KR101819816B1 - Wood panels for furniture, and a method of manufacturing the same - Google Patents

Wood panels for furniture, and a method of manufacturing the same Download PDF

Info

Publication number
KR101819816B1
KR101819816B1 KR1020160005818A KR20160005818A KR101819816B1 KR 101819816 B1 KR101819816 B1 KR 101819816B1 KR 1020160005818 A KR1020160005818 A KR 1020160005818A KR 20160005818 A KR20160005818 A KR 20160005818A KR 101819816 B1 KR101819816 B1 KR 101819816B1
Authority
KR
South Korea
Prior art keywords
layer
weight
wood
environmentally friendly
delete delete
Prior art date
Application number
KR1020160005818A
Other languages
Korean (ko)
Other versions
KR20170086236A (en
Inventor
소병명
Original Assignee
소병명
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 소병명 filed Critical 소병명
Priority to KR1020160005818A priority Critical patent/KR101819816B1/en
Publication of KR20170086236A publication Critical patent/KR20170086236A/en
Application granted granted Critical
Publication of KR101819816B1 publication Critical patent/KR101819816B1/en

Abstract

이 발명은, 스티렌(styrene)과 같이 인체에 유해한 화학물질을 사용하지 않고서 친환경 UV 프라이머층과 친환경 상도층을 형성하여 목재를 마감함으로써 사용자 건강을 보호할 수 있는, 가구용 목재 패널 및 그의 제조방법에 관한 것으로서,
이 발명의 가구용 목재 패널은, 표면에 LPM층이 형성되어 있는 심재와, 상기한 LPM층상에 형성되어 있는 친환경 UV 프라이머층과, 상기한 친환경 UV 프라이머층상에 형성된 샌딩 실러층과, 상기한 샌딩 실러층상에 형성된 친환경 상도층을 포함하여 이루어지며, 상기한 친환경 상도층은 불포화 폴리에스테르 수지 30~40 중량%, 모노머 50~60 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하여 이루어진다.The present invention relates to a wood panel for furniture and a method of manufacturing the same, which can protect the user's health by forming an environment-friendly UV primer layer and an environmentally friendly top layer without using harmful chemicals such as styrene As a matter of fact,
The wood panel for furniture of the present invention comprises a core material having a surface on which an LPM layer is formed, an environmentally friendly UV primer layer formed on the LPM layer, a sanding sealer layer formed on the environmentally friendly UV primer layer, Wherein the environmentally friendly top layer comprises 30 to 40% by weight of an unsaturated polyester resin, 50 to 60% by weight of a monomer, 2 to 5% by weight of a photoinitiator, and 0 to 5% by weight of an additive .

Figure 112016005152251-pat00002
Figure 112016005152251-pat00002

Description

가구용 목재 패널의 제조방법{Wood panels for furniture, and a method of manufacturing the same}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wood panel for furniture,

이 발명은 가구용 목재 패널의 제조방법에 관한 것으로서, 좀더 세부적으로 말하자면 스티렌(styrene)과 같이 인체에 유해한 화학물질을 사용하지 않고서 친환경 UV 프라이머층과 친환경 상도층을 형성하여 목재를 마감함으로써 사용자의 건강을 보호할 수 있는, 가구용 목재 패널의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a wood panel for furniture, and more particularly, by forming an environmentally friendly UV primer layer and an environmentally friendly top layer without using harmful chemical substances such as styrene, To a method of manufacturing a wood panel for furniture.

일반적으로 싱크대, 식탁, 수납장, 탁자, 책상, 문갑 등과 같은 가구는 목재패널을 이용하여 제작된다.Typically, furniture such as sinks, dining tables, cabinets, tables, desks, and palettes are made of wood panels.

가구용 목재 패널을 제작하는 경우에, 도료를 여러층(하도층, 중도층, 상도층)에 걸쳐서 도포하고 건조시키게 된다.In the case of making a wooden panel for furniture, the paint is applied over several layers (sublayer, middle layer, upper layer) and dried.

참고로, 각 도포층(하도층, 중도층, 상도층)의 도포, 건조조건(도포회수, 건조온도, 건조시간) 등에 각 도포층이 고르면서 견실하게 도포됨과 아울러 상호간에 박리가 발생되지 않으므로 제품의 내구성 및 신뢰성을 향상시키는 기술이 대한민국 공개특허공보 공개번호 10-2006-0033758(공개일자 2006년 04월 19일)의 "가구 및 건축용 목재 도장방법"에서 개시된 바 있다.For reference, each coating layer is uniformly and uniformly applied to each coating layer (undercoating layer, intermediate layer, upper coating layer), drying conditions (coating frequency, drying temperature, drying time), and peeling does not occur between the coating layers A technique for improving the durability and reliability of products has been disclosed in Korean Patent Application Laid-Open Publication No. 10-2006-0033758 (published on April 19, 2006) entitled " Wood and Furniture Coating Method ".

그러나, 상기한 공개특허공보 공개번호 10-2006-0033758를 포함한 종래의 가구용 목재 패널 및 그의 제조방법은, 인체에 유해한 화학성분의 도료를 사용하기 때문에 피부 접촉이나 호흡기 흡입을 통해 신경계 장애를 일으키는 발암물질인 총휘발성유기화합물(Total Volatile Organic Compounds, TVOC)이 도료로부터 발생하게 됨으로써 사용자 건강에 유해하게 되는 문제점이 있다.However, since the conventional wooden panel for furniture and the manufacturing method thereof including the above-mentioned Patent Publication No. 10-2006-0033758 uses a chemical composition paint harmful to human body, the carcinogen that causes the nervous system trouble through skin contact or breathing inhalation Total Volatile Organic Compounds (TVOC), which is a substance, are generated from the paint, which is detrimental to the user's health.

공개특허공보 공개번호 10-2006-0033758Published Patent Publication No. 10-2006-0033758

본 발명의 목적은 상기한 바와 같은 종래의 문제점을 해결하기 위한 것으로서, 스티렌(styrene)과 같이 인체에 유해한 화학물질을 사용하지 않고서 친환경 UV 프라이머층과 친환경 상도층을 형성하여 목재를 마감함으로써 사용자 건강을 보호할 수 있는, 가구용 목재 패널의 제조방법을 제공하는 데 있다. It is an object of the present invention to solve the above-mentioned problems of the prior art, and it is an object of the present invention to provide an environmentally friendly UV primer layer and an environmentally friendly top layer without using a chemical substance harmful to human body such as styrene, And a method for manufacturing a wood panel for furniture.

상기한 목적을 달성하기 위한 수단으로서 이 발명의 구성은, 표면에 LPM층이 형성되어 있는 심재와, 상기한 LPM층상에 형성되어 있는 친환경 UV 프라이머층과, 상기한 친환경 UV 프라이머층상에 형성된 샌딩 실러층과, 상기한 샌딩 실러층상에 형성된 친환경 상도층을 포함하여 이루어지며, 상기한 친환경 상도층은 불포화 폴리에스테르 수지 30~40 중량%, 모노머 50~60 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하여 이루어지면 바람직하다.As a means for achieving the above object, the present invention provides a method for producing a green UV primer layer, comprising: a core material having a surface on which an LPM layer is formed; an environmentally friendly UV primer layer formed on the LPM layer; And an environmentally friendly top layer formed on the sanding sealer layer, wherein the environmentally friendly top layer comprises 30 to 40% by weight of an unsaturated polyester resin, 50 to 60% by weight of a monomer, 2 to 5% by weight of a photoinitiator, 0 to 5% by weight.

이 발명의 구성은, 상기한 친환경 상도층상에 광촉매제와 방염제가 혼합되어 있는 광촉매 및 방염 코팅층을 더 포함하여 이루어지면 바람직하다.It is preferable that the constitution of the present invention further comprises a photocatalyst and a flame retardant coating layer in which a photocatalyst and a flame retardant are mixed on the above environmentally friendly top coat layer.

이 발명의 구성은, 상기한 친환경 UV 프라이머층은 우레탄 아크릴레이트 수지 20~30 중량%, 모노머 40~50 중량%, 안료 10~20 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하여 이루어지면 바람직하다.The composition of the present invention is such that the environmentally friendly UV primer layer comprises 20 to 30% by weight of a urethane acrylate resin, 40 to 50% by weight of a monomer, 10 to 20% by weight of a pigment, 2 to 5% by weight of a photoinitiator, 0 to 5% . ≪ / RTI >

이 발명의 구성은, 상기한 모노머는 TMPTA(Trimethylol Propane Triacrylate)와 같은 3관능기 모노머, TPGDA(Tripropylene Glycol Diacrylate)와 같은 2관능기 모노머, HEA(Hydroxy Ethyl Acrylate), HPA(Hydroxy Propyl Acrylate)와 같은 단관능기 모노머중에서 하나를 선택하여 사용하면 바람직하다.The constitution of the present invention is such that the above-mentioned monomers may be used as monomers such as trifunctional monomer such as TMPTA (Trimethylol Propane Triacrylate), 2 functional monomer such as TPGDA (Tripropylene Glycol Diacrylate), HEA (Hydroxy Ethyl Acrylate) It is preferable to select one of the functional monomer.

상기한 목적을 달성하기 위한 수단으로서 이 발명의 방법의 구성은, 심재의 표면에 LPM층이 형성된 목재를 준비하는 단계와, 상기한 LPM층상에 롤코터를 이용하여 친환경 UV 프라이머를 도포한 뒤에 자외선으로 경화시키는 단계와, 상기한 친환경 UV 프라이머층상에 롤코터를 이용하여 샌딩 실러를 도포한 뒤에 자외선으로 경화시키는 단계와, 상기한 친환경 UV 프라이머층상에 도포된 샌딩 실러를 연마한 뒤에 연마된 샌딩 실러를 브러시로 털어낸 후 목재에 발생된 정전기를 제거함과 동시에 에어 샤워를 시키는 단계와, 상기한 샌딩 실러층상에 커텐코터를 이용하여 친환경 상도를 도포한 뒤에 프레시오프존을 통과시키면서 잔류 유기용제를 제거하는 단계와, 상기한 프레시오프존을 통과한 목재를 TL 램프존을 통과시키면서 자외선으로 예비 경화를 시킨 후에 하이파워존을 통과시키면서 자외선으로 완전 경화를 시키는 단계와, 상기한 하이파워존을 통과한 목재를 냉각부스를 통과시키면서 제트 샤워를 이용하여 쿨링시키는 단계를 포함하여 이루어지면 바람직하다.As a means for achieving the above object, the present invention provides a method of manufacturing a method for manufacturing a semiconductor device, comprising the steps of: preparing a wood material having an LPM layer formed on a surface of a core material; applying an environmentally friendly UV primer onto the LPM layer using a roll coater; A step of applying a sanding sealer to the green UV primer layer using a roll coater and then curing the green UV primer layer with ultraviolet rays; polishing the sanding sealer applied on the environmentally friendly UV primer layer, Removing the static electricity generated on the wood and air shower; applying an environmentally-friendly top coat on the sanding sealer layer using a curtain coater, passing the organic solvent through the openoff zone, A step of preliminarily curing the wood passing through the above-mentioned fresh off zone through ultraviolet rays while passing through the TL lamp zone; After the step was passed through the high-power zone to a fully cured with ultraviolet rays, while the high-power that has passed through the one zone through the timber preferably comprising cooling booth, including the step of cooling using a shower jet.

이 발명의 방법의 구성은, 상기한 친환경 UV 프라이머를 도포한 뒤에 자외선으로 경화시키는 경우에, 16.8KW UV 램프 1개 광량의 자외선으로 경화를 시키면 바람직하다.The constitution of the method of the present invention is preferable in the case of curing with ultraviolet light of one light of 16.8 KW UV lamp after application of the environmentally friendly UV primer described above.

이 발명의 방법의 구성은, 상기한 친환경 UV 프라이머층상에 샌딩 실러가 도포된 목재를 자외선으로 경화시키는 경우에, 16.8KW UV 램프 3개 광량의 자외선으로 경화시키면 바람직하다. The constitution of the method of the present invention is preferable when the wood coated with the sanding sealer on the environmentally friendly UV primer layer is cured by ultraviolet rays of three light quantities of 16.8 KW UV lamp.

이 발명의 방법의 구성은, 상기한 프레시오프존은 0.1~0.5 m/s의 풍속으로 25~40도의 온풍을 발생시키면 바람직하다.The constitution of the method of the present invention is preferably such that the above-mentioned openoff zone generates hot air of 25 to 40 degrees at an air velocity of 0.1 to 0.5 m / s.

이 발명의 방법의 구성은, 상기한 TL 램프존(TL lamp zone)을 통과시키면서 자외선으로 예비 경화를 시키는 경우에, 140W 용량의 TL 램프를 100개 사용한 광량의 자외선으로 예비 경화를 시키면 바람직하다.The constitution of the method of the present invention is preferable in the case of preliminarily curing with ultraviolet light having a light quantity using 100 TL lamps having a capacity of 140 W when ultraviolet rays are preliminarily cured while passing through the TL lamp zone.

이 발명의 방법의 구성은, 상기한 하이파워존(high power zone)을 통과시키면서 자외선으로 완전 경화를 시키는 경우에, 16.8KW 용량의 UV 램프를 5개 사용한 광량의 자외선으로 경화를 시키면 바람직하다.The composition of the method of the present invention is preferably used when curing is performed with ultraviolet light having a light quantity using five UV lamps having a capacity of 16.8 KW in the case of completely curing by ultraviolet rays while passing through the high power zone.

이 발명은, 스티렌(styrene)과 같이 인체에 유해한 화학물질을 사용하지 않고서 친환경 UV 프라이머층과 친환경 상도층을 형성하여 목재를 마감함으로써 사용자 건강을 보호할 수 있는, 효과를 갖는다.The present invention has the effect of protecting the user's health by forming an environmentally friendly UV primer layer and an environmentally friendly top layer without using harmful chemicals such as styrene to finish the wood.

도 1은 이 발명의 일 실시예에 따른 가구용 목재 패널의 단면 구성도이다.
도 2는 이 발명의 일 실시예에 따른 가구용 목재 패널의 제조방법의 흐름도이다.1 is a cross-sectional view of a wood panel according to an embodiment of the present invention.
2 is a flowchart of a method of manufacturing a wood panel for furniture according to an embodiment of the present invention.

이하, 이 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 이 발명을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 이 발명의 바람직한 실시예를 첨부된 도면을 참조로 하여 상세히 설명하기로 한다. 이 발명의 목적, 작용, 효과를 포함하여 기타 다른 목적들, 특징점들, 그리고 동작상의 이점들이 바람직한 실시예의 설명에 의해 보다 명확해질 것이다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings, so that those skilled in the art can easily carry out the present invention. Other objects, features, and operational advantages, including the purpose, operation, and effect of the present invention will become more apparent from the description of the preferred embodiments.

참고로, 여기에서 개시되는 실시예는 여러가지 실시가능한 예중에서 당업자의 이해를 돕기 위하여 가장 바람직한 실시예를 선정하여 제시한 것일 뿐, 이 발명의 기술적 사상이 반드시 제시된 실시예에만 의해서 한정되거나 제한되는 것은 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위내에서 다양한 변화와 부가 및 변경이 가능함은 물론, 균등한 타의 실시예가 가능함을 밝혀 둔다. It is to be understood that both the foregoing general description and the following detailed description of the present invention are exemplary and explanatory only and are not to be construed as limiting the scope of the invention as disclosed in the accompanying claims. It is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and similarities, many of which are within the scope of the present invention.

또한, 본원의 명세서 및 청구범위에 사용된 용어나 단어의 표현은, 발명자가 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 정의된 것으로서, 통상적이거나 사전적인 의미로만 한정해서 해석되어서는 아니되며, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 일예로서, 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한 복수의 표현을 포함하며, 방향에 관한 표현은 설명상의 편의를 위하여 도면상에 표현된 위치를 기준으로 설정하기로 한다.It should also be understood that the expressions of terms or words used in the specification and claims of the present application are defined based on the principle that the inventor can properly define the concept of a term in order to explain its invention in the best way , Should not be construed as limited to ordinary or dictionary meanings and should be construed in a meaning and a concept consistent with the technical idea of the present invention. As an example, the singular " include " includes plural representations unless the context clearly dictates otherwise, and the expressions relating to directions are to be set based on the position represented on the drawing for convenience of explanation.

도 1은 이 발명의 일 실시예에 따른 가구용 목재 패널의 단면 구성도이다.1 is a cross-sectional view of a wood panel according to an embodiment of the present invention.

도 1에 도시되어 있는 바와 같이, 이 발명의 일실시예에 따른 가구용 목재 패널의 구성은, 표면에 LPM층(2)이 형성되어 있는 심재(1)와, 상기한 LPM층(2)상에 형성되어 있는 친환경 UV 프라이머층(3)과, 상기한 친환경 UV 프라이머층(3)상에 형성된 샌딩 실러층(4)과, 상기한 샌딩 실러층(4)상에 형성된 친환경 상도층(5)을 포함하여 이루어진다.1, the construction of a wooden panel for furniture according to an embodiment of the present invention includes a core 1 having an LPM layer 2 formed on a surface thereof, (3), a sanding sealer layer (4) formed on the environmentally friendly UV primer layer (3) and an environmentally friendly topcoat layer (5) formed on the sanding sealer layer .

상기한 심재(1)로서는 MDF(Medium Density Fiber board), PB(Particle Board), 합판(Plywood), 원목을 사용한다.As the core 1, a medium density fiber board (MDF), a particle board (PB), a plywood, and a wood are used.

상기한 MDF는 목질 재료를 원료로 하여 얻는 목섬유를 접착제와 함께 고온, 고압으로 압착 성형한 판재로서, 조직이 치밀하고 균일한 특성이 있으며, 기계 가공성과 강도가 우수하므로 일반 목재를 대신하여 가구, 스피커 외관, 탁구대 등의 재료로 널리 이용된다. 또한, 표면이 단단하고 평활하여 페인트를 칠하거나 장식용 필름을 접착하여 사용하기 쉽다. The above-mentioned MDF is a plate material obtained by compression molding of wood fiber obtained by using wood material as a raw material with adhesive at high temperature and high pressure. Since the structure is dense and uniform and has excellent machinability and strength, Speaker exterior, and table tennis table. In addition, the surface is hard and smooth, so it is easy to use by painting or decorating film.

상기한 PB는 원목으로 목재를 생산하고 남은 폐 잔재를 부수어 작은 조각으로 만든 후에 접착제를 섞어서 고온 고압으로 압착시켜서 만든 가공재로서, 원목이 가지는 단점을 보완할 수 있으며, 소리를 잘 흡수하고, 크기나 모양을 다양하게 할 수 있으며, 여러 가지 원목의 가공 과정에서 발생하는 폐 잔재를 재활용한다는 측면에서 효율적이고 경제적이다.The above-mentioned PB is a processing material which is made by cutting wood remnant from the wood, crushing the remaining waste into small pieces, and then mixing the adhesive with high temperature and high pressure. It can compensate the disadvantages of the wood, absorb sound, It is efficient and economical in terms of recycling the waste residue generated in the processing of various logs.

상기한 합판은 목재의 얇은 판을 나뭇결의 방향이 서로 직교(直交)하도록 접착제로 붙인 것으로서, 합판을 만드는 데 쓰는 박판(薄板)을 베니어(veneer)라고 한다. 단판(單板)으로는 나뭇결을 따라 쪼개지기 쉽고, 수분에 의하여 수축 또는 팽창하기 쉽다는 결점을 보완할 수 있을 뿐만 아니라, 중심부에는 반드시 양질재(良質材)를 쓸 필요가 없으므로 목재의 이용 효율이 높아진다. The above-mentioned plywood is a thin plate of wood, which is adhered with an adhesive so that the directions of the grain are orthogonal to each other, and a thin plate used for making plywood is called a veneer. As a single plate, it is possible to compensate for the drawback that it is easily broken along the grain and is liable to shrink or expand due to moisture. In addition, since it is not necessary to use a good quality material in the center portion, .

상기한 친환경 UV 프라이머층(3)은 우레탄 아크릴레이트 수지 20~30 중량%, 모노머 40~50 중량%, 안료 10~20 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하여 이루어진다.The environmentally friendly UV primer layer 3 comprises 20 to 30% by weight of a urethane acrylate resin, 40 to 50% by weight of a monomer, 10 to 20% by weight of a pigment, 2 to 5% by weight of a photoinitiator and 0 to 5% .

상기한 모노머는 반응성 희석제로 사용되는데, TMPTA(Trimethylol Propane Triacrylate)와 같은 3관능기 모노머, TPGDA(Tripropylene Glycol Diacrylate)와 같은 2관능기 모노머, HEA(Hydroxy Ethyl Acrylate), HPA(Hydroxy Propyl Acrylate)와 같은 단관능기 모노머중에서 선택하여 사용한다.The above-mentioned monomers are used as reactive diluents. They include trifunctional monomer such as TMPTA (Trimethylol Propane Triacrylate), 2 functional monomer such as TPGDA (Tripropylene Glycol Diacrylate), HEA (Hydroxy Ethyl Acrylate) and HPA (Hydroxy Propyl Acrylate) Functional monomer is selected and used.

상기한 광개시제는 모노머가 광 중합하는데 필요한 에너지를 가함으로써 모노머가 경화된 후의 고분자 물질로 바뀌도록 광 중합을 개시시키는 역할을 한다.The above-mentioned photoinitiator serves to initiate photopolymerization so that the monomer is converted into a polymer substance after curing by applying energy required for photo-polymerization.

상기한 샌딩 실러층(4)은 샌딩 실러를 이용하여 형성한다. The above-described sanding sealer layer 4 is formed by using a sanding sealer.

상기한 샌딩 실러는 밑칠한 도막위에 도장하는 도료로서, 연마에 의해 사용한 후에 평탄한 도장 소지를 작성함으로써 위칠 도료의 도장 품질을 향상시키고, 산소를 차단하는 역할을 한다.The above-described sanding sealer is a paint which is coated on a primer coat, and after the primer is used by polishing, a smooth coat is formed to improve the paint quality of the primer paint and to block oxygen.

상기한 친환경 상도층(5)은 불포화 폴리에스테르 수지 30~40 중량%, 모노머 50~60 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하여 이루어진다.The environmentally friendly top coat layer 5 comprises 30 to 40% by weight of an unsaturated polyester resin, 50 to 60% by weight of a monomer, 2 to 5% by weight of a photoinitiator, and 0 to 5% by weight of an additive.

상기한 불포화 폴리에스테르 수지는 무색 투명한 열경화성 수지로, 무수(無水) 말레인산과 푸마르산 같은 불포화 디카르본산(dicarboxylic acid) 및 2가(二價)알코올을 반응시켜 제조한다. 뛰어난 내열성, 내식성을 갖고 있으며, 그 대부분이 FRP(섬유강화 플라스틱)의 매트릭스로 사용되고 있다. 최근에는 아라미드 섬유 같은 새로운 강화재가 개발됨에 따라 보다 고강도의 FRP가 실현되었기 때문에 그 용도는 더욱 확대되고 있다.The above unsaturated polyester resin is a colorless transparent thermosetting resin prepared by reacting an anhydride (maleic anhydride) with an unsaturated dicarboxylic acid such as fumaric acid and a divalent alcohol. They have excellent heat resistance and corrosion resistance, and most of them are used as a matrix of FRP (fiber reinforced plastic). In recent years, new reinforcements such as aramid fibers have been developed, and the use of FRP has been further expanded because of the realization of higher strength FRP.

상기한 모노머는 반응성 희석제로 사용되는데, TMPTA(Trimethylol Propane Triacrylate)와 같은 3관능기 모노머, TPGDA(Tripropylene Glycol Diacrylate)와 같은 2관능기 모노머, HEA(Hydroxy Ethyl Acrylate), HPA(Hydroxy Propyl Acrylate)와 같은 단관능기 모노머중에서 선택하여 사용한다.The above-mentioned monomers are used as reactive diluents. They include trifunctional monomer such as TMPTA (Trimethylol Propane Triacrylate), 2 functional monomer such as TPGDA (Tripropylene Glycol Diacrylate), HEA (Hydroxy Ethyl Acrylate) and HPA (Hydroxy Propyl Acrylate) Functional monomer is selected and used.

상기한 광개시제는 모노머가 광 중합하는데 필요한 에너지를 가함으로써 모노머가 경화된 후의 고분자 물질로 바뀌도록 광 중합을 개시시키는 역할을 한다.The above-mentioned photoinitiator serves to initiate photopolymerization so that the monomer is converted into a polymer substance after curing by applying energy required for photo-polymerization.

도 2는 이 발명의 일 실시예에 따른 가구용 목재 패널의 제조방법의 흐름도이다.2 is a flowchart of a method of manufacturing a wood panel for furniture according to an embodiment of the present invention.

도 2에 도시되어 있는 바와 같이, 이 발명의 일실시예에 따른 가구용 목재 패널의 제조방법의 구성은, 심재(1)의 표면에 LPM층(2)이 형성된 목재를 준비하는 단계(S10)와, 상기한 LPM층(2)상에 롤코터를 이용하여 친환경 UV 프라이머를 도포하는 단계(S20)와, 상기한 LPM층(2)상에 친환경 UV 프라이머가 도포된 목재를 16.8KW UV 램프 1개 광량의 자외선으로 경화시키는 단계(S30)와, 상기한 친환경 UV 프라이머층(3)상에 롤코터를 이용하여 샌딩 실러를 도포하는 단계(S40)와, 상기한 친환경 UV 프라이머층(3)상에 샌딩 실러가 도포된 목재를 16.8KW UV 램프 3개 광량의 자외선으로 경화시키는 단계(S50)와, 상기한 친환경 UV 프라이머층(3)상에 도포된 샌딩 실러를 연마하는 단계(S60)와, 연마된 샌딩 실러를 브러시로 털어내는 단계(S70)와, 연마된 샌딩실러를 브러시로 털어낸 목재에 발생된 정전기를 제거함과 동시에 에어 샤워를 시키는 단계(S80)와, 상기한 샌딩 실러층(4)상에 커텐코터를 이용하여 친환경 상도를 도포하는 단계(S90)와, 상기한 샌딩 실러층(4)상에 친환경 상도가 도포된 목재를 0.1~0.5 m/s의 풍속으로 25~40도의 온풍을 발생시키는 프레시오프존을 통과시키면서 잔류 유기용제를 제거하는 단계(S100)와, 상기한 프레시오프존을 통과한 목재를 TL 램프존을 통과시키면서 140W TL 램프 100개 광량의 자외선으로 예비 경화를 시키는 단계(S110)와, 상기한 TL 램프존을 통과한 목재를 하이파워존을 통과시키면서 16.8KW UV 램프 5개 광량의 자외선으로 완전 경화를 시키는 단계(S120)와, 상기한 하이파워존을 통과한 목재를 냉각부스를 통과시키면서 제트 샤워를 이용하여 쿨링시키는 단계(S130)와, 냉각된 목재의 친환경 상도층(5)상에 보호랩을 부착시키는 단계(S140)를 포함하여 이루어진다.As shown in FIG. 2, the method for manufacturing a wood panel for furniture according to an embodiment of the present invention includes steps (S10) of preparing wood on which a LPM layer 2 is formed on the surface of a core 1 (S20) of applying an environmentally friendly UV primer on the LPM layer (2) using a roll coater; and applying a green UV primer on the LPM layer (2) (S30) of applying a sanding sealer on the environmentally friendly UV primer layer (3) using a roll coater, and a step (S40) of applying a sanding sealer on the environmentally friendly UV primer layer A step (S50) of curing the wood on which the sanding sealer is applied with ultraviolet rays of three light quantities of 16.8 KW UV lamps, a step (S60) of polishing the sanding sealer applied on the environmentally friendly UV primer layer (3) A step (S70) of pouring the sanding sealer with a brush, and a step (S90) of applying an environmentally-friendly top coat by using a curtain coater on the sanding sealer layer (4), a step (S90) of applying a sand shower sealer layer (S100) of passing residual organic solvent through a fresh off-zone which generates hot air of 25 to 40 degrees at an air velocity of 0.1 to 0.5 m / s on the surface of the fresh off- (S110) of preliminarily curing the wood having passed through the TL lamp zone with ultraviolet rays of a light intensity of 140 lightwave TL lamps, passing the wood passing through the TL lamp zone through a high power zone, (S130) of cooling the wood having passed through the high power zone through a cooling booth using a jet shower (S130); and a step (S130) of cooling the wood through the high- Protection on layer (5) It comprises the step (S140) of attaching.

상기한 TL 램프는 자외선 형광등의 일종이다.The TL lamp described above is a kind of ultraviolet fluorescent lamp.

상기한 구성에 의한, 이 발명의 일실시예에 따른 가구용 목재 패널의 제조방법의 작용은 다음과 같다.The operation of the method for manufacturing a wooden panel for furniture according to an embodiment of the present invention is as follows.

먼저, 심재(1)의 표면에 LPM층(2)이 형성된 목재를 준비한 후에(S10), 상기한 LPM층(2)상에 롤코터를 이용하여 친환경 UV 프라이머를 도포한다(S20).First, a wood material having an LPM layer 2 formed on the surface of the core material 1 is prepared (S10), and an environmentally friendly UV primer is coated on the LPM layer 2 using a roll coater (S20).

이와 같이 LPM층(2)상에 친환경 UV 프라이머를 도포한 후에, LPM층(2)상에 친환경 UV 프라이머가 도포된 목재를 16.8KW UV 램프 1개 광량의 자외선으로 경화시킨다(S30).After the environmentally friendly UV primer is applied on the LPM layer 2, the wood coated with the environmentally friendly UV primer on the LPM layer 2 is cured by one ultraviolet ray of 16.8 KW UV lamp (S30).

이어서, 상기한 친환경 UV 프라이머층(3)상에 롤코터를 이용하여 샌딩 실러를 도포한 후에(S40), 이와 같이 친환경 UV 프라이머층(3)상에 샌딩 실러가 도포된 목재를 16.8KW UV 램프 3개 광량의 자외선으로 경화시킨다(S50).Then, a sanding sealer is coated on the environmentally friendly UV primer layer 3 using a roll coater (S40). Then, the wood coated with the sanding sealer on the environmentally friendly UV primer layer 3 is transferred to a 16.8 KW UV lamp And cured by ultraviolet rays of three light quantities (S50).

다음에, 친환경 UV 프라이머층(3)상에 도포된 샌딩 실러를 연마한 후에(S60), 연마된 샌딩 실러를 브러시로 털어낸다(S70).Next, the sanding sealer applied on the environmentally friendly UV primer layer 3 is polished (S60), and then the polished sanding sealer is brushed off (S70).

이어서, 연마된 샌딩실러를 브러시로 털어낸 목재에 발생된 정전기를 제거함과 동시에 에어 샤워를 시킨 후에(S80), 상기한 샌딩 실러층(4)상에 커텐코터를 이용하여 친환경 상도를 도포한다(S90).Subsequently, the polished sanding sealer is subjected to an air shower (S80) after the static electricity generated in the wood is removed by brushing, and then an environmentally friendly top coat is applied on the sanding sealer layer 4 using a curtain coater S90).

다음에, 상기한 샌딩 실러층(4)상에 친환경 상도가 도포된 목재를 0.1~0.5 m/s의 풍속으로 25~40도의 온풍을 발생시키는 프레시오프존(fresh off zone)을 통과시키면서 잔류 유기용제를 제거하고(S100), 이와 같이 프레시오프존을 통과한 목재를 TL 램프존(TL lamp zone)을 통과시키면서 140W TL 램프 100개 광량의 자외선으로 예비 경화를 시킨 후에(S110), 상기한 TL 램프존을 통과한 목재를 다시 하이파워존(high power zone)을 통과시키면서 16.8KW UV 램프 5개 광량의 자외선으로 완전 경화를 시킨다(S120).Next, the wood coated with the environmentally-friendly top coat on the sanding sealer layer 4 is passed through a fresh off zone which generates hot wind at 25 to 40 degrees at an air velocity of 0.1 to 0.5 m / s, The solvent is removed (S100), and the wood passed through the fresh off zone is preliminarily cured by ultraviolet rays of a light quantity of 100 light of 140 W TL lamp while passing through the TL lamp zone (S110) The wood passing through the lamp zone is completely cured by ultraviolet rays of 5 light of 16.8 KW UV lamp while passing through a high power zone (S120).

이어서, 상기한 하이파워존을 통과한 목재를 냉각부스를 통과시키면서 제트 샤워를 이용하여 쿨링시킨 후에(S130), 냉각된 목재의 친환경 상도층(5)상에 보호랩을 부착시키게 된다(S140).Subsequently, the wood passed through the high power zone is cooled by using a jet shower while passing through the cooling booth (S130), and a protective wrap is attached on the eco-friendly upper layer 5 of the cooled wood (S140) .

이 경우에, 상기한 친환경 상도층(5)상에 광촉매 및 방염 코팅을 한 후에, 상기한 광촉매 및 방염 코팅층(6)상에 보호랩을 부착시킬 수도 있다.In this case, it is also possible to attach a protective wrap on the photocatalyst and the flame-retardant coating layer 6 after the photocatalyst and flame-retardant coating are applied on the environmentally-friendly top coat layer 5.

이와 같이 스티렌(styrene)과 같이 인체에 유해한 화학물질을 사용하지 않고서 친환경 UV 프라이머층과 친환경 상도층을 형성하여 목재를 마감함으로써 사용자 건강을 보호할 수 있게 된다.As described above, it is possible to protect the user's health by forming an environmentally friendly UV primer layer and an environmentally friendly top layer without using chemical substances harmful to the human body such as styrene.

1 : 심재 2 : LPM층
3 : 친환경 UV 프라이머층 4 : 샌딩 실러층
5 : 친환경 상도층 6 : 광촉매 및 방염 코팅층1: Core 2: LPM layer
3: environmentally friendly UV primer layer 4: sanding sealer layer
5: Environmentally friendly top layer 6: Photocatalyst and flame retardant coating layer

Claims (11)

삭제delete 삭제delete 삭제delete 삭제delete 심재의 표면에 LPM층이 형성된 목재를 준비하는 단계와,
상기한 LPM층상에 우레탄 아크릴레이트 수지 20~30 중량%, 모노머 40~50 중량%, 안료 10~20 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하는 친환경 UV 프라이머를 롤코터를 이용하여 도포한 뒤에 16.8KW 용량의 UV 램프를 1개 사용한 광량의 자외선으로 경화시키는 단계와,
상기한 친환경 UV 프라이머층상에 롤코터를 이용하여 샌딩 실러를 도포한 뒤에 16.8KW UV 램프 3개 광량의 자외선으로 경화시키는 단계와,
상기한 친환경 UV 프라이머층상에 도포된 샌딩 실러를 연마한 뒤에 연마된 샌딩 실러를 브러시로 털어낸 후 목재에 발생된 정전기를 제거함과 동시에 에어 샤워를 시키는 단계와,
상기한 샌딩 실러층상에 불포화 폴리에스테르 수지 30~40 중량%, 모노머 50~60 중량%, 광개시제 2~5 중량%, 첨가제 0~5 중량%를 포함하는 친환경 상도를 커텐코터를 이용하여 도포한 뒤에 0.1~0.5 m/s의 풍속으로 25~40도의 온풍을 발생시키는 프레시오프존을 통과시키면서 잔류 유기용제를 제거하는 단계와,
상기한 프레시오프존을 통과한 목재를 TL 램프존을 통과시키면서 140W 용량의 TL 램프를 100개 사용한 광량의 자외선으로 예비 경화를 시킨 후에, 하이파워존을 통과시키면서 16.8KW 용량의 UV 램프를 5개 사용한 광량의 자외선으로 완전 경화를 시키는 단계와,
상기한 하이파워존을 통과한 목재를 냉각부스를 통과시키면서 제트 샤워를 이용하여 쿨링시키는 단계와,
상기한 친환경 상도층상에 광촉매제와 방염제가 혼합되어 있는 광촉매 및 방염 코팅층을 형성하는 단계를 포함하며,
상기한 모노머는 TMPTA(Trimethylol Propane Triacrylate)의 3관능기 모노머, TPGDA(Tripropylene Glycol Diacrylate)의 2관능기 모노머, HEA(Hydroxy Ethyl Acrylate), HPA(Hydroxy Propyl Acrylate)의 단관능기 모노머중에서 하나를 선택하여 사용하는 것을 특징으로 하는 가구용 목재 패널의 제조방법.
Preparing a wood material on which an LPM layer is formed on the surface of the core material,
An environmentally friendly UV primer containing 20 to 30% by weight of a urethane acrylate resin, 40 to 50% by weight of a monomer, 10 to 20% by weight of a pigment, 2 to 5% by weight of a photoinitiator and 0 to 5% A UV lamp having a capacity of 16.8 KW is cured by ultraviolet light having a light quantity using one UV lamp,
Applying a sanding sealer on the environmentally friendly UV primer layer using a roll coater and then curing the UV light with a light quantity of three 16.8 KW UV lamps,
Polishing the sanding sealer applied on the environmentally-friendly UV primer layer, brushing the sanding sealer with the brush, removing the static electricity generated in the wood, and air-showering the sanding sealer,
An environmentally friendly top coat comprising 30 to 40% by weight of an unsaturated polyester resin, 50 to 60% by weight of a monomer, 2 to 5% by weight of a photoinitiator and 0 to 5% by weight of an additive is coated on the sanding sealer layer using a curtain coater Removing residual organic solvent while passing through a fresh off zone generating a warm air of 25 to 40 degrees at an air velocity of 0.1 to 0.5 m / s,
The wood passed through the above-mentioned free-off zone was preliminarily cured with ultraviolet light having a light quantity using 100 TL lamps having a capacity of 140 W while passing through the TL lamp zone. Thereafter, a UV lamp having a capacity of 16.8 KW A step of performing complete curing with ultraviolet light of a used light amount,
Cooling the wood passing through the high power zone using a jet shower while passing through the cooling booth;
Forming a photocatalyst and a flame-retardant coating layer on the environmentally-friendly top layer by mixing a photocatalyst and a flame retardant;
The above-mentioned monomers may be selected from among three functional monomer of TMPTA (Trimethylol Propane Triacrylate), a bifunctional monomer of TPGDA (Tripropylene Glycol Diacrylate), a monofunctional monomer of HEA (Hydroxy Ethyl Acrylate) and HPA (Hydroxy Propyl Acrylate) ≪ / RTI >
삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete
KR1020160005818A 2016-01-18 2016-01-18 Wood panels for furniture, and a method of manufacturing the same KR101819816B1 (en)