KR101870942B1 - 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법 - Google Patents
황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법 Download PDFInfo
- Publication number
- KR101870942B1 KR101870942B1 KR1020170001800A KR20170001800A KR101870942B1 KR 101870942 B1 KR101870942 B1 KR 101870942B1 KR 1020170001800 A KR1020170001800 A KR 1020170001800A KR 20170001800 A KR20170001800 A KR 20170001800A KR 101870942 B1 KR101870942 B1 KR 101870942B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- loess
- solidifying agent
- sound
- Prior art date
Abstract
본 발명은 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법에 관한 것으로서, 더욱 상세하게는 흡음성과 난연 및 단열성이 우수한 황토를 이용하여 친환경적이고 안전한 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법에 관한 것이다.
본 발명은 황토 100중량부에 대하여 고화제 160 내지 240중량부와, 물 40 내지 80중량부와, 식물성 기포제 2 내지 6중량부와, 맥반석 및 숯과 실리카를 포함하는 첨가제 10 내지 20중량부를 함유한다.
본 발명은 황토 100중량부에 대하여 고화제 160 내지 240중량부와, 물 40 내지 80중량부와, 식물성 기포제 2 내지 6중량부와, 맥반석 및 숯과 실리카를 포함하는 첨가제 10 내지 20중량부를 함유한다.
Description
본 발명은 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법에 관한 것으로서, 더욱 상세하게는 흡음성과 난연 및 단열성이 우수한 황토를 이용하여 친환경적이고 안전한 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법에 관한 것이다.
일반적으로 건축용 마감보드는 건축물의 외부에 사용되는 외부마감보드와 건축물의 내부를 마감하는 내부마감보드를 포함한다.
이러한 건축용 마감보드는 사용처에 적합한 기능을 가져야 하며, 대체적으로, 실내마감보드는 난연성(또는 불연성), 흡음성 및 건강에 좋은 기능을 요구한다.
내부마감보드는 대개 암면, 석고보드 또는 합판보드 등이 이용된다. 이들 중, 암면은 발암성 물질의 배출 논란에 의해 현재는 거의 사용되지 않는다. 그리고, 합판보드는 무게가 가볍고 가격이 저렴하며 내충격성도 강할 뿐만 아니라 타 건축자재와의 혼합사용이 용이한 장점이 있으나 화재에 취약한 단점이 있다.
또한, 석고보드는 비교적 가격이 저렴하고 시공이 비교적 어렵지 않은 장점이 있으나, 강도대비 중량이 무겁고 내충격성이 약해 다루기 쉽기 않고 차음성, 내수성 등이 다소 떨어지는 단점을 갖는다. 게다가, 합판보드에 비해 내화성이 강하지만 화재발생시 석고보드의 결정수가 유리되어 벽체가 쉽게 붕괴되는 단점을 갖는다.
특히, 이들 종래의 내부마감보드는 흡음성능이 취약하며, 대개 별도로 구비되는 흡음재가 시공된다.
주로 사용되는 흡음재는 크게 무기계와 유기계 재료가 사용되어지며, 무기계 재료는 암면, 글라스 울, 유리섬유 등이 알려져 있고, 유기계 재료는 폴리에스터 섬유가 이용되거나 우레탄, 폴리프로필렌, 폴리에틸렌 등의 수지를 발포시킨 재료가 알려져 있다.
무기계 재료가 사용된 흡음재는 유기계 재료가 사용된 흡음재에 비하여 불에 잘 타지 않기 때문에 난연성 측면에서 우수하지만, 제조 공정상 발생하는 각종 분진 등이 인체에 유해할 뿐만 아니라 수분 등에 취약하여 장시간 사용시 흡음 및 단열성능이 저하되는 단점을 갖는다.
그리고, 유기계 재료가 사용된 흡음재중 발포 공정을 통해 제조되는 것들은 무기계 재료가 사용된 흡음재에 비하여 무게가 가볍고 내수성이 우수한 장점을 갖는 반면, 화재 발생시 유독가스가 발생할 뿐만 아니라 단독 사용이 곤란하며 충격에 약한 단점을 갖는다.
한편, 일반적으로 건축자재는 강도적인 측면에 중점을 두고 있어, 압축강도가 우수한 시멘트 성분이 건축자재가 주를 이루고 있다.
대한민국 등록특허 제10-0963907호에는 시멘트나 석고를 이용하여 얻은 경량기포단열재의 제조방법이 개시되어 있다. 그러나, 시멘트 성분은 장시간에 걸쳐 다량의 유해물질을 방출하므로, 그 실내에서 활동하는 인체에 좋지 않은 영향을 주게 되며, 노후로 인한 폐기처리시 유해한 건축폐기물이 다량 발생되는 문제점이 있었다.
상기와 같은 시멘트 성분 건축자재의 문제점으로 인하여 친환경적인 소재 개발에 대한 연구가 활발하게 진행되고 있으며, 이러한 영향으로 황토에 대한 연구가 활발하게 진행되고 있다. 그러나 황토는 시멘트에 대비할 경우, 압축강도가 현저하게 떨어지고, 황토자체만으로 블록 등의 건축자재를 형성할 경우, 쉽게 부서지는 문제점이 있었다.
본 발명은 상기의 문제점을 개선하고자 창출된 것으로서, 흡음성과 난연 및 단열성이 우수한 황토를 이용하여 친환경적이고 안전하며 물성이 우수한 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법을 제공하는 데 그 목적이 있다.
상술한 목적을 달성하기 위한 본 발명의 황토 흡음재용 조성물은 황토 100중량부에 대하여 고화제 160 내지 240중량부와, 물 40 내지 80중량부와, 식물성 기포제 2 내지 6중량부와, 맥반석 및 숯과 실리카를 포함하는 첨가제 10 내지 20중량부를 함유한다.
상기 고화제는 액상 고화제와 분말 고화제를 혼합하여 형성하며, 상기 액상 고화제는 규산나트륨 48 내지 52중량%, 염화칼슘 11 내지 14중량%, 염화칼륨 7 내지 9중량%, 염화마그네슘 7 내지 9중량%, 탄산나트륨 22 내지 24중량%를 함유하고, 상기 분말 고화제는 실리카퓸인 것을 특징으로 한다.
상기 황토 100중량부에 대하여 긴병꽃풀 추출물을 1 내지 10중량부를 더 함유한다.
그리고 상술한 목적을 달성하기 위한 본 발명의 황토 흡음재의 제조방법은 황토 100중량부에 대하여 분말 고화제 80 내지 120중량부를 혼합한 후 액상 고화제 80 내지 120중량부를 첨가하여 교반하는 교반단계와; 상기 교반단계에서 수득한 혼합물에 상기 황토 100중량부를 기준으로 물을 40 내지 80중량부를 첨가하여 반죽하는 반죽단계와; 상기 반죽단계에서 수득한 황토 반죽에 맥반석 및 숯과 실리카를 포함하는 첨가제를 상기 황토 100중량부를 기준으로 10 내지 20중량부를 첨가하여 교반하는 첨가단계와; 상기 첨가단계 후 상기 황토 반죽에 상기 황토 100중량부를 기준으로 식물성 기포제 2 내지 6중량부를 첨가하여 교반하는 기포형성단계와; 상기 기포형성단계 후 상기 황토 반죽을 성형틀에 주입하여 성형하는 성형단계와; 상기 성형틀에서 성형된 성형체를 양생하는 양생단계;를 포함한다.
상기 첨가단계는 상기 황토 100중량부를 기준으로 긴병꽃풀 추출물을 2 내지 10중량부를 더 첨가한다.
상술한 바와 같이 본 발명은 흡음성과 난연 및 단열성이 우수한 황토를 이용하여 친환경적이고 안전하며 물성이 우수한 황토 흡음재를 제조할 수 있다.
본 발명의 황토흡음재는 특히 항균성과 항곰팡이 특성이 우수하여 쾌적한 실내환경을 조성할 수 있다.
도 1 및 도 2는 본 발명의 황토 흡음재에 대한 항균 실험결과이고,
도 3 및 도 4는 본 발명의 황토 흡음재에 대한 항곰팡이 실험결과이다.
도 3 및 도 4는 본 발명의 황토 흡음재에 대한 항곰팡이 실험결과이다.
이하, 본 발명의 바람직한 실시 예에 따른 황토 흡음재용 조성물 및 이를 이용한 황토 흡음재의 제조방법에 대하여 구체적으로 설명한다.
본 발명의 일 예에 따른 황토 흡음재용 조성물은 황토, 고화제, 물, 식물성 기포제, 첨가제를 함유한다.
가령, 황토 흡음재용 조성물은 황토 100중량부에 대하여 고화제 160 내지 240중량부와, 물 40 내지 80중량부와, 식물성 기포제 2 내지 6중량부와, 첨가제 10 내지 20중량부로 조성될 수 있다. 이러한 황토 흡음재용 조성물은 모르타르와 같은 반죽 형태로 제공될 수 있다.
황토는 탄산칼슘(CaCO3), 실리카(SiO2), 알루미나(Al2O3), 철분, 마그네슘(Mg), 나트륨(Na), 칼리(K2O) 등을 포함하며, 주로 0.05~0.01mm 실트(silt) 입자로 구성된 황색의 광물질로서, 다량의 원적외선을 방사하기 때문에 혈액순환 및 신진대사 촉진 등 인체에 유익한 효과를 가지며 시멘트 독성 등을 중화시키는 작용을 하는 것으로 알려져 있다.
황토는 체에 걸러 입자가 큰 이물질을 분리한 후 분쇄기에서 분쇄하여 미분화된 황토분말을 이용한다. 분쇄를 용이하게 하기 위해 이물질 분리 후 황토를 건조시킨 다음에 분쇄할 수 있다.
고화제로 액상 고화제 또는 분말 고화제를 사용할 수 있다. 또한, 고화제로 액상 고화제와 분말 고화제가 동시에 사용할 수 있다. 가령, 황토 100중량부에 대하여 분말 고화제 80 내지 120중량부와 액상 고화제 80 내지 120중량부를 사용할 수 있다.
액상 고화제는 일 예로 규산나트륨 48 내지 52중량%, 염화칼슘 11 내지 14중량%, 염화칼륨 7 내지 9중량%, 염화마그네슘 7 내지 9중량%, 탄산나트륨 22 내지 24중량%를 함유할 수 있다.
액상 고화제의 주성분인 액상 규산나트륨은 다른 화학성분인 염화칼슘, 염화칼슘, 염화마그네슘, 탄산나트륨과 결합하여 규산화합물을 형성하고, 규산화합물은 황토에 화학성분인 실리카, 알루미나, 산화칼슘 등과 반응하여 고화를 촉진시킨다.
그리고 분말 고화제로 실리카퓸을 이용할 수 있다. 실리카퓸은 제련소의 아크전기로에서 규소, 금속 혹은 규소철합금을 생산하는 과정에서 생기는 부산물로서, 집진기를 통해 수집되는 미립 분말이다. 이러한 실리카퓸은 입자의 약 95중량% 이상이 1㎛ 미만의 크기로, 황토 입자 사이의 큰 공간을 메워 작아지게 하며, 미세한 공간을 많아지게 하여 황토 입자들 간의 결합력을 증대시키는 역할을 한다. 특히, 실리카퓸은 비결정 이산화규소를 다량 함유하고 있는 포졸란 물질의 일종이므로, 물과 반응하여 강도를 향상시키는 기능을 한다.
고화제는 황토 100중량부에 대하여 160 내지 240중량부를 사용한다. 고화제가 160중량부 미만이면 흡음재의 물성이 저하되고, 240중량부를 초과하면 황토의 비율이 낮아져 친환경성이 저하된다.
조성물의 적절한 점성유지를 위해 물은 황토 100중량부에 대하여 40 내지 80중량부를 혼합하는 것이 적절하다.
식물성 기포제는 흡음재의 경량화, 단열성, 시공성, 흡음성 등의 물리적 특성을 증대시키기 위한 것이다. 식물성 기포제로 알킬벤젠 설포네이트계 내지는 소디움 라우릴 설페이트계를 이용할 수 있다.
식물성 기포제는 황토 100중량부에 대하여 2 내지 6중량부를 혼합하는 것이 적절하다.
한편, 본 발명의 다른 예로 황토 흡음재용 조성물은 첨가제가 더 혼합될 수 있다. 가령, 황토 100중량부에 대하여 고화제 150 내지 250중량부와, 물 40 내지 80중량부와, 식물성 기포제 2 내지 6중량부, 첨가제 1 내지 10중량부를 혼합하여 황토 흡음재용 조성물을 조성할 수 있다.
첨가제로 맥반석과 숯, 실리카를 이용할 수 있다. 맥반석과 숯, 실리카는 분말 형태로 이용한다. 맥반석과 숯, 실리카는 1:1~2:1~2의 중량비로 혼합하여 사용할 수 있다.
맥반석은 석영반암(石英班岩), 장석반암류에 속하는 반심성암으로서 구성성분은 지역에 따라 다르며 알카리 장석과 석영을 주성분으로 하고 있으며, 구성물질 및 외관상으로 화강암반과 매우 유사하다. 이러한 맥반석은 다공성에 의한 인체에 유해한 성분의 흡착 및 여과작용, 알카리 금속의 이온교환 능력으로 물 중에서 용이하게 중금속류를 흡착하여 제거하고, 상대적으로 알카리 이온을 용출하는 능력, 원적외선 방출 능력, 악취 탈취 능력을 가진다.
숯은 공기의 공급을 차단하고 목재를 가열하거나 또는 공기가 희박한 상태로 가열하였을 때 생기는 고체생성물로, 목탄(木炭)이라고도 한다. 재료로는 일반적으로 재질이 단단한 나무가 사용되며, 참나무류(갈참나무, 굴참나무, 물참나무, 줄참나무 등)가 바람직하다. 숯은 흡착력과 정화력, 탈취력이 뛰어날 뿐 아니라 원적외선 발생, 미네랄 공급, 정화작용, 항균작용과 항곰팡이 작용 등이 있는 것으로 알려져 있다. 특히, 숯은 무수한 기공이 표면 및 내부에 형성된 다공질 구조를 갖기 때문에 흡착력과 탈취력이 우수하다.
실리카는 수분을 흡수 및 배출하는 성능을 가지고 있어서 황토가 기본적으로 보유하고 있는 실내 습도를 조절하는 조습기능을 보완할 수 있다.
한편, 본 발명은 황토 흡음재용 조성물은 긴병꽃풀 추출물을 더 함유할 수 있다. 가령, 황토 흡음재용 조성물은 황토 100중량부에 대하여 고화제 160 내지 240중량부와, 물 40 내지 80중량부와, 식물성 기포제 2 내지 6중량부와, 맥반석 및 숯과 실리카를 포함하는 첨가제 10 내지 20중량부와, 긴병꽃풀 추출물을 1 내지 10중량부로 조성될 수 있다.
긴병꽃풀 추출물은 항균활성을 증대시켜 황토 흡음재의 기능성을 강화시킬 수 있다.
긴병꽃풀(Glechoma hederacea)은 북부 산지의 습한 양지에서 자라는 꿀풀과(Labiatae)의 다년생초본으로 높이 5∼20cm이고, 처음에는 위로 자라다가 옆으로 길이 50cm 정도 뻗으며 퍼진 털을 가지고 있다. 긴병꽃풀의 잎은 대생하고 신장상 원형이며 끝이 둥글고 잎겨드랑이에 1∼3개씩 달린다. 그리고 긴병꽃풀의 꽃받침은 길이 7∼9mm로서 5개로 갈라지며 꽃받침잎의 끝은 바늘처럼 뾰족하다(이창복. 2003. 원색 대한식물도감. 하권. pp.123. 향문사. 서울). 긴병꽃풀 및 동속의 근연식물의 전초 혹은 뿌리를 포함한 전초를 금전초 혹은 연전초(連錢草), 마제초(馬蹄草), 활혈단(活血丹)이라 하는데, 국내의 민간에서는 수종, 해독, 말라리아, 각혈, 토혈, 류마티즘통, 소아빈혈증을 치료하는데 사용하고 있다(정보섭, 신민교. 1990. 도해 향약(생약)대사전. pp.844. 영림사. 서울).
긴병꽃풀은 줄기나 잎 또는 전초를 이용할 수 있다.
긴병꽃풀 추출물은 추출용매를 중량비로 10 내지 20배를 가한 후 80 내지 150℃에서 4 내지 12시간 동안 열수추출한 후 여과하여 액상의 긴병꽃풀 추출물을 얻을 수 있다.
이하, 본 발명의 황토 흡음재의 제조방법에 대하여 설명한다.
먼저, 황토 100중량부에 대하여 분말 고화제 80 내지 120중량부를 혼합한 후 액상 고화제 80 내지 120중량부를 첨가하여 교반한다.
황토와 분말 고화제를 1차로 혼합하여 건비빔한 다음 액상 고화제를 첨가하여 교반한다.
그리고 황토, 분말 고화제, 액상 고화제가 혼합된 혼합물에 물을 첨가하여 반죽한다. 이때 물은 황토 100중량부를 기준으로 물을 40 내지 80중량부를 첨가한다.
다음으로, 수득한 황토 반죽에 맥반석 및 숯과 실리카를 포함하는 첨가제를 첨가하여 교반한다. 이때 첨가제는 황토 100중량부를 기준으로 10 내지 20중량부를 첨가한다. 한편, 첨가제의 첨가시 긴병꽃풀 추출물이 2 내지 10중량부가 더 첨가될 수 있다.
다음으로, 첨가제가 첨가된 황토 반죽에 기포를 형성하기 위해 식물성 기포제를 첨가하여 교반한다. 이때 식물성 기포제는 황토 100중량부를 기준으로 2 내지 6중량부를 첨가한다. 식물성 기포제의 첨가 후 생성된 기포의 부피가 작아지지 않도록 교반은 1분 이상 충분히 수행한다. 기포를 생성시킨 후 황토 반죽의 비중은 기포 생성 전 황토 반죽의 비중과 비교하여 60 내지 80% 정도인 것이 바람직하다. 이 범위 내의 수준이 강도 및 흡음성능 측면에서 가장 유리하다.
다음으로, 기포를 형성시킨 후 황토 반죽을 성형틀에 주입하여 성형한다.
그리고 성형틀에서 성형된 성형체를 양생한다. 양생은 15 내지 25℃, 상대습도 50 내지 70% 조건의 양생실에서 수행할 수 있다.
이하, 본 발명을 하기 실시예를 통하여 구체적으로 설명한다. 이는 본 발명을 보다 상세하게 설명하기 위한 것으로, 본 발명의 권리 범위를 하기의 실시 예로 한정하는 것은 아니다.
(실시예)
황토 분말 100중량부에 대하여 분말 고화제 100중량부를 혼합한 후 액상 고화제 100중량부를 첨가하여 교반하였다. 그리고 황토, 분말 고화제, 액상 고화제가 혼합된 혼합물에 물 60중량부를 첨가하여 반죽 한 다음 첨가제 15중량부를 첨가하여 교반하였다.
다음으로, 첨가제가 첨가된 황토 반죽에 식물성 기포제로 소디움 라우릴 설페이트를 4중량부 첨가한 다음 3분 동안 교반시킨 후 성형틀에 주입하여 성형한 다음 20±2℃, 상대습도 60±3% 조건의 양생실에서 20일 동안 양생하여 판상의 황토 흡음재를 제조하였다.
상기에서 액상 고화제로 규산나트륨 49중량%, 염화칼슘 12중량%, 염화칼륨 8중량%, 염화마그네슘 8중량%, 탄산나트륨 23중량%를 혼합한 것을 이용하였다. 그리고 분말 고화제는 입자의 약 95중량% 이상이 1㎛ 미만의 크기인 실리카퓸을 이용하였다.
<항균실험 및 항곰팡이 실험>
실시 예에서 제조한 황토 흡음재를 시편으로 이용하여 항균 실험 및 항곰팡이 실험을 시험의뢰하였다.
2개의 시편에 대한 항균 실험결과를 도 1 및 도 2에 나타내었고, 항곰팡이 실험결과를 도 3 및 도 4에 나타내었다.
도 1 및 도 2를 참조하면, 대장균, 녹농균, 황색포도상구균에 대하여 세균감소율이 99.9% 이상으로 나타나 항균효과가 우수한 것으로 확인되었다.
그리고 도 3 및 도 4를 참조하면, 시험편에 접종한 곰팡이의 균사 발육이 4주 동안 관찰되지 않은 것으로 나타난 항곰팡이 효과 또한 우수한 것으로 확인되었다.
이상, 본 발명은 일 실시 예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 실시 예가 가능하다는 점을 이해할 것이다.
Claims (5)
- 삭제
- 삭제
- 삭제
- 황토 100중량부에 대하여 분말 고화제 80 내지 120중량부를 혼합한 후 액상 고화제 80 내지 120중량부를 첨가하여 교반하는 교반단계와;
상기 교반단계에서 수득한 혼합물에 상기 황토 100중량부를 기준으로 물을 40 내지 80중량부를 첨가하여 반죽하는 반죽단계와;
상기 반죽단계에서 수득한 황토 반죽에 맥반석 및 숯과 실리카를 포함하는 첨가제를 상기 황토 100중량부를 기준으로 10 내지 20중량부를 첨가하여 교반하는 첨가단계와;
상기 첨가단계 후 상기 황토 반죽에 상기 황토 100중량부를 기준으로 식물성 기포제로 소디움 라우릴 설페이트를 2 내지 6중량부를 첨가하여 3분 동안 교반하는 기포형성단계와;
상기 기포형성단계 후 상기 황토 반죽을 성형틀에 주입하여 성형하는 성형단계와;
상기 성형틀에서 성형된 성형체를 양생하는 양생단계;를 포함하고,
상기 액상 고화제는 규산나트륨 48 내지 52중량%, 염화칼슘 11 내지 14중량%, 염화칼륨 7 내지 9중량%, 염화마그네슘 7 내지 9중량%, 탄산나트륨 22 내지 24중량%를 함유하고,
상기 분말 고화제는 실리카퓸이며,
상기 기포형성단계에서 상기 황토 반죽은 기포 생성 후 비중이 기포 생성 전 비중의 60 내지 80%인 것을 특징으로 하는 항균 및 항곰팡이 활성을 갖는 황토 흡음재의 제조방법. - 제 4항에 있어서, 상기 첨가단계는 상기 황토 100중량부를 기준으로 긴병꽃풀 추출물을 2 내지 10중량부를 더 첨가하는 것을 특징으로 하는 항균 및 항곰팡이 활성을 갖는 황토 흡음재의 제조방법.