KR20100027322A - High impact strength polypropylene composition having excellent rigidity - Google Patents

High impact strength polypropylene composition having excellent rigidity Download PDF

Info

Publication number
KR20100027322A
KR20100027322A KR1020080086191A KR20080086191A KR20100027322A KR 20100027322 A KR20100027322 A KR 20100027322A KR 1020080086191 A KR1020080086191 A KR 1020080086191A KR 20080086191 A KR20080086191 A KR 20080086191A KR 20100027322 A KR20100027322 A KR 20100027322A
Authority
KR
South Korea
Prior art keywords
propylene
polypropylene resin
copolymer
weight
high impact
Prior art date
Application number
KR1020080086191A
Other languages
Korean (ko)
Inventor
임형규
임재곤
홍종수
유영성
Original Assignee
삼성토탈 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼성토탈 주식회사 filed Critical 삼성토탈 주식회사
Priority to KR1020080086191A priority Critical patent/KR20100027322A/en
Publication of KR20100027322A publication Critical patent/KR20100027322A/en

Abstract

PURPOSE: A high impact strength polypropylene composition is provided to secure impact strength required as automobile interiors by adding a rubber component to homopolypropylene with excellent rigidity and to improve rigidity and inner surface resistance by adding filler such as whisker and talc. CONSTITUTION: A high impact strength polypropylene composition comprises 20 ~ 92 weight% of highly crystalline polypropylene resin with 96% or more of isotactic peptide fraction by a C-NMR method; 3 ~ 30 weight% of impact reinforcing material of a rubber component; and 5 ~ 50 weight% of inorganic filler. The highly crystalline polypropylene resin has a melt index of 8~60 g/10 min and is an isotactic polypropylene, propylene-ethylene comonomer, propylene-1-butene copolymer, propylene-1-hexane copolymer, propylene-4-methyl-1-pentene copolymer, a copolymer with propylene, a random copolymer of propylene and ethylene or their mixture.

Description

강성이 우수한 　고충격 폴리프로필렌 수지 조성물{High impact strength Polypropylene composition　having excellent rigidity}High impact strength polypropylene composition having excellent rigidity

본 발명은 충격특성이 우수하면서도 고강성도 함께 확보하여 내충격성과 강성이 모두 우수한 자동차 내장재용으로 적합한 폴리프로필렌 수지 조성물에 관한 것으로, 보다 상세하게는 운전자 및 승객에 직접 노출되는 내장 부품에 중요한 내충격성을 확보하면서 동시에 우수한 강성을 통하여 표면 손상성과 하중변형을 현저히 낮추고, 내열성 및 가공성을 확보한 고충격 폴리프로필렌 수지 조성물에 관한 것이다. 　The present invention relates to a polypropylene resin composition suitable for automotive interior materials having excellent impact characteristics and high rigidity together with excellent impact resistance and rigidity, and more particularly, impact resistance important for interior components directly exposed to drivers and passengers. The present invention relates to a high-impact polypropylene resin composition which secures heat resistance and workability while significantly lowering surface damage and load deformation through excellent rigidity.

기존 수지 조성물의 경우 자동차를 사용하는 과정에서 성형품의 표면이 쉽게 손상되거나 오염에 의하여 색상이 변색되는 문제를 갖고 있었으며, 이러한 문제의 해결을 위하여 폴리프로필렌 컴파운드 소재 또는 엔지니어링 플라스틱을 코아재로 사용하고, 폴리우레탄 폼과 염화비닐수지(P.V.C) 또는 열가소성 엘라스토머(T.P.E)를 표피재로 사용하고 있다. 그러나, 폴리우레탄 폼 및 염화비닐수지 또는 열가소 성 엘라스토머　표피재의 추가 공정에 따른 원가 상승과 재생이 불가능함에 따른 환경오염 문제가 제기되어 왔다.In the case of the existing resin composition, the surface of the molded product was easily damaged or discolored due to contamination, and in order to solve such a problem, a polypropylene compound material or an engineering plastic was used as a core material. Polyurethane foam and vinyl chloride resin (PVC) or thermoplastic elastomer (TPE) are used as the skin material. However, there have been problems of environmental pollution due to the cost increase and the inability to regenerate the polyurethane foam and the addition process of the vinyl chloride resin or the thermoplastic elastomer skin.

이와 같이 내장재로 사용되는 소재의 한계성을 극복하기 위하여 폴리프로필렌 수지 조성물의 내손상성을 향상시키기 위한 많은 연구가 진행되어 오고 있으며, 본 발명에서는 이런 문제를 해결하기 위하여 베이스 수지로서 고결정성 호모 폴리프로필렌(High Isotactic Polypropylene)을 적용하여 강성을 극대화하고 고무성분을 첨가하여 충격특성을 확보하였으며, 그에 따른 강성저하를 보완하기 위하여 특수한 무기충전제를 사용함으로써, 강성이 우수한 고충격 폴리프로필렌 수지 조성물을 개발하였다.In order to overcome the limitations of the materials used as interior materials, many studies have been conducted to improve the damage resistance of the polypropylene resin composition, and in the present invention, in order to solve such a problem, highly crystalline homopolypropylene ( High Isotactic Polypropylene) was applied to maximize the stiffness and add the rubber component to secure the impact characteristics, and the high impact polypropylene resin composition was developed by using a special inorganic filler to compensate for the decrease in stiffness.

자동차 분야에 있어서 경량화(Weight reduction) 및 고성능화가 지속적으로 이루어짐에 따라, 자동차용 부품으로 사용되는 플라스틱 소재에 대한 수요는 지속적으로 증가하고 있으며, 특히 폴리프로필렌은 저비중으로 인한 경량화 및 재활용의 용이성, 상대적으로 낮은 가격 등으로 인해 다른 플라스틱 소재에 비해 그 수요가 급격히 늘고 있는 추세이다. As the weight reduction and high performance are continuously made in the automobile field, the demand for plastic materials used as automotive parts is continuously increasing. In particular, the polypropylene has a low weight, easy to recycle and easy to recycle, Due to the relatively low price, the demand is increasing rapidly compared to other plastic materials.

또한 자동차 내장재는 부품별로 그 구조에 따라서 요구 물성 수준이 다양하게 구별되어 적용하고 있기 때문에 적용되는 소재 또한 강성과 충격강도의 균형을 이루기 위하여 함유되는 무기 첨가제와 고무성분 함량을 조절한 다양한 재료가 적용되고 있다. 따라서 내장재용으로 적용되는 폴리프로필렌 수지조성물의 가지 수가 많아지면서 그에 따른 부품 성형조건이나 금형기술 등 관련 생산성 문제를 가지고 있었다.In addition, since the required material properties are distinguished and applied according to the structure of automobile parts, the applied materials are also applied with various materials that adjust the content of inorganic additives and rubber components contained in order to balance stiffness and impact strength. It is becoming. Therefore, as the number of polypropylene resin compositions applied for interior materials increases, there are related productivity problems such as part molding conditions and mold technology.

이에 본 발명은 고입체 규칙성의 폴리프로필렌을 베이스로 충격강도를 유지한 상태에서 고무의 최적화와 강성보완 능력이 탁월한 특수한 무기충전재를 기존 탈크(talc)류와 함께 사용하여 강성 향상에 의한 충격특성 저하를 최소화한 수지 조성물을 개발하였다.Therefore, the present invention uses a special inorganic filler having excellent optimization of stiffness and stiffness of the rubber in the state of maintaining the impact strength on the basis of polypropylene of high solidity regularity, in combination with the existing talc, thereby deteriorating the impact characteristics by improving the rigidity. The resin composition which minimized was developed.

이와 관련하여 대한민국공개특허 2005-0093186호에서는 강성 확보를 위하여 무기계 충전제인 탈크 혹은 유리섬유 등을 적용 하였으나, 탈크의 경우 충격강도 저하가 문제가 되고, 유리섬유의 경우 휨 변형 및 성형성 저하 문제가 있으며, 외관이 거칠어져서 자동차용 내장재로 사용하기에는 한계가 있었다.In this regard, in Korean Patent Laid-Open Publication No. 2005-0093186, talc or glass fiber, which is an inorganic filler, is used to secure rigidity. However, in the case of talc, the impact strength is deteriorated, and in the case of glass fiber, there is a problem of warpage deformation and moldability. In addition, the exterior was rough, there was a limit to use as interior materials for automobiles.

본 발명은 상기와 같은 종래기술들의 문제점을 해결하고자 하는 것으로, 본 발명의 목적은 강성이 우수한 호모 폴리프로필렌에 고무성분을 첨가함으로서 자동차용 내장재로서 요구되어지는 충격강도를 확보하고, 휘스커와 탈크 등 필러(Filler)를 첨가하여 강성과 내 표면 손상성을 향상시킨 고충격 폴리프로필렌 수지 조성물을 제공하는 것을 그 목적으로 한다.The present invention is to solve the problems of the prior art as described above, the object of the present invention is to add a rubber component to the homopolypropylene excellent in rigidity to secure the impact strength required as a vehicle interior material, whiskers and talc It is an object to provide a high impact polypropylene resin composition in which a filler is added to improve rigidity and surface damage resistance.

본 발명은 상기의 문제점을 해결하기 위한 것으로, C-NMR법에 의한 아이소탁틱 펩타드분율이 96% 이상인 고결정성 폴리프로필렌 수지(HIPP) 20 ~ 92 중량%, 고무성분의 충격보강제 3 ~ 30 중량%, 및 무기충전재 5 ~ 50 중량%인 강성이 우수한 고충격 폴리프로필렌 수지 조성물을 제공한다.The present invention is to solve the above problems, 20 to 92% by weight of a high crystalline polypropylene resin (HIPP) isotactic peptides by C-NMR method is 96% or more, 3 ~ 30 weight of the impact modifier of the rubber component It provides a high impact polypropylene resin composition having excellent rigidity of 5% to 50% by weight, and inorganic filler.

또한, 상기 고결정성 폴리프로필렌 수지는 용융지수 1∼60g/10min이며, 아이소탁틱 폴리프로필렌, 프로필렌-에틸렌 코모노머, 프로필렌 1 부텐 코폴리머, 프로필렌 1 헥센 코폴리머, 프로필렌 4 메틸 1 펜텐 코폴리머, 　프로필렌과의 코폴리머, 　프로필렌과 에틸렌의 랜덤 공중합체 또는 이들의 혼합물을 혼용하는 것을 특징으로 한다.In addition, the high crystalline polypropylene resin has a melt index of 1 to 60 g / 10 min, isotactic polypropylene, propylene-ethylene comonomer, propylene 1 butene copolymer, propylene 1 hexene copolymer, propylene 4 methyl 1 pentene copolymer, propylene It is characterized by mixing a copolymer with, a random copolymer of propylene and ethylene, or a mixture thereof.

또한, 상기 무기충전제는 평균입경이 1.0 ㎛이하이고, 길이가 10 ~ 80㎛ 범위의 마그네슘 휘스커를 사용하는 것을 특징으로 한다.In addition, the inorganic filler is characterized by using a magnesium whisker having an average particle diameter of 1.0 ㎛ or less, the length of 10 ~ 80㎛ range.

또한, 상기 고무 성분의 충격보강재는 프로필렌, 부텐1, 펜텐1, 헥산1, 옥텐1, 4-메틸 펜텐1, 헵텐1, SEBS, SEPS, SEP, SEEPS, SBS, SIS를 첨가하는 것을 특징으로 한다.In addition, the impact modifier of the rubber component is characterized in that propylene, butene 1, pentene 1, hexane 1, octene 1, 4-methyl pentene 1, heptene 1, SEBS, SEPS, SEP, SEEPS, SBS, SIS is added. .

또한, 상기 무기충전제는 탈크, 유리섬유, 활석, 운모, 탄산칼슘, 규회석, 황산바륨, 클레이 또는 그 혼합물을 포함하는 것을 특징으로 한다.In addition, the inorganic filler is characterized in that it comprises talc, glass fibers, talc, mica, calcium carbonate, wollastonite, barium sulfate, clay or mixtures thereof.

본 발명에 의하면, 강성 및 내충격성, 내표면 손상성이 향상된 고충격 폴리프로필렌 수지 조성물을 제공하여, 인판넬 등 탑승자의 안전성이 중요시되는 자동차용 내장재용 소재로 사용하기에 적합하다.According to the present invention, by providing a high-impact polypropylene resin composition with improved rigidity, impact resistance, and surface damage resistance, it is suitable for use as an interior material for automobiles where safety of occupants such as inpanel is important.

본 발명에 사용된 폴리프로필렌 수지로서는 내백화성을 확보하기 위해 결정성이 높은 호모 폴리프로필렌을 기본으로 하여 충격특성을 보완하기 위하여 고무성분을 첨가하였으며, 충격특성 향상에 의한 강성 저하를 최소화 하기 위해 　위해 기존의 탈크 외에 마그네슘 결정 섬유 형태의 휘스커를 사용함으로서 강성도 우수한 수지 조성물을 얻었다.As the polypropylene resin used in the present invention, a rubber component was added to complement the impact characteristics based on homocrystalline polypropylene having high crystallinity to secure whitening resistance, and to minimize the stiffness deterioration due to the improvement of the impact characteristics. In addition to the conventional talc, by using a whisker in the form of magnesium crystal fibers, a resin composition excellent in rigidity was obtained.

특히 고결정성의 폴리프로필렌 수지의 경우 아이소택틱 지수가 높은 호모 폴리프로필렌 수지가 적당하며, 강성과 충격강도의 균형을 이루기 위하여 일부 고결정성 에틸렌-프로필렌 공중합 수지를 혼합하여 사용하는 것이 바람직하다.Particularly, in the case of high crystalline polypropylene resin, a homo polypropylene resin having a high isotactic index is suitable, and in order to balance stiffness and impact strength, it is preferable to use a mixture of some high crystalline ethylene-propylene copolymer resins.

바람직한 고결정성 폴리프로필렌 수지는 C-NMR법에 의한 아이소탁틱 펩타드분율이 96% 이상인 폴리프로필렌 수지로, 그 용융지수는 1∼60g/10min이며, 아이소탁틱 폴리프로필렌, 프로필렌-에틸렌 코모노머, 프로필렌 1 부텐 코폴리머, 프로필렌 1 헥센 코폴리머, 프로필렌 4 메틸 1 펜텐 코폴리머, 　프로필렌과의 코폴리머, 　프로필렌과 에틸렌의 랜덤 공중합체 또는 이들의 혼합물을 혼용하여 사용할 수 있다. 　용융지수가 1g/10min　미만이면 사출성형성이 저하되므로 생산성이Preferred high crystalline polypropylene resins are polypropylene resins having an isotactic peptide content of 96% or more by C-NMR method, and their melt index is 1 to 60 g / 10 min, and isotactic polypropylene, propylene-ethylene comonomer, and propylene. A 1 butene copolymer, a propylene 1 hexene copolymer, a propylene 4 methyl 1 pentene copolymer, a copolymer with propylene, a random copolymer of propylene and ethylene, or a mixture thereof can be used in combination. If the melt index is less than 1g / 10min, the injection moldability is lowered, resulting in increased productivity.

저하되어 바람직하지 못하며, 60g/10min을 초과하면 충격강도 등 기계적 물성이 저하되므로 바람직하지 못하다.It is not preferable because it is lowered, and when it exceeds 60 g / 10 min, mechanical properties such as impact strength are lowered.

본 발명의 고결정성 폴리프로필렌 수지(HIPP)의 함량은 20 ~ 92 중량%를 사용하는 것이 바람직한데, 20 중량%　미만인 경우는 가공이 어렵기 때문에 바람직하지 못하고, 92 중량%　이상이면 무기 필러의 첨가량이 미약하여 강도개선 효과가 　낮아져서 바람직하지 못하다.The content of the high crystalline polypropylene resin (HIPP) of the present invention is preferably 20 to 92% by weight, but less than 20% by weight 하지 because it is difficult to process, if the content of the inorganic filler is more than 92% by weight 첨가 This is weak and the strength improvement effect is low, which is undesirable.

본 발명의 폴리프로필렌 조성물의 적당한 유연성 및 강성 균형을 위해서 고무 성분과 무기충전재의 쌍방을 함유하고 있는 것이 바람직한데, 상기 고무 성분의 첨가에 의하여 적절한 유연성을 얻을 수 있고, 저온 내충격 특성을 향상시키는 것이 가능하다.In order to balance the flexibility and rigidity of the polypropylene composition of the present invention, it is preferable to contain both the rubber component and the inorganic filler. By adding the rubber component, it is possible to obtain appropriate flexibility and to improve the low temperature impact resistance characteristics. It is possible.

상기 고무 성분으로 사용되는 충격보강재는 α올레핀 성분으로서 프로필렌, 부텐1, 펜텐1, 헥산1, 옥텐1, 4-메틸 펜텐1, 헵텐1 등이 있으며, 스티렌계 열가소성 일래스토머로서는 SEBS이외에 SEPS, SEP, SEEPS, SBS, SIS 등이 있다. The impact modifiers used as the rubber component include propylene, butene 1, pentene 1, hexane 1, octene 1, 4-methyl pentene 1, heptene 1, and the like as the α-olefin component, and SEPS, in addition to SEBS, as a styrene-based thermoplastic elastomer. SEP, SEEPS, SBS, and SIS.

본 발명에서 사용되는 고무성분의 함량은 3 ~ 30 중량%를 사용하는 것이 바람직한데, 3 중량%미만인 경우 충격강도 개선효과가 미약하여　바람직하지 못하며, 30 중량%을 초과하면 경제성이 떨어지고 제품 생산성도 저하되므로 바람직하지 못하다.　The content of the rubber component used in the present invention is preferably used in the range of 3 to 30% by weight, but less than 3% by weight of the impact strength improvement effect is not desirable, less than 30% by weight, economical efficiency and product productivity It is not preferable because it is lowered.

본 발명에서 사용되는 무기충전제는 평균입경이 1.0 ㎛이하이고, 길이가 10 ~ 80㎛ 범위의 마그네슘 휘스커를 첨가하여, 강성과 충격 특성의 균형을 확보할 수 있다.　마그네슘 휘스커는 각주형태와 같은 결정구조적인 특성 때문에 충격강도와 강성의 균형이 우수하다. The inorganic filler used in the present invention has an average particle diameter of 1.0 μm or less, and a magnesium whisker having a length of 10 to 80 μm is added to secure a balance between stiffness and impact characteristics. Magnesium whiskers have a good balance of impact strength and stiffness due to the crystal structure characteristics such as footnote shape.

상기의 마그네슘 결정구조를 갖는 휘스커 이외에 유리섬유, 활석, 운모, 탄산칼슘, 규회석, 황산바륨, 클레이 등의 그룹으로부터 선택된 1종 이상을 혼용하여 강성을 조절하는 것도 가능하다. In addition to the whiskers having the magnesium crystal structure described above, the stiffness may be adjusted by mixing one or more selected from the group consisting of glass fibers, talc, mica, calcium carbonate, wollastonite, barium sulfate, clay and the like.

본 발명에서 사용되는 무기충전제의 함량은 5 ~ 50 중량%를 사용하는 것이 바람직한데, 5 중량%　미만인 경우 일반PP에 비하여 무기물의 충전효과가 미약하기 때문에 바람직하지 못하며, 50 중량%을 초과하면 생산성이 저하되므로 바람직하지 못하다.The content of the inorganic filler used in the present invention is preferably used 5 to 50% by weight, less than 5% by weight not preferable because the filling effect of the inorganic material is weak compared to the general PP, if the content exceeds 50% by weight It is not preferable because it is lowered.

본 발명의 조성물에는 색을 위하여 첨가될 수 있는 무기 안료와 유기 안료, 안정제로서 첨가될 수 있는 각종 첨가제, 예를 들면 장기 내열안정제, 내후안정제, 대전방지제, 활제, 슬립제(SLIP제), 핵제, 난연제 등을 본 발명의 목적에 어긋나지 않는 범위에서 첨가하는 것이 가능하다.Inorganic pigments and organic pigments that can be added for color, various additives that can be added as stabilizers, for example, long-term heat stabilizers, weather stabilizers, antistatic agents, lubricants, slip agents (SLIP agents), nucleating agents , Flame retardants and the like can be added within a range not inconsistent with the object of the present invention.

　

이하, 본 발명을 실시예를 통하여 더욱 구체적으로 설명하지만, 본 발명이 하기의 실시예에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited by the following Examples.

　

실시예Example 1~2 및  1 and 2 and 비교예Comparative example 1~2 1 ~ 2

하기에 기재된 성분을 포함하여 실시예 1~2 및 비교예 1~2의 폴리프로필렌 수지 조성물을 표　2와 같이 합성하였다.The polypropylene resin compositions of Examples 1 and 2 and Comparative Examples 1 and 2 were synthesized as shown in Table 2, including the components described below.

　　1) 폴리프로필렌: 고결정성 호모 폴리프로필렌, 삼성토탈, 용융지수(MI): 25g/10분 1) Polypropylene: Highly crystalline homo polypropylene, Samsung Total, Melt index (MI): 25g / 10min

　　2) 무기충전제1 : Whisker, BASF, 비중 : 2.3, 직경 : <　1.0 ㎛, 길이 : 10 ~ 80㎛2) Inorganic filler 1: Whisker, BASF, specific gravity: 2.3, diameter: <1.0 ㎛, length: 10 ~ 80㎛

　　3) 무기충전제2 : 탈크, KoCH, 비중 2.7, 직경 3 -4 ㎛3) Inorganic filler 2: Talc, KoCH, specific gravity 2.7, diameter 3-4 ㎛

　　4) 충격보강제 　: EXRB Rubber, Dow, E-88424) Impact modifier EX: EXRB Rubber, Dow, E-8842

하기 표 1은 충격보강제의 고무성분의 특성을 나타낸 것이다.Table 1 shows the characteristics of the rubber component of the impact modifier.

　

밀 도 [g/cm3]Density [g / cm 3 ] Comonomer 함량[wt%]Comonomer content [wt%] 경도 [Shore A]Shore A 유동 지수[g/10min]Flow index [g / 10min] 0.8570.857 4545 5050 1.01.0

　

조성Furtherance 비교예-1Comparative Example-1 비교예-2Comparative Example-2 비교예-3Comparative Example-3 실시예-1Example-1 실시예-2Example-2 폴리프로필렌Polypropylene 100100 8383 6969 6969 6969 무기충전제1Inorganic filler 1 　 　 　 1414 77 무기충전제2Inorganic fillers 2 　 　 1414 　 77 충격보강제Impact modifier 　 1717 1717 1717 1717

이와 같은 성분 및 배합 비율(표　1 참조)로, 폴리프로필렌, 탈크, 충격보강제 및 안정제(산화방지제 등)를 헨셀믹서로 드라이 블렌드 한 후, JSW TEX44 알파(ALPHA) 2축 혼련압출기의 호퍼에 한번에 모두 투입시키고, 휘스커는 압출기 도중 측면공급으로 투입하여 압출기 내부에서 함께 용융 혼련하여 동 수지 조성물을 제조한 후, 삼성클뢰크너 FCM-110(형체력=110톤)을 이용하여 사출성형방법으로 ASTM D790 규격에서 규정한 굴곡강도 측정용 시편과 ASTM D256 규격에서 규정한 Izod 충격강도 측정용 시편을 제작하였다.With these ingredients and blending ratios (see Table 1), dry blend polypropylene, talc, impact modifiers and stabilizers (antioxidants, etc.) with a Henschel mixer, and then at once in the hopper of the JSW TEX44 Alpha (ALPHA) twin-screw kneading extruder. The whiskers were fed into the side feed during the extruder, melt kneaded together in the extruder to prepare the copper resin composition, and then using Samsung Kleukner FCM-110 (molding force = 110 tons) as an injection molding method using ASTM D790 standard. Specimens for bending strength measurement as defined in US and Izod impact strength measurement specimens as specified in ASTM D256 standard were fabricated.

다음으로, 　ASTM 　규격에서 정하는 시편을 제작하여 기계적 물성을 비교 측정한 결과, 기계적 물성 특히 강성과 충격 균형이 매우 우수함을 확인할 수 있었다. 측정 결과를 하기 표 3에 나타내었다.Next, as a result of measuring and measuring the mechanical properties of the specimens specified in the ASTM standard, it was confirmed that the mechanical properties, in particular, the stiffness and impact balance are very good. The measurement results are shown in Table 3 below.

　물성 항목Property item 단위unit 비교예-1Comparative Example-1 비교예-2Comparative Example-2 비교예-3Comparative Example-3 실시예-1Example-1 실시예-2Example-2 　굴곡탄성율Flexural modulus kg/cm2kg / cm2 12,50012,500 8,6008,600 16,70016,700 32,18032,180 28,25028,250 　IZOD충격(23℃)IZOD Shock (23 ℃) kg.cm/cmkg.cm/cm 7.87.8 NBNB 31.231.2 30.630.6 30.930.9

물성 평가 결과에서 보면, 실시예 1에서 보듯이 기본적으로 휘스커를 사용한 수지조성물은 비교예 2의 탈크만을 사용했을 경우보다 굴곡탄성율이 월등히 향상됨을 알 수 있으며, 이를 통해 실시예 2에서처럼 휘스커와 탈크를 적당량 조합 함으로서 충격특성이 유지되고 굴곡탄성이 월등히 우수한 최적의 내장재용 수지 조성물을 확보 할 수 있었다.In the results of evaluation of physical properties, as shown in Example 1, the resin composition using the whisker basically shows that the flexural modulus is significantly improved compared with the case of using only talc of Comparative Example 2. By combining the appropriate amount, it was possible to secure an optimal resin composition for interior materials having impact characteristics and excellent flexural elasticity.

Claims (5)

C-NMR법에 의한 아이소탁틱 펩타드분율이 96% 이상인 고결정성 폴리프로필렌 수지(HIPP) 20　~ 92 중량%, 고무성분의 충격보강제 3 ~ 30 중량%, 및 무기충전재 5 ~ 50중량%인 강성이 우수한 고충격 폴리프로필렌 수지 조성물.Rigid polypropylene resin (HIPP) having 20% to 92% by weight of isotactic peptide content by C-NMR method, 3 to 30% by weight of impact modifier of rubber component, and 5 to 50% by weight of inorganic filler This excellent high impact polypropylene resin composition. 　　 제 1항에 있어서, 상기 고결정성 폴리프로필렌 수지는 용융지수 8∼60g/10min이며, 아이소탁틱 폴리프로필렌, 프로필렌-에틸렌 코모노머, 프로필렌 1 부텐 코폴리머, 프로필렌 1 헥센 코폴리머, 프로필렌 4 메틸 1 펜텐 코폴리머, 　프로필렌과의 코폴리머, 프로필렌과 에틸렌의 랜덤 공중합체 또는 이들의 혼합물을 혼용하는 것을 특징으로 하는 강성이 우수한 고충격 폴리프로필렌 수지 조성물.The method of claim 1, wherein the high crystalline polypropylene resin has a melt index of 8 to 60g / 10min, isotactic polypropylene, propylene-ethylene comonomer, propylene 1 butene copolymer, propylene 1 hexene copolymer, propylene 4 methyl 1 pentene A high impact polypropylene resin composition having excellent rigidity, characterized by mixing a copolymer, a copolymer with propylene, a random copolymer of propylene and ethylene, or a mixture thereof. 　 제 1항에 있어서, 상기 무기충전제는 평균입경이 1.0 ㎛이하이고, 길이가 10 ~ 80㎛ 범위의 마그네슘 휘스커를 사용하는 것을 특징으로 하는 강성이 우수한 고충격 폴리프로필렌 수지 조성물.The high impact polypropylene resin composition of claim 1, wherein the inorganic filler has an average particle diameter of 1.0 µm or less and a magnesium whisker having a length of 10 to 80 µm. 　 제 1항에 있어서, 상기 고무 성분의 충격보강재는 프로필렌, 부텐1, 펜텐1, 헥산1, 옥텐1, 4-메틸 펜텐1, 헵텐1, SEBS, SEPS, SEP, SEEPS, SBS, SIS를 첨가하는 것을 특징으로 하는 강성이 우수한 고충격 폴리프로필렌 수지 조성물.According to claim 1, wherein the impact modifier of the rubber component is propylene, butene 1, pentene 1, hexane 1, octene 1, 4-methyl pentene 1, heptene 1, SEBS, SEPS, SEP, SEEPS, SBS, SIS is added A high impact polypropylene resin composition excellent in rigidity. 　 제 3항에 있어서, 상기 무기충전제는 탈크, 유리섬유, 활석, 운모, 탄산칼슘, 규회석, 황산바륨, 클레이 또는 그 혼합물을 포함하는 것을 특징으로 하는 강성이 우수한 고충격 폴리프로필렌 수지 조성물.The high impact polypropylene resin composition having excellent rigidity of claim 3, wherein the inorganic filler comprises talc, glass fiber, talc, mica, calcium carbonate, wollastonite, barium sulfate, clay, or a mixture thereof.
KR1020080086191A 2008-09-02 2008-09-02 High impact strength polypropylene composition having excellent rigidity KR20100027322A (en)