수한 내충격성, 유연성, 가공성 및 기계적 강도를 기대할 수 있도록 하기 위한 무수말레인산으로 개질된 알파-올레핀 공중합체 5 내지 30중량부, 마찰특성과 충격흡수성은 물론 고온 및 저온에서의 내크랙성을 유지하면서 잔디보호매트의 접착성을 개선하기 위한 무수말레인산으로 개질된 스티렌계 블록 공중합체 1 내지 25중량부를 포함하는 혼합 조성으로 하여 펠렛으로 제조하는 단계; 및 폴리프로필렌 수지 50중량부에 대해서 기능성 첨가제를 포함하는 혼합 조성으로 하여 마스터배치를 제조하는 단계; 를 포함하고,
상기 (B)단계에서는 상기 펠렛과 마스터배치를 용융 혼합 및 사출하는 단계; 및 상기 사출되는 잔디보호매트 조성물에 대해 일정 형태를 갖는 판상형의 잔디보호매트로 성형하는 단계; 를 포함하며,
상기 폴리프로필렌 수지는 폴리프로필렌 랜덤 공중합체, 폴리프로필렌 블록 공중합체, 폴리프로필렌과 폴리에틸렌의 화합물 중에서 선택된 어느 1군을 사용하되, 다른 원료들과의 중합성이 저하됨을 방지 및 사출 성형되는 잔디보호매트의 기계적 물성이 저하됨을 방지함과 더불어 사출 성형성 및 치수 안정성을 갖도록 중량평균분자량 80000~1000000 및 용융지수 10~100g/10mim인 것을 사용하고;
상기 무수말레인산으로 개질된 알파-올레핀계 공중합체는 폴리프로필렌 수지의 저온에서의 내충격성과 유연성을 보완 및 제조되는 잔디보호매트의 표면 접착력을 개선하는 기능을 하되, 그래프트 반응 및 개질 효과를 높이기 위해 중량평균분자량 48000~100000이고 밀도 0.9~0.925g/㎤이며 용융지수 10~25g/10min인 무수말레인산 1~10중량%를 첨가하여 그래프팅 반응에 의한 개질을 수행함으로써 개질에 의한 인장특성을 증대 및 폴리프로필렌 수지와의 상용성을 개선하도록 하고, 유리전이온도 0℃ 이하 및 결정화도 35% 이하인 것을 사용함으로써 제조되는 잔디보호매트의 저온에서의 내충격성과 유연성을 보완하도록 하고, 상기 알파 올레핀계 공중합체는 에틸렌 비닐알코올 공중합체 또는 에틸렌 초산비닐 공중합체를 사용하며;
상기 기능성 첨가제는 사출 성형시 폴리프로필렌 수지의 큰 열팽창율로 인한 잔디보호매트의 변형을 방지하기 위한 치수안정제를 포함하되, 상기 치수안정제는 몬모릴로나이트, 벤토나이트, 버미큘라이트, 울라스토나이트 중에서 선택된 어느 1군 이상을 사용하고 치수안정효과가 우수하도록 폴리프로필렌 수지 100중량부에 대해서 10~40중량부를 첨가하는 것을 특징으로 하는 잔디보호매트 제조방법.
It is used for protecting lawns that are planted on the grass vegetation area. It is made of plastic material. It is used to (A) improve defects such as twisting, deformation, breakage and cutting, Comprising the steps of: preparing a composition for lawn protection mat using a polypropylene resin as a main material; (B) preparing a grass protection mat comprising a vegetation part having a grass vegetation space secured by a square grid arrangement structure by injection molding the composition for grass protection mat, the method comprising:
In the step (A), 5 to 30 parts by weight of an alpha-olefin copolymer modified with maleic anhydride to provide excellent impact resistance, flexibility, workability and mechanical strength at a low temperature with respect to 50 parts by weight of the polypropylene resin, 1 to 25 parts by weight of a styrene block copolymer modified with maleic anhydride to improve the adhesion of the lawn protection mat while maintaining the characteristics and impact absorbability as well as crack resistance at high temperature and low temperature, Producing; And 50 parts by weight of a polypropylene resin with a functional additive; Lt; / RTI >
In the step (B), the pellet and the master batch are melt-mixed and injected; And shaping the grass protection mat into a sheet-like grass protection mat having a predetermined shape with respect to the grass protection mat composition; / RTI >
The polypropylene resin may be any one selected from the group consisting of a polypropylene random copolymer, a polypropylene block copolymer, and a compound of polypropylene and polyethylene, Weight average molecular weight of from 80000 to 1000000 and a melt index of from 10 to 100 g / 10 mm in order to prevent injection molding property and dimensional stability,
The alpha-olefin-based copolymer modified with maleic anhydride serves to improve the surface adhesion of the lawn protective mat, which complements the impact resistance and flexibility at low temperatures of the polypropylene resin. In order to improve the graft reaction and the modifying effect, 1 to 10% by weight of maleic anhydride having an average molecular weight of 48,000 to 100,000 and a density of 0.9 to 0.925 g / cm 3 and a melt index of 10 to 25 g / 10 min is added to the resin to modify the grafting reaction, To improve the compatibility with the propylene resin, and to complement the impact resistance and flexibility at low temperatures of the lawn protective mat produced by using a material having a glass transition temperature of 0 DEG C or less and a degree of crystallinity of 35% or less, and the alpha olefin- A vinyl alcohol copolymer or an ethylene-vinyl acetate copolymer is used;
Wherein the functional additive includes a dimension stabilizer for preventing the deformation of the lawn protection mat due to a large thermal expansion rate of the polypropylene resin during injection molding, wherein the dimension stabilizer is at least one selected from montmorillonite, bentonite, vermiculite and wollastonite And 10 to 40 parts by weight based on 100 parts by weight of the polypropylene resin is added so as to improve the dimensional stability effect.
제 1항에 있어서,
상기 펠렛과 마스터배치를 용융 혼합 및 사출하는 단계에서는 사출기본체의 내부로 고음압용 초음파 펄스를 인가함으로써 사출기본체 내 형성되는 압력을 감소시켜 부하를 최소화함과 더불어 분산성을 높여줄 수 있도록 하며 용융 혼합 및 사출효율을 높일 수 있도록 처리하는 것을 특징으로 하는 잔디보호매트 제조방법.
The method according to claim 1,
In the step of melt-mixing and injecting the pellets and the master batch, ultrasonic pulses for high-pressure sound are applied to the inside of the main body of the injector to reduce the pressure formed in the main body of the injector, thereby minimizing the load and increasing the dispersibility. Mixing and injection efficiency of the grass protection mat.
삭제delete 제 1항에 있어서,
상기 무수말레인산으로 개질된 스티렌계 블록 공중합체는 그래프트 반응 및 개질 효과를 높이기 위해 중량평균분자량 48000~100000과 밀도 0.9~0.925g/㎤ 및 용융지수 10~25g/10min인 무수말레인산 1~5중량%를 첨가하여 그래프팅 반응에 의한 개질을 수행함으로써 개질에 의한 인장특성을 증대 및 폴리프로필렌 수지와의 상용성을 개선하도록 하고, 유리전이온도 110~150℃ 및 결정화도 60~85%인 것을 사용함으로써 제조되는 잔디보호매트에 대한 강도와 사출 성형성을 보완하도록 하며,
상기 스티렌계 블록 공중합체는 스티렌-부타디엔-스티렌(SBS), 스티렌-에틸렌-부타디엔-스티렌(SEBS), 스티렌-에틸렌-프로필렌-스티렌(SEPS), 스티렌-이소프로필렌-스티렌(SIS) 중에서 선택된 어느 1군인 것을 특징으로 하는 잔디보호매트 제조방법.
The method according to claim 1,
The styrene block copolymer modified with maleic anhydride preferably has a weight average molecular weight of 48,000 to 100,000, a density of 0.9 to 0.925 g / cm 3 and a melt index of 10 to 25 g / 10 min to 1 to 5% by weight of maleic anhydride to improve the graft reaction and modification effect. To improve the tensile properties by the modification and to improve the compatibility with the polypropylene resin, and by using a resin having a glass transition temperature of 110 to 150 ° C and a crystallinity of 60 to 85% To improve the strength and injection moldability of the lawn mats,
The styrenic block copolymer may be any one selected from styrene-butadiene-styrene (SBS), styrene-ethylene-butadiene-styrene (SEBS), styrene-ethylene-propylene-styrene (SEPS), and styrene- 1 < / RTI > group.
삭제delete 삭제delete 삭제delete 제 1항에 있어서,
상기 기능성 첨가제는 미끄럼방지제를 더 포함하되, 미끄럼방지와 더불어 내오존성, 내마모성, 내후성, 내열성, 내한성의 기능을 확보하도록 폴리우레탄, 니트릴, 부틸, 부타디엔, 에틸렌프로필렌의 고무계 재질 중에서 선택된 어느 1군 이상을 사용하고 폴리프로필렌수지 100중량부에 대해서 5~20중량부를 첨가하며, 사출 성형되는 잔디보호매트의 표면 평활성을 저해하지 않도록 하기 위해 0.1~10㎛의 입자 크기의 것을 사용하면서 우수한 미끄럼방지 효과를 위해 밀도가 1.15~1.35g/㎤인 것을 사용함을 특징으로 하는 잔디보호매트 제조방법.
The method according to claim 1,
The functional additive may further comprise at least one selected from the group consisting of polyurethane, nitrile, butyl, butadiene and ethylene propylene rubber materials so as to ensure the function of ozone resistance, abrasion resistance, weather resistance, heat resistance and cold resistance, And 5 to 20 parts by weight based on 100 parts by weight of the polypropylene resin are added. In order to prevent the surface smoothness of the injection-molded lawn mats from being deteriorated, an excellent anti-slip effect is obtained while using particles having a particle size of 0.1 to 10 μm And a density of 1.15 to 1.35 g / cm < 3 > is used.
제 1항에 있어서,
상기 기능성 첨가제는 자외선차단제를 더 포함하되, 호모살레이트, 아보벤젠, 옥틸메톡시신나메이트, 에칠헥실메톡시신나메이트, 옥시녹세이트, 옥토크릴, 옥시벤존 중에서 선택된 어느 1군 이상을 사용하고 폴리프로필렌수지 100중량부에 대해서 5~25중량부를 첨가하는 것을 특징으로 하는 잔디보호매트 제조방법.
The method according to claim 1,
Wherein the functional additive further comprises an ultraviolet screening agent, wherein at least one selected from the group consisting of homosalate, avobenzene, octylmethoxycinnamate, ethylhexylmethoxycinnamate, oxynosate, octocryl, and oxybenzone is used, And 5 to 25 parts by weight based on 100 parts by weight of the propylene resin.
제 1항에 있어서,
상기 잔디보호매트는,
연속되는 사각 격자배열구조로 이루어지는 베이스프레임틀; 상기 베이스프레임틀이 갖는 격자들 사이에 형성되고 잔디통과공간을 형성하는 잔디식생공간; 상기 베이스프레임틀의 하부에서 하측방향으로 돌출되고 상부에서 가해지는 하중에 대해 완충기능을 발휘하도록 구비 및 간격 배열되는 제1완충돌부; 상기 베이스프레임틀의 하부에서 하측방향으로 돌출되고 상기 제1완충돌부와 함께 상부에서 가해지는 하중에 대해 완충기능을 발휘하도록 구비 및 간격 배열되는 제2완충돌부; 상기 베이스프레임틀의 외곽에 구비되고 이웃하는 두 측면 상에 외측방향으로 돌출되어 잔디보호매트간의 연결에 사용되는 고리형 연결부; 상기 베이스프레임틀의 네 모서리 부분 내측에 고정핀 등의 고정부재 삽입에 의한 지면 고정력을 제공하는데 사용되는 핀고정부; 상기 베이스프레임틀의 상부에서 상측방향으로 돌출되고 잔디줄기 형태로 촘촘하게 배치되는 잔디보호돌부; 를 포함하며,
상기 베이스프레임틀은 전체적으로 사각형상의 몸체를 갖되 사각형을 이루는 단위격자가 반복 배열되는 구성으로서, 상기 사각형 단위격자마다 서로 이격되는 이중 프레임틀 구조로 형성하여 잔디의 통과가 가능하도록 구비되며;
상기 이중 프레임틀의 각 상면에서 잔디보호돌부를 이중 구조로 돌출 형성하며;
상기 제1완충돌부는 사각 배열구조를 갖도록 간격 배치하되, 내부가 비어있고 원형 둘레의 외주연을 갖는 원통몸체로서, 상기 원통몸체의 비어있는 내부에 십자형 구조의 연결지지부가 연결 구비되며;
상기 제2완충돌부는 원기둥의 형태로 이루어지고, 상기 제1완충돌부에 이웃하여 사방 배치 및 상기 제1완충돌부의 간격 배치되는 사이사이에 돌출 형성되는 것을 특징으로 하는 잔디보호매트 제조방법.
The method according to claim 1,
The grass protection mat
A base frame frame made up of successive rectangular grid arrangements; A grass vegetation space formed between the lattices of the base frame frame and forming a grass passage space; A first full collision portion protruding downward from a lower portion of the base frame frame and arranged and spaced apart to exert a buffer function against a load applied at an upper portion thereof; A second full collision portion protruding downward from a lower portion of the base frame frame and arranged and spaced apart to exert a buffer function against a load applied at an upper portion together with the first full collision portion; An annular connecting portion provided on an outer periphery of the base frame frame and protruding outwardly on two adjacent sides to be used for connection between the lawn protection mats; A pinching portion used to provide a ground fixing force by inserting fixing members such as fixing pins into four corner portions of the base frame frame; A grass protecting protrusion protruding upward from an upper portion of the base frame frame and closely arranged in the form of a grass stem; / RTI >
Wherein the base frame frame has a rectangular frame body and a rectangular unitary grid is repeatedly arranged, and the base frame frame is formed to have a double frame frame structure that is spaced apart from each other for each rectangular unit grid,
A grass protection protrusion protruding from each upper surface of the double frame frame in a double structure;
Wherein the first free end collision portion is spaced apart from the first free end portion to have a rectangular array structure, the hollow cylindrical body having an outer periphery and a circular periphery, the hollow portion having a cross shape and connected to the hollow support portion;
Wherein the second free end collision portion is formed in a cylindrical shape and is formed between the first free end collision portion and the first free end collision portion adjacent to the first free end collision portion.
삭제delete
KR1020180091345A 2018-08-06 2018-08-06 Manufacture method of lawn grass protecting mat KR101935742B1 (en)