KR101738865B1 - Preparing method of light chopping board by double injection molding - Google Patents

Preparing method of light chopping board by double injection molding Download PDF

Info

Publication number
KR101738865B1
KR101738865B1 KR1020160018537A KR20160018537A KR101738865B1 KR 101738865 B1 KR101738865 B1 KR 101738865B1 KR 1020160018537 A KR1020160018537 A KR 1020160018537A KR 20160018537 A KR20160018537 A KR 20160018537A KR 101738865 B1 KR101738865 B1 KR 101738865B1
Authority
KR
South Korea
Prior art keywords
board
reinforcing plate
injection
inner reinforcing
double injection
Prior art date
Application number
KR1020160018537A
Other languages
Korean (ko)
Inventor
박정호
Original Assignee
박정호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박정호 filed Critical 박정호
Priority to KR1020160018537A priority Critical patent/KR101738865B1/en
Application granted granted Critical
Publication of KR101738865B1 publication Critical patent/KR101738865B1/en

Abstract

The present invention relates to a method for preparing a double-injection molded chopping board in which an internal reinforcing plate and a picture sheet are embedded in the plastic chopping board and, more specifically, to a method for preparing a light double-injection molded chopping board which is lighter than an existing double-injection molded chopping board using medium density fiberboard (MDF) as an internal reinforcing plate by using a hard and light porous plastic board as an internal reinforcing plate.

Description

경량 이중사출 도마의 제조방법{Preparing method of light chopping board by double injection molding}BACKGROUND OF THE INVENTION 1. Field of the Invention [0002] The present invention relates to a lightweight double injection molding machine,

본 발명은 플라스틱 재질의 도마 내부에 내부보강판과 그림시트지가 내장되어 있는 이중사출 도마의 제조방법에 관한 것으로, 좀더 상세하게 설명하자면 상기 내부보강판의 재료로서 단단하고 가벼운 다공성 플라스틱 판재를 사용함으로써, MDF(medium density fiberboard)를 내부보강판으로 사용하는 종래의 이중사출 도마에 비해 무게가 절반정도로 가벼운 경량 이중사출 도마의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a double injection board in which an internal reinforcing plate and a picture sheet are embedded in a plastic cutting board. More specifically, the present invention relates to a method of manufacturing a double injection board using a rigid and lightweight porous plastic plate , And a method of manufacturing a lightweight double injection board that is light in weight by half compared to a conventional double injection board using a medium density fiberboard (MDF) as an internal reinforcing plate.

도마는 주방에서 식재료를 다듬거나 절단할 때 사용하는 도구로서, 종래에는 목재 도마를 주로 사용하였으나, 최근에는 다양한 기능과 구조를 갖는 플라스틱 도마가 널리 사용되고 있다. 예를 들면, 국내 등록특허 제10-0483959호(2005년 04월 08일) 및 국내 공개실용신안 제20-2008-0000863호(2008년 05월 07일) 등에는 내부에 그림시트지가 내장되고 플라스틱 수지원료를 이중 사출하여서 제조되는 도마(이하, ‘이중사출 도마’라 한다.)가 소개되어 있다.[0002] A cutting board is a tool used for cutting or cutting foodstuffs in a kitchen. Conventionally, a wood cutting board is mainly used. Recently, a plastic cutting board having various functions and structures is widely used. For example, in domestic registered patent No. 10-0483959 (April 08, 2005) and domestic public utility model 20-2008-0000863 (May 07, 2008), etc., (Hereinafter referred to as a 'double injection board') which is manufactured by double injection of a resin raw material.

첨부 도 1은 종래 이중사출 도마의 구조를 나타낸 것으로, 내부보강판(10)의 양면에 각각 그림시트지(20a,20b)와 투명 또는 반투명 재질의 덮개판(30a,30b)이 적층되어 있다. 그리고, 상기 덮개판(30a,30b)의 테두리에는 각각 상기 내부보강판(10)의 모서리 부분을 둘러싸는 절곡단턱부(31a,31b)가 구비되어 있으며, 상기 절곡단턱부(31a,31b)의 바깥둘레에는 상기 덮개판(30a,30b)을 서로 결합시켜 주는 마감테두리(40)가 사출 성형되어 있다. 그래서, 상기 그림시트지(20a,20b)에 인쇄되어 있는 그림이나 문자, 도안 등이 상기 덮개판(30a,30b)을 통해서 도마 양면으로 투시되기 때문에 제품 디자인이 다양하게 장식할 수 있고, 판촉용이나 홍보용 등으로도 널리 사용된다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 shows a structure of a conventional double injection board. Illustrated sheets 20a and 20b and cover plates 30a and 30b made of transparent or semitransparent material are laminated on both sides of an internal reinforcing plate 10, respectively. The lid plates 30a and 30b are respectively provided with bending step portions 31a and 31b surrounding the corner portions of the inner reinforcing plate 10 and the bending step portions 31a and 31b And a finishing edge 40 for joining the cover plates 30a and 30b to each other is injection-molded on the outer periphery. Thus, since the pictures, characters, and drawings printed on the picture sheets 20a and 20b are viewed through the cover plates 30a and 30b on both sides of the board, the product design can be variously decorated, It is also widely used for promotional purposes.

상기와 같은 종래의 이중사출 도마에서 내부보강판(10)은 도마를 구성하는 플라스틱 수지원료의 사용량을 절감하고 도마의 형태를 물리적으로 지탱해 주는 기능을 하는 것으로, 종래에는 주로 MDF(medium density fiberboard) 판재를 사용해 왔다. 그런데 MDF 판재를 내부보강판(10)으로 사용한 종래의 도마는 무게가 너무 무거워서 제조 및 유통 과정에서 운송 부담이 과중하고, 특히 이를 사용하는 주부들의 손목에 많은 부담을 주는 문제가 있었다.In the conventional double injection molding machine as described above, the internal reinforcing plate 10 functions to reduce the amount of the plastic resin raw material constituting the cutting board and to physically support the shape of the cutting board. Conventionally, the internal reinforcing plate 10 mainly includes a medium density fiberboard ) Plate. However, the conventional board using the MDF plate as the inner reinforcing plate 10 is too heavy, so that the transportation burden is heavy during manufacture and distribution, and especially the wrists of the housewives who use the MDF plate are burdened.

이러한 문제점을 해소하기 위하여 종이 박스의 재료로 널리 사용되는 골판지를 내부보강판(10)으로 사용할 수도 있으나, 상기 골판지는 도마의 형태를 물리적으로 지탱해 주는 지지력이 약하기 때문에 도마의 크기가 소형으로 제한되어야 하는 한계가 있었다. In order to overcome such a problem, a corrugated cardboard widely used as a material of a paper box may be used as the inner reinforcing plate 10. However, since the corrugated cardboard has a weak supporting force to physically support the shape of the board, There was a limit to be made.

또한 상기 내부보강판(10)의 재료로서 단단하고 가벼운 다공성 플라스틱 판재를 사용할 경우, 상기 마감테두리(40)를 사출 성형할 때 상기 덮개판(30a,30b)의 양쪽 절곡단턱부(31a,31b) 사이로 고온 및 고압의 사출재료가 침투하여 상기 내부보강판(10)의 형태를 변형시켜서 결국 불량품을 발생하는 문제가 있었다.
When the rigid and lightweight porous plastic plate material is used as the material of the inner reinforcing plate 10, when the finishing frame 40 is injection-molded, both of the bending step portions 31a and 31b of the cover plates 30a and 30b, The high-temperature and high-pressure injection material penetrates into the inner reinforcing plate 10, thereby deforming the inner reinforcing plate 10 and eventually producing defective products.

등록특허 제10-0483959호(2005년 04월 08일)Registration No. 10-0483959 (April 08, 2005) 공개실용신안 제20-2008-0000863호(2008년 05월 07일)Published Utility Model No. 20-2008-0000863 (May 07, 2008)

이에 본 발명의 목적은 MDF 판재를 내부보강판으로 사용한 종래의 이중사출 도마에 비해 무게가 훨씬 가벼워서 제조 및 유통과정에서 운송 및 취급이 용이하고, 특히 주부들이 주방용으로 사용하기에 편리한 경량 이중사출 도마의 제조방법을 제공하는 것이다.Accordingly, it is an object of the present invention to provide a lightweight double injection molding machine, which is easy to carry and handle in manufacturing and distribution processes, and is particularly convenient for housewives to use in a kitchen, because it is much lighter than a conventional double injection molding machine in which MDF plate is used as an internal reinforcing plate And a method for producing the same.

또한 본 발명의 목적은 내부보강판의 재료로서 단단하고 가벼운 다공성 플라스틱 판재를 사용하더라도 마감테두리를 사출 성형할 때 고온 및 고압의 사출재료에 의해서 상기 내부보강판의 형태가 변형되는 하자를 방지할 수 있는 경량 이중사출 도마의 제조방법을 제공하는 것이다.
It is also an object of the present invention to provide a method of manufacturing an inner reinforcing plate, which can prevent the deformation of the inner reinforcing plate by the injection material of high temperature and high pressure when injection molding the finishing rim, even if a rigid and lightweight porous plastic plate is used as the material of the inner reinforcing plate To provide a method of manufacturing a lightweight double injection board.

본 발명에 따라 제조되는 경량 이중사출 도마는, 내부보강판의 양면에 각각 그림시트지와 투명 또는 반투명 플라스틱 재질의 덮개판이 적층되고, 상기 덮개판의 테두리에는 각각 상기 내부보강판의 모서리 부분을 둘러싸는 절곡단턱부가 구비되어 있으며, 상기 절곡단턱부의 바깥둘레에는 상기 덮개판을 서로 결합시켜 주는 마감테두리가 사출 성형되어 있는 구조로 이루어진다.In the lightweight double injection molding machine manufactured according to the present invention, a sheet of picture paper and a cover plate of transparent or semitransparent plastic material are laminated on both sides of the inner reinforcing plate, and a rim of the inner reinforcement plate A bending step portion is provided on the outer periphery of the bending step portion, and a rim portion for joining the lid plate to each other is injection-molded on the outer periphery of the bending step portion.

삭제delete

본 발명에 따른 경량 이중사출 도마의 제조방법은, 상기 내부보강판으로 단단하고 가벼운 다공성 플라스틱 판재를 사용하고, 상기 내부보강판 주변에는 상기 마감테두리를 사출 성형할 때 고온 고압의 사출재료에 의해서 상기 내부보강판이 변형되는 것을 방지해 주는 내열성 보호대를 배치한 상태로 사출성형 하는 것을 특징으로 한다.A method of manufacturing a lightweight double injection board according to the present invention is characterized in that a rigid and lightweight porous plastic plate is used as the inner reinforcing plate and the outer periphery of the inner reinforcing plate is injection- And the heat resistant protector for preventing the inner reinforcing plate from being deformed is disposed in the outer periphery of the inner reinforcing plate.

본 발명에 따라 제조되는 경량 이중사출 도마는, MDF 판재를 내부보강판으로 사용한 종래의 이중사출 도마에 비해 무게가 절반 정도로 가벼워서 제조 및 유통 과정에서 운송 및 취급이 용이하고, 특히 주부들이 주방용으로 사용하기에 편리한 효과가 있다.The lightweight double injection board manufactured according to the present invention is easy to carry and handle during manufacture and distribution because the weight is about half that of the conventional double injection board using MDF plate as an inner reinforcing board, There is an advantageous effect to be described below.

본 발명에 따른 경량 이중사출 도마의 제조방법은, 마감테두리를 사출 성형할 때 상기 내열성 보호대가 고온 및 고압의 사출재료에 의해서 상기 내부보강판의 형태가 변형되는 것을 방지함으로써 불량품의 발생을 방지할 수 있는 효과가 있다.
The method for manufacturing a lightweight double injection board according to the present invention is a method for manufacturing a lightweight double injection board by preventing the shape of the internal reinforcing plate from being deformed by injection material of high temperature and high pressure when injection molding the finishing rim, There is an effect that can be.

도 1은 통상적인 이중사출 도마의 구조를 나타낸 부분절개 사시도,
도 2는 본 발명의 일 실시예에 따른 경량 이중사출 도마의 구조를 나타낸 분리 사시도,
도 3은 상기 도 2의 이중사출 도마에 대한 부분절개 사시도,
도 4는 본 발명의 다른 실시예에 따른 이중사출 도마의 부분절개 사시도이다.1 is a partially cutaway perspective view showing a structure of a conventional double injection molding machine,
FIG. 2 is an exploded perspective view showing a structure of a lightweight double injection molding machine according to an embodiment of the present invention; FIG.
FIG. 3 is a partially cutaway perspective view of the double injection board of FIG. 2,
4 is a partially cutaway perspective view of a dual injection board according to another embodiment of the present invention.

이하, 도면을 참조하여 본 발명을 상세하게 설명한다. 다만, 첨부한 도 2 내지 도 5는 본 발명에 대한 설명과 이해를 용이하게 하기 위한 실시예를 나타낸 것이므로, 이들 도면에 의해서 본 발명의 권리범위가 제한되는 것은 아니다. 또한, 편의상 명칭과 기능이 동일한 구성요소에 대해서는 구조가 상이하더라도 동일한 도면부호를 부여한다. Hereinafter, the present invention will be described in detail with reference to the drawings. 2 to 5 show embodiments for facilitating explanation and understanding of the present invention, and thus the scope of the present invention is not limited by these drawings. For the sake of convenience, components having the same name and function are given the same reference numerals even if their structures are different.

본 발명에 따라 제조되는 경량 이중사출 도마는, 도 2 내지 도 4에서 보는 바와 같이, 내부보강판(10)의 양면에 각각 그림시트지(20a,20b)와 투명 또는 반투명 재질의 덮개판(30a,30b)이 적층되고, 상기 덮개판(30a,30b)의 둘레 부분에는 마감테두리(40)가 사출 성형되어 있는 구조로 이루어진다.As shown in FIGS. 2 to 4, the lightweight double injection molding machine manufactured in accordance with the present invention is characterized in that picture sheets 20a and 20b and cover plates 30a and 30b made of transparent or translucent materials are formed on both sides of the inner reinforcing plate 10, 30b are stacked on the cover plates 30a, 30b, and a rim 40 is injection-molded around the cover plates 30a, 30b.

먼저 상기 내부보강판(10)은 도마를 구성하는 플라스틱 수지원료의 사용량을 절감하고 도마의 형태를 물리적으로 지탱해 주는 기능을 하는 것으로, 단단하고 가벼운 다공성 플라스틱 판재로 이루어진다.First, the inner reinforcing plate 10 functions to reduce the amount of the plastic resin material used in the cutting board and to physically support the shape of the cutting board. The inner reinforcing plate 10 is made of a rigid and lightweight porous plastic plate material.

상기 내부보강판(10)은 플라스틱 재질의 허니컴 보드(honeycomb board)나 플라스틱 골판지 또는 압축 스티로폼 보드(styrofoam board)로 이루어지는 것이 바람직하다. 여기서, 상기 허니컴 보드는 도 2 및 도 3에서 보는 바와 같이, 육각형 벌집 모양의 셀(cell)이 평면 방향으로 촘촘히 배치되어 있는 판재로서, 각 셀은 상기 평면과 직교하는 방향으로 상하 양면이 개방되어 있다. 상기 허니컴 보드는 다양한 재질과 다양한 규격으로 상용화 되어 있다.The inner reinforcing plate 10 is preferably made of a plastic honeycomb board, a plastic corrugated board, or a compressed styrofoam board. As shown in FIGS. 2 and 3, the honeycomb board is a plate material in which hexagonal honeycomb cells are densely arranged in a planar direction, and each cell has both upper and lower surfaces opened in a direction orthogonal to the plane have. The honeycomb board is commercially available in various materials and various standards.

또한, 플라스틱 골판지는 도 4에서 보는 바와 같이, 종이 박스의 재료로 널리 사용되는 종이 골판지와 동일한 구조를 갖되, 재질이 플라스틱 재질이고 골의 방향이 서로 교차하도록 2층 또는 3층 구조로 적층된 골판지를 사용하는 것이 바람직하다. 그리고 상기 압축 스티로폼 보드는 통상적인 발포 폴리스티렌 보드를 압축하여 강도를 강화시킨 것을 사용한다. 상기 플라스틱 골판지와 압축 스티로폼 보드 역시 상용화 되어 있는 것을 사용할 수 있다.As shown in FIG. 4, the plastic corrugated cardboard has the same structure as that of the paper corrugated cardboard widely used as a material of a paper box, and is made of a plastic material and has a two- or three- Is preferably used. The compressed styrofoam board is made by compressing a conventional expanded polystyrene board and strengthening it. The plastic corrugated cardboard and the compressed styrofoam board may also be used.

상기 내부보강판(10)의 두께는 특별한 제한은 없으나 5 ~ 15mm인 것이 바람직하다. 상기 내부보강판(10)의 두께가 5mm에 미치지 못하면 도마의 형태를 지탱해 주는 지지력이 취약하고, 반대로 15mm를 초과하면 도마의 두께가 너무 두꺼워져서 바람직하지 않다. 상기 내부보강판(10)의 바람직한 두께는 10mm 정도이다.The thickness of the inner reinforcing plate 10 is not particularly limited, but is preferably 5 to 15 mm. If the thickness of the inner reinforcing plate 10 is less than 5 mm, the supporting force for supporting the shape of the board is weak. On the contrary, if the thickness exceeds 15 mm, the thickness of the board becomes too thick. A preferable thickness of the inner reinforcing plate 10 is about 10 mm.

상기 그림시트지(20a,20b)는 예컨대 통상적인 종이 재질이나 합성수지 시트지로 이루어진다. 양쪽 그림시트지(20a,20b)에 인쇄되는 그림이나 문자, 도형 등은 아무런 제한이 없으며, 서로 다를 수도 있고, 같을 수도 있다.The picture sheets 20a and 20b are made of, for example, a typical paper material or a synthetic resin sheet. There are no restrictions on pictures, characters, figures, etc. printed on the two picture sheets 20a and 20b, and they may be different or may be the same.

상기 덮개판(30a,30b)은 도마의 양면을 덮어서 사용자가 음식 재료를 올려놓고 도마질을 하는 부분으로서, 상기 그림시트지(20a,20b)에 인쇄된 내용을 사용자가 투시할 수 있도록 투명 또는 반투명 플라스틱 재질로 이루어진다. 또한, 도마질 하는 칼날이 쉬이 무디어지지 않도록 연질 플라스틱 재질로 이루어진다. 상기 덮개판(30a,30b)의 재료로는 인체에 무해한 폴리에틸렌이나 폴리프로필렌을 사용하는 것이 바람직하다.The cover plates 30a and 30b cover the both sides of the board so that the user places the food material on the board and performs a cutting operation. The cover plates 30a and 30b are made of transparent or translucent plastic such that the user can see the contents printed on the picture sheets 20a and 20b. . In addition, the cutting blade is made of a soft plastic material so as not to be smeared. As the material of the cover plates 30a and 30b, it is preferable to use polyethylene or polypropylene that is harmless to the human body.

상기 덮개판(30a,30b)의 테두리에는 상기 내부보강판(10)의 모서리 부분을 둘러싸는 절곡단턱부(31a,31b)가 구비되어 있다. 양쪽 덮개판(30a,30b)의 절곡단턱부(31a,31b)는 서로 대향하는 방향으로 절곡되어 있어서, 양쪽 절곡단턱부(31a,31b)가 상기 내부보강판(10) 및 그림시트지(20a,20b)의 사변 모서리 부분을 각각 두께 방향으로 덮고 있다.The cover plates 30a and 30b are provided at their edges with folding step portions 31a and 31b surrounding the edge portions of the internal reinforcing plate 10, respectively. The folded step portions 31a and 31b of the two cover plates 30a and 30b are bent in directions opposite to each other so that both of the bent step portions 31a and 31b are in contact with the inner reinforcing plate 10 and the picture sheet 20a, 20b are respectively covered in the thickness direction.

그리고 상기 절곡단턱부(31a,31b)에는 도 2 및 도 4에서 보는 바와 같이 서로 대응하는 부위에 요철결합부(32a,32b)를 형성할 수 있다. 상기 요철결합부(32a,32b)는 상기 덮개판(30a,30b)이 일정한 위치에서 서로 결합하도록 자리를 잡아주는 기능을 한다.As shown in FIGS. 2 and 4, the bending step portions 31a and 31b can be provided with concave-convex engaging portions 32a and 32b at portions corresponding to each other. The concave-convex engaging portions 32a and 32b function to hold the cover plates 30a and 30b to be engaged with each other at a predetermined position.

상기 마감테두리(40)는 상기 덮개판(30a,30b)을 서로 결합시켜 주는 기능을 하는 것으로 상기 절곡단턱부(31a,31b)의 바깥둘레에 사출 성형된다. 즉, 미리 준비해 둔 내부보강판(10)의 양면에 그림시트지(20a,20b)와 덮개판(30a,30b)을 적층한 상태에서 상기 내부보강판(10)의 절곡단턱부(31a,31b)의 바깥둘레에다 상기 마감테두리(40)를 인서트 사출하는 것이다.The finishing rim 40 functions to join the cover plates 30a and 30b to each other and is injection-molded on the outer circumferences of the bending step portions 31a and 31b. That is to say, the bending step portions 31a and 31b of the inner reinforcing plate 10 are stacked on the both surfaces of the inner reinforcing plate 10 prepared beforehand, with the sheet sheets 20a and 20b and the lid plates 30a and 30b being laminated. And inserts the finishing rim 40 on the outer periphery of the frame 40. [

상기 마감테두리(40)의 사출재료로는 통상적으로 폴리에틸렌이나 폴리프로필렌을 사용하는데, 사출시에는 유동성을 확보하기 위하여 고온 및 고압 상태로 사출하게 된다. 이때 고온 및 고압의 사출재료가 양쪽 절곡단턱부(31a,31b) 사이로 침투하여 내부보강판(10)을 녹이는 등 그 형태를 변형시키는 문제가 발생한다. 본 발명에서 내부보강판(10)으로 사용하고 있는 단단하고 가벼운 다공성 플라스틱 판재는 내열성이 취약하기 때문이다.As the injection material of the finishing frame 40, polyethylene or polypropylene is usually used. In order to ensure fluidity, the injection material is injected at a high temperature and a high pressure. At this time, the high-temperature and high-pressure injection material penetrates between the bending step portions 31a and 31b to melt the inner reinforcing plate 10, thereby deforming the shape thereof. This is because the rigid and light porous plastic plate used as the inner reinforcing plate 10 in the present invention is poor in heat resistance.

그래서 상기 내부보강판(10)의 둘레 부위에다 상기 마감테두리(40)의 사출재료가 주입되는 방향으로 적어도 일부 구간에 걸쳐서 내열성 보호대(11)를 배치한다. 상기 내열성 보호대(11)는 상기 마감테두리(40)를 사출 성형할 때 고온 고압의 사출재료에 의해서 상기 내부보강판(10)이 변형되는 것을 방지해 주는 기능을 하는 것으로, 예컨대 상기 내부보강판(10)과 두께가 동일한 MDF 막대나 나무 막대, 또는 내열성 폴리카보네이트 막대 등을 사용할 수 있다.Therefore, the heat resistant protector 11 is disposed on at least a part of the circumference of the inner reinforcing plate 10 in a direction in which the injection material of the finishing rim 40 is injected. The heat resistant protector 11 functions to prevent the inner reinforcing plate 10 from being deformed by injection material of high temperature and high pressure when injection molding the finishing frame 40. For example, MDF bars, wooden bars, or heat-resistant polycarbonate bars having a thickness equal to that of the MDF 10 may be used.

첨부 도면은 사각형 도마를 예시한 것으로, 상기 내부보강판(10) 역시 사각형 구조를 이루고 있다. 이때, 상기 내열성 보호대(11)는 상기 내부보강판(10)의 사변에 모두 설치될 수도 있으나, 상기 마감테두리(40)의 사출재료가 주입되는 방향에 인접한 일변에만 설치되어 있어도 무방하다.In the drawings, a rectangular board is illustrated, and the inner reinforcing plate 10 also has a rectangular structure. At this time, the heat resistant protector 11 may be installed on the oblique side of the inner reinforcing plate 10, but may be provided only on one side adjacent to the injection direction of the injection material of the closing frame 40.

첨부 도 2 및 도 3에서는 상기 사출재료를 손잡이(41) 부분으로 주입하는 것으로 간주하고, 상기 손잡이(41)에 인접하는 일변에만 내열성 보호대(11)가 배치되어 있다. 그러나, 상기 내열성 보호대(11)가 배치된 변과 접하고 있는 다른 두변을 포함하여 모두 세변에다 내열성 보호대(11)를 배치할 수도 있다.2 and 3, it is assumed that the injection material is injected into the knob 41, and the heat resistant protector 11 is disposed only on one side adjacent to the knob 41. [ However, the heat resistant protector 11 may be disposed on all three sides including the other two sides in contact with the side where the heat resistant protector 11 is disposed.

한편, 본 발명은 사각형 도마 이외에 원형이나 타원형, 다각형, 사물 모양 등 거의 형태의 도마에 적용할 수 있다.Meanwhile, the present invention can be applied to almost any type of board, such as a circle, an ellipse, a polygon, an object, etc., in addition to a rectangular board.

이하, 본 발명에 대한 실시예 및 비교예를 설명한다.Hereinafter, examples and comparative examples of the present invention will be described.

[ 실시예 및 비교예 ][Examples and Comparative Examples]

본 발명의 실시예에서는 규격(가로×세로×높이)이 385×230×10mm 인 폴리프로필렌 재질의 허니컴 보드를 내부보강판(10)으로 사용하고, 규격이 10×230× 10mm인 MDF 막대를 내열성 보호대(11)로 사용하여 직사각형 형태의 이중사출 도마를 제조하였다. 이때, 상기 내부보강판(10)의 4변 중에서 손잡이(41)에 인접한 일측 단변 쪽에 상기 내열성 보호대(11)를 배치하고, 상기 손잡이(41)의 안쪽 부위를 통해서 마감테두리(40)를 구성하는 사출재료를 주입 하였다.In the embodiment of the present invention, a honeycomb board made of a polypropylene material having dimensions of 385 x 230 x 10 mm (width x length x height) is used as the inner reinforcing plate 10, and a MDF rod having a size of 10 x 230 x 10 mm is heat- (11) to produce a rectangular shaped double injection board. At this time, the heat resistant protector 11 is disposed on one side of one side of the four sides of the internal reinforcing plate 10 adjacent to the handle 41, and the finishing edge 40 is formed through an inner portion of the handle 41 The injection material was injected.

한편, 비교예에서는 규격이 395×230×10mm 인 MDF 판재를 내부보강판(10)으로 사용하여 직사각형 형태의 이중사출 도마를 제조하였다. 그 외 그림시트지(20a,20b)와 덮개판(30a,30b)은 동일한 것을 사용하였고, 내열성 보호대(11)는 배치하지 않았으며, 마감테두리(40)의 사출 재료 및 사출 조건은 상기 실시예와 동일하게 하였다.On the other hand, in the comparative example, a double injection board having a rectangular shape was manufactured by using a MDF plate having a size of 395 x 230 x 10 mm as an internal reinforcing plate 10. [ The same material is used for the other sheet members 20a and 20b and the cover plates 30a and 30b and the heat resistant protector 11 is not disposed and the injection material and injection condition of the finishing frame 40 are the same as those of the embodiment Respectively.

상기 실시예 및 비교예에 따라 제조된 이중사출 도마에 대하여 각각 무게를 측정한 결과, 실시예 도마의 무게는 평균 100g(±5g)이고, 비교예 도마의 무게는 평균 190g(±5g)인 것으로 나타났다. 이와 같이 본 발명에 따라 제조되는 경량 이중사출 도마는 종래의 이중사출 도마에 비해 무게를 거의 절반 정도로 현저하게 경감 시킬 수 있는 효과가 있다.As a result of weighing each of the double injection boards manufactured according to the above Examples and Comparative Examples, the weight of the example board was 100 g (± 5 g), and the weight of the comparative example board was 190 g (± 5 g) appear. As described above, the lightweight double injection board manufactured according to the present invention has the effect of significantly reducing the weight by about half compared with the conventional double injection board.

또한, 상기 이중사출 도마들을 각각 5명의 여성들에게 제공하고, 각각 한손으로 수회씩 상하로 흔들어 보도록 한 다음 여성들이 느끼는 무게감과 피로감을 조사한 결과, 상기 실시예 도마가 상기 비교예 도마에 비해 훨씬 경미한 무게감과 피로감을 주는 것으로 확인 되었다.In addition, the double injection boards were each provided to five women, and each one of them was shaken up and down several times with one hand. The weight and fatigue felt by the women were examined. As a result, the embodiment board had a much smaller weight And fatigue.

10; 내부보강판 11; 내열성 보호대
20a,20b; 그림시트지 30a,30b; 덮개판
31a,31b; 절곡단턱부 32a,32b; 요철결합부
40; 마감테두리 41; 손잡이10; Internal reinforcing plate 11; Heat Resistant Protector
20a, 20b; Picture sheets 30a, 30b; Cover plate
31a, 31b; Bending step portions 32a, 32b; The concavo-
40; Deadline 41; handle

Claims (5)

삭제delete 삭제delete 삭제delete 내부보강판(10)의 양면에 각각 그림시트지(20a,20b)를 적층하고, 상기 그림시트지(20a,20b)의 양면에는 각각 상기 내부보강판(10)의 모서리 부분을 둘러싸는 절곡단턱부(31a,31b)가 구비되어 있는 투명 또는 반투명 플라스틱 재질의 덮개판(30a,30b)을 덮은 다음, 상기 절곡단턱부(31a,31b)의 바깥둘레에다 상기 덮개판(30a,30b)을 결합시켜 주는 마감테두리(40)를 사출 성형하여서 제조되는 이중사출도마의 제조방법에 있어서,
상기 내부보강판(10)으로는 단단하고 가벼운 다공성 플라스틱 판재로서 플라스틱 허니컴 보드나 플라스틱 골판지 또는 압축 스티로폼 보드를 사용하고, 상기 마감테두리(40)를 사출 성형할 때 상기 내부보강판(10) 주변에 사출재료가 주입되는 방향으로 적어도 일부 구간에 고온 고압의 사출재료에 의해서 상기 내부보강판(10)이 변형되는 것을 방지해 주는 내열성 보호대(11)를 배치한 상태로 사출 성형 하는 것을 특징으로 하는 경량 이중사출 도마의 제조방법.
The sheets 20a and 20b are laminated on both sides of the inner reinforcing plate 10 and on both sides of the sheets of the sheets 20a and 20b are formed folded step portions 30b of the transparent or translucent plastic material provided with the cover plates 30a, 31b and the cover plates 30a, 30b on the outer circumferences of the bent tiers 31a, 31b, A method of manufacturing a double injection board, which is manufactured by injection molding a finishing edge (40)
A plastic honeycomb board, a plastic corrugated board, or a compressed styrofoam board is used as the rigid and lightweight porous plastic plate, and the inner edge of the inner reinforcing plate 10 (11) for preventing the inner reinforcing plate (10) from being deformed by the injection material of high temperature and high pressure in at least a part of the region in the direction of injection of the injection material. (Manufacturing method of double injection board).
제4항에 있어서, 상기 내열성 보호대(11)는 상기 내부보강판(10)과 두께가 동일한 MDF(medium density fiberboard) 막대 또는 나무 막대인 것을 특징으로 하는 경량 이중사출 도마의 제조방법.5. The method of claim 4, wherein the heat resistant protector (11) is a medium density fiberboard (MDF) rod or a wooden bar having the same thickness as the internal reinforcing plate (10).
KR1020160018537A 2016-02-17 2016-02-17 Preparing method of light chopping board by double injection molding KR101738865B1 (en)