KR101882416B1 - Adhesive composition for sports taping having phytoncide oil capsule and functional tape for sports taping having the same - Google Patents

Abstract

The present invention provides an adhesive composition comprising 100 parts by weight of an adhesive; And 0.05 to 5.5 parts by weight of a phytoncide oil capsule, wherein the phytoncide oil capsule comprises a capsule and a phytoncide oil contained in the capsule. Thus, by introducing the composition containing the phytoncide oil capsules of the present invention into the adhesive layer of the tape used for sports taping, the pharmacological treatment of the muscles is performed, and at the same time the pharmacological treatment is directly absorbed to the skin, The wound can be treated effectively.

Description

TECHNICAL FIELD [0001] The present invention relates to an adhesive composition for sports taping comprising a phytoncide oil capsule, and a functional tape for sports taping including the same. BACKGROUND OF THE INVENTION 1. Field of the Invention < RTI ID = 0.0 &

The present invention relates to an adhesive composition for sports taping and a functional tape for sports taping comprising the same. More particularly, the present invention relates to a functional tape for sports taping comprising a composition comprising a phytoncide oil capsule as an adhesive layer on a sheet, And a functional tape for sports taping comprising the same.

Nowadays, modern people suffer from pain caused by various factors. Various causes such as exercise or work, improper posture, and mental stress can inflame the muscles and cause pain. For example, there may be a variety of symptoms, such as stiff shoulder muscles due to computer work over a long period of time, swollen leg muscles when standing or standing.

In this way, the muscles become tense or damaged and the muscles are swollen, so that circulation of the blood vessels, the lymph and the tissue fluid can not be smoothly performed, and the pain can be caused thereby. In this case, when the tape having elasticity similar to the elasticity of the muscle is stuck to the painful area, the space of the skin and the muscle is increased to increase the circulation of the blood and the lymph fluid and the tissue fluid to relieve the pain, Can help mitigate. It is called taping therapy to help relieve pain by attaching specially treated tape like this.

Taping therapy was developed during the study of sports taping by Dr. Kase Kenzo of Japan in the 1970s for the purpose of treating muscle and arthritis. This method has the effect of preventing the pain from being relieved and injured by sticking the stretchable tape having the same elasticity as that of the human body to the skin by stretching the muscles of the affected part with the effect of preventing the pain or pre-exercise. The principle is to increase the circulation of blood, lymph and nervous system by increasing the tension between the skin and the muscles by lifting the skin with the same contractile force as that of the human body, thereby improving the natural healing power of the pain area. Taping therapy is a non-surgical, non-pharmacologic therapy with little side effects and can be easily applied to pregnant women, children, and the elderly, regardless of sex.

Taping therapy is a method of applying a tape to the muscles in order to normalize the movement of the main muscles of the moving body, thereby promoting the circulation of the blood, lymph and tissue fluid, and the method of suppressing or promoting the tension of the muscles, Kinesiotaping, a stretch tape, is used for therapeutic purposes by increasing the blood and lymph circulation between the muscles and skin by improving the movement of the muscles by attaching the joints according to the motion of the moving muscles. These Kinesio taping therapies are widely used in daily life as well as sports, and can be applied without any particularly worrying side effects.

However, most current sports taping is limited to the physical treatment of muscles as described above, and there is a lack of research on techniques that can easily perform the pharmacological treatment and the physical treatment of muscles.

Korean Patent Registration No. 10-1327400 Korean Patent Publication No. 10-2016-0057811

It is an object of the present invention to provide a method and an apparatus for applying physical therapy to muscles by introducing a composition comprising a phytoncide oil capsule into an adhesive layer of a tape used for sports taping, The present invention provides a functional tape capable of efficiently treating the functional tape.

According to an aspect of the present invention,

100 parts by weight of an adhesive; And 0.05 to 5.5 parts by weight of a phytoncide oil capsule, wherein the phytoncide oil capsule comprises a capsule and phytoncide oil contained in the capsule.

The phytoncide oil may be extracted from at least one plant selected from the group consisting of cottonwood, bamboo, pine, fir and cedar.

The capsule may be a biodegradable polymer compound.

The biodegradable polymer compound may be at least one selected from a natural polymer compound and a synthetic polymer compound.

Wherein the biodegradable polymer compound has a number average molecular weight (Mn) of 50,000 to 80,000.

The natural polymer compound may be at least one selected from starch, chitin, and cellulose.

The synthetic polymer compound may be at least one selected from the group consisting of PCL (caprolactone), PLA (poly (lactic acid), PGA (poly glycolic acid), and PLGA (poly lactate-co-glycolate)).

The capsules may have an average diameter of 0.5 to 5 탆.

The capsule may have a wall thickness of 0.05 to 0.5 탆.

The weight ratio of the adhesive to the phytoncide oil capsules may be from 10: 1 to 2: 1.

According to another aspect of the present invention,

(a) preparing an adhesive; (b) encapsulating phytoncide oil to produce a phytoncide oil capsule; And (c) mixing the adhesive and the phytoncide oil capsules.

The phytoncide oil can be extracted by any one method selected from steam distillation method, compression method, oil absorption method and supercritical fluid extraction method.

The step (b) comprises: (b-1) preparing phytoncide oil extracted from a predetermined plant;

(b-2) mixing the phytoncide oil, the biodegradable polymer compound, the organic solvent and the dispersing agent to prepare a mixed solution; And

(b-3) evaporating the organic solvent in the mixed solution to encapsulate the phytoncide oil to prepare a phytoncide oil capsule.

In the step (b), the diameter of the phytoncide oil capsule can be controlled by adjusting the amount of the dispersant or by controlling the mixing rate of the mixed solution.

In the step (b), the thickness of the wall material of the phytoncide oil capsule can be controlled by controlling the amount of the biodegradable polymer compound for the phytoncide oil.

According to another aspect of the present invention,

Sheet; And an adhesive layer formed on one side of the sheet, wherein the adhesive layer comprises the adhesive composition for sports taping.

The sheet can be a fabric sheet.

The functional tape for sports taping may have a moisture permeability of 5.000 g / m2 24 hours to 6.000 g / m2 24 hours.

The content of the phytoncide oil capsules per unit area (m ² ) of the adhesive layer may be 100 to 5,000 mg.

The thickness of the adhesive layer may be 3 to 15 mu m.

According to another aspect of the present invention,

 (1) preparing a sheet and an adhesive composition for sports taping prepared according to the above-described method; And (2) applying the adhesive composition for sports taping on one side of the sheet to form an adhesive layer.

In step (2), the adhesive layer may be formed by any one method selected from roll coating, bar coating, dip coating, and spin coating.

The present invention relates to a method and apparatus for applying physical therapy to muscles by introducing a composition comprising a phytoncide oil capsule into an adhesive layer of a tape used for sports taping, and simultaneously performing pharmacological treatment in which pharmacological substances are directly absorbed by the skin, .

1 is a schematic view of a section of a functional tape for sports taping according to the present invention.
2 is a view showing that the functional tape for sports taping of the present invention is wound in a roll form.
3 is a scanning electron microscope (SEM) photograph of the phytoncide oil capsule used in Example 1 of the present invention.
Fig. 4 shows an optical microscope image of the surface of the functional tape for sports taping produced according to Example 1. Fig.

BRIEF DESCRIPTION OF THE DRAWINGS The present invention is capable of various modifications and various embodiments, and specific embodiments are illustrated in the drawings and described in detail in the detailed description. It is to be understood, however, that the invention is not to be limited to the specific embodiments, but includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

The terms first, second, etc. may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another.

The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises" or "having" and the like are used to specify that there is a feature, a number, a step, an operation, an element, a component or a combination thereof described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. Referring to the accompanying drawings, the same or corresponding components are denoted by the same reference numerals, do.

First, the adhesive composition for sports taping of the present invention will be described.

The adhesive composition for sports taping of the present invention includes an adhesive and a phytoncide oil capsule. Specifically, the composition comprises 100 parts by weight of an adhesive; And 0.05 to 5.5 parts by weight of a phytoncide oil capsule.

The phytoncide oil capsule may include a capsule and phytoncide oil contained in the capsule.

The phytoncide oil can be extracted from cotton, wood, pine, fir, cedar and the like, but the scope of the present invention is not limited thereto, and various plants containing phytoncide oil can be applied.

The adhesive may be an acrylic adhesive, a urethane adhesive, a silicone adhesive, a styrene-butadiene adhesive or the like, preferably a urethane adhesive.

The capsule may be a biodegradable polymer compound.

The biodegradable polymer compound may have a number average molecular weight (Mn) of 50,000 to 80,000, more preferably 60,000 to 80,000.

By using the biodegradable polymer compound, it is possible to produce a sustained-release capsule which slowly releases the pharmacological agent.

The biodegradable polymer compound may be a natural polymer compound or a synthetic polymer compound.

The natural polymer compound may be starch, chitin, cellulose, gelatin, or the like.

The synthetic polymer compound may be PCL (caprolactone), PLA (poly (lactic acid), PGA (poly (glycolic acid), PLGA (poly (lactate-co-glycolate)

The types of the biodegradable polymer compounds exemplified above are not limited thereto, and various possible materials can be applied within the scope of the present invention.

The capsules contained in the phytoncide oil capsules preferably have an average diameter of 0.5 to 5 mu m, more preferably 1 to 4 mu m, and still more preferably 1 to 3 mu m.

The thickness of the wall material of the capsule is preferably 0.05 to 5 mu m, more preferably 0.5 to 4 mu m, further preferably 1 to 3 mu m.

The thinner the thickness of the capsule, the higher the moisture permeability can be, and thus the release of the pharmacological substance contained in the capsule may be advantageous. Therefore, the thickness of the capsule can be adjusted as necessary in consideration of the release rate of the pharmacological agent and the density of the capsule.

The weight ratio of the adhesive to the phytoncide oil capsules is preferably 10: 1 to 2: 1 as an adhesive: phytoncide oil capsules. However, the scope of the present invention is not limited thereto, and the adhesiveness of the adhesive, The content ratio can be adjusted.

Hereinafter, a method of manufacturing an adhesive composition for sports taping of the present invention will be described.

First, an adhesive is prepared (step a).

Since the kind of the adhesive is the same as that described above, the details will be referred to.

In addition, phytoncide oil is encapsulated to produce phytoncide oil capsules (step b).

Step (b) can be embodied as the following steps.

First, a phytoncide oil extracted from a predetermined plant such as Japanese white rice is prepared (b-1).

At this time, phytoncide oil may be prepared by extracting from the plant using steam distillation method, compression method, oil absorption method, supercritical fluid extraction method or the like, or, in some cases, commercially available phytoncide oil may be purchased and used.

Then, a mixed solution is prepared by mixing the phytoncide oil, the biodegradable polymer compound, the organic solvent and the dispersant (b-2).

The biodegradable polymer compound is the same as described above.

The organic solvent may be dichloromethane (DCM) or the like, but the scope of the present invention is not limited thereto.

The dispersant (stabilizer) is used to uniformly disperse phytoncide oil in a mixed solution. Poly (vinyl alcohol) (number average molecular weight: 15,000 to 30,000) may be used, but the scope of the present invention is not limited thereto Do not.

Next, a phytoncide oil capsule is prepared by evaporating the organic solvent in the mixed solution to encapsulate the phytoncide oil (b-3).

It is preferable to encapsulate the phytoncide oil in accordance with the solution evaporation method as described above. The capsules of phytoncide oil can be prepared by causing the wall material, that is, the biodegradable polymer compound, to solidify on the outer wall of the phytoncide oil by reducing the pressure while maintaining the mixed solution at 30 ° C to evaporate the organic solvent.

In the encapsulation process, the diameter of the phytoncide oil capsules can be controlled by adjusting the amount of the dispersing agent (stabilizer) in the mixed solution or by controlling the mixing rate of the mixed solution.

In addition, the thickness of the wall material of the phytoncide oil capsule can be controlled by controlling the amount of the biodegradable polymer compound to the phytoncide oil during the encapsulation process.

Hereinafter, the functional tape 10 for sports taping of the present invention will be described with reference to Figs. 1 and 2. Fig.

Fig. 1 is a schematic view of a section of a functional tape 100 for sports taping according to the present invention, and Fig. 2 is a view showing that a functional tape 100 for sports taping according to the present invention is wound in a roll form.

1 and 2, a functional tape 100 for sports taping according to the present invention comprises a sheet 10; And an adhesive layer (20) formed on one side of the sheet (10).

The adhesive layer (20) comprises 100 parts by weight of the adhesive (22); And 0.05 to 5.5 parts by weight of a phytoncide oil capsule (24), and the phytoncide oil capsule (24) may comprise a capsule and phytoncide oil contained in the capsule. In other words, the adhesive layer may comprise the above-described adhesive composition for sports taping of the present invention.

The sheet 20 is preferably a fabric sheet, but the scope of the present invention is not limited thereto. The sheet 20 may be applied to skin of a human body and the like, so that it can be deformed according to bending or movement of the skin surface. And a sheet of the shape can be applied.

The functional tape 100 for sports taping is preferably that the moisture permeability of the adhesive layer 20 is 5.000 g / m2 24 hours to 6.000 g / m2 24 hours, but the scope of the present invention is not limited thereto. The moisture permeability of the adhesive layer 20 is related to the rate at which the oil contained in the phytoncide oil capsule 24 contained in the adhesive layer 20 is discharged to the outside. Therefore, the moisture permeability can be controlled according to the required amount of absorbed into the skin in contact with the adhesive layer 20.

Unit area (m ² ) of the adhesive layer 20 The content of the phytoncide oil capsule (24) is preferably 100 to 5,000 mg, but the scope of the present invention is not limited thereto. The strength of the pharmacological treatment, The content can be controlled by taking into consideration the degree and the like.

The thickness of the adhesive layer is preferably 3 to 15 mu m, more preferably 4 to 8 mu m.

Hereinafter, a method of manufacturing a functional tape for sports taping according to the present invention will be described.

First, a sheet and an adhesive composition for sports taping prepared according to the above-described method are prepared (step 1).

Next, the adhesive composition for sports taping is applied on one side of the sheet to form an adhesive layer to produce a functional tape for sports taping (Step 2).

The adhesive layer may be formed by a roll coating method, a bar coating method, an immersion coating method, or a spin coating method. However, the scope of the present invention is not limited thereto. Any coating method capable of forming an adhesive layer having a uniform thickness can be used have.

[Example]

≪ Preparation of adhesive composition for sports taping >

Manufacturing example  One

Phytoncide oil extracted from commercially available pine trees (Tisserand (Young), Pine Oil) was used. .

The phytoncide oil was encapsulated by solution evaporation method using PCL (Polycaprolactone) (number average molecular weight (Mn) = 80,000) to encapsulate the phytoncide oil.

Specifically, in order to encapsulate the phytoncide oil, a mixture of a co-solvent of dichloromethane (DCM) and a PCL as a wall material is prepared, and the mixture is poured into water. To disperse the phytoncide oil, an appropriate amount of polyvinyl alcohol (PVA) Number average molecular weight: 15,000 to 30,000) was added and mixed to prepare a mixed solution.

Thereafter, solution evaporation was performed on the mixed solution. That is, the temperature of the mixed solution was reduced while maintaining the temperature at 30 캜 to vaporize the co-solvent DCM to solidify the wall material of the capsule on the outer wall of the phytoncide oil, thereby preparing a phytoncide oil capsule. The phytoncide oil capsules were collected by filtration and the PVA remaining on the capsule surface was removed by washing with distilled water during filtration.

The final prepared phytoncide oil capsules had an average diameter of 3 탆 and a wall thickness of 1.5 탆 on average.

A polyurethane adhesive (molecular weight: 8400 g / mole, glass transition temperature (Tg): -30 캜 as a result of GPC measurement) was prepared as an adhesive.

The adhesive composition for sports taping was prepared by mixing and mixing the phytoncide oil capsules prepared by the above method and the polyurethane adhesive in a weight ratio of 10: 100.

Manufacturing example  2

An adhesive composition for sports taping was prepared in the same manner as in Production Example 1, except that the weight ratio of phytonchid oil capsules: polyurethane adhesive was 25: 100 instead of 10: 100.

Manufacturing example  3

An adhesive composition for sports taping was prepared in the same manner as in Production Example 1, except that the weight ratio of phytonchid oil capsules: polyurethane adhesive was 50: 100 instead of 10: 100.

Manufacturing example  4

An adhesive composition for sports taping was prepared in the same manner as in Production Example 1, except that the wall thickness of the phytoncide oil capsules was 2.5 m on average instead of 1.5 m.

Manufacturing example  5

Except that the weight ratio of the phytoncide oil capsules: polyurethane adhesive was 25: 100 instead of 10: 100, and the wall thickness of the phytoncide oil capsules was 2.5 占 퐉 on average instead of 1.5 占 퐉. To prepare an adhesive composition for taping.

Manufacturing example  6

Except that the weight ratio of the phytoncide oil capsules: polyurethane adhesive was 50: 100 instead of 10: 100, and the thickness of the wall material of the phytoncide oil capsules was 2.5 占 퐉 on average instead of 1.5 占 퐉. To prepare an adhesive composition for taping.

Manufacturing example  7

An adhesive composition for sports taping was prepared in the same manner as in Preparation Example 1, except that the wall thickness of the phytolocidal oil capsules was adjusted to 3.0 mu m on average instead of 1.5 mu m.

Manufacturing example  8

Except that the weight ratio of the phytoncide oil capsule: polyurethane adhesive was 25: 100 instead of 10: 100, and the thickness of the wall material of the phytoncide oil capsule was 3.0 mu m on average instead of 1.5 mu m. To prepare an adhesive composition for taping.

Manufacturing example  9

Except that the weight ratio of the phytoncide oil capsule: polyurethane adhesive was 50: 100 instead of 10: 100, and the thickness of the wall material of the phytoncide oil capsule was 3.0 mu m on average instead of 1.5 mu m. To prepare an adhesive composition for taping.

≪ Preparation of functional tapes for sports taping >

Example  One

The adhesive sheet prepared in Production Example 1 was roll-coated on one surface of the fabric sheet to form a sheet having a thickness of 5 占 퐉 to a thickness of 5 占 퐉. To form a functional tape for sports taping.

Example  2

A functional tape for sports taping was prepared in the same manner as in Example 1, except that the adhesive composition prepared according to Preparation Example 2 was used instead of Preparation Example 1.

Example  3

A functional tape for sports taping was produced in the same manner as in Example 1, except that the adhesive composition prepared according to Production Example 3 was used instead of Production Example 1.

Example  4

A functional tape for sports taping was produced in the same manner as in Example 1, except that the adhesive composition prepared according to Production Example 4 was used instead of Production Example 1.

Example  5

A functional tape for sports taping was produced in the same manner as in Example 1, except that the adhesive composition prepared according to Production Example 5 was used instead of Production Example 1.

Example  6

A functional tape for sports taping was prepared in the same manner as in Example 1, except that the adhesive composition prepared according to Production Example 6 was used instead of Production Example 1.

Example  7

A functional tape for sports taping was prepared in the same manner as in Example 1, except that the adhesive composition prepared according to Preparation Example 7 was used instead of Production Example 1.

Example  8

A functional tape for sports taping was prepared in the same manner as in Example 1, except that the adhesive composition prepared according to Production Example 8 was used instead of Production Example 1.

Example  9

A functional tape for sports taping was produced in the same manner as in Example 1, except that the adhesive composition prepared according to Production Example 9 was used instead of Production Example 1.

The contents of Examples 1 to 9 of the present invention are summarized in Table 1 below.

division Adhesive layer Capsule wall material thickness (㎛) Ratio (% by weight) of capsule / adhesive Example 1 Production Example 1 1.5 10 Example 2 Production Example 2 1.5 25 Example 3 Production Example 3 1.5 50 Example 4 Production Example 4 2.5 10 Example 5 Production Example 5 2.5 25 Example 6 Production Example 6 2.5 50 Example 7 Production Example 7 3.0 10 Example 8 Production Example 8 3.0 25 Example 9 Production Example 9 3.0 50

[Test Example]

Test Example  1: Phytoncide oil capsules and sports For taping  Confirmation of manufacture of functional tape

A scanning electron micrograph of the phytoncide oil capsules used in the present invention is shown in FIG. According to FIG. 3, it can be seen that the phytoncide oil capsules are mainly distributed in a size of about 5 μm.

An optical microscope image of the surface of the functional tape for sports taping produced according to Example 1 is shown in Fig. According to Fig. 4, it can be seen that an adhesive layer in which phytoncide oil capsules are mixed on one side of the fabric sheet is formed on the fabric sheet.

Test Example  2: Adhesive composition Percutaneous  Absorption test

Percutaneous absorption tests were carried out using the respective adhesive compositions prepared according to Preparation Examples 1 to 9. Specifically, the compositions of Preparations 1 to 9 were each measured for the amount of phytoncide through a transdermal permeable membrane using a Franz cell analyzer

Transdermal Diffusion Test Model (size 25mm Discs, Qty: 60) was used at this time, and the amount of phytoncide absorbed into water was measured at a temperature of 35 ° C, which is similar to body temperature, after 24 hours. The amount of phytoncide absorbed in water was measured by ultraviolet spectroscopy, and the amount of phytoncide eluted was determined by comparing the absorbance at a certain wavelength band with the black concentration.

The results according to Test Example 2 are shown in Table 2 below.

division Capsule wall material thickness (㎛) Ratio (% by weight) of capsule / adhesive Water vapor permeability (g / m ² · 24 hours) Production Example 1 1.5 10 5.792 Production Example 2 1.5 25 5.786 Production Example 3 1.5 50 5.791 Production Example 4 2.5 10 5.711 Production Example 5 2.5 25 5.710 Production Example 6 2.5 50 5.707 Production Example 7 3.0 10 5.677 Production Example 8 3.0 25 5.664 Production Example 9 3.0 50 5.676

According to Table 2, the thinner the capsule wall material of the phytoncide oil capsule is, the higher the moisture permeability is, and the ratio of the phytoncide oil capsule to the adhesive has little influence on the moisture permeability.

Therefore, it is considered that the release rate of the pharmacological material of the functional tape for sports taping of the present invention can be controlled by adjusting the thickness of the wall material of the capsule.

Test Example  3: Sports For taping  Analysis of moisture permeability of functional tape

The moisture permeability was analyzed in the same manner as in Test Example 2 using the functional tapes for sports taping prepared according to Examples 1 to 9.

The results according to Test Example 3 are shown in Table 3 below.

division Capsule wall material thickness (㎛) Ratio (% by weight) of capsule / adhesive Water vapor permeability (g / m ² · 24 hours) Production Example 1 1.5 10 5.776 Production Example 2 1.5 25 5.790 Production Example 3 1.5 50 5.844 Production Example 4 2.5 10 5.691 Production Example 5 2.5 25 5.713 Production Example 6 2.5 50 5.787 Production Example 7 3.0 10 5.579 Production Example 8 3.0 25 5.629 Production Example 9 3.0 50 5.686

According to Table 3, as the result of Test Example 2, the thinner the capsule wall material of the phytoncide oil capsule was, the higher the moisture permeability was in the functional tapes for sports taping. The ratio of the phytoncide oil capsule to the adhesive hardly affected the moisture permeability It is not.

Accordingly, it is considered that the release rate of the pharmacological material of the functional tape for sports taping of the present invention can be controlled by adjusting the thickness of the wall material of the capsule contained in the adhesive layer.

While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, many modifications and changes may be made by those skilled in the art without departing from the spirit and scope of the invention as defined in the appended claims. The present invention can be variously modified and changed by those skilled in the art, and it is also within the scope of the present invention.

10: Sheet
20: Adhesive layer
22: Adhesive
24: Phytoncide oil capsules
100: Functional tape for sports taping

Claims (15)

Sheet; And
And an adhesive layer formed on one side of the sheet,
Wherein the adhesive layer comprises an adhesive composition for sports taping,
The adhesive composition for sports taping,
100 parts by weight of an adhesive; And
0.05 to 5.5 parts by weight of a phytoncide oil capsule,
Wherein the phytoncide oil capsule comprises a capsule and phytoncide oil contained in the capsule,
The capsule has a thickness of 1 to 3 占 퐉,
The moisture permeability of the adhesive layer is 5.000 g / m2 24 hours to 6.000 g / m2 24 hours,
Functional tape for sports taping, a percutaneous absorption type of phytoncide oil. The method according to claim 1,
Wherein the capsule is a biodegradable polymeric compound. 3. The method of claim 2,
Wherein the biodegradable polymer compound has a number average molecular weight (Mn) of 50,000 to 80,000. 3. The method of claim 2,
The biodegradable polymer compound is at least one selected from the group consisting of PCL (caprolactone), PLA (poly (lactic acid)), PGA (poly glycolic acid), and PLGA (poly lactate-co-glycolate) Functional tapes for sports taping. delete delete (1) preparing an adhesive composition for sheet and sports taping; And
(2) applying the adhesive composition for sports taping on one side of the sheet to form an adhesive layer,
The adhesive composition for sports taping,
(a) preparing an adhesive;
(b) encapsulating phytoncide oil to produce a phytoncide oil capsule; And
(c) mixing the adhesive and the phytoncide oil capsule,
(B) adjusting the amount of the biodegradable polymer compound to the phytoncide oil so that the wall thickness of the phytoncide oil capsule is 1 to 3 탆,
The moisture permeability of the adhesive layer is set to 5.000 g / m 2 24 hours to 6.000 g / m 2 24 hours,
A method for manufacturing a functional tape for sports taping which is a percutaneous absorption type of phytoncide oil. 8. The method of claim 7,
The step (b)
(b-1) preparing phytoncide oil extracted from a predetermined plant;
(b-2) mixing the phytoncide oil, the biodegradable polymer compound, the organic solvent and the dispersing agent to prepare a mixed solution; And
(b-3) evaporating the organic solvent in the mixed solution to encapsulate the phytoncide oil to produce a phytoncide oil capsule. 9. The method of claim 8,
Wherein the diameter of the phytoncide oil capsule is controlled by controlling the amount of the dispersant or adjusting the mixing speed of the mixed solution in the step (b). delete delete delete The method according to claim 1,
Wherein the content of the phytoncide oil capsules per unit area (m ² ) of the adhesive layer is 100 to 5,000 mg. The method according to claim 1,
Wherein the adhesive layer has a thickness of 3 to 15 占 퐉.
delete