KR101822434B1 - Silk-like polyester yarn - Google Patents

Silk-like polyester yarn Download PDF

Info

Publication number
KR101822434B1
KR101822434B1 KR1020160181816A KR20160181816A KR101822434B1 KR 101822434 B1 KR101822434 B1 KR 101822434B1 KR 1020160181816 A KR1020160181816 A KR 1020160181816A KR 20160181816 A KR20160181816 A KR 20160181816A KR 101822434 B1 KR101822434 B1 KR 101822434B1
Authority
KR
South Korea
Prior art keywords
silk
monofilaments
sheath
core type
cross
Prior art date
Application number
KR1020160181816A
Other languages
Korean (ko)
Inventor
이의열
이창헌
송민규
전초현
Original Assignee
한국섬유개발연구원
주식회사 덕우실업
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국섬유개발연구원, 주식회사 덕우실업 filed Critical 한국섬유개발연구원
Priority to KR1020160181816A priority Critical patent/KR101822434B1/en
Application granted granted Critical
Publication of KR101822434B1 publication Critical patent/KR101822434B1/en

Abstract

A silk-like polyester yarn according to the present invention comprises sheath core type monofilaments (1) in a modified cross section form. The sheath core type monofilaments (1) have a different fineness. The sheath core type monofilaments (1) have a triangle cross section having three protrusion units, wherein a distance (L1) from a central point (P) of a triangle inscribed in the cross section to one protrusion unit among the three protrusion units is 1.2 to 1.5 times longer than a distance (L2) from the central point (P) to remaining two protrusion units. A sheath component (S) comprising the sheath core type monofilaments (1) is made of recycled polyester resin adding inorganic materials. A core component (C) comprising the sheath core type monofilaments (1) is made of recycled polyester resin. The present invention implements a gloss, a touch, and a drape property similar to silk, a natural fiber, and minimizes a dye difference between monofilaments. Accordingly, the present invention is useful as a material for clothes replacing silk.

Description

실크-라이크 폴리에스테르 원사{Silk-like polyester yarn}Silk-like polyester yarn < RTI ID = 0.0 >

본 발명은 실크-라이크(Silk-like) 폴리에스테르 원사에 관한 것으로서, 구체적으로는 실크와 유사한 광택, 감촉 및 드레이프성(Drape property)을 구현하면서도 모노필라멘트간의 염색차를 최소화 시킬 수 있는 실크-라이크 폴리에스테르 원사에 관한 것이다.The present invention relates to a silk-like polyester yarn, and more particularly to a silk-like polyester yarn which is capable of minimizing the dyeing difference between monofilaments while realizing silk-like gloss, texture and drape properties, To a polyester yarn.

실크와 유사한 유사한 광택, 감촉 및 드레이프성을 갖는 폴리에스테르 원사(이하 "실크-라이크 폴리에스테르 원사"라고 한다)를 제조하는 종래기술로는 실크-라이크 폴리에스테르 원사를 구성하는 모노필라멘트의 단면 형태를 원형 대신에 이형으로 하고, 상기 모노필라멘트들의 섬도가 서로 상이하게 하는 형성시키는 방법이 사용되어 왔다.(Hereinafter referred to as "silk-like polyester yarn") having similar gloss, feel, and drape characteristics similar to those of silk (hereinafter referred to as " silk-like polyester yarn ") has a cross-sectional shape of a monofilament constituting a silk- A method has been used in which a mono-filament is formed in a shape different from a circular shape and the fineness of the monofilaments is made different from each other.

단면 형태가 원형인 모노필라멘트들로 이루어진 통상적인 멀티필라멘트 섬유(폴리에스테르 원사) 보다는 단면 형태가 이형(Non-round) 이면서 섬도가 서로 상이한 이형단면 / 이섬도 멀티필라멘트 섬유(폴리에스테르 원사)가 실크와 유사한 광택, 감촉 및 드레이프를 구현하는데 바람직하다.(Polyester yarn) having a non-round cross-sectional shape and a different fineness than that of conventional multifilament fibers (polyester yarns) made of monofilaments having circular cross-sectional shapes, To provide a shine, feel, and drape similar to the shine.

이형단면 멀티필라멘트 섬유를 제조하는 종래기술로서 대한민국 공개특허 제10-2013-0056528호에서는 단면형상이 6엽형인 방사구금 홀을 통해 폴리머를 방사(토출)하여 꽃잎형 이형단면 섬유를 제조하는 방법을 게재하고 있으며, 대한민국 등록특허 제10-1222201호에서는 단면형상이 8엽형인 방사구금 홀을 통해 폴리에스테르 폴리머를 방사(토출)하여 꽃잎형 이형단면 섬유를 제조하는 방법을 게재하고 있으며, 대한민국 공개특허 제10-2016-0000508호에서는 시스성분 폴리머 토출용 슬릿 5~8개가 방사상으로 형성되어 있고 중앙에는 코어성분 폴리머 토출공이 형성된 복합방사 구금 홀을 통해 시스성분 폴리머와 코어성분 폴리머를 복합방사하여 복합섬유를 제조한 다음 상기 복합섬유 내 코어성분 폴리머를 용출시켜 중공형 이형단면사를 제조하는 방법을 게재하고 있으며, 대한민국 등록특허 제10-1387465호에서는 다분할 방사노즐을 통해 폴리머를 방사(토출)하여 이형단면의 다분할 중공사를 제조하는 방법을 게재하고 있다.Korean Patent Laid-Open Publication No. 10-2013-0056528 discloses a method for producing a petal-shaped modified cross-section fiber by spinning (discharging) a polymer through a spinneret hole having a hexagonal cross-sectional shape as a conventional technique for producing a cross-section multifilament fiber Korean Patent No. 10-1222201 discloses a method for producing a petal-shaped modified cross-section fiber by spinning (discharging) a polyester polymer through a spinneret hole having an octahedral cross-sectional shape, No. 10-2016-0000508 discloses a method of spinning composite filaments of composite filaments, wherein a sheath component polymer and a core component polymer are spun through a composite spinneret hole in which 5 to 8 slits for discharging sheath component polymer are formed radially and a core component polymer discharge hole is formed in the center, And then eluting the core component polymer in the composite fiber to produce a hollow shaped cross-section yarn And which, in the Republic of Korea Patent No. 10-1387465 and No. and emission (discharge) the polymer through a spinneret Multi-section showing a method of manufacturing a multi-hollow fiber to the modified cross-section.

그러나, 이형단면/이섬도 실크-라이크 합성섬유 원사를 제조할 때 상기와 같은 종래방법으로 모노필라멘트의 단면 형태를 이형(Non-round)으로 형성시키게 되면, 모노필라멘트간의 염색차가 심하게 발생하고, 광택이나 감촉이 실크와 유사하지 않게 되고, 특히 드레이프성이 크게 저하되는 문제점들이 발생하였다.However, when the cross-sectional shape of the monofilament is formed in a non-round manner by the above-described conventional method in the production of the modified / cross-linked silk-like synthetic fiber yarn, the staining difference between the monofilaments is seriously generated, And the feeling is not similar to the silk, and particularly the drapeability is greatly lowered.

본 발명의 과제는 천연섬유인 실크(Sike)와 유사한 광택, 감촉(Touch) 및 드레이프성(Drape property)를 구현하면서도 모노필라멘트간의 염색 차이를 최소화시킬 수 있는 실크-라이크 폴리에스테르 원사를 제공하는 것이다.It is an object of the present invention to provide a silk-like polyester yarn capable of minimizing the difference in dyeing between monofilaments while realizing a glossy, touch and drape property similar to that of natural fiber Sike .

이와 같은 과제를 달성하기 위해서, 본 발명에서는 실크-라이크 폴리에스테르 원사를 도 1에 도시된 바와 같이 이형단면 형태와 서로 상이한 섬도를 갖는 쉬스-코어형(Sheath-core type) 모노필라멘트(1)들로 구성한다.In order to achieve the above object, in the present invention, a silk-like polyester yarn is formed into a sheath-core type monofilament (1) having a different cross-sectional shape and a different fineness from each other as shown in FIG. 1 .

이때, 상기 쉬스-코어형 모노필라멘트(1)들의 단면형태를 3개의 돌기부를 갖는 삼각 단면 형태로 형성시켜주면서 도 2에 도시된 바와 같이 모노필라멘트(1)의 단면에 내접하는 삼각형의 중심점(P)으로부터 상기 3개의 돌기부들 중 1개의 돌기부 까지의 거리(L1)를 상기 중심점(P)으로부터 상기 3개의 돌기부들 중 나머지 2개의 돌기부 까지의 거리(L2) 대비 1.2~1.5배 길게 해준다.At this time, the cross-sectional shape of the sheath-core type monofilaments 1 is formed into a triangular cross-sectional shape having three protrusions, while a center point P (shown in FIG. 2) ) To one protrusion of the three protrusions is 1.2 to 1.5 times longer than the distance (L2) from the center point (P) to the other two protrusions of the three protrusions.

또한, 상기 쉬스-코어형 모노필라멘트(1)를 이루는 쉬스성분(S)은 무기물이 첨가된 재생 폴리에스테르 수지로 구성되고, 상기 쉬스-코어형 모노필라멘트(1)를 이루는 코어성분(C)은 재생 폴리에스테르 수지로 구성해 준다.The sheath component S constituting the sheath-core type monofilament 1 is composed of a recycled polyester resin to which an inorganic substance is added, and the core component C constituting the sheath-core type monofilament 1 is composed of It is composed of recycled polyester resin.

본 발명은 천연섬유인 실크(Sike)와 유사한 광택, 감촉(Touch) 및 드레이프성(Drape property)를 구현하면서도 모노필라멘트간의 염색 차이를 최소화시켜 준다.The present invention implements similar gloss, touch and drape properties as the natural fiber Sike, while minimizing the difference in dyeing between monofilaments.

본 발명은 특히 드레이프성(Drape property)이 크게 향상된다.The present invention greatly improves drape property in particular.

그로 인해, 본 발명은 실크를 대체하는 의류용 소재 등으로 유용하다.Therefore, the present invention is useful as a material for clothing or the like replacing silk.

도 1은 본 발명에 따른 실크-라이크 폴리에스테르 원사의 단면 사진.
도 2는 본 발명을 구성하는 쉬스-코어형 모노필라멘트의 단면 모식도.
도 3 본 발명에 따른 실크-라이크 폴리에스테르 원사를 제조하는데 사용되는 방사장치의 저면 개략도.1 is a cross-sectional photograph of a silk-like polyester yarn according to the present invention.
Fig. 2 is a schematic cross-sectional view of a sheath-core type monofilament constituting the present invention. Fig.
3 is a bottom schematic view of a spinning device used to produce a silk-like polyester yarn according to the present invention.

이하, 첨부한 도면등을 통하여 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

본 발명에 따른 실크-라이크(Silk-like) 폴리에스테르 원사는 도 1에 도시된 바와 같이 이형단면 형태의 쉬스-코어형(Sheath-core type) 모노필라멘트(1)들로 구성되며, 상기 쉬스-코어형 모노필라멘트(1)들은 서로 상이한 섬도를 구비하고 있으며, 상기 쉬스-코어형 모노필라멘트(1)는 3개의 돌기부를 갖는 삼각단면 형태를 구비하면서 단면에 내접하는 삼각형의 중심점(P)으로부터 상기 3개의 돌기부들 중 1개의 돌기부 까지의 거리(L1)가 상기 중심점(P)으로부터 나머지 2개의 돌기부 까지의 거리(L2) 대비 1.2~1.5배이고, 상기 쉬스-코어형 모노필라멘트(1)를 이루는 쉬스성분(S)은 무기물이 첨가된 재생 폴리에스테르 수지로 구성되고, 상기 쉬스-코어형 모노필라멘트(1)를 이루는 코어성분(C)은 재생 폴리에스테르 수지로 구성되는 것을 특징으로 한다.The silk-like polyester yarn according to the present invention is composed of sheath-core type monofilaments 1 having an irregular cross-sectional shape as shown in FIG. 1, and the sheath- The core-type monofilaments (1) have different finenesses. The sheath-core monofilament (1) has a triangular cross-sectional shape having three protrusions, Core type monofilament (1), wherein the distance (L1) to one protrusion of the three protrusions is 1.2 to 1.5 times the distance (L2) from the center point (P) to the remaining two protrusions The component (S) is composed of a recycled polyester resin to which an inorganic material is added, and the core component (C) constituting the sheath-core type monofilament (1) is constituted of a recycled polyester resin.

상기 쉬스-코어형 모노필라멘트(1)를 이루는 쉬스성분(S)은 무기물이 첨가된 재생 폴리에스테르로 구성되고, 코어성분(C)은 무기물이 첨가안된 재생 폴리에스테르로 구성된다.The sheath component (S) constituting the sheath-core type monofilament (1) is composed of a recycled polyester to which an inorganic material is added, and the core component (C) is composed of a recycled polyester to which an inorganic material is not added.

쉬스성분(S)과 코어성분(C) 중에서 상기 쉬스성분(S)에만 TiO2등과 같은 무기물이 첨가되어 있기 때문에 드레이프성이 크게 향상된다.The drapability is improved significantly since the sheath component is inorganic material is added, such as TiO 2 only the sheath component (S) from (S) and the core component (C).

상기 쉬스성분(S)과 코어성분(C)들이 재생 폴리에스테르로 구성되기 때문에 실크와 유사한 광택을 발현하는데 바람직하다.Since the sheath component (S) and the core component (C) are composed of recycled polyester, it is preferable to exhibit a gloss similar to silk.

본 발명을 구성하는 쉬스-코어형 모노필라멘트(1)들은 모노필라멘트 모두가 동일한 섬도를 갖는 것이 아니라 일부는 섬도가 동일하고 나머지 일부는 섬도가 서로 상이하거나 모노필라멘트 모두의 섬도가 상이하게 형성된다.In the sheath-core type monofilaments 1 constituting the present invention, not all of the monofilaments have the same fineness, but some of them are the same in fineness, and the remaining portions of the monofilaments are different in fineness or different in fineness of both monofilaments.

상기 쉬스-코어형 모노필라멘트(1)는 도 2에 도시된 바와 같이 3개의 돌기부를 갖는 삼각 단면 형태를 구비하면서 단면에 내접하는 삼각형의 중심점(P)으로부터 3개의 돌기부들 중 1개의 돌기부 까지의 거리(L1)가 상기 중심점(P)으로부터 3개 돌기부들 중 나머지 2개의 돌기부 까지의 거리(L2) 대비 1.2~1.5배이다.As shown in FIG. 2, the sheath-core type monofilament 1 has a triangular cross-sectional shape having three protrusions, and has a triangular cross-sectional shape ranging from a center point P of a triangle which is in contact with a cross section to one protrusion of three protrusions The distance L1 is 1.2 to 1.5 times the distance L2 from the center point P to the other two protrusions of the three protrusions.

상기 L1 거리가 L2 거리대비 1.2 미만이거나 1.5배를 초과하는 경우에는 실크와 같은 감촉과 광택을 구현하기 어렵게 된다.When the L1 distance is less than 1.2 or more than 1.5 times the L2 distance, it is difficult to realize a feeling of silk and gloss.

본 발명에 따른 실크-라이크 폴리에스테르 원사를 제조하는 일례를 살펴보면, 도 3에 도시된 바와 같이 쉬스-코어형 복합방사장치(D)의 저면에 동심원을 따라 배열된 삼각 단면 형태의 토출공(B)들을 통해 무기물이 첨가된 재생 폴리에스테르 수지 용융액인 쉬스성분(S)과 무기물이 첨가안된 재생 폴리에스테르 수지 용융액인 코어성분(C)은 복합방사한 후, 상기 토출공(B)을 통해 방사되는 쉬스-코어형 모노필라멘트(1)들을 집속한 다음 응고, 건조 및 연신하여 실크-라이크 폴리에스테르 원사를 제조한다.As shown in FIG. 3, an example of producing the silk-like polyester yarn according to the present invention will be described. In FIG. 3, (C), which is a regenerated polyester resin melt to which an inorganic substance is not added, and a sheath component (S) which is a regenerated polyester resin melt to which an inorganic substance is added through a composite spinning process, The sheath-core type monofilaments (1) are collected and then coagulated, dried and stretched to produce silk-like polyester yarn.

본 발명은 천연섬유인 실크(Sike)와 유사한 광택, 감촉(Touch) 및 드레이프성(Drape property)를 구현하면서도 모노필라멘트간의 염색 차이를 최소화시켜 준다.The present invention implements similar gloss, touch and drape properties as the natural fiber Sike, while minimizing the difference in dyeing between monofilaments.

그로 인해, 본 발명은 실크를 대체하는 의류용 소재 등으로 유용하다.Therefore, the present invention is useful as a material for clothing or the like replacing silk.

이하, 실시예 및 비교실시예를 통하여 본 발명을 보다 구체적으로 살펴본다.Hereinafter, the present invention will be described in more detail with reference to examples and comparative examples.

그러나 본 발명의 보호범위는 하기 실시예만으로 한정되게 해석되어서는 안된다.However, the scope of protection of the present invention should not be construed as being limited only to the following examples.

실시예 1Example 1

도 3에 도시된 바와 같이 복합방사장치(D)의 저면에 동심원 상으로 형성된 삼각단면 형태의 토출공(B)들을 통해서 TiO2가 5중량% 첨가된 재생 폴리에스테르 수지 용융액인 쉬스성분(S)과 TiO2가 첨가안된 재생 폴리에스테르 수지 용융액인 코어성분(C)을 복합방사하여 도 2에 도시된 바와 같이 3개의 돌기부를 갖는 삼각 단면 형태를 구비하면서 L1 거리가 L2 거리대비 1.3배이고 섬도가 서로 상이한 쉬스-코어형 모노필라멘트(1)들 형성하였다.As shown in FIG. 3, the sheath component S, which is a reclaimed polyester resin melt having 5% by weight of TiO 2 added through discharging holes B having a triangular cross section and formed concentrically on the bottom surface of the composite spinneret D, And a core component (C) as a melt of a recycled polyester resin to which no TiO 2 is added to form a triangular cross-sectional shape having three protrusions as shown in FIG. 2, wherein the L1 distance is 1.3 times the L2 distance and the fineness Different sheath-core type monofilaments (1) were formed.

다음으로는, 방사된 상기 쉬스-코어형 모노필라멘트(1)들을 집속한 후 응고, 수세 및 연신하여 실크-라이크 폴리에스테르 원사를 제조하였다.Next, the irradiated sheath-core type monofilaments (1) were collected, coagulated, washed and stretched to produce a silk-like polyester yarn.

상기와 같이 제조된 실크-라이크 폴리에스테르 원사의 감촉, 광택 및 드레이프성과 모노필라멘트간 염색차이 정도를 평가한 결과는 표 1과 같았다.Table 1 shows the results of evaluating the degree of difference in texture, gloss, drape and dyeing between the monofilaments of the silk-like polyester yarn produced as described above.

비교실시예 1Comparative Example 1

도 3에 도시된 바와 같이 방사구금 장치(D)의 저면에 동심원 상으로 형성된 삼각단면 형태의 토출공(B)들을 통해서 폴리에스테르 수지 용융액을 방사하여 도 2에 도시된 바와 같이 3개의 돌기부를 갖는 삼각 단면 형태를 구비하면서 L1 거리가 L2 거리대비 1.6배이고 섬도가 서로 상이한 모노필라멘트(1)들 형성하였다.As shown in FIG. 3, the polyester resin melt is spun through discharge holes B having a triangular cross-sectional shape formed concentrically on the bottom surface of the spinneret D so as to have three protrusions as shown in FIG. 2 Monofilaments (1) having a triangular cross-sectional shape and having a L1 distance of 1.6 times the L2 distance and different fineness were formed.

다음으로는, 방사된 상기 모노필라멘트(1)들을 집속한 후 응고, 수세 및 연신하여 실크-라이크 폴리에스테르 원사를 제조하였다.Next, the irradiated monofilaments (1) were collected, coagulated, washed and stretched to produce a silk-like polyester yarn.

상기와 같이 제조된 실크-라이크 폴리에스테르 원사의 감촉, 광택 및 드레이프성과 모노필라멘트간 염색차이 정도를 평가한 결과는 표 1과 같았다.Table 1 shows the results of evaluating the degree of difference in texture, gloss, drape and dyeing between the monofilaments of the silk-like polyester yarn produced as described above.

구분division 감촉Texture 광택Polish 드레이프성Drape Castle 모노필라멘트간 염색차이Dyeing difference between monofilaments 실시예 1Example 1 실크와 유사Similar to silk 실크와 유사Similar to silk 실크와 유사Similar to silk 염색차이 거의 없음Little difference in dyeing 비교실시예 1Comparative Example 1 실크와 상이Silk and different 실크와 상이Silk and different 실크와 상이Silk and different 염색차이 발생Dyeing difference occurred

표1의 감촉, 광택, 드레이프성은 염색차이는 전문가 10인의 관능검사 결과 전문가 8명 이상이 실크와 유사하다고 판정하면 "실크와 유사"로, 전문가 7명 이하가 실크와 상이하다고 판정하면 "실크와 상이"로 구분하였다.The sensory, gloss and drape properties of Table 1 indicate that the difference in dyes is "similar to silk" when it is judged that 8 or more experts are similar to silk as a result of sensory evaluation by 10 experts. When judging that 7 or less experts are different from silk, Differentiated ".

표 1의 모노필라멘트간 염색차이는 전문가 10인의 관능검사결과 전문가 8명 이상이 모노필라멘트간 염색차이가 없다고 판정하면 "염색차이 거의 없음"으로, 전문가 7명 이하가 모노필라멘트간 염색차이가 있다고 판정하면 "염색차이 발생"으로 구분하였다.The difference in staining between monofilaments in Table 1 indicates that there was no difference in staining between the monofilaments when more than 8 experts of the experts judged that there was no difference in staining between the monofilaments. And "Dyeing difference occurred".

Y : 실크-라이크 폴리에스테르 원사
1 : 실크-라이크 폴리에스테르를 구성하는 쉬스-코어형 모노필라멘트
P : 쉬스-코어형 모노필라멘트의 단면에 내접하는 삼각형의 중심점
L1,L2,L3 : 쉬스-코어형 모노필라멘트의 단면에 내접하는 삼각형의 중심점(P)으로부터 쉬스-코어형 모노필라멘트 단면의 돌기부 까지의 거리
D : 복합방사장치
B : 토출공
A : 토출용 슬릿Y: Silk-like polyester yarn
1: Sheath-core type monofilament constituting silk-like polyester
P: a center point of a triangle in contact with the end surface of the sheath-core type monofilament
L1, L2, and L3: the distance from the center point P of the triangle in contact with the end surface of the sheath-core type monofilament to the projection of the sheath-core type monofilament section
D: Composite spinning device
B: Discharge ball
A: Discharge slit

Claims (1)

이형단면 형태의 쉬스-코어형(Sheath-core type) 모노필라멘트(1)들로 구성되며, 상기 쉬스-코어형 모노필라멘트(1)들은 서로 상이한 섬도를 구비하고 있으며, 상기 쉬스-코어형 모노필라멘트(1)는 3개의 돌기부를 갖는 삼각단면 형태를 구비하면서 단면에 내접하는 삼각형의 중심점(P)으로부터 상기 3개의 돌기부들 중 1개의 돌기부 까지의 거리(L1)가 상기 중심점(P)으로부터 나머지 2개의 돌기부 까지의 거리(L2) 대비 1.2~1.5배이고, 상기 쉬스-코어형 모노필라멘트(1)를 이루는 쉬스성분(S)은 무기물이 첨가된 재생 폴리에스테르 수지로 구성되고, 상기 쉬스-코어형 모노필라멘트(1)를 이루는 코어성분(C)은 재생 폴리에스테르 수지로 구성되는 것을 특징으로 하는 실크-라이크(Silk-like) 폴리에스테르 원사.Core-type monofilaments (1), wherein the sheath-core type monofilaments (1) have different finenesses, and the sheath-core type monofilaments (1) has a triangular cross-sectional shape having three protrusions, and a distance (L1) from a center point (P) of a triangle which is in contact with a cross section to one protrusion of the three protrusions Core type monofilament (1) is composed of a recycled polyester resin to which an inorganic material is added, and the sheath-core type monofilament (1) comprises a sheath-core type monofilament A silk-like polyester yarn characterized in that the core component (C) constituting the filament (1) is composed of a recycled polyester resin.
KR1020160181816A 2016-12-29 2016-12-29 Silk-like polyester yarn KR101822434B1 (en)